Rigid polyurethane foams containing siloxane-rich nucleating agents.

Abstract

The present technology provides a method for producing low thermal conductivity polyurethane foams from a foam formulation containing a polyol, an isocyanate, a polyurethane catalyst, a surfactant, water, and a siloxane-rich composition that can act as a nucleating agent to reduce the foam's cell size and lower its thermal conductivity.

Description

[Technical field]

[0001] This application claims priority to and the benefit of U.S. Provisional Application No. 62 / 769,060, entitled "Rigid Polyurethane Foams with Siloxane-Rich Nucleating Agent," filed November 19, 2018, the disclosure of which is incorporated herein by reference in its entirety.

[0002] The present technology relates generally to polyurethane foam compositions and foams made from such compositions. More specifically, the present technology relates to rigid or semi-rigid polyurethane foams that use siloxane-rich compounds of specific molecular weights as nucleating agents. [Background technology]

[0003] Rigid polyurethane foams are divided into two categories, PUR and PIR types. Rigid PUR foams are produced with a low isocyanate excess and contain primarily urethane and urea linkages formed from the isocyanate reaction. Rigid PIR foams are produced with a large excess of isocyanate, resulting in a significant amount of isocyanurate linkages resulting from the isocyanate trimerization reaction in addition to the urethane and urea linkages. Both foam types are widely used in the construction industry and as insulation for domestic or commercial refrigeration. These foams exhibit excellent thermal insulation properties.

[0004] Conventional rigid polyurethane foams, such as those that may be used in thermal insulation applications, are generally prepared by the reaction of at least one polyol with at least one isocyanate in the presence of suitable catalysts, surfactants, chemical and / or physical blowing agents, and optionally other additives, such as flame retardants or other processing or foam property improving additives.

[0005] Silicone-polyether copolymers are widely used as surfactants in such rigid polyurethane foam formulations. Attempts have been made to optimize these types of copolymers to improve or maximize the nucleation effect without compromising other foam properties. Opportunities remain to develop rigid polyurethane foams with improved thermal conductivity properties for use in insulation applications. Summary of the Invention

[0006] The present technology provides a siloxane-based additive composition for use in semi-rigid or rigid polyurethane foam formulations to provide improved thermal conductivity.

[0007] In one aspect, the present technology provides a rigid polyurethane or polyisocyanurate foam composition comprising a polyol or mixture thereof, an isocyanate, a polyurethane catalyst or mixture thereof, a surfactant, a siloxane-rich composition, water, a blowing agent that is either a physical blowing agent or mixture thereof, or a combination of both, optionally a co-chemical blowing agent or mixture thereof, optionally a flame retardant additive or mixture thereof, and optionally other processing additives. It has been found that the use of siloxane-rich materials of specific molecular weights can act as nucleating agents when used in combination with conventional rigid foam surfactants, especially those based on silicone-polyether copolymers. Applicant has found that the use of these siloxane-rich materials of specific molecular weights and / or molecular weight distributions can have a distinct nucleation effect in the initial mixing stage without resulting in defoaming or lack of cell size control in later reaction stages, thus providing foams with small cell sizes and resulting in low foam thermal conductivity.

[0008] In one embodiment, there is provided a composition comprising a siloxane-rich compound of the formula: M 3 a D 3 b D 4 c T d Qe (II) where M 3 is a trialkyl end-capping unit R 3 R 4 R 5 SiO 1 / 2 - and; D 3 is a dialkyl unit -O 1 / 2 R 6 R 7 SiO 1 / 2 -And: D 4 is an alkyl unit -O 1 / 2 R 8 R 9 SiO 1 / 2 - is; T is -O 1 / 2 Si(O 1 / 2 -)2R 10 and; Q is Si(O 1 / 2 -)4; R 3 , R 4 , R 6 , R 7 , R 8 , and R 10 are independently fluorine, phenyl, or a C1 to C10 alkyl group, further partially or fully substituted with fluorine or phenyl; R 5 is fluorine; phenyl; or a C1 to C10 alkyl group optionally partially or fully substituted with fluorine or phenyl; or -R 11 -O m -(CH2-CH2-O) q (CH2-CH(CH3)-O) p -R 12 and; R 9 -R 11 -O m -(CH2-CH2-O) q (CH2-CH(CH3)-O) p -R 12 and; R 11 is a C1 to C10 hydrocarbon group; R 12is hydrogen, phenyl, fluorine, or a C1-C8 hydrocarbon group, in embodiments partially or fully substituted with fluorine or phenyl, and optionally interrupted by a urethane, urea or carbonyl group; a and b are independently 0 to 30; c, d, and e are independently 0 to 5; m is 0 or 1; q and p are independently from 0 to 10; provided that b+c is at least 1; With the proviso that the siloxane-rich compound has a silicon content of at least 25% by weight.

[0009] In one embodiment, the siloxane-rich compound or mixture thereof has a number average molecular weight between 200 and 3000 Daltons.

[0010] In one embodiment, the siloxane-rich compound or mixture thereof has a number average molecular weight between 300 and 2500 Daltons.

[0011] In one embodiment, the siloxane-rich compound or mixture thereof has a number average molecular weight between 450 and 2000 Daltons.

[0012] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich compound or mixture thereof has a silicon content of greater than 28% by weight.

[0013] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich compound or mixture thereof has a silicon content of greater than 25% to about 32% by weight.

[0014] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich compound or mixture thereof has an average of no more than two reactive groups per molecule capable of reacting with an isocyanate.

[0015] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich compound or mixture thereof has, on average, less than two or no reactive groups capable of reacting with an isocyanate.

[0016] In one embodiment of the composition of any of the preceding embodiments, the subscript a of the siloxane-rich compound is equal to at least one.

[0017] In one embodiment of the composition of any of the preceding embodiments, the subscript a is 1 to 30; 2 to 20; or 2 to 10.

[0018] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich composition is based on a distribution of molecular weights that includes no more than 2.5% of siloxane-based species having a molecular weight less than 400.

[0019] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich composition is based on a molecular weight distribution containing 2.5% or less of siloxane-based species having a molecular average molecular weight of less than 400; less than 350; less than 300; or less than 250.

[0020] In one embodiment of the composition of any of the preceding embodiments, the siloxane-rich composition contains about 5% or less; 3.5% or less; 2.5% or less; 1% or less; or 0.5% or less of cyclic siloxane species containing 3 to 6 siloxane groups, commonly referred to as D3, D4, and D6.

[0021] In one aspect, there is provided a foam formulation comprising: a polyol; an isocyanate; a catalyst; a surfactant; a physical blowing agent; and a siloxane-rich composition according to any of the preceding embodiments.

[0022] In another aspect, there is provided a method for producing a polyurethane foam by reacting different components of a formulation including a polyol; an isocyanate; a catalyst; a surfactant; a physical blowing agent; and a siloxane-rich composition according to any of the preceding embodiments.

[0023] In one embodiment, the siloxane-rich composition or mixture is used in an amount of at least 0.02% by weight, based on the total weight of the formulation ingredients excluding the physical blowing agent.

[0024] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture is present in an amount of at least 0.03 wt %, based on the total weight of the formulation components excluding the physical blowing agent.

[0025] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture is present in an amount of at least 0.05% by weight, based on the total weight of the formulation ingredients excluding the physical blowing agent.

[0026] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture is present in an amount of 3 wt % or less, based on the total weight of the formulation components excluding the physical blowing agent.

[0027] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture is present in an amount of about 0.05% to about 3% by weight based on the total weight of the formulation ingredients excluding the physical blowing agent.

[0028] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture thereof is added to a formulated preblend and mixed with an isocyanate component to produce a polyurethane foam for use as an insulating material.

[0029] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture thereof is added as a separate component in a foam dispensing unit to produce polyurethane foam for use as thermal insulation.

[0030] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture thereof is added to an isocyanate component and mixed with an isocyanate-reactive component to produce a polyurethane foam for use as an insulating material.

[0031] In one embodiment of the method of any of the preceding embodiments, the siloxane-rich composition or mixture thereof is added to the polyurethane foam formulation in addition to a surfactant that optionally includes a siloxane, where the siloxane-containing portion of such surfactant, if present, has a silicon content of less than 25% and a number average molecular weight greater than 2000 Daltons.

[0032] In one embodiment of the method of any of the preceding embodiments, the polyol is selected from polyester polyols, polyether polyols, polycarbonate polyols, polythioether polyols, polycaprolactones, brominated polyether polyols, acrylic polyols, or combinations of two or more thereof.

[0033] In one embodiment of the process of any of the preceding embodiments, the catalyst package is made of a tertiary amine that provides blowing and gelling catalytic activity, and optionally a trimerization catalyst that provides isocyanurate catalytic activity.

[0034] In one embodiment of the process of any of the preceding embodiments, the physical blowing agent is selected from hydrocarbons, particularly pentane, and any isomeric mixtures of hydrofluorocarbons, hydrofluoroolefins, hydrochlorofluorocarbons, hydrochlorofluoroolefins, and any combination thereof.

[0035] In one embodiment of the method of any of the previous embodiments, the method forms a rigid or semi-rigid polyurethane foam. In one embodiment, the rigid or semi-rigid polyurethane foam has a viscosity of 10 to 100 kg / m 3 and an isocyanate index between 100 and 500.

[0036] In one embodiment, the foam is used as a thermal insulation material.

[0037] In one embodiment, the foam has an initial thermal conductivity of about 23 mW / m·K or less at an average temperature of 0 to 30° C.

[0038] In yet another aspect, an article is provided that includes the polyurethane foam formed from the method.

[0039] In one aspect, there is provided a polyurethane or polyisocyanurate foam formed from the composition of any of the preceding embodiments.

[0040] In one embodiment, the isocyanate composition of the foam is selected from aromatic polyisocyanates, aliphatic polyisocyanates, or any combination thereof.

[0041] In one aspect, an article is provided that includes the polyurethane or polyisocyanurate foam of any of the preceding embodiments.

[0042] In one aspect, there is provided a method of forming a polyurethane or polyisocyanurate foam comprising reacting a composition of any of the preceding embodiments. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0043] The present technology provides an additive composition for use in foam-forming formulations and foams made from such formulations. The foam formulations include (a) a polyol component; (b) an isocyanate component; (c) a catalyst component; (d) a surfactant; and (e) a siloxane-rich composition. The use of the siloxane-rich composition provides foams with good properties, including, for example, low thermal conductivity. Without being bound by a particular theory, the siloxane-rich composition may function as a good nucleating agent, allowing for controlling or providing foams with good properties, including, for example, low thermal conductivity.

[0044] The polyol component is not particularly limited and can be selected as desired for a particular purpose or intended application. In various embodiments, the polyol can be selected from polyester polyols, polyether polyols, polycarbonate polyols, hydroxyl-terminated polyolefin polyols, and the like, or a combination of two or more thereof. The polyol can be, for example, polyester diols, polyester triols, polyether diols, polyether triols, and the like. Alternatively, the polyol can be selected from the group of polythioether polyols, polycaprolactones, brominated polyether polyols, acrylic polyols, and the like, or a combination of two or more thereof. When a high functionality polyether polyol is used, the high functionality polyether polyol can have a functionality of about 3 to about 6. Polyols such as sucrose or sorbitol initiators can be mixed with low functionality glycols or amines to bring the functionality of the polyol to a range of about 3.5 to about 5.

[0045] Further, particularly suitable polyols include aromatic polyester polyols. Aromatic polyester polyols can be prepared from substantially pure reactant materials or more complex starting materials such as polyethylene terephthalate can be used. Furthermore, dimethyl terephthalate (DMT) process residues can be used to form aromatic polyester polyols.

[0046] The aromatic polyester polyol may contain halogen atoms. It may be saturated or unsaturated. The aromatic polyester polyol may have an aromatic ring content that is at least about 30 weight percent, 35 weight percent, or even about 40 weight percent, based on the total compound weight. Here, as elsewhere in the specification and claims, numerical values ​​may be combined to form new or undisclosed ranges. Polyester polyols having an acid component that advantageously includes at least about 30 weight percent of phthalic acid residues or residues of isomers thereof are particularly useful.

[0047] The aromatic polyester polyols may have a hydroxyl number of greater than about 50 mg KOH / g, greater than about 100 mg KOH / g, greater than about 150 mg KOH / g, greater than about 200 mg KOH / g, and greater than about 250 mg KOH / g. In one embodiment, the aromatic polyester polyols have a hydroxyl number of about 100 mg KOH / g to about 300 mg KOH / g. Here, as elsewhere in the specification and claims, numbers may be combined to form new, undisclosed ranges.

[0048] In one embodiment, the aromatic polyester polyol has a functionality greater than about 1, or greater than about 2. In one embodiment, the aromatic polyester polyol has a functionality of from about 1 to about 4, or from about 1 to about 2. Here, as elsewhere in the specification and claims, numerical values ​​may be combined to form new, undisclosed ranges.

[0049] The foam composition also includes an isocyanate composition. The isocyanate may include at least one isocyanate and may include more than one isocyanate. The isocyanate may be selected from an aromatic isocyanate, an aliphatic isocyanate, or any combination thereof. The isocyanate composition may include an aromatic isocyanate, such as a polymeric MDI. When the isocyanate composition includes an aromatic isocyanate, the aromatic isocyanate may be represented by the formula R 1 (NCO) z where R 1 is an aromatic polyvalent organic radical, and z is R 1 Generally, z is at least 2.

[0050] The isocyanate composition may be selected from the group consisting of 1,4-diisocyanatobenzene, 1,3-diisocyanato-o-xylene, 1,3-diisocyanato-p-xylene, 1,3-diisocyanato-m-xylene, 2,4-diisocyanato-1-chlorobenzene, 2,4-diisocyanato-1-nitrobenzene, 2,5-diisocyanato-1-nitrobenzene, m-phenylene diisocyanate, p-phenylene diisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, a mixture of 2,4- and 2,6-toluene diisocyanate, 1,5-naphthalene diisocyanate, 1-methoxy-2,4-phenylene diisocyanate, 4,4'-diphenylmethane diisocyanate, 2,4'-diphenylmethane diisocyanate, 4,4'-biphenylene diisocyanate, 3, The isocyanates may include, but are not limited to, 3'-dimethyl-4,4'-diphenylmethane diisocyanate, and 3,3'-dimethyldiphenylmethane-4,4'-diisocyanate, triisocyanates such as 4,4',4''-triphenylmethane triisocyanate polymethylene polyphenylene polyisocyanate and 2,4,6-toluene triisocyanate, tetraisocyanates such as 4,4'-dimethyl-2,2'-5,5'-diphenylmethane tetraisocyanate, toluene diisocyanate, 2,2'-diphenylmethane diisocyanate, 2,4'-diphenylmethane diisocyanate, 4,4'-diphenylmethane diisocyanate, polymethylene polyphenylene polyisocyanate, their corresponding isomeric mixtures, and any combinations thereof.

[0051] The foam composition also includes one or more catalysts. The catalyst is not particularly limited and can be selected from any catalyst material suitable for catalyzing the reaction between hydroxyl groups from either water, polyol or any hydroxyl-terminated compound and isocyanate to form a foamed thermosetting polyurethane-based polymer. Examples of suitable catalysts are selected from, but are not limited to, gelling catalysts and / or blowing catalysts, and / or trimerization catalysts. Specifically, gelling catalysts can catalyze the reaction of hydroxyl with isocyanate to produce urethane bonds. Blowing catalysts can promote the reaction of water with isocyanate to produce urea bonds. Trimerization catalysts can promote the reaction of three isocyanate groups to form isocyanurate bonds. The catalyst can include one or more catalysts, and typically includes a combination of catalysts. The catalyst may or may not be consumed in the exothermic reaction depending on whether it contains isocyanate-reactive groups. The catalyst can include any suitable catalyst or mixture of catalysts known in the art. Examples of suitable catalysts include, but are not limited to, amine catalysts in a suitable diluent, such as dipropylene glycol, and metal catalysts, such as tin, bismuth, lead, and the like. If included, the catalyst may be included in various amounts. In one embodiment, the catalyst is N,N-dimethylcyclohexylamine (DMCHA), N,N,N',N',N''-pentamethyldiethylenetriamine (PMDETA), bis-(2-dimethylaminoethyl)ether, amidines, such as 2,3-dimethyl-3,4,5,6-tetrahydropyrimidine, other tertiary amines, such as triethylamine, tributylamine, dimethylbenzylamine, N-methylmorpholine, N-ethylmorpholine, N-cyclohexyl ... phosphorus, N,N,N',N'-tetramethylethylenediamine, N,N,N',N'-tetramethylbutanediamine, N,N,N',N'-tetramethylhexane-1,6-diamine, mono- or bis(dimethylaminopropyl)urea dimethylpiperazine, 1,2-dimethylimidazole, 1-azabicyclo[3.3.0]octane, 1,4-diazabicyclo[2.2.2]octane, alkanolamine compounds such as triethanolamine, triisopropanolamine,N-Methyldiethanolamine, N-Ethyldiethanolamine, Dimethylethanolamine, Tris(N,N-dimethylaminopropyl)-s-hexahydrotriazine, Tris(dialkylaminoalkyl)-s-hexahydrotriazine, Tetraalkylammonium hydroxides, including tetramethylammonium hydroxide, Quaternary ammonium carboxylate salts, Tetramethylammonium acrylate, Tetraethylammonium acrylate, Tetrapropylammonium acrylate, Tetrabutylammonium acrylate, (2-hydroxypropyl)trimethylammonium formate, (2-hydroxypropyl)trimethylammonium 2-ethylhexanoate, Tetramethylammonium pivalate, Tetraethylammonium pivalate, Tetrapropylammonium pivalate, Tetrabutylammonium pivalate, Tetramethylammonium triethyl acetate, Tetraethylammonium triethyl acetate, Tetrapropylammonium triethyl acetate, Tetrabutylammonium triethyl acetate, Tetramethylammonium ammonium neoheptanoate, tetraethylammonium neoheptanoate, tetrapropylammonium neoheptanoate, tetrabutylammonium neoheptanoate, tetramethylammonium neooctanoate, tetraethylammonium neooctanoate, tetrapropylammonium neooctanoate, tetrabutylammonium neooctanoate, tetramethylammonium neodecanoate, tetraethylammonium neodecanoate, tetrapropylammonium neodecanoate, tetrabutylammonium neo decanoate, alkali metal hydroxides including sodium hydroxide and potassium hydroxide, alkali metal alkoxides including sodium methoxide and potassium isopropoxide, alkali metal salts of long chain fatty acids having 5 to 20 carbon atoms and / or lateral hydroxyl groups, tin, iron, lead, bismuth, mercury, titanium, hafnium, zirconium, iron(II) chloride, zinc chloride, lead octoate stabilized stannous octoate, tin(II) salts of organic carboxylic acids such as stannous acetate, stannous octoate, tin(II) ethylhexanoate,and tin(II) laurate, and dialkyltin(IV), salts of organic carboxylic acids such as dibutyltin dilaurate, dibutyltin diacetate, dibutyltin maleate and dioctyltin diacetate, potassium formate, potassium acetate, potassium propionate, potassium butanoate, potassium pentanoate, potassium hexanoate, potassium heptanoate, potassium octanoate, potassium 2-ethylhexanoate, potassium decanoate, potassium butyrate, potassium isobutyrate, potassium nonanoate, potassium stearate, 2-hydroxypropyltrimethylammonium octoate solution, sodium salts such as sodium octanoate, sodium acetate, sodium caprioate, lithium salts such as lithium stearate, lithium octanoate, or any combination thereof. In various embodiments, the catalyst may be included in an amount of 0.5 to 8 weight percent of the total foam composition. Here, as elsewhere in the specification and claims, numerical values ​​may be combined to form new or undisclosed ranges.,

[0052] The foam composition includes a surfactant. The surfactant can be any surfactant suitable for use in the production of rigid foams, including, for example, those that can contribute to controlling or regulating cell size. Examples of such surfactants are sodium salts of castor oil sulfonates, sodium salts of fatty acids, salts of fatty acids with amines, alkali metal or ammonium salts of sulfonic acids, polyether siloxane copolymers, or mixtures of two or more thereof. In one aspect, the composition includes a silicone surfactant, particularly a silicone polyether type surfactant. Other types of surfactants, such as non-silicone surfactants, or combinations of both, can be used. In one embodiment, the surfactant can include nonionic surfactants, cationic surfactants, anionic surfactants, amphoteric surfactants, and combinations thereof. In various embodiments, the surfactant can include, but is not limited to, polyoxyalkylene polyol surfactants, alkylphenol ethoxylate surfactants, and combinations thereof. In one embodiment, salts of sulfonic acids, such as, for example, alkali metal and / or ammonium salts of oleic acid, stearic acid, dodecylbenzene-disulfonic acid or dinaphthylmethane-disulfonic acid and ricinoleic acid, and cell modulating agents such as other organopolysiloxanes, oxyethylated alkylphenols, oxyethylated fatty alcohols, paraffin oil, castor oil, castor oil esters, and ricinoleic acid esters, and fatty alcohols, and combinations thereof.

[0053] In one embodiment, the surfactant is selected from the group of silicone surfactants. In general, silicone surfactants can control cell size, closed cell content, flow, and limit void formation in rigid foams produced from the reaction of the resin composition with the isocyanate composition. Examples of suitable surfactants include silicone polyether type surfactants, including those of the formula: M 1 D 1 x D 2 y M 2 (I) Here, M 1 and M. 2 are independently (CH3)3SiO 1 / 2 , or (CH3)2R 1 SiO 1 / 2 represents D 1 is (CH3)2SiO 2 / 2 represents D 2 (CH3)R 1 SiO 2 / 2 represents x+y is usually between 10 and 150; y is usually at least 2; the ratio x / y is usually between 2 and 15; and R 1 are independently selected polyethers or mixtures, and the average thereof is represented by the formula -C n H 2n O(C2H4O) t (C3H6O) z R 2 and having a number average molecular weight of 150 to 5000, where n is from 2 to 4, t is a number such that the oxyethylene residues constitute 40 to 100 weight percent of the alkylene oxide residues of the polyoxyalkylene polyether, z is a number such that the propylene oxide residues constitute 60 to 0 weight percent of the alkylene oxide residues of the polyoxyalkylene polyether, and R 2 represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or -C(O)CH3.

[0054] Silicone copolymer surfactants can be prepared by several synthetic approaches, including stepwise addition of polyether. Furthermore, the polyoxyalkylene polyether component is well known in the art and / or can be produced by any conventional process. For example, hydroxy-terminated polyoxyalkylene polyethers, which are convenient starting materials in the preparation of terpolymers, can be prepared by reacting a suitable alcohol with ethylene oxide and propylene oxide (1,2-propylene oxide) to produce a polyoxyalkylene polyether of the desired molecular weight. Suitable alcohols are hydroxyalkenyl compounds, such as vinyl alcohol, allyl alcohol, methallyl alcohol, and the like. In general, the alcohol starter is placed in an autoclave or other high-pressure vessel, preferably with a catalytic amount of a suitable catalyst, such as sodium hydroxide, potassium hydroxide, other alkali metal hydroxides, or sodium or other alkali metals. Further details of the preparation are described, for example, in U.S. Pat. No. 3,980,688, the entire contents of which are incorporated herein by reference.

[0055] The above alcohol-oxide reaction produces monohydroxy endblocked polyoxyalkylene polyethers in which the other endblocking group is an unsaturated olefinic group consisting of either an allyl or methallyl or vinyloxy group. These polyethers can be converted to non-isocyanate reactive polyoxyalkylene polyethers by capping the hydroxy endgroups of the monohydroxy endblocked poly(oxyethyleneoxypropylene) copolymers by any conventional means.

[0056] The foam composition may include two or more different types of silicone surfactants.

[0057] Non-limiting examples of conventional silicone surfactants suitable for the foam composition include those available under the Niax® trade name available from Momentive Performance Materials Inc. Suitable surfactants include, but are not limited to, Niax® L-6900, L-5111, L-6972, L-6633, L-6635, L-6190, L-6100, and the like, or combinations of two or more thereof.

[0058] The surfactant may be present in any suitable amount. In various embodiments, the surfactant is present in an amount of 0.5 to 5, 1 to 3, or about 2 weight percent of the foam composition. Here, as elsewhere in the specification and claims, numerical values ​​may be combined to form new or unspecified ranges.

[0059] The foam composition may also include a non-silicone surfactant. The non-silicone surfactant may be used with or without a silicone surfactant. Any surfactant known in the art may be used in the present invention. Thus, the surfactant may include a non-ionic surfactant, a cationic surfactant, an anionic surfactant, an amphoteric surfactant, and combinations thereof. In various embodiments, the surfactant may include, but is not limited to, a polyoxyalkylene polyol surfactant, an alkylphenol ethoxylate surfactant, and combinations thereof. When a surfactant is included in the resin composition, the surfactant may be present in any suitable amount.

[0060] The foam composition includes an additive composition comprising a siloxane-rich compound of a defined molecular weight, the additive sometimes referred to herein as the siloxane-rich composition. The siloxane-rich composition may include a compound of the formula: M 3 a D 3 b D 4 c T d Qe (II) Here, M 3 is a trialkyl end-capping unit R 3 R 4 R 5 SiO 1 / 2 -And ;D 3 is a dialkyl unit -O 1 / 2 R 6 R 7 SiO 1 / 2 -And ;D 4 is an alkyl unit -O 1 / 2 R 8 R 9 SiO 1 / 2 - is; T is -O 1 / 2 Si(O 1 / 2 -)2R 10 and Q is Si(O 1 / 2 -)4; R 3 , R 4 , R 6 , R 7 , R 8 , and R 10 are independently fluorine, phenyl, or a C1 to C10 alkyl group, further partially or fully substituted with fluorine or phenyl; R 5 is fluorine; phenyl; or a C1 to C10 alkyl group optionally partially or fully substituted with fluorine or phenyl; or -R 11 -O m -(CH2-CH2-O) q (CH2-CH(CH3)-O) p -R 12 and; R 9 -R 11 -O m -(CH2-CH2-O) q (CH2-CH(CH3)-O) p -R 12 and; R 11 is a C1 to C10 hydrocarbon group; R 12is hydrogen, phenyl, fluorine, or a C1-C8 hydrocarbon group, in embodiments partially or fully substituted with fluorine or phenyl, and optionally interrupted by a urethane, urea or carbonyl group; a and b are independently 0 to 30; c, d, and e are independently 0 to 5; m is 0 or 1; q and p are independently from 0 to 10; provided that b+c is at least 1; With the proviso that the siloxane-rich compound has a silicon content of at least 25% by weight.

[0061] In embodiments, the siloxane-rich compounds have a number average molecular weight of about 200 to about 3000 Daltons; about 300 to about 2500 Daltons; about 400 to about 2000 Daltons; about 450 to about 2000 Daltons. Values ​​can be combined to form new ranges and unspecified ranges. Number average molecular weights can be determined by silicon NMR ( 29 It can be determined by SiNMR.

[0062] In an embodiment, the siloxane-rich composition is based on a molecular weight distribution that includes no more than 2.5 wt.% of siloxane-based species having a molecular weight of less than 400. In an embodiment, a composition according to any of the preceding embodiments is provided, wherein the siloxane-rich composition is based on a molecular weight distribution that includes no more than 2.5 wt.% of siloxane-based species having a molecular weight of less than 400; less than 350; less than 300; or less than 250. Molecular weight can be assessed and quantified using gas chromatography recalculated to weight percent using a calibration factor.

[0063] In embodiments, the siloxane-rich composition comprises standard low molecular weight cyclic siloxanes having 3 to 6 siloxane units in an amount of about 5% or less; 4% or less; 2.5% or less; 1% or less; or 0.5% or less. In embodiments, the siloxane-rich composition has very low levels of these residual cyclic siloxane species, less than 0.1% each. Exemplary of such low molecular weight cyclic siloxanes are hexamethylcyclotrisiloxane (D3), octamethylcyclotetrasiloxane (D4), decamethylcyclopentasiloxane (D5), and dodecamethylcyclohexasiloxane (D6).

[0064] The silicon content of the siloxane-rich composition is at least 25% by weight or more; at least 28% by weight or more; at least 30% by weight or more, up to about 32% by weight.

[0065] In one embodiment, the siloxane-rich composition preferably has an average of no more than two reactive groups per molecule capable of reacting with isocyanates; no more than one reactive group per molecule capable of reacting with isocyanates; or no reactive groups capable of reacting with isocyanates.

[0066] In one embodiment, the siloxane-rich composition is a polydimethylsiloxane having a number average molecular weight of about 200 to 3000 Daltons; about 300 to 2500 Daltons; about 450 to 2000 Daltons, with less than 2.5% by weight of species having a molecular weight less than 400.

[0067] The composition comprising the siloxane-rich compound may comprise a combination of different siloxane-rich compounds as described in formula (II).Provided are siloxane-rich compounds in the foam formulation such that the siloxane-rich composition is present in an amount of about 0.02% to about 5%; about 0.03% to about 4%; about 0.05% to about 3% by weight based on the total weight of the formulation excluding the physical blowing agent.

[0068] The siloxane-rich composition may be provided as a separate additive or may be added as part of a composition that includes a surfactant, the siloxane-rich composition, and ultimately a diluent or other component relevant for incorporation as an ingredient into a foam formulation. Examples of suitable diluents include, for example, dipropylene glycol, hexylene glycol, or polymers derived from alkoxylated initiators of different functionalities from 1 to 10, and the like.

[0069] The foam composition may also include one or more blowing agents, including but not limited to physical blowing agents, chemical blowing agents, or any combination thereof. In an embodiment, the blowing agent may include both physical blowing agents and co-chemical blowing agents, and the blowing agent may be included in the foam composition. A physical blowing agent typically does not chemically react with the resin composition and / or isocyanate to provide a blowing gas. A physical blowing agent may be a gas or a liquid. A liquid physical blowing agent may evaporate to a gas when heated and return to a liquid when cooled. A physical blowing agent may reduce the thermal conductivity of the rigid polyurethane foam. Blowing agents may include, but are not limited to, methylene chloride, acetone, and liquid carbon dioxide, aliphatic and / or cycloaliphatic hydrocarbons, halogenated hydrocarbons and alkanes, acetals, water, alcohols, formic acid, and any combination thereof. In an embodiment, the composition includes a chemical blowing agent selected from water, formic acid, or a combination thereof.

[0070] In various embodiments, the blowing agent is selected from the group consisting of hydrocarbons, hydrofluorocarbons, hydrochlorofluoroolefins (HCFOs) and hydrofluoroolefins (HFOs), volatile non-halogenated C2-C7 hydrocarbons, such as alkanes, e.g., N-pentane, isopentane, cyclopentane, alkenes, cycloalkanes having up to 6 carbon atoms, dialkyl ethers, cycloalkylene ethers and ketones, and hydrofluorocarbons, C1-C4 hydrofluorocarbons, volatile non-halogenated hydrocarbons, linear or branched alkanes. butane, isobutane, 2,3-dimethylbutane, n- and isohexane, n- and isoheptane, n- and isooctane, n- and isononane, n- and isodecane, n- and isoundecane, and n- and isodedecane; alkenes, for example 1-pentene, 2-methylbutene, 3-methylbutene, and 1-hexene; cycloalkanes, for example cyclobutane, and cyclohexane; linear and / or cyclic ethers, for example dimethyl ether, diethyl ether, methyl ethyl ether, vinyl methyl ether; Vinyl ethyl ether, divinyl ether, dimethoxymethane (methylal), tetrahydrofuran and furan, ketones such as acetone, methyl ethyl ketone and cyclopentanone and their isomers, esters of carboxylic acids such as methyl methanoate (methyl formate), hydrofluorocarbons such as difluoromethane (HFC-32), 1,1,1,2-tetrafluoroethane (HFC-134a), 1,1,2,2-tetrafluoroethane (HFC-134), 1,1-difluoroethane (HFC-152a), 1,2-difluoroethane (HFC-152b), 1,2-difluoroethane (HFC-152c), 1,2-difluoroethane (HFC-152d), 1,2-difluoroethane (HFC-152e), 1,2-difluoroethane (HFC-152f), 1,2-difluoroethane (HFC-152g), 1,2-difluoroethane (HFC-152h), 1,2-difluoroethane (HFC-152i ... Oroethane (HFC-142), trifluoromethane, heptafluoropropane (R-227a), hexafluoropropane (R-136), 1,1,1-trifluoroethane, 1,1,2-trifluoroethane, fluoroethane (R-161), 1,1,1,2,2-pentafluoropropane, pentafluoropropylene (R-2125a), 1,1,1,3-tetrafluoropropane, tetrafluoropropylene (R-2134a), difluoropropylene (R-2152b), 1,1,2,3,3-pentafluoropropane, 1,1,1,3,The blowing agent may be selected from 3-pentafluoro-n-butane, and 1,1,1,3,3-pentafluoropentane (245fa), isomers thereof, 1,1,1,2-tetrafluoroethane (HFC-134a), isomers thereof, and combinations thereof. In various embodiments, the blowing agent may be further defined as 1,1,1,3,3-pentafluoropentane (245fa) or a combination of HFC 245fa, 365MFC, 227ea, and 134a. In an alternative embodiment, the blowing agent may be further defined as 365MFC, which may be blended with 227ea. In a further embodiment, the blowing agent may be further defined as cis or trans isomers of 1-chloro-3,3,3-trifluoro-propene or 1,1,1 4,4,4 hexafluoro-2-butene, or combinations thereof with each other or with any other blowing agent listed above.

[0071] In various embodiments, the blowing agent may be present in an amount of 0.1 to 30, 1 to 25, 2 to 20, 3 to 18, 5 to 15 weight percent of the foam composition. Here, as elsewhere in the specification and claims, numerical values ​​may be combined to form new or undisclosed ranges. In general, the amount of blowing agent and / or water may be selected based on the desired density of the rigid foam and the solubility of the blowing agent in the associated resin composition.

[0072] The foam composition may also include a crosslinker and / or a chain extender. The crosslinker may include, but is not limited to, additional polyols, amines, and any combination thereof. When a crosslinker is included in the foam composition, the crosslinker may be present in any suitable amount. Chain extenders contemplated for use in the present technology include, but are not limited to, hydrazines, primary and secondary diamines, alcohols, amino acids, hydroxy acids, glycols, and combinations thereof. Specific chain extenders contemplated for use include, but are not limited to, mono- and diethylene glycol, mono- and dipropylene glycol, 1,4-butanediol, 1,3-butanediol, propylene glycol, dipropylene glycol, diethylene glycol, methylpropylene diol, mono-, di-, and tri-ethanolamine, N-N'-bis-(2 hydroxy-propylaniline), trimethylolpropane, glycerin, hydroquinone bis(2-hydroxyethyl)ether, 4,4'-methylene-bis(2-chloroaniline, diethyltoluenediamine, 3,5-dimethylthio-toluenediamine, hydrazine, isophoronediamine, adipic acid, silanes, and any combination thereof.

[0073] The foam composition may also include one or more additives. Suitable additives include non-reactive flame retardants (e.g., various phosphates, various phosphonates, triethyl phosphate, trichloropropyl phosphate, triphenyl phosphate, or diethylethyl phosphonate, tris(2-chloroethyl)phosphate, tris-ethyl-phosphate, tris(2-chloro-propyl)phosphate, tris(1,3-dichloropropyl)phosphate, diammonium phosphate, various halogenated aromatic compounds, antimony oxide, alumina trihydrate, polyvinyl chloride, and any combination thereof), OH Additives that may be present in the foam composition include, but are not limited to, free / non-reactive flame retardants, chain terminators, modified or unmodified phenolic resins, inert diluents, amines, defoamers, air release agents, wetting agents, surfactants, waxes, inert inorganic fillers, molecular sieves, reactive inorganic fillers, other types of glass such as cut glass, glass mat, processing additives, surfactants, adhesion promoters, antioxidants, dyes, pigments, UV stabilizers, thixotropic agents, anti-aging agents, antistatic additives, lubricants, coupling agents, solvents, rheology enhancers, cell openers, release additives, and combinations thereof. One or more additives may be present in the foam composition in any amount.

[0074] In addition to foam compositions, the art also provides methods for forming foams and methods for forming foams on surfaces.

[0075] The process for forming rigid foams typically involves combining the polyol, the isocyanate composition, the surfactant, the siloxane-rich composition, and any other additives. The isocyanate index of the foam is generally not limited. Most typically, the polyol and isocyanate composition are combined such that the isocyanate index is generally greater than 120 and can reach values ​​of up to 500 or 600, depending on the foam being produced, either PUR or PIR type. Those skilled in the art will understand that the foam can be a polyurethane type foam (PUR, typically with an index less than 200) or a polyisocyanurate (PIR, typically with an index much greater than 200, usually greater than 250) foam. However, it will be understood that there is no absolute value of the index to describe PUR foam from PIR foam.

[0076] The method of forming a rigid foam on a surface may include combining the ingredients to form a foam mixture. Generally, the combining step may occur in a mixing device such as a static mixer, a mechanical or impingement mixing chamber, or a mixing pump. In one embodiment, the mixing step occurs in a static mixing tube. Alternatively, the foam composition and the isocyanate composition may be combined in a spray nozzle.

[0077] The process of forming rigid or semi-rigid foams may involve air nucleation of one or more of the compounding ingredients when processed in industrial mixing equipment.

[0078] The components can be combined on the surface or at a location remote from the surface. In one embodiment, the components can be combined in the head of a spray gun or in the air above the surface to which the composition is being applied. The components can be combined and applied to the surface by any method known in the art, including spraying, dipping, pouring, coating, painting, and the like.

[0079] The present technology provides semi-rigid or rigid polyurethane foams ("rigid or semi-rigid foams"). Rigid foams can be open or closed cell and can include a highly crosslinked polymer structure that allows the foam to have good thermal stability, high compressive strength at low density, low thermal conductivity, and good barrier properties. Typically, the rigid foams of this technology have a glass transition temperature higher than room temperature (about 23°C + / - 2°C (about 73.4°F + / - 3.6°F)) and are typically rigid at room temperature. In general, the foams are rigid below the glass transition temperature, especially in the glassy region of the storage modulus. Polyurethane foam materials have a strength of about 10 to about 900 kg / m 3 , from about 15 to about 800 kg / m 3 , from about 20 to about 500 kg / m 3 , from about 30 to about 400 kg / m 3 In one embodiment, the rigid foam may have a density of about 10 to about 60 kg / m 3 Here, as elsewhere in the specification and claims, numerical values ​​may be combined to form new or undisclosed ranges.

[0080] The foam mixture can be applied to any suitable surface, such as brick, concrete, masonry, drywall, sheetrock, plaster, metal, stone, wood, plastic, polymer composites, or any combination thereof. Additionally, the surface can be the surface of a mold, so that a rigid foam can be formed within the mold.

[0081] The resulting rigid or semi-rigid foam can be used in the form of slabstock, moldings, panels, or filled cavities. The filled cavities can be, for example, pipes, insulated walls, insulated ship hull structures. The rigid foam can be a spray foam, a blown foam, or a continuously produced laminate product, or a discontinuously produced laminate product, such as, but not limited to, a laminate or laminate product formed with other materials, such as hardboard, gypsum board, plastic, paper, metal, or combinations thereof.

[0082] Rigid foams prepared according to embodiments of the present technology may exhibit improved processability. The foams may exhibit reduced defects, including but not limited to reduced shrinkage and deformation. This property may be useful in the manufacture of sandwich panels. A sandwich panel may include at least one relatively planar layer of rigid foam (i.e., a layer having two generally larger dimensions and one generally smaller dimension) facing each of its larger dimension sides, with at least one layer of rigid or flexible material, such as foil or metal or other structure-providing material, on each such side. Such layers may, in certain embodiments, function as substrates during the formation of the foam.

[0083] Additionally, foam mixtures produced from the above ingredients in the above manner may have improved thermal insulation properties, e.g., lower thermal conductivity. In particular, the present compositions using siloxane compositions having specific molecular weights of the described structures may reduce the thermal conductivity of the foam compared to similar foam compositions lacking the described siloxane compositions.

[0084] The rigid foams comprising the above-described siloxane-rich compositions can be further understood with reference to the following examples. EXAMPLES

[0085] Foam Preparation and Testing Methodology

[0086] The foams were generally prepared by first making resin blends containing various polyols, flame retardants, catalysts, and water in one-liter plastic cups.

[0087] Adequate weights were used to obtain sufficient free rise height while maintaining the blend component ratios as shown in Tables 1a-1c and 3. The conventional surfactant and siloxane rich compositions are then added separately or as a mixture when low levels would prevent good metering accuracy. In either case, it is mixed gently with a spatula until the homogeneity of the premix blend is obtained. The physical blowing agent is a pentane isomer or a mixture thereof and is added to this resin blend to the target weight, then mixed gently with a spatula until the homogeneity of the premix blend is achieved. Small amounts of another pentane are added until the weight required to compensate for the small amount lost by evaporation during the blend is obtained. This is repeated until the required weight is reached and stabilized. The resulting mixture is further mixed at 4000 rpm for 10 seconds using a mechanical mixer. The required amount of isocyanate is pre-weighed in a separate cup and quickly added to the cup containing the polyol-pentane premix to provide the reactive blend. The reactive blend is further mixed for 5 seconds at 4000 rpm using a high energy mechanical mixer with a 6 cm circular propeller and immediately after the end of mixing, poured into a square open paper cup mould with a section of 23x23 cm and a height of 20 cm, surrounded on the sides by a square wooden frame. Pouring is done in the middle of the square section. The foam is allowed to rise freely in the vertical direction. Cream time and gel time are measured from the remaining reactive material in the cup. A rigid free rise foam is obtained and left to cool and harden for a further 24 hours at room temperature in the open paper mould.

[0088] A portion of the foam is then cut from the center of the block measuring 20x20x4cm after 24 hours and the thermal conductivity is evaluated. This portion is used to measure the core foam density measurements and thermal conductivity (also called lambda value) from 0°C to 20°C (average temperature 10°C) or 10 to 36°C (average temperature 23°C) using a FOX Lasercomp 200 heat flow meter. The recorded value is referred to as the initial thermal conductivity.

[0089] Raw materials used in the composition

[0090] Stepanpol PS 2412 is an aromatic polyester polyol obtained from Stepan Voranol. RN411 is a polyether polyol obtained from Dow Chemicals. Daltocel R585 is a polyether polyol obtained from Huntsman Co. TCPP liquid flame retardant is (tris(1-chloro-2-propyl) phosphate. Niax A-1, C-5, C-8, and potassium octoate are commercial catalysts in the Momentive Urethane Additives portfolio. Desmodur 44V70L and Suprase c5025 are polymeric MDI grades obtained from Covestro and Huntsman Co, respectively.

[0091] Tables 1a-1c show typical formulations of PIR foams, e.g., foams produced with formulations having an isocyanate index typically above 200. In the experiments described, an index of 300 was chosen, which is a typical value used for PIR foams, e.g., for flexible or metal-faced construction panels. The blowing agent used was n-pentane, and the lambda values ​​were measured at an average temperature of 10°C between plate temperatures of 0°C and 20°C. [Table 1] [Table 2] [Table 3] [Table 4] Notes for Tables 1a-1c * Eliminate excess polyether reactant in case of siloxane modification ** Excluding the weight of physical blowing agents For both Tables 1a-c and 3, the following silicone-based compositions are used: Conventional rigid foam silicone stabilizer: A copolymer obtained by reacting a linear silicone hydride of 65 D units and 7.5 D' units on an allyl hydroxy terminated EO / PO polyether with 30% polyether excess, the polyether containing about 12.8 EO units and 3.2 PO. The siloxane copolymer has a silicone content of about 19% and a number average molecular weight of about 11,000 Daltons. Siloxane-based compositions 1 to 4 are shown in Table 2. Siloxane composition 5: Hexamethyldisiloxane, or MM Siloxane composition 6: Unmodified polydimethylsiloxane, T type with average structure M3D7T Siloxane composition 7: Modified siloxane obtained by reacting MD'M with allylhydroxy-terminated polyethylene oxide, 6.6 EO units Siloxane composition 8: Modified siloxane obtained by reacting MD'M with allylmethoxy-terminated polyethylene oxide, 6.6 EO units [Table 5] Notes regarding Table 2 * as the average number of D units per two M termini 29 Determined by SiNMR ** Determined by gas chromatography and recalculated to weight percent using calibration factors *** Determined by gel permeation chromatography (GPC) as the molecular weight that contributes less than 0.5% of the total integral on the low molecular weight side - polydimethylsiloxane standards are used for calibration **** Determined by gel permeation chromatography (GPC) as the molecular weight that contributes less than 1% of the total integral on the high molecular weight side - polydimethylsiloxane standards are used for calibration *****D4, D5, and D6 are common cyclic residual species in the siloxane composition, octamethylcyclotetrasiloxane (D4), decamethylcyclopentasiloxane (D5), and dodecamethylcyclohexasiloxane (D6), respectively. The levels were obtained by liquid extraction of the composition followed by gas chromatography of the extracted mixture. The results show that conventional silicone surfactant incorporated at standard levels of 1.6 to 2.8 parts per 100 parts of primary polyol results in initial foam thermal conductivity values ​​(or lambda values) in the range of 24 to 24.5 mW / m·K for foams 1a to 1c. Some standard scattering is observed in foams without added siloxane composition, but in the range of 24 to 24.5 mW / m·K. By increasing the conventional surfactant level to a much higher value, such as 5 parts, a slightly lower lambda value at 23.81 mw / m·K can be obtained, but this is a very small advantage that is considered to be of no consequence. It has been found that by adding a selected molecular weight siloxane-rich composition at a low level of 0.2 parts per 100 parts of primary polyol in addition to the conventional silicone surfactant, significantly lower foam lambda values ​​can be obtained. This can be seen in the added siloxane compositions 1 to 3 or 6, which are included in the aspects and embodiments of the present invention. Comparative examples using added siloxane compositions 4, 5, 7, or 8, which have lower or higher molecular weights or lower silicon content and are outside the scope of the present invention, did not provide such benefits. All foams produced from these experiments did not differ significantly in other fundamental foam properties such as reactivity (quantified by gel time) and foam density.

[0092] Table 3 shows typical formulations of PUR foams, for example, made with formulations having a calculated isocyanate excess significantly less than 200. In the experiments described in Table 3, a 30% molar isocyanate excess was used, which means an isocyanate index of 130. The blowing agent used in this formulation was cyclopentane, and the lambda values ​​were measured at an average temperature of 23°C between plate temperatures of 0°C and 36°C. [Table 6] * Eliminate excess polyether reactant in case of siloxane modification ** Excluding the weight of physical blowing agents These PUR formulations show comparable effects to those obtained with the PIR formulations. Significant thermal conductivity benefits of 0.4 mW / m·K or more are achieved with additive siloxane compositions 2 and 6, which are within the scope of aspects and embodiments of the present invention, compared to control foam 2. Comparative examples using additive siloxane compositions 5, 7, or 8, which are outside the scope of the present invention, do not improve the lambda values ​​of siloxane compositions 5 and 8, or show a slight benefit, on the order of 0.2 mW / m·K for siloxane composition 7. Again, other fundamental foam properties such as reactivity quantified by gel time and foam density produced foams are not significantly different.

[0093] While embodiments of the technology have been described above, other modifications and alterations may occur to those skilled in the art upon reading and understanding this specification, and it is intended that the following claims include all such modifications and alterations insofar as they come within the scope of the claims or equivalents thereof.

Claims

1. 1. A composition for use as an additive in polyurethane foam formulations comprising a compound of formula M ３ ａ D ３ ｂ D ４ ｃ T ｄ Q ｅ (II) a siloxane-rich compound, M ３ is a trialkyl end-capping unit R ３ R ４ R ５ SiO １／２ - and D ３ is a dialkyl unit -O １／２ R ６ R ７ SiO １／２ - and D ４ is an alkyl unit -O １／２ R ８ R ９ SiO １／２ - and T is -O １／２ Si(O １／２ -) ２ R １０ and Q is Si(O １／２ -) ４ and R ３ , R ４ , R ６ , R ７ , R ８ , and R １０ are independently fluorine, phenyl, or a C1 to C10 alkyl group, further partially or fully fluorine or phenyl substituted; R ５ is fluorine, phenyl, or a C1 to C10 alkyl group optionally partially or fully substituted with fluorine or phenyl, or -R １１ -O ｍ - (CH ２ -CH ２ -O) ｑ (CH ２ -CH(CH ３ ) -O) ｐ -R １２ and R ９ Ha-R １１ -O ｍ - (CH ２ -CH ２ -O) ｑ (CH ２ -CH(CH ３ ) -O) ｐ -R １２ and R １１ is a C1 to C10 hydrocarbon group, R １２ is hydrogen, phenyl, fluorine, or a C1-C8 hydrocarbon group, in embodiments partially or fully substituted with fluorine or phenyl, and optionally interrupted by urethane, urea or carbonyl groups; a is 1 to 30, b is 0 to 30, c, d, and e are independently 0 to 5; m is 0 or 1; q and p are 0; The condition is that b+c is at least 1, provided that the siloxane-rich compound has a silicon content of at least 25% by weight, and the siloxane-rich compound has a number average molecular weight between 300 and 2500 Daltons and does not have any reactive groups capable of reacting with isocyanates.

2. The composition of claim 1 , wherein the siloxane-rich compound has a number average molecular weight between 450 and 2000 Daltons.

3. 3. The composition of claim 1 or 2, wherein the siloxane-rich compound has a silicon content of greater than 28% by weight.

4. 4. The composition of claim 1, wherein the siloxane-rich compound has a silicon content of greater than 28% to 32% by weight.

5. 5. The composition of claim 1, wherein the siloxane-rich compound has an average of no more than two reactive groups per molecule capable of reacting with isocyanates.

6. 6. The composition of claim 1, wherein the siloxane-rich compound has on average less than two or no reactive groups capable of reacting with isocyanates.

7. 7. The composition of claim 1, wherein the siloxane-rich compounds are based on a distribution of molecular weights that includes no more than 2.5% by weight of siloxane-based species having a molecular weight of less than 400.

8. 8. The composition of any one of claims 1 to 7, wherein the siloxane-rich compounds comprise up to 5% by weight of cyclic siloxane species having 3 to 6 siloxane groups selected from hexamethylcyclotrisiloxane (D3), octamethylcyclotetrasiloxane (D4), decamethylcyclopentasiloxane (D5), and dodecamethylcyclohexasiloxane (D6).

9. Polyol, Isocyanates, catalyst, Surfactants, A physical blowing agent, and 9. A method for producing polyurethane foam by reacting different components of a formulation comprising the siloxane-rich compound of any one of claims 1 to 8.

10. 10. The method of claim 9, comprising the siloxane-rich compound in an amount of at least 0.02% by weight based on the total weight of the ingredients excluding the physical blowing agent.

11. 11. The method of claim 9 or 10, comprising the siloxane-rich compound in an amount of at least 0.03% by weight based on the total weight of the formulation ingredients excluding the physical blowing agent.

12. 11. The method of claim 9 or 10, comprising the siloxane-rich compound in an amount of at least 0.05% by weight based on the total weight of the formulation ingredients excluding the physical blowing agent.

13. 13. The method of any one of claims 9 to 12, comprising the siloxane-rich compound in an amount of 3% by weight or less, based on the total weight of the ingredients excluding the physical blowing agent.

14. 14. The method of any one of claims 9 to 13, comprising the siloxane-rich compound in an amount of 0.05% to 3% by weight based on the total weight of the ingredients excluding the physical blowing agent.

15. 15. The method of any one of claims 9 to 14, wherein the siloxane-rich compound is added to the formulated preblend and mixed with the isocyanate component to produce a polyurethane foam for use as an insulating material.

16. 16. The method of any one of claims 9 to 15, wherein the siloxane-rich compound is added as a separate component in a foam dispensing unit to produce a polyurethane foam for use as an insulating material.

17. 17. The method of any one of claims 9 to 16, wherein the siloxane-rich compound is added to an isocyanate component and mixed with an isocyanate-reactive component to produce a polyurethane foam for use as an insulating material.

18. 18. The method of any one of claims 9 to 17, wherein the siloxane-rich compound is added to the polyurethane foam formulation in addition to a surfactant that optionally comprises siloxane, where the siloxane-containing portion of such surfactant, if present, has a silicon content of less than 25% and a number average molecular weight of greater than 2000 Daltons.

19. 19. The method of any one of claims 9 to 18, wherein the method forms a rigid or semi-rigid polyurethane foam.

20. Rigid or semi-rigid polyurethane foam with a strength of 10 to 100 kg / m ３ and an isocyanate index of between 100 and 500.

21. A polyurethane foam formed from the composition of any one of claims 1 to 8.

22. The foam has a melting point of 10 to 100 kg / m ３ 21. The polyurethane foam of claim 20, which is a rigid or semi-rigid polyurethane foam having a density between 0.1 and 0.5 and an Isocyanate Index between 100 and 500.

23. 22. The polyurethane foam of claim 21, wherein the foam has an initial thermal conductivity of 23 mW / m·K or less at an average temperature of 0 to 30° C.

24. 24. An insulating material comprising the polyurethane foam of claim 22 or 23.

25. 24. An article comprising the polyurethane foam of any one of claims 21 to 23.