Battery manufacturing method

Abstract

To provide a technique of obtaining a battery including a wound electrode body equipped with an adhesive layer, with high productivity.SOLUTION: A manufacturing method for a battery 100 disclosed herein includes a first forming step S1 of forming a first adhesive layer 81 on a surface of a first separator 71, a second forming step S2 of forming a second adhesive layer 82 on a surface of a positive electrode sheet 22, and a stacking step S3 of stacking the first separator 71, the positive electrode sheet 22, a second separator 72, and a negative electrode sheet 24.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present disclosure relates to a method for manufacturing a battery. [Background technology]

[0002] Japanese Patent No. 5328034 discloses a wound electrode assembly in which a separator is bonded and integrated to at least one of a positive electrode sheet and a negative electrode sheet by an adhesive resin contained in the separator. It is described that such a wound electrode assembly can be manufactured by a manufacturing method including a step of forming a wound electrode assembly using a separator previously provided with an adhesive resin, and a step of subjecting the wound electrode assembly to a hot press to integrate at least one of a positive electrode sheet and a negative electrode sheet with the separator. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Patent No. 5328034 Summary of the Invention [Problem to be solved by the invention]

[0004] Meanwhile, there is a demand for further development of technology that can produce batteries including a wound electrode body provided with an adhesive layer with high productivity. [Means for solving the problem]

[0005] The method for manufacturing a battery disclosed herein is a method for manufacturing a battery including a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator are bonded by a first adhesive layer, and the positive electrode sheet and the second separator are bonded by a second adhesive layer, and includes the following steps: a first forming step of forming the first adhesive layer on the surface of the first separator; a second forming step of forming the second adhesive layer on the surface of the positive electrode sheet; and a laminating step of laminating the first separator, the positive electrode sheet, the second separator, and the negative electrode sheet. According to this method for manufacturing a battery, in the first forming step and the second forming step, the first adhesive layer and the second adhesive layer can be formed at desired positions according to the wound electrode body. This makes it possible to obtain a battery including a wound electrode body provided with an adhesive layer with high productivity. [Brief description of the drawings]

[0006] [Figure 1] FIG. 2 is a flow diagram showing a method for manufacturing a battery according to an embodiment. [Diagram 2] FIG. 2 is a schematic diagram showing a configuration of an electrode body manufacturing apparatus according to one embodiment. [Figure 3A] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 3B] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 3C] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 3D] 1 is an explanatory diagram for explaining a method for winding a member around a winding core according to one embodiment. FIG. [Figure 4A] FIG. 11 is an explanatory diagram for explaining a pressing step. [Figure 4B] FIG. 11 is an explanatory diagram for explaining a pressing step. [Diagram 5]FIG. 1 is a perspective view showing a battery according to an embodiment of the present invention. [Figure 6] FIG. 6 is a schematic vertical cross-sectional view taken along line VI-VI in FIG. 5. [Figure 7] FIG. 7 is a schematic vertical cross-sectional view taken along line VII-VII in FIG. 5. [Figure 8] FIG. 6 is a schematic cross-sectional view taken along line VIII-VIII in FIG. 5. [Figure 9] FIG. 2 is a perspective view showing a schematic view of an electrode body attached to a sealing plate. [Figure 10] FIG. 2 is a perspective view that shows a schematic diagram of an electrode assembly to which a positive electrode second current collector and a negative electrode second current collector are attached. [Figure 11] FIG. 2 is a schematic diagram showing the configuration of a wound electrode body according to one embodiment. [Figure 12] FIG. 2 is a schematic diagram showing a state in which a wound electrode body according to one embodiment is unfolded. [Figure 13] FIG. 13 is an exploded view of FIG. [Figure 14] FIG. 14 is a schematic vertical cross-sectional view taken along line XIV-XIV in FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0007] Hereinafter, some embodiments of the technology disclosed herein will be described with reference to the drawings. It should be noted that matters other than those specifically mentioned in this specification and necessary for implementing the technology disclosed herein (for example, the general configuration and manufacturing process of a battery that does not characterize the present invention) can be understood as design matters of a person skilled in the art based on the conventional technology in the field. The technology disclosed herein can be implemented based on the contents disclosed in this specification and the technical common sense in the field. In addition, the following explanation is not intended to limit the technology disclosed herein to such explanation. In this specification, the expression "A to B" indicating a range includes the meaning of "A or more and B or less", as well as "greater than A" and "less than B".

[0008] In this specification, the term "battery" refers to a general term for an electricity storage device capable of extracting electric energy, and is a concept that includes primary batteries and secondary batteries. In addition, in this specification, the term "secondary battery" refers to a general term for an electricity storage device capable of repeated charging and discharging by the movement of charge carriers between a positive electrode sheet and a negative electrode sheet via an electrolyte. The electrolyte may be any of a liquid electrolyte (electrolytic solution), a gel electrolyte, and a solid electrolyte. Such secondary batteries include so-called storage batteries (chemical batteries) such as lithium ion secondary batteries and nickel hydrogen batteries, as well as capacitors (physical batteries) such as electric double layer capacitors. In the following, an embodiment in which a lithium ion secondary battery is the subject will be described. In the following description, the adhesive layer formed on the first separator 71 will be referred to as the first adhesive layer 81, and the adhesive layer formed on the positive electrode sheet 22 will be referred to as the second adhesive layer 82.

[0009] <Battery manufacturing method> First, a method for manufacturing a battery according to this embodiment will be described. FIG. 1 is a flow diagram showing a method for manufacturing a battery according to this embodiment. As shown in FIG. 1, the method for manufacturing a battery according to this embodiment includes a first forming step (step S1) of forming a first adhesive layer 81 on the surface of a first separator 71; a second forming step (step S2) of forming a second adhesive layer 82 on the surface of a positive electrode sheet 22; and a lamination step (step S3) of laminating the first separator 71, the positive electrode sheet 22, the second separator 72, and the negative electrode sheet 24. Here, the "surface of the positive electrode sheet" may be the surface of the positive electrode active material layer 22a or the surface of the positive electrode collector 22c. When the first adhesive layer 81 and / or the second adhesive layer 82 are provided on the surface of the positive electrode sheet 22, preferably, the positive electrode sheet 22 is provided with the positive electrode active material layer 22a on both surfaces of the positive electrode collector 22c, and the first adhesive layer 81 and / or the second adhesive layer 82 are provided on the surface of the positive electrode active material layer 22a. The battery manufacturing method disclosed herein may further include other steps at any stage, and if the steps are not described as essential, they may be deleted as appropriate. In addition, the order of the steps may be changed as long as the effects of the technology disclosed herein are achieved. The battery manufacturing method according to this embodiment will be described below with reference to an electrode body manufacturing apparatus 200 that embodies the battery manufacturing method.

[0010] FIG. 2 is a schematic diagram showing the configuration of an electrode assembly manufacturing apparatus 200 according to this embodiment. The electrode assembly manufacturing apparatus 200 is an apparatus for manufacturing a wound electrode assembly 20 in which a strip-shaped first separator 71, a strip-shaped positive electrode sheet 22, a strip-shaped second separator 72, and a strip-shaped negative electrode sheet 24 are wound together, in which the positive electrode sheet 22 and the first separator 71 are bonded together by a first adhesive layer 81, and the positive electrode sheet 22 and the second separator 72 are bonded together by a second adhesive layer 82. As shown in FIG. 2, the electrode assembly manufacturing apparatus 200 includes a winding core 210, a plurality of rollers 220, and a coating device 230. The electrode assembly manufacturing apparatus 200 also includes a cutter (not shown), a pressing tool, and a control device. Here, the cutter is a cutter that cuts the first separator 71 and the second separator 72. The pressing jig is a jig that presses the first separator 71 and the second separator 72 against the winding core 210. Each component of the electrode body manufacturing apparatus 200 has a required actuator as appropriate. The control device is configured to control each component of the electrode body manufacturing apparatus 200 so that a required operation is performed at a specified timing according to a preset program. The control device can be embodied by a computer such as a microcontroller, for example.

[0011] The positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72 are prepared in a state of being wound around a reel (not shown) or the like. The positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72 are transported along predetermined transport paths k1 to k4. The transport path k1 is a path along which the positive electrode sheet 22 is fed from a reel (not shown) toward the winding core 210. The transport path k2 is a path along which the negative electrode sheet 24 is fed from a reel (not shown) toward the winding core 210. The transport path k3 is a path along which the first separator 71 is fed from a reel (not shown) toward the winding core 210. The transport path k4 is a path along which the second separator 72 is fed from a reel (not shown) toward the winding core 210. It is preferable that a dancer roll mechanism for removing slack in the positive electrode sheet 22, negative electrode sheet 24, first separator 71, and second separator 72 being fed, a tensioner for adjusting tension, and the like are appropriately disposed on each of the transport paths k1 to k4.

[0012] The multiple rollers 220 are disposed on the transport paths k1 to k4 of the positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72, respectively. The multiple rollers 220 are an example of a transport device. The multiple rollers 220 are disposed at predetermined positions to define the transport paths k1 to k4. The positive electrode sheet 22, the negative electrode sheet 24, the first separator 71, and the second separator 72 are each transported by the multiple rollers 220.

[0013] The winding core 210 has a function of holding the first separator 71 and the second separator 72 wound around the side peripheral surface. The winding core 210 is a substantially cylindrical member here, but a flat winding core may be used when winding into a flat shape. A winding core divided along the radial direction is used as the winding core 210 here, but an undivided winding core may be used, or a winding core with a variable diameter may be used. The winding core 210 has a first slit Sa and a second slit Sb. The first slit Sa and the second slit Sb are arranged at positions 180° apart along the rotation direction of the winding core 210 here. Each separator can be fixed to the winding core 210 by sandwiching the tip of the first separator 71 in the first slit Sa and sandwiching the tip of the second separator 72 in the second slit Sb.

[0014] The winding core 210 may further have a suction hole, a groove, or the like. The suction hole is a hole for adsorbing the first separator 71 and the second separator 72 wound around the side peripheral surface. The shape of the suction hole in a plan view may be circular or rectangular. Alternatively, the suction hole may be slit-shaped. The suction hole typically has a suction flow path that is a flow path formed inside the winding core 210 and connected to the suction hole. The suction path is a flow path for forming a negative pressure in the suction hole. The suction path may be configured to be appropriately connected to a vacuum line installed outside, for example, so that a negative pressure is formed. The groove can function as a receiving portion for lowering the blade of the cutter when the first separator 71 and the second separator 72 are cut. This suppresses damage to the winding core or the cutter due to contact between the winding core 210 and the blade of the cutter.

[0015] The coating device 230 is a device that applies a binder liquid (adhesive) to the surfaces of the first separator 71 and the positive electrode sheet 22 along the conveying direction. The coating device 230 is configured to be able to coat the binder liquid in a desired amount on a desired region of the first separator 71 and the positive electrode sheet 22. The binder liquid includes, for example, an adhesive layer binder as described later, and a solvent. As the solvent for the binder liquid, a so-called aqueous solvent is preferably used from the viewpoint of reducing the environmental load. In this case, water or a mixed solvent mainly composed of water can be used. As the solvent component other than water that constitutes such a mixed solvent, one or more organic solvents (lower alcohols, lower ketones, etc.) that can be mixed uniformly with water can be appropriately selected and used. For example, it is preferable to use an aqueous solvent in which 80 mass % or more (more preferably 90 mass % or more, and even more preferably 95 mass % or more) of the aqueous solvent is water. A particularly preferable example is an aqueous solvent that is substantially composed of water. In addition, the solvent for the binder liquid is not limited to a so-called aqueous solvent, and may be a so-called organic solvent system. An example of an organic solvent-based solvent is N-methylpyrrolidone. For example, a suitable example of the binder liquid is one in which water is used as a solvent and an acrylic resin (e.g., polymethacrylic acid ester resin) is mixed as a binder. The binder liquid may contain one or more additives such as a known thickener or surfactant for the purpose of improving wettability with respect to the positive electrode sheet 22 or the separator, as long as the effect of the technology disclosed herein is not hindered.

[0016] As the coating device 230, various coating devices can be used, for example, inkjet printing, various intaglio printing machines such as a gravure roll coater, a spray coater, die coaters such as a slit coater, a comma coater, a Capillary Coater (CAP coater), a lip coater, a calendar machine, etc.

[0017] As shown in Fig. 2, in this embodiment, a formation area for forming a first adhesive layer 81 on the surface of the first separator 71 facing the positive electrode sheet 22 and a formation area for forming a second adhesive layer 82 on the surface of the positive electrode sheet 22 are provided on one side of a vertical line l1 that passes through the winding center O of the winding core 210 and extends in the vertical direction (see Area 1 in Fig. 2). By providing the adhesive layer formation areas separately in this manner, the space required for the coating device can be reduced, which is preferable. In Area 1, the positive electrode sheet 22 is disposed above the first separator 71, and in Area 2, the negative electrode sheet 24 is disposed below the second separator 72.

[0018] Although not particularly limited, the angle θ between the adhesive layer forming region of the first separator 71 (in other words, the conveying path k3) and the straight line l2 that passes through the winding center O of the winding core 210 and extends in the horizontal direction is k3 From the viewpoint of improving coating unevenness in the width direction of the first separator 71 and forming a more uniform adhesive layer, the angle θ is preferably −30° to +30°, and more preferably −15° to +15°. From the same viewpoint, the angle θ of the adhesive layer formation region of the positive electrode sheet 22 (in other words, the conveying path k1) with respect to the straight line l3 existing in a position parallel to the straight line l2 is k1 is preferably −30° to +30°, and more preferably −15° to +15°. k1 and θ k3 is set to approximately -30°.

[0019] 3A to 3D are explanatory diagrams for explaining a method of winding a member around the winding core 210 according to the present embodiment. Here, the arrows in FIGS. 3A to 3D indicate the rotation direction of the winding core 210, but are not intended to limit the rotation direction of the winding core 210 to this direction. Also, the star marks in the figures are added to make the rotation mode of the winding core 210 easier to understand. Also, in the figures, the positive electrode tab 22t and the negative electrode tab 24t are omitted for ease of viewing.

[0020] 3A, the leading end of the first separator 71 (in other words, the winding start end 71a of the first separator) is sandwiched in the first slit Sa, and the leading end of the second separator 72 (in other words, the winding start end 72a of the second separator) is sandwiched in the second slit Sb. In this embodiment, the first slit Sa and the second slit Sb function as electrostatic chucks, thereby fixing the leading end of the first separator 71 and the leading end of the second separator 72 to the winding core 210. This configuration is preferable because it can prevent the leading end of the first separator 71 and the leading end of the second separator 72 from being left with a clamping mark or the like.

[0021] Next, as shown in Fig. 3B, the winding core 210 is rotated approximately half a turn in the direction of the arrow to bring the first separator 71 and the second separator 72 into contact with the winding core 210, and the first separator 71 and the second separator 72 are wound around the winding core 210. As shown in Fig. 3B, in this embodiment, the first separator 71 is in contact with the side wall of the first slit Sa and the side surface of approximately half the winding core 210 (see the first contact area A1 in Fig. 3B). Also, the second separator 72 is in contact with the side wall of the second slit Sb and the side surface of approximately half the winding core 210 (see the second contact area A2 in Fig. 3B).

[0022] Next, as shown in FIG. 3C, the negative electrode sheet 24 is sandwiched between the first separator 71 wound around the winding core 210 and the second separator 72 to be supplied. Then, as shown in FIG. 3D, after the winding core 210 is rotated approximately half a turn, the positive electrode sheet 22 is sandwiched between the second separator 72 wound around the winding core 210 and the first separator 71 to be supplied. Then, the application device 230 starts forming the first adhesive layer 81 on the surface of the first separator 71 and the application device 230 starts forming the second adhesive layer 82 on the surface of the positive electrode sheet 22 (first forming step, second forming step). Then, the winding core 210 is rotated in the direction of the arrow to stack the first separator 71, the positive electrode sheet 22, the second separator 72, and the negative electrode sheet 24 (stacking step). This stacking step is preferably a winding step. Then, each member is wound around the winding core 210 until a predetermined number of windings is reached. In this manner, a wound body 20a can be obtained in which the positive electrode sheet 22 and the first separator 71 are bonded together by the first adhesive layer 81, and the positive electrode sheet 22 and the second separator 72 are bonded together by the second adhesive layer .

[0023] 3C, in this embodiment, the negative electrode sheet 24 is sandwiched when the first separator 71 is wound around the winding core 210 by approximately half a turn, but this is not limited to this. For example, in other embodiments, from the viewpoint of making it easier to remove the wound body 20a from the winding core 210, the negative electrode sheet 24 may be sandwiched when the first separator 71 is wound around the side wall of the first slit Sa and approximately one turn of the winding core 210. However, these are merely examples, and the timing of sandwiching the negative electrode sheet 24 can be appropriately adjusted depending on the type of wound electrode body to be manufactured, etc.

[0024] Although not particularly limited, in the first forming step, the formation start position of the first adhesive layer 81 on the first separator 71 may be the same position as the position where the positive electrode sheet 22 is sandwiched, or may be a position closer to the winding start end 71a of the first separator than the position where the positive electrode sheet 22 is sandwiched (for example, a position 10 mm or 20 mm closer to the winding start end 71a of the first separator). This configuration is preferable because it allows the first adhesive layer 81 to be formed more reliably in the region of the first separator 71 facing the positive electrode sheet 22. Note that in this embodiment, in the first forming step, the formation start position of the first adhesive layer 81 on the first separator 71 is a position closer to the winding start end 71a of the first separator than the position where the positive electrode sheet 22 is sandwiched (see FIG. 13 and FIG. 14).

[0025] Although not particularly limited, the end position of the formation of the first adhesive layer 81 in the first separator 71 may be a position facing the end end 22T of the positive electrode sheet in the first separator 71, or may be a position closer to the end end 71b of the first separator than the position facing the end end 22T of the positive electrode sheet in the first separator 71 (for example, a position 10 mm or 20 mm closer to the end end 71b of the first separator). According to such a configuration, the first adhesive layer 81 can be formed more reliably in the region facing the positive electrode sheet 22 in the first separator 71, which is preferable. In this embodiment, the end position of the formation of the first adhesive layer 81 (here, the first adhesive layer 81a) in the first separator 71 is closer to the end end 71b of the first separator than the position facing the end end 22T of the positive electrode sheet in the first separator 71 (see FIG. 13 and FIG. 14). In this embodiment, a first adhesive layer 81b is further formed in the vicinity of the winding end 71b of the first separator (see FIGS. 13 and 14).

[0026] According to the battery manufacturing method disclosed herein, in the first forming step and the second forming step, the first adhesive layer 81 is formed on one side of the first separator 71, and the second adhesive layer 82 is formed on one side of the positive electrode sheet 22. According to the battery manufacturing method having such a configuration, for example, it is possible to suitably suppress adhesion of the adhesive layer to the roller 220. As a result, the conveyance of the first separator 71 and the positive electrode sheet 22 is not hindered due to the adhesive layer attached to the roller 220. Therefore, continuous production of the wound electrode body 20 is not hindered, and it is possible to suitably suppress a decrease in the yield of the wound electrode body 20. As a result, it is possible to obtain the battery 100 having the wound electrode body 20 including the separator provided with the adhesive layer with high productivity. In addition, it is preferable because the adhesive layer formed by the roller 220 is less likely to be damaged. In this embodiment, the first forming step and the second forming step are performed simultaneously, but this is not limited thereto, and one of the steps may be performed first and the other step may be performed later.

[0027] In the battery manufacturing method disclosed herein, in the lamination step, the first separator 71, the positive electrode sheet 22, the second separator 72, and the negative electrode sheet 24 may be transported and wound while being stacked in a predetermined order. Also, in the first forming step, a first adhesive layer 81 may be formed on the surface of the first separator 71 being transported in the lamination step that is to be stacked on the positive electrode sheet 22. Then, in the second forming step, a second adhesive layer 82 may be formed on the surface of the positive electrode sheet 22 being transported in the lamination step that is to be stacked on the second separator 72. According to the battery manufacturing method having such a configuration, it is not necessary to wind up the first separator 71 and the positive electrode sheet 22 on a reel after the formation of the adhesive layer, and therefore unintended adhesion of the formed adhesive layer can be suitably suppressed, which is preferable.

[0028] In a preferred embodiment, the adhesive layer forming step (here, the first forming step and the second forming step) is performed immediately before the lamination step. In other words, it is preferable to perform the adhesive layer forming step and the lamination step consecutively with the separator unfolded. According to the manufacturing method of the battery having such a configuration, the position where the adhesive layer is formed can be more suitably controlled, so that the adhesive layer can be arranged at a more appropriate position in the wound electrode body 20. Here, the distance between the position where the adhesive layer is formed (here, the position where the coating device 230 exists) and the position of the winding core 210 is, for example, less than 50 m, may be less than 10 m, or may be less than 3 m. In addition, the time from the end of the adhesive layer forming step to the start of the lamination step is, for example, less than 60 minutes, may be less than 20 minutes, or may be less than 5 minutes. The above-mentioned distance and time can be appropriately changed according to the actual embodiment.

[0029] In the battery manufacturing method disclosed herein, in the first forming step, a region where the first adhesive layer 81 is not formed and / or a region where the first adhesive layer 81 is formed with a smaller basis weight than the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22 may be formed in a predetermined first region near the winding start end 71a of the first separator. That is, in the battery manufacturing method disclosed herein, the first adhesive layer 81 may be formed in the entire first region, or the first adhesive layer 81 may be formed in the entire first region. Alternatively, the first adhesive layer 81 may be formed in the region where the first adhesive layer 81 is not formed in the first region. Note that the "first region near the winding start end of the first separator" refers to a region from the winding start end 71a of the first separator to, for example, 50%, or may be a region up to 100%, 120%, 150%, or 200%, when the length of the innermost circumference of the winding core 210 is taken as 100%. Alternatively, when the length of the innermost circumference of the wound electrode body 20 is taken as 100%, it may be, for example, a region up to 50%, 100%, 120%, 150%, or 200% from the winding start end 71a of the first separator. For example, in this embodiment, the vicinity of the winding start end 71a of the first separator is a region within 2 cm from the winding start end 71a of the first separator. However, this is not limited to this. In addition, the "basis weight" (basis weight amount) refers to the value obtained by dividing the mass of the adhesive layer by the area of ​​the formation area (mass of the adhesive layer / area of ​​the formation area).

[0030] According to the manufacturing method of the battery having such a configuration, the first adhesive layer 81 is not formed near the winding start end 71a of the first separator, or the basis weight of the first adhesive layer 81 formed is small. Therefore, the amount of the first adhesive layer 81 attached to the winding core 210 is suitably suppressed. As a result, even if the first adhesive layer 81 is attached to the winding core 210, the amount is small. And, the continuous production of the wound electrode body 20 is not hindered due to the first adhesive layer 81 attached to the winding core 210, and it is possible to suitably suppress a decrease in the yield of the wound electrode body 20. As a result, it is possible to obtain the battery 100 including the wound electrode body 20 including the separator provided with the adhesive layer with higher productivity.

[0031] Although not particularly limited, when the first adhesive layer 81 is formed in the first region in the first formation step, the ratio (B / A) of the basis weight B of the first adhesive layer 81 in the first region to the basis weight A of the first adhesive layer 81 in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and from the viewpoint of appropriately controlling the amount of the first adhesive layer 81 that can adhere to the winding core, is preferably 0.8 or less, more preferably 0.5 or less, and particularly preferably 0.3 or less, and may be, for example, 0.1 or less.

[0032] In this embodiment, in the first formation process, a region in which the first adhesive layer 81 is not formed is formed in a predetermined first region (here, the first contact region A1 and the region A3 described later) near the winding start end 71a of the first separator.

[0033] 3D, in this embodiment, a region in which the second separator 72 is disposed is formed between the first separator 71 and the winding core 210. In other words, in this embodiment, the first separator 71 extends to a region other than the first contact region A1 to form a region in which the first adhesive layer 81 is not formed (see region A3 in FIG. 3D).

[0034] That is, in the battery manufacturing method disclosed herein, the first region may be formed by extending to a region other than the first contact region (here, the first contact region A1) in the first separator 71. According to the battery manufacturing method configured in this way, in addition to improving the productivity of the battery 100 including the wound electrode body 20 provided with an adhesive layer, excessive formation of the first adhesive layer 81 on the first separator 71 can be suppressed, which is preferable because it can realize suppression of an increase in the resistance of the battery 100 and suppression of a decrease in the impregnation property of the wound electrode body 20.

[0035] In the manufacturing method of the battery disclosed herein, the first separator 71 and the second separator 72 may have a region in which the corresponding adhesive layer (i.e., the first adhesive layer 81 and / or the second adhesive layer 82) is not formed, and / or a region in which the corresponding adhesive layer having a smaller basis weight than the corresponding adhesive layer formed in the region facing the positive electrode sheet 22 in the corresponding separator is formed. In other words, in the wound electrode body 20 disclosed herein, an adhesive layer corresponding to the entire region that will be the outermost surface of the wound electrode body 20 may not be formed, or an adhesive layer corresponding to the entire region that will be the outermost surface of the wound electrode body 20 may be formed. Alternatively, a region in which a corresponding adhesive layer is formed and a region in which a corresponding adhesive layer is not formed may be formed. According to the manufacturing method of the battery having such a configuration, adhesion of the adhesive layer to the electrode body manufacturing apparatus 200 can be suitably prevented, and therefore the productivity of the battery 100 including the wound electrode body 20 provided with the adhesive layer can be more suitably improved.

[0036] Although not particularly limited, when forming an adhesive layer corresponding to the region that will become the outermost surface of the wound electrode body 20, the ratio (D / C) of the basis weight D of the corresponding adhesive layer in the region that will become the outermost surface of the wound electrode body 20 to the basis weight C of the corresponding adhesive layer in the region facing the positive electrode sheet 22 is, for example, 0.9 or less, and may be 0.8 or less, 0.5 or less, 0.3 or less, or 0.1 or less.

[0037] In this embodiment, the first separator 71 has a region that is to become the outermost surface of the wound electrode body 20, where the first adhesive layer 81 is not formed (see P in FIG. 14).

[0038] In the manufacturing method of the battery disclosed herein, the first separator 71 may have a region where the first adhesive layer 81 is not formed near the winding end 71b of the first separator on the surface on which the first adhesive layer 81 is formed, and / or a region where the first adhesive layer 81 is formed with a smaller basis weight than the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22. That is, in the wound electrode body 20 disclosed herein, the first separator 71 may have a region where the first adhesive layer 81 is not formed near the entire winding end 71b of the first separator on the surface on which the first adhesive layer 81 is formed, or the first separator 71 may have a region where the first adhesive layer 81 is not formed near the entire winding end 71b of the first separator on the surface on which the first adhesive layer 81 is formed. Alternatively, a region where the first adhesive layer 81 is formed and a region where the first adhesive layer 81 is not formed may be formed. According to the manufacturing method of a battery having such a configuration, adhesion of the first adhesive layer to the cutter that cuts the separator can be effectively suppressed, and therefore the productivity of the battery 100 including the wound electrode body 20 provided with the adhesive layer can be effectively improved.

[0039] In addition, the "near the end of the first separator" refers to, for example, a region of up to 5%, or may be within 10%, or may be within 20%, from the end of the first separator when the outermost circumference of the wound body 20a is taken as 100%. Alternatively, the "near the end of the first separator" refers to, for example, a region of up to 5%, or may be within 10%, or may be within 20%, from the end of the first separator when the outermost circumference of the wound electrode body 20 is taken as 100%. For example, in this embodiment, the "near the end of the first separator" refers to a region of up to 2 cm from the end of the first separator. However, this is not limited to this.

[0040] Although not particularly limited, when the first adhesive layer 81 is formed on the surface of the first separator 71 on which the first adhesive layer 81 is formed, the ratio (F / E) of the basis weight F of the first adhesive layer 81 in the vicinity of the end winding end 71b of the first separator to the basis weight E of the corresponding adhesive layer in the area facing the positive electrode sheet 22 is, for example, 0.9 or less, and may be 0.8 or less, 0.5 or less, 0.3 or less, or 0.1 or less.

[0041] In this embodiment, the first separator 71 has a first adhesive layer 81b formed near the winding end 71b of the first separator on the surface on which the first adhesive layer 81 is formed, the first adhesive layer 81b having a smaller basis weight than the first adhesive layer 81a in the region facing the positive electrode sheet 22 (see FIG. 14). This battery manufacturing method is preferable from the viewpoint of simplifying battery manufacturing because it effectively prevents the first adhesive layer 81 from sticking to a cutter that cuts the separator and does not require application of a winding stop tape around the winding end 71b of the first separator.

[0042] 13, in this embodiment, the formation area of ​​the first adhesive layer (here, first adhesive layers 81a and 81b) formed on the first separator 71 is larger than the formation area of ​​the second adhesive layer 82 formed on the positive electrode sheet 22. In other words, in the battery manufacturing method disclosed herein, the first adhesive layer 81 and the second adhesive layer 82 may be formed so that the formation area of ​​the first adhesive layer 81 formed on the first separator 71 is larger than the formation area of ​​the second adhesive layer 82 formed on the positive electrode sheet 22 when the wound electrode body 20 is unfolded. According to the battery manufacturing method having such a configuration, it is possible to suppress excessive formation of adhesive layers on the first separator 71 and the positive electrode sheet 22, which is preferable because it is possible to suppress an increase in the resistance of the battery 100 and a decrease in the impregnation property of the wound electrode body 20.

[0043] Although not particularly limited, the ratio (H / G) of the formation area H of the first adhesive layer 81 formed on the first separator 71 to the formation area G of the second adhesive layer 82 formed on the positive electrode sheet 22 is, for example, 1.1 or more, and may be 1.2 or more, or 1.5 or more. The upper limit of the ratio (H / G) is, for example, 3 or less, 2.5 or less, or 2 or less.

[0044] As shown in FIG. 2, in this embodiment, the first separator 71 and the positive electrode sheet 22 are supplied to the winding core 210 from one side with respect to the vertical line l1. As in this embodiment, it is preferable to form a first adhesive layer 81 and a second adhesive layer 82 on the upper surface of the first separator 71 and the upper surface of the positive electrode sheet 22, respectively. In addition, the first separator 71 is supplied to the winding core 210 from one side with respect to the vertical line l1, and the second separator 72 is supplied to the winding core 210 from the other side. This configuration allows the position of the winding end end 71a of the first separator, the position of the winding end end 72a of the second separator, the length of each separator, the cutting position, etc. to be set with a higher degree of freedom, and is preferable because the adhesive layer formed on the separator makes it easier to eliminate the winding stop tape. The positive electrode sheet 22 is supplied to the winding core 210 from the same side as the first separator 71 with respect to the vertical line l1, and the negative electrode sheet 24 is supplied to the winding core 210 from the other side of the vertical line l1 as the second separator. The first separator 71 is supplied from above the positive electrode sheet 22, and the second separator 72 is supplied from below the negative electrode sheet 24.

[0045] In the battery manufacturing method disclosed herein, the angle θ of the conveying path k3 with respect to a straight line l2 that passes through the winding center O of the winding core 210 and extends in the horizontal direction is k3 It is preferable that the first adhesive layer 81 is formed on the first separator 71 when the first separator 71 passes through a region in which the angle between the first separator 71 and the straight line l3, which is parallel to the straight line l2, is θ k4It is preferable to form the second adhesive layer 82 on the positive electrode sheet 22 when the sheet passes through a region where the inclination angle is, for example, −30° to +30° (preferably, −15° to +15°). This improves uneven coating in the width direction of the separator, and allows the adhesive layer to be formed more uniformly.

[0046] In this embodiment, after the lamination step, the laminated (wound) first separator 71, positive electrode sheet 22, second separator 72, and negative electrode sheet 24 are pressed (pressing step). Here, FIG. 4A and FIG. 4B are explanatory views for explaining the pressing step. In the pressing step, the wound body 20a manufactured as described above is removed from the winding core 210 and pressed by a press machine 300. This makes it possible to obtain a flat-shaped wound electrode body 20. In addition, it is preferable to press the positive electrode sheet 22 and the first separator 71 so that the adhesive strength of the positive electrode sheet 22 and the first separator 71 after the pressing step is greater than the adhesive strength of the positive electrode sheet 22 and the first separator 71 before the pressing step. It is preferable to press the positive electrode sheet 22 and the second separator 72 so that the adhesive strength of the positive electrode sheet 22 and the second separator 72 after the pressing step is greater than the adhesive strength of the positive electrode sheet 22 and the second separator 72 before the pressing step. The manufacturing method for a battery having such a configuration is preferable because it provides an opportunity to loosen the wound body 20a after winding in order to prevent buckling.

[0047] Although not particularly limited, the ratio (N / M) of the adhesive strength M of the positive electrode sheet 22 and the first separator 71 before the pressing process to the adhesive strength N of the positive electrode sheet 22 and the first separator 71 after the pressing process is, for example, 1.2 or more, and may be 1.5 or more, or 2 or more. Note that this adhesive strength may mean, for example, an adhesive strength measured by a conventionally known measuring method using a positive electrode sheet-separator laminate of a predetermined area (e.g., a sample of 5 cm x 5 cm). Note that the above description can also be referred to for the ratio of the adhesive strength of the positive electrode sheet 22 and the second separator 72 before the pressing process to the adhesive strength of the positive electrode sheet 22 and the second separator 72 after the pressing process.

[0048] Three of the above-mentioned wound electrode bodies 20 are prepared, inserted into a battery case 10, and sealed to produce a battery 100. Specifically, as shown in FIG. 6, a positive electrode second current collecting member 52 is joined to the positive electrode tab group 25 of the wound electrode body 20, and a negative electrode second current collecting member 62 is joined to the negative electrode tab group 27. Then, as shown in FIG. 9, a plurality of (three in this case) wound electrode bodies 20 are arranged so that the flat portions face each other. A sealing plate 14 is placed above the plurality of wound electrode bodies 20, and the positive electrode tab group 25 of each wound electrode body 20 is folded so that the positive electrode second current collecting member 52 faces one side surface 20e of the wound electrode body 20. This connects the positive electrode first current collecting member 51 and the positive electrode second current collecting member 52. Similarly, the negative electrode tab group 27 of each of the wound electrode bodies 20 is bent so that the negative electrode second current collecting member 62 and the other side surface 20h of the wound electrode body 20 face each other. This connects the negative electrode first current collecting member 61 and the negative electrode second current collecting member 62. As a result, the wound electrode body 20 is attached to the sealing plate 14 via the positive electrode current collecting portion 50 and the negative electrode current collecting portion 60. Next, the wound electrode body 20 attached to the sealing plate 14 is covered with an electrode body holder 29 (see FIG. 7) and then housed inside the exterior body 12. As a result, the flat portion of the wound electrode body 20 faces the long side wall 12b of the exterior body 12 (i.e., the flat surface of the battery case 10). In addition, the upper curved portion 20r faces the sealing plate 14, and the lower curved portion 20r faces the bottom wall 12a of the exterior body 12. Then, opening 12h on the top surface of exterior body 12 is closed with sealing plate 14, and then exterior body 12 and sealing plate 14 are joined (welded) to construct battery case 10. After that, electrolyte is injected into battery case 10 through injection hole 15 of sealing plate 14, and injection hole 15 is closed with sealing member 16. In this manner, battery 100 can be manufactured.

[0049] <Battery configuration> Next, a battery 100 manufactured by the battery manufacturing method disclosed herein will be described with reference to FIGS. 5 to 11. FIG. 5 is a perspective view of the battery 100. FIG. 6 is a schematic longitudinal sectional view taken along line VI-VI in FIG. 5. FIG. 7 is a schematic longitudinal sectional view taken along line VII-VII in FIG. 5. FIG. 8 is a schematic transverse sectional view taken along line VIII-VIII in FIG. 5. FIG. 9 is a perspective view showing an electrode body attached to a sealing plate. FIG. 10 is a perspective view showing an electrode body to which a positive electrode second current collector and a negative electrode second current collector are attached. FIG. 11 is a diagram showing the configuration of a wound electrode body. In FIG. 11, the first adhesive layer 81 and the second adhesive layer 82 are omitted for ease of viewing.

[0050] 5 and 6, the battery 100 includes a wound electrode body 20 and a battery case that houses the wound electrode body 20. Although not shown, the battery 100 further includes an electrolyte. The battery 100 is preferably a non-aqueous electrolyte secondary battery such as a lithium ion secondary battery.

[0051] The battery case 10 is a housing that houses the wound electrode body 20. Here, as shown in FIG. 5, the battery case 10 has a rectangular parallelepiped (square) outer shape with a bottom. The material of the battery case 10 may be the same as that conventionally used, and is not particularly limited. The battery case 10 is preferably made of metal. Examples of materials for the battery case 10 include aluminum, aluminum alloy, iron, and iron alloy.

[0052] As shown in FIG. 5 and FIG. 6, the battery case 10 includes an exterior body 12 and a sealing plate 14. The exterior body 12 is a flat, bottomed, rectangular container having an opening 12h on the upper surface. The exterior body 12 includes a bottom wall 12a that is substantially rectangular in plan view, a pair of long side walls 12b that extend from the bottom wall 12a and face each other, and a pair of short side walls 12c that extend from the bottom wall 12a and face each other. The area of ​​the short side walls 12c is smaller than the area of ​​the long side walls 12b. The sealing plate 14 is a member that closes the opening 12h of the exterior body 12, and is a plate-like member that is substantially rectangular in plan view. The battery case 10 is integrated by joining (for example, welding) the sealing plate 14 to the periphery of the opening 12h of the exterior body 12. The battery case 10 is hermetically sealed (sealed).

[0053] 6, sealing plate 14 is provided with injection hole 15, gas exhaust valve 17, and two terminal withdrawal holes 18, 19. Injection hole 15 is a through hole for injecting an electrolyte into battery case 10 after sealing plate 14 is assembled to exterior body 12. Injection hole 15 is sealed with sealing member 16 after the electrolyte is injected. Gas exhaust valve 17 is a thin-walled portion configured to break when the pressure inside battery case 10 reaches or exceeds a predetermined value, thereby discharging gas inside battery case 10 to the outside.

[0054] The battery case 10 may accommodate an electrolyte together with the wound electrode body 20 as described above. As the electrolyte, any electrolyte used in conventionally known batteries may be used without any particular limitation. As an example, a non-aqueous electrolyte solution in which a supporting salt is dissolved in a non-aqueous solvent may be used. As an example of the non-aqueous solvent, carbonate-based solvents such as ethylene carbonate, dimethyl carbonate, and ethyl methyl carbonate may be used. As an example of the supporting salt, fluorine-containing lithium salts such as LiPF6 may be used. The non-aqueous electrolyte solution may contain various additives as necessary. The electrolyte may be in a solid state (solid electrolyte) and may be integrated with the electrode body.

[0055] A positive electrode terminal 30 is attached to one end of the sealing plate 14 in the long side direction Y (left side in Figs. 5 and 6). A negative electrode terminal 40 is attached to the other end of the sealing plate 14 in the long side direction Y (right side in Figs. 5 and 6). The positive electrode terminal 30 and the negative electrode terminal 40 are inserted through the terminal pull-out holes 18 and 19 and exposed on the outer surface of the sealing plate 14. The positive electrode terminal 30 is electrically connected to a plate-shaped positive electrode external conductive member 32 on the outside of the battery case 10. The negative electrode terminal 40 is electrically connected to a plate-shaped negative electrode external conductive member 42 on the outside of the battery case 10. The positive electrode external conductive member 32 and the negative electrode external conductive member 42 are connected to other secondary batteries and external devices via external connection members such as bus bars. The positive electrode external conductive member 32 and the negative electrode external conductive member 42 are preferably made of a metal having excellent electrical conductivity, for example, aluminum, an aluminum alloy, copper, a copper alloy, or the like. However, the positive electrode external conductive member 32 and the negative electrode external conductive member 42 are not essential and may be omitted in other embodiments.

[0056] 7 to 9, the battery 100 here has a plurality (three) of wound electrode bodies 20 housed within a battery case 10. A detailed structure of the wound electrode body 20 will be described later, but each wound electrode body 20 is provided with a positive electrode tab group 25 and a negative electrode tab group 27 (see FIG. 8). As shown in FIG. 8, these electrode tab groups (positive electrode tab group 25 and negative electrode tab group 27) are folded with the electrode current collecting parts (positive electrode current collecting part 50 and negative electrode current collecting part 60) joined together.

[0057] The positive electrode tab group 25 of each of the plurality of wound electrode bodies 20 is connected to the positive electrode terminal 30 via a positive electrode current collector 50. The positive electrode current collector 50 is housed inside the battery case 10. As shown in FIG. 6 and FIG. 9, the positive electrode current collector 50 includes a positive electrode first current collector 51 and a positive electrode second current collector 52. The positive electrode first current collector 51 is a plate-shaped conductive member extending in the long side direction Y along the inner side surface of the sealing plate 14. The positive electrode second current collector 52 is a plate-shaped conductive member extending in the up-down direction Z of the battery 100. The lower end 30c of the positive electrode terminal 30 is inserted into the battery case 10 through the terminal pull-out hole 18 of the sealing plate 14 and is connected to the positive electrode first current collector 51 (see FIG. 6). As shown in Figs. 8 to 10, the battery 100 includes a number of positive electrode second current collecting members 52 corresponding to the number of the plurality of wound electrode bodies 20. Each positive electrode second current collecting member 52 is connected to a positive electrode tab group 25 of the wound electrode body 20. As shown in Fig. 8, the positive electrode tab group 25 of the wound electrode body 20 is bent so that the positive electrode second current collecting member 52 faces one side surface 20e of the wound electrode body 20. This electrically connects the upper end of the positive electrode second current collecting member 52 to the positive electrode first current collecting member 51. The positive electrode terminal 30 and the positive electrode current collecting part 50 are preferably made of a metal having excellent electrical conductivity. The positive electrode terminal 30 and the positive electrode current collecting part 50 may be made of, for example, aluminum or an aluminum alloy.

[0058] On the other hand, the negative electrode tab group 27 of each of the plurality of wound electrode bodies 20 is connected to the negative electrode terminal 40 via the negative electrode current collecting portion 60. The connection structure on the negative electrode side is substantially the same as the connection structure on the positive electrode side described above. Specifically, as shown in FIG. 6 and FIG. 9, the negative electrode current collecting portion 60 includes a negative electrode first current collecting member 61 and a negative electrode second current collecting member 62. The negative electrode first current collecting member 61 is a plate-shaped conductive member extending in the long side direction Y along the inner side surface of the sealing plate 14. The negative electrode second current collecting member 62 is a plate-shaped conductive member extending in the up-down direction Z of the battery 100. The lower end portion 40c of the negative electrode terminal 40 is inserted into the battery case 10 through the terminal pull-out hole 19 and connected to the negative electrode first current collecting member 61 (see FIG. 6). As shown in Figs. 8 to 10, the battery 100 includes negative electrode second current collecting members 62 in a number corresponding to the number of the plurality of wound electrode bodies 20. Each negative electrode second current collecting member 62 is connected to the negative electrode tab group 27 of the wound electrode body 20. As shown in Figs. 8 and 9, the negative electrode tab group 27 of the wound electrode body 20 is bent so that the negative electrode second current collecting member 62 faces the other side surface 20h of the wound electrode body 20. This electrically connects the upper end of the negative electrode second current collecting member 62 to the negative electrode first current collecting member 61. The negative electrode terminal 40 and the negative electrode current collecting part 60 are preferably made of a metal having excellent electrical conductivity. The negative electrode terminal 40 and the negative electrode current collecting part 60 may be made of, for example, copper or a copper alloy.

[0059] In the battery 100, various insulating members are attached to prevent conduction between the wound electrode body 20 and the battery case 10. For example, as shown in FIG. 5 and FIG. 6, the positive electrode external conductive member 32 and the negative electrode external conductive member 42 are insulated from the sealing plate 14 by an external insulating member 92. Also, as shown in FIG. 6, a gasket 90 is attached to each of the terminal pull-out holes 18, 19 of the sealing plate 14. This can prevent the positive electrode terminal 30 (or the negative electrode terminal 40) inserted into the terminal pull-out holes 18, 19 from being conducted to the sealing plate 14. Also, an internal insulating member 94 is disposed between the positive electrode current collector 50 and the negative electrode current collector 60 and the inner surface side of the sealing plate 14. This can prevent the positive electrode current collector 50 and the negative electrode current collector 60 from being conducted to the sealing plate 14. The internal insulating member 94 may have a protruding portion protruding toward the wound electrode body 20. Furthermore, the multiple wound electrode bodies 20 are arranged inside the exterior body 12 while being covered with an electrode body holder 29 (see FIG. 7) made of an insulating resin sheet. This can prevent direct contact between the wound electrode body 20 and the exterior body 12. The material of each of the insulating members described above is not particularly limited as long as it has a predetermined insulating property. Examples of such materials include synthetic resin materials such as polyolefin resins such as polypropylene (PP) and polyethylene (PE), and fluorine-based resins such as perfluoroalkoxyalkane and polytetrafluoroethylene (PTFE).

[0060] Here, three wound electrode bodies 20 are housed in the exterior body 12. However, the number of wound electrode bodies arranged inside one exterior body 12 is not particularly limited, and may be four or more, or may be one. The wound electrode body 20 is preferably flat. As shown in FIG. 3, the wound electrode body 20 is, for example, flat and has a pair of curved parts 20r that face the bottom wall 12a and the sealing plate 14 of the exterior body 12, and a flat part 20f that connects the pair of curved parts 20r and faces the long side wall 12b of the exterior body 12. In this specification, the flat wound electrode body refers to a wound electrode body that is substantially oval in cross section and has a so-called racetrack shape (see FIG. 3).

[0061] As shown in FIG. 11, the wound electrode body 20 is configured by stacking a strip-shaped positive electrode sheet 22 and a strip-shaped negative electrode sheet 24 in a state of being insulated via a strip-shaped first separator 71 and a strip-shaped second separator 72, and winding them in the longitudinal direction around a winding axis WL. Here, the wound electrode body 20 is arranged inside the exterior body 12 with the winding axis WL (see FIG. 11) oriented parallel to the long side direction Y of the exterior body 12. In other words, the wound electrode body 20 is arranged inside the exterior body 12 with the winding axis WL oriented parallel to the bottom wall 12a and perpendicular to the short side wall 12c. An end face of the wound electrode body 20 (in other words, a lamination surface where the positive electrode sheet 22 and the negative electrode sheet 24 are laminated) faces the short side wall 12c.

[0062] As shown in FIG. 11, the positive electrode sheet 22 is a strip-shaped member. The positive electrode sheet 22 has a strip-shaped positive electrode collector 22c, and a positive electrode active material layer 22a and a positive electrode protective layer 22p fixed on at least one surface of the positive electrode collector 22c. However, the positive electrode protective layer 22p is not essential and can be omitted in other embodiments. For each member constituting the positive electrode sheet 22, a conventionally known material that can be used in a general battery (e.g., a lithium ion secondary battery) can be used without any particular restriction. For example, the positive electrode collector 22c is preferably made of a conductive metal such as aluminum, an aluminum alloy, nickel, or stainless steel. Here, the positive electrode collector 22c is a metal foil, specifically, an aluminum foil.

[0063] As shown in FIG. 11, the positive electrode sheet 22 has a plurality of positive electrode tabs 22t at one end (the left end in FIG. 11) in the long side direction Y of the wound electrode body 20. The plurality of positive electrode tabs 22t are provided at a predetermined interval (intermittently) along the longitudinal direction. The positive electrode tabs 22t are connected to the positive electrode sheet 22. Here, the positive electrode tab 22t is a part of the positive electrode collector 22c, and is made of metal foil (specifically, aluminum foil). The positive electrode tab 22t is a region where the positive electrode active material layer 22a is not formed and the positive electrode collector 22c is exposed. However, the positive electrode tab 22t may be partially provided with the positive electrode active material layer 22a and / or the positive electrode protective layer 22p, and may be a member different from the positive electrode collector 22c. Here, each of the plurality of positive electrode tabs 22t is trapezoidal. However, the shape of the positive electrode tab 22t is not limited thereto. The size of the positive electrode tabs 22t is not particularly limited. The shape and size of the positive electrode tabs 22t can be appropriately adjusted depending on the position of the positive electrode tabs 22t, for example, in consideration of the state of connection to the positive electrode current collecting part 50. The positive electrode tabs 22t are stacked at one end of the positive electrode sheet 22 in the long side direction Y (the left end in FIG. 8) as shown in FIG. 8, to form a positive electrode tab group 25.

[0064] As shown in FIG. 11, the positive electrode active material layer 22a is provided in a strip shape along the longitudinal direction of the strip-shaped positive electrode current collector 22c. The positive electrode active material layer 22a contains a positive electrode active material (for example, a lithium transition metal composite oxide such as a lithium nickel cobalt manganese composite oxide) that can reversibly store and release charge carriers. The positive electrode active material layer 22a preferably contains a lithium transition metal composite oxide as a positive electrode active material, and the lithium transition metal composite oxide preferably contains a positive electrode active material with a high nickel (Ni) content. For example, in the lithium transition metal composite oxide, when the total of metal elements other than lithium is taken as 100 mol%, the nickel content is preferably 55 mol% or more, more preferably 70 mol% or more, and even more preferably 75 mol% or more. This can further increase the capacity of the nonaqueous electrolyte secondary battery.

[0065] When the entire solid content of the positive electrode active material layer 22a is taken as 100 mass%, the positive electrode active material may account for approximately 80 mass% or more, typically 90 mass% or more, for example 95 mass% or more. The positive electrode active material layer 22a may contain any component other than the positive electrode active material, such as a conductive material, a binder, various additive components, etc. An example of the conductive material is a carbon material such as acetylene black (AB). An example of the binder is a fluorine-based resin such as polyvinylidene fluoride (PVdF).

[0066] Although not particularly limited, when the weight per unit area of ​​the positive electrode active material layer 22a is a (g) and the amount of moisture generated when the positive electrode active material layer 22a is heated from 150°C to 300°C is b (g), it is preferable that the ratio (b / a) of the moisture amount b to the weight a be less than 0.2%.

[0067] The positive electrode protective layer 22p is a layer configured to have lower electrical conductivity than the positive electrode active material layer 22a. As shown in FIG. 11, the positive electrode protective layer 22p is provided at the boundary between the positive electrode collector 22c and the positive electrode active material layer 22a in the long side direction Y. Here, the positive electrode protective layer 22p is provided at one end (the left end in FIG. 11) of the positive electrode collector 22c in the long side direction Y. However, the positive electrode protective layer 22p may be provided at both ends in the long side direction Y. By providing the positive electrode protective layer 22p, it is possible to prevent the positive electrode collector 22c and the negative electrode active material layer 24a from coming into direct contact with each other when the first separator 71 and the second separator 72 are damaged, and thus prevent the battery 100 from being internally short-circuited.

[0068] The positive electrode protective layer 22p contains an insulating inorganic filler, for example, ceramic particles such as alumina. When the entire solid content of the positive electrode protective layer 22p is taken as 100 mass%, the inorganic filler may occupy approximately 50 mass% or more, typically 70 mass% or more, for example 80 mass% or more. The positive electrode protective layer 22p may contain optional components other than the inorganic filler, for example, a conductive material, a binder, various additive components, and the like. The conductive material and binder may be the same as those exemplified as those that may be contained in the positive electrode active material layer 22a.

[0069] As shown in FIG. 11, the negative electrode sheet 24 is a strip-shaped member. The negative electrode sheet 24 has a strip-shaped negative electrode collector 24c and a negative electrode active material layer 24a fixed on at least one surface of the negative electrode collector 24c. For each member constituting the negative electrode sheet 24, a conventionally known material that can be used in a general battery (e.g., a lithium ion secondary battery) can be used without any particular restriction. For example, the negative electrode collector 24c is preferably made of a conductive metal such as copper, a copper alloy, nickel, or stainless steel. Here, the negative electrode collector 24c is a metal foil, specifically, a copper foil.

[0070] As shown in FIG. 11, the negative electrode sheet 24 has a plurality of negative electrode tabs 24t at one end (the right end in FIG. 11) in the long side direction Y of the wound electrode body 20. The plurality of negative electrode tabs 24t are provided at a predetermined interval (intermittently) along the longitudinal direction. The negative electrode tabs 24t are connected to the negative electrode sheet 24. Here, the negative electrode tab 24t is a part of the negative electrode collector 24c, and is made of metal foil (specifically, copper foil). Here, the negative electrode tab 24t is a region where the negative electrode active material layer 24a is not formed, and the negative electrode collector 24c is exposed. However, the negative electrode tab 24t may have the negative electrode active material layer 24a formed in a part thereof, and may be a member different from the negative electrode collector 24c. Here, each of the plurality of negative electrode tabs 24t is trapezoidal. However, the shape and size of the plurality of negative electrode tabs 24t can be appropriately adjusted in the same manner as the positive electrode tab 22t. As shown in FIG. 8, the negative electrode tabs 24t are stacked at one end in the long side direction Y of the negative electrode sheet 24 (the right end in FIG. 8) to form a negative electrode tab group 27.

[0071] As shown in FIG. 11, the negative electrode active material layer 24a is provided in a strip shape along the longitudinal direction of the strip-shaped negative electrode current collector 24c. The negative electrode active material layer 24a contains a negative electrode active material (e.g., a carbon material such as graphite) that can reversibly store and release charge carriers. The width (length in the long side direction Y; the same applies below) of the negative electrode active material layer 24a is preferably larger than the width of the positive electrode active material layer 22a. When the entire solid content of the negative electrode active material layer 24a is taken as 100 mass%, the negative electrode active material may occupy approximately 80 mass% or more, typically 90 mass% or more, for example 95 mass% or more. The negative electrode active material layer 24a may contain any component other than the negative electrode active material, such as a conductive material, a binder, a dispersant, various additive components, etc. An example of the binder is a rubber such as styrene butadiene rubber (SBR). An example of the dispersant is a cellulose such as carboxymethyl cellulose (CMC).

[0072] The first separator 71 and the second separator 72 are strip-shaped members. The first separator 71 and the second separator 72 are insulating sheets in which a plurality of fine through-holes through which charge carriers can pass are formed. The widths of the first separator 71 and the second separator 72 are greater than the width of the negative electrode active material layer 24a. By interposing the first separator 71 and the second separator 72 between the positive electrode sheet 22 and the negative electrode sheet 24, contact between the positive electrode sheet 22 and the negative electrode sheet 24 can be prevented, and charge carriers (e.g., lithium ions) can be moved between the positive electrode sheet 22 and the negative electrode sheet 24.

[0073] As the base layer 85, a microporous film used in a separator of a conventionally known battery can be used without any particular limitation. The base layer 85 is preferably, for example, a porous sheet-like member. The base layer 85 may have a single-layer structure or a structure of two or more layers, for example, a three-layer structure. The base layer 85 is preferably made of a polyolefin resin. This ensures sufficient flexibility of the separator, and allows the wound electrode body 20 to be easily produced (wound and press-molded). As the polyolefin resin, polyethylene (PE), polypropylene (PP), or a mixture thereof is preferable, and PE is more preferable. In addition, although not particularly limited, the thickness of the base layer 85 is preferably 3 μm or more and 25 μm or less, more preferably 3 μm or more and 18 μm or less, and even more preferably 5 μm or more and 14 μm or less.

[0074] Here, the heat-resistant layer 87 is provided on the base layer 85. The heat-resistant layer 87 may be provided directly on the surface of the base layer 85, or may be provided on the base layer 85 via another layer. However, the heat-resistant layer 87 is not essential and may be omitted in other embodiments. The basis weight of the heat-resistant layer 87 is uniform in the longitudinal and width directions of the separator. Although not particularly limited, the thickness of the heat-resistant layer 87 is preferably 0.3 μm or more and 6 μm or less, more preferably 0.5 μm or more and 6 μm or less, and even more preferably 1 μm or more and 4 μm or less.

[0075] The heat-resistant layer 87 preferably contains an inorganic filler and a heat-resistant layer binder. As the inorganic filler, any inorganic filler that has been publicly known and has been used for this type of application can be used without any particular limitation. The inorganic filler preferably contains insulating ceramic particles. Among them, in consideration of heat resistance, availability, and the like, inorganic oxides such as alumina, zirconia, silica, titania, metal hydroxides such as aluminum hydroxide, and clay minerals such as boehmite are preferred, and alumina and boehmite are more preferred. In addition, from the viewpoint of suppressing the thermal contraction of the separator, compounds containing aluminum are particularly preferred. The ratio of the inorganic filler to the total mass of the heat-resistant layer 87 is preferably 80 mass% or more, more preferably 90 mass% or more, and even more preferably 95 mass% or more.

[0076] As the heat-resistant layer binder, any binder that has been conventionally used for this type of application can be used without any particular limitation. Specific examples include acrylic resins, fluorine-based resins, epoxy resins, urethane resins, ethylene vinyl acetate resins, etc. Among these, acrylic resins are preferred.

[0077] FIG. 14 is a schematic cross-sectional view taken along line XIV-XIV in FIG. 10. For convenience, FIG. 14 omits the description of the members in the middle part of the wound electrode body 20. In addition, D1 in the figure indicates the winding direction, but it is not intended to limit the winding direction to this direction. As shown in FIG. 14, in the wound electrode body 20, the positive electrode sheet 22 and the first separator 71 are bonded by an adhesive layer 81, and the positive electrode sheet 22 and the second separator 72 are bonded by a second adhesive layer 82. In addition, the first separator 71 has a first region (see between AB in FIG. 14) in the vicinity of the winding start end 71a of the first separator. Here, the first adhesive layer 81 is not formed in the first region.

[0078] In another embodiment, the first region may include a region where the first adhesive layer 81 is not formed, and / or a region where the first adhesive layer 81 is formed with a smaller basis weight than the basis weight of the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22. That is, the first adhesive layer 81 may be formed in the entire first region, or the first region may include a region where the first adhesive layer 81 is formed and a region where the first adhesive layer 81 is not formed. For the ratio (B / A) of the basis weight B of the first adhesive layer 81 in the first region to the basis weight A of the first adhesive layer 81 in the region facing the positive electrode sheet 22, please refer to the description in <Method of manufacturing a battery>. In the wound electrode body 20 having such a configuration, excessive formation of the adhesive layer is suitably suppressed, so that it is possible to suitably suppress an increase in the resistance of the battery 100 and a decrease in the impregnation of the wound electrode body 20.

[0079] Fig. 12 is a schematic diagram showing a state in which the wound electrode body 20 according to this embodiment is developed, and Fig. 13 is an exploded view of Fig. 12. Note that in Fig. 11, for ease of viewing, each member is shown shifted in the width direction. Here, r a (r a1 ,r a2 ,r an-1 ,r an ) indicates that it corresponds to the apex of one R portion of the wound electrode body 20. b (r b1 ,r b2 ,r b3 ,r bn ) indicates that it corresponds to the apex of the other R portion of the wound electrode body 20.

[0080] In this embodiment, the first adhesive layer 81 is not formed on the first separator 71 constituting the outermost surface of the wound electrode body 20 (see P in FIG. 14). In the wound electrode body 20 having such a configuration, the excessive formation of the adhesive layer is suitably suppressed, so that an increase in the resistance of the battery 100 and a decrease in the impregnation property of the wound electrode body 20 can be suitably suppressed.

[0081] In another embodiment, the region of the first separator 71 that is to be the outermost surface of the wound electrode body 20 may have a region where the first adhesive layer 81 is not formed, and / or a region where the first adhesive layer 81 is formed with a smaller basis weight than the basis weight of the first adhesive layer 81 formed in the region of the first separator 71 that faces the positive electrode sheet 22. That is, the first adhesive layer 81 may be formed in the entire region of the first separator 71 that is to be the outermost surface of the wound electrode body 20, or the region of the first separator 71 that is to be the outermost surface of the wound electrode body 20 may have a region where the first adhesive layer 81 is formed and a region where the first adhesive layer 81 is not formed. Please refer to the description in <Battery manufacturing method> for the ratio (D / C) of the basis weight D of the first adhesive layer 81 in the region that is to be the outermost surface of the wound electrode body 20 to the basis weight C of the first adhesive layer 81 in the region that faces the positive electrode sheet 22. The above ratio can also be referred to when the separators constituting the outermost surface of the wound electrode body are the second separator, the first separator, and the second separator.

[0082] In this embodiment, a first adhesive layer 81b having a smaller basis weight than the first adhesive layer 81a in the region facing the positive electrode sheet 22 is formed near the end 71b of the first separator 71 on the surface on which the first adhesive layer 81 is formed. Note that 72b in the figure indicates the end of the second separator. Here, for example, if the first adhesive layer 81 is not formed near the end 71b of the first separator 71 on the surface on which the first adhesive layer 81 is formed, a winding stop tape may be applied. As such a winding stop tape, a conventionally known tape of this type may be used. However, even in this embodiment, a winding stop tape may be further applied near the end 71b of the first separator 71.

[0083] In another embodiment, the first separator 71 may have a region where the first adhesive layer 81 is not formed and / or a region where the first adhesive layer 81 is formed with a smaller basis weight than the first adhesive layer 81 formed in the region of the first separator 71 facing the positive electrode sheet 22, in the vicinity of the first separator's winding end 71b on the surface on the side on which the first adhesive layer 81 is formed. In other words, the first separator 71 may not have the first adhesive layer 81 formed in the entire vicinity of the first separator's winding end 71b on the surface on which the first adhesive layer 81 is formed, or may have a region where the first adhesive layer 81 is formed and a region where the first adhesive layer 81 is not formed. For the ratio (F / E) of the basis weight F of the first adhesive layer 81 in the vicinity of the first separator's winding end 71b to the basis weight E of the corresponding adhesive layer in the region facing the positive electrode sheet 22, please refer to the description in <Battery manufacturing method>.

[0084] 13, in this embodiment, the formation area of ​​the first adhesive layer (here, first adhesive layers 81a and 81b) formed on the first separator 71 is larger than the formation area of ​​the second adhesive layer 82 formed on the positive electrode sheet 22. Note that with regard to the ratio (H / G) of the formation area H of the first adhesive layer 81 formed on the first separator 71 to the formation area G of the second adhesive layer 82 formed on the positive electrode sheet 22, please refer to the description in <Battery manufacturing method>.

[0085] The first adhesive layer 81 and the second adhesive layer 82 are bonded to the electrodes (the positive electrode sheet 22 and / or the negative electrode sheet 24) by, for example, heating or pressing (typically, press molding), etc. The first adhesive layer 81 and the second adhesive layer 82 may have the same configuration or may have different configurations.

[0086] The first adhesive layer 81 and the second adhesive layer 82 contain an adhesive layer binder. As the adhesive layer binder, a conventionally known resin material having a certain viscosity with respect to the electrode can be used without any particular limitation. Specific examples include acrylic resin, fluorine resin, epoxy resin, urethane resin, polyamide resin, polyimide resin, polyamideimide resin, polyethylene oxide resin, ethylene vinyl acetate resin, polyamic acid resin, and the like. Among them, fluorine resin and acrylic resin are preferable because they have high flexibility and can more suitably exhibit adhesiveness to the electrode. Examples of fluorine resin include polyvinylidene fluoride (PVdF) and polytetrafluoroethylene (PTFE), and the like. Examples of acrylic resin include polyacrylonitrile and polymethyl methacrylate, and the like. The type of the adhesive layer binder may be the same as or different from the heat-resistant layer binder. The ratio of the adhesive layer binder to the total mass of the adhesive layer is preferably 25 mass% or more, may be 50 mass% or more, and more preferably 80 mass% or more. This allows the adhesive to adequately exhibit a desired adhesiveness to the electrode.

[0087] The first adhesive layer 81 and the second adhesive layer 82 may contain other materials (such as the inorganic filler listed as a component of the heat-resistant layer 73) in addition to the adhesive layer binder. When the adhesive layer contains an inorganic filler, the ratio of the inorganic filler to the total mass of the adhesive layer is preferably 75 mass% or less, more preferably 50 mass% or less, and even more preferably 20 mass% or less. The thickness of the first adhesive layer 81 and the second adhesive layer 82 is preferably approximately 0.3 μm or more and 6 μm or less, more preferably 0.5 μm or more and 6 μm or less, and even more preferably 1 μm or more and 4 μm or less.

[0088] Although not particularly limited, the basis weight of the first adhesive layer 81 and the second adhesive layer 82 is 0.005 to 1.0 g / m 2 is preferable, and 0.02 to 0.06 g / m 2 is more preferred.

[0089] The adhesive layer may be formed over the entire surface, or may have a predetermined pattern, such as a dotted, striped, wavy, banded (stripe), dashed line, or a combination thereof, in plan view.

[0090] Battery 100 can be used for various purposes, but can be suitably used, for example, as a power source (driving power source) for a motor mounted on a vehicle such as a passenger car, truck, etc. The type of vehicle is not particularly limited, but examples include a plug-in hybrid electric vehicle (PHEV), a hybrid electric vehicle (HEV), a battery electric vehicle (BEV), etc.

[0091] Although several embodiments of the present disclosure have been described above, the above embodiments are merely examples. The present disclosure can be implemented in various other forms. The present disclosure can be implemented based on the contents disclosed in this specification and the technical common sense in the field. The technology described in the claims includes various modifications and changes to the above-exemplified embodiments. For example, it is possible to replace a part of the above-mentioned embodiment with another modified form, and it is also possible to add another modified form to the above-mentioned embodiment. In addition, if the technical feature is not described as essential, it is also possible to delete it as appropriate.

[0092] For example, in the above-mentioned battery manufacturing method, the first contact area A1 includes the side wall of the first slit Sa in the first separator 71 and the area that contacts the side surface of the winding core 210, but is not limited thereto. For example, when a winding core without a slit is used, the first contact area can be the area that contacts the side surface of the winding core. Also, for example, in the above-mentioned battery manufacturing method, the second contact area A2 includes the side wall of the second slit Sb in the second separator 72 and the area that contacts the side surface of the winding core 210, but is not limited thereto. For example, when a winding core without a slit is used, the second contact area can be the area that contacts the side surface of the winding core.

[0093] For example, the battery manufacturing method described above includes a pressing step, but is not limited thereto. The battery manufacturing method disclosed herein may not include a pressing step, for example, when the wound electrode body is cylindrical. In addition, the battery manufacturing method disclosed herein may include a drying step after forming an adhesive layer on the separator by a coating device. In the wound electrode body 20, the content of the organic solvent and / or water in the adhesive layer (first adhesive layer 81, second adhesive layer 82) is preferably 1% or less, more preferably 0.1% or less, and particularly preferably 0.01% or less.

[0094] For example, in the above-described battery manufacturing method, the first adhesive layer 81 is formed in the region of the first separator 71 facing the positive electrode sheet 22, and the second adhesive layer 82 is formed on the positive electrode sheet 22, but the present invention is not limited thereto. In the battery manufacturing method disclosed herein, the first adhesive layer 81 may be formed in a region of the first separator 71 other than the region facing the positive electrode sheet 22, and the second adhesive layer 82 may be formed in a region other than the positive electrode sheet 22. In the battery manufacturing method disclosed herein, for example, the first adhesive layer 81 may be formed in a region of the first separator 71 facing the negative electrode sheet 24, and a third adhesive layer may be formed in a region of the second separator 72 facing the negative electrode sheet 24. In such a case, the basis weight of the first adhesive layer 81 is preferably smaller than the basis weight of the first adhesive layer 81 in the region facing the positive electrode sheet 22 of the first separator 71, and the basis weight of the third adhesive layer is preferably smaller than the basis weight of the second adhesive layer 82 in the region facing the positive electrode sheet 22 of the second separator 72.

[0095] For example, in the above-mentioned battery, the positive electrode tab 22t protrudes from one end in the winding axis direction of the wound electrode body 20, and the negative electrode tab 24t protrudes from the other end, but is not limited to this. The wound electrode body manufactured by the manufacturing method of the battery disclosed herein may be configured so that the positive electrode tab and the negative electrode tab protrude from one end in the winding axis direction of the wound electrode body, or may be configured so as not to have electrode tabs.

[0096] For example, in the battery described above, the outermost surface of the wound electrode body 20 is constituted by the first separator 71, but is not limited to this. The outermost surface of the wound electrode body manufactured by the battery manufacturing method disclosed herein may be constituted by the second separator, or may be constituted by the first separator and the second separator.

[0097] As described above, specific aspects of the technology disclosed herein include those described in the following items. Item 1: A method for manufacturing a battery including a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator being bonded by a first adhesive layer, and the positive electrode sheet and the second separator being bonded by a second adhesive layer, the method for manufacturing a battery including the following steps: a first forming step of forming the first adhesive layer on a surface of the first separator; a second forming step of forming the second adhesive layer on a surface of the positive electrode sheet; and a lamination step of laminating the first separator, the positive electrode sheet, the second separator, and the negative electrode sheet. Item 2: The method for manufacturing a battery according to item 1, wherein in the lamination step, the first separator, the positive electrode sheet, the second separator, and the negative electrode sheet are transported and wound while being stacked in a predetermined order, and in the first formation step, the first adhesive layer is formed on a surface of the first separator being transported in the lamination step that is to be overlapped with the positive electrode sheet, and in the second formation step, the second adhesive layer is formed on a surface of the positive electrode sheet being transported in the lamination step that is to be overlapped with the second separator. Item 3: The method for producing a battery according to item 1 or 2, wherein the first separator has a first region near a winding start end of the first separator, and the first region includes a region where the first adhesive layer is not formed, and / or a region where the first adhesive layer is formed and has a smaller basis weight than the first adhesive layer formed in the region of the first separator facing the positive electrode sheet. Item 4: The method for producing a battery according to item 3, wherein the first region is formed in the first separator by extending to a region that does not contact the winding core. Item 5: The method for producing a battery according to any one of Items 1 to 4, wherein the first separator and the positive electrode sheet are supplied to the winding core from one side with respect to a vertical line that passes through a winding center of the winding core and extends in the vertical direction. Item 6: The method for manufacturing a battery according to any one of Items 1 to 5, wherein the first separator is supplied to the winding core from one side with respect to a vertical line that passes through a winding center of the winding core and extends in the vertical direction, and the second separator is supplied to the winding core from the other side. Item 7: The method for producing a battery according to any one of Items 1 to 6, wherein in the first separator and the second separator, in a region that is to be the outermost surface of the wound electrode body, there is a region in which a corresponding adhesive layer is not formed, and / or a region in which the corresponding adhesive layer is formed and has a smaller basis weight than the corresponding adhesive layer formed in the region of the corresponding separator that faces the positive electrode sheet. Item 8: The method for manufacturing a battery according to any one of Items 1 to 7, wherein, in a state in which the wound electrode body is unfolded, a formation area of ​​the first adhesive layer formed on the first separator is larger than a formation area of ​​the second adhesive layer formed on the positive electrode sheet. Item 9: The method for manufacturing a battery according to any one of Items 1 to 8, wherein in the first separator, in the surface on which the first adhesive layer is formed, there is a region in which the first adhesive layer is not formed, and / or a region in which the first adhesive layer is formed and has a smaller basis weight than the first adhesive layer formed in the region of the first separator facing the positive electrode sheet, near a winding end of the first separator. [Explanation of symbols]

[0098] 10 Battery case 12 Exterior body 14 Sealing plate 20 Wound electrode body 20a Winding body 22 Positive electrode sheet 24 Negative electrode sheet 30 Positive terminal 40 Negative terminal 50 Positive electrode current collector 60 Negative electrode current collector 71 First separator 72 Second separator 81 1st adhesive layer 82 Second adhesive layer 100 batteries 200 Electrode body manufacturing equipment 210 Roll core 220 Lola 230 Coating Equipment 300 Press Machine

Claims

1. A method for manufacturing a battery including a wound electrode body in which a strip-shaped first separator, a strip-shaped positive electrode sheet, a strip-shaped second separator, and a strip-shaped negative electrode sheet are wound in a predetermined winding direction around a winding axis, the positive electrode sheet and the first separator being bonded together by a first adhesive layer, and the positive electrode sheet and the second separator being bonded together by a second adhesive layer, the method comprising the steps of: a first forming step of forming the first adhesive layer on a surface of the first separator; A second forming step of forming the second adhesive layer on the surface of the positive electrode sheet; and a lamination step of laminating the first separator, the positive electrode sheet, the second separator, and the negative electrode sheet; Inclusive of a first roller is positioned on a surface side of the first separator opposite to a surface on which the first adhesive layer is formed; The first separator passes over the first roller, a second roller is positioned on a surface side of the positive electrode sheet opposite to the surface on which the second adhesive layer is formed; The method of manufacturing a battery, wherein the positive electrode sheet is passed over the second roller.

2. In the stacking step, the first separator, the positive electrode sheet, the second separator, and the negative electrode sheet are transported and wound while being stacked in a predetermined order; In the first forming step, the first adhesive layer is formed on a surface of the first separator that is being transported in the lamination step, the surface being placed on the positive electrode sheet; The method for manufacturing a battery according to claim 1 , wherein in the second forming step, the second adhesive layer is formed on a surface of the positive electrode sheet being transported in the laminating step, the surface being placed on the second separator.

3. the first separator has a first region in the vicinity of a winding start end of the first separator, 3. The method for manufacturing a battery according to claim 1, wherein the first region includes a region in which the first adhesive layer is not formed, and / or a region in which the first adhesive layer is formed, the weight of the first adhesive layer being smaller than the weight of the first adhesive layer formed in the region of the first separator facing the positive electrode sheet.

4. The method for manufacturing a battery according to claim 3 , wherein the first region is formed so as to extend to a region of the first separator that does not abut against a winding core.

5. 3. The method for manufacturing a battery according to claim 1, wherein the first separator and the positive electrode sheet are supplied to the winding core from one side with respect to a vertical line that passes through a winding center of the winding core and extends in a vertical direction.

6. 3. The method for manufacturing a battery according to claim 1, wherein the first separator is supplied to the winding core from one side with respect to a vertical line that passes through a winding center of the winding core and extends in the vertical direction, and the second separator is supplied to the winding core from the other side.

7. 3. The method for manufacturing a battery according to claim 1, wherein in an area of ​​the first separator and the second separator that is to become the outermost surface of the wound electrode body, there is an area where a corresponding adhesive layer is not formed, and / or an area where the corresponding adhesive layer is formed having a smaller basis weight than the corresponding adhesive layer formed in the area of ​​the corresponding separator that faces the positive electrode sheet.

8. 3. The method for manufacturing a battery according to claim 1, wherein, in a state in which the wound electrode body is unfolded, a formation area of ​​the first adhesive layer formed on the first separator is larger than a formation area of ​​the second adhesive layer formed on the positive electrode sheet.

9. 3. The method for manufacturing a battery according to claim 1, wherein in the first separator, near a winding end end on the surface on which the first adhesive layer is formed, there is a region in which the first adhesive layer is not formed, and / or a region in which the first adhesive layer is formed and has a smaller basis weight than the first adhesive layer formed in the region of the first separator facing the positive electrode sheet.