Cellulose filler, method for producing the same, and synthetic resin structure

Abstract

To provide a cellulose filler having high productivity, from which a synthetic resin structure having less variation in strength distribution can be made.SOLUTION: A cellulose filler comprises a solvent-spun cellulose fiber including a main fiber having a mean fiber length of 0.1 to 1 mm and a fibrillated fiber generated from the main fiber.SELECTED DRAWING: Figure 1

Description

Technical Field

[0001] The present invention relates to a cellulose filler for enhancing the strength of a synthetic resin structure, a method for producing the cellulose filler, and a synthetic resin structure in which the cellulose filler is dispersed.

Background Art

[0002] Efforts have been made to enhance the strength of synthetic resin structures by incorporating fillers into the synthetic resin structures. Among them, fillers formed from plant-derived cellulose fibers have attracted attention because they are non-plastic materials and have abundant raw materials.

[0003] However, it is well known that fillers formed from plant-derived cellulose fibers have poor dispersibility in synthetic resins, and as a result, it is difficult to enhance the strength of synthetic resin structures.

[0004] For example, in paragraph

[0002] of Patent Document 1, it is pointed out that "in recent years, various proposals have been made to use cellulose nanofibers (CNF) as a reinforcing material for resins. However, cellulose nanofibers irreversibly aggregate due to intermolecular hydrogen bonds derived from the hydroxyl groups of polysaccharides. Therefore, even when cellulose nanofibers are used as a reinforcing material for resins, the reinforcing effect of the resin is not sufficiently exerted due to the poor dispersibility of cellulose nanofibers in the resin." Therefore, in this Patent Document 1, as described in claim 1 thereof, "a fibrous cellulose composite resin comprising microfibrillated cellulose having an average fiber width of 0.1 μm or more, a synthetic resin, and maleic anhydride-modified polypropylene" is produced, and this fibrous cellulose composite resin is incorporated into a synthetic resin structure to thereby enhance the strength of the synthetic resin structure.

[0005] Furthermore, paragraph

[0003] of Patent Document 2 states, "Currently, there are proposals to use cellulose nanofibers obtained by micronizing plant fibers as a reinforcing material for resins. However, when cellulose nanofibers are used as a resin reinforcing material, the cellulose nanofibers irreversibly aggregate due to intermolecular hydrogen bonds derived from the hydroxyl groups of polysaccharides. Also, even if one tries to force the mixing with the resin, the fibers break, making it impossible to construct a sufficient three-dimensional network in the resin. Therefore, even when cellulose nanofibers are used as a reinforcing material, the dispersibility of the cellulose nanofibers in the resin is poor, and a sufficient three-dimensional network cannot be constructed. As a result, there is a problem that the reinforcing effect of the resin is not fully exhibited." Therefore, as described in claim 1 of this Patent Document 2, a fibrous cellulose composite resin is produced by "a method for producing a fibrous cellulose composite resin, characterized in that raw fibers are defibrated to a range in which the average fiber width remains 0.1 μm or more to obtain a dispersion of microfiber cellulose, the dispersion of microfiber cellulose is dried, and a resin is added and kneaded, wherein prior to drying the dispersion of microfiber cellulose, the dispersion of microfiber cellulose is dehydrated until its water content is 93% by mass or less," and this fibrous cellulose composite resin is mixed into a synthetic resin structure to increase the strength of the synthetic resin structure.

[0006] Furthermore, paragraph

[0002] of Patent Document 3 states that "It has been proposed to use fibrillated lyocell as a reinforcing material for various materials. However, the applicants have found that fibrillated lyocell alone does not function well as a reinforcing material. Fibrillated lyocell does not disperse properly and therefore does not provide the necessary physical properties such as toughness. Fibrillated lyocell is prone to aggregation or bundling. For this reason, it is difficult to use fibrillated lyocell as a reinforcing material or a filter material. This is because it bundles together and does not disperse throughout the material." Therefore, Patent Document 3 attempts to enhance the dispersion effect on synthetic resin structures by "a fibrillated blend obtained by fibrillating a mixture of cellulose pulp having a degree of polymerization of 200 to 1000 as measured by ASTM Test 1795-96 and lyocell, wherein at least a portion of the lyocell fibers in the fibrillated blend have a length of 3 to 12 mm," as described in Claim 1. In other words, since lyocell alone cannot improve dispersibility, the cellulose pulp mentioned above is blended in to enhance dispersibility. [Prior art documents] [Patent Documents]

[0007] [Patent Document 1] Japanese Patent Publication No. 2020-70379 [Patent Document 2] Japanese Patent Publication No. 2020-19874 [Patent Document 3] Patent No. 5551768 specification [Overview of the Initiative] [Problems that the invention aims to solve]

[0008] In the above-mentioned Patent Documents 1 and 2, a fibrous cellulose composite synthetic resin is created, for example, in the form of pellets, by including plant-derived microfiber cellulose, a synthetic resin, and maleic anhydride-modified polypropylene, and this fibrous cellulose composite synthetic resin is mixed into a synthetic resin structure. By forming the microfiber cellulose into pellets using synthetic resin in this way, it is indeed possible to improve the dispersibility of the microfiber cellulose into the synthetic resin structure because it does not aggregate.

[0009] However, producing, for example, pelletized fibrous cellulose composite synthetic resins containing plant-derived microfiber cellulose, synthetic resin, and maleic anhydride-modified polypropylene requires separate, dedicated equipment, resulting in low productivity. Moreover, depending on the type of synthetic resin used in the pelletized fibrous cellulose composite synthetic resin, it may modify the synthetic resin structure being mixed in, potentially leading to variations in strength distribution.

[0010] Furthermore, Patent Document 3 states that since lyocell alone cannot improve dispersibility, it attempts to improve dispersibility by blending it with the aforementioned cellulose pulp. However, this requires new equipment to blend plant-derived cellulose pulp with lyocell, resulting in low productivity. Moreover, uniformly mixing plant-derived cellulose pulp and lyocell is extremely difficult, which may lead to variations in the strength distribution of the synthetic resin structure.

[0011] Therefore, the present invention aims to provide a cellulose filler that is highly productive and less prone to variations in strength distribution in synthetic resin structures using the cellulose filler. [Means for solving the problem]

[0012] To achieve the above-mentioned objective, the cellulose filler of the present invention consists of solvent-spun cellulose fibers. Solvent-spun cellulose fibers are lyocell, Multiple main fibers with an average fiber length of 0.1 to 1 mm, and multiple fibrillated fibers generated from the outer periphery of the main fibers by beating. It is composed of the above, with the average fiber diameter of the main fibers being 5 to 15 μm and the average fiber diameter of the fibrillated fibers being 0.01 to 3 μm. It is a cellulose filler.

[0013] Furthermore, the present invention provides a method for producing cellulose filler, which involves beating solvent-spun cellulose fibers in water, drying the solvent-spun cellulose fibers after beating, and then dry grinding them using a dry grinding means to form the aforementioned main fibers and fibrillated fibers.

[0014] Furthermore, the synthetic resin structure of the present invention is one in which the cellulose filler of the present invention is dispersed in the synthetic resin.

Advantages of the Invention

[0015] The cellulose filler of the present invention is composed of solvent-spun cellulose fibers, Solvent-spun cellulose fibers are lyocell, a plurality of main fibers with an average fiber length of 0.1 to 1 mm and a plurality of fibrillated fibers generated by beating from the outer peripheral portion of the main fibers coexist The average fiber diameter of the main fibers is 5 to 15 μm, and the average fiber diameter of the fibrillated fibers is 0.01 to 3 μm. as the cellulose filler. That is, the cellulose filler of the present invention is the first in the world to practically use a non-aggregating cellulose filler even with only solvent-spun cellulose fibers.

[0016] The main fibers and fibrillated fibers constituting the cellulose filler of the present invention will be uniformly dispersed when mixed into the synthetic resin constituting the synthetic resin structure and subjected to a kneading process. The cellulose filler thus obtained can be easily dispersed in the synthetic resin constituting the synthetic resin structure, particularly when manufacturing a polypropylene (PP) synthetic resin structure as an example of a thermoplastic synthetic resin, and moreover, has good dispersibility in the synthetic resin. Therefore, the productivity is high, the variation in the strength distribution in the synthetic resin structure is unlikely to occur, and the strength of the synthetic resin structure can be increased.

[0017] Also, generally, in PP or the like containing CNF or natural pulp, brown coloring derived from components other than cellulose such as lignin is observed due to heating in the kneading process or molding process. On the other hand, in the present invention, since solvent-spun cellulose fibers with high cellulose purity are used, no coloring is observed even when the cellulose filler is blended. Therefore, there is a great advantage that the need for color materials and the like, which is required in the kneading process etc. for whitening, is eliminated.

Brief Description of the Drawings

[0018] [Figure 1]An electron micrograph showing the cellulose filler according to an embodiment of the present invention. [Figure 2] It is a diagram showing the change in bending strength when applied to polypropylene.

Embodiments for Carrying Out the Invention

[0019] The cellulose filler of the present invention is a cellulose filler in which there are a plurality of main fibers made of solvent-spun cellulose fibers and having an average fiber length of 0.1 to 1 mm, and a plurality of fibrillated fibers generated by beating from the outer peripheral portion of the main fibers.

[0020] In the cellulose filler of the present invention described above, preferably, the average fiber diameter of the main fibers is further set to 5 to 15 μm, and the average fiber diameter of the fibrillated fibers is set to 0.01 to 3 μm.

[0021] Further, the method for producing the cellulose filler of the present invention is to beat the solvent-spun cellulose fibers in water, and then dry the solvent-spun cellulose fibers after the beating treatment, and dry-grind them by dry-grinding means to form the main fibers and fibrillated fibers described above.

[0022] Furthermore, the synthetic resin structure of the present invention is one in which the cellulose filler of the present invention is dispersed in a synthetic resin.

[0023] The cellulose filler produced by the production method of the present invention described above has the total number of a plurality of fibrillated fibers being larger than the total number of a plurality of main fibers.

[0024] Hereinafter, embodiments of the cellulose filler of the present invention, its production method, and the synthetic resin structure will be described.

[0025] (Preparation of Raw Material Fibers) In the present embodiment, the same solvent-spun cellulose fibers as those described as lyocell in paragraph

[0019] of Patent Document 3 above are used as the starting material and beaten in water. Beating methods can include beaters, high-pressure homogenizers, high-pressure homogenization devices, grinders, refiners, and the like. In particular, it is preferable to use a refiner because it can efficiently apply shear force to the raw fibers and promote defibration.

[0026] Next, the beaten solvent-spun cellulose fibers dispersed in water are dehydrated on a suspension wire, dried, and then wound up.

[0027] (Dry grinding process) Next, the rolled-up sheet is dry-crushed. For grinding, cutter mills, turbo mills, ball mills, etc., can be used. In particular, it is preferable to use a turbo mill because it can process the sheet continuously and efficiently.

[0028] Figure 1 is an electron microscope image showing a cellulose filler according to one embodiment of the present invention. As shown in Figure 1, the material consists of multiple main fibers 1 made of solvent-spun cellulose fibers with an average fiber length of 0.1 to 1 mm, and multiple fibrillated fibers 2 generated from the outer periphery of the main fibers 1, all of which are mixed together.

[0029] By mixing the main fiber 1 and fibrillated fiber 2, which constitute this cellulose filler, into a synthetic resin and performing a kneading process, a uniformly dispersed synthetic resin structure can be obtained. Therefore, productivity is high, variations in the strength distribution within the synthetic resin structure are less likely to occur, and the strength of the synthetic resin structure can be increased.

[0030] (Morphology of the main fiber) The reason why the average fiber diameter of the main fiber 1 is preferably set to 5 to 15 μm is as follows: In other words, when solvent-spun cellulose fibers are used as the starting material, if the average fiber diameter is to be less than 5 μm, the viscosity of the resin becomes too high when mixed with the synthetic resin, which causes aggregation of cellulose fillers in the synthetic resin structure. Furthermore, if the average fiber diameter exceeds 15 μm, the fiber diameter becomes excessive when dispersed in synthetic resin, which can cause variations in the strength distribution within the synthetic resin structure.

[0031] (Formation of fibrillated fibers) The reason why the average fiber diameter of the fibrillated fiber 2 is preferably set to 0.01 to 3 μm is as follows: When the average fiber diameter of fibrillated fiber 2 is less than 0.01 μm, the surface area of ​​the fiber becomes large, causing aggregation due to hydrogen bonding of the hydroxyl groups of cellulose. This is similar to the irreversible aggregation of cellulose nanofibers (CNF) as described above. Furthermore, if the average fiber diameter of the fibrillated fibers 2 exceeds 3 μm, the fibers are too large, making it impossible to strengthen the bonding force between the fibrillated fibers 2, and thus the reinforcing effect of the synthetic resin structure cannot be expected.

[0032] Furthermore, the total number of multiple fibrillated fibers 2 is greater than the total number of multiple main fibers 1. Furthermore, the number of main fibers 1 and fibrillated fibers 2 can be easily determined by imaging with an electron microscope.

[0033] In this embodiment, the key features are the use of solvent-spun cellulose fibers as the starting material and the control of the length of the main fiber 1 after pulverization to an average fiber length of 0.1 to 1 mm. By controlling the average fiber length within this range, while it was difficult to avoid aggregation when using solvent-spun cellulose fibers alone as described in Patent Document 3, in this embodiment, the main fibers 1, the fibrillated fibers 2, and the main fibers 1 and fibrillated fibers 2 do not aggregate with each other and can be dispersed homogeneously. Then, by mixing and kneading the aforementioned main fiber 1 and fibrillated fiber 2 into a synthetic resin, a synthetic resin structure can be obtained in which the main fiber 1 and fibrillated fiber 2 are uniformly dispersed.

[0034] (synthetic resin structure) The cellulose filler obtained in this way can be easily dispersed together with a compatibilizer within the synthetic resin constituting the synthetic resin structure during the manufacturing of the synthetic resin structure, and moreover, it exhibits good dispersibility within the synthetic resin. Therefore, productivity is high, variations in the strength distribution within the synthetic resin structure are less likely to occur, and as a result, the overall strength of the synthetic resin structure can be increased.

[0035] Examples of synthetic resins used in synthetic resin structures include thermoplastic resins such as high-density polyethylene (HDPE), medium-density polyethylene (MDPE), low-density polyethylene (LDPE), polypropylene, polyvinyl chloride (PVC), polyvinylidene chloride, polystyrene (PS), polyvinyl acetate (PVAc), polyurethane (PUR), fluororesin (polytetrafluoroethylene, PTFE), ABS resin (acrylonitrile butadiene styrene resin), AS resin, and acrylic resin (PMMA). Examples of thermosetting resins include phenolic resin (PF), epoxy resin (EP), melamine resin (MF), urea synthetic resin (urea resin, UF), unsaturated polyester resin (UP), and polyurethane (PUR).

[0036] Thus, in this embodiment, a cellulose filler that does not aggregate even when solvent-spun cellulose fibers are used alone has been put into practical use for the first time in the world. In other words, conventionally, it was considered difficult to increase the strength of synthetic resin structures containing fillers when their length was short. However, if solvent-spun cellulose fibers are uniformly present in the synthetic resin, it has become possible to provide a product that is sufficiently practical even if the filler is short.

[0037] Examples of the synthetic resin structures mentioned above include the structural components of automobiles and the structural components of electronic devices. The cellulose filler in this embodiment can contribute to increasing the strength of these structures, and by enabling thinner designs due to increased strength, it can also contribute to reducing the amount of plastic used.

[0038] (Mixing process) The cellulose filler obtained in this way is kneaded with a synthetic resin to form a hybrid product. For the mixing process of thermoplastic synthetic resins, one or more types of equipment can be selected and used from, for example, single-screw or multi-screw mixers, mixing rolls, kneaders, roll mills, Banbury mixers, screw presses, dispersers, etc. However, among these, it is preferable to use a multi-screw mixer with two or more shafts. The mixing process should be carried out at a temperature above the glass transition temperature of the synthetic resin.

[0039] Furthermore, a compatibilizer may be used to improve the dispersibility of the cellulose filler in the synthetic resin and the compatibility between the cellulose filler and the synthetic resin when it is incorporated into a synthetic resin structure. Various compatibilizers can be selected, generally including polar monomer copolymers and graft-modified polymers, but the type is not limited. Maleic anhydride-modified PP (MAPP) and maleic anhydride-modified PE (MAPE) are particularly effective as cellulose fillers.

[0040] Furthermore, the hydroxyl groups of the cellulose filler may be modified. Modification of hydroxyl groups can be performed using various methods, and these are not limited to those mentioned above. Examples include acetylation, treatment with various silane coupling agents, and polymer graft polymerization.

[0041] Furthermore, since cellulose filler is a fibrous, dried material, the following steps can also be taken as part of the resin molding method. In other words, cellulose filler and thermoplastic fibers such as PP are mixed in any proportion, and then formed into a sheet using a nonwoven fabric formation technique, such as the airlaid method. This ensures that the cellulose filler is homogeneously dispersed. By heat-molding this sheet, a molded body of any shape can be obtained.

[0042] (Molding process) The cellulose filler and synthetic resin (compound) has dispersed cellulose filler and also exhibits excellent moldability. The size, thickness, and shape of the molded product are not particularly limited and can be, for example, in the form of a sheet, pellet, or powder. The temperature during the molding process of the thermoplastic synthetic resin should be above the glass transition temperature of the synthetic resin.

[0043] For the molding process, one or more types can be selected and used from, for example, injection molding machines, blow molding machines, hollow molding machines, blow molding machines, compression molding machines, extrusion molding machines, vacuum molding machines, and pressure molding machines.

[0044] This molding process can be carried out immediately after the kneading process, or it can be performed by first cooling the kneaded material, then crushing it into chips using a crusher or the like, and finally feeding these chips into a molding machine such as an extruder or injection molder. [Examples]

[0045] Cellulose filler and structures using cellulose filler according to the present invention were fabricated and their properties were investigated.

[0046] The preparation of cellulose fillers and the measurement of their properties were carried out using the following methods.

[0047] (Cellulose filler) Solvent-spun cellulose fibers with the fiber lengths and diameters listed in Table 1 were used as starting materials. These were beaten using a double disc refiner (DDR), formed into sheets by papermaking, coarsely ground with a cutter mill, and then ground with a turbo mill to obtain cellulose filler.

[0048] (Average fiber length) The obtained cellulose filler was dispersed in water, and the length-weighted average fiber length was measured using an L&W Fiber Tester Plus fiber shape analyzer (manufactured by Lorenzen). This measured value was defined as the average fiber length.

[0049] (Average fiber diameter) The obtained cellulose filler was photographed with an electron microscope, and the diameters of 300 randomly selected main fibers and 300 fibrillated fibers were measured. The average of the measured values ​​was then calculated. This average value was defined as the average fiber diameter.

[0050] (Other examples and comparative examples) Cellulose fillers were prepared by modifying the average fiber diameter, average fiber length, and average fiber length of the fibrillated main fiber, and these were used as samples for Examples 1 to 5 and Comparative Examples 1 to 7. The binding, dispersion, and aggregation states of each sample in each example and comparative example were assessed, and the results are shown in Table 1.

[0051] (Presence or absence of aggregation) 100 ml of water was measured into a glass beaker, 0.5 g of cellulose filler was added, and the mixture was stirred with a glass rod. The presence or absence of flocs (aggregated clumps) in the water was then visually observed to determine whether or not aggregation occurred.

[0052] (Fabrication of synthetic resin structures) Synthetic resin structures were prepared from the cellulose fillers obtained in the examples and comparative examples using the following methods. 90 parts by mass of polypropylene and 10 parts by mass of cellulose filler obtained in the examples and comparative examples were kneaded in a twin-screw kneader at a temperature of 170°C and a screw rotation speed of 400 rpm, and a dumbbell-shaped test sample was prepared in accordance with JIS K7171:2016 by injection molding at a temperature of 180°C. Comparative Example 1 is a sample that does not contain cellulose filler, and the sample was prepared using only polypropylene without any kneading treatment, via an injection molding machine.

[0053] The properties of the dumbbell-shaped test samples of the fabricated synthetic resin structure were measured using the following method.

[0054] (Presence or absence of aggregation in synthetic resin structures) The central part of the above dumbbell-shaped test sample was cut out, and a 5mm x 5mm area was imaged using a high-resolution 3D X-ray microscope (manufactured by Rigaku Corporation) to check for the presence or absence of flocs (aggregates) with a diameter of 0.2mm or more.

[0055] (Bending strength) The bending strength was measured in accordance with JIS K7171:2016 and expressed as a ratio, with the bending strength of polypropylene alone (without cellulose filler) set to 100.

[0056] As described above, the cellulose filler and synthetic resin structures were fabricated and evaluated, and the results are shown in Table 1.

[0057] [Table 1]

[0058] As shown in the results of Examples 1 to 5 in Table 1, it can be seen that aggregation does not occur when the average fiber length of the main fibers is within the range of 0.1 to 1 mm. Furthermore, by controlling the fiber diameter of the fibrillated fibers to 0.01-3 μm and the fiber diameter of the main fibers to 5-15 μm, it was found that aggregation does not occur when mixed with synthetic resin, and the flexural strength is also improved.

[0059] As an example, Figure 2 shows the change in the flexural strength of the propylene resin structure when the amount of cellulose filler in Example 1 is increased to 30 mass percent. Figure 2 shows that the variation is small at the same blending amount, and furthermore, the flexural strength of the propylene resin structure increases linearly with increasing cellulose filler content, indicating that the cellulose filler is uniformly dispersed within the resin structure.

[0060] It has been revealed that synthetic resin structures containing approximately 30% by mass of the cellulose filler of the present invention have sufficient flexural strength and can be used without any problems. [Explanation of Symbols]

[0061] 1. Main fiber, 2. Fibrilized fiber

Claims

1. It consists of solvent-spun cellulose fibers, wherein the solvent-spun cellulose fibers are lyocell, It is composed of a main fiber having an average fiber length of 0.1 to 1 mm and fibrillated fibers generated from the main fiber, wherein the average fiber diameter of the main fiber is 5 to 15 μm and the average fiber diameter of the fibrillated fiber is 0.01 to 3 μm. A cellulose filler characterized by the following features.

2. A method for producing the cellulose filler described in Claim 1, The solvent-spun cellulose fibers are beaten in water, then dried, and the main fibers and fibrillated fibers are formed by dry grinding. A method for producing cellulose filler, characterized by the features described above.

3. The cellulose filler according to Claim 1 is dispersed in a synthetic resin. A synthetic resin structure characterized by the following features.