Laminate and decorated article

Description

[Technical field]

[0001] The present invention relates to a laminate and a decorated article. [Background technology]

[0002] Conventionally, decorative resin molded products in which a decorative sheet is laminated on the surface of a resin molded product have been used for vehicle interior and exterior parts, building material interior materials, home appliance housings, etc. In the manufacture of such decorative resin molded products, a molding method is used in which a decorative sheet to which a design has been previously applied is integrated with a resin by injection molding. A representative example of such a molding method is an insert molding method in which a decorative sheet is previously molded into a three-dimensional shape using a vacuum molding die, the decorative sheet is inserted into an injection molding die, and a resin in a fluid state is injected into the die to integrate the resin and the decorative sheet.

[0003] Decorated resin molded products obtained by such molding methods are used for various applications such as vehicle interior and exterior parts as described above, and therefore, in addition to three-dimensional formability that can follow three-dimensional molding and surface properties such as scratch resistance, diverse design sensations are being demanded in response to the recent diversification of consumer tastes. For example, developments have been made to impart texture to resin molded products by imparting matte finish or unevenness to specific parts of a pattern (e.g., Patent Document 1). In addition, synthetic resin molded parts with changing design surfaces have been proposed as products with diverse design sensations (e.g., Patent Document 2).

[0004] Furthermore, a decorative sheet has also been proposed in which a light source is disposed on the opposite side of the decorative sheet from the viewer side, and which exhibits a different design when the light source is on and off (for example, Patent Document 3). [Prior art documents] [Patent documents]

[0005] [Patent Document 1] JP 2009-132145 A [Patent Document 2] JP 2010-125817 A [Patent Document 3] JP 2013-14051 A [Patent Document 4] JP 2020-49844 A Summary of the Invention [Problem to be solved by the invention]

[0006] As described above, laminates that exhibit different designs when a light source is turned on and off are known.

[0007] For example, Patent Document 4 discloses a laminate having a first main surface arranged on the viewer side and a second main surface arranged on the light source side, and including, in order from the second main surface side, at least a first design layer, a second design layer, and a transparent base layer, in which an uneven shape is provided on the surface of the transparent base layer on the second design layer side. This laminate is excellent in that the design that appears when the light source is turned on is not visible when the light source is turned off, and the design is visible only when the light source is turned on.

[0008] On the other hand, there is a demand for a laminate that presents a different design when the light source is on and when it is off, such that the design that appears when the light source is off is difficult to see when the light source is on, but the design can be seen when the light source is off.

[0009] The main object of the present invention is to provide a laminate that exhibits a different design when a light source is turned on and when it is turned off, in which the design that appears when the light source is turned off is difficult to see when the light source is turned on, and the design is visible when the light source is turned off. Another object of the present invention is to provide a decorative article that uses the laminate. [Means for solving the problem]

[0010] The present inventors have conducted intensive research to solve the above problems. As a result, the inventors have found that a laminate having a first main surface arranged on the viewer side and a second main surface arranged on the light source side, in which the first main surface has an uneven shape, further comprising, in order from the first main surface side, at least a first design layer, a transparent resin layer, a second design layer, and a third design layer on the first main surface side or the second main surface side of the second design layer, the surface of the first main surface side of the second design layer is relatively flatter than the uneven shape of the first main surface, and the laminate partially provided with the third design layer exhibits different designs when the light source is turned on and off, and when the light source is turned on, the design that appears when the light source is turned off (specifically, the design based on the uneven shape of the first main surface side surface of the laminate and the design by the first design layer) is difficult to see, and the design is visible when the light source is turned off. The present invention was completed based on these findings and through further investigation.

[0011] That is, the present invention provides the following aspects. Item 1. A first main surface is disposed on the viewer side, and a second main surface is disposed on the light source side. The first main surface has an uneven shape, A laminate including, in order from the first main surface side, at least a first design layer, a transparent resin layer, and a second design layer, A third design layer is further provided on the first main surface side or the second main surface side of the second design layer, The surface of the second design layer on the first main surface side is relatively flatter than the uneven shape of the first main surface, The third design layer is provided partially on the laminate. Item 2. The laminate according to item 1, wherein a surface on the first main surface side of the transparent resin layer has an uneven shape corresponding to the uneven shape of the first main surface. Item 3. The laminate according to item 1 or 2, further comprising a surface protective layer on an outermost surface on the first main surface side. Item 4. The laminate according to any one of Items 1 to 3, further comprising a transparent substrate layer on the second main surface side of the second design layer and the third design layer. Item 5. The laminate according to any one of Items 1 to 4, wherein the laminate is in the form of a sheet. Item 6. The laminate according to any one of items 1 to 5, comprising, in order from the second main surface side, at least a transparent molded resin layer, the second design layer, the transparent resin layer, and the first design layer. Item 7. The laminate according to any one of items 1 to 6, A light source disposed on a second main surface side of the laminate; A decorative article comprising: Effect of the Invention

[0012] According to the present invention, it is possible to provide a laminate that expresses a different design when a light source is turned on and when it is turned off, in which the design that is expressed when the light source is turned off is difficult to see when the light source is turned on, and the design is visible when the light source is turned off. Furthermore, according to the present invention, it is also possible to provide a decorated article using the laminate. [Brief description of the drawings]

[0013] [Figure 1] FIG. 1 is a schematic cross-sectional view of an example of a laminate of the present invention. [Diagram 2] FIG. 1 is a schematic cross-sectional view of an example of a laminate of the present invention. [Diagram 3] FIG. 1 is a schematic cross-sectional view of an example of a laminate of the present invention. [Figure 4] FIG. 1 is a schematic cross-sectional view of an example of a laminate of the present invention. [Diagram 5] FIG. 1 is a schematic cross-sectional view of an example of a decorated article using the laminate of the present invention. [Figure 6] FIG. 2 is an example of an image diagram of the laminate of the present invention when observed from the first main surface side (observer side) when a light source 30 is turned on. [Figure 7] FIG. 2 is an example of an image diagram of the laminate of the present invention when observed from the first main surface side (observer side) when a light source 30 is turned on. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] 1.Laminate The laminate of the present invention has a first main surface arranged on the observer side and a second main surface arranged on the light source side, the first main surface having an uneven shape, and is a laminate having at least a first design layer, a transparent resin layer, and a second design layer in order from the first main surface side, and further has a third design layer on the first main surface side or the second main surface side of the second design layer, the surface of the first main surface side of the second design layer is relatively flatter than the uneven shape of the first main surface, and the third design layer is partially provided. By having such a configuration, the laminate of the present invention expresses a different design when the light source is turned on and when it is turned off, and when the light source is turned on, the design that appears when the light source is turned off (specifically, the design based on the uneven shape of the first main surface side surface of the laminate and the design by the first design layer) is difficult to see, and when the light source is turned off, the design is visible.

[0015] The laminate of the present invention can be suitably used for decorating the surface of resin molded products such as vehicle interior and exterior parts, building materials, and home appliance housings. Therefore, the laminate of the present invention can be suitably used as a decorative sheet for three-dimensional molding. In particular, when the laminate of the present invention is in the form of a sheet, it can be molded as a decorative sheet for three-dimensional molding and laminated with a molded resin layer 5 described later to suitably form a decorated resin molded product.

[0016] The laminate of the present invention will be described in detail below with reference to Figs. 1 to 5. In this specification, except where it is clearly stated as "not less than" or "not more than", a numerical range indicated by "to" means "not less than" or "not more than". For example, the expression "2 to 15 mm" means 2 mm or more and 15 mm or less. In this specification, "(meth)acrylate" means "acrylate or methacrylate", and other similar terms have the same meaning.

[0017] Layer structure and uneven shape of laminate 1 to 5, the laminate 10 of the present invention has a first main surface 11 arranged on the viewer side and a second main surface 12 arranged on the light source side. Specifically, when the laminate 10 of the present invention is used for various applications such as vehicle interior / exterior parts, building materials and interior materials, and home appliance housings, the first main surface 11 is arranged on the viewer side and the second main surface 12 is arranged on the light source side.

[0018] The laminate 10 of the present invention is a laminate comprising, in order from the first main surface side 11, at least a first design layer 21, a transparent resin layer 1, and a second design layer 22, and further comprising a third design layer 23 on the first main surface 11 side or the second main surface 12 side of the second design layer 22. Furthermore, in the laminate 10 of the present invention, the first main surface 11 has an uneven shape.

[0019] When observed from the first main surface 11 side, the laminate 10 exhibits different designs when the light source 30 is turned on and off. When the light is turned off, the design based on the uneven shape of the surface on the first main surface 11 side and the design based on the first design layer 21 are visible. When the light is turned on, the designs based on the second design layer 22 and the third design layer 23 are visible. In the laminate 10 of the present invention, when the light source 30 is turned on, the design that appears when the light source 30 is turned off is difficult to see, and when the light source is turned off, the design is visible. In order to exhibit such characteristics, in the laminate 10 of the present invention, it is important to arrange the transparent resin layer 1 between the first design layer 21 and the second design layer 22, and further, to make the surface 22a on the first main surface 11 side of the second design layer 22 relatively flatter than the uneven shape of the first main surface 11.

[0020] In addition, the surface 22a on the first main surface 11 side of the second design layer 22 may have a relatively flat shape compared to the uneven shape of the first main surface 11. Specifically, the depth of the recess of the surface 22a on the first main surface 11 side of the second design layer 22 is relatively smaller than the depth of the recess of the uneven shape of the first main surface 11. From the viewpoint of more suitably exerting the effects of the present invention, it is preferable that the surface 22a on the first main surface 11 side of the second design layer 22 is approximately flat. For example, it is preferable that the uneven shape of the first main surface 11 is flat to the extent that it is not reflected in the shape of the surface 22a on the first main surface 11 side of the second design layer 22, and even in this case, it is acceptable to have a slight uneven shape.

[0021] The surface on the second principal surface 12 side of the second design layer 22 also preferably has a shape that is relatively flat compared to the uneven shape of the first principal surface 11, and is more preferably approximately flat.

[0022] For example, as shown in FIG. 4 and FIG. 5, in the laminate 10 of the present invention, a surface protective layer 3 may be further provided on the first design layer 21 (on the first main surface 11 side) for the purpose of imparting surface protection performance such as scratch resistance and chemical resistance to the surface. In addition, a primer layer (not shown) may be provided as necessary for the purpose of increasing the adhesion between the surface protective layer 3 and the layer located thereunder (such as the first design layer 21). In addition, for example, an adhesive layer (not shown) may be provided on at least one surface of the second design layer 22. Furthermore, for example, as shown in FIG. 5, when a molded resin layer 5 is laminated on the second main surface 12 side, a back adhesive layer (not shown) may be provided on the second main surface 12 side of the transparent substrate layer 4 (the back surface side of the transparent substrate layer 4) as necessary for the purpose of increasing the adhesion between the laminate 10 of the present invention and the molded resin layer 5.

[0023] The laminate of the present invention may further include one or more other layers depending on the function to be imparted to the laminate or the decorative article.

[0024] The laminate structure of the laminate of the present invention includes, in order from the first main surface side, a laminate structure in which a first design layer / transparent resin layer 1 / second design layer / third design layer are laminated; a laminate structure in which a first design layer / transparent resin layer 1 / third design layer / second design layer are laminated; a laminate structure in which a first design layer / transparent resin layer 1 / second design layer / third design layer / transparent substrate layer are laminated; a laminate structure in which a first design layer / transparent resin layer 1 / third design layer / second design layer / transparent substrate layer are laminated; a surface Laminated structure of surface protective layer / first design layer / transparent resin layer 1 / second design layer / third design layer / transparent substrate layer;Laminated structure of surface protective layer / first design layer / transparent resin layer 1 / third design layer / second design layer / transparent substrate layer;Laminated structure of surface protective layer / first design layer / transparent resin layer 1 / second design layer / adhesive layer / third design layer / transparent substrate layer;Laminated structure of surface protective layer / first design layer / transparent resin layer 1 / third design layer / second design layer / adhesive layer / Laminated structure in which a transparent substrate layer is laminated;Laminated structure in which a surface protective layer / first design layer / transparent resin layer 1 / adhesive layer / second design layer / third design layer / transparent substrate layer is laminated;Laminated structure in which a surface protective layer / first design layer / transparent resin layer 1 / third design layer / adhesive layer / second design layer / transparent substrate layer is laminated;Laminated structure in which a surface protective layer / first design layer / transparent resin layer 1 / third design layer / second design layer / transparent substrate layer / molded resin layer is laminated; Examples of such structures include a laminated structure having a design layer / transparent resin layer 1 / second design layer / adhesive layer / third design layer / transparent substrate layer / molded resin layer; a laminated structure having a surface protective layer / first design layer / transparent resin layer 1 / third design layer / second design layer / transparent substrate layer / back surface adhesive layer / molded resin layer; and a laminated structure having a surface protective layer / first design layer / transparent resin layer 1 / second design layer / adhesive layer / third design layer / transparent substrate layer / back surface adhesive layer / molded resin layer.

[0025] FIG. 1 shows a schematic cross-sectional view of an example of a laminate in which a first design layer / transparent resin layer 1 / second design layer / third design layer are laminated in order from the first main surface side as one embodiment of the laminate structure of the laminate of the present invention. FIG. 2 shows a schematic cross-sectional view of an example of a laminate in which a first design layer / transparent resin layer 1 / third design layer / second design layer are laminated in order from the first main surface side as one embodiment of the laminate structure of the laminate of the present invention. FIG. 3 shows a schematic cross-sectional view of an example of a laminate in which a first design layer / transparent resin layer / second design layer / third design layer / transparent substrate layer are laminated in order from the first main surface side as one embodiment of the laminate structure of the laminate of the present invention. FIG. 4 shows a schematic cross-sectional view of an example of a laminate in which a surface protective layer / first design layer / transparent resin layer / second design layer / third design layer / transparent substrate layer are laminated in order from the first main surface side as one embodiment of the laminate structure of the laminate of the present invention. Figure 5 shows a schematic cross-sectional view of an example of a laminate in which, from the first main surface side, a surface protective layer / first design layer / transparent resin layer 1 / second design layer / third design layer / transparent substrate layer / molded resin layer are laminated, as one embodiment of the laminate structure of the laminate of the present invention.

[0026] In addition, in the laminate 10 of the present invention, it is preferable that the surface of the first design layer 21 on the first main surface 11 side has an uneven shape 21a. It is preferable that the uneven shape of the first main surface 11 of the laminate 10 and the uneven shape 21a of the surface on the first main surface 11 side of the first design layer 21 correspond to each other. As shown in Figures 1 and 2, when the first design layer 21 constitutes the first main surface 11 of the laminate 10, the uneven shape 21a of the surface on the first main surface 11 side of the first design layer 21 matches the uneven shape of the first main surface 11.

[0027] In the laminate 10 of the present invention, it is also preferable that the surface of the first design layer 21 on the second main surface 12 side has an uneven shape. As shown in Figures 1 and 2, the uneven shape 21a on the surface of the first design layer 21 on the first main surface 11 side and the uneven shape on the second main surface 12 side preferably have corresponding shapes.

[0028] Furthermore, in the laminate 10 of the present invention, the transparent resin layer 1 may have an uneven shape. When the transparent resin layer 1 has an uneven shape, the uneven shape is preferably provided on the first main surface 11 side (i.e., the transparent resin layer 1 has an uneven shape 1a on the first main surface 11 side) as shown in Figs. 1 to 5. The uneven shape 1a on the first main surface side of the transparent resin layer 1 corresponds to, for example, the uneven shape 21a on the surface on the first main surface 11 side of the first design layer 21. That is, in the laminate 10 of the present invention, an uneven shape corresponding to the uneven shape of the first main surface 11 can be provided, for example, from the first main surface 11 to the transparent resin layer 1 (particularly, to the surface on the first main surface 11 side of the transparent resin layer 1).

[0029] From the viewpoint of more suitably exerting the effects of the present invention, in the laminate 10 of the present invention, the ratio of the depth D of the recesses of the uneven shape of the first main surface 11 to the thickness of the transparent resin layer 1 is preferably 60% or less, and preferably 10% or more, with a preferred range being 10 to 60%.

[0030] Furthermore, from the viewpoint of more suitably exerting the effects of the present invention, in the laminate 10 of the present invention, the depth D of the recesses of the uneven shape on the first main surface 11 is preferably 10 μm or more and 100 μm or less.

[0031] The depth of the recesses can be measured, for example, by observing the cross section with a microscope. The depth D of the recesses is the height from the recesses to the protrusions of the uneven shape of the first main surface 11 as shown in Figs.

[0032] From the same viewpoint, the width W of the recesses in the uneven shape of the first main surface 11 is preferably about 30 to 500 μm, and more preferably about 100 to 300 μm. The width W of the recesses can be measured, for example, by observing a cross section with a microscope. The width W of the recesses is the distance between adjacent protrusions in the uneven shape of the first main surface 11, as shown in Figs. 1 to 3.

[0033] The uneven shape of the first main surface 11 can be suitably formed, for example, by embossing. For example, a laminate in which at least the first design layer 21 and the transparent resin layer 1 are laminated is prepared, and embossing is performed from the first main surface 11 side, thereby forming an uneven shape on the first main surface 11 side of the first design layer 21. At this time, by adjusting the depth of the recesses formed by embossing, it is also possible to form an uneven shape in the first design layer 21 and the transparent resin layer 1 by a single embossing process.

[0034] The embossing is a known method, for example, a method in which a heated and softened layer is pressed with an embossing plate to form a concave-convex pattern on the surface of the laminate, and then cooled and fixed. A known sheet-fed or rotary embossing machine can be used for the embossing.

[0035] Even when other layers such as the surface protective layer 3 and the primer layer are present, the uneven shape can be formed in these layers as well by, for example, forming an uneven shape by embossing the laminate in which these layers and the first design layer 21 are laminated on the transparent resin layer 1. In this case, the uneven shapes formed in each layer can be made to match. For example, as shown in FIG. 4, the uneven shape of the surface protective layer 3 corresponds to the uneven shape of the first design layer 21.

[0036] Each layer that forms the laminate [First design layer 21] The first design layer 21 is a layer provided on the first main surface 11 side of the transparent resin layer 1 for the purpose of imparting decorativeness to the laminate. When the laminate 10 of the present invention is observed from the first main surface 11 side, the design of the first design layer 21 is a design that is visible when the light source 30 on the second main surface 12 side is turned off. When the light source 30 is turned on, the design of the first design layer 21 is difficult to see from the first main surface 11 side, and the designs of the second design layer 22 and the third design layer 23 are visible. On the other hand, when the light source 30 is turned off, when the laminate 10 of the present invention is observed from the first main surface 11 side, the designs of the second design layer 22 and the third design layer 23 are difficult to see.

[0037] 6 and 7 show images of the laminate 10 of the present invention when observed from the first main surface 11 side (observer side) when the light source 30 is turned on. In FIG. 6 and FIG. 7, the black part is the design of the third design layer 23, and the three rectangular parts therein (geometric pattern in FIG. 6, gray gradation pattern in FIG. 7) are the design of the second design layer 22. The third design layer 23 functions as a light-shielding layer that blocks light transmission, while the second design layer functions as a pattern layer that transmits light. The design of the first design layer 21 is difficult to see from the first main surface 11 side. That is, for example, in the case of FIG. 6, the observer can see three rectangles that shine with a geometric pattern. Also, for example, in the case of FIG. 7, the observer can see three rectangles that shine with a gradation.

[0038] From the viewpoint of more suitably exerting the effects of the present invention, it is preferable that the surface of the first design layer 21 on the first main surface 11 side has an uneven shape 21a. Furthermore, it is preferable that the uneven shape of the first main surface 11 and the uneven shape 21a of the surface of the first design layer 21 on the first main surface 11 side are corresponding shapes. As shown in Figures 1 and 2, when the first design layer 21 constitutes the first main surface 11 of the laminate 10, the uneven shape 21a of the surface of the first design layer 21 on the first main surface 11 side coincides with the uneven shape of the first main surface 11.

[0039] In the laminate 10 of the present invention, it is also preferable that the surface of the first design layer 21 on the second main surface 12 side has an uneven shape. As shown in Figures 1 and 2, the uneven shape 21a on the surface of the first design layer 21 on the first main surface 11 side and the uneven shape on the second main surface 12 side preferably have corresponding shapes.

[0040] Since light is scattered by the first design layer 21 having an uneven shape, it becomes easier to achieve the effect of making the designs based on the second design layer 22 and the third design layer 23 less visible when the light is off.

[0041] When the first design layer 21 has an uneven shape, the uneven shape may be provided only on the first main surface 11 side, or may be provided also on the second main surface 12 side as shown in Figures 1 to 5.

[0042] The first design layer 21 can be, for example, a layer on which a desired pattern is formed using an ink composition. For example, if the first design layer 21 has a monochromatic design over the entire surface, and the second design layer 22 and the third design layer 23 have patterned designs, when the light source is turned off, the monochromatic design over the entire surface of the first design layer 21 is visible, and the designs of the second design layer 22 and the third design layer 23 are not visible, and when the light source is turned on, the patterned designs of the second design layer 22 and the third design layer 23 (for example, the aforementioned patterns such as symbols and text information) can be configured to be visible.

[0043] The first design layer 21 may be provided partially on the transparent resin layer 1 or may be provided over the entire surface, and is preferably provided over the entire surface.

[0044] The first design layer 21 can be formed, for example, by printing an ink for forming the first design layer onto the transparent resin layer 1 by a conventionally known printing method such as gravure printing, silk screen printing, offset printing, etc. Examples of the ink composition used to form the first design layer 21 include the same ones as those exemplified for the second design layer 22 described below, including binders, colorants, etc.

[0045] The patterns formed by the first design layer 21 are exemplified as the same as those exemplified for the second design layer 22 described below, but as mentioned above, it is preferable that the first design layer 21 has a monochrome design all over.

[0046] The first design layer 21 may also include a portion configured of a metal thin film. The metals and formation methods for forming the metal thin film are the same as those exemplified for the second design layer 22.

[0047] The thickness of the first design layer 21 is not particularly limited, but the lower limit is preferably 1 μm or more, and the upper limit is preferably 20 μm or less, more preferably 10 μm or less, and the preferred range is about 1 to 20 μm, or about 1 to 10 μm. Note that when the first design layer 21 has an uneven shape, the thickness of the first design layer 21 is the thickness at the position of the convex part of the uneven shape.

[0048] To more effectively exert the effects of the present invention, the optical density (OD value) of the first design layer 22 is preferably 2.5 or less and preferably 0.3 or more, with a preferred range of 0.3 to 2.5. It is preferable that the sum of the OD value of the first design layer and the OD value of the second design layer described below is less than 3.5.

[0049] [Transparent resin layer 1] The transparent resin layer 1 is provided between the first design layer 21 and the second and third design layers 22 and 23, and when the light source 30 is turned on, it exerts a function of making the design (for example, the design of the first design layer 21) that appears when the light source 30 is turned off difficult to see, while making the design by the second design layer 22 and the third design layer 23 easy to see, and when the light source 30 is turned off, it exerts a function of making the design (for example, the design of the first design layer 21) that appears when the light source 30 is turned off easy to see, while making the design by the second design layer 22 and the third design layer 23 difficult to see. If the transparent resin layer 1 does not exist, for example, even when the light source 30 is turned on, the design (for example, the design of the first design layer 21) that appears when the light source 30 is turned off is visible together with the design by the second design layer 22 and the third design layer 23, making it difficult to achieve the object of the present invention.

[0050] As shown in FIG. 5, the transparent resin layer 1 is transparent enough to transmit light from the light source 30 when the light source 30 is disposed on the second main surface 12 side (transparent in the present invention includes translucency). That is, the transparent resin layer 1 is usually transparent (colorless transparent, colored transparent, translucent), and may be colored as long as the design based on the second design layer 22 and the third design layer 23 is visible when the laminate 10 of the present invention is observed from the first main surface 11 side. For example, the transparent resin layer 1 may contain a matting agent such as silica or a coloring agent. As the coloring agent, the coloring agent exemplified in the second design layer 22 described later can be used. In addition, the transparent resin layer 1 may be painted to adjust the color, or a pattern may be formed to impart design.

[0051] As described above, the transparent resin layer 1 may have an uneven shape. When the transparent resin layer 1 has an uneven shape, the uneven shape is preferably provided on the first main surface 11 side (the transparent resin layer 1 has an uneven shape 1a on the first main surface 11 side) as shown in Figs. 1 to 5. The uneven shape 1a on the first main surface 11 side of the transparent resin layer 1 corresponds to, for example, the uneven shape of the first main surface 11 and the uneven shape of the first design layer 21 described above. That is, in the laminate 10 of the present invention, the uneven shape can be provided so as to extend from the first main surface 11 to the transparent resin layer 1. Note that the surface on the second main surface 12 side of the transparent resin layer 1 is preferably flatter than the uneven shape of the first main surface 11 of the laminate 10, and more preferably is substantially flat. When the surface on the second main surface 12 side of the transparent resin layer 1 is flat, the layer in contact with the surface on the second main surface 12 side of the transparent resin layer 1 (for example, the surface of the second design layer 22 in contact with the surface on the second main surface 12 side of the transparent resin layer 1, the surface of the third design layer 23 in contact with the surface on the second main surface 12 side of the transparent resin layer 1, etc.) is preferably flatter than the uneven shape of the first main surface 11 of the laminate 10, and more preferably approximately flat. Although there are no particular limitations on the term "relatively flat," the maximum height roughness Rz of the surface on the second main surface 12 side of the transparent resin layer 1 is preferably 50% or less of the Rz of the uneven shape of the first main surface 11. Rz is measured in accordance with JIS B0601 (1996).

[0052] The transparent resin layer 1 can be made of a transparent resin from the viewpoint of making the laminate 10 suitable for three-dimensional molding and suitably expressing a different design when the light source is turned on and off. The transparent resin is preferably made of a transparent thermoplastic resin. Examples of the transparent thermoplastic resin include, but are not limited to, transparent acrylonitrile-butadiene-styrene resin (hereinafter sometimes referred to as "ABS resin"), acrylic resin, polyolefin resin such as polypropylene and polyethylene, polycarbonate resin, vinyl chloride resin, polyethylene terephthalate (PET) resin, acrylonitrile-styrene-acrylic ester resin, and the like. Among these, the transparent resin layer 1 is preferably made of a transparent acrylic resin. The resin forming the transparent resin layer 1 may be one type or two or more types.

[0053] The thickness of the transparent resin layer 1 is not particularly limited, but from the viewpoint of making the laminate 10 suitable for three-dimensional molding and suitably expressing a design that differs between when the light source is on and when it is off, the lower limit is preferably 50 μm or more, more preferably 70 μm or more, and the upper limit is preferably 200 μm or less, more preferably 150 μm or less, and preferred ranges include about 50 to 200 μm, about 50 to 150 μm, about 70 to 200 μm, and about 70 to 150 μm. When the transparent resin layer 1 has an uneven shape, the thickness of the transparent resin layer 1 is the thickness at the positions of the convex parts of the uneven shape.

[0054] In order to improve adhesion with adjacent layers, the transparent resin layer 1 may be subjected to physical or chemical surface treatment such as oxidation or roughening on one or both sides as necessary. Examples of the oxidation method performed as the surface treatment of the transparent resin layer 1 include corona discharge treatment, plasma treatment, chromium oxidation treatment, flame treatment, hot air treatment, and ozone ultraviolet treatment. Examples of the roughening method performed as the surface treatment of the transparent resin layer 1 include sandblasting and solvent treatment. These surface treatments are appropriately selected depending on the type of resin constituting the transparent resin layer 1, but from the viewpoints of effect and operability, a corona discharge treatment is preferably used.

[0055] In order to more suitably exert the effects of the present invention, the total light transmittance of the transparent resin layer 1 is preferably about 70% or more, more preferably about 80% or more, and further preferably about 90% or more. The total light transmittance is measured using a haze meter in accordance with JIS K7361-1.

[0056] [Second design layer 22] The second design layer 22 is a layer provided on the second principal surface 12 side of the transparent resin layer 1 for the purpose of imparting decorativeness to the laminate 10. The design of the second design layer 22 is a design that is visible from the first principal surface 11 side when the light source on the second principal surface 12 side is turned on, and when the light source 30 is turned off, the design of the second design layer 22 is difficult to see from the first principal surface 11 side, and the design of the first design layer 21 is visible.

[0057] When the laminate 10 of the present invention is observed from the first main surface 11 side, the second design layer 22, together with the third design layer 23 described later, is provided so as to express a design when the light source 30 is turned on. For example, if the second design layer 22 and the third design layer 23 have a patterned design and the first design layer 21 described above has a monochromatic design, when the light source 30 is turned off, the monochromatic design of the first design layer 21 is visible, and the designs of the second design layer 22 and the third design layer 23 are not visible, and when the light source 30 is turned on, the patterned design of the second design layer 22 and the third design layer 23 (for example, a pattern such as a symbol or text information described later) can be configured to be visible.

[0058] In addition, when the main surface of one side of the laminate is the entire surface, the second design layer 22 may be provided partially or entirely, and it is preferable that it be provided entirely.

[0059] The optical density (OD value) of the second design layer 22 is preferably 3.0 or less, and is preferably 0.5 or more, with a preferred range of 0.5 to 3.0.

[0060] The second design layer 22 can be, for example, a layer in which a desired pattern is formed using an ink composition. The second design layer 22 can be formed, for example, by printing an ink for forming the second design layer using a conventionally known printing method such as gravure printing, silk screen printing, or offset printing. The ink composition used to form the second design layer 22 is a suitable mixture of a binder, a colorant such as a pigment or dye, an extender pigment, a solvent, a stabilizer, a plasticizer, a catalyst, a hardener, and the like.

[0061] The binder used in the ink composition is not particularly limited, but examples thereof include polyurethane resin, vinyl chloride / vinyl acetate copolymer resin, vinyl chloride / vinyl acetate / acrylic copolymer resin, chlorinated polypropylene resin, acrylic resin, polyester resin, polyamide resin, butyral resin, polystyrene resin, nitrocellulose resin, cellulose acetate resin, etc. These binders may be used alone or in combination of two or more.

[0062] The colorant used in the ink composition is not particularly limited, but examples thereof include inorganic pigments such as carbon black, iron black, titanium white, antimony white, yellow lead, titanium yellow, red iron oxide, cadmium red, ultramarine blue, and cobalt blue; organic pigments or dyes such as quinacridone red, isoindolinone yellow, and phthalocyanine blue; metal pigments consisting of scaly foil flakes of aluminum, brass, and the like; and pearlescent pigments consisting of scaly foil flakes of titanium dioxide-coated mica, basic lead carbonate, and the like.

[0063] The pattern formed by the second design layer 22 is not particularly limited, but examples thereof include symbols and text information, as well as geometric patterns such as dot patterns, line patterns, and carbon patterns, gradation patterns, wood grain patterns, stone patterns that imitate the surface of rocks such as marble patterns (e.g., travertine marble patterns), fabric patterns that imitate cloth grain or cloth-like patterns, tile patterns, brick masonry patterns, and the like. These may also be combined to form a parquet, patchwork, or other pattern, or may be a single solid color (so-called solid color). These patterns are formed by multi-color printing using normal process colors of yellow, red, blue, and black, but can also be formed by multi-color printing using special colors prepared by preparing plates of the individual colors that make up the pattern.

[0064] The second design layer 22 may also include a portion formed of a metal thin film. Examples of metals forming the metal thin film include tin, indium, chromium, aluminum, nickel, copper, silver, gold, platinum, zinc, and alloys containing at least one of these metals. There are no particular limitations on the method of forming the metal thin film, and examples include deposition methods such as vacuum deposition, sputtering, and ion plating using the above metals. In addition, in order to improve adhesion with adjacent layers, a primer layer using a known resin may be provided on the front and back surfaces of the metal thin film.

[0065] As described above, the surface 22a on the first main surface 11 side of the second design layer 22 is relatively flatter than the uneven shape of the first main surface 11. The surface 22a on the first main surface 11 side of the second design layer 22 may be relatively flatter than the uneven shape of the first main surface 11. Specifically, the depth of the recess of the surface 22a on the first main surface 11 side of the second design layer 22 is relatively smaller than the depth of the recess of the uneven shape of the first main surface 11. From the viewpoint of more suitably exerting the effects of the present invention, it is preferable that the surface 22a on the first main surface 11 side of the second design layer 22 is approximately flat. For example, it is preferable that the uneven shape of the first main surface 11 is flat to the extent that it is not reflected in the shape of the surface 22a on the first main surface 11 side of the second design layer 22, and even in this case, it is acceptable to have a slight uneven shape. Although there are no particular limitations on the term "relatively flat," it is preferable that the maximum height roughness Rz of the surface on the first main surface 11 side of the second design layer 22 be 50% or less of the Rz of the uneven shape of the first main surface 11. Rz is measured in accordance with JIS B0601 (1996). In the region where the transparent resin layer 1 and the second design layer 22 are in contact, the shape of the surface on the second main surface side of the transparent resin layer and the shape of the surface on the first main surface side of the second design layer are complementary to each other.

[0066] The surface on the second principal surface 12 side of the second design layer 22 is also preferably flatter than the uneven shape of the first principal surface 11, and more preferably is substantially flat. Although there are no particular limitations on "relatively flat," the maximum height roughness Rz of the surface on the second principal surface 12 side of the second design layer 22 is preferably 50% or less of the Rz of the uneven shape of the first principal surface 11. Rz is measured in accordance with JIS B0601 (1996).

[0067] The thickness of the second design layer 22 is not particularly limited, but the lower limit is preferably 1 μm or more, and the upper limit is preferably 30 μm or less, more preferably 20 μm or less, and preferred ranges are about 1 to 30 μm, and about 1 to 20 μm. Note that when the second design layer 22 has an uneven shape, the thickness of the second design layer 22 is the thickness at the position of the convex parts of the uneven shape.

[0068] [Third design layer 23] The third design layer 23 is a layer provided on the first main surface 11 side or the second main surface 12 side of the second design layer 22 for the purpose of providing decorativeness to the laminate 10. Specifically, as shown in FIG. 2, when the third design layer 23 is provided on the first main surface 11 side of the second design layer 22, the third design layer 23 exists between the transparent resin layer 1 and the second design layer 22. Also, as shown in FIG. 3, when the laminate 10 includes a transparent substrate layer 4 described later and the third design layer 23 is provided on the second main surface 12 side of the second design layer 22, the third design layer 23 exists between the second design layer 22 and the transparent substrate layer 4. 2, when the third design layer 23 is provided on the first main surface 11 side of the second design layer 22, in the area where the second design layer and the transparent resin layer are in direct contact with each other, the surface on the first main surface side of the second design layer may be relatively flatter than the uneven shape of the first main surface. In other words, in the area where the third design layer 23 is not provided, the surface on the first main surface side of the second design layer may be relatively flatter than the uneven shape of the first main surface.

[0069] The third design layer 23 is provided partially when the main surface of the laminate 10 is the entire surface. When the laminate 10 of the present invention is observed from the first main surface 11 side, the third design layer 23 is provided so as to express a design together with the second design layer 22 described above when the light source 30 is turned on. As described above, for example, when the second design layer 22 and the third design layer 23 have a patterned design and the first design layer 21 has a monochromatic design over the entire surface, when the light source 30 is turned off, the monochromatic design over the entire surface of the first design layer 21 is visible, and the design by the second design layer 22 and the third design layer 23 is not visible, and when the light source 30 is turned on, the patterned design by the second design layer 22 and the third design layer 23 (for example, a pattern such as a symbol or text information, which will be described later) can be configured to be visible.

[0070] The optical density (OD value) of the third design layer 23 is preferably 3.5 or more and preferably 7.0 or less, and preferably in the range of 3.5 to 7.0.

[0071] The third design layer 23 can be formed, for example, by printing an ink for forming the third design layer by a conventionally known printing method such as gravure printing, silk screen printing, offset printing, etc. Examples of the ink composition used to form the third design layer 23 include the same ones as those exemplified for the second design layer 22 described above, including binders, colorants, etc.

[0072] The patterns formed by the third design layer 23 can be exemplified as the same as those exemplified for the second design layer 22 described above, but as mentioned above, it is preferable that the third design layer 23 is formed partially and, together with the second design layer 22, expresses the desired design.

[0073] The third design layer 23 may also include a portion configured of a metal thin film. The metals and forming methods for forming the metal thin film are the same as those exemplified for the second design layer 22.

[0074] The thickness of the third design layer 23 is not particularly limited, but the lower limit is preferably 1 μm or more, and the upper limit is preferably 20 μm or less, more preferably 10 μm or less, and preferred ranges include approximately 1 to 20 μm, and approximately 1 to 10 μm.

[0075] [Transparent base layer 4] The transparent substrate layer 4 is a layer that is provided as necessary on the second main surface 12 side of the second design layer 22 and the third design layer 23 in order to provide rigidity and maintain the shape of the laminate 10. When the laminate 10 is in a sheet form, the transparent substrate layer 4 is provided to make the laminate suitable for vacuum molding (three-dimensional molding) by insert molding or the like.

[0076] As shown in Figs. 3 to 5, when the light source 30 is disposed on the second main surface 12 side, the transparent substrate layer 4 is transparent enough to transmit light from the light source (as described above, in the present invention, transparent includes translucency). That is, the transparent substrate layer 4 is usually transparent (colorless transparent, colored transparent, translucent), and may be colored as long as the design based on the second design layer 22 and the third design layer 23 is visible when the laminate 10 of the present invention is observed from the first main surface 11 side. For example, the transparent substrate layer 4 may contain a matting agent such as silica, a coloring agent, etc. As the coloring agent, the coloring agent exemplified for the second design layer 22 described above can be used.

[0077] The transparent substrate layer 4 can be made of a transparent resin, a paper substrate, or the like, from the viewpoint of making the laminate 10 suitable for three-dimensional molding and suitably expressing different designs when the light source is turned on and off. The transparent resin is preferably made of a transparent thermoplastic resin. Examples of the transparent thermoplastic resin include, but are not limited to, transparent acrylonitrile-butadiene-styrene resin (hereinafter sometimes referred to as "ABS resin"), acrylic resin, polyolefin resin such as polypropylene and polyethylene, polycarbonate resin, vinyl chloride resin, polyethylene terephthalate (PET) resin, acrylonitrile-styrene-acrylic ester resin, and the like. Among these, the transparent substrate layer 4 is preferably made of a transparent ABS resin. The resin forming the transparent substrate layer 4 may be one type or two or more types.

[0078] The thickness of the transparent substrate layer 4 is not particularly limited, but from the viewpoint of making the laminate 10 suitable for three-dimensional molding and suitably expressing a design that differs between when the light source is on and when it is off, the lower limit is preferably 50 μm or more, more preferably 100 μm or more, and the upper limit is preferably 1000 μm or less, more preferably 500 μm or less, and preferred ranges include about 50 to 1000 μm, and about 100 to 500 μm. More specifically, when a transparent ABS resin is used as the transparent substrate layer 4, the thickness is more preferably about 100 to 500 μm, and even more preferably 200 to 400 μm.

[0079] In order to improve adhesion with adjacent layers, the transparent substrate layer 4 may be subjected to physical or chemical surface treatment such as oxidation or roughening on one or both sides as necessary. Examples of the oxidation method performed as the surface treatment of the transparent substrate layer 4 include corona discharge treatment, plasma treatment, chromium oxidation treatment, flame treatment, hot air treatment, and ozone ultraviolet treatment. Examples of the roughening method performed as the surface treatment of the transparent substrate layer 4 include sandblasting and solvent treatment. These surface treatments are appropriately selected depending on the type of resin constituting the transparent substrate layer 4, but from the viewpoints of effect and operability, a corona discharge treatment is preferably used.

[0080] [Surface protection layer 3] The surface protective layer 3 is a layer that is provided as necessary in order to protect the surface of the laminate 10. In the laminate 10, the surface protective layer 3 is provided on the outermost surface on the first main surface 11 side.

[0081] As described above, even when the laminate 10 has the surface protective layer 3, the surface protective layer 3 can be formed with a concave-convex shape by embossing the laminate together with the first design layer 21, the transparent resin layer 1, etc., in a laminated state. Thus, as shown in the schematic diagrams of Figures 4 and 5, the surface protective layer 3 may have a concave-convex shape 3a. The concave-convex shape 3a may be provided on the first main surface 11 side, or may be provided on the second main surface 12 side.

[0082] From the viewpoint of more suitably exerting the effects of the present invention, it is preferable that the surface on the first main surface 11 side of the surface protective layer 3 has an uneven shape 3a. Furthermore, it is preferable that the uneven shape of the first main surface 11 and the uneven shape 3a of the surface on the first main surface 11 side of the surface protective layer 3 correspond to each other. As shown in Fig. 4 and Fig. 5, when the surface protective layer 3 constitutes the first main surface 11 of the laminate 10, the uneven shape 3a of the surface on the first main surface 11 side of the surface protective layer 3 matches the uneven shape of the first main surface 11.

[0083] In the laminate 10 of the present invention, the surface protective layer 3 may be provided on the entire surface of the first main surface 11 side, or may be provided partially. However, from the viewpoint of suitably protecting the surface of the laminate 10, it is preferable that the surface protective layer 3 is provided on the entire surface of the first main surface 11 side.

[0084] Furthermore, the surface protective layer 3 is usually transparent (colorless transparent, colored transparent, translucent), but may be colored or may contain a matting agent such as silica, as long as the designs of the second design layer 22 and the third design layer 23 are visible when the light source 30 is turned on when the laminate 10 of the present invention is observed from the first main surface 11 side. As the colorant, the colorants exemplified for the first design layer 21 described above can be used.

[0085] The material constituting the surface protective layer 3 is not particularly limited, and examples thereof include thermoplastic resins, thermosetting resins, ionizing radiation curable resins, etc. Among these, from the viewpoint of improving scratch resistance, etc., it is preferable that the surface protective layer 3 is composed of a cured product of an ionizing radiation curable resin composition. The ionizing radiation curable resin used to form the surface protective layer 3 will be described in detail below.

[0086] (ionizing radiation curable resin) The ionizing radiation curable resin used in the formation of the surface protective layer 3 is a resin that is crosslinked and cured by irradiation with ionizing radiation, and specifically includes a suitable mixture of at least one of prepolymers, oligomers, and monomers having polymerizable unsaturated bonds or epoxy groups in the molecule. Here, the ionizing radiation means electromagnetic waves or charged particle beams that have an energy quantum capable of polymerizing or crosslinking molecules, and usually ultraviolet rays (UV) or electron beams (EB) are used, but also includes electromagnetic waves such as X-rays and γ-rays, α-rays, ion beams, and other charged particle beams. Among the ionizing radiation curable resins, electron beam curable resins are preferably used in the formation of the surface protective layer 3 because they can be made solvent-free, do not require a photopolymerization initiator, and have stable curing properties.

[0087] The monomer used as the ionizing radiation curable resin is preferably a (meth)acrylate monomer having a radical polymerizable unsaturated group in the molecule, and among them, a polyfunctional (meth)acrylate monomer is preferable. The polyfunctional (meth)acrylate monomer may be a (meth)acrylate monomer having two or more (bifunctional or more), preferably three or more (trifunctional or more), polymerizable unsaturated bonds in the molecule. Specific examples of the polyfunctional (meth)acrylate include ethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, hydroxypivalic acid neopentyl glycol di(meth)acrylate, dicyclopentanyl di(meth)acrylate, caprolactone-modified dicyclopentenyl di(meth)acrylate, ethylene oxide-modified phosphoric acid di(meth)acrylate, allylated cyclohexyl di(meth)acrylate, isocyanurate di(meth)acrylate, trimethylol propionate, and the like. Examples of the monomer include propane tri(meth)acrylate, ethylene oxide modified trimethylolpropane tri(meth)acrylate, dipentaerythritol tri(meth)acrylate, propionic acid modified dipentaerythritol tri(meth)acrylate, pentaerythritol tri(meth)acrylate, propylene oxide modified trimethylolpropane tri(meth)acrylate, tris(acryloxyethyl)isocyanurate, propionic acid modified dipentaerythritol penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, ethylene oxide modified dipentaerythritol hexa(meth)acrylate, caprolactone modified dipentaerythritol hexa(meth)acrylate, etc. These monomers may be used alone or in combination of two or more.

[0088] As the oligomer used as the ionizing radiation curable resin, a (meth)acrylate oligomer having a radical polymerizable unsaturated group in the molecule is preferable, and among them, a polyfunctional (meth)acrylate oligomer having two or more (two or more functional) polymerizable unsaturated bonds in the molecule is preferable. Examples of the polyfunctional (meth)acrylate oligomer include polycarbonate (meth)acrylate, acrylic silicone (meth)acrylate, urethane (meth)acrylate, epoxy (meth)acrylate, polyester (meth)acrylate, polyether (meth)acrylate, polybutadiene (meth)acrylate, silicone (meth)acrylate, and oligomers having a cationic polymerizable functional group in the molecule (e.g., novolac type epoxy resin, bisphenol type epoxy resin, aliphatic vinyl ether, aromatic vinyl ether, etc.). Here, the polycarbonate (meth)acrylate is not particularly limited as long as it has a carbonate bond in the polymer main chain and a (meth)acrylate group at the end or side chain, and can be obtained, for example, by esterifying a polycarbonate polyol with (meth)acrylic acid. The polycarbonate (meth)acrylate may be, for example, a urethane (meth)acrylate having a polycarbonate skeleton. The urethane (meth)acrylate having a polycarbonate skeleton can be obtained, for example, by reacting a polycarbonate polyol with a polyvalent isocyanate compound and a hydroxy (meth)acrylate. The acrylic silicone (meth)acrylate can be obtained by radical copolymerization of a silicone macromonomer with a (meth)acrylate monomer. The urethane (meth)acrylate can be obtained, for example, by esterifying a polyurethane oligomer obtained by the reaction of a polyether polyol or a polyester polyol with a polyisocyanate compound with (meth)acrylic acid. Epoxy (meth)acrylates can be obtained, for example, by reacting an oxirane ring of a relatively low molecular weight bisphenol type epoxy resin or novolac type epoxy resin with (meth)acrylic acid to effect esterification.In addition, a carboxyl-modified epoxy (meth)acrylate obtained by partially modifying this epoxy (meth)acrylate with a dibasic carboxylic anhydride can also be used. The polyester (meth)acrylate can be obtained, for example, by esterifying the hydroxyl group of a polyester oligomer having hydroxyl groups at both ends obtained by condensation of a polyvalent carboxylic acid and a polyhydric alcohol with (meth)acrylic acid, or by esterifying the terminal hydroxyl group of an oligomer obtained by adding an alkylene oxide to a polyvalent carboxylic acid with (meth)acrylic acid. The polyether (meth)acrylate can be obtained by esterifying the hydroxyl group of a polyether polyol with (meth)acrylic acid. The polybutadiene (meth)acrylate can be obtained by adding (meth)acrylic acid to the side chain of a polybutadiene oligomer. The silicone (meth)acrylate can be obtained by adding (meth)acrylic acid to the end or side chain of a silicone having a polysiloxane bond in the main chain. These oligomers may be used alone or in combination of two or more.

[0089] Among the above-mentioned ionizing radiation curable resins, it is preferable to use polycarbonate (meth)acrylate from the viewpoint of obtaining excellent three-dimensional moldability while further improving the appearance design, wear resistance and moldability. It is also preferable to use a combination of polycarbonate (meth)acrylate and urethane (meth)acrylate.

[0090] (Other added ingredients) Various additives can be blended into the surface protective layer 3 depending on the desired physical properties to be provided to the surface protective layer 3. Examples of the additives include weather resistance improvers such as ultraviolet absorbers and light stabilizers, abrasion resistance improvers, polymerization inhibitors, crosslinking agents, infrared absorbers, antistatic agents, adhesion improvers, leveling agents, thixotropy imparting agents, coupling agents, plasticizers, defoamers, fillers, solvents, colorants, and the like. These additives can be appropriately selected from commonly used ones. In addition, reactive ultraviolet absorbers and light stabilizers having a polymerizable group such as a (meth)acryloyl group in the molecule can also be used as the ultraviolet absorbers and light stabilizers.

[0091] (Formation of Surface Protection Layer 3) The surface protection layer 3 can be formed, for example, by preparing an ionizing radiation curable resin composition containing an ionizing radiation curable resin, applying this to form an uncured resin layer, and crosslinking and curing the uncured resin layer.

[0092] The viscosity of the ionizing radiation curable resin composition may be any viscosity that allows the formation of an uncured resin layer by a coating method described below.

[0093] In the present invention, the prepared resin is applied by a known method such as gravure coating, bar coating, roll coating, reverse roll coating or comma coating, preferably gravure coating, to form an uncured resin layer.

[0094] The uncured resin layer thus formed is irradiated with ionizing radiation such as an electron beam or ultraviolet light to cure the uncured resin layer, thereby forming the surface protective layer 3. When an electron beam is used as the ionizing radiation, the acceleration voltage can be appropriately selected depending on the resin used and the thickness of the layer, but a typical acceleration voltage is about 70 to 300 kV.

[0095] In addition, since the higher the acceleration voltage is in the irradiation of the electron beam, the greater the penetration ability, when a resin that is easily deteriorated by electron beam irradiation is used under the surface protective layer 3, the acceleration voltage is selected so that the penetration depth of the electron beam is substantially equal to the thickness of the surface protective layer 3. This makes it possible to prevent excess irradiation of the electron beam to the layer located under the surface protective layer 3, and to minimize the deterioration of each layer due to excess electron beams.

[0096] The radiation dose is preferably an amount at which the crosslink density of the surface protective layer 3 becomes saturated, and is usually selected within the range of 5 to 300 kGy (0.5 to 30 Mrad), preferably 10 to 50 kGy (1 to 5 Mrad).

[0097] Furthermore, the electron beam source is not particularly limited, and various electron beam accelerators such as Cockcroft-Walton type, Van de Graft type, resonant transformer type, insulating core transformer type, linear type, dynamitron type, and high frequency type can be used.

[0098] When ultraviolet light is used as the ionizing radiation, light rays containing ultraviolet light having a wavelength of 190 to 380 nm may be emitted. The source of ultraviolet light is not particularly limited, but examples thereof include high pressure mercury lamps, low pressure mercury lamps, metal halide lamps, and carbon arc lamps.

[0099] The surface protective layer 3 thus formed may be treated by adding various additives to impart functions such as a hard coat function, an anti-fogging coat function, an anti-fouling coat function, an anti-glare coat function, an anti-reflection coat function, an ultraviolet shielding coat function, and an infrared shielding coat function.

[0100] The thickness of the surface protection layer 3 is not particularly limited, but from the viewpoint of imparting surface protection performance such as scratch resistance and chemical resistance to the surface, the lower limit is preferably 5 μm or more, more preferably 10 μm or more, and the upper limit is preferably 30 μm or less, more preferably 20 μm or less, and preferred ranges include about 5 to 20 μm, about 5 to 10 μm, and about 5 to 15 μm.

[0101] [Primer layer] The primer layer is a layer that is provided, if necessary, between the surface protection layer 3 and the first design layer 21 so as to be in contact with the surface on the second main surface 12 side of the surface protection layer 3, for the purpose of increasing adhesion between the surface protection layer 3 and the layer located below it.

[0102] As the primer composition constituting the primer layer, those containing urethane resin, (meth)acrylic resin, (meth)acrylic-urethane copolymer resin, vinyl chloride-vinyl acetate copolymer, polyester resin, butyral resin, chlorinated polypropylene, chlorinated polyethylene, etc. as a binder resin are preferably used, and these resins can be used alone or in combination of two or more. Among these, urethane resin, (meth)acrylic resin, and (meth)acrylic-urethane copolymer resin are preferred.

[0103] As the urethane resin, polyurethane containing polyol (polyhydric alcohol) as a main component and isocyanate as a crosslinking agent (curing agent) can be used. As the polyol, one having two or more hydroxyl groups in the molecule, such as polyester polyol, polyethylene glycol, polypropylene glycol, acrylic polyol, polyether polyol, etc. can be used. As the isocyanate, a polyvalent isocyanate having two or more isocyanate groups in the molecule, an aromatic isocyanate such as 4,4-diphenylmethane diisocyanate, or an aliphatic (or alicyclic) isocyanate such as hexamethylene diisocyanate, isophorone diisocyanate, hydrogenated tolylene diisocyanate, hydrogenated diphenylmethane diisocyanate, etc. can also be used to form the resin by mixing the urethane resin and the butyral resin.

[0104] It is preferable to use a combination of an acrylic polyol or a polyester polyol as the polyol and hexamethylene diisocyanate or 4,4-diphenylmethane diisocyanate as the crosslinking agent, and it is particularly preferable to use a combination of an acrylic polyol and hexamethylene diisocyanate.

[0105] Examples of the (meth)acrylic resin include a homopolymer of a (meth)acrylic acid ester, a copolymer of two or more different (meth)acrylic acid ester monomers, or a copolymer of a (meth)acrylic acid ester and another monomer. Specifically, (meth)acrylic resins consisting of a homopolymer or copolymer containing a (meth)acrylic acid ester, such as polymethyl(meth)acrylate, polyethyl(meth)acrylate, polypropyl(meth)acrylate, polybutyl(meth)acrylate, a methyl(meth)acrylate-butyl(meth)acrylate copolymer, an ethyl(meth)acrylate-butyl(meth)acrylate copolymer, an ethylene-methyl(meth)acrylate copolymer, or a styrene-methyl(meth)acrylate copolymer, are preferably used.

[0106] As the (meth)acrylic-urethane copolymer resin, for example, an acrylic-urethane (polyester urethane) block copolymer resin is preferable. As the curing agent, the above-mentioned various isocyanates are used. As for the acrylic-urethane (polyester urethane) block copolymer resin, it is preferable to adjust the acrylic / urethane ratio (mass ratio) to a range of preferably 9 / 1 to 1 / 9, more preferably 8 / 2 to 2 / 8, as desired.

[0107] The thickness of the primer layer is not particularly limited, but is, for example, about 0.5 to 20 μm, and preferably about 1 to 5 μm.

[0108] The primer layer is formed using a primer composition by a normal coating method such as gravure coating, gravure reverse coating, gravure offset coating, spinner coating, roll coating, reverse roll coating, kiss coating, wheeler coating, dip coating, solid coating by silk screen, wire bar coating, flow coating, comma coating, flow coating, brush coating, spray coating, or transfer coating. Here, the transfer coating method is a method in which a coating film of a primer layer or an adhesive layer is formed on a thin sheet (film substrate), and then the coating is applied to the surface of a target layer in a laminate.

[0109] [Adhesive layer] The adhesive layer (not shown) is a layer provided as necessary for the purpose of bonding each layer. The adhesive layer is provided, for example, on at least one side of the second design layer 22, and can bond the second design layer 22 to the transparent resin layer 1, the third design layer 23, the transparent substrate layer 4, or the like.

[0110] The adhesive layer may be made of a thermoplastic resin, a curable resin, or the like, depending on the type of layer to be adhered.

[0111] Examples of the thermoplastic resin used to form the adhesive layer include acrylic resin, acrylic modified polyolefin resin, chlorinated polyolefin resin, vinyl chloride / vinyl acetate copolymer, thermoplastic urethane resin, thermoplastic polyester resin, polyamide resin, rubber resin, etc. These thermoplastic resins may be used alone or in combination of two or more.

[0112] Examples of the thermosetting resin used to form the adhesive layer include urethane resin, epoxy resin, etc. These thermosetting resins may be used alone or in combination of two or more.

[0113] The thickness of the adhesive layer is, for example, about 0.1 to 20 μm.

[0114] [Back adhesive layer] The back surface adhesive layer (not shown) is a layer that is provided, if necessary, on the second main surface 12 side (the side opposite to the first design layer 21) of the transparent substrate layer 4 for the purpose of increasing adhesion with the molded resin layer 5 when the laminate 10 is molded, when the laminate 10 is provided with a molded resin layer 5.

[0115] For the back surface adhesive layer, a thermoplastic resin or a curable resin is used depending on the type of molded resin layer 5 used in the laminate 10.

[0116] Examples of thermoplastic resins used to form the back surface adhesive layer include acrylic resins, acrylic-modified polyolefin resins, chlorinated polyolefin resins, vinyl chloride / vinyl acetate copolymers, thermoplastic urethane resins, thermoplastic polyester resins, polyamide resins, rubber-based resins, etc. These thermoplastic resins may be used alone or in combination of two or more.

[0117] Examples of the thermosetting resin used to form the back surface adhesive layer include urethane resin, epoxy resin, etc. These thermosetting resins may be used alone or in combination of two or more.

[0118] The thickness of the back surface adhesive layer is not particularly limited as long as it can adhere the molded resin layer 5, and may be, for example, about 0.1 to 20 μm.

[0119] [Molded resin layer 5] In the laminate 10 of the present invention, a transparent molded resin layer 5 may be integrally formed on the second main surface 12 side. That is, as shown in FIG. 5, the laminate 10 of the present invention is a laminate including at least the molded resin layer 5, the second design layer, the transparent resin layer 1, and the first design layer 21 in this order, and further including the third design layer 23 on the first main surface 11 side or the second main surface 12 side of the second design layer 22. The molded resin layer 5 is transparent to such an extent that light from the light source can be transmitted when the light source 30 is arranged on the second main surface 12 side, similar to the transparent substrate layer 4. That is, the molded resin layer 5 is usually transparent (colorless transparent, colored transparent, translucent), and may be colored as long as the design of the second design layer 22 and the third design layer 23 can be visually recognized when the laminate 10 of the present invention is observed from the first main surface 11 side. For example, the molded resin layer 5 may contain a matting agent such as silica, a colorant, or the like. As the colorant, the colorants exemplified for the second design layer 22 described above can be used.

[0120] The molded resin layer 5 can be made of a transparent resin or the like. The transparent resin is preferably made of a transparent thermoplastic resin. Examples of the transparent thermoplastic resin include, but are not limited to, transparent acrylonitrile-butadiene-styrene resin (hereinafter sometimes referred to as "ABS resin"), acrylic resin, polyolefin resin such as polypropylene and polyethylene, polycarbonate resin, vinyl chloride resin, polyethylene terephthalate (PET) resin, acrylonitrile-styrene-acrylic ester resin, and the like. Among these, the molded resin layer 5 is preferably made of a polycarbonate resin because of its excellent transparency. The resin forming the molded resin layer 5 may be one type or two or more types. In addition, examples of the shape of the molded resin layer 5 include a plate-like body, a molded body, and the like.

[0121] The laminate 10 including the molded resin layer 5 is produced by laminating the molded resin layer 5 using a known method. When the molded resin layer 5 is a resin molded body, it may be produced by an injection molding method such as an insert molding method.

[0122] In the insert molding method, first, in the vacuum forming process, the laminate before laminating the molded resin layer 5 (i.e., a laminate having at least the second design layer 22, the transparent resin layer 1, and the first design layer 21, in order from the second main surface 12 side, and further having the third design layer 23 on the first main surface 11 side or the second main surface 12 side of the second design layer 22) is vacuum-formed (offline preforming) into the molded product surface shape in advance using a vacuum forming mold, and then, if necessary, excess parts are trimmed to obtain a molded sheet. This molded sheet is inserted into an injection mold, the injection mold is clamped, and a resin in a fluid state is injected into the mold from the transparent substrate layer 4 side of the laminate, solidified, and the molded sheet is integrated with the outer surface of the resin molded product at the same time as the injection molding, thereby producing a laminate 10 having the molded resin layer 5.

[0123] More specifically, the laminate 10 including the molded resin layer 5 is manufactured by an insert molding method including the following steps. a vacuum forming process in which the laminate before the molded resin layer 5 is laminated is molded into a three-dimensional shape using a vacuum forming mold; a trimming process in which excess parts of the vacuum formed laminate are trimmed off to obtain a molded sheet; and an integration process in which the molded sheet is inserted into an injection mold, the injection mold is closed, and a resin in a fluid state is injected into the injection mold from the transparent substrate layer 4 side to integrate the resin and the molded sheet.

[0124] In the vacuum molding step in the insert molding method, the laminate may be heated and molded. The heating temperature is not particularly limited and may be appropriately selected depending on the type of resin constituting the laminate, the thickness of the laminate, etc., but is usually about 120°C to 200°C. In the integration step, the temperature of the resin in a fluid state is not particularly limited, but is usually about 180°C to 320°C.

[0125] As described above, the molded resin layer 5 may be formed by selecting a resin according to the application. The molded resin forming the molded resin layer 5 may be the above-mentioned thermoplastic resin or may be a thermosetting resin.

[0126] Examples of the thermosetting resin include urethane resin, epoxy resin, etc. These thermosetting resins may be used alone or in combination of two or more.

[0127] The laminate 10 of the present invention expresses a different design when the light source is on and when it is off, and therefore, by using it in combination with a light source, it can be used as, for example, interior or exterior materials for vehicles such as automobiles; building fittings such as window frames and door frames; interior materials for buildings such as walls, floors, and ceilings; housings for home appliances such as television sets and air conditioners; containers, etc.

[0128] [Decorative items] The decorative article 20 of the present invention utilizes the laminate 10 of the present invention, and includes the laminate 10 and a light source 30. As shown in Fig. 5, the light source 30 is disposed on the second main surface 12 side of the laminate 10. Details of the laminate 10 of the present invention are as described above.

[0129] The type of light source is not particularly limited, and examples include light-emitting diode (LED) bulbs, incandescent bulbs, fluorescent lights, and natural light.

[0130] The decorative article of the present invention exhibits a different design when the light source is on and when it is off, and therefore can be used, for example, as interior or exterior materials for vehicles such as automobiles; building fittings such as window frames and door frames; interior materials for buildings such as walls, floors and ceilings; housings for home appliances such as television sets and air conditioners; containers, etc. EXAMPLES

[0131] The present invention will be described in detail below with reference to examples and comparative examples, but the present invention is not limited to the examples.

[0132] [Laminate manufacturing] <Example> A laminate (decorative sheet) was manufactured by the following procedure. A geometric patterned picture layer made of acrylic resin containing carbon black (ink) as a coloring agent was formed as a second design layer on the second main surface side of a transparent resin layer made of acrylic resin with a thickness of 125 μm and a total light transmittance of 90%. The total light transmittance was measured using a haze / transmittance meter HM-150L2N manufactured by Murakami Color Research Laboratory. Next, a striped design layer made of acrylic resin containing carbon black (ink) as a coloring agent was printed as a third design layer. Next, a single-color solid layer made of acrylic resin containing aluminum metal pigment was formed as a first design layer on the first main surface side of the transparent resin layer. Next, a transparent substrate layer made of ABS resin was heat laminated to the third design layer side to obtain a laminate in which the first design layer / transparent resin layer / second design layer / third design layer / transparent substrate layer were laminated in this order. Next, the first design layer side of the obtained laminate was embossed using an embossing plate with a geometric pattern and an embossing plate depth of 60 μm to form a concave-convex shape on the first design layer. The decorative sheet of the embodiment has a first main surface arranged on the observer side and a second main surface arranged on the light source side, the first main surface has a concave-convex shape, and is a laminate having, in order from the first main surface side, at least a first design layer, a transparent resin layer, and a second design layer, and further has a third design layer on the second main surface side of the second design layer, the surface on the first main surface side of the second design layer is relatively flatter than the concave-convex shape of the first main surface, and the third design layer is provided partially. The obtained decorative sheet had a transparent resin layer thickness of 125 μm, an embossed recess depth of 60 μm, a transparent base layer thickness of 400 μm, an OD value of the first design layer of 0.8, an OD value of the second design layer of 1.2, and an OD value of the third design layer of 6.0. A transmittance meter X-rite 341C was used to measure the OD value. The Rz of the uneven shape on the first main surface side measured according to JIS B0601 (1996) was 55 μm. The Rz of the surface on the second main surface side of the transparent resin layer was 3 μm. The cutoff value λc was set to 0.8 mm. In this embodiment, the transparent resin layer and the second design layer are in contact with each other over the entire surface, and the shape of the surface on the second main surface side of the transparent resin layer and the shape of the surface on the first main surface side of the second design layer are complementary to each other.

[0133] <Comparative Example> A laminate (decorative sheet) was manufactured by the following procedure. On the first main surface side of a 475 μm-thick transparent substrate layer made of ABS resin, a striped design layer made of acrylic resin containing carbon black (ink) as a coloring agent was printed as the third design layer, and then a geometric patterned picture layer made of acrylic resin containing carbon black (ink) as a coloring agent was formed as the second design layer. Furthermore, a single-color solid layer made of acrylic resin containing aluminum metal pigment was formed as the first design layer, and a laminate in which the first design layer / second design layer / third design layer / transparent substrate layer were laminated in order was obtained. Next, a geometric pattern was embossed on the first design layer side of the obtained laminate using an embossing plate with an embossing plate depth of 60 μm, and a concave-convex shape was formed on the first design layer. The decorative sheet of the comparative example does not have a transparent resin layer between the first design layer and the second design layer, unlike the decorative sheet of the example. The resulting decorative sheet had an embossed depression depth of 60 μm, a transparent base layer thickness of 475 μm, an OD value of the second design layer of 2.2, and an OD value of the third design layer of 6.0. The OD values ​​were measured using a transmittance meter, X-rite 341C.

[0134] [Design evaluation of the second design layer when lit] The decorative sheet obtained above (laminate before molding) and the decorated resin molded product (after molding) were visually observed from the surface protection layer side (observation surface dimensions: 230.4 mm x 135.4 mm). Correlated color temperature: 5200 (±300 K), average brightness: 1500 ± 300 cd / m 2 The appearance of the second design layer was visually evaluated when the light was turned on. The design of the second design layer when the light was turned on was evaluated according to the following criteria. The results are shown in Table 1. ○: A design based on the second design layer can be confirmed ×: The design based on the first design layer can be seen to overlap with the design based on the second design layer.

[0135] [Design evaluation of the third design layer when lit] The decorative sheet obtained above (laminate before molding) and the decorated resin molded product (after molding) were visually observed from the surface protection layer side (observation surface dimensions: 230.4 mm x 135.4 mm). Correlated color temperature: 5200 (±300 K), average brightness: 1500 ± 300 cd / m 2 The appearance of the third design layer was visually evaluated when the light was turned on. The design of the third design layer when the light was turned on was evaluated according to the following criteria. The results are shown in Table 1. ○: A design based on the third design layer can be confirmed ×: The design based on the first design layer can be seen to overlap with the design based on the third design layer.

[0136] [Table 1]

[0137] The decorative sheet of the embodiment is a laminate that expresses different designs when the light source is on and off, and when the light source is on, the design that appears when the light source is off (the design based on the first design layer) is difficult to see, but the designs based on the second and third design layers are visible. Also, when the light source is off, the design based on the first design layer is visible, and the designs based on the second and third design layers are difficult to see. [Explanation of symbols]

[0138] 1...Transparent resin layer 1a...Uneven shape of the first main surface side of the transparent resin layer 21…First design layer 21a... Concave and convex shape on the first main surface side of the first design layer 22…Second design layer 22a... Surface on the first main surface side of the second design layer 23…Third design layer 3…Surface protective layer 3a…Concave and recess shape of the first main surface side of the surface protection layer 4…Transparent base material layer 5...Molded resin layer 10...Laminate 11...First main surface 11a...Concave and recessed shape on the first main surface side 12...Second main surface 30…Light source

Claims

1. a first main surface disposed on the viewer side and a second main surface disposed on the light source side; The first main surface has an uneven shape, A laminate including, in order from the first main surface side, at least a first design layer, a transparent resin layer, and a second design layer, A third design layer is further provided on the first main surface side or the second main surface side of the second design layer, The surface of the second design layer on the first main surface side is relatively flatter than the uneven shape of the first main surface, The third design layer is provided partially, A laminate, wherein the surface of the transparent resin layer on the first main surface side has an uneven shape corresponding to the uneven shape of the first main surface.

2. The laminate according to claim 1 , further comprising a surface protective layer on an outermost surface on the first main surface side.

3. The laminate according to claim 1 or 2, further comprising a transparent substrate layer on the second main surface side of the second design layer and the third design layer.

4. The laminate according to claim 1 or 2, which is in the form of a sheet.

5. The laminate according to claim 1 or 2, comprising, in order from the second main surface side, at least a transparent molded resin layer, the second design layer, the transparent resin layer, and the first design layer.

6. A laminate according to claim 1 or 2; A light source disposed on a second main surface side of the laminate; A decorative article comprising: