Stretched films, metal laminated films, and film capacitors

Abstract

The present invention provides a stretched film that has high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and moreover, exhibits little change in dielectric breakdown strength in high-temperature environments compared to room temperature (e.g., 25°C), thereby improving the long-term durability of capacitor elements. The present invention relates to a stretched film containing a polypropylene resin, The following formula (1A) can be derived from the birefringence value. ΔP = (ΔNxz + ΔNyz) / 2 (1A) (In equation (1A), ΔNxz represents the birefringence value in the x-axis direction relative to the thickness direction (z-axis direction), and ΔNyz represents the birefringence value in the y-axis direction relative to the thickness direction (z-axis direction).) The orientation coefficient ΔP, represented by the formula, is 0.007 or more and 0.0125 or less. Alternatively, the present invention relates to a stretched film containing a polypropylene resin, wherein the in-plane birefringence value ΔNyx is 0.009 or more and 0.016 or less.

Description

[Technical Field]

[0001] The present invention relates to a stretched film formed from a polypropylene resin, a metal laminated film having the stretched film, and a film capacitor. [Background technology]

[0002] Stretched films primarily composed of polypropylene are used in film capacitor applications due to their excellent electrical properties. In electronic and electrical equipment, film capacitors made from stretched polypropylene are used as, for example, high-voltage capacitors, various switching power supplies, filter capacitors for converters and inverters, and smoothing capacitors. Film capacitors are also increasingly used in automobiles, such as electric vehicles and hybrid vehicles, where demand has been growing in recent years, for example, in inverters and converters that control drive motors.

[0003] Film capacitors, particularly automotive film capacitors, are increasingly being used in high-temperature environments. For example, in devices that control automotive drive motors (inverters, converters, etc.), the use of highly heat-resistant semiconductors (such as silicon carbide semiconductors) has increased in recent years. Consequently, capacitors used in these devices are required to have high heat resistance, such as 120°C or higher, preferably 130°C or higher. Conventional capacitors using polypropylene film are said to have an upper limit of operating temperature of about 110°C, and it is extremely difficult to stably maintain electrical insulation in high-temperature environments exceeding this.

[0004] One example of a resin film with high heat resistance is a film made of a resin composition containing a polyolefin mainly composed of polypropylene and a hydrogenated block copolymer, which exhibits excellent heat resistance and, in particular, excellent water vapor impermeability (Patent Document 1). [Prior art documents] [Patent Documents]

[0005] [Patent Document 1] Japanese Patent Publication No. 2014-37532 [Overview of the Initiative] [Problems that the invention aims to solve]

[0006] Polypropylene-based resin films tend to exhibit a decline in physical properties, such as reduced rigidity and decreased electrical insulation, as their operating temperature increases. In this regard, stretching a polypropylene-based resin film in at least one direction, preferably two directions, improves rigidity and electrical insulation, allowing these properties to be maintained even in high-temperature regions exceeding 110°C. However, at operating temperatures above 120°C, and even above 130°C, maintaining rigidity and electrical insulation becomes difficult even with a stretched film, and improving the long-term durability of the capacitor element also becomes challenging.

[0007] The present invention has been made in view of the above, and aims to provide a stretched film that has high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and moreover, the change in dielectric breakdown strength in high-temperature environments compared to room temperature (e.g., 25°C) is small, thereby improving the long-term durability of capacitor elements. The present invention also aims to provide a metal laminated film and a film capacitor comprising the stretched film. [Means for solving the problem]

[0008] The inventors, through diligent research to achieve the above objectives, discovered that the objectives can be achieved by adjusting the birefringence value to a specific range, and thus completed the present invention. Furthermore, the inventors, through diligent research to achieve the above objectives, discovered that the stress characteristics of the stretched film contribute to the dielectric breakdown strength at high temperatures and long-term durability, and discovered that the above objectives can be achieved by appropriately adjusting these stress characteristics, thus completing the present invention.

[0009] In other words, the present invention encompasses, for example, the subject matter described in the following sections. Item 1 A stretched film containing a polypropylene resin, The following formula (1A) can be derived from the birefringence value. ΔP = (ΔNxz + ΔNyz) / 2 (1A) (In equation (1A), ΔNxz represents the birefringence value in the x-axis direction relative to the thickness direction (z-axis direction), and ΔNyz represents the birefringence value in the y-axis direction relative to the thickness direction (z-axis direction).) A stretched film in which the orientation coefficient ΔP, represented by [formula], has a value of 0.007 or greater and 0.0125 or less. Section 2 A stretched film containing a polypropylene resin, A stretched film having an in-plane birefringence value ΔNyx of 0.009 or greater and 0.016 or less. Section 3 A stretched film containing a polypropylene resin, When the stress at 100% elongation in the film flow direction measured at 23°C is defined as F100(23), and the stress at 100% elongation in the flow direction measured at 135°C is defined as F100(135), then the following equation (1) F100(135) / F100(23)>0.13 (1) A stretched film that satisfies the requirements. Section 4 A stretched film containing a polypropylene resin, Let F(23M) be the stress at the point of maximum stress in the film flow direction measured at 23℃. Let F(23T) be the stress at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 23°C, and let F(135M) be the stress at the point of maximum stress in the film flow direction, measured at 135°C. When the stress at the point of maximum stress in a direction perpendicular to the film flow direction, measured at 135°C, is defined as F(135T), The following formula (2) {F(135M)+F(135T)} / {F(23M)+F(23T)}>0.31 (2) A stretched film that satisfies the requirements. Item 5 The stretched film according to any one of Items 1 to 4, which has a peak of loss tangent tanδ in a region of 140°C or higher in the temperature dispersion data with respect to the TD direction at a frequency of 1 Hz obtained from dynamic viscoelasticity measurement. Item 6 The stretched film according to any one of Items 1 to 4, in which the loss tangent tanδ at 100°C is 0.15 or less in the temperature dispersion data with respect to the TD direction at a frequency of 1 Hz obtained from dynamic viscoelasticity measurement. Item 7 The stretched film according to Item 1 or 2, in which the crystallite size determined by the Scherrer's equation based on the half-width of the (110) plane derived from isotactic polypropylene in X-ray diffraction intensity measurement is 120 Å or more. Item 8 In infrared absorption spectrum measurement, having at least one of an absorption peak in the range of 880 to 890 cm -1 and a shoulder peak due to absorption around 1450 cm -1 The stretched film according to Item 1 or 2. Item 9 The stretched film according to Item 3 or 4, in which the heat shrinkage rate in the film flow direction measured at 140°C is 1.0% or more and 6.0% or less, and the heat shrinkage rate in the direction orthogonal to the film flow direction is 4.0% or less. Item 10 The polypropylene-based resin is 80% by mass or more and 99% by mass or less of an isotactic polypropylene resin, and 1% by mass or more and 20% by mass or less of a polymer having an alicyclic structure The stretched film according to any one of Items 1 to 4. Item 11 The stretched film according to Item 10, in which the polymer having an alicyclic structure contains two or more polymers having different glass transition temperatures. Item 12 The stretched film according to claim 10, wherein the polymer having the alicyclic structure comprises polymer B1 having an alicyclic structure with a glass transition temperature of 133°C or more and 155°C or less, and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C or more and less than 133°C. Item 13 The stretched film according to claim 12, wherein the mass ratio B2 / B1 of polymer B2 to polymer B1 is less than 0.85. Section 14 The stretched film according to claim 10, wherein the polymer having the alicyclic structure is hydrogenated polystyrene. Section 15 The aforementioned hydride polystyrene has an atactic structure, The stretched film according to claim 14, having a hydrogenation rate of 95% or more. Section 16 A stretched film according to any one of items 1 to 4, having a thickness of 1.8 μm or more and 10 μm or less, and a total light transmittance of 80% or more. Section 17 A metal laminated film having a metal layer on one or both sides of a stretched film as described in any one of items 1 to 4. Section 18 A film capacitor comprising the metal laminated film described in item 17. [Effects of the Invention]

[0010] The stretched film of the present invention has high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and moreover, the change in dielectric breakdown strength in high-temperature environments compared to room temperature (e.g., 25°C) is small, which can improve the long-term durability of capacitor elements in high-temperature environments. [Brief explanation of the drawing]

[0011] [Figure 1] The results of dynamic viscoelasticity measurements of stretched film 1 obtained in the examples and comparative examples are shown, illustrating the temperature dispersion data of the stretched film in the TD direction at a frequency of 1 Hz, with the X axis representing temperature, the first Y axis representing the logarithm of the storage modulus E' (logE'(Pa)), and the second Y axis representing the loss tangent tanδ. [Figure 2] The results of the infrared absorption spectrum of stretched film 1 are shown, with (a) showing the range of 850-950 cm⁻¹ in the infrared absorption spectrum measurement, and (b) showing the range of 1400-1500 cm⁻¹. [Figure 3] The results of dynamic viscoelasticity measurements of the stretched film 2 obtained in the examples and comparative examples are shown, illustrating the temperature dispersion data of the stretched film in the TD direction at a frequency of 1 Hz, with the X axis representing temperature, the first Y axis representing the logarithm of the storage modulus E' (logE'(Pa)), and the second Y axis representing the loss tangent tanδ. [Modes for carrying out the invention]

[0012] Embodiments of the present invention will be described in detail below. In this specification, the expressions "containing" and "including" include the concepts of "containing," "including," "substantially consisting of," and "consisting only of."

[0013] In the numerical ranges described stepwise in this specification, the upper or lower limit of a numerical range in one step can be arbitrarily combined with the upper or lower limit of a numerical range in another step. In the numerical ranges described in this specification, the upper or lower limit of a numerical range may be replaced with values ​​shown in the examples or values ​​that can be uniquely derived from the examples. Furthermore, in this specification, numbers connected by "~" mean a numerical range that includes the numbers before and after "~" as the lower and upper limits.

[0014] 1. Stretched film The stretched film of the present invention includes the following stretched film A and stretched film B, as well as stretched film C and stretched film D.

[0015] (Stretched films A and B) First, the stretched films A and B of the present invention will be described. Stretched films A and B are as follows: Stretched film A: For materials containing polypropylene resin, the following formula (1A) can be used to determine the birefringence value. ΔP = (ΔNxz + ΔNyz) / 2 (1A) The value of the orientation coefficient ΔP, represented by [formula], is between 0.007 and 0.0125. Stretched film B: The material contains a polypropylene resin, and its in-plane birefringence value ΔNyx is between 0.009 and 0.016. In equation (1A), ΔNxz represents the birefringence value in the x-axis direction relative to the thickness direction (z-axis direction), and ΔNyz represents the birefringence value in the y-axis direction relative to the thickness direction (z-axis direction). More precisely, ΔNxz can be defined as the difference obtained by subtracting the refractive index in the thickness direction (Nz) from the refractive index in the x-axis direction (Nx).

[0016] The stretched film A of the present invention can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and specifically, it has high dielectric breakdown strength even in high-temperature environments of 140°C. Moreover, the stretched film A of the present invention shows little change in dielectric breakdown strength in high-temperature environments (e.g., 140°C) compared to room temperature (e.g., 25°C). In addition, the stretched film A of the present invention can improve the long-term durability of capacitor elements in high-temperature environments.

[0017] Similarly, the stretched film B of the present invention can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and specifically, it has high dielectric breakdown strength even in high-temperature environments of 140°C. Moreover, the stretched film B of the present invention shows little change in dielectric breakdown strength in high-temperature environments (e.g., 140°C environment) compared to room temperature (e.g., 25°C). In addition, the stretched film B of the present invention can improve the long-term durability of capacitor elements.

[0018] Here, in the stretched film described herein, the small change in dielectric breakdown strength under high-temperature conditions relative to dielectric breakdown strength at room temperature (e.g., 25°C) means, specifically, that when the dielectric breakdown strength of the stretched film at 25°C is V25 (Vdc / μm) and the dielectric breakdown strength at 140°C is V140 (Vdc / μm), the value of the strength ratio "V140 / V25" is close to 1. In particular, in stretched film A and stretched film B of the present invention, the value of V140 / V25 is preferably 0.75 or higher, more preferably 0.78 or higher, even more preferably 0.79 or higher, and particularly preferably 0.80 or higher. The value of V140 / V25 is usually 1 or less, preferably 0.99 or less, and more preferably 0.95 or less.

[0019] In the following, the value "V140 / V25," which represents the degree of change in dielectric breakdown strength at 140°C (high temperature) compared to room temperature (e.g., 25°C), may be simply abbreviated as "dielectric breakdown strength ratio."

[0020] In the present invention, the ratio of dielectric breakdown strengths can be measured by the method described in the examples below.

[0021] Furthermore, in this specification, when a stretched film improves the long-term durability of a capacitor element, it means, for example, that even when a voltage of 200 Vdc / μm is continuously applied for 500 hours or more at a high temperature of 135°C or above 135°C, the capacitor element can maintain excellent insulation without causing a short circuit and suppress the decrease in capacitance (i.e., the rate of change in capacitance can be reduced).

[0022] In the stretched film A of the present invention, the value of the orientation coefficient ΔP is between 0.007 and 0.0125, which results in a good orientation range for the stretched film. As a result, the stretched film A can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, the change in dielectric breakdown strength is small (the V140 / V25 ratio becomes larger), and the long-term durability of the capacitor element can be improved.

[0023] When the orientation coefficient ΔP of the stretched film A of the present invention exceeds 0.0125, the molecular orientation within the stretched film improves. As a result, the dielectric breakdown strength at 25°C improves, but the dielectric breakdown strength at high temperatures of 120°C or higher tends to decrease. Consequently, the change in dielectric breakdown strength becomes larger, meaning that the aforementioned V140 / V25 value decreases. Therefore, when the orientation coefficient ΔP exceeds 0.0125, the decrease in dielectric breakdown strength at high temperatures makes short circuits in the capacitor element more likely, which is undesirable in practical terms.

[0024] In the stretched film A of the present invention, if the value of the orientation coefficient ΔP is less than 0.007, the molecular orientation within the stretched film is insufficient, resulting in a decrease in dielectric breakdown strength not only in high-temperature environments but also at 25°C, and making it difficult to improve the long-term durability of the capacitor element.

[0025] The stretched film A of the present invention preferably has an orientation coefficient ΔP of 0.0075 or more, more preferably 0.008 or more, even more preferably 0.0085 or more, and particularly preferably 0.0090 or more.

[0026] The method for adjusting the orientation coefficient ΔP of the stretched film A of the present invention to 0.007 or more and 0.0125 or less is not particularly limited, and known methods that can be used to suppress the lattice relaxation motion of isotactic polypropylene can be widely employed. In particular, by manufacturing the stretched film A with a polypropylene resin containing an isotactic polypropylene resin, it becomes easier to adjust the orientation coefficient ΔP to 0.007 or more and 0.0125 or less. In particular, as described below, when the stretched film A is manufactured using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure, it becomes even easier to adjust the orientation coefficient ΔP to 0.007 or more and 0.0125 or less.

[0027] Furthermore, the value of the in-plane birefringence value ΔNyx can also be controlled by the stretching method of the stretched film, and this method may also be adopted. For example, the birefringence value of the present invention can be controlled by the stretching ratio in the MD (flow direction) and / or TD (width direction), the temperature during stretching and / or the temperature gradient, or the heat treatment (relaxation) temperature immediately after stretching. As long as the birefringence value of the present invention can be adjusted to a desired range, there are no restrictions on the method and conditions for controlling the birefringence value, and any of them can be adopted.

[0028] In the present invention, the orientation coefficient ΔP can be measured by calculating the birefringence values ​​ΔNyx, ΔNxz, and ΔNyz from the measured retardation (phase difference) of the stretched film A by the tilt method, and then using the above-mentioned equation (1A) based on these values. For measuring retardation (phase difference) by the tilt method, the retardation measuring device "RE-100" manufactured by Otsuka Electronics Co., Ltd. can be used, and an LED light source with a wavelength of 550 nm is used as the light source. More specifically, as described below, the birefringence values ​​ΔNyx, ΔNxz, and ΔNyz can be calculated by measuring the angular dependence of the retardation value by the tilt method.

[0029] Specifically, the in-plane principal axes of the film are defined as the x and y axes, and the thickness direction of the film (normal to the in-plane direction) is defined as the z axis. The y axis is defined as the slow axis in the direction of higher refractive index within the in-plane direction. The retardation values ​​are then calculated by tilting the y axis at 10° intervals relative to the z axis within the range of 0° to 50°. From the obtained retardation values, the birefringence ΔNyz in the y-axis direction relative to the thickness direction (z-axis direction), the birefringence ΔNxz in the x-axis direction relative to the thickness direction (z-axis direction) with the x-axis perpendicular to the y axis, and the in-plane birefringence ΔNyx (referred to as in-plane birefringence ΔNyx) are calculated. These calculation methods are as follows: Non-patent literature; "Yutaka Awaya, Introduction to Polarizing Microscopy of Polymer Materials, pp. 105-120, 2001." You can refer to the description and proceed as follows: First, for each tilt angle φ, calculate R / d by dividing the measured retardation value R by the tilt-corrected thickness d. The R / d when φ=0° is the in-plane birefringence ΔNyx.

[0030] Furthermore, for each R / d at φ=10°, 20°, 30°, 40°, and 50°, the difference between this and the R / d at φ=0° is calculated, and these differences are then divided by sin2r(r: angle of refraction) to obtain the birefringence ΔNzx at each φ. By reversing the sign of this value, the birefringence value ΔNxz is obtained. The average value of ΔNzx at φ=20°, 30°, 40°, and 50° is calculated, and the birefringence value ΔNxz is obtained from this average value. In addition, ΔNyz can be calculated from the difference between the in-plane birefringence ΔNyx and ΔNxz.

[0031] Furthermore, the values ​​of the refraction angle r for polypropylene at each tilt angle, and the values ​​of the intrinsic refractive index of polypropylene for obtaining the thickness correction value, can be found on page 109 of the aforementioned non-patent document as needed.

[0032] Here, for example, in a stretched film produced by a sequential stretching method, if the stretching ratio in the TD direction (width direction) is higher than the stretching ratio in the MD direction (flow direction), then the TD direction generally becomes the slow axis (y-axis) and the MD direction becomes the x-axis.

[0033] By calculating the birefringence value as described above, the ΔP of the stretched film A can be derived using equation (1A) mentioned earlier.

[0034] In stretched film B, the in-plane birefringence value ΔNyx is between 0.009 and 0.016. As a result, stretched film B can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength is small (the V140 / V25 ratio increases). Furthermore, because the in-plane birefringence value ΔNyx is between 0.009 and 0.016, stretched film B of the present invention can improve the long-term durability of capacitor elements in high-temperature environments.

[0035] When the in-plane birefringence value ΔNyx of the stretched film B of the present invention exceeds 0.016 (especially exceeding 0.0160), the molecular orientation within the stretched film improves. As a result, the dielectric breakdown strength at 25°C improves, but the dielectric breakdown strength at high temperatures above 120°C tends to decrease. Consequently, the change in dielectric breakdown strength becomes larger, meaning that the aforementioned V140 / V25 value decreases. Therefore, when the in-plane birefringence value ΔNyx exceeds 0.016 (especially exceeding 0.0160), the decrease in dielectric breakdown strength at high temperatures makes short circuits in the capacitor element more likely, which is undesirable in practical terms. In order to control and / or optimize the motion of the amorphous region within the stretched film B and maintain dielectric breakdown strength at high temperatures without a decrease, it is necessary to keep the in-plane birefringence value ΔNyx below 0.016.

[0036] In the stretched film B of the present invention, when the in-plane birefringence value ΔNyx is less than 0.009 (particularly less than 0.0090), the molecular orientation within the stretched film is insufficient. As a result, the dielectric breakdown strength decreases not only in high-temperature environments but also at 25°C, and the long-term durability of the capacitor element is difficult to improve.

[0037] The stretched film B of the present invention preferably has an in-plane birefringence value ΔNyx of 0.0095 or more, more preferably 0.010 or more, even more preferably 0.011 or more, and particularly preferably 0.0115 or more.

[0038] The stretched film B of the present invention preferably has an in-plane birefringence value ΔNyx of 0.0160 or less, more preferably 0.0155 or less, even more preferably 0.0150 or less, and particularly preferably 0.0145 or less.

[0039] The method for adjusting the in-plane birefringence value ΔNyx of the stretched film B of the present invention to 0.009 or higher and 0.016 or lower is not particularly limited, and known methods that can be used to suppress the lattice relaxation motion of isotactic polypropylene can be widely employed. In particular, by manufacturing the stretched film B with a polypropylene resin containing an isotactic polypropylene resin, it becomes easier to adjust the in-plane birefringence value ΔNyx to 0.009 or higher and 0.016 or lower. In particular, as described below, when the stretched film B is manufactured using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure, it becomes even easier to adjust the in-plane birefringence value ΔNyx to 0.009 or higher and 0.016 or lower.

[0040] Furthermore, the value of the in-plane birefringence value ΔNyx can also be controlled by the stretching method of the stretched film, and this method may also be adopted. For example, the birefringence value of the present invention can be controlled by the stretching ratio in the MD (flow direction) and / or TD (width direction), the temperature during stretching and / or the temperature gradient, or the heat treatment (relaxation) temperature immediately after stretching. As long as the birefringence value of the present invention can be adjusted to a desired range, there are no restrictions on the method and conditions for controlling the birefringence value, and any of them can be adopted.

[0041] In the present invention, the in-plane birefringence value ΔNyx can be determined from the measured retardation (phase difference) of the stretched film B. The in-plane birefringence value obtained by measuring the retardation (phase difference) can be calculated using the procedure described above for measuring the retardation (phase difference) of the stretched film A by the tilt method.

[0042] The above-described features of the stretched film B of the present invention may also be present in the stretched film A of the present invention. That is, similar to the stretched film B, the in-plane birefringence value ΔNyx of the stretched film A of the present invention may be 0.009 or more and 0.016 or less.

[0043] The following details the characteristics that the stretched film A and stretched film B of the present invention share in common. In the following description, stretched film A and stretched film B of the present invention will be collectively referred to as "stretched film 1 of the present invention."

[0044] In the stretched film 1 of the present invention, it is preferable that the crystallite size, determined by Scherrer's formula based on the half-width of the (110) plane derived from the α-crystal of isotactic polypropylene, is 120 Å or more (12 nm or more) in the X-ray diffraction intensity measurement. In this case, the stretched film can have a higher dielectric breakdown strength even in a high-temperature environment of 120°C or higher, and the change in dielectric breakdown strength tends to be smaller. Therefore, it is preferable that the polypropylene resin for forming the stretched film contains at least isotactic polypropylene, as described below. In particular, in order to adjust the crystallite size to the above range, the polypropylene resin may contain a polymer having an alicyclic structure as described below, in addition to isotactic polypropylene.

[0045] The crystallite size of the stretched film 1 of the present invention is preferably 160 Å or less, more preferably 155 Å or less, and even more preferably 150 Å or less.

[0046] The stretched film 1 of the present invention exhibits an infrared absorption spectrum of 880-890 cm⁻¹. -1 Absorption peaks are observed in the range, and at 1450 cm. -1 It is preferable that the stretched film 1 has at least one of the shoulder peaks due to absorption in the vicinity. In this case, the stretched film 1 can have a higher dielectric breakdown strength even in a high-temperature environment of 120°C or higher, and the change in dielectric breakdown strength is also likely to be smaller. The stretched film 1 of the present invention has an infrared absorption spectrum of 880-890 cm⁻¹. -1 Absorption peaks are observed in the range, and at 1450 cm. -1 It is more preferable to have both a shoulder peak due to absorption in the vicinity.

[0047] 880-890cm-1 To have an absorption peak within the range of, and / or a shoulder peak due to absorption near 1450 cm -1 For example, the composition ratio of each component in the polypropylene-based resin for forming the stretched film 1 may be adjusted. For example, the characteristic peak of the infrared absorption of the polymer having an alicyclic structure described later is within the range of 880 to 890 cm -1 and / or near 1450 cm -1 Therefore, it is preferable that the polypropylene-based resin contains a polymer component having the alicyclic structure. For example, the content ratio of the polymer component having the alicyclic structure described later in the polypropylene-based resin for forming the stretched film 1 may be adjusted to 6% by mass or more, preferably 10% by mass or more.

[0048] (Stretched Films C and D) First, the stretched films C and D of the present invention will be described. The stretched films C and D are as follows. Stretched Film C: A stretched film containing a polypropylene-based resin, When the stress at 100% elongation in the film flow direction measured at 23°C is defined as F100(23), and the stress at 100% elongation in the flow direction measured at 135°C is defined as F100(135), the following formula (1) F100(135) / F100(23)>0.13 (1) is satisfied. Stretched Film D: A stretched film containing a polypropylene-based resin, When the stress at the maximum point in the film flow direction measured at 23°C is defined as F(23M), the stress at the maximum point in the direction perpendicular to the film flow direction measured at 23°C is defined as F(23T), the stress at the maximum point in the film flow direction measured at 135°C is defined as F(135M), and the stress at the maximum point in the direction perpendicular to the film flow direction measured at 135°C is defined as F(135T), the following formula (2) {F(135M)+F(135T)} / {F(23M)+F(23T)}>0.31 (2) It satisfies the condition.

[0049] Hereafter, "F100(135) / F100(23)" in equation (1) will be denoted as "Fa", and "{F(135M)+F(135T)} / {F(23M)+F(23T)}" in equation (2) will be denoted as "Fb".

[0050] In this specification, "film flow direction" means the MD direction of the stretched film, and "direction perpendicular to the film flow direction" means the TD direction of the stretched film. Therefore, "film flow direction" can be read as "MD direction," and "direction perpendicular to the film flow direction" can be read as "TD direction."

[0051] The stretched film C of the present invention can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and specifically, it has high dielectric breakdown strength even in high-temperature environments of 140°C. Moreover, the stretched film C of the present invention shows little change in dielectric breakdown strength in high-temperature environments (e.g., 140°C environment) compared to room temperature (e.g., 25°C environment). In addition, the stretched film C of the present invention can improve the long-term durability of capacitor elements in high-temperature environments.

[0052] Similarly, the stretched film D of the present invention can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and specifically, it has high dielectric breakdown strength even in high-temperature environments of 140°C. Moreover, the stretched film D of the present invention shows little change in dielectric breakdown strength in high-temperature environments (e.g., 140°C environment) compared to room temperature (e.g., 25°C). In addition, the stretched film D of the present invention can improve the long-term durability of capacitor elements.

[0053] Here, "the change in dielectric breakdown strength under high-temperature conditions relative to the dielectric breakdown strength at room temperature (e.g., 25°C) is small" is synonymous with "the change in dielectric breakdown strength under high-temperature conditions relative to the dielectric breakdown strength at room temperature (e.g., 25°C) is small" for the stretched films A and B described above. In the stretched films C and D of the present invention, the V140 / V25 value is preferably 0.75 or higher, more preferably 0.78 or higher, even more preferably 0.79 or higher, and particularly preferably 0.80 or higher. The V140 / V25 value is usually 1 or less, preferably 0.99 or less, and more preferably 0.95 or less.

[0054] In the present invention, the ratio of dielectric breakdown strengths can be measured by the method described in the examples below.

[0055] The stretched film C of the present invention satisfies formula (1) above (i.e., satisfies Fa > 0.13), thereby having high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength is reduced (the V140 / V25 ratio becomes larger), and the long-term durability of the capacitor element can be improved.

[0056] When Fa of the stretched film C of the present invention falls below 0.13, the dielectric breakdown strength tends to decrease under high-temperature environments of 120°C or higher. As a result, the change in dielectric breakdown strength becomes larger, and the aforementioned V140 / V25 values ​​decrease. Therefore, when Fa falls below 0.13, the decrease in dielectric breakdown strength under high temperatures makes short circuits in the capacitor element more likely, which is undesirable in practical terms.

[0057] The stretched film C of the present invention preferably has a Fa value of 0.14 or higher, more preferably 0.15 or higher, and even more preferably 0.16 or higher. The upper limit of the Fa value is not particularly limited; for example, it is preferably 0.30 or lower, and more preferably 0.25 or lower.

[0058] In this invention, the stress F100(23) at 100% elongation in the film flow direction, measured at 23°C, and the stress F100(135) at 135°C, measured at 100% elongation in the flow direction, can both be measured using a tensile testing machine with a constant temperature chamber. The specific measurement method is as follows.

[0059] [Stress F100 (23) at 100% elongation in the film flow direction, measured at 23℃] The stress F100(23) at 100% elongation in the film flow direction, measured at 23℃, is calculated using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm is cut out. At this time, the sample is cut so that the flow direction is in the length direction. The sample is set in the chuck of a tensile testing machine (A&D Co., Ltd. "Tensilon Universal Testing Machine RTG-1210") with a chuck distance of 50 mm, and a tensile test is performed at a test speed of 100 mm / min. F100(23)(MPa) is calculated by dividing the load value at 100% elongation in the tensile test by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm).

[0060] [Stress F100(135) at 100% elongation in the film flow direction measured at 135℃] The stress F100(135) at 100% elongation in the film flow direction measured at 135℃ is calculated using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm is cut out. At this time, the sample is cut out so that the flow direction is the length direction. The sample is set in the chuck of a tensile testing machine (A&D Co., Ltd. "Tensilon Universal Testing Machine RTG-1210") with a distance of 50 mm between the chucks, and then the chuck is placed in an oven heated to 135℃, heated for 1 minute, and then a tensile test is performed at a test speed of 100 mm / min. F100(135)(MPa) is calculated by dividing the load value at 100% elongation in the tensile test by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm).

[0061] The method for adjusting the value of Fa in the stretched film C of the present invention to 0.13 or higher is not particularly limited. For example, the stretched film C can be manufactured using a polypropylene resin containing an isotactic polypropylene resin. As will be described later, when the stretched film C is manufactured using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure, it becomes easier to adjust the value of Fa to 0.13 or higher.

[0062] The stretched film D of the present invention satisfies formula (2) above (i.e., satisfies Fb > 0.31), thereby having high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength is reduced (the V140 / V25 ratio becomes larger), and the long-term durability of the capacitor element can be improved.

[0063] When the Fb of the stretched film D of the present invention falls below 0.31, the dielectric breakdown strength in high-temperature environments above 120°C tends to decrease. As a result, the change in dielectric breakdown strength becomes larger, and the aforementioned V140 / V25 value decreases. Therefore, when Fb falls below 0.31, the decrease in dielectric breakdown strength at high temperatures makes short circuits in the capacitor element more likely, which is undesirable in practical terms.

[0064] The stretched film D of the present invention preferably has an Fb value of 0.32 or higher, more preferably 0.33 or higher, even more preferably 0.34 or higher, and particularly preferably 0.35 or higher. The upper limit of the Fb value is not particularly limited; for example, it is preferably 0.6 or lower, and more preferably 0.5 or lower.

[0065] In this invention, the stress F(23M) at the point of maximum stress in the film flow direction measured at 23°C, the stress F(23T) at the point of maximum stress in the direction perpendicular to the film flow direction measured at 23°C, the stress F(135M) at the point of maximum stress in the film flow direction measured at 135°C, and the stress F(135T) at the point of maximum stress in the direction perpendicular to the film flow direction measured at 135°C can all be measured using a tensile testing machine with a constant temperature chamber. The specific measurement method is as follows.

[0066] [Measurement method for F(23M) and F(23T)] The stress F(23M) at the point of maximum stress in the film flow direction and the stress F(23T) at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 23°C, are measured using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm is cut out. At this time, the sample is cut out so that the measurement direction is the length direction. The sample is set in the chuck of a tensile testing machine (A&D Co., Ltd. "Tensilon Universal Testing Machine RTG-1210") with a chuck distance of 50 mm, and a tensile test is performed at a test speed of 100 mm / min. The load value at which the sample breaks in the tensile test is divided by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm), and the value when the measurement direction is the MD direction is calculated as F(23M) (MPa), and the value when the measurement direction is the TD direction is calculated as F(23T) (MPa).

[0067] [Measurement methods for F(135M) and F(135T)] The stress F(135M) at the point of maximum stress in the film flow direction and the stress F(135T) at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 135°C, are measured using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm is cut out. At this time, the sample is cut out so that the measurement direction is the length direction. The sample is set in the chuck of a tensile testing machine (A&D Company, Limited "Tensilon Universal Testing Machine RTG-1210") with a distance of 50 mm between the chucks, and then the chuck and the sample are placed in an oven heated to 135°C, heated for 1 minute, and then a tensile test is performed at a test speed of 100 mm / min. The load value at which the sample breaks in the tensile test is divided by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm), and the value when the measurement direction is the MD direction is calculated as F(135M) (MPa), and the value when the measurement direction is the TD direction is calculated as F(135T) (MPa).

[0068] The method for adjusting the Fb value of the stretched film D of the present invention to 0.31 or higher is not particularly limited. For example, the stretched film D can be manufactured using a polypropylene resin containing an isotactic polypropylene resin. As will be described later, when the stretched film D is manufactured using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure, it becomes easier to adjust the Fb value to 0.31 or higher.

[0069] The above-described features of the stretched film D of the present invention may also be present in the stretched film C of the present invention. That is, the stretched film C of the present invention can satisfy formula (2) above (i.e., Fb > 0.31), just like the stretched film D.

[0070] The following details the characteristics that the stretched film C and stretched film D of the present invention share in common. In the following description, the stretched film C and stretched film D of the present invention will be collectively referred to as "stretched film 2 of the present invention."

[0071] Preferably, the stretched film 2 of the present invention has a thermal shrinkage rate of 1.0% or more and 6.0% or less in the film flow direction (MD direction) measured at 140°C, and a thermal shrinkage rate of 4.0% or less in the direction perpendicular to the film flow direction (TD direction).

[0072] The method for adjusting the thermal shrinkage rate of the stretched film 2 of the present invention to the above range is not particularly limited. For example, the stretched film 2 may be manufactured using a polypropylene resin containing an isotactic polypropylene resin. When the stretched film 2 is manufactured using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure, the thermal shrinkage rate can be adjusted more easily. Furthermore, the thermal shrinkage rate of the stretched film 2 can also be controlled by the stretching method of the stretched film 2, and this method may also be adopted. For example, it can be controlled by the stretching ratio in the MD direction and / or TD direction, the temperature during stretching and / or the temperature gradient, or the heat treatment (relaxation) temperature immediately after stretching.

[0073] Next, the characteristics common to stretched film 1 (i.e., stretched films A and B) and stretched film 2 (i.e., stretched films C and D) of the present invention will be described in detail. In the following description, stretched film 1 and stretched film 2 of the present invention will be collectively referred to as "the stretched film of the present invention."

[0074] The stretched film of the present invention preferably has a peak in the loss tangent tanδ in the region of 140°C or higher in the temperature dispersion data in the TD direction at a frequency of 1 Hz obtained from dynamic viscoelasticity measurement. As a result, the stretched film can have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength is also small (the V140 / V25 ratio becomes larger).

[0075] In this specification, "having a peak in the loss tangent (tanδ) in the region above 140°C" specifically means that, in the temperature dispersion data (also called temperature-dependent data) of dynamic viscoelasticity, the loss tangent (tanδ) has a clear principal dispersion peak (i.e., the peak with the largest tanδ value) in the region above 140°C.

[0076] Here, "having a clear main dispersion peak in the region above 140°C" means, for example, that in the temperature range of 140 to 160°C of the temperature dispersion data (also called temperature-dependent data) for the dynamic viscoelasticity described above, the difference between the maximum and minimum values ​​of the tanδ (range of change in the temperature range) is ±0.03 or more, preferably ±0.04 or more, more preferably ±0.05 or more, and particularly preferably ±0.06 or more.

[0077] In the stretched film of the present invention, the method for having a loss tangent (tanδ) peak in the region of 140°C or higher is not particularly limited. For example, known methods for raising the glass transition temperature or methods using resin blends can be widely employed. In particular, a method of producing the stretched film using a polypropylene resin containing an isotactic polypropylene resin is preferred. Among these, as described below, when the stretched film is produced using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure, it is more likely to have a loss tangent (tanδ) peak in the region of 140°C or higher.

[0078] In the stretched film of the present invention, temperature dispersion data can be obtained by dynamic viscoelasticity measurement of each stretched film.

[0079] Specifically, for example, temperature dispersion data can be obtained by performing dynamic viscoelasticity measurements in accordance with JIS-K7244-1 and -4 (1999 edition) using test pieces cut from the stretched film of the present invention into strips. The conditions for such dynamic viscoelasticity measurements are tensile mode, vibration frequency of 1 Hz, chuck distance of 20 mm, strain amplitude of 10 μm, minimum tension of 20 mN, and heating rate of 2 °C / min. The tensile direction of the stretched film is perpendicular to the flow direction (MD direction) of the stretched film, i.e., the TD direction. By performing dynamic viscoelasticity measurements of the stretched film in this way, the relationship between temperature (X axis) and the storage modulus E' (Y axis) and / or the loss tangent tanδ (Y axis) can be obtained as temperature dispersion (also called temperature dependence) data.

[0080] Preferably, the stretched film of the present invention has a loss tangent (tanδ) of 0.15 or less at 100°C, obtained based on the temperature dispersion data. This allows the stretched film to have high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength is also small (the V140 / V25 ratio becomes larger).

[0081] In the stretched film of the present invention, the loss tangent (tanδ) at 100°C is preferably 0.145 or less, more preferably 0.140 or less, even more preferably 0.135 or less, and particularly preferably 0.130 or less. In the stretched film of the present invention, the loss tangent (tanδ) at 100°C is, for example, 0.05 or more, preferably 0.08 or more, more preferably 0.10 or more, and even more preferably 0.11 or more.

[0082] Here, in the stretched film of the present invention, a loss tangent (tanδ) of 0.15 or less at 100°C means that the temperature dispersion (temperature dependence) data of the tanδ value described above does not substantially have a peak at 100°C. The absence of a substantially peak at 100°C means that, in the loss tangent tanδ temperature dispersion data, there is almost no fluctuation in the value of the loss tangent tanδ around 100°C (for example, in the range of 80-120°C), and the characteristic increase in the tanδ value in this temperature range due to the movement based on the lattice relaxation of polypropylene does not occur. In other words, the movement of lattice relaxation is suppressed, and for example, there is a simple increase towards the main dispersion peak of tanδ in the range of 80-120°C.

[0083] The method for adjusting the 100°C loss tangent (tanδ) of the stretched film of the present invention to 0.15 or less is not particularly limited. For example, known methods that can be used to suppress the lattice relaxation motion of isotactic polypropylene can be widely employed. In particular, it is easier to adjust the 100°C loss tangent (tanδ) to 0.15 or less by manufacturing the stretched film with a polypropylene resin containing an isotactic polypropylene resin. In particular, as described below, it is easier to adjust the 100°C loss tangent (tanδ) to 0.15 or less when the stretched film is manufactured using a polypropylene resin containing an isotactic polypropylene resin and a polymer having an alicyclic structure.

[0084] The thickness of the stretched film of the present invention can be adjusted to an appropriate range depending on the application, and can be, for example, to the same range as the thickness of stretched films used in capacitor applications. For example, the stretched film of the present invention preferably has a thickness of 1.8 μm or more and 10 μm or less. The thickness of the stretched film was measured in accordance with JIS-C2330:2014, except that it was measured at 100 ± 10 kPa using a paper thickness gauge MEI-11 manufactured by Citizen Seimitsu Co., Ltd.

[0085] From the viewpoint of having high transparency, the stretched film of the present invention preferably has a total light transmittance of 80% or more. In particular, the stretched film of the present invention preferably has a thickness of 1.8 μm or more and 10 μm or less, and a total light transmittance of 80% or more. In this case, the stretched film of the present invention can be used particularly suitably for capacitor applications.

[0086] The surface roughness of the stretched film of the present invention is preferably, for example, 0.015 μm or more and 0.03 μm or less, more preferably 0.025 μm or less, and even more preferably 0.020 μm or less. In this specification, the surface roughness of the stretched film means the arithmetic mean height (Sa).

[0087] The stretched film of the present invention may have a single-layer structure or a multilayer structure in which multiple layers are laminated. If the stretched film has a multilayer structure, some or all of the layers may be different. In this case, at least one layer is a layer containing the polypropylene resin.

[0088] (Polypropylene resin) Next, the polypropylene resin included in the stretched film of the present invention will be described. The stretched film of the present invention is formed using a polypropylene resin.

[0089] A wide variety of polypropylene resins can be included in the stretched film. In particular, the polypropylene resin is preferably an isotactic polypropylene resin that contains at least a heat-resistant resin having a high glass transition temperature, as it is likely to satisfy the orientation coefficient ΔP of the stretched film to be between 0.007 and 0.0125, or the in-plane birefringence value ΔNyx to be between 0.009 and 0.016, and furthermore, as it is likely to satisfy formula (1) and / or formula (2). The heat-resistant resin having a high glass transition temperature can be crystalline or amorphous, but an amorphous resin is preferable in order to better demonstrate the effect of having a high glass transition temperature. In particular, the polypropylene resin is preferably an isotactic polypropylene resin that contains an alicyclic polymer. In this case, it is possible to have a higher dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength is also likely to be smaller.

[0090] As described above, in the stretched film of the present invention, the polypropylene resin is preferably a resin (so-called blended resin) that includes an isotactic polypropylene resin and a polymer having an alicyclic structure.

[0091] <Isotactic polypropylene resin> For example, known isotactic polypropylene resins can be widely used.

[0092] The melt mass flow rate (MFR) of the isotactic polypropylene resin is preferably 0.5 g / 10 min or more and 6 g / 10 min or less, more preferably 1 g / 10 min or more and 5 g / 10 min or less, and even more preferably 1.5 g / 10 min or more and 4 g / 10 min or less, as measured at 230°C and 2.16 kgf. In this case, appropriate resin fluidity is obtained when stretching the film, and the stretchability is improved.

[0093] The melting point of the isotactic polypropylene resin is preferably 155°C or higher. In this case, the electrical insulation and stretchability at high temperatures are improved. The melting point is more preferably 160°C to 180°C, and even more preferably 164°C to 175°C.

[0094] It is preferable that the mesopentad fraction of the isotactic polypropylene resin is 95 mol% or more and 99.9 mol% or less. If it is 95 mol% or more, the rigidity and electrical insulation of the stretched film of the present invention tend to improve, and if it is 99.9 mol% or less, the stretchability tends to improve. The mesopentad fraction is more preferably 96 mol% or more and 99.5 mol%, even more preferably 96 mol% or more and 99 mol%, and particularly preferably 97 mol% or more and 98 mol%.

[0095] The heptane-insoluble content (HI) of the isotactic polypropylene resin is preferably 94% by mass or more and 99.9% by mass or less. If it is 94% by mass or more, the rigidity and electrical insulation of the stretched film tend to improve, and if it is 99.9% by mass or less, the stretchability tends to improve. The heptane-insoluble content is more preferably 96% by mass or more and 99.5% by mass or less, even more preferably 97% by mass or more and 99.2% by mass or less, and particularly preferably 98% by mass or more and 99% by mass or less.

[0096] The number-average molecular weight (Mn) of the isotactic polypropylene resin is preferably between 30,000 and 70,000, and more preferably between 35,000 and 65,000. In this case, the rigidity, electrical insulation, and stretchability of the stretched film of the present invention tend to improve.

[0097] The weight-average molecular weight (Mw) of the isotactic polypropylene resin is preferably between 250,000 and 500,000, and more preferably between 300,000 and 450,000. In this case, the rigidity, electrical insulation, and stretchability of the stretched film of the present invention tend to improve.

[0098] The molecular weight distribution (Mw / Mn) of the isotactic polypropylene resin is preferably 3 or more and 12 or less, more preferably 5 or more and 10 or less, and even more preferably 5.5 or more and 9.5 or less. In this case, the rigidity, electrical insulation, and stretchability of the stretched film of the present invention are easily improved.

[0099] The z-average molecular weight (Mz) of the isotactic polypropylene resin is preferably between 700,000 and 3,000,000, and more preferably between 1,000,000 and 2,500,000. In this case, the rigidity, electrical insulation, and stretchability of the stretched film of the present invention tend to improve.

[0100] The Mz / Mw ratio of the isotactic polypropylene resin is preferably 2 to 7, more preferably 2.5 to 6, and even more preferably 3 to 5. In this case, the rigidity, electrical insulation, and stretchability of the stretched film of the present invention tend to improve.

[0101] Isotactic polypropylene resin can be manufactured, for example, by known methods, or it can be obtained from the market.

[0102] Polymerization methods for obtaining isotactic polypropylene resins include, for example, gas-phase polymerization, bulk polymerization, and slurry polymerization. Polymerization may be a single-stage polymerization using one polymerization reactor, or a multi-stage polymerization using two or more polymerization reactors. Alternatively, hydrogen or comonomers may be added to the reactor as molecular weight modifiers during polymerization. Conventional known Ziegler-Natta catalysts or metallocene catalysts can be used as polymerization catalysts, and the polymerization catalysts may contain co-catalyst components or donors. The mesopentade fraction, melt mass flow rate, molecular weight, and molecular weight distribution of the polypropylene resin can be controlled by appropriately adjusting the polymerization catalyst and other polymerization conditions.

[0103] Polypropylene resins may include one or more isotactic polypropylene resins.

[0104] Furthermore, when the polypropylene resin includes isotactic polypropylene resin, the X-ray diffraction intensity measurement of the stretched film reveals diffraction peaks from the (110) plane originating from the α-crystal of the isotactic polypropylene mentioned above.

[0105] <Polymers having an alicyclic structure> A polymer with an alicyclic structure is a polymer that has an alicyclic structure in its main chain or side chains. Typically, the alicyclic structure exists covalently bonded to the main chain or side chains.

[0106] An alicyclic structure is defined as comprising one or more non-aromatic saturated and / or unsaturated carbon ring structures. There may be two or more such carbon ring structures. The carbon ring structures may have branching aliphatic hydrocarbon structures. The carbon ring structures are bonded directly or via hydrocarbon chains to the hydrocarbon chains of the polymer backbone.

[0107] Examples of the aforementioned carbocyclic structures include cycloalkane structures such as cyclopropane, cyclobutane, cyclopentane, cyclohexane, cycloheptane, cyclooctane, cyclononane, cyclodecane, cycloundecane, and cyclododecane, as well as cycloalkene structures such as cyclopropene, cyclobutene, cyclopropene, cyclohexene, cycloheptene, and cyclooctene. Examples of bicyclic structures include bicyclic alkane structures such as bicycloundecane, and bicyclic alkene structures such as norbornene and norbornadiene, which can be suitably used. In particular, having a carbocyclic structure with 4 to 8 carbon atoms is preferred from the viewpoint of extensibility, having a monocyclic carbocyclic structure with 4 to 8 carbon atoms is more preferred, having a monocyclic cycloalkane carbocyclic structure with 4 to 8 carbon atoms is even more preferred, and having a cyclohexane structure is particularly preferred.

[0108] The main chain of a polymer having an alicyclic structure can be mainly composed of aliphatic hydrocarbons. The aliphatic hydrocarbons in the polymer main chain may have branches of aliphatic hydrocarbon structures and / or aromatic hydrocarbon structures. The main chain of a polymer having an alicyclic structure may further contain the alicyclic structure, but it is preferable that the main chain does not have an alicyclic structure, and that it is contained in the side chains, in order to easily maintain high dielectric breakdown strength even in high-temperature environments of 120°C or higher. Therefore, it is preferable that a polymer having an alicyclic structure is a polymer in which the side chain has an alicyclic structure.

[0109] A polymer having an alicyclic structure in its side chain may be a homopolymer whose constituent units are structures having an alicyclic structure in its side chain. For example, it may be a polyvinylcycloolefin obtained by homopolymerizing vinylcycloolefins. Examples of polyvinylcycloolefins include polyvinylcyclopropane, polyvinylcyclobutane, polyvinylcyclopentane, polyvinylcyclohexane, polyvinylcycloheptane, polyvinylcyclooctane, polyvinylcyclononane, polyvinylcyclodecane, polyvinylcycloundecane, and polyvinylcyclododecane. In the case of a homopolymer, it is preferable that rigidity and electrical insulation properties tend to be high in high-temperature environments. Among these, polyvinylcyclopentane, polyvinylcyclohexane, and polyvinylcycloheptane are preferred, with polyvinylcyclohexane being the most preferred.

[0110] Another example of a polymer having an alicyclic structure in its side chain is a hydrogenated block copolymer. The type of hydrogenated block copolymer is not particularly limited, and for example, known hydrogenated block copolymers can be broadly mentioned. A hydrogenated block copolymer can be, for example, a copolymer obtained by hydrogenating a block copolymer having at least a vinyl aromatic polymer block and a conjugated diene polymer block. That is, a hydrogenated block copolymer is a copolymer having at least a hydrogenated vinyl aromatic polymer block and a hydrogenated conjugated diene polymer block. Hydrogenated block copolymers will be described below.

[0111] ≪Hydrogenated vinyl aromatic polymer block≫ The hydrogenated vinyl aromatic polymer block contains constituent units derived from vinyl aromatic compounds, which have been hydrogenated. The hydrogenated vinyl aromatic polymer block contains 50% by mass or more, preferably 80% by mass or more, more preferably 90% by mass or more, and particularly preferably 100% by mass, constituent units derived from vinyl aromatic compounds. By having 50% by mass or more of constituent units derived from vinyl aromatic compounds, rigidity and electrical insulation properties in high-temperature environments are easily improved.

[0112] Examples of vinyl aromatic compounds include styrene, α-methylstyrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, 4-propylstyrene, 4-cyclohexylstyrene, 4-dodecylstyrene, 2-ethyl-4-benzylstyrene, 4-(phenylbutyl)styrene, vinyltoluene, 1-vinylnaphthalene, and 2-vinylnaphthalene. The vinyl aromatic compound is preferably selected from styrene and α-methylstyrene, and more preferably styrene.

[0113] The hydrogenated vinyl aromatic polymer block may consist of only one of the vinyl aromatic compounds, or it may consist of two or more. The hydrogenated vinyl aromatic polymer block may contain other constituent units other than those derived from the vinyl aromatic compounds. Examples of other constituent units include those derived from isoprene, butadiene, 2,3-dimethylbutadiene, 1,3-pentadiene, 1,3-hexadiene, etc.

[0114] The content of the vinyl hydrogenated aromatic polymer block is preferably 50% by mass or more and less than 100% by mass, relative to 100% by mass of the total of the vinyl hydrogenated aromatic polymer block and the hydrogenated conjugated diene polymer block. A content of 50% by mass or more tends to increase rigidity and electrical insulation at high temperatures. More preferably 60% by mass or more, even more preferably 70% by mass or more, and particularly preferably 80% by mass or more.

[0115] Hydrogen-conjugated diene polymer block The hydrogenated conjugated diene polymer block contains constituent units derived from a conjugated diene, which has been hydrogenated. The hydrogenated conjugated diene polymer block contains 50% by mass or more, preferably 80% by mass or more, more preferably 90% by mass or more, and particularly preferably 100% by mass of constituent units derived from the conjugated diene.

[0116] Examples of conjugated dienes include butadiene, 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-butadiene, 1,3-pentadiene, and 1,3-hexadiene. The conjugated diene is preferably selected from butadiene and isoprene, and more preferably butadiene.

[0117] The hydrogenated conjugated diene polymer block may contain structural units derived from a conjugated diene without side chains. Examples of conjugated dienes without side chains include butadiene, 1,3-pentadiene, and 1,3-hexadiene. Butadiene is preferred as the conjugated diene without side chains.

[0118] In hydrogenated conjugated diene polymer blocks, the bonding configuration of the conjugated diene, i.e., the microstructure, is not particularly limited. For example, butadiene can have 1,2-bonds and 1,4-bonds. Isoprene can have 1,2-bonds, 3,4-bonds, and 1,4-bonds. Only one of these bonding configurations may be present, or two or more may be present. If two or more bonding configurations are present, the proportion of each configuration is not particularly limited.

[0119] Hydrogenated conjugated diene polymer blocks may contain other constituent units besides those derived from conjugated dienes. Examples of other constituent units include those derived from styrene, α-methylstyrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, 4-propylstyrene, 4-cyclohexylstyrene, 4-dodecylstyrene, 2-ethyl-4-benzylstyrene, 4-(phenylbutyl)styrene, vinyltoluene, 1-vinylnaphthalene, 2-vinylnaphthalene, and the like.

[0120] The content of the hydrogenated conjugated diene polymer block is preferably more than 0% by mass (e.g., 1% or more by mass) and 50% by mass or less, based on 100% by mass of the total of the hydrogenated vinyl aromatic polymer block and the hydrogenated conjugated diene polymer block. A content of 50% by mass or less is preferable because it tends to increase rigidity and electrical insulation at high temperatures. More preferably 40% by mass or less, even more preferably 30% by mass or less, and particularly preferably 20% by mass or less.

[0121] ≪Hydrogenation Rate≫ In the hydrogenated vinyl aromatic polymer block according to this embodiment, the hydrogenation rate of the aromatic ring of the hydrogenated vinyl aromatic polymer block is preferably 50 mol% or more, more preferably 80 mol% or more, even more preferably 85 mol% or more, particularly preferably 90 mol% or more, and even more preferably 95 mol% or more. The hydrogenation rate may be 100 mol%. Furthermore, the hydrogenation rate of the carbon-carbon double bond derived from the conjugated diene in the hydrogenated conjugated diene polymer block is preferably 90 mol% or more, more preferably 95 mol% or more. The hydrogenation rate may be 100 mol%.

[0122] By setting the hydrogenation rate of the aromatic rings in the vinyl hydrogenated aromatic polymer block and / or the hydrogenation rate of the carbon-carbon double bonds derived from the conjugated diene in the hydrogenated conjugated diene polymer block within the above-mentioned range, the stretchability is improved, and the glass transition temperature (Tg) tends to be 100°C or higher, which is preferable.

[0123] ≪Bonding patterns of hydrogenated block copolymers≫ The bonding pattern of polymer blocks in a hydrogenated block copolymer may be linear, branched, or radial, or a combination thereof.

[0124] For example, if we represent a vinyl hydrogenated aromatic polymer block as "X" and a hydrogenated conjugated diene polymer block as "Y", the bonding modes include diblock copolymers (XY), triblock copolymers (XYX), tetrablock copolymers (XYXY), and pentablock copolymers (XYXYX, or YXYXY). From the viewpoint of ease of manufacture, the bonding modes are preferably diblock copolymers, triblock copolymers, or tetrablock copolymers.

[0125] Specific examples of hydrogenated block copolymers include hydrogenated block copolymers obtained by hydrogenating styrene-isoprene diblock copolymer (SI), styrene-butadiene diblock copolymer (SB), styrene-isoprene-styrene triblock copolymer (SIS), styrene-butadiene / isoprene-styrene triblock copolymer (SB / IS), and styrene-butadiene-styrene triblock copolymer (SBS), styrene-ethylene-butylene-styrene copolymer (SEBS), styrene-ethylene-propylene-styrene copolymer (SEPS), styrene-ethylene-ethylene-propylene-styrene copolymer (SEEPS), and styrene-butylene-butadiene-styrene copolymer (SBBS). Among these, hydrogenated block copolymers obtained by hydrogenating styrene-butadiene diblock copolymer (SB) are particularly preferred.

[0126] ≪Method for producing hydrogenated block copolymers≫ The method for producing hydrogenated block copolymers is not particularly limited, and known methods such as anionic polymerization can be used. Specifically, hydrogenated block copolymers can be produced by a polymerization reaction using an alkyllithium compound as an initiator to sequentially polymerize a vinyl aromatic compound and a conjugated diene; a method using an alkyllithium compound as an initiator to sequentially polymerize a vinyl aromatic compound and a conjugated diene, and then adding a coupling agent for coupling; or a method using a dilithium compound as an initiator to sequentially polymerize a conjugated diene, and then a vinyl aromatic compound, followed by a hydrogenation reaction.

[0127] Examples of alkyllithium compounds include methyllithium, ethyllithium, n-butyllithium, sec-butyllithium, tert-butyllithium, and pentyllithium.

[0128] Examples of coupling agents include polyvalent epoxy compounds such as divinylbenzene, epoxidized 1,2-polybutadiene, epoxidized soybean oil, and 1,3-bis(N,N-glycidylaminomethyl)cyclohexane; halogen compounds such as dimethyldichlorosilane, dimethyldibromosilane, trichlorosilane, methyltrichlorosilane, tetrachlorosilane, and tetrachlorotin; ester compounds such as methyl benzoate, ethyl benzoate, phenyl benzoate, diethyl oxalate, diethyl malonate, diethyl adipate, dioctyl adipate, dimethyl phthalate, diethyl phthalate, dimethyl isophthalate, and dimethyl terephthalate; carbonate ester compounds such as dimethyl carbonate, diethyl carbonate, and diphenyl carbonate; and alkoxysilane compounds such as dimethyldimethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, tetramethoxysilane, tetraethoxysilane, bis(trimethoxysilyl)hexane, and bis(triethoxysilyl)ethane.

[0129] Examples of dilithium compounds include naphthalenedithium and dilithiohexylbenzene.

[0130] The polymerization reaction is preferably carried out in the presence of a solvent. The solvent is not particularly limited as long as it is inert to the initiator and does not adversely affect the reaction. Examples include saturated aliphatic hydrocarbons such as hexane, cyclohexane, heptane, octane, and decane; and aromatic hydrocarbons such as toluene, benzene, and xylene. The polymerization reaction temperature is usually preferably 0 to 100°C, more preferably 30 to 90°C, even more preferably 40 to 80°C, and particularly preferably 50 to 80°C, from the viewpoint of microstructure control. The polymerization reaction time is preferably 0.5 to 50 hours, from the viewpoint of microstructure control.

[0131] Furthermore, Lewis bases may be used as co-catalysts during polymerization reactions. Examples of Lewis bases include ethers such as dimethyl ether, diethyl ether, and tetrahydrofuran; glycol ethers such as ethylene glycol dimethyl ether and diethylene glycol dimethyl ether; and amines such as triethylamine, N,N,N',N'-tetramethylethylenediamine, and N-methylmorpholine. These Lewis bases may be used individually or in combination of two or more.

[0132] The hydrogenation reaction may be carried out immediately after the polymerization reaction, or it may be carried out after the block copolymer has been isolated following the polymerization reaction.

[0133] To isolate a block copolymer after a polymerization reaction, the polymerization reaction solution obtained after the polymerization reaction can be poured into a poor solvent for the block copolymer, such as methanol, to solidify the block copolymer. Alternatively, the polymerization reaction solution can be poured into hot water along with steam to remove the solvent by azeotropic removal (steam stripping), and then the block copolymer can be isolated by drying.

[0134] The hydrogenation reaction of block copolymers can be carried out, for example, by reacting them for 0.1 to 100 hours under conditions of a reaction temperature of 20 to 200°C and a hydrogen pressure of 0.1 to 20 MPa, in the presence of a hydrogenation catalyst.

[0135] Examples of hydrogenation catalysts include Raney nickel; heterogeneous catalysts in which metals such as platinum (Pt), palladium (Pd), ruthenium (Ru), rhodium (Rh), and nickel (Ni) are supported on carriers such as carbon, alumina, and diatomaceous earth; Ziegler catalysts consisting of combinations of transition metal compounds (nickel octoate, nickel naphthenate, nickel acetylacetonate, cobalt octoate, cobalt naphthenate, cobalt acetylacetonate, etc.) and organoaluminum compounds such as triethylaluminum and triisobutylaluminum, or organolithium compounds; and metallocene catalysts consisting of combinations of bis(cyclopentadienyl) compounds of transition metals such as titanium, zirconium, and hafnium and organometallic compounds consisting of lithium, sodium, potassium, aluminum, zinc, or magnesium.

[0136] When the hydrogenation reaction is carried out immediately following the polymerization reaction, the hydrogenated block copolymer can be isolated by pouring the hydrogenation reaction solution into a poor solvent for the hydrogenated block copolymer, such as methanol, and allowing it to solidify, or by pouring the hydrogenation reaction solution into hot water with steam to remove the solvent by azeotrope (steam stripping), followed by drying.

[0137] <Polymers having an alicyclic structure in their main chain> In polymers having an alicyclic structure, the alicyclic structure may be present in the main chain. As polymers having an alicyclic structure in the main chain, known cycloolefin copolymers (so-called COCs) can be widely applied. Specifically, examples include polymers in which an alkylene skeleton is used as the main chain, and a portion of the alkylene is replaced by an alicyclic structure. The alkylene skeleton can be, for example, an ethylene unit (-CH2-CH2-).

[0138] A specific example of a polymer having an alicyclic structure in its main chain is a polymer of norbornene and ethylene. In this case, the polymer having an alicyclic structure in its main chain is a polymer in which an alicyclic structure derived from norbornene is introduced into the polyethylene main chain. Polymers having an alicyclic structure in their main chain can be manufactured by known methods or obtained from commercially available products. Examples of commercially available polymers having an alicyclic structure in their main chain include the "Topas (registered trademark) COC" series from Polyplastics Co., Ltd., such as "COC6013F-04" (glass transition temperature Tg of 137°C) and "COC8007F-04" (Tg of 76°C).

[0139] <Preferred embodiments of polymers having an alicyclic structure> As described above, the polymer having an alicyclic structure may be a homopolymer or a copolymer. When the polymer having an alicyclic structure is a homopolymer, it is preferable that such a polymer is a hydrogenated polymer, a so-called hydrogenated polymer. When the polymer having an alicyclic structure in its side chain is a hydrogenated polymer, a specific example is hydrogenated polystyrene (for example, polyvinylcyclohexane). The stereoregularity of the hydrogenated polystyrene may be isotactic, syndiotactic, or atactic, but in order to better demonstrate the effect of having a high glass transition temperature, it is more preferable that it be an atactic, amorphous resin.

[0140] When the polymer having the alicyclic structure contains hydrogenated polystyrene, it can have particularly high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength tends to be particularly small. It is preferable that the hydrogenated polystyrene has an atactic structure and a hydrogenation rate of 95% or more.

[0141] When the polymer having an alicyclic structure is a copolymer, a block copolymer having at least a vinyl aromatic polymer block and a conjugated diene polymer block is preferred, and a hydrogenated block copolymer obtained by hydrogenating a styrene-butadiene diblock copolymer (SB) is particularly preferred.

[0142] The glass transition temperature (Tg) of polymers having an alicyclic structure in their side chains is preferably, for example, 100°C to 180°C. Setting the glass transition temperature to 100°C or higher tends to increase rigidity and electrical insulation at high temperatures, while setting it to 180°C or lower can improve stretchability. A glass transition temperature of 120°C to 165°C is more preferable, 130°C to 160°C is even more preferable, and 140°C to 155°C is particularly preferable.

[0143] In particular, polymers having an alicyclic structure preferably contain two or more polymers with different glass transition temperatures.

[0144] In this case, it is preferable that the polymer having an alicyclic structure includes polymer B1 having an alicyclic structure with a glass transition temperature of 133°C to 155°C and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C to less than 133°C. In this case, heat resistance is improved by B1, and the compatibility between polypropylene and B1 is easily increased by B2, resulting in particularly high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and the change in dielectric breakdown strength tends to be particularly small. Hereinafter, polymer B1 having an alicyclic structure with a glass transition temperature of 133°C to 155°C will be abbreviated as "polymer B1", and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C to less than 133°C will be abbreviated as "polymer B2".

[0145] The glass transition temperature of polymer B1 is preferably 135°C or higher. Furthermore, the glass transition temperature of polymer B2 is preferably 80°C or higher, more preferably 90°C or higher, even more preferably 100°C or higher, and particularly preferably 110°C or higher.

[0146] The mass ratio of polymer B2 to polymer B1, B2 / B1 (where B2 represents the content (parts by mass) of polymer B2 in a polymer having an alicyclic structure, and B1 represents the content (parts by mass) of polymer B1 in a polymer having an alicyclic structure), is not particularly limited. For example, the mass ratio of polymer B2 to polymer B1, B2 / B1, is preferably less than 0.85. In this case, the compatibility between polymer B1 and polymer B2 is increased, which tends to result in a particularly high dielectric breakdown strength at room temperature and a particularly small change in dielectric breakdown strength. B2 / B1 is preferably 0.80 or less, more preferably 0.75 or less, even more preferably 0.70 or less, particularly preferably 0.65 or less, and also preferably 0.10 or more, more preferably 0.20 or more, even more preferably 0.25 or more, and particularly preferably 0.30 or more.

[0147] Even when the polymer having an alicyclic structure includes polymer B1 and / or polymer B2, it is preferable that both polymer B1 and polymer B2 are the aforementioned hydrogenated polystyrene, block copolymer, etc. For example, a combination can be given in which polymer B1 is hydrogenated polystyrene and polymer B2 is a block copolymer (for example, a hydrogenated block copolymer obtained by hydrogenating a styrene-butadiene diblock copolymer).

[0148] The Vicat softening point (1 kg, 50°C / hr) of polymers having an alicyclic structure in their side chains is preferably between 100°C and 170°C. Setting the Vicat softening point above 100°C tends to increase rigidity and electrical insulation at high temperatures, while setting it below 170°C improves stretchability. A Vicat softening point of 120°C to 165°C is more preferable, 130°C to 160°C is even more preferable, and 140°C to 155°C is particularly preferable.

[0149] The glass transition temperature (Tg) and Vicat softening point of polymers having an alicyclic structure can be adjusted by the type of constituent unit having an alicyclic structure in the side chain, or by the type and ratio of one or more other constituent units.

[0150] The weight-average molecular weight (Mw) of the polymer having an alicyclic structure is preferably, for example, between 50,000 and 400,000. In this case, the rigidity, electrical insulation, and stretchability of the stretched film of the present invention tend to be improved.

[0151] The melt mass flow rate (MFR) of a polymer having an alicyclic structure is preferably 1 g / 10 min or more and 40 g / 10 min or less, more preferably 2 g / 10 min or more and 20 g / 10 min or less, and even more preferably 3 g / 10 min or more and 15 g / 10 min or less, as measured at 260°C and 2.16 kgf. In this case, appropriate resin fluidity is obtained when stretching the film, and the stretchability is easily improved.

[0152] Polymers having an alicyclic structure can be manufactured, for example, by known methods, or they can be obtained from the market. An example of a commercially available product is ViviOn® (manufactured by USI Corporation).

[0153] Polypropylene resins may contain polymers having one or more alicyclic structures.

[0154] <Method for producing polymers having an alicyclic structure> The method for producing polymers having an alicyclic structure is not particularly limited, and they can be produced using known methods such as radical polymerization, ionic polymerization (anionic polymerization, coordination anionic polymerization, etc.), bulk polymerization, solution polymerization, and suspension polymerization. Specifically, polymers having an alicyclic structure can be produced by carrying out a polymerization reaction using known initiators such as alkyllithium compounds and dilithium compounds to sequentially polymerize monomers having an alicyclic structure (e.g., vinylcycloolefins); or by sequentially polymerizing monomers having an alicyclic structure and then adding a coupling agent to perform coupling.

[0155] In particular, polymers having an alicyclic structure in their side chains can be produced by polymerizing a monomer having an aromatic ring structure (e.g., styrene) by a known method, followed by a hydrogenation reaction. The hydrogenation reaction can be carried out, for example, by the method described later in the method for producing hydrogenated block copolymers.

[0156] When a hydrogenation reaction is carried out, the hydrogenation rate to the aromatic ring structure is preferably 50 mol% or more, more preferably 80 mol% or more, even more preferably 85 mol% or more, particularly preferably 90 mol% or more, and even more preferably 95 mol% or more. The hydrogenation rate may also be 100 mol%. It is preferable to set the hydrogenation rate within the above range because it improves the stretchability while also tending to result in a glass transition temperature (Tg) of 100°C or higher.

[0157] A polymer having an alicyclic structure may be, for example, a copolymer having structural units with an alicyclic structure in their side chains and one or more other structural units. The copolymer may be a random copolymer or a block copolymer having at least two polymer blocks. From the viewpoint of stretchability, copolymers are preferred, and block copolymers are more preferred. Examples of other structural units include ethylene, propylene, butene, pentene, hexene, heptene, octene, etc., and may or may not have side chains. It may also contain both structural units with side chains and structural units without side chains. Examples of structural units with side chains include propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, etc. The other structural units may be unsaturated hydrocarbons, but saturated hydrocarbons are preferred from the viewpoint of electrical insulation.

[0158] When a polymer having an alicyclic structure contains propylene as another constituent unit, the propylene content in the polymer is less than 50% by mass, preferably 20% by mass or less, and more preferably 10% by mass or less, based on 100% by mass of the polymer.

[0159] Polymers having an alicyclic structure can be obtained, for example, by polymerizing monomers having their respective constituent units using known methods. Furthermore, if the side chain has an aromatic ring structure, a polymer with an alicyclic structure in the side chain can be obtained by hydrogenation. Hydrogenation of polymers with aromatic ring structures in the side chain allows for the industrially inexpensive production of polymers with an alicyclic structure in the side chain.

[0160] <Polypropylene resin> The polypropylene resin contained in the stretched film of the present invention preferably contains the isotactic polypropylene resin described above and the polymer having the alicyclic structure described above, more preferably containing the isotactic polypropylene resin and hydrogenated polystyrene (e.g., polyvinylcyclohexane), and even more preferably containing the isotactic polypropylene resin and hydrogenated polystyrene (polyvinylcyclohexane) having an atactic structure and a hydrogenation rate of 95% or more. Furthermore, the polypropylene resin contained in the stretched film of the present invention may contain the isotactic polypropylene resin and the block copolymer, or it may contain the isotactic polypropylene resin and the polymer B1 and the polymer B2.

[0161] When the polypropylene resin contains an isotactic polypropylene resin and the aforementioned polymer having an alicyclic structure, it is preferable that the isotactic polypropylene resin is present in an amount of 80% to 99% by mass and the polymer having an alicyclic structure is present in an amount of 1% to 20% by mass relative to the total mass of the polypropylene resin. In this case, the range of the polymer having an alicyclic structure, which is a high heat-resistant component, becomes more appropriate, and the orientation of the film tends to be within a good range. As a result, particularly high dielectric breakdown strength can be achieved even in high-temperature environments of 120°C or higher, changes in dielectric breakdown strength tend to be particularly small, and in addition, the long-term durability of the capacitor element in high-temperature environments tends to be improved.

[0162] The polypropylene resin more preferably contains 83% by mass or more of isotactic polypropylene resin, even more preferably 85% by mass or more, even more preferably 97% by mass or less, and even more preferably 95% by mass or less.

[0163] The polypropylene resin more preferably contains 3% by mass or more of a polymer having an alicyclic structure, even more preferably 5% by mass or more, even more preferably 17% by mass or less, and even more preferably 15% by mass or less. In these cases as well, the polymer having an alicyclic structure may preferably be, for example, hydride polystyrene (polyvinylcyclohexane) or the block copolymer, or the polymer having an alicyclic structure may include polymer B1 and polymer B2.

[0164] Polypropylene resins can include other resins besides isotactic polypropylene resins and polymers having an alicyclic structure. Examples of other resins include polyolefin resins and copolymer resins thereof, such as polyethylene, poly(1-butene), polyisobutene, poly(1-pentene), and poly(4-methyl-1-pentene), and copolymers thereof, such as copolymers of α-olefins, such as ethylene-propylene copolymer, propylene-butene copolymer, ethylene-butene copolymer, and ethylene-(4-methyl-1-pentene) copolymer. Other examples include polystyrene resins, elastomers, polyvinyl resins, polyester resins, polyurethane resins, nylon resins, and copolymers thereof. Commercially available resins can be used as other resins, for example, Tuffmer® (manufactured by Mitsui Chemicals, Inc.) is an example of a copolymer of α-olefins and can be suitably used for the aforementioned purposes.

[0165] The polypropylene resin preferably contains 90% or more by mass of isotactic polypropylene resin and polymers having an alicyclic structure, more preferably 95% or more by mass, and even more preferably 99% or less by mass. The polypropylene resin also preferably does not contain any resins other than isotactic polypropylene resin and polymers having an alicyclic structure.

[0166] When the polypropylene resin contains isotactic polypropylene resin and a polymer having an alicyclic structure, the orientation coefficient ΔP is likely to be between 0.007 and 0.0125, or the in-plane birefringence value ΔNyx is likely to be between 0.009 and 0.016. Alternatively, when the polypropylene resin contains isotactic polypropylene resin and a polymer having an alicyclic structure, the above formula (1) and / or formula (2) are likely to be satisfied.

[0167] In stretched films, the birefringence value increases as the orientation (stretching) progresses. Typically, when a polypropylene resin contains isotactic polypropylene resin and a polymer with an alicyclic structure, the orientation coefficient tends to decrease as the content of the alicyclic polymer increases. While this increases the content of the alicyclic polymer improves heat resistance (high-temperature retention rate of dielectric strength), it tends to decrease dielectric strength itself. This is presumed to be due to the "phase separation structure" confirmed by dynamic viscoelasticity measurements. As phase separation progresses, the film becomes more difficult to stretch overall, leading to a decrease in molecular orientation. In this respect, the stretched film 1 of the present invention has its orientation coefficient ΔP or the in-plane birefringence value ΔNyx adjusted to a predetermined range; that is, the orientation is restricted, thus improving dielectric strength and maintaining dielectric strength at high temperatures, achieving an excellent balance between the two. This can also be determined from X-ray diffraction measurements, specifically by determining whether the crystallite size, calculated from the half-width of the diffraction peak ((110) plane originating from the isotactic polypropylene crystal (α-crystal), falls within the aforementioned range. In particular, an increase in crystallite size signifies crystal growth, which positively contributes to improved dielectric strength.

[0168] When polypropylene resins contain isotactic polypropylene resin and polymers with alicyclic structures, they may exhibit a clear peak in the loss tangent (tanδ) in the region above 140°C. Such a peak is the main dispersion peak and may correspond to the glass transition temperature (Tg) of the polymer with an alicyclic structure (e.g., hydride polystyrene). This peak becomes clearer as the content of the polymer with an alicyclic structure (e.g., hydride polystyrene) increases. At the same time, the gentle swelling around 100°C present in polypropylene (100% polypropylene) (which may correspond to lattice relaxation in typical isotactic polypropylene) is lost with the addition of polymers with an alicyclic structure because molecular mobility due to lattice relaxation is suppressed. That is, the loss tangent (tanδ) at 100°C becomes more easily satisfied at 0.15 or less.

[0169] While we do not necessarily desire a restrictive interpretation, the fact that the loss tangent (tanδ) at 100°C is easily less than or equal to 0.15, or that there is a peak in the loss tangent (tanδ) in the region above 140°C, may indicate that the isotactic polypropylene resin and the polymer having an alicyclic structure have a phase-separated structure upon mixing. The structure consisting of the isotactic polypropylene resin and the polymer having an alicyclic structure is by no means a brittle phase-separated structure, and this can be judged from the fact that the film is not cloudy, that it maintains a high Tg (the presence of the aforementioned main dispersion peak), that the loss tangent (tanδ) at 100°C is small, that the lattice relaxation motion of polypropylene is contained (motion suppression effect), and that the temperature dependence of the storage modulus is small and flat with respect to temperature.

[0170] When a polypropylene resin contains isotactic polypropylene resin and polymers having an alicyclic structure, the presence of polymers having an alicyclic structure can be confirmed, for example, by changes in the infrared absorption spectrum. In particular, changes in the infrared absorption spectrum are more likely to occur when the polymer having an alicyclic structure contains hydrogenated polystyrene.

[0171] When the polypropylene resin contains isotactic polypropylene resin and polymers having an alicyclic structure, dynamic viscoelasticity measurements suggest that a "phase separation structure" is formed. By forming such a "phase separation structure," the relaxation motion (molecular chain motion) of polypropylene that occurs at high temperatures can be suppressed. As a result, the decrease in dielectric strength at high temperatures can be suppressed, and the stretched film of the present invention has high dielectric breakdown strength even in high-temperature environments of 120°C or higher, and moreover, the change in dielectric breakdown strength at high temperatures compared to room temperature (e.g., 25°C) is small.

[0172] When the polypropylene resin contains isotactic polypropylene resin and polymers having an alicyclic structure, the ratio of dielectric breakdown strengths (V140 / V25) mentioned above may be closer to 1, and when it contains 10% by mass or more of polymers having an alicyclic structure, the V140 / V25 value will be particularly close to 1.

[0173] While it is preferable that the polypropylene resin includes isotactic polypropylene resin and polymers having an alicyclic structure, the polypropylene resin may be composed of other resins, for example, propylene homopolymers such as syndiotactic polypropylene; copolymers of propylene and other olefins (e.g., ethylene, 1-butene, etc.) (the copolymer may be a random copolymer or a block copolymer having at least two polymer blocks); long-chain branched polypropylene; or polypropylene resin produced from plant-derived raw materials. In this case, the MFR, melting point, mesopentad fraction, heptane insoluble matter (HI), Mn, Mw, Mw / Mn, Mz, and Mz / Mw of the polypropylene resin can all be within the same range as those for the isotactic polypropylene resin described above.

[0174] (Other features of the stretched film of the present invention) The stretched film of the present invention can be obtained using the polypropylene resin described above. The stretched film of the present invention is stretched in at least one direction. Preferably, the stretched film of the present invention is a biaxially oriented film stretched in two directions. Preferably, such a biaxially oriented film is stretched in the MD (flow) direction and the TD (width) direction, respectively.

[0175] The stretched film of the present invention may also contain various additives, to the extent that the effects of the present invention are not impaired. Examples of additives include those found in stretched films used in known capacitor applications, such as antioxidants, necessary stabilizers such as chlorine absorbers and ultraviolet absorbers, lubricants, plasticizers, flame retardants, antistatic agents, and colorants.

[0176] Examples of antioxidants include hindered phenol antioxidants. Among hindered phenol antioxidants, examples of hindered phenol antioxidants having a carbonyl group include triethylene glycol-bis[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl)propionate] (trade name: Irganox 245), 1,6-hexanediol-bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] (trade name: Irganox 259), pentaerythrultyl tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] (trade name: Irganox 1010), and 2,2- Examples include o-diethylenebis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] (trade name: Irganox 1035), octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate (trade name: Irganox 1076), and N,N'-hexamethylenebis(3,5-di-tert-butyl-4-hydroxy-hydrocinnamamide) (trade name: Irganox 1098), but pentaerythrultyl tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], which has excellent heat resistance, is particularly preferred. All Irganox® products are manufactured by BASF Japan Ltd.

[0177] When the stretched film of the present invention contains an antioxidant, the amount is preferably 1,000 ppm by mass or more and 7,000 ppm by mass or less, and more preferably 2,000 ppm by mass or more and 6,000 ppm by mass or less, relative to the total mass of the stretched film. In addition, a portion of the hindered phenol-based antioxidant is oxidized and decomposed during the extrusion process during the stretched film manufacturing process, and the remaining amount in the stretched film is generally 60 to 80% by mass of the above-mentioned content.

[0178] The stretched film of the present invention can be applied to capacitor applications, as well as to various other applications such as packaging and separator applications. In particular, the stretched film of the present invention can be suitably used in capacitor applications, and is suitable for use in high-temperature environments of 120°C or higher, and is extremely suitable for small and high-capacitance capacitors (for example, 5 μF or more, preferably 10 μF or more, and even more preferably 20 μF or more).

[0179] The method for producing the stretched film of the present invention is not particularly limited. For example, the stretched film of the present invention can be produced by manufacturing a cast raw material sheet (unstretched film) using the polypropylene resin and then stretching the cast raw material sheet.

[0180] If the polypropylene resin includes an isotactic polypropylene resin and a polymer having an alicyclic structure, it can be obtained by mixing each resin in a predetermined ratio. For example, melt blending can be used as a mixing method. The polypropylene resin may be subjected to drying treatment or the like as needed.

[0181] The method for manufacturing the cast raw material sheet (unstretched film) is not particularly limited, and a wide range of known methods can be employed. For example, the cast raw material sheet can be manufactured by melt-kneading a polypropylene resin and then extruding it. As for the melt-kneading method, a single-screw type, twin-screw type, or multi-screw type melt-kneader can be used. The temperature during melt-kneading is preferably 200°C to 300°C, and more preferably 220°C to 280°C, considering the balance between suppressing resin degradation and the quality of the kneading. During melt-kneading, it is preferable to purge the kneader with an inert gas such as nitrogen in order to suppress resin degradation.

[0182] The extrusion molding method is not particularly limited; for example, a cast raw material sheet (unstretched film) can be obtained by extruding a molten and kneaded polypropylene resin into a film extruder. The extrusion molding method is not particularly limited, and known extrusion molding methods can be used. The molten and kneaded polypropylene resin may be filtered beforehand. The temperature during extrusion molding is not particularly limited, for example, 200 to 300°C, preferably 210 to 280°C, more preferably 215 to 270°C, and even more preferably 220 to 260°C.

[0183] The extruded, molten polypropylene resin can be cooled using a cooling roll. The surface temperature of the cooling roll is, for example, 30 to 130°C, preferably 35 to 120°C, and more preferably 40 to 110°C. This yields a cast raw material sheet. The thickness of the cast raw material sheet is not particularly limited, but is, for example, 20 to 300 μm.

[0184] The stretched film of the present invention can be obtained by stretching a cast raw material sheet. The stretching method is not particularly limited and examples include: a method of stretching the cast raw material sheet in the longitudinal direction (flow direction, MD) by heating it with a heating roll (longitudinal uniaxial roll stretching method); a method of stretching the cast raw material sheet in the transverse direction (width direction, TD) in an oven at a predetermined temperature (generally called a tenter) (transverse uniaxial stretching method); a method of performing transverse uniaxial stretching after longitudinal uniaxial roll stretching (sequential biaxial stretching method); a method of performing transverse uniaxial stretching after longitudinal uniaxial roll stretching, and then longitudinal uniaxial (roll or tenter method) stretching (multi-stage sequential biaxial stretching method); a method of sequentially stretching the cast raw material sheet longitudinally and transversely in a tenter at a predetermined temperature (tenter method sequential biaxial stretching method); a method of simultaneously stretching the cast raw material sheet longitudinally and transversely in a tenter (simultaneous biaxial stretching method); and so on. As for the stretching method, a method in which longitudinal uniaxial roll stretching is followed by transverse uniaxial stretching (sequential biaxial stretching method) is preferable because it provides excellent rigidity, electrical insulation, and stretchability of the stretched film.

[0185] One example of a sequential biaxial stretching method is to maintain a cast raw material sheet at a temperature of approximately 100-180°C (longitudinal stretching temperature), pass it between rolls with a speed difference to stretch it 3-7 times (longitudinal stretching ratio) in the flow direction, and immediately cool it to room temperature. After cooling, the stretched film is guided to a tenter and stretched at a stretching angle of 5-17° (transverse stretching angle) at a temperature of 150°C or higher (transverse stretching temperature) to approximately 3-11 times (transverse stretching ratio) in the width direction. After relaxation and heat setting, it can be wound up. The wound film is then subjected to an aging treatment in an atmosphere of approximately 20-45°C and can be cut to the desired product width. The transverse stretching angle is defined as the angle formed by a straight line Lx connecting one edge Px in the width direction of the stretched film at the start of the transverse stretching process and the other edge Py (on the same side as Px) in the width direction of the stretched film at the end of the transverse stretching process, and a straight line Ly that starts at Px and is parallel to the extrusion direction. The control of the orientation coefficient ΔP and the in-plane birefringence value ΔNyx, or the control to satisfy equation (1) and / or equation (2), can also be controlled by the stretching method of the stretched film. For example, the birefringence values ​​can be controlled by the stretching ratio in the MD (flow direction) and / or TD (width direction), the temperature during stretching and / or the temperature gradient, or the heat treatment (relaxation) temperature immediately after stretching. As long as the values ​​can be adjusted to within the range of the present invention, there are no particular restrictions on the methods and conditions within the range described in the preceding paragraph.

[0186] The resulting stretched film may be subjected to corona treatment, electrostatic discharge treatment, heating treatment, etc. Appropriate implementation of corona treatment, electrostatic discharge treatment, heating treatment, etc. can improve passability in the vapor deposition process. The heating treatment temperature is preferably 20°C to 80°C, more preferably 25°C to 60°C, and even more preferably 30°C to 55°C. The heating treatment time is preferably 3 hours to 50 hours, and more preferably 6 hours to 30 hours.

[0187] 2. Metal Multilayer Film Capacitors / Film Capacitors The stretched film of the present invention may have a metal layer on one or both sides thereof. That is, a metal laminated film having a metal layer on one or both sides of the stretched film can be obtained using the stretched film of the present invention.

[0188] In a metal laminated film, the metal film can act as an electrode. Examples of the metal film include metal foil, paper with at least one side metallized, and plastic film with at least one side metallized. The metal can be a single metal such as zinc, lead, silver, chromium, aluminum, copper, and nickel, a mixture of several of these, or an alloy thereof. However, considering the environment, economy, and capacitor performance, zinc and aluminum are preferred.

[0189] The metal film can be formed, for example, by vacuum deposition and sputtering, and vacuum deposition is preferred from the viewpoint of productivity and economic efficiency. Vacuum deposition methods generally include the crucible method and the wire method.

[0190] The film resistance of the metal film is preferably about 1 to 100 Ω / □, more preferably 5 Ω / □ or higher, and even more preferably 10 Ω / □ or higher, from the viewpoint of the capacitor's electrical characteristics. Furthermore, from the viewpoint of safety as a capacitor, the film resistance of the metal film is more preferably 50 Ω / □ or lower, and even more preferably 30 Ω / □ or lower. The film resistance of the metal film can be measured during metal deposition, for example, by the four-terminal method known to those skilled in the art. The film resistance of the metal film can be adjusted, for example, by adjusting the output of the evaporation source to adjust the evaporation rate. For the sake of clarity, in this specification, the unit "Ω / □" means "Ω / square".

[0191] When forming a metal film on one side of the film, an insulating margin is formed from one end of the film without deposition for a certain width, so that the film acts as a capacitor when wound. Furthermore, to strengthen the bond between the metal laminated film and the metallicon electrode, it is preferable to form a heavy edge structure at the end opposite the insulating margin. The film resistance of the heavy edge is usually about 1 to 8 Ω / □, and preferably about 1 to 5 Ω / □. The thickness of the metal film is not particularly limited, but for example, 1 to 200 nm is preferred.

[0192] There are no particular restrictions on the margin pattern, and from the standpoint of improving characteristics such as the safety of the capacitor, patterns including so-called special margins such as fishnet patterns and T-margin patterns can be used. As for the method of forming the margin, any known method can be used without any restrictions, such as the tape method, which involves masking with tape during deposition, or the oil method, which involves masking by applying oil.

[0193] The metal laminated film can be processed into the capacitor of the present invention, as described later, by winding it along the longitudinal direction of the film. Specifically, two metal laminated films are stacked as a pair, with the metal vapor-deposited film and polypropylene film alternately laminated and wound together. Then, a pair of metallicon electrodes are formed on both end faces by thermal spraying to produce a film capacitor.

[0194] A capacitor can be manufactured using the above-mentioned metal laminated film for capacitors. As long as the capacitor includes the above-mentioned metal laminated film for capacitors, its other components are not particularly limited; for example, it can have a configuration similar to that of a known capacitor.

[0195] Since the above capacitor is equipped with the stretched film of the present invention, it can have a high dielectric breakdown voltage, and moreover, the change in dielectric breakdown strength under high-temperature environments compared to the dielectric breakdown strength at room temperature (e.g., 25°C) is small. Therefore, the above capacitor can maintain its insulation and capacitance for more than 500 hours without short-circuiting, even when a voltage of, for example, 200 (Vdc / μm) is continuously applied at high temperatures of 135°C or higher. In other words, the above capacitor does not short-circuit at 135°C, and even with a continuous voltage load, the decrease in capacitance is minimal.

[0196] The capacitor of the present invention, utilizing the stretched film of the present invention, is suitable for use in high-temperature environments and can be made into a small and high-capacitance capacitor (for example, 5 μF or more, preferably 10 μF or more, and even more preferably 20 μF or more). Therefore, the capacitor of the present invention can be used in electronic equipment, electrical equipment, etc., as a high-voltage capacitor; various switching power supplies; filter capacitors and smoothing capacitors for converters and inverters, etc. Furthermore, the capacitor of the present invention can be suitably used as an inverter capacitor and converter capacitor for controlling drive motors in electric vehicles, hybrid vehicles, etc., for which demand has been increasing in recent years.

[0197] In identifying the inventions contained herein, the components (properties, structures, functions, etc.) described in each embodiment of this disclosure may be combined in any way. That is, this disclosure encompasses all subject matter consisting of any combination of the combinatable components described herein. [Examples]

[0198] The present invention will be described more specifically below with reference to examples, but the present invention is not limited to the embodiments of these examples.

[0199] (1)Measurement method The various measurement methods are as follows:

[0200] (1-1) Mn, Mw, Mz, Mw / Mn and Mz / Mw of isotactic polypropylene resin Using GPC (gel permeation chromatography), the number-average molecular weight (Mn), weight-average molecular weight (Mw), z-average molecular weight (Mz), molecular weight distribution (Mw / Mn), and molecular weight distribution (Mz / Mw) of isotactic polypropylene resin were measured under the following conditions.

[0201] Specifically, a high-temperature GPC instrument with a built-in differential refractometer (RI), the HLC-8121GPC-HT model, manufactured by Tosoh Corporation, was used. Three TSKgel GMHHR-H(20)HT columns, also manufactured by Tosoh Corporation, were used in conjunction. Measurements were taken at a column temperature of 140°C, with trichlorobenzene flowing as the eluent at a flow rate of 1.0 ml / min. A calibration curve for the molecular weight M was created using standard polystyrene manufactured by Tosoh Corporation, and the measured values ​​were converted to the molecular weight of polypropylene using the Q-factor to obtain the number-average molecular weight (Mn), weight-average molecular weight (Mw), and z-average molecular weight (Mz). The molecular weight distribution (Mw / Mn) was obtained using the Mw and Mn values. The molecular weight distribution (Mz / Mw) was also obtained using the Mz and Mw values.

[0202] (1-2) Mesopentad fraction of isotactic polypropylene resin The isotactic polypropylene resin was dissolved in a solvent and measured using a high-temperature Fourier transform nuclear magnetic resonance spectrometer (high-temperature FT-NMR) under the following conditions. High-temperature nuclear magnetic resonance (NMR) spectrometer: JEOL Ltd., High-temperature Fourier transform nuclear magnetic resonance spectrometer (High-temperature FT-NMR), JNM-ECP500 Observed nucleus: 13C (125MHz) Measurement temperature: 135℃ Solvent: Ortho-dichlorobenzene (ODCB: a mixed solvent of ODCB and deuterated ODCB (mixing ratio = 4 / 1)) Measurement mode: Single-pulse proton broadband decoupling Pulse width: 9.1 μsec (45° pulse) Pulse interval: 5.5 sec Total number of times: 4,500 Shift reference: CH3 (mmmm) = 21.7 ppm The mesopentad fraction, which represents the degree of stereoregularity, was calculated as a percentage (%) from the integral intensity values ​​of each signal derived from combinations of five pentads (mmmm, mrrm, etc.) consisting of pentads arranged in the same direction ("meso(m)") and pentads arranged in opposite directions ("racemo(r)"). For the assignment of each signal derived from mmmm, mrrm, etc., we referred to spectral descriptions such as "T. Hayashi et al., Polymer, Vol. 29, p. 138 (1988)".

[0203] (1-3) Meltmass flow rate (MFR) The melt flow rate (MFR) was measured using a melt indexer from Toyo Seiki Co., Ltd. in accordance with JIS K 7210-1:2014. Specifically, 4 g of raw material was first inserted into a cylinder heated to the test temperature (230°C for isotactic polypropylene resin and 260°C for polymers with an alicyclic structure), and preheated for 3.5 minutes under a load of 2.16 kgf. Then, the weight of the resin extruded from the bottom hole over 30 seconds was measured, and the MFR (g / 10 min) was determined. The above measurement was repeated three times, and the average value was used as the measured MFR.

[0204] (1-4) Melting point, glass transition temperature The following procedure was used to calculate the melting point and glass transition temperature using a PerkinElmer input-compensated DSC, DiamondDSC. 5 mg of each resin was weighed out, placed in an aluminum sample holder, and set in the DSC instrument. The temperature was increased from 30°C to 230°C at a rate of 20°C / min under a nitrogen flow, held at 230°C for 5 minutes, cooled to 30°C at a rate of 20°C / min, and held at 30°C for 5 minutes. The melting point and glass transition temperature were then determined from the DSC curve obtained when the temperature was increased again to 230°C at a rate of 20°C / min. Specifically, the melting point was defined as the melting peak (the largest melting peak if multiple melting peaks were observed) as defined in JIS-K7121:1987 9.1(1), and the glass transition temperature was defined as the midpoint glass transition temperature as defined in JIS-K7121:1987 9.3(1).

[0205] (1-5) Heptane-insoluble content (HI) of polypropylene resins A sample of approximately 3 g was prepared for measurement by press-molding a polypropylene resin to 10 mm x 35 mm x 0.3 mm. Next, approximately 150 mL of heptane was added, and Soxhlet extraction was performed for 8 hours. The heptane-insoluble portion was calculated from the sample mass before and after extraction.

[0206] (2) Raw materials To prepare polypropylene resins for obtaining stretched films, the following isotactic polypropylene resins and polymers having an alicyclic structure were prepared. [A1; Isotactic polypropylene resin A1] As isotactic polypropylene resin A1, we prepared an isotactic polypropylene resin "Prime Polypro (registered trademark); manufactured by Prime Polymer Co., Ltd." having the following physical properties. In addition, BASF Japan Ltd.'s "Irganox 1010" was pre-mixed into isotactic polypropylene resin A1 as an antioxidant at a concentration of 3500 ppm by mass relative to the isotactic polypropylene resin A1. MFR: 3.5g / 10min (measurement temperature 230℃, weight 2.16kg) Melting point: 164℃ Mesopentafil fraction: 98.6 mol% Heptane-insoluble content: 98.1% by mass Number average molecular weight (Mn): 49000 Weight average molecular weight (Mw): 390000 z average molecular weight (Mz): 1520000 Molecular weight distribution (Mw / Mn): 8.0 Molecular weight distribution (Mz / Mw): 3.9

[0207] [B1; Polymer B1 having an alicyclic structure] As polymer B1 having an alicyclic structure, we prepared hydrogenated polystyrene "ViviOn® 0645; manufactured by USI Corporation" having the following physical properties. Glass transition temperature: 143°C (measured by DSC) MFR: 5.5g / 10min (measurement temperature 260℃, weight 2.16kg) Such polymers are polymers having an alicyclic structure with a cyclohexane structure in the side chain, the cyclohexane structure being formed by hydrogenation of the aromatic ring structure, and the hydrogenation rate is 99 mol% or more.

[0208] [B2; Polymer B2 having an alicyclic structure] As polymer B1 having an alicyclic structure, we prepared "ViviOn® 1325; manufactured by USI Corporation" which has the following physical properties. Glass transition temperature: 128℃ MFR: 13g / 10min (measurement temperature 260℃, 2.16kg weight) Such polymer B2 is a polymer having an alicyclic structure with a cyclohexane structure in its side chain, and is a hydrogenated block copolymer obtained by hydrogenating a styrene-butadiene diblock copolymer, and is not a hydrogenated polystyrene polymer. The cyclohexane structure is formed by hydrogenation of the aromatic ring structure derived from styrene, and the other structures are formed by hydrogenation of the carbon-carbon double bond derived from butadiene, with a hydrogenation rate of 99 mol% or more.

[0209] [Examples and comparative examples of stretched film 1] Examples of stretched film 1 (i.e., stretched film A and stretched film B) are shown below. (Example 1) The isotactic polypropylene resin A1 and the polymer B1 having an alicyclic structure were blended and mixed in amounts of 95% by mass and 5% by mass, respectively (i.e., a mass ratio of A1:B1 = 95:5) to prepare the raw material. After dry blending this raw material, it was supplied to a single-screw type film extruder (GM-50, L / D=32, manufactured by GM Engineering Co., Ltd.) and melted at 260°C. The molten raw material was extruded using a T-die, and then solidified by winding it onto a metal drum with a surface temperature maintained at 100°C to produce a cast raw material sheet (unstretched film) with a thickness of approximately 96 μm. Subsequently, this cast raw material sheet was stretched four times in the flow direction at a temperature of 160°C, immediately cooled to room temperature, and then stretched eight times in the transverse direction at a temperature of 165°C using a tenter to obtain a biaxially oriented film with a thickness of 3 μm.

[0210] (Example 2) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymer B1 having the alicyclic structure were blended in amounts of 90% by mass and 10% by mass, respectively (i.e., the mass ratio A1:B1 = 90:10).

[0211] (Example 3) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymer B1 having the alicyclic structure were blended in amounts of 85% by mass and 15% by mass, respectively (i.e., the mass ratio A1:B1 = 85:15).

[0212] (Example 4) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymers B1 and B2 having the alicyclic structure were blended in amounts of 86% by mass, 10% by mass, and 4% by mass, respectively (i.e., the mass ratio A1:B1:B2 = 86:10:4).

[0213] (Example 5) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymers B1 and B2 having the alicyclic structure were blended in amounts of 84% by mass, 7.2% by mass, and 8.8% by mass, respectively (i.e., the mass ratio A1:B1:B2 = 84:7.2:8.8).

[0214] (Comparative Example 1) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that a cast raw material sheet was prepared using only isotactic polypropylene resin A1 without using polymer B1 having the aforementioned alicyclic structure.

[0215] (Comparative Example 2) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymer B1 having the alicyclic structure were blended in amounts of 75% by mass and 25% by mass, respectively (i.e., the mass ratio A1:B1 = 75:25).

[0216] (Comparative Example 3) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymer B2 having the alicyclic structure were blended in amounts of 86% by mass and 14% by mass, respectively (i.e., the mass ratio A1:B2 = 86:14).

[0217] [Examples and Comparative Examples of Stretched Film 2] Examples of stretched film 2 (i.e., stretched film C and stretched film D) are shown below. (Example 1A) The isotactic polypropylene resin A1 and the polymer B1 having an alicyclic structure were blended and mixed in amounts of 95% by mass and 5% by mass, respectively (i.e., a mass ratio of A1:B1 = 95:5) to prepare the raw material. After dry blending this raw material, it was supplied to a single-screw type film extruder (GM-50, L / D=32, manufactured by GM Engineering Co., Ltd.) and melted at 260°C. The molten raw material was extruded using a T-die, and then wrapped around a metal drum with a surface temperature maintained at 95°C to solidify, producing a cast raw material sheet (unstretched film) with a thickness of approximately 96 μm. Subsequently, this cast raw material sheet was stretched four times in the flow direction at a temperature of 158°C, immediately cooled to room temperature, and then stretched eight times in the transverse direction at a temperature of 165°C using a tenter to obtain a biaxially oriented film with a thickness of 3 μm.

[0218] (Example 2A) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1A, except that the isotactic polypropylene resin A1 and the polymer B1 having the alicyclic structure were blended in amounts of 90% by mass and 10% by mass, respectively (i.e., the mass ratio A1:B1 = 90:10).

[0219] (Example 3A) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1A, except that the isotactic polypropylene resin A1 and the polymer B1 having the alicyclic structure were blended in amounts of 85% by mass and 15% by mass, respectively (i.e., the mass ratio A1:B1 = 85:15).

[0220] (Example 4A) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1A, except that the isotactic polypropylene resin A1 and the polymers B1 and B2 having the alicyclic structure were blended in amounts of 86% by mass, 10% by mass, and 4% by mass, respectively (i.e., the mass ratio A1:B1:B2 = 86:10:4).

[0221] (Example 5A) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1A, except that the isotactic polypropylene resin A1 and the polymers B1 and B2 having the alicyclic structure were blended in amounts of 84% by mass, 7.2% by mass, and 8.8% by mass, respectively (i.e., the mass ratio A1:B1:B2 = 84:7.2:8.8).

[0222] (Comparative Example 1A) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that a cast raw material sheet was prepared using only isotactic polypropylene resin A1 without using polymer B1 having the aforementioned alicyclic structure.

[0223] (Comparative example 2A) A biaxially oriented film with a thickness of 3 μm was obtained in the same manner as in Example 1, except that the isotactic polypropylene resin A1 and the polymer B2 having the alicyclic structure were blended in amounts of 86% by mass and 14% by mass, respectively (i.e., the mass ratio A1:B2 = 86:14).

[0224] (Evaluation method) <Dynamic Viscoelasticity Measurement> As a dynamic viscoelasticity measuring instrument, we used the "Viscoelasticity Measuring Device (Model: DMS6100)" manufactured by Seiko Instruments Corporation. As a measurement sample, we cut a stretched film into strips of 50 mm in the longitudinal direction and 10 mm in the transverse direction, with the TD direction being perpendicular to the film flow direction (MD direction) as the long axis. In accordance with JIS-K7244 (1999 edition), we measured the temperature dependence (temperature dispersion data) of the dynamic viscoelasticity of the film under the measurement conditions shown below. Test mode: Tensile mode Chuck spacing: 20mm Vibration frequency: 1Hz Distortion amplitude: 10μm Minimum tension: 20mN Tension gain: 1.2 Initial force amplitude: 100mN Temperature range: -30 to 180°C Heating rate: 2°C / min Measurement atmosphere: In air Measured thickness: Approximately 3.0 μm From the measurement results obtained by the above measurement method, temperature dispersion data of the dynamic viscoelasticity of the stretched film can be obtained. From the temperature dispersion data, the temperature of the main dispersion peak of the loss tangent (tanδ), the loss tangent (tanδ) value at 100 °C, and the storage elastic modulus (E') at 25 °C and 135 °C were determined. Examples of the measurement results of the logarithmic value of the storage elastic modulus (logE') and the temperature dependence of the loss tangent (tanδ) are shown in FIG. 1 (Stretched film 1) and FIG. 2 (Stretched film 1).

[0225] <Differential scanning calorimeter (DSC): Melting peak measurement> A 5 mg sample was cut out from the stretched film, sealed in an aluminum pan, and input compensation differential scanning calorimetry was performed using a differential scanning calorimeter (Diamond DSC manufactured by PerkinElmer). In the measurement, the temperature was raised from -50 °C to 280 °C at a rate of 20 °C / min under a nitrogen atmosphere. The melting peak temperature was determined from the results of the first heating.

[0226] <X-ray diffraction intensity measurement (XRD)> The X-ray diffraction intensity measurement of the stretched film was carried out using an XRD (wide-angle X-ray diffraction) apparatus (manufactured by Rigaku) under the following conditions. Measuring device: Manufactured by Rigaku, X-ray diffractometer Mini-FLEX300 X-ray source: CuKα ray monochromator wave (wavelength: 0.15418 nm) Irradiation output: 30 KV - 10 mA Scattering slit: 1.25 deg Receiving slit: 1.25 deg Scanning axis: 2θ / θ Scanning speed: 0.5 deg / min From the obtained data, using an analysis computer and the integrated powder X-ray analysis software PDXL (Ver. 2.1.3.4) attached to the device, the interplanar spacing value d of the diffraction line of the α crystal (110) plane was calculated.

[0227] <Infrared absorption spectrum measurement (IR)> The infrared absorption spectrum of the stretched film was measured using a Fourier transform infrared spectrophotometer (manufactured by JASCO Corporation). The absorbance spectrum against wavenumber was measured using the ATR method with a prism in close contact with the stretched film (sample) under the following conditions. Measurement equipment: JASCO Corporation, Fourier transform infrared spectrophotometer FT / IR-4000; ATR unit: ATR-PRO410-M Prism: ZnSe Incident angle: 45° Scanning range: 4000cm -1 ~650cm -1 Count: Auto (121 times) Resolution: 4cm -1 Gain: Auto Aperture: Auto Scan speed: Auto Filter: Auto

[0228] <Film thickness> The thickness of the stretched film was measured in accordance with JIS-C2330:2014, except that it was measured at 100±10kPa using a Citizen Seimitsu MEI-11 paper thickness gauge.

[0229] <Total light transmittance> The total light transmittance of the stretched film was measured using a haze meter NDH-5000 manufactured by Nippon Denshoku Industries Co., Ltd., in accordance with JIS-K7361:1997.

[0230] <Evaluation of surface roughness (arithmetic mean height Sa)> The arithmetic mean height Sa of the stretched films obtained in the examples and comparative examples was measured as follows. A "VertScan2.0 (model: R5500GML)" manufactured by Ryoka Systems Co., Ltd. was used as the optical interferometry non-contact surface shape measuring instrument. As a sample for measurement, the film was cut to an arbitrary size of about 20 cm square, and with the wrinkles sufficiently smoothed out, it was set on the measurement stage using an electrostatic contact plate or the like. The WAVE mode was used for measurement, and a 530 white filter and a 1×BODY microscope tube were applied, and observations were made for each field of view (470.92 μm × 353.16 μm) using a 10x objective lens. This operation was performed at 5 locations (total of 10 locations) at 1 cm intervals in both the flow direction and the width direction, starting from the center point in both directions of the surface on the chill roll side of the target sample, and data was obtained. The data obtained from the above measurements was subjected to noise reduction using a median filter (3x3), and then Gaussian filtering with a cutoff value of 30 μm was applied to remove the waviness component. This made it possible to appropriately measure the condition of the roughened surface. Next, the analysis was performed using the "ISO parameter" function in the "Bearing" plugin of the "VS-Viewer" analysis software for "VertScan2.0" to determine the arithmetic mean height Sa (μm), and the average value of each value obtained at the above 10 locations was calculated. Measurements were taken on both the front and back sides, and the value from the larger side was adopted for all parameters.

[0231] <Calculation of orientation coefficient ΔP and measurement of birefringence value> The orientation coefficient ΔP of the stretched film was calculated using equation (1A) above, based on the birefringence values ​​ΔNyx, ΔNxz, and ΔNyz obtained from the retardation (phase difference) measurements using the tilt method. For the retardation (phase difference) measurement using the tilt method, an Otsuka Electronics RE-100 retardation measuring device was used, with a 550 nm wavelength LED light source. More specifically, the birefringence values ​​ΔNyx, ΔNxz, and ΔNyz were calculated using the following procedure.

[0232] Specifically, the principal axes in the in-plane direction of the film were defined as the x-axis and y-axis, and the thickness direction of the film (normal to the in-plane direction) was defined as the z-axis. The lagging axis in the direction with a higher refractive index within the in-plane direction was defined as the y-axis. The retardation values ​​were then determined when the y-axis was tilted at 10° intervals with respect to the z-axis in the range of 0° to 50°. From the obtained retardation values, referring to the description in the aforementioned non-patent literature, the birefringence ΔNyz in the y-axis direction relative to the thickness direction (z-axis direction), the birefringence ΔNxz in the x-axis direction relative to the thickness direction (z-axis direction) with the x-axis perpendicular to the y-axis were used, and the in-plane birefringence ΔNyx (referred to as in-plane birefringence ΔNyx) was calculated as follows. First, for each tilt angle φ, the measured retardation value R was divided by the tilt-corrected thickness d to obtain R / d, and the R / d when φ=0° was defined as the in-plane birefringence ΔNyx.

[0233] Furthermore, for each R / d at φ=10°, 20°, 30°, 40°, and 50°, the difference with the R / d at φ=0° was calculated, and these differences were further divided by sin2r(r: angle of refraction) to obtain the birefringence ΔNzx at each φ. By reversing the sign of this value, the birefringence value ΔNxz was obtained. The average value of ΔNzx at φ=20°, 30°, 40°, and 50° was calculated, and the birefringence value ΔNxz was obtained from this average value. ΔNyz was calculated from the difference between the in-plane birefringence ΔNyx and ΔNxz. The values ​​of the angle of refraction r at each tilt angle for polypropylene, and the values ​​of the intrinsic refractive index of polypropylene for obtaining the thickness correction value, were based on the description on page 109 of the aforementioned non-patent document.

[0234] The birefringence values ​​were calculated as described above, and ΔP of the stretched film A was derived using equation (1A) mentioned earlier.

[0235] <Method for calculating the ratio of dielectric breakdown strength (V140 / V25)> The ratio of the dielectric breakdown strength of the stretched films obtained in the examples and comparative examples at high temperature (140°C) and 25°C was evaluated as follows. First, a measuring apparatus conforming to JIS C2151:2006 17.2.2 (flat plate electrode method) was prepared. However, instead of the elastic material described in JIS C2151:2006 17.2.2, conductive rubber (E12S10 manufactured by Seiwa Electric Co., Ltd.) was used as the lower electrode, and no aluminum foil wrapping was performed. The measurement environment was a forced-circulation oven set to a temperature of 140°C or 25°C. The electrodes and film were preheated in the oven for 30 minutes before use. The voltage increase was started from 0V and increased at a rate of 100V / second, and the voltage when the current value exceeded 5mA was defined as the dielectric breakdown voltage. Dielectric breakdown voltage measurements were taken 20 times. Each dielectric breakdown voltage value Vdc was divided by the thickness of the stretched film (μm), and the average of the 16 values ​​obtained by excluding the top 2 and bottom 2 values ​​from the 20 calculations was defined as the dielectric breakdown strength (Vdc / μm). The obtained dielectric breakdown strength was defined as the dielectric breakdown strength of the stretched film, and the dielectric breakdown strength V140 (Vdc / μm) of the stretched film at high temperature (140°C environment) was divided by the dielectric breakdown strength of the stretched film at room temperature (25°C) to calculate the dielectric breakdown strength ratio "V140 / V25".

[0236] <Short-time withstand voltage and long-term durability of the element (capacitance change rate ΔC)> An aluminum metal layer was formed on the polypropylene film described above using a vapor deposition apparatus (ULVAC, Inc., product name: EWE-060 roll-type vacuum vapor deposition apparatus) such that the surface resistivity of the metal film was 20 Ω / □. At this time, the vapor deposition was performed using the oil margin method so that after slitting, an insulating groove (insulating margin: length 1 mm in the width direction) continuous in the longitudinal direction of the film was formed at one end in the width direction of the film. After slitting this film, a metallized film with a total width of 30 mm was obtained. The thickness of the metallized film was 3 μm.

[0237] Next, two metallized films were joined together. Using a 3KAW-N2 automatic winding machine manufactured by Kaito Seisakusho Co., Ltd., the joined metallized films were wound 1527 times at a winding tension of 140-180g, a contact pressure of 200-255g, and a winding speed of 4m / s. The element wound under a load of 5.2kg / cm 2 The element was heat-treated at 135°C for 15 hours while being pressed. After that, zinc metal was sprayed onto the end faces of the element. The spraying conditions were a feed rate of 15 mm / s, a spraying voltage of 22 V, and a spraying pressure of 0.3 MPa, and the spraying was carried out to a thickness of 0.7 mm. A flat-type capacitor was thus obtained. Lead wires were soldered to the end faces of the flat-type capacitor. After that, the flat-type capacitor was sealed with epoxy resin. The epoxy resin was cured by heating at 90°C for 2.5 hours, followed by heating at 120°C for another 2.5 hours. The capacitance of the finished capacitor was 50 μF.

[0238] [Short-time withstand voltage of the element at 135°C] The capacitor obtained above was preheated at 135°C for 1 hour, and its capacitance was measured using a HIOKI LCR HiTester 3522-50 (initial capacitance). Next, a DC voltage of 800V was applied to the capacitor for 10 seconds in a constant temperature bath at 135°C. The capacitance of the capacitor after voltage application was measured in the same manner, and the capacitance change rate before and after application was calculated using the following formula. (Percentage change in capacitance) = [(Capacitance after voltage application) - (Initial capacitance)] / (Initial capacitance) × 100 (%) Next, the capacitor was placed back into the constant temperature bath at 135°C, the DC voltage was increased by 50V (i.e., to 850V), and the capacitance change rate was measured in the same procedure. Thereafter, while increasing the DC voltage by 50V each time, the capacitance change rate was repeatedly measured in the same procedure until the capacitance change rate reached -0.5% or less. The voltage value when the capacitance change rate reached -0.5% or less was calculated as the value converted per film thickness. The above tests were conducted using a total of five capacitors, and the voltage values when the capacitance change rate reached -0.5% or less in the same procedure were calculated as the values converted per film thickness for each capacitor. Based on the average value of these, the short-time withstand voltage of the element at 135°C was evaluated.

[0239] [Long-term durability of the element (life characteristics)] The initial capacitance of the obtained capacitor before the test was measured using an LCR high tester 3522-50 manufactured by Hioki E.E. Corporation. Next, in a high-temperature bath at 135°C, a DC voltage of 650V (about 217V / μm) was continuously applied to the capacitor for 500 hours. After 500 hours, the capacitance of the capacitor was similarly measured, and the capacitance change rate before and after the voltage application was calculated using the following formula (Rate of change of capacitance)=[(Capacitance after voltage application)-(Initial capacitance)] / (Initial capacitance)×100(%) The test was conducted with two samples, and the long-term durability of the element was evaluated based on the average value.

[0240] [Heating and tensile test] [Stress F100(23) at 100% elongation in the film flow direction measured at 23°C] The stress F100(23) at 100% elongation in the film flow direction, measured at 23℃, was determined using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm was cut out. At this time, the sample was cut so that the flow direction was in the length direction. The sample was set in the chuck of a tensile testing machine (A&D Co., Ltd. "Tensilon Universal Testing Machine RTG-1210") with a chuck distance of 50 mm, and a tensile test was performed at a test speed of 100 mm / min. F100(23)(MPa) was calculated by dividing the load value at 100% elongation in the tensile test by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm).

[0241] [Stress F100(135) at 100% elongation in the film flow direction measured at 135℃] The stress F100(135) at 100% elongation in the film flow direction measured at 135℃ was performed using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm was cut out. At this time, the sample was cut so that the flow direction was the length direction. The sample was set in the chuck of a tensile testing machine (A&D Co., Ltd. "Tensilon Universal Testing Machine RTG-1210") with a distance of 50 mm between the chucks, and then the chuck and the sample were placed in an oven heated to 135℃, heated for 1 minute, and then a tensile test was performed at a test speed of 100 mm / min. F100(135)(MPa) was calculated by dividing the load value at 100% elongation in the tensile test by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm).

[0242] [Measurement method for F(23M) and F(23T)] The stress F(23M) at the point of maximum stress in the film flow direction and the stress F(23T) at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 23°C, were measured using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm was cut out. At this time, the sample was cut out so that the measurement direction was the length direction. The sample was set in the chuck of a tensile testing machine (A&D Co., Ltd. "Tensilon Universal Testing Machine RTG-1210") with a chuck distance of 50 mm, and a tensile test was performed at a test speed of 100 mm / min. The load value at which the sample broke in the tensile test was divided by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm), and the value when the measurement direction was the MD direction was calculated as F(23M) (MPa), and the value when the measurement direction was the TD direction was calculated as F(23T) (MPa).

[0243] [Measurement methods for F(135M) and F(135T)] The stress F(135M) at the point of maximum stress in the film flow direction and the stress F(135T) at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 135°C, were measured using the following procedure. First, a rectangular sample with a length of 150 mm and a width of 15 mm was cut out. At this time, the sample was cut out so that the measurement direction was the length direction. The sample was set in the chuck of a tensile testing machine (A&D Company, Limited "Tensilon Universal Testing Machine RTG-1210") with a distance of 50 mm between the chucks, and then the chuck and the sample were placed in an oven heated to 135°C. After heating for 1 minute, a tensile test was performed at a test speed of 100 mm / min. The load value at which the sample broke in the tensile test was divided by the cross-sectional area of ​​the sample before the tensile test (thickness of the sample before the tensile test × width of 15 mm), and the value when the measurement direction was the MD direction was calculated as F(135M) (MPa), and the value when the measurement direction was the TD direction was calculated as F(135T) (MPa).

[0244] <Thermal shrinkage rate> [MD direction] Biaxially oriented films obtained in the examples and comparative examples were cut into rectangles 20 mm wide and 130 mm long to prepare measurement samples. At this time, the samples were cut so that the length direction coincided with the MD direction. Three of these measurement samples were prepared. Next, the length 100 mm was measured with a ruler and a mark was made at that point. The three measurement samples were suspended without load in a 140°C hot air circulating constant temperature bath and held for 15 minutes. After that, they were cooled to room temperature (23°C), the distance between the markings was measured with a ruler, and the thermal shrinkage rate (%) in the MD direction was calculated using the following formula. Thermal shrinkage rate (%) = [(gauge before heating - gauge after heating) / (gauge before heating)] × 100 The average of the three measured values ​​was used as the thermal shrinkage rate (%) in the MD direction. Other measurement conditions were followed according to JIS C 2151:2019, "25. Dimensional Change". [TD direction] Biaxially oriented films obtained in the examples and comparative examples were cut into rectangles with a width of 20 mm and a length of 130 mm to prepare measurement samples. The thermal shrinkage rate (%) in the TD direction was calculated in the same manner as the thermal shrinkage rate in the MD direction, except that the sample was cut so that its length coincided with the TD direction.

[0245] (Evaluation results of stretched film 1) Table 1 shows the physical properties and evaluation results of the stretched film. In Table 1, A1 refers to isotactic polypropylene resin A1, A2 refers to "isotactic polypropylene resin A2", B1 refers to "polymer B1 having an alicyclic structure", and B2 refers to "polymer B2 having an alicyclic structure". In Table 1, blank spaces indicate 0% by mass (i.e., the corresponding resin was not used).

[0246] In Table 1, "temperature at which the main dispersion peak was observed" refers to the loss tangent (tanδ) peak clearly observed in the region above 140°C, and "tanδ at 100°C" refers to the loss tangent (tanδ) at 100°C obtained based on the temperature dispersion data. Furthermore, the first melting peak temperature (DSC) and the second melting peak temperature (DSC) refer to the peak top temperatures observed at 170–175°C and 165–170°C, respectively, in the DSC measurement. In Table 1, the infrared absorption spectrum is 80–890 cm⁻¹. -1 Absorption peaks are observed in the range, and at 1450 cm. -1 If a shoulder peak due to absorption was observed in the vicinity, it was indicated as "present," and if not observed, it was indicated as "absent."

[0247] Table 1 shows that when the orientation coefficient ΔP of the stretched film 1 is 0.007 or more and 0.0125 or less, or when the in-plane birefringence value ΔNyx is 0.009 or more and 0.016 or less, it has high dielectric breakdown strength even in high-temperature environments. In other words, the stretched film 1 of the example has a high ratio of dielectric breakdown strength at 140°C to room temperature (e.g., 25°C) "V140 / V25" (close to "1"), the change in dielectric breakdown strength between high temperature and room temperature is small, the dielectric breakdown strength is maintained, and the long-term durability of the capacitor element in high-temperature environments can be improved, which is desirable.

[0248] Based on the above, the capacitor using the stretched film 1 obtained in the example as the dielectric film does not short-circuit even when a voltage of, for example, 200 (Vdc / μm) or more is continuously applied at a high temperature of 135°C, and can maintain its insulation and capacitance for more than 500 hours. In other words, the above capacitor does not short-circuit even at 135°C, and the decrease in capacitance is small even when a continuous voltage load is applied.

[0249] [Table 1]

[0250] Figure 1 shows an example of temperature dispersion data for dynamic viscoelasticity obtained by dynamic viscoelasticity measurement. This temperature dispersion (temperature dependence) data shows the relationship between temperature (X axis) and tanδ (second Y axis), and the relationship between temperature (X axis) and the logarithm of the storage modulus (first Y axis). In Figure 1, the solid line represents the storage modulus LogE'(Pa), and the dashed line represents the loss tangent tanδ.

[0251] As shown in Figure 1, the stretched film 1 obtained in the example had a loss tangent tanδ of 0.15 or less at 100°C, and a clear main dispersion peak of the loss tangent (tanδ) was observed in the region above 140°C.

[0252] Figure 2 shows the results of the infrared absorption spectrum of stretched film 1, where (a) shows the infrared absorption spectrum measurement at 850-950 cm⁻¹. -1 (b) is within the range of 1400-1500 cm. -1 This indicates the range.

[0253] Figure 2 shows that the infrared absorption spectrum of the stretched film 1 obtained in the example was 880-890 cm⁻¹. -1 Absorption peaks are observed in the range, and at 1450 cm. -1 It was found that there is a shoulder peak due to absorption in the vicinity.

[0254] (Evaluation results of stretched film 2) Table 2 shows the physical properties and evaluation results of stretched film 2. In Table 2, A1 refers to isotactic polypropylene resin A1, B1 refers to "polymer B1 having an alicyclic structure", and B2 refers to "polymer B2 having an alicyclic structure". In Table 2, "temperature at which the main dispersion peak was observed" is the same as in Table 1.

[0255] Table 2 shows that when Fa > 0.13 (Fa is the same as above) or Fb > 0.31 (Fb is the same as above), the stretched film has high dielectric breakdown strength even in high-temperature environments. In other words, the stretched film 2 of the example has a high ratio of dielectric breakdown strength at 140°C to room temperature (e.g., 25°C) "V140 / V25" (close to "1"), the change in dielectric breakdown strength between high temperature and room temperature is small, the dielectric breakdown strength is maintained, and the long-term durability of the capacitor element in high-temperature environments can be improved, which is desirable.

[0256] Based on the above, the capacitor using the stretched film 2 obtained in the example as the dielectric film does not short-circuit even when a voltage of, for example, 200 (Vdc / μm) or more is continuously applied at a high temperature of 135°C, and can maintain its insulation and capacitance for more than 500 hours. In other words, the above capacitor does not short-circuit even at 135°C, and the decrease in capacitance is small even when a continuous voltage load is applied.

[0257] [Table 2]

[0258] Figure 3 shows an example of temperature dispersion data for dynamic viscoelasticity obtained by dynamic viscoelasticity measurement of stretched film 2. This temperature dispersion (temperature dependence) data shows the relationship between temperature (X axis) and tanδ (second Y axis), and the relationship between temperature (X axis) and the logarithm of the storage modulus (first Y axis). In Figure 3, the solid line represents the storage modulus LogE'(Pa), and the dashed line represents the loss tangent tanδ.

[0259] As shown in Figure 3, the stretched film 2 obtained in the example had a loss tangent tanδ of 0.15 or less at 100°C, and a clear main dispersion peak of the loss tangent (tanδ) was observed in the region above 140°C.

Claims

1. A stretched film containing a polypropylene resin, The polypropylene resin comprises an isotactic polypropylene resin and a polymer having an alicyclic structure, wherein the polymer having an alicyclic structure comprises polymer B1 having an alicyclic structure with a glass transition temperature of 133°C to 155°C and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C to less than 133°C. The following formula (1A) can be derived from the birefringence value. ΔP=(ΔNxz+ΔNyz) / 2 (1A) (In equation (1A), ΔNxz represents the birefringence value in the x-axis direction relative to the thickness direction (z-axis direction), and ΔNyz represents the birefringence value in the y-axis direction relative to the thickness direction (z-axis direction).) A stretched film in which the value of the orientation coefficient ΔP, represented by [formula], is 0.007 or greater and 0.0125 or less.

2. A stretched film containing a polypropylene resin, The polypropylene resin comprises an isotactic polypropylene resin and a polymer having an alicyclic structure, wherein the polymer having an alicyclic structure comprises polymer B1 having an alicyclic structure with a glass transition temperature of 133°C to 155°C and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C to less than 133°C. A stretched film having an in-plane birefringence value ΔNyx of 0.009 or greater and 0.016 or less.

3. A stretched film containing a polypropylene resin, The polypropylene resin comprises an isotactic polypropylene resin and a polymer having an alicyclic structure, wherein the polymer having an alicyclic structure comprises polymer B1 having an alicyclic structure with a glass transition temperature of 133°C to 155°C and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C to less than 133°C. When the stress at 100% elongation in the film flow direction measured at 23°C is F100(23) and the stress at 100% elongation in the flow direction measured at 135°C is F100(135), then the following formula (1) F100(135) / F100(23)>0.13 (1) A stretched film that satisfies the requirements.

4. A stretched film containing a polypropylene resin, The polypropylene resin comprises an isotactic polypropylene resin and a polymer having an alicyclic structure, wherein the polymer having an alicyclic structure comprises polymer B1 having an alicyclic structure with a glass transition temperature of 133°C to 155°C and polymer B2 having an alicyclic structure with a glass transition temperature of 70°C to less than 133°C. Let F(23M) be the stress at the point of maximum stress in the film flow direction measured at 23°C. Let F(23T) be the stress at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 23°C, and let F(135M) be the stress at the point of maximum stress in the film flow direction, measured at 135°C. When the stress at the point of maximum stress in the direction perpendicular to the film flow direction, measured at 135°C, is denoted as F(135T), The following formula (2) {F(135M)+F(135T)} / {F(23M) + F(23T)} > 0.31 (2) A stretched film that satisfies the requirements.

5. The stretched film according to any one of claims 1 to 4, wherein the mass ratio B2 / B1 of polymer B2 to polymer B1 is less than 0.85.