Highly functional polyisocyanates modified with allophanate groups and optionally isocyanurate groups, and production thereof

Abstract

The invention relates to a polyisocyanate which is modified with allophanate groups and optionally isocyanurate groups and has a proportion of allophanate groups of ≥ 50 mol.% to ≤ 100 mol.%, preferably ≥ 50 mol.% to ≤ 99 mol.%, preferably ≥ 60 mol.% to ≤ 98 mol.%, particularly preferably ≥ 70 mol.% to ≤ 98 mol.%, in each case based on the total amount of allophanate groups and isocyanurate groups in the modified polyisocyanate and determined by means of NMR spectroscopic analysis, and which can be obtained from the reaction of a composition containing or consisting of A) a mixture of A1) 1,1,1-trimethylolpropane and A2) 1,3-butanediol and / or 1,4-butanediol and B) at least one monomeric diisocyanate which has aliphatically and / or cycloaliphatically bonded isocyanate groups. The invention likewise relates to a method for producing said modified polyisocyanates.

Description

[0001] 2024PF30016-Abroad

[0002] 1

[0003] Highly functional polyisocyanates modified with allophanate groups and optionally isocyanurate groups, and their production

[0004] The invention relates to a polyisocyanate modified with allophane groups and optionally isocyanurate groups, having an allophane group content of > 50 mol% to < 100 mol%, preferably > 50 mol% to < 99 mol%, more preferably > 60 mol% to < 98 mol%, and particularly preferably > 70 mol% to < 98 mol%, in each case based on the total amount of allophane groups and isocyanurate groups in the modified polyisocyanate and determined by NMR spectroscopic analysis, which is obtainable from the reaction of a composition containing or consisting of A) a mixture of A1,1,1-trimethylolpropane and A2) 1,3-butanediol and / or 1,4-butanediol and B) at least one monomeric diisocyanate having aliphatic and / or cycloaliphatic isocyanate groups bonded to it. The invention also relates to the process for producing these modified polyisocyanates.

[0005] Monomeric diisocyanates are practically never used as crosslinking agents in polyurethane systems due to their volatility and toxicological properties. Higher molecular weight derivatives, modified with, for example, uretdione, isocyanurate, iminooxadiazine, urethane, or allophanate groups, are generally used. An overview of these polyisocyanates and their preparation methods is given, for example, in Laas et al., J. Prakt. Chem. 336, 1994, 185-200.

[0006] The modification of monomeric diisocyanates with allophane groups is achieved by addition to isocyanate-reactive species. WO 2019 / 062383 Al and EP 4 303 246 Al describe the synthesis of highly functional allophane-modified polyisocyanates, including those based on 1,1,1-trimethylolpropane (TMP) and hexamethylene diisocyanate (HDI). A problem with this synthesis is the poor miscibility of the isocyanate with TMP, which is solid at room temperature. The mixture cannot be completely homogenized, even with molten TMP. This can lead to gel particle formation and thus to the formation of inhomogeneous products. One object of the present invention was to solve this problem.

[0007] Allophane-modified polyisocyanates based on TMP are highly functional but also exhibit high viscosity. The former leads to products with high hardness and chemical resistance in application. However, the high viscosity makes handling the polyisocyanates difficult. Therefore, a further objective of the present invention was to provide corresponding highly functional, yet low-viscosity, allophane-modified polyisocyanates.

[0008] The aforementioned problems were solved by using a mixture of 1,1,1-trimethylolpropane with 1,3-butanediol and / or 1,4-butanediol in the synthesis of the allophane-modified polyisocyanates. 2024PF30016-Abroad

[0009] 2

[0010] The present invention relates to a polyisocyanate modified with allophane groups and optionally isocyanurate groups, having an allophane group content of > 50 mol% to < 100 mol%, preferably > 50 mol% to < 99 mol%, more preferably > 60 mol% to < 98 mol%, and particularly preferably > 70 mol% to < 98 mol%, in each case based on the total amount of allophane groups and isocyanurate groups in the modified polyisocyanate and determined by NMR spectroscopic analysis, which is obtainable from the reaction of a composition containing or consisting of

[0011] A) a mixture of Al) 1,1,1-trimethylolpropane and A2) 1,3-butanediol and / or 1,4-butanediol, and

[0012] B) at least one monomeric diisocyanate having aliphatic and / or cycloaliphatic isocyanate groups bonded to it.

[0013] Another subject matter is a process for the production of polyisocyanates modified with allophane groups and optionally isocyanurate groups according to the above description, wherein a composition of the above-mentioned type is reacted.

[0014] Mixture A):

[0015] According to the invention, a mixture of Al) 1,1,1-trimethylolpropane and A2) 1,3-butanediol and / or 1,4-butanediol is used.

[0016] In a preferred embodiment, the weight ratio of Al to A2 is from 1 : 10 to 10 : 1, preferably from 1 : 5 to 5 : 1, particularly preferably from 1 : 2 to 2 : 1.

[0017] It is also possible to use other alcohols besides mixture A), i.e. mono- and / or polyols with a functionality > 2 A'), wherein their total proportion is a maximum of 20 wt% (> 0 to < 20 wt%), preferably a maximum of 10 wt% (> 0 to < 10 wt%), in each case based on the weight of mixture A).

[0018] Examples of such alcohols A') include mono- or polyhydric alcohols with up to 15 carbon atoms, preferably 2 to 6 carbon atoms, such as methanol, ethanol, n-propanol, isopropanol, n-butanol, n-hexanol, 2-ethyl-1-hexanol, ethylene glycol, propylene glycol, 2-ethyl-1,3-hexanediol or glycerol; ether alcohols, such as 1-methoxy-2-propanol, 3-ethyl-3-hydroxymethyloxetane, tetrahydrofurfuryl alcohol, ethylene glycol monomethyl ether,

[0019] Ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, diethylene glycol, dipropylene glycol or also liquid higher molecular weight polyethylene glycols, polypropylene glycols, mixed polyethylene / polypropylene glycols and their monoalkyl ethers; ester alcohols, such as ethylene glycol monoacetate, propylene glycol monolaurate, glycerol mono- and diacetate, 2024PF30016-Abroad

[0020] 3

[0021] Glycerol monobutyrate or 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate; unsaturated alcohols such as allyl alcohol, 1,1-dimethylallyl alcohol or oleic alcohol; araliphatic alcohols such as benzyl alcohol; N-monosubstituted amides, such as N-methylformamide, N-methylacetamide, cyanacetamide or 2-pyrrolidinone, tetrahydrofuryl alcohol, the isomeric pentanediols, hexanediols, heptanediols and octanediols, 1,10-decanediol, 1,2- and 1,4-cyclohexanediol, 1,4-cyclohexanedimethanol, 4,4'-(1-methylethylidene)-biscyclohexanol, 1,1,1-trimethylolethane, 1,2,6-hexanetriol, 2,2-bis(hydroxymethyl)-1,3-propanediol, bis-(2-hydroxyethyl)-hydroquinone, 1,2,4- and 1,3,5-trihydroxycyclohexane or 1,3,5-tris(2-hydroxyethyl)-isocyanurate, but also simple ester alcohols, such as Hydroxypivalic acid neopentyl glycol ester.

[0022] Suitable hydroxy-functional compounds also include the higher molecular weight polyhydroxyl compounds of the polyester, polycarbonate, polyester carbonate or polyether type, which are known per se, especially those in the molecular weight range of 200 to 2000 g / mol.

[0023] Polyester polyols suitable as hydroxy-functional compounds are, for example, those with a medium molecular weight of 200 to 4000 g / mol, preferably 250 to 2500 g / mol, calculable from functionality and hydroxyl number, with a hydroxyl group content of 1 to 21 wt.%, preferably 2 to 18 wt.%, as they can be produced in a manner known per se by reacting polyhydric alcohols, for example those mentioned above with 2 to 14 carbon atoms, with subtractive amounts of polyhydric carboxylic acids, corresponding carboxylic anhydrides, corresponding polycarboxylic acid systems of lower alcohols or lactones.

[0024] The acids or acid derivatives used to produce polyester polyols can be aliphatic, cycloaliphatic, and / or aromatic in nature and may be substituted and / or unsaturated, for example, by halogen atoms. Examples of suitable acids include polyhydric carboxylic acids with a molecular weight in the range of 118 to 300 g / mol or their derivatives, such as buccane, adipic acid, sebacic acid, phthalic acid, isophthalic acid, trimellitic acid, phthalic anhydride, tetrahydrophthalic acid, maleic acid, maleic anhydride, dimeric and trimeric fatty acids, dimethyl terephthalate, and bisglycol terephthalate.

[0025] Any mixtures of these exemplary starting compounds can also be used to produce polyester polyols.

[0026] An alternative type of polyester polyol to be used as a hydroxyfunctional compound are those that can be prepared in a known manner from lactones and simple polyhydric alcohols, such as those mentioned above, as starter molecules via ring opening. Suitable lactones for the preparation of these polyester polyols include, for example, β-propiolactone, γ-butyrolactone, γ- and 5-valerolactone, β-caprolactone, 3,5,5- and 3,3,5-trimethylcaprolactone, or any mixtures of such lactones. 2024PF30016-Abroad

[0027] 4

[0028] Polyhydroxyl compounds of the polycarbonate type that are suitable as hydroxy-functional compounds include, in particular, the polycarbonate diatoms known per se, such as those that can be produced, for example, by reacting dihydric alcohols, such as those mentioned above in the list of polyhydric alcohols of the molecular weight range 62 to 400 g / mol, with diaryl carbonates, such as diphenyl carbonate, dialkyl carbonates, such as dimethyl carbonate, or phosgene.

[0029] Polyhydroxyl compounds of the polyester carbonate type suitable as hydroxyfunctional compounds are in particular the diols having known ester and carbonate groups, such as those that can be obtained, for example, according to the teaching of DE-A 1 770 245 or WO 03 / 002630 by reacting dihydric alcohols with lactones of the type mentioned above as examples, in particular s-caprolactone, and subsequently reacting the resulting polyester diols with diphenyl carbonate or dimethyl carbonate.

[0030] Polyether polyols suitable as hydroxyfunctional compounds are, in particular, those with a medium molecular weight of 200 to 2000 g / mol, preferably 250 to 1000 g / mol, calculable from functionality and hydroxyl number, with a hydroxyl group content of 1.6 to 25 wt.%, preferably 3.6 to 20 wt.%, as they can be obtained in a manner known per se by alkoxylation of suitable starter molecules. Any polyhydric alcohols, such as the simple polyhydric alcohols with 2 to 14 carbon atoms described above, can be used as starter molecules for the preparation of these polyether polyols. Alkylene oxides suitable for the alkoxylation reaction are, in particular, ethylene oxide and propylene oxide, which can be used in any order or in a mixture in the alkoxylation reaction.

[0031] Suitable polyether polyols are also the polyoxytetramethylene glycols known per se, such as those that can be obtained by polymerization of tetrahydrofuran according to H. Meerwein et al., Angew. Chem. 72, 1960, 927 - 934.

[0032] However, the use of such higher molecular weight polyols is not preferred.

[0033] Mixtures of the above-mentioned alcohols A') can also be used.

[0034] Diisocyanate B):

[0035] In this context, the term "aliphatic" is defined as non-aromatic hydrocarbon groups that are saturated or unsaturated.

[0036] In the present context, the term "alicyclic" or "cycloaliphatic" is defined as possibly substituted, carbocyclic or heterocyclic compounds or units that are not aromatic.

[0037] According to the invention, monomeric diisocyanates having aliphatic and / or cycloaliphatic isocyanate groups are used. 2024PF30016-Abroad

[0038] 5

[0039] Suitable monomeric diisocyanates can be produced by any method, e.g. by phosgenation or by a phosgene-free method, for example by urethane cleavage.

[0040] Suitable monomeric diisocyanates, hereinafter also referred to as starting diisocyanates, are, for example, those in the molecular weight range of 154 to 400 g / mol, such as 1,6-diisocyanatohexane (HDI), 1,5-diisocyanatopentane (PDI), 1,5-diisocyanato-2,2-dimethylpentane, 2,2,4- or 2,2,4-diisocyanate.2,4,4-Trimethyl-1,6-diisocyanatohexane, 1,8-Diisocyanatooctane, 1,9-Diisocyanatoonane, 1,10-Diisocyanatodecane, 1,3- and 1,4-Diisocyanatocyclohexane, 1,4-Diisocyanato-3,3,5-trimethylcyclohexane, 1,3-Diisocyanato-2-methylcyclohexane, 1,3-Diisocyanato-4-methylcyclohexane, 1-Isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane (isophorone diisocyanate; IPDI), 1-Isocyanato-1-methyl-4(3)-isocyanatomethylcyclohexane, 2,4'- and 4,4'-Diisocyanatodicyclohexylmethane (H12-MDI), 1,3- and 1,4-Bis(isocyanatomethyl)cyclohexane 4,4'-Diisocyanato-3,3'-dimethyldicyclohexylmethane, 4,4'-Diisocyanato-3,3',5,5'-tetramethyldicyclohexylmethane, 4,4'-Diisocyanato-1,1'-bi(cyclohexyl), 4,4'-Diisocyanato-3,3'-dimethyl-1,1'-bi(cyclohexyl), 4,4'-Diisocyanato-2,2',5,5'-tetra-methyl-1,1'-bi(cyclohexyl), 1,8-Diisocyanato-p-menthane, 1,3-Diisocyanatoadamantane, 1,3-Dimethyl-5,7-diisocyanatoadamantane, and any mixtures of such diisocyanates.Further suitable diisocyanates can also be found, for example, in Justus Liebig's Annalen der Chemie, 562, 1949, 75-136.

[0041] Particularly preferred starting diisocyanates are aliphatic diisocyanates of the type mentioned, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane, 2,4'- and 4,4'-diisocyanatodicyclohexylmethane, as well as any mixtures of these diisocyanates. 1,5-Diisocyanatopentane (PDI) and 1,6-Diisocyanatohexane (HDI) and mixtures thereof are especially suitable.

[0042] In the case that mixtures of different starting diisocyanates are used, it is particularly preferred that < 30 wt.%, preferably < 10 wt.% and particularly preferably > 0 to < 5 wt.% of the total starting diisocyanates used are cycloaliphatic diisocyanates and the remainder are aliphatic diisocyanates.

[0043] Proceedings

[0044] To produce the polyisocyanates according to the invention, modified with allophane groups and optionally isocyanurate groups, a composition containing or consisting of component A) and B) is reacted.

[0045] The starting diisocyanates of component B) and hydroxy functional compounds of components A) and, if present, A'), are reacted, preferably in an equivalent ratio of isocyanate groups to hydroxyl groups of 4:1 to 200:1, preferably from 5:1 to 50:1, and particularly preferably from 7:1 to 30:1. 2024PF30016-Abroad

[0046] 6

[0047] Allophanatization is a two-step process in which a hydroxyl group first reacts with an isocyanate group to form a urethane. This is then reacted with another isocyanate group to form an allophanate. These two processes can be carried out simultaneously or sequentially. A sequential approach is preferred to better control the resulting exothermic reaction.

[0048] Urethanization is preferably carried out thermally and without a catalyst, but can also be catalyzed at lower temperatures. Suitable urethanization catalysts include those known to those skilled in the art, such as organotin compounds or amine catalysts. Examples of organotin compounds include dibutyltin diacetate, dibutyltin dilaurate, dibutyltin bisacetoacetonate, and tin carboxylates such as tin octoate. These tin catalysts can optionally be used in combination with amine catalysts such as aminosilanes or 1,4-diazabicyclo[2.2.2]octane. Further examples of urethanization catalysts suitable for use according to the invention are inorganic tin compounds such as SnC12 or tin-free compounds such as salts of bismuth, e.g., bismuth octoate, or other metals such as zinc compounds, titanium compounds, or zirconium compounds.The catalyst used in the subsequent allophanatization reaction can also be used. This would then take place at a lower temperature and / or lower catalyst concentration, so that little or no allophanatization reaction occurs in this step.

[0049] It is also possible in this way to use the entire amount of allophanatization catalyst at elevated temperature and simplify the two-step process into a one-step reaction. However, this is not preferred, so the allophanatization catalyst is only added when the urethane groups are to be converted wholly or partially to allophanate groups. The subsequent conversion to allophanate can be carried out uncatalyzed as a thermally induced allophanatization. Preferably, however, suitable catalysts are used to accelerate the reaction. Catalysts can be used that accelerate the formation of allophanate groups or of allophanate and simultaneously isocyanurate groups.

[0050] Suitable catalysts include, for example, simple tertiary amines such as triethylamine, tributylamine, N,N-dimethylaniline, N-ethylpiperidine, N,N'-dimethylpiperazine, or tertiary phosphines such as triethylphosphine, tributylphosphine or dimethylphenylphosphine.

[0051] Other suitable catalysts are the tertiary hydroxyalkylamines described in GB 2 221 465, such as triethanolamine, N-methyldiethanolamine, dimethylethanolamine, N-isopropyldiethanolamine, and l-(2-hydroxyethyl)pyrrolidine, or the catalyst systems known from GB 2 222 161, which consist of mixtures of tertiary bicyclic amines, such as DBU, with simple, low-molecular-weight aliphatic alcohols. 2024PF30016-Abroad

[0052] 7

[0053] A variety of different metal compounds are also suitable as catalysts.

[0054] Suitable examples include the octoates and naphthenates of manganese, iron, cobalt, nickel, copper, zinc, zirconium, cerium, or lead, or their mixtures with acetates of lithium, sodium, potassium, calcium, or barium, as described in DE-A 3 240 613 as catalysts; the sodium and potassium salts of linear or branched alkanecarboxylic acids with up to 10 carbon atoms, such as those of propionic acid, butyric acid, valeric acid, caproic acid, heptanoic acid, caprylic acid, pelargonic acid, capric acid, and undecylenic acid, as known from DE-A 3 219 608; and the alkali or alkaline earth metal salts of aliphatic, cycloaliphatic, or aromatic mono- and polycarboxylic acids with 2 to 20 carbon atoms, such as sodium benzoate or potassium benzoate, as known from EP-A 0 100 129. the alkali metal phenoxides known from GB 1 391 066 A and GB 1 386 399 A, such as sodium phenoxide or potassium phenoxide;the alkali and alkaline earth metal oxides, hydroxides, carbonates, alkoxides and phenoxides known from GB 809 809, alkali metal salts of enolizable compounds, and metal salts of weak aliphatic and / or cycloaliphatic carboxylic acids, such as sodium methoxide, sodium acetate, potassium acetate, sodium acetoacetate, lead 2-ethylhexanoate and lead aphthenate; the basic alkali metal compounds complexed with crown ethers or polyether alcohols known from EP-A 0 056 158 and EP-A 0 056 159, such as complexed sodium or potassium carboxylates; the pyrrolidinone potassium salt known from EP-A 0 033 581; the monocyclic or polycyclic complex compounds of titanium, zirconium and / or hafnium known from EP-A 2 883 895, such as zirconium tetra-n-butoxide, zirconium tetra-2-ethylhexanoate and zirconium tetra-2-ethylhexylate;as well as tin compounds of the type described in the European Polymer Journal, 16, 1979, 147-148, such as dibutyltin dichloride, diphenyltin dichloride, triphenylstannanol, tributyltin acetate, tributyltin oxide, zinn octoate, dibutyl(dimethoxy)stannan and tributyltin imidazolate.;

[0055] Other suitable catalysts include, for example, the quaternary ammonium hydroxides known from DE-A 1 667 309, EP-A 0 013 880 and EP-A 0 047 452, such as

[0056] Tetraethylammonium hydroxide, trimethylbenzylammonium hydroxide, N-(2-Hydroxyethyl)-N,N-Dimethyl-N-(2,2'-dihydroxymethyl 1)-ammonium hydroxide and 1-(2-Hydroxyethyl)-1,4-diazabicyclo[2.2.2]octane hydroxide (monoadduct of ethylene oxide and water to 1,4-diazabicyclo[2.2.2]octane); the quaternary hydroxyalkylammonium hydroxides known from EP-A 37 65 or EP-A 10 589, such as N,N,N-trimethyl-N-(2-hydroxyethyl)-ammonium hydroxide; the trialkylhydroxyalkylammonium carboxylates known from DE-A 2631733, EP-A 0 671 426, EP-A 1 599 526 and US 4,789,705, such as N,N,N-trimethyl-N-2-hydroxypropyl-ammonium p-tert-butyl benzoate and N,N,N-trimethyl-N-2-hydroxypropylammonium 2-ethylhexanoate; the quaternary 2024PF30016-Ausland known from EP-A 1 229 016

[0057] 8

[0058] Benzylammonium carboxylates, such as N-benzyl-N,N-dimethyl-N-ethylammonium pivalate, N-benzyl-N,N-dimethyl-N-ethylammonium-2-ethylhexanoate, N-benzyl-N,N,N-tributylammonium-2-ethylhexanoate, N,N-dimethyl-N-ethyl-N-(4-methoxybenzyl)-ammonium-2-ethylhexanoate or N,N,N-tributyl-N-(4-methoxybenzyl)-ammonium pivalate; the tetrasubstituted ammonium α-hydroxycarboxylates known from WO 2005 / 087828, such as tetramethylammonium lactate; the quaternary ammonium or phosphonium fluorides known from EP-A 0 339 396, EP-A 0 379 914 and EP-A 0 443 167, such as N-methyl-N,N,N-trialkylammonium fluorides with C8-C 1 O -alkyl radicals, N,N,N,N,N-tetra-n-butylammonium fluoride, N,N,N-trimethyl-N-benzylammonium fluoride, tetramethylphosphonium fluoride,

[0059] Tetraethylphosphonium fluoride or tetra-n-butylphosphonium fluoride; the quaternary ammonium and phosphonium polyfluorides known from EP-A 0 798 299, EP-A 0 896 009 and EP-A 0 962 455, such as benzyltrimethylammonium hydrogen polyfluoride; the tetraalkylammonium alkyl carbonates known from EP-A 0 668 271, which are obtainable by reacting tertiary amines with dialkyl carbonates; or quaternary ammonium alkyl carbonates with a betaine structure; the quaternary ammonium hydrogen carbonates known from WO 1999 / 023128, such as choline bicarbonate; the quaternary ammonium salts obtained from tertiary amines and alkylating esters of phosphoric acids, known from EP 0 102 482, such as reaction products of triethylamine, DABCO or N-methylmorpholine with dimethylmethanephosphonate; or the tetrasubstituted ammonium salts of lactams known from WO 2013 / 167404, such as trioctylammonium caprolactamate or dodecyltrimethylammonium caprolactamate.

[0060] These catalysts can be used individually or in any mixture with each other.

[0061] The catalysts are generally used in an amount of 0.0005 to 5.0 wt.%, preferably 0.0010 to 1.0 wt.% and particularly preferably 0.0015 to 0.1 wt.%, in each case based on the amount of starting diisocyanates B) used.

[0062] The catalysts are added either as such or dissolved in a suitable organic solvent. Preferred catalyst solvents are those that possess reactive groups towards isocyanates and can therefore be incorporated into the polymer. These include, for example, mono- or polyhydric alcohols such as methanol, ethanol, α-propanol, isopropanol, α-butanol, α-hexanol, 2-ethyl-1-hexanol, ethylene glycol, propylene glycol, isomers of butanediol, 2-ethyl-1,3-hexanediol, glycerol, and ether alcohols such as α-methoxy-2-propanol, 3-ethyl-3-hydroxymethyloxetane, tetrahydrofurfuryl alcohol, and ethylene glycol monomethyl ether.

[0063] Ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, diethylene glycol, dipropylene glycol, polyethylene glycols, polypropylene glycols, mixed polyethylene-polypropylene glycols and their monoalkyl ethers, 2024PF30016-Foreign

[0064] 9

[0065] Ester alcohols such as ethylene glycol monoacetate, propylene glycol monolaurate, glycerin diacetate, glycerol monobutyrate or 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, unsaturated alcohols such as allyl alcohol, 1,1-dimethylallyl alcohol or oleyl alcohol, araliphatic alcohols such as benzyl alcohol or monosubstituted amides such as N-methylformamide, N-methylacetamide, cyanoacetamide or 2-pyorrolidinone or mixtures of such solvents.

[0066] The dilution level of the catalyst solutions typically corresponds to a concentration of 0.05 to 20 wt.%, preferably 0.1 to 10 wt.%, particularly preferably 0.5 to 5 wt.%.

[0067] The quantities of polyols used as catalyst solvents are not included in the quantities of components A) or A') used.

[0068] The reaction preferably takes place under an inert gas atmosphere at a temperature in the range of 0 °C to 150 °C, preferably in the range between 40 °C and 130 °C and particularly preferably between 70 °C and 120 °C.

[0069] The allophanatization is preferably continued until all urethane groups have been largely converted to allophanate groups. The degree of conversion is preferably at least 70% and particularly preferably at least 80%.

[0070] Once the desired degree of conversion is reached, the reaction can be stopped to prevent subsequent side reactions. This can be achieved, for example, by cooling the reaction mixture. Preferably, the reaction is stopped by adding a catalyst poison and optionally by subsequently heating the reaction mixture to a temperature above 80 °C.

[0071] Suitable catalyst poisons (stoppers) are known to those skilled in the art. These include, for example, hydrochloric acid, phosphoric acid, phosphonic acid, carboxylic acid chlorides such as acetyl chloride, benzoyl chloride or isophthaloyl dichloride, sulfonic acids or sulfonic acid esters such as methanesulfonic acid esters, p-toluenesulfonic acid, trifluoromethanesulfonic acid, perfluorobutanesulfonic acid, dodecylbenzenesulfonic acid, p-toluenesulfonic acid methyl ester, p-toluenesulfonic acid ethyl ester, mono- or dialkyl phosphates such as tridecyl phosphate, dibutyl phosphate, dioctyl phosphate, or silylated acids such as trimethylsilyl methanesulfonic acid ester, trimethylsilyl trifluoromethanesulfonic acid ester, tris(trimethylsilyl) phosphate or diethyl(trimethylsily) phosphate.

[0072] The amount of catalyst poison required to stop the reaction depends significantly on the amount of catalyst used. Generally, an equivalent amount of the stopper is necessary, but since some of the catalyst can be deactivated by other means, a smaller amount of stopper may suffice.

[0073] The catalyst poison can also be added as such or in solution, with the previously listed catalyst solvents being suitable as solvents. In addition to these, 2024PF30016-Abroad

[0074] 10

[0075] Solvents can also be used as starting isocyanates to dissolve the catalyst poisons.

[0076] After the reaction is complete, the starting diisocyanate is separated from the reaction product. This is preferably done by distillation, for example at a pressure below 5 mbar, more preferably below 1 mbar, and particularly preferably below 0.5 mbar, and for example at a temperature in the range of 100 to 200 °C, preferably in the range of 120 to 180 °C. The residual content of monomeric diisocyanate after distillation is preferably < 0.50 wt.%, more preferably < 0.3 wt.%, and more preferably < 0.10 wt.%.

[0077] The modified polyisocyanates obtainable by the processes described above are characterized by an allophanate group content of at least 50 mol% (> 50 mol% to < 100 mol%), based on the total amount of allophanate and isocyanurate groups in the modified polyisocyanate. Preferably, they exhibit an allophanate group content of > 50 mol% to < 99 mol%, particularly preferably > 60 mol% to < 98 mol%, and most preferably > 70 mol% to < 98 mol%, in each case based on the total amount of allophanate and isocyanurate groups in the modified polyisocyanate.

[0078] The isocyanurate group content is accordingly a maximum of 50 mol% (> 0 mol% to < 50 mol%), preferably > 1 mol% to < 50 mol%, particularly preferably > 2 mol% to < 40 mol%, most preferably > 2 mol% to < 30 mol%, based on the total amount of allophanate groups and isocyanurate groups in the modified polyisocyanate.

[0079] The levels of allophanate groups and isocyanurate groups in the modified polyisocyanate are determined by NMR spectroscopic analysis.

[0080] In addition to modification with allophanate groups and optionally isocyanurate groups, the polyisocyanates may also contain urethane, urea, uretdione, and / or hninooxadiazine ione groups in minor amounts. "Minor amounts" means that their total proportion is a maximum of 15 mol% (> 0 to < 15 mol%), preferably a maximum of 10 mol% (> 0 to < 10 mol%), based on the total amount of allophanate and isocyanurate groups in the modified polyisocyanate. Their contents are also determined by NMR spectroscopic analysis.

[0081] The contents (mol %) of allophanate groups and isocyanurate groups, as well as of urethane, uretdione and / or hninooxadiazindeione groups, are preferably determined from the integrals of proton-decoupled 13C-NMR spectra were calculated. A Bruker AV III HD 600 NMR spectrometer with probe Z150361 001 (CP BBO 600SS3 BB-H&F-05 ZE T) was used. With a repetition time (Dl) of 4 s and a measurement time (AQ) of 1.57 s, it is generally assumed that very similar carbonyl carbon atoms are comparable via integration. In the case of hexamethylene diisocyanate-based polyisocyanates dissolved in CDCL, the individual structural elements exhibit 2024PF30016-Ausland

[0082] The following chemical shifts (in ppm) were observed: Allophanate: 155.7 and 153.8 (one carbon atom each); Isocyanurate: 148.4 (three carbon atoms); Iminooxadiazindione: 147.8, 144.3 and 135.3 (one carbon atom each); Uretdione: 157.1 (two carbon atoms); Urethane: 156.3 (one carbon atom); Urea: 158-161 (one carbon atom).

[0083] Preferably, the polyisocyanates modified according to the invention with allophanate groups and optionally isocyanurate groups have a mean isocyanate functionality > 4 and / or a weight-average molecular weight of 5 = 1000 g / mol, particularly preferably a mean isocyanate functionality > 5 and / or a weight-average molecular weight of > 1500 g / mol determined according to EN ISO 13885-1:2021-11.

[0084] The average isocyanate functionality of the polyisocyanate contained is determined according to the following formula:

[0085] Mn(GPC)

[0086] F(GPC) = -

[0087] 100 x 42

[0088] %NCO(Titr.)

[0089] Where the isocyanate group content is given as wt.% and is determined titrimetrically according to DIN EN ISO 11909:2007-05 and the number-mean molecular weight is determined by GPC according to DIN EN ISO 13885-1:2021-11 using polystyrene as standard and tetrahydrofuran as eluent.

[0090] Preferably, the polyisocyanates modified according to the invention with allophanate groups and optionally isocyanurate groups have a viscosity of at most 50,000 mPas at 23°C, preferably at most 25,000 mPas at 23°C, particularly preferably at most 10,000 mPas at 23°C, wherein the viscosity is determined according to DIN EN ISO 3219: 1994-10 at a shear rate of 250 s-1.

[0091] The present invention also relates to the use of the polyisocyanates modified according to the invention with allophanate groups and optionally isocyanurate groups for the production of coatings, sealants and adhesives, as well as the coatings, sealants and adhesives themselves. These can be one- or two-component systems.

[0092] To produce one-component systems, the isocyanate groups of the polyisocyanates modified according to the invention can be blocked. In one embodiment, the isocyanate groups of the polyisocyanates modified according to the invention are therefore present at least partially in a form blocked by at least one blocking agent G). This means that at least (>) 70 mol%, preferably at least (>) 85 mol%, particularly preferably at least (>) 95 mol% of the isocyanate groups are present in a form blocked by blocking agents. 2024PF30016-Abroad

[0093] 12

[0094] A blocking agent is a compound that reacts with an isocyanate group and can be cleaved from it again under defined conditions. All blocking agents commonly used in polyurethane chemistry can be employed for this purpose. Examples include alcohols, lactams, oximes, malonic acid esters, alkylacetoacetates, triazoles, imidazoles, pyrazoles and amines such as butanone oxime, diisopropylamine, 1,2,4-triazole, dimethyl-1,2,4-triazole, imidazole, diethyl malonate, acetoacetic acid esters, acetone oxime, 3,5-dimethylpyrazole, 8-caprolactam, N-methyl, N-ethyl, N-(iso)propyl, Nn-butyl, N-isobutyl, N-tert-butylbenzylamine or 1,1-dimethylbenzylamine, N-alkyl-N-1,1-dimethylmethylphenylamine, adducts of benzylamine to compounds with activated double bonds such as malonic esters, N,N-dimethylaminopropylbenzylamine and other tertiary amino groups containing optionally substituted benzylamines and / or dibenzylamine.Other examples of suitable blocking agents are CH-acidic cyclic ketones with an electron-withdrawing group in the ortho position to the keto group, such as an ester group, a sulfoxide group, a sulfone group, a nitro group, a phosphonate group, a nitrile group, an isonitrile group or a carbonyl group, as well as hydrocarbon resins with phenolic OH groups and optionally substituted phenols, such as cashew nut shell products containing at least cardanol and / or cardol, as described, for example, in WO 2021 / 204741 Al.

[0095] However, its use in 2-component applications without blocking agents is preferred.

[0096] The coatings, sealants, and adhesives may contain compounds with isocyanate-reactive groups. The isocyanate-reactive compounds preferably have a functional group count of > 2 to < 6 and are preferably selected from the group consisting of -OH, -SH, -NH, -NH2, and -(H)N-N2H.

[0097] Preferred are hydroxyfunctional compounds, for example the hydroxyfunctional compounds already described above.

[0098] In a preferred embodiment, polyacrylate polyols, polyether polyols, polyester polyols and / or polyester urethane polyols are used.

[0099] The coating materials, sealants, and adhesives according to the invention can also contain catalysts for controlling the curing rate, for example, catalysts commonly used in isocyanate chemistry, such as tert-amines like triethylamine, pyridine, methylpyridine, benzyldimethylamine, N,N-endoethylenepiperazine, N-methylpiperidine, pentamethyldiethylenetriamine, N,N-dimethylaminocyclohexane, N,N'-dimethylpiperazine, or metal salts like iron(III) chloride, zinc chloride, zinc 2-ethylcaproate, tin(II) octanoate, tin(II) ethylcaproate, dibutyltin(IV) dilaurate, bismuth(III) 2-ethylhexanoate, bismuth(III) octoate, or molybdenum glycolate. 2024PF30016-Abroad

[0100] 13

[0101] The coating materials, sealants, and adhesives according to the invention may also contain the following components: additives for the formulation of coating materials such as leveling agents, wetting agents, adhesion promoters, thickeners, antioxidants, color pigments, pigments, coalescing agents, defoamers, deaerators, etc. A further object of the invention is substrates comprising the coating materials, sealants, or adhesives in uncured, partially cured, or fully cured form.

[0102] Depending on the application, substrates such as glass, metal, fabric, leather, fibers, paper, wood, plastic, stone and concrete are suitable.

[0103] Another object of the invention is a method for coating a substrate comprising the steps i) providing an optionally pretreated substrate, ii) applying a coating agent available according to the above use and iii) partially or completely hardening the coating agent.

[0104] 2024PF30016-Abroad

[0105] 14

[0106] Examples:

[0107] Unless otherwise stated, all percentages refer to weight.

[0108] The NCO content was determined titrimetrically according to DIN EN ISO 11909:2007-05.

[0109] The residual monomer contents were measured by gas chromatography with an internal standard according to DIN EN ISO 10283:2007-11.

[0110] All viscosity measurements were performed using a Physica MCR 51 rheometer from Anton Paar Germany GmbH (DE) according to DIN EN ISO 3219: 1994-10 at a shear rate of 250 s-1.

[0111] Discharge times were determined according to DIN EN ISO 2431 :2012-03 using a discharge cup with a 5 mm nozzle.

[0112] The drying properties of the coating systems were determined according to DIN 53 150:2002-09.

[0113] The gloss of the coatings obtained was measured reflectometrically according to DIN EN ISO 2813: 1999-06 at a 20° angle.

[0114] The determination of the pendulum damping according to König was carried out according to DIN EN ISO 1522:2007-04 on glass plates.

[0115] 13C-NMR spectra were acquired using a Bruker AV III HD 600 NMR spectrometer with probe Z150361 001 (CP BBO 600SS3 BB-H&F-05 ZE T). 512 scans were performed, with a repetition time (Dl) of 4 s and a measurement time (AQ) of 1.57 s.

[0116] Molecular weights were measured by gel permeation chromatography according to DIN EN ISO 13885-1:2021-11. Four columns were used (2x PSS SDV 50A, 5p, 2x PSS SDV 100A, 5p).

[0117] To test the coatings for solvent resistance, small amounts of the solvents xylene, 1-methoxypropyl-2-acetate, ethyl acetate, and acetone were placed in test tubes and a cotton ball was placed at the opening to create a solvent-saturated atmosphere inside the test tubes. The test tubes, with the cotton ball still attached, were then placed on the surface of the coatings applied to glass and left there for 5 minutes. After wiping off the solvent, the film was inspected for damage / softening / loss of adhesion and evaluated (0 = no change, 5 = film completely dissolved). The evaluations for the four solvents (2024PF30016-Foreign) are given in the following order: xylene, 1-methoxypropyl-2-acetate, ethyl acetate, and acetone, in the form of four consecutive numbers.

[0118] Polyisocyanate 1 (according to the invention)

[0119] 49.56 kg of hexamethylenediisocyanate (Desmodur® H, Covestro Deutschland AG) were placed in a 1001 reactor, inerted three times with nitrogen, and heated to 100°C. A mixture of 554.6 g of trimethylolpropane and 690.3 g of 1,3-butanediol was added slowly, dropwise, over one hour. The mixture dissolved immediately in the polyisocyanate. Stirring continued at 100°C for approximately 1.5 hours until an NCO of 46.5% was reached. Subsequently, the catalyst (2.54 g of zinc octoate dissolved in 48.26 g of 2-ethylhexanol) was added in four equal portions, successively (approximately five minutes each). Stirring continued at 100°C for approximately one hour until an NCO of 44.2% was reached. The reaction was then stopped by adding the stopper solution (5.08g ortho-phosphoric acid in 45.72g 2-ethylhexanediol).

[0120] After filtration, the excess HDI was separated using a thin-film evaporator at 130°C. 0.22 g of isophthaloyl chloride in 4.14 g of isopropanol was added to the resin (approx. 11 kg) for stabilization. It had the following properties:

[0121] NCO content: 19.8% monomeric HDI: 0.07%

[0122] Viscosity (23°C): 5200 mPas

[0123] Polyisocyanate 2 (non-inventive, polyisocyanurate polyisocyanate)

[0124] HDI polyisocyanate containing isocyanurate groups, prepared by catalytic trimerization of HDI according to Example 11 of EP-A 330 966, with the modification that the reaction was stopped at an NCO content of 40% in the crude mixture by the addition of dibutyl phosphate. Subsequently, unreacted HDI was separated by thin-film distillation at a temperature of 130°C and a pressure of 0.2 mbar. The resulting polyisocyanate initially had a viscosity of 3000 mPas (23°C) and was then diluted with butyl acetate to a polyisocyanate content of 90 wt%. It exhibited the following characteristics.

[0125] NCO content: 19.6% monomeric HDI: 0.08%

[0126] Viscosity (23°C): 500 mPas

[0127] Polyisocyanate 3 (non-inventory, polyisocyanurate / allophanate polyisocyanate)

[0128] 100 parts of hexamethylene diisocyanate (HDI) were placed in a container and heated to 105 °C. At this temperature, 10 parts of trimethylolpropane were added while stirring. This resulted in a reaction (2024PF30016-Ausland).

[0129] 16

[0130] A turbidity appeared, which only cleared after some time. After completion of the urethanation reaction, the reaction temperature was lowered to 95 °C. Subsequently, the trimerization and allophantation reactions were initiated by adding a 0.5% trimethylbenzylammonium hydroxide solution in 2-ethylhexanol. Upon reaching an NCO value of 36%, the reaction was stopped by adding a stopper solution (10% dibutyl phosphate in HDI) in a weight ratio of 100 parts catalyst solution to 3 parts stopper solution. The mixture was stirred for a further 30 minutes at 95 °C, and then the remaining monomeric HDI was separated in a short-path evaporator at 140 °C and 0.1 mbar. The resulting polyisocyanate initially had a viscosity of 35,000 mPas (23 °C) and was diluted with butyl acetate to 80 wt% polyisocyanate content. It then exhibited the following characteristics.

[0131] NCO content: 15.4% monomeric HDI: 0.07%

[0132] Viscosity (23°C): 500 mPas

[0133] Application example

[0134] Varying parts by weight of a commercially available polyester polyol (SETALUX® DA 665; Allnex GmbH, Wiesbaden, Germany) with a solids content of 65 wt% (in butyl acetate / xylene) and another polyester polyol (SETALUX® 91767 VX-60; Allnex GmbH, Wiesbaden, Germany) with a solids content of 60 wt% (in solvent naphtha / xylene) were mixed with 4 parts by weight of a 40% solution of a commercially available HALS light stabilizer (Hostavin® 3070P, Clariant International Ltd, Muttenz, Switzerland) in methoxypropyl acetate, 16 parts by weight of a 50% solution of a commercially available UV absorber (Hostavin® 3400 liq, Clariant International Ltd, Muttenz, Switzerland) in methoxypropyl acetate, and 4 parts by weight of a A 10% solution of a commercially available leveling agent (Byk 331, Byk-Chemie GmbH) was added and mixed homogeneously by intensive stirring. The respective mixtures were adjusted with varying amounts of methoxypropyl acetate / solvent naphtha 100 (1:1) to a settling time of 30 seconds (ISO 5 cup).

[0135] Subsequently, varying weights of the polyisocyanates 1, 2, 3 were stirred in by hand as the Vemetzer component using a stirring rod.

[0136] The coating compositions 1 to 3 were applied to glass plates using a film-pulling frame in a wet film thickness of approximately 150 pm and cured within 30 minutes at 140°C and aged for 16 hours at 60°C.

[0137] Table 1 below shows the compositions of coating components 1 to 3 in parts by weight, and Table 2 shows the results of the application tests of the resulting coatings in comparison. 2024PF30016-Abroad

[0138] 17

[0139] Table 1: Comparative examples 2 and 3 and example 1 according to the invention - Composition of the coating materials

[0140] Table 2: Comparative examples 2 and 3 and example 1 according to the invention - Coating properties

[0141] As can be seen in Table 2, the allophane-based isocyanate system according to the invention (Example 1) achieves better solvent resistance than the non-inventive isocyanurate-based system (Comparative Example 2). It does not quite reach the resistance of the allophane-based system, which is based exclusively on TMP as the polyol component (Comparative Example 3). However, compared to the latter, it exhibits a significantly reduced viscosity (5,700 mPas vs. 35,000 mPas, 100% systems), which is reflected in the formulation by a higher solids content. 2024PF30016-Abroad

[0142] 18

[0143] Furthermore, the isocyanate crosslinker according to the invention is easier to produce because the polyol mixture can be added as a liquid at room temperature and is miscible with the isocyanate provided.

Claims

2024PF30016-Abroad 19 Claims 1. Polyisocyanate modified with allophane and optionally isocyanurate groups, having an allophane group content > 50 mol%, preferably > 50 mol% to < 99 mol%, preferably > 60 mol% to < 98 mol%, particularly preferably > 70 mol% to < 98 mol%, in each case based on the total amount of allophane and isocyanurate groups in the modified polyisocyanate and determined by NMR spectroscopic analysis as described above, which is obtainable from the reaction of a composition containing or consisting of A) a mixture of Al) 1,1,1-trimethylolpropane and A2) 1,3-butanediol and / or 1,4-butanediol, and B) at least one monomeric diisocyanate having aliphatic and / or cycloaliphatic isocyanate groups bonded to it.

2. A process for producing a polyisocyanate modified with allophane groups and optionally isocyanurate groups, having an allophane group content > 50 mol%, preferably > 50 mol% to < 99 mol%, preferably > 60 mol% to < 98 mol%, particularly preferably > 70 mol% to < 98 mol%, in each case based on the total amount of allophane groups and isocyanurate groups in the modified polyisocyanate and determined by NMR spectroscopic analysis, wherein a composition containing or consisting of A) a mixture of Al) 1,1,1-trimethylolpropane and A2) 1,3-butanediol and / or 1,4-butanediol, and B) at least one monomeric diisocyanate, which has aliphatic and / or cycloaliphatic isocyanate groups, is reacted.

3. Polyisocyanate modified with allophanate groups and optionally isocyanurate groups according to claim 1 or process according to claim 2, wherein the formation of the allophanate groups and optionally isocyanurate groups in the presence of at least one 2024PF30016-Abroad 20 Allophanate groups and, if applicable, the isocyanurate group accelerating catalyst, is carried out.

4. Polyisocyanate modified with allophane groups and optionally isocyanurate groups according to claim 1 or 3 or method according to one of claims 2 to 3, wherein the modified polyisocyanate has a number-average isocyanate functionality of > 4 and / or a weight-average molecular weight of > 1000g / mol, determined according to DIN EN ISO 13885-1:2021-11.

5. Polyisocyanate modified with allophanate groups and optionally isocyanurate groups according to claim 1 or 3 to 4 or method according to one of claims 2 to 4, wherein the modified polyisocyanate has a viscosity of at most 50,000 mPas at 23°C, preferably at most 25,000 mPas at 23°C, particularly preferably at most 10,000 mPas at 23°C, determined according to DIN EN ISO 3219: 1994-10 at a shear rate of 250 s-1 .

6. Use of a modified polyisocyanate according to claim 5 for the manufacture of coatings, sealants or adhesives.

7. Coating materials, sealants or adhesives obtainable from the use according to claim 6.

8. Use according to claim 6 or coating materials, sealants or adhesives according to claim 7, wherein the systems are 1- or 2-component.

9. Substrates comprising coating materials, sealants or adhesives according to claim 7 or 8 in uncured, partially cured or fully cured form.

10. A method for coating a substrate comprising the steps i) providing a substrate that may be pretreated, ii) applying a coating material according to claim 7 or 8, and iii) partially or completely hardening the coating material.