Silicone-free foam stabilizer for producing polyurethane foams

Abstract

The present invention relates to a method for producing polyurethane foams, comprising combining (a) a polyisocyanate, (b) a polymeric compound having isocyanate-reactive groups, (c) a silicone-free stabilizer, (d) optionally a chain extender and / or crosslinker, (e) a catalyst, (f) a blowing agent, and (g) optionally an auxiliary and / or additive to provide a reaction mixture, and reacting the reaction mixture to provide a polyurethane. The silicone-free stabilizer (c) can be obtained by alkoxylating a starter molecule having a functionality of 1 to 8 with an alkylene oxide, wherein 0 to 9% by weight of the alkylene oxide used is ethylene oxide, 0 to 50% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 50% by weight of the alkylene oxide used contains at least 4 carbon atoms, the number average molecular weight of the silicone-free stabilizer (c) is 500 to 20,000 g / mol, and the content of silicone-based foam stabilizer is less than 0.3% by weight based on the total weight of compounds (b), (c), (d), (e) and (f). The present invention further relates to a polyol component containing the silicone-free stabilizer (c), to a polyurethane foam obtainable by the method according to the present invention, and to a method for using the polyurethane foam according to the present invention in an enclosed space or in the interior of a vehicle.

Description

[Technical field]

[0001] The present invention relates to a process for producing a polyurethane foam, comprising combining (a) a polyisocyanate, (b) a polymeric compound having isocyanate-reactive groups, (c) a silicone-free stabilizer, (d) optionally a chain extender and / or crosslinker, (e) a catalyst, (f) a blowing agent, and (g) optionally an auxiliary and / or additive to provide a reaction mixture, and reacting the reaction mixture to provide a polyurethane. The silicone-free stabilizer (c) can be obtained by alkoxylation of starter molecules with a functionality of 1 to 8 with alkylene oxide, wherein 0% to 9% by weight of the alkylene oxide used is ethylene oxide, 0% to 50% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 50% by weight of the alkylene oxide used contains at least 4 carbon atoms, the number average molecular weight of the silicone-free stabilizer (c) is 500 to 20000 g / mol, and the content of silicone-based foam stabilizer is less than 0.3% by weight, based on the total weight of compounds (b), (c), (d), (e) and (f). The invention further relates to a polyol component comprising the silicone-free stabilizer (c), to a polyurethane foam obtainable by the process according to the invention, and to a method for using the polyurethane foam according to the invention in an enclosed space or in the interior of a vehicle. [Background technology]

[0002] In the production of polyurethane foams, liquid polyisocyanates are usually mixed with similarly liquid compounds containing isocyanate-reactive high molecular weight groups and blowing agents and allowed to react to provide polyurethane foam. The blowing agents used include chemical blowing agents, which react with isocyanate groups to form carbon dioxide, and / or physical blowing agents, which evaporate as a result of heat released during the production of polyurethane. This allows the reaction to form the polyurethane and the foaming reaction to proceed substantially simultaneously. To ensure the formation of a stable foam, it is customary to use foam stabilizers. These compounds ensure that gases formed during the polyurethane reaction do not escape from the reaction mixture and that the resulting foam remains stable until the polyurethane reaction is completed to the extent that it can no longer collapse.

[0003] The foam stabilizer usually used is polysiloxane-polyoxyalkylene copolymer / polyether siloxane. Such siloxane-based foam stabilizers are described, for example, in "Kunststoffhandbuch", Vol. 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapter 3.4.4.2. These silicone stabilizers are usually very expensive and are often the most expensive component in the production of polyurethane foam. Therefore, attempts have been made to replace silicone-based foam stabilizers with other substances that have the same effect. Thus, WO2016095128 describes isocyanate-containing, perfluoro-based surface-active substances for the production of polyurethane foam. WO95 / 16721 further describes silicone-free polyether compounds as foam stabilizers in the production of polyurethane foam. These are used particularly in the production of rigid polyurethane foams, and consist of a polyether containing 10% by mass to 90% by mass of oxyethylene units and 90% by mass to 10% by mass of oxyalkylene units, based on the mass fraction of the oxyalkylene units in the polyether, having at least 4 carbon atoms, and substantially free of oxypropylene units. A drawback of these foam stabilizers is that they are poorly useful, particularly in the production of flexible polyurethane foams. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] WO2016095128 [Patent Document 2] WO95 / 16721 Summary of the Invention [Problem to be solved by the invention]

[0005] It is therefore an object of the present invention to provide a method for producing polyurethane foams that results in fine cell polyurethane foams, particularly flexible polyurethane foams, without the use of conventional silicone-based foam stabilizers. [Means for solving the problem]

[0006] This object is achieved by a process for producing a polyurethane foam, comprising mixing (a) a polyisocyanate, (b) a polymeric compound having isocyanate-reactive groups, (c) a silicone-free stabilizer, (d) optionally a chain extender and / or crosslinker, (e) a catalyst, (f) a blowing agent, and (g) optionally an auxiliary and / or additive to provide a reaction mixture, and reacting the reaction mixture to provide a polyurethane. wherein the silicone-free stabilizer (c) is obtainable by alkoxylation of starter molecules having a functionality of 1 to 8 with alkylene oxide, wherein 0% to 9% by weight of the alkylene oxide used is ethylene oxide, 0% to 50% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 50% by weight of the alkylene oxide used contains at least 4 carbon atoms, the number average molecular weight of the silicone-free stabilizer (c) is 500 to 20000 g / mol, and the content of silicone-based foam stabilizer is less than 0.3% by weight, based on the total weight of compounds (b), (c), (d), (e) and (f).

[0007] In the present invention, the term polyurethane foam includes all known foamed polyisocyanate polyaddition products. These include addition products derived from isocyanates and alcohols, and also include modified polyurethanes that can contain isocyanurate structures, allophanate structures, urea structures, carbodiimide structures, uretonimine structures, biuret structures, and other isocyanate addition products. These polyurethane foams according to the present invention include in particular flexible, semi-rigid, rigid or integral foams based on polyurethane. The term polyurethane foam according to the present invention is understood to further include foamed polymer blends comprising polyurethane and further polymers. The polyurethane foam according to the present invention is preferably a polyurethane foam that does not contain further polymers in addition to the polyurethane units (a) to (g) and their reaction products described below. In the present invention, "polyurethane foam" is understood to mean foams according to DIN 7726. The flexible polyurethane foams according to the invention have a compressive stress at 10% compression / compressive strength according to DIN 53421 / DIN EN ISO 604 of less than or equal to 15 kPa, preferably 1 to 14 kPa and in particular 4 to 14 kPa, and a density preferably of 10 to 100 g / L. The semi-rigid polyurethane foams according to the invention have a compressive stress at 10% compression according to DIN 53421 / DIN EN ISO 604 of more than 15 kPa and less than 80 kPa. According to DIN ISO 4590, the semi-rigid and flexible polyurethane foams according to the invention preferably have an open cell content of more than 85%, particularly preferably more than 90%. Further details about the flexible and semi-rigid polyurethane foams according to the invention can be found in "Kunststoffhandbuch", Volume 7, "Polyurethane", Carl Hanser Verlag, 3rd edition, 1993, Chapter 5.

[0008] The rigid polyurethane foams according to the invention exhibit a compressive stress at 10% compression of 80 kPa or more, preferably 120 kPa or more, particularly preferably 150 kPa or more. Furthermore, the rigid polyurethane foams have a closed cell content of more than 80%, preferably more than 90%, according to DIN ISO 4590. Further details about the rigid polyurethane foams according to the invention can be found in "Kunststoffhandbuch", Volume 7, "Polyurethane", Carl Hanser Verlag, 3rd edition, 1993, Chapter 6.

[0009] In the present invention, "elastomeric polyurethane foam" is to be understood as meaning a polyurethane foam according to DIN 7726 which does not show a persistent deformation of more than 2% of its initial thickness after 10 minutes of a short-term deformation of its thickness of 50% according to DIN 53577. Rigid, semi-rigid or soft polyurethane foams may be relevant.

[0010] "Integral polyurethane foam" means a polyurethane foam according to DIN 7726 and is to be understood as having an edge region with a higher density than the center as a result of the molding process. The overall apparent density averaged over the center and edge regions is preferably greater than 100 g / L. In the present invention, integral polyurethane foams may be rigid, semi-rigid or flexible polyurethane foams. Further details regarding integral polyurethane foams according to the present invention can be found in "Kunststoffhandbuch", Volume 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapter 7.

[0011] The polyurethanes according to the invention are obtained by mixing a polyisocyanate (a) with a polymeric compound having isocyanate-reactive groups (b), a silicone-free stabilizer (c), optionally a chain extender and / or crosslinker (d), a catalyst (e), a blowing agent (f) and optionally auxiliaries and additives (f) to provide a reaction mixture and reacting this reaction mixture to provide a polyurethane.

[0012] In a preferred embodiment, the polyurethane foam according to the invention is a polyurethane foam having an average density of 10 to 850 g / L, preferably a semi-rigid polyurethane foam or a flexible polyurethane foam or a rigid polyurethane foam, particularly preferably an elastomeric flexible polyurethane foam, a semi-rigid polyurethane foam or an elastomeric integral polyurethane foam. The elastomeric integral polyurethane foam preferably has an average density of 150 g / L to 500 g / L over the center and edge regions. The flexible polyurethane foam preferably has an average density of 10 g / L to 100 g / L, the semi-rigid polyurethane foam preferably has an average density of 70 to 150 g / L and the rigid polyurethane foam preferably has an average density of 30 to 120 g / L.

[0013] The polyurethanes according to the invention are preferably used in the interiors, for example in the interiors of buildings or means of transport, particularly preferably in the interiors of means of transport, for example ships, planes, lorries, cars or buses, more preferably in cars or buses, and especially in cars. The interiors of cars or buses are hereinafter referred to as automobile interior parts. Flexible polyurethane foams may be used in furniture manufacture, for example as seat cushions, as mattresses or as carpet backing foams, semi-rigid polyurethane foams as door trim elements or lining foams for instrument panels, integral polyurethane foams as steering wheels, shift knobs or headrests, and rigid polyurethane foams as headlinings.

[0014] The polyisocyanate component (a) used in the preparation of polyurethanes according to the invention includes all polyisocyanates known for the preparation of polyurethanes. This includes aliphatic, cycloaliphatic and aromatic di- or polyvalent isocyanates known from the prior art, and any desired mixtures thereof. Examples include diphenylmethane 2,2'-, 2,4'- and 4,4'-diisocyanate, mixtures of monomeric diphenylmethane diisocyanate and its higher ring homologues (polymeric MDI), isophorone diisocyanate (IPDI) and its oligomers, tolylene 2,4- or 2,6-diisocyanate (TDI) and their mixtures, tetramethylene diisocyanate and its oligomers, hexamethylene diisocyanate (HDI) and its oligomers, naphthylene diisocyanate (NDI), and their mixtures.

[0015] Preference is given to 2,4- and / or 2,6-tolylene diisocyanate (TDI) or mixtures thereof, monomeric diphenylmethane diisocyanate and / or higher nuclear homologues of diphenylmethane diisocyanate (polymeric MDI) and mixtures thereof. Further possible isocyanates are listed, for example, in "Kunststoffhandbuch", Volume 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapters 3.2 and 3.3.2.

[0016] The polyisocyanate component (a) may be used in the form of a polyisocyanate prepolymer, which can be obtained by reacting an excess of the above polyisocyanate (constituent (a-1)) with a polymeric compound (b) having isocyanate-reactive groups (constituent (a-2)) and / or a chain extender (d) (constituent (a-3)) at a temperature of, for example, 20°C to 100°C, preferably about 80°C, to provide an isocyanate prepolymer.

[0017] Polymer compounds having an isocyanate-reactive group (a-2) and a chain extender (a3) ​​are known to those skilled in the art and are described, for example, in "Kunststoffhandbuch (Plastics Handbook)", Vol. 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition 1993, Chapter 3.1. Thus, as the polymer compound having an isocyanate-reactive group (a-2), the polymer compound having an isocyanate-reactive group described below in (b) can also be used.

[0018] The polymeric compounds (b) having isocyanate-reactive groups that can be used include all known compounds having at least two isocyanate-reactive hydrogen atoms, for example those having a functionality of 2 to 8 and a number average molecular weight of 400 to 20000 g / mol. Thus, for example, it is possible to use compounds selected from the group of polyether polyols, polyester polyols and mixtures thereof.

[0019] Polyetherols are prepared, for example, from epoxides, such as propylene oxide and / or ethylene oxide, or from tetrahydrofuran, together with hydrogen-active starting compounds, such as aliphatic alcohols, phenols, amines, carboxylic acids, water, and compounds based on natural substances, such as sucrose, sorbitol or mannitol, using catalysts. These include basic catalysts or double metal cyanide catalysts, as described, for example, in PCT / EP2005 / 010124, EP90444 or WO05 / 090440. The number-average molecular weight M of polyetherols can be calculated by the formula:

number

[0020] Polyesterols are prepared, for example, from aliphatic or aromatic dicarboxylic acids and polyhydric alcohols, polythioether polyols, polyesteramides, hydroxylated polyacetals and / or hydroxylated aliphatic polycarbonates, preferably in the presence of an esterification catalyst. Further possible polyols are listed, for example, in "Kunststoffhandbuch", Vol. 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapter 3.1.

[0021] In addition to the polyetherols and polyesterols mentioned, filled polyetherols and polyesterols, also known as polymeric polyetherols or polymeric polyesterols, can also be used. Such compounds preferably contain dispersed particles of thermoplastics (for example composed of olefinic monomers such as acrylonitrile, styrene, methacrylate, methacrylic acid and / or acrylamide). Such filled polyols are known and commercially available. Their preparation is described, for example, in DE111394, US3304273, US3383351, US3523093, DE1152536, DE1152537, WO2008 / 055952 and WO2009 / 128279.

[0022] In a particularly preferred embodiment, the polymeric compounds used having isocyanate-reactive groups (b) are polyetherols (b1) which can be obtained by adding ethylene oxide, 1,2-propylene oxide or mixtures thereof onto the starter molecules. It is particularly preferred when these polyetherols have an average functionality of 1.8 to 3, an OH value of 20 to 120, particularly preferably 25 to 100 and in particular 30 to 80 KOH / g. The proportion of propylene oxide and ethylene oxide, based on the total combined weight of the alkylene oxides used to prepare the polyether alcohols (b1), is preferably at least 80% by weight, particularly preferably at least 90% by weight, furthermore particularly preferably 95% by weight and in particular 100% by weight.

[0023] The silicone-free stabilizer (c) can be obtained by alkoxylation of starter molecules having a functionality of 1 to 8 with alkylene oxide, wherein 0% to 9% by weight of the alkylene oxide used is ethylene oxide, 0% to 50% by weight of the alkylene oxide used is 1,2-propylene oxide and at least 50% by weight of the alkylene oxide used contains at least 4 carbon atoms, and the number average molecular weight of the silicone-free stabilizer (c) is 500 to 20 000 g / mol, preferably 1000 to 15 000 g / mol, particularly preferably 1500 to 8000 g / mol, further preferably 1800 to 7000 g / mol and in particular 2000 to 5000 g / mol and even further preferably 2500 to 4500 g / mol.

[0024] Starter molecules that can be used to prepare the silicone-free foam stabilizer (c) include any known starter molecule having a functionality of 1 to 8. These include the starter molecules described above for preparing polyetherols. Such starter molecules are, for example, methanol, ethanol, propanol, butanol, pentanol, hexanol, heptanol, octanol, nonanol, decanol, water, ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, glycerol, trimethylolpropane, pentaerythritol, sugar derivatives such as sucrose, hexorbitol derivatives such as sorbitol, methylamine, ethylamine, isopropylamine, butylamine, benzylamine, aniline, toluidine, toluenediamine, naphthylamine, ethylenediamine, diethylenetriamine, 4,4'-methylenedianiline, 1,3-propanediamine, 1,6-hexanediamine, ethanolamine, diethanolamine, triethanolamine and other mono-, di- or polyhydric alcohols, or mono- or polyhydric amines, or mixtures thereof. Polyether polyols, for example polyalkylene oxides, such as polyethylene oxide or polypropylene oxide, can also be used as starter molecules. If polyalkylene oxides are used as starter molecules, they preferably have a functionality of 2 to 6 and a number average molecular weight of 200 to 5000, particularly preferably 300 to 3000, further preferably 500 to 2000 and in particular 500 to 1000 g / mol. Compounds containing groups that accelerate the polyurethane reaction can also be used as starter molecules. Examples of such starter molecules are 3-(dimethylamino)-1-propylamine and 3-(pyrrolidin-1-yl)propan-1-amine. It is preferred if the average functionality, preferably the average hydroxyl functionality, of the starter molecules for producing the silicone-free stabilizer (c) is 1 to 6, further preferably 1 to 4, further preferably 1 to 3, particularly preferably 1.5 to 2.5 and in particular 2.Preferred starter molecules are methanol, ethanol, propanol, butanol, water, ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, and particularly preferably water or dipropylene glycol.

[0025] The alkylene oxide used for producing the silicone-free foam stabilizer is at least 50% by weight of an alkylene oxide having at least 4 carbon atoms, for example 4-20, preferably 4-12 and in particular 4-10 carbon atoms, such as epoxybutane, epoxypentane, epoxyhexane, epoxyheptane, epoxyoctane, epoxynonane or epoxydecane. It is further preferred to use 1,2-epoxy compounds. It is particularly preferred when the alkylene oxide having at least 4 carbon atoms comprises 1,2-epoxybutane and / or 1,2-epoxypentane, in particular 1,2-epoxybutane. In a particularly preferred embodiment, the alkylene oxide having at least 4 carbon atoms consists of 1,2-epoxybutane, 1,2-epoxypentane or mixtures thereof, in particular 1,2-epoxybutane. It is preferred if the proportion of alkylene oxides having at least 4 carbon atoms during the preparation of component (c) is at least 70% by weight, particularly preferably at least 90% by weight, furthermore preferably at least 95% by weight and in particular 100% by weight, in each case based on the total weight of alkylene oxides used to prepare the silicone-free foam stabilizer (c).

[0026] The alkylene oxide for producing the silicone-free foam stabilizer (c) further comprises less than 9% by weight, preferably less than 5% by weight, more preferably less than 2% by weight of ethylene oxide, in particular no ethylene oxide. If propylene oxide, preferably 1,2-propylene oxide, is present, the proportion of propylene oxide is less than 50% by weight, preferably 5% to 40% by weight, and particularly preferably 10% to 30% by weight, in each case based on the total weight of alkylene oxide used to produce the silicone-free foam stabilizer (c). In a further, likewise preferred embodiment, no propylene oxide is used to produce the compound (c). The alkylene oxide may be arranged randomly or in a block-like manner along the chain, for example, it is possible to add first a block of butylene oxide, then subsequently propylene oxide, or first propylene oxide, and then butylene oxide or a mixture of propylene oxide and butylene oxide, onto the starter molecule. Conventional catalysts for polyalkoxylation may be used as catalysts. These may include, for example, basic catalysts or double metal cyanide catalysts, as described in PCT / EP2005 / 010124, EP90444 or WO05 / 090440.

[0027] All or part of the retained OH groups of the silicone-free stabilizer (c) may be "capped" after alkoxylation. This is understood to refer to the reaction of polyol hydroxyl groups, for example a) with, for example, isocyanates to provide urethanes, b) with, for example, anhydrides, acid chlorides, etc., c) with, for example, alkylating agents or sulfonic acid derivatives to provide ethers, or d) with, for example, silanes or silyl halides to provide silyl ethers. This reduces the functionality towards isocyanates, which can result in an isocyanate-non-reactive stabilizer (c) when all OH groups are completely converted. It is preferred when the silicone-free foam stabilizer (c) contains 1 to 8, particularly preferably 1.5 to 4, and especially 1.8 to 2.5 isocyanate-reactive groups, especially hydroxyl groups. When component (c) contains isocyanate-reactive groups, it is part of the compound (b) with isocyanate-reactive groups. If the compound (c) contains isocyanate-reactive groups, it is preferred to use, in addition to the silicone-free foam stabilizer (c) having isocyanate-reactive groups, further compounds having isocyanate-reactive groups, particularly preferably polyetherols, in particular polyetherols (b1).

[0028] The proportion of the silicone-free foam stabilizer (c) based on the total mass of the compounds (b), (c), (d), (e) and (f) is preferably 0.01% by mass to 10% by mass, more preferably 0.05% by mass to 5% by mass, even more preferably 0.05% by mass to 3% by mass, particularly preferably 0.1% by mass to 2% by mass, even more preferably 0.1% by mass to 1.5% by mass, even more preferably 0.1% by mass to 1% by mass, and in particular 0.1% by mass to 0.5% by mass, and mixtures of different silicone-free foam stabilizers may also be used.

[0029] Chain extenders and crosslinkers (d) that can be used include compounds having at least two isocyanate-reactive groups and a molecular weight of less than 400 g / mol, where molecules having two isocyanate-reactive hydrogen atoms are called chain extenders, and molecules having more than two isocyanate-reactive hydrogen atoms are called crosslinkers.However, it is also possible here to omit the chain extender or crosslinker.However, the addition of a chain extender, crosslinker, or optionally a mixture thereof, proves to be advantageous for modifying mechanical properties, such as hardness.

[0030] When using chain extenders and / or crosslinkers (d), chain extenders and / or crosslinkers well known in the production of polyurethanes may be used. These are preferably low molecular weight compounds with isocyanate-reactive functional groups, such as glycerol, trimethylolpropane, glycols and diamines. Further possible low molecular weight chain extenders and / or crosslinkers are listed, for example, in "Kunststoffhandbuch", Vol. 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapters 3.2 and 3.3.2.

[0031] The catalyst e) significantly accelerates the reaction of the polyol (b) and optionally the chain extension and crosslinking agent (d) and the chemical blowing agent (f) with the organic, optionally modified polyisocyanate (a). The catalyst (e) preferably comprises an incorporable amine catalyst, for example if the emissions of organic compounds are to be as low as possible. The catalyst has at least one, preferably 1 to 8, and particularly preferably 1 to 2, isocyanate-reactive groups, such as primary amine groups, secondary amine groups, hydroxyl groups, amide or urea groups, preferably primary amine groups, secondary amine groups, hydroxyl groups. Incorporable amine catalysts are primarily used for the production of low-emission polyurethanes, in particular for use in the interior of automobiles. Such catalysts are known and described, for example, in EP 1 888 664. They comprise compounds which, in addition to the isocyanate-reactive group(s), preferably contain one or more tertiary amino groups. It is preferred if at least one of the tertiary amino groups of the incorporable catalyst has at least two aliphatic hydrocarbon radicals, preferably with 1 to 10 carbon atoms per radical, particularly preferably with 1 to 6 carbon atoms per radical. It is particularly preferred if the tertiary amino group has, in addition to the two radicals independently selected from the methyl and ethyl radicals, a further organic radical, for example a pyrrolidinyl radical.Examples of incorpo rable catalysts that can be used include, for example, bis(dimethylaminopropyl)urea, bis(N,N-dimethylaminoethoxyethyl)carbamate, dimethylaminopropylurea, N,N,N-trimethyl-N-hydroxyethyl bis(aminopropyl ether), N,N,N-trimethyl-N-hydroxyethyl bis(aminoethyl ether), diethylethanolamine, bis(N,N-dimethyl-3-aminopropyl)amine, dimethylaminopropylamine, 3-(pyrrolidin-1-yl)propan-1-amine, dimethyl-2-(2-aminoethoxyethanol) and (1,3-bis(dimethylamino)propan-2-ol), N,N-bis(3-dimethylaminopropyl)-N-isopropanolamine, bis(dimethylaminopropyl)-2-hydroxyethylamine, N,N,N-trimethyl-N-(3-aminopropyl)-bis(aminoethyl ether), 3-dimethylaminoisopropyldiisopropanolamine or mixtures thereof.

[0032] Further conventional catalysts for making polyurethanes may be used in addition to the incorporable amine catalyst. Examples include amidines such as 2,3-dimethyl-3,4,5,6-tetrahydropyrimidine, tertiary amines such as triethylamine, tributylamine, dimethylbenzylamine, N-methyl-, N-ethyl- and N-cyclohexylmorpholine, N,N,N',N'-tetramethylethylenediamine, N,N,N',N'-tetramethylbutanediamine, N,N,N',N'-tetramethylhexanediamine, pentamethyldiethylenetriamine, tetramethyldiaminoethyl ether, bis(dimethylaminopropyl)urea, dimethylpiperazine, 1,2-dimethylimidazole, 1-azabicyclo[3.3.0]octane, and preferably 1,4-diazabicyclo[2.2.2]octane, and alkanolamine compounds such as triethanolamine, triisopropanolamine, N-methyl- and N-ethyldiethanolamine and dimethylethanolamine. Also contemplated are organometallic compounds, preferably organotin compounds, such as tin(II) salts of organic carboxylic acids, such as tin(II) acetate, tin(II) octoate, tin(II) ethylhexanoate and tin(II) laurate, and dialkyltin(IV) salts of organic carboxylic acids, such as dibutyltin diacetate, dibutyltin dilaurate, dibutyltin maleate and dioctyltin diacetate, and bismuth carboxylates, such as bismuth(III) neodecanoate, bismuth 2-ethylhexanoate and bismuth octanoate, or mixtures thereof. The organometallic compounds can be used alone or, preferably, in combination with a strongly basic amine. When component (b) is an ester, it is preferred to use only amine catalysts. In a particularly preferred embodiment, only incorporable catalysts are used as catalyst (e).

[0033] When catalysts (e) are used, they may be used, for example, in a concentration of from 0.001% to 5% by weight, especially from 0.05% to 2% by weight, for example as a catalyst / catalyst combination based on the weight of component (b).

[0034] Any blowing agent known for the production of polyurethanes may be used as blowing agent (f). This may include chemical and / or physical blowing agents. Such blowing agents are described, for example, in "Kunststoffhandbuch", volume 7, "Polyurethane", Carl Hanser Verlag, 3rd edition, 1993, chapter 3.4.5. "Chemical blowing agents" are understood to mean compounds which form gaseous products by reaction with isocyanates. Examples of such blowing agents are water or carboxylic acids. "Physical blowing agents" are understood to mean compounds which are dissolved or emulsified in the input materials for polyurethane production and which evaporate under the conditions of polyurethane formation. Examples include hydrocarbons, halogenated hydrocarbons and other compounds, such as perfluorinated alkanes, e.g. perfluorohexane, chlorofluorohydrocarbons, and ethers, esters, ketones, acetals and / or liquid carbon dioxide. The blowing agents may be used in any desired amount. The blowing agent is preferably used in an amount such that the resulting polyurethane foam has a density of 10 to 850 g / L, particularly preferably 20 to 800 g / L, and in particular 25 to 500 g / L. It is particularly preferred to use a water-containing blowing agent, in particular water, as the only blowing agent.

[0035] Auxiliaries and / or additives (g) may also be used. Here, any auxiliary and additive substances known in the production of polyurethanes may be used. Examples include surface-active substances, cell regulators, release agents, fillers, dyes, pigments, flame retardants, hydrolysis stabilizers, fungistatic and bacteriostatic substances. These substances are known and are described, for example, in "Kunststoffhandbuch, Band 7, Polyurethane" (Plastics Handbook, Volume 7, Polyurethane), Carl Hanser Verlag, 3rd Edition 1993, Chapters 3.4.4 and 3.4.6 to 3.4.11. Known silicone-based foam stabilizers may also be used. The silicone-based foam stabilizers used are silicone-based compounds which reduce the surface tension of the polyol (b) and in which at least two silicon atoms are each connected via an oxygen atom. These compounds are preferably compounds with an amphiphilic structure, i.e. which contain two molecular parts of different polarity. Silicone-based foam stabilizers preferably have molecular parts that contain organosilicon units, such as dimethylsiloxane or methylphenylsiloxane, and molecular parts that have a chemical structure similar to polyol (b). These are preferably polyoxyalkylene units. Particularly preferably used as silicone-based foam stabilizers are polysiloxane-polyoxyalkylene block copolymers that have an oxyethylene content of less than 75% by weight, based on the total content of polyoxyalkylene units. These preferably have polyethylene oxide and / or polypropylene oxide units. The molecular weight of the polyoxyalkylene side chain is preferably at least 1000 g / mol side chain. These compounds are known and are described, for example, in "Kunststoffhandbuch", Volume 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapter 3.4.4.2, and are produced, for example, by reaction of siloxanes, such as polydimethylsiloxane, with polyoxyalkylenes, in particular polyethylene oxide, polypropylene oxide or copolymers of polyethylene oxide and polypropylene oxide.This makes it possible to obtain polysiloxane-polyoxyalkylene block copolymers having oxyalkylene chains as terminal groups or one or more side groups. The silicone-based foam stabilizer may contain OH groups, but preferably does not contain OH groups. This is achieved when the starter used to prepare the polyoxyalkylene is a monohydric alcohol such as butanol.Silicone-based foam stabilizers which can be used include, for example, known silicone-based foam stabilizers, such as Niax Silicone L1501, L1505, L1540, L1593, L1602 or L1609 from Momentive; Dabco® DC193, Dabco® DC3041, Dabco® DC3042, Dabco® DC3043, Dabco® DC5000, Dabco® DC5169, Dabco® DC2525, Dabco® DC2584, Dabco® SI1101, Dabco® SI1103 or Dabco® DC5160 from Goldschmidt; Tegostab® BF2270, Tegostab® BF2370, Tegostab® BF2470, Tegostab® B8110, Tegostab® B8225, Tegostab® B8255, Tegostab® B8317, Tegostab® B83 from Goldschmidt; 25, Tegostab (registered trademark) B8905, Tegostab (registered trademark) B8946PF, Tegostab (registered trademark) B8948, Tegostab (registered trademark) B8950, Tegostab (registered trademark) B8952, Tegostab (registered trademark) B8960, Tegostab (registered trademark) B8715LF2, Tegostab (registered trademark) B8734LF2, Tegostab (registered trademark) B8736L F2, Tegostab® B8761LF2, Tegostab® B8724LF2, Tegostab® B8738LF2, Tegostab® B8742LF2, Tegostab® B8747LF2, Tegostab® B8745LF2, Tegostab® B8749LF2 or Tegostab® B8486. In the present invention, less than 0.3% by weight of the silicone-based stabilizer is used, based on the total weight of the compounds (b), (c), (d), (e) and (f).In a preferred embodiment of the present invention, less than 0.2% by weight, particularly preferably less than 0.1% by weight, even more preferably less than 0.01% by weight, of a silicone-based foam stabilizer is used, based on the total weight of compounds (b), (c), (d), (e) and (f), and in particular no silicone-based foam stabilizer is used.

[0036] The preparation of the polyurethanes according to the invention generally involves reacting the compounds (a) to (g) in such amounts that the equivalent ratio of the NCO groups of the polyisocyanate (a) to the sum of the reactive hydrogen atoms of components (b), (c), (e) and (f) and optionally (d) and (g) is 0.60 to 1.5:1, preferably 0.70 to 1.25:1, and particularly preferably 0.80 to 1.10:1. If the cellular plastic contains at least partially isocyanurate groups, a ratio of the NCO groups of the polyisocyanate (a) to the sum of the reactive hydrogen atoms of components (b), (c), (e), (f) and optionally (d) and (g) of 1.5 to 20:1, preferably 1.5 to 8:1, and particularly preferably 1.50 to 5:1, is usually used. A ratio of 1:1 here corresponds to an isocyanate index of 100.

[0037] The specific starting materials (a) to (g) for preparing the polyurethane according to the invention only differ quantitatively and qualitatively slightly in each case, when the polyurethane according to the invention to be prepared is a flexible foam, a semi-rigid foam, a rigid foam or an integral foam. Furthermore, the elasticity and hardness of the polyurethane according to the invention can be varied, for example, by the functionality and the chain length of the high molecular weight compound having at least two reactive hydrogen atoms. Such variations are known to those skilled in the art.

[0038] The reactants for producing flexible foams are described, for example, in PCT / EP2005 / 010124 and EP1529792, the reactants for producing semi-rigid foams in "Kunststoffhandbuch", Vol. 7, "Polyurethane", Carl Hanser Verlag, 3rd Edition, 1993, Chapter 5.4, the reactants for producing rigid foams in PCT / EP2005 / 010955, and the reactants for producing integral foams in EP364854, US5506275 or EP897402. And to the reactants described in these documents, in each case a silicone-free foam stabilizer (c) is added. It is particularly preferred if the polyurethane foam according to the invention is a flexible polyurethane foam.

[0039] The so-called "two-component process" is often used to produce polyurethane foams according to the invention. This involves combining an isocyanate-reactive component, often also a non-reactive component (e.g. from the group of auxiliary and additive substances (g)), to provide a polyol component that is mixed with the isocyanate of the isocyanate component during the production of the polyurethane foam. The isocyanate component may contain not only the isocyanate (a) but also further compounds. Thus, the invention also provides a polyol component that contains (b) a polymeric compound having isocyanate-reactive groups, (c) a silicone-free stabilizer, (d) optionally a chain extender and / or crosslinker, (e) a catalyst, (f) a blowing agent, and (g) optionally auxiliaries and additives. The silicone-free stabilizer (c) can be obtained by alkoxylation of starter molecules with a functionality of 1 to 8 with alkylene oxide, wherein 0% to 9% by weight of the alkylene oxide used is ethylene oxide, 0% to 50% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 50% by weight of the alkylene oxide used contains at least 4 carbon atoms, the number average molecular weight of the silicone-free stabilizer (c) is 500 to 20000 g / mol, and the content of silicone-based foam stabilizer is less than 0.3% by weight based on the total weight of compounds (b), (c), (d), (e) and (f). The silicone-free stabilizer (c) may be added to the isocyanate component, especially when the silicone-free stabilizer (c) does not contain isocyanate-reactive groups.

[0040] The present invention provides not only the process according to the invention, but also the polyurethane foam obtainable by the process according to the invention. The polyurethane according to the invention surprisingly emits only small amounts of organic substances and is therefore preferably used in enclosed spaces, for example as insulation material in residential buildings, for example as insulation for pipes and refrigerators, in furniture construction, for example as seat cushions, as mattresses and in the interior of vehicles, for example as steering wheels, dashboards, door trims, carpet foam linings, acoustic foams, for example as headliners and headrests or gear knobs. Finally, the present invention also provides silicone-free stabilizers (c) of the invention, in particular silicone-free stabilizers (c) obtainable by alkoxylation of starter molecules with functionality 1 to 8 with 1,2-epoxybutane and / or 1,2-epoxypentane. At least 50% by weight of the alkylene oxides used to prepare the stabilizer (c) are 1,2-epoxybutane and / or 1,2-epoxypentane, and the number average molecular weight of the silicone-free stabilizer (c) is 500 to 20,000 g / mol.

[0041] The present invention will now be described with reference to examples. EXAMPLES

[0042] The following input materials were used:

[0043] Polyol A: A glycerol-initiated polyether polyol based on ethylene oxide and propylene oxide having an average OH number of 28 mg KOH / g and a propylene oxide content of 84 wt. %, based on the total weight of the polyether.

[0044] Polyol B: A glycerol-initiated polyether polyol based on ethylene oxide and propylene oxide having an average OH number of 42 mg KOH / g and an ethylene oxide content of 74 wt. %, based on the total weight of the polyether.

[0045] Isocyanate 1: A mixture of 41.5% by weight of 4,4'-MDI, 25.3% by weight of 2,4'-MDI and 33.2% by weight of a mixture of diphenylmethane diisocyanate and higher nuclear homologues of diphenylmethane diisocyanate (Lupranat® M20S from BASF SE).

[0046] Catalyst 1: Lupragen® N201, an amine catalyst from BASF SE. Catalyst 2: Niax A-1, an amine catalyst from Momentive. Catalyst 3: Jeffcat® ZF10, an amine catalyst from Huntsman. Catalyst 4: Jeffcat® Z-130, an amine catalyst from Huntsman.

[0047] Stabilizer 1: Tegostab® B8715LF2, an organosiloxane-polyether copolymer from Evonik, a conventional silicone-based foam stabilizer Stabilizer 2: A 1,2-propylene glycol initiated polyether polyol having an average OH number of 74 mg KOH / g and containing 53.7% by weight butylene oxide and 42.2% by weight ethylene oxide, in each case based on the total weight of the polyether polyol. Ethylene oxide was used as an end block. Stabilizer 3: 1,2-propylene glycol initiated polyether polyol having an average OH number of 34 mg KOH / g and containing 79% by weight butylene oxide and 19.3% by weight ethylene oxide, in each case based on the total weight of the polyether polyol. Ethylene oxide was used as an end block. Stabilizer 4: 1,2-propylene glycol initiated polyether polyol having an average OH number of 26 mg KOH / g and containing 60.6 wt. % butylene oxide and 38.3 wt. % ethylene oxide, in each case based on the total weight of the polyether polyol. Ethylene oxide was used as an end block. Stabilizer 5: A dipropylene glycol initiated polyether polyol containing only 1,2-epoxybutane as the alkylene oxide and having an average OH number of 44 mg KOH / g. Stabilizer 6: A dipropylene glycol initiated polyether polyol containing only 1,2-epoxybutane as the alkylene oxide and having an average OH number of 33 mg KOH / g. Stabilizer 7: A dipropylene glycol initiated polyether polyol containing only 1,2-epoxybutane as the alkylene oxide and having an average OH number of 26 mg KOH / g. Stabilizer 8: A dipropylene glycol initiated polyether polyol containing only 1,2-epoxybutane as the alkylene oxide and having an average OH number of 21 mg KOH / g. Stabilizer 9: A dipropylene glycol initiated polyether polyol containing only 1,2-epoxypentane as the alkylene oxide and having an average OH number of 47 mg KOH / g.

[0048] Synthesis of silicone-free foam stabilizers. The preparation of the foam stabilizers Stabilizers 1-8 was carried out in a two-step process in a steel reactor. It involved the first step of butoxylating propylene glycol / dipropylene glycol under KOH catalysis to produce a precursor, followed by the second step of butoxylating and optionally ethoxylating the precursor, also under KOH catalysis. The hydroxyl numbers of the resulting polyols were determined by titration after purification and drying. The preparation of Stabilizer 9 was by a similar procedure, but using CsOH instead of KOH.

[0049] To prepare the examples and comparative examples, 94 parts by weight of polyol A, 6 parts by weight of polyol B, 0.6 parts by weight of catalyst 1, 0.1 parts by weight of catalyst 2, 3.3 parts by weight of water and the respective amounts of stabilizers reported in Table 1 were mixed at room temperature for 2 minutes using a laboratory mixer and left for 30 minutes. Subsequently, isocyanate 1 was added, and with an isocyanate index of 90, the mixture was mixed at 1800 rpm using a laboratory mixer for 5 seconds and reacted to provide a polyurethane foam in a beaker. The free-rise density was about 45 g / L. The quality, cell structure, and appearance of the foam were evaluated. Molded foams were similarly obtained by placing the reaction mixture in a mold with a volume of 8 liters (40 cm x 40 cm x 5 cm) and controlling the temperature at 50°C after mixing. The amounts used were selected so that the average density of the molded foam was 53 g / L. After 4 minutes, the film was removed from the mold, bent, and left at room temperature for 24 hours. Test specimens for mechanical and emission measurements were taken from the molded foams. The quality of the free foamed and molded foams was rated as "good" if they were dimensionally stable, did not shrink, had a continuous fine cell structure and a uniform surface without defects. Foams were rated as "poor" if they had a coarse cell structure and holes in the center and on the surface of the foam.

[0050] [Table 1]

[0051] mechanical measurements The mechanical measurements in Table 2 were determined as follows. Density: DIN EN ISO845 Compressive strength and hysteresis: DIN EN ISO3386 Tensile strength and elongation at break: DIN EN ISO1798 Compression set: DIN EN ISO1856 Breathability: DIN EN ISO7231 Resilience: DIN EN ISO8307

[0052] [Table 2]

[0053] The results in Tables 1 and 2 demonstrate that the use of silicone-free foam stabilizers according to the present invention results in foams that are normally only obtainable when using silicone-based foam stabilizers.

[0054] Furthermore, the foam stabilizer according to the present invention exhibits significantly lower organic matter emissions values, as shown in Table 4.

[0055] emissions Foam specimens were prepared in the same manner as in the above examples and comparative examples to determine emission values. The input materials shown in Table 3 were used. Isocyanate 1 was used as the isocyanate component. An isocyanate index of 90 was used. The density of the resulting foam was approximately 50 kg / m 3 The emissions were determined as specified below.

[0056] [Table 3]

[0057] Formaldehyde was determined by a procedure similar to ASTM D-5116-06. The chamber dimensions were 4.7 liters. The polyurethane samples used were sections with dimensions 100 mm x 100 mm x 25 mm from the inside of the foam. The temperature in the measurement chamber during the measurements was 65 °C and the relative humidity was 50%. The air exchange rate was 3.0 liters per hour. The exhaust air stream containing the volatile aldehydes from the polyurethane was passed over a cartridge containing silica coated with 2,4-dinitrophenylhydrazine for 120 min. The DNPH cartridge was then eluted with a mixture of acetonitrile and water. The concentrations of formaldehyde and acetaldehyde in the eluate were measured by HPLC. In this setup, the detection limit was ≤ 11 μg / m of formaldehyde emissions. 3 and acetaldehyde emissions are ≦6 μg / m 3It was.

[0058] VOC and FOG were determined by VDA278.

[0059] [Table 4]

Claims

1. (a) a polyisocyanate, (b) a polymeric compound having an isocyanate-reactive group; (c) a silicone-free foam stabilizer; (d) optionally a chain extender and / or a crosslinker; (e) a catalyst; (f) a blowing agent, (g) Optional Auxiliaries and / or Additives to provide a reaction mixture, and reacting the reaction mixture to provide a polyurethane; The silicone-free foam stabilizer (c) is obtainable by alkoxylation of starter molecules having a functionality of 1 to 8 with alkylene oxide, wherein 0% to 5% by weight of the alkylene oxide used is ethylene oxide, 0% to 10% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 90% by weight of the alkylene oxide used contains 4 to 10 carbon atoms, the number average molecular weight of the silicone-free foam stabilizer (c) is 500 to 20000 g / mol, and the content of silicone-based foam stabilizer is less than 0.3% by weight, based on the total weight of compounds (b), (c), (d), (e) and (f), The proportion of the silicone-free foam stabilizer (c) is 0.01% by weight to 10% by weight, based on the total weight of the compounds (b), (c), (d), (e) and (f); and The method for producing a polyurethane foam, wherein the polymer compound (b) having an isocyanate-reactive group is a compound selected from the group consisting of polyether polyols, polyester polyols, and mixtures thereof.

2. 2. The method according to claim 1, wherein the silicone-free foam stabilizer (c) is obtainable by alkoxylation of starter molecules of functionality 1 to 8 with alkylene oxide, wherein 0% to 2% by weight of the alkylene oxide used is ethylene oxide, 0% to 5% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 95% by weight of the alkylene oxide used contains from 4 to 10 carbon atoms.

3. 3. The method of claim 1 or 2, wherein 100% by weight of the alkylene oxide used in making the silicone-free foam stabilizer (c) contains from 4 to 10 carbon atoms.

4. The method according to any one of claims 1 to 3, wherein the alkylene oxide used in the preparation of the silicone-free foam stabilizer (c) is selected from the group consisting of epoxybutane, epoxypentane, epoxyhexane, epoxyheptane, epoxyoctane, epoxynonane, epoxydecane and mixtures thereof.

5. 5. The process according to claim 1, wherein the average functionality of the starter molecules for the preparation of the silicone-free foam stabilizer (c) has a functionality of 1 to 3.

6. 6. The method of any one of claims 1 to 5, wherein some or all of the retained OH groups of the non-silicone-containing foam stabilizer (c) are capped after alkoxylation.

7. 7. The process according to claim 1, wherein the polymeric compound having isocyanate-reactive groups comprises a polyether alcohol (b1) obtainable by adding ethylene oxide, propylene oxide or mixtures thereof onto a starter molecule, and wherein at least 90% by weight of the alkylene oxides used for the preparation of polyether alcohol (b1) are selected from the group consisting of ethylene oxide, 1,2-propylene oxide and mixtures thereof.

8. 8. The method of claim 1, wherein no silicone-based foam stabilizer is used.

9. The method according to any one of claims 1 to 8, wherein the polyurethane foam is a flexible polyurethane foam having a compressive stress at 10% compression of 15 kPa or less according to DIN 53421 / DIN EN ISO 604 and a density of 10 to 100 g / L.

10. 10. The method of any one of claims 1 to 9, wherein the catalyst (e) comprises an incorporateable amine catalyst.

11. (b) a polymeric compound having an isocyanate-reactive group; (c) a silicone-free foam stabilizer; (d) optionally a chain extender and / or a crosslinker; (e) a catalyst; (f) a blowing agent, and (g) Optional Auxiliaries and / or Additives Including, The silicone-free foam stabilizer (c) is obtainable by alkoxylation of starter molecules with a functionality of 1 to 8 with alkylene oxide, wherein 0% to 5% by weight of the alkylene oxide used is ethylene oxide, 0% to 10% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 90% by weight of the alkylene oxide used contains 4 to 10 carbon atoms, the number average molecular weight of the silicone-free foam stabilizer (c) is 500 to 20,000 g / mol, and the proportion of silicone-free foam stabilizer (c) is 0.01% to 10% by weight, based on the total weight of the compounds (b), (c), (d), (e) and (f), and the content of silicone-based foam stabilizer is less than 0.3% by weight, based on the total weight of the compounds (b), (c), (d), (e) and (f), A polyol mixture, wherein the polymeric compound (b) having an isocyanate-reactive group is a compound selected from the group consisting of polyether polyols, polyester polyols and mixtures thereof.

12. 12. Polyol mixture according to claim 11, wherein the silicone-free foam stabilizer (c) is obtainable by alkoxylation of starter molecules with a functionality of 1 to 8 with alkylene oxide, wherein 0% to 2% by weight of the alkylene oxide used is ethylene oxide, 0% to 5% by weight of the alkylene oxide used is 1,2-propylene oxide, and at least 95% by weight of the alkylene oxide used contains from 4 to 10 carbon atoms.

13. A polyurethane foam obtainable by the process according to any one of claims 1 to 10.

14. 14. Use of the polyurethane foam according to claim 13 in an enclosed space or inside a vehicle.

15. Use according to claim 14 for manufacturing a mattress or a seat cushion or a vehicle seat cushion or a headrest.