Method for reducing sheet resistance of articles coated with transparent conductive oxides

Abstract

To provide a method of reducing a sheet resistance or emissivity of a coated article.SOLUTION: A method of reducing a sheet resistance of a coated article comprises applying a coating to a substrate, where the coating comprises a transparent conductive oxide layer having a thickness of 125 nm to 950 nm at room temperature; and processing the transparent conductive oxide layer. The processing step comprises flash-annealing the transparent conductive oxide layer so that the transparent conductive oxide layer reaches 224°C to 470°C. The flash annealing of the transparent conductive oxide layer heats a surface of the transparent conductive oxide layer. The sheet resistance of the coated article after the processing step is 20 Ω / sq. or less.SELECTED DRAWING: Figure 7a

Description

[Technical field]

[0001] The present invention relates to coated articles having low emissivity and neutral color. [Background technology]

[0002] To provide coated articles with lower emissivity and lower sheet resistance, transparent conductive oxides ("TCOs") are applied to substrates. This makes them particularly useful in electrodes (e.g., solar cells) or heating layers that activate glazing units or screens. TCOs are usually applied by vacuum deposition techniques such as magnetron sputtering vacuum deposition ("MSVD"). Generally, thicker TCO layers provide lower sheet resistance. However, the thickness of the TCO affects the color of the coated article. Therefore, there is a need to adjust the coloring effect caused by the TCO layer. Furthermore, there is a need to minimize the thickness of the TCO layer to minimize the effect of the TCO on the color of the coated article while still maintaining the required sheet resistance.

[0003] The coating stack may corrode over time. To protect against this, a protective overcoat can be applied to the coating. For example, titanium dioxide films disclosed in U.S. Pat. Nos. 4,716,086 and 4,786,563 are protective films that provide chemical resistance to the coating. Silicon oxide, disclosed in Canadian Patent No. 2,156,571, aluminum oxide and silicon nitride, disclosed in U.S. Pat. Nos. 5,425,861, 5,344,718, 5,376,455, 5,584,902, and 5,532,180, and PCT International Patent Publication No. 95 / 29883, are also protective films that provide chemical resistance to the coating. This technology can also be improved with protective overcoats that are more chemically and / or mechanically durable. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] U.S. Patent No. 4,716,086 [Patent Document 2] U.S. Patent No. 4,786,563 [Patent Document 3] Canadian Patent No. 2,156,571 [Patent Document 4] U.S. Patent No. 5,425,861 [Patent Document 5] U.S. Patent No. 5,344,718 [Patent Document 6] U.S. Patent No. 5,376,455 [Patent Document 7] U.S. Patent No. 5,584,902 [Patent Document 8] U.S. Patent No. 5,532,180 [Patent Document 9] PCT International Patent Publication No. 95 / 29883 Summary of the Invention [Means for solving the problem]

[0005] The coated article includes a substrate and an underlayer over the substrate. The underlayer includes a first layer. The first layer includes a high refractive index material. A second layer is positioned over at least a portion of the first layer. The second layer includes a low refractive index material. A transparent conductive film is positioned over at least a portion of the underlayer. The coated article has a sheet resistance of at least 5 Ω / □ and at most 25 Ω / □. The coated article has a color with an a* of at least -9 and at most 1, and a b* of at least -9 and at most 1.

[0006] Optionally, the coated article can have a protective layer over at least a portion of the transparent conductive oxide layer. The protective layer includes a first protective film over at least a portion of the transparent conductive oxide layer and a second protective film over at least a portion of the first protective film. The second protective film is the outermost film in the coating stack and includes a mixture of titania and alumina. Optionally, the protective layer can include a third protective film positioned between the first protective film and the second protective film.

[0007] A method of forming a coated substrate includes providing a substrate. A transparent conductive oxide is identified and a thickness is determined for the transparent conductive oxide that provides a sheet resistance of at least 5 Ω / □ and at most 25 Ω / □. An underlayer having a first underlayer material and a second underlayer material is identified. A thickness is determined for the first underlayer and the second underlayer that provides the coated substrate with a color having an a* of at least -9 and at most 1, and a b* of at least -9 and at most 1. The thicknesses of the two films in the underlayer are used to adjust the color of the coated substrate. The color is adjusted after the thickness of the transparent conductive oxide film is determined, since the color is affected by the thickness of the transparent conductive oxide film. A first underlayer film including the first underlayer material is deposited on at least a portion of the substrate at a first underlayer thickness. A second underlayer film including the second underlayer material is deposited on at least a portion of the first underlayer at a second underlayer thickness. A transparent conductive oxide layer having a transparent conductive oxide is deposited on at least a portion of the second underlayer film at a transparent conductive oxide thickness.

[0008] A coated article having a color with an a* of at least -9 and at most 1 and a b* of at least -9 and at most 1 made by the following steps: A transparent conductive oxide is identified and a thickness is determined for the transparent conductive oxide that provides a sheet resistance of at least 5 Ω / □ and at most 25 Ω / □; An underlayer is identified having a first underlayer material and a second underlayer material; A thickness is determined for the first underlayer and the second underlayer that provides the coated substrate with a color with an a* of at least -9 and at most 1 and a b* of at least -9 and at most 1; The thicknesses of the two films in the underlayer are used to adjust the color of the coated substrate; The color is adjusted after the thickness of the transparent conductive oxide film is determined, since the color is affected by the thickness of the transparent conductive oxide film; A first underlayer film including a first underlayer material is deposited on at least a portion of the substrate at a first underlayer film thickness; A second underlayer film including a second underlayer material is deposited on at least a portion of the first underlayer at a second underlayer thickness. A transparent conductive oxide layer having a transparent conductive oxide thickness is deposited over at least a portion of the second underlayer film.

[0009] A coated article comprising a substrate. An underlayer is positioned over at least a portion of the substrate. The underlayer includes at least a first underlayer film over at least a portion of the substrate and an optional second underlayer film over at least a portion of the first underlayer film. The first underlayer film contains a first high refractive index material. The optional second underlayer film contains a first low refractive index layer. A transparent conductive oxide layer is positioned over at least a portion of the first underlayer film or the optional second underlayer film. A second high refractive index material is embedded within the transparent conductive oxide layer. The coated article has a sheet resistance of at least 5 Ω / □ and at most 25 Ω / □. The sheet resistance is at least 35% higher than when the second high refractive index material is not embedded within the transparent conductive oxide layer.

[0010] Optionally, the coated article can have a protective layer over at least a portion of the transparent conductive oxide layer. The protective layer includes a first protective film over at least a portion of the transparent conductive oxide layer and a second protective film over at least a portion of the first protective film. The second protective film is the outermost film in the coating stack and includes a mixture of titania and alumina. Optionally, the protective layer can include a third protective film positioned between the first protective film and the second protective film.

[0011] A coated article comprising a substrate. An underlayer is positioned over at least a portion of the substrate. The underlayer includes at least a first underlayer film over at least a portion of the substrate and an optional second underlayer film over at least a portion of the first underlayer film. The first underlayer film contains a first high refractive index material. The optional second underlayer film contains a first low refractive index layer. A first transparent conductive oxide layer is positioned over at least a portion of the first underlayer film or the optional second underlayer film. A buried film is positioned over at least a portion of the first transparent conductive oxide layer. The buried film has a second high refractive index material. A second transparent conductive oxide layer is positioned over at least a portion of the second transparent conductive oxide layer. The coated article has a sheet resistance of at least 5 Ω / □ and at most 25 Ω / □. The sheet resistance is at least 35% higher than without the buried film.

[0012] Optionally, the coated article can have a protective layer over at least a portion of the transparent conductive oxide layer. The protective layer includes a first protective film over at least a portion of the transparent conductive oxide layer and a second protective film over at least a portion of the first protective film. The second protective film is the outermost film in the coating stack and includes a mixture of titania and alumina. Optionally, the protective layer can include a third protective film positioned between the first protective film and the second protective film.

[0013] A method of forming a coated article, increasing sheet resistance, or increasing light transmission of a coated article. A substrate is provided. An underlayer is deposited over at least a portion of the substrate. A first underlayer film is deposited over at least a portion of the substrate. The first underlayer film has a first high refractive index material. An optional second underlayer film is deposited over at least a portion of the first underlayer film. The optional second underlayer film has a first low refractive index layer. A first transparent conductive oxide layer is deposited over at least a portion of the first underlayer film or the optional second underlayer film. A buried film is deposited over at least a portion of the first transparent conductive oxide film. The buried film has a second high refractive index material. A second transparent conductive oxide film is deposited over at least a portion of the buried film. Optionally, a protective layer can be deposited over the second transparent conductive oxide film. The optional protective layer includes a first protective film over at least a portion of the transparent conductive oxide layer and a second protective film over at least a portion of the first protective film. The second protective film is the outermost film in the coating stack and includes a mixture of titania and alumina. Optionally, the protective layer can include a third protective film positioned between the first protective film and the second protective film.

[0014] A coated article made by the steps of: A substrate is provided; an underlayer is deposited on at least a portion of the substrate; a first underlayer film is deposited on at least a portion of the substrate; the first underlayer film has a first high refractive index material; an optional second underlayer film is deposited on at least a portion of the first underlayer film; the optional second underlayer film has a first low refractive index layer; a first transparent conductive oxide layer is deposited on at least a portion of the first underlayer film or the optional second underlayer film; a buried film is deposited on at least a portion of the first transparent conductive oxide film; the buried film has a second high refractive index material; a second transparent conductive oxide film is deposited on at least a portion of the buried film; optionally, a protective layer can be deposited on the second transparent conductive oxide film; the optional protective layer includes a first protective film on at least a portion of the transparent conductive oxide layer and a second protective film on at least a portion of the first protective film. The second protective coating is the outermost coating in the coating stack and comprises a mixture of titania and alumina. Optionally, the protective layer can include a third protective coating positioned between the first and second protective coatings.

[0015] A method for increasing the sheet resistance of a coated article. A coated article is provided. The coated article has a substrate and a transparent conductive oxide layer on at least a portion of the substrate. The coated article is treated by a post-deposition process. The post-deposition process can be tempering the coated article, heating the entire coated article by placing the coated article in a furnace, flash annealing only one surface of the transparent conductive oxide layer, or passing an eddy current through the transparent conductive oxide layer. Alternatively, a coated article having a sheet resistance of less than 25 ohms / square is produced by the method described in this paragraph.

[0016] A method for increasing the sheet resistance of a coated article. A substrate is provided. A transparent conductive oxide is deposited over at least a portion of the substrate. A post-deposition process is applied to the transparent conductive oxide coated substrate. The post-deposition process can be tempering the coated article, heating the entire coated article by placing the coated article in a furnace, flash annealing only one surface of the transparent conductive oxide layer, or passing an eddy current through the transparent conductive oxide layer.

[0017] The coated article is a substrate having a coating stack. At least a portion of the substrate is coated with a functional coating. A protective layer is applied over at least a portion of the functional coating. The protective layer has a first protective film over at least a portion of the functional coating and a second protective film over at least a portion of the functional coating. The second protective film is the last film in the coating stack and includes titania and alumina. Optionally, a third protective film can be positioned between the first and second protective films or between the first protective film and the functional coating.

[0018] A method of making a coated article includes providing a substrate. A functional coating is deposited over at least a portion of the substrate. A first protective coating is deposited over at least a portion of the functional coating. A second protective coating comprising titania and alumina is deposited over at least a portion of the first protective coating. Optionally, a third protective coating is deposited between the first and second protective coatings or between the first protective coating and the functional coating.

[0019] A method for reducing the absorptivity, resistivity, or emissivity of a transparent conductive oxide layer. A substrate is provided. A transparent conductive oxide layer is deposited on at least a portion of the substrate in an atmosphere containing 0% to 2.0% oxygen.

[0020] A coated article having reduced absorptivity, resistivity, or emissivity comprising a transparent conductive oxide layer made by the steps of: providing a substrate; depositing a transparent conductive oxide layer over at least a portion of the substrate in an atmosphere containing 0% to 2.0% oxygen;

[0021] The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee. [Brief description of the drawings]

[0022] [Figure 1a] 1 is a side view (not to scale) of a coating incorporating features of the present invention; [Figure 1b] 1 is a side view (not to scale) of a coating incorporating features of the present invention; [Figure 1c] 1 is a side view (not to scale) of a coating incorporating features of the present invention; [Figure 1d] 1 is a side view (not to scale) of a coating incorporating features of the present invention; [Figure 2a] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 2b] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 2c] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 2d] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 2e] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 3a] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 3b] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 3c] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 3d] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 3e] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 4a]1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 4b] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 5a] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 5b] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6a] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6b] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6c] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6d] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6e] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6f] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6g] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 6h] 1 is a side view (not to scale) of another coating incorporating features of the present invention; [Figure 7a] 1 is a graph showing the relationship between ITO sheet resistance and thickness for samples having an ITO transparent conductive oxide layer surface heated to specified temperatures. [Figure 7b] 1 is a graph showing the relationship between ITO sheet resistance and thickness for samples having an ITO transparent conductive oxide layer surface heated to specified temperatures. [Figure 8a] 1 is an XRD graph showing the crystallization of a transparent conductive oxide layer of tin-doped indium oxide. [Figure 8b] 1 is an XRD graph showing the crystallization of a transparent conductive oxide layer of tin-doped indium oxide. [Figure 8c]1 is an XRD graph showing the crystallization of a transparent conductive oxide layer of tin-doped indium oxide. [Figure 9] FIG. 1 shows the sheet resistance of a transparent conductive oxide layer of gallium doped zinc oxide as deposited and after heating. [Figure 10] FIG. 1 shows the sheet resistance of a transparent conductive oxide layer of aluminum doped zinc oxide as deposited and after heating. [Figure 11] 1 is a graph showing the effect of an underlayer on the color of a substrate having a 170 nm thick transparent conductive oxide layer of tin-doped indium oxide. [Figure 12] 1 is a graph showing the effect of underlayer on color of a substrate having a 175-225 nm thick transparent conductive oxide layer of tin-doped indium oxide and a protective layer of silica. [Figure 13a] 1 is a graph showing the effect of a buried film on sheet resistance. [Figure 13b] 1 is a graph showing the effect of a buried film on emissivity. [Figure 13c] 1 is an XRD graph of indium doped tin oxide with a buried film. [Figure 14] 1 is a bar graph showing the durability of different protective layers. [Figure 15] 1 is a bar graph showing the durability of different protective layers. [Figure 16a] 1 is a line graph showing normalized absorptance for a transparent conductive oxide layer including indium doped tin oxide in an atmosphere having 0% to 2% oxygen. [Figure 16b] 1 is a line graph showing normalized absorptance for a transparent conductive oxide layer including indium doped tin oxide in an atmosphere having 0% to 2% oxygen. [Figure 17a] 1 is a graph showing emissivity for a transparent conductive oxide layer including indium doped tin oxide in an atmosphere having 0% to 2% oxygen. [Figure 17b] 1 is a graph showing emissivity for a transparent conductive oxide layer including indium doped tin oxide in an atmosphere having 0% to 2% oxygen. [Figure 18] 1 is a graph showing normalized absorptance for a transparent conductive oxide layer including zinc oxide doped with aluminum in an atmosphere having 0% to 6% oxygen. [Figure 19] 1 is a graph showing normalized absorptance as a function of oxygen content supplied to the coater. [Figure 20] 1 is a graph showing sheet resistance for a transparent conductive oxide layer comprising indium doped tin oxide after post-deposition treatment as a function of the surface temperature of the transparent conductive oxide layer. [Figure 21] 1 is a graph showing sheet resistance as a function of surface temperature of a transparent conductive oxide. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0023] Spatial or directional terms used herein, such as "left," "right," "upper," "lower," etc., relate to the present invention as depicted in the drawings. It is understood that the present invention may assume various alternative orientations, and therefore such terms should not be considered limiting.

[0024] As used herein, terms expressing space or direction, such as "left", "right", "inside", "outside", "above", "below", etc., refer to the present invention as depicted in the drawings. However, it should be understood that the present invention can assume various alternative orientations, and therefore such terms should not be considered limiting. Furthermore, as used herein, all numbers expressing dimensions, physical properties, processing parameters, quantities of ingredients, reaction conditions, and the like, used in the specification and claims are to be understood in all instances to be modified by the term "about". Thus, unless otherwise indicated, the numerical values ​​set forth in the following specification and claims may vary depending on the desired properties sought to be obtained by the present invention. At the very least, and without attempting to limit the application of the doctrine of equivalents to the scope of the claims, each numerical value should be construed at least in light of the number of reported significant digits and by applying ordinary rounding techniques. Furthermore, all ranges disclosed herein should be understood to encompass the beginning and end values ​​of the range, as well as any subranges subsumed therein. For example, a stated range of "1-10" should be considered to include all subranges from a minimum value of 1 to a maximum value of 10 (inclusive), i.e., all subranges beginning with a minimum value of 1 or greater and ending with a maximum value of 10 or less, such as 1-3.3, 4.7-7.5, 5.5-10, etc. Additionally, without limitation, all documents, such as issued patents and patent applications, referenced herein should be considered to be "incorporated by reference" in their entirety. Unless otherwise specified, all references to amounts are in "weight percent" units. The term "film" refers to a region of a coating having a desired or selected composition. A "layer" includes one or more "films." A "coating" or "coating stack" is composed of one or more "layers." The terms "metal" and "metal oxide" should be considered to include silicon and silica, respectively, as well as conventionally recognized metals and metal oxides, even though silicon is not strictly a metal.

[0025] All numbers used in the specification and claims are to be understood in all instances to be modified by the term "about." All ranges disclosed herein are to be understood to encompass the beginning and ending values ​​of the range, as well as any subranges subsumed therein. The ranges set forth herein represent average values ​​in the specified range.

[0026] The term "over" means "further from the substrate." For example, a second layer located "over" a first layer means that the second layer is located further from the substrate than the first layer. The second layer may be in direct contact with the first layer, or there may be one or more other layers located between the second layer and the first layer.

[0027] All documents referenced herein should be considered "incorporated by reference" in their entirety.

[0028] Unless otherwise specified, all references to amounts are in "weight percent" units.

[0029] The term "visible light" means electromagnetic radiation having wavelengths within the range of 380 nm to 780 nm. The term "infrared radiation" means electromagnetic radiation having wavelengths within the range of greater than 780 nm to 100,000 nm. The term "ultraviolet radiation" means electromagnetic energy having wavelengths within the range of 100 nm to less than 380 nm.

[0030] The terms "metal" and "metal oxide" include silicon and silica, respectively, as well as conventionally recognized metals and metal oxides, even though silicon may not traditionally be considered a metal. "At least" means "greater than or equal to." "Less than or equal to" means "less than or equal to."

[0031] All haze and transmission values ​​herein are determined in accordance with ASTM D1003-07 using a Haze-Gard Plus visibility meter (available from BYK-Gardner USA).

[0032] In instances where the percent oxygen in a coater is referenced, the percent oxygen is the amount of oxygen added to the coater chamber relative to other gases. For example, if 2% oxygen is added to the coater chamber atmosphere, then 2% oxygen and 98% argon is added to the coater chamber. The argon can be replaced with other gases, but in many cases the gas is an inert gas.

[0033] In the discussion of the invention herein, certain features may be described as "particularly" or "preferably" within certain limits (e.g., "preferably," "more preferably," or "even more preferably" within certain limits). It is to be understood that the invention is not limited to these specific or preferred limits, but rather encompasses the entire scope of the disclosure.

[0034] The present invention comprises, consists of, or consists essentially of the following aspects of the invention, in any combination. Various aspects of the invention are shown in separate drawings. However, it should be understood that this is for ease of illustration and discussion only. In practicing the invention, one or more aspects of the invention shown in one drawing may be combined with one or more aspects of the invention shown in one or more of the other drawings.

[0035] An exemplary article includes a substrate 10, an underlayer 12 on the substrate 10, and a transparent conductive oxide 14 on the underlayer 12, as shown in FIG.

[0036] Article 2 can be a window, a solar mirror, a solar cell, or an organic light emitting diode. The coating applied to substrate 10 can provide low emissivity, low resistivity, scratch resistance, radio frequency attenuation, or a desired color.

[0037] Substrate 10 can be transparent, translucent, or opaque to visible light. "Transparent" means having a visible light transmittance greater than 0% up to 100%. Alternatively, substrate 12 can be translucent or opaque. "Translucent" means allowing electromagnetic energy (e.g., visible light) to pass through but diffusing this energy such that objects on the opposite side to the viewer are not clearly visible. "Opaque" means having a visible light transmittance of 0%.

[0038] The substrate 10 can be glass, plastic, or metal. Examples of suitable plastic substrates include acrylic polymers, such as polyacrylates; polyalkyl methacrylates, such as polymethyl methacrylate, polyethyl methacrylate, polypropyl methacrylate, and the like; polyurethanes; polycarbonates; polyalkyl terephthalates, such as polyethylene terephthalate (PET), polypropylene terephthalate, polybutylene terephthalate, and the like; polysiloxane-containing polymers; or copolymers of any monomers for preparing the same, or any mixtures thereof, or glass substrates. Examples of suitable glass substrates include conventional soda-lime silicate glass, borosilicate glass, or leaded glass. The glass can be clear glass. By "clear glass" is meant untinted or colorless glass. Alternatively, the glass can be colored or otherwise colored glass. The glass can be annealed or heat treated glass. As used herein, the term "heat treated" means tempered or at least partially tempered. The glass can be of any type, such as conventional float glass, and can be of any composition with any optical properties, such as visible light transmittance, ultraviolet light transmittance, infrared light transmittance, and / or overall solar energy transmittance. Examples of suitable metal substrates include aluminum or stainless steel.

[0039] The substrate 10 can have high visible light transmittance at a reference wavelength of 550 nanometers (nm) and a thickness of 2 millimeters. By "high visible light transmittance" is meant a visible light transmittance of 85% or more, such as 87% or more, such as 90% or more, such as 91% or more, such as 92% or more at 550 nm.

[0040] The underlayer 12 can be a single layer, a homogeneous layer, a gradient layer, a bilayer, or can include multiple layers. By "homogeneous layer" we mean a layer in which the material is randomly distributed throughout the coating. By "gradient layer" we mean a layer having two or more components in which the concentration of the components varies (gradient or continuous) as the distance from the substrate 12 changes.

[0041] The underlayer 12 can include two films, a first underlayer film 20 and a second underlayer film 22. The first underlayer film 20 is positioned on the substrate 10 and is closer to the substrate 10 than the second underlayer film 22. The first underlayer film 20 can be a material having a higher refractive index than the second underlayer film 22 and / or the substrate 10. For example, the first underlayer film 20 can include a metal oxide, nitride, or oxynitride. Examples of suitable metals for the first underlayer film 20 include silicon, titanium, aluminum, zirconium, hafnium, niobium, zinc, bismuth, lead, indium, tin, tantalum, alloys thereof, or mixtures thereof. For example, the first underlayer film 20 can include oxides of zinc, tin, aluminum, and / or titanium, alloys thereof, or mixtures thereof. For example, the first underlayer film 20 can include oxides of zinc and / or tin. For example, the first underlayer film 20 can include zinc oxide and tin oxide, or zinc stannate.

[0042] The first underlayer film 20 may include zinc oxide. A zinc target for sputtering a zinc oxide film may include one or more other materials to improve the sputtering properties of the zinc target. For example, the zinc target may include up to 15% by weight, such as up to 10% by weight, such as up to 5% by weight of such material. The resulting zinc oxide layer should include a small percentage of oxide of the additive material, such as up to 15% by weight, such as up to 10% by weight, such as up to 9% by weight of the material oxide. In this specification, a layer deposited from a zinc target having up to 10% by weight, such as up to 5% by weight of additive material to enhance the sputtering properties of the zinc target, even if a small amount of additive material (or oxide of additive material) is present, is referred to as a "zinc oxide layer". An example of such a material is tin.

[0043] The first underlayer film 20 can include an alloy of zinc oxide and tin oxide. For example, the first underlayer film 20 can include or be a zinc stannate layer. "Zinc stannate" refers to a compound having the formula ZnX Sn 1-X O 2-X (Formula 1) refers to a composition where "x" varies in a range from greater than 0 to less than 1. For example, "x" can be greater than 0 and can be any fraction or decimal greater than 0 to less than 1. The zinc stannate layer has a predominant amount of one or more of the forms of Formula 1. Conventionally, a zinc stannate layer with x=2 / 3 is referred to as "Zn2SnO4". Zinc oxide and tin oxide alloys can include about 90% zinc and 10% tin by weight, such as 80% to 99% zinc and 20% to 1% tin by weight, 85% zinc to 99% zinc and 15% tin to 1% tin by weight, 90% zinc to 99% zinc and 10% tin to 1% tin by weight, and the like.

[0044] The second underlayer film 22 can be a material having a lower refractive index than the first underlayer film 20. For example, the second underlayer film 22 can include a metal oxide, nitride, or oxynitride. Examples of suitable metals for the second underlayer film 22 include silicon, titanium, aluminum, zirconium, phosphorus, hafnium, niobium, zinc, bismuth, lead, indium, tin, tantalum, alloys thereof, or mixtures thereof.

[0045] For example, the second underlayer film 22 can include silica and alumina. According to this example, the second underlayer film 22 should have at least 50% by weight silica, 50-99% by weight silica and 50-1% by weight alumina, 60-98% by weight silica and 40-2% by weight alumina, 70-95% by weight silica and 30-5% by weight alumina, 80-90% by weight silica and 10-20% by weight alumina, or 8% by weight silica and 15% by weight alumina.

[0046] A transparent conductive oxide layer 14 is located on the underlayer 12. The transparent conductive oxide layer 14 can be a single layer or can have multiple layers or regions. The transparent conductive oxide layer 14 has at least one conductive oxide layer. For example, the transparent conductive oxide layer 14 can include one or more metal oxide materials. For example, the transparent conductive oxide layer 14 can include one or more oxides including one or more of Zn, Fe, Mn, Al, Ce, Sn, Sb, Hf, Zr, Ni, Bi, Ti, Co, Cr, Si, In, or an alloy of two or more of these materials. For example, the transparent conductive oxide layer 14 can include tin oxide. In another example, the transparent conductive oxide layer 14 includes zinc oxide.

[0047] The transparent conductive oxide layer 14 may include one or more dopant materials, such as, but not limited to, F, In, Al, P, Cu, Mo, Ta, Ti, Ni, Nb, W, Ga, Mg, and / or Sb. For example, the dopant may be In, Ga, Al, or Mg. The dopant may be present in an amount less than 10% by weight, such as less than 5% by weight, such as less than 4% by weight, such as less than 2% by weight, such as less than 1% by weight. The transparent conductive oxide layer 14 can be a doped metal oxide such as gallium-doped zinc oxide ("GZO"), aluminum-doped zinc oxide ("AZO"), indium-doped zinc oxide ("IZO"), magnesium-doped zinc oxide ("MZO"), or tin-doped indium oxide ("ITO").

[0048] The transparent conductive oxide layer 14 can have a thickness in the range of 75 nm to 950 nm, such as 90 nm to 800 nm, such as 100 nm to 700 nm. For example, the transparent conductive oxide layer 14 can have a thickness in the range of 125 nm to 450 nm, at least 150 nm, or at least 175 nm. The transparent conductive oxide layer 14 can have a thickness of 600 nm, 500 nm, 400 nm, 350 nm, 300 nm, 275 nm, 250 nm, or 225 nm or less.

[0049] Different transparent conductive oxide layer 14 materials have different sheet resistances at the same thickness, which also affect the optical properties of the article in different ways. In theory, the sheet resistance should be less than 25 Ω / □ (ohms / square), or less than 20 Ω / □, or less than 18 Ω / □. For example, if the transparent conductive oxide layer 14 includes GZO, it can have a thickness of at least 300 nm and at most 400 nm. If the transparent conductive oxide layer 14 includes AZO, it should have a thickness of at least 350 nm or at least 400 nm, and at most 950 nm, or at most 800 nm, or at most 700 nm, or at most 600 nm. When the transparent conductive oxide layer 14 comprises ITO, it can have a thickness of at least 75 nm, at least 90 nm, at least 100 nm, at least 125 nm, or at least 150 nm, or at least 175 nm, and at most 350 nm, at most 300 nm, at most 275 nm, or at most 250 nm, or at most 225 nm.

[0050] The transparent conductive oxide layer 14 can have a surface roughness (RMS) in the range of 5 nm to 60 nm, such as 5 nm to 40 nm, such as 5 nm to 30 nm, such as 10 nm to 30 nm, such as 10 nm to 20 nm, such as 10 nm to 15 nm, such as 11 nm to 15 nm.

[0051] For example, when the transparent conductive oxide layer 14 is indium oxide doped with tin, the thickness of the transparent conductive oxide layer 14 can be within the range of 75 nm to 350 nm, 100 nm to 300 nm, 125 nm to 275 nm, 150 nm to 250 nm, or 175 nm to 225 nm.

[0052] The transparent conductive oxide layer 14 can have a sheet resistance within a range of 5Ω / □ to 25Ω / □, 8Ω / □ to 20Ω / □, etc. For example, 10Ω / □ to 18Ω / □.

[0053] For example, the article may be a glass substrate 10 over which is situated an underlayer 12. The underlayer 12 may have at least two films, a first underlayer film 20 and a second underlayer film 22. The first underlayer film 20 may be an alloy of zinc oxide and tin oxide, and the second underlayer film 22 may be an alloy of silica and alumina. Over the second film 22 may be situated a transparent conductive oxide layer 14. The transparent conductive oxide layer 14 may be ITO, GZO, or AZO.

[0054] The transparent conductive oxide film provides the article with a particular sheet resistance, for example, less than 25 Ω / □. Generally, as the thickness of the transparent conductive oxide increases, the sheet resistance decreases. After the desired sheet resistance and the thickness required for the transparent conductive oxide to achieve the desired sheet resistance are identified, the thickness of the first film and the second film can be determined using optical design software. One example of a suitable optical modeling software is FILM STAR. In theory, the color of a*, b* is sought to be -1, -1. Some variation in the color is acceptable. For example, a* can be increased to 1, 0, or -0.5, and decreased to -9, -4, -3, or -1.5, and the value of b* can be increased to 1, 0, or -0.5, and decreased to -9, -4, -3, or -1.5. To obtain the desired color, the thickness of the first film 20 and the second film 22 is changed to obtain the desired color for the specified transparent conductive oxide and transparent conductive oxide thickness. For example, the first film may be 10 to 20 nm thick or 11 to 15 nm thick, and the second film may be 25 to 35 nm thick or 29 to 34 nm thick.

[0055] 1c and 1d, the article 2 can optionally include a protective layer 16, such as a protective layer described herein, over the transparent conductive oxide layer 14. For example, the protective layer 16 can include a first protective film 60 and a second protective film 62. The second protective film 62 can include a mixture of titania and silica. For example, the protective layer 16 can have a first protective film 60, a second protective film 62, and a third protective film 64.

[0056] An exemplary method of the present invention is to form a coated substrate. A substrate 10 is provided. A transparent conductive oxide is identified. After the transparent conductive oxide is identified, a thickness can be identified for the transparent conductive film that provides the coated substrate with a sheet resistance of at least 5 Ω / □ and / or 25 Ω / □ or less, specifically 20 Ω / □ or less, more specifically 18 Ω / □ or less. A desired color of the coated substrate is also identified. A first underlayer material and a second underlayer material are identified using optical design software, and a first underlayer film thickness and a second underlayer film thickness that provide a color to an article having the transparent conductive oxide layer identified above are determined, where a* can be as high as 1 and as low as -9, and a value of b* can be as high as 1 and as low as -9. An underlayer 12 is deposited on the substrate by depositing a first underlayer material on the substrate to form a first underlayer film 20 to a specified first thickness, and depositing a second underlayer material on the first underlayer film to a specified second underlayer thickness to form a second underlayer film 22. A transparent conductive oxide material is deposited onto underlayer 12 to a specified transparent conductive thickness to form transparent conductive oxide layer 14 .

[0057] The thickness of the transparent conductive oxide layer 14 affects the sheet resistance and color of the substrate. The underlayer 12 is used to adjust the color of an article having a specific thickness of the transparent conductive oxide layer 14. This is done by identifying a first underlayer material and a second underlayer material, and then using a tool such as FILM STAR to identify a thickness for each underlayer material that provides the desired color. After the first and second underlayer materials are identified, the thickness of each of these materials can be adjusted to achieve any desired color. Typically, the desired color is to have a*, b* of -1, -1. Some variation in color is acceptable. For example, a* can be as high as 1 and as low as -9, and the value of b* can be as high as 1 and as low as -9.

[0058] For example, one may wish to create a solar cell having a color with an a* of -1 and a b* of -1. A glass substrate would be provided. The transparent conductive oxide material may be specified as indium doped tin oxide ("ITO"). It will be appreciated that the invention disclosed herein can achieve a sheet resistance of 5Ω / □ to 25Ω / □ when the ITO transparent conductive oxide film has a thickness of 125 nm to 275 nm. To achieve the desired color, an underlayer 12 can be selected having a first underlayer film 20 comprising zinc oxide and tin oxide and a second underlayer film 22 comprising silica and alumina. The first underlayer film 20 should have a thickness of 10 nm to 15 nm and the second underlayer film 22 should have a thickness of 29 nm to 34 nm. The first underlayer film 20 is deposited on the substrate 10 at a specified thickness and the second underlayer film 22 is deposited on the first underlayer film 20 at a specified thickness. The transparent conductive oxide layer 14 is deposited over the second underlayer film 22 at a specified thickness, thus forming an article having a color having an a* of -9 to 1, specifically -4 to 0, more specifically -3 to 1, more specifically -1.5 to -0.5, and a b* of -9 to 1, specifically -4 to 0, more specifically -1.5 to -0.5.

[0059] In another example, a glass substrate 10 is provided. The transparent conductive oxide layer material can be specified as indium doped tin oxide ("ITO"). It is understood that the ITO transparent conductive oxide film should have a thickness of 125 nm to 275 nm and should achieve a sheet resistance of 5 Ω / □ to 25 Ω / □, specifically 20 Ω / □ or less, more specifically 18 Ω / □ or less. To achieve the desired color, the underlayer 12 can be selected having a first underlayer film 20 including zinc oxide and tin oxide and a second underlayer film 22 including silica, and further considering the effect of the protective layer 16 on the color of the coated substrate. In this example, a protective layer of silica having a thickness of at least 30 nm and not more than 45 nm is used. The first underlayer film 20 should have a thickness of 10 nm to 15 nm, and the second underlayer film 22 should have a thickness of 29 nm to 34 nm. A first underlayer film 20 is deposited on the substrate 10 at a specified thickness, and a second underlayer film 22 is deposited on the substrate 10 at a specified thickness. A transparent conductive oxide layer 14 is deposited on the substrate 10 at a specified thickness that provides the sheet resistance discussed above, thus forming a coated substrate having a color with an a* of -9 to 1, or -4 to 0, or -3 to 1, or -1.5 to -0.5, and a b* of -9 to 1, or -4 to 0, or -3 to 1, or -1.5 to -0.5.

[0060] In these instances, the underlayer is used to adjust the color of the coated substrate.

[0061] FIG. 2 shows another exemplary article 2 including a substrate 10, an underlayer 12 over the substrate, a transparent conductive oxide layer 14 over the underlayer 12, and an embedded film 24 including a second high refractive index material embedded within the transparent conductive oxide layer 14.

[0062] The substrate 10 can be any of the substrates discussed herein.

[0063] The underlayer 12 can have a first underlayer film 20 and an optional second underlayer film 22. The first underlayer film 20 has a first high refractive index material. The optional second underlayer film 22 has a first low refractive index material. The first high refractive index material has a higher refractive index than the first lower refractive index material.

[0064] The transparent conductive oxide layer 14 can be any of the transparent conductive oxides discussed above.

[0065] The buried film 24 has a second high refractive index material embedded within the transparent conductive oxide layer 14. The second high refractive index material can be any material having a higher refractive index than the first low refractive index material. For example, the second high refractive index material forming the buried film 24 can include a metal oxide, nitride, or oxynitride. Examples of suitable oxide materials for the buried film 24 include oxides of silicon, titanium, aluminum, zirconium, phosphorus, hafnium, niobium, zinc, bismuth, lead, indium, tin, and / or alloys and / or mixtures thereof. For example, the buried film 24 can include oxides of silicon and / or aluminum.

[0066] For example, embedded film 24 may include oxides of silicon and aluminum. According to this example, second underlayer film 22 should have at least 50% by volume silica, 50-99% by volume silica and 50-1% by volume alumina, 60-98% by volume silica and 40-2% by volume alumina, 70-95% by volume silica and 30-5% by volume alumina, 80-90% by weight silica and 10-20% by weight alumina, or 8% by weight silica and 15% by weight alumina.

[0067] The buried film 24 may have a thickness in the range of 5 nm to 50 nm, 10 to 40 nm, or 15 to 30 nm.

[0068] The article may optionally include a protective layer 16, such as a protective layer described herein, over the transparent conductive oxide layer 14. For example, the protective layer 16 may include a first protective film 60 and a second protective film 62. The second protective film 62 may include a mixture of titania and silica. For example, the protective layer 16 may include a first protective film 60, a second protective film 62, and a third protective film 64.

[0069] 3 shows another exemplary article 2 including a substrate 10, an underlayer 12 on the substrate, a first transparent conductive oxide layer 114 on the underlayer 12, and an embedded film 124 on the first transparent conductive oxide layer 114. Located on top of the embedded film 124 is a second transparent conductive oxide layer 115. Optionally, a protective layer 16 can be deposited on top of the second transparent conductive oxide layer 115.

[0070] The buried film 124 may include a metal oxide, nitride, or oxynitride. Examples of suitable materials for the second high refractive index metal include oxides of silicon, titanium, aluminum, zirconium, phosphorus, hafnium, niobium, zinc, bismuth, lead, indium, tin, and / or alloys and / or mixtures thereof. For example, the second high refractive index material may include silica and / or alumina.

[0071] For example, the embedded film 124 may include silica and alumina. The second high refractive index material should have at least 50% by volume silica, 50-99% by volume silica and 50-1% by volume alumina, 60-98% by volume silica and 40-2% by volume alumina, or 70-95% by volume silica and 30-5% by volume alumina, 80-90% by weight silica and 10-20% by weight alumina, or 8% by weight silica and 15% by weight alumina.

[0072] The buried film 124 may have a thickness in the range of 5 nm to 50 nm, 10 to 40 nm, or 15 to 30 nm.

[0073] The first transparent conductive oxide layer 114 and the second transparent conductive oxide layer 115 have a total thickness in a range of 75 nm to 950 nm, such as 90 nm to 800 nm, such as 125 nm to 700 nm. For example, the total thickness can be 950 nm, 800 nm, 700 nm, 600 nm, 500 nm, 400 nm, 350 nm, 300 nm, 275 nm, 250 nm, or 225 nm or less. The total thickness can be at least 75 nm, at least 90 nm, at least 100 nm, at least 125 nm, 150 nm, or 175 nm. The first transparent conductive oxide layer 114 can have a thickness of at least 10 nm, at least 25 nm, 50 nm, 75 nm, or 100 nm, and at most 650 nm, 550 nm, 475 nm, 350 nm, 250 nm, or 150. The second transparent conductive oxide layer 115 can have a thickness of at least 10 nm, at least 25 nm, 50 nm, 75 nm, or 100 nm, and at most 650 nm, 550 nm, 475 nm, 350 nm, 250 nm, or 150. For example, when the first transparent conductive oxide layer 114 and the second transparent conductive oxide layer 115 include ITO, the first transparent conductive oxide layer 114 can have a thickness of at least 25 nm, 50 nm, 75 nm, or 100 nm, and at most 200 nm, 175 nm, 150 nm, or 125 nm, and the second transparent conductive oxide layer 115 can have a thickness of at least 25 nm, 50 nm, 75 nm, or 100 nm, and at most 200 nm, 175 nm, 150 nm, or 125 nm. In another example, when the transparent conductive oxide layer 114 and the second transparent conductive oxide layer 115 include AZO, the first transparent conductive oxide layer 114 can have a thickness of at least 100 nm, at least 150 nm, at least 200 nm, 250 nm, or 300 nm, and at most 650 nm, 550 nm, at most 450 nm, at most 325 nm, or at most 200 nm, and the second transparent conductive oxide layer 115 can have a thickness of at least 100 nm, at least 150 nm, at least 200 nm, 250 nm, or 300 nm, and at most 650 nm, 550 nm, at most 450 nm, at most 325 nm, or at most 200 nm.In another example, when the transparent conductive oxide layer 114 and the second transparent conductive oxide layer 115 comprise GZO, the first transparent conductive oxide layer 114 can have a thickness of at least 30 nm, at least 60 nm, at least 75 nm, at least 90 nm, at least 100 nm, at least 125 nm, at least 150 nm, 200 nm, or 300 nm, and at most 350 nm, at most 300 nm, 275 nm, at most 250 nm, or at most 225 nm, and the second transparent conductive oxide layer 115 can have a thickness of at least 30 nm, at least 60 nm, at least 75 nm, at least 90 nm, at least 100 nm, at least 125 nm, at least 150 nm, 200 nm, or 300 nm, and at most 350 nm, at most 300 nm, 275 nm, at most 250 nm, or at most 225 nm.

[0074] By varying the thickness of the first transparent conductive oxide layer 114 and the second transparent conductive oxide layer 115, the buried film 124 is moved to a higher position in the transparent conductive oxide layer 14 or to a lower position in the transparent conductive oxide layer 14. Surprisingly, regardless of where the buried film 24, 124 is positioned in the coating stack, the sheet resistance increases significantly (see FIG. 13a). Even more surprisingly, the position of the buried film 24, 124 in the transparent conductive oxide layer 14 has a different effect on the light transmittance (see FIG. 13b). When the first transparent conductive oxide layer 114 is thinner than the second transparent conductive oxide layer 115, thereby the buried film 124 is positioned lower in the transparent conductive oxide layer 14, the light transmittance increases (see FIG. 13b). This increase is more pronounced when the first transparent conductive oxide layer 114 is thicker than the second transparent conductive oxide layer 115, whereby the buried film 124 is positioned higher within the transparent conductive oxide layer 14 (see FIG. 13b). However, when the thickness of the first transparent conductive oxide layer 114 is approximately equal to the thickness of the second transparent conductive oxide layer 115, whereby the buried film 124 is positioned approximately in the center of the transparent conductive oxide layer 14, the transmittance decreases (see FIG. 13b). For example, the second transparent conductive oxide film 115 can be at least 25%, at least 50%, at least 75%, at least 100% (i.e., at least twice as thick), at least 125%, or at least 150% thicker than the first transparent conductive oxide film 114, and can be at most 250% thicker, at most 200% thicker, at most 150% thicker, at most 125% thicker, at most 100% (i.e., at most twice as thick), at most 75% thicker, at most 50% thicker, or at most 25% thicker than the first transparent conductive oxide film 114.Alternatively, the second transparent conductive oxide film 115 can be at least 25%, at least 50%, at least 75%, at least 100% (i.e., at least twice), at least 125%, or at least 150% thinner than the first transparent conductive oxide film 114, and can be at most 250% thinner, at most 200% thinner, at most 150% thinner, at most 125% thinner, at most 100% (i.e., at most twice) thinner, at most 75% thinner, at most 50% thinner, or at most 25% thinner than the first transparent conductive oxide film 114.

[0075] Another example of the invention is a method of making a coated article 2. A substrate 10 is provided. A first underlayer film 20 having a first high refractive index material is deposited on at least a portion of the substrate 10. A second underlayer film 22 having a first low refractive index material is deposited on at least a portion of the first underlayer film 20, the first lower refractive index material having a lower refractive index than the first high refractive index film. A first transparent conductive oxide film 114 is deposited on at least a portion of the underlayer 12. A buried film 124 having a second high refractive index material is deposited on at least a portion of the first transparent conductive oxide film 114, the second high refractive index material having a refractive index greater than the first low refractive index material, or having a refractive index within 10% or 5% of the refractive index of the first high refractive index material, or being the same material as the first high refractive index material, or having the same refractive index as the first high refractive index material. A second transparent conductive oxide film 115 is deposited on at least a portion of the buried film 124. The second high refractive index film divides the transparent conductive oxide film into two portions: a first transparent conductive oxide film and a second transparent conductive oxide film.

[0076] The embedded film 124 also allows for tuning of the color for the coated substrate. The color can have an a* of at least -9, -4, -3, or -1.5, and at most 1, 0, or -0.5, and a b* of at least -9, -4, -3, or -1.5, and at most 1, 0, or -0.5.

[0077] By varying the thickness of the two high and low refractive index materials, the color of the coated substrate can be adjusted. For this purpose, the material used in the transparent conductive oxide films 114 and 115 should first be identified. After the material is identified, the desired sheet resistance is identified. By knowing the material and the sheet resistance, the thickness of the transparent conductive oxide layer 14, or the total thickness of the first transparent conductive oxide film 114 and the second transparent conductive oxide film 115, can be determined. The transparent conductive oxide layer 14 affects the color of the coated substrate. To counteract this color effect, an optical design tool (e.g., FILM STAR) can be used to specify the thicknesses for the first and second underlayer films 20 and 22, as well as the thicknesses of the buried films 24, 124. This is done by inputting the thickness of the transparent conductive oxide layer 14 into the software and specifying the first high refractive index material, the second high refractive index material, and the first lower refractive index material. With these parameters, the thicknesses of the first and second underlayer films 20 and 24, as well as the buried films 24, 124 can be determined. These films are then deposited to their specified thickness.

[0078] For example, the method can include identifying a first transparent conductive oxide material for use in the first transparent conductive oxide film 114 and a second transparent conductive oxide material for use in the second transparent conductive oxide film 115. These transparent conductive oxides can be GZO, AZO, IZO, MZO, or ITO.

[0079] The thickness for the transparent conductive oxide layer 14 can be specified by first specifying the desired sheet resistance. After the sheet resistance is specified, the total thickness of both transparent conductive oxide films 114, 115 can then be specified. The sheet resistance can be at least 8 Ω / □, at least 10 Ω / □, or at least 12 Ω / □, and can be at most 25 Ω / □, at most 20 Ω / □, or at most 18 Ω / □. To achieve these values, the total transparent conductive oxide layer 14 thickness can be at least 75 nm, at least 90 nm, at least 100 nm, at least 175 nm, at least 180 nm, at least 190 nm, at least 200 nm, at least 205 nm, at least 225 nm, or at least 360 nm. Because the transparent conductive oxide layer 14 affects the color of the coated substrate, it is important to minimize the total thickness of the transparent conductive oxide films 114, 115. For this purpose, the total thickness of the transparent conductive oxide films 114, 115 can be at most 800 nm, at most 700 nm, at most 360 nm, at least 350 nm, at most 300 nm, at most 275 nm, at most 250 nm, at most 225 nm, at most 205 nm, at most 200 nm, at most 190 nm, at most 180 nm, or at most 175 nm.

[0080] It is also possible to determine the location of the buried film 24, 124 in the transparent conductive oxide, taking into account whether it is desired to increase or decrease the transmittance (see FIG. 13(b)). The first transparent conductive oxide film 114 can be thicker, thinner, or about the same thickness as the second conductive oxide film 115.

[0081] A first high refractive index material is specified for the first underlayer film 20, a first low refractive index material for the second underlayer film 22, and a second high refractive index material for the buried film 24, 124. Optionally, the protective layer 16 can be specified with a specified thickness for each protective layer film 60, 62, and / or 64. The desired color is specified. These parameters are input into an optical design tool, such as FILM STAR, and thicknesses are specified for the first and underlayer films 20 and 22 and the buried film 124.

[0082] The coating stack, including the underlayer 12, the transparent conductive oxide layer 14, the buried films 24, 124, and the optional protective layer 16, is deposited on the substrate at a specified thickness. The thicknesses of the underlayer films 20, 22 and the buried films 24, 124 adjust the color of the article 2 to a desired color.

[0083] 4a and 4b show another exemplary article 2 including a substrate 10, an underlayer 12 on the substrate 10, a transparent conductive oxide layer 14 on the underlayer 12, and a protective layer 16 on the transparent conductive oxide layer 14. The substrate 10, the underlayer 12, and the transparent conductive oxide layer 14 can be any of the substrates or underlayers discussed herein. The transparent conductive oxide layer 14 can be separated by buried layers 24, 124 discussed herein.

[0084] The protective layer 16 overlies, or optionally is in direct contact with, the transparent conductive oxide layer 14. The protective layer 16 can include at least two protective films 60, 62 or at least three protective films 60, 62, 64.

[0085] 4a shows an example of an article in which the protective layer has two protective films 60, 62. The first protective film 60 is positioned above the transparent conductive oxide layer 14 and is closer to the transparent conductive oxide layer 14 than the second protective film 62. The second protective film 62 is the outermost film in the coating 18 on the coated article.

[0086] The first protective coating 60 can include alumina, silica, titania, zirconia, tin oxide, or a mixture thereof. For example, the first protective coating can include a mixture of silica and alumina. In another example, the first protective coating 60 can include zinc stannate. In another example, the first protective coating 60 can include zirconia.

[0087] The second protective coating 62 comprises a mixture of titania and alumina. The second protective coating 62 is the final coating in the coating 18 deposited on the substrate 10.

[0088] The second protective film 62 contains 40 to 60 weight percent alumina and 60 to 40 weight percent titania, 45 to 55 weight percent alumina and 55 to 45 weight percent titania, 48 to 52 weight percent alumina and 52 to 48 weight percent titania, 49 to 51 weight percent alumina and 51 to 49 weight percent titania, or 50 weight percent alumina and 50 weight percent titania.

[0089] As shown in FIG. 4b, the protective layer 16 may further include a third protective coating 64 positioned between the first protective coating 60 and the second protective coating 62. The third protective coating 64 may include alumina, silica, titania, zirconia, tin oxide, or a mixture thereof. For example, the third protective coating 64 may include a mixture of silica and alumina. In another example, the third protective coating 64 includes zinc stannate. In another example, the third protective coating 64 includes zirconia.

[0090] Another exemplary article including a substrate 10, a functional coating 112, and a protective layer 16 is shown in Figures 5a and 5b. The substrate in this method can be glass, plastic, or metal.

[0091] The functional coating 112 can be any functional coating. For example, the functional coating 112 can include multiple dielectric films or multiple metal films. The functional coating can include an underlayer 12 as described herein, and / or a transparent conductive oxide layer 14 as described herein. The protective layer 16 can be a first protective film 60 and a second protective film 62 as described herein. In this example, the second protective film 62 is the outermost film and includes alumina and titania.

[0092] The protective layer can have a total thickness of at least 20 nm, 40 nm, 60 nm, or 80 nm, 100 nm, or 120 nm, and at most 275 nm, 255 nm, 240 nm, 170 nm, 150 nm, 125 nm, or 100 nm. The first protective film can have a thickness of at least 10 nm, at least 15 nm, at least 27 nm, at least 35 nm, at least 40 nm, at least 54 nm, at least 72 nm, and at most 85 nm, 70 nm, 60 nm, 50 nm, 45 nm, 30 nm. The second protective film can have a thickness of at least 10 nm, at least 15 nm, at least 27 nm, at least 35 nm, at least 40 nm, at least 54 nm, at least 72 nm, and at most 85 nm, 70 nm, 60 nm, 50 nm, 45 nm, 30 nm. The optional third protective film can have a thickness of at least 10 nm, at least 15 nm, at least 27 nm, at least 35 nm, at least 40 nm, at least 54 nm, at least 72 nm, and at most 85 nm, 70 nm, 60 nm, 50 nm, 45 nm, 30 nm. For example, the protective layer can have a thickness as listed in Table 1 below. In one embodiment, the first protective film has a thickness of at least 20 nm or at least 30 nm, and at most 60 nm or at most 50 nm. The second protective film has a thickness of at least 15 nm or at least 20 nm, and at most 50 nm or at most 40 nm. The optional third protective layer has a thickness of at least 5 nm or at least 10 nm, and at most 30 nm or at most 20 nm. The optional third protective layer can be positioned between the first protective film and the functional layer or between the first protective film and the second protective film. [Table 1]

[0093] The functional coating 112 may be a single film functional coating or may be a multi-film functional coating that includes one or more dielectric layers and / or one or more infrared reflective layers.

[0094] The functional coating 112 can be, for example, a solar control coating. The term "solar control coating" refers to a coating comprised of one or more layers or films that affect the solar properties of a coated article, such as, but not limited to, the amount of solar radiation, e.g., the amount of visible, infrared, or ultraviolet radiation reflected from, absorbed by, or transmitted through the coated article, the shading coefficient, the emissivity, etc. A solar control coating can block, absorb, or filter selected portions of the solar radiation spectrum, such as, but not limited to, the IR, UV, and / or visible spectrum.

[0095] The functional coating 112 may include, for example, one or more dielectric films. The dielectric film may include anti-reflective materials, including, but not limited to, metal oxides, oxides of metal alloys, nitrides, oxynitrides, or mixtures thereof. The dielectric film may be transparent to visible light. Examples of suitable metal oxides for the dielectric film include oxides of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, and mixtures thereof. These metal oxides may have small amounts of other materials, such as manganese in bismuth oxide, tin in indium oxide, etc. In addition, oxides of metal alloys or mixtures of metals may be used, such as oxides containing zinc and tin (e.g., zinc stannate, as defined below), indium-tin alloys, silicon nitride, silicon aluminum nitride, or oxides of aluminum nitride. Furthermore, doped metal oxides may be used, such as tin oxide doped with antimony or indium, or silicon oxide doped with nickel or boron. The dielectric film may be a substantially single phase film such as a metal alloy oxide film, for example zinc stannate, or may be a mixture of phases composed of zinc and tin oxide, or may be composed of multiple films.

[0096] The functional coating 112 may include a radiation-reflective coating. The radiation-reflective coating may include a reflective metal such as, but not limited to, metallic gold, copper, palladium, aluminum, silver, or mixtures thereof. In one embodiment, the radiation-reflective coating includes a metallic silver layer.

[0097] In one embodiment, the functional coating includes a first dielectric layer 120 on the substrate 10, a second dielectric layer 122 on the first dielectric layer 120, and a metal layer 126 located between the first and second dielectric layers 120 (see FIG. 7a) or on the second dielectric layer 122 (see FIG. 6a). The protective coating 16 is positioned on the metal layer 126 (see FIG. 6b). Optionally, a primer 128 can be applied between the metal film and the first dielectric layer (see FIG. 6c) or the second dielectric layer (see FIG. 6d).

[0098] The dielectric films 120 and 122 may be transparent to visible light. Examples of suitable metal oxides for the dielectric films 120 and 122 include oxides of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, and mixtures thereof. These metal oxides may have small amounts of other materials, such as manganese in bismuth oxide, tin in indium oxide, and the like. In addition, oxides of metal alloys or mixtures of metals may be used, such as oxides containing zinc and tin (e.g., zinc stannate as defined above), indium-tin alloys, silicon nitride, silicon aluminum nitride, or oxides of aluminum nitride. Furthermore, doped metal oxides may be used, such as tin oxide doped with antimony or indium, or silicon oxide doped with nickel or boron. The dielectric films 120 and 122 may be substantially single-phase films, such as metal alloy oxide films, e.g., zinc stannate, or may be mixtures of phases composed of zinc and tin oxide. The dielectric films 120 and 122 may have a total thickness in the range of 100 Å to 600 Å, such as 200 Å to 500 Å, such as 250 Å to 350 Å.

[0099] The metal film 126 may be selected from the group consisting of metallic gold, copper, palladium, aluminum, silver, and alloys thereof. For example, the metal film 126 may be silver.

[0100] The optional primer 128 can be a single film or multiple films. For example, the primer 128 can include an oxygen scavenging material that can be sacrificed during the deposition process to prevent degradation or oxidation of the metal film 126 during the sputtering process or subsequent heating processes. The primer 128 can also absorb at least a portion of the electromagnetic radiation, such as visible light, that passes through the coating. Examples of materials useful as the primer 128 include titanium, silicon, silicon dioxide, silicon nitride, silicon oxynitride, nickel-chromium alloys (such as Inconel), zirconium, aluminum, alloys of silicon and aluminum, alloys containing cobalt and chromium (e.g., Stellite®), and mixtures thereof. For example, the primer 148 can be titanium.

[0101] The protective layer 16 may include a first protective film 60 and a second protective film 62, or a first protective film 60 (see Figures 5a and 6a to 6d), a second protective film 62, and a third protective film 64 (Figures 5b and 6e to 6h).

[0102] In a method of making a coated article, an underlayer 12 is applied over a substrate 10, and a transparent conductive oxide layer 14 is applied over the underlayer 12. An undercoat 12 can be applied over the substrate 10, a transparent conductive oxide layer 14 can be applied over at least a portion of the underlayer 12, or a substrate 10 can be provided having an undercoat 12 and a transparent conductive oxide layer 14. A protective layer 16 is applied over at least a portion of the transparent conductive oxide. The protective layer 16 is applied by first applying a first protective film 60 over the transparent conductive oxide, and then applying a second protective film 62 over the first protective film 60. Optionally, a third protective film 64 can be applied over the first protective film 60, and a second protective film 62 can be applied over the third protective film 64.

[0103] In a method of making a coated article, a functional coating 112 is applied over a substrate 10. The functional coating 112 can be applied over the substrate 10, or a substrate can be provided having the functional coating 112. A protective layer 16 is applied over the functional coating 112. The protective layer 16 is applied by first applying a first protective film 60 over the transparent conductive oxide, and then applying a second protective film 62 over the first protective film 60. Optionally, a third protective film 64 can be applied over the first protective film 60, and the second protective film 62 can be applied over the third protective film 64.

[0104] Another exemplary method of the present invention is a method of increasing the sheet resistance of a coated article. A coated article is provided. The coated article has a substrate and a transparent conductive oxide layer on at least a portion of the substrate. The coated article is treated with a post-deposition process.

[0105] The post-deposition process can be tempering the coated article, flash annealing only one surface of the transparent conductive oxide layer, or passing an eddy current through the transparent conductive oxide layer.

[0106] Tempering the coated article is accomplished by heating the entire article such that the surface of the transparent conductive oxide layer reaches greater than 193.3°C (380°F), at least 223.9°C (435°F), or at least 335°C (635°F) for at least 5, 10, 15, 20, 25, or 30 seconds, and at most 120, 90, 60, 55, 50, 45, 40, 35, or 30 seconds. The transparent conductive oxide layer should not be heated above 335°C (635°F) or 430°C (806°F). After the coated article is heated, it is rapidly cooled to room temperature at a specific rate.

[0107] The coated article may be flash annealed to increase the sheet resistance. This is done by heating one surface of the coated article using a flash lamp. The surface that is heated is the surface on which the transparent conductive oxide layer is located. The surface is heated to a temperature of greater than 193.3°C (380°F), at least 223.9°C (435°F), or at least 335°C (635°F) for at least 5, 10, 15, 20, 25, or 30 seconds, and at most 120, 90, 60, 50, 55, 45, 40, 35, or 30 seconds. The surface should be heated to no more than 520°C (968°F), no more than 470°C (878°F), no more than 430°C (806°F), or no more than 335°C (635°F). After the surface is heated, it is cooled to room temperature.

[0108] Passing eddy currents through a transparent conductive oxide ("TCO") can be accomplished by exposing the transparent conductive oxide layer to a changing magnetic field. For example, a magnetic field can be applied over a substrate coated with a TCO. The TCO faces the magnetic field. Eddy currents are passed through the transparent conductive oxide layer.

[0109] Another exemplary method is a method of reducing the sheet resistance of a coated article. A substrate is provided. The substrate of this method can be glass, plastic, or metal. Optionally, the substrate is coated with an underlayer. The underlayer can include one film, two films, or more. The substrate is coated with a transparent conductive oxide by depositing the transparent conductive oxide on at least a portion of the substrate or the underlayer. Optionally, a buried film is deposited within the transparent conductive oxide layer. This optional step is performed by depositing a first portion of a transparent conductive oxide layer, depositing a buried layer on at least a portion of the first portion of the transparent conductive oxide layer, and depositing a second portion of the transparent conductive oxide layer on at least a portion of the buried layer. The coated article is treated by one of the post-deposition processes described above.

[0110] Optionally, the method can further include depositing a protective layer as described herein on at least a portion of the transparent conductive oxide layer. The protective layer can have two protective films or three protective films.

[0111] By treating the article with a post-deposition process, the sheet resistance of the article is reduced to less than 25 ohms / square, less than 20 ohms / square, less than 18 ohms / square, less than 16 ohms / square, or less than 15 ohms / square. This is particularly useful for reducing the thickness of the TCO. For example, AZO can have a thickness of less than 400nm or 320nm and greater than 160nm. AZO should have a thickness of less than 344nm and greater than 172nm. ITO should have a thickness of less than 275nm or 175nm and greater than 95nm.

[0112] One illustrative example is a method of making a coated glass article, in which a glass substrate is provided. An undercoat is applied onto the glass substrate, preferably by a magnetron sputtering vacuum deposition process, or any other process that does not use radiant heat, or an undercoat is applied onto the substrate at room temperature. Preferably, the undercoat comprises two films, a first film comprising zinc oxide and tin oxide, and a second film comprising silica and titania. A transparent conductive oxide is applied onto the undercoat, preferably by a magnetron sputtering vacuum deposition process, or any other process that does not use radiant heat, or a transparent conductive oxide is applied onto the undercoat at room temperature. Preferably, the transparent conductive oxide is indium oxide doped with tin. An optional protective layer is applied onto the transparent conductive oxide, preferably by a magnetron sputtering vacuum deposition process, or any other process that does not use radiant heat, or an optional protective layer is applied onto the transparent conductive oxide at room temperature. The absorptivity of the transparent conductive oxide is less than or equal to 0.2 and / or at least as high as 0.05.

[0113] In one exemplary embodiment, the article is a refrigerator door. The refrigerator door should be treated with a post-deposition process at some point before assembly, but should be properly treated after the metal for the exterior of the door is coated. Typically, the refrigerator door is heated, allowing the coated article to bend into a shape that properly fits the door. This heating process should crystallize the transparent conductive oxide and reduce the sheet resistance.

[0114] Those skilled in the art will readily appreciate that modifications may be made to the present invention without departing from the concepts disclosed in the above description. Accordingly, the specific embodiments detailed herein are for illustrative purposes only and are not intended to limit the scope of the present invention, which is to be accorded the full breadth of the appended claims and any equivalents thereof.

[0115] Example 1 (010761) A glass substrate was coated with an underlayer and a transparent conductive oxide layer. The underlayer had a first underlayer film and a second underlayer film. The first underlayer film was zinc stannate on the glass substrate, and the second underlayer film was a silica-alumina alloy on the first underlayer film, having about 85 weight percent silica and 15 weight percent alumina. The transparent conductive oxide layer on the second underlayer film was tin-doped indium oxide ("ITO").

[0116] To improve the conductivity of the coated article, the entire article was placed in an oven and the temperature of the transparent conductive oxide layer was measured (see Figures 7a and 7b).

[0117] The following samples were tested to establish the improved conductivity for each thickness of ITO. [Table 2]

[0118] As can be seen in Figures 7a and 7b, post-deposition heating of ITO reduced the sheet resistance from about 55-70 Ω / □ to about 10-25 Ω / □, regardless of thickness. When the ITO thickness was at least 96.8 nm, the sheet resistance was less than 25 Ω / □, regardless of heating temperature. When the ITO thickness was at least 109.2, the sheet resistance was less than 20 Ω / □ when the ITO surface reached 520°C (968°F). When about 127.9 nm, ITO had a sheet resistance of less than 20 Ω / □ when heated to any temperature. The improvement in sheet resistance was unexpected. Similar results were obtained with other transparent conductive oxides, which suggests that regardless of the transparent conductive oxide, the temperature should be greater than 193.3°C (380°F), at least 223.9°C (435°F), or no greater than 430°C (806°F).

[0119] Post-deposition heating increased the crystallinity of the ITO layer, as shown in Figures 8a-8c. The samples tested are listed in Table 3 below. [Table 3]

[0120] By focusing on the minimum surface temperature required to enhance ITO crystal formation, large gains in energy savings are realized.

[0121] Example 2 A glass substrate was coated with a transparent conductive oxide layer. The transparent conductive oxide was zinc oxide doped with gallium ("GZO"). Several samples with different GZO thicknesses were prepared and the sheet resistance for the samples was measured to compare the effect of post-deposition treatment on the sheet resistance of the as-deposited GZO. The post-deposition process was to place the coated article in a furnace. The sheet resistance of each sample was tested before and after flash annealing and the results are shown in Figure 9. The thickness and sheet resistance for the tested samples are listed in Table 4 below. [Table 4]

[0122] As shown in Figure 9, post-deposition flash annealing of GZO improved the sheet resistance for all thicknesses tested. The improvement was most significant when the GZO was between approximately 320 and 480 nm thick. When the GZO layer was approximately 320 nm thick, the “as-deposited” GZO layer provided a sheet resistance of 35.6 Ω / □, whereas after thermal treatment the sheet resistance was 12.7 Ω / □. This is significant because at this thickness, flash annealing reduced the sheet resistance to an acceptable range, whereas without flash annealing the sheet resistance was unacceptably high.

[0123] Similar results were observed when the GZO was 480 nm thick: the sheet resistance of the “as-deposited” GZO sample was about 21.8 Ω / □, whereas the heat-treated sample was 7.8 Ω / □.

[0124] The difference in sheet resistance is reduced until the thickness of GZO becomes very large. For example, at about 950 nm, the “as-deposited” GZO sample had a sheet resistance of about 8 Ω / □, whereas the flash-annealed sample had a sheet resistance of about 5 Ω / □. In this case, both samples had sufficiently low sheet resistance.

[0125] Thus, as shown in FIG. 9, for samples with GZO as the transparent conductive oxide, the thickness that provides the largest and most significant difference in sheet resistance is when the GZO layer is at least 300 nm thick and at most 500 nm thick.

[0126] The heat treatment reduces the thickness of the transparent conductive oxide layer required to reach an acceptable sheet resistance. Without any post-deposition treatment, GZO would have to be deposited at least 550 nm before the sheet resistance would be less than 20 Ω / □. Heating allows a thinner GZO layer to be deposited. This not only reduces the cost of making a suitable coated article, but also reduces the effect of GZO on the optical properties and color of the coated article.

[0127] This was an unexpected discovery and provided a cost-effective approach to improving the sheet resistance of thinner transparent conductive oxide layers.

[0128] Example 3 A glass substrate was coated with a transparent conductive oxide layer of aluminum doped zinc oxide ("AZO"). Several samples with different AZO thicknesses were prepared and the sheet resistance for the samples was measured to compare the effect of post-deposition treatment on the sheet resistance of the as-deposited AZO. The post-deposition process involved placing the coated article in an oven. The sheet resistance of each sample was tested before and after flash annealing and the results are shown in Figure 10. The thicknesses and sheet resistances for the tested samples are listed in Table 5 below. [Table 5]

[0129] As shown in Figure 10, post-deposition heating of AZO improved the sheet resistance for all thicknesses tested. The improvement was most pronounced when the AZO was between about 344 and 860 nm thick. When the AZO layer was 344 nm thick, the "as-deposited" AZO layer provided a sheet resistance of about 78.3 Ω / □, whereas after heat treatment the sheet resistance was 19.5 Ω / □. This is significant because at this thickness, heating reduced the sheet resistance to an acceptable range whereas without heating the sheet resistance was unacceptably high.

[0130] Similar results were observed when the AZO was 860 nm thick: the sheet resistance of the "as-deposited" AZO sample was about 26.6 Ω / □, whereas the heat-treated sample was about 7.1 Ω / □.

[0131] The difference in sheet resistance is reduced until the thickness of AZO becomes very large. For example, at about 1050 nm, the "as-deposited" AZO sample had a sheet resistance of about 17.0 Ω / □, whereas the heat-treated sample had a sheet resistance of 3.9 Ω / □. In this case, both samples had sufficiently low sheet resistance.

[0132] Thus, as shown in FIG. 10, for samples having AZO as the transparent conductive oxide, the thickness that provides the largest and most significant difference in sheet resistance is when the AZO layer is at least 344 nm thick and at most 860 nm thick.

[0133] Heating also reduces the thickness of the transparent conductive oxide layer required to reach an acceptable sheet resistance. Without any post-deposition treatment, AZO would have to be deposited to at least 1032 nm before the sheet resistance would be less than 20 Ω / □. Heating allows a thinner AZO layer to be deposited. This not only reduces the cost of making a suitable coated article, but also reduces the impact of AZO on the optical properties and color of the coated article.

[0134] This was an unexpected discovery and provided a cost-effective approach to improving the sheet resistance of thinner transparent conductive oxide layers.

[0135] Example 4 Using the FILM STAR, various underlayer thicknesses were tested to determine which thicknesses provided acceptable or neutral colors. A glass substrate with an underlayer and a transparent conductive oxide was used. The underlayer had a first film and a second film. The first underlayer film was zinc stannate on the glass substrate, and the second underlayer film was a silica-alumina alloy on the first underlayer film, with about 85 weight percent silica and 15 weight percent alumina. The transparent conductive oxide layer on the second underlayer film was a 170 nm thick tin-doped indium oxide ("ITO") layer.

[0136] First, the desired sheet resistance was determined. In this example, the desired sheet resistance was about 10 Ω / □ to 15 Ω / □. To achieve this sheet resistance, it was determined that the transparent conductive oxide layer should be about 170 nm thick.

[0137] Using FILM STAR, the materials and thicknesses of the glass and transparent conductive oxide layers were entered. Then, the materials for the first and second underlayer films were determined. In this example, the first underlayer film material was zinc stannate and the second underlayer film material was a silica-alumina alloy with 85 weight percent silica and 15 weight percent alumina. The following coatings were analyzed by FILM STAR (see Table 6 and Figure 11). First, the thickness of the first underlayer in the samples ranged from 8 nm to 17 nm, and the thickness of the second underlayer film ranged from 27 nm to 35 nm. [Table 6]

[0138] As shown in Figure 11, when the first underlayer film was 13 nm thick and the second underlayer film was 31 nm thick, intermediate colors of a* and b* of -1 and -1 were obtained. When the first underlayer film was 11 nm to 15 nm thick and the second underlayer film was 29 nm to 33.5 nm thick, acceptable colors of a* of -3 to 1 and b* of -3 to 1 were obtained.

[0139] Example 5 Using FILM STAR, varying thicknesses of the transparent conductive oxide layer were tested to determine the appropriate thickness for the underlayer. In this example, the FILM STAR parameters included an underlayer-coated glass substrate with a first underlayer film and a second underlayer film. The first underlayer film was zinc stannate and the second underlayer film was silica. The transparent conductive oxide layer on top of the second underlayer film was indium oxide doped with tin ("ITO"). A protective layer of silica was located on top of the ITO layer. Table 7 and Figure 12 show the samples tested. Table 7 shows the values ​​entered into FILM STAR for the ITO layer and the SiO2 layer. The output provided thicknesses for the two underlayer films that should provide a color of -1, -1 (a*, b*). [Table 7]

[0140] These samples show that when the transparent conductive oxide layer is 175-225 nm thick and the protective coating is 30 nm thick, to achieve a color of about -1, -1(a*, b*), the first underlayer film should be at least 10 nm thick and at most 15 nm thick, and the second underlayer film should be at least 28 nm thick and at most 36 nm thick. These samples also show that when the transparent conductive oxide layer is 175-225 nm thick and the protective coating is 45 nm thick, to achieve a suitable color, the first underlayer film should be at least 11 nm thick and at most 14 nm thick, and the second underlayer film should be at least 32 nm thick and at most 38 nm thick.

[0141] Figure 12 shows the ideal thicknesses that result in a color of -1, -1. Although -1, -1 is preferred, other colors such as those circled in Figure 11 (i.e., -3 to 1 a*, and -3 to 1 b*) are acceptable.

[0142] Example 6 The effect of the buried film at various depths and thicknesses was tested and compared to a transparent conductive oxide layer without a buried layer. A glass substrate was coated with a bottom transparent conductive oxide film. The bottom transparent conductive oxide film was made of indium oxide doped with tin ("ITO") and was 120 nm, 180 nm, or 240 nm thick. A buried film was deposited on top of the bottom transparent conductive oxide layer. The buried film was 15 nm or 30 nm thick and was a zinc stannate film. A top transparent conductive oxide film was deposited on top of the buried film. The top transparent conductive oxide film was ITO and was 240 nm, 180 nm, or 120 nm thick. The total thickness of the bottom and top transparent conductive oxide films was 360 nm. For control, ITO oxide without a buried film was deposited on top of the substrate at a thickness of 360 nm. Sheet resistance and transmittance at 550 nm were measured for the samples. These samples are listed in Table 8 below and in FIG. 13. [Table 8]

[0143] As shown in FIG. 13a, experimental samples A-F had at least a 35% improvement in sheet resistance compared to control sample G. Samples A and B had at least a 40% improvement in sheet resistance compared to sample G. Samples C and D had at least a 35% improvement in sheet resistance compared to sample G. Samples E and F had at least a 37% improvement in sheet resistance compared to sample G.

[0144] Based on this data, the buried film, regardless of its location or thickness, unexpectedly significantly reduces the sheet resistance of the transparent conductive oxide layer.

[0145] As shown in FIG. 13b, samples E and F provided the greatest increase in transmittance. Samples A and B showed smaller improvements. Thus, by having a thickness difference between the top and bottom transparent conductive oxide layers, the amount of light transmission can be increased. Furthermore, it was an unexpected discovery that the transmittance is much increased when the top transparent conductive oxide layer is thinner than the bottom transparent conductive oxide layer, whereby the buried layer is positioned closer to the top surface of the transparent conductive oxide layer than the bottom of the transparent conductive oxide layer. In contrast, when the top and bottom transparent conductive oxide layers are approximately equal, the light transmittance is unexpectedly decreased.

[0146] Figure 13c shows that the embedded film also affects the crystallinity of the transparent conductive oxide. It can be seen from the XRD data that by having an embedded film, the crystallinity is unexpectedly improved.

[0147] Example 7 In this example, various protective layers were investigated. The protective layer was placed on a glass substrate. The coated article included a transparent conductive oxide of zinc oxide doped with aluminum between the substrate and the protective layer. It would not be expected that the underlayer, functional layer, or transparent conductive oxide layer would not affect the observed results.

[0148] The glass substrates were different protective layers. Samples 1 to 3 had protective layers containing a single film. A list of these samples is provided in Table 9. [Table 9]

[0149] Samples 5-11 had a protective layer including a first protective film and a second protective film on the first protective film. A list of these samples is provided in Table 10. The first film is closer to the substrate than the second film, and the second film is the outermost film. [Table 10]

[0150] Samples 12-15 had a protective layer that included three films. A list of these samples is provided in Table 11. The first film was closer to the substrate than the second or third films. For consistency with other figures and the above description, the second protective film was the outermost film, and the third protective film was positioned between the first and third films. [Table 11]

[0151] The durability of these samples was tested using the ASTM Cleveland Condensation test, and the overcoat with TiAlO as the outermost layer performed best, as shown in Figures 14 and 15. These figures show the dEcmc for Samples 1-15 listed in Tables 9-11.

[0152] Specifically, FIG. 14 shows that samples with two or three protective layers, with the outermost layer being TiAlO, had unexpectedly better durability, specifically, Sample 6 (SiAlO / TiAlO), Sample 7 (SnZn / TiAlO), and Sample 13 (SnZn / SiAlO / TiAlO). FIG. 15 further demonstrates that protective layers with titania and alumina as the outermost layers unexpectedly provided greater durability. In FIG. 15, Sample 19 (ZrO2 / SiAlO / TiAlO) and Sample 20 (SiAlO / ZrO2 / TiAlO) show unexpectedly better durability when compared to protective layer samples including the other three layers (Samples 16, 17, 18, and 21).

[0153] This data shows the unexpected result that the titania-alumina outermost protective coating provides significantly improved durability.

[0154] Example 8 Samples in which transparent conductive oxides were sputtered in various atmospheres were tested. Glass substrates were coated with indium doped tin oxide ("ITO") or aluminum doped zinc oxide ("AZO") via magnetron sputtering vacuum deposition ("MSVD") method as shown in Figures 16-20. ITO samples were sputtered in atmospheres containing 0%, 0.5%, 1%, 1.5%, or 2% oxygen and then heat treated, and AZO samples were sputtered in atmospheres containing 0%, 1%, 2%, 3%, 4%, 5%, or 6% oxygen and then heat treated. The remainder of the atmosphere was argon. ITO samples had ITO thicknesses of 225 nm, 175 nm, or 150 nm, and AZO samples had thicknesses of 300 nm to 350 nm of AZO deposited on the substrate. The samples were tested to determine emissivity, absorptivity, and / or sheet resistance (emissivity is a measure of conductivity). The samples were heat treated by placing the coated article in an oven for a period of time such that the transparent conductive oxide surface of the sample reached at least 223.9°C (435°F) in about 30 seconds.

[0155] When a transparent article is coated with a transparent conductive oxide, an article with low absorptivity and low sheet resistance (corresponding to emissivity) is desired. Figure 16 shows that as oxygen is added to the atmosphere, the absorptivity decreases. However, as shown in Figure 17, when the atmosphere has 0% oxygen, the article has the highest emissivity / sheet resistance. Using Figures 16 and 17, an ideal balance between absorptivity and emissivity is obtained when the sputtering atmosphere has 0.75% to 1.25% oxygen in the atmosphere. As shown in Figure 17, when the atmosphere has less than 2.0% oxygen, the sheet resistance of the heat-treated article coated with ITO is lower than the unheated article coated with ITO. When the atmosphere contains 1.5% oxygen, the sheet resistance increases significantly. Extrapolating from this data, it is concluded that the atmosphere in the coating chamber should have no more than 1.5% oxygen, preferably no more than 1.25% oxygen. To obtain a significant reduction in absorptivity for the ITO coated article, the atmosphere should contain at least 0.5% oxygen, preferably at least 0.75% oxygen.

[0156] Example 9 A glass substrate was coated with an aluminum-doped zinc oxide layer by a magnetron sputtering vacuum deposition ("MSVD") process. The target was a ceramic aluminum-doped zinc oxide containing a specific amount of oxygen. When the MSVD process is used to deposit materials such as transparent conductive oxides, the process dissociates the ceramic raw material and potentially allows some of the oxygen to escape. Oxygen is often supplied to the coating chamber along with an inert gas to ensure that the deposited material oxidizes. In this example, AZO was deposited in the coating chamber by MSVD, and the oxygen content supplied to the chamber was 0%, 1%, 2%, 3%, 4%, 5%, or 6%. The remainder of the atmosphere supplied to the coating chamber was argon, but any inert gas can be used. The normalized absorptance of the coating was determined. As shown in Figure 18, the normalized absorptance at 550 nm was best when 0% oxygen was supplied to the coating chamber. It was also acceptable when 1% oxygen was supplied to the coating chamber. Based on the data shown in FIG. 18, it can be estimated that less than 0.5% oxygen in the coating chamber provides significantly better absorption rates than when 1% oxygen is used.

[0157] As shown in Figure 19, the normalized absorptance has a steep decrease from 0% oxygen to 1% oxygen, and a minimal decrease from 1% oxygen to 2% oxygen. This data further supports the conclusion that, by estimation, less than 1% oxygen, less than 0.5% oxygen, or less than 0.25% oxygen, or less than 0.1% oxygen, or 0% oxygen provided to the coating chamber provides the best absorptance.

[0158] Example 10 One problem with post-deposition heating of coated articles is the amount of energy that is wasted. As discussed above, post-deposition heating of a transparent conductive oxide ("TCO") layer provides improved performance at smaller thicknesses. When the coated article is placed in an oven to heat the entire article, energy is wasted above the temperature required to crystallize the TCO layer. To determine the surface temperature required to improve the performance of the transparent conductive oxide layer, glass substrates were coated with either 115 nm or 171 nm of indium-doped tin oxide. The samples had the surface of the ITO layer heated to the temperatures listed in Tables 12 and 13. For the purposes of this experiment, the surface was heated by placing the entire coated article in an oven, although flash lamps could alternatively be used.

[0159] After post-deposition heating of the surface, the sheet resistance of each sample was measured (see FIG. 21 and Tables 12 and 13). The results show that the layer reaches its minimum sheet resistance at about 435°F. In addition, heating of the surface does not provide any additional sheet resistance reduction. Therefore, in order to reduce the sheet resistance of the transparent conductive oxide layer, the post-deposition heating should heat the surface of the transparent conductive oxide layer to more than 380°F, at least 435°F, between 435°F and 806°F, between 435°F and 635°F, or up to 435°F. [Table 12] [Table 13]

[0160] The invention is further described in the following numbered clauses.

[0161] Clause 1: A coated article comprising a substrate and an underlayer over the substrate, the underlayer comprising a first underlayer film comprising a high refractive index material, a second underlayer film over the first layer comprising a low refractive index material, and a transparent conductive oxide layer over the underlayer.

[0162] Clause 2: The coated article of claim 1, wherein the high refractive index material comprises zinc oxide and tin oxide.

[0163] Clause 3: The coated article of clause 1 or 2, wherein the low refractive index material comprises silica and alumina.

[0164] Clause 4: The coated article of any one of clauses 1 to 3, wherein the transparent conductive film comprises indium oxide doped with tin.

[0165] Clause 5: The coating of any one of clauses 1 to 4, wherein the transparent conductive oxide layer has a thickness of at least 75 nm, particularly at least 90 nm, more particularly at least 100 nm, more particularly at least 125 nm, more particularly at least 150 nm, or more particularly at least 175 nm.

[0166] Clause 6: The coated article of any one of clauses 1 to 5, wherein the transparent conductive oxide layer has a thickness of at most 350 nm, particularly at most 300 nm, particularly at most 275 nm, particularly at most 250 nm, and more particularly at most 225 nm.

[0167] Clause 7: The coated article of any one of clauses 1 to 6, wherein the coated article has a sheet resistance in the range of 5 to 25 ohms / square, specifically 5 to 20 ohms / square, more specifically 8 to 18 ohms / square, and even more specifically 5 to 15 ohms / square.

[0168] Clause 8: The coated article of any one of clauses 1 to 7, wherein the first underlayer film has a first underlayer thickness and the second underlayer film has a second underlayer thickness to provide the coated article with a color having an a* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1, and a b* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1.

[0169] Clause 9: The coated article of any one of clauses 1 to 8, wherein the high refractive index material comprises zinc oxide.

[0170] Clause 10: The coated article of any one of clauses 1 to 9, further comprising a protective layer on the transparent conductive oxide layer, the protective layer comprising a first protective film and a second protective film on at least a portion of the first protective film, the second protective film being the outermost film, and the second protective film comprising titania and alumina.

[0171] Clause 11: The coated article of clause 10, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0172] Clause 12. The coated article of clause 9 or 10, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, and more specifically 50 weight percent titania.

[0173] Clause 13: The coated article of any one of clauses 10 to 12, wherein the second protective coating comprises 65 to 35 weight percent alumina, specifically 55 to 45 weight percent alumina, and more specifically 50 weight percent alumina.

[0174] Clause 14: The coated article of any one of clauses 10 to 13, further comprising a third protective coating positioned over at least a portion of the first protective coating, between the first protective coating and the second protective coating or between the first protective coating and the functional coating, the third protective coating comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0175] Clause 15: A method of adjusting the color of a coated substrate, comprising the steps of: providing a substrate; identifying a transparent conductive oxide and a transparent conductive oxide layer thickness for a transparent conductive oxide layer that provides a sheet resistance of at least 5 Ω / □ and not more than 25 Ω / □ (particularly not more than 20 Ω / □, more particularly not more than 18 Ω / □); and providing a transparent conductive oxide and a transparent conductive oxide layer thickness for the coated substrate having the transparent conductive oxide of the transparent conductive layer thickness with an a* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5, and an a* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more specifically, identifying a first underlayer material and first underlayer thickness and a second underlayer material and second underlayer thickness for a first underlayer film that provides a color having a b* of -1.5 to -0.5; depositing the first underlayer film having the first underlayer thickness over at least a portion of a substrate; depositing a second underlayer film having a second underlayer thickness over at least a portion of the first underlayer film; and depositing a transparent conductive oxide layer of a transparent conductive oxide thickness over at least a portion of the underlayer.

[0176] Clause 16: The method of clause 15, wherein the transparent conductive oxide is indium oxide doped with tin.

[0177] Clause 17: The method of clause 15 or 16, wherein the transparent conductive layer thickness is at least 125 nm (particularly at least 150 nm, more particularly at least 175 nm) and not more than 950 nm (particularly 500 nm, more particularly 350 nm, more particularly 225 nm).

[0178] Clause 18: The method of any one of clauses 15 to 17, wherein the first underlayer material comprises zinc oxide and tin oxide.

[0179] Clause 19: The method of any one of clauses 15 to 18, wherein the first underlayer thickness is at least 11 nm and not more than 15 nm.

[0180] Clause 20. The method of any one of clauses 15 to 19, wherein the second underlayer material comprises silica and alumina.

[0181] Clause 21: The method of any one of clauses 15 to 20, wherein the second underlayer thickness is at least 29 nm and not more than 34 nm.

[0182] Clause 22: The method of any one of clauses 15 to 21, further comprising the step of depositing a protective layer over a portion of the transparent conductive oxide layer, the protective layer comprising a first protective film and a second protective film over at least a portion of the first protective film, the second protective film being an outermost film, and the second protective film comprising titania and alumina.

[0183] Clause 23. The method of clause 22, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0184] Clause 24. The method of clause 22 or 23, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, and more specifically 50 weight percent titania.

[0185] Clause 25. The method of any one of clauses 22 to 25, wherein the second protective coating comprises 65 to 35 weight percent alumina, specifically 55 to 45 weight percent alumina, and more specifically 50 weight percent alumina.

[0186] Clause 26. The method of any one of clauses 22 to 25, further comprising a third protective coating positioned over at least a portion of the first protective coating, between the first protective coating and the second protective coating or between the first protective coating and the functional coating, the third protective coating comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0187] Clause 27: A coated article comprising a substrate, an underlayer over at least a portion of the substrate, and a transparent conductive oxide layer over at least a portion of the underlayer. The underlayer has a first underlayer film and an optional second underlayer film. The first underlayer film comprises a first high refractive index material. The optional second underlayer film comprises a low refractive index material. The first high refractive index material has a higher refractive index than the low refractive index material. The transparent conductive oxide layer has an embedded film embedded within the transparent conductive oxide layer. The embedded film comprises a second high refractive index material. The second high refractive index material has a higher refractive index than the low refractive index material.

[0188] Clause 28: The coated article of clause 27, wherein the buried film has a thickness of 5 nm to 50 nm, particularly 10 nm to 40 nm, and more particularly 15 nm to 30 nm.

[0189] Clause 29: The coated article of clause 27 or 29, wherein the second high refractive index material comprises tin oxide and zinc oxide.

[0190] Clause 30: The coated article of any one of clauses 27 to 29, wherein the buried film is positioned closer to the top of the transparent conductive oxide layer.

[0191] Clause 31: The coated article of any one of clauses 27 to 29, wherein the buried film is positioned closer to the bottom of the transparent conductive oxide layer.

[0192] Clause 32: The coated article of any one of clauses 27 to 29, wherein the embedded film is positioned approximately in the center of the transparent conductive oxide layer.

[0193] Clause 33: The coated article of any one of clauses 27 to 32, wherein the transparent conductive oxide layer is selected from the group consisting of gallium-doped zinc oxide ("GZO"), aluminum-doped zinc oxide ("AZO"), indium-doped zinc oxide ("IZO"), magnesium-doped zinc oxide ("MZO"), or tin-doped indium oxide ("ITO"), particularly GZO, AZO, and ITO, more particularly ITO.

[0194] Clause 34: The coated article of any one of clauses 27 to 33, wherein the high refractive index material comprises zinc oxide and tin oxide.

[0195] Clause 35: A coated article described in any one of clauses 27 to 34, wherein the low refractive index material includes silica and alumina.

[0196] Clause 36: The coated article of any one of clauses 27 to 35, wherein the transparent conductive oxide layer has a thickness of at least 75 nm, more particularly at least 90 nm, more particularly at least 100 nm, more particularly at least 125 nm, more particularly at least 150 nm, more particularly at least 175 nm, or more particularly at least 320 nm.

[0197] Clause 37: A coated article described in any one of clauses 27 to 34, wherein the transparent conductive oxide layer has a thickness of at most 950 nm, particularly at most 550 nm, more particularly at most 480 nm, more particularly at most 350 nm, more particularly at most 300 nm, more particularly at most 275 nm, more particularly at most 250 nm, more particularly at most 225 nm.

[0198] Clause 38: The coated article of any one of clauses 27 to 37, wherein the coated article has a sheet resistance in the range of 5 to 20 ohms / square, particularly 8 to 18 ohms / square, and more particularly 5 to 15 ohms / square.

[0199] Clause 39: The coated article of any one of clauses 27 to 38, wherein the first underlayer film has a first underlayer thickness, the second underlayer film has a second underlayer thickness, and the embedded film has an embedded film thickness, so as to provide the coated article with a color having an a* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1, and a b* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1.

[0200] Clause 40. The coated article of clause 39, wherein the first underlayer thickness is from 11 nm to 15 nm and / or the second underlayer thickness is from 29 nm to 34 nm.

[0201] Clause 41: The coated article of any one of clauses 27 to 40, further comprising a protective layer on the transparent conductive oxide layer, the protective layer comprising a first protective film and a second protective film on at least a portion of the first protective film, the second protective film being the outermost film, and the second protective film comprising titania and alumina.

[0202] Clause 42. The coated article of clause 41, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0203] Clause 43: The coated article of clause 41 or 42, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, more specifically 50 weight percent titania.

[0204] Clause 44: The coated article of any one of clauses 40 to 43, wherein the second protective coating comprises 65 to 35 weight percent alumina, specifically 55 to 45 weight percent alumina, and more specifically 50 weight percent alumina.

[0205] Clause 45: The coated article of any one of clauses 40 to 44, further comprising a third protective coating positioned over at least a portion of the first protective coating, between the first protective coating and the second protective coating or between the first protective coating and the functional coating, the third protective coating comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0206] Clause 46: A method of adjusting the color of a coated article. The method includes depositing a first underlayer film over at least a portion of a substrate. The first underlayer film includes a first high refractive index material. Optionally, a second underlayer film including a low refractive index material is deposited over at least a portion of the first underlayer film. The first high refractive index material has a higher refractive index than the low refractive index material. A first transparent conductive oxide film is deposited over at least a portion of the first underlayer film or the optional second underlayer film. A buried film is deposited over at least a portion of the first transparent conductive oxide layer. The buried film includes a second high refractive index material. The second high refractive index material has a higher refractive index than the low refractive index material. A second transparent conductive oxide film is deposited over at least a portion of the buried film.

[0207] Clause 47: The method of clause 46, wherein the buried film has a thickness of 5 nm to 50 nm, particularly 10 nm to 40 nm, and more particularly 15 nm to 30 nm.

[0208] Clause 48: The method of clause 46 or 47, wherein the second high refractive index material comprises tin oxide and zinc oxide.

[0209] Clause 49: The method of any one of clauses 46 to 47, wherein the buried film is positioned closer to the top of the transparent conductive oxide layer.

[0210] Clause 50: The method of any one of clauses 46 to 47, wherein the buried film is positioned closer to the bottom of the transparent conductive oxide layer.

[0211] Clause 51: A method according to any one of clauses 46 to 47, wherein the embedding film is positioned approximately in the centre of the transparent conductive oxide layer.

[0212] Clause 52: The method of any one of clauses 46 to 51, wherein the first transparent conductive oxide film and / or the second transparent conductive oxide film are selected from the group consisting of gallium-doped zinc oxide ("GZO"), aluminum-doped zinc oxide ("AZO"), indium-doped zinc oxide ("IZO"), magnesium-doped zinc oxide ("MZO"), or tin-doped indium oxide ("ITO"), particularly GZO, AZO, and ITO, more particularly ITO.

[0213] Clause 53: The method of any one of clauses 46 to 52, wherein the high refractive index material comprises zinc oxide and tin oxide.

[0214] Clause 54: The method of any one of clauses 46 to 53, wherein the low refractive index material comprises silica and alumina.

[0215] Clause 55: The method of any one of clauses 46 to 55, wherein the first transparent conductive oxide layer and / or the second transparent conductive oxide layer has a thickness of at least 80 nm, or particularly at least 120 nm, more particularly at least 180 nm, more particularly at least 240 nm, or more particularly at least 360 nm.

[0216] Clause 56: The method of any one of clauses 46 to 55, wherein the first transparent conductive oxide layer and / or the second transparent conductive oxide layer has a thickness of at most 400 nm, particularly at most 360 nm, more particularly at most 240 nm, more particularly at most 180 nm, more particularly at most 120 nm, or more particularly at most 80 nm.

[0217] Clause 57: The method of any one of clauses 46 to 56, wherein the coated article has a sheet resistance in the range of 5 to 25 ohms / square, particularly 5 to 20 ohms / square, more particularly 5 to 18 ohms / square.

[0218] Clause 58: The method of any one of clauses 46 to 57, wherein the first underlayer film has a first underlayer thickness, the second underlayer film has a second underlayer thickness, and the embedded film has an embedded film thickness, so as to provide the coated article with a color having an a* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1, and a b* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1.

[0219] Clause 59: The method of any one of clauses 46 to 58, wherein the first underlayer thickness is from 11 nm to 15 nm and / or the second underlayer thickness is from 29 nm to 34 nm.

[0220] Clause 60: The method of any one of clauses 46 to 59, further comprising the step of depositing a protective layer on the transparent conductive oxide layer, the protective layer comprising a first protective film and a second protective film on at least a portion of the first protective film, the second protective film being an outermost film, and the second protective film comprising titania and alumina.

[0221] Clause 61: The method of clause 60, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0222] Clause 62. The method of clause 60 or 61, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, and more specifically 50 weight percent titania.

[0223] Clause 63: The method of any one of clauses 60 to 62, wherein the second protective coating comprises 65 to 35 weight percent alumina, specifically 55 to 45 weight percent alumina, and more specifically 50 weight percent alumina.

[0224] Clause 64. The method of any one of clauses 60 to 63, further comprising a third protective coating positioned over at least a portion of the first protective coating, between the first protective coating and the second protective coating or between the first protective coating and the functional coating, the third protective coating comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0225] Clause 65: The method of any one of clauses 47 to 64, wherein the first transparent conductive oxide film and the second transparent conductive oxide film contain the same metal oxide.

[0226] Clause 66: A coated article comprising a substrate and an underlayer over at least a portion of the substrate. The underlayer has a first underlayer film and a second underlayer film. The first underlayer film comprises a first high refractive index material. The second underlayer film comprises a low refractive index material. The first high refractive index material has a higher refractive index than the low refractive index material. A first transparent conductive oxide film is located over at least a portion of the second underlayer film. A buried film is located over at least a portion of the first transparent conductive oxide film. The buried film comprises a second high refractive index material. The second high refractive index material has a higher refractive index than the low refractive index material. A second transparent conductive oxide film is located over at least a portion of the buried film.

[0227] Clause 67: The coated article of clause 66, wherein the embedded film has a thickness of 5 nm to 50 nm, particularly 10 nm to 40 nm, and more particularly 15 nm to 30 nm.

[0228] Clause 68: A coated article described in clause 66 or 67, wherein the second high refractive index material comprises tin oxide and zinc oxide.

[0229] Clause 69: The coated article of any one of clauses 66 to 68, wherein the first transparent conductive oxide film is thicker than the second transparent conductive oxide film.

[0230] Clause 70: The coated article of any one of clauses 66 to 68, wherein the first transparent conductive oxide film is thinner than the second transparent conductive oxide film.

[0231] Clause 71: The coated article of any one of clauses 66 to 68, wherein the first transparent conductive oxide film is about the same thickness as the second transparent conductive oxide film.

[0232] Clause 72: A coated article described in any one of clauses 66 to 71, wherein the first transparent conductive oxide film and / or the second transparent conductive oxide film are selected from the group consisting of gallium-doped zinc oxide ("GZO"), aluminum-doped zinc oxide ("AZO"), indium-doped zinc oxide ("IZO"), magnesium-doped zinc oxide ("MZO"), or tin-doped indium oxide ("ITO"), particularly GZO, AZO, and ITO, more particularly ITO.

[0233] Clause 73: A coated article described in any one of clauses 66 to 72, wherein the high refractive index material comprises zinc oxide and tin oxide.

[0234] Clause 74: A coated article described in any one of clauses 66 to 73, wherein the low refractive index material comprises silica and alumina.

[0235] Clause 75: A coated article described in any one of clauses 66 to 74, wherein the transparent conductive oxide layer has a thickness of at most 950 nm, particularly at most 550 nm, and more particularly at most 360 nm.

[0236] Clause 76: The coated article of any one of clauses 66 to 75, wherein the coated article has a sheet resistance in the range of 5 to 20 ohms / square, particularly 8 to 18 ohms / square, and more particularly 5 to 15 ohms / square.

[0237] Clause 77: The coated article of any one of clauses 66 to 80, wherein the first underlayer film has a first underlayer thickness, the second underlayer film has a second underlayer thickness, and the embedded film has an embedded film thickness, so as to provide the coated article with a color having an a* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1, and a b* of at least -9 and at most 1, particularly at least -4 and at most 0, more particularly at least -3 and at most 1, more particularly at least -1.5 and at most -0.5, and more particularly -1.

[0238] Clause 78: The coated article of any one of clauses 76 to 77, wherein the first underlayer thickness is from 11 nm to 15 nm and / or the second underlayer thickness is from 29 nm to 34 nm.

[0239] Clause 79: A coated article described in any one of clauses 66 to 78, further comprising a protective layer on the transparent conductive oxide layer, the protective layer comprising a first protective film and a second protective film on at least a portion of the first protective film, the second protective film being the outermost film, and the second protective film comprising titania and alumina.

[0240] Clause 80. The coated article of clause 79, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0241] Clause 81: The coated article of clause 79 or 80, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, more specifically 50 weight percent titania.

[0242] Clause 82: The coated article of any one of clauses 79 to 81, wherein the second protective coating comprises 65 to 35 weight percent alumina, specifically 55 to 45 weight percent alumina, and more specifically 50 weight percent alumina.

[0243] Clause 83: The coated article of any one of clauses 79 to 82, further comprising a third protective coating positioned over at least a portion of the first protective coating, between the first protective coating and the second protective coating or between the first protective coating and the functional coating, the third protective coating comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0244] Clause 84: A coated article described in any one of clauses 66 to 83, wherein the first transparent conductive oxide layer and / or the second transparent conductive oxide layer has a thickness of at most 400 nm, particularly at most 360 nm, more particularly at most 240 nm, more particularly at most 180 nm, more particularly at most 120 nm, or more particularly at most 80 nm.

[0245] Clause 85: A coated article comprising a substrate, a functional layer on at least a portion of the substrate, a first protective coating on at least a portion of the functional layer, and a second protective coating on at least a portion of the first protective coating. The second protective coating comprises titania and alumina and is an outermost coating.

[0246] Clause 86: The coated article of clause 85, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof.

[0247] Clause 87: The coated article of clause 85 or 86, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, more specifically 50 weight percent titania.

[0248] Clause 88: The coated article of any one of clauses 85 to 87, wherein the second protective coating comprises 65 to 35 weight percent silica, specifically 55 to 45 weight percent silica, and more specifically 50 weight percent silica.

[0249] Clause 89: The coated article of any one of clauses 85 to 88, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0250] Clause 90: A coated article according to any one of clauses 85 to 89, wherein the functional layer comprises a transparent conductive oxide layer selected from the group consisting of zinc oxide doped with aluminum, zinc oxide doped with gallium, and indium oxide doped with tin, in particular indium oxide doped with tin.

[0251] Clause 91: A coated article according to any one of clauses 85 to 90, wherein the functional layer comprises a metal selected from the group consisting of silver, gold, palladium, copper or mixtures thereof, in particular silver.

[0252] Clause 92: A coated article described in any one of clauses 85 to 91, further comprising a third protective film located over at least a portion of the first protective film, between the first protective film and the second protective film or between the first protective film and the functional coating.

[0253] Clause 93: The coated article of any one of clauses 85 to 91, wherein the third protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0254] Clause 94: A method for protecting a functional layer, comprising the steps of providing an article coated with a functional layer, depositing a first protective film over at least a portion of the functional coating, and depositing a second protective film over at least a portion of the first protective film, wherein the second protective film comprises titania and alumina.

[0255] Clause 95: The method of clause 94, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof.

[0256] Clause 96. The method of clause 94 or 95, wherein the second protective coating comprises 35 to 65 weight percent titania, specifically 45 to 55 weight percent titania, more specifically 50 weight percent titania.

[0257] Clause 97: The method of any one of clauses 94 to 99, wherein the second protective coating comprises 65 to 35 weight percent silica, specifically 55 to 45 weight percent silica, and more specifically 50 weight percent silica.

[0258] Clause 98. The method of any one of clauses 94 to 97, wherein the first protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the first protective coating does not comprise a mixture of titania and alumina.

[0259] Clause 99: The method of any one of clauses 94 to 98, wherein the functional layer comprises a transparent conductive oxide layer selected from the group consisting of aluminum doped zinc oxide, gallium doped zinc oxide, and tin doped indium oxide, in particular tin doped indium oxide.

[0260] Clause 100: The method according to any one of clauses 94 to 99, wherein the functional layer comprises a metal selected from the group consisting of silver, gold, palladium, copper or mixtures thereof, in particular silver.

[0261] Clause 101: The method of any one of clauses 94 to 100, further comprising a third protective film positioned over at least a portion of the first protective film, between the first protective film and the second protective film or between the first protective film and the functional coating.

[0262] Clause 102. The method of any one of clauses 94 to 101, wherein the third protective coating comprises titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof. Optionally, the third protective coating does not comprise a mixture of titania and alumina.

[0263] Clause 103: A method of reducing the absorptance of a transparent conductive oxide layer, the emissivity of a coated article, and / or the absorptance of a coated article, comprising the steps of providing a substrate, depositing a transparent conductive oxide layer, and heat treating the coated article including the transparent conductive oxide layer in an atmosphere containing 0% to 1.0% oxygen, particularly 0% to 0.5% oxygen.

[0264] Clause 104: The method of clause 103, wherein the transparent conductive oxide layer comprises indium doped tin oxide ("ITO") or aluminum doped zinc oxide ("AZO").

[0265] Clause 105: The method of clause 103 or 104, wherein the transparent conductive oxide layer has a thickness of at least 125 nm, particularly at least 150 nm, more particularly at least 175 nm, and at most 450 nm, at most 400 nm, at most 350 nm, at most 300 nm, at most 250 nm, or at most 250 nm.

[0266] Clause 106: The method of any one of clauses 103 to 105, wherein the transparent conductive oxide layer comprises indium doped tin oxide ("ITO") and the atmosphere comprises 0.75% to 1.25% oxygen.

[0267] Clause 107: The method of any one of clauses 103 to 106, wherein the transparent conductive oxide layer comprises a thickness of at least 95 nm and at most 225 nm.

[0268] Clause 108: The method of any one of clauses 103 to 107, wherein the transparent conductive oxide layer comprises aluminum doped zinc oxide ("AZO") and the atmosphere comprises 0% to 0.5% oxygen, particularly 0% to 0.25% oxygen, more particularly 0% to 0.1% oxygen by volume, or even more particularly 0% oxygen by volume.

[0269] Clause 109: The method of clause 108, wherein the transparent conductive oxide layer comprises a thickness of at least 225 nm and at most 440 nm.

[0270] Clause 110: The method of any one of clauses 103 to 109, further comprising depositing a functional coating on at least a portion of the substrate, the functional coating being positioned between the substrate and the transparent conductive oxide layer.

[0271] Clause 111: The method of any one of clauses 103 to 110, further comprising depositing a first protective film comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof on at least a portion of the transparent conductive oxide layer, and depositing a second protective film comprising titania and alumina on at least a portion of the first protective film, the second protective film being an outermost film.

[0272] Clause 112: A method for reducing the sheet resistance of a coated article, comprising: depositing a coating comprising a transparent conductive oxide layer on a substrate at room temperature; and heating a top surface of the transparent conductive oxide layer to greater than 193.3°C (380°F) or at least 223.9°C (435°F) for at least 5 seconds, at least 10 seconds, at least 30 seconds, and no more than 120 seconds, 90 seconds, 60 seconds, 55 seconds, 50 seconds, 45 seconds, 40 seconds, or 35 seconds.

[0273] Clause 113: The method of clause 112, wherein the heating step is flash annealing.

[0274] Clause 114: The method of clause 112 or 113, wherein the transparent conductive oxide layer is at least 125 nm and at most 950 nm.

[0275] Clause 115: A method according to any one of clauses 112 to 114, wherein the transparent conductive oxide layer comprises indium oxide doped with tin and is at least 105 nm and at most 171 nm, and the sheet resistance of the coated article after the treatment step is less than 20 Ω / □.

[0276] Clause 116: A method according to any one of clauses 112 to 115, wherein the transparent conductive oxide layer comprises zinc oxide doped with gallium and has a thickness of at least 320 nm and at most 480 nm, and the sheet resistance of the coated article after the treatment step is less than 20 Ω / □.

[0277] Clause 117: A method according to any one of clauses 112 to 116, wherein the transparent conductive oxide layer comprises an oxide doped with alumina and has a thickness of at least 344 nm and at most 880 nm, and the sheet resistance of the coated article after the treatment step is less than 20 Ω / □.

[0278] Clause 118: The method of any one of clauses 112 to 117, wherein the step of depositing the coating comprises a magnetron sputtering vacuum deposition process.

[0279] Clause 119: The method of any one of clauses 112 to 118, wherein the step of applying the coating does not use radiant heat.

[0280] Clause 120: The method of any one of clauses 112 to 119, further comprising the steps of: depositing a first protective film on at least a portion of the transparent conductive oxide layer, the first protective film comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof; and depositing a second protective film on at least a portion of the transparent conductive oxide layer, the second protective film comprising titania and alumina, wherein the steps of depositing the first protective film and depositing the second protective film are performed before or after the processing step.

[0281] Clause 121: The method of any one of clauses 112 to 120, wherein the heating step does not raise the top surface of the transparent conductive oxide above 335°C (635°F).

[0282] Clause 122: The method of any one of clauses 112 to 121, wherein the substrate is glass and the transparent conductive oxide has an absorptivity of 0.3 or less.

[0283] Clause 123: The method of any one of clauses 112 to 122, wherein the substrate is glass and the transparent conductive oxide has an absorptivity at least as high as 0.05.

[0284] Clause 124: The method of any one of clauses 112 to 123, wherein the coated article is a refrigerator door.

[0285] Clause 125: The method of any one of clauses 112 to 124, wherein the depositing step is carried out in an atmosphere having an oxygen content of 0% to 1.5% supplied to the atmosphere.

[0286] Clause 126: The method of any one of clauses 112 to 125, wherein the substrate is glass and the transparent conductive oxide has an absorptivity of less than or equal to 0.2 and at least as high as 0.05.

[0287] Clause 127: A method of making a coated article, comprising depositing a transparent conductive oxide layer on a substrate, and raising a top surface of the transparent conductive oxide to greater than 193.3°C (380°F), or to at least 223.9°C (435°F), for at least 5 seconds, at least 10 seconds, at least 15 seconds, at least 20 seconds, at least 25 seconds, at least 30 seconds, and no more than 120 seconds, 90 seconds, 60 seconds, 55 seconds, 50 seconds, 45 seconds, 40 seconds, or 35 seconds, and not raising the top surface of the transparent conductive oxide above 430°C (806°F) (or specifically 335°C (635°F)).

[0288] Clause 128: The method of clause 127, further comprising the step of not heating the coated article above 335°C (635°F).

[0289] Clause 129: A method according to any one of clauses 127 to 128, wherein the transparent conductive oxide layer comprises indium oxide doped with tin and has a thickness of at least 96 nm and at most 171 nm and a sheet resistance of less than 25 Ω / □.

[0290] Clause 130: The method of any one of clauses 1127 to 129, further comprising the step of depositing a protective layer over the transparent conductive oxide, the protective layer comprising titania and alumina.

[0291] Clause 131: A coated substrate produced by the method of any one of clauses 15 to 26, having an a* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5, and a b* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5.

[0292] Clause 132: A coated substrate produced by the method of any one of clauses 46 to 65, having an a* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5, and a b* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5.

[0293] Clause 133: A coated article made by the method of any one of clauses 103 to 111.

[0294] Clause 134: A coated article made by the method of any one of clauses 112 to 126.

[0295] Clause 135: A coated article made by the method of any one of clauses 127 to 130.

[0296] Clause 136: Use of an underlayer according to any one of clauses 1 to 14 or 27 to 45 to provide an a* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5, and a b* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, or more particularly -1.5 to -0.5.

[0297] Clause 137: Use of a first underlayer film and a second underlayer film according to any one of clauses 15 to 26 or 46 to 65 to provide an a* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, more particularly -1.5 to -0.5, and a b* of -9 to 1, particularly -4 to 0, more particularly -3 to 1, or more particularly -1.5 to -0.5.

[0298] Clause 138: Use of a buried film according to any one of clauses 27 to 65 for reducing sheet resistance.

[0299] Clause 139: Use of a protective layer according to any one of clauses 85 to 93 for increasing the durability of a coating on a substrate.

[0300] Clause 140: The coated article of any one of clauses 85 to 91, wherein the protective layer has a thickness of at least 20 nm, 40 nm, 60 nm, or 80 nm, 100 nm, or 120 nm, and at most 275 nm, 255 nm, 240 nm, 170 nm, 150 nm, 125 nm, or 100 nm.

[0301] Clause 141: The coated article of any one of clauses 85 to 91 or 140, wherein the first protective film can have a thickness of at least 10 nm, at least 15 nm, at least 20 nm, at least 27 nm, at least 30 nm, at least 35 nm, at least 40 nm, at least 54 nm, at least 72 nm, and at most 85 nm, 70 nm, 60 nm, 50 nm, 45 nm, or 30 nm.

[0302] Clause 142: The coated article of any one of clauses 85 to 91, 140, or 141, wherein the second protective film can have a thickness of at least 10 nm, at least 15 nm, at least 20 nm, at least 27 nm, at least 35 nm, at least 40 nm, at least 54 nm, at least 72 nm, and at most 85 nm, 70 nm, 60 nm, 50 nm, 40 nm, 45 nm, 30 nm.

[0303] Clause 143: The coated article of any one of clauses 85 to 91 or 140 to 142, wherein the optional third protective film can have a thickness of at least 5 nm, at least 10 nm, at least 15 nm, at least 27 nm, at least 35 nm, at least 40 nm, at least 54 nm, at least 72 nm, and at most 85 nm, 70 nm, 60 nm, 50 nm, 45 nm, 30 nm, or at most 30.

Claims

1. 1. A method for reducing the sheet resistance of a coated article, comprising: depositing a coating on a substrate comprising a transparent conductive oxide layer having a thickness of 125 nm to 950 nm at room temperature; and treating the transparent conductive oxide layer, wherein the treating step includes flash annealing the transparent conductive oxide layer to reach a temperature of at least 224° C. (435° F.) and no more than 470° C. (878° F.), the transparent conductive oxide layer being flash annealed to heat a surface of the transparent conductive oxide layer, and wherein the sheet resistance of the coated article after the treating step is 20 Ω / □ or less; 13. The method of claim 12, further comprising depositing a first protective film comprising titania, alumina, zinc oxide, tin oxide, zirconia, silica, or a mixture thereof on at least a portion of a transparent conductive oxide layer, and depositing a second protective film comprising titania and alumina on at least a portion of the transparent conductive oxide layer, wherein the depositing of the first protective film and the depositing of the second protective film occur before or after the treating step.

2. The method of claim 1 , wherein the transparent conductive oxide layer comprises indium oxide doped with tin.

3. The method of claim 1 , wherein the transparent conductive oxide layer comprises zinc oxide doped with gallium and has a thickness of at least 320 nm and at most 480 nm.

4. The method of claim 1 , wherein the transparent conductive oxide layer comprises zinc oxide doped with aluminum and has a thickness of at least 344 nm and at most 860 nm.

5. The method of claim 1 , wherein the step of depositing the coating comprises a magnetron sputtering vacuum deposition process.

6. 10. The method of claim 1, wherein the heating step does not raise the top surface of the transparent conductive oxide above 335°C (635°F).

7. The method of claim 1 , wherein the coated article is a refrigerator door.

8. The method of claim 1 , wherein the depositing step occurs in an atmosphere having an oxygen content of between 0% and 1.5% provided to the atmosphere.