Polymerizable composition, cured product, and method for producing the cured product

Abstract

To provide a polymerizable composition that can be cured sufficiently at low temperature in a short time to form a cured product excellent in surface smoothness.SOLUTION: The polymerizable composition contains a triazine peroxide derivative represented by the general formula (1) in the figure, a cobalt-based curing accelerator, and a radical-polymerizable compound.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a polymerizable composition, a cured product, and a method for producing the cured product. [Background technology]

[0002] Photosensitive compositions that can be rapidly cured by irradiation with light are used in coating agents, inks, adhesives, and various photoresists.

[0003] In general, photosensitive compositions contain additives such as colorants depending on the application, in addition to photopolymerization initiators and radically polymerizable compounds. Additives such as colorants absorb the irradiated light and attenuate it, or block the irradiated light, preventing the light from reaching the depths of the applied coating film, resulting in a problem of insufficient curing.

[0004] In order to solve the above problems, Patent Document 1 describes a composition containing a triazine peroxide derivative that has a peroxide bond (-OO-) in the molecule and generates radicals by light or heat, and discloses that the curing property of a dual-curing type polymerizable composition that has both photocurable and thermosetting properties can be improved by heating after light irradiation.

[0005] On the other hand, for liquid crystal display elements, a change from the conventional glass substrate to a resin substrate is being considered in order to reduce weight and flexibility. Resin substrates have inferior heat resistance compared to glass substrates, and therefore have problems such as being unable to undergo high-temperature treatment required for manufacturing liquid crystal display elements as with conventional materials. Patent Document 2 describes that a composition containing a specific thermal polymerization crosslinking agent and a specific benzophenone-based compound is suitable for use with resin substrates. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] International Publication No. 2018 / 221177 [Patent Document 2] JP 2003-113224 A Summary of the Invention [Problem to be solved by the invention]

[0007] However, Patent Document 2 requires a specific thermal polymerization crosslinking agent, which limits the composition of the polymerizable composition and requires high-temperature treatment at 150° C. or higher. Thus, a polymerizable composition that can be cured at a lower temperature is desired.

[0008] Furthermore, Patent Document 1 suggests that a polymerizable composition containing a triazine peroxide derivative and a curing accelerator can be cured at a low temperature when it is thermally cured. However, it has been found that thermal curing takes longer than photocuring, and therefore uneven shrinkage occurs during curing, resulting in a loss of smoothness on the coating surface.

[0009] The present invention has been made in consideration of the above-mentioned circumstances, and an object of the present invention is to provide a polymerizable composition that can be sufficiently cured at a low temperature in a short time to give a cured product having excellent surface smoothness. [Means for solving the problem]

[0010] That is, the present invention relates to a compound represented by the general formula (1): [ka] (In formula (1), R 1 and R 2 R independently represents a methyl group or an ethyl group. 3 X represents an aliphatic hydrocarbon group having 1 to 5 carbon atoms, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. 1 , Ar 2 , Ar 3 or Ar 4 where n is an integer of 0 to 2. [ka] (In formula (2), m represents an integer of 0 to 3. 4 are independent substituents, and each is an alkyl group having 1 to 6 carbon atoms; 5 The R represents a substituent represented by -Y-, a nitro group, or a cyano group. The Y represents an oxygen atom or a sulfur atom. 5 represents a hydrocarbon group having 1 to 6 carbon atoms which may have at least one of an ether bond, a thioether bond, and a hydroxyl group at a terminal in the carbon skeleton, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. 4 R is two adjacent 5 The present invention relates to a polymerizable composition comprising a triazine peroxide derivative represented by the formula (I): wherein -Y- may form a 5- or 6-membered ring, a cobalt-based curing accelerator, and a radically polymerizable compound.

[0011] The present invention also relates to a cured product formed from the polymerizable composition.

[0012] The present invention also relates to a method for producing a cured product, which comprises a step of heating the polymerizable composition. Effect of the Invention

[0013] The polymerizable composition of the present invention contains the triazine peroxide derivative, a cobalt-based curing accelerator, and a radical polymerizable compound. Generally, as the curing accelerator, for example, amine compounds, thiourea compounds, and compounds of fourth period transition metals such as vanadium, cobalt, and copper are known, but in the present invention, by using a cobalt-based curing accelerator, it is possible to sufficiently cure at low temperature and in a short time, and a cured product having excellent surface smoothness can be obtained. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] The polymerizable composition of the present invention contains a triazine peroxide derivative represented by the following general formula (1), a cobalt-based curing accelerator, and a radically polymerizable compound.

[0015] <Triazine peroxide derivatives> The triazine peroxide derivative of the present invention can be represented by the following general formula (1): The triazine peroxide derivatives may be used alone or in combination of two or more kinds. [ka] (In formula (1), R 1 and R 2 R independently represents a methyl group or an ethyl group. 3 X represents an aliphatic hydrocarbon group having 1 to 5 carbon atoms, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. 1 , Ar 2 , Ar 3 or Ar 4 where n is an integer of 0 to 2. [ka] (In formula (2), m represents an integer of 0 to 3. 4 are independent substituents, and each is an alkyl group having 1 to 6 carbon atoms; 5 The R represents a substituent represented by -Y-, a nitro group, or a cyano group. The Y represents an oxygen atom or a sulfur atom. 5 represents a hydrocarbon group having 1 to 6 carbon atoms which may have at least one of an ether bond, a thioether bond, and a hydroxyl group at a terminal in the carbon skeleton, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. 4 R is two adjacent 5 -Y- may form a 5- or 6-membered ring.

[0016] In the general formula (1), R 1 and R 2 R independently represents a methyl group or an ethyl group. From the viewpoint that the storage stability of the polymerizable composition is improved as the cleavage temperature of the peroxide bond contained in the triazine peroxide derivative is higher, 1 and R 2 is preferably a methyl group.

[0017] In the general formula (1), R 3 R is an aliphatic hydrocarbon group having 1 to 5 carbon atoms, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. The alkyl group may be either a straight chain or a branched chain. 3 Specific examples of the group include a methyl group, an ethyl group, a propyl group, a 2,2-dimethylpropyl group, a phenyl group, and an isopropylphenyl group. Among these, from the viewpoint of ease of synthesis of the triazine peroxide derivative, a methyl group, an ethyl group, a propyl group, a 2,2-dimethylpropyl group, and a phenyl group are preferred. From the viewpoints of high decomposition temperature of the triazine peroxide derivative, high storage stability of the polymerizable composition, and high sensitivity to irradiated light, a methyl group and an ethyl group are more preferred.

[0018] In the general formula (1), n ​​is an integer of 0 to 2. From the viewpoint of easiness in synthesis of the triazine peroxide derivative, n is preferably 0 or 1. When n is 0, X is Ar 2 , Ar 3 , or Ar 4 When n is 1, X is Ar 1 It is more preferable from the viewpoint of efficiently absorbing the irradiated light and reducing the yellowness of the cured product.

[0019] In the general formula (2), m is an integer of 0 to 3. From the viewpoint of easiness in synthesis of the triazine peroxide derivative, m is preferably 0 to 2, and from the viewpoint of efficient absorption of irradiated light, m ​​is more preferably 1.

[0020] In the general formula (2), R 4 are independent substituents, and each is an alkyl group having 1 to 6 carbon atoms; 5 The R represents a substituent represented by -Y-, a nitro group, or a cyano group. Y represents an oxygen atom or a sulfur atom. 5represents a hydrocarbon group having 1 to 6 carbon atoms which may have at least one of an ether bond, a thioether bond, and a hydroxyl group at a terminal in the carbon skeleton, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. 4 R is two adjacent 5 -Y- may form a 5- or 6-membered ring.

[0021] R 4 is an independent substituent from the viewpoint of efficiently absorbing irradiated light, and is an alkyl group having 1 to 6 carbon atoms, or a group represented by the general formula (3): R 5 represents a substituent represented by -Y-, Y represents an oxygen atom, R 5 is preferably a hydrocarbon group having 1 to 6 carbon atoms which may have at least one of an ether bond and a hydroxyl group at a terminal in the carbon skeleton, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. 4 R is two adjacent 5 It is preferable that --X-- forms a 5- or 6-membered ring.

[0022] R 4Specific examples of the aryloxy group include alkyl groups such as a methyl group, an ethyl group, an n-propyl group, an isopropyl group, and an n-hexyl group; a methoxy group, an ethoxy group, an n-propyloxy group, an isopropyloxy group, an n-butyloxy group, a sec-butyloxy group, a tert-butyloxy group, an n-pentyloxy group, a cyclopentyloxy group, an n-hexyloxy group, a cyclohexyloxy group, a 2-hydroxyethoxy group, a 2-methoxyethoxy group, a 2-ethoxyethoxy group, a 2-butoxyethoxy group, a 2-(2-hydroxyethoxy)ethoxy group, a 2-(2-ethoxyethoxy)ethoxy group, a 2-(2-ethoxyethoxy)ethoxy group, a 2-(2-ethoxyethoxy)ethoxy group, a 2-(2-hydroxy ... Examples of such functional groups include alkoxy groups such as 2-methoxy group, 1,2-dihydroxypropoxy group, methylenedioxy group, dimethylmethylenedioxy group, and ethylenedioxy group; aryloxy groups such as phenyloxy group and 4-isopropylphenyloxy group; alkylsulfanyl groups such as methylsulfanyl group, ethylsulfanyl group, hexylsulfanyl group, 2-methoxyethylsulfanyl group, and 2-(2-methoxyethoxy)ethylsulfanyl group; and arylsulfanyl groups such as phenylsulfanyl group, 2-methylphenylsulfanyl group, and 4-methylphenylsulfanyl group. Compounds represented by the general formula (1) having such functional groups are preferred because they have high absorbance at 365 nm and efficiently absorb irradiated light.

[0023] Among these, the triazine derivatives R 1 is more preferably a methoxy group, an ethoxy group, or a 2-hydroxyethoxy group.

[0024] R 4 The substitution position of X is not particularly limited, but 1 In the case of R 4 At least one of the following is preferably substituted at the 4-position of the benzene ring substituted with the triazine group. 2 In the case of R 4 It is preferable that at least one of the following is substituted at the 4-position of a benzene ring other than the benzene ring substituted with the triazine group. 3 In the case of R4 is preferably substituted at the 4-position of the triazine group substituted at the 1-position. 4 In the case of R 4 In order to efficiently absorb irradiated light, it is preferable that at least one of the above is substituted at the 4-position of a benzene ring other than the benzene ring substituted with the triazine group.

[0025] Specific examples of the triazine peroxide derivative of the present invention are shown below, but the invention is not limited to these. [ka] TIFF0007625840000006.tif240152TIFF0007625840000007.tif230150TIFF0007625840000008.tif130160

[0026] The triazine peroxide derivative of the present invention preferably includes Compound 19, Compound 23, Compound 25, Compound 26, Compound 27, Compound 28, Compound 31, Compound 32, Compound 33, Compound 35, Compound 37, Compound 38, Compound 39, Compound 40, Compound 41, Compound 42, Compound 43, Compound 44, Compound 46, Compound 47, and Compound 48, and more preferably includes Compound 25, Compound 26, Compound 31, Compound 32, Compound 35, Compound 37, Compound 38, Compound 41, Compound 44, Compound 47, and Compound 48.

[0027] <Cobalt-based curing accelerator> Examples of the cobalt-based hardening accelerator include fatty acid cobalt salts such as cobalt octylate, cobalt naphthenate, and cobalt rhodanate, and cobalt octylate and / or cobalt naphthenate are preferred, and cobalt octylate is more preferred. The cobalt-based hardening accelerators may be used alone or in combination of two or more kinds.

[0028] <Radical polymerizable compound> As the radical polymerizable compound, a compound having an ethylenically unsaturated group can be preferably used. As the radical polymerizable compound, for example, (meth)acrylic acid esters, styrenes, maleic acid esters, fumaric acid esters, itaconic acid esters, cinnamic acid esters, crotonic acid esters, vinyl ethers, vinyl esters, vinyl ketones, allyl ethers, allyl esters, N-substituted maleimides, N-vinyl compounds, unsaturated nitriles, olefins, etc. are listed. Among these, it is preferable to include (meth)acrylic acid esters having high reactivity. The radical polymerizable compound may be used alone or in combination of two or more kinds.

[0029] The (meth)acrylic acid esters may be monofunctional or polyfunctional compounds. Examples of the monofunctional compounds include alkyl (meth)acrylates such as methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, tert-butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, and stearyl (meth)acrylate; cyclohexyl (meth)acrylate, isobornyl (meth)acrylate, dicyclopentanyl (meth)acrylate, dicyclopentenyl (meth)acrylate, and dicyclopentenyloxyethyl (meth)acrylate. (meth)acrylate, 2-ethyl-2-adamantyl (meth)acrylate and other ester compounds of (meth)acrylic acid and aliphatic alcohol; aryl (meth)acrylates such as phenyl (meth)acrylate and benzyl (meth)acrylate; 2-hydroxyethyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, 2-hydroxy-3-phenoxypropyl (meth)acrylate, 3-hydroxy-1-adamantyl (meth)acrylate, polyethylene glycol mono (meth)acrylate, poly Monomers having a hydroxy group, such as propylene glycol mono(meth)acrylate; methoxyethyl(meth)acrylate, methoxypolyethylene glycol(meth)acrylate, phenoxypolyethylene glycol(meth)acrylate, 2-phenylphenoxyethyl(meth)acrylate, tetrahydrofurfuryl(meth)acrylate, (2-methyl-2-ethyl-1,3-dioxolan-4-yl)methyl(meth)acrylate, (3-ethyloxetan-3-yl)methyl(meth)acrylate, cyclic trimethylol Monomers having a linear or cyclic ether bond, such as methylolpropaneformal (meth)acrylate; monomers having a nitrogen atom, such as N,N-dimethylaminoethyl (meth)acrylate, N,N-dimethyl(meth)acrylamide, N-methylol(meth)acrylamide, N-isopropyl(meth)acrylamide, N,N-dimethylaminopropyl(meth)acrylamide, diacetone(meth)acrylamide, (meth)acryloylmorpholine, and N-(meth)acryloyloxyethylhexahydrophthalimide;Monomers having an isocyanate group such as 2-(meth)acryloyloxyethyl isocyanate; monomers having an epoxy group such as glycidyl (meth)acrylate and 4-hydroxybutyl (meth)acrylate glycidyl ether; monomers having a phosphorus atom such as 2-((meth)acryloyloxy)ethyl phosphate; monomers having a silicon atom such as 3-(meth)acryloxypropyltrimethoxysilane; monomers having a fluorine atom such as 2,2,2-trifluoroethyl (meth)acrylate, 2,2,3,3,3-pentafluoropropyl (meth)acrylate, and 2-(perfluorohexyl)ethyl (meth)acrylate; monomers having a carboxyl group such as (meth)acrylic acid, succinic acid mono(2-(meth)acryloyloxyethyl), phthalic acid mono(2-(meth)acryloyloxyethyl), maleic acid mono(2-(meth)acryloyloxyethyl), and ω-carboxy-polycaprolactone mono(meth)acrylate;

[0030] Examples of the polyfunctional compound include ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, polypropylene glycol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,9-nonanediol di(meth)acrylate, glycerin di(meth)acrylate, glycerin tri(meth)acrylate, glycerin propoxy tri(meth)acrylate, trimethylolethane tri(meth)acrylate, trimethylolpropane tri(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, pentaerythritol di(meth)acrylate monostearate, dipentaerythritol penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, and neopentane hydroxypivalate. Polyhydric alcohols such as butyl glycol di(meth)acrylate, tricyclodecane dimethanol di(meth)acrylate, 2,2-bis(4-(meth)acryloxyethoxyphenyl)propane, 2,2-bis(4-(meth)acryloxypolyethoxyphenyl)propane, 9,9-bis(4-(2-(meth)acryloyloxyethoxy)phenyl)fluorene, and 9,9-bis(4-(2-(2-(meth)acryloyloxyethoxy)ethoxy)phenyl)fluorene. ester compounds of aryl and (meth)acrylic acid; bis(4-(meth)acryloxyphenyl)sulfide, bis(4-(meth)acryloylthiophenyl)sulfide, tris(2-(meth)acryloyloxyethyl)isocyanurate, ethylene bis(meth)acrylamide, zinc (meth)acrylate, zirconium (meth)acrylate, aliphatic urethane acrylate, aromatic urethane acrylate, epoxy acrylate, polyester acrylate, and the like.

[0031] The polymerizable composition may contain a copolymer obtained from the radically polymerizable compound.

[0032] The content of the triazine peroxide derivative is preferably 0.1 to 40 parts by mass, more preferably 0.5 to 20 parts by mass, and even more preferably 1 to 15 parts by mass, relative to 100 parts by mass of the radical polymerizable compound. If the content of the triazine peroxide derivative is less than 0.1 parts by mass relative to 100 parts by mass of the radical polymerizable compound, the curing reaction does not proceed, which is not preferable. If the content of the triazine peroxide derivative is more than 40 parts by mass relative to 100 parts by mass of the radical polymerizable compound, the solubility in the radical polymerizable compound reaches saturation, and crystals of the triazine peroxide derivative are precipitated during film formation of the polymerizable composition, which may cause problems such as roughness of the film surface, or the strength of the coating film of the cured product may decrease due to an increase in decomposition residue of the triazine peroxide derivative.

[0033] The content of the cobalt-based curing accelerator is preferably 0.01 to 20 parts by mass, more preferably 0.1 to 10 parts by mass, and even more preferably 0.1 to 5 parts by mass, relative to 100 parts by mass of the radical polymerizable compound. If the content of the cobalt-based curing accelerator is less than 0.01 parts by mass relative to 100 parts by mass of the radical polymerizable compound, the curing acceleration effect is not exhibited, which is not preferable. If the content of the cobalt-based curing accelerator is more than 20 parts by mass relative to 100 parts by mass of the radical polymerizable compound, the strength of the coating film of the cured product may decrease, which is not preferable.

[0034] <Solvent> The polymerizable composition may further contain a solvent in order to improve the viscosity, coatability, and smoothness of the cured film. The solvent that can be used in the present invention is not particularly limited as long as it can dissolve or disperse the triazine peroxide derivative, the cobalt-based curing accelerator, and the radical polymerizable compound, and is volatilized at the drying temperature.

[0035] Examples of the solvent include aprotic solvents such as hydrocarbon solvents and unsaturated hydrocarbon solvents, water, alcohol solvents, carbitol solvents, ester solvents, ketone solvents, ether solvents, lactone solvents, cellosolve acetate solvents, carbitol acetate solvents, propylene glycol monomethyl ether acetate, diethylene glycol dimethyl ether, etc. The solvents may be used alone or in combination of two or more.

[0036] The amount of the solvent used is preferably 1 to 1000 parts by mass, more preferably 2 to 500 parts by mass, per 100 parts by mass of the solid content of the polymerizable composition. If the amount of the solvent used is less than 1 part by mass per 100 parts by mass of the solid content of the polymerizable composition, the coating property deteriorates, which is not preferable. If the amount of the solvent used is more than 1000 parts by mass per 100 parts by mass of the solid content of the polymerizable composition, the thermosetting property deteriorates, which is not preferable.

[0037] <Polymerizable composition> The polymerizable composition of the present invention contains the triazine peroxide derivative, the cobalt-based curing accelerator, and the radical polymerizable compound. The polymerizable composition may contain other components in appropriate combination.

[0038] <Other ingredients> As the other components, the polymerizable composition may contain additives that are generally used in applications such as coating agents, paints, printing inks, photosensitive printing plates, adhesives, and various photoresists such as color resists and black resists. Examples of additives include sensitizers (isopropylthioxanthone, diethylthioxanthone, 4,4'-bis(diethylamino)benzophenone, 9,10-dibutoxyanthracene, coumarin, ketocoumarin, acridine orange, camphorquinone, etc.), polymerization inhibitors (p-methoxyphenol, hydroquinone, 2,6-di-t-butyl-4-methylphenol, phenothiazine, etc.), ultraviolet absorbers, infrared absorbers, light stabilizers, antioxidants, leveling agents, surface conditioners, surfactants, thickeners, defoamers, adhesion promoters, plasticizers, epoxy compounds, thiol, etc. Examples of the additives include all-compounds, resins having ethylenically unsaturated bonds, saturated resins, coloring dyes, fluorescent dyes, pigments (organic pigments, inorganic pigments), carbon-based materials (carbon fibers, carbon black, graphite, graphitized carbon black, activated carbon, carbon nanotubes, fullerenes, graphene, carbon microcoils, carbon nanohorns, carbon aerogels, etc.), metal oxides (titanium oxide, iridium oxide, zinc oxide, alumina, silica, etc.), metals (silver, copper, etc.), inorganic compounds (glass powder, layered clay minerals, mica, talc, calcium carbonate, etc.), dispersants, flame retardants, etc. The additives may be used alone or in combination of two or more.

[0039] The content of the additives is appropriately selected depending on the purpose of use and is not particularly limited, but is usually preferably 500 parts by mass or less, and more preferably 100 parts by mass or less, per 100 parts by mass of the radical polymerizable compound.

[0040] <Method for preparing polymerizable composition> When preparing the polymerizable composition, the triazine peroxide derivative, the cobalt-based curing accelerator, the radically polymerizable compound, and, if necessary, the solvent and other components may be charged into a container, and dissolved or dispersed according to a conventional method using a paint shaker, a bead mill, a sand grind mill, a ball mill, an attritor mill, a two-roll mill, a three-roll mill, etc. Also, if necessary, the mixture may be filtered through a mesh or membrane filter, etc.

[0041] In the preparation of the polymerizable composition, the triazine peroxide derivative and the cobalt-based curing accelerator may be added to the polymerizable composition from the beginning. However, when the polymerizable composition is to be stored for a relatively long period of time, it is preferable that the triazine peroxide derivative and the cobalt-based curing accelerator are dissolved or dispersed in a composition containing a radical polymerizable compound immediately before use.

[0042] <Method of manufacturing the cured product> The cured product of the present invention is formed from the polymerizable composition. The method for producing the cured product includes a step of applying the polymerizable composition onto a substrate and then heating the polymerizable composition. The method may also include a step of irradiating the composition with active energy rays before the heating step. In particular, a cured film having excellent surface smoothness can be obtained by quickly curing the surface by light irradiation and then further curing by heating.

[0043] Examples of the coating method include various methods such as spin coating, bar coating, spray coating, dip coating, flow coating, slit coating, doctor blade coating, gravure coating, screen printing, offset printing, inkjet printing, dispenser printing, etc. Examples of the substrate include films and sheets of glass, silicon wafers, metals, plastics, etc., and molded products having a three-dimensional shape, and the shape of the substrate is not limited.

[0044] In the step of heating the polymerizable composition, examples of the heating method include heating, ventilation heating, etc. The heating method is not particularly limited, and examples thereof include an oven, a hot plate, infrared irradiation, electromagnetic wave irradiation, etc. Furthermore, examples of the ventilation heating method include a ventilation drying oven, etc.

[0045] The active energy rays are preferably light having a wavelength of 250 to 450 nm. As a light source for the light irradiation, a low pressure mercury lamp, a high pressure mercury lamp, an ultra-high pressure mercury lamp, a metal halide lamp, an ultraviolet electrodeless lamp, a light emitting diode (LED), a xenon arc lamp, a carbon arc lamp, sunlight, a solid laser such as a YAG laser, a semiconductor laser, a gas laser such as an argon laser, etc. can be used. The exposure dose of the active energy rays should be appropriately set according to the wavelength, intensity, etc. of the active energy rays.

[0046] In the step of heating the polymerizable composition, the heating temperature is preferably 80 to 140° C., more preferably 100 to 130° C. At this temperature, the composition can be cured without deteriorating the resin substrate, etc. The heating time is preferably 1 to 180 minutes, more preferably 5 to 120 minutes.

[0047] The dry film thickness of the polymerizable composition (film thickness of the cured product) is appropriately set depending on the application, but is preferably 0.05 μm to 500 mm, and more preferably 0.1 μm to 10 mm.

[0048] The polymerizable composition of the present invention is useful for a wide variety of applications, including color resists, black resists, protective films for color filters, photospacers, black column spacers, frame resists, photoresists for TFT wiring, interlayer insulating films, and other resists for FPDs; liquid solder resists, dry film resists, and other resists for printed circuit boards; semiconductor resists, buffer coat films, and other semiconductor materials; offset printing inks, gravure printing inks, screen printing inks, inkjet printing inks, conductive inks, insulating inks, light guide plate inks, and other printing inks; photosensitive printing plates; nanoimprint materials; resins for 3D printers; hard coat agents, photodisplays, and other optical devices. They can be used for a variety of applications, including coatings for disks, coatings for optical fibers, paints for mobile devices, paints for home appliances, paints for cosmetic containers, paints for woodworking, internal anti-reflection paints for optical elements, high / low refractive index coatings, heat-shielding coatings, heat-dissipating coatings, and anti-fogging agents; holographic recording materials; dental materials; waveguide materials; black stripes for lens sheets; green sheets and electrode materials for capacitors; adhesives for FPDs, adhesives for HDDs, adhesives for optical pickups, adhesives for image sensors, sealants for organic EL, OCA for touch panels, OCR for touch panels, and other adhesives and sealants, with no particular limitations on their applications. EXAMPLES

[0049] The present invention will be described in more detail below by way of examples, but the present invention is not limited to these examples.

[0050] (1) Preparation of polymerizable composition The radical polymerizable compound, triazine peroxide derivative, thermal polymerization initiator, curing accelerator, and solvent in the amounts shown in Table 1 were mixed and stirred to prepare the polymerizable compositions of Examples 1 to 5 and Comparative Examples 1 to 4.

[0051] (2) Evaluation of hardening properties The polymerizable composition prepared above was applied to a glass substrate to a thickness of 100 μm using a bar coater. After application, the composition was dried in an oven at 90° C. for 2.5 minutes, and then irradiated with 30 mJ / cm 2 using a conveyor-type UV irradiation device equipped with a high-pressure mercury lamp. 2The film was then heated in an oven at 100°C for 30 minutes to obtain a cured film. The polymerization conversion rate of the obtained cured film was measured, and the curability was evaluated according to the following criteria. The polymerization conversion rate was measured by attenuated total reflection infrared spectroscopy (ATR-IR), and in this measurement, the absorption spectrum (810 cm) derived from the double bond group was -1 ) and the absorption spectrum (1740 cm -1 The polymerization conversion rate was calculated based on the following formula using the peak area B of the peak obtained by the above calculation. The results are shown in Table 1. Polymerization conversion rate = (1-(A / B after curing) / (A / B before curing)) x 100 ◎: Polymerization conversion rate is 80% or more ○: Polymerization conversion rate is 60% or more but less than 80% ×: Polymerization conversion rate is less than 60%

[0052] (3) Evaluation of surface smoothness The presence or absence of wrinkles on the surface of the cured film obtained above was observed under an optical microscope in a field of view of 70 μm × 70 μm and evaluated according to the following criteria. The results are shown in Table 1. ○: No micrometer-order wrinkles are observed on the surface ×: Micrometer-order wrinkles are noticeable on the surface

[0053] [Table 1]

[0054] In Table 1 above, TMPTA is trimethylolpropane triacrylate (manufactured by Shin-Nakamura Chemical Co., Ltd.); PE4A, pentaerythritol tetraacrylate (Fujifilm Wako Pure Chemical Reagents); Perbutyl O is t-butylperoxy-2-ethylhexanoate (NOF Corp.); PGMEA, propylene glycol monomethyl ether acetate (Sigma-Aldrich Japan Reagent); Mineral spirits refers to a mixture of petroleum-based hydrocarbon solvents.

[0055] From the results in Table 1, it is clear that the polymerizable composition containing a triazine peroxide derivative, a cobalt-based curing accelerator, and a radical polymerizable compound has excellent surface smoothness and can be cured sufficiently even at low temperatures.

Claims

1. General formula (1): 【Chemistry 1】 (In formula (1), R １ and R ２ R independently represents a methyl group or an ethyl group. ３ X represents an aliphatic hydrocarbon group having 1 to 5 carbon atoms, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. １ , Ar ２ , Ar ３ Or Ar ４ where n is an integer of 0 to 2. 【Chemistry 2】 (In formula (2), m represents an integer of 0 to 3. ４ are independent substituents, an alkyl group having 1 to 6 carbon atoms, a general formula (3): R ５ The R represents a substituent represented by -Y-, a nitro group, or a cyano group. The Y represents an oxygen atom or a sulfur atom. ５ represents a hydrocarbon group having 1 to 6 carbon atoms which may have one or more of an ether bond, a thioether bond, and a hydroxyl group at a terminal in the carbon skeleton, or an aromatic hydrocarbon group having 6 to 9 carbon atoms which may have an alkyl group. ４ is two adjacent groups of the general formula (3): R ５ (wherein —Y— may form a 5- or 6-membered ring), a cobalt-based curing accelerator, and a radically polymerizable compound.

2. 2. The polymerizable composition according to claim 1, wherein the cobalt-based curing accelerator is cobalt octoate and / or cobalt naphthenate.

3. A cured product formed from the polymerizable composition according to claim 1 or 2.

4. A method for producing a cured product, comprising a step of heating the polymerizable composition according to claim 1 or 2.

5. The method for producing a cured product according to claim 4, characterized in that the heating step is performed at a heating temperature of 80 to 140°C.