Abstract

at least one alkenyl-derivatized polysiloxane and a compound of formula (I): R 1 (R)2SiO((R 3 R 4 )SiO) x Si(R)2R 2 (I) wherein R is independently C(1-12) alkyl; 1 , R 2 , R 3 , R 4 is independently C(1-12)alkyl, or mercapto-C(1-12)alkyl, and x is 1 or more, provided that R 1 , R 2 , R 3 , R 4 wherein at least one is mercapto-C(1-12)alkyl), where the at least one alkenyl-derivatized polysiloxane and the at least one mercapto-derivatized polysiloxane crosslinker form a stable emulsion, their use in additive manufacturing, and 3D printed silicone objects obtained from these compositions are disclosed.

Description

[Technical field]

[0001] The present invention relates to additive manufacturing compositions comprising at least one alkenyl-derivatized polysiloxane and at least one mercapto-derivatized polysiloxane crosslinker, where the at least one alkenyl-derivatized polysiloxane and the at least one mercapto-derivatized polysiloxane crosslinker form a stable emulsion; their use in additive manufacturing, and three-dimensional (3D) printed silicone objects obtained by using these compositions. [Background technology]

[0002] Additive manufacturing, also commonly known as 3D printing, refers to a process used to fabricate three-dimensional objects by depositing and solidifying various forms of material (e.g., layers, droplets, etc.) to obtain the entire three-dimensional object layer-by-layer or sequentially, or to solidify the entire volume simultaneously to obtain the entire object all in one piece.

[0003] Today, a large number of materials are available for additive manufacturing, ranging from metals to synthetic resins. In one type of additive manufacturing, layers of liquid crosslinkable material are deposited according to a predetermined pattern using a device with a nozzle. Examples of such types of additive manufacturing are 3D printing of elastomers and hydrogels, both of which require crosslinking. After depositing a layer of crosslinkable material (either as a layer or as multiple droplets forming a layer), the crosslinkable material is crosslinked, for example by exposure to radiation, temperature changes, or by contact with a chemical crosslinking agent, to obtain a free-standing structure on which further layers can then be deposited and crosslinked. Alternatively, an object may be integrally formed from the crosslinkable material in a first step and integrally crosslinked in a subsequent step.

[0004] Polysiloxanes, also known as silicones, have not been widely used in the field of additive manufacturing so far due to several problems inherent to this class of compounds. On the one hand, polysiloxanes exhibit high viscosity, which makes them difficult to dose accurately, while on the other hand, polysiloxanes have rather poor viscoelastic properties, which makes it difficult to provide inks that retain their shape after deposition (e.g., do not flow or bleed). The above problems are exacerbated by the fact that most of the crosslinking chemistries that can be used to crosslink polysiloxanes utilize (toxic) (organo)metallic catalysts and / or require impractical crosslinking times (reducing the attractive effect on molding) and / or require high temperatures (requiring additional heating equipment).

[0005] It is therefore desirable to provide an alternative type of silicone-based ink that can be better used in the context of additive manufacturing by reducing the cure time, and that does not leave (toxic) catalyst residues in its crosslinked product.

[0006] US Patent No. 5,399,633 discloses a UV-curable silicone resin-organo mercaptan composition, in which a polysiloxane is functionalized with at least two aliphatically unsaturated radicals capable of reacting with a mercaptan having two or more mercapto groups, as well as a free radical photoinitiator and a free radical inhibitor. The composition is formed by mixing the components of the composition into a transparent, compatible mixture, which is then cast onto different substrates to form a coating.

[0007] Patent Document 2 discloses a crosslinkable composition for producing a microlens, which comprises a polysiloxane having an unsaturated bond group, a polysiloxane different from the aforementioned polysiloxane, a mercapto compound, a photoinitiator, and an organic solvent for dissolving the aforementioned compound. The composition is applied to a substrate as a film coating and crosslinked using radiation and heat.

[0008] US Patent No. 5,399,633 discloses a UV crosslinkable composition useful as a protective coating in the electronics industry, which comprises an alkenyl-containing polymethylsiloxane, a mercaptoalkyl-containing compound such as glycol dimercaptoacetate, a photoinitiator such as benzophenone, as well as a dye that indicates the degree of crosslinking via a change in color.

[0009] Patent Document 4 discloses a curable resin composition containing a modified silicone compound having two or more alkenyl groups, a polythiol compound having two or more thiol groups, as well as a free radical photoinitiator for coating touch screens with a protective layer.

[0010] US Patent No. 5,999,633 discloses a composition that forms a dry silicone gel that can act as a crosslinker / chain extender having two or more thiol groups, a free radical initiator, and a reinforcing agent such as fumed silica, and the composition can be crosslinked by UV radiation or heat.

[0011] Non-Patent Document 1 discloses a composition capable of crosslinking vinyl-polysiloxanes and thiol-polysiloxanes by UV irradiation. A coating of the above composition was applied onto a coverslip, allowing further characterization of the coating.

[0012] US Pat. No. 5,399,633 discloses a low viscosity composition for UV-curable thin films for use in the field of optical fibers, the composition comprising a polysiloxane resin functionalized with aliphatically unsaturated groups and an organic mercaptan as a crosslinking agent.

[0013] Patent Document 7 discloses a photocurable silicone composition for use in 3D printing, which comprises a mixture of at least a polysiloxane resin functionalized with an aliphatic unsaturated group and a polysiloxane resin functionalized with a thiol group as a crosslinker.

[0014] US Patent No. 5,399,633 discloses a polymer composition including a siloxane polymer component having multiple vinyl groups and a siloxane polymer component having multiple thiol groups for use in a bottom-up 3D printer to form an elastomeric 3D structure. [Prior art documents] [Patent documents]

[0015] [Patent Document 1] European Patent Application Publication No. 0437247 [Patent Document 2] JP 2010-0185991 A [Patent Document 3] U.S. Pat. No. 5,302,627 [Patent Document 4] JP 2015-193820 A [Patent Document 5] International Publication No. 2013 / 160252 [Patent Document 6] JP 2010-185991 A [Patent Document 7] International Publication No. 2016 / 044547 [Patent Document 8] International Publication No. 2018 / 026829 [Non-patent literature]

[0016] [Non-Patent Document 1] Khai DQ Nguyen, et al, Polym. Chem., 2016,7, 5281-5293 Summary of the Invention

[0017] The Applicant has now realised that the above problems can be solved by providing an additive manufacturing composition comprising at least one alkenyl-derivatised polysiloxane and at least one mercapto-derivatised polysiloxane as a crosslinker, which can be directly used in conventional additive manufacturing equipment due to its excellent rheological properties, both at rest and under shear, which are achieved by the formation of a stable emulsion of at least one mercapto-derivatised polysiloxane crosslinker and at least one alkenyl-derivatised polysiloxane, such that polymerization is initiated in a controlled manner at the droplet interface or continuous phase of the emulsion, resulting in a product with excellent optical and mechanical properties.

[0018] The object of the present invention is to provide a method for producing a compound according to the present invention, comprising the steps of: 1 (R)2SiO((R 3 R 4 )SiO) x Si(R)2R 2 (I) where R is independently C(1-12)alkyl, preferably methyl; R 1 , R 2 , R 3 , R 4 are independently C(1-12)alkyl, preferably methyl, or mercapto-C(1-12)alkyl, and x is 1 or more, preferably 1 to 1,000,000, provided that R 1 , R 2 , R 3 , R 4 wherein at least one alkenyl-derivatized polysiloxane and the at least one mercapto-derivatized polysiloxane crosslinker form a stable emulsion.

[0019] It is a further object of the present invention to provide a process for producing the above additive manufacturing composition, wherein at least one alkenyl-derivatized polysiloxane and at least one mercapto-derivatized polysiloxane crosslinker are formed into a stable emulsion.

[0020] A further object of the present invention is to provide the use of the additive manufacturing composition of the present invention for the additive manufacturing of objects composed of one or more materials and exhibiting different mechanical and optical properties.

[0021] A further object of the present invention is to provide a process for additively manufacturing an object, such as a cured composition, from the additive manufacturing composition of the present invention, wherein said object is preferably manufactured by material extrusion, such as stereolithography, e.g. laser-based stereolithography (SLA) and digital light processing (DLP), material-jetting, drop-on-demand, volumetric 3D printing, i.e. holographic laser 3D printing, robocasting, etc. Thus, in some embodiments, the 3D object is manufactured by dispensing and solidifying the additive manufacturing composition of the present invention on a platform, successively or layer-by-layer, such as by SLA or DLP, preferably DLP with top-down orientation. In other embodiments, the 3D object is manufactured by simultaneously solidifying the additive manufacturing composition of the present invention in one part, such as by volumetric 3D printing, i.e. holographic laser 3D printing.

[0022] It is a further object of the present invention to provide digitally fabricated silicone.

[0023] It is a further object of the present invention to provide a cured composition produced by the method disclosed herein.

[0024] The following detailed description, together with specific examples, is intended to provide an overview or framework for understanding the nature and character of the present disclosure. The accompanying drawings are included to provide a further understanding, and are incorporated in and constitute a part of this specification. [Brief description of the drawings]

[0025] [Figure 1] FIG. 1 is a schematic diagram of emulsion formation (Step 1) upon mixing an alkenyl-derivatized polysiloxane and a mercapto-derivatized polysiloxane-based crosslinker and the step-growth polymerization that occurs at the emulsion interface. [Diagram 2] Figure 1 shows a UV-cured composition of the present invention (no markers) compared to commercially available addition-cured silicones using the silicones Eco-flex® 00-20 Part A (▼), PlatSil® 73-15 Part A (▲), Dragon Skin™ 30 Part A (●), Sorta-Clear® 40 (black hexagon), Sylgard® 184 (◆), and LS-8941 Part A (■). The x-axis represents strain (%) and the y-axis represents strain (N / mm2). [Diagram 3] Tensile tests of DragonSkin™ 30 at crosslinker concentrations of 0.50% (▲), 0.75% (■), 1.00% (black hexagon), and 1.25 wt% (●) compared to a commercial addition cure silicone (no marker). The x-axis represents strain (%) and the y-axis represents strain (N / mm2). [Figure 4] Polysiloxane PlatSil® 73-15 polymerized alone (◆) or as a 9:1 mixture with Polysiloxane Q resin using MPMS (3.25%, ●). The x-axis represents strain (%) and the y-axis represents strain (N / mm2). [Figure 5a]The transmittance of six silicone objects (1 mm thick) obtained by photopolymerization of alkenyl-derivatized polysiloxanes (Ecoflex® 00-20 (●), PlatSil® 73-15 (right filled triangle), DragoSkin™ 30 (filled hexagon), Sorta-Clear® 40 (right filled triangle), Sylgard® 184 (■), LS-8941 (◆)) according to the invention using MPMS at concentrations of 0.5%, 3.5%, 0.8%, 1.5%, 4.5%, and 6.5%, respectively. [Figure 5b] Figure 5a shows the in-line transmittance of six silicone objects (from left to right: Ecoflex® 00-20, PlatSil® 73-15, DragoSkin™ 30, Sorta-Clear® 40, Sylgard® 184, LS-8941). The x-axis represents wavelength (nm) and the y-axis represents transmittance (%). [Figure 6] Figure 1 shows the decrease in viscosity of KE-2061 A30 with 3% MPMS at room temperature (■), 60 °C (▲), and 100 °C (●). The x-axis represents viscosity (Pas) and the y-axis represents shear rate (1 / s). DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0026] The object of the present invention is to provide a method for producing a siloxane comprising the steps of: 1 (R)2SiO((R 3 R 4 )SiO) x Si(R)2R 2 (I) where R is independently C(1-12)alkyl, preferably methyl; R 1 , R 2 , R 3 , R 4 are independently C(1-12)alkyl, preferably methyl, or mercapto-C(1-12)alkyl, and x is 1 or more, preferably 1 to 1,000,000, provided that R 1 , R 2 , R 3 , R4 wherein at least one alkenyl-derivatized polysiloxane and the at least one mercapto-derivatized polysiloxane crosslinker form a stable emulsion.

[0027] As used herein, the term "additive manufacturing" refers to methods such as stereolithography, e.g., laser-based stereolithography (SLA) and digital light processing (DLP), material-jetting, drop-on-demand, volumetric 3D printing, i.e., holographic laser 3D printing, and material extrusion, e.g., robocasting.

[0028] In a typical stereolithography process, a build platform is positioned in a vat or tank containing the additive manufacturing composition of the present invention at a distance of one layer height from the surface of the liquid, and a light source selectively polymerizes and solidifies the additive manufacturing composition to produce the next layer. While SLA printers use a laser source that moves over a predetermined area of ​​some layers, DLP printers use a digital light projector that flashes a single image of each layer at a time, which can also raster larger areas for a larger build volume than the projection. The build platform is then moved a distance so that a recoater can recoat or wipe the surface. The process steps are repeated until the 3D object is complete. Further post-treatment under UV / Vis light ensures that the 3D object is fully crosslinked, which is especially needed when high mechanical and thermal properties are desired.

[0029] "Top-down" orientation refers to a printer in which the light source is placed above the tank and the build platform starts at the top of the tank and moves downward after each layer. Typically, the direction perpendicular to the 3D printed layers of the 3D object is called the z direction (or axis), and the direction parallel to the 3D printed layers of the 3D object (and thus perpendicular to the z axis) is called the xy plane. Objects in a top-down printer are built up.

[0030] "Bottom-up" orientation refers to a printer in which the light source is located below a tank with a suitable transparent bottom to allow the light source to pass through. After each layer, the cured additive manufacturing composition is detached from the bottom of the tank as the build platform moves upward. Objects in bottom-up printers are built upside down.

[0031] In a typical material-jetting process, a print head deposits droplets of an additive manufacturing composition at desired locations on a build platform. A radiation source attached to the print head cures and solidifies the additive manufacturing composition to produce a first layer, and the build platform is moved downwards to allow the process steps to be repeated until the 3D object is complete. Droplet deposition can be done in a continuous manner, where droplets are generated by breaking a continuous stream of droplets, or by drop-on-demand, where droplets are generated when needed.

[0032] In a typical volumetric (i.e. holographic) printing method, a 3D object is generated simultaneously in one piece by projecting a hologram-like pattern of a light source(s) onto a transparent tank containing the additive manufacturing composition, allowing the additive manufacturing composition to harden in one piece. After the 3D object is completed, excess additive manufacturing composition can be drained off to reveal the completed 3D object.

[0033] In a typical material extrusion printing process, an additive manufacturing composition is extruded through a nozzle onto a build platform or substrate, whereby the nozzle follows a predetermined path to build up a 3D object layer by layer.

[0034] The additive manufacturing composition can be used in any typical 3D printer. In one embodiment, the additive manufacturing composition can be used in an SLA or DLP printer, preferably a top-down SLA or DLP printer, where a build platform is positioned on top of a tank filled with liquid photopolymer resin, and a light source located above the tank selectively hardens and solidifies the additive manufacturing composition layer by layer (by moving the platform downward after each layer) to create the desired 3D product (upward). In another embodiment, the additive manufacturing composition can be used in volumetric or holographic 3D printing, where a 3D image such as a laser-generated hologram is flashed onto the additive manufacturing composition contained in the tank to create the desired 3D product in one piece.

[0035] The use of additive manufacturing compositions in DLP printers is a particularly advantageous embodiment for the production of cured compositions, since the cured compositions produced in this way can have a high degree of transparency. The high degree of transparency can be attributed to a variety of factors, including the smooth surface of the cured composition and the low thickness of the layer solidified during the printing process. The low thickness of the solidified layer means that a high degree of polymerization is achieved during the printing process, resulting in little or no residual monomer that causes opacity. The smoothness of the surface reduces light diffraction.

[0036] The term "emulsion" as used in the context of the present invention refers to a mixture of two or more immiscible (polysiloxane) liquid components, in which (at least) one component (the dispersed phase) is dispersed in the form of droplets in (at least) another component (the continuous phase). It is understood that the term "immiscible" also includes predominantly or substantially immiscible phases, whereby the dispersed phase has a finite solubility in the continuous phase. The mixture may be further stabilized by the presence of additives such as emulsifiers or surfactants.

[0037] The term "stable emulsion" as used in connection with the present invention means a composition in which (at least one) component constituting the dispersed phase is 、1 months or more, ambient temperature Degree 2 It refers to an emulsion that remains substantially dispersed in the continuous phase after resting at 5° C. or after being subjected to centrifugal rotation at about 3,500 rpm for an hour or more. In particular, in a stable emulsion under these conditions, no signs of creaming of the emulsion or separation of the two phases of the emulsion are observed.

[0038] As used herein, the term "transparent" refers to the property of transmitting (without diffusion) at least 70%, preferably at least 80%, and more preferably at least 90% of incident visible light. The term "semi-transparent" refers to the property of reducing the passage of light, such as less than 60% transmission, preferably less than 50% transmission.

[0039] The term "polysiloxane" refers to a compound having the general formula (R)Si-(O-Si(R)) n refers to linear, branched and cyclic polyorganosiloxanes characterized by the formula O-Si(R)3, where R is H or an organic group, and n is an integer, typically 1 to 10. 9 In polyorganosiloxanes, the organic moieties can be the same (such as the methyl groups in polydimethylsiloxane or PDMS) or can be different within a single molecule (for example, in polydimethyldiphenylsiloxane or diphenyldimethicone).

[0040] In the alkenyl-derivatized polysiloxanes for use in the present invention, at least one, and preferably at least two, R groups comprise an alkenyl moiety, preferably a vinyl, allyl, butenyl or pentenyl group, more preferably a vinyl group, which may be located at the terminus and / or in the side chain.

[0041] Al useful in the present invention Keni The alkyl-derivatized polysiloxane comprises at least one, typically 1 to 10, alkyl groups in the form of a homopolymer, or a random or block copolymer, preferably a homopolymer. 9 , preferably polymers, prepolymers, oligomers or macromonomers having 100 to 10,000,000 siloxane repeat units. Optionally, the alkenyl-derivatized polysiloxanes may carry additional functional groups, for example as end groups or disposed on the side chain(s) of the siloxane backbone.

[0042] The weight average molecular weight of the alkenyl-derivatized polysiloxane is in the range of 100 to 10 9 The alkenyl-derivatized polysiloxanes useful in the present invention have a shear modulus of 0.1 to 10 g / mol, preferably 1,000 to 10,000,000, when measured at a shear rate of 1 / s according to standard steady-state rheological measurements. 4 Pa * s, preferably 1 to 10 2 Pa * The viscosity may be between 0.01 and 0.1.

[0043] Alkenyl-derivatized polysiloxanes include, for example, alkenyl-derivatized poly(alkylsiloxanes), alkenyl-derivatized poly(arylsiloxanes), alkenyl-derivatized poly(alkylarylsiloxanes), and alkenyl-derivatized poly(alkyl(aryl)siloxanes), preferably alkenyl-derivatized polyalkylsiloxanes (optionally carrying additional functional groups). In specific embodiments, the alkenyl-derivatized polysiloxanes include alkenyl-derivatized poly((C1-12)alkyl-siloxanes). In some embodiments, the alkenyl-derivatized polysiloxanes are preferably alkenyl-derivatized poly((C1-6)alkyl-siloxanes), where the C(1-6)alkyl is preferably methyl, ethyl, propyl, butyl.

[0044] Some exemplary preferred polysiloxanes are alkenyl-derivatized poly(dimethylsiloxane), alkenyl-derivatized poly(diphenylsiloxane), alkenyl-derivatized poly(methylphenylsiloxane), alkenyl-derivatized poly(dimethyldiphenylsiloxane). Such polymers can be prepared as described in numerous patents and publications or can be prepared from liquid silicone rubbers (LSR) or room temperature vulcanizing (RTV) silicones such as Ecoflex® 00-15, Ecoflex® 00-20, Dragon Skin™ 30, Sorta-Clear® 40 (KauPo, Germany), PlatSil® 73-15 (Mouldlife, UK), Sylgard® 184 (Sigma-Aldrich, Switzerland), Zhermack 00 Zhermack 08, Zhermack 13 (Zhermack, Germany), LS-8941 (NuSil, USA), KE-2061 (Shin-Etsu Chemical Co., Ltd., Japan), Vinyl Q Resin Dispersion in Vinyl Terminated Polydimethylsiloxane (Gelest). It is commercially available under the name Sigma-Aldrich Co., Ltd., Germany.

[0045] The additive manufacturing polysiloxane composition can include one alkenyl-derivatized polysiloxane or a mixture of two or more alkenyl-derivatized polysiloxanes.

[0046] Mercapto-derivatized polysiloxane crosslinkers useful in the present invention have the formula (I): R 1 (R)2SiO((R 3 R 4 )SiO) x Si(R)2R 2 (I) where R is independently C(1-12)alkyl, preferably methyl; R 1 , R 2 , R 3 , R 4 are independently C(1-12)alkyl, preferably methyl, or mercapto-C(1-12)alkyl, and x is 1 or more, preferably 1 to 1,000,000, provided that R 1 , R 2 , R 3 , R 4 At least one of, preferably 10 to 100,000, is mercapto-C(1-12)alkyl.

[0047] In some embodiments, C(1-12) alkyl is preferably C(1-8) alkyl, more preferably C(1-6) alkyl, more preferably methyl, ethyl, butyl, propyl. Thus, the mercaptoalkyl group preferably has 1 to 8 C atoms, preferably 1 to 6 C atoms, more preferably mercaptomethyl, mercaptoethyl, mercaptobutyl, mercaptopropyl, most preferably mercaptopropyl.

[0048] In some embodiments, x is about 100.

[0049] In a preferred embodiment, the mercapto-derivatized polysiloxane crosslinker useful in the present invention has the formula (I), where R, R 1 , R 2 , R 4is independently C(1-12)alkyl, preferably methyl; R 3 is independently mercapto-C(1-12)alkyl, preferably mercapto-C(1-6)alkyl, or C(1-12)alkyl, preferably methyl; and x is 1 or more, preferably 2 to 100,000, preferably 5 to 1,000.

[0050] If x>1, R 3 may be the same (e.g., a homopolymer), and preferably R 3 is mercapto-C(1-12)alkyl, more preferably mercapto-C(1-6)alkyl as defined above. Alternatively, R 3 may be different (e.g., alternating or block copolymers), preferably R 3 is -(mercapto-C(1-6)alkyl) n -(C(1-12)alkyl) m or -(C(1-12))alkyl) m -(Mercapto-C(1-6)alkyl) n -, where -(mercapto-C(1-6)alkyl) n -(C(1-12)alkyl) m - is as defined above, and n and m are independently 1 to 100,000, preferably n is 1 to 10,000 and m is 1 to 10,000.

[0051] In another preferred embodiment, the mercapto-derivatized polysiloxane crosslinker useful in the present invention has the formula (I), 1 , R 2 is independently C(1-12)alkyl, preferably methyl; R 3 , R 4 is independently mercapto-C(1-12)alkyl, preferably mercapto-C(1-6)alkyl, or C(1-12)alkyl, preferably methyl; and x is 1 or more, preferably 2 to 100,000, preferably 5 to 1,000.

[0052] If x>1, R3 , R 4 may independently be the same (e.g., a homopolymer), and preferably R 3 , R 4 is independently mercapto-C(1-12)alkyl, more preferably mercapto-C(1-6)alkyl as defined above. Alternatively, R 3 , R 4 may be independently different (e.g., alternating or block copolymers), preferably R 3 , R 4 are independently -(mercapto-C(1-6)alkyl) n -(C(1-12)alkyl) m or -(C(1-12))alkyl) m -(Mercapto-C(1-6)alkyl) n -, where -(mercapto-C(1-6)alkyl) n -(C(1-12)alkyl) m - is as defined above, and n and m are independently 1 to 100,000, preferably n is 1 to 10,000 and m is 1 to 10,000.

[0053] In another preferred embodiment, the mercapto-derivatized polysiloxane crosslinker useful in the present invention has the formula (I), 1 , R 2 , R 4 is independently C(1-12)alkyl, preferably methyl; R 3 is independently mercaptomethyl, mercaptobutyl, mercaptoethyl or mercaptopropyl, and x is 1 or more, preferably 2 to 100,000, preferably 2 to 10,000.

[0054] In a specific embodiment, the mercapto-derivatized polysiloxane crosslinker of formula (I) useful in the present invention is a (mercaptopropyl)methylsiloxane homopolymer (MPMS) having one or more, preferably 2 to 100,000, preferably 2 to 10,000 mercaptopropyl units.

[0055] In another specific embodiment, the mercapto-derivatized polysiloxane crosslinkers of formula (I) useful in the present invention are (mercaptopropyl)methylsiloxane-dimethylsiloxane copolymers, where n and m are independently from 1 to 100,000, preferably n is from 1 to 10,000 and m is from 1 to 10,000.

[0056] The additive manufacturing polysiloxane composition can include one mercapto-derivatized polysiloxane crosslinker or a mixture of two or more mercapto-derivatized polysiloxane crosslinkers, preferably one mercapto-derivatized polysiloxane crosslinker.

[0057] In a further embodiment of the additive manufacturing composition according to the invention, the mercapto-derivatized polysiloxane crosslinker has a molecular weight of less than 100,000 g / mol, preferably less than 90,000 g / mol, more preferably less than 80,000 g / mol.

[0058] In a further embodiment of the additive manufacturing composition according to the invention the mercapto-derivatized polysiloxane crosslinker is present between 0.01 and 35 wt%, preferably between 0.1 and 10 wt%, based on the total weight of the additive manufacturing composition.

[0059] In a preferred embodiment, the alkenyl-derivatized polysiloxane and the mercapto-derivatized polysiloxane crosslinker are immiscible and can form an emulsion, preferably a stable emulsion. Thus, in a preferred embodiment of the additive manufacturing composition according to the invention, the alkenyl-derivatized polysiloxane forms the continuous phase of the emulsion and the mercapto-derivatized crosslinker forms the discontinuous phase. More specifically, the emulsion is obtained by mixing or shearing (e.g., effective mixing in a suitable high shear mixer) at more than 100 rpm, such as 500-5,000 rpm, for several minutes, e.g., at 2000 rpm for at least 2 minutes, preferably 5-15 minutes.

[0060] Within said emulsion, the discontinuous phase is present mainly as droplets having a diameter of 100 micrometers or less, preferably less than 10 micrometers, preferably 0.1-10 micrometers, which allows the emulsion to be sufficiently stable to prevent creaming of the dispersed phase, droplet aggregation, droplet coalescence and coarsening, and therefore to exhibit a good shelf life of (at least) 3 months (e.g., when stored below ambient temperature, e.g., 15°C). Step-growth polymerization occurs selectively near or at the emulsion interface until the crosslinker is completely exhausted. Consumption of the dispersed phase (droplets) in the polymerization process reduces the droplet size and scattering of visible light, allowing the production of transparent 3D objects. Thus, in a specific embodiment, the 3D silicone object obtained according to the present invention is transparent.

[0061] The emulsions of the present invention also allow the polymerized 3D objects to distinguish themselves by exhibiting unidirectional properties (also in the z-direction) and therefore achieve a certain light penetration depth by light scattering (in the xy plane and in the z-direction), which allows printing at high resolution (such as 30 μm for example) due to the limited penetration depth. Thus, in a specific embodiment, the 3D silicone objects obtained according to the present invention are of high resolution.

[0062] In another embodiment, the additive manufacturing composition further comprises at least one free radical photoinitiator, which can be activated by exposure to radiation, i.e. UV A, UV B, UV C and the full visible range, preferably UVA and the visible range, more preferably the visible range from 355 to 420 nm.

[0063] Exemplary free radical photoinitiators suitable for additive manufacturing compositions according to the invention are: (i) Acylphosphine oxides and bisacylphosphine oxides, such as 2,4,6-trimethylbenzoyldiphenylphosphine oxide and bis-(2,4,6-trimethylbenzoyl)phenylphosphine oxide; (ii) anisoin; (iii) Benzoin and benzoin alkyl ethers, such as benzoin ethyl ether, benzoin isobutyl ether, and benzoin methyl ether; (iv) benzyl and benzyl dialkyl ketals, such as benzyl dimethyl ketal; (v) Acetophenone; hydroxyacetophenones such as 1-hydroxycyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenyl-1-propanone, 2-hydroxy-1-[4-(2-hydroxyethoxy)-phenyl]-2-methyl-1-propanone, 3'-hydroxyacetophenone, 4'-hydroxyacetophenone, 2-hydroxy-2-methylpropiophenone; (di)alkoxyacetophenones such as 2,2-diethoxyacetophenone, 2,2-dimethoxy-2-phenylacetophenone, 4'-ethoxyacetophenone; aminoacetophenones such as 2-benzyl-2-(dimethylamino)-1-[4-(4-morpholinyl)-phenyl]-1-butanone, 2-methyl-1-[4-(methylthio)-phenyl]-2-(4-morpholinyl)-1-propanone; aryloxyacetophenones such as 4'-phenoxyacetophenone; (vi) (di)hydroxybenzophenones such as benzophenone, 3,3',4,4'-benzophenonetetracarboxylic dianhydride, benzoylbiphenyl, 4'-dihydroxybenzophenone, 3-hydroxybenzophenone, and 4-hydroxybenzophenone; and (di)alkylbenzophenones such as 4-(dimethylamino)benzophenone, 2-methylbenzophenone, 3-methylbenzophenone, 2,5-dimethylbenzophenone, and 3,4-dimethylbenzophenone, (di)aminobenzophenones such as 4,4'-bis(dimethylamino)benzophenone, and 2-benzyl-2-(dimethylamino)-4'-morpholinobutyrophenone and 2-methyl-4'-(methylthio)-2-morpholinopropiophenone; (vii) anthraquinones and alkylanthraquinones, such as 2-ethylanthraquinone; (viii) Thioxanthones; alkylthioxanthones such as i-propylthioxanthone; and thioxanthene-9-ones such as 2-chlorothioxanthen-9-one; (ix) dibenzosuberenone; (x) a-diketones or their derivatives, such as camphorquinone, 9,10-phenanthrenequinone, 1-phenyl-propane-1,2-dione, 4,4'-dichlorobenzil, methylbenzoylformate, etc.; (xi) monoacyl and diacylgermanium compounds, such as benzoyltrimethylgermanium, dibenzoyldiethylgermanium, and bis-(4-methoxybenzoyl)-diethylgermanium; (xii) Bis-(ethoxy) 5 -2,4-cyclopentadien-1-yl)-bis-[2,6-difluoro-3-(1H-pyrrol-1-yl)phenyl]-titanium.

[0064] Specific examples are acetophenone, anisoin, anthraquinone, benzil, benzoin, benzoin ethyl ether, benzoin isobutyl ether, benzoin methyl ether, benzophenone, 1-hydroxycyclohexyl phenyl ketone, 3,3',4,4'-benzophenonetetracarboxylic dianhydride, benzoylbiphenyl, 2-benzyl-2-(dimethylamino)-4'-morpholinobutyrophenone, 4,4'-bis(diethylamino)benzophenone, 4,4'-bis(dimethylamino)benzophenone, camphorquinone, 2-chlorothioxanthen-9-one, dibenzosuberenone, 2,2-diethoxyacetophenone, 4,4'-dihydroxybenzophenone, 2,2-dimethoxy-2-phenylacetophenone, 4-(dimethylamino)benzophenone, 4, 4'-Dimethylbenzyl, 2,5-dimethylbenzophenone, 3,4-dimethylbenzophenone, diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide / 2-hydroxy-2-methylpropiophenone, 4'-ethoxyacetophenone, 2-ethylanthraquinone, 3'-hydroxyacetophenone, 4'-hydroxyacetophenone, 3-hydroxybenzophenone, 4-hydroxybenzophenone, 1-hydroxycyclohexyl phenyl ketone, 2-hydroxy-2-methylpropiophenone, 2-methylbenzophenone, 3-methylbenzophenone, methylbenzoyl formate, 2-methyl-4'-(methylthio)-2-morpholinopropiophenone, phenanthrenequinone, 4'-phenoxyacetophenone, and thioxanthen-9-one.

[0065] In a specific embodiment, the additive manufacturing composition comprises as free radical photoinitiators 1-hydroxycyclohexyl phenyl ketone (98%, Alfa Aesar, USA) and / or bis(4-methoxybenzoyl)diethylgermanium (Ivocerin®, Synthon Chemicals, Germany) and / or 2,2-dimethoxy-2-phenylacetophenone.

[0066] Typically, the at least one photoinitiator is present in an amount of from 0.01 wt % to 1 wt %.

[0067] In one preferred embodiment, the additive manufacturing composition comprises one free radical photoinitiator.

[0068] In another preferred embodiment, the additive manufacturing composition comprises a first free radical photoinitiator and a second free radical photoinitiator, for example a first free radical photoinitiator and a second free radical photoinitiator having the same, overlapping or different absorption behavior. In one embodiment, the additive manufacturing composition comprises a first free radical photoinitiator and a second free radical photoinitiator having overlapping absorption behavior. In another embodiment, the additive manufacturing composition comprises a first free radical photoinitiator and a second free radical photoinitiator having different absorption behavior.

[0069] It is understood that the absorption spectra of the first and second photoinitiators may overlap somewhat. For example, the difference between the longest wavelength absorption maxima of the first and second photoinitiators may be at least 5 nm, preferably at least 10 nm, and more preferably at least 15 nm.

[0070] In a specific embodiment, the longest wavelength absorption maximum of the first photopolymerization initiator is less than 400 nm, for example, less than 300 to 400 nm, preferably less than 330 to 400 nm, more preferably 340 to 380 nm. The longest wavelength absorption maximum of the second photopolymerization initiator is at least 380 nm, for example, 380 to 600 nm, preferably 400 to 500 nm, more preferably 400 to 480 nm.

[0071] A preferred embodiment includes a combination of a germanium compound and a hydroxyacetophenone, in particular bis(4-methoxybenzoyl)diethylgermanium (Ivocerin) and 1-hydroxycyclohexyl phenyl ketone. The preferred ratio is in the range of 0.1-1 wt% of the hydroxyacetophenone, such as 1-hydroxycyclohexyl phenyl ketone, and 0.05-0.5 wt% of the germanium compound, such as Ivocerin.

[0072] In a further embodiment, the additive manufacturing composition further comprises at least one inhibitor, so as to allow the photocatalytic reaction to be limited to the area of ​​direct exposure and not initiated prematurely, ensuring a suitable shelf life. Suitable inhibitors include, for example, light blocking agents with an absorption maximum in the range of the beam wavelength of the light source used for photopolymerization, or colorants, such as (inorganic or organic) color pigments (e.g. carbon black, blue, red), organic dyes, etc., that absorb light and do not retransmit it. Other suitable inhibitors (especially for transparent compositions) include fluorescent agents / optical brighteners, photochromic and thermochromic dyes, leuco dyes, or absorbers that absorb light and emit light at a different frequency.

[0073] Commercially available inhibitors suitable for use in the additive manufacturing compositions include avobenzone, coumarin, 1-(4-tert-butylphenyl)-3-(4-methoxyphenyl)-1,3-propanedione (TCI, Germany), 5-tert-butyl-2-hydroxybenzaldehyde (Sigma-Aldrich, Switzerland), 2,2'-(2,5-thiophenediyl)bis(5-tert-butylbenzoxazole (Sigma-Aldrich, Switzerland), 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid (Alfa Aesar, USA), or 2-hydroxy-4-methoxybenzophenone (Alfa Aesar, USA).

[0074] The inhibitor may be present in the additive manufacturing composition in an amount of 0 to 5 weight percent, preferably 0.05 to 5 weight percent for pigments and 0.05 to 3 weight percent for optical brighteners.

[0075] Determination of the wavelength of absorption maximum and molar extinction coefficient of the photoinitiator and inhibitor is typically performed by UV-VIS spectroscopy, such as a conventional double beam UV-VIS spectrometer, at room temperature using solutions in a suitable solvent, such as acetonitrile, preferably at a concentration of 1 mM. For example, a conventional double beam UV-VIS spectrometer can be used for the measurements.

[0076] The additive manufacturing composition of the invention may further comprise additives, such as polysiloxane resins, which make it possible to adjust certain mechanical and optical properties of the final product.

[0077] Thus, in a further embodiment, the additive manufacturing composition of the invention may comprise a reinforcing polysiloxane resin, such as a silanol-trimethylsilyl modified polysiloxane Q resin or a polysiloxane MQ resin. If present, the reinforcing polysiloxane resin may be present in an amount of up to 100 wt%, preferably up to 50 wt%, relative to the total amount of alkenyl derivatized polysiloxane in the additive manufacturing composition, i.e. the weight ratio between the reinforcing polysiloxane resin and the alkenyl derivatized polysiloxane, if present, may range from 0 to 50 wt%, preferably from 0.1 to 10 wt%.

[0078] A reinforcing polysiloxane resin may be included in the additive manufacturing composition if the crosslinked additive manufacturing composition exhibits a moderate Shore hardness, e.g., A30-A50, or a high Shore hardness, e.g., greater than A50, such as a moderate or high elastic modulus (e.g., greater than 3 MPa and 5 MPa, respectively) and / or a moderate or low elongation at break (e.g., less than 500% and less than 250%, respectively).

[0079] If the crosslinked additive manufacturing composition exhibits a low Shore hardness, e.g. less than A30, such as a low elastic modulus (e.g. less than 1 MPa) and / or a high elongation at break (e.g. more than 500%), the reinforcing polysiloxane resin is preferably omitted.

[0080] Furthermore, the additive manufacturing composition may optionally contain one or more further additives to modify properties such as flowability, mechanical properties, storage properties, etc., i.e. electrically or thermally conductive materials, reinforcing fibers, colorants, surfactants, preservatives, stabilizers, plasticizers, lubricants, defoamers, leveling agents.

[0081] Typically, the mercapto-derivatized polysiloxane crosslinks contained in the additive manufacturing composition according to the invention are activated by exposure to radiation, in particular UV / Vis radiation. UV / Vis radiation with a wavelength between 190 nm and 900 nm can be easily generated using mercury vapor lamps or energy-efficient LED lamps and has the advantage of being able to penetrate deeply into the bulk of the additive manufacturing composition according to the invention so as to allow effective crosslinking of thicker layers of the additive manufacturing composition according to the invention. Generally, LED lamps have a relatively low intensity, i.e. 20 mW / cm2. 2 (measured at the surface of the projection plane).

[0082] Alternatively, the cross-linking agent may also be capable of being activated by exposure to a change in temperature, such as an increase or decrease in temperature, or by using a high energy beam, for example an electron beam.

[0083] In certain embodiments, the ratio of at least one alkenyl-derivatized polysiloxane to at least one mercapto-derivatized polysiloxane crosslinker is 1,000:1 to 5:1, preferably 500:1 to 10:1. In particular, in embodiments of additive manufacturing compositions for silicones with low Shore hardness, the ratio of at least one alkenyl-derivatized polysiloxane to at least one mercapto-derivatized polysiloxane crosslinker is 1,000:1 to 50:1, preferably 500:1 to 50:1. In embodiments of additive manufacturing compositions for silicones with high Shore hardness, the ratio of at least one alkenyl-derivatized polysiloxane to at least one mercapto-derivatized polysiloxane crosslinker is 50:1 to 5:1, preferably 25:1 to 10:1.

[0084] The mechanical properties of the crosslinked additive manufacturing composition can be modified by varying the nature of the alkenyl-derivatized polysiloxane, the mercapto-derivatized polysiloxane crosslinker, and the initiator, in particular by varying the amount and mercapto functionality of the crosslinker, the molecular weight (length), the amount of alkenyl derivatization, and the viscosity of the polysiloxane, or by adding reinforcing fillers.

[0085] If the silicone product exhibits a high elongation at break, i.e., greater than 500%, but a low Shore hardness, e.g., less than A30, the mercapto-derivatized polysiloxane crosslinker is preferably present in an amount between 0.01 wt % and 5 wt %, based on the total weight of the additive manufacturing composition, and / or is essentially free of reinforcing polysiloxane resin, and / or the polysiloxane has a hardness of up to 100,000 mPa. * s or 100~20,000mPa * It has a viscosity of s.

[0086] If the crosslinked additive manufacturing composition (also referred to herein as silicone product) exhibits a moderate Shore hardness, e.g., A30 to A50, such as a moderate elongation at break, i.e., less than 500%, the mercapto-derivatized polysiloxane crosslinker is preferably present in an amount of 2 wt. % to 10 wt. %, based on the total weight of the additive manufacturing composition, and / or the polysiloxane has a viscosity of up to 100,000 mPa. * s, or preferably 1,000 to 30,000 mPa * It has a viscosity between s.

[0087] If the crosslinked additive manufacturing composition (also referred to herein as silicone product) exhibits a low elongation at break, i.e. less than 250%, and a high Shore hardness, e.g. greater than A50, the mercapto-derivatized polysiloxane crosslinker is preferably present in an amount between 5 wt. % and 15 wt. %, based on the total weight of the additive manufacturing composition, and / or optionally comprises a reinforcing polysiloxane resin in an amount of up to 50 wt. %, relative to the total amount of polysiloxane in the additive manufacturing composition, and / or the polysiloxane has a viscosity of up to 100,000 mPa. * s, up to 500,000mPa * s, or preferably 5,000 to 50,000 mPa * It has a viscosity of s.

[0088] The additive manufacturing compositions according to the invention can be further tailored to exhibit specific optical properties by polymerization at or near the droplet surface and by controlling the nature and amount of the components and the polymerization mechanism, for example, the crosslinked composition can be transparent to visible light or translucent to visible light.

[0089] It is also an object of the present invention to provide a process for producing the additive manufacturing composition of the present invention, wherein the alkenyl-derivatized polysiloxane and the mercapto-derivatized polysiloxane crosslinker are formed into an emulsion with at least one photoinitiator. The at least one alkenyl-derivatized polysiloxane and the at least one mercapto-derivatized polysiloxane crosslinker may be used as such or dissolved in a suitable solvent (0-99%).

[0090] The viscosity of the compositions of the present invention can be controlled by lowering or raising the temperature of the composition. For example, the temperature can be lowered to -50°C or raised to +250°C, preferably 100°C, more preferably 60°C.

[0091] The viscosity of the compositions of the present invention may be controlled by using more than one alkenyl-derivatized polysiloxane (mixture) of different viscosities, i.e., by diluting the compositions of the present invention with (at least) one low viscosity alkenyl-derivatized polysiloxane or functionalized silicone fluid. Alternatively, the viscosity of the compositions of the present invention may be controlled by diluting with unmodified silicone fluid or oil. Depending on the final viscosity to be achieved, the organic solvent is preferably present in an amount of 0.1% to 20%.

[0092] As a further alternative, the viscosity may be controlled by dilution with a solvent. Thus, the composition may be solvent-free or diluted with a suitable solvent. Preferably, the composition has a viscosity of 100 Pa measured at 1 Hz. * s or less, more preferably 0.1 to 50 Pa * s, more preferably 0.1 to 30 Pa * s. In particular, the viscosity is selected so that the composition of the invention exhibits a flow behavior that is particularly well suited for the 3D printing process according to the invention, in which a recoater or wiper is used to wipe the printing surface, i.e. a flow behavior that allows fast and smooth recoating and thus fast printing times. Suitable solvents for dilution include organic solvents, such as linear and cyclic alkanes, e.g. pentane, hexane, heptane, cyclopentane, cyclohexane and higher alkanes, halogenated alkanes, e.g. dichloromethane, trichloromethane, tetrachloromethane, 1,2-dichloroethane, or aromatic solvents, e.g. benzene, toluene, xylene. Depending on the final viscosity to be achieved, the organic solvent is present in an amount of 0% to 20%.

[0093] In a specific embodiment, the emulsion is obtained by effective mixing as described above, preferably achieved by commonly used techniques such as a suitable high shear mixer at above 1000 rpm, such as 1500-2500 rpm, e.g. 2000 rpm, for at least 2 minutes, preferably 5-15 minutes, or a 3-roll mill with a gap size of 100 microns or less, preferably 40 microns or less, more preferably about 10 microns, at above 30 rpm, such as 50-500 rpm, e.g. 250 rpm.

[0094] It is also an object of the present invention to provide a 3D printed silicone structure using the composition of the present invention, wherein the silicone structure comprises a thioether group. In some embodiments, the 3D printed silicone structure comprises a repeat unit derived from MPMS.

[0095] In some embodiments, the 3D printed silicone structure is transparent.

[0096] As will be readily understood by those skilled in the art, 3D printed silicone structures obtained by layer-based methods include multiple layers, with a single layer having a layer thickness of, for example, 0.01 to 1 mm, while 3D printed silicone structures obtained by volumetric 3D methods do not have layers, since they are formed en masse.

[0097] 3D printed silicone according to the present invention can be manufactured by the process according to the present invention described above.

[0098] Another aspect of the invention includes a method for producing a cured composition, particularly a 3D printed silicone structure, comprising the steps of: a) Preparation of a 3D model of the semi-finished product; b) additive manufacturing of a semi-finished product from a 3D model of the semi-finished product using an additive manufacturing composition and an additive manufacturing device according to any of the embodiments described herein; c) curing the semi-finished product, thereby providing a cured composition.

[0099] It is understood that the semi-finished product is the product obtained directly by step b) before the curing step c). Typically, the 3D model of the semi-finished product is prepared as a CAD (Computer Aided Design) file or a 3D scan. The resulting CAD data can then be converted into a format suitable for or readable by the additive manufacturing device. The 3D model of the semi-finished product usually contains all the relevant information required for the additive manufacturing of the actual semi-finished product in step b). For example, the 3D model may contain information about the dimensions, structure, size, color, etc. of the semi-finished product. Furthermore, the 3D model may contain information about the orientation of the semi-finished product. In particular, the 3D model of the semi-finished product may contain information about the orientation of the actual semi-finished product relative to the additive manufacturing device or to certain components of the additive manufacturing device.

[0100] In some embodiments, the additive manufacturing apparatus comprises a radiation source for irradiating at least a portion of the additive manufacturing composition.

[0101] Preferably, the radiation source may be an LED lamp. In particular, the intensity of the LED lamp is 1 to 1000 mW / cm 2 , preferably 10 to 100 mW / cm 2 It is.

[0102] In a further embodiment, the additive manufacturing of step b) is carried out by photopolymerization, where the additive manufacturing is carried out by VAT photopolymerization, volumetric 3D printing, holographic laser 3D printing, or any other suitable method. In a preferred embodiment, the additive manufacturing is carried out by DLP or SLA VAT photopolymerization. In particular, the photopolymerization is carried out in a top-down orientation.

[0103] In another embodiment, the additive manufacturing apparatus comprises a chamber containing the additive manufacturing composition and a platform within the chamber that is moved in the z-direction during step b), such an additive manufacturing apparatus is suitable for use in a top-down or bottom-up orientation.

[0104] In a further embodiment, the 3D model of step a) is prepared in such a way that the stability of the semi-finished product is maximized. Stabilization, such as mechanical and positional stabilization, especially lateral stabilization, is important for 3D printed silicone, since the elastic and soft properties of silicone, in contrast to common 3D printed hard materials, lead to a high instability of the semi-finished product appearing during additive manufacturing.

[0105] For example, in some embodiments, the center of mass of the actual workpiece is determined in step a). A 3D model of the workpiece is prepared such that the distance between the determined center of mass of the workpiece and the platform is minimized. Thus, in these embodiments, the 3D model of the workpiece includes data on the orientation of the workpiece relative to the platform. Minimizing this distance significantly improves the stability of the workpiece. In particular, the lateral stability is improved, which is typically more affected by the use of a recoater. As a result, the need to print large support structures is reduced.

[0106] In a further embodiment, the 3D model of the workpiece of step a) is prepared such that the surface area of ​​the actual workpiece in contact with the platform and / or the projected surface area of ​​the workpiece to the build platform is maximized, thereby increasing the stability of the workpiece.

[0107] Alternatively or additionally, the stability of the semi-finished product may be increased by providing support structures, which may be larger than those typically used for rigid 3D printed polymers. Typically, these support structures may already be included in the 3D model of the semi-finished product. Such support structures are generally removed from the semi-finished product after additive manufacturing is completed. Thus, embodiments having support structures may include removal of the support structures before or after step c). Removal may be achieved by any suitable method, such as cutting, slicing, ripping, etc. in the swollen state.

[0108] In some embodiments, the additive manufacturing apparatus comprises a recoater or wiper, e.g. a blade. Furthermore, step b) of the method according to the invention may comprise the following steps: i) immersing the platform into the additive manufacturing composition at a predefined height to apply a layer of the additive manufacturing composition to the surface of the platform or the emerging semi-finished product; ii) moving the platform so that at least the applied layer of the additive manufacturing composition is above the additive manufacturing composition; iii) providing a film of the additive manufacturing composition of a predefined thickness by wiping off the applied layer of the additive manufacturing composition with a recoater; iv) irradiating the film to which the additive manufacturing composition has been applied with a radiation source; v) optionally, moving the platform in the z direction; vi) Optionally, repeating steps ii), iii), iv), and / or v).

[0109] In some embodiments, the method comprises steps i) through vi).

[0110] Typically, in step i), the predefined height is typically selected such that the platform is immersed in the additive manufacturing composition more than the height of the additive manufacturing layer. The height of the additive manufacturing layer is the height of the layer formed during step iv) and may preferably range from 5 to 1,000 μm. Preferably, the predefined height is selected such that the additive manufacturing composition covers the entire surface of the platform or the entire surface of the emerging semi-finished product. Thereby, the predefined height is influenced by the immersion speed of the platform, the material flow behavior and the surface tension. Alternatively or additionally, the predefined height may be selected such that the distance between the platform and the surface of the additive manufacturing composition in the chamber is at least between 1,000 and 50,000 μm.

[0111] In some exemplary embodiments, self-leveling of the applied film is performed after step ii) and before step iii) by providing a self-leveling time, preferably between 100 and 10,000 ms, that is sufficient for efficient self-leveling of the additive manufacturing composition.

[0112] In some embodiments, wiping can be done by mechanical wiping in a circular orbit or linear motion. Generally, wiping removes excess material, leaving only the thickness of the additive manufacturing layer of raw material above the emerging object.

[0113] It will be readily understood by those skilled in the art that the emerging product surface refers to the most recently produced layer, which is then covered with additional layers by repeating steps ii) to iv).

[0114] In step iv), the z-direction refers to the printing direction. The z-direction is therefore the direction across the manufactured layers of the workpiece. For example, if the additive manufacturing is performed in a top-down orientation, the platform is moved downwards, i.e. towards the bottom of the chamber.

[0115] The movement in the z-direction is carried out at least a monolayer thick, preferably 5-1000 μm.

[0116] In a further embodiment, the distance from the platform to the radiation source is adjusted after step ii) and before irradiating the applied film.

[0117] In some embodiments, the radiation source is moved to a predefined focal distance prior to step iv), for example the predefined focal distance may be between 10 and 100 cm, preferably between 15 and 30 cm.

[0118] In a further embodiment, the irradiation of the applied film in step iv) is carried out for more than 50 ms, in particular more than 150 ms. Preferably, the applied film is irradiated for 100 to 5,000 ms, more preferably for 150 to 4,000 ms.

[0119] In some embodiments, the recoater is operated at a speed of 50 to 3000 strokes / sec. The speed steps / sec refers to the number of strokes per second of the stepper motor driving the recoater. This value not only allows for fast printing speeds, but has been found to have no significant effect on the lateral stability of the emerging workpiece.

[0120] In some embodiments, the additive manufacturing apparatus comprises a sealable housing. Preferably, the housing is hermetically sealable. Typically, the housing is oxygen-free. Preferably, the sealed housing is essentially filled or pressurized with only an inert gas, such as nitrogen or argon. Utilizing an inert atmosphere increases the yield of the polymerization reaction, since oxygen, if present, may react with and / or quench any of the radical species formed during the thiol-ene reaction.

[0121] In a further embodiment, the additive manufacturing composition is maintained at a predetermined temperature during step b) of the method according to the invention, thereby adjusting the viscosity of the additive manufacturing composition. * It has been observed that the viscosity does not exceed 0.5° C. The higher the viscosity, the slower the self-leveling to provide a smooth surface before irradiation can take place. Therefore, if the viscosity of the additive manufacturing composition is too high, its temperature can be increased. In some embodiments, the predefined temperature can be in the range of 0 to 250° C.

[0122] In some embodiments, the irradiation intensity, typically measured at the surface of the additive manufacturing composition and / or applied film irradiated by the radiation source, is reduced by 0-99%, preferably 50-90%, of its original value. The use of the additive manufacturing composition described herein has the advantage of its high reactivity in the polymerization reaction. Therefore, the intensity of the radiation source can be reduced, which significantly reduces overexposure due to scattering and therefore improves the printing resolution.

[0123] For example, in some embodiments, the intensity of the irradiation is reduced by digitally changing the grayscale of the projector and / or by providing a physical light filter between the radiation source and the additive manufacturing composition.

[0124] In a further embodiment, in step c), the curing comprises pre-cleaning the semi-finished product. Pre-cleaning can typically be carried out by pre-cleaning the semi-finished product with a solvent, for example an alkane, such as cyclohexane, n-hexane, pentane, etc., to remove residues of the additive manufacturing composition. Additionally or alternatively, the semi-finished product is then swollen, preferably in the same or alternatively another solvent, by rinsing the semi-finished product or by immersing the semi-finished product in this other solvent. As an alternative to the preferred alkane solvent, an alcohol, such as i-propanol, n-propanol or ethanol, may be used to swell the semi-finished product. In a preferred embodiment, stirring, agitation, vibration, ultrasonic treatment and / or heating can be performed to improve the swelling of the product. Additionally or alternatively, the semi-finished product is post-cured under UV irradiation, preferably for 10 seconds to 30 minutes. Post-curing is preferably carried out in the swollen state of the semi-finished product. Post-curing ensures complete polymerization of the components of the additive manufacturing composition. It is particularly advantageous to combine swelling of the semi-finished product with subsequent post-curing under UV irradiation, since swelling leads to higher light transmission and thus enhances the mechanical properties of the cured composition. Additionally or alternatively, the semi-finished product can be further cured at room temperature or in an oven at temperatures between 20 and 200° C. Preferably, the step-wise curing consists of the following steps in the following order: pre-cleaning the semi-finished product, swelling the semi-finished product, post-curing the semi-finished product with UV radiation, and curing at room temperature or in an oven.

[0125] It will be understood that the examples are merely selective illustrations of the present invention and that various modifications may be made without departing from the spirit and scope of the present invention. EXAMPLES

[0126] method: Preparation of test samples: All components of the composition were mixed using a planetary centrifugal mixer (THINKY mixer, ARE-250) at 2000 rpm for 3 minutes. The mixture was then degassed at 2200 rpm for 3 minutes. 10 mg of the composition was poured between glass slides using a 0.4 mm spacer. The system was then exposed to UV light (OmniCure® S1000) for a specified time (e.g., 300 seconds) with an appropriate distance between the lamp and the sample (e.g., 10 cm) to polymerize. After polymerization, the resulting silicone film was removed and the samples were punched out for testing.

[0127] Tensile testing: Tensile testing was performed using a Shimadzu AGS-X tensile machine equipped with a 100N force load cell with a preload setting of 0.01N.

[0128] Transparency Measurements: Transparency measurements of silicone parts of defined thickness were performed using a JASCO V-660 UV-VIS spectrophotometer (187-900 nm) measuring total in-line absorption.

[0129] UV / VIS measurements: UV-VIS measurements were performed in absorption mode on a JASCO V-630 UV-VIS spectrophotometer (330-800 nm). Samples were tested in quartz cuvettes at 0.01 M in appropriate solvents (e.g., acetone, toluene, etc.).

[0130] DLP printing: An Octave Light R1 (405 nm) was used in a top-down configuration with a building volume of 32.4 × 57.6 × 120.0 mm. Projector brightness was adjusted digitally or using physical filters.

[0131] Working Example Example 1: Stress-strain relationship of additive manufacturing compositions with different Shore hardness The mechanical properties of the following silicones were tested: Ecoflex® 00-20 Part A, PlatSil® 73-15 Part A, Dragon Skin™ 30 Part A, Sorta-Clear® 40, Sylgard® 184, and LS-8941 Part A. Figure 2 shows a UV-cured composition of the present invention (red) compared to a commercially available addition-cured silicone (black). The data shows that the Young's modulus of the UV-cured composition of the present invention can be precisely tuned to match their commercially available counterparts.

[0132] Example 2: Stress-strain relationship of additive manufacturing compositions using different crosslinker concentrations Figure 3 shows tensile testing of DragonSkin™ 30 using different crosslinker concentrations (0.50-1.25 wt%). It shows that lower crosslinker concentrations resulted in higher strains and lower break stresses. Increasing the crosslinker concentration resulted in a stiffening effect until a maximum value was reached. At higher concentrations the maximum stress is reduced.

[0133] Example 3: Tailoring the mechanical properties of additive manufacturing compositions using polysiloxane mixtures Polysiloxane PlatSil® 73-15 was polymerized alone or as a 9:1 mixture with polysiloxane Q resin using MPMS (3.25%). Figure 4 shows that the addition of Q resin to PlatSil® 73-15 was able to enhance or improve the stiffness of the cured product. The same stiffness effect was observed when mixtures with ratios of 1 to 9 were used.

[0134] Example 4: Optical properties of the additive manufacturing composition Six silicone objects (1 mm thick) with different transmission properties were prepared by photopolymerizing alkenyl-derivatized polysiloxanes Ecoflex® 00-20, PlatSil® 73-15, DragoSkin™ 30, Sorta-Clear® 40, Sylgard® 184, and LS-8941 with MPMS (0.5%, 3.5%, 0.8%, 1.5%, 4.5%, and 6.5%, respectively), 0.5% 1-hydroxycyclohexyl phenyl ketone, and 0.05% bis(4-methoxybenzoyl)diethylgermanium, and polymerized by exposure to UV light for 30 seconds according to the present invention. Figure 5b shows the in-line transmission of the six silicone objects shown in Figure 5a (from left to right: Ecoflex® 00-20, PlatSil® 73-15, DragoSkin™ 30, Sorta-Clear® 40, Sylgard® 184, LS-8941). These figures show that the silicone objects have different absorption in the visible light range (380-720 nm). Sylgard® 184 and LS-8941 are the most transparent with a transmission of about 90%, while PlatSil® 73-15 and Sorta-Clear 40 are translucent with a transmission of about 50%.

Claims

1. 1. An additive manufacturing composition comprising at least one alkenyl-derivatized polysiloxane and a compound of formula (I): R 1 (R) 2 SiO((R 3 R 4 )SiO) x Si(R) 2 R 2 (I)、 wherein R is independently C(1-12)alkyl; R 1 , R 2 , R 3 , R 4 is independently C(1-12)alkyl, or mercapto-C(1-12)alkyl; x is 1 or more; However, R 1 , R 2 , R 3 , R 4 At least one of the groups is mercapto-C(1-12)alkyl. wherein the alkenyl-derivatized polysiloxane and the mercapto-derivatized polysiloxane crosslinker form a stable emulsion; the alkenyl-derivatized polysiloxane forms a continuous phase of the emulsion and the mercapto-derivatized polysiloxane crosslinker forms a discontinuous phase of the emulsion, the discontinuous phase being present as droplets having a diameter of 100 micrometers or less; Additive manufacturing composition.

2. In the formula, R, R 1 , R 2 , R 3 , R 4 The additive manufacturing composition of claim 1 , wherein each is independently methyl.

3. The composition for additive manufacturing according to claim 1 or 2, wherein x is 1 to 100.

4. The additive manufacturing composition according to any one of claims 1 to 3, further comprising at least one photoinitiator.

5. The composition for additive manufacturing according to any one of claims 1 to 4, which is curable by UV-visible light.

6. The additive manufacturing composition according to any one of claims 1 to 5, wherein the at least one alkenyl-derivatized polysiloxane is one polysiloxane or a mixture of two or more polysiloxanes.

7. 7. The additive manufacturing composition according to claim 1, wherein the at least one alkenyl-derivatized polysiloxane is selected from an alkenyl-derivatized poly(dimethylsiloxane), an alkenyl-derivatized poly(diphenylsiloxane), an alkenyl-derivatized poly(methylphenylsiloxane), an alkenyl-derivatized poly(dimethyldiphenylsiloxane).

8. 8. The additive manufacturing composition of claim 7, wherein the at least one alkenyl derivatized polysiloxane is selected from Ecoflex® 00-15, Ecoflex® 00-20, Dragon Skin™ 30, Sorta-Clear® 40 (Kaupo, Germany), PlatSil® 73-15 (Mouldlife, UK), Sylgard® 184 (Sigma-Aldrich, Switzerland), Zhermack 00 Zhermack 08, Zhermack 13 (Zermack, Germany), LS-8941 (Nucil, USA), KE-2061 (Shin-Etsu Chemical Co., Japan), Vinyl Q Resin Dispersion in Vinyl-Terminated Polydimethylsiloxane (Gelest, Germany).

9. The composition for additive manufacturing according to any one of claims 1 to 8, wherein the alkenyl group in the at least one alkenyl-derivatized polysiloxane is a vinyl group, an allyl group, a butenyl group, or a pentenyl group.

10. The composition for additive manufacturing according to any one of claims 1 to 9, wherein the mercapto-C(1-12)alkyl is mercapto-C(1-6)alkyl.

11. The additive manufacturing composition according to claim 10, wherein the mercapto-C(1-12)alkyl is mercapto-methyl, mercapto-ethyl, mercapto-butyl, mercapto-propyl.

12. At least one mercapto-derivatized polysiloxane crosslinker is a mercapto-derivatized polysiloxane crosslinker of formula (I), where R, R 1 , R 2 , R 4 is independently C(1-12)alkyl; R 3 The additive manufacturing composition according to any one of claims 1 to 11, wherein is independently mercapto-C(1-12)alkyl and x is 1 or more.

13. In the formula, R, R 1 , R 2 , R 4 The additive manufacturing composition of claim 12 , wherein is independently methyl.

14. The composition for additive manufacturing according to claim 12 or 13, wherein x is 1 to 10,000,000.

15. At least one mercapto-derivatized polysiloxane crosslinker is a mercapto-derivatized polysiloxane crosslinker of formula (I), where R, R 1 , R 2 is independently C(1-12)alkyl; R 3 , R 4 The additive manufacturing composition according to any one of claims 1 to 11, wherein is independently mercapto-C(1-12)alkyl and x is 1 or more.

16. The composition for additive manufacturing according to claim 15, wherein x is 1 to 10,000,000.

17. The composition for additive manufacturing according to any one of claims 1 to 16, wherein x is 1 to 100,000.

18. 18. The additive manufacturing composition according to any one of claims 1 to 17, wherein at least one mercapto-derivatized polysiloxane is a (mercaptopropyl)methylsiloxane homopolymer having one or more mercaptopropyl units.

19. 19. The additive manufacturing composition of claim 18, wherein the at least one mercapto-derivatized polysiloxane is a (mercaptopropyl)methylsiloxane homopolymer having from 2 to 100,000 mercaptopropyl units.

20. 100 Pa * The composition for additive manufacturing according to any one of claims 1 to 19, having a viscosity of 0.1 s or less.

21. Use of the additive manufacturing composition according to any one of claims 1 to 20 for forming three-dimensional objects using stereolithography, material-jetting, drop-on-demand, volumetric 3D printing, material extrusion.

22. 22. The use according to claim 21, wherein the three-dimensional object is formed using Laser-Based Stereolithography (SLA) or Digital Light Processing (DLP).

23. 23. The use according to claim 22, wherein the three-dimensional object is formed using DLP in a top-down orientation.

24. 21. A method for producing an additive manufacturing composition according to any one of claims 1 to 20, comprising combining at least one alkenyl-derivatized polysiloxane and at least one mercapto-derivatized polysiloxane crosslinker of formula (I) under shear to obtain a composition in the form of an emulsion.

25. 25. The method of claim 24, wherein the at least one alkenyl-derivatized polysiloxane and the at least one mercapto-derivatized polysiloxane crosslinker of formula (I) are combined under shear to provide a composition in the form of a stable emulsion.

26. A cured product of the composition for layered manufacturing according to any one of claims 1 to 20.

27. 27. The cured product of claim 26 having a transparency of >80%.

28. 1. A method for producing a cured composition, particularly 3D printed silicone, comprising: a) preparation of a 3D model of the semi-finished product; b) additive manufacturing of a semi-finished product according to a 3D model of the semi-finished product using a composition for additive manufacturing according to any one of claims 1 to 20 and an additive manufacturing device; c) curing the semi-finished product, thereby providing a cured composition. The method includes:

29. 29. The method of claim 28, wherein the additive manufacturing apparatus comprises a radiation source for irradiating at least a portion of the additive manufacturing composition.

30. 30. The method of claim 29, wherein in step b) additive manufacturing is performed by photopolymerization, the additive manufacturing being performed by VAT photopolymerization, volumetric 3D printing, or holographic laser 3D printing.

31. 31. The method according to any one of claims 28 to 30, wherein the additive manufacturing apparatus comprises a chamber containing the additive manufacturing composition and a platform within the chamber which is moved in the z-direction during step b).

32. 32. The method of claim 31, wherein in step a) the centre of mass of the workpiece is determined and a 3D model of the workpiece is prepared such that the distance between the centre of mass of the workpiece and the platform is minimized.

33. 33. The method according to any one of claims 31 to 32, wherein in step a) the 3D model of the workpiece is prepared such that a surface area of ​​the workpiece in contact with the platform and / or a projected surface area of ​​the workpiece to the build platform is maximized.

34. The additive manufacturing apparatus includes a recoater, and step b) includes: i) immersing a platform at a predefined height into the additive manufacturing composition; ii) moving the platform so that at least the applied layer of the additive manufacturing composition is above the additive manufacturing composition; iii) wiping off the applied layer of the additive manufacturing composition with a recoater to provide a film of the additive manufacturing composition of a predefined thickness; iv) irradiating the film to which the additive manufacturing composition has been applied with a radiation source; v) optionally moving the platform in the z direction; 34. The method of any one of claims 29 to 33, comprising optionally repeating steps ii), iii), iv), and / or v).

35. 35. The method of claim 34, wherein the radiation source is moved to a predefined focal distance before step iv).

36. 36. The method according to claim 34 or 35, wherein in step iv) the irradiation of the applied film is carried out for more than 50 ms.

37. A method according to any one of claims 28 to 36, wherein the additive manufacturing apparatus comprises a sealable housing, and the housing is oxygen-free.

38. 38. The method of claim 37, wherein the housing is filled with an inert gas or is pressurized.

39. The method according to any one of claims 28 to 38, wherein the additive manufacturing composition is maintained at a predefined printing temperature during step b).

40. 40. The method according to any one of claims 29 to 39, wherein the intensity of the irradiation is reduced by 0 to 99%.

41. 41. The method of claim 40, wherein the intensity is reduced by digitally modifying the greyscale of the projector and / or by providing a physical filter between the radiation source and the additive manufacturing composition.

42. The method according to any one of claims 28 to 41, wherein in step c) the curing comprises pre-cleaning the semi-finished product, and / or post-curing under UV irradiation, and / or swelling the semi-finished product with a solvent, and / or drying the semi-finished product at the curing temperature.

43. 30. A hardened composition produced by the method of claim 28.