Manufacturing method for watch parts

Abstract

To provide a method for manufacturing a resin multilayer forming mold for manufacturing a timepiece component having a complicated shape and a method for manufacturing the timepiece component.SOLUTION: A method for manufacturing, by photolithography, a resin multilayer forming mold 10 including a cavity 11 with an inlet 110 in order to manufacture a timepiece component includes, for producing at least two resin layers of the forming mold, sub-steps of producing a first resin layer C10 including an aperture or open hole 111 in a direction of the inlet of the forming mold as a boundary of a first volume of the cavity of the forming mold, and sub-steps of producing a second resin layer C20 including a rigid film, wherein the second resin layer includes a second through aperture 112 defining a boundary of a second volume of the cavity of the forming mold and the second through aperture is at least partially superposed on the aperture or open hole of the first resin layer and the second resin layer partially covers the same aperture or open hole of the first resin layer.SELECTED DRAWING: Figure 7

Description

[Technical field]

[0001] The present invention relates to a method for manufacturing a watch part. The present invention also relates to a method for manufacturing a mould intended to be used in the method for manufacturing a watch part. The present invention further relates to such a mould. [Background technology]

[0002] Non-Patent Document 1 describes the use of LIGA (Lithographie Galvanik Abformung: a technology invented by W. Ehrfeld of the Karlsruhe Nuclear Research Centre, Germany) for the manufacture of high-precision metal watch parts, such as anchors and escape wheels. This method involves forming an X-ray-sensitive resin mold by irradiation with a high-energy beam of X-rays, especially as generated by a synchrotron, which may have disadvantages from the standpoint of equipment.

[0003] Non-Patent Document 2 describes the fabrication of metal structures by electrodeposition of metal onto a polyimide-based photosensitive resin (photoresist) mold prepared using a method called the LIGA-UV technique, which is similar to the above-mentioned LIGA technique, but instead of X-ray irradiation, the resin is irradiated with UV light.

[0004] Nos. 5,393,633 and 5,433,363, for example, describe how this type of technology can be applied to the manufacture of complex metal watch parts, in particular multi-layer watch parts.

[0005] These existing solutions make it possible to produce watch components with a desirable precision, however, they often require difficult finishing operations that complicate the manufacturing process, especially when the components have delicate geometries. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] European Patent Application Publication No. 2004881 [Patent Document 2] European Patent Application Publication No. 2405301 [Patent Document 3] International Publication No. 2017 / 102661 [Non-patent literature]

[0007] [Non-Patent Document 1] DGC Mitteilungen No.104, 2005 [Non-Patent Document 2] ABFrazier et al., Journal of Microelectromechanical systems, 2, 2, June 1993 Summary of the Invention [Problem to be solved by the invention]

[0008] The object of the invention is to propose an improved solution for manufacturing watch components.

[0009] More specifically, one of the objectives of the invention is to enable the manufacture of a timepiece part with a complex shape, such as a shaft pinion, in order to achieve a sufficient precision, and in particular a sufficient surface condition, for all functional surfaces, and in particular for the functional surfaces of the pinion, so as to be able to effectively perform its function. "Functional surfaces of the pinion" refers in particular to the surfaces which take part in the gear function of the pinion. It may be a tooth surface, for example the lower or upper surface of the tooth. "Pinion" refers to any toothed part having a gear function. [Means for solving the problem]

[0010] The invention therefore relates to a method for the photolithographic manufacture of a resin multi-layer mould having a cavity provided with an inlet for the manufacture of a watch part, comprising the following sub-steps for producing at least two resin layers of the mould: the substeps of creating a first resin layer having a first through opening or aperture oriented toward an entrance portion of the mold cavity to define a first volume of the mold cavity; and Substeps for producing a second resin layer including a hard coating, the second layer including a second through opening defining a second volume of the mold cavity, the second through opening in the second layer at least partially overlapping the first through opening or open hole in the first layer, the second resin layer partially covering the same first through opening or open hole in the first resin layer.

[0011] The invention also relates to a method for producing a watch part, comprising a first step of producing a mould by the manufacturing method described above, and a second filling step of at least partially filling the cavity of the mould produced by the preceding step, in particular filling said first and second volumes of said cavity of the mould, in order to produce all or part of the watch part.

[0012] The invention further provides a photolithographically produced resin multi-layer mold for producing a watch part, the mold comprising a cavity with an inlet, comprising: a first resin layer having a first through opening or aperture oriented toward an entrance portion of the mold cavity to define a first volume of the mold cavity; and A second resin layer including a hard coating, the second layer having a second through opening defining a second volume of the mold cavity, the second through opening in the second layer at least partially overlapping the first through opening or open hole in the first layer, and the second resin layer partially covering the same first through opening or open hole in the first resin layer.

[0013] The invention is more particularly defined in the claims.

[0014] The objects, features and advantages of the present invention will be explained in detail in the following description of specific embodiments, which are given in a non-limiting manner with reference to the accompanying drawings. [Brief description of the drawings]

[0015] [Figure 1] FIG. 1 illustrates the steps of a method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Diagram 2] FIG. 2 illustrates another step of the method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Diagram 3] FIG. 3 illustrates another step of the method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 4] FIG. 4 illustrates another step of the method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Diagram 5] FIG. 5 illustrates another step of the method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 6] FIG. 6 illustrates another step of the method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 7] FIG. 7 illustrates another step of the method according to a first embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 8] FIG. 8 shows a method according to a first embodiment of the invention for producing a watch part using the method for producing a mould according to FIGS. [Figure 9] FIG. 9 shows a method according to a first embodiment of the invention for producing a watch part using the method for producing a mould according to FIGS. [Figure 10]FIG. 10 shows an example of a timepiece component manufactured by the manufacturing method according to the first embodiment of the present invention. [Figure 11] FIG. 11 illustrates steps of a method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 12] FIG. 12 illustrates another step of the method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 13] FIG. 13 illustrates another step of the method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 14] FIG. 14 illustrates another step of the method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 15] FIG. 15 illustrates another step of the method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 16] FIG. 16 illustrates another step of the method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 17] FIG. 17 illustrates another step of the method according to a second embodiment of the invention for producing a resin multi-layer mould for producing a watch part by photolithography. [Figure 18] FIG. 18 shows a method according to a second embodiment of the invention for producing a watch part using a mould according to the manufacturing method according to FIGS. [Figure 19] FIG. 19 shows a method according to a second embodiment of the invention for producing a watch part using a mould according to the manufacturing method according to FIGS. [Figure 20] FIG. 20 shows a method according to a second embodiment of the invention for producing a watch part using a mould according to the manufacturing method according to FIGS. [Figure 21]FIG. 21 is a top view showing details regarding the manufacture of a molding die according to a modification of the second embodiment of the present invention. [Figure 22] FIG. 22 shows an example of a watch part manufactured using the manufacturing method according to the second embodiment of the present invention. [Figure 23] FIG. 23 shows an example of a cross section of a timepiece component produced using a manufacturing method according to a modified example of the second embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] The invention comprises firstly a first step consisting of a particularly advantageous method for producing a multi-layer mould, which then allows in a second step to produce a watch part.

[0017] The different sub-steps of the first step E1 of producing a production mould according to one embodiment will now be described.

[0018] A first substep E10, shown in FIG. 1, consists of preparing a substrate 20. This substrate may consist of a metal wafer, in particular of an alloy such as stainless steel, or of silicon, or of glass, or of ceramic. This substrate may also include structures produced by micromachining. The substrate is prepared according to rules known to the person skilled in the art, in particular of degreasing and cleaning, and, where applicable, of passivation and / or activation. This substrate is advantageously planar. It may alternatively include patterns, in particular machined patterns, and / or cavities and / or other structures according to the teachings of the prior art. The substrate is preferably provided with markings that allow it to be positioned very precisely during the various steps. The substrate 20 consists of an electrically conducting material, for example stainless steel. Alternatively, it may be a semiconductor material substrate, for example silicon, or an electrical insulator, for example ceramic.

[0019] 1, on the substrate 20, a conductive layer 21 is optionally deposited, for example by thermal evaporation. The conductive layer 21 is intended in particular to act as an electrode for initiating electrochemical deposition, electrochemical deposition or electroforming during the implementation of step E2. According to known methods, this initial conductive layer 21 may comprise a sub-layer of chromium, nickel or titanium covered with a layer of gold or copper, i.e. it may have such a multi-layer structure.

[0020] The substrate serves as a support for the manufacture of a mold, which will be described in detail below. For ease of explanation, "longitudinal" refers to one direction parallel to the horizontal plane of the substrate, and "vertical" refers to one of the directions perpendicular to the horizontal plane of the substrate. The mold is constructed by stacking multiple longitudinal layers in the vertical direction. Similarly, "upper" refers to a region or surface that is overlaid on a "lower" region or surface that is on the substrate side relative to the vertical direction.

[0021] In a second substep E11 shown in Figure 2, the substrate 20, and in particular the optional conductive layer 21, is covered with a first layer C10 of a first photosensitive resin 31, up to a defined height corresponding or substantially corresponding to the height of the portion C1 of the watch part 1 to be manufactured, as will be described below with reference to Figure 10. This resin is deposited according to a method known to those skilled in the art, for example by spin coating.

[0022] The first resin 31 is a photosensitive resin suitable for photolithography. This resin may be negative or positive. In the former case, it is designed to be rendered insoluble or difficult to dissolve by the use of a developer and a treatment with radiation (for example, the irradiated areas are not developed), while in the latter case, it is designed to be dissolved by the use of a developer and a treatment with radiation, the parts not exposed to radiation remaining insoluble or difficult to dissolve. In an advantageous variant of the second sub-step E11, the resin 31 used is of the "SU-8" type, which is a negative photosensitive resin that polymerizes by treatment with ultraviolet radiation, such as, for example, MicroChem SU-8-100 resin.

[0023] Alternatively, the first resin 31 may take the form of a dry resin film applied to the substrate 20, in particular to the optional conductive layer 21, thereby defining a first layer C10 of the first photosensitive resin 31. This dry film is applied in particular by a lamination process. This dry resin film may for example be a SUEX or ADEX film made by DJ Microlaminates Co., Ltd. or a TMMF S2000 film made by Tokyo Ohka Kogyo Co., Ltd. All three films are negative-acting dry resin films.

[0024] The resin layer 31 is then subjected to a third photolithography substep E12, shown in FIG. 3. The latter consists of exposing a first layer C10 of the first resin 31 to optical radiation or light rays through a first mask 41 containing openings and opaque areas. The mask defines the pattern to be produced to form the part of the watch component corresponding to the height of this first layer. Here, the optical radiation used to irradiate or expose the resin 31 is ultraviolet radiation. Apart from that, X-rays, electron beams (in which case "electron beam lithography" is used) or any type of irradiation suitable for the resin used can be used. This irradiation is perpendicular to the horizontal plane along which the mask extends, so as to irradiate only the areas of the resin located along the openings formed in the mask. These areas are defined by vertical or substantially vertical walls, i.e. walls perpendicular or substantially perpendicular to the horizontal plane of the substrate 20. Alternatively, a transmission-varying mask may be used to form non-vertical or inclined walls in these areas.

[0025] This substep E12 may optionally be followed by a thermal crosslinking step of the resin 31.

[0026] Then, a fourth development substep E13, shown in FIG. 3, is carried out. In the illustrated example, the first layer C10 of the first resin 31 is dissolved locally therefor, forming first open holes 111 in the resin. By "open holes" is meant openings that open outwards in the direction of the inlet 110 of the cavity 11 of the mould, as will be explained below. Moreover, openings of this kind have a bottom in the direction opposite to the inlet 110 of the cavity 11 of the mould. Alternatively, the first layer C10 may comprise a plurality of openings. In the illustrated example, where the resin 31 is negative, the development consists in removing the non-exposed areas of the resin using a method suitable for the resin 31, for example by dissolving it with chemicals or by using a plasma treatment. In the example of a positive photosensitive resin that can alternatively be used, the exposed areas are removed during development, for example chemically, and the non-exposed areas remain on the substrate. After dissolving, the substrate 20 or any conductive layer 21 is exposed in the positions where the first resin 31 has been removed.

[0027] As will be described below, the remaining portion of the first resin 31 forms a first layer C10 of the mould 10 having a first volume defined by a first opening 111, the bottom of which is bounded by the substrate 20 or the conductive layer 21, if applicable.

[0028] A fifth sub-step E14, shown in FIG. 4, consists of covering the first layer C10 of the first resin 31 with a second layer C20 of the second resin 32.

[0029] As will be explained in more detail below with reference to figure 10, this second resin 32 takes the form of a dry film applied to the first layer C10 so as to define a second layer C20 of second photosensitive resin 32 having a height that corresponds or substantially corresponds to the height of the second layer C2 of the watch part to be manufactured. This dry film is applied in particular by a lamination process.

[0030] Due to its rigidity, the use of this type of film advantageously allows the second resin 32 to be positioned precisely, especially in a vertical position, over the first opening 111 in the first layer of the first resin. This type of film is advantageously self-supporting, i.e. the geometrical integrity of the film is guaranteed by its own rigidity. In other words, this type of film is rigid. For this embodiment, the modulus of elasticity of this type of film is in particular between 2 and 5 GPa (at 20° C.). The use of this type of film thus advantageously allows the formation of the second layer C20 of the second resin 32 during the fifth sub-step E14, whose longitudinal surface does not completely overlap the longitudinal surface of the first layer C10 of the first resin 31. This type of longitudinal surface, which does not completely overlap the longitudinal surface of the first layer C10 of the first resin 31, advantageously ensures that the parts not supported by the first layer do not deform under the influence of gravity and can therefore be positioned precisely, especially in the vertical direction.

[0031] The resin film may be, for example, SUEX or ADEX film manufactured by DJ Microlaminates Co., Ltd., or TMMF film S2000 manufactured by Tokyo Ohka Kogyo Co., Ltd. The thickness of the film may be 100 μm or more and 1 mm or less.

[0032] Then, a sixth substep E15, shown in figure 5, is carried out, which consists in subjecting the second layer of second resin 32 to photolithographic processing. The latter consists in exposing the second layer of second resin 32 to optical radiation or light rays through a second mask 42 containing openings and opaque areas, which defines the pattern to be produced to form the further portion C2 of the watch part, as will be explained in more detail below with reference to figure 10.

[0033] This substep E15 may optionally be followed by a thermal crosslinking step of the second resin 32.

[0034] Then, a seventh development substep E16, shown in figure 5, is carried out. In the illustrated example, where the second resin 32 is negative-toning, development consists in removing the non-exposed areas of the second resin using a method suitable for this second resin 32, for example by dissolving it with chemicals or using a plasma treatment.

[0035] According to the example shown in the embodiment, after dissolving, at the location where the resin was removed, a second through opening 112 is formed in the second layer C20 of the mold. This second through opening 112 at least partially overlaps the first opening 111. By "through opening" is meant an opening that passes completely through the layer in which it is formed vertically. In other words, as will be explained later, this type of opening opens towards the first opening 111, in particular in the direction of the inlet 110 of the cavity 11 of the mold 10. This type of opening does not have a bottom.

[0036] The remaining portion of the resin forms a second layer C20, the second opening 112 of which defines a second volume of the cavity 11 of the mould 10 and complements the first volume defined by the first opening 111.

[0037] The resulting shape has the feature that, on the one hand, the second opening 112 through the second layer C20 overlaps the first opening 111 opening into the first layer C10, forming a continuous volume of the cavity of the future mould, and, on the other hand, the resin of the second layer C20 partially covers the same first opening 111 opening into the first layer of resin. In other words, the contour of the second layer C20 at the level of the second opening 112 projects inside the vertical height of the contour formed by the first opening 111. The dry film of the second resin 32 has sufficient rigidity to support the part that is placed above the gap at the level of the first opening 111.

[0038] In the embodiment described, the two overlapping openings 111 and 112 are centered, in particular coaxial. The cross-sectional area of ​​the second opening 112 is smaller than the cross-section of the first opening 111. Of course, in alternative embodiments, the two openings 111 and 112 may at least partially overlap without being centered.

[0039] This method for manufacturing a mould according to the first embodiment comprises an eighth sub-step E17, shown in FIG. 6, consisting in covering the second layer C20 of the second resin 32 with a surface layer C30 of the third resin 33.

[0040] As will be explained below with reference to figure 10, this third resin 33 may be in the form of a dry film that is photosensitive and that is applied, in particular by a lamination process, to the second layer C20 so as to define a third layer C30 of third resin 33, the height of which corresponds or substantially corresponds to the height of the portion C3 of the watch part to be manufactured. Alternatively, this third resin 33 may be deposited to the required height by methods known to those skilled in the art, for example by spin coating.

[0041] Then, a ninth substep E18, shown in figure 7, of photolithographic processing of the third layer of third resin 33 is performed, which consists in exposing the layer of resin 33 to optical radiation or light rays through a third mask 43 containing openings and opaque areas. In the example chosen, this mask defines a pattern that is replicated to manufacture the portion of the watch part that corresponds to the height of said third layer.

[0042] This sub-step E18 may optionally be followed by a thermal cross-linking step of the third resin 33.

[0043] A tenth development substep E19 is then carried out, also shown in figure 7. In the example of the embodiment in question where the resin 33 is negative-toning, development consists in removing the non-exposed areas of the resin using a method suitable for the resin 33, for example by dissolving it with chemicals or using a plasma treatment.

[0044] The remaining portion of the resin forms a third layer C30 of the mold, which in the selected example includes a third through opening 113 that at least partially overlaps the first two openings 111 and 112. This third opening forms a third volume of the mold cavity.

[0045] Thus, the three openings 111, 112 and 113 at least partially overlap to form the cavity 11. Steps E10 to E19 result in a multi-layer resin mould 10 having a cavity 11 with an inlet port 110. The volume of this cavity 11 corresponds to the three openings 111, 112 and 113 of the three layers C10, C20 and C30, respectively. All or part of the cavity 11 is intended to be filled during a second step E2 described herein below.

[0046] The invention further relates to a method for producing a watch part using a mould previously formed by the method for producing a mould forming the first step E1 of the method according to the first embodiment of the invention for producing a watch part.

[0047] The method for manufacturing the watch component further comprises a second step E2, which includes sub-steps that will be explained in more detail below.

[0048] A first substep E20 consists of filling all or part of the cavity of the mould 10 with metal 12 by electro-deposition, electro-forming or electro-casting.

[0049] The conductive layer 21 or the substrate 20 directly serves as a cathode to start the substep E20. This substep uses a metal or alloy 12, for example nickel (Ni) or nickel-phosphorous (NiP), and a LIGA process. Advantageously, alloys such as those described in US Pat. No. 5,999,333 can be employed. This metal or alloy 12 is deposited in all or part of the cavity 11 of the mould 10 through an inlet 110 formed on the upper surface of the third opening 113 of the third layer C30.

[0050] This sub-step E20 has the advantage of making it possible to grow the metal or alloy in the three volumes formed by the openings 111, 112 and 113 of the cavity 11 of the mould 10 in one piece, and is preferably carried out until it fills the entire height of the cavity 11 of the mould 10, as shown in figure 8. Thus, unlike the parts resulting from the manufacturing methods described in patent documents 1 and 2, the watch part formed using the mould 10 is the result of a single and unique step of growing a metal or alloy. Moreover, the watch part has on its functional surface a controlled shape, in particular a surface state, which corresponds to all or part of the surface of the cavity 11 of the mould 10.

[0051] Moreover, the resulting watch part preferably has the same height corresponding to the stacking of the three layers C10, C20 and C30 of the mould 10.

[0052] This substep E20 may optionally comprise a finishing of the thickness by simultaneous mechanical polishing of the metal layer and of the mould 10 in order to obtain a perfectly flat and horizontal upper surface whose surface condition is satisfactory.

[0053] The method further comprises a substep E21 of removing the metallic material 12 and its mould 10 from the substrate 20, for example by delaminating layer 21 of the substrate.

[0054] A final substep E22 finally makes it possible to separate the watch part 1 formed by depositing the metal in the cavity 11 of the mould 10 from the resin forming the mould 10, for example with the aid of a chemical attack or plasma, thus resulting in the release of the watch part 1, as shown in figure 9.

[0055] A watch part 1 obtained according to an example of the first embodiment described above is shown in more detail in FIG. 10. This watch part 1 is a shaft pinion and comprises three parts C1, C2 and C3, which are respectively formed in the three openings 111, 112 and 113 in the cavity 11 of the mould 10 described above. The two ends C1 and C3 are similar cylinders with the same diameter and height, arranged coaxially. An intermediate area C2 forms the pinion mounted on the shaft formed by the cylinders of the parts C1 and C3. This intermediate area C2 is inscribed in the cylinder defined by the extension of the parts C1 and C3. This intermediate area C2 forms the pinion of the watch part 1 and is defined in the manufacturing stage by a second volume formed in the second opening 112 in the second layer C20 of the mould 10, so that it has a shape corresponding to the pinion to be manufactured, in particular the teeth to be formed. Moreover, this intermediate part C2 has a cross-section with a smaller area than the parts C1 and C3.

[0056] A first advantage of the method for manufacturing a watch part 1 is that it makes it possible to form a multi-layer watch part 1 as a completely integral and homogeneous one-piece, in this example by a single electroforming step, whereas conventional methods are based on separate galvanic depositions or successive electroforming steps for each layer, thereby forming a non-homogeneous multi-layer structure with weak areas at the joints between the layers of the finished watch part. On the other hand, the functional part of the watch part 1 formed by the intermediate part C2 has a contour whose vertical sides are completely defined by one or more surfaces of the cavity 11 of the mould 10, and likewise its longitudinal upper and lower sides are completely defined by being bounded by the parts C1 and C3 of the part, which are also precisely defined by one or more surfaces of the cavity 11 of the mould 10. Thus, no final reworking of the watch part 1, once it has left the mould, is required to improve the definition, and in particular the surface condition, of the functional part of the part C2. This method makes it possible to obtain a reliable watch part in a simple manner.

[0057] The watch part has been described based on electrochemical deposition of the cavity 11 of the mould 10. Alternatively, the watch part may consist of other materials, for example metal matrix or polymer matrix composites, or the watch part may be formed by filling the mould cavity in a way other than electrochemical deposition.

[0058] Naturally, the invention is not limited to the first embodiment described above. In relation to a second embodiment, the method of the invention may also comprise the step of adding an insert to at least part of the cavity of the mould produced by a method similar to that described above, and then producing a part of the watch part by filling a part of the cavity of the mould in a manner similar to the first embodiment, thereby making it possible not only to produce said part of the watch part 1 but also to fix it to the insert, forming a final watch part consisting of the insert and a part fixed to and gripping the insert. An insert of this kind is advantageously made from a different metal than the part of the watch part produced by filling the part of the cavity of the mould.

[0059] This second embodiment will now be described in more detail.

[0060] In connection with this second embodiment, the present invention is also based primarily on a method for producing a resin multilayer mold by photolithography, constituting a first step E1' of the method according to the second embodiment for producing a watch part.

[0061] The first two first substeps shown in Figure 11 consist, on the one hand, of a substep E100' of obtaining a substrate, and, on the other hand, of a substep E101' of creating a lower layer C10' of resin 31'. These two substeps are similar to the two first substeps E10 and E11 of the first embodiment and will not be described here. In the example shown, this substrate 20' does not have any intermediate layer 21.

[0062] The method further comprises two sub-steps E102' and E103' shown in Fig. 12, which correspond to the two sub-steps E12 and E13 of the first embodiment and will not be described again here. Following the above-mentioned sub-steps, a bottom-open hole 114' is formed in the inner layer C10' to form the lower volume of the cavity of the future mold.

[0063] The method comprises a fifth substep E104' of metallizing the upper surface of the lower layer C10' of resin 31', as shown in Fig. 13. More precisely, this substep consists in depositing a conductive layer 21' intended in particular to act as an electrode for starting electrochemical deposition, electrochemical deposition or electroforming when carrying out the second step E2' described below. In a known manner, this starting conductive layer 21' may have a sublayer of chromium, nickel or titanium covered with gold or copper, or may take the form of a multilayer structure. This conductive layer 21' may not only cover the surface of the lower layer C10', but also the bottom of the opening 114', i.e. the surface of the illustrated substrate 20' or the side of the opening 114'.

[0064] The method comprises a sixth sub-step E105', shown in FIG. 14, which consists of applying a first layer C20' of a first photosensitive resin 32' on the conductive layer 21' to the required height.

[0065] This first resin 32' may be in the form of a dry film applied to the conductive layer 21', in particular by a lamination process. This resin film may be, for example, a SUEX or ADEX film from DJ Microlaminates Co., Ltd., or a TMMF S2000 film from Tokyo Ohka Kogyo Co., Ltd. These three films are negative resin films. Alternatively, this first resin 32' may be deposited to the required height by methods known to those skilled in the art, for example by spin coating. Alternatively, the first resin 32' may be of the "SU-8" type, which is a negative photosensitive resin that polymerizes by a UV irradiation process, such as, for example, MicroChem SU-8-100 resin.

[0066] The method then comprises two sub-steps E106' and E107', shown in Figure 15, which substantially correspond to the two sub-steps E18 and E19 of the first embodiment. A first through opening 111' is formed in the first layer C20', thereby forming a first volume of the cavity 11' of the mould 10', complementing the volume formed by the lower opening 114'.

[0067] The method then comprises a ninth substep E108' consisting in covering the first layer C20' of the first resin 32' with a second layer C30' of a second resin 33', as shown in FIG.

[0068] The second resin 33' is formed by arranging the second layer C30' of the second photosensitive resin 33' so as to define a second layer C30' of the second photosensitive resin 33' having a predetermined height. 30’ This type of film has the particular feature of being in the form of a dry film applied, in particular by a lamination process, to the first layer C20'. As will be explained later, the use of this type of film, which has rigidity, advantageously allows the second resin 33' to be positioned precisely, in particular vertically, over the first opening 111' formed in the first layer C20'. This type of film is advantageously self-supporting, i.e. its geometric integrity is ensured only by its own rigidity; in other words, this type of film is rigid. The modulus of elasticity of this type of film is advantageously between 2 and 5 GPa (at 20° C.). The thickness of the film may be between 100 μm and 1 mm.

[0069] The method then comprises two sub-steps E109' and E110', shown in Figure 17, making it possible to form a second through opening 112' in the second layer C30', in a manner similar to the two sub-steps E15 and E16 of the first embodiment, thereby forming a second volume of the cavity 11' of the mould 10'.

[0070] Finally, the three openings 114', 111', 112' respectively form three volumes corresponding to the volumes of the cavities 11' of the mold 10', in other words, the openings at least partially overlap to form the respective cavities 11'.

[0071] As in the first embodiment, the resulting shape has the particular feature that, on the one hand, the second through opening 112' of the second layer C30' overlaps the first through opening 111' of the first layer C20', and, on the other hand, the second layer C30' of resin partially covers the same first through opening 111' of the first layer of resin. In other words, the contour of the second layer C30' at the height of the second opening 112' projects inside the vertical height of the contour formed by the first opening 111'. The second resin 33' has sufficient rigidity to support this position, partially overhanging the gap at the height of the first opening 111'.

[0072] In this embodiment, the two overlapping openings 111' and 112' are centered, in particular coaxial. The cross section of the second opening 112' has a smaller area than the cross section of the first opening 111'. Of course, in other embodiments, the two openings 111' and 112' may not be centered, but may at least partially overlap.

[0073] The result of steps E100' to E110' is a multi-layer resin mold 10' including a cavity 11' with an inlet 110'. The volume of this cavity 11' corresponds to three volumes corresponding respectively to the three openings 114', 111', 112' in the three layers C10', C20', C30'.

[0074] The invention also relates to a method for producing a watch part using a mould formed as described above in relation to the method for producing a mould which forms the first step E1' of the method for producing a watch part according to the second embodiment of the invention.

[0075] The method for manufacturing a watch part according to the second embodiment comprises an intermediate step E3' of inserting an element or insert into a part of the cavity of the mould, followed by the performance of a second step E2' of filling said part of the cavity of the mould, similar to the second step E2 of the first embodiment. Each of these manufacturing sub-steps is explained in more detail below.

[0076] With regard to the second embodiment shown, a part of the element 1b', in this example the shaft, is inserted into three openings 112', 111', 114' of the mould 10', as shown in Fig. 18. For this purpose, the lower opening 114' of the lower layer C10' of the mould 10' preferably has a cross section with a shape substantially equivalent to the shape of the cross section of the inserted part of the element 1b', in particular a circular cross section with a diameter substantially equivalent to the diameter of the cross section of the inserted part of the element 1b'. Preferably, this inserted shaft part is penetrated into the lower opening 114' such that the shaft fits with less clearance to the cavity 11' of the mould 10', according to the defined assembly tolerances, while the axis A1b' of the shaft is perpendicular to the horizontal plane of the substrate 20'. Inserting the shaft by penetrating it into the lower layer of the "SU-8" type resin 31' advantageously allows the shaft to be held strongly during the rest of the process.

[0077] In this embodiment, the insertion portion of the shaft 1b' also has a diameter equivalent to the diameter of the receiving part 10b' of the shaft 1b' intended to receive the subsequently manufactured part 1a', as will be described below. Of course, these two parts of the shaft may have different diameters and / or shapes.

[0078] Furthermore, in this embodiment, the shaft is penetrated until it abuts the substrate 20', in particular until it abuts the metal layer 21' on the substrate 20' formed during step E104'. Alternatively, the substrate 20' may have an opening below the lower opening 114' that allows a portion of the shaft to pass through, in particular a portion that guides the shaft, in particular a pivot for the shaft.

[0079] In this embodiment, the element 1b' forming the insert in the method is fully machined in advance, prior to the intermediate step E3'. In other words, the element is in a finished state when it is incorporated into the mould 10' during the intermediate step E3'. Alternatively, it may have an intermediate state when it is incorporated into a part of the cavity 11' of the mould 10' during the intermediate step E3' and be finished after the second step E2'.

[0080] In addition, the second opening 112' of the second layer C30' also has a shape that substantially corresponds to the diameter of the element 1b'. Once this element 1b' is placed in a part of the cavity 11' of the mold 10', the first opening 111', located between the lower opening 114' and the upper opening 112' (i.e. the second opening), is almost closed, if we ignore the gap formed between the element 1b' and these two openings 114', 112'. More precisely, the first opening 111' is closed on its vertical sides by the first layer C20', on its central vertical side by the element 1b', on its lower longitudinal side by the upper longitudinal side of the lower layer C10' (more precisely the metallization layer 21' deposited on the lower layer C10') and on its upper longitudinal side by the lower longitudinal side of the second layer C30'.

[0081] The aim of the second step E2' of the method is to use the mould 10' to form a portion 1a' of a watch part 1' which is shown in more detail in Figure 22. To this end, part of the volume of the cavity 11' of the mould 10', in particular the part of the first volume defined by the first opening 111', i.e. the volume of the cavity 11' not occupied by the element 1b', is filled with material in a manner similar to the second step E2 of the first embodiment.

[0082] The portion 1a' of the watch part may consist of a metal or a metal alloy, or it may consist of a composite material, for example a composite material with a metal or polymer matrix.

[0083] In this embodiment, the second filling step E2' comprises the following sub-steps:

[0084] The first substep E20', shown in figure 19, consists of depositing a metallic material by electro-deposition, electro-forming or electro-deposition on a part of the cavity of the mould 10', i.e. around the element 1b'. The resulting metal part, in particular isotropically electro-deposited or electro-formed, has internal stresses which completely support and grip the element 1b' and hold the future part 1a' of the watch part 1' against it. In this example, the volume of the part of the cavity 11' of the mould 10' to be filled is limited to a part of the volume defined by the first opening 111', the remaining part of the volume being occupied by the element 1b' to be inserted.

[0085] In this substep, the conductive layer 21' serves as a cathode to initiate the deposition. This step uses, for example, the LIGA process and metals or alloys, such as nickel (Ni) or nickel-phosphite (NiP), advantageously alloys such as those described in US Pat. No. 5,399,633.

[0086] As described in the first embodiment example, this substep E20' has the advantage of making it possible to grow the portion 1a' of the watch part 1' in one piece from a metal or alloy. Moreover, this metal is formed over a height completely defined by the first layer C20'. Since the part of the cavity of the mould formed by the first opening 111' is completely delimited on all sides, including the top and bottom, the portion 1a' is formed with a high degree of finished surface condition, including the longitudinal surfaces. It is particularly interesting that growing the metal or alloy on the second layer C30' of the second resin makes it possible to obtain a high quality surface condition on the upper surface of the portion 1a'. The presence of the second layer C30' overhanging a part of the first opening 111' thus results in a portion 1a' of the watch part 1', the functional surface of which is completely controlled and finished without the need for any mechanical reworking.

[0087] Nevertheless, substep E20' may optionally comprise a finishing step at the level of the interface between element 1b' and the metal forming part 1a'. This finishing process may for example be carried out by means of a laser, in particular a femtosecond laser.

[0088] Finally, the method comprises sub-steps E21' and E22' for the separation of the watch part 1', for example by chemical attack or by using plasma, similar to steps E21 and E22 of the first embodiment, to obtain the result shown in FIG.

[0089] The pattern 330' of the second layer C30' at the level of the second opening 112' shown in Figure 21 may advantageously have elastic structures 331'. This type of structure advantageously makes it possible to center the element 1b' and hold it perpendicular to the substrate 20', and in particular to the lower layer C10' of resin 31' on which its part 1a' is intended to be placed.

[0090] Additionally or alternatively, the selected pattern 330' is advantageously designed to define a suitable gap between the element 1b' and the second layer C30' of the second resin 33' to allow the electrolyte to pass through the first opening 111' during the second step E2'. This gap represents a gap constituting the inlet 110' of the mold cavity 11'. Alternatively or additionally, the pattern 330' may have one or more holes 332' to allow the electrolyte to pass through. Each hole is part of the inlet 110' of the mold cavity 11'. Alternatively or additionally, the mold 10' may have one or more holes arranged on different sides of the pattern 330'. Each of these holes is also part of the inlet 110' of the mold cavity 11'.

[0091] The pattern 330' of this second layer C30' is produced during the above-mentioned substeps E109', E110', consisting of exposing the second layer of resin 33' to optical radiation or light rays through a third mask 43' comprising openings and opaque areas, which defines the pattern 330' that is to be replicated during a second step E2' to allow the passage of electrolyte in the first openings 111'.

[0092] Of course, as shown in Fig. 23, element 1b' may be specially adapted to optimize the retention of part 1a' relative to element 1b'. For example, shaft portion 10b' may have grooves 101b' designed to optimize the retention of the pinion on the shaft by torque. Metal is for example accommodated in these grooves 101b' during step E2'. Alternatively or additionally, shaft portion 10b' may have a bearing surface 102b' designed to maximize the axial retention of the pinion on the shaft. Alternatively or additionally, shaft portion 10b' may have a structured surface with the purpose of locally increasing the roughness in order to optimize the retention of the pinion on the shaft.

[0093] A timepiece part 1' obtained in relation to an example of implementation of the second embodiment described above is shown in more detail in figure 22. This timepiece part 1' is a shaft pinion. The shaft is formed by the aforementioned insertion and the pinion corresponds to the part 1a' formed around the part of the shaft inserted. The timepiece part 1' therefore advantageously has a first part 1a' made of a first metallic material, here the pinion, and a second part corresponding to element 1b' made of a second material, preferably non-conductive and different from the first material, here the shaft.

[0094] In this example, the shaft of the watch part 1' passes completely through the pinion. The shaft may be made of a non-conductive material, for example a ceramic, in particular zirconia, in particular yttria stabilized zirconia 3%, or monocrystalline alumina, or an alumina-zirconia combination. Alternatively, the shaft of the watch part may consist of a composite material.

[0095] The shaft has a portion 10b' for receiving a pinion with a cross section of a first diameter D10b'. The shaft advantageously further has at least one portion 11b' for guiding the shaft pinion 1', preferably two guiding portions 11b', in particular two pivots 11b', the cross section of which has a second diameter D11b'. The second diameter D11b' is preferably smaller or much smaller than the first diameter D10b'.

[0096] Thanks to the inherent extremely hard properties of ceramics cited above, the pivots of the shaft are not damaged when subjected to impacts. Unlike steel pivots, which can bend in the event of a strong impact, impairing the timekeeping and / or functioning of the watch movement, these pivots advantageously do not deform. Furthermore, ceramics offer the additional advantage of being particularly insensitive to magnetic fields, and therefore not affecting the operation of the watch when exposed to magnetic fields, especially those greater than 80 kA / m (1000 G).

[0097] The first diameter D10b' is preferably 2 mm or less, or 1 mm or less, or 0.5 mm or less, or 0.3 mm or less, and the diameter D10b' is preferably 0.1 mm or more, or 0.2 mm or more.

[0098] The second diameter D11b' is preferably 0.5 mm or less, or 0.4 mm or less, or 0.2 mm or less, or 0.1 mm or less, or 0.08 mm or less, and the second diameter D11b' is preferably 0.03 mm or more, or 0.05 mm or more.

[0099] More preferably, the ratio D10b' / D11b' is 2 or more and 8 or less, and particularly 3 or more and 6 or less.

[0100] Alternatively, the shaft may take the shape of a cylinder including a portion 10b' for receiving the pinion, which is machined following the second step E2'. In particular the guiding portion 11b' may be machined subsequently.

[0101] Of course, the invention is not limited to the described embodiments. For example, the first portion 1a' of the part 1' may have several portions arranged at different heights, like the part 1. Alternatively, the second portion 1b' of the part 1' may take the form of an insert, the total height of which is smaller or equal to that of the portion 1a', so that it can be inscribed in the volume defined by the first portion 1a'. As a further alternative, the portion 1a' may constitute the whole of the part 1'. In the latter two examples, the use of a lower layer C10' is not mandatory. In all examples, at least one functional surface of all or part of the part 1', in particular the surface condition of which is important, is completely defined by the second layer C30'.

[0102] The invention allows any shape of watch part and the associated moulds to be produced.

[0103] Finally, the invention is based on a method for photolithographically producing a resin multi-layer mould for manufacturing a watch part, comprising the following sub-steps for producing at least two resin layers of the mould: creating a first resin layer having a first through opening or hole oriented toward an entrance portion of the mold cavity to define a first volume of the mold cavity; and A substep of creating a second resin layer including a hard coating, the second layer including a second through opening defining a second volume of the mold cavity, the second through opening in the second layer at least partially overlapping the first through opening or open hole in the first layer, the second resin layer partially covering the same first through opening or open hole in the first resin layer.

[0104] This type of method allows for a mould having: a first resin layer having a first through opening or aperture oriented toward an entrance portion of the mold cavity to define a first volume of the mold cavity; and A second resin layer having a hard coating, the second layer having a second through opening that defines a second volume of the mold cavity, the second through opening in the second layer at least partially overlapping the first through opening or open hole in the first layer, and the second resin layer partially covering the same first through opening or open hole in the first resin layer.

[0105] As mentioned above, the second layer has a part that overhangs part of the opening of the first lower layer. For this reason, the second layer has a resin that includes a hard coating, which, despite this particular configuration, allows the free end of the second layer that overhangs the first opening of the first layer to be subjected to a force and to maintain a continuous and stable shape. To achieve this goal, the second resin layer may comprise the application of a resin with a dry film, for example a SUEX or ADEX film from DJ Micro Laminates Co., Ltd., or a TMMF S2000 film from Tokyo Ohka Kogyo Co., Ltd. Naturally, any resin film that can achieve a satisfactory stiffness is suitable. For example, such a resin film advantageously has a stiffness that is characterized in particular by an elastic modulus (at 20° C.) of 2 GPa to 5 GPa. Such a film is advantageously self-supporting or rigid, i.e. its geometric integrity is ensured only by its own stiffness. In addition, the second layer advantageously has a thickness of 100 μm or more, advantageously 100 μm to 1 mm.

[0106] The various resins of the other layers may or may not be the same as the resin of this second layer, as described above.

[0107] Naturally, the invention is not particularly concerned with the design of one or more openings. The latter may be cylindrical or of any other shape. Furthermore, there may be more than one opening per layer. The mould may include a number of holes. The shape of the openings is determined by the watch part to be produced. Finally, the mould may include at least two superimposed layers as described above, and may have three or more layers. That is to say, the mould may have a number of groups of two layers as described above, with a number of resin layers including a hard coating similar to the second layer described above.

[0108] The invention also relates to a method for producing a watch part, comprising a first step of producing a mould according to the manufacturing method described above in order to produce all or part of the watch part, and a second step of filling, in particular the first and second volumes of the mould cavity, with an insert and / or filling material which at least partially fills the mould cavity produced in the preceding step.

[0109] The second filling step may comprise inserting an electrolyte through an inlet of the cavity of the mould and filling at least two openings in each of at least two layers of the mould, so that all or part of the watch part thus electroformed in the cavity of the mould has a one-piece shape (monolithic casting) without the superposition of separate layers.

[0110] In all instances, the second opening in the mold at least partially overlaps the first through opening or open hole in the first layer such that a contiguous volume is formed corresponding to the volume of the mold cavity and such that the second resin layer partially covers the same first through opening or opening in the first layer.

[0111] Thanks to the particular structure of the mould according to the invention, in which the first step of producing the mould comprises the production of a layer of the mould, partially covered by another layer, with through openings or open holes oriented in the direction of the mould inlet, the longitudinal lower or upper functional surface of all or part of the watch part obtained by the second filling step has a perfectly defined shape and in particular a surface condition, delimited by the respective surface of the mould cavity, so that the watch part can advantageously have a very good surface condition immediately after demoulding from the mould cavity.

[0112] Furthermore, the method of the invention advantageously allows the manufacture of a toothed watch shaft, which has a non-metallic part gripped by a pinion, the upper and lower functional surfaces of which are completely defined and whose surface condition is completely controlled by the surface condition of the resin surface of the mould cavity.

[0113] Naturally, the method for manufacturing the above-described timepiece parts is not limited to the manufacture of toothed shafts, but can be used to manufacture timepiece parts such as, by way of non-limiting example, shafts with cams, pivot anchors (i.e. the anchor and its pivot pin), pivot balances (i.e. the balance and its pivot shaft), etc. [Explanation of symbols]

[0114] 10 mold 11 Cavity 31 Daiichi Resin 32 Second resin 33 Third resin 110 Entrance 111 First opening 112 Second opening C10 First layer C20 second layer C30 third layer

Claims

1. A method for producing a resin multilayer mold (10; 10') for producing a watch part by photolithography, the method comprising the steps of: producing at least two resin layers (C10, C20; C20', C30') of said mold (10; 10'), the at least two resin layers (C10, C20; C20', C30') of said mold (10; 10'), Substeps (E11, E12, E13; E105', E106', E107') for creating a first resin layer (C10; C20') comprising a first through opening or open hole (111; 111') oriented towards the inlet (110; 110') of the cavity (11; 11') of the mould (10; 10') to delimit a first volume of the cavity (11; 11') of the mould; and Sub-steps (E14, E15, E16; E108', E109', E110') for producing a second resin layer (C20:C30'), said second resin layer comprising a second through opening (112; 112') which bounds a second volume of said cavity (11; 11') of said mould (10; 10'), said second through opening (112; 112') in said second resin layer at least partially overlapping said first through opening or open hole (111: 111') in said first resin layer, said second resin layer partially covering said same first through opening or open hole (111: 111') in said first resin layer. Each of the sub-steps of The method for producing a molding die, wherein the second resin layer has an elastic modulus of 2 GPa or more and 5 GPa or less.

2. The second resin layer is formed by a lamination process of a dry film. A method for producing the mold of claim 1.

3. Each of the sub-steps (E14, E15, E16; E108', E109', E110') for creating a second resin layer comprises applying a resin comprising a dry film, and / or the second resin layer has a thickness of 100 μm or more and / or is self-supporting. A method for producing the mold according to claim 1 or 2.

4. forming a film of a first photosensitive resin (E11; E105'); and exposing the first photosensitive resin through a mask (E12; E106') to light in order to form a mould (10; 10') comprising a first through opening or aperture (111; 111') oriented towards the inlet (110; 110') of the mould cavity (11; 11') to delimit a first volume of the cavity (11; 11') of the mould, and developing the resin (E13; E107'); The sub-step of creating the first resin layer (C10; C20') comprises: depositing a second photosensitive resin including a dry film applied onto the first resin (E14; E108'); and exposing said second photosensitive resin through a mask (E15; E109') to light in order to form a cavity (11; 11') in the mold (10; 10') comprising said second through opening (112; 112') and developing said resin (E16; E110'); A sub-step of producing the second resin layer (C20; C30'), comprising: A method for producing the mold of claim 1 , comprising:

5. The second through opening (112; 112') in the second resin layer (C20; C30') is centered on the first through opening or open hole (111; 111') in the first resin layer (C10; C20'). A method for producing a mold according to any one of claims 1 to 4.

6. A method for producing a watch part (1; 1'), comprising a first step (E1; E1') of producing a mould (10; 10') by a manufacturing method described in any one of claims 1 to 5, and a second step (E2; E2') of at least partially filling the cavity of the mould produced by the first step to produce all or part of the watch part.

7. The second step (E2; E2') comprises electrolytically filling all or part of the cavity (11; 11') of the mould (10; 10'), comprising inserting an electrolyte through the inlet (110; 110') of the cavity of the mould. A method for manufacturing a watch component according to claim 6.

8. A method for producing a watch part as described in claim 7, wherein the second step includes inserting an electrolyte through the entrance portion of the cavity of the mold to fill at least two openings in each of the two layers of the mold, and wherein all or part of the watch part electroformed in the cavity of the mold by the above method is formed as a single piece without superimposing separate layers.

9. The first step (E1; E1') of producing a mould (10; 10') comprises the formation of a layer of the mould, partly covered by another layer (C20; C30'), which includes through openings or holes (111; 111') oriented towards the inlet (110; 110') of the mould cavity (11; 11'), the through openings or holes (111; 111') of the layer oriented towards the inlet (110: 110') of the mould cavity (11; 11') forming a first volume of the mould cavity which defines all or part of the watch part to be produced, so that a surface of all or part of the watch part formed by the second step (E2; E2') has a shape which is completely defined by the boundaries of the mould cavity. A method for manufacturing a watch component according to any one of claims 6 to 8.

10. A method for producing a watch part comprising the steps of: (1a'), (1b'), (112'), (114'), (112 ... A method for manufacturing a watch component according to any one of claims 6 to 9.

11. The first step (E1') of producing the mould (10') comprises creating a lower layer (C10') including a lower opening (114'), a second upper layer (C30') including a second upper opening (112') centred on the lower opening (114') of the lower layer (C10'), and a first intermediate layer (C20') between the lower layer (C10') and the second upper layer (C30'), the first intermediate layer (C20') including a first intermediate through opening (111') centred on the openings (114', 112') of the lower layer and second upper layer, said first intermediate through opening (111') has a cross section with a larger area than the respective cross sections of said openings (114', 112') in said lower layer and in said second upper layer, said first intermediate through opening (111') forming a cavity portion (11') of a mould (10') for a portion (1a') of said watch part (1'), said second step (E2') on a portion of said cavity (11') of said mould (10') making it possible to produce a watch part (1') comprising said portion (1a') of said watch part (1') surrounding said element (1b') to be inserted in said mould, A method for manufacturing a watch component according to claim 10.

12. The method comprises the steps of: coating the lower layer (C10') of the mold with a metal layer (21'), and the second step (E2') of a portion of the cavity (11') of the mold (10') comprises filling by electroforming. A method for manufacturing a watch component according to claim 11.

13. A mold (10') comprising an opening (112') for guiding and / or holding an element (1b') in an upper layer (C30') of the mold (10') having a shape substantially corresponding to an element (1b') to be inserted, said upper layer (C30') being adapted to: and / or comprising, in said opening (112'), a pattern (330') with an elastic structure (331') for elastically retaining said element during said second step (E2'); a pattern (330') forming a structure comprising at least one hole (332') in the top layer (C30') of the mould (10') that is part of the inlet (110:110') of the cavity (11, 11') of the mould and / or a structure defining a void at the level of the inserted element, allowing the passage of material to fill the cavity of the mould, A method for manufacturing a watch component according to claim 11 or 12.

14. The inserted element (1b') is a substantially cylindrical shaft, so that the second step (E2') enables a pinion to surround said shaft, the upper and lower functional surfaces of which are completely defined by the resin surface of the mould during this second step (E2') to form a watch part, which is a watch shaft including teeth. A method for manufacturing a watch component according to any one of claims 11 to 13.

15. The inserted element (1b') is a substantially cylindrical ceramic shaft and the pinion is made of metal, the shaft including at least one bearing surface (102b') at the height of the pinion to maximize axial retention of the pinion on the shaft, and / or including at least one groove (101b') to maximize torque retention of the pinion on the shaft, and / or including a roughness differential suitable for mounting of the pinion on the shaft. A method for manufacturing a watch component according to claim 14.

16. A resin multilayer mold (10; 10') for producing a watch part (1; 1') comprising a cavity (11; 11') having an inlet portion (110; 110') produced by photolithography, a first resin layer (C10; C20') comprising a first through opening or open hole (111; 111') oriented towards the inlet (110; 110') of the cavity (11; 11') of the mould to delimit a first volume of the cavity of the mould; and Second resin layer (C20:C30') Including, the second resin layer comprises a second through opening (112; 112') which defines a boundary of a second volume of the cavity of the mould, the second through opening (112; 112') in the second resin layer (C20:C30') at least partially overlapping the first through opening or open hole (111:111') in the first resin layer (C10:C20'), the second resin layer (C20;C30') partially covering the same first through opening or open hole (111:111') in the first resin layer (C10;C20'); The second resin layer has an elastic modulus of 2 GPa or more and 5 GPa or less.