Magnetic recording medium and magnetic storage device

Abstract

To provide a magnetic recording medium capable of having excellent electromagnetic conversion characteristics.SOLUTION: A magnetic recording medium according to the present invention includes a substrate, a ground layer, and a magnetic layer containing an alloy having an L10 type crystal structure laminated in this order. The ground layer contains MgO, the magnetic layer has at least three or more layers, when the three magnetic layers are a first magnetic recording layer, a second magnetic recording layer, and a third magnetic recording layer in order from the substrate side, Curie temperature Tc of the second magnetic recording layer is -30K to -100K lower than the Curie temperature Tc of the first magnetic recording layer and the third magnetic recording layer, respectively, and the average grain size of a bottom portion of magnetic grains forming the first magnetic recording layer is more than 15% smaller than the average grain size of the bottom portion of the magnetic grains forming the second magnetic recording layer and the third magnetic recording layer.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a magnetic recording medium and a magnetic storage device. [Background technology]

[0002] A magnetic recording medium generally comprises an underlayer, a magnetic layer, and a protective layer laminated in that order on a substrate. Methods for recording magnetic information on a magnetic recording medium include a thermally assisted recording method and a microwave-assisted recording method, in which the magnetic recording medium is irradiated with laser light or microwaves to locally reduce the coercive force and record magnetic information. The thermally assisted recording method and the microwave-assisted recording method can achieve a recording capacity of 2 Tbit / inch 2 Since it is possible to achieve an areal recording density of up to 1000 times the normal level, it is being considered as a next-generation magnetic recording method that can increase storage capacity as magnetic recording media become smaller, thinner, and have higher recording densities.

[0003] As a magnetic recording medium that can be used in the thermally assisted recording method, for example, a magnetic recording medium that is composed of a substrate, a plurality of underlayers formed on the substrate, and a magnetic layer mainly composed of an alloy having an L10 structure, the plurality of underlayers including a NiO underlayer and an orientation control layer has been disclosed (see, for example, Patent Document 1). In this magnetic recording medium, the orientation control layer includes an underlayer made of an alloy having a BCC structure and an underlayer such as MgO having a NaCl structure, and causes the NiO underlayer to have a (100) orientation.

[0004] When an FePt alloy having an L10 structure is used as the magnetic layer of a magnetic recording medium, the (001) plane is used as the crystal orientation plane of the magnetic layer. In order to orient the FePt alloy in (001), MgO with (100) orientation is generally used as the underlayer. That is, since the (100) plane of MgO has high lattice matching with the (001) plane of the FePt alloy, by forming a magnetic layer containing the FePt alloy above the MgO layer, the FePt alloy is easily oriented in (001). In addition, in the magnetic recording medium of Patent Document 1, MgO is used as the underlayer of the orientation control layer to make the NiO underlayer also have a (100) orientation. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] JP 2016-26368 A Summary of the Invention [Problem to be solved by the invention]

[0006] Here, the lattice constant of MgO is 0.42 nm, while that of FePt is 0.39 nm. Therefore, when the FePt film is epitaxially grown on the MgO film, a slight lattice mismatch (misfit) occurs, and tensile stress occurs in the FePt film. The tensile stress generated in the FePt film acts in a direction to enlarge the FePt particles, so that the magnetic particles enlarge, and the electromagnetic conversion characteristics of the magnetic recording medium are likely to deteriorate, and the high recording density of the magnetic recording medium is likely to be hindered. Furthermore, the particles that have become even larger and have a larger contact area are more likely to receive large stress, so they are more likely to enlarge further, and the variation in crystal grain size increases, which is likely to deteriorate the electromagnetic conversion characteristics of the magnetic recording medium.

[0007] An object of one aspect of the present invention is to provide a magnetic recording medium that can have excellent electromagnetic conversion characteristics. [Means for solving the problem]

[0008] A magnetic recording medium according to one embodiment of the present invention comprises a substrate, an underlayer, and a magnetic layer containing an alloy having an L10 crystal structure, stacked in this order, the underlayer containing MgO, and the magnetic layer has at least three layers, and when the three magnetic layers are, from the substrate side, a first magnetic recording layer, a second magnetic recording layer, and a third magnetic recording layer, the Curie temperature Tc of the second magnetic recording layer is -30K to -100K lower than the Curie temperatures Tc of the first magnetic recording layer and the third magnetic recording layer, respectively, and the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer is 15% or more smaller than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer and the third magnetic recording layer, respectively. Effect of the Invention

[0009] According to one aspect of the present invention, it is possible to provide excellent electromagnetic conversion characteristics. [Brief description of the drawings]

[0010] [Figure 1] 1 is a cross-sectional view showing an example of the configuration of a magnetic recording medium according to an embodiment of the present invention. [Diagram 2] 1 is a TEM photograph showing an example of a cross section of a magnetic recording medium 1 according to the present embodiment. [Diagram 3] 1 is a perspective view showing an example of a magnetic storage device using a magnetic recording medium according to an embodiment of the present invention. [Figure 4] FIG. 2 is a schematic diagram showing an example of a magnetic head. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] Hereinafter, an embodiment of the present invention will be described in detail. In order to facilitate understanding of the description, the same components in each drawing are given the same reference numerals, and duplicated descriptions will be omitted. In addition, the scale of each member in the drawings may differ from the actual scale. In this specification, "~" indicating a numerical range means that the numerical values ​​before and after it are included as the lower and upper limits, unless otherwise specified.

[0012] [Magnetic recording media] Fig. 1 is a cross-sectional view showing an example of the configuration of a magnetic recording medium according to the present embodiment. As shown in Fig. 1, the magnetic recording medium 1 includes a substrate 10, an underlayer 20, and a magnetic layer 30, which are laminated in this order from the substrate 10 side.

[0013] In this specification, the thickness direction (vertical direction) of the magnetic recording medium 1 is defined as the Z-axis direction, and the lateral direction (horizontal direction) perpendicular to the thickness direction is defined as the X-axis direction. The magnetic layer 30 side in the Z-axis direction is defined as the +Z-axis direction, and the substrate 10 side is defined as the -Z-axis direction. In the following description, for convenience of explanation, the +Z-axis direction is referred to as the top or upper direction, and the -Z-axis direction is referred to as the bottom or lower direction, but this does not represent a universal up-down relationship.

[0014] Although FIG. 1 shows the underlayer 20 and the magnetic layer 30 only above the substrate 10, the magnetic recording medium 1 also includes an underlayer 20 and a magnetic layer 30 laminated in this order from the substrate 10 side below the substrate 10.

[0015] The magnetic recording medium 1 has an underlayer 20 and a magnetic layer 30 on both the top and bottom surfaces of the substrate 10, and information can be recorded on both the top and bottom surfaces of the substrate 10 (double-sided recording). However, the magnetic recording medium 1 may have an underlayer 20 and a magnetic layer 30 on only one of the top and bottom surfaces of the substrate 10, and information can be recorded on only one side of the substrate 10 (single-sided recording).

[0016] The material constituting the substrate 10 is not particularly limited as long as it is a material that can be used for a magnetic recording medium. Examples of materials constituting the substrate 10 include Al alloys such as AlMg alloys, soda glass, aluminosilicate glass, amorphous glasses, silicon, titanium, ceramics, sapphire, quartz, resins, etc. Among these, Al alloys and glasses such as crystallized glass and amorphous glass are preferred.

[0017] When manufacturing the magnetic recording medium 1, the substrate 10 may be heated to a temperature of 500°C or higher. Therefore, it is preferable to use, as the substrate 10, for example, a heat-resistant glass substrate having a softening temperature of 500°C or higher, preferably 600°C or higher.

[0018] The underlayer 20 is provided above the substrate 10. The underlayer 20 includes a layer containing MgO.

[0019] The layer containing MgO preferably contains MgO and essentially consists of MgO, and more preferably consists of only MgO. "Substantially" means that, in addition to MgO, it may contain inevitable impurities that are inevitably contained during the manufacturing process.

[0020] In this embodiment, since the underlayer 20 is in contact with the first magnetic recording layer 31, it becomes easier for the (100) plane of MgO to lattice match with the (001) plane of the magnetic alloy having the L10 structure contained in the first magnetic recording layer 31, thereby improving the crystal orientation of the magnetic alloy.

[0021] The underlayer 20 preferably contains a NaCl type compound. Examples of the NaCl type compound include, other than MgO, TiO, NiO, TiN, TaN, HfN, NbN, ZrC, HfC, TaC, NbC, TiC, and the like, and two or more of them may be used in combination.

[0022] The underlayer 20 may have a multi-layer structure including other layers, so long as it is possible to orient the magnetic grains having the L10 structure contained in the magnetic layer 30 in the (001) plane.

[0023] The magnetic layer 30 is provided above the underlayer 20. The magnetic layer 30 includes a first magnetic recording layer 31, a second magnetic recording layer 32, and a third magnetic recording layer 33, which are stacked in this order from the underlayer 20 side. The magnetic layer 30 may be composed of the first magnetic recording layer 31, the second magnetic recording layer 32, and the third magnetic recording layer 33. The magnetic layer 30 may further include one or more magnetic layers other than the first magnetic recording layer 31, the second magnetic recording layer 32, and the third magnetic recording layer 33.

[0024] The magnetic layer 30 contains magnetic grains having an L10 structure. That is, the first magnetic recording layer 31, the second magnetic recording layer 32, and the third magnetic recording layer 33 included in the magnetic layer 30 contain magnetic grains having an L10 structure.

[0025] By making the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer 31 at least 15% smaller than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer 32 and the third magnetic recording layer 33, respectively, and more preferably within the range of 30% to 60%, it is possible to prevent the magnetic grains from enlarging and to reduce the degree of variation in the average grain size of the bottom surface portions of the magnetic grains.

[0026] Here, the average grain size of the bottom surface of the magnetic grains refers to the average grain size at the interface below the magnetic grains. That is, the grains constituting the underlayer 20, the first magnetic recording layer 31, the second magnetic recording layer 32, and the third magnetic recording layer 33 grow epitaxially, so that these grains become continuous columnar crystals. In this columnar crystal, the average grain size at the interface between the underlayer 20 and the first magnetic recording layer 31 is defined as the average grain size of the bottom surface of the magnetic grains constituting the first magnetic recording layer 31. The average grain size at the interface between the first magnetic recording layer 31 and the second magnetic recording layer 32 is defined as the average grain size of the bottom surface of the magnetic grains constituting the second magnetic recording layer 32. The average grain size at the interface between the second magnetic recording layer 32 and the third magnetic recording layer 33 is defined as the average grain size of the bottom surface of the magnetic grains constituting the third magnetic recording layer 33.

[0027] In this embodiment, the average particle size of the bottom surface of the magnetic particles is measured using a scanning electron microscope (SEM) or a transmission electron microscope (TEM). For example, when a cross-section of the magnetic recording layer is observed using a TEM, the electron beam penetrates 10 nm or more, so that depth information of the cross-section can be obtained. The average particle size of the magnetic particles can be measured by analyzing this cross-sectional information.

[0028] The Curie temperature Tc of the second magnetic recording layer 32 is set to be lower by −30K to −100K than the Curie temperatures Tc of the first magnetic recording layer 31 and the third magnetic recording layer 33. As described above, the volume of the magnetic grains constituting the first magnetic recording layer 31 is smaller than those of the first magnetic recording layer 31 and the second magnetic recording layer 32, so that the magnetic properties of the first magnetic recording layer 31 are weaker than those of the second magnetic recording layer 32 in contact with the first magnetic recording layer 31. In this embodiment, the Curie temperature Tc of the second magnetic recording layer 32 is set to be lower than the Curie temperatures Tc of the first magnetic recording layer 31 and the third magnetic recording layer 33 within a predetermined range, thereby acting to strengthen the magnetic properties of the first magnetic recording layer 31. This strengthens the magnetic properties of the first magnetic recording layer 31, and reduces noise caused by the first magnetic recording layer 31.

[0029] FIG. 2 is a TEM photograph showing an example of a cross section of the magnetic recording medium 1 according to this embodiment. The magnetic recording medium shown in FIG. 2 has a structure in which an underlayer 20 containing MgO, a first magnetic recording layer 31, a second magnetic recording layer 32, a third magnetic recording layer 33, and a protective layer 40 are laminated in this order on a substrate 10. The three dashed lines in FIG. 2 indicate, from the bottom side in the figure, the average grain size of the bottom part of the magnetic grains constituting the first magnetic recording layer 31, the average grain size of the bottom part of the magnetic grains constituting the second magnetic recording layer 32, and the average grain size of the bottom part of the magnetic grains constituting the third magnetic recording layer 33, respectively. The first magnetic recording layer 31, the second magnetic recording layer 32, and the third magnetic recording layer 33 are different in composition of the materials constituting them, so that the boundary positions of each can be distinguished from the difference in contrast in the TEM photograph. It can be confirmed that the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer 31 is smaller than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer 32 and the average grain size of the bottom surface portions of the magnetic grains constituting the third magnetic recording layer 33.

[0030] A method for making the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer 31 smaller than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer 32 and the third magnetic recording layer 33, respectively, within a range of 5% to 40% is, for example, to use a sputtering method to deposit the first magnetic recording layer 31 and apply a positive bias potential to the substrate 10.

[0031] The film thickness of first magnetic recording layer 31 is preferably 0.4 nm to 1.5 nm, more preferably 0.5 nm to 1.0 nm, and even more preferably 0.6 nm to 0.8 nm. If the film thickness of first magnetic recording layer 31 is within the above preferred range, it can withstand the tensile stress generated at the interface between first magnetic recording layer 31 and second magnetic recording layer 32, and therefore first magnetic recording layer 31 can exhibit magnetic properties.

[0032] In this embodiment, the film thickness of the first magnetic recording layer 31 refers to the length in the direction perpendicular to the main surface of the first magnetic recording layer 31. The film thickness of the first magnetic recording layer 31 may be, for example, the thickness measured at any location on the cross section of the first magnetic recording layer 31. When measurements are taken at several arbitrary locations on the cross section of the first magnetic recording layer 31, the film thickness may be the average value of the thicknesses at these measurement locations.

[0033] The film thickness of the second magnetic recording layer 32 is preferably 0.8 nm to 3.0 nm, more preferably 1.0 nm to 2.5 nm, and even more preferably 1.2 nm to 2.0 nm. If the film thickness of the second magnetic recording layer 32 is within the above preferred range, the second magnetic recording layer 32 can withstand the tensile stress generated at the interface with the first magnetic recording layer 31 or the third magnetic recording layer 33, and therefore the second magnetic recording layer 32 can exhibit its magnetic properties.

[0034] The film thickness of the third magnetic recording layer 33 is preferably 3 nm or more, more preferably 3.5 nm to 10.0 nm, and even more preferably 4.5 nm to 6.0 nm. If the film thickness of the third magnetic recording layer 33 is within the above preferred range, the third magnetic recording layer 33 can withstand the tensile stress generated at the interface with the second magnetic recording layer 32, and therefore the third magnetic recording layer 33 can exhibit magnetic properties.

[0035] By setting the film thickness of each of the first magnetic recording layer 31, the second magnetic recording layer 32, and the third magnetic recording layer 33 within the above-mentioned preferred range, the first magnetic recording layer 31 can withstand the effect of tensile stress generated at the interface between each magnetic recording layer, thereby improving the electromagnetic conversion characteristics of the magnetic recording medium 1.

[0036] As the magnetic grains having the L10 structure contained in the magnetic layer 30, for example, FePt alloy grains, CoPt alloy grains, etc. can be used. The magnetocrystalline anisotropy constant (Ku) of the FePt alloy is 7×10 6 J / m 3 The Ku content of the CoPt alloy is 5×10 6 J / m 3 The following are all 1×10 6 J / m 3 The FePt alloy or the CoPt alloy is a material with a high Ku value (high Ku material) in the magnetic layer 30. Therefore, by including the FePt alloy or the CoPt alloy in the magnetic layer 30, the magnetic grains constituting the magnetic layer 30 can be finely divided to have a grain size of, for example, 6 nm or less while maintaining the thermal stability of the magnetic layer 30.

[0037] The magnetic layer 30 may also have a granular structure including grain boundaries.

[0038] When the magnetic layer 30 has a granular structure, the content of the grain boundary parts in the magnetic layer 30 is preferably in the range of 25 volume % to 50 volume %, and more preferably in the range of 35 volume % to 45 volume %. By setting the content of the grain boundary parts in the magnetic layer 30 within the above preferred range, the anisotropy of the magnetic particles contained in the magnetic layer 30 can be increased.

[0039] Here, the grain boundary portion can be made of carbide, nitride, oxide, boride, etc. Specific examples of these include BN, B4C, C, MoO3, GeO2, etc.

[0040] It is preferable that the magnetic grains contained in the magnetic layer 30 are c-axis oriented, i.e., (001) plane oriented, with respect to the substrate 10. The method for c-axis oriented of the magnetic grains contained in the magnetic layer 30 with respect to the substrate 10 is not particularly limited, and for example, a method of epitaxially growing the magnetic layer 30 in the c-axis direction using the underlayer 20 can be used.

[0041] The magnetic recording medium 1 preferably further has a protective layer 40 on the magnetic layer 30. The protective layer 40 has the function of protecting the magnetic recording medium 1 from damage caused by contact with a magnetic head or the like.

[0042] The protective layer 40 may be, for example, a hard carbon film.

[0043] Methods for forming the protective layer 40 include, for example, RF-CVD (Radio Frequency-Chemical Vapor Deposition) method, in which a film is formed by decomposing a hydrocarbon gas (raw material gas) using high frequency plasma, IBD (Ion Beam Deposition) method, in which a film is formed by ionizing a raw material gas using electrons emitted from a filament, and FCVA (Filtered Cathodic Vacuum Arc) method, in which a film is formed by using a solid carbon target without using a raw material gas.

[0044] The thickness of the protective layer 40 is preferably 1 nm to 6 nm. If the thickness of the protective layer 40 is 1 nm or more, the flying characteristics of the magnetic head are improved, the magnetic spacing is reduced, and the SNR of the magnetic recording medium 1 is improved.

[0045] The magnetic recording medium 1 may further include a lubricant layer 50 on the protective layer 40 .

[0046] The wetting agent may be, for example, a fluororesin such as perfluoropolyether.

[0047] The magnetic recording medium 1 according to this embodiment includes a substrate 10, an underlayer 20, and a magnetic layer 30 laminated in this order, with the underlayer 20 including MgO, and the magnetic layer 30 including a first magnetic recording layer 31, a second magnetic recording layer 32, and a third magnetic recording layer 33 laminated in this order from the substrate 10 side. In the magnetic recording medium 1, the Curie temperature Tc of the second magnetic recording layer 32 is lower by −30K to −100K than the Curie temperatures Tc of the first magnetic recording layer 31 and the third magnetic recording layer 33, respectively, and the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer 31 is smaller by 15% or more than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer 32 and the third magnetic recording layer 33, respectively. The average grain size of the bottom surface portion of the magnetic grains constituting the first magnetic recording layer 31 is smaller than the average grain size of the bottom surface portion of the magnetic grains constituting the second magnetic recording layer 32 and the third magnetic recording layer 33 by 15% or more, so that the magnetic properties of the first magnetic recording layer 31 are usually lower than those of the second magnetic recording layer 32 and the third magnetic recording layer 33. In this embodiment, the second magnetic recording layer 32 has a Curie temperature Tc that is smaller than those of the first magnetic recording layer 31 and the third magnetic recording layer 33 by a predetermined range, so that the magnetic properties of the second magnetic recording layer 32 can act to strengthen the first magnetic recording layer 31 and the third magnetic recording layer 33. Therefore, even if the magnetic properties of the first magnetic recording layer 31 are lower than those of the second magnetic recording layer 32 and the third magnetic recording layer 33 that are in direct or indirect contact with each other, the magnetic properties of the first magnetic recording layer 31 can be improved by the second magnetic recording layer 32 and the third magnetic recording layer 33. This enhances the magnetic properties of the first magnetic recording layer 31, and reduces noise caused by the first magnetic recording layer 31. Therefore, the magnetic recording medium 1 can exhibit excellent electromagnetic conversion properties.

[0048] The electromagnetic conversion characteristics of the magnetic recording medium 1 can be evaluated from the SNR (signal / noise ratio (S / N ratio)). The smaller the SNR of the magnetic recording medium, the better the electromagnetic conversion characteristics of the magnetic recording medium 1 can be evaluated. The measurement of the SNR is not particularly limited, and can be performed, for example, using a read / write analyzer RWA1632 and a spinstand S1701MP (both manufactured by GUZIK Corporation).

[0049] The magnetic recording medium 1 can contain magnetic particles in each magnetic recording layer, with the average particle size of the bottom surface of the magnetic particles constituting the first magnetic recording layer 31 being smaller within a range of 30% to 60% than the average particle size of the bottom surface of the magnetic particles constituting the second magnetic recording layer 32 and the third magnetic recording layer 33. Even if the size of the magnetic particles constituting the first magnetic recording layer 31 is smaller within the above range than the second magnetic recording layer 32 and the third magnetic recording layer 33, the magnetic properties of the first magnetic recording layer 31 can be strengthened and noise caused by the first magnetic recording layer 31 can be reduced. Therefore, the magnetic recording medium 1 can exhibit excellent electromagnetic conversion properties.

[0050] In the magnetic recording medium 1, the film thickness of the first magnetic recording layer 31 can be set to 0.4 nm to 1.5 nm. This allows the magnetic recording medium 1 to fully exhibit the magnetic characteristics of the first magnetic recording layer 31, and therefore ensures the excellent electromagnetic conversion characteristics.

[0051] In the magnetic recording medium 1, the film thickness of the second magnetic recording layer 32 can be set to 0.8 nm to 3.0 nm. This allows the magnetic recording medium 1 to fully exhibit the magnetic characteristics of the second magnetic recording layer 32, and therefore ensures the excellent electromagnetic conversion characteristics.

[0052] In the magnetic recording medium 1, the film thickness of the third magnetic recording layer 33 can be set to 3 nm or more. This allows the magnetic recording medium 1 to fully exhibit the magnetic properties of the third magnetic recording layer 33, and therefore ensures the excellent electromagnetic conversion properties.

[0053] The magnetic recording medium 1 includes a magnetic layer 30 that includes at least one of an FePt alloy and a CoPt alloy having an L10 structure. 6 J / m 3 It is a high Ku material of the order of 1000. Therefore, by using at least one of the FePt alloy and the CoPt alloy as the material constituting the magnetic layer 30, the magnetic particles constituting the magnetic layer 30 can be finely divided to, for example, a particle size of 6 nm or less while maintaining thermal stability. Therefore, when the thermally assisted recording method or the microwave assisted recording method is used as the recording method, the magnetic layer 30 can have a coercive force of several tens of kOe at room temperature, and magnetic information can be easily recorded in the magnetic layer 30 by the recording magnetic field of the magnetic head.

[0054] [Magnetic storage device] A magnetic storage device using the magnetic recording medium according to the present embodiment will be described. The magnetic storage device according to the present embodiment is not particularly limited in form as long as it has the magnetic recording medium according to the present embodiment. Here, a case will be described in which the magnetic storage device uses a thermally assisted recording method to record magnetic information on the magnetic recording medium.

[0055] The magnetic storage device of this embodiment may have, for example, a magnetic recording medium driving unit for rotating the magnetic recording medium of this embodiment, a magnetic head having a near-field light generating element at its tip, a magnetic head driving unit for moving the magnetic head, and a recording / playback signal processing unit.

[0056] The magnetic head is a thermally assisted recording type magnetic head, and has, for example, a laser light generating unit for heating the magnetic recording medium, and a waveguide for guiding the laser light generated from the laser light generating unit to the near-field light generating element.

[0057] Fig. 3 is a perspective view showing an example of a magnetic storage device using the magnetic recording medium according to this embodiment. As shown in Fig. 3, the magnetic storage device 100 can have a magnetic recording medium 101, a magnetic recording medium driving unit 102 for rotating the magnetic recording medium 101, a magnetic head 103 having a near-field light generating element at its tip, a magnetic head driving unit 104 for moving the magnetic head 103, and a recording / reproducing signal processing unit 105. The magnetic recording medium 1 according to this embodiment described above is used as the magnetic recording medium 101.

[0058] 4 is a schematic diagram showing an example of the magnetic head 103. As shown in FIG.

[0059] The recording head 110 has a main magnetic pole 111, an auxiliary magnetic pole 112, a coil 113 that generates a magnetic field, a laser diode (LD) 114 which is a laser light generating unit, and a waveguide 116 which transmits the laser light L generated from the LD 114 to a near-field light generating element 115.

[0060] The reproducing head 120 has a shield 121 and a reproducing element 122 sandwiched between the shield 121 .

[0061] As shown in FIG. 3, in the magnetic storage device 100, the center of a magnetic recording medium 101 is attached to the rotating shaft of a spindle motor, and information is written to or read from the magnetic recording medium 101 while a magnetic head 103 floats and runs above the surface of the magnetic recording medium 101, which is rotated by the spindle motor.

[0062] In the magnetic storage device 100 according to this embodiment, by using the magnetic recording medium 1 according to this embodiment as the magnetic recording medium 101, the recording density of the magnetic recording medium 101 can be increased, and therefore the recording density can be increased.

[0063] The magnetic storage device may use a microwave-assisted recording type magnetic head for the magnetic head 103 instead of the thermally-assisted recording type magnetic head. EXAMPLES

[0064] Hereinafter, the embodiment will be specifically described with reference to examples and comparative examples, but the embodiment is not limited to these examples and comparative examples.

[0065] <Manufacture of magnetic recording media> [Example 1] A magnetic recording medium was manufactured by the following method.

[0066] On a glass substrate, a 100 nm thick Cr-50 at% Ti alloy layer and a 30 nm thick Co-27 at% Fe-5 at% Zr-5 at% B alloy layer were sequentially formed as an underlayer. Next, the glass substrate was heated to 250°C, and then a 10 nm thick Cr layer and a 5 nm thick MgO layer were sequentially formed. Next, the glass substrate was heated to 450°C, and then a 1 nm thick FePt-40 mol% C film was formed as a first magnetic recording layer while applying a bias potential of +10 V to the substrate. Next, the glass substrate was heated to 630°C, and then a 2 nm thick FePt5 at% Rh-40 mol% C film was formed as a second magnetic recording layer. Next, a 3 nm thick FePt-16SiO2 film was sequentially formed as a third magnetic recording layer. Next, a 3 nm thick carbon film was formed as a protective layer, and a magnetic recording medium was produced.

[0067] [Examples 2 to 10, Comparative Examples 1-1 to 1-5] A magnetic recording medium was prepared in the same manner as in Example 1, except that the materials constituting at least one of the first magnetic recording layer, the second magnetic recording layer, and the third magnetic recording layer were changed as shown in Table 1.

[0068] [Comparative Examples 2-1 to 2-5] A magnetic recording medium was manufactured in the same manner as in Example 1, except that the glass substrate temperature during deposition of the first magnetic recording layer was 650°C and no bias potential was applied during deposition of the first magnetic recording layer.

[0069] [Comparative Example 3-1] A magnetic recording medium was manufactured in the same manner as in Example 1, except that the material constituting the magnetic layer was changed as shown in Table 1 and no bias potential was applied during deposition of the first magnetic recording layer.

[0070] The cross sections of the magnetic recording media manufactured in each of the examples and comparative examples were observed using a TEM to measure the average grain size of the bottom surface of the magnetic grains constituting the first magnetic recording layer, the average grain size of the bottom surface of the magnetic grains constituting the second magnetic recording layer, and the average grain size of the bottom surface of the magnetic grains constituting the third magnetic recording layer. The respective measurement results are shown in Table 1.

[0071] <Evaluation of magnetic recording media> (Electromagnetic conversion characteristics) The signal / noise ratio (S / N ratio) (SNR) was evaluated as the electromagnetic conversion characteristic of each of the magnetic recording media manufactured in each of the examples and comparative examples using a read / write analyzer RWA1632 and a spinstand S1701MP manufactured by GUZIK Corporation of the United States.

[0072] [Table 1]

[0073] As seen from Table 1, the SNR was 6.2 or more in Examples 1 to 11. On the other hand, the SNR was 5.8 or less in Comparative Examples 1-1 to 1-5, 2-1 to 2-4, and 3-1.

[0074] Thus, the magnetic recording media of Examples 1 to 11 differ from the magnetic recording media of Comparative Examples 1-1 to 1-5, 2-1 to 2-4, and 3-1 in that the Curie temperature Tc of the second magnetic recording layer 32 is −30K to −100K lower than the Curie temperatures Tc of the first magnetic recording layer 31 and the third magnetic recording layer 33, respectively, and the average grain size of the bottom surface portion of the magnetic grains constituting the first magnetic recording layer 31 is 15% or more smaller than the average grain size of the bottom surface portion of the magnetic grains constituting the second magnetic recording layer 32 and the third magnetic recording layer 33. As a result, it can be said that the magnetic recording medium 1 can exhibit excellent electromagnetic conversion characteristics because the grain size of the magnetic grains contained in the magnetic layer 30 can be made small.

[0075] Although the embodiment has been described above, the above embodiment is presented as an example, and the present invention is not limited to the above embodiment. The above embodiment can be implemented in various other forms, and various combinations, omissions, substitutions, modifications, etc. can be made without departing from the gist of the invention. These embodiments and their modifications are included in the scope and gist of the invention, and are included in the scope of the invention and its equivalents described in the claims. [Explanation of symbols]

[0076] 1, 101 Magnetic recording media 10 Substrate 20 Base layer 30 Magnetic layer 31 First magnetic recording layer 32 Second magnetic recording layer 33 Third magnetic recording layer 100 Magnetic storage device

Claims

1. Substrate, underlayer, and L1 ０ a magnetic layer including an alloy having a crystalline structure, the underlayer contains MgO; The magnetic layer has at least three layers, A magnetic recording medium in which, when the three magnetic layers are, in order from the substrate side, a first magnetic recording layer, a second magnetic recording layer, and a third magnetic recording layer, the Curie temperature Tc of the second magnetic recording layer is -30K to -100K lower than the Curie temperatures Tc of the first magnetic recording layer and the third magnetic recording layer, respectively, and the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer is 15% or more smaller than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer and the third magnetic recording layer, respectively.

2. The magnetic recording medium according to claim 1, wherein the average grain size of the bottom surface portions of the magnetic grains constituting the first magnetic recording layer is 30% to 60% smaller than the average grain size of the bottom surface portions of the magnetic grains constituting the second magnetic recording layer and the third magnetic recording layer.

3. 3. The magnetic recording medium according to claim 1, wherein the first magnetic recording layer has a thickness of 0.4 nm to 1.5 nm.

4. 4. The magnetic recording medium according to claim 1, wherein the second magnetic recording layer has a thickness of 0.8 nm to 3.0 nm.

5. 5. The magnetic recording medium according to claim 1, wherein the third magnetic recording layer has a thickness of 3 nm or more.

6. A magnetic storage device comprising the magnetic recording medium according to any one of claims 1 to 5.