Improved device for thermal insulation and manufacturing process

Abstract

Improved device for thermal insulation and manufacturing process. Multilayer insulating product strip comprising: a primary layer (10) extending in a longitudinal and a transverse direction, a top metallized film (20), comprising a tack layer (24) and a metallized layer (22), the material forming the tack layer (24) having a melting point less than or equal to the melting point of the material forming the primary layer (10), the top metallized film (20) being calendered onto the primary layer (10). Figure for the abstract: Fig. 1.

Description

Title of the invention: Improved device for thermal insulation and manufacturing method technical field

[0001] The present invention relates to reflective thermal insulators. Previous technique

[0002] Reflective thermal insulation is an insulating system used in confined spaces. Unlike conventional insulation, which is bulky, this type of insulation has a reduced footprint, which is advantageous, for example, in terms of layout, typically for spaces located under roofs.

[0003] However, the problems associated with such insulators imply that an improvement in insulation requires an improvement in the product, rather than a simple increase in the thickness of the insulation as can be achieved with conventional insulators such as rock wool.

[0004] The proposed invention thus aims to improve the thermal insulation properties of such reflective insulators. Description of the invention

[0005] To this end, the present invention proposes a multilayer insulating product strip comprising: - a primary aquifer extending along a longitudinal and a transverse direction, - a superior metallized film, comprising an adhesion layer, a support layer and a metallized layer, the support layer being interposed between the adhesion layer and the metallized layer, the primary layer comprising a layer of low-density polyethylene, the support layer being composed of high-density polyethylene, the tack layer comprising low-density polyethylene, the upper metallized film being calendered onto the primary layer, so that the tack layer is bonded to the low-density polyethylene layer of the primary layer.

[0006] According to one example, the insulating product strip further comprises a lower metallized film, comprising an adhesive layer, a support layer and a metallized layer, the support layer being interposed between the adhesive layer and the metallized layer, the support layer being composed of high-density polyethylene, the adhesive layer comprising low-density polyethylene, said lower metallized film being calendered on the primary layer, so that the tack layer is bonded to the low-density polyethylene layer of the primary layer, and so that the primary layer is positioned between the upper metallized film and the lower metallized film.

[0007] The present invention also relates to an assembly comprising a plurality of insulating product strips as defined above, said strips defining: - a top band, - a lower band, - a plurality of intermediate bands, positioned between the upper band and the lower band, said intermediate bands forming an openwork structure.

[0008] The present invention also relates to a method for manufacturing a thermal insulation mat, in which: - or provides a primary layer extending in a longitudinal and transverse direction, the primary layer comprising a layer of low-density polyethylene - a superior metallized film is provided, comprising an adhesion layer, a support layer and a metallized layer, the support layer being interposed between the adhesion layer and the metallized layer, the support layer being composed of high-density polyethylene, the adhesion layer comprising low-density polyethylene, - the upper metallized film is applied to the upper face of the primary layer using a heating cylinder, so as to partially melt the tack layer, and to calender the upper metallized film onto the primary layer, so that the tack layer is bonded to the low-density polyethylene layer of the primary layer.

[0009] According to one example, - a lower metallized film is provided, comprising an adhesion layer, a support layer and a metallized layer, the support layer being interposed between the adhesion layer and the metallized layer, the support layer being composed of high-density polyethylene, the adhesion layer comprising low-density polyethylene, - the lower metallized film is applied to the underside of the primary sheet by means of a heating cylinder, so as to partially melt the material of the adhesion layer of the lower metallized film, and to calender the lower metallized film onto the primary sheet, so that the adhesion layer is bonded to the low-density polyethylene layer of the primary sheet, and so that the primary sheet is positioned between the upper metallized film and the lower metallized film.

[0010] According to one example, prior to the primary layer supply step, a primary layer perforation step is carried out, in which: - or provides a primary aquifer extending in both a longitudinal and a transverse direction, - cuts are made in the primary layer, these cuts being made in such a way as to extend along the longitudinal direction, - The primary sheet is stretched along the transverse direction, so as to stretch the cutouts and form openings in the primary sheet, - the primary sheet thus stretched is fixed by heating or heat fixing.

[0011] The present invention also relates to a method for forming a strip of insulating product, in which: - or provides a primary aquifer extending in both a longitudinal and a transverse direction, - cuts are made in the primary layer, these cuts being made in such a way as to extend along the longitudinal direction, - The primary sheet is stretched along the transverse direction, so as to stretch the cutouts and form openings in the primary sheet, - The primary sheet, thus stretched, is fixed by heating or heat fixing. - a top metallized film and a bottom metallized film are provided, - the upper metallized film and the lower metallized film are joined to the primary layer, so that the primary layer is positioned between the upper metallized film and the lower metallized film.

[0012] According to one example, the bonding of the upper metallized film and the lower metallized film to the primary layer is achieved by gluing or by calendering.

[0013] According to one example, the primary layer is perforated so as to have an openness rate of between 10% and 80%, or between 40% and 60%. Brief description of the drawings

[0014] The invention and its advantages will be better understood upon reading the detailed description below of various embodiments of the invention given by way of non-limiting examples.

[0015] [Fig-1] Fig. 1 schematically presents an example of a product according to one aspect of the invention.

[0016] [Fig.2] Fig.2 schematically presents another example of a product according to a aspect of the invention.

[0017] [Fig.3] Fig.3 schematically presents another example of a product according to a aspect of the invention.

[0018] [Fig.4] Fig.4 schematically presents an example of an insulating system formed at means of products according to the invention.

[0019] [Fig. 5] Fig. 5 schematically presents another example of an insulating system formed using products according to the invention.

[0020] [Fig. 6] Figure 6 schematically presents another example of an insulating system formed using products according to the invention.

[0021] [Fig.7] Fig.7 schematically illustrates an example of apparatus for the production of a product according to the invention.

[0022] [Fig.8] Figure 8 schematically illustrates an example of a step in a process of formation of hollowed-out areas in a primary band.

[0023] [Fig.9] Figure 9 schematically illustrates an example of a primary band featuring recesses.

[0024] [Fig. 10] The [Fig. 10] schematically presents an example of a product according to the invention.

[0025] Throughout all the figures, the common elements are identified by identical numerical references. Description of the implementation methods

[0026] Fig. 1 schematically presents an example of product 1 according to one aspect of the invention.

[0027] The product as presented is an insulating product in the form of a strip or plate, comprising a primary layer 10 extending in a longitudinal and a transverse direction, as well as a top metallized film 20.

[0028] In the illustrated example, the primary layer 10 comprises a single layer, on which the upper metallized film 20 is positioned.

[0029] In this text, the designations "superior" and "inferior" are purely indicative and not limiting, and are intended solely to facilitate understanding.

[0030] The upper metallized film 20 comprises an adhesion layer 24, a support layer 23 and a metallized layer 22. The support layer 23 is interposed between the adhesion layer 24 and the metallized layer 22.

[0031] The primary layer 10 is typically made of foam, typically low-density polyethylene (LDPE). In the case of a multilayer layer, it may also include other materials, in particular high-density polyethylene (HDPE).

[0032] The upper metallized film 20 is typically a polyethylene or polypropylene-based metallized film whose emissivity, measured on the metallized face according to EN16012, is typically between 0.02 and 0.2, more precisely between 0.05 and 0.07. The metallization is, for example, aluminum. The layer The metallized layer typically has a thickness of around one hundred Angstroms. The tack coat 24 is thus typically made of low-density polyethylene (LDPE). The support layer 23 is typically made of high-density polyethylene (HDPE).

[0033] The upper metallized film 20 is attached to the upper face of the primary layer 10 via its tack layer 24, so that the tack layer 24 in LDPE is attached to an LDPE layer of the primary layer 10.

[0034] Figure 2 schematically presents another example of product 1 according to one aspect of the invention.

[0035] This embodiment includes the elements already presented with reference to [Fig.1], as well as the elements detailed below.

[0036] In this embodiment, the product also includes a lower metallized film 30, attached to the lower face of the primary layer 10, i.e. to the lower face of the lower layer 300 by calendering.

[0037] The lower metallized film 30 comprises an adhesion layer 34, a support layer 33 and a metallized layer 32. The support layer 33 is interposed between the adhesion layer 34 and the metallized layer 32.

[0038] The lower metallized film 30 is typically a polyethylene or polypropylene-based metallized film whose emissivity, measured on the metallized face according to EN16012, is typically between 0.02 and 0.2, more precisely between 0.05 and 0.07. The metallization is, for example, aluminum. The tack coat 34 is thus typically made of low-density polyethylene (LDPE). The support layer 33 is typically made of high-density polyethylene (HDPE).

[0039] The lower metallized film 30 is attached to the lower face of the primary layer 10 via its tack layer 34, so that the tack layer 34 in LDPE is attached to an LDPE layer of the primary layer 10.

[0040] Figure 3 schematically presents another example of product 1 according to one aspect of the invention.

[0041] This embodiment includes the elements already presented with reference to Figures 1 and 2, as well as the elements detailed below.

[0042] In this embodiment, primary layer 10 is formed of three superimposed layers, designated successively by 102, 101 and 103, in a direction going from the upper metallized film 20 to the lower metallized film 30. Layers 101, 102 and 103 are typically made of low-density polyethylene (LDPE), or are typically predominantly made of low-density polyethylene (LDPE).

[0043] More generally, the primary layer 10 can be formed from a stack of any number of layers. The layers forming the primary layer 10 can be arranged symmetrically or asymmetrically.

[0044] The various products offered are thin products, typically having a thickness between 2 and 10 mm.

[0045] Figure 4 schematically presents an example of an insulating system formed using products according to the invention.

[0046] In this example, four products designated by the reference numerals IA, IB, IC, and 1D are superimposed. These products may be identical or distinct. For example, they may be four identical products, each having a structure as described previously with reference to one of Figures 1 to 3.

[0047] The assembly thus defines an insulating plate or panel, the rigidity of which depends in particular on the number of superimposed products and the structure of each of the products.

[0048] Such a superposition of products makes it possible to obtain an assembly having improved properties in terms of thermal insulation.

[0049] Figure 5 schematically presents another example of an insulating system formed using products according to the invention.

[0050] In this embodiment, two products 1F and IG form two horizontal panels, while products 1H are positioned between these two products 1F and IG so as to form an openwork structure. In the illustrated example, the products 1H are positioned so as to form a corrugated, interlocking, or crenellated structure, thus defining recesses between the products 1F and IG.

[0051] Such a structure makes it possible to form a panel-type product comprising air pockets which thus contribute to thermal insulation.

[0052] The illustrated embodiment is not limiting; in particular, several assemblies constructed in this manner can be superimposed, or different layers of products can be superimposed to form an openwork structure. In particular, several layers of product 1H can be positioned in a staggered pattern between products 1F and IG.

[0053] Figure 6 schematically presents another example of an insulating system formed using products according to the invention.

[0054] This figure shows an insulating system comprising an outer film 4, typically a metallized film, to which are associated a plurality of assemblies, each assembly being composed of a product 1 as defined above and a film 5, typically a metallized film. Such an assembly is typically referred to as a "simplex". A first assembly is bonded to the outer film 4 such that the product is located between the outer film 4 and the film 5 of the assembly.

[0055] A second assembly can be assembled to the first assembly, so that the product 1 of the second assembly is between two films 5. Several assemblies can be superimposed in this way to obtain a system of the desired thickness and exhibiting the desired thermal insulation properties.

[0056] In the illustrated example, the products 1 form a wavy, interlaced or crenellated structure. In the case of a system comprising several superimposed assemblies, the different assemblies are typically positioned in a staggered pattern, so that the undulations or patterns formed by the products 1 are offset by half a step to allow for their assembly.

[0057]

[0058] Figure 7 schematically illustrates an example of apparatus for carrying out of a product as previously presented.

[0059] A device for calendering the metallized films 20 and 30 on either side of the primary layer 10 is schematically represented in this figure. It is clear that, depending on the structure of the desired product, the device can be modified, in particular to apply only one of the metallized films 20 and 30.

[0060] The device as presented thus comprises two pairs of rollers; a first pair of rollers RI 1 and R12, and a second pair of rollers R21 and R22. The direction of movement of the product is symbolized by an arrow.

[0061] The primary sheet 10 is brought between each of the pairs of rollers.

[0062] The upper metallized film 20 is supplied at the level of the first pair of rollers RI 1 and R12. In the illustrated example, the upper metallized film 20 is driven by the roller RI 1 of the first pair of rollers.

[0063] The RI 1 roller of the first pair of rollers is typically a heating roller, suitable for applying thermal energy to the elements in contact.

[0064] The rollers RI 1 and R12 are positioned so as to define a gap for the passage of the primary layer 10 and the first metallized film 20.

[0065] The gap between the rollers RI 1 and R12 and the heating effect achieved by the roller RI 1 are dimensioned so as to achieve at least partial melting of the tack layer 22 of the upper metallized film 20, and thus to bond the upper metallized film 20 to the primary layer 10.

[0066] The heating temperature of the RI 1 roller is defined in particular as a function of the rotation speed of the RI 1 roller, the materials forming the upper metallized film 20 and the primary layer 10, and also the dimensions of the RI 1 roller.

[0067] The heating temperature of the roller RI 1 is typically defined so as not to cause the melting of the support layer 23 of the upper metallized film 20.

[0068] The passage between the rollers RI 1 and R12 thus allows the upper metallized film 20 to be assembled onto the primary layer 10 by calendering.

[0069] Similarly, the lower metallized film 30 is supplied at the level of the second pair of rollers R21 and R22. In the illustrated example, the lower metallized film 30 is driven by roller R21 of the second pair of rollers.

[0070] The R21 roller of the first pair of rollers is typically a heated roller, suitable for applying thermal energy to the elements in contact.

[0071] The rollers R21 and R22 are positioned so as to define a gap for the passage of the primary layer 10 and the second metallized film 30.

[0072] The gap between rollers R21 and R22 and the heating effect produced by roller R21 are dimensioned so as to achieve at least partial melting of the tack layer 32 of the lower metallized film 30, and thus to bond the lower metallized film 30 to the primary layer 10.

[0073] The heating temperature of roller R21 is defined in particular as a function of the rotation speed of roller R21, the materials forming the lower metallized film 30 and the primary layer 10, and also the dimensions of roller R21. The heating temperature of roller RI 1 is typically defined so as not to cause the melting of the support layer 33 of the lower metallized film 30.

[0074] The passage between rollers R21 and R22 thus allows the lower metallized film 30 to be assembled onto the primary layer 10 by calendering.

[0075] According to another aspect of the invention, the primary layer 10 can be perforated.

[0076] The primary layer 10 is typically a layer of foam, typically in Polyethylene. This foam sheet is typically solid (or not perforated) when it is formed, and is then typically perforated by a suitable process, in particular a process such as will be described later.

[0077] Figure 8 shows an example of a primary sheet 10. In this example, cuts 54 are made in this primary sheet 10, typically in a staggered pattern. The cuts 54 as shown are made along a vertical or longitudinal direction XX of the primary sheet 10.

[0078] The primary sheet 10 can then be stretched along the transverse direction YY perpendicular to the longitudinal direction XX, i.e. along the horizontal direction in Figures 8 and 9.

[0079] The effect of this stretching is shown in [Fig. 9]. Here, we observe a stretching of the primary sheet 10 along the transverse direction YY, and a contraction of the primary sheet 10 along the transverse direction XX. The cuts 54 previously formed in the primary sheet open up and here form openings 52 schematically represented here as having the shape of squares or diamonds.

[0080] The primary sheet 10 thus stretched is then typically heated so as to fix this shaping.

[0081] The primary sheet 10 thus obtained is a perforated sheet, the degree of openness of which depends in particular on the cuts made and the stretching carried out.

[0082] Obtaining a primary layer 10 in the form of an open-cell foam is advantageous in terms of insulation. Indeed, once the primary layer 10 is wrapped On either side, for example, using metallized films—typically a 20 mm upper metallized film and a 30 mm lower metallized film as described previously—the perforated areas form air gaps or air bubbles that offer better thermal insulation properties than foam. The application of metallized films can be achieved, in particular, by bonding or by calendering as defined previously.

[0083] Figure 10 schematically presents an example of the product thus obtained. The upper metallized film 20 and the lower metallized film 30 are bonded to the primary layer 10 at the non-perforated areas.

[0084] According to one example, the primary aquifer 10 has an openness rate between 10% and 80%, or between 40% and 60%.

[0085] The opening ratio is defined as the surface area of ​​the recesses in relation to the total surface area of ​​the primary layer 10, viewed along a plane defined by the longitudinal direction XX and the transverse direction YY of the primary layer 10.

[0086] Although the present invention has been described with reference to specific embodiments, it is evident that modifications and changes can be made to these examples without departing from the general scope of the invention as defined by the claims. In particular, individual features of the various embodiments illustrated / mentioned can be combined in additional embodiments. Therefore, the description and drawings should be considered in an illustrative rather than a restrictive sense.

[0087] It is also evident that all the characteristics described with reference to a process are transposable, alone or in combination, to a device, and conversely, all the characteristics described with reference to a device are transposable, alone or in combination, to a process.

Claims

Demands

1. Multilayer insulating product strip comprising: - a primary layer (10) extending in a longitudinal and a transverse direction, - a top metallized film (20), comprising an adhesion layer (24), a support layer (23) and a metallized layer (22), the support layer (23) being interposed between the adhesion layer (24) and the metallized layer (22), the primary layer (10) comprising a layer of low-density polyethylene, the support layer (23) being composed of high-density polyethylene, the adhesion layer (24) comprising low-density polyethylene, the top metallized film (20) being calendered onto the primary layer (10), so that the adhesion layer (24) is bonded to the low-density polyethylene layer of the primary layer (10).

2. Insulating product strip according to claim 1, further comprising a lower metallized film (30), comprising an adhesion layer (34), a support layer (33) and a metallized layer (32), the support layer (33) being interposed between the adhesion layer (34) and the metallized layer (32), the support layer (23) being composed of high-density polyethylene, the adhesion layer (24) comprising low-density polyethylene, said lower metallized film (30) being calendered onto the primary layer (10), so that the adhesion layer (34) is bonded to the low-density polyethylene layer of the primary layer (10), and so that the primary layer (10) is positioned between the upper metallized film (20) and the lower metallized film (30).

3. Assembly comprising a plurality of insulating product strips according to any one of claims 1 or 2, said strips defining: - an upper strip, - a lower strip, - a plurality of intermediate strips, positioned between the upper strip and the lower strip, said intermediate strips forming an openwork structure.

4. A method for manufacturing a thermal insulation mat, wherein: - or provides a primary sheet (10) extending in a longitudinal and a transverse direction, the primary sheet (10) comprising a layer of low-density polyethylene; - a top metallized film (20) is provided, comprising an adhesive layer (24), a support layer (23) and a metallized layer (22), the support layer (23) being interposed between the adhesive layer (24) and the metallized layer (22), the support layer (23) being composed of high-density polyethylene, the adhesive layer (24) comprising low-density polyethylene; - the top metallized film (20) is applied to the upper surface of the primary sheet (10) by means of a heating cylinder (RI 1), so as to partially melt the adhesive layer (24), and to calender the top metallized film (20) onto the primary sheet (10), so as to bond the adhesive layer (24) to the low-density polyethylene layer of the sheet primary (10).

5. A method according to claim 4, wherein: - a bottom metallized film (30) is provided, comprising an adhesive layer (34), a support layer (33) and a metallized layer (32), the support layer (33) being interposed between the adhesive layer (34) and the metallized layer (32), the support layer (23) being composed of high-density polyethylene, the adhesive layer (24) comprising low-density polyethylene, - the bottom metallized film (30) is applied to the underside of the primary sheet (10) by means of a heating cylinder (R21), so as to partially melt the material of the adhesive layer (34) of the bottom metallized film (30), and to calender the bottom metallized film (30) onto the primary sheet (10), so as to bond the adhesive layer (34) to the low-density polyethylene layer of the primary sheet (10),and in such a way that the primary layer (10) is positioned between the upper metallized film (20) and the lower metallized film (30).

6. A method according to any one of claims 4 or 5, wherein prior to the primary sheet supply step (10), a primary sheet (10) perforation step is carried out, wherein: - either a primary sheet (10) is supplied extending along a longitudinal direction and a transverse direction, - cuts (54) are made in the primary layer (10), said cuts being made in such a way as to extend along the longitudinal direction, - the primary sheet (10) is stretched along the transverse direction, so as to stretch the cutouts and form openings (52) in the primary sheet, - the primary sheet (10) thus stretched is fixed by heating or heat fixing.