Method for producing heterophasic propylene polymerized material

Abstract

A heterophasic propylene polymeric material including a propylene-based polymer A, a propylene-based polymer B, and a propylene copolymer C, wherein the polymer A contains 80 mass% or more of monomer units derived from propylene and has a limiting viscosity of 2.0 dL / g or less, the polymer B contains 80 mass% or more of monomer units derived from propylene and has a limiting viscosity of 2.1-4.9 dL / g, the copolymer C contains monomer units derived from propylene and 30-55 mass% of monomer units derived from ethylene or the like and has a limiting viscosity of 1.5-4.5 dL / g, and the polymer A, the polymer B, and the copolymer C are respectively contained in ratios of 50-75 mass%, 5-20 mass%, and 5-40 mass%.

Description

[Technical field]

[0001] The present invention relates to heterophasic propylene polymerization materials. [Background technology]

[0002] Patent Document 1 describes a polypropylene resin composition and a molded article made of the same, and describes that the polypropylene resin composition contains a propylene block copolymer made of a polymer component (I) and a polymer component (II), a so-called heterophasic propylene polymerization material. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] International Publication No. 2009 / 038237 Summary of the Invention [Problem to be solved by the invention]

[0004] Meanwhile, materials capable of producing molded articles having high dimensional stability are useful for various applications.

[0005] Therefore, an object of the present invention is to provide a heterophasic propylene polymerization material from which molded articles having excellent dimensional stability can be produced. [Means for solving the problem]

[0006] The heterophasic propylene polymer material of the present invention is a heterophasic propylene polymer material containing a propylene polymer A, a propylene polymer B, and a propylene copolymer C, in which the propylene polymer A contains 80% by mass or more of a monomer unit derived from propylene and has an intrinsic viscosity of 2.0 dL / g or less, the propylene polymer B contains 80% by mass or more of a monomer unit derived from propylene and has an intrinsic viscosity of 2.1 to 4.9 dL / g, and the propylene copolymer C is an ethylene copolymer. The heterophasic propylene polymerization material contains 30 to 55 mass% of monomer units derived from at least one α-olefin selected from the group consisting of olefins and α-olefins having 4 to 12 carbon atoms, and monomer units derived from propylene, has an intrinsic viscosity of 1.5 to 4.5 dL / g, and the contents of propylene-based polymer A, propylene-based polymer B, and propylene copolymer C are 50 to 75 mass%, 5 to 20 mass%, and 5 to 40 mass%, respectively, relative to the total mass of the heterophasic propylene polymerization material being 100 mass%.

[0007] In the heterophasic propylene polymerization material, the propylene polymer A has an intrinsic viscosity of 0.3 to 1.2 dL / g, the propylene polymer B has an intrinsic viscosity of 2.5 to 4.0 dL / g, and the propylene copolymer C has an intrinsic viscosity of 2.0 to 4.0 dL / g. The content of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms in the propylene copolymer C is 35 to 50 mass%, and the contents of the propylene polymer A, the propylene polymer B, and the propylene copolymer C may be 60 to 75 mass%, 7 to 18 mass%, and 7 to 33 mass%, respectively, based on the total mass of the heterophasic propylene polymerization material being 100 mass%. Effect of the Invention

[0008] According to the present invention, there is provided a heterophasic propylene polymerization material from which molded articles having excellent dimensional stability can be produced. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] [Definition] As used herein, the term "α-olefin" refers to an aliphatic unsaturated hydrocarbon having an α-position carbon-carbon unsaturated double bond. In this specification, the term "heterophagic propylene polymerization material" means a mixture having a structure in which a propylene copolymer containing monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms and monomer units derived from propylene is dispersed in a matrix of a propylene-based polymer containing 80% by mass or more of monomer units derived from propylene (wherein the total mass of the propylene-based polymer is taken as 100% by mass).

[0010] Hereinafter, some embodiments of the present invention will be described in detail. However, the present invention is not limited to the following embodiments. In this specification, the description "lower limit to upper limit" expressing a numerical range means "not less than the lower limit, not more than the upper limit", and the description "upper limit to lower limit" expresses "not more than the upper limit, not less than the lower limit". In other words, these descriptions express a numerical range including the upper limit and the lower limit.

[0011] [Heterophasic Propylene Polymerization Materials] The heterophasic propylene polymer material of the present embodiment is a heterophasic propylene polymer material containing a propylene-based polymer A, a propylene-based polymer B, and a propylene copolymer C, in which the propylene-based polymer A contains 80% by mass or more of a monomer unit derived from propylene and has an intrinsic viscosity of 2.0 dL / g or less, the propylene-based polymer B contains 80% by mass or more of a monomer unit derived from propylene and has an intrinsic viscosity of 2.1 to 4.9 dL / g, and the propylene copolymer C is The heterophasic propylene polymerization material contains 30 to 55 mass% of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having from 4 to 12 carbon atoms, and monomer units derived from propylene, has an intrinsic viscosity of 1.5 to 4.5 dL / g, and contains 50 to 75 mass% of propylene polymer A, 5 to 20 mass% of propylene polymer B, and 5 to 40 mass% of propylene copolymer C, respectively, relative to the total mass of the heterophasic propylene polymerization material being 100 mass%. Such a heterophasic propylene polymerization material can be used to produce a molded product having excellent dimensional stability.

[0012] In this specification, the intrinsic viscosity ([η], unit: dL / g) is a value measured at a temperature of 135° C. using tetralin as a solvent by the following method.

[0013] Using an Ubbelohde viscometer, the reduced viscosity is measured at three concentrations: 0.1 g / dL, 0.2 g / dL, and 0.5 g / dL. The reduced viscosity is plotted against the concentration, and the intrinsic viscosity is calculated by the extrapolation method in which the concentration is extrapolated to zero. The method for calculating the intrinsic viscosity by the extrapolation method is described, for example, in page 491 of "Polymer Solutions, Polymer Experiments 11" (published by Kyoritsu Publishing Co., Ltd. in 1982).

[0014] The intrinsic viscosity of the propylene polymer A may be from 0.3 to 1.2 dL / g, may be from 0.4 to 1.0 dL / g, or may be from 0.5 to 0.8 dL / g.

[0015] The propylene polymer A may be, for example, a propylene homopolymer, or may contain a monomer unit derived from a monomer other than propylene. When the propylene polymer A contains a monomer unit derived from a monomer other than propylene, the content of the monomer unit may be, for example, 0.01% by mass or more and less than 20% by mass based on the total mass of the propylene polymer A.

[0016] Examples of the monomer other than propylene include ethylene and α-olefins having 4 to 12 carbon atoms. Among them, at least one selected from the group consisting of ethylene and α-olefins having 4 to 10 carbon atoms is preferred, at least one selected from the group consisting of ethylene, 1-butene, 1-hexene, and 1-octene is more preferred, and at least one selected from the group consisting of ethylene and 1-butene is even more preferred.

[0017] Examples of propylene-based polymers containing monomer units derived from a monomer other than propylene include propylene-ethylene copolymers, propylene-1-butene copolymers, propylene-1-hexene copolymers, propylene-1-octene copolymers, propylene-ethylene-1-butene copolymers, propylene-ethylene-1-hexene copolymers, and propylene-ethylene-1-octene copolymers.

[0018] From the viewpoint of rigidity of the molded product, the propylene polymer A is preferably a propylene homopolymer, a propylene-ethylene copolymer, a propylene-1-butene copolymer, or a propylene-ethylene-1-butene copolymer, and more preferably a propylene homopolymer.

[0019] The heterophasic propylene polymer material of the present embodiment may contain only one type of propylene polymer A, or may contain two or more types.

[0020] The intrinsic viscosity of the propylene polymer B may be from 2.5 to 4.0 dL / g, may be from 2.6 to 3.9 dL / g, or may be from 2.8 to 3.7 dL / g.

[0021] The propylene polymer B may be, for example, a propylene homopolymer, or may contain a monomer unit derived from a monomer other than propylene. When the propylene polymer B contains a monomer unit derived from a monomer other than propylene, the content of the monomer unit may be, for example, 0.01% by mass or more and less than 20% by mass based on the total mass of the propylene polymer A.

[0022] Examples of the monomer other than propylene include ethylene and α-olefins having 4 to 12 carbon atoms. Among them, at least one selected from the group consisting of ethylene and α-olefins having 4 to 10 carbon atoms is preferred, at least one selected from the group consisting of ethylene, 1-butene, 1-hexene, and 1-octene is more preferred, and at least one selected from the group consisting of ethylene and 1-butene is even more preferred.

[0023] Examples of propylene-based polymers containing monomer units derived from a monomer other than propylene include propylene-ethylene copolymers, propylene-1-butene copolymers, propylene-1-hexene copolymers, propylene-1-octene copolymers, propylene-ethylene-1-butene copolymers, propylene-ethylene-1-hexene copolymers, and propylene-ethylene-1-octene copolymers.

[0024] From the viewpoint of rigidity of the molded article, the propylene polymer B is preferably a propylene homopolymer, a propylene-ethylene copolymer, a propylene-1-butene copolymer, or a propylene-ethylene-1-butene copolymer, and more preferably a propylene homopolymer.

[0025] The heterophasic propylene polymer material of the present embodiment may contain only one type of propylene polymer B, or may contain two or more types.

[0026] The intrinsic viscosity of the propylene copolymer C may be from 2.0 to 4.0 dL / g, may be from 2.1 to 3.5 dL / g, or may be from 2.1 to 3.0 dL / g.

[0027] In the propylene copolymer C, the content of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms may be 35 to 50 mass%, 36 to 48 mass%, or 38 to 45 mass%.

[0028] In the propylene copolymer C, the at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms is preferably at least one selected from the group consisting of ethylene and α-olefins having 4 to 10 carbon atoms, more preferably at least one selected from the group consisting of ethylene, 1-butene, 1-hexene, 1-octene and 1-decene, and even more preferably at least one selected from the group consisting of ethylene and 1-butene.

[0029] Examples of the propylene copolymer C include propylene-ethylene copolymer, propylene-ethylene-1-butene copolymer, propylene-ethylene-1-hexene copolymer, propylene-ethylene-1-octene copolymer, propylene-ethylene-1-decene copolymer, propylene-1-butene copolymer, propylene-1-hexene copolymer, propylene-1-octene copolymer and propylene-1-decene copolymer. Among them, the propylene copolymer C is preferably propylene-ethylene copolymer, propylene-1-butene copolymer or propylene-ethylene-1-butene copolymer, more preferably propylene-ethylene copolymer.

[0030] The heterophasic propylene polymer material of the present embodiment may contain only one type of propylene copolymer C, or may contain two or more types.

[0031] Examples of the heterophasic propylene polymerization material of this embodiment include (propylene)-(propylene-ethylene) polymerization materials, (propylene)-(propylene-ethylene-1-butene) polymerization materials, (propylene)-(propylene-ethylene-1-hexene) polymerization materials, (propylene)-(propylene-ethylene-1-octene) polymerization materials, (propylene)-(propylene-1-butene) polymerization materials, (propylene)-(propylene-1-hexene) polymerization materials, (propylene)-(propylene-1-octene) polymerization materials, (propylene)-(propylene-1-octene) polymerization materials, and (propylene)-(propylene-1-octene) polymerization materials. (propylene-1-decene) polymerization materials, (propylene-ethylene)-(propylene-ethylene) polymerization materials, (propylene-ethylene)-(propylene-ethylene-1-butene) polymerization materials, (propylene-ethylene)-(propylene-ethylene-1-hexene) polymerization materials, (propylene-ethylene)-(propylene-ethylene-1-octene) polymerization materials, (propylene-ethylene)-(propylene-ethylene-1-decene) polymerization materials, (propylene-ethylene)-(propylene-1-butene) polymerization materials, (propylene-ethylene)-(propylene-1 -hexene) polymerization materials, (propylene-ethylene)-(propylene-1-octene) polymerization materials, (propylene-ethylene)-(propylene-1-decene) polymerization materials, (propylene-1-butene)-(propylene-ethylene) polymerization materials, (propylene-1-butene)-(propylene-ethylene-1-butene) polymerization materials, (propylene-1-butene)-(propylene-ethylene-1-hexene) polymerization materials, (propylene-1-butene)-(propylene-ethylene-1-octene) polymerization materials, (propylene-1-butene)-(propylene-ethylene -1-decene) polymerization materials, (propylene-1-butene)-(propylene-1-butene) polymerization materials, (propylene-1-butene)-(propylene-1-hexene) polymerization materials, (propylene-1-butene)-(propylene-1-octene) polymerization materials, (propylene-1-butene)-(propylene-1-decene) polymerization materials, (propylene-1-hexene)-(propylene-1-hexene) polymerization materials, (propylene-1-hexene)-(propylene-1-octene) polymerization materials, (propylene-1-hexene)-(propylene-1-decene) polymerization materials,Examples of the polymerizable composition include (propylene-1-octene)-(propylene-1-octene) polymerizable materials and (propylene-1-octene)-(propylene-1-decene) polymerizable materials. Among them, (propylene)-(propylene-ethylene) polymerizable materials, (propylene)-(propylene-ethylene-1-butene) polymerizable materials, (propylene-ethylene)-(propylene-ethylene-1-butene) polymerizable materials, and (propylene-1-butene)-(propylene-1-butene) polymerizable materials are preferred, and (propylene)-(propylene-ethylene) polymerizable materials are more preferred.

[0032] Here, the above description indicates "(type of propylene-based polymer containing 80% by mass or more of monomer units derived from propylene)-(type of propylene copolymer C)". In other words, the description "(propylene)-(propylene-ethylene) polymerization material" means "a heterophasic propylene polymerization material in which propylene-based polymers A and B are propylene homopolymers, and propylene copolymer C is a propylene-ethylene copolymer". The same applies to other similar expressions.

[0033] The contents of the propylene polymer A, the propylene polymer B and the propylene copolymer C may be 60 to 75 mass%, 7 to 18 mass%, and 7 to 33 mass%, respectively, relative to 100 mass% of the total mass of the heterophasic propylene polymerization material.

[0034] In the heterophasic propylene polymerization material of this embodiment, the propylene polymer A has an intrinsic viscosity of 0.3 to 1.2 dL / g, the propylene polymer B has an intrinsic viscosity of 2.5 to 4.0 dL / g, and the propylene copolymer C has an intrinsic viscosity of 2.0 to 4.0 dL / g. In the propylene copolymer C, the content of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms is 35 to 50 mass%, and the contents of the propylene polymer A, propylene polymer B, and propylene copolymer C are 60 to 75 mass%, 7 to 18 mass%, and 7 to 33 mass%, respectively, based on the total mass of the heterophasic propylene polymerization material being 100 mass%, which are preferable from the viewpoint of dimensional stability.

[0035] The isotactic pentad fraction (also referred to as the [mmmm] fraction) of the heterophasic propylene polymer material is preferably 0.950 or more, more preferably 0.970 or more, from the viewpoint of the rigidity and dimensional stability of a molded article made of the resin composition. The isotactic pentad fraction of component A may be, for example, 1.000 or less. A polymer having an isotactic pentad fraction close to 1 is considered to have a high stereoregularity of the molecular structure and high crystallinity.

[0036] The isotactic pentad fraction means the isotactic fraction in pentad units. That is, the isotactic pentad fraction indicates the content ratio of a structure in which five consecutive monomer units derived from propylene are meso-bonded when viewed in pentad units. In addition, when the target component is a copolymer, it means a value measured for the chain of monomer units derived from propylene.

[0037] In this specification, the isotactic pentad fraction is 13 This refers to the value measured by C-NMR spectroscopy. Specifically, 13 The ratio of the area of ​​the mmmm peak to the area of ​​all absorption peaks in the methyl carbon region obtained by C-NMR spectrum is defined as the isotactic pentad fraction. 13The method for measuring the isotactic pentad fraction by C-NMR spectroscopy is described, for example, in Macromolecules, 6, 925 (1973) by A. Zambelli et al. 13 The assignment of absorption peaks obtained by C-spectrum is based on the description in Macromolecules, 8, 687 (1975).

[0038] Additives such as heat stabilizers, UV stabilizers, antioxidants, crystal nucleating agents, lubricants, colorants, antiblocking agents, antistatic agents, antifogging agents, flame retardants, petroleum resins, foaming agents, foaming assistants, and organic or inorganic fillers can be added to the heterophasic propylene polymer material as needed. The amount of additives added is preferably 0.01% by weight or more and 30% by weight or less based on the total amount of the heterophasic propylene polymer material. The additives may be used alone or in combination of two or more kinds at any ratio.

[0039] [Method for producing heterophasic propylene polymer material] An example of a method for producing the heterophasic propylene polymerization material will be described. This method includes steps 1, 2, and 3.

[0040] Step 1: Step 1-1 of polymerizing a monomer containing propylene in a liquid phase under the condition that the hydrogen / propylene ratio is 1000 mol ppm or more to obtain at least a part of a propylene-based polymer A; and A step 1-2 of polymerizing a monomer containing propylene in a gas phase under conditions where the hydrogen / propylene ratio is 50,000 mol ppm or more to obtain at least a part of a propylene-based polymer A. At least one step selected from the group consisting of Step 2: Step 2-1 of polymerizing a monomer containing propylene in a liquid phase under conditions where the hydrogen / propylene ratio is 40 mol ppm or more and less than 1000 mol ppm to obtain at least a part of a propylene-based polymer B; and A step 2-2 of polymerizing a monomer containing propylene in a gas phase under conditions where the hydrogen / propylene ratio is 40 mol ppm or more and less than 50,000 mol ppm to obtain at least a part of a propylene-based polymer B. At least one step selected from the group consisting of Step 3: A step of polymerizing a monomer containing propylene and at least one α-olefin selected from the group consisting of α-olefins having 4 to 12 carbon atoms under the condition that the hydrogen / propylene ratio is 9,000 mol ppm or more and 310,000 mol ppm or less to obtain a propylene copolymer C.

[0041] In this specification, the hydrogen / propylene ratio is defined as follows. In the case of polymerization in the liquid phase, the hydrogen / propylene ratio refers to the ratio of the amounts of hydrogen, which is a gas, to propylene, which is a liquid, in the reactor supply section. In the case of polymerization in the gas phase, the hydrogen / propylene ratio refers to the ratio of the amounts of gaseous hydrogen to the amount of gaseous propylene at the outlet of the reactor. In this specification, for example, the description "the hydrogen / propylene ratio is 1 mol ppm" means "the hydrogen / propylene ratio is 1×10 -6 mol / mol" and 1 mole of propylene is equivalent to 1×10 hydrogen. -6 This means that it is mol.

[0042] [Process 1-1] In step 1-1, for example, a liquid phase polymerization reactor is used to polymerize a monomer containing propylene in the presence of a polymerization catalyst and hydrogen. The composition of the monomers used in the polymerization can be appropriately adjusted based on the type and content of the monomer units constituting the propylene-based polymer A. The content of propylene in the monomers may be, for example, 80% by mass or more, 90% by mass or more, or 100% by mass, based on the total mass of the monomers.

[0043] Examples of liquid phase polymerization reactors include loop type liquid phase reactors and vessel type liquid phase reactors.

[0044] Examples of the polymerization catalyst include Ziegler-Natta catalysts and metallocene catalysts, and Ziegler-Natta catalysts are preferred. Examples of the Ziegler-Natta catalyst include Ti-Mg catalysts such as a solid catalyst component obtained by contacting a magnesium compound with a titanium compound; and a catalyst containing a solid catalyst component obtained by contacting a magnesium compound with a titanium compound, an organoaluminum compound, and a third component such as an electron donor compound as required. A catalyst containing a solid catalyst component obtained by contacting a magnesium compound with a titanium compound, an organoaluminum compound, and a third component such as an electron donor compound as required is preferred. A catalyst containing a solid catalyst component obtained by contacting a magnesium compound with a titanium compound, an organoaluminum compound, and a third component such as an electron donor compound as required is more preferred. A catalyst containing a solid catalyst component obtained by contacting a magnesium compound with a titanium halide compound, an organoaluminum compound, and an electron donor compound can also be used as a polymerization catalyst by contacting a small amount of olefin and preactivating it.

[0045] As the polymerization catalyst, a prepolymerized catalyst component obtained by prepolymerizing an olefin in the presence of the above-mentioned solid catalyst component, n-hexane, triethylaluminum, tert-butyl-n-propyldimethoxysilane, etc. can also be used. The olefin used in the prepolymerization is preferably any one of the olefins constituting the heterophasic propylene polymerization material.

[0046] The polymerization temperature can be, for example, from 0 to 120° C. The polymerization pressure can be, for example, from normal pressure to 10 MPaG.

[0047] The hydrogen / propylene ratio in step 1-1 may be 1500 mol ppm or more and 100000 mol ppm or less, or may be 3000 mol ppm or more and 50000 mol ppm or less.

[0048] [Step 1-2] In step 1-2, for example, a gas phase polymerization reactor is used to polymerize a monomer containing propylene in the presence of a polymerization catalyst and hydrogen. The composition of the monomers used in the polymerization can be appropriately adjusted based on the type and content of the monomer units constituting the propylene-based polymer A. The content of propylene in the monomers may be, for example, 80% by mass or more, 90% by mass or more, or 100% by mass, based on the total mass of the monomers.

[0049] Gas phase polymerization reactors include, for example, fluidized bed reactors and spouted bed reactors.

[0050] The gas-phase polymerization reactor may be a multi-stage gas-phase polymerization reactor having a plurality of reaction zones connected in series. The multi-stage gas-phase polymerization reactor may be a multi-stage gas-phase polymerization reactor having a plurality of polymerization vessels connected in series. It is considered that such an apparatus makes it easy to adjust the intrinsic viscosity of the propylene polymer A to the above range.

[0051] The multistage gas phase polymerization reaction apparatus may, for example, comprise a cylindrical section extending in the vertical direction, and a reduced diameter section formed in the cylindrical section, the inner diameter of which decreases downward and which has a gas introduction opening at its lower end, and may comprise a spouted bed type olefin polymerization reaction region surrounded by the inner surface of the reduced diameter section and the inner surface of the cylindrical section above the reduced diameter section, within which a spouted bed is formed, and a fluidized bed type olefin polymerization reaction region.

[0052] The multistage gas phase polymerization reactor preferably has a plurality of reaction zones in the vertical direction. From the viewpoint of the intrinsic viscosity of the propylene polymer A, the multistage gas phase polymerization reactor preferably has a plurality of reaction zones in the vertical direction, of which the uppermost one is a fluidized bed type olefin polymerization reaction zone and the remaining ones are a plurality of spouted bed type olefin polymerization reaction zones. In such an apparatus, for example, a solid component is supplied from the top of the apparatus and a gas component is supplied from the bottom of the apparatus to form a fluidized bed or spouted bed in the reaction zone. The gas component may contain an inert gas such as nitrogen in addition to a monomer containing propylene and hydrogen. In the apparatus, the number of spouted bed type olefin polymerization reaction zones is preferably 3 or more.

[0053] When multiple reaction zones are provided vertically, the lower reaction zone may be disposed obliquely below the upper reaction zone. In such an apparatus, for example, the solid components obtained in the upper reaction zone are discharged obliquely downward, and the discharged solid components are supplied to the lower reaction zone from obliquely above. In this case, the gas components are, for example, gas components discharged from the upper part of the lower reaction zone and supplied from the lower part of the upper reaction zone.

[0054] Specific examples of the polymerization catalyst are the same as those mentioned above.

[0055] The polymerization temperature may be, for example, 0 to 120° C., 20 to 100° C., or 40 to 100° C. The polymerization pressure may be, for example, normal pressure to 10 MPaG, or 1 to 5 MPaG.

[0056] The hydrogen / propylene ratio in step 1-2 may be 65,000 mol ppm or more and 1,500,000 mol ppm or less, or may be 80,000 mol ppm or more and 1,000,000 mol ppm or less.

[0057] [Step 2-1] In step 2-1, for example, a liquid phase polymerization reactor is used to polymerize a monomer containing propylene in the presence of a polymerization catalyst and hydrogen. The composition of the monomers used in the polymerization can be appropriately adjusted based on the type and content of the monomer units constituting the propylene-based polymer B. The content of propylene in the monomers may be, for example, 80% by mass or more, 90% by mass or more, or 100% by mass, based on the total mass of the monomers.

[0058] The liquid phase polymerization reactor used in step 2-1 may be, for example, a loop type liquid phase reactor or a vessel type liquid phase reactor.

[0059] Specific examples of the polymerization catalyst are the same as those mentioned above.

[0060] The polymerization temperature can be, for example, from 0 to 120° C. The polymerization pressure can be, for example, from normal pressure to 10 MPaG.

[0061] The hydrogen / propylene ratio in step 2-1 may be 50 mol ppm or more and 900 mol ppm or less, or may be 75 mol ppm or more and 750 mol ppm or less.

[0062] [Step 2-2] In step 2-2, for example, a gas phase polymerization reactor is used to polymerize a monomer containing propylene in the presence of a polymerization catalyst and hydrogen. The composition of the monomers used in the polymerization can be appropriately adjusted based on the type and content of the monomer units constituting the propylene-based polymer B. The content of propylene in the monomers may be, for example, 80% by mass or more, 90% by mass or more, or 100% by mass, based on the total mass of the monomers.

[0063] The gas phase polymerization reactor used in step 2-2 may be, for example, a fluidized bed reactor or a spouted bed reactor.

[0064] Specific examples of the polymerization catalyst are the same as those mentioned above.

[0065] The polymerization temperature may be, for example, 0 to 120° C., 20 to 100° C., or 40 to 100° C. The polymerization pressure may be, for example, normal pressure to 10 MPaG, or 1 to 5 MPaG.

[0066] The hydrogen / propylene ratio in step 2-2 may be 100 mol ppm or more and 35,000 mol ppm or less, or may be 300 mol ppm or more and 20,000 mol ppm or less.

[0067] [Process 3] Step 3 may be performed in either liquid or gas phase, but is performed, for example, in gas phase. When performed in liquid phase, for example, a liquid phase reactor such as a loop type or vessel type can be used. When performed in gas phase, for example, a gas phase reactor such as a fluidized bed type reactor or a spouted bed type reactor can be used.

[0068] In step 3, for example, in the presence of a polymerization catalyst and hydrogen, a monomer containing at least one α-olefin selected from the group consisting of α-olefins having 4 to 12 carbon atoms and propylene is polymerized. The composition of the monomers used in the polymerization can be appropriately adjusted based on the type and content of the monomer units constituting the propylene copolymer C. The content of at least one α-olefin selected from the group consisting of α-olefins having 4 to 12 carbon atoms in the monomers used in the polymerization may be, for example, 30 to 55 mass% or 35 to 50 mass% based on the total mass of the monomers.

[0069] Specific examples of the polymerization catalyst are the same as those mentioned above.

[0070] In the case of polymerization in a liquid phase, the polymerization temperature is, for example, 40 to 100° C., and the polymerization pressure is, for example, normal pressure to 5 MPaG. In the case of polymerization in a gas phase, the polymerization temperature is, for example, 40 to 100° C., and the polymerization pressure is, for example, 0.5 to 5 MPaG.

[0071] The hydrogen / propylene ratio in step 3 may be 12,000 mol ppm or more and 250,000 mol ppm or less, or may be 15,000 mol ppm or more and 200,000 mol ppm or less.

[0072] The propylene polymer A, the propylene polymer B and the propylene copolymer C may be produced in respective steps, and the polymerization catalyst may be deactivated before mixing them in a solution state, a molten state or the like, or the polymer may be continuously produced by supplying the resulting polymer to the next step without deactivating the catalyst. When the polymerization is continuously carried out without deactivating the catalyst, the polymerization catalyst in the previous step also acts as a polymerization catalyst in the subsequent step.

[0073] There is no particular limitation on the order of steps 1, 2, and 3. Step 1 preferably includes step 1-1 and step 1-2, and step 2 preferably includes step 2-2.

[0074] The manufacturing method according to this embodiment may include, for example, step 1-1, step 1-2, step 2-2, and step 3 in this order.

[0075] In the production method according to the present embodiment, from the viewpoint of dimensional stability of the molded body, the hydrogen / propylene ratio in step 1-1 is 1500 molppm or more and 100000 molppm or less, the hydrogen / propylene ratio in step 1-2 is 65000 molppm or more and 1500000 molppm or less, the hydrogen / propylene ratio in step 2-1 is 50 molppm or more and 900 molppm or less, the hydrogen / propylene ratio in step 2-2 is 100 molppm or more and 35000 molppm or less, and the hydrogen / propylene ratio in step 3 is 12000 molppm or more and 250000 molppm or less. m or less, and more preferably, the hydrogen / propylene ratio in step 1-1 is 3000 molppm or more and 50000 molppm or less, the hydrogen / propylene ratio in step 1-2 is 80000 molppm or more and 1000000 molppm or less, the hydrogen / propylene ratio in step 2-1 is 75 molppm or more and 750 molppm or less, the hydrogen / propylene ratio in step 2-2 is 300 molppm or more and 20000 molppm or less, and the hydrogen / propylene ratio in step 3 is 15000 molppm or more and 200000 molppm or less.

[0076] That is, the method for producing the heterophasic propylene polymerization material according to this embodiment may include steps 1, 2, and 3.

[0077] Step 1: Step 1-1 of polymerizing a monomer containing propylene in a liquid phase under the condition that the hydrogen / propylene ratio is 1000 mol ppm or more to obtain at least a part of a propylene-based polymer A; and A step 1-2 of polymerizing a monomer containing propylene in a gas phase under conditions where the hydrogen / propylene ratio is 50,000 mol ppm or more to obtain at least a part of a propylene-based polymer A. At least one step selected from the group consisting of Step 2: Step 2-1 of polymerizing a monomer containing propylene in a liquid phase under conditions where the hydrogen / propylene ratio is 40 mol ppm or more and less than 1000 mol ppm to obtain at least a part of a propylene-based polymer B; and A step 2-2 of polymerizing a monomer containing propylene in a gas phase under conditions where the hydrogen / propylene ratio is 40 mol ppm or more and less than 50,000 mol ppm to obtain at least a part of a propylene-based polymer B. At least one step selected from the group consisting of Step 3: A step of polymerizing a monomer containing propylene and at least one α-olefin selected from the group consisting of α-olefins having 4 to 12 carbon atoms under the condition that the hydrogen / propylene ratio is 9,000 mol ppm or more and 310,000 mol ppm or less to obtain a propylene copolymer C.

[0078] In the method for producing the heterophasic propylene polymerization material, the hydrogen / propylene ratio in step 1-1 can be 1500 molppm or more and 100,000 molppm or less, the hydrogen / propylene ratio in step 1-2 can be 65,000 molppm or more and 1,500,000 molppm or less, the hydrogen / propylene ratio in step 2-1 can be 50 molppm or more and 900 molppm or less, the hydrogen / propylene ratio in step 2-2 can be 100 molppm or more and 35,000 molppm or less, and the hydrogen / propylene ratio in step 3 can be 12,000 molppm or more and 250,000 molppm or less.

[0079] In the method for producing the heterophasic propylene polymerization material, the hydrogen / propylene ratio in step 1-1 can be 3,000 molppm or more and 50,000 molppm or less, the hydrogen / propylene ratio in step 1-2 can be 80,000 molppm or more and 1,000,000 molppm or less, the hydrogen / propylene ratio in step 2-1 can be 75 molppm or more and 750 molppm or less, the hydrogen / propylene ratio in step 2-2 can be 300 molppm or more and 20,000 molppm or less, and the hydrogen / propylene ratio in step 3 can be 15,000 molppm or more and 200,000 molppm or less. EXAMPLES

[0080] The present invention will be described in more detail below with reference to examples, although the present invention is not limited to these examples.

[0081] The measurement and evaluation methods for each item in the examples and comparative examples are shown below.

[0082] [Intrinsic viscosity ([η], unit: dL / g)] The reduced viscosity was measured at three concentrations, 0.1 g / dL, 0.2 g / dL, and 0.5 g / dL, using an Ubbelohde viscometer. The intrinsic viscosity was calculated by the calculation method described in the reference "Polymer Solutions, Polymer Experiments 11" (published by Kyoritsu Shuppan Co., Ltd. in 1982), page 491, that is, by plotting the reduced viscosity against the concentration and extrapolating the concentration to zero. The measurement was performed at a temperature of 135°C using tetralin as a solvent.

[0083] [Ethylene unit content in the obtained heterophasic propylene polymerization material (unit: mass%)] The ethylene unit content in the heterophasic propylene polymerization material obtained by IR spectroscopy was determined in accordance with the IR spectroscopy measurement described on page 619 of the Polymer Handbook (published by Kinokuniya Shoten in 1995). Note that the "ethylene unit" here means a structural unit derived from ethylene. The ethylene content in the heterophasic propylene polymerization material was divided by the proportion (X) of the ethylene-propylene copolymer in the heterophasic propylene polymerization material to determine the ethylene content in the propylene copolymer C. Note that the proportion (X) of the ethylene-propylene copolymer in the heterophasic propylene polymerization material was determined by the method described below.

[0084] For the evaluation of the dimensional stability and the number of gels in the examples and comparative examples, pellets prepared by the following method were used. 100 parts by weight of heterophasic propylene polymerization material was mixed with 0.05 parts by weight of calcium stearate (manufactured by Nippon Oil & Fats Co., Ltd.), 0.1 parts by weight of octadecyl-3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate, and 0.1 parts by weight of 6-[3-(3-t-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butyldibenzo[d,f][1.3.2]dioxaphosphepine (Sumilizer GP, manufactured by Sumitomo Chemical Co., Ltd.), and then melt-kneaded using a single-screw extruder (manufactured by Tanabe Plastics Co., Ltd., barrel inner diameter: 40 mm, screw rotation speed: 100 rpm, cylinder temperature: 200°C), and the resulting melt-kneaded product was then extruded from the die. The extrudate was cooled and solidified with cold water, cut, and pellets were obtained.

[0085] [Dimensional stability] The heterophasic propylene polymer materials of the Examples and Comparative Examples pelletized by the above-mentioned method were injection molded to obtain injection molded articles, and their dimensional stability was evaluated by measuring the linear expansion coefficients of the injection molded articles.

[0086] [Manufacturing of injection molded products] The heterophasic propylene polymerization material was injection molded to produce an injection molded body under the following conditions: the injection molding machine was a Sumitomo Heavy Industries SE180D with a clamping force of 180 tons, the mold was 100 mm x 400 mm x 3 mm (thickness) with one gate from the end face, and the molding temperature was 180°C, the injection speed was 5 mm / sec, and the mold temperature was 30°C.

[0087] [Measurement of linear expansion coefficient] The linear expansion coefficient of the injection molded body was measured by the following method using a thermomechanical analyzer TMA / SS6100 manufactured by SII Nano Technology Co., Ltd.

[0088] A test piece of 5 x 10 x 3 (mm) was cut out from the center of the longitudinal direction of the injection molded body. The test piece was set in the above-mentioned device and heated from -50°C to 130°C at a heating rate of 5°C / min to remove residual strain during molding. The test piece was then set again in the device so that the dimensional change in the MD direction (resin flow direction) or TD direction (orthogonal to the MD direction) during injection molding could be measured, and the dimensions at 23°C were accurately measured. The temperature was raised from -20 to 80°C at a heating rate of 5°C / min, and the dimensional changes in the MD and TD directions during that time were measured. The dimensional change per unit length and unit temperature was calculated as the linear expansion coefficient. The sum of the linear expansion coefficient in the MD direction and the linear expansion coefficient in the TD direction divided by 2 was defined as the "MDTD average linear expansion coefficient" (unit: 1 / °C). The smaller the MDTD linear expansion coefficient value, the better the dimensional stability.

[0089] [Number of gels] The heterophasic propylene polymer materials of the Examples and Comparative Examples which were pelletized by the above-mentioned method were extruded to obtain sheets, and the number of gels in the sheets was measured.

[0090] [Sheet manufacturing] The sheet for measuring the number of gels was prepared according to the following method: the material was melt-extruded into a sheet at a resin temperature of 230°C using a single-screw extruder (VS20-14 model, manufactured by Tanabe Plastic Machinery Co., Ltd.) with a screw diameter of 20 mm, and the melt-extruded sheet was cooled using a cooling roll through which cooling water at 30°C was passed to prepare a sheet with a thickness of 50 μm.

[0091] [Measurement of gel number] The surface of the sheet was observed using a GT-X970 scanner manufactured by Epson, and an image of the sheet surface was obtained. The image of the sheet surface obtained was imported into a computer at 900 dpi and 8 bit, and a binarization process was carried out in which areas with a threshold value of 120 or more were designated white, and areas with a threshold value of less than 120 were designated black. The binarization process was carried out using "Azo-kun", an image analysis software manufactured by Asahi Kasei Engineering. The white areas were regarded as gels. Since the shape of the gel was irregular, the equivalent circle diameter was regarded as the size of the gel. For a 100 cm sheet 2 Number of gels with diameters of 100 μm or more per 100 cm2 ) was sought.

[0092] [Reference Example: Production of solid catalyst component] After replacing the atmosphere in a 100mL flask equipped with a stirrer, a dropping funnel, and a thermometer with nitrogen, 36.0mL of toluene and 22.5mL of titanium tetrachloride were added to the flask and stirred to obtain a titanium tetrachloride solution. After the temperature in the flask was set to 0°C, 1.88g of magnesium diethoxide was added four times at 30 minute intervals at the same temperature, and then the mixture was stirred at 0°C for 1.5 hours. Next, 0.60mL of ethyl 2-ethoxymethyl-3,3-dimethylbutanoate was added to the flask, and the temperature in the flask was raised to 10°C. After that, the mixture was stirred at the same temperature for 2 hours, and 9.8mL of toluene was added. Next, the temperature in the flask was raised, and at 60°C, 3.15mL of ethyl 2-ethoxymethyl-3,3-dimethylbutanoate was added to the flask, and the temperature was raised to 110°C. The mixture in the flask was stirred at the same temperature for 3 hours.

[0093] The resulting mixture was subjected to solid-liquid separation to obtain a solid, which was washed three times with 56.3 mL of toluene at 100°C.

[0094] To the washed solid, 38.3 mL of toluene was added to form a slurry. To the slurry, 15.0 mL of titanium tetrachloride and 0.75 mL of ethyl 2-ethoxymethyl-3,3-dimethylbutanoate were added to form a mixture, and the mixture was stirred at 110° C. for 1 hour. Thereafter, the stirred mixture was subjected to solid-liquid separation, and the solid was washed three times with 56.3 mL of toluene at 60° C., and further washed three times with 56.3 mL of hexane at room temperature. The washed solid was dried under reduced pressure to obtain a solid catalyst component.

[0095] The solid catalyst component had a titanium atom content of 2.53% by mass, an ethoxy group content of 0.44% by mass, and an internal electron donor content of 13.7% by mass. The median particle size measured by the laser diffraction / scattering method was 59.5 μm, and the cumulative percentage of components with a particle size distribution of 10 μm or less on a volume basis was 5.3%. The amount of peak components originating from the oxygen atom 1s orbital and having a peak position in the range of binding energy of 532 to 534 eV measured by XPS analysis was 85.0%, and the amount of peak components having a peak position in the range of binding energy of 529 to 532 eV was 15.0%. The total pore volume measured by the mercury intrusion method was 1.43 mL / g, the total volume of pores with a pore radius of 5 to 30 nm was 0.160 mL / g, the total volume of pores with a pore radius of 30 to 700 nm was 0.317 mL / g, and the specific surface area was 107.44 m 2 / g.

[0096] Example 1: Preparation of heterophasic propylene polymer material [Prepolymerization] In a SUS autoclave equipped with a stirrer and having an internal volume of 3 L, 1.0 L of n-hexane that had been thoroughly dehydrated and degassed, 35 mmol of triethylaluminum (hereinafter sometimes referred to as "TEA"), and 3.5 mmol of tert-butyl-n-propyldimethoxysilane were placed. 22 g of the solid catalyst component produced in the Reference Example was added thereto, and while maintaining the temperature inside the autoclave at about 10°C, 22 g of propylene was continuously fed over about 30 minutes to carry out prepolymerization. Thereafter, the prepolymerized slurry was transferred to a SUS316L autoclave equipped with a stirrer and having an internal volume of 150 L, and 100 L of liquid butane was added to obtain a slurry of the prepolymerized catalyst component.

[0097] [Main polymerization] For this polymerization, an apparatus in which a slurry polymerization reactor, a multistage gas phase polymerization reactor, and two gas phase polymerization reactors were arranged in series was used. Specifically, a propylene homopolymer was produced in the following polymerization step 1-1, polymerization step 1-2, and polymerization step 2, and the produced polymer was transferred to the subsequent step without being deactivated, and an ethylene-propylene copolymer was produced in the following polymerization step 3.

[0098] [Polymerization process 1-1 (propylene homopolymerization using a slurry polymerization reactor)] Propylene homopolymerization was carried out using a SUS304 vessel-type slurry polymerization reactor equipped with an agitator. That is, propylene, hydrogen, TEA, tert-butyl-n-propyldimethoxysilane, and the above-mentioned slurry of prepolymerized catalyst components were continuously fed into the reactor to carry out the polymerization reaction. The reaction conditions were as follows.

[0099] Polymerization temperature: 50℃ Stirring speed: 150rpm Reactor liquid level: 18L Propylene supply: 25kg / hour Hydrogen supply: 160NL / hour Hydrogen / propylene ratio: 12000 mol ppm TEA supply: 31.3mmol / hour Supply amount of tert-butyl-n-propyldimethoxysilane: 6.39 mmol / hour Supply amount of slurry of prepolymerization catalyst component (converted into polymerization catalyst component): 0.94 g / hour Polymerization pressure: 3.93MPa (gauge pressure)

[0100] The intrinsic viscosity [η]L1 of the propylene homopolymer sampled from the outlet of the slurry polymerization reactor was 0.69 dL / g.

[0101] The hydrogen / propylene ratio in the examples and comparative examples refers to the ratio of the amounts of hydrogen (gas) and propylene (liquid) at the hydrogen / propylene reactor supply section in the vessel-type slurry polymerization reactor and loop-type liquid phase polymerization reactor, and refers to the ratio of the amounts of hydrogen (gas) and propylene (gas) at the reactor outlet in the gas phase polymerization reactor.

[0102] [Polymerization process 1-2 (Propylene homopolymerization (gas phase polymerization) using a multistage gas phase polymerization reactor)] Propylene homopolymerization was carried out using a multistage gas phase polymerization reactor having six reaction zones in the vertical direction, of which the uppermost zone was a fluidized bed and the remaining five zones were spouted beds.

[0103] A slurry containing polypropylene particles and liquid propylene was continuously fed from the preceding slurry polymerization reactor to the fluidized bed, which was the uppermost stage of the multistage gas phase polymerization reactor, without being deactivated.

[0104] The polypropylene particles were transferred between stages in the multi-stage gas phase polymerization reactor using a double valve system. This transfer means connected the upper and lower reaction zones with a 1-inch piping, equipped the piping with two on-off valves, and while closing the lower valve, opened the upper valve to accumulate powder from the upper reaction zone between the valves, and then closed the upper valve and opened the lower valve to transfer the polypropylene particles to the lower reaction zone.

[0105] Propylene and hydrogen were continuously fed into the lower part of the multistage gas phase polymerization reactor having the above-mentioned configuration. In this way, a fluidized bed or a spouted bed was formed in each reaction zone, and the feed rates of propylene and hydrogen were controlled to keep the gas composition and pressure constant, and propylene homopolymerization was further carried out while purging excess gas. The reaction conditions were as follows:

[0106] Polymerization temperature: 80℃ Polymerization pressure: 1.80MPa (gauge pressure)

[0107] In the reactor, the hydrogen / propylene ratio in the reactor was set to 230,000 mol ppm.

[0108] The intrinsic viscosity [η]G1 of the propylene homopolymer sampled from the reactor outlet was 0.65 dL / g. [η]L1 and [η]G1 are almost the same value, and the propylene homopolymer obtained up to the polymerization step 1-2 is the propylene polymer A. In Example 1, [η]G1 is the intrinsic viscosity of the propylene polymer A.

[0109] [Polymerization process 2 (Propylene homopolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the upstream multistage gas phase polymerization reactor were continuously fed to the fluidized bed reactor, which was equipped with a gas dispersion plate, and the polypropylene particles were transferred from the upstream multistage gas phase polymerization reactor to the fluidized bed reactor by the double valve system described above.

[0110] Propylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply rate and purging excess gas so as to keep the gas composition and pressure constant, propylene homopolymerization was carried out in the presence of polypropylene particles. The reaction conditions were as follows.

[0111] Polymerization temperature: 80℃ Polymerization pressure: 1.76MPa (gauge pressure)

[0112] In the reactor, the hydrogen / propylene ratio of the reactor outlet gas was set to 1700 mol ppm.

[0113] The intrinsic viscosity [η]G2 of the propylene polymer sampled from the reactor outlet was 1.05 dL / g. The polymer obtained from the reactor outlet in the polymerization step 2 was a mixture of the propylene polymer A and the propylene polymer B. The intrinsic viscosity [η]B of the propylene polymer B was calculated by the following method. [η]B=([η]G2-[η]G1×xi) / xii (5) xi: ratio of the mass of the propylene polymer A to the total mass of the polymer obtained from the reactor outlet in the polymerization step 2 (mass of the propylene polymer A / (total mass of the propylene polymer A and the propylene polymer B)) xii: Ratio of mass of propylene polymer B to the total mass of polymers obtained from the reactor outlet in polymerization step 2 (mass of propylene polymer B / (total mass of propylene polymer A and propylene polymer B)) Here, xi and xii can be determined from the material balance during polymerization.

[0114] [Polymerization step 3 (propylene-ethylene copolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the fluidized bed reactor in polymerization step 2 were continuously supplied to a subsequent fluidized bed reactor. The fluidized bed reactor in polymerization step 3 was equipped with a gas dispersion plate, similar to the fluidized bed reactor in polymerization step 2, and the transfer means for the polypropylene particles from the fluidized bed reactor in polymerization step 2 to the fluidized bed reactor in polymerization step 3 was a double valve system.

[0115] Propylene, ethylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply amount and purging excess gas to keep the gas composition and pressure constant, propylene and ethylene were copolymerized in the presence of polypropylene particles to obtain a heterophasic propylene polymerization material. The reaction conditions were as follows.

[0116] Polymerization temperature: 70℃ Polymerization pressure: 1.72MPa (gauge pressure)

[0117] In the reactor, the concentration ratio of the reactor outlet gas was ethylene / (propylene+ethylene) 38.4 mol % and hydrogen / propylene 69000 mol ppm.

[0118] The proportion (X) of the ethylene-propylene copolymer in the obtained heterophasic propylene polymer material was calculated by measuring the heat of crystal fusion of the propylene homopolymer and the entire heterophasic propylene polymer material, respectively, using the following formula: The heat of crystal fusion was measured by differential scanning calorimetry (DSC). X = 1-(ΔHf)T / (ΔHf)P (ΔHf)T: Heat of fusion of the entire heterophasic propylene polymer material (J / g) (ΔHf)P: Heat of fusion of propylene homopolymer (J / g)

[0119] The intrinsic viscosity [η]G3 of the propylene polymer sampled from the reactor outlet was 1.33 dL / g. The polymer obtained from the reactor outlet in the polymerization step 3 was a mixture of propylene polymer A, propylene polymer B, and propylene polymer C. The intrinsic viscosity [η]C of the propylene polymer C was calculated by the following method. [η]C=([η]G3-[η]G2×(1-X)) / X ···(6)

[0120] The intrinsic viscosity ([η]Total) of the obtained heterophasic propylene polymer material was 1.33 dL / g, and the ethylene content was 9.4 mass%. The polymerization ratio of the propylene polymer A, the propylene polymer B, and the propylene polymer C was 65 / 12 / 23, respectively. The ethylene content in the propylene polymer C was 41 mass%, and the intrinsic viscosity [η]C of the propylene polymer C was 2.3 dL / g.

[0121] Example 2: Preparation of heterophasic propylene polymer material [Prepolymerization] 1.4 L of n-hexane, 49 mmol of TEA, and 4.9 mmol of tert-butyl-n-propyldimethoxysilane, which had been thoroughly dehydrated and degassed, were placed in a SUS autoclave with an internal volume of 3 L and equipped with a stirrer. 21 g of the solid catalyst component produced in the Reference Example was added thereto, and while maintaining the temperature inside the autoclave at about 10°C, 103 g of propylene was continuously fed over about 30 minutes to carry out prepolymerization. The prepolymerized slurry was then transferred to a SUS316L autoclave with an internal volume of 260 L and equipped with a stirrer, and 180 L of liquid butane was added to obtain a slurry of the prepolymerized catalyst component.

[0122] [Main polymerization] For this polymerization, an apparatus in which a slurry polymerization reactor, a multistage gas phase polymerization reactor, and two gas phase polymerization reactors were arranged in series was used. Specifically, a propylene homopolymer was produced in the following polymerization step 1-1, polymerization step 1-2, and polymerization step 2, and the produced polymer was transferred to the subsequent step without being deactivated, and an ethylene-propylene copolymer was produced in the following polymerization step 3.

[0123] [Polymerization process 1-1 (propylene homopolymerization using a slurry polymerization reactor)] Propylene homopolymerization was carried out using a SUS304 vessel-type slurry polymerization reactor equipped with an agitator. That is, propylene, hydrogen, TEA, tert-butyl-n-propyldimethoxysilane, and the above-mentioned slurry of prepolymerized catalyst components were continuously fed into the reactor to carry out the polymerization reaction. The reaction conditions were as follows.

[0124] Polymerization temperature: 50℃ Stirring speed: 150rpm Reactor liquid level: 18L Propylene supply: 25kg / hour Hydrogen supply: 150NL / hour Hydrogen / propylene ratio: 11300 mol ppm TEA supply: 34.3mmol / hour Supply amount of tert-butyl-n-propyldimethoxysilane: 7.76mmol / hour Amount of slurry of prepolymerized catalyst component fed (converted into polymerization catalyst component): 0.72 g / hour Polymerization pressure: 3.99MPa (gauge pressure)

[0125] The intrinsic viscosity [η]L1 of the propylene homopolymer sampled from the outlet of the slurry polymerization reactor was 0.65 dl / g.

[0126] [Polymerization process 1-2 (Propylene homopolymerization (gas phase polymerization) using a multi-stage gas phase polymerization reactor)] Propylene homopolymerization was carried out using a multi-stage gas phase polymerization reactor having six reaction zones in the vertical direction, of which the top stage was a fluidized bed and the remaining five stages were spouted beds.

[0127] A slurry containing polypropylene particles and liquid propylene was continuously fed from the preceding slurry polymerization reactor to the fluidized bed, which was the uppermost stage of the multistage gas phase polymerization reactor, without being deactivated.

[0128] The polypropylene particles were transferred between stages in the multi-stage gas phase polymerization reactor using a double valve system. This transfer means connected the upper and lower reaction zones with a 1-inch piping, equipped the piping with two on-off valves, and while closing the lower valve, opened the upper valve to accumulate powder from the upper reaction zone between the valves, and then closed the upper valve and opened the lower valve to transfer the polypropylene particles to the lower reaction zone.

[0129] Propylene and hydrogen were continuously fed from the bottom of the multi-stage gas phase polymerization reactor having the above-mentioned configuration. As a result, a fluidized bed or a spouted bed was formed in each reaction zone, and the feed rates of propylene and hydrogen were controlled to keep the gas composition and pressure constant, and propylene homopolymerization was further carried out while purging excess gas. The reaction conditions were as follows.

[0130] Polymerization temperature: 80℃ Polymerization pressure: 1.99MPa (gauge pressure)

[0131] In the reactor, the hydrogen / propylene ratio in the reactor was set to 229,000 mol ppm.

[0132] The intrinsic viscosity [η]G1 of the propylene homopolymer sampled from the reactor outlet was 0.68 dl / g. [η]L1 and [η]G1 are almost the same value, and the propylene homopolymer obtained up to the polymerization step 1-2 is the propylene polymer A. In Example 2, [η]G1 is the intrinsic viscosity of the propylene polymer A.

[0133] [Polymerization process 2 (Propylene homopolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the upstream multistage gas phase polymerization reactor were continuously fed to the fluidized bed reactor, which was equipped with a gas dispersion plate, and the polypropylene particles were transferred from the upstream multistage gas phase polymerization reactor to the fluidized bed reactor by the double valve system described above.

[0134] Propylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply rate and purging excess gas so as to keep the gas composition and pressure constant, propylene homopolymerization was carried out in the presence of polypropylene particles. The reaction conditions were as follows.

[0135] Polymerization temperature: 80℃ Polymerization pressure: 1.59MPa (gauge pressure)

[0136] In the reactor, the hydrogen / propylene ratio of the reactor outlet gas was set to 2100 mol ppm.

[0137] The intrinsic viscosity [η]G2 of the propylene polymer sampled from the reactor outlet was 1.14 dl / g. The polymer obtained from the reactor outlet in the polymerization step 2 was a mixture of the propylene polymer A and the propylene polymer B. The intrinsic viscosity [η]B of the propylene polymer B was calculated in the same manner as in Example 1.

[0138] [Polymerization step 3 (propylene-ethylene copolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the fluidized bed reactor in polymerization step 2 were continuously supplied to a subsequent fluidized bed reactor. The fluidized bed reactor in polymerization step 3 was equipped with a gas dispersion plate, similar to the fluidized bed reactor in polymerization step 2, and the transfer means for the polypropylene particles from the fluidized bed reactor in polymerization step 2 to the fluidized bed reactor in polymerization step 3 was a double valve system.

[0139] Tetraethoxysilane was added to the fluidized bed reactor of the above configuration in an amount equivalent to 2.0 moles per mole of triethylaluminum supplied to the polymerization step 1-1. Propylene, ethylene and hydrogen were continuously supplied to the reactor, and while adjusting the gas supply amount and purging excess gas to keep the gas composition and pressure constant, copolymerization of propylene and ethylene was carried out in the presence of polypropylene particles to obtain a heterophasic propylene polymerization material. The reaction conditions were as follows.

[0140] Polymerization temperature: 70℃ Polymerization pressure: 1.54MPa (gauge pressure)

[0141] In the reactor, the concentration ratio of the reactor outlet gas was ethylene / (propylene+ethylene) 30.8 mol % and hydrogen / propylene 52,300 mol ppm.

[0142] The proportion (X) of the ethylene-propylene copolymer in the obtained heterophasic propylene polymer material was determined in the same manner as in Example 1.

[0143] The intrinsic viscosity [η]G3 of the propylene polymer sampled from the reactor outlet was 1.21 dl / g. The polymer obtained from the reactor outlet in the polymerization step 3 was a mixture of the propylene polymer A, the propylene polymer B, and the propylene polymer C. The intrinsic viscosity [η]C of the propylene polymer C was calculated in the same manner as in Example 1.

[0144] The intrinsic viscosity ([η]Total) of the obtained heterophasic propylene polymer material was 1.21 dL / g, and the ethylene content was 4.9 mass%. The polymerization ratio of the propylene polymer A, the propylene polymer B, and the propylene polymer C was 72 / 18 / 10, respectively. The ethylene content in the propylene polymer C was 51 mass%, and the intrinsic viscosity [η]C of the propylene polymer C was 1.9 dL / g.

[0145] Example 3: Preparation of heterophasic propylene polymer material [Prepolymerization] 1.7 L of n-hexane, 60 mmol of TEA, and 6.0 mmol of tert-butyl-n-propyldimethoxysilane, which had been thoroughly dehydrated and degassed, were placed in a SUS autoclave with an internal volume of 3 L and equipped with a stirrer. 25 g of the solid catalyst component produced in the Reference Example was added thereto, and while maintaining the temperature inside the autoclave at about 10° C., 25 g of propylene was continuously fed over about 30 minutes to carry out prepolymerization. The prepolymerized slurry was then transferred to a SUS316L autoclave with an internal volume of 260 L and equipped with a stirrer, and 180 L of liquid butane was added to obtain a slurry of the prepolymerized catalyst component.

[0146] [Main polymerization] For this polymerization, an apparatus in which a slurry polymerization reactor, a multistage gas phase polymerization reactor, and two gas phase polymerization reactors were arranged in series was used. Specifically, a propylene homopolymer was produced in the following polymerization step 1-1, polymerization step 1-2, and polymerization step 2, and the produced polymer was transferred to the subsequent step without being deactivated, and an ethylene-propylene copolymer was produced in the following polymerization step 3.

[0147] [Polymerization process 1-1 (propylene homopolymerization using a slurry polymerization reactor)] Propylene homopolymerization was carried out using a SUS304 vessel-type slurry polymerization reactor equipped with an agitator. That is, propylene, hydrogen, TEA, tert-butyl-n-propyldimethoxysilane, and the above-mentioned slurry of prepolymerized catalyst components were continuously fed into the reactor to carry out the polymerization reaction. The reaction conditions were as follows.

[0148] Polymerization temperature: 50℃ Stirring speed: 150rpm Reactor liquid level: 18L Propylene supply: 25kg / hour Hydrogen supply: 175NL / hour Hydrogen / propylene ratio: 13100 mol ppm TEA supply: 34.7mmol / hour Supply amount of tert-butyl-n-propyldimethoxysilane: 7.15mmol / hour Amount of slurry of prepolymerized catalyst component fed (converted into polymerization catalyst component): 0.96 g / hour Polymerization pressure: 4.12MPa (gauge pressure)

[0149] The intrinsic viscosity [η]L1 of the propylene homopolymer sampled from the outlet of the slurry polymerization reactor was 0.64 dl / g.

[0150] [Polymerization process 1-2 (Propylene homopolymerization (gas phase polymerization) using a multi-stage gas phase polymerization reactor)] Propylene homopolymerization was carried out using a multi-stage gas phase polymerization reactor having six reaction zones in the vertical direction, of which the top stage was a fluidized bed and the remaining five stages were spouted beds.

[0151] A slurry containing polypropylene particles and liquid propylene was continuously fed from the preceding slurry polymerization reactor to the fluidized bed, which was the uppermost stage of the multistage gas phase polymerization reactor, without being deactivated.

[0152] The polypropylene particles were transferred between stages in the multi-stage gas phase polymerization reactor using a double valve system. This transfer means connected the upper and lower reaction zones with a 1-inch piping, equipped the piping with two on-off valves, and while closing the lower valve, opened the upper valve to accumulate powder from the upper reaction zone between the valves, and then closed the upper valve and opened the lower valve to transfer the polypropylene particles to the lower reaction zone.

[0153] Propylene and hydrogen were continuously fed from the bottom of the multi-stage gas phase polymerization reactor having the above-mentioned configuration. As a result, a fluidized bed or a spouted bed was formed in each reaction zone, and the feed rates of propylene and hydrogen were controlled to keep the gas composition and pressure constant, and propylene homopolymerization was further carried out while purging excess gas. The reaction conditions were as follows.

[0154] Polymerization temperature: 80℃ Polymerization pressure: 2.00MPa (gauge pressure)

[0155] In the reactor, the hydrogen / propylene ratio in the reactor was set to 255,000 mol ppm.

[0156] The intrinsic viscosity [η]G1 of the propylene homopolymer sampled from the reactor outlet was 0.64 dl / g. [η]L1 and [η]G1 are almost the same value, and the propylene homopolymer obtained up to the polymerization step 1-2 is the propylene polymer A. In Example 3, [η]G1 is the intrinsic viscosity of the propylene polymer A.

[0157] [Polymerization process 2 (Propylene homopolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the upstream multistage gas phase polymerization reactor were continuously fed to the fluidized bed reactor, which was equipped with a gas dispersion plate, and the polypropylene particles were transferred from the upstream multistage gas phase polymerization reactor to the fluidized bed reactor by the double valve system described above.

[0158] Propylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply rate and purging excess gas so as to keep the gas composition and pressure constant, propylene homopolymerization was carried out in the presence of polypropylene particles. The reaction conditions were as follows.

[0159] Polymerization temperature: 80℃ Polymerization pressure: 1.60MPa (gauge pressure)

[0160] In the reactor, the hydrogen / propylene ratio of the reactor outlet gas was set to 1800 mol ppm.

[0161] The intrinsic viscosity [η]G2 of the propylene polymer sampled from the reactor outlet was 0.94 dl / g. The polymer obtained from the reactor outlet in the polymerization step 2 was a mixture of the propylene polymer A and the propylene polymer B. The intrinsic viscosity [η]B of the propylene polymer B was calculated in the same manner as in Example 1.

[0162] [Polymerization step 3 (propylene-ethylene copolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the fluidized bed reactor in polymerization step 2 were continuously supplied to a subsequent fluidized bed reactor. The fluidized bed reactor in polymerization step 3 was equipped with a gas dispersion plate, similar to the fluidized bed reactor in polymerization step 2, and the transfer means for the polypropylene particles from the fluidized bed reactor in polymerization step 2 to the fluidized bed reactor in polymerization step 3 was a double valve system.

[0163] Propylene, ethylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply amount and purging excess gas to keep the gas composition and pressure constant, propylene and ethylene were copolymerized in the presence of polypropylene particles to obtain a heterophasic propylene polymerization material. The reaction conditions were as follows.

[0164] Polymerization temperature: 70℃ Polymerization pressure: 1.39MPa (gauge pressure)

[0165] In the reactor, the concentration ratio of the reactor outlet gas was 40.1 mol % for ethylene / (propylene+ethylene), and 71,000 mol ppm for hydrogen / propylene.

[0166] The proportion (X) of the ethylene-propylene copolymer in the obtained heterophasic propylene polymer material was determined in the same manner as in Example 1.

[0167] The intrinsic viscosity [η]G3 of the propylene polymer sampled from the reactor outlet was 1.31 dl / g. The polymer obtained from the reactor outlet in the polymerization step 3 was a mixture of the propylene polymer A, the propylene polymer B, and the propylene polymer C. The intrinsic viscosity [η]C of the propylene polymer C was calculated in the same manner as in Example 1.

[0168] The intrinsic viscosity ([η]Total) of the obtained heterophasic propylene polymer material was 1.31 dL / g, and the ethylene content was 9.0 mass%. The polymerization ratio of the propylene polymer A, the propylene polymer B, and the propylene polymer C was 72 / 8 / 20, respectively. The ethylene content in the propylene polymer C was 45 mass%, and the intrinsic viscosity [η]C of the propylene polymer C was 2.8 dL / g.

[0169] Example 4: Preparation of heterophasic propylene polymer material [Prepolymerization] 1.7 L of n-hexane, 60 mmol of TEA, and 6.0 mmol of tert-butyl-n-propyldimethoxysilane, which had been thoroughly dehydrated and degassed, were placed in a SUS autoclave with an internal volume of 3 L and equipped with a stirrer. 25 g of the solid catalyst component produced in the Reference Example was added thereto, and while maintaining the temperature inside the autoclave at about 10° C., 25 g of propylene was continuously fed over about 30 minutes to carry out prepolymerization. The prepolymerized slurry was then transferred to a SUS316L autoclave with an internal volume of 260 L and equipped with a stirrer, and 180 L of liquid butane was added to obtain a slurry of the prepolymerized catalyst component.

[0170] [Main polymerization] For this polymerization, an apparatus in which a slurry polymerization reactor, a multistage gas phase polymerization reactor, and two gas phase polymerization reactors were arranged in series was used. Specifically, a propylene homopolymer was produced in the following polymerization step 1-1, polymerization step 1-2, and polymerization step 2, and the produced polymer was transferred to the subsequent step without being deactivated, and an ethylene-propylene copolymer was produced in the following polymerization step 3.

[0171] [Polymerization process 1-1 (propylene homopolymerization using a slurry polymerization reactor)] Propylene homopolymerization was carried out using a SUS304 vessel-type slurry polymerization reactor equipped with an agitator. That is, propylene, hydrogen, TEA, tert-butyl-n-propyldimethoxysilane, and the above-mentioned slurry of prepolymerized catalyst components were continuously fed into the reactor to carry out the polymerization reaction. The reaction conditions were as follows.

[0172] Polymerization temperature: 50℃ Stirring speed: 150rpm Reactor liquid level: 18L Propylene supply: 25kg / hour Hydrogen supply: 176NL / hour Hydrogen / propylene ratio: 13200 mol ppm TEA supply: 37.9mmol / hour Supply amount of tert-butyl-n-propyldimethoxysilane: 7.64mmol / hour Amount of slurry of prepolymerized catalyst component fed (converted into polymerization catalyst component): 1.0 g / hour Polymerization pressure: 4.12MPa (gauge pressure)

[0173] The intrinsic viscosity [η]L1 of the propylene homopolymer sampled from the outlet of the slurry polymerization reactor was 0.64 dl / g.

[0174] [Polymerization process 1-2 (Propylene homopolymerization (gas phase polymerization) using a multi-stage gas phase polymerization reactor)] Propylene homopolymerization was carried out using a multi-stage gas phase polymerization reactor having six reaction zones in the vertical direction, of which the top stage was a fluidized bed and the remaining five stages were spouted beds.

[0175] A slurry containing polypropylene particles and liquid propylene was continuously fed from the preceding slurry polymerization reactor to the fluidized bed, which was the uppermost stage of the multistage gas phase polymerization reactor, without being deactivated.

[0176] The polypropylene particles were transferred between stages in the multi-stage gas phase polymerization reactor using a double valve system. This transfer means connected the upper and lower reaction zones with a 1-inch piping, equipped the piping with two on-off valves, and while closing the lower valve, opened the upper valve to accumulate powder from the upper reaction zone between the valves, and then closed the upper valve and opened the lower valve to transfer the polypropylene particles to the lower reaction zone.

[0177] Propylene and hydrogen were continuously fed from the bottom of the multi-stage gas phase polymerization reactor having the above-mentioned configuration. As a result, a fluidized bed or a spouted bed was formed in each reaction zone, and the feed rates of propylene and hydrogen were controlled to keep the gas composition and pressure constant, and propylene homopolymerization was further carried out while purging excess gas. The reaction conditions were as follows.

[0178] Polymerization temperature: 80℃ Polymerization pressure: 2.00MPa (gauge pressure)

[0179] In the reactor, the hydrogen / propylene ratio in the reactor was set to 253,000 mol ppm.

[0180] The intrinsic viscosity [η]G1 of the propylene homopolymer sampled from the reactor outlet was 0.64 dl / g. [η]L1 and [η]G1 are almost the same value, and the propylene homopolymer obtained up to the polymerization step 1-2 is the propylene polymer A. In Example 4, [η]G1 is the intrinsic viscosity of the propylene polymer A.

[0181] [Polymerization process 2 (Propylene homopolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the upstream multistage gas phase polymerization reactor were continuously fed to the fluidized bed reactor, which was equipped with a gas dispersion plate, and the polypropylene particles were transferred from the upstream multistage gas phase polymerization reactor to the fluidized bed reactor by the double valve system described above.

[0182] Propylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply rate and purging excess gas so as to keep the gas composition and pressure constant, propylene homopolymerization was carried out in the presence of polypropylene particles. The reaction conditions were as follows.

[0183] Polymerization temperature: 80℃ Polymerization pressure: 1.59MPa (gauge pressure)

[0184] In the reactor, the hydrogen / propylene ratio of the reactor outlet gas was set to 1600 mol ppm.

[0185] The intrinsic viscosity [η]G2 of the propylene polymer sampled from the reactor outlet was 1.07 dl / g. The polymer obtained from the reactor outlet in the polymerization step 2 was a mixture of the propylene polymer A and the propylene polymer B. The intrinsic viscosity [η]B of the propylene polymer B was calculated in the same manner as in Example 1.

[0186] [Polymerization step 3 (propylene-ethylene copolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the fluidized bed reactor in polymerization step 2 were continuously supplied to a subsequent fluidized bed reactor. The fluidized bed reactor in polymerization step 3 was equipped with a gas dispersion plate, similar to the fluidized bed reactor in polymerization step 2, and the transfer means for the polypropylene particles from the fluidized bed reactor in polymerization step 2 to the fluidized bed reactor in polymerization step 3 was a double valve system.

[0187] Propylene, ethylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply amount and purging excess gas to keep the gas composition and pressure constant, propylene and ethylene were copolymerized in the presence of polypropylene particles to obtain a heterophasic propylene polymerization material. The reaction conditions were as follows.

[0188] Polymerization temperature: 70℃ Polymerization pressure: 1.49MPa (gauge pressure)

[0189] In the reactor, the concentration ratio of the reactor outlet gas was ethylene / (propylene+ethylene) 39.8 mol % and hydrogen / propylene 70,800 mol ppm.

[0190] The proportion (X) of the ethylene-propylene copolymer in the obtained heterophasic propylene polymer material was determined in the same manner as in Example 1.

[0191] The intrinsic viscosity [η]G3 of the propylene polymer sampled from the reactor outlet was 1.30 dl / g. The polymer obtained from the reactor outlet in the polymerization step 3 was a mixture of the propylene polymer A, the propylene polymer B, and the propylene polymer C. The intrinsic viscosity [η]C of the propylene polymer C was calculated in the same manner as in Example 1.

[0192] The intrinsic viscosity ([η]Total) of the obtained heterophasic propylene polymer material was 1.30 dL / g, and the ethylene content was 9.1 mass%. The polymerization ratio of the propylene polymer A, the propylene polymer B, and the propylene polymer C was 69 / 12 / 19, respectively. The ethylene content in the propylene polymer C was 47 mass%, and the intrinsic viscosity [η]C of the propylene polymer C was 2.3 dL / g.

[0193] Example 5: Preparation of heterophasic propylene polymer material [Prepolymerization] 1.7 L of n-hexane, 60 mmol of TEA, and 6.0 mmol of tert-butyl-n-propyldimethoxysilane, which had been thoroughly dehydrated and degassed, were placed in a SUS autoclave with an internal volume of 3 L and equipped with a stirrer. 25 g of the solid catalyst component produced in the Reference Example was added thereto, and while maintaining the temperature inside the autoclave at about 10° C., 25 g of propylene was continuously fed over about 30 minutes to carry out prepolymerization. The prepolymerized slurry was then transferred to a SUS316L autoclave with an internal volume of 260 L and equipped with a stirrer, and 180 L of liquid butane was added to obtain a slurry of the prepolymerized catalyst component.

[0194] [Main polymerization] For this polymerization, an apparatus in which a slurry polymerization reactor, a multistage gas phase polymerization reactor, and two gas phase polymerization reactors were arranged in series was used. Specifically, a propylene homopolymer was produced in the following polymerization step 1-1, polymerization step 1-2, and polymerization step 2, and the produced polymer was transferred to the subsequent step without being deactivated, and an ethylene-propylene copolymer was produced in the following polymerization step 3.

[0195] [Polymerization process 1-1 (propylene homopolymerization using a slurry polymerization reactor)] Propylene homopolymerization was carried out using a SUS304 vessel-type slurry polymerization reactor equipped with an agitator. That is, propylene, hydrogen, TEA, tert-butyl-n-propyldimethoxysilane, and the above-mentioned slurry of prepolymerized catalyst components were continuously fed into the reactor to carry out the polymerization reaction. The reaction conditions were as follows.

[0196] Polymerization temperature: 50℃ Stirring speed: 150rpm Reactor liquid level: 18L Propylene supply: 25kg / hour Hydrogen supply: 176NL / hour Hydrogen / propylene ratio: 13200 mol ppm TEA supply: 37.9mmol / hour Supply amount of tert-butyl-n-propyldimethoxysilane: 7.55mmol / hour Amount of slurry of prepolymerized catalyst component fed (converted into polymerization catalyst component): 0.96 g / hour Polymerization pressure: 4.12MPa (gauge pressure)

[0197] The intrinsic viscosity [η]L1 of the propylene homopolymer sampled from the outlet of the slurry polymerization reactor was 0.66 dl / g.

[0198] [Polymerization process 1-2 (Propylene homopolymerization (gas phase polymerization) using a multi-stage gas phase polymerization reactor)] Propylene homopolymerization was carried out using a multi-stage gas phase polymerization reactor having six reaction zones in the vertical direction, of which the top stage was a fluidized bed and the remaining five stages were spouted beds.

[0199] A slurry containing polypropylene particles and liquid propylene was continuously fed from the preceding slurry polymerization reactor to the fluidized bed, which was the uppermost stage of the multistage gas phase polymerization reactor, without being deactivated.

[0200] The polypropylene particles were transferred between stages in the multi-stage gas phase polymerization reactor using a double valve system. This transfer means connected the upper and lower reaction zones with a 1-inch piping, equipped the piping with two on-off valves, and while closing the lower valve, opened the upper valve to accumulate powder from the upper reaction zone between the valves, and then closed the upper valve and opened the lower valve to transfer the polypropylene particles to the lower reaction zone.

[0201] Propylene and hydrogen were continuously fed from the bottom of the multi-stage gas phase polymerization reactor having the above-mentioned configuration. As a result, a fluidized bed or a spouted bed was formed in each reaction zone, and the feed rates of propylene and hydrogen were controlled to keep the gas composition and pressure constant, and propylene homopolymerization was further carried out while purging excess gas. The reaction conditions were as follows.

[0202] Polymerization temperature: 80℃ Polymerization pressure: 1.99MPa (gauge pressure)

[0203] In the reactor, the hydrogen / propylene ratio in the reactor was set to 253,000 mol ppm.

[0204] The intrinsic viscosity [η]G1 of the propylene homopolymer sampled from the reactor outlet was 0.66 dl / g. [η]L1 and [η]G1 are almost the same value, and the propylene homopolymer obtained up to the polymerization step 1-2 is the propylene polymer A. In Example 5, [η]G1 is the intrinsic viscosity of the propylene polymer A.

[0205] [Polymerization process 2 (Propylene homopolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the upstream multistage gas phase polymerization reactor were continuously fed to the fluidized bed reactor, which was equipped with a gas dispersion plate, and the polypropylene particles were transferred from the upstream multistage gas phase polymerization reactor to the fluidized bed reactor by the double valve system described above.

[0206] Propylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply rate and purging excess gas so as to keep the gas composition and pressure constant, propylene homopolymerization was carried out in the presence of polypropylene particles. The reaction conditions were as follows.

[0207] Polymerization temperature: 79℃ Polymerization pressure: 1.60MPa (gauge pressure)

[0208] In the reactor, the hydrogen / propylene ratio of the reactor outlet gas was set to 1800 mol ppm.

[0209] The intrinsic viscosity [η]G2 of the propylene polymer sampled from the reactor outlet was 1.09 dl / g. The polymer obtained from the reactor outlet in the polymerization step 2 was a mixture of the propylene polymer A and the propylene polymer B. The intrinsic viscosity [η]B of the propylene polymer B was calculated in the same manner as in Example 1.

[0210] [Polymerization step 3 (propylene-ethylene copolymerization (gas phase polymerization) using a fluidized bed reactor)] The polypropylene particles discharged from the fluidized bed reactor in polymerization step 2 were continuously supplied to a subsequent fluidized bed reactor. The fluidized bed reactor in polymerization step 3 was equipped with a gas dispersion plate, similar to the fluidized bed reactor in polymerization step 2, and the transfer means for the polypropylene particles from the fluidized bed reactor in polymerization step 2 to the fluidized bed reactor in polymerization step 3 was a double valve system.

[0211] Propylene, ethylene and hydrogen were continuously supplied to the fluidized bed reactor having the above-mentioned configuration, and while adjusting the gas supply amount and purging excess gas to keep the gas composition and pressure constant, propylene and ethylene were copolymerized in the presence of polypropylene particles to obtain a heterophasic propylene polymerization material. The reaction conditions were as follows.

[0212] Polymerization temperature: 70℃ Polymerization pressure: 1.49MPa (gauge pressure)

[0213] In the reactor, the concentration ratio of the reactor outlet gas was ethylene / (propylene+ethylene) 34.3 mol % and hydrogen / propylene 67,600 mol ppm.

[0214] The proportion (X) of the ethylene-propylene copolymer in the obtained heterophasic propylene polymer material was determined in the same manner as in Example 1.

[0215] The intrinsic viscosity [η]G3 of the propylene polymer sampled from the reactor outlet was 1.25 dl / g. The polymer obtained from the reactor outlet in the polymerization step 3 was a mixture of the propylene polymer A, the propylene polymer B, and the propylene polymer C. The intrinsic viscosity [η]C of the propylene polymer C was calculated in the same manner as in Example 1.

[0216] The intrinsic viscosity ([η]Total) of the obtained heterophasic propylene polymer material was 1.25 dL / g, and the ethylene content was 6.4 mass%. The polymerization ratio of the propylene polymer A, the propylene polymer B, and the propylene polymer C was 70 / 12 / 18, respectively. The ethylene content in the propylene polymer C was 35 mass%, and the intrinsic viscosity [η]C of the propylene polymer C was 2.0 dL / g.

[0217] Comparative Example 1: Production of heterophasic propylene polymer material [Prepolymerization] Into a jacketed SUS reactor, degassed and dehydrated n-hexane, a solid catalyst component (a) produced by the method described in Example 5 of JP-A-7-216017, cyclohexylethyldimethoxysilane (b), and TEA (c) were fed so that the ratio of the amount of TEA to the amount of solid catalyst component was 1.67 mmol / g and the ratio of the amount of cyclohexylethyldimethoxysilane to the amount of TEA was 0.13 mmol / mmol, to prepare a prepolymerization catalyst component with a degree of prepolymerization of propylene of 3.5. The degree of prepolymerization is defined as the number of grams of prepolymer generated per 1 g of solid catalyst component.

[0218] [Main polymerization] (I) First-stage polymerization process (I-1) Liquid phase polymerization A polymerization reaction was carried out in two SUS loop-type liquid-phase polymerization reactors. First, the internal gas of the loop-type liquid-phase polymerization reactor was fully replaced with propylene. Then, TEA, cyclohexylethyldimethoxysilane (cyclohexylethyldimethoxysilane / TEA ratio=0.15 mol / mol), and the above prepolymerization catalyst component were continuously fed into the first loop-type liquid-phase polymerization reactor at a rate of 3.7 g / hour, and polymerization was started by feeding propylene and hydrogen to a hydrogen / propylene feed ratio of 8500 mol ppm while adjusting the internal temperature to 70° C. and the pressure to 4.5 MPa by feeding propylene and hydrogen.

[0219] A slurry containing polypropylene particles and liquid propylene was continuously fed from the first loop-type liquid phase polymerization reactor to the second loop-type liquid phase polymerization reactor without deactivation. In the second loop-type liquid phase polymerization reactor, the internal temperature was adjusted to 70°C, and the pressure was adjusted to 4.5 MPa by feeding propylene and hydrogen, while feeding propylene and hydrogen so that the hydrogen / propylene ratio was 8500 mol ppm, to continuously carry out polymerization.

[0220] The intrinsic viscosity of the propylene homopolymer sampled from the outlet of the second loop type liquid phase polymerization reactor was 1.06 dL / g.

[0221] Then, the powdery propylene homopolymer produced in the second loop-type liquid-phase polymerization reactor was extracted and transferred to a fluidized-bed gas-phase polymerization reactor, which was composed of a first fluidized-bed gas-phase polymerization reactor, a second fluidized-bed gas-phase polymerization reactor, and a third fluidized-bed gas-phase polymerization reactor arranged in series, the first fluidized-bed gas-phase polymerization reactor being connected to the second loop-type liquid-phase polymerization reactor and the second fluidized-bed gas-phase polymerization reactor, and the second fluidized-bed gas-phase polymerization reactor being connected to the first fluidized-bed gas-phase polymerization reactor and the third fluidized-bed gas-phase polymerization reactor.

[0222] (I-2) Gas Phase Polymerization Propylene homopolymerization was continuously carried out in the first and second fluidized bed gas phase polymerization reactors. In the first fluidized bed gas phase polymerization reactor, propylene was continuously fed so as to maintain the reaction temperature at 80°C and the reaction pressure at 2.1 MPa, and hydrogen was fed so as to maintain the hydrogen concentration in the gas phase at 7.5 mol%, while gas phase polymerization was continuously carried out in the presence of the powdered propylene homopolymer component transferred from the second loop type liquid phase polymerization reactor to produce a polymer component.

[0223] Then, a part of this polymer component was intermittently transferred to a second fluidized bed gas phase polymerization reactor, and gas phase polymerization was continued while continuously supplying propylene and hydrogen so as to maintain the reaction temperature at 80°C, the reaction pressure at 1.7 MPa, and the hydrogen concentration in the gas phase at 7.5 mol%, thereby producing a propylene homopolymer component. The intrinsic viscosity of the obtained propylene homopolymer component (hereinafter also referred to as "polymer component (I)") was 1.06 dL / g.

[0224] The hydrogen / propylene ratio in each of the first and second fluidized bed gas phase polymerization reactors was 80,000 mol ppm.

[0225] (II) Second-stage polymerization process A part of the obtained propylene homopolymer component was transferred to a jacketed fluidized bed gas phase polymerization reactor (third fluidized bed gas phase polymerization reactor), and the production of a propylene-ethylene copolymer component (hereinafter also referred to as "polymer component (II)") by copolymerization of propylene and ethylene was started. Propylene and ethylene were continuously supplied at a ratio of propylene / ethylene = 2 / 1 (mass ratio) so that the reaction temperature was kept at 70°C and the reaction pressure was kept at 1.4 MPa, and the gas phase polymerization was continued while adjusting the mixed gas concentration so that the hydrogen concentration in the gas phase was kept at 2.1 mol%, to produce polymer component (II).

[0226] Next, the powder in the third fluidized bed gas phase polymerization reactor was intermittently introduced into a deactivation tank, and the catalyst components were deactivated with water. The powder was then dried with nitrogen at 65°C to obtain a heterophasic propylene polymerization material.

[0227] The intrinsic viscosity ([η]Total) of the obtained heterophasic propylene polymerization material was 1.4 dL / g, and the ethylene content was 7.0 mass%. The polymerization ratio of polymer component (I) to polymer component (II) was 79 / 21. This ratio was calculated from the mass of the finally obtained propylene-based block copolymer and the amount of polymer component (I). The ethylene content in polymer component (II) was 33 mass%, and the intrinsic viscosity [η] of polymer component (II) was 1.4 dL / g, and the ethylene content was 7.0 mass%. II was 2.7 dL / g.

[0228] The hydrogen / propylene ratio in the third fluidized bed gas phase polymerization reactor was 39,000 mol ppm.

[0229] A summary of the results is shown in Tables 1 and 2.

[0230] [Table 1]

[0231] [Table 2]

[0232] In Tables 1 and 2, "P portion" and "EP portion" respectively refer to "a propylene-based polymer portion containing 80% by mass or more of monomer units derived from propylene" and "a propylene copolymer portion containing monomer units derived from ethylene and propylene."

[0233] It can be seen from Tables 1 and 2 that the injection molded articles according to the examples have a low MDTD average linear expansion coefficient and excellent dimensional stability. That is, it was confirmed that the heterophasic propylene polymerization material according to the present embodiment can produce molded articles with excellent dimensional stability.

Claims

1. A method for producing a heterophasic propylene polymerization material, comprising steps 1, 2 and 3, The heterophasic propylene polymer material is A heterophasic propylene polymer material comprising a propylene-based polymer A, a propylene-based polymer B, and a propylene copolymer C, The propylene polymer A contains 80% by mass or more of monomer units derived from propylene and has an intrinsic viscosity of 2.0 dL / g or less, the propylene polymer B contains 80% by mass or more of monomer units derived from propylene and has an intrinsic viscosity of 2.1 to 4.9 dL / g; Propylene copolymer C contains 30 to 55 mass % of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms, and monomer units derived from propylene, and has an intrinsic viscosity of 1.5 to 4.5 dL / g; the heterophasic propylene polymerization material has contents of the propylene polymer A, the propylene polymer B and the propylene copolymer C of 50 to 75 mass%, 5 to 20 mass% and 5 to 40 mass%, respectively, relative to 100 mass% of the total mass of the heterophasic propylene polymerization material; A method for producing a heterophasic propylene polymeric material. Step 1: Step 1-1 of polymerizing a monomer containing propylene in a liquid phase under the condition that the hydrogen / propylene ratio is 1000 mol ppm or more to obtain at least a part of a propylene-based polymer A; and A step 1-2 of polymerizing a monomer containing propylene in a gas phase under the condition that the hydrogen / propylene ratio is 50,000 mol ppm or more to obtain at least a part of a propylene-based polymer A. At least one step selected from the group consisting of Step 2: Step 2-1 of polymerizing a monomer containing propylene in a liquid phase under conditions where the hydrogen / propylene ratio is 40 mol ppm or more and less than 1000 mol ppm to obtain at least a part of a propylene-based polymer B; and A step 2-2 of polymerizing a monomer containing propylene in a gas phase under the condition that the hydrogen / propylene ratio is 40 mol ppm or more and less than 50,000 mol ppm to obtain at least a part of a propylene-based polymer B. At least one step selected from the group consisting of Step 3: A step of polymerizing a monomer containing propylene and at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms under the condition that the hydrogen / propylene ratio is 9,000 mol ppm or more and 310,000 mol ppm or less to obtain a propylene copolymer C.

2. The heterophasic propylene polymer material comprises: The propylene polymer A has an intrinsic viscosity of 0.3 to 1.2 dL / g; The propylene polymer B has an intrinsic viscosity of 2.5 to 4.0 dL / g; The intrinsic viscosity of the propylene copolymer C is 2.0 to 4.0 dL / g; In the propylene copolymer C, the content of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms is 35 to 50 mass %, The method for producing a heterophasic propylene polymerization material according to claim 1, wherein the contents of the propylene polymer A, the propylene polymer B and the propylene copolymer C are 60 to 75 mass%, 7 to 18 mass%, and 7 to 33 mass%, respectively, based on the total mass of the heterophasic propylene polymerization material being 100 mass%.

3. The heterophasic propylene polymer material comprises: The method for producing a heterophasic propylene polymerization material according to claim 1 or 2, wherein the content of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms in the propylene copolymer C is 36 to 48 mass%.

4. The heterophasic propylene polymer material comprises: The method for producing a heterophasic propylene polymerization material according to claim 3, wherein the content of monomer units derived from at least one α-olefin selected from the group consisting of ethylene and α-olefins having 4 to 12 carbon atoms in the propylene copolymer C is 38 to 45 mass%.

5. The hydrogen / propylene ratio in step 1-1 is 1500 molppm or more and 100,000 molppm or less, The hydrogen / propylene ratio in step 1-2 is 65,000 molppm or more and 1,500,000 molppm or less; The hydrogen / propylene ratio in step 2-1 is 50 mol ppm or more and 900 mol ppm or less, The hydrogen / propylene ratio in step 2-2 is 100 molppm or more and 35,000 molppm or less, The method for producing a heterophasic propylene polymerization material according to any one of claims 1 to 4, wherein the hydrogen / propylene ratio in step 3 is 12,000 mol ppm or more and 250,000 mol ppm or less.

6. The hydrogen / propylene ratio in step 1-1 is 3000 molppm or more and 50000 molppm or less, The hydrogen / propylene ratio in step 1-2 is 80,000 molppm or more and 1,000,000 molppm or less, The hydrogen / propylene ratio in step 2-1 is 75 mol ppm or more and 750 mol ppm or less, The hydrogen / propylene ratio in step 2-2 is 300 molppm or more and 20,000 molppm or less, The method for producing a heterophasic propylene polymerization material according to any one of claims 1 to 5, wherein the hydrogen / propylene ratio in step 3 is 15,000 mol ppm or more and 200,000 mol ppm or less.