Battery manufacturing method

Abstract

To provide a technique of obtaining a battery including a wound electrode body including a separator equipped with an adhesive layer, with high productivity.SOLUTION: A preferred aspect of a manufacturing method for a battery 100 includes a first winding step S1 of winding a first separator 71 and a second separator 72 around a winding core 210 with the first separator 71 and the second separator 72 in contact with the winding core 210, a second adhesive layer forming step S2 of forming a second adhesive layer 82 on the second separator 72, a first adhesive layer forming step S3 of forming a first adhesive layer 81 on the first separator 71, a second winding step S4 of winding a positive electrode sheet 22 and a negative electrode sheet 24 together with the first separator 71 and the second separator 72 on the winding core 210, and a pressing step S5 of, after the second winding step, pressing the first separator 71, the positive electrode sheet 22, the second separator 72, and the negative electrode sheet 24 that are wound.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present disclosure relates to a method for manufacturing a battery. [Background technology]

[0002] Japanese Patent No. 5328034 discloses a wound electrode assembly in which a separator is bonded to at least one of a positive electrode sheet and a negative electrode sheet by an adhesive resin contained in the separator, and integrated. It is described that such a wound electrode assembly can be manufactured by a manufacturing method including a step of forming a wound electrode assembly using a separator provided with an adhesive resin, and a step of subjecting the wound electrode assembly to a hot press to integrate at least one of a positive electrode sheet and a negative electrode sheet with the separator. It should be noted that Japanese Patent No. 5328034 does not include any description of the position and amount of formation of the adhesive layer on the separator. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Patent No. 5328034 Summary of the Invention [Problem to be solved by the invention]

[0004] Meanwhile, there is a demand for the development of a technology that can produce, with high productivity, a battery having a wound electrode assembly including a separator provided with an adhesive layer. [Means for solving the problem]

[0005] The method for manufacturing a battery disclosed herein is a method for manufacturing a battery including a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator being bonded by a first adhesive layer, and the positive electrode sheet and the second separator being bonded by a second adhesive layer, the method comprising the following steps: a first winding step of abutting the first separator and the second separator against a winding core, and winding the first separator and the second separator around the winding core; and a second winding step of winding the positive electrode sheet and the negative electrode sheet together with the first separator and the second separator around the winding core. the first separator has a first region in the vicinity of a winding start end of the first separator, and the first region includes a region where the first adhesive layer is not formed and / or a region where the first adhesive layer is formed with a basis weight smaller than that of the first adhesive layer formed in the region of the first separator facing the positive electrode sheet, and the second separator has a second region in the vicinity of a winding start end of the second separator, and the second region includes a region where the second adhesive layer is not formed and / or a region where the second adhesive layer is formed with a basis weight smaller than that of the second adhesive layer formed in the region of the second separator facing the positive electrode sheet. According to this battery manufacturing method, a battery including a wound electrode body including a separator provided with an adhesive layer can be obtained with high productivity. [Brief description of the drawings]

[0006] [Figure 1] FIG. 2 is a flow diagram showing a method for manufacturing a battery according to an embodiment. [Diagram 2] FIG. 2 is a schematic diagram showing a configuration of an electrode body manufacturing apparatus according to one embodiment. [Figure 3A] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 3B] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 3C] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 3D] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 4A] FIG. 11 is an explanatory diagram for explaining a pressing step. [Figure 4B] FIG. 11 is an explanatory diagram for explaining a pressing step. [Diagram 5] FIG. 1 is a perspective view showing a battery according to an embodiment of the present invention. [Figure 6] FIG. 6 is a schematic vertical cross-sectional view taken along line VI-VI in FIG. 5. [Figure 7] FIG. 7 is a schematic vertical cross-sectional view taken along line VII-VII in FIG. 5. [Figure 8] FIG. 6 is a schematic cross-sectional view taken along line VIII-VIII in FIG. 5. [Figure 9] FIG. 2 is a perspective view showing a schematic view of an electrode body attached to a sealing plate. [Figure 10] FIG. 2 is a perspective view that shows a schematic diagram of an electrode assembly to which a positive electrode second current collector and a negative electrode second current collector are attached. [Figure 11] FIG. 2 is a schematic diagram showing the configuration of a wound electrode body according to one embodiment. [Figure 12] FIG. 2 is a schematic diagram showing a state in which a wound electrode body according to one embodiment is unfolded. [Figure 13] FIG. 13 is an exploded view of FIG. [Figure 14] FIG. 14 is a schematic vertical cross-sectional view taken along line XIV-XIV in FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0007] Hereinafter, some embodiments of the technology disclosed herein will be described with reference to the drawings. It should be noted that matters other than those specifically mentioned in this specification and necessary for implementing the technology disclosed herein (for example, the general configuration and manufacturing process of a battery that does not characterize the present invention) can be understood as design matters of a person skilled in the art based on the conventional technology in the field. The technology disclosed herein can be implemented based on the contents disclosed in this specification and the technical common sense in the field. In addition, the following explanation is not intended to limit the technology disclosed herein to such explanation. In this specification, the expression "A to B" indicating a range includes the meaning of "A or more and B or less", as well as "greater than A" and "less than B".

[0008] In this specification, the term "battery" refers to a general term for an electricity storage device capable of extracting electric energy, and is a concept that includes primary batteries and secondary batteries. In addition, in this specification, the term "secondary battery" refers to a general term for an electricity storage device capable of repeated charging and discharging by the movement of charge carriers between a positive electrode sheet and a negative electrode sheet via an electrolyte. The electrolyte may be any of a liquid electrolyte (electrolytic solution), a gel electrolyte, and a solid electrolyte. Such secondary batteries include so-called storage batteries (chemical batteries) such as lithium ion secondary batteries and nickel hydrogen batteries, as well as capacitors (physical batteries) such as electric double layer capacitors. In the following, an embodiment in which a lithium ion secondary battery is the subject will be described. In the following description, the adhesive layer formed on the first separator 71 will be referred to as the first adhesive layer 81, and the adhesive layer formed on the second separator 72 will be referred to as the second adhesive layer 82.

[0009] <Battery manufacturing method> First, a method for manufacturing a battery according to the present embodiment will be described. In the method for manufacturing a battery disclosed herein, an adhesive layer may be formed on a separator during battery manufacturing, or a separator with an adhesive layer formed in advance may be used. In the following, the former method will be described as an example.

[0010] Fig. 1 is a flow diagram showing a method for manufacturing a battery according to this embodiment. As shown in Fig. 1, the method for manufacturing a battery according to this embodiment includes a first winding step (step S1) of bringing a first separator 71 and a second separator 72 into contact with a winding core 210 and winding the first separator 71 and the second separator 72 around the winding core 210; a second adhesive layer forming step (step S2) of forming a second adhesive layer 82 on the surface of the second separator 72; a first adhesive layer forming step (step S3) of forming a first adhesive layer 81 on the surface of the first separator 71; and a second winding step (step S4) of winding the positive electrode sheet 22 and the negative electrode sheet 24 together with the first separator 71 and the second separator 72 around the winding core 210. In this embodiment, the method further includes a pressing step (step S5) of pressing the wound first separator 71, positive electrode sheet 22, second separator 72, and negative electrode sheet 24 after the second winding step (step S4). The battery manufacturing method disclosed herein may further include other steps at any stage, and if the steps are not described as essential, they may be deleted as appropriate. The order of the steps may be changed as long as the effects of the technology disclosed herein are achieved. The battery manufacturing method according to this embodiment will be described below with reference to an electrode body manufacturing apparatus 200 that embodies the battery manufacturing method.

[0011] FIG. 2 is a schematic diagram showing the configuration of an electrode assembly manufacturing apparatus 200 according to this embodiment. The electrode assembly manufacturing apparatus 200 is an apparatus for manufacturing a wound electrode assembly 20 in which a strip-shaped first separator 71, a strip-shaped positive electrode sheet 22, a strip-shaped second separator 72, and a strip-shaped negative electrode sheet 24 are wound together, in which the positive electrode sheet 22 and the first separator 71 are bonded together by a first adhesive layer 81, and the positive electrode sheet 22 and the second separator 72 are bonded together by a second adhesive layer 82. As shown in FIG. 2, the electrode assembly manufacturing apparatus 200 includes a winding core 210, a plurality of rollers 220, and a coating device 230. The electrode assembly manufacturing apparatus 200 also includes a cutter (not shown), a pressing tool, and a control device. Here, the cutter is a cutter that cuts the first separator 71 and the second separator 72. The pressing jig is a jig that presses the first separator 71 and the second separator 72 against the winding core 210. Each component of the electrode body manufacturing apparatus 200 has a required actuator as appropriate. The control device is configured to control each component of the electrode body manufacturing apparatus 200 so that a required operation is performed at a specified timing according to a preset program. The control device can be embodied by a computer such as a microcontroller, for example.

[0012] The positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72 are prepared in a state of being wound around a reel (not shown) or the like. The positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72 are transported along predetermined transport paths k1 to k4. The transport path k1 is a path along which the positive electrode sheet 22 is fed from a reel (not shown) toward the winding core 210. The transport path k2 is a path along which the negative electrode sheet 24 is fed from a reel (not shown) toward the winding core 210. The transport path k3 is a path along which the first separator 71 is fed from a reel (not shown) toward the winding core 210. The transport path k4 is a path along which the second separator 72 is fed from a reel (not shown) toward the winding core 210. It is preferable that a dancer roll mechanism for removing slack in the positive electrode sheet 22, negative electrode sheet 24, first separator 71, and second separator 72 being fed, a tensioner for adjusting tension, and the like are appropriately disposed on each of the transport paths k1 to k4.

[0013] The multiple rollers 220 are disposed on the transport paths k1 to k4 of the positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72, respectively. The multiple rollers 220 are an example of a transport device. The multiple rollers 220 are disposed at predetermined positions to define the transport paths k1 to k4. The positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72 are each transported by the multiple rollers 220.

[0014] The winding core 210 has a function of holding the first separator 71 and the second separator 72 wound around the side peripheral surface. The winding core 210 is a substantially cylindrical member here, but a flat winding core may be used when winding into a flat shape. A winding core divided along the radial direction is used as the winding core 210 here, but an undivided winding core may be used, or a winding core with a variable diameter may be used. The winding core 210 has a first slit Sa and a second slit Sb. The first slit Sa and the second slit Sb are arranged at positions 180° apart along the rotation direction of the winding core 210 here. Each separator can be fixed to the winding core 210 by sandwiching the tip of the first separator 71 in the first slit Sa and sandwiching the tip of the second separator 72 in the second slit Sb.

[0015] The winding core 210 may further have a suction hole, a groove, or the like. The suction hole is a hole for adsorbing the first separator 71 and the second separator 72 wound around the side peripheral surface. The shape of the suction hole in a plan view may be circular or rectangular. Alternatively, the suction hole may be slit-shaped. The suction hole typically has a suction flow path that is a flow path formed inside the winding core 210 and connected to the suction hole. The suction path is a flow path for forming a negative pressure in the suction hole. The suction path may be configured to be appropriately connected to a vacuum line installed outside, for example, so that a negative pressure is formed. The groove can function as a receiving portion for lowering the blade of the cutter when the first separator 71 and the second separator 72 are cut. This suppresses damage to the winding core or the cutter due to contact between the winding core 210 and the blade of the cutter.

[0016] The coating device 230 is a device that applies a binder liquid (adhesive) to the surfaces of the first separator 71 and the second separator 72 along the conveying direction. The coating device 230 is configured to be able to coat the binder liquid in a desired amount on a desired region of the first separator 71 and the second separator 72. The binder liquid includes, for example, an adhesive layer binder as described later, and a solvent. As the solvent for the binder liquid, a so-called aqueous solvent is preferably used from the viewpoint of reducing the environmental load. In this case, water or a mixed solvent mainly composed of water can be used. As the solvent component other than water that constitutes such a mixed solvent, one or more organic solvents (lower alcohols, lower ketones, etc.) that can be mixed uniformly with water can be appropriately selected and used. For example, it is preferable to use an aqueous solvent in which 80 mass % or more (more preferably 90 mass % or more, and even more preferably 95 mass % or more) of the aqueous solvent is water. A particularly preferable example is an aqueous solvent that is substantially composed of water. The solvent of the binder liquid is not limited to a so-called aqueous solvent, and may be a so-called organic solvent. An example of an organic solvent is N-methylpyrrolidone. For example, a suitable example of the binder liquid is one in which water is used as the solvent and an acrylic resin (e.g., polymethacrylic acid ester resin) is mixed as a binder. The binder liquid may contain one or more additives such as a known thickener or surfactant for the purpose of improving wettability with respect to the positive electrode sheet 22 or the separator, as long as the effect of the technology disclosed herein is not hindered.

[0017] As the coating device 230, various coating devices can be used, for example, inkjet printing, various intaglio printing machines such as a gravure roll coater, a spray coater, die coaters such as a slit coater, a comma coater, a Capillary Coater (CAP coater), a lip coater, a calendar machine, etc.

[0018] As shown in FIG. 2, in this embodiment, a formation area (see Area 1 in FIG. 2) for forming a first adhesive layer 81 on the surface of the first separator 71 facing the positive electrode sheet 22 is provided on one side of a vertical line l1 that passes through the winding center O of the winding core 210 and extends in the vertical direction, and a formation area (see Area 2 in FIG. 2) for forming a second adhesive layer 82 on the surface of the second separator 72 facing the positive electrode sheet 22 is provided on the other side of the vertical line l1. In this way, by separately providing the adhesive layer formation areas, the space of the coating device can be reduced, which is preferable. In Area 1, the positive electrode sheet 22 is disposed above the first separator 71, and in Area 2, the negative electrode sheet 24 is disposed below the second separator 72.

[0019] Although not particularly limited, the angle θ between the adhesive layer forming region of the first separator 71 (in other words, the conveying path k3) and the straight line l2 that passes through the winding center O of the winding core 210 and extends in the horizontal direction is k3 From the viewpoint of improving coating unevenness in the width direction of the first separator 71 and forming a more uniform adhesive layer, the angle θ is preferably −30° to +30°, and more preferably −15° to +15°. From the same viewpoint, the angle θ of the adhesive layer forming region of the second separator 72 (in other words, the conveying path k4) with respect to a straight line l2 that passes through the winding center O of the winding core 210 and extends in the horizontal direction is k4 is preferably −30° to +30°, and more preferably −15° to +15°. k3 About -30°, θ k4 is set to about +30°.

[0020] 3A to 3D are explanatory diagrams for explaining a method of winding a member around the winding core 210 according to the present embodiment. Here, the arrows in FIGS. 3A to 3D indicate the rotation direction of the winding core 210, but are not intended to limit the rotation direction of the winding core 210 to this direction. Also, the star marks in the figures are added to make the rotation mode of the winding core 210 easier to understand. Also, in the figures, the positive electrode tab 22t and the negative electrode tab 24t are omitted for ease of viewing.

[0021] 3A, the leading end of the first separator 71 (in other words, the winding start end 71a of the first separator) is sandwiched in the first slit Sa, and the leading end of the second separator 72 (in other words, the winding start end 72a of the second separator) is sandwiched in the second slit Sb. In this embodiment, the first slit Sa and the second slit Sb function as electrostatic chucks, thereby fixing the leading end of the first separator 71 and the leading end of the second separator 72 to the winding core 210. This configuration is preferable because it can prevent the leading end of the first separator 71 and the leading end of the second separator 72 from being left with a clamping mark or the like.

[0022] 3B, the winding core 210 is rotated approximately half a turn in the direction of the arrow to bring the first separator 71 and the second separator 72 into contact with the winding core 210, and the first separator 71 and the second separator 72 are wound around the winding core 210 (first winding step). As shown in FIG. 3B, in this embodiment, the first separator 71 is brought into contact with the side wall of the first slit Sa and the side surface of approximately half the winding core 210 (see the first contact area A1 in FIG. 3B). Also, the second separator 72 is brought into contact with the side wall of the second slit Sb and the side surface of approximately half the winding core 210 (see the second contact area A2 in FIG. 3B).

[0023] Next, as shown in FIG. 3C, the application device 230 starts forming the second adhesive layer 82 on the surface of the second separator 72 (second adhesive layer forming process). In addition, the negative electrode sheet 24 is sandwiched between the first separator 71 wound around the core 210 and the second separator 72 to be supplied. Next, as shown in FIG. 3D, after the core 210 is rotated approximately half a turn, the application device 230 starts forming the first adhesive layer 81 on the surface of the first separator 71 (first adhesive layer forming process). In addition, the positive electrode sheet 22 is sandwiched between the second separator 72 wound around the core 210 and the first separator 71 to be supplied. Then, the core 210 is rotated in the direction of the arrow, so that the positive electrode sheet 22 and the negative electrode sheet 24 are wound around the core 210 together with the first separator 71 and the second separator 72 (second winding process). Then, each component is wound around the winding core 210 until a predetermined number of windings is reached. In this manner, a wound body 20a can be obtained in which the positive electrode sheet 22 and the first separator 71 are bonded together by the first adhesive layer 81, and the positive electrode sheet 22 and the second separator 72 are bonded together by the second adhesive layer 82.

[0024] As shown in FIG. 3C, in this embodiment, the negative electrode sheet 24 is sandwiched when the first separator 71 and the second separator 72 are wound around the winding core 210 by approximately half a circumference, but this is not limited to this. For example, in another embodiment, from the viewpoint of minimizing the adhesion of an adhesive layer to the winding core 210, the first separator 71 may be wound around the side wall of the first slit Sa and approximately half a circumference of the winding core 210, and the negative electrode sheet 24 may be sandwiched when the second separator 72 is wound around the side wall of the second slit Sb. Alternatively, from the viewpoint of making it easier to remove the wound body 20a from the winding core 210, the first separator 71 may be wound around the side wall of the first slit Sa and approximately one circumference of the winding core 210, and the negative electrode sheet 24 may be sandwiched when the second separator 72 is wound around the side wall of the second slit Sb and approximately one circumference of the winding core 210. However, these are merely examples, and the timing at which the negative electrode sheet 24 is sandwiched can be adjusted as appropriate depending on the type of wound electrode body to be manufactured, etc.

[0025] Although not particularly limited, in the first adhesive layer forming step, the formation start position of the first adhesive layer 81 in the first separator 71 may be the same position as the position where the positive electrode sheet 22 is sandwiched, or may be a position closer to the winding start end 71a of the first separator than the position where the positive electrode sheet 22 is sandwiched (for example, a position 10 mm or 20 mm away from the winding start end 71a of the first separator). In addition, in the second adhesive layer forming step, the formation start position of the second adhesive layer 82 in the second separator 72 may be the same position as the position where the negative electrode sheet 24 is sandwiched, or may be a position closer to the winding start end 72a of the second separator than the position where the negative electrode sheet 24 is sandwiched (for example, a position 10 mm or 20 mm away from the winding start end 72a of the second separator). For example, the latter case is preferable because the adhesive layer can be formed more reliably in the region of the first separator 71 and the second separator 72 facing the positive electrode sheet 22. In this embodiment, in the first adhesive layer forming step, the formation start position of the first adhesive layer 81 in the first separator 71 is closer to the winding start end 71a of the first separator than the position where the positive electrode sheet 22 is sandwiched. In the second adhesive layer forming step, the formation start position of the second adhesive layer 82 in the second separator 72 is closer to the winding start end 72a of the second separator than the position where the negative electrode sheet 24 is sandwiched (see FIGS. 13 and 14).

[0026] Although not particularly limited, the end position of the formation of the first adhesive layer 81 in the first separator 71 may be a position facing the winding end 22T of the positive electrode sheet in the first separator 71, or may be a position closer to the winding end 71b of the first separator than the position facing the winding end 22T of the positive electrode sheet in the first separator 71 (for example, a position 10 mm or 20 mm toward the winding end 71b of the first separator). Also, the end position of the formation of the second adhesive layer 82 in the second separator 72 may be a position facing the winding end 22T of the positive electrode sheet in the second separator 72, or may be a position closer to the winding end 72b of the second separator than the position facing the winding end 22T of the positive electrode sheet in the second separator 72 (for example, a position 10 mm or 20 mm toward the winding end 72b of the second separator). For example, the latter case is preferable because the adhesive layer can be formed more reliably in the region of the first separator 71 and the second separator 72 facing the positive electrode sheet 22. In this embodiment, the formation end position of the first adhesive layer 81 (here, the first adhesive layer 81a) in the first separator 71 is closer to the winding end end 71b of the first separator than the position facing the winding end end 22T of the positive electrode sheet in the first separator 71. In addition, the formation end position of the second adhesive layer 82 in the second separator 72 is closer to the winding end end 72b of the second separator than the position facing the winding end end 22T of the positive electrode sheet in the second separator 72 (see FIG. 13 and FIG. 14). In this embodiment, the first adhesive layer 81b is further formed in the vicinity of the winding end end 71b of the first separator. Further, the second adhesive layer 82 is not formed on the outermost surface of the second separator 72 (see FIGS. 13 and 14).

[0027] According to the manufacturing method of the battery disclosed herein, a wound electrode body 20 is obtained in which a strip-shaped first separator 71, a strip-shaped positive electrode sheet 22, a strip-shaped second separator 72, and a strip-shaped negative electrode sheet 24 are wound in a predetermined winding direction around a winding axis WL. Among them, the positive electrode sheet 22 and the first separator 71 are bonded by a first adhesive layer 81. The positive electrode sheet 22 and the second separator 72 are bonded by a second adhesive layer 82. The first separator 71 has a first region in the vicinity of the winding start end 71a of the first separator. In the first region, there is a region where the first adhesive layer 81 is not formed, and / or a region where the first adhesive layer 81 is formed with a basis weight smaller than that of the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22. The second separator 72 has a second region in the vicinity of the winding start end 72a of the second separator. In the second region, there are regions where the second adhesive layer 82 is not formed, and / or regions where the second adhesive layer 82 is formed with a smaller basis weight than the basis weight of the second adhesive layer 82 formed in the region of the second separator 72 facing the positive electrode sheet 22.

[0028] That is, according to the manufacturing method disclosed herein, a battery 100 including such a wound electrode body 20 can be obtained. In the wound electrode body 20 disclosed herein, the first adhesive layer 81 may not be formed in the entire first region, or the first adhesive layer 81 may be formed in the entire first region. Alternatively, the first region may have a region where the first adhesive layer 81 is not formed and a region where the first adhesive layer 81 is formed. In addition, in the wound electrode body 20 disclosed herein, the second adhesive layer 82 may not be formed in the entire second region, or the second adhesive layer 82 may be formed in the entire second region. Alternatively, the second region may have a region where the second adhesive layer 82 is not formed and a region where the second adhesive layer 82 is formed.

[0029] In addition, the "first region near the winding start end of the first separator" refers to a region from the winding start end 71a of the first separator to, for example, 50%, or may be a region up to 100%, a region up to 120%, a region up to 150%, or a region up to 200%, when the length of the innermost circumference of the winding core 210 is taken as 100%. Alternatively, the "first region near the winding start end 71a of the first separator to, for example, 50%, or may be a region up to 100%, a region up to 120%, a region up to 150%, or a region up to 200%, when the length of the innermost circumference of the wound electrode body 20 is taken as 100%. For example, in this embodiment, the vicinity of the winding start end 71a of the first separator is a region within 2 cm from the winding start end 71a of the first separator. In addition, the "second region near the winding start end of the second separator" may be, for example, a region up to 50%, 60%, 80%, 100%, 120%, 150%, or 200% from the winding start end 72a of the second separator when the length of the innermost circumference of the winding core 210 is taken as 100%. Alternatively, it may be, for example, a region up to 50%, 60%, 80%, 100%, 120%, 150%, or 200% from the winding start end 72a of the second separator when the length of the innermost circumference of the wound electrode body 20 is taken as 100%. For example, in this embodiment, the vicinity of the winding start end 72a of the second separator is a region within 2 cm from the winding start end 72a of the second separator. However, it is not limited to these. Moreover, the term "weight per unit area" refers to the value obtained by dividing the mass of the adhesive layer by the area of ​​the region in which it is formed (mass of adhesive layer / area of ​​the region in which it is formed).

[0030] In the wound electrode body 20 according to the present embodiment, a first region (here, the first contact region A1 and region A3) in the vicinity of the winding start end 71a of the first separator has a region where the first adhesive layer 81 is not formed. Also, a second region (here, the second contact region A2) in the vicinity of the winding start end 72a of the second separator has a region where the second adhesive layer 82 is not formed (see FIG. 14).

[0031] Moreover, the battery 100 including the wound electrode body 20 as described above includes the wound electrode body 20 in which a strip-shaped first separator 71, a strip-shaped positive electrode sheet 22, a strip-shaped second separator 72, and a strip-shaped negative electrode sheet 24 are wound in a predetermined winding direction around a winding axis WL. In the wound electrode body 20, the positive electrode sheet 22 and the first separator 71 are bonded by a first adhesive layer 81. Also, the positive electrode sheet 22 and the second separator 72 are bonded by a second adhesive layer 82. The manufacturing method of such a battery includes a first adhesive layer forming step, a second adhesive layer forming step, a first winding step, and a second winding step. Here, the first adhesive layer forming step is a step of forming the first adhesive layer 81 on the surface of the first separator 71. The second adhesive layer forming step is a step of forming the second adhesive layer 82 on the surface of the second separator 72. The first winding step is a step of bringing the first separator 71 and the second separator 72 into contact with the winding core 210 and winding the first separator 71 and the second separator 72 around the winding core 210. The second winding step is a step of winding the positive electrode sheet 22 and the negative electrode sheet 24 together with the first separator 71 and the second separator 72 around the winding core 210. In the first adhesive layer forming step, a first adhesive layer 81 having a predetermined basis weight is formed in a region facing the positive electrode sheet 22, and a first adhesive layer 81 having a basis weight smaller than that of a region where the first adhesive layer 81 is not formed and / or that of a region of the first separator 71 facing the positive electrode sheet 22 is formed in a predetermined first region near the winding start end 71a of the first separator. In the second adhesive layer formation process, a second adhesive layer 82 having a predetermined basis weight is formed in the region facing the positive electrode sheet 22, and a second adhesive layer 82 having a smaller basis weight than the region where the second adhesive layer 82 is not formed and / or the region of the second separator 72 facing the positive electrode sheet 22 is formed in a predetermined second region near the winding start end 72a of the second separator.

[0032] That is, in the manufacturing method disclosed herein, the first adhesive layer 81 may be formed over the entire first region, or the first adhesive layer 81 may not be formed over the entire first region. Alternatively, a region where the first adhesive layer 81 is not formed and a region where the first adhesive layer 81 is formed may be formed in the first region. Also, in the manufacturing method for a battery disclosed herein, the second adhesive layer 82 may be formed over the entire second region, or the second adhesive layer 82 may be formed over the entire second region. Alternatively, a region where the second adhesive layer 82 is not formed and a region where the second adhesive layer 82 is formed may be formed in the second region.

[0033] According to the manufacturing method of the battery having such a configuration, in the vicinity of the winding start end of the first separator 71 and the second separator 72, either no adhesive layer is formed or the basis weight of the adhesive layer formed is small. Therefore, the amount of the adhesive layer attached to the winding core 210 is suitably suppressed. As a result, even if an adhesive layer is attached to the winding core 210, the amount is small. And, continuous production of the wound electrode body 20 is not hindered due to the adhesive layer attached to the winding core 210, and a decrease in the yield of the wound electrode body 20 can be suitably suppressed. As a result, the battery 100 including the wound electrode body 20 including the separator provided with the adhesive layer can be obtained with high productivity.

[0034] Although not particularly limited, when the first adhesive layer 81 is formed in the first region in the first adhesive layer formation step, the ratio (B / A) of the basis weight B of the first adhesive layer 81 in the first region to the basis weight A of the first adhesive layer 81 in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and from the viewpoint of appropriately controlling the amount of the first adhesive layer 81 that can adhere to the winding core 210, is preferably 0.8 or less, more preferably 0.5 or less, and particularly preferably 0.3 or less, and may be, for example, 0.1 or less.

[0035] Although not particularly limited, when the second adhesive layer 82 is formed in two regions in the second adhesive layer formation step, the ratio (D / C) of the basis weight D of the second adhesive layer 82 in the second region to the basis weight C of the second adhesive layer 82 in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and from the viewpoint of appropriately controlling the amount of the second adhesive layer 82 that can adhere to the winding core 210, is preferably 0.8 or less, more preferably 0.5 or less, and particularly preferably 0.3 or less, and may be, for example, 0.1 or less.

[0036] In this embodiment, in the first adhesive layer forming step, a first adhesive layer 81 having a predetermined basis weight is formed in a region facing the positive electrode sheet 22, and a region where the first adhesive layer 81 is not formed is formed in a predetermined first region (here, the first contact region A1 and region A3) near the winding start end 71a of the first separator. In the second adhesive layer forming step, a second adhesive layer 82 having a predetermined basis weight is formed in a region facing the positive electrode sheet 22, and a region where the second adhesive layer 82 is not formed is formed in a predetermined second region (here, the second contact region A2) near the winding start end 72a of the second separator.

[0037] Also, as in this embodiment, it is preferable that the adhesive layer forming step (here, the first adhesive layer forming step and the second adhesive layer forming step) and the winding step (here, the first winding step and the second winding step) are performed continuously. By performing these steps continuously, it is not necessary to store the separator after the adhesive layer forming step in a wound state on a reel, so that blocking (for example, unintended adhesion between the adhesive layer and the separator) when the separator is unrolled from the reel can be suitably suppressed. This is preferable because it is possible to more reliably obtain a wound electrode body in which the adhesive layer is formed in a desired amount at a desired position. Here, the distance between the position where the adhesive layer is formed (here, the position where the coating device 230 exists) and the position of the winding core 210 is, for example, less than 50 m, may be less than 10 m, or may be less than 3 m. Also, the time from the end of the adhesive layer forming step to the start of the winding step is, for example, less than 60 minutes, may be less than 20 minutes, or may be less than 5 minutes. Note that the above-mentioned distances and times can be appropriately changed according to the actual embodiment.

[0038] In the battery manufacturing method disclosed herein, in the first winding step, a region where the first adhesive layer 81 is not formed and / or a region where the first adhesive layer 81 is formed having a smaller basis weight than the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22 may be formed in a first contact region (here, the first contact region A1) that contacts the winding core 210 of the first separator 71. Also, in the battery manufacturing method disclosed herein, in the first winding step, a region where the second adhesive layer 82 is not formed and / or a second adhesive layer 82 having a smaller basis weight than the second adhesive layer 82 formed in the region of the second separator 72 facing the positive electrode sheet 22 may be formed in a second contact region (here, the second contact region A2) that contacts the winding core 210 of the second separator 72.

[0039] That is, in the battery manufacturing method disclosed herein, the first adhesive layer 81 may not be formed over the entire first contact region, or the first adhesive layer 81 may be formed over the entire first contact region. Alternatively, a region where the first adhesive layer 81 is formed and a region where the first adhesive layer 81 is not formed may be formed in the first contact region. Also, in the battery manufacturing method disclosed herein, the second adhesive layer 82 may not be formed over the entire second contact region, or the second adhesive layer 82 may be formed over the entire second contact region. Alternatively, a region where the second adhesive layer 82 is formed and a region where the second adhesive layer 82 is not formed may be formed in the second contact region.

[0040] According to the manufacturing method of the battery having such a configuration, in the regions of the first separator 71 and the second separator 72 that contact the winding core 210, either no adhesive layer is formed or the basis weight of the adhesive layer that is formed is small. Therefore, the amount of the adhesive layer attached to the winding core 210 is suitably suppressed. As a result, even if an adhesive layer is attached to the winding core 210, the amount is small. And, the continuous production of the wound electrode body 20 is not hindered due to the adhesive layer attached to the winding core 210, and it is possible to more suitably suppress a decrease in the yield of the wound electrode body 20. As a result, it is possible to obtain the battery 100 including the wound electrode body 20 including the separator provided with the adhesive layer with higher productivity.

[0041] Although not particularly limited, when the first adhesive layer 81 is formed in the first contact region, the ratio (F / E) of the basis weight F of the first adhesive layer 81 in the first contact region to the basis weight E of the first adhesive layer 81 in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and from the viewpoint of appropriately controlling the amount of the first adhesive layer 81 that can adhere to the winding core 210, is preferably 0.8 or less, more preferably 0.5 or less, and particularly preferably 0.3 or less, and may be, for example, 0.1 or less.

[0042] Although not particularly limited, when the second adhesive layer 82 is formed in the second contact region, the ratio (H / G) of the basis weight H of the second adhesive layer 82 in the second contact region to the basis weight G of the second adhesive layer 82 in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and from the viewpoint of appropriately controlling the amount of the second adhesive layer 82 that can adhere to the winding core 210, is preferably 0.8 or less, more preferably 0.5 or less, and particularly preferably 0.3 or less, and may be, for example, 0.1 or less.

[0043] In this embodiment, an area where the first adhesive layer 81 is not formed is formed over the entire first contact area A1, and an area where the second adhesive layer 82 is not formed is formed over the entire second contact area A2.

[0044] 3C and 3D, in this embodiment, the timing at which adhesive application starts on the first separator 71 is delayed by approximately half a circumference from the timing at which adhesive application starts on the second separator 72. That is, in this embodiment, the first separator 71 extends to an area other than the first contact area A1 to form an area where the first adhesive layer 81 is not formed (see area A3 in FIG. 3D). Area A3 here indicates the area where the second separator 72 is disposed between the first separator 71 and the winding core 210.

[0045] That is, in the battery manufacturing method disclosed herein, the first region may be formed by extending to a region other than the first contact region (here, the first contact region A1) in the first separator 71. According to the battery manufacturing method having such a configuration, it is possible to suppress excessive formation of the first adhesive layer 81 on the first separator 71, which is preferable because it is possible to suppress an increase in the resistance of the battery 100 and a decrease in the impregnation property of the wound electrode body 20.

[0046] In this embodiment, the first separator 71 extends to an area other than the first contact area A1 to form an area where the first adhesive layer 81 is not formed (see area A3 in FIG. 3D).

[0047] In the battery manufacturing method disclosed herein, the first and second regions may be formed such that the length L1 of the first region from the winding start end 71a of the first separator in the longitudinal direction is greater than the length L2 of the second region from the winding start end 72a of the second separator in the longitudinal direction. A battery manufacturing method having such a configuration is preferable because it is possible to suppress excessive formation of an adhesive layer on the separator, thereby suppressing an increase in the resistance of the battery 100 and suppressing a decrease in the impregnation of the wound electrode body 20.

[0048] In this embodiment, the first region and the second region are formed so that the length L1 from the winding start end 71a of the first separator in the longitudinal direction of the first region (here, the first contact region A1 and region A3) is greater than the length L2 from the winding start end 72a of the second separator in the longitudinal direction of the second region (here, the second contact region A2) (see Figure 13).

[0049] Although not particularly limited, the ratio (L1 / L2) of the length L1 from the winding start end 71a of the first separator in the longitudinal direction of the first region to the length L2 from the winding start end 72a of the second separator in the longitudinal direction of the second region is, for example, 1.2 or more, and from the viewpoint of easily achieving the effects described above, is preferably 1.5 or more, and may be 2 or more. The upper limit of the ratio (L1 / L2) is, for example, 3 or less, and may be 2.5 or less.

[0050] In the battery manufacturing method disclosed herein, in the first separator 71 and the second separator 72, a region that is to become the outermost surface of the wound electrode body 20 may have a region where the corresponding adhesive layer (i.e., the first adhesive layer 81 and / or the second adhesive layer 82) is not formed, and / or a region where the corresponding adhesive layer is formed with a smaller basis weight than the corresponding adhesive layer formed in the region facing the positive electrode sheet 22 in the corresponding separator. That is, in the battery manufacturing method disclosed herein, an adhesive layer corresponding to the entire region that is to become the outermost surface of the wound electrode body 20 may not be formed, or an adhesive layer corresponding to the entire region that is to become the outermost surface of the wound electrode body 20 may be formed. Alternatively, a region where a corresponding adhesive layer is formed and a region where a corresponding adhesive layer is not formed may be formed in the region that is to become the outermost surface of the wound electrode body 20. According to the battery manufacturing method having such a configuration, adhesion of the adhesive layer to the electrode body manufacturing apparatus 200 can be suitably prevented, and therefore the productivity of the battery 100 including the wound electrode body 20 provided with the adhesive layer can be more suitably improved.

[0051] Although not particularly limited, when forming an adhesive layer corresponding to the region that will become the outermost surface of the wound electrode body 20, the ratio (J / I) of the basis weight I of the corresponding adhesive layer in the region that will become the outermost surface of the wound electrode body 20 to the basis weight J of the corresponding adhesive layer in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and may be 0.8 or less, 0.5 or less, 0.3 or less, or 0.1 or less.

[0052] In this embodiment, the first separator 71 has a region that is to become the outermost surface of the wound electrode body 20, where the first adhesive layer 81 is not formed (see P in FIG. 14).

[0053] In this embodiment, the first adhesive layer 81b is formed near the end 71b of the first separator on the surface on which the first adhesive layer 81 is formed, and has a basis weight smaller than that of the first adhesive layer 81a in the region facing the positive electrode sheet 22 (see FIG. 14). According to the manufacturing method of the battery having such a configuration, it is not necessary to apply a stop tape around the end 71b of the first separator, which is preferable from the viewpoint of simplifying the manufacturing of the battery. In addition, in this embodiment, the second adhesive layer 82 is not formed on the outermost surface of the second separator 72. Note that "near the end 71b of the first separator" refers to a region of, for example, 5% from the end 71b of the first separator when the outermost periphery of the wound body 20a is taken as 100%, and may be a region of 10% or less, or 20% or less. Alternatively, when the outermost peripheral length of the wound electrode body 20 is taken as 100%, the vicinity of the winding end 71b of the first separator may be, for example, up to 5%, or may be within 10%, or may be within 20%. For example, in this embodiment, the vicinity of the winding end 71b of the first separator is within 2 cm of the winding end 71b of the first separator.

[0054] As shown in FIG. 2, in the first winding step, the first separator 71 is supplied to the winding core 210 from one side of the vertical line l1, and the second separator 72 is supplied to the winding core 210 from the other side of the vertical line l1. With this configuration, the position of the winding end 71a of the first separator, the position of the winding end 72a of the second separator, the length of each separator, the cutting position, and the like can be suitably adjusted. In the second winding step, the positive electrode sheet 22 is supplied to the winding core 210 from the same side as the first separator 71 with respect to the vertical line l1, and the negative electrode sheet 24 is supplied to the winding core 210 from the other side of the vertical line l1 with the second separator. The first separator 71 is supplied from above the positive electrode sheet 22, and the second separator 72 is supplied from below the negative electrode sheet 24.

[0055] In the battery manufacturing method disclosed herein, the angle θ of the conveying path k3 with respect to a straight line l2 that passes through the winding center O of the winding core 210 and extends in the horizontal direction isk3 It is preferable that the first adhesive layer 81 is formed on the first separator 71 when the first separator 71 passes through a region in which the inclination angle is, for example, −30° to +30° (preferably, −15° to +15°). k4 It is preferable to form the first adhesive layer 82 on the second separator 72 when the separator passes through a region where the angle is, for example, −30° to +30° (preferably, −15° to +15°). This improves uneven coating in the width direction of the separator, and allows the adhesive layer to be formed more uniformly.

[0056] In this embodiment, the wound first separator 71, the positive electrode sheet 22, the second separator 72, and the negative electrode sheet 24 are pressed (pressing step) after the second winding step. Here, FIG. 4A and FIG. 4B are explanatory views for explaining the pressing step. In the pressing step, the wound body 20a manufactured as described above is removed from the winding core 210 and pressed by a press machine 300. This makes it possible to suitably obtain a flat-shaped wound electrode body 20. In addition, it is preferable to press the positive electrode sheet 22 and the first separator 71 so that the adhesive strength of the positive electrode sheet 22 and the first separator 71 after the pressing step is greater than the adhesive strength of the positive electrode sheet 22 and the first separator 71 before the pressing step. It is preferable to press the positive electrode sheet 22 and the second separator 72 so that the adhesive strength of the positive electrode sheet 22 and the second separator 72 after the pressing step is greater than the adhesive strength of the positive electrode sheet 22 and the second separator 72 before the pressing step. The manufacturing method for a battery having such a configuration is preferable because it provides an opportunity to loosen the wound body 20a after winding in order to prevent buckling.

[0057] Although not particularly limited, the ratio (N / M) of the adhesive strength M of the positive electrode sheet 22 and the first separator 71 before the pressing process to the adhesive strength N of the positive electrode sheet 22 and the first separator 71 after the pressing process is, for example, 1.2 or more, and may be 1.5 or more, or 2 or more. Note that this adhesive strength may mean, for example, an adhesive strength measured by a conventionally known measuring method using a positive electrode sheet-separator laminate of a predetermined area (e.g., a sample of 5 cm x 5 cm). Note that the above description can also be referred to for the ratio of the adhesive strength of the positive electrode sheet 22 and the second separator 72 before the pressing process to the adhesive strength of the positive electrode sheet 22 and the second separator 72 after the pressing process.

[0058] Three of the above-mentioned wound electrode bodies 20 are prepared, inserted into a battery case 10, and sealed to produce a battery 100. Specifically, as shown in FIG. 6, a positive electrode second current collecting member 52 is joined to the positive electrode tab group 25 of the wound electrode body 20, and a negative electrode second current collecting member 62 is joined to the negative electrode tab group 27. Then, as shown in FIG. 9, a plurality of (three in this case) wound electrode bodies 20 are arranged so that the flat portions face each other. A sealing plate 14 is placed above the plurality of wound electrode bodies 20, and the positive electrode tab group 25 of each wound electrode body 20 is folded so that the positive electrode second current collecting member 52 faces one side surface 20e of the wound electrode body 20. This connects the positive electrode first current collecting member 51 and the positive electrode second current collecting member 52. Similarly, the negative electrode tab group 27 of each of the wound electrode bodies 20 is bent so that the negative electrode second current collecting member 62 and the other side surface 20h of the wound electrode body 20 face each other. This connects the negative electrode first current collecting member 61 and the negative electrode second current collecting member 62. As a result, the wound electrode body 20 is attached to the sealing plate 14 via the positive electrode current collecting portion 50 and the negative electrode current collecting portion 60. Next, the wound electrode body 20 attached to the sealing plate 14 is covered with an electrode body holder 29 (see FIG. 3) and then housed inside the exterior body 12. As a result, the flat portion of the wound electrode body 20 faces the long side wall 12b of the exterior body 12 (i.e., the flat surface of the battery case 10). In addition, the upper curved portion 20r faces the sealing plate 14, and the lower curved portion 20r faces the bottom wall 12a of the exterior body 12. Then, opening 12h on the top surface of exterior body 12 is closed with sealing plate 14, and then exterior body 12 and sealing plate 14 are joined (welded) to construct battery case 10. After that, electrolyte is injected into battery case 10 through injection hole 15 of sealing plate 14, and injection hole 15 is closed with sealing member 16. In this manner, battery 100 can be manufactured.

[0059] <Battery configuration> Next, a battery 100 manufactured by the battery manufacturing method disclosed herein will be described with reference to FIGS. 5 to 11. FIG. 5 is a perspective view of the battery 100. FIG. 6 is a schematic longitudinal sectional view taken along line VI-VI in FIG. 5. FIG. 7 is a schematic longitudinal sectional view taken along line VII-VII in FIG. 5. FIG. 8 is a schematic transverse sectional view taken along line VIII-VIII in FIG. 5. FIG. 9 is a perspective view showing an electrode body attached to a sealing plate. FIG. 10 is a perspective view showing an electrode body to which a positive electrode second current collector and a negative electrode second current collector are attached. FIG. 11 is a diagram showing the configuration of a wound electrode body. In FIG. 11, the first adhesive layer 81 and the second adhesive layer 82 are omitted for ease of viewing.

[0060] 5 and 6, the battery 100 includes a wound electrode body 20 and a battery case that houses the wound electrode body 20. Although not shown, the battery 100 further includes an electrolyte. The battery 100 is preferably a non-aqueous electrolyte secondary battery such as a lithium ion secondary battery.

[0061] The battery case 10 is a housing that houses the wound electrode body 20. Here, as shown in FIG. 5, the battery case 10 has a rectangular parallelepiped (square) outer shape with a bottom. The material of the battery case 10 may be the same as that conventionally used, and is not particularly limited. The battery case 10 is preferably made of metal. Examples of materials for the battery case 10 include aluminum, aluminum alloy, iron, and iron alloy.

[0062] As shown in FIG. 5 and FIG. 6, the battery case 10 includes an exterior body 12 and a sealing plate 14. The exterior body 12 is a flat, bottomed, rectangular container having an opening 12h on the upper surface. The exterior body 12 includes a bottom wall 12a that is substantially rectangular in plan view, a pair of long side walls 12b that extend from the bottom wall 12a and face each other, and a pair of short side walls 12c that extend from the bottom wall 12a and face each other. The area of ​​the short side walls 12c is smaller than the area of ​​the long side walls 12b. The sealing plate 14 is a member that closes the opening 12h of the exterior body 12, and is a plate-like member that is substantially rectangular in plan view. The battery case 10 is integrated by joining (for example, welding) the sealing plate 14 to the periphery of the opening 12h of the exterior body 12. The battery case 10 is hermetically sealed (sealed).

[0063] 6, sealing plate 14 is provided with injection hole 15, gas exhaust valve 17, and two terminal withdrawal holes 18, 19. Injection hole 15 is a through hole for injecting an electrolyte into battery case 10 after sealing plate 14 is assembled to exterior body 12. Injection hole 15 is sealed with sealing member 16 after the electrolyte is injected. Gas exhaust valve 17 is a thin-walled portion configured to break when the pressure inside battery case 10 reaches or exceeds a predetermined value, thereby discharging gas inside battery case 10 to the outside.

[0064] The battery case 10 may accommodate an electrolyte together with the wound electrode body 20 as described above. As the electrolyte, any electrolyte used in conventionally known batteries may be used without any particular limitation. As an example, a non-aqueous electrolyte solution in which a supporting salt is dissolved in a non-aqueous solvent may be used. As an example of the non-aqueous solvent, carbonate-based solvents such as ethylene carbonate, dimethyl carbonate, and ethyl methyl carbonate may be used. As an example of the supporting salt, fluorine-containing lithium salts such as LiPF6 may be used. The non-aqueous electrolyte solution may contain various additives as necessary. The electrolyte may be in a solid state (solid electrolyte) and may be integrated with the electrode body.

[0065] A positive electrode terminal 30 is attached to one end of the sealing plate 14 in the long side direction Y (left side in Figs. 5 and 6). A negative electrode terminal 40 is attached to the other end of the sealing plate 14 in the long side direction Y (right side in Figs. 5 and 6). The positive electrode terminal 30 and the negative electrode terminal 40 are inserted through the terminal pull-out holes 18 and 19 and exposed on the outer surface of the sealing plate 14. The positive electrode terminal 30 is electrically connected to a plate-shaped positive electrode external conductive member 32 on the outside of the battery case 10. The negative electrode terminal 40 is electrically connected to a plate-shaped negative electrode external conductive member 42 on the outside of the battery case 10. The positive electrode external conductive member 32 and the negative electrode external conductive member 42 are connected to other secondary batteries and external devices via external connection members such as bus bars. The positive electrode external conductive member 32 and the negative electrode external conductive member 42 are preferably made of a metal having excellent electrical conductivity, for example, aluminum, an aluminum alloy, copper, a copper alloy, or the like. However, the positive electrode external conductive member 32 and the negative electrode external conductive member 42 are not essential and may be omitted in other embodiments.

[0066] 7 to 9, the battery 100 here has a plurality (three) of wound electrode bodies 20 housed within a battery case 10. A detailed structure of the wound electrode body 20 will be described later, but each wound electrode body 20 is provided with a positive electrode tab group 25 and a negative electrode tab group 27 (see FIG. 8). As shown in FIG. 8, these electrode tab groups (positive electrode tab group 25 and negative electrode tab group 27) are folded with the electrode current collecting parts (positive electrode current collecting part 50 and negative electrode current collecting part 60) joined together.

[0067] The positive electrode tab group 25 of each of the plurality of wound electrode bodies 20 is connected to the positive electrode terminal 30 via a positive electrode current collector 50. The positive electrode current collector 50 is housed inside the battery case 10. As shown in FIG. 6 and FIG. 9, the positive electrode current collector 50 includes a positive electrode first current collector 51 and a positive electrode second current collector 52. The positive electrode first current collector 51 is a plate-shaped conductive member extending in the long side direction Y along the inner side surface of the sealing plate 14. The positive electrode second current collector 52 is a plate-shaped conductive member extending in the up-down direction Z of the battery 100. The lower end 30c of the positive electrode terminal 30 is inserted into the battery case 10 through the terminal pull-out hole 18 of the sealing plate 14 and is connected to the positive electrode first current collector 51 (see FIG. 6). As shown in Figs. 8 to 10, the battery 100 includes a number of positive electrode second current collecting members 52 corresponding to the number of the plurality of wound electrode bodies 20. Each positive electrode second current collecting member 52 is connected to a positive electrode tab group 25 of the wound electrode body 20. As shown in Fig. 8, the positive electrode tab group 25 of the wound electrode body 20 is bent so that the positive electrode second current collecting member 52 faces one side surface 20e of the wound electrode body 20. This electrically connects the upper end of the positive electrode second current collecting member 52 to the positive electrode first current collecting member 51. The positive electrode terminal 30 and the positive electrode current collecting part 50 are preferably made of a metal having excellent electrical conductivity. The positive electrode terminal 30 and the positive electrode current collecting part 50 may be made of, for example, aluminum or an aluminum alloy.

[0068] On the other hand, the negative electrode tab group 27 of each of the plurality of wound electrode bodies 20 is connected to the negative electrode terminal 40 via the negative electrode current collecting portion 60. The connection structure on the negative electrode side is substantially the same as the connection structure on the positive electrode side described above. Specifically, as shown in FIG. 6 and FIG. 9, the negative electrode current collecting portion 60 includes a negative electrode first current collecting member 61 and a negative electrode second current collecting member 62. The negative electrode first current collecting member 61 is a plate-shaped conductive member extending in the long side direction Y along the inner side surface of the sealing plate 14. The negative electrode second current collecting member 62 is a plate-shaped conductive member extending in the up-down direction Z of the battery 100. The lower end portion 40c of the negative electrode terminal 40 is inserted into the battery case 10 through the terminal pull-out hole 19 and connected to the negative electrode first current collecting member 61 (see FIG. 6). As shown in Figs. 8 to 10, the battery 100 includes negative electrode second current collecting members 62 in a number corresponding to the number of the plurality of wound electrode bodies 20. Each negative electrode second current collecting member 62 is connected to the negative electrode tab group 27 of the wound electrode body 20. As shown in Figs. 8 and 9, the negative electrode tab group 27 of the wound electrode body 20 is bent so that the negative electrode second current collecting member 62 faces the other side surface 20h of the wound electrode body 20. This electrically connects the upper end of the negative electrode second current collecting member 62 to the negative electrode first current collecting member 61. The negative electrode terminal 40 and the negative electrode current collecting part 60 are preferably made of a metal having excellent electrical conductivity. The negative electrode terminal 40 and the negative electrode current collecting part 60 may be made of, for example, copper or a copper alloy.

[0069] In the battery 100, various insulating members are attached to prevent conduction between the wound electrode body 20 and the battery case 10. For example, as shown in FIG. 5 and FIG. 6, the positive electrode external conductive member 32 and the negative electrode external conductive member 42 are insulated from the sealing plate 14 by an external insulating member 92. Also, as shown in FIG. 6, a gasket 90 is attached to each of the terminal pull-out holes 18, 19 of the sealing plate 14. This can prevent the positive electrode terminal 30 (or the negative electrode terminal 40) inserted into the terminal pull-out holes 18, 19 from being conducted to the sealing plate 14. Also, an internal insulating member 94 is disposed between the positive electrode current collector 50 and the negative electrode current collector 60 and the inner surface side of the sealing plate 14. This can prevent the positive electrode current collector 50 and the negative electrode current collector 60 from being conducted to the sealing plate 14. The internal insulating member 94 may have a protruding portion protruding toward the wound electrode body 20. Furthermore, the multiple wound electrode bodies 20 are arranged inside the exterior body 12 while being covered with an electrode body holder 29 (see FIG. 7) made of an insulating resin sheet. This can prevent direct contact between the wound electrode body 20 and the exterior body 12. The material of each of the insulating members described above is not particularly limited as long as it has a predetermined insulating property. Examples of such materials include synthetic resin materials such as polyolefin resins such as polypropylene (PP) and polyethylene (PE), and fluorine-based resins such as perfluoroalkoxyalkane and polytetrafluoroethylene (PTFE).

[0070] Here, three wound electrode bodies 20 are housed in the exterior body 12. However, the number of wound electrode bodies arranged inside one exterior body 12 is not particularly limited, and may be four or more, or may be one. The wound electrode body 20 is preferably flat. As shown in FIG. 3, the wound electrode body 20 is, for example, flat and has a pair of curved parts 20r that face the bottom wall 12a and the sealing plate 14 of the exterior body 12, and a flat part 20f that connects the pair of curved parts 20r and faces the long side wall 12b of the exterior body 12. In this specification, the flat wound electrode body refers to a wound electrode body that is substantially oval in cross section and has a so-called racetrack shape (see FIG. 3).

[0071] As shown in FIG. 11, the wound electrode body 20 is configured by stacking a strip-shaped positive electrode sheet 22 and a strip-shaped negative electrode sheet 24 in a state of being insulated via a strip-shaped first separator 71 and a strip-shaped second separator 72, and winding them in the longitudinal direction around a winding axis WL. Here, the wound electrode body 20 is arranged inside the exterior body 12 with the winding axis WL (see FIG. 11) oriented parallel to the long side direction Y of the exterior body 12. In other words, the wound electrode body 20 is arranged inside the exterior body 12 with the winding axis WL oriented parallel to the bottom wall 12a and perpendicular to the short side wall 12c. An end face of the wound electrode body 20 (in other words, a lamination surface where the positive electrode sheet 22 and the negative electrode sheet 24 are laminated) faces the short side wall 12c.

[0072] As shown in FIG. 11, the positive electrode sheet 22 is a strip-shaped member. The positive electrode sheet 22 has a strip-shaped positive electrode collector 22c, and a positive electrode active material layer 22a and a positive electrode protective layer 22p fixed on at least one surface of the positive electrode collector 22c. However, the positive electrode protective layer 22p is not essential and can be omitted in other embodiments. For each member constituting the positive electrode sheet 22, a conventionally known material that can be used in a general battery (e.g., a lithium ion secondary battery) can be used without any particular restriction. For example, the positive electrode collector 22c is preferably made of a conductive metal such as aluminum, an aluminum alloy, nickel, or stainless steel. Here, the positive electrode collector 22c is a metal foil, specifically, an aluminum foil.

[0073] As shown in FIG. 11, the positive electrode sheet 22 has a plurality of positive electrode tabs 22t at one end (the left end in FIG. 11) in the long side direction Y of the wound electrode body 20. The plurality of positive electrode tabs 22t are provided at a predetermined interval (intermittently) along the longitudinal direction. The positive electrode tabs 22t are connected to the positive electrode sheet 22. Here, the positive electrode tab 22t is a part of the positive electrode collector 22c, and is made of metal foil (specifically, aluminum foil). The positive electrode tab 22t is a region where the positive electrode active material layer 22a is not formed and the positive electrode collector 22c is exposed. However, the positive electrode tab 22t may be partially provided with the positive electrode active material layer 22a and / or the positive electrode protective layer 22p, and may be a member different from the positive electrode collector 22c. Here, each of the plurality of positive electrode tabs 22t is trapezoidal. However, the shape of the positive electrode tab 22t is not limited thereto. The size of the positive electrode tabs 22t is not particularly limited. The shape and size of the positive electrode tabs 22t can be appropriately adjusted depending on the position of the positive electrode tabs 22t, for example, in consideration of the state of connection to the positive electrode current collecting part 50. The positive electrode tabs 22t are stacked at one end of the positive electrode sheet 22 in the long side direction Y (the left end in FIG. 8) as shown in FIG. 8, to form a positive electrode tab group 25.

[0074] As shown in FIG. 11, the positive electrode active material layer 22a is provided in a strip shape along the longitudinal direction of the strip-shaped positive electrode current collector 22c. The positive electrode active material layer 22a contains a positive electrode active material (for example, a lithium transition metal composite oxide such as a lithium nickel cobalt manganese composite oxide) that can reversibly store and release charge carriers. The positive electrode active material layer 22a preferably contains a lithium transition metal composite oxide as a positive electrode active material, and the lithium transition metal composite oxide preferably contains a positive electrode active material with a high nickel (Ni) content. For example, in the lithium transition metal composite oxide, when the total of metal elements other than lithium is taken as 100 mol%, the nickel content is preferably 55 mol% or more, more preferably 70 mol% or more, and even more preferably 75 mol% or more. This can further increase the capacity of the nonaqueous electrolyte secondary battery.

[0075] When the entire solid content of the positive electrode active material layer 22a is taken as 100 mass%, the positive electrode active material may account for approximately 80 mass% or more, typically 90 mass% or more, for example 95 mass% or more. The positive electrode active material layer 22a may contain any component other than the positive electrode active material, such as a conductive material, a binder, various additive components, etc. An example of the conductive material is a carbon material such as acetylene black (AB). An example of the binder is a fluorine-based resin such as polyvinylidene fluoride (PVdF).

[0076] Although not particularly limited, when the weight per unit area of ​​the positive electrode active material layer 22a is a (g) and the amount of moisture generated when the positive electrode active material layer 22a is heated from 150°C to 300°C is b (g), it is preferable that the ratio (b / a) of the moisture amount b to the weight a be less than 0.2%.

[0077] The positive electrode protective layer 22p is a layer configured to have lower electrical conductivity than the positive electrode active material layer 22a. As shown in FIG. 11, the positive electrode protective layer 22p is provided at the boundary between the positive electrode collector 22c and the positive electrode active material layer 22a in the long side direction Y. Here, the positive electrode protective layer 22p is provided at one end (the left end in FIG. 11) of the positive electrode collector 22c in the long side direction Y. However, the positive electrode protective layer 22p may be provided at both ends in the long side direction Y. By providing the positive electrode protective layer 22p, it is possible to prevent the positive electrode collector 22c and the negative electrode active material layer 24a from coming into direct contact with each other when the first separator 71 and the second separator 72 are damaged, and thus prevent the battery 100 from being internally short-circuited.

[0078] The positive electrode protective layer 22p contains an insulating inorganic filler, for example, ceramic particles such as alumina. When the entire solid content of the positive electrode protective layer 22p is taken as 100 mass%, the inorganic filler may occupy approximately 50 mass% or more, typically 70 mass% or more, for example 80 mass% or more. The positive electrode protective layer 22p may contain optional components other than the inorganic filler, for example, a conductive material, a binder, various additive components, and the like. The conductive material and binder may be the same as those exemplified as those that may be contained in the positive electrode active material layer 22a.

[0079] As shown in FIG. 11, the negative electrode sheet 24 is a strip-shaped member. The negative electrode sheet 24 has a strip-shaped negative electrode collector 24c and a negative electrode active material layer 24a fixed on at least one surface of the negative electrode collector 24c. For each member constituting the negative electrode sheet 24, a conventionally known material that can be used in a general battery (e.g., a lithium ion secondary battery) can be used without any particular restriction. For example, the negative electrode collector 24c is preferably made of a conductive metal such as copper, a copper alloy, nickel, or stainless steel. Here, the negative electrode collector 24c is a metal foil, specifically, a copper foil.

[0080] As shown in FIG. 11, the negative electrode sheet 24 has a plurality of negative electrode tabs 24t at one end (the right end in FIG. 11) in the long side direction Y of the wound electrode body 20. The plurality of negative electrode tabs 24t are provided at a predetermined interval (intermittently) along the longitudinal direction. The negative electrode tabs 24t are connected to the negative electrode sheet 24. Here, the negative electrode tab 24t is a part of the negative electrode collector 24c, and is made of metal foil (specifically, copper foil). Here, the negative electrode tab 24t is a region where the negative electrode active material layer 24a is not formed, and the negative electrode collector 24c is exposed. However, the negative electrode tab 24t may have the negative electrode active material layer 24a formed in a part thereof, and may be a member different from the negative electrode collector 24c. Here, each of the plurality of negative electrode tabs 24t is trapezoidal. However, the shape and size of the plurality of negative electrode tabs 24t can be appropriately adjusted in the same manner as the positive electrode tab 22t. As shown in FIG. 8, the negative electrode tabs 24t are stacked at one end in the long side direction Y of the negative electrode sheet 24 (the right end in FIG. 8) to form a negative electrode tab group 27.

[0081] As shown in FIG. 11, the negative electrode active material layer 24a is provided in a strip shape along the longitudinal direction of the strip-shaped negative electrode current collector 24c. The negative electrode active material layer 24a contains a negative electrode active material (e.g., a carbon material such as graphite) that can reversibly store and release charge carriers. The width (length in the long side direction Y; the same applies below) of the negative electrode active material layer 24a is preferably larger than the width of the positive electrode active material layer 22a. When the entire solid content of the negative electrode active material layer 24a is taken as 100 mass%, the negative electrode active material may occupy approximately 80 mass% or more, typically 90 mass% or more, for example 95 mass% or more. The negative electrode active material layer 24a may contain any component other than the negative electrode active material, such as a conductive material, a binder, a dispersant, various additive components, etc. An example of the binder is a rubber such as styrene butadiene rubber (SBR). An example of the dispersant is a cellulose such as carboxymethyl cellulose (CMC).

[0082] The first separator 71 and the second separator 72 are strip-shaped members. The first separator 71 and the second separator 72 are insulating sheets in which a plurality of fine through-holes through which charge carriers can pass are formed. The widths of the first separator 71 and the second separator 72 are greater than the width of the negative electrode active material layer 24a. By interposing the first separator 71 and the second separator 72 between the positive electrode sheet 22 and the negative electrode sheet 24, contact between the positive electrode sheet 22 and the negative electrode sheet 24 can be prevented, and charge carriers (e.g., lithium ions) can be moved between the positive electrode sheet 22 and the negative electrode sheet 24.

[0083] As the base layer 85, a microporous film used in a separator of a conventionally known battery can be used without any particular limitation. The base layer 85 is preferably, for example, a porous sheet-like member. The base layer 85 may have a single-layer structure or a structure of two or more layers, for example, a three-layer structure. The base layer 85 is preferably made of a polyolefin resin. This ensures sufficient flexibility of the separator, and allows the wound electrode body 20 to be easily produced (wound and press-molded). As the polyolefin resin, polyethylene (PE), polypropylene (PP), or a mixture thereof is preferable, and PE is more preferable. In addition, although not particularly limited, the thickness of the base layer 85 is preferably 3 μm or more and 25 μm or less, more preferably 3 μm or more and 18 μm or less, and even more preferably 5 μm or more and 14 μm or less.

[0084] Here, the heat-resistant layer 87 is provided on the base layer 85. The heat-resistant layer 87 may be provided directly on the surface of the base layer 85, or may be provided on the base layer 85 via another layer. However, the heat-resistant layer 87 is not essential and may be omitted in other embodiments. The basis weight of the heat-resistant layer 87 is uniform in the longitudinal and width directions of the separator. Although not particularly limited, the thickness of the heat-resistant layer 87 is preferably 0.3 μm or more and 6 μm or less, more preferably 0.5 μm or more and 6 μm or less, and even more preferably 1 μm or more and 4 μm or less.

[0085] The heat-resistant layer 87 preferably contains an inorganic filler and a heat-resistant layer binder. As the inorganic filler, any inorganic filler that has been publicly known and has been used for this type of application can be used without any particular limitation. The inorganic filler preferably contains insulating ceramic particles. Among them, in consideration of heat resistance, availability, and the like, inorganic oxides such as alumina, zirconia, silica, titania, metal hydroxides such as aluminum hydroxide, and clay minerals such as boehmite are preferred, and alumina and boehmite are more preferred. In addition, from the viewpoint of suppressing the thermal contraction of the separator, compounds containing aluminum are particularly preferred. The ratio of the inorganic filler to the total mass of the heat-resistant layer 87 is preferably 80 mass% or more, more preferably 90 mass% or more, and even more preferably 95 mass% or more.

[0086] The heat-resistant layer binder may be any binder that has been conventionally used for this type of application without any particular limitation. Specific examples include acrylic resins, fluorine-based resins, epoxy resins, urethane resins, ethylene vinyl acetate resins, etc. Among these, acrylic resins are preferred.

[0087] FIG. 14 is a schematic cross-sectional view taken along line XIV-XIV in FIG. 10. For convenience, FIG. 14 omits the description of the members in the middle part of the wound electrode body 20. In addition, D1 in the figure indicates the winding direction, but it is not intended to limit the winding direction to this direction. As shown in FIG. 14, in the wound electrode body 20, the positive electrode sheet 22 and the first separator 71 are bonded by an adhesive layer 81, and the positive electrode sheet 22 and the second separator 72 are bonded by a second adhesive layer 82. In addition, the first separator 71 has a first region (see between AB in FIG. 14) in the vicinity of the winding start end 71a of the first separator. Here, the first adhesive layer 81 is not formed in this first region. In addition, the second separator 72 has a second region (see between CD in FIG. 14) in the vicinity of the winding start end 72a of the second separator. In this second region, the second adhesive layer 82 is not formed. In the wound electrode body 20 having such a configuration, the excessive formation of the adhesive layer is suitably suppressed, and therefore, an increase in the resistance of the battery 100 and a decrease in the impregnation property of the wound electrode body 20 can be suitably suppressed.

[0088] In another embodiment, the first region may include a region where the first adhesive layer 81 is not formed, and / or a region where the first adhesive layer 81 is formed with a basis weight smaller than that of the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22. That is, the first adhesive layer 81 may be formed in the entire first region, or the first region may include a region where the first adhesive layer 81 is formed and a region where the first adhesive layer 81 is not formed. The second region may include a region where the second adhesive layer 82 is not formed, and / or a region where the second adhesive layer 82 is formed with a basis weight smaller than that of the second adhesive layer 82 formed in the region of the second separator 72 facing the positive electrode sheet 22. That is, the second adhesive layer 82 may be formed in the entire second region, or the second region may include a region where the second adhesive layer 82 is formed and a region where the second adhesive layer 82 is not formed. Please refer to the description in <Battery manufacturing method> for the ratio (B / A) of the basis weight B of the first adhesive layer 81 in the first region to the basis weight A of the first adhesive layer 81 in the region facing the positive electrode sheet 22. Also, please refer to the description in <Battery manufacturing method> for the ratio (D / C) of the basis weight D of the second adhesive layer 82 in the second region to the basis weight C of the second adhesive layer 82 in the region facing the positive electrode sheet 22.

[0089] Fig. 12 is a schematic diagram showing a state in which the wound electrode body 20 according to this embodiment is developed, and Fig. 13 is an exploded view of Fig. 12. Note that in Fig. 11, for ease of viewing, each member is shown shifted in the width direction. Here, r a (r a1 ,r a2 ,r an-1 ,r an ) corresponds to the apex of one R portion of the wound electrode body 20. b (r b1 ,r b2 ,r b3 ,r bn) indicates that it corresponds to the apex of the other R portion of the wound electrode body 20. As shown in FIG. 13, the length L1 from the winding start end 71a of the first separator in the winding direction of the first region is greater than the length L2 from the winding start end 72a of the second separator in the winding direction of the second region. This configuration is preferable because it is possible to suppress excessive formation of an adhesive layer on the separator, thereby suppressing an increase in the resistance of the battery 100 and suppressing a decrease in the impregnation of the wound electrode body 20. For the ratio (L1 / L2), please refer to the description in <Battery manufacturing method>.

[0090] In this embodiment, the first adhesive layer is not formed in the region of the first separator 71 that will be the outermost surface of the wound electrode body 20 (see P in FIG. 14). In the wound electrode body 20 having such a configuration, excessive formation of the first adhesive layer 81 is preferably suppressed, and therefore an increase in the resistance of the battery 100 and a decrease in the impregnation property of the wound electrode body 20 can be preferably suppressed.

[0091] In another embodiment, the first separator 71 may have a region in which the first adhesive layer 81 is not formed, and / or a region in which the first adhesive layer 81 is formed with a smaller basis weight than the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22. That is, the first adhesive layer 81 may be formed in the entire region of the first separator 71 that is to be the outermost surface of the wound electrode body 20, or the first separator 71 may have a region in which the first adhesive layer 81 is formed and a region in which the first adhesive layer 81 is not formed in the region of the first separator 71 that is to be the outermost surface of the wound electrode body 20. Here, for example, when the first adhesive layer 81 is not formed in the region of the first separator 71 that is to be the outermost surface of the wound electrode body 20, a winding stop tape can be applied to the winding end 71b of the first separator. As such a winding stop tape, a conventionally known tape used for this type of battery can be used. With regard to the ratio (J / I) of the basis weight J of the first adhesive layer 81 in the region that becomes the outermost surface of the wound electrode body 20 to the basis weight I of the first adhesive layer 81 in the region facing the positive electrode sheet 22, please refer to the description in <Battery manufacturing method>.

[0092] Also, as shown in FIG. 14, in this embodiment, a first adhesive layer 81b having a smaller basis weight than the first adhesive layer 81a in the area facing the positive electrode sheet 22 is formed near the end 71b of the first separator on the surface on which the first adhesive layer 81 is formed.

[0093] The first adhesive layer 81 and the second adhesive layer 82 are bonded to the positive electrode sheet 22 by, for example, heating or pressing (typically, press molding). The first adhesive layer 81 and the second adhesive layer 82 may have the same configuration or different configurations. The first adhesive layer 81 and the second adhesive layer 82 may be formed at a position facing the surface of the positive electrode active material layer 22a, or at a position facing the surface of the positive electrode current collector 22c. Alternatively, they may be formed at a position facing the surface of the positive electrode active material layer 22a and the surface of the positive electrode current collector 22c.

[0094] The first adhesive layer 81 and the second adhesive layer 82 contain an adhesive layer binder. As the adhesive layer binder, a conventionally known resin material having a certain viscosity with respect to the electrode can be used without any particular limitation. Specific examples include acrylic resin, fluorine resin, epoxy resin, urethane resin, polyamide resin, polyimide resin, polyamideimide resin, polyethylene oxide resin, ethylene vinyl acetate resin, polyamic acid resin, and the like. Among them, fluorine resin and acrylic resin are preferable because they have high flexibility and can more suitably exhibit adhesiveness to the electrode. Examples of fluorine resin include polyvinylidene fluoride (PVdF) and polytetrafluoroethylene (PTFE), and the like. Examples of acrylic resin include polyacrylonitrile and polymethyl methacrylate, and the like. The type of the adhesive layer binder may be the same as or different from the heat-resistant layer binder. The ratio of the adhesive layer binder to the total mass of the adhesive layer is preferably 25 mass% or more, may be 50 mass% or more, and more preferably 80 mass% or more. This allows the adhesive to adequately exhibit a desired adhesiveness to the electrode.

[0095] The first adhesive layer 81 and the second adhesive layer 82 may contain other materials (such as the inorganic filler listed as a component of the heat-resistant layer 73) in addition to the adhesive layer binder. When the adhesive layer contains an inorganic filler, the ratio of the inorganic filler to the total mass of the adhesive layer is preferably 75 mass% or less, more preferably 50 mass% or less, and even more preferably 20 mass% or less. The thickness of the first adhesive layer 81 and the second adhesive layer 82 is preferably approximately 0.3 μm or more and 6 μm or less, more preferably 0.5 μm or more and 6 μm or less, and even more preferably 1 μm or more and 4 μm or less.

[0096] Although not particularly limited, the basis weight of the first adhesive layer 81 and the second adhesive layer 82 is 0.005 to 1.0 g / m 2 is preferable, and 0.02 to 0.06 g / m 2 is more preferred.

[0097] The adhesive layer may be formed over the entire surface, or may have a predetermined pattern, such as a dotted, striped, wavy, banded (stripe), dashed line, or a combination thereof, in plan view.

[0098] Battery 100 can be used for various purposes, but can be suitably used, for example, as a power source (driving power source) for a motor mounted on a vehicle such as a passenger car, truck, etc. The type of vehicle is not particularly limited, but examples include a plug-in hybrid electric vehicle (PHEV), a hybrid electric vehicle (HEV), a battery electric vehicle (BEV), etc.

[0099] Although several embodiments of the present disclosure have been described above, the above embodiments are merely examples. The present disclosure can be implemented in various other forms. The present disclosure can be implemented based on the contents disclosed in this specification and the technical common sense in the field. The technology described in the claims includes various modifications and changes to the above-exemplified embodiments. For example, it is possible to replace a part of the above-mentioned embodiment with another modified form, and it is also possible to add another modified form to the above-mentioned embodiment. In addition, if the technical feature is not described as essential, it is also possible to delete it as appropriate.

[0100] For example, in the battery manufacturing method described above, an adhesive layer is formed on the separator, but this is not limited thereto. In the battery manufacturing method disclosed herein, a separator on which an adhesive layer is formed in advance in a desired amount in a desired area can also be used. In such a case, the first adhesive layer forming step and the second adhesive layer forming step described above do not need to be performed.

[0101] For example, in the above-mentioned battery manufacturing method, the first contact area A1 includes the side wall of the first slit Sa in the first separator 71 and the area that contacts the side surface of the winding core 210, but is not limited thereto. For example, when a winding core without a slit is used, the first contact area can be the area that contacts the side surface of the winding core. Also, for example, in the above-mentioned battery manufacturing method, the second contact area A2 includes the side wall of the second slit Sb in the second separator 72 and the area that contacts the side surface of the winding core 210, but is not limited thereto. For example, when a winding core without a slit is used, the second contact area can be the area that contacts the side surface of the winding core.

[0102] For example, the battery manufacturing method described above includes a pressing step, but is not limited thereto. The battery manufacturing method disclosed herein may not include a pressing step, for example, when the wound electrode body is cylindrical. In addition, the battery manufacturing method disclosed herein may include a drying step after forming an adhesive layer on the separator by the coating device 230. In the wound electrode body 20, the content of the organic solvent and / or water in the adhesive layer (first adhesive layer 81, second adhesive layer 82) is preferably 1% or less, more preferably 0.1% or less, and particularly preferably 0.01% or less.

[0103] For example, in the above-mentioned battery manufacturing method, the first adhesive layer 81 is formed in the region of the first separator 71 facing the positive electrode sheet 22, and the second adhesive layer 82 is formed in the region of the second separator 72 facing the positive electrode sheet 22, but this is not limited thereto. In the battery manufacturing method disclosed herein, the first adhesive layer 81 may be formed in a region of the first separator 71 other than the region facing the positive electrode sheet 22, and the second adhesive layer 82 may be formed in a region of the second separator 72 other than the region facing the positive electrode sheet 22. In the battery manufacturing method disclosed herein, for example, the first adhesive layer 81 may be formed in a region of the first separator 71 facing the negative electrode sheet 24, and the second adhesive layer 82 may be formed in a region of the second separator 72 facing the negative electrode sheet 24. In such a case, it is preferable that the basis weight of the first adhesive layer 81 is smaller than the basis weight of the first adhesive layer 81 in the region of the first separator 71 facing the positive electrode sheet 22, and it is preferable that the basis weight of the second adhesive layer 82 is smaller than the basis weight of the second adhesive layer 82 in the region of the second separator 72 facing the positive electrode sheet 22.

[0104] For example, in the above-mentioned battery, the positive electrode tab 22t protrudes from one end in the winding axis direction of the wound electrode body 20, and the negative electrode tab 24t protrudes from the other end, but is not limited to this. The wound electrode body manufactured by the manufacturing method of the battery disclosed herein may be configured so that the positive electrode tab and the negative electrode tab protrude from one end in the winding axis direction of the wound electrode body, or may be configured so as not to have electrode tabs.

[0105] For example, in the battery described above, the outermost surface of the wound electrode body 20 is constituted by the first separator 71, but is not limited to this. The outermost surface of the wound electrode body manufactured by the battery manufacturing method disclosed herein may be constituted by the second separator, or may be constituted by the first separator and the second separator.

[0106] As described above, specific aspects of the technology disclosed herein include those described in the following items. Item 1: A method for manufacturing a battery including a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode and the first separator being bonded by a first adhesive layer, and the positive electrode sheet and the second separator being bonded by a second adhesive layer, the method including the following steps: a first winding step of bringing the first separator and the second separator into contact with a winding core, and winding the first separator and the second separator around the winding core; and a second winding step of winding the positive electrode sheet and the negative electrode sheet together with the first separator and the second separator around the winding core, a first separator having a first region in the vicinity of a winding start end of the first separator, the first region including a region where the first adhesive layer is not formed and / or a region where the first adhesive layer is formed having a smaller basis weight than the first adhesive layer formed in the region of the first separator facing the positive electrode sheet; and a second separator having a second region in the vicinity of a winding start end of the second separator, the second region including a region where the second adhesive layer is not formed and / or a region where the second adhesive layer is formed having a smaller basis weight than the second adhesive layer formed in the region of the second separator facing the positive electrode sheet. Item 2: A method for manufacturing a battery described in item 1, wherein a length L1 of the first region from a winding start end of the first separator in the winding direction is greater than a length L2 of the second region from a winding start end of the second separator in the winding direction. Item 3: The method for producing a battery according to item 1 or 2, wherein in the first winding step, the first separator has a first contact region in contact with the winding core, and the first contact region includes a region where the first adhesive layer is not formed and / or a region where the first adhesive layer is formed and has a smaller basis weight than the first adhesive layer formed in the region of the first separator that faces the positive electrode sheet, and the second separator has a second contact region in contact with the winding core, and the second contact region includes a region where the second adhesive layer is not formed and / or a region where the second adhesive layer is formed and has a smaller basis weight than the second adhesive layer formed in the region of the second separator that faces the positive electrode sheet. Item 4: The method for producing a battery according to item 3, wherein the first region is formed in the first separator, extending to a region other than the first contact region. Item 5: The method for manufacturing a battery according to any one of Items 1 to 4, wherein the first separator is supplied to the winding core from one side with respect to a vertical line that passes through a winding center of the winding core and extends in the vertical direction, and the second separator is supplied to the winding core from the other side. Item 6: The method for producing a battery according to any one of Items 1 to 5, wherein in the first separator and the second separator, in a region that is to be the outermost surface of the wound electrode body, there is a region in which a corresponding adhesive layer is not formed, and / or a region in which the corresponding adhesive layer is formed and has a smaller basis weight than the corresponding adhesive layer formed in the region of the corresponding separator that faces the positive electrode sheet. Item 7: The method for producing a battery according to any one of items 1 to 6, further comprising, after the second winding step, a pressing step of pressing the wound first separator, the positive electrode sheet, the second separator, and the negative electrode sheet, wherein the positive electrode sheet and the first separator are bonded together in the second winding step, and an adhesive strength between the positive electrode sheet and the first separator after the pressing step is greater than an adhesive strength between the positive electrode sheet and the first separator before the pressing step. [Explanation of symbols]

[0107] 10 Battery case 12 Exterior body 14 Sealing plate 20 Wound electrode body 20a Winding body 22 Positive electrode sheet 24 Negative electrode sheet 30 Positive terminal 40 Negative terminal 50 Positive electrode current collector 60 Negative electrode current collector 71 First separator 72 Second separator 81 1st adhesive layer 82 Second adhesive layer 100 batteries 200 Electrode body manufacturing equipment 210 Roll core 220 Lola 230 Coating Equipment 300 Press Machine

Claims

1. A method for manufacturing a battery including a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator being bonded together by a first adhesive layer, and the positive electrode sheet and the second separator being bonded together by a second adhesive layer, the method comprising the steps of: a first winding step of bringing the first separator and the second separator into contact with a winding core and winding the first separator and the second separator around the winding core; and a second winding step of winding the positive electrode sheet and the negative electrode sheet, together with the first separator and the second separator, around the core; Inclusive of the first separator has a first region in the vicinity of a winding start end of the first separator, the first region includes a region in which the first adhesive layer is formed, the region having a basis weight smaller than a basis weight of the first adhesive layer formed in a region of the first separator facing the positive electrode sheet, the second separator has a second region in the vicinity of a winding start end of the second separator, the second region includes a region in which the second adhesive layer is not formed, and / or a region in which the second adhesive layer is formed and has a basis weight smaller than that of the second adhesive layer formed in a region of the second separator facing the positive electrode sheet, a length L1 of the first region from a winding start end of the first separator in the winding direction is greater than a length L2 of the second region from a winding start end of the second separator in the winding direction.

2. A method for manufacturing a battery having a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator being bonded together by a first adhesive layer, and the positive electrode sheet and the second separator being bonded together by a second adhesive layer, the method comprising the following steps: a first winding step of bringing the first separator and the second separator into contact with a winding core and winding the first separator and the second separator around the winding core; and a second winding step of winding the positive electrode sheet and the negative electrode sheet, together with the first separator and the second separator, around the core; Inclusive of the first separator has a first region in the vicinity of a winding start end of the first separator, the first region includes a region in which the first adhesive layer is not formed, and / or a region in which the first adhesive layer is formed and has a basis weight smaller than that of the first adhesive layer formed in a region of the first separator facing the positive electrode sheet, However, except when the amount of the first adhesive layer is constant in all parts of the first separator, the second separator has a second region in the vicinity of a winding start end of the second separator, the second region includes a region in which the second adhesive layer is not formed, and / or a region in which the second adhesive layer is formed and has a basis weight smaller than that of the second adhesive layer formed in a region of the second separator facing the positive electrode sheet, a length L1 of the first region from a winding start end of the first separator in the winding direction is greater than a length L2 of the second region from a winding start end of the second separator in the winding direction.

3. A method for manufacturing a battery having a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator being bonded together by a first adhesive layer, and the positive electrode sheet and the second separator being bonded together by a second adhesive layer, the method comprising the following steps: a first winding step of bringing the first separator and the second separator into contact with a winding core and winding the first separator and the second separator around the winding core; and a second winding step of winding the positive electrode sheet and the negative electrode sheet, together with the first separator and the second separator, around the core; Inclusive of In the first winding step, the first separator has a first contact region that contacts the winding core, the first contact region includes a region in which the first adhesive layer is formed, the region having a basis weight smaller than a basis weight of the first adhesive layer formed in a region of the first separator facing the positive electrode sheet, the first separator has a first region in the vicinity of a winding start end of the first separator, the first region includes a region in which the first adhesive layer is not formed, and / or a region in which the first adhesive layer is formed and has a basis weight smaller than that of the first adhesive layer formed in a region of the first separator facing the positive electrode sheet, the second separator has a second region in the vicinity of a winding start end of the second separator, the second region includes a region where the second adhesive layer is not formed, and / or a region where the second adhesive layer is formed having a smaller basis weight than the second adhesive layer formed in the region of the second separator facing the positive electrode sheet.

4. 4. The method for manufacturing a battery according to claim 3, wherein a length L1 of the first region from a winding start end of the first separator in the winding direction is greater than a length L2 of the second region from a winding start end of the second separator in the winding direction.

5. In the first winding step, the first separator has a first contact region that contacts the winding core, in the first contact region, there is a region in which the first adhesive layer is not formed, and / or a region in which the first adhesive layer is formed and has a basis weight smaller than that of the first adhesive layer formed in a region of the first separator facing the positive electrode sheet, the second separator has a second contact region that contacts the winding core, 3. The method for manufacturing a battery according to claim 1, wherein the second contact region includes a region in which the second adhesive layer is not formed, and / or a region in which the second adhesive layer is formed, the second adhesive layer having a basis weight smaller than that of the second adhesive layer formed in the region of the second separator facing the positive electrode sheet.

6. The method for manufacturing a battery according to claim 3 , wherein the first region is formed in the first separator so as to extend to a region other than the first contact region.

7. With respect to a vertical line passing through the winding center of the winding core and extending in the vertical direction, the first separator is supplied to the core from one side, The method for manufacturing a battery according to any one of claims 1 to 3, wherein the second separator is supplied to the core from the other side.

8. The method for manufacturing a battery according to any one of claims 1 to 3, wherein in an area of ​​the first separator and the second separator that is to be the outermost surface of the wound electrode body, there is a area where a corresponding adhesive layer is not formed, and / or a area where the corresponding adhesive layer is formed and has a smaller basis weight than the corresponding adhesive layer formed in the area of ​​the corresponding separator that faces the positive electrode sheet.

9. a pressing step of pressing the wound first separator, the positive electrode sheet, the second separator, and the negative electrode sheet after the second winding step, In the second winding step, the positive electrode sheet and the first separator are bonded to each other, The method for manufacturing a battery according to any one of claims 1 to 3, wherein an adhesive strength between the positive electrode sheet and the first separator after the pressing step is greater than an adhesive strength between the positive electrode sheet and the first separator before the pressing step.