Deposition processes for piezoelectric coatings.

Abstract

A method is disclosed for depositing a coating comprising a material with a highly oriented crystalline structure, the material being subjected to at least the following sequence of processing steps: - providing a flat substrate in a first vacuum processing chamber; - etching one surface of the substrate by physical vapor etching (PVE); - depositing a first metal layer (Me1) on the etched substrate surface by sputtering in a first metal deposition step; - the compound deposition temperature T of the subsequent compound deposition step COMP Annealing temperature T at least 50°C higher than A Annealing the metal layer (Me1) with In a first compound deposition step, a first compound layer (Comp1) is deposited by reactive sputtering at a temperature T COMP depositing on the outer surface of the metal layer (Me1) - depositing a second metal layer (Me2) on the outer surface of the first compound layer by sputtering in a second metal deposition step; Includes:

Description

[Technical field]

[0001] The invention relates to a method for depositing a coating comprising a material with a highly oriented microstructure according to claim 1 and to a coated substrate according to claim 20. [Background technology]

[0002] Due to the ever-increasing miniaturization of piezoelectric devices such as microphones, electrical frequency filters, ultrasonic generators, sensors, and actuators, the material properties of piezoelectric materials, especially piezoelectric layers and coatings, are becoming increasingly important. Such properties are a uniform and highly oriented microstructure, as indicated by the θ / 2θ X-ray diffraction pattern and expressed as a narrow full width at half maximum (FWHM) value of the rocking curve, and a low dielectric loss characteristic, as expressed by a low tan δ value, etc. It is well known that the piezoelectric response can be improved by alloying piezoelectric AlN films with other metals, whereby the hexagonal structure of AlN is still preserved. The most promising material for industrial use is Sc, up to a Sc concentration of 43 at.%. Other known materials are Cr and MgHf. Summary of the Invention [Problem to be solved by the invention]

[0003] It is an object of the present invention to provide a method for improving the material properties of the thin piezoelectric layer that each coating comprises at least one of and for providing an improved coating on a substrate. With respect to the piezoelectric layer materials as mentioned in the background, it should be mentioned that the present invention is directed to improving such state-of-the-art materials, despite the fact that the examples and embodiments of the present invention may be considered through specific materials for reasons of feasibility. [Means for solving the problem]

[0004] Therefore, a method for depositing a coating comprising a material with a highly oriented crystal structure is provided, which comprises at least the following sequence of process steps: - providing a flat substrate in a first vacuum processing chamber; - etching one surface of the substrate by physical vapor etching (PVE); - depositing, by sputtering, in a first metal deposition step, on the etched substrate surface a first metal layer (Me1), which is a base layer in terms of crystallographic growth for a subsequent compound layer and a base electrode in terms of the functionality of the coating; - the compound deposition temperature T of the first subsequent compound deposition step COMP Annealing temperature T at least 50°C higher than A annealing the metal layer (Me1) in the step of annealing at In a first compound deposition step, a first compound layer (Comp1) is deposited by reactive sputtering at a temperature T COMP on the outer surface of the metal layer (Me1) with - depositing, by sputtering, a second metal layer (Me2) on the outer surface of the first compound layer in a second metal deposition step; A method is disclosed that includes:

[0005] In a further embodiment of the method of the invention, between the PVE step and the first metal deposition step, a seed layer (Seed) is provided by metal sputtering or reactive sputtering.

[0006] At least one further compound layer (CompN) is deposited on the outer surface of the second metal layer (Me2) by reactive sputtering in a further compound deposition step, where N is an integer between 1 and 10; A multilayer stack can be made of a base layer Me1 or an inventively deposited base coating comprising a seed and an annealing step of Me1, with at least one further metal layer (MeN+1) deposited on the outer surface of each further compound layer by sputtering in a further metal deposition step. The base coating comprises a base layer and Comp1 with Me2.

[0007] In a further embodiment, the second metal deposition step and one of the further metal deposition steps are followed by a respective subsequent annealing step before a respective further compound layer (CompN) is deposited.

[0008] With regard to the material of the metal layer, the metal layer can be deposited to include at least one of molybdenum (Mo), ruthenium (Ru), platinum (Pt), tungsten (W), aluminum (Al), or a mixture thereof as the main component, the sum of the main components being at least 80%, 90%, or even about 100% of the atomic percentage of the respective layer material. Alternatively, the as-deposited metal layer can be composed of the respective components or mixtures, meaning that potential other alloying or interfering components represent less than 0.5% of the total amount. At least the first metal layer (Me1) can be deposited as one of molybdenum (Mo) in this sense.

[0009] With regard to the material of at least one compound layer, the material may comprise at least one of aluminum (Al), chromium (Cr), scandium (Sc), magnesium (Mg), hafnium (Hf), AlSc, AlCr, and MgHf as metals or alloys, and nitrogen (N) as a nonmetal, as main components. Alternatively, the compound layer may consist of AlN, AlScN, AlCrN, or AlMgHfN, within the definition as given, which again means that potential other alloying or interfering components represent less than 0.5% of the total amount. Subsequent compound layers Comp1, Comp2, ... CompN may be of different piezoelectric materials, but using the same material allows the process to be more easily handled and controlled, and keeps equipment costs lower, for example by multiple use of the same coating / sputtering chamber.

[0010] In one embodiment, the seed layer is deposited as an AlN, AlScN, AlCrN, HfMgN, or titanium (Ti) layer.

[0011] The process temperature T for depositing the compound layers Comp1, 2, ...n COMP 200℃≦T COMP The annealing temperature T of at least one annealing step may be selected from the range of ≦500 °C. A may be selected to be at least one or more of the following values, depending on the degree of alignment and the material properties to be tailored: T A ≦500℃, T A ≦600℃, T A ≦700℃, T A ≦800℃, or T A ≦1000℃

[0012] 700℃~1000℃(800℃≦T A ≦1000°C), annealing has been found to be effective for a wide range of metal layer (Me1) materials.

[0013] Subsequent processing steps may be applied in different processing chambers of the vacuum system, but so repeated processes such as metal deposition and a final compound deposition when the same metal or compound is used, or repeated annealing steps may be performed in the same processing compartment of a multi-chamber vacuum processing system (MCS) by a central handler to transport substrates, e.g. wafers, under vacuum from the metal deposition compartment to the annealing compartment and compound deposition compartment as required for each process.

[0014] Alternatively, at least one of the annealing step and the subsequent annealing step is applied in a separate annealing furnace, i.e., separate from the MCS, whereby the substrate needs to be transferred from the vacuum atmosphere out through a load lock chamber and back into the vacuum atmosphere. Further separate processing steps may be introduced, for example before the compound layer or the second metal layer is deposited, using a respective separate processing system. Clearly, such further processing steps can be carried out just before or just after the separate annealing step. Such further processing step may be one of structuring the metal layer (Me1), including sub-steps such as placing a (positive) photoresist on the metal surface, exposing it to light in a lithographic process, dissolving the exposed parts of the lacquer, and finally etching the unprotected metal surface parts in order to remove the resist from the conductive tracks formed on the semiconductor surface.

[0015] Furthermore, after the annealing step or at least one of the subsequent annealing steps, a further PVE step may be applied to each metal surface. This step is mandatory if the annealing step and / or further processing steps are applied in another annealing furnace or another processing system, and the substrate needs to be transferred from the atmosphere back to the vacuum system. However, surprisingly, such specific etching of the surface seems to have a beneficial effect even when the substrate is kept under vacuum throughout the processing cycle. This is called by the inventors a surface purification process initiated by the PVE step, which requires some further experiments to equalize and prove in detail the defects or steps of crystal growth in each surface. Thereby, at least one of the PVE step and the further PVE step may include inductively coupled plasma etching (ICPE).

[0016] The inventive deposition process as described above is particularly suitable for the semiconductor industry for depositing coatings with piezoelectric properties on substrates, which may be wafers or separate parts of wafers, and which may thus be used as electrical frequency filters, sensors or actuators, for example for microphones or the like, or may constitute intermediates for such devices.

[0017] It is therefore a further object of the present invention to provide a piezoelectric coating on a substrate having improved material properties, for example due to better crystal orientation. - a first sputter-deposited and annealed metal layer (Me1) on the pre-etched substrate surface; - a first reactive sputter deposited compound layer (Comp1) on the outer surface of the metal base layer; a second sputter-deposited metal layer (Me2) on the outer surface of the first compound layer (Comp1); Equipped with The following metallurgical properties: - of at least one of the annealed metal layer (Me1) and the as-deposited compound layer (Comp1) characteristics X-ray line full width at half maximum A (FWHM A ) are the respective full width at half maximum B(FWHM B ) at least 0.1°, 0.2°, or 0.3° smaller than - the dielectric loss angle δ, tan δ, is at least 2 × 10 greater than the respective loss tan δ of the as-deposited coating without the annealing step -4 , 3×10 -4 , or 4 × 10 -4 It is small and such values ​​are measured for the layer Comp1 with a reference layer thickness of 550 nm. It goes without saying that the improvement of the stack of thicker layers or coatings is substantially more pronounced.

[0018] A further measure to improve the crystal alignment is to provide a sputtering seed layer (Seed) provided between the substrate surface and the first metal layer (Me1), for example a seed layer corresponding to the piezoelectric material forming the compound layer, so that the seed layer (Seed) can be of the same material as the compound layer and / or the further compound layer.

[0019] In a further embodiment of the invention, - at least one further compound layer (CompN) is deposited on the outer face of the second metal layer (Me2); - at least one further metal layer (MeN) is deposited on the outer surface of each further compound layer.

[0020] The compound layer and further compound layer may comprise the following materials: AlN, AlScN, AlCrN, AlMgHfN, or mixtures thereof. It should be mentioned that such compound materials may comprise different component stoichiometries from the simplified chemical formulas used above. Thus, by way of example, AlN represents Al:N in a 1:1 ratio, but also sub-stoichiometric or hyperstoichiometric compositions. It should be mentioned that in relation to AlN layers containing Sc, e.g. seed layers or compound layers, Sc may be present in a range of 5-43%, in particular between 10-35%, in order to enhance the piezoelectric response of the layer.

[0021] With respect to the metal layers, at least one of the metal layer Me1, the second metal layer Me2, and the further metal layer Me-n can be molybdenum (Mo), ruthenium (Ru), platinum (Pt), aluminum (Al), or a mixture thereof, and the seed layer can be AlN, AlScN, AlCrN, HfMgN, Ti, or a mixture of each.

[0022] In relation to the material properties of the compound layer or further compound layer made of AlN or AlScN, <002> The FWHM of the X-ray lines may be 1.5° or less, 1.4° or less, or even 1.3° or less for a layer thickness of about 550 nm.

[0023] With respect to the material properties of the metal layers, the metal layer Me1, the second metal layer Me2, and the further metal layer Me-n, which are made of molybdenum (Mo), have a diffraction pattern of Mo of 2.1° or less, 2.0° or less, or even 1.9° or less. <110> The FWHM of the X-ray lines may have a reference layer thickness of about 15-20 nm, and again may be substantially smaller for metal layers of greater thickness.

[0024] Thereby, referring to the coatings with the materials and layer thicknesses mentioned for Me1, Comp1 and Me2, for example, the loss tan δ of the stack I type coating described in detail later is 1.3×10 -3 Below, 1.2 x 10 -3 Below, 1.1×10 -3 Less than or even 1.0×10 -3 It can be the following:

[0025] It has been found that the volume stress of the piezoelectric coating should be set in the preferred range of −500 to +500 MPa in relation to the volume stress of the compound layer (Comp1···N).

[0026] Such coated substrates may also be applied to microphones, frequency filters, sensors, actuators, or intermediates for such devices.

[0027] The invention will now be further illustrated with the aid of examples and figures. [Brief description of the drawings]

[0028] [Figure 1] FIG. 1 is a diagram of the principle concept of the process of the present invention. [Diagram 2] FIG. 2 is an example of a coating of the present invention. [Diagram 3] FIG. [Figure 4] FIG. 1 is a graph of tan δ versus annealing temperature. [Diagram 5] FIG. 1 is a diagram of tan δ versus volume stress. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0029] In Fig. 1, a basic flow diagram of the method of the invention is shown. Preliminary activities such as normal cleaning steps or degassing treatments between 200°C and 400°C, which may be performed in situ, for example in the load lock chamber of a multi-chamber vacuum processing system MCS or another degassing chamber, as well as post-processing steps such as cooling, for example in a further load lock chamber or another cooling chamber of the processing system, are not shown as they are well known to those skilled in the art and do not require further explanation here. In Fig. 1, all steps drawn with bold lines are mandatory with respect to the acts / materials in bold, which means an etching step of the substrate surface, followed by a deposition step of a first metal Me1 to provide a first conductive layer or electrode, followed by an annealing step to align the crystal structure of Me1, followed by a deposition step of a first compound Comp1 to provide a minimum process cycle to fabricate a highly aligned piezoelectric layer with a highly oriented microstructure according to the invention. An additional measure to improve the arrangement of this minimal layer system can be to provide a seed layer (Seed) directly on the surface of the substrate to form a base layer for crystallographic growth for the first metal layer Me1, which is then deposited directly on the Seed. Thereby, the seed layer (Seed) can be of the same or different material as Comp1, 2, ... n. Furthermore, to provide a viable piezoelectric layer stack I, a second metal layer Me2 can be provided on the outer surface of the first compound layer to form a second electrode. Me1 and Me2 can be the same or different metals, but using the same material makes handling easier for reasons explained above. As an example, using Mo for all metal layers Me1, Me2, Me3, ... Me-n is a good choice for all metal layers. Comp1 can be one of AlN, AlScN, AlCrN, AlHfMgN, or a mixture thereof. Each material is listed in FIG. 1, and the layer thickness of each layer (Seed, Me1···n, Comp1···n) can be selected within the ranges provided in FIG.

[0030] In addition, substrates or wafers of Si, SiC, SiN, GaAs, or Al2O3 (sapphire) can be used. Si wafers can be oxidized (insulating) or blank (semiconducting). The etching time used to etch -5nm silicon oxide from the surface, also called 5nm oxide equivalent, is usually adequate to prepare the surface, which also applies to metal surfaces. In relation to the etching process, ICPE processes and equipment as detailed in CH00992 / 18 (PR1803) provide the best results, and therefore this application is declared as an integral part of the actual invention.

[0031] Such an etching apparatus comprises a vacuum chamber for at least one plate-shaped substrate, the side wall of which is looped about a central axis A, the chamber comprising: - A substrate handling opening which can be a load lock if there is a large pressure difference between the two sides of the opening. - at least one inlet for a reducing gas and an inert gas. - a platform formed as a support for the substrate or workpiece in the central lower region of the etching compartment of the chamber, which is connected to a first pole of a first source, which may be an RF source, thereby forming a first electrode and which surrounds the first heating and cooling means. - a second electrode which is a counter electrode, RF-connected to ground and surrounding the first electrode, where RF-connection here means a conductive connection adapted to safely ground the parts exposed to the RF plasma. Examples of such connections are described in detail in WO2017 / 207144 and WO2017 / 215806 of the same assignee, which are presented later, and which can be positioned towards the first electrode at a darkroom distance which can be 0.5-5 mm or 0.8-2 mm in a typical processing pressure range when reactive ion etching (RIE) is applied, which can be 0.05 Pa-0.7 Pa or 0.1 Pa-0.5 Pa. - a third electrode, also a counter electrode and RF-connected to ground, comprising at least one upper shield and a screen shield connected to each other both thermally and electrically, whereby the screen shield is looped around the etching compartment and is vertically between the second electrode and the upper shield, the upper shield being attached to the upper wall of the vacuum chamber, said shields protecting the inner surface of the chamber ceiling formed by the upper wall and at least the upper part of the chamber side walls from the etching residues, whereby the screen shield is slotted parallel or at least approximately parallel to the central axis A. - whereby, at least one of the upper shielding and the screen shielding is provided with at least one further heating and / or cooling means configured to permanently maintain said shieldings at a constant temperature level. The etching apparatus further comprises a vacuum pump system and an induction coil looped around the upper sidewall, which defines a vacuum-tight sidewall of the etching compartment and surrounds the screen shield, whereby a first end of one of the coils is connected to a first pole of a second voltage supply source, which may be a MF supply, and a second end of one of the coils is connected to ground for generating an inductively coupled plasma in the etching compartment of the vacuum chamber, whereby at least the upper wall of the vacuum chamber, at least in the region between the top or upper shield of the vacuum chamber and the pedestal, is made from a ceramic, for example aluminum oxide or boron nitride, or made from quartz.

[0032] It should be mentioned that in the basic version of the etching system, the heating and cooling means and further or later mentioned supplementary heating and / or cooling means can be supplied with the respective heating or cooling fluid depending on the process requirements by a first heating and cooling device.

[0033] For example, body-centered cubic <110> on the surface of a completely differently oriented metal Me1, such as wurtzite, <002> Without attempting to provide a thorough analysis of the exact phenomena that surprisingly allow for a better and more ordered growth of AlN or AlScN piezoelectric compound layers with the orientation of the first metal layer Me1 or the alignment of the base layer system, which is the seed layer (Seed) and the first metal layer Me1, is assumed to provide the basis for a better ordered piezoelectric layer Comp1, which means that the alignment of the microstructure of the Me1 layer and ultimately the seed layer, as well as the alignment of the Comp1 layer, is higher than in the absence of the annealing step of the Me1 layer. It should be mentioned that such a specific annealing step certainly gives, again surprisingly, much better results than an "all at once" annealing at the end of the coating step that would try to anneal the entire coating stack at once. Furthermore, such annealing steps can be short, e.g., 30-120 seconds or even 60-90 seconds, since the layers to be treated are very thin, e.g., 15-80 nm or even 10-50 nm, and the annealing can be stopped immediately, e.g., when pyrometry on the backside of the coated wafer to be used for treatment indicates that the required temperature has been reached, or with a very short hold time at the target temperature.

[0034] Only optional features are shown with dashed lines, such as additional etching steps to etch the surface of the first metal layer Me1 or to anneal the entire layer stack I at the end. However, for the annealing step, if the substrate is kept out of the vacuum system instead of annealing it in the system, it is highly recommended to introduce a PVE etching step, for example by ICPE, to ensure that the metal layer is in good condition for the next coating step to deposit Comp1.

[0035] Analogous to each sub-step of the process of the invention as discussed in Fig. 1, further compound layers (CompN) can be deposited on the outer surface of the second metal layer (Me2), whereby one further metal layer (Me-n) on the outer surface of each further compound layer forms a layer of type stack II with layers of type stack I of Fig. 1. Despite the fact that all process steps are applied in a closed multi-chamber vacuum system MCS, i.e. there is no interruption of the vacuum conditions for the substrate, a second etching step is applied to refine the surface of Me1 before depositing Comp2, since it has been found to have an additional, but not significant effect on the alignment of the subsequent growth of the Comp2 layer. Likewise, a specific subsequent annealing step helps further alignment. Such thicker coatings are useful to enhance the piezoelectric response of the coating and may be referred to as "multiple" in reference to the sequence of layers Me1,2,3...n+1 and Comp1,2,3...n or in reference to the number of layer stacks (stack I (Me1+Comp1+Me2), stack II (Me1+Comp1+Me2+Comp2+Me3), stack III,...stack N). Thus, in addition to alternating Me1 or seed, substrates of the invention may also be fabricated comprising multiple layers of Me1-MeN+1 and Comp1-CompN layers, whereby N may be an integer between 1 and 20 or between 2 and 10. This corresponds to layer stacks I-XX or II-X.

[0036] All coatings are applied in material specific sputter compartments of the MCS. Anneals up to temperatures of 600°C can be handled in the coating compartment equipped with a high temperature chuck. For higher temperatures, anneals are performed in a specific annealing compartment equipped with a flat carbon heater facing the heated substrate surface. The top and bottom of the compartment are equipped with cooling reflective surfaces. The substrate is held by three finger supports near its outer periphery.

[0037] Figure 2 shows the coating of the invention as deposited by the process as described in Figure 1. For measurements of full width at half maximum FWMH and loss tan δ, as detailed below, a coating of stack I type with Me2 has been applied to SiO2 wafers with different annealing temperatures. The layer compositions and thicknesses as shown in Figure 2 have been used. For more detailed investigation, the following smaller ranges have been investigated: Seed: AlN or AlScN, 15~30nm Me1: Mo, 15-50 nm Comp1: AlN or AlScN, 300-700nm Me2: Mo, 15-50 nm

[0038] It should be mentioned that such layer thickness range is also suitable for depositing multiple layers or layers of different materials, such as a seed layer of AlN, AlScN, AlCrN, or titanium (Ti), at least one metal layer Me having as a main component molybdenum (Mo), ruthenium (Ru), platinum (Pt), aluminum (Al), tungsten (W), or a mixture thereof, and at least one compound layer Comp of AlN, AlScN, AlCrN, or AlMgHfN.

[0039] The processing was carried out on a commercial Clusterline 200 II MCS equipped with a PVE module, an annealing module, one module for AlN deposition equipped with an inlet for an Al target and reactive gases, and one module for molybdenum deposition equipped with a Mo target, for processing 200 mm wafers. The modules are arranged around a central handler equipped with a programmable handle to pick up single wafers from an input load lock chamber, with alignment and heating means for degassing the wafer surface, and feed / eject the wafers into / from the respective processing modules or load locks according to the processing requirements. At the end of the processing, the substrates are provided by the handler back to an output load lock chamber equipped with cooling means for cooling the wafers before being released to the atmosphere. To accelerate the completion cycle in production, an additional module for AlN coating and a second module for Mo deposition or a second annealing chamber can be provided.

[0040] The process parameters as shown later and in the following table were used to fabricate the stack I type coatings with an AlN or AlScN seed layer (Seed), two Mo metal layers (Me1 and Me2) and an AlN or AlScN compound layer (Comp1), as measured above and discussed in FIG. 2. In brackets, the range of process parameters that can be applied for fine tuning of the layer or coating properties for stack I, stack II, ... stack n type coatings is provided. The sputter targets are driven by a pulsed DC source with a pulse frequency of 100 kHz, whereby a range of 50-400 kHz is applicable. The respective target diameter is 304 mm and the distance between the wafer surface and the target surface is 60 mm. A clamp is applied to the wafer during sputtering and the pedestal can be at RF potential for adjustment of the film stress.

[0041] [Table 1]

[0042] In FIG. 3 the effect of the annealing step of certain layers for a stack I type coating of the same design as shown previously is shown through the diagram of rocking curves. Film crystallization measurements (θ-2θ, rocking curves) were carried out on a BRUKER D8 Discover X-ray diffraction (XRD) tool with Cu Kα radiation. On the primary beam side a 0.2 mm slit and 2xGe monochromator were used, on the secondary side a 1B-crystal was placed (three axes) and used. Rocking curves expressed in FWHM values ​​are displayed for a stack II type coating without annealing and therefore the FWHM B Annealing temperature T with a value of 0°C A , and for the coating of the present invention, a specific annealing step was performed after the deposition of the Me1 layer and before the subsequent deposition of the Comp1 layer. It goes without saying that the seed layer of the system is not annealed due to the very thin structure of the two base layers on the substrate front side and the temperature control on the back side of the wafer. In each diffraction pattern, the most prominent peaks in the Mo diffraction pattern (at about 40.5°) are related to Mo. <110> The FWHM values ​​of the X-ray lines are used, with the most prominent (at about 36°) being related to AlN. <002> The FWHM values ​​of the X-ray lines were used. Measurements for both materials were performed at the center and edge of the wafer for all temperatures. For the Mo material with an annealing temperature of 500°C, FWHM between 0.05 and 0.1 A Only a small decrease in the FWHM value is seen for both locations, with a more moderate decrease at 700°C and a sharp decrease at 800°C giving an overall decrease compared to the state of the art of about 0.5° for both locations. Surprisingly, the graph for AlN (lower pair of lines) does not mirror that for Mo (upper pair of lines), but rather shows a large difference in the FWHM values, ending up with a difference between about 0.15 and 0.2 for layer stack II with the Mo1 layer annealed, especially at an annealing temperature of 800°C, which was the temperature at which the annealing was stopped after 90 seconds. AThis shows a more linear phenomenon of the backside gas. Further experiments with the same 800°C annealing step and supplying backside gas to cool the backside of the substrate (backside on) resulted in still slightly better performance. With backside gas, the substrate is thermally coupled to the heated chuck with the aid of additional (Ar) gas introduced between the substrate and the heating / cooling chuck. The gas pressure is typically in the range of 5±1 mbar, so the substrate needs to be fixed with clamps or weight rings.

[0043] Therewith, clear evidence of better crystallographic alignment can be shown with only one specific annealing step of the base layer Me1 or seed and Me1.

[0044] At the same time, measurements of stress and loss tan δ have been carried out on the different samples, which are shown in Table 2. Here too, a specific annealing step was carried out after the deposition of the Me1 layer with the Mo metal layer on the AlN seed layer was completed. From the results in Table 1, it can be seen below that the average volume stress of the AlN layer is smaller when an annealing step is applied to Me1, looking at samples 1 to 3. Furthermore, compared to the samples without a specific annealing step (samples 4 and 5), all annealed samples show essentially up to two times smaller loss tan δ, again indicating the great potential of the method of the invention and the respective coated substrates such as wafers.

[0045] [Table 2]

[0046] In FIG. 4, a diagram of tan δ against annealing temperature is shown, referring to a coating of the type of stack I with 15 nm AlN (seed), 15 nm Mo (Me1) after etching the outermost 5 nm oxide equivalent from the 20 nm layer, 550 nm AlN (Comp1) deposited later, and 15 nm Mo (Me2). On the x-axis is shown the specific annealing temperature of the 20 nm thick Me1, here the Mo layer, and the y-axis shows the total stress of each specific annealed stack I coating. The upper solid line refers to the 550 nm AlN coating with an average stress of -300 MPa, the middle dashed line refers to the respective coating with an average stress of -100 MPa, and the lower dashed-dotted line refers to the respective coating with an average stress of +400 MPa. The diagram clearly shows that tan δ decreases at an annealing temperature of about 800 °C, but also shows that the tensile stress (+) of the coating is favored compared to the compressive stress (-).

[0047] FIG. 5 shows tan δ versus volume stress for annealed and unannealed coatings, respectively. The upper line shows the values ​​for the unannealed Me1 layer at different stresses (-300 MPa, -100 MPa and +400 MPa), where the negative (-) stress is compressive and the positive (+) stress is tensile, and the lower line shows the tan δ values ​​for the coating, Me1, which has been specifically annealed up to a temperature of 829°C and also for the specific annealing temperatures of 729°C and 866°C, which are very close to each other. Thereby, again the beneficial influence of the specific annealing step can be seen, as well as the benefit of setting the volume stress of the piezoelectric layer to a value in the region around zero (±100 MPa) and / or in the low tensile stress range of 0 to +500 or +100 to +400 MPa. Similar improvements as shown in Figures 4 and 5 through the AlN compound layer can be achieved for coatings containing AlScN as Comp1 and / or Seed material at various Sc concentrations by adjusting the respective specific Me1 annealing steps and / or bulk layer stress of Comp1.

[0048] It should be mentioned that all features illustrated or discussed in relation to only one of the embodiments of the invention and not further discussed in other embodiments can be considered to be features well adapted to improve the performance of the other embodiments of the invention as well, unless readily recognizable as obviously inappropriate by a person skilled in the art. Therefore, all combinations of features of a particular embodiment, except as mentioned, can be combined with other embodiments in which such features are not explicitly mentioned, and form part of the present invention.

Claims

1. A method for depositing a piezoelectric coating comprising a highly oriented crystalline material, comprising at least the following sequence of processing steps: Providing a flat substrate in a first vacuum processing chamber; Etching one surface of the substrate by physical vapor etching (PVE); In a first metal deposition step, a first metal layer (Me1) is deposited on the etched substrate surface by sputtering, the first metal layer (Me1) mainly comprising at least one of molybdenum (Mo), ruthenium (Ru), platinum (Pt), aluminum (Al), tungsten (W) or a mixture thereof; The compound deposition temperature T of the subsequent compound deposition step ＣＯＭＰ An annealing temperature T Ａ annealing the metal layer (Me1) in a step of annealing at In the first compound deposition step, a first compound layer (Comp1) is deposited by reactive sputtering at a temperature T ＣＯＭＰ on the outer surface of the metal layer (Me1), the first compound layer mainly comprising aluminum (Al) as a metal or alloy, or aluminum (Al) and at least one of chromium (Cr), scandium (Sc), magnesium (Mg), hafnium (Hf), and nitrogen (N) as a non-metal; In a second metal deposition step, a second metal layer (Me2) is deposited by sputtering on the outer surface of the first compound layer, the second metal layer (Me2) mainly comprising at least one of molybdenum (Mo), ruthenium (Ru), platinum (Pt), aluminum (Al), tungsten (W), or a mixture thereof; The method includes:

2. 2. The method of claim 1, wherein between the PVE step and the first metal deposition step, a seed layer (Seed) is provided by metal sputtering or reactive sputtering, the seed layer being deposited as one of AlN, AlScN, AlCrN, or titanium (Ti).

3. 3. A method according to claim 1 or 2, characterized in that the first metal layer (Me1) is deposited as a molybdenum (Mo) layer.

4. 4. The method of claim 1, wherein the compound layer is one of AlN, AlScN, AlCrN, or AlMgHfN.

5. The process temperature T ＣＯＭＰ About 200℃≦T ＣＯＭＰ ≦500℃ 5. The method according to claim 1 , wherein the step of:

6. The annealing temperature T Ａ About T Ａ <500° C., T Ａ ≦600° C., T Ａ ≦700° C., T Ａ ≦800° C., or T Ａ ≦1000° C. The method according to any one of claims 1 to 5, characterized in that the following is effective:

7. 7. The method according to claim 1, characterized in that subsequent processing steps are applied in different processing chambers of the vacuum system.

8. 8. The method according to any one of claims 1 to 7, characterized in that the annealing step is applied in a separate annealing furnace.

9. 9. The method according to any one of claims 1 to 8, characterized in that further processing steps are applied in a separate processing system.

10. 10. A method according to claim 9, characterized in that the further processing step comprises etching the surface of the metal layer (Me1) before the compound layer (Comp1) is deposited.

11. 11. A method according to any one of claims 1 to 10, characterized in that after the annealing step a further PVE step is applied to each metal surface.

12. 12. The method of claim 1, wherein at least one of the PVE step and the further PVE step comprises inductively coupled plasma etching (ICPE).

13. 13. The method according to claim 1, wherein the volume stress of the piezoelectric coating is set in the range of -500 to +500 MPa.

14. 14. A method for producing a coated substrate comprising the deposition method of any one of claims 1 to 13, wherein the piezoelectric coating has piezoelectric properties.

15. 15. The method of claim 14, wherein the substrate is a wafer.

16. 16. The method according to claim 14 or 15, characterized in that the coated substrate is part of a piezoelectric device used for a microphone, an electrical frequency filter, a sensor or an actuator.

17. A coated substrate, the coating comprising: a first sputter-deposited and annealed metal layer (Me1) on the pre-etched substrate surface, the metal layer (Me1) comprising at least one of molybdenum (Mo), ruthenium (Ru), platinum (Pt), aluminum (Al), tungsten (W), or a mixture thereof as a main component; a first reactive sputter-deposited compound layer (Comp1) on the outer surface of the metal layer (Me1), the compound layer mainly comprising aluminum (Al) as a metal or alloy, or aluminum (Al) and at least one of chromium (Cr), scandium (Sc), magnesium (Mg), and hafnium (Hf), and nitrogen (N) as a non-metal; a second sputter-deposited metal layer (Me2) on the outer surface of the first compound layer (Comp1), the metal layer (Me2) comprising as a main component at least one of molybdenum (Mo), ruthenium (Ru), platinum (Pt), aluminum (Al), tungsten (W), or a mixture thereof; A piezoelectric coating comprising: The following metallurgical properties: The full width at half maximum A (FWHM) of the characteristic X-ray line of at least one of the annealed metal layer (Me1) and the as-deposited compound layer (Comp1) Ａ ) are the full width at half maximum B (FWHM) of the as-deposited coating without the annealing step. Ｂ ) at least 0.1° smaller than The dielectric loss angle δ of the coating is at least 3×10 greater than the respective loss tan δ of the as-deposited coating without the annealing step. －４ Small things, 13. A coated substrate, characterized in that at least one of the following applies:

18. 18. The substrate of claim 17, characterized in that a sputtering seed layer (Seed) is provided between the substrate surface and the first metal layer (Me1), the seed layer being AlN, AlScN, AlCrN, Ti, or a mixture thereof.

19. 19. The substrate of claim 17 or 18, wherein the compound layer is AlN, AlScN, AlCrN, AlMgHfN, or a mixture thereof.

20. 20. The substrate according to claim 18 or 19, characterized in that the seed layer (Seed) is of the same material as the first compound layer.

21. 21. The substrate of claim 17, wherein the compound layer is AlN or AlScN, and the FWHM of the <002> X-ray line in the diffraction pattern of AlN or AlScN is less than or equal to 1.5[deg.].

22. 22. The substrate according to claim 17, wherein at least one of the metal layers (Me1) and (Me2) is molybdenum (Mo), and the FWHM of the <110> X-ray lines in the Mo diffraction pattern is less than or equal to 2.1°.

23. The loss tan δ of the coating is 1.3×10 －３ 23. Substrate according to any one of claims 17 to 22, characterized in that:

24. 24. Substrate according to any one of claims 17 to 23, characterized in that the coated substrate is a membrane for a microphone, a frequency filter, a sensor, an actuator or an intermediate for such a device.

25. 25. The substrate according to claim 17, characterized in that the substrate comprises a multilayer, the multilayer comprising alternating layers of metal and compound, the number of the metal layers being N+1 and the number of the compound layers being N, where N is an integer between 1 and 10.

Images