Electrode Substrate

Abstract

An electrode substrate comprises an insulation substrate (110) and a reference electrode (120). The reference electrode (120) is formed on the insulation substrate (110). The reference electrode (120) includes a silver layer (121), a first silver chloride layer (122), and a second silver chloride layer (123). The silver layer (121) is formed on the insulation substrate (110). The first silver chloride layer (122) is formed on the silver layer (121) so as to span the area above the insulation substrate (110), and covers the silver layer (121). The second silver chloride layer (123) is formed on the first silver chloride layer (122) so as to span the area above the insulation substrate (110), and covers the first silver chloride layer (122). In an arbitrary vertical cross section, the surface area gap ratio of the first silver chloride layer (122) is larger than the surface area gap ratio of the second silver chloride layer (123).

Description

[Technical field]

[0001] The present invention relates to an electrode substrate. [Background technology]

[0002] A prior art document disclosing a method for manufacturing a reference electrode is JP 2005-292022 A (Patent Document 1). The reference electrode described in Patent Document 1 comprises a conductive pattern formed on an insulating substrate and a composite containing silver formed on the reference electrode portion of the conductive pattern, and the surface of the composite is composed of a silver chloride layer. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2005-292022 A Summary of the Invention [Problem to be solved by the invention]

[0004] Since silver chloride has a higher coefficient of thermal expansion than the constituent materials of the insulating substrate and silver, stress concentration occurs at the interface between the insulating substrate and the silver chloride layer when temperature changes occur, which may cause the reference electrode to peel off from the insulating substrate. [Means for solving the problem]

[0005] The electrode substrate according to the present invention includes an insulating substrate and a reference electrode. The reference electrode is formed on the insulating substrate. The reference electrode includes a silver layer, a first silver chloride layer, and a second silver chloride layer. The silver layer is formed on the insulating substrate. The first silver chloride layer is formed on the silver layer and on the insulating substrate, covering the silver layer. The second silver chloride layer is formed on the first silver chloride layer and on the insulating substrate, covering the first silver chloride layer. In any longitudinal section, the areal porosity of the first silver chloride layer is greater than the areal porosity of the second silver chloride layer. Effect of the Invention

[0006] According to the present invention, peeling of the reference electrode from the insulating substrate can be suppressed. [Brief description of the drawings]

[0007] [Figure 1] FIG. 2 is a plan view showing a configuration of an electrode substrate according to an embodiment of the present invention. [Diagram 2] 2 is a cross-sectional view of the electrode substrate of FIG. 1, taken along the line II-II. [Diagram 3] FIG. 1 is a perspective view illustrating a schematic configuration of a graphene transistor using an electrode substrate according to an embodiment of the present invention. [Figure 4] 1 is a photograph of a vertical cross section of a reference electrode of an electrode substrate according to one embodiment of the present invention, taken under magnification by a scanning electron microscope. [Diagram 5] This is a further enlarged photograph of part V in Figure 4. [Figure 6] FIG. 2 is a partial vertical cross-sectional view showing the shear stress distribution occurring when the temperature of a reference electrode according to a comparative example changes from 20° C. to 100° C. [Figure 7] FIG. 2 is a partial vertical cross-sectional view showing the shear stress distribution occurring when the temperature of the reference electrode according to the present embodiment changes from 20° C. to 100° C. [Figure 8] 8 is a graph showing the transition of shear stress at a position from point A along the interface between the insulating substrate and the silver chloride layer shown in FIGS. 6 and 7 between points AA′. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0008] Hereinafter, an electrode substrate according to an embodiment of the present invention will be described with reference to the drawings. In the following description of the embodiment, the same or corresponding parts in the drawings are given the same reference characters, and the description thereof will not be repeated.

[0009] Fig. 1 is a plan view showing a configuration of an electrode substrate according to one embodiment of the present invention. Fig. 2 is a cross-sectional view of the electrode substrate of Fig. 1 as viewed from the direction of the arrows II-II. As shown in Figs. 1 and 2, an electrode substrate 100 according to one embodiment of the present invention includes an insulating substrate 110 and a reference electrode 120. The reference electrode 120 is formed on the insulating substrate 110. The electrode substrate 100 further includes a metal wiring layer 170 formed on the insulating substrate 110.

[0010] The insulating substrate 110 may be made of a semiconductor such as silicon or germanium, glass such as quartz glass, lead glass or borosilicate glass, ceramic, or resin.

[0011] Examples of resin materials that can be used to form the insulating substrate 110 include polystyrene (PS), polypropylene (PP), polyimide (PI), polytetrafluoroethylene (PTFE), polyphenylene sulfide (PPS), polyether ether ketone (PEEK), polyethylene terephthalate (PET), polymethyl methacrylate (PMMA), and polyethylene-2,6-naphthalate (PEN). As described below, when the metal wiring layer is made of gold, it is preferable to form the insulating substrate 110 from polyethylene terephthalate, which has high adhesion to gold.

[0012] In this embodiment, the insulating substrate 110 is made of silicon, and has a SiO2 film formed on its surface.

[0013] The material for the metal wiring layer 170 may be a precious metal such as gold, platinum, or palladium, or carbon. From the standpoint of the stability of the surface state, it is preferable to form the metal wiring layer 170 from gold.

[0014] Possible methods for forming the metal wiring layer 170 include a method in which a conductive material is printed, sputtered or evaporated onto the entire surface of the insulating substrate 110, and then the conductive material is partially removed by etching or a laser to form a wiring pattern, or a method in which a wiring pattern is formed on the insulating substrate 110 by sputtering using a mask.

[0015] In this embodiment, the surface portion of the SiO2 film located at the planned formation position of the metal wiring layer 170 is removed to make it thinner, a titanium layer is formed at that location, and a gold layer is formed on the titanium layer. That is, the metal wiring layer 170 is configured with a laminated structure of a titanium layer and a gold layer. The thickness of the titanium layer is, for example, 10 nm. The thickness of the gold layer is, for example, 90 nm.

[0016] 1, a first connection terminal 162, a second connection terminal 163, a third connection terminal 164, a first electrode 130, and a second electrode 140 are formed by a patterned metal wiring layer 170. Each of the first connection terminal 162, the second connection terminal 163, and the third connection terminal 164 is formed along the edge of the insulating substrate 110, and can be electrically connected to an external terminal.

[0017] The first connection terminal 162 is connected to the reference electrode 120. The second connection terminal 163 is connected to the first electrode 130. The third connection terminal 164 is connected to the second electrode 140. The first electrode 130 and the second electrode 140 face each other with a gap therebetween. The first electrode 130 and the second electrode 140 are configured to be electrically connectable to each other through the transmission path 150.

[0018] In this embodiment, the transmission path 150 is composed of a semiconductor channel. Specifically, the transmission path 150 is composed of graphene. A pair of electrodes consisting of a first electrode 130 and a second electrode 140 is joined to a semiconductor channel formed in an insulating substrate 110. However, the transmission path 150 is not limited to a semiconductor channel, and may be a solution such as blood placed on the electrode substrate 100. In this case, the electrode substrate 100 is applicable to an enzyme sensor such as a glucose sensor.

[0019] As shown in FIGS. 1 and 2, the reference electrode 120 includes a metal wiring layer 170, a silver layer 121, a first silver chloride layer 122, and a second silver chloride layer 123.

[0020] Silver layer 121 is formed from above metal wiring layer 170 onto insulating substrate 110, covering at least a portion of metal wiring layer 170. A portion of silver layer 121 is formed on insulating substrate 110. Silver layer 121 is a plating film formed by electrolytic plating. The thickness of silver layer 121 is, for example, 3 μm.

[0021] 1, the silver layer 121 covers only a portion of the metal wiring layer 170. The portion of the metal wiring layer 170 that is not covered by the silver layer 121 constitutes a pair of electrodes, which are made up of a first electrode 130 and a second electrode 140 formed on the insulating substrate 110.

[0022] The first silver chloride layer 122 is formed from above the silver layer 121 onto the insulating substrate 110, and covers the silver layer 121. A portion of the first silver chloride layer 122 is formed on the insulating substrate 110.

[0023] The second silver chloride layer 123 is formed from above the first silver chloride layer 122 onto the insulating substrate 110, and covers the first silver chloride layer 122. A portion of the second silver chloride layer 123 is formed on the insulating substrate 110.

[0024] The first silver chloride layer 122 and the second silver chloride layer 123 are formed by immersing a silver plating film in hypochlorous acid. The first silver chloride layer 122 and the second silver chloride layer 123 may be formed by immersing the silver plating film in another oxidizing agent containing chlorine instead of hypochlorous acid. In this way, the silver layer 121, the first silver chloride layer 122, and the second silver chloride layer 123 are formed from a single silver plating film.

[0025] The reference electrode 120 may be formed by stacking the silver layer 121, the first silver chloride layer 122, and the second silver chloride layer 123 one by one in order. Specifically, a solvent containing silver-silver chloride particles is dispense-coated or spin-coated at the relevant location, and the solvent is evaporated to obtain a silver chloride layer. At this time, a member that evaporates at a relatively low temperature, such as resin beads, is mixed with the solvent and filled, and the resin-filled portion is made void by heat treatment, so that the first silver chloride layer 122 can be formed. Furthermore, the second silver chloride layer 123 can be obtained by forming a silver chloride layer by heat treatment without filling the resin beads in the solvent. Alternatively, if a similar structure is obtained, the first silver chloride layer 122 and the second silver chloride layer 123 may be stacked one by one in order by sputtering or vapor deposition.

[0026] As described later, in any longitudinal section, the area porosity of the first silver chloride layer 122 is greater than the area porosity of the second silver chloride layer 123. The sum of the thicknesses of the first silver chloride layer 122 and the second silver chloride layer 123 is 20 μm or less. The ratio of the thickness of the first silver chloride layer 122 to the sum of the thicknesses of the first silver chloride layer 122 and the second silver chloride layer 123 is 20% or more. In this embodiment, the sum of the thicknesses of the first silver chloride layer 122 and the second silver chloride layer 123 is about 10 μm. The ratio of the thickness of the first silver chloride layer 122 to the sum of the thicknesses of the first silver chloride layer 122 and the second silver chloride layer 123 is about 50%.

[0027] 3 is a perspective view showing a schematic configuration of a graphene transistor using an electrode substrate according to an embodiment of the present invention. As shown in FIG. 3, in the graphene transistor, an electrolyte solution 180 is disposed on an electrode substrate 100. A transmission path 150 made of graphene on a surface layer portion of an insulating substrate 110 contacts the electrolyte solution 180. The first electrode 130 functions as a source electrode, and the second electrode 140 functions as a drain electrode. The reference electrode 120 is provided to control the potential of the electrolyte solution 180.

[0028] A power supply that applies a gate voltage Vg is connected to the first connection terminal 162. The second connection terminal 163 is grounded. The third connection terminal 164 is connected to a power supply that applies a voltage between the source electrode and the drain electrode.

[0029] With the above-described configuration, in the graphene transistor, it is possible to modulate the electrical conductivity of the graphene by applying an electric field to the graphene via the electric double layer of the electrolyte 180.

[0030] A biosensor or a chemical sensor may be constructed using a graphene transistor. Specifically, a receptor or a functional film that specifically binds to a target molecule to be measured is formed on the graphene. The electric conductivity of the graphene is modulated by the charge of the target molecule bound to the surface of the graphene, so that it is possible to measure the presence or absence of the molecule to be measured or the concentration of the molecule in the solution.

[0031] The configuration of the reference electrode 120 of the electrode substrate 100 according to one embodiment of the present invention will be described in detail below.

[0032] Fig. 4 is a photograph of a vertical cross section of a reference electrode of an electrode substrate according to one embodiment of the present invention, taken by a scanning electron microscope. Fig. 5 is a further enlarged photograph of part V in Fig. 4.

[0033] 4 and 5, a SiO2 film 190 is formed on the surface of an insulating substrate 110, and a metal wiring layer 170 is formed on the SiO2 film 190. A silver layer 121, a first silver chloride layer 122, and a second silver chloride layer 123 are laminated in this order on the metal wiring layer 170. The silver layer 121 is formed of a polycrystalline body.

[0034] The first silver chloride layer 122 is formed of a porous body containing a large number of small crystallites and voids. The area porosity of the first silver chloride layer 122 is 10% or more. For the region R shown in FIG. 5, the area porosity of the first silver chloride layer 122 calculated using image analysis software "A-zo-kun" (registered trademark) manufactured by Asahi Kasei Engineering was 13%.

[0035] The second silver chloride layer 123 is formed of polycrystals with an average grain size of 1 μm or more. The second silver chloride layer 123 has a dense structure in which large crystallites are combined. As can be seen from Figures 4 and 5, in any longitudinal section, the areal porosity of the first silver chloride layer 122 is greater than the areal porosity of the second silver chloride layer 123.

[0036] The following chemical reaction is considered to be the mechanism by which the first silver chloride layer 122 and the second silver chloride layer 123 are formed. When the silver plating film is immersed in hypochlorous acid, silver located on the surface of the plating film is dissolved, and silver chloride containing many voids is formed on the surface. This portion becomes the first silver chloride layer 122. The silver dissolved from the surface becomes high-concentration silver chloride near the surface and precipitates outside the surface. This portion becomes the second silver chloride layer 123. As a result, the silver plating film expands in volume and becomes a laminated structure of the silver layer 121, the first silver chloride layer 122, and the second silver chloride layer 123.

[0037] [Table 1]

[0038] Table 1 summarizes the physical properties of the materials constituting the electrode substrate 100. However, for the first silver chloride layer, instead of physical properties or evaluation values, values ​​with a small thermal expansion coefficient and a small Young's modulus were adopted, taking into consideration the inclusion of voids. Qualitatively, as long as the first silver chloride layer has a smaller thermal expansion coefficient and a smaller Young's modulus than the second silver chloride layer, the thermal stress relaxation effect is exhibited. Also, as long as the thermal stress relaxation effect is exhibited, it is sufficient that either the thermal expansion coefficient or the Young's modulus of the first silver chloride layer is smaller than that of the second silver chloride layer.

[0039] Here, we will explain the results of a simulation analysis of the shear stress distribution that occurs when the temperature changes from 20°C to 100°C for a reference electrode according to a comparative example in which the second silver chloride layer 123 is formed even in the portion of the first silver chloride layer 122 and the first silver chloride layer 122 is not formed, and a reference electrode according to this embodiment.

[0040] FIG. 6 is a partial vertical cross-sectional view showing the shear stress distribution occurring when the temperature changes from 20° C. to 100° C. in a reference electrode according to a comparative example. FIG. 7 is a partial vertical cross-sectional view showing the shear stress distribution occurring when the temperature changes from 20° C. to 100° C. in a reference electrode according to this embodiment. FIG. 8 is a graph showing the transition of the shear stress at a position from point A between AA′ along the interface between the insulating substrate and the silver chloride layer shown in FIG. 6 and FIG. 7. In FIG. 8, the vertical axis shows the shear stress (MPa) and the horizontal axis shows the position (μm) from point A between AA′. The transition of the reference electrode according to the comparative example is shown by a dotted line, and the transition of the reference electrode according to this embodiment is shown by a solid line.

[0041] 6 to 7, in the reference electrode according to this embodiment, the shear stress generated when the temperature changed from 20° C. to 100° C. was lower than that in the reference electrode according to the comparative example. This is because the amount of thermal expansion of first silver chloride layer 122 is small, and the expansion of second silver chloride layer 123 causes deformation of first silver chloride layer 122, which has a small Young's modulus, thereby mitigating stress concentration at the interface between insulating substrate 110 and the silver chloride layer.

[0042] From the above simulation analysis results, it was confirmed that by including the first silver chloride layer 122 in the reference electrode 120, stress concentration at the interface between the insulating substrate 110 and the silver chloride layer can be alleviated, thereby suppressing peeling of the reference electrode 120 from the insulating substrate 110.

[0043] The electrode substrate 100 according to one embodiment of the present invention includes an insulating substrate 110 and a reference electrode 120. The reference electrode 120 is formed on the insulating substrate 110. The reference electrode 120 includes a silver layer 121, a first silver chloride layer 122, and a second silver chloride layer 123. The silver layer 121 is formed on the insulating substrate 110. The first silver chloride layer 122 is formed from on the silver layer 121 to on the insulating substrate 110, and covers the silver layer 121. The second silver chloride layer 123 is formed from on the first silver chloride layer 122 to on the insulating substrate 110, and covers the first silver chloride layer 122. In any longitudinal section, the area porosity of the first silver chloride layer 122 is larger than the area porosity of the second silver chloride layer 123. This makes it possible to suppress peeling of the reference electrode 120 from the insulating substrate 110.

[0044] In the electrode substrate 100 according to one embodiment of the present invention, the area porosity of the first silver chloride layer 122 is 10% or more. This reduces the amount of thermal expansion of the first silver chloride layer 122 when the temperature changes, and also reduces stress concentration at the interface between the insulating substrate 110 and the silver chloride layer due to deformation of the first silver chloride layer 122.

[0045] In the electrode substrate 100 according to one embodiment of the present invention, the ratio of the thickness of the first silver chloride layer 122 to the total thickness of the first silver chloride layer 122 and the second silver chloride layer 123 is 20% or more. This makes it possible to sufficiently ensure the stress relaxation effect of the first silver chloride layer 122.

[0046] In the electrode substrate 100 according to one embodiment of the present invention, the sum of the thickness of the first silver chloride layer 122 and the thickness of the second silver chloride layer 123 is 20 μm or less, which can reduce the magnitude of the shear stress generated at the interface between the insulating substrate 110 and the silver chloride layer when the temperature changes.

[0047] In the electrode substrate 100 according to one embodiment of the present invention, the second silver chloride layer 123 is formed of a polycrystal having an average grain size of 1 μm or more, which makes it possible to make the reference electrode 120 robust as a bulk body.

[0048] The electrode substrate 100 according to one embodiment of the present invention further includes a metal wiring layer 170 formed on the insulating substrate 110, and the silver layer 121 is formed from on the metal wiring layer 170 to on the insulating substrate 110 to cover at least a part of the metal wiring layer 170. This allows the silver layer 121 to be closely attached to the insulating substrate 110 via the metal wiring layer 170.

[0049] In the electrode substrate 100 according to one embodiment of the present invention, the silver layer 121 is formed of a polycrystalline material, which makes it possible to make the silver layer 121 robust as a bulk material.

[0050] In the electrode substrate 100 according to one embodiment of the present invention, the silver layer 121 is a plated film. This allows the silver layer 121 to be closely attached to the insulating substrate 110 via the metal wiring layer 170.

[0051] In the electrode substrate 100 according to one embodiment of the present invention, the silver layer 121 covers only a portion of the metal wiring layer 170. A pair of electrodes formed on the insulating substrate 110 is constituted by a portion of the metal wiring layer 170 that is not covered by the silver layer 121. This makes it possible to integrate the reference electrode 120 and the pair of electrodes, the first electrode 130 and the second electrode 140, on the insulating substrate 110.

[0052] In the electrode substrate 100 according to one embodiment of the present invention, a pair of electrodes is bonded to a semiconductor channel formed in an insulating substrate 110. This makes it possible to integrate a reference electrode 120 and a sensor unit including the semiconductor channel on the insulating substrate 110.

[0053] In the above description of the embodiments, configurations that can be combined may be combined with each other.

[0054] In the electrode substrate 100 according to one embodiment of the present invention, a reference electrode 120 and a sensor portion including a semiconductor channel are integrated on an insulating substrate 110, but a counter electrode or other elements may also be integrated on the same insulating substrate 110.

[0055] The embodiments disclosed herein should be considered to be illustrative and not restrictive in all respects. The scope of the present invention is defined by the claims, not the above description, and is intended to include all modifications within the meaning and scope of the claims. [Explanation of symbols]

[0056] 100 electrode substrate, 110 insulating substrate, 120 reference electrode, 121 silver layer, 122 first silver chloride layer, 123 second silver chloride layer, 130 first electrode, 140 second electrode, 150 transmission path, 162 first connection terminal, 163 second connection terminal, 164 third connection terminal, 170 metal wiring layer, 180 electrolyte, 190 SiO2 film.

Claims

1. An insulating substrate; a reference electrode formed on the insulating substrate; The reference electrode is a silver layer formed on the insulating substrate; a first silver chloride layer formed on the silver layer and extending over the insulating substrate, the first silver chloride layer covering the silver layer; a first silver chloride layer formed on the insulating substrate; a second silver chloride layer overlying the first silver chloride layer; An electrode substrate, wherein in any longitudinal section, the areal porosity of the first silver chloride layer is greater than the areal porosity of the second silver chloride layer.

2. The electrode substrate according to claim 1 , wherein the area porosity of the first silver chloride layer is 10% or more.

3. 2 . The electrode substrate according to claim 1 , wherein a ratio of a thickness of the first silver chloride layer to a total thickness of the first silver chloride layer and the second silver chloride layer is 20% or more.

4. 2. The electrode substrate according to claim 1, wherein the sum of the thickness of the first silver chloride layer and the thickness of the second silver chloride layer is 20 μm or less.

5. 2. The electrode substrate according to claim 1, wherein the second silver chloride layer is formed of polycrystals having an average grain size of 1 [mu]m or more.

6. A metal wiring layer is further formed on the insulating substrate. The electrode substrate according to claim 1 , wherein the silver layer is formed from above the metal wiring layer onto the insulating substrate, and covers at least a portion of the metal wiring layer.

7. The electrode substrate according to claim 6 , wherein the silver layer is formed of a polycrystalline material.

8. The electrode substrate according to claim 6 , wherein the silver layer is a plating film.

9. the silver layer covers only a portion of the metal wiring layer; 7. The electrode substrate according to claim 6, wherein a pair of electrodes formed on the insulating substrate is constituted by portions of the metal wiring layer that are not covered with the silver layer.

10. The electrode substrate according to claim 9 , wherein the pair of electrodes are bonded to a semiconductor channel formed in the insulating substrate.

Images