Resin composition for cores and cores

Abstract

The present invention provides a core resin composition that exhibits high heat resistance and can be used to produce a core that does not deform even under molding conditions of super engineering plastics. Also provided is a core obtained by using the core resin composition. The present invention is a core resin composition that contains a polyvinyl alcohol resin and has a melt flow rate (MFR) of 35 g / 10 min or less under a load condition of 10 kg at 230°C.

Description

[Technical Field]

[0001] This invention relates to a resin composition for cores and a core. [Background technology]

[0002] Conventionally, in order to obtain molded bodies with complex internal structures by injection molding, the use of cores made of water-soluble resin compositions has been considered. For example, a core with a shape corresponding to the complex internal structure is placed inside a mold and injection molded. After that, a molded body with a complex internal structure can be obtained by removing the core from the resulting molded body. From the viewpoint of reducing environmental impact, the use of water-soluble resins is being considered for the resin used in the core. For example, Patent Document 1 discloses a core resin containing a polyvinyl alcohol-based resin and an easy-release agent. [Prior art documents] [Patent Documents]

[0003] [Patent Document 1] International Publication No. 2021 / 157375 [Overview of the project] [Problems that the invention aims to solve]

[0004] In recent years, from the perspective of weight reduction, there has been research into replacing the materials used in automobile and other parts with super engineering plastics (super engineering plastics) that have excellent heat resistance. As a result of diligent research, the present inventors have found that because the molding temperature of super engineering plastics is higher than that of general-purpose thermoplastic resins, when a core resin such as that described in Patent Document 1 is used, the core resin deforms during molding. When the core resin deforms during molding, the problem is that a molded product with the desired shape cannot be obtained.

[0005] The present invention aims to provide a resin composition for cores that exhibits high heat resistance and can be used to manufacture cores that do not deform even under the molding conditions of super engineering plastics. Furthermore, the invention aims to provide a core made using this resin composition. [Means for solving the problem]

[0006] (1) This disclosure relates to a core resin composition comprising a polyvinyl alcohol resin, wherein the melt flow rate (MFR) under conditions of 230°C and a 10 kg load is 35 g / 10 min or less. Disclosure (2) is a core resin composition of Disclosure (1), wherein the polyvinyl alcohol resin has a weight-average molecular weight (Mw) of 200,000 or less and a degree of saponification of 72% or more and 99.8% or less. Disclosure (3) is a core resin composition according to Disclosure (1) or (2), wherein the polyvinyl alcohol resin has a viscosity of 30 mPa·s or less when aqueously dissolved in a 4% by mass solution. This disclosure (4) further contains particle fillers, and the total surface area of ​​the particle fillers per unit mass of the core resin composition calculated by the following formula (1) is 10 m² 2 The core resin composition according to disclosure (1), (2), or (3) is 1 / g or more.

number

[0007] As a result of intensive studies, the inventors of the present invention have found that a resin composition for cores containing a polyvinyl alcohol resin can exhibit high heat resistance by adjusting the melt flow rate (MFR) under the conditions of 230°C and a load of 10 kg. Further, by using such a resin composition for cores, it has been found that a core that does not deform even under high-temperature conditions such as the molding conditions of super engineering plastics can be manufactured, and the present invention has been completed. Regarding the measurement of MFR, it can be measured in accordance with ASTM D-1238 except for the above conditions.

[0008] The melt flow rate (MFR) of the above resin composition for cores under the conditions of 230°C and a load of 10 kg is 35 g / 10 min or less. By adopting the above configuration, high heat resistance can be exhibited, and a core that does not deform even under high-temperature conditions such as the molding conditions of super engineering plastics can be manufactured. The above MFR is preferably 25 g / 10 min or less, more preferably 20 g / 10 min or less, still more preferably 10 g / 10 min or less, and particularly preferably 5 g / 10 min or less. The lower limit of the MFR is not particularly limited, but it is sufficient if it can be molded by a molding machine for molding the core, and it depends on the capacity of the molding machine. The above MFR can be measured by a method in accordance with ASTM D 1238, for example, under the conditions of an initial weight of 7.5 g and a measurement time interval of 0.25 minutes.

[0009] The melt flow rate (MFR) under the conditions of 230°C and a load of 10 kg can be adjusted by the composition such as the weight average molecular weight and saponification degree of the polyvinyl alcohol resin, the blending amount, the type of the particle filler described below, the blending amount, the average particle diameter, the total surface area, other various shaped particle fillers, crosslinking agents, plasticizers, mold release agents, etc. In particular, the contribution of the total surface area of the particle filler is large, and the MFR can be reduced by adjusting the total surface area through the interaction between the polyvinyl alcohol resin and the particle filler. Also, in the following points, it can be adjusted by the type of the filler, the molecular weight of the polyvinyl alcohol resin, and the saponification degree of the polyvinyl alcohol resin. Other various shaped particle fillers include plate-like, needle-like, rugby ball-shaped, fibrous, or higher-order structures (for example, chain-shaped, agglomerate-shaped, layered) in which primary particles are connected.

[0010] <Polyvinyl alcohol resin> The above resin composition for the core contains a polyvinyl alcohol resin. By using the polyvinyl alcohol resin, it can be easily removed from the molded body by immersing it in water or the like.

[0011] The polymerization degree of the above polyvinyl alcohol resin is preferably 4000 or less. When the polymerization degree is 4000 or less, the easy solubility in water can be sufficiently exhibited. The degree of polymerization is more preferably 180 or higher, even more preferably 200 or higher, even more preferably 220 or higher, preferably 3400 or lower, more preferably 2300 or lower, even more preferably 1200 or lower, and even more preferably 900 or lower. The degree of polymerization can be determined, for example, by measuring the polyvinyl acetate before saponification using gel permeation chromatography (GPC) or by measuring the viscosity of the aqueous solution in accordance with JIS K6726.

[0012] The degree of saponification of the above polyvinyl alcohol resin is preferably 72 mol% or more, and preferably 99.8 mol% or less. By setting the range as described above, the solubility in water can be fully exhibited. The degree of saponification is more preferably 80 mol% or more, even more preferably 87 mol% or more, even more preferably 92 mol% or more, particularly preferably 95 mol% or more, more preferably 99.5 mol% or less, and even more preferably 99 mol% or less. The degree of saponification described above can be measured, for example, by a method compliant with JIS K6726. The degree of saponification indicates the proportion of vinyl ester units that are actually converted to vinyl alcohol units out of the vinyl ester units that can be converted to vinyl alcohol units by saponification. The degree of saponification can be controlled, for example, by adjusting the saponification conditions, i.e., the hydrolysis conditions.

[0013] The polyvinyl alcohol resin described above may be an unmodified polyvinyl alcohol resin or a modified polyvinyl alcohol resin. Here, an unmodified polyvinyl alcohol resin means a polyvinyl alcohol resin containing only vinyl ester units and vinyl alcohol units, and a modified polyvinyl alcohol resin means a modified polyvinyl alcohol resin having other constituent units other than vinyl ester units and vinyl alcohol units. Examples of the modified polyvinyl alcohol resins mentioned above include those modified with hydrophilic groups such as sulfonic acid groups, pyrrolidone ring groups, amino groups, and carboxyl groups. These hydrophilic groups also include sodium and potassium salts of the functional groups mentioned above.

[0014] The content of the structural units having a modified group in the above polyvinyl alcohol resin is preferably 1 mol% or more, more preferably 3 mol% or more, even more preferably 5 mol% or more, preferably 20 mol% or less, more preferably 15 mol% or less, and even more preferably 12 mol% or less.

[0015] The weight-average molecular weight (Mw) of the above polyvinyl alcohol resin is preferably 8000 or more, more preferably 9000 or more, even more preferably 10000 or more, even more preferably 11000 or more, particularly preferably 15500 or more, particularly more preferably 17000 or more, preferably 200000 or less, more preferably 150000 or less, even more preferably 100000 or less, even more preferably 50000 or less, and particularly preferably 40000 or less. When two or more types of polyvinyl alcohol resins are included, the weight-average molecular weight (Mw) of the entire polyvinyl alcohol resin is calculated based on the weight-average molecular weight and weight fraction of each resin, and is obtained by summing the values ​​obtained by multiplying the weight-average molecular weight of each polyvinyl alcohol resin by its weight fraction. When two or more types of polyvinyl alcohol resins are included, the weight-average molecular weight (Mw) is preferably 8000 or more, more preferably 9000 or more, even more preferably 10000 or more, even more preferably 11000 or more, particularly preferably 15500 or more, particularly more preferably 17000 or more, preferably 200000 or less, more preferably 150000 or less, even more preferably 100000 or less, even more preferably 50000 or less, and particularly preferably 40000 or less. Furthermore, if a plasticizer is included, the plasticizer and the entire PVA should be included in the calculation of the weight-average molecular weight as the average molecular weight of the entire matrix. The weight-average molecular weight (Mw) is calculated based on the weight-average molecular weight and weight fraction of each resin, as described above, and is obtained by summing the values ​​obtained by multiplying the weight-average molecular weight of each plasticizer and polyvinyl alcohol resin by their weight fraction. When a plasticizer and one or more polyvinyl alcohol resins are included, the weight-average molecular weight (Mw) is preferably 8000 or more, more preferably 9000 or more, even more preferably 10000 or more, even more preferably 14000 or more, particularly preferably 15500 or more, even more particularly preferably 20000 or more, particularly more preferably 22000 or more, preferably 150000 or less, more preferably 100000 or less, even more preferably 50000 or less, and even more preferably 40000 or less.

[0016] The number-average molecular weight (Mn) of the above polyvinyl alcohol resin is preferably 4000 or more, more preferably 4500 or more, even more preferably 5000 or more, preferably 90000 or less, more preferably 60000 or less, and even more preferably 30000 or less.

[0017] The ratio (Mw / Mn) of the weight-average molecular weight (Mw) to the number-average molecular weight (Mn) of the above polyvinyl alcohol resin is preferably 1.0 or higher, more preferably 1.2 or higher, even more preferably 1.4 or higher, even more preferably 1.6 or higher, preferably 5.0 or lower, more preferably 4.0 or lower, even more preferably 3.5 or lower, and even more preferably 2.0 or lower. The weight-average molecular weight (Mw) and number-average molecular weight (Mn) mentioned above can be determined, for example, by gel permeation chromatography (GPC), by GPC measurement of polyvinyl ester before saponification, by GPC measurement of polyvinyl ester obtained by re-esterification of polyvinyl alcohol resin, or by measuring the viscosity of an aqueous solution in accordance with JIS K6726. For example, polystyrene can be used as the standard, and columns such as TSKgel (Tosoh Corporation), PLgel (AMR Corporation), KF-806, and KF-807 (Shodex Corporation) can be used.

[0018] The polyvinyl alcohol resin described above preferably has a viscosity of 30 mPa·s or less when used in a 4% by mass aqueous solution. A viscosity of 30 mPa·s or less when used in a 4% by mass aqueous solution provides the fluidity suitable for injection molding and appropriate water solubility when used as a core. The viscosity of the above 4% by mass aqueous solution is preferably 3 mPa·s or higher, more preferably 5 mPa·s or higher, preferably 20 mPa·s or lower, and more preferably 10 mPa·s or lower. The viscosity of the above 4% by mass aqueous solution can be measured, for example, by a method conforming to JIS K6276 3.11.1 rotational viscometer method.

[0019] The content of the polyvinyl alcohol resin in the above core resin composition is preferably 40% by mass or more, more preferably 50% by mass or more, even more preferably 65% ​​by mass or more, preferably 85% by mass or less, more preferably 75% by mass or less, and even more preferably 70% by mass or less. The above-mentioned polyvinyl alcohol resin may contain multiple types of polyvinyl alcohol resins with different degrees of polymerization, saponification, etc. If the above-mentioned polyvinyl alcohol resin contains multiple types of polyvinyl alcohol resins, the content of the above-mentioned polyvinyl alcohol resin represents the total content of the multiple types of polyvinyl alcohol resins.

[0020] The above polyvinyl alcohol resin is obtained by polymerizing vinyl esters according to conventionally known methods, and then saponifying, i.e., hydrolyzing, the polymer. Generally, alkalis or acids are used as saponification catalysts.

[0021] Examples of the vinyl esters mentioned above include vinyl acetate, vinyl formate, vinyl propionate, vinyl butyrate, vinyl pivalate, vinyl versatate, vinyl laurate, vinyl stearate, and vinyl benzoate.

[0022] The polymerization method for vinyl esters is not particularly limited, but examples include solution polymerization, bulk polymerization, and suspension polymerization.

[0023] Examples of polymerization catalysts used when polymerizing the above vinyl ester include 2-ethylhexyl peroxydicarbonate (Tianjin McEIT's "TrigonoxEHP"), 2,2'-azobisisobutyronitrile (AIBN), t-butyl peroxyneodecanoate, bis(4-t-butylcyclohexyl) peroxydicarbonate, di-n-propyl peroxydicarbonate, di-n-butyl peroxydicarbonate, di-cetyl peroxydicarbonate, and di-s-butyl peroxydicarbonate. Only one of these polymerization catalysts may be used, or two or more may be used in combination.

[0024] The polyvinyl alcohol resin described above may also be a saponified polymer of a vinyl ester and another unsaturated monomer. Other unsaturated monomers include monomers other than the vinyl esters mentioned above that have an unsaturated double bond such as a vinyl group. Specifically, examples include olefins, (meth)acrylic acid and its salts, (meth)acrylic acid esters, unsaturated acids other than (meth)acrylic acid, their salts and esters, (meth)acrylamides, N-vinylamides, vinyl ethers, nitriles, vinyl halides, allyl compounds, vinylsilyl compounds, isopropenyl acetate, sulfonic acid group-containing compounds, amino group-containing compounds, and the like.

[0025] Examples of olefins include ethylene, propylene, 1-butene, and isobutene. Examples of (meth)acrylic acid esters include methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, i-propyl (meth)acrylate, n-butyl (meth)acrylate, and 2-ethylhexyl (meth)acrylate. Examples of unsaturated acids other than (meth)acrylic acid, their salts and esters include maleic acid and its salts, maleic acid esters, itaconic acid and its salts, itaconic acid esters, methylenemalonic acid and its salts, and methylenemalonic acid esters. Examples of (meth)acrylamides include acrylamide, n-methylacrylamide, N-ethylacrylamide, and N,N-dimethylacrylamide. Examples of N-vinylamides include N-vinylpyrrolidone. Examples of vinyl ethers include methyl vinyl ether, ethyl vinyl ether, n-propyl vinyl ether, i-propyl vinyl ether, and n-butyl vinyl ether. Examples of nitriles include (meth)acrylonitrile. Examples of vinyl halides include vinyl chloride and vinylidene chloride. Examples of allyl compounds include allyl acetate and allyl chloride. Examples of vinylsilyl compounds include vinyltrimethoxysilane. Examples of sulfonic acid group-containing compounds include (meth)acrylamide alkanesulfonic acids such as (meth)acrylamidepropanesulfonic acid and their salts, olefin sulfonic acids such as ethylenesulfonic acid, allylsulfonic acid, and metaallylsulfonic acid, and their salts. Examples of amino group-containing compounds include allylamine, polyoxyethylene allylamine, polyoxypropylene allylamine, polyoxyethylene vinylamine, and polyoxypropylene vinylamine.

[0026] <Particle filler> The above-mentioned core resin composition preferably further contains particulate fillers. By including particulate fillers, heat resistance can be further enhanced.

[0027] In the above-mentioned core resin composition, the total surface area of ​​the particle filler per unit mass of the core resin composition, calculated by the following formula (1), is 10 m². 2 It is preferable that the amount is 1 / g or more.

number

Number

[0028] Furthermore, the total surface area of ​​the particle filler per unit mass can be adjusted by the average particle diameter, density, and amount of particle filler used. Furthermore, while the surface area of ​​the above-mentioned particle filler is calculated from the average particle diameter, density, and amount of primary particles, the particle shape is not necessarily limited to spherical. Other shapes include, for example, plate-like, needle-like, rugby-shaped, hollow, and porous shapes, and these may also have higher-order structures formed by multiple connected or overlapping particles.

[0029] The average particle diameter of the above particle filler is preferably 1 nm or more, and preferably 100 nm or less. By setting it within this range, the surface area of ​​the particle filler in the core resin composition can be kept within a certain range, and the heat resistance required for the resin composition can be imparted. The above average particle diameter is more preferably 2 nm or more, even more preferably 3 nm or more, even more preferably 4 nm or more, more preferably 70 nm or less, even more preferably 50 nm or less, and even more preferably 30 nm or less. Furthermore, the above average particle diameter is particularly preferably 5 nm or more, and particularly preferably 29 nm or less. By setting it within the above range, the particle filler and polyvinyl alcohol resin can be easily kneaded and mixed. The average particle size of the above-mentioned particle filler can be measured, for example, by a particle size distribution analyzer.

[0030] The density of the above particle filler is 0.5 g / cm³. 3 The above is preferable, 0.7 g / cm³ 3 The above is more preferable, 0.9 g / cm³ 3 The above is even more preferable, 1.1 g / cm³ 3 The above is particularly preferred, 22 g / cm³ 3 The following is preferable: 13 g / cm³ 3 The following is more preferable: 6 g / cm³ 3 The following is even more preferable: 4.5 g / cm³ 3 The following are particularly preferable. The above density can be measured, for example, by an electronic hydrometer. Regarding the density of the particle filler, even if the particle filler is a hollow particle or a porous particle, the particle density is adopted that takes into account the volume including cavities and pores inside the particle.

[0031] Examples of materials for the above-mentioned particle filler include metals, metal oxides, ceramics, carbon materials, and glass. Furthermore, resin particles with a melting point of 200°C or higher can also be used as the particle filler. Examples of the above metal oxides include titanium oxide, aluminum oxide, calcium oxide, lithium oxide, molybdenum oxide, vanadium oxide, zinc oxide, nickel oxide, cesium oxide, and iron oxide. Other examples include boron nitride, aluminum nitride, gold, silver, copper, platinum, palladium, and silicon carbide. Examples of the carbon materials mentioned above include carbon black, graphite, and diamond. Among these, titanium dioxide and carbon black are preferred from the standpoint of cost performance and availability. Examples of resins with a melting point of 200°C or higher include polyethylene terephthalate, polyamide, aromatic polyamide (aramid), polyimide, and polyether ether ketone (PEEK).

[0032] The content of the particle filler in the above-mentioned core resin composition is preferably 5% by mass or more, and preferably 70% by mass or less. This range improves heat resistance. The content of the above-mentioned particle filler is more preferably 10% by mass or more, even more preferably 15% by mass or more, even more preferably 19% by mass or more, more preferably 50% by mass or less, even more preferably 40% by mass or less, and even more preferably 35% by mass or less.

[0033] <Crosslinking agent> The resin composition for the core described above may contain a crosslinking agent. Examples of the crosslinking agents mentioned above include oxoacids, boron compounds, divalent or higher metal hydroxides, diamines, and polyamines. Alternatively, metal salts of the above acids may also be used.

[0034] Examples of the oxoacids mentioned above include boric acid, silicic acid, phosphorous acid, polycarboxylic acid, and hydroxycarboxylic acid. The polycarboxylic acid is preferably an acid having two or more carboxyl groups, and the hydroxycarboxylic acid is preferably an acid having two or more carboxyl groups. Metal salts of the acids may also be used. Among the oxoacids, boric acid is particularly preferred. Using boric acid allows for a temporary protective material that has sufficient water resistance during processing but can be easily removed with hot water when removal is necessary. Examples of boric acid include orthoboric acid, metaboric acid, and tetraboric acid. In addition to boric acid, which was listed as an oxoacid above, other boron compounds include, for example, salts of boric acid. Furthermore, the boron compounds may be hydrates. Examples of salts of boric acid include borax, alkali metal salts such as sodium salt and potassium salt, alkaline earth metal salts such as calcium salt and magnesium salt, aluminum salt, and organic amine salts such as triethylamine, triethanolamine, morpholine, piperazine, and pyrrolidine. Among these, boric acid and borax are preferred.

[0035] Examples of the polycarboxylic acids mentioned above include oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, and poly(meth)acrylic acid. Among these, succinic acid is preferred. Examples of the hydroxycarboxylic acids mentioned above include glycolic acid, lactic acid, tartaric acid, glyceric acid, hydroxybutyric acid, malic acid, tartaric acid, citomalic acid, citric acid, isocitric acid, leucic acid, mevalonic acid, pantoic acid, ricinoleic acid, ricineradicic acid, cerebronic acid, quinic acid, shikimic acid, hydroxybenzoic acid, salicylic acid, creosoteic acid, vanillic acid, syringic acid, pyrocatechuic acid, resorcylic acid, protocatechuic acid, gentisic acid, orceric acid, gallic acid, mandelic acid, benzyl acid, atrolactinic acid, melilotic acid, floretic acid, coumaric acid, umbellic acid, caffeic acid, ferulic acid, sinapic acid, and hydroxystearic acid. Among these, malic acid and citric acid are preferred. Examples of the above-mentioned metal hydroxides with a valency of 2 or higher include calcium hydroxide, magnesium hydroxide, barium hydroxide, aluminum hydroxide, iron hydroxide, zinc hydroxide, manganese hydroxide, and copper hydroxide. The above crosslinking agents may be used individually or in combination of two or more. In particular, boron compounds are preferred as the crosslinking agent from the viewpoint of both imparting heat resistance and maintaining water solubility, and boric acid is more preferred.

[0036] The content of the crosslinking agent in the above-mentioned core resin composition is preferably 0.01% by mass or more, and preferably 2% by mass or less. By keeping it within this range, an appropriate crosslinked structure can be imparted, and heat resistance can be improved.

[0037] <Easy-to-remove agent> The resin composition for the core described above may contain an easy-release agent. The inclusion of an easy-release agent makes it easier to remove the core resin from the molded product.

[0038] As the above-mentioned easy-release agent, for example, a glycerin fatty acid ester compound can be used. Examples of the glycerol fatty acid ester compounds mentioned above include monoglyceride stearate, monoglyceride oleate, and diglyceride laurate.

[0039] The content of the release agent in the above-mentioned core resin composition is preferably 0.1% by mass or more, and preferably 2% by mass or less. By setting it within this range, the surface smoothness of the inside of the resulting molded article can be sufficiently improved. The content of the above-mentioned peeling agent is more preferably 0.2% by mass or more, even more preferably 0.5% by mass or more, more preferably 1.6% by mass or less, and even more preferably 1.1% by mass or less.

[0040] <Plasticizer> The resin composition for the core described above may contain a plasticizer, provided that it does not exceed the limits of achieving the present invention. The inclusion of plasticizers can improve moldability.

[0041] Examples of the plasticizers mentioned above include polyhydric alcohols. Examples of the polyhydric alcohols mentioned above include ethylene glycol, glycerin, propylene glycol, diethylene glycol, diglycerin, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, trimethylolpropane, polyethylene glycol, and polypropylene glycol.

[0042] From the viewpoint of making it easier to control the MFR of the resin composition for the core within the range described above, it is preferable that the above-mentioned plasticizer is not included. The content of the plasticizer in the resin composition for the core described above is preferably 0.1% by mass or more, and preferably 10% by mass or less. This range allows for good extrusion and injection moldability and good water solubility. The content of the plasticizer is more preferably 0.5% by mass or more, even more preferably 1% by mass or more, even more preferably 7% by mass or less, and even more preferably 5% by mass or less.

[0043] <Other> The resin composition for the core described above may also contain other additives such as antioxidants, colorants, defoamers, UV absorbers, and preservatives.

[0044] As antioxidants, known antioxidants such as phenolic antioxidants, phosphorus-based antioxidants, amine-based antioxidants, and sulfur-containing antioxidants can be used. Furthermore, antioxidants containing both phenolic and phosphorus-based functional groups within a single molecule can also be used.

[0045] Examples of the above phenolic antioxidants include acrylate compounds such as 2-t-butyl-6-(3-t-butyl-2-hydroxy-5-methylbenzyl)-4-methylphenyl acrylate and 2,4-di-t-amyl-6-(1-(3,5-di-t-amyl-2-hydroxyphenyl)ethyl)phenyl acrylate, 2,6-di-t-butyl-4-methylphenol, 2,6-di-t-butyl-4-ethylphenol, octadecyl-3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate, and 2,2 '-Methylene-bis(4-methyl-6-t-butylphenol), 4,4'-Butylidene-bis(4-methyl-6-t-butylphenol), 4,4'-Butylidene-bis(6-t-butyl-m-cresol), 4,4'-Thiobis(3-methyl-6-t-butylphenol), Bis(3-cyclohexyl-2-hydroxy-5-methylphenyl)methane, 3,9-Bis(2-(3-(3-t-butyl-4-hydroxy-5-methylphenyl)propionyloxy)-1,1-dimethylethyl)-2,4,8,10-tetraoxy Suspiro[5,5]undecane, 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl)butane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, tetrakis(methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate)methane, or alkyl-substituted phenol compounds such as triethylene glycol bis(3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate), 6-(4-H Examples include triazine group-containing phenolic compounds such as droxy-3,5-di-t-butylanilino)-2,4-bis-octylthio-1,3,5-triazine, 6-(4-hydroxy-3,5-dimethylanilino)-2,4-bis-octylthio-1,3,5-triazine, 6-(4-hydroxy-3-methyl-5-t-butylanilino)-2,4-bis-octylthio-1,3,5-triazine, or 2-octylthio-4,6-bis-(3,5-di-t-butyl-4-oxyanilino)-1,3,5-triazine.

[0046] Examples of the phosphorus-based antioxidants mentioned above include triphenyl phosphite, diphenylisodecyl phosphite, phenyl diisodecyl phosphite, tris(nonylphenyl) phosphite, tris(dinonylphenyl) phosphite, tris(2-t-butyl-4-methylphenyl) phosphite, tris(cyclohexylphenyl) phosphite, 2,2-methylenebis(4,6-di-t-butylphenyl)octyl phosphite, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 10-(3,5-di-t-butyl-4-hydroxybenzyl)-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, Alternatively, examples include monophosphite compounds such as 10-decyloxy-9,10-dihydro-9-oxa-10-phosphaphenanthrene, diphosphite compounds such as 4,4'-butylidene-bis(3-methyl-6-t-butylphenyl-di-tridecyl phosphite), 4,4'-isopropylidene-bis(phenyl-di-alkyl(C12~C15) phosphite), 4,4'-isopropylidene-bis(diphenylmonoalkyl(C12~C15) phosphite), 1,1,3-tris(2-methyl-4-di-tridecyl phosphite-5-t-butylphenyl)butane, or tetrakis(2,4-di-t-butylphenyl)-4,4'-biphenylene phosphite.

[0047] Antioxidants possessing both phenolic and phosphorus functional groups within a single molecule are not particularly limited, but examples include phosphite ester compounds having a phenolic skeleton. Specifically, these include 6-[3-(3-t-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,10-tetra-t-butyldibenz[d,f][1,3,2]dioxaphosfepine, 2,10-dimethyl-4,8-di-t-butyl-6-[3-(3,5-di-t-butyl-4-hydroxyphenyl)propoxy]-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, and 2,4,8,10-tetra-t-butyl-6-[3-(3,5-di-t-butyl-4-hydroxyphenyl )propoxy]dibenzo[d,f][1,3,2]dioxaphosfepine, 2,4,8,10-tetra-t-pentyl-6-[3-(3,5-di-t-butyl-4-hydroxyphenyl)propoxy]-12-methyl-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, 2,10-dimethyl-4,8-di-t-butyl-6-[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyloxy]-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, 2,4,8,1 0-Tetra-t-pentyl-6-[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyloxy]-12-methyl-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, 2,4,8,10-Tetra-t-butyl-6-[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyloxy]-dibenzo[d,f][1,3,2]dioxaphosfepine, 2,10-dimethyl-4,8-di-t-butyl-6-(3,5-di-t-butyl-4-hydroxybenzoyl Xy)-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, 2,4,8,10-tetra-t-butyl-6-(3,5-di-t-butyl-4-hydroxybenzoyloxy)-12-methyl-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, 2,10-dimethyl-4,8-di-t-butyl-6[3-(3-methyl-4-hydroxy-5-t-butylphenyl)propoxy]-12H-dibenzo[d,g][1,3,2]dioxaphosphosine, 2,10-di-t-pentyl-4,Examples include 8-di-t-butyl-6[3-(3,5-di-t-butyl-4-hydroxyphenyl)propoxy]-12H-dibenzo[d,g][1,3,2]dioxaphosphosine and 2,4,8,10-tetra-t-butyl-6-[2,2-dimethyl-3-(3-t-butyl-4-hydroxy-5-methylphenyl)propoxy]-dibenzo[d,f][1,3,2]dioxaphosfepine.

[0048] The content of the antioxidant in the above-mentioned core resin composition is preferably 0.2% by mass or more, more preferably 0.4% by mass or more, even more preferably 0.7% by mass or more, preferably 2% by mass or less, more preferably 1.5% by mass or less, and even more preferably 1.2% by mass or less.

[0049] The above-mentioned core resin composition can be obtained by mixing, for example, polyvinyl alcohol resin, particle fillers, and other additives such as release agents, plasticizers, and antioxidants as needed. The method for mixing the above components is not particularly limited, but examples include mixing using a known kneading apparatus or using an extrusion molding machine. Alternatively, mixing may be done within the cylinder of an injection molding machine.

[0050] The shape of the resin composition for the core described above is not particularly limited and may be, for example, in the form of pellets, powder, etc.

[0051] A core can be produced by molding the above-mentioned core resin composition. A core made using the above-mentioned core resin composition is also one of the present inventions. The above molding method is not particularly limited, but examples include injection molding.

[0052] The above core can be used to manufacture a molded body. The material that is molded together with the core to form a composite is not particularly limited, but since the resin composition for the core has particularly excellent heat resistance, it is possible to prevent deformation even when using super engineering plastics that are molded at high temperatures.

[0053] Examples of the above-mentioned super engineering plastics include highly heat-resistant plastics such as polyphenylene sulfide (PPS), polyether ether ketone (PEEK), liquid crystal polymer (LCP), polyimide (PI), polyamide imide (PAI), polyetherimide (PEI), polyphenyl sulfone (PPSU), polysulfone (PSF), polyethersulfone (PES), polyarylate (PAR), polyvinylidene fluoride (PVDF), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), tetrafluoroethylene-ethylene copolymer (ETFE), polychlorotrifluoroethylene (PCTFE), and chlorotrifluoroethylene-ethylene copolymer (ECTFE). By using the above-mentioned super engineering plastic, it is possible to obtain molded articles with excellent heat resistance, durability, and mechanical strength.

[0054] By removing the core from the above composite, a molded body having a hollow portion can be obtained. One method for removing the core mentioned above is to immerse the complex in water or hot water.

[0055] The shape of the molded body described above may be straight, or it may be L-shaped, S-shaped, T-shaped, or various other shapes. For example, L-shaped, S-shaped, or similar molded bodies can be used as joints. Examples of molded articles having the above-mentioned hollow portion include automotive piping fittings and electronic equipment housings. [Effects of the Invention]

[0056] According to the present invention, it is possible to provide a resin composition for cores that exhibits high heat resistance and can be used to manufacture cores that do not deform even under the molding conditions of super engineering plastics. Furthermore, it is possible to provide cores made using this resin composition. [Modes for carrying out the invention]

[0057] The embodiments of the present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples.

[0058] (Synthesis Example 1) [PVA1 (Saponification degree 98.4 mol%, weight-average molecular weight 15000)] In a reactor equipped with a thermometer, stirrer, and condenser, 2000 parts by weight of vinyl acetate monomer and 200 parts by weight of methanol were added. Nitrogen gas was blown in for 30 minutes to purge the reactor with nitrogen, and then the reactor was heated to 60°C for 30 minutes. Next, 456.5 parts by weight of 2,2'-azobisisobutyronitrile, a polymerization initiator, was added, and the reaction was carried out at 60°C for 4 hours. After the reaction time was complete, the reaction mixture was cooled. After cooling... 1 The polymerization rate was measured by 1H-NMR, and it was found to be 99%. Next, under reduced pressure, the remaining vinyl acetate monomer was removed along with methanol, with methanol being added as needed, to obtain a methanol solution containing 50% by weight of polyvinyl acetate. To this methanol solution, a methanol solution of sodium hydroxide was added to a concentration of 0.07 mol% sodium hydroxide relative to vinyl acetate, and saponification was carried out at 40°C. The resulting solid was pulverized, washed with methanol, and dried to obtain PVA1. The degree of saponification of the obtained PVA1 was measured according to the method in accordance with JIS K6726. The weight-average molecular weight of the polyvinyl alcohol resin was determined by gel permeation chromatography using an LF-804 column (SHOKO Co., Ltd.) to measure the weight-average molecular weight in terms of polystyrene. As a result, the degree of saponification and weight-average molecular weight were 98.4 mol% and 15000, respectively. The viscosity of the 4% by mass aqueous solution of the obtained polyvinyl alcohol resin was measured using a rotational viscometer (TVB-10, manufactured by Toki Sangyo Co., Ltd.) in accordance with the rotational viscometer method specified in JIS K6276 3.11.1, and was found to be 3.5 mPa·s.

[0059] (Synthesis Example 2) [PVA2 (saponification degree 88.0 mol%, weight-average molecular weight 30000)] Except for changing the amount of 2,2'-azobisisobutyronitrile added to 4.2 parts by weight and the amount of methanol solution of sodium hydroxide added to 0.02 mol% of the sodium hydroxide relative to vinyl acetate, the same procedure as in Synthesis Example 1 was performed to obtain PVA2 with a degree of saponification, weight-average molecular weight, and viscosity of 88.0 mol%, 30000, and 5.3 mPa·s, respectively.

[0060] (Synthesis Example 3) [PVA3 (Saponification degree 98.4 mol%, weight-average molecular weight 22000)] Except for changing the amount of 2,2'-azobisisobutyronitrile added to 22.9 parts by weight and the amount of methanol solution of sodium hydroxide added to 0.07 mol% of the sodium hydroxide relative to vinyl acetate, the same procedure as in Synthesis Example 1 was performed to obtain PVA3 with a degree of saponification, weight-average molecular weight, and viscosity of 98.4 mol%, 22000, and 6.9 mPa·s, respectively.

[0061] The following were used as particle fillers, antioxidants, plasticizers, and release agents other than polyvinyl alcohol resin. Titanium dioxide 1: Ishihara Sangyo Co., Ltd. TTO-51(A), average particle size 20 nm, density 3.7 g / cm³ 3 Titanium dioxide 2: PF-690, manufactured by Ishihara Sangyo Co., Ltd., average particle size 210 nm, density 4.0 g / cm³ 3 Carbon Black 1: TOKABLACK #5500 manufactured by Tokai Carbon Co., Ltd., average particle size 25nm, density 1.9g / cm³ 3 Carbon Black 2: Tokai Carbon Co., Ltd. seast TA, average particle size 122nm, density 1.9g / cm³ 3 Antioxidant: Sumitomo Chemical Co., Ltd., SumiLizer GP Plasticizer: Diglycerin S (Chemical name: Diglycerin, Molecular weight: 166.17), manufactured by Sakamoto Pharmaceutical Co., Ltd. Easy stripping agent: Monoglyceride stearate, manufactured by Kao Corporation, Electro Stripper TS-5 The average particle size of the particle filler was taken from the catalog value. The density was measured using a Shimadzu AccuPic II 1345.

[0062] (Example 1) Polyvinyl alcohol resin, particle filler, and antioxidant were mixed according to the formulations shown in Table 1, and pelletized using a Toshiba Machine Co., Ltd. processing machine "TEM26SX" at an extrusion temperature of 190°C to 210°C to obtain pellets of the core resin composition.

[0063] (Examples 2-6) Polyvinyl alcohol resin, particle filler, antioxidant, and release agent were mixed in the proportions shown in Table 1, and pellets of the core resin composition were obtained in the same manner as in Example 1.

[0064] (Comparative Examples 1-2) Pellet core resin compositions were obtained in the same manner as in Example 1, except that no particle fillers were added and the polyvinyl alcohol resin and antioxidant were mixed to the formulation shown in Table 1.

[0065] (Comparative Examples 3-6) Polyvinyl alcohol resin, particle filler, antioxidant, and plasticizer were mixed according to the formulations shown in Table 1, and pellets of the core resin composition were obtained in the same manner as in Example 1.

[0066] (Evaluation method) The obtained core resin compositions were evaluated by the following method. The results are shown in Table 1.

[0067] (1) Total surface area of ​​particle fillers per unit mass of core resin composition (m²) 2 / g) The total surface area of ​​particle fillers per unit mass of the core resin composition was calculated based on the following formula (1).

number

[0068] (2) Melt Flow Rate (MFR) The melt flow rate (MFR) of the core resin composition was measured using a Melt Index Tester No. 120-FWP (manufactured by Yasuda Seiki Seisakusho Co., Ltd.) in accordance with ASTM D 1238, under the following conditions: initial weight of 7.5 g of core resin composition, temperature of 230°C, load of 10 kg, and measurement time interval of 0.25 minutes.

[0069] (3) Heat resistance A 10mm diameter SUS304 steel ball was heated to 300°C and placed on a plate-shaped resin composition at room temperature (20°C) for 1 minute. The diameter of the resulting indentation (mm) was measured and evaluated as follows: less than 2mm was marked "◎", 2mm to less than 3mm was marked "〇", and 3mm or more was marked "×".

[0070] [Table 1] [Industrial applicability]

[0071] According to the present invention, it is possible to provide a resin composition for cores that exhibits high heat resistance and can be used to manufacture cores that do not deform even under the molding conditions of super engineering plastics. Furthermore, it is possible to provide cores made using this resin composition.

Claims

1. Contains polyvinyl alcohol resin, A core resin composition having a melt flow rate (MFR) of 15.7 g / 10 min or less under conditions of 230°C and a 10 kg load.

2. The core resin composition according to claim 1, wherein the polyvinyl alcohol resin has a weight-average molecular weight (Mw) of 200,000 or less and a degree of saponification of 72% or more and 99.8% or less.

3. The core resin composition according to claim 1 or 2, wherein the polyvinyl alcohol resin has a viscosity of 30 mPa·s or less when used in a 4% by mass aqueous solution.

4. Furthermore, the resin composition for the core contains particle fillers, and the total surface area of ​​the particle fillers per unit mass of the core resin composition, calculated by the following formula (1), is 10 m². ２ The core resin composition according to claim 1 or 2, wherein the amount is 1 / g or more. [Math 1] A: Total surface area of ​​particle fillers per unit mass of core resin composition (m²) ２ / g) B: Average particle diameter (m) of particle fillers D: Content of particle fillers in the core resin composition (mass%) E: Density of particle filler (g / m³) ３ )

5. The core resin composition according to claim 4, wherein the average particle size of the particle filler is 1 nm or more and 100 nm or less.

6. The core resin composition according to claim 4, wherein the content of the particle filler is 5% by mass or more and 70% by mass or less.

7. The core resin composition according to claim 1 or 2, comprising 0.1% by mass or more and 2% by mass or less of an easy-release agent.

8. The core resin composition according to claim 7, wherein the easily removable agent is a glycerin fatty acid ester compound.

9. The core resin composition according to claim 8, wherein the glycerin fatty acid ester compound is at least one selected from the group consisting of monoglyceride stearate, monoglyceride oleate, and diglyceride laurate.

10. A resin composition for cores according to claim 1 or 2, which is in the form of pellets.

11. A core made using the core resin composition according to claim 1 or 2.

Images