Filter composite materials

Abstract

The present invention provides a filtration composite material including multiple layers of filtration media, a method for producing the same, and a method for filtering a liquid stream. [Solution] The filtration composite material is preferably substantially glass-free or completely glass-free. When the composite material is glass-free or substantially glass-free, it preferably exhibits filtration capacity and filtration efficiency equivalent to or better than similar glass-containing filtration media. The composite material comprises a first nonwoven filtration medium containing two-component fibers, filtration efficiency fibers having a fiber diameter in the range of 1 to 5 microns, and microfibrillated fibers; an optional second nonwoven filtration medium; and a third nonwoven filtration medium containing filtration efficiency fibers having a fiber diameter of at least 0.1 microns and less than 1 micron.

Description

Technical Field

[0001] Cross - reference to Related Applications This application claims the benefit of U.S. Provisional Patent Application No. 63 / 004,926 (filed April 3, 2020) and U.S. Provisional Patent Application No. 63 / 081,159 (filed September 21, 2020), and incorporates by reference the disclosures thereof in their entireties herein.

Background Art

[0002] Filter media, such as those used for fuel filtration, often contain glass microfibers. However, in certain types of filtration, the glass microfibers can detach from the filter media, causing environmental pollution or, in the case of filtered fuel, damaging its internal combustion engine.

Summary of the Invention

Means for Solving the Problems

[0003] Disclosed herein are composite materials comprising multi - layers of filter media, methods of making such composite materials, and methods of using such composite materials. These compositions are preferably substantially glass - free or glass - free and exhibit a filtration capacity and filtration efficiency equal to or greater than that of similar glass - containing filter media.

[0004] In one embodiment, the disclosure describes a composite material comprising a first nonwoven filter medium; optionally, a second nonwoven filter medium; and a third nonwoven filter medium. The composite material is substantially free of glass fibers. The first nonwoven filter medium comprises 40% to 90% by weight of first binary fibers having a fiber diameter in the range of 5 to 50 microns and a fiber length in the range of 0.1 cm to 15 cm; 0% to 25% by weight of first high-filtration efficiency fibers having a fiber diameter in the range of 1 to 5 microns; and 10% to 60% by weight of first microfibrillated fibers, most of which have a transverse dimension of up to 4 microns. The optional second nonwoven filter medium includes 40% to 90% by weight of second bicomponent fibers having a fiber diameter in the range of 5 to 50 microns and a fiber length in the range of 0.1 cm to 15 cm; 0% to 25% by weight of second high-filtration efficiency fibers having a fiber diameter in the range of 1 to 5 microns; and 10% to 60% by weight of second microfibrillated fibers, most of which have a transverse dimension of up to 4 microns. The third nonwoven filter medium includes low-filtration efficiency fibers having a fiber diameter of at least 0.1 microns and less than 1 micron.

[0005] In some embodiments, the structural polymer portion of the two-component fiber has a melting point of at least 240°C, and the binder polymer portion of the two-component fiber has a melting point in the range of 100°C to 190°C.

[0006] In some embodiments, the first high-filtration efficiency fiber comprises polyethylene terephthalate (PET), the second high-filtration efficiency fiber comprises PET, or both the first and second high-filtration efficiency fibers comprise PET.

[0007] In some embodiments, the low-filtration efficiency fibers have a fiber diameter in the range of 0.6 microns to 0.8 microns.

[0008] In some embodiments, the low-filtration efficiency fibers include polyethylene terephthalate (PET).

[0009] In some embodiments, the composite material is substantially resin-free.

[0010] In some embodiments, the composite material does not contain glass fibers.

[0011] In some embodiments, the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium are separate layers.

[0012] In some embodiments, the nonwoven filtration media are configured such that the liquid passes through a first nonwoven filtration medium, then a second nonwoven filtration medium, and then a third nonwoven filtration medium.

[0013] In some embodiments, the nonwoven filter medium further includes a support layer. The third nonwoven filter medium may be in contact with the support layer.

[0014] In some embodiments, the microfibrillated fibers include microfibrillated cellulose fibers.

[0015] In another embodiment, the disclosure describes a method for filtering a liquid stream, which includes passing a liquid stream containing contaminants through a composite nonwoven fabric filter medium described herein to remove the contaminants from the liquid stream. The liquid stream may contain air.

[0016] In another embodiment, the present disclosure describes a method for producing a composite material as described herein, the method comprising independently producing a first nonwoven filter medium, a second nonwoven filter medium, and a third nonwoven filter medium.

[0017] As used herein, a micron is equivalent to a micrometer (μm).

[0018] As used herein, “fiber” has an aspect ratio (i.e., length to transverse dimension) greater than 3:1, preferably greater than 5:1. For example, fiberglass typically has an aspect ratio greater than 100:1. In this context, its “transverse dimension” is either the width (two-dimensional) or diameter (three-dimensional) of the fiber. The term “diameter” refers to either the diameter of the circular cross-section of the fiber or the maximum cross-sectional dimension of the non-circular cross-section of the fiber. The fiber length may be finite or infinite, depending on the desired result.

[0019] As used herein, "β ratio" or "β" refers to the ratio of upstream particles to downstream particles under steady flow conditions (ISO 16889:2008), which will be explained in the Examples section. The higher the filter efficiency, the higher this β ratio. The β ratio is defined by the following equation:

number

[0020] As used herein, the term "substantially free" indicates that the filter medium does not contain the component in question (e.g., glass fibers or resin) in an amount that substantially affects either the activity or function of the filter medium. The term is intended to mean that the filter medium contains only a negligible amount of the component that does not substantially contribute to its filtration performance. For example, a filter medium that is substantially free of glass may contain less than 1% by weight of glass fibers.

[0021] As used herein, the term "free" indicates that the filter medium does not contain any of the components mentioned (e.g., glass fibers or resins). For example, a "glass-free" filter medium contains no glass, and a "resin-free" medium contains no resins.

[0022] Where a standard test method (e.g., ASTM, TAPPI, etc.) is mentioned, unless otherwise specified, it refers to the latest version of that method available at the time of filing of this disclosure.

[0023] The terms "preferred" or "preferred" indicate that, in certain environments, embodiments of the present invention may provide certain benefits. However, other embodiments may also be preferred in the same or other environments. Furthermore, the selection of one or more preferred embodiments does not mean that other embodiments are useless, nor is there any intention to exclude other embodiments from the scope of this specification.

[0024] The term "includes" and its derivatives are not limited in meaning when they appear in this specification and the claims. Such terms are understood to mean that they include the steps or elements or groups of steps or elements described, but not that they exclude other steps or elements or groups of steps or elements.

[0025] "Consists of" means that it includes and is limited to everything that follows the phrase "consists of." Thus, the phrase "consists of" indicates that the enumerated elements are necessary or essential and that no other elements may be present. "Essentially consists of" means that it includes the elements enumerated after this phrase, and is limited to other elements that do not interfere with or contribute to the activity or action specified in this disclosure for the enumerated elements. Thus, the phrase "essentially consists of" indicates that the enumerated elements are necessary or essential, but the other elements are optional and may or may not be present depending on whether they have a material effect on the activity or action of the enumerated elements.

[0026] Unless otherwise specified, "a," "an," "that," and "at least one" are used interchangeably and mean one or more.

[0027] As used herein, the term "or" is used in its ordinary sense, generally including "and / or," unless the context clearly indicates otherwise.

[0028] The term "and / or" means one or all of the enumerated elements or any combination of two or more of the enumerated elements.

[0029] In this specification, when a numerical range is described using endpoints, all numerical values ​​within that range are also included (for example, 1 to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, 5, etc.).

[0030] In this specification, “up to the maximum number” (for example, up to 50) includes that number (for example, 50).

[0031] The term "in the range" or "within a range" (and similar phrases) includes the end of the range being described.

[0032] In any of the methods disclosed herein, which include separate steps, those steps may be carried out in any order that is appropriate. If appropriate, two or more steps may be combined and carried out simultaneously.

[0033] All titles are provided for the reader's convenience and should not be assumed, unless otherwise stated, to be used to limit the meaning of the text that follows.

[0034] Throughout this specification, references to “one embodiment,” “embodiment,” “a particular embodiment,” or “some embodiments” mean that the specific features, configurations, compositions, or characteristics described in relation to an embodiment are included in at least one embodiment of this disclosure. Therefore, the appearance of such phrases in various parts throughout this specification does not necessarily refer to the same embodiment of this disclosure. Furthermore, specific features, configurations, compositions, or characteristics can be combined in any appropriate manner in one or more embodiments.

[0035] Unless otherwise specified, all figures used herein and in the claims, such as amounts and molecular weights of components, should be understood to be modified in all cases by the term "approximately." The term "approximately" as used herein in relation to measured quantities refers to the variation in the measured quantity expected by a person skilled in the art who performs the measurement and takes a level of care commensurate with the purpose of the measurement and the precision of the measuring instrument used. Therefore, unless otherwise indicated, the numerical parameters described herein and in the claims are approximations that may vary depending on the desired properties to be obtained by the invention. At the very least, and not as an attempt to limit the principle of equivalence to the claims, each numerical parameter should be interpreted by applying the usual rounding rules, at least in light of the reported number of significant figures.

[0036] Although the numerical ranges and parameters representing the broad scope of this invention are approximations, the numerical values ​​shown in specific examples are reported as accurately as possible. However, all numerical values ​​inherently include a range that inevitably arises from the standard deviation found in each test measurement.

[0037] The above summary of the present invention is not intended to describe each disclosed embodiment or all practices of the invention. The following description more specifically illustrates exemplary embodiments. In several parts of this specification, guidance is provided by lists of examples that can be used in various combinations. In any case, the enumerated lists serve only as representative groups and should not be construed as exclusive lists. [Brief explanation of the drawing]

[0038] [Figure 1A] This figure shows the supported filtration capacity of the composite material prepared according to the description in Example 1. [Figure 1B] This figure shows the filtration efficiency of a composite material containing a fine fiber layer prepared according to the description in Example 1. [Figure 2A] This is a schematic diagram of an exemplary composite material that can be prepared in some embodiments according to the description in Example 1. [Figure 2B] This is a schematic diagram illustrating a composite material. [Figure 2C] This is a schematic diagram of an exemplary composite material that can be prepared in some embodiments according to the description in Example 2. [Modes for carrying out the invention]

[0039] This disclosure describes composite materials comprising multiple layers of filtration media, methods for producing such composite materials, and methods for using such composite materials. These compositions are preferably substantially glass-free or glass-free and exhibit filtration capacity and filtration efficiency equivalent to or better than similar glass-containing filtration media.

[0040] composite material In one embodiment, the disclosed material is a composite material comprising a plurality of nonwoven filter media. In some embodiments, each of the nonwoven filter media is preferably substantially glass-free or glass-free.

[0041] The composite material includes a first nonwoven filter medium, an optional second nonwoven filter medium, and a third nonwoven filter medium. The first nonwoven filter medium includes a first binary fiber; a first high-filtration efficiency fiber having a fiber diameter in the range of 1 to 5 microns; and a first microfibrillated fiber. If a second nonwoven filter medium is present, it includes a second binary fiber; a second high-filtration efficiency fiber having a fiber diameter in the range of 1 to 5 microns; and a second microfibrillated fiber. The third nonwoven filter medium includes a low-filtration efficiency fiber having a fiber diameter of at least 0.1 microns and less than 1 micron. As used herein, "high-filtration efficiency fiber" refers to a fiber having a fiber diameter in the range of 1 to 5 microns. As used herein, "low-filtration efficiency fiber" refers to a fiber having a fiber diameter of at least 0.1 microns and less than 1 micron.

[0042] In some embodiments, the low-filtration efficiency fibers preferably include polyethylene terephthalate (PET). In some embodiments, the first high-filtration efficiency fibers preferably include PET. In some embodiments, the second high-filtration efficiency fibers preferably include PET.

[0043] In some embodiments, one or more fibers of the composite material or a layer of the composite material may be selected or treated to alter the electrostatic charge of the medium. Typical examples of such charges include layers of positive or negative charges trapped on or near the surface of the polymer, or charge clouds stored within the polymer body. These charges may also include polarization charges frozen within the molecular dipole arrangement. Methods for charging materials are well known to those skilled in the art. These methods include, for example, heating, liquid contact, electron beam, plasma, and corona discharge.

[0044] In some embodiments, the composite material further includes a support layer.

[0045] In some embodiments, the first nonwoven filter medium, an optional second nonwoven filter medium (if present), and a third nonwoven filter medium are separate layers. That is, there is no gradient between the first nonwoven filter medium and the second nonwoven filter medium, or between the second nonwoven filter medium and the third nonwoven filter medium. If the second nonwoven filter medium is not present, there is no gradient between the first nonwoven filter medium and the third nonwoven filter medium.

[0046] In some embodiments, the first nonwoven filter medium is in contact with the second nonwoven filter medium, and the second nonwoven filter medium is in contact with the third nonwoven filter medium. If the composite material further includes a support layer, the third nonwoven filter medium may be in contact with the support layer.

[0047] In some embodiments, the composite material is configured such that a liquid passes through a first nonwoven filter medium, then a second nonwoven filter medium, and then a third nonwoven filter medium.

[0048] In some embodiments, if the composite material includes a support layer, the composite material is configured such that a liquid passes through a first nonwoven filter medium, then a second nonwoven filter medium, then a third nonwoven filter medium, and then the support layer.

[0049] In some embodiments, the first nonwoven filter medium is in contact with the third nonwoven filter medium. If the composite material further includes a support layer, the third nonwoven filter medium may also be in contact with the support layer.

[0050] In some embodiments, the composite material is configured such that a liquid passes through a first nonwoven filter medium, and then a third nonwoven filter medium. If the composite material further includes a support layer, the composite material is configured such that a liquid passes through a first nonwoven filter medium, then a third nonwoven filter medium, and then the support layer.

[0051] In some embodiments, the composite material is substantially resin-free.

[0052] The composite material is substantially free of glass (including, for example, glass fibers). In some embodiments, the composite material is glass-free.

[0053] In one exemplary embodiment, the composite material includes a first nonwoven filter medium, an optional second nonwoven filter medium, and a third nonwoven filter medium. The first nonwoven filter medium includes 40% to 90% by weight of first binary fibers having a fiber diameter in the range of 5 to 50 microns and a fiber length of 0.1 cm to 15 cm; 0% to 25% by weight of first high-filtration efficiency fibers; and 10% to 60% by weight of first microfibrillated fibers (the majority of the microfibrillated fibers having a transverse dimension of up to 4 microns). The optional second nonwoven filter medium contains 40% to 90% by weight of second bicomponent fibers having a fiber diameter in the range of 5 to 50 microns and a fiber length of 0.1 cm to 15 cm; 0% to 25% by weight of second high-filtration efficiency fibers; and 10% to 60% by weight of second microfibrillated fibers (the majority of which have a transverse dimension of up to 4 microns). The third nonwoven filter medium contains low-filtration efficiency fibers.

[0054] One exemplary embodiment is shown in Figure 2C.

[0055] As explained in Example 1, by adding an electrospun fiber layer with a diameter of 1 μm to the filter medium composite material, the filtration efficiency of the composite material is improved compared to the composite material without the fiber layer. As further explained in Example 2 and shown in Figure 2C, it is also possible to replace the fiber layer with a layer containing low-filtration-efficiency fiber, and the composite material obtained in this way is expected to have a filtration efficiency comparable to that of the composite material containing the fiber layer.

[0056] The results of Example 1 were unexpected, because previous reports had stated that it was undesirable to provide intermediate layers between media layers, and that a gradient structure should be pursued instead (see, for example, U.S. Patent Application Publication No. 2014 / 0360145). Speaking without being bound by theory, it is thought that providing intermediate layers between media layers (including layers of nonwoven filtration media containing layers of fine fibers with low filtration efficiency, and layers of filtration media functioning as a support layer) would enable higher filtration efficiency than when using a gradient structure, because the heterogeneity of each layer does not extend throughout the entire thickness direction of the media.

[0057] First and second nonwoven filter media Each of the first nonwoven filtration medium and an optional second nonwoven filtration medium (if present) includes two-component fibers, high-filtration-efficiency fibers having a fiber diameter in the range of 1 to 5 microns, and microfibrillated fibers.

[0058] In some embodiments, either or both of the first nonwoven filtration medium and the second nonwoven filtration medium function as a support layer, i.e., a filter medium that disperses the location where contaminants accumulate in the depth direction of the medium. An exemplary embodiment in which both the first and second nonwoven filtration mediums function as a support layer is shown in Figure 2C. An exemplary embodiment in which the second nonwoven filtration is not included is shown in Figure 2B.

[0059] In some embodiments, one or both of the first non-woven filter medium and the second non-woven filter medium have a solidity of at least 2%, at least 3%, at least 4%, at least 5%, at least 6%, at least 7%, at least 8%, at least 9%, or at least 10%. In some embodiments, the non-woven filter medium has a solidity of up to 5%, up to 6%, up to 7%, up to 8%, up to 9%, up to 10%, up to 11%, up to 12%, up to 13%, up to 14%, up to 15%, up to 16%, up to 17%, up to 18%, up to 19%, or up to 20%. In one exemplary embodiment, the first non-woven filter medium has a solidity within the range of 5% to 15%. In one exemplary embodiment, the second non-woven filter medium has a solidity within the range of 5% to 15%. In some embodiments, the solidity is preferably measured as described in the examples.

[0060] In some embodiments, one or both of the first non-woven filter medium and the second non-woven filter medium are at least 20 g / m 2 , at least 24 g / m 2 , at least 25 g / m 2 , at least 30 g / m 2 , at least 35 g / m 2 , at least 40 g / m 2 , at least 50 g / m<00管理用009>, at least 60 g / m 2 , or at least 70 g / m 2 and have a basis weight. In some embodiments, the non-woven filter medium is up to 25 g / m 2 up to, up to 30 g / m 2 up to, up to 35 g / m 2 up to, up to 40 g / m 2 up to, up to 50 g / m 2 up to, up to 60 g / m 2 up to, up to 70 g / m 2 up to, up to 75 g / m2 Up to a maximum of 80g / m 2 Up to a maximum of 85g / m² 2 Up to a maximum of 90g / m 2 Up to a maximum of 95g / m 2 Up to a maximum of 100g / m 2 Up to, or a maximum of 105g / m² 2 It has a basic weight up to [a certain value]. In one exemplary embodiment, the first nonwoven filter medium is 24 g / m². 2 ~100g / m 2 It has a basic weight within the range of . In one exemplary embodiment, the second nonwoven filter medium is 24 g / m². 2 ~100g / m 2 It has a base weight within the range. In some embodiments, the base weight is preferably measured using ASTM D646-13.

[0061] In some embodiments, either or both of the first and second nonwoven filter media have pore sizes of at least 0.5 microns, at least 1 micron, at least 1.5 microns, at least 2 microns, at least 3 microns, at least 5 microns, or at least 10 microns. In some embodiments, the nonwoven filter media have pore sizes up to 5 microns, up to 10 microns, up to 15 microns, or up to 20 microns. In one exemplary embodiment, the first nonwoven filter media has pore sizes in the range of 0.5 microns to 20 microns. In another exemplary embodiment, the second nonwoven filter media has pore sizes in the range of 0.5 microns to 20 microns. In yet another exemplary embodiment, the first nonwoven filter media has pore sizes in the range of 2 microns to 15 microns. In yet another exemplary embodiment, the second nonwoven filter media has pore sizes in the range of 2 microns to 15 microns. When used herein, pore size refers to the flow pore size calculated according to ASTM F316-03.

[0062] In some embodiments, either or both of the first and second nonwoven filter media have a thickness of at least 0.1 mm, at least 0.12 mm, at least 0.15 mm, or at least 0.2 mm. In some embodiments, the nonwoven filter media have a thickness of up to 0.2 mm, up to 0.4 mm, up to 0.5 mm, up to 0.7 mm, or up to 1 mm. In one exemplary embodiment, the first nonwoven filter media has a thickness in the range of 0.12 mm to 1 mm. In one exemplary embodiment, the second nonwoven filter media has a thickness in the range of 0.12 mm to 1 mm. In some embodiments, the thickness of the filter media is preferably measured using a foot pressure of 1.5 psi according to the TAPPI T411 om-15 test method.

[0063] In some embodiments, either or both of the first nonwoven filter medium and the second nonwoven filter medium are at least 1 ft in 0.5 inches of water. 3 / ft 2 / min, at least 5ft in 0.5 inches of water 3 / ft 2 / min, or at least 10ft in 0.5 inches of water 3 / ft 2 It has a permeability of / min. In some embodiments, the nonwoven filter medium has a permeability of up to 10 ft in 0.5 inches of water. 3 / ft 2 Up to 20ft in 0.5 inches of water per minute 3 / ft 2 Up to 50 ft in 0.5 inches of water per minute 3 / ft 2 Up to 75ft in 0.5 inches of water per minute 3 / ft 2 Up to 100 ft in 0.5 inches of water per minute, or 0.5 inches in water. 3 / ft 2 It has permeability up to 1 ft / min. In one exemplary embodiment, the first nonwoven filter medium is 0.5 inches of water at 1 ft 3 / ft2 From / min, 100ft with 0.5 inches of water 3 / ft 2 It has permeability within a range of up to / min. In one exemplary embodiment, the second nonwoven filter medium is 1 ft in 0.5 inches of water. 3 / ft 2 From / min, 100ft with 0.5 inches of water 3 / ft 2 It has permeability within a range of up to / min. In another exemplary embodiment, the first nonwoven filter medium is 10 ft in 0.5 inches of water. 3 / ft 2 From / min, 75ft in 0.5 inches of water 3 / ft 2 It has permeability within a range of up to / min. In another exemplary embodiment, the second nonwoven filter medium is 10 ft in 0.5 inches of water. 3 / ft 2 From / min, 75ft in 0.5 inches of water 3 / ft 2 It has permeability within a range of up to / min. In some embodiments, it is preferable to measure air permeability according to ASTM D737-18.

[0064] In some embodiments, either or both of the first nonwoven filter medium and the second nonwoven filter medium are substantially resin-free.

[0065] In some embodiments, either or both of the first nonwoven filter medium and the second nonwoven filter medium are substantially free of glass fibers.

[0066] Two-component fiber Each of the first and second filtration media contains a binary fiber. Any suitable binary fiber can be used in each medium, and these binary fibers can be selected according to the intended use of the medium.

[0067] In some embodiments, the first nonwoven filter medium and the second nonwoven filter medium each contain at least 25% by weight, at least 30% by weight, at least 35% by weight, at least 40% by weight, at least 45% by weight, at least 50% by weight, at least 55% by weight, at least 60% by weight, at least 65% by weight, or at least 70% by weight of bicomponent fibers. In some embodiments, the first filter medium and the second filter medium each contain up to 30% by weight, up to 35% by weight, up to 40% by weight, up to 45% by weight, up to 50% by weight, up to 55% by weight, up to 60% by weight, up to 65% by weight, up to 70% by weight, up to 75% by weight, up to 80% by weight, up to 85% by weight, or up to 90% by weight of bicomponent fibers. In one exemplary embodiment, the first filter medium contains 40% to 90% by weight of bicomponent fibers. In one exemplary embodiment, the second filter medium contains 40% to 90% by weight of binary fibers. In another exemplary embodiment, the first filter medium contains 40% to 75% by weight of binary fibers. In one exemplary embodiment, the second filter medium contains 40% to 75% by weight of binary fibers.

[0068] In some embodiments, the binary fiber has a fiber diameter of at least 1 micron, at least 5 microns, at least 10 microns, at least 15 microns, or at least 20 microns. In some embodiments, the binary fiber has a fiber diameter of up to 5 microns, up to 10 microns, up to 15 microns, up to 20 microns, up to 25 microns, up to 30 microns, up to 35 microns, up to 40 microns, up to 45 microns, or up to 50 microns. In one exemplary embodiment, the binary fiber has a fiber diameter in the range of 5 microns to 50 microns. In another exemplary embodiment, the binary fiber has a fiber diameter in the range of 5 microns to 25 microns. In yet another exemplary embodiment, the binary fiber has a fiber diameter of 14 microns.

[0069] In some embodiments, the binary fiber has a fiber length of at least 0.1 cm, at least 0.5 cm, or at least 1 cm. In some embodiments, the binary fiber has a fiber length of up to 0.5 cm, up to 1 cm, up to 5 cm, up to 10 cm, or up to 15 cm. In one exemplary embodiment, the binary fiber has a fiber length in the range of 0.1 cm to 15 cm. In another exemplary embodiment, the binary fiber has a fiber length of 6 mm.

[0070] In some embodiments, the two-component fiber includes a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a higher melting point than the binder polymer portion.

[0071] The structural polymer portion and the binder polymer portion can be made from any suitable material. For example, the structural polymer portion may contain PET, and the binder polymer portion may contain copolymer PET (coPET). In additional examples, the structural polymer portion may contain PET, and the binder polymer portion may contain: polyethylene (PE), PET, nylon, polypropylene (PP), polytetrafluoroethylene (PTFE), polyethersulfone (PES), polyphenylene sulfide (PPS), meta-aramid, or para-aramid. In further examples, the binder polymer portion may contain: polyethylene (PE), polylactic acid (PLA), nylon, ethylene vinyl alcohol (EVOH), polyvinyl chloride (PVC), polyvinylidene fluoride (PVDF) (e.g., KYNAR), or any other polymer or modified polymer designed to have a lower melting point than the polymer of the core structure.

[0072] In some embodiments, the structural polymer portion is the core, and the thermoplastic binder polymer portion is the sheath of the two-component fiber.

[0073] In some embodiments, the structural polymer portion of the binary fiber has a melting point of at least 240°C, and the binder polymer portion of the binary fiber has a melting point of up to 115°C. An exemplary binary fiber in which the structural polymer portion has a melting point of at least 240°C and the binder polymer portion has a melting point of up to 115°C is 271P, which is a 14 μm diameter fiber available from Advansa (Hamm, Germany).

[0074] In some embodiments, the structural polymer portion of the binary fiber has a melting point of at least 240°C, and the binder polymer portion of the binary fiber has a melting point in the range of 100°C to 190°C. In one exemplary embodiment, the structural polymer portion of the binary fiber has a melting point of at least 240°C, and the binder polymer portion of the binary fiber has a melting point in the range of 120°C to 170°C. In another exemplary embodiment, the structural polymer portion of the binary fiber has a melting point of at least 240°C, and the binder polymer portion of the binary fiber has a melting point in the range of 140°C to 160°C.

[0075] Examples of two-component fibers in which the structural polymer portion has a melting point of at least 240°C and the binder polymer portion has a melting point in the range of 100°C to 190°C include: TJ04CN (with a binder polymer portion having a melting point of 110°C), TJ04BN (with a binder polymer portion having a melting point of 150°C) (both available from Teijin Fiber Limited (Osaka, Japan); 271P (with a binder polymer portion having a melting point of 110°C) (available from Advansa (Hamm, Germany); and T-202 or T-217 (each having a binder polymer portion having a melting point of 180°C) (both available from Fiber Innovation Technology, Inc. (Johnson City, TN)).

[0076] In some embodiments, the first and second binary fibers may comprise two different binary fibers, or a combination of two different binary fibers. In one exemplary embodiment, the binary fiber may comprise a first binary fiber whose structural portion has a melting point of at least 240°C and whose binder polymer portion has a melting point up to 115°C, and a second binary fiber whose structural polymer portion has a melting point of at least 240°C and whose binder polymer portion has a melting point in the range of 100°C to 190°C. For example, both Advansa 271P and TJ04BN are examples of such binary fibers.

[0077] High filtration efficiency fibers The first and second filtration media each contain "high-filtration efficiency fibers," where "high-filtration efficiency fibers" are fibers having a fiber diameter in the range of 1 to 5 microns when used herein. In some embodiments, one or both of the first and second nonwoven filtration media do not contain high-filtration efficiency fibers.

[0078] In some embodiments, the high-filtration efficiency fibers are preferably PET fibers. In some embodiments, the high-filtration efficiency fibers may be substantially made of PET. In some embodiments, the high-filtration efficiency fibers may be made of PET.

[0079] Additionally or as an alternative, the low-filtration efficiency fibers may include: nylon, acrylic, rayon, polypropylene, polyethylene, ethylene vinyl alcohol (EVOH), polylactic acid (PLA), polyvinyl alcohol (PVA), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE), or other suitable fused polymers.

[0080] In some embodiments, the first and second filtration media each contain at least 0% by weight, at least 0.1% by weight, at least 1% by weight, at least 5% by weight, at least 10% by weight, at least 15% by weight, at least 20% by weight, or at least 25% by weight of high-filtration efficiency fibers. In some embodiments, the first and second filtration media each contain up to 15% by weight, up to 20% by weight, or up to 25% by weight of high-filtration efficiency fibers. In one exemplary embodiment, the first filtration media contains 0% to 25% by weight of high-filtration efficiency fibers. In another exemplary embodiment, the first filtration media contains 10% to 25% by weight of high-filtration efficiency fibers. In yet another exemplary embodiment, the second filtration media contains 10% to 25% by weight of high-filtration efficiency fibers.

[0081] In some embodiments, the high-filtration efficiency fibers have a fiber diameter of at least 1 micron, at least 1.5 microns, at least 2 microns, at least 3 microns, or at least 4 microns. In some embodiments, the high-filtration efficiency fibers have a fiber diameter of up to 1.5 microns, up to 2 microns, up to 3 microns, up to 4 microns, or up to 5 microns. For example, in one exemplary embodiment, the high-filtration efficiency fibers have a fiber diameter in the range of 2 to 4 microns. In another exemplary embodiment, the high-filtration efficiency fibers have a fiber diameter of 2.7 microns. In yet another exemplary embodiment, the high-filtration efficiency fibers have a fiber diameter of 2.5 microns.

[0082] In several examples, the high-filtration efficiency fibers contain PET and have a fiber diameter of 2.7 microns.

[0083] In some embodiments, the high-filtration efficiency fibers have a length of at least 0.5 mm, at least 1 mm, or at least 1.5 mm. In some embodiments, the high-filtration efficiency fibers have a length of up to 10 mm, up to 11 mm, up to 12 mm, or up to 15 mm. In one exemplary embodiment, the high-filtration efficiency fibers have a length in the range of 1 mm to 15 mm. In a further exemplary embodiment, the high-filtration efficiency fibers have a length in the range of 1 mm to 12 mm.

[0084] In some embodiments, if the high-filtration-efficiency fibers include PET, the PET has a melting point of at least 250°C, more preferably at least 275°C, and even more preferably at least 290°C.

[0085] Microfibrillated fibers Each of the first and optional second filtration media contains microfibrillated fibers. As used herein, microfibrillated fibers are fibers that have been processed to produce fibers with a larger surface area and a more branched structure than unprocessed fibers.

[0086] In some embodiments, the microfibrillated fibers may be microfibrillated acrylic fibers, including, for example, fibrillated CFF fibers (available from Engineered Fiber Technology (Shelton, CT)). In some embodiments, the microfibrillated fibers may be microfibrillated cellulose fibers, including, for example, rayon such as Lyocell or TENCEL. In some embodiments, the microfibrillated fibers may be microfibrillated para-aramid fibers, including, for example, TWARON Pulp (Teijin Aramid, BV (The Netherlands)). In some embodiments, the microfibrillated fibers may be microfibrillated liquid crystal polymers (LCPs), including, for example, microfibrillated VECTRAN fibers (available from Engineered Fiber Technology (Shelton, CT)). In some embodiments, the microfibrillated fibers may be microfibrillated poly-p-phenylenebenzobisoxazole (PBO) fibers, including, for example, fibrillated ZYLON fibers (available from Engineered Fiber Technology (Shelton, CT)).

[0087] In some embodiments, the first and second filtration media each contain at least 10% by weight, at least 15% by weight, at least 20% by weight, at least 25% by weight, at least 30% by weight, at least 35% by weight, at least 40% by weight, at least 50% by weight, or at least 55% by weight of microfibrillated fibers. In some embodiments, the filtration media contains up to 15% by weight, up to 20% by weight, up to 25% by weight, up to 30% by weight, up to 35% by weight, up to 40% by weight, up to 45% by weight, up to 50% by weight, up to 55% by weight, or up to 60% by weight of microfibrillated fibers. In one exemplary embodiment, the filtration media contains 10% to 60% by weight of microfibrillated fibers. In another exemplary embodiment, the filtration media contains 10% to 40% by weight of microfibrillated fibers.

[0088] In some embodiments, the microfibrillated fibers may contain microfibrillated cellulose. As used herein, microfibrillated cellulose (MFC) refers to a material as defined by G. Chinga-Carrasco, Nanoscale Research Letters, 2011;6:417: “MFC material” consists of (1) nanofibrils, (2) small fibrous microparticles, (3) fibrous fragments, and (4) fibers. This suggests that MFC is not necessarily synonymous with microfibrils, nanofibrils, or any other cellulose nanostructure. However, a properly manufactured MFC material contains nanostructures, i.e., nanofibrils, as its main component. The diameters of these components (or, in the case of microfibrillated cellulose fibers, the "lateral dimensions") are reproduced in Table 1 of the same literature, and they are as follows: (1) nanofibrils (<0.1 μm); (2) small fibrous particles (<1 μm); (3) fibers or fibrous fragments (10-50 μm).

[0089] Furthermore, the term "microfibrillated cellulose," as used herein, does not include dried, ground cellulose (also known as microfibrillated cellulose or ultrafine cellulose), nor does it include microcrystalline cellulose obtained by removing amorphous portions by acid hydrolysis, as described in U.S. Patent No. 5,554,287.

[0090] In some embodiments, the majority (i.e., more than half) of the microfibrillated fibers have a transverse dimension (e.g., width in two dimensions) of up to 1 micron, up to 1.5 microns, up to 2 microns, up to 3 microns, or up to 4 microns. In some embodiments, the majority of the microfibrillated fibers have a transverse dimension of at least 0.5 microns, or at least 0.7 microns. In one exemplary embodiment, the majority of the microfibrillated fibers have a transverse dimension in the range of 0.5 to 4 microns. In another exemplary embodiment, the majority of the microfibrillated fibers have a transverse dimension in the range of 0.5 to 1.5 microns. In a further exemplary embodiment, the majority of the microfibrillated fibers have a transverse dimension of up to 2 microns.

[0091] In some embodiments, the microfibrillated fibers are incorporated into the fibrous medium (i.e., dispersed throughout) to form a filter medium (also referred to herein as “filter medium” or “filter media”).

[0092] Third nonwoven fabric filtration medium The third filtration medium includes "low filtration efficiency fibers," which, as used herein, are fibers having a fiber diameter of at least 0.1 microns and less than 1 micron.

[0093] In some embodiments, the low-filtration efficiency fibers preferably include PET. In some embodiments, the low-filtration efficiency fibers may be substantially made of PET. In some embodiments, the low-filtration efficiency fibers may be made of PET.

[0094] Additionally or as an alternative, the low-filtration efficiency fibers may include: nylon, acrylic, rayon, polypropylene, polyethylene, ethylene vinyl alcohol (EVOH), polylactic acid (PLA), polyvinyl alcohol (PVA), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE), or other suitable fused polymers.

[0095] In some embodiments, the third nonwoven filtration medium may contain fibers and components in addition to its low-filtration efficiency fibers. These additional fibers and components may include two-component fibers, one-component heat-meltable fibers, resins, and the like.

[0096] If the third nonwoven filtration medium may contain fibers and components in addition to low-filtration efficiency fibers, the third nonwoven filtration medium preferably contains at least 10% by weight, at least 15% by weight, at least 20% by weight, at least 25% by weight, at least 30% by weight, at least 35% by weight, at least 40% by weight, or at least 45% by weight of low-filtration efficiency fibers. In some embodiments, the third nonwoven filtration medium contains up to 15% by weight, up to 20% by weight, up to 25% by weight, up to 30% by weight, up to 35% by weight, up to 40% by weight, up to 45% by weight, or up to 50% by weight of low-filtration efficiency fibers.

[0097] In some embodiments, the low-filtration efficiency fibers have a fiber diameter of at least 0.1 microns, at least 0.2 microns, at least 0.3 microns, at least 0.4 microns, at least 0.5 microns, at least 0.6 microns, or at least 0.7 microns. In some embodiments, the low-filtration efficiency fibers have a fiber diameter of up to 0.7 microns, up to 0.8 microns, up to 0.9 microns, or less than 1 micron. For example, in one exemplary embodiment, the low-filtration efficiency fibers have a fiber diameter of at least 0.4 microns and less than 1 micron. In another exemplary embodiment, the low-filtration efficiency fibers have a fiber diameter in the range of 0.6 microns to 0.8 microns. In a further exemplary embodiment, the low-filtration efficiency fibers have a fiber diameter of 0.7 microns (700 nm).

[0098] In some embodiments, the small filtration efficiency fibers have a length of at least 0.5 mm, at least 1 mm, or at least 1.5 mm. In some embodiments, the small filtration efficiency fibers have a length of up to 10 mm, up to 11 mm, up to 12 mm, or up to 15 mm. In one exemplary embodiment, the small filtration efficiency fibers have a length in the range of 1 mm to 15 mm. In a further exemplary embodiment, the small filtration efficiency fibers have a length in the range of 1 mm to 12 mm.

[0099] In one exemplary embodiment, the low-filtration efficiency fiber is a PET fiber having a fiber diameter of 0.7 microns.

[0100] In some embodiments, if the low-filtration efficiency fibers include PET, the PET in the low-filtration efficiency fibers has a melting point of at least 250°C, more preferably at least 275°C, and even more preferably at least 290°C.

[0101] support layer In some embodiments, the composite material includes a support layer (also called a scrim). Any suitable support layer can be used.

[0102] The support layer may contain or be made from any suitable porous material. In some embodiments, the support layer may preferably be a polymer material.

[0103] Examples of materials suitable for the support layer include: nonwoven fabrics produced by the spunbond, wet-laid, carded, or melt-blown methods, or combinations thereof, such as those produced by the spunbond-meltblown-spunbond method. The fibers may be in the form of woven fabrics or nonwoven fabrics. Examples of synthetic nonwoven fabrics include: polyester nonwovens, nylon nonwovens, polyolefin (e.g., polypropylene) nonwovens, polycarbonate nonwovens, or blends or multi-component nonwovens thereof. Sheet-like support layers (e.g., cellulose-based, synthetic, and / or glass, or composite webs) are typical examples of filter support layers. Other suitable support layer examples include: polyester or bicomponent polyester fibers, or polypropylene / polyethylene terephthalate, or polyethylene / polyethylene terephthalate bicomponent fibers in the form of spunbond.

[0104] In some embodiments, the support layer includes multiple fibers or strands. The fibers or strands in the support layer may be continuous or discontinuous. Continuous fibers (e.g., strands) are produced by "continuous" fiber formation processes, such as melt-blown, melt-spun, extrusion, woven yarn, laid-scrim, and / or spunbond processes, and are typically longer than discontinuous fibers, which will be discussed in more detail below. Discontinuous fibers are, for example, generally staple fibers cut (e.g., from a filament), or are formed as discontinuous individual fibers having a specific length or a range of lengths.

[0105] In certain embodiments, the supporting layer may include synthetic fibers or strands (e.g., synthetic polymer fibers or strands). The synthetic fibers or strands in the supporting layer may be continuous fibers. Not limited examples of suitable synthetic fibers / strands include: polyester, polyaramid, polyimide, polyolefin (e.g., polyethylene, e.g., high-density polyethylene, low-density polyethylene, and / or linear low-density polyethylene), ethylene-vinyl acetate, polyacrylamide, polylactic acid, polypropylene, Kevlar, Nomex, halogenated polymers (e.g., polyethylene terephthalate), acrylic, polyphenylene oxide, polyphenylene sulfide, thermoplastic elastomers (e.g., thermoplastic polyurethane), polymethylpentene, and combinations thereof.

[0106] In some embodiments, the average pore size of the support layer is 100 microns or less, and in many cases at least 0.5 microns.

[0107] In some embodiments, the porosity of the supporting scrim is 20% or more, and typically 90% or less.

[0108] Examples of support layers include those available under the product names FINON C303NW and FINON C3019NW (manufactured by Midwest Filtration (Cincinnati, Ohio)), or those available under the product name CEREX 23200 (Cerex Advanced Fabrics, Inc. (Cantoment, FL)). CEREX 23200 contains nylon 6,6, has a thickness of 8.4 mils (0.21 mm), and a base weight of 67.8 g / m². 2The solidity is 28%, and the permeability per solidity is 615.1. Other exemplary scrim materials are described, for example, in U.S. Patent Application Publication No. 2009 / 0120868.

[0109] How to use composite materials In another aspect, this disclosure describes methods of using the composite materials described herein.

[0110] In some embodiments, the use of the composite material includes filtering a liquid stream. For example, such a method may include passing a liquid stream containing contaminants through the composite material and removing the contaminants from the liquid stream.

[0111] Examples of such liquid streams include: fuel, hydraulic fluid, process water, air, diesel engine fluid (DEF), diesel engine lubricant, blow-by gas, and combinations thereof.

[0112] In some embodiments, the method of using the composite material includes passing a liquid stream through a first nonwoven filter medium, then a second nonwoven filter medium, then a third nonwoven filter medium.

[0113] Method for fabricating composite materials In a further aspect, the disclosure describes a method for producing a composite material.

[0114] In some embodiments, the first nonwoven filter medium and the second nonwoven filter medium may be manufactured independently. In some embodiments, the first nonwoven filter medium and the third nonwoven filter medium may be manufactured independently. In some embodiments, the second nonwoven filter medium and the third nonwoven filter medium may be manufactured independently. In some embodiments, the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium may be manufactured independently. When these nonwoven filter media are manufactured independently, even if they are formed in the same way, they are not manufactured in the same process. For example, even if each of the three types of filter media is manufactured using a wet-laid process, if they are manufactured independently, they are formed in separate wet-laid processes and then brought into contact with each other, rather than being formed in a single wet-laid process.

[0115] In some embodiments, at least one of the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium is formed using a wet-laid process.

[0116] In some embodiments, the method for producing the composite material includes placing a first nonwoven filter medium in contact with a second nonwoven filter medium, or placing the second nonwoven filter medium in contact with a third nonwoven filter medium, or both.

[0117] If the composite material includes a support layer, the method may further include placing a third nonwoven filter medium in contact with the support layer. In some embodiments, the method may include forming a third nonwoven filter medium on top of the support layer.

[0118] In some embodiments, the method for producing the composite material includes bonding a first nonwoven filter medium to a second nonwoven filter medium, or bonding a second nonwoven filter medium to a third nonwoven filter medium, or both. Any suitable bonding means may be used, including, for example, lamination.

[0119] Exemplary aspects of composite materials [Aspect A1] A composite material comprising: a first two-component fiber having a fiber diameter in the range of 5 to 50 microns and a fiber length of 0.1 cm to 15 cm, comprising 40% to 90% by weight; a first high-filtration efficiency fiber having a fiber diameter in the range of 1 to 5 microns, comprising 0% to 25% by weight; and a first nonwoven filter medium comprising 10% to 60% by weight, mostly consisting of first microfibrillated fibers having a transverse dimension of up to 4 microns; optionally comprising 40% to 90% by weight, with a fiber length of 5 to 50 microns. A composite material comprising: a second bicomponent fiber having a fiber diameter within the range and a fiber length of 0.1 cm to 15 cm; a second high-filtration efficiency fiber comprising 0% to 25% by weight; a second nonwoven filtration medium comprising 10% to 60% by weight, mostly consisting of second microfibrillated fibers having a transverse dimension of up to 4 microns; and a third nonwoven filtration medium comprising low-filtration efficiency fibers having a fiber diameter of at least 0.1 microns and less than 1 micron, wherein the composite material substantially does not contain glass fibers. [Aspect A2] The composite material according to embodiment A1, wherein the first two-component fiber comprises a structural polymer portion and a thermoplastic binder polymer portion, and the structural polymer portion has a melting point higher than that of the binder polymer portion. [Aspect A3] The composite material according to embodiment A1 or A2, wherein the second two-component fiber comprises a structural polymer portion and a thermoplastic binder polymer portion, and the structural polymer portion has a melting point higher than the melting point of the binder polymer portion. [Aspect A4] The composite material according to embodiment A2 or A3, wherein the structural polymer portion of the two-component fiber has a melting point of at least 240°C, and the binder polymer portion of the two-component fiber has a melting point of up to 115°C. [Aspect A5] The composite material according to embodiment A2 or A3, wherein the structural polymer portion of the two-component fiber has a melting point of at least 240°C, and the binder polymer portion of the two-component fiber has a melting point in the range of 100°C to 190°C. [Aspect A6] The composite material according to embodiment A5, wherein the binder polymer portion of the two-component fiber has a melting point in the range of 140°C to 160°C. [Aspect A7] The composite material according to any one of embodiments A1 to A6, wherein the first two-component fiber or the second two-component fiber comprises at least two different types of two-component fibers. [Aspect A8] The composite material according to any one of embodiments A1 to A7, wherein the first nonwoven filter medium contains 40% to 60% by weight of the first two-component fiber. [Aspect A9] The composite material according to any one of embodiments A1 to A8, wherein the second nonwoven filter medium contains 40% to 60% by weight of the second two-component fiber. [Aspect A10] The composite material according to any one of embodiments A1 to A9, wherein the first high-filtration efficiency fiber has a fiber diameter of 2.7 microns. [Aspect A11] The composite material according to any one of embodiments A1 to A10, wherein the first high-filtration efficiency fiber includes PET. [Aspect A12] The composite material according to any one of embodiments A1 to A11, wherein the second high-filtration efficiency fiber has a fiber diameter of 2.7 microns. [Aspect A13] The composite material according to any one of embodiments A1 to A12, wherein the second high-filtration efficiency fiber includes PET. [Aspect A14] The composite material according to any one of embodiments A1 to A13, wherein the first nonwoven filtration medium contains at least 10% by weight of the first high-filtration efficiency fibers. [Aspect A15] The composite material according to any one of embodiments A1 to A14, wherein the second nonwoven filtration medium contains at least 10% by weight of the second high-filtration efficiency fibers. [Aspect A16] The composite material according to any one of embodiments A1 to A15, wherein the majority of the microfibrillated fibers of the first nonwoven filter medium have a transverse dimension of up to 2 microns. [Aspect A17] The composite material according to any one of embodiments A1 to A16, wherein the majority of the microfibrillated fibers of the second nonwoven filter medium have a transverse dimension of up to 2 microns. [Aspect A18] The composite material according to any one of embodiments A1 to A17, wherein the majority of the microfibrillated fibers of the first nonwoven filter medium have a transverse dimension in the range of 0.5 microns to 1.5 microns. [Aspect A19] The composite material according to any one of embodiments A1 to A18, wherein the majority of the microfibrillated fibers of the second nonwoven filter medium have a transverse dimension in the range of 0.5 microns to 1.5 microns. [Aspect A20] The composite material according to any one of embodiments A1 to A19, wherein the first nonwoven filter medium contains 10% to 40% by weight of microfibrillated fibers. [Aspect A21] The composite material according to any one of embodiments A1 to A20, wherein the second nonwoven filter medium contains 10% to 40% by weight of microfibrillated fibers. [Aspect A22] The composite material according to any one of embodiments A1 to A21, wherein the first nonwoven filter medium has a solidity in the range of 5% to 15%. [Aspect A23] The first nonwoven filter medium has a concentration of 24 g / m². 2 ~100g / m 2 A composite material according to any of embodiments A1 to A22, having a basic weight within the range. [Aspect A24] The composite material according to any one of embodiments A1 to A23, wherein the first nonwoven filter medium has a pore size of 0.5 microns to 20 microns. [Aspect A25] The composite material according to any one of embodiments A1 to A24, wherein the first nonwoven filter medium has a thickness in the range of 0.12 mm to 1 mm. [Aspect A26] The first nonwoven fabric filter medium is used in 1 ft of water at 0.5 inches. 3 / ft 2 From / min, 100ft with 0.5 inches of water3 / ft 2 A composite material according to any one of embodiments A1 to A25, having permeability within a range of up to / min. [Aspect A27] The composite material according to any one of embodiments A1 to A26, wherein the second nonwoven filter medium has a solidity in the range of 5% to 15%. [Aspect A28] The second nonwoven filter medium is 24 g / m². 2 ~100g / m 2 A composite material according to any of embodiments A1 to A27, having a basic weight within the range. [Aspect A29] The composite material according to any one of embodiments A1 to A28, wherein the second nonwoven filter medium has a pore size of 0.5 microns to 20 microns. [Aspect A30] The composite material according to any one of embodiments A1 to A29, wherein the second nonwoven filter medium has a thickness in the range of 0.12 mm to 1 mm. [Aspect A31] The second nonwoven fabric filter medium is used in 1 ft of water at 0.5 inches. 3 / ft 2 From / min, 100ft with 0.5 inches of water 3 / ft 2 A composite material according to any one of embodiments A1 to A30, having permeability within a range of up to / min. [Aspect A32] The composite material according to any one of embodiments A1 to A31, wherein the low-filtration efficiency fibers have a fiber diameter of at least 0.4 microns and less than 1 micron. [Aspect A33] The composite material according to any one of embodiments A1 to A32, wherein the low-filtration efficiency fibers have a fiber diameter in the range of 0.6 microns to 0.8 microns. [Aspect A34] The composite material according to any one of embodiments A1 to A33, wherein the low-filtration efficiency fibers include fibers having a fiber diameter of 0.7 microns. [Aspect A35] The composite material according to any one of embodiments A1 to A34, wherein the low-filtration efficiency PET fiber contains polyethylene terephthalate (PET). [Aspect A36] The composite material according to any one of embodiments A1 to A35, wherein the composite material substantially does not contain resin. [Aspect A37] The composite material does not contain glass fibers. The composite material according to any one of embodiments A1 to A36. [Aspect A38] The composite material according to any one of embodiments A1 to A37, wherein the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium are separate layers. [Aspect A39] The composite material according to any one of embodiments A1 to A38, wherein the nonwoven filtration medium is configured such that a liquid passes through the first nonwoven filtration medium, then the second nonwoven filtration medium, and then the third nonwoven filtration medium. [Aspect A40] The composite material according to any one of embodiments A1 to A39, wherein the nonwoven filter medium further comprises a support layer. [Aspect A41] The composite material according to embodiment A40, wherein the support layer includes a porous polymer material. [Aspect A42] The composite material according to Aspect A40 or A41, wherein the non-woven filter medium is configured such that liquid passes through the first non-woven filter medium, then the second non-woven filter medium, then the third non-woven filter medium, and then the support layer. [Aspect A43] The composite material according to any one of Aspects A40 to A42, wherein the third non-woven filter medium is in contact with the support layer. [Aspect A44] The composite material according to any one of Aspects A1 to A43, wherein the first non-woven filter medium is in contact with the second non-woven filter medium, and the second non-woven filter medium is in contact with the third non-woven filter medium. [Aspect A45] The composite material according to any one of Aspects A1 to A44, wherein the first high filtration efficiency fibers contain PET, and the PET has a melting point of at least 250 °C, at least 275 °C, or at least 290 °C. [Aspect A46] The composite material according to any one of Aspects A1 to A45, wherein the second high filtration efficiency fibers contain PET, and the PET has a melting point of at least 250 °C, at least 275 °C, or at least 290 °C. [Aspect A47] The composite material according to any one of Aspects A1 to A46, wherein the microfibrillated fibers of the first non-woven filter medium contain microfibrillated cellulose fibers. [Aspect A48] The composite material according to any one of Aspects A1 to A47, wherein the microfibrillated fibers of the second non-woven filter medium contain microfibrillated cellulose fibers.

[0120] Exemplary uses of composite materials [Aspect B1] A method for filtering a liquid stream, the method comprising the steps of passing a liquid stream containing contaminants through a composite material described in any one of “Exemplary Embodiments of Composite Materials” (Aspects A1 to A48), and removing the contaminants from the liquid stream. [Aspect B2] The method according to embodiment B1, wherein the liquid stream includes fuel, hydraulic oil, process water, air, diesel engine fluid (DEF), diesel engine lubricant, or blow-by gas, or a combination thereof. [Aspect B3] The method according to embodiment B1 or B2, wherein the liquid stream is passed through the first nonwoven filter medium, then the second nonwoven filter medium, then the third nonwoven filter medium.

[0121] Exemplary Method for Preparing Composite Materials [Aspect C1] A method for producing the composite material described in any one of the "Exemplary Embodiments of Composite Materials" (Aspects A1 to A48), wherein the method includes independently producing the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium. [Aspect C2] The method according to embodiment C1, wherein the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium are formed using a wet laid process. [Aspect C3] The method according to aspect C1 or C2, further comprising bringing the first non-woven filter medium into contact with the second non-woven filter medium and bringing the second non-woven filter medium into contact with the third non-woven filter medium. [Aspect C4] The method according to aspect C3, further comprising bonding the first non-woven filter medium to the second non-woven filter medium or bonding the second non-woven filter medium to the third non-woven filter medium, or both. [Aspect C5] The method according to aspect C4, wherein the bonding includes lamination. [Aspect C6] The method according to any one of aspects C1 to C5, further comprising bringing the third non-woven filter medium into contact with a support layer.

[0122] The present invention will be described by the following examples. It should be understood that specific examples, substances, amounts, and procedures should be interpreted broadly in accordance with the scope and spirit of the invention referred to in this specification.

Examples

[0123] All reactants, starting materials, and solvents used in the following examples were purchased from commercial suppliers (e.g., Sigma Aldrich (St. Louis, MO)) and used without further purification unless otherwise specified.

[0124] Characterization of Media Liquid Filtration Performance Test Using a circular flat sheet, differential pressure and 4 μm Beta (β 4μmThe following calculations were performed. The medium was tested according to the description in ISO 16889:2008 (Hydraulic fluid power - Filters - Multi-pass method for evaluating filtration performance of a filter element), however, for the hydraulic fluid, ISO Fine Test Dust was used instead of ISO Medium Test Dust for loading. The area of ​​the medium was 0.0507 m². 2 The test flow rate was 2 L / min, and the test was carried out until the differential pressure at the terminal element reached 200 kPa.

[0125] Solidity The solidity (c) of a nonwoven fabric layer (for example, a nonfiber layer, or a composite layer containing both a fiber layer and a nonfiber layer) is calculated using the following formula: c = BW / ρZ Here, BW is the base weight, ρ is the fiber density, and Z is the thickness of the medium.

[0126] Thickness was measured according to TAPPI T411 om-15, named "Thickness (caliper) of paper, paperboard, and combined board," using a foot pressure of 1.5 psi. Base weight was measured using TAPPI T410.

[0127] Example 1 This embodiment describes the improvement in filtration efficiency and lifespan achieved by using a composite material containing a fine fiber layer.

[0128] Scrim (1 oz / yd 2 Flat sheets were prepared using either polyester (sold under the trade name Reemy) and Synteq® 10XP (Donaldson Company Inc. (Minneapolis, MN)) (Figure 2A, left panel) superimposed on the scrim, or the same scrim having 1 μm diameter fine-fiber electrospun yarn with a layer formed thereon, and Synteq® 10XP (Figure 2A, right panel) superimposed on the fine-fiber layer.

[0129] As shown in Figure 1A, the addition of the fine fiber layer increased the filtration capacity (i.e., lifespan) of the flat sheet compared to a flat sheet without the fine fiber layer. As shown in Figure 1B, the addition of the fine fiber layer increased the filtration efficiency of the flat sheet compared to a flat sheet without the fine fiber layer.

[0130] These results were unexpected, because there had been previous reports suggesting that it was undesirable to have intermediate layers between media layers, and that a gradient structure should be pursued instead (see, for example, U.S. Patent Application Publication 2014 / 0360145).

[0131] Speaking without being bound by theory, it is thought that higher filtration efficiency can be achieved by creating an intermediate layer between the layers of the medium, because the heterogeneity of each layer does not extend throughout the entire thickness of the medium.

[0132] Example 2 The same improvements in supported filtration capacity and filtration efficiency reported in Example 1 are also expected in a flat sheet comprising scrim, a layer of PET fibers with a diameter of 700 nm, and a hand sheet prepared according to the description in Example 1 (containing 40% to 60% binary fibers with a diameter of 14 μm, 0 to 25% PET fibers with a diameter of 2.5 μm, and 10 to 40% fibrillated rayon fibers with a diameter of 1 μm) (Figure 2B).

[0133] Speaking without being bound by theory, it can be considered that the layer of 700nm diameter PET fibers functions as the filtration efficiency layer, and the hand sheet functions as the support layer. Alternatively, it is expected that the fluctuations in filtration efficiency that would be observed if the hand sheet were used alone are eliminated by combining it with the 700nm diameter PET fibers (which function as the filtration efficiency layer).

[0134] Speaking without being bound by theory, it is thought that higher filtration efficiency can be achieved by creating an intermediate layer between the layers of the medium, because the heterogeneity of each layer does not extend throughout the entire thickness of the medium.

[0135] The complete disclosure of all patents, patent applications, and publications, as well as electronically available materials, cited herein are incorporated by reference. In the event of any inconsistency between the disclosure of this application and the disclosure of the documents incorporated herein by reference, the disclosure of this application shall prevail. The above-mentioned detailed descriptions and examples are provided solely for the purpose of clarifying understanding. They do not imply any unnecessary limitations. The present invention is not limited to the exact details illustrated and described, and variations that are obvious to those skilled in the art are included in the claims of the invention.

Claims

1. It is a composite material, A first two-component fiber having a fiber diameter in the range of 5 microns to 50 microns and a fiber length of 0.1 cm to 15 cm, comprising 40% to 90% by weight; A first high-filtration efficiency fiber having a fiber diameter in the range of 1 micron to 5 microns, comprising 0% to 25% by weight; and Microfibrillated fibers, consisting of 10% to 60% by weight, with most having a transverse dimension of up to 4 microns. A first nonwoven filter medium, Optionally, A second two-component fiber comprising 40% to 90% by weight, with a fiber diameter in the range of 5 to 50 microns and a fiber length of 0.1 cm to 15 cm; A second high-filtration efficiency fiber having a fiber diameter in the range of 1 micron to 5 microns, comprising 0% to 25% by weight; and Secondary microfibrillated fibers, comprising 10% to 60% by weight, with most having a transverse dimension of up to 4 microns. A second nonwoven fabric filter medium containing, A third nonwoven filter medium comprising small filtration efficiency fibers having a fiber diameter of at least 0.1 microns and less than 1 micron, and Includes, A composite material that contains virtually no glass fibers.

2. The composite material according to claim 1, wherein the structural polymer portion of the two-component fiber has a melting point of at least 240°C, and the binder polymer portion of the two-component fiber has a melting point in the range of 100°C to 190°C.

3. The composite material according to claim 1 or 2, wherein the first high-filtration efficiency fiber contains polyethylene terephthalate (PET), or the second high-filtration efficiency fiber contains PET, or both.

4. The composite material according to any one of claims 1 to 3, wherein the low-filtration efficiency fibers have a fiber diameter in the range of 0.6 microns to 0.8 microns.

5. The composite material according to any one of claims 1 to 4, wherein the low-filtration efficiency fibers include polyethylene terephthalate (PET).

6. The composite material according to any one of claims 1 to 5, wherein the composite material substantially contains no resin.

7. The composite material according to any one of claims 1 to 6, wherein the composite material does not contain glass fibers.

8. The composite material according to any one of claims 1 to 7, wherein the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium are separate layers.

9. The composite material according to any one of claims 1 to 8, wherein the nonwoven filter medium is configured such that a liquid passes through the first nonwoven filter medium, then the second nonwoven filter medium, and then the third nonwoven filter medium.

10. The composite material according to any one of claims 1 to 9, wherein the nonwoven filter medium further comprises a support layer.

11. The composite material according to any one of claims 1 to 10, wherein the third nonwoven filter medium is in contact with the support layer.

12. The composite material according to any one of claims 1 to 11, wherein the microfibrillated fibers include microfibrillated cellulose fibers.

13. A method for filtering a liquid stream, A step of passing a liquid stream containing contaminants through a composite material according to any one of claims 1 to 12, and Steps to remove the contaminants from the liquid stream. A method that includes this.

14. The method according to claim 13, wherein the liquid stream includes air.

15. A method for producing the composite material described in claim 1, comprising independently producing the first nonwoven filter medium, the second nonwoven filter medium, and the third nonwoven filter medium.