tire

Abstract

This tire comprises a pair of side wall rubbers, a carcass cord topping rubber, a breaker topping rubber, and an inner liner rubber, wherein: at least one of the rubbers contains recycled carbon black; at least one rubber member forming the tire contains oil; and if the total amount (g) of recycled carbon black is A and the total amount (g) of oil included in the tire is B, A and B satisfy expression (1). The objective of the present invention is to improve durability.　(1) … (A / B)×100>1

Description

[Technical field]

[0001] The present invention relates to a tire. [Background technology]

[0002] The need for environmental consideration is increasing year by year throughout all industries. With regard to tires, there are attempts to reuse used raw materials. As for carbon black, carbon black obtained by pyrolysis of used tires is known.

[0003] Patent Document 1 discloses that carbon black, a high-end material, is obtained by pyrolysis of used tires, and the surface of the recycled carbon black is supplemented with hydroxyl groups and carboxyl groups, and then the carbon black is used as part of regular carbon black. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] European Patent Application Publication No. 3173251 Summary of the Invention [Problem to be solved by the invention]

[0005] An object of the present invention is to provide a tire having improved durability by using recycled carbon black. [Means for solving the problem]

[0006] The present invention provides a tire comprising a pair of sidewall rubbers arranged on both sides of a tread portion, a carcass cord topping rubber constituting a carcass arranged on the inner side of the sidewall rubber in the tire width direction, a breaker topping rubber constituting a breaker arranged on the outer side of the carcass in the tire radial direction and on the inner side of the tread portion, and an inner liner rubber arranged on the inner side of the carcass in the tire radial direction, at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains recycled carbon black, the total amount (g) of the recycled carbon black contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is A, At least one rubber component constituting the tire contains oil, and the total amount (g) of oil contained in the tire is B. The tire relates to a tire in which A and B satisfy the following formula (1). (A / B)×100>1 (1) Effect of the Invention

[0007] According to the present invention, a tire having improved durability can be provided by using recycled carbon black. [Brief description of the drawings]

[0008] [Figure 1] 1 is a schematic diagram showing a portion of a cross section (upper right portion of the cross section) taken along a tire meridian of a tire according to one embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] The tire of the present invention comprises a pair of sidewall rubbers arranged on both sides of a tread portion, a carcass cord topping rubber constituting a carcass arranged on the inner side of the sidewall rubber in the tire width direction, an inner liner rubber arranged on the inner side of the carcass in the tire radial direction, and a breaker topping rubber constituting a breaker arranged on the outer side of the carcass in the tire radial direction and on the inner side of the tread portion, wherein at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains recycled carbon black, and the total amount (g) of recycled carbon black contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is A, and at least one rubber component constituting the tire contains oil, and the total amount (g) of oil contained in the tire is B, A and B satisfy the following formula (1). (A / B)×100>1 (1)

[0010] Without intending to be bound by theory, the mechanism by which tire durability is improved in the present invention is believed to be as follows. That is, recycled carbon black containing a predetermined amount or more of ash has the characteristic of being less likely to absorb oil. It is believed that rubber containing such recycled carbon black has improved durability due to its low thermal diffusivity and less susceptible to thermal oxidative deterioration. Since oil can move between members, in the present invention, it is sufficient that at least one of the sidewall rubber, carcass cord topping rubber, breaker topping rubber, and inner liner rubber contains recycled carbon black, and at least one of the sidewall rubber, carcass cord topping rubber, breaker topping rubber, and inner liner rubber contains oil.

[0011] The right side of formula (1) is preferably 5.

[0012] It is believed that the effect of the present invention is more pronounced when the amount of recycled carbon black relative to the oil is increased.

[0013] The right side of formula (1) is preferably 6.

[0014] It is believed that the effect of the present invention is more pronounced when the amount of recycled carbon black relative to the oil is increased.

[0015] When the total thickness of the sidewall rubber, the carcass cord topping rubber, and the inner liner rubber at the position where the tire width is maximum in the tire rotational axis direction is W (mm), it is preferable that A, B, and W satisfy the following formula (2). (A / B) / W×1000>5 (2)

[0016] It is believed that the effect of the present invention can be more effectively achieved by setting the ratio of the amount of recycled carbon black to the unit amount of oil to a certain amount or more relative to the thickness of the member.

[0017] When the total thickness of the breaker topping rubber, the carcass cord topping rubber, and the inner liner rubber at a position on the tire equatorial plane is H (mm), it is preferable that A, B, and H satisfy the following formula (3). (A / B) / H×1000>6 (3)

[0018] It is believed that the effect of the present invention can be more effectively achieved by setting the ratio of the amount of recycled carbon black to the unit amount of oil to a certain amount or more relative to the thickness of the member.

[0019] It is preferred that at least one rubber containing the recycled carbon black also contains the oil.

[0020] It is believed that the effects of the present invention are more easily achieved by having recycled carbon black and oil coexist in one rubber in advance.

[0021] The at least one rubber containing recycled carbon black is preferably a carcass cord topping rubber.

[0022] The carcass cord topping rubber can be adjacent to any of the sidewall rubber, the inner liner rubber and the breaker topping rubber, and is therefore considered to be able to easily exert the effects of the present invention.

[0023] The rubber containing the recycled carbon black is preferably at least two rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0024] The effects of the present invention are expected to be applicable to a wider range of rubbers.

[0025] The rubber containing the recycled carbon black is preferably at least three rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0026] The effects of the present invention are expected to be applicable to a wider range of rubbers.

[0027] It is preferable that the rubber containing recycled carbon black is all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0028] The effects of the present invention are expected to be applicable to a wider range of rubbers.

[0029] The oil-containing rubber is preferably at least two rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0030] The effects of the present invention are expected to be applicable to a wider range of rubbers.

[0031] The oil-containing rubber is preferably at least three rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0032] The effects of the present invention are expected to be applicable to a wider range of rubbers.

[0033] It is preferable that the oil-containing rubber is all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0034] The effects of the present invention are expected to be applicable to a wider range of rubbers.

[0035] When at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains a filler, and the total amount (g) of the filler contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is C, it is preferable that A and C satisfy the following formula (4). (A / C)×100>1.0 (4)

[0036] It is believed that the effects of the present invention are more pronounced when the amount of recycled carbon black in the filler is equal to or greater than a predetermined amount.

[0037] When at least one rubber component constituting the tire contains a plasticizer other than oil, and the total amount (g) of the plasticizer other than oil contained in the tire is D, it is preferable that A and D satisfy the following formula (5). A / (A+D)×100>16.0 (5)

[0038] It is believed that the effect of the present invention is more pronounced when the amount of oil in the total amount of oil and plasticizer other than oil is equal to or greater than a predetermined amount.

[0039] <Definition> Unless otherwise specified, the "dimensions of each part of the tire" are values ​​specified when the tire is mounted on a standard rim, inflated to the standard internal pressure, and in a standard unloaded state.

[0040] "Genuine rim" refers to a rim that is specified for each tire by the standard system that includes the standard on which the tire is based, such as the standard rim for the applicable size listed in the "JATMA YEAR BOOK" for JATMA (Japan Automobile Tire Manufacturers Association), the "Measuring Rim" listed in the "STANDARDS MANUAL" for ETRTO (The European Tyre and Rim Technical Organisation), and the "Design Rim" listed in the "YEAR BOOK" for TRA (The Tire and Rim Association, Inc.), referring to JATMA, ETRTO, and TRA in that order, and following the standard if there is an applicable size at the time of reference. In the case of a tire not specified in the standard, it refers to a rim that can be assembled to a rim and can hold internal pressure, that is, a rim that does not leak air from between the rim and tire, with the smallest rim diameter and the next narrowest rim width.

[0041] "Regular internal pressure" refers to the air pressure set for each tire by each standard in the standard system including the standard on which the tire is based. For JATMA, it is the "maximum air pressure", for TRA, it is the "maximum value" listed in the table "TIRE LOAD LIMITS AT VARIOUS COLD INFLATION PRESSURES", and for ETRTO, it is the "INFLATION PRESSURE". As with regular rims, refer to JATMA, ETRTO, and TRA in that order, and follow the standard if there is an applicable size at the time of reference. In the case of a tire not specified in the standard, it refers to the regular internal pressure (250KPa or more) of another tire size (specified in the standard) that is listed with the regular rim as the standard rim. Note that if multiple regular internal pressures of 250KPa or more are listed, it refers to the smallest value among them.

[0042] "Normal load" means the load specified in the standard system including the standard on which the tire is based. The "Maximum load capacity" in the JATMA standard, the "Maximum value" listed in "TIRE LOAD LIMITS AT VARIOUS COLD INFLATION PRESSURES" in the TRA standard, and the "LOAD CAPACITY" in the ETRTO standard are normal loads, and like the normal rim and normal internal pressure, refer to JATMA, ETRTO, and TRA in that order, and follow the standard if there is an applicable size at the time of reference. For tires not specified in the standard, the normal load WL (kg) is calculated as follows. WL=0.000011×V+175 V={(Dt / 2)2-(Dt / 2-Ht)2}×π×Wt V: Virtual volume of the tire (mm 3 ) Dt: Tire outer diameter Dt (mm) Ht: Section height of the tire (mm) Wt: tire section width (mm)

[0043] "Recycled carbon black" refers to carbon black obtained from a pyrolysis process of products such as used tires that contain carbon black, and in which the mass ratio of ash (ash content), which is a component that does not burn, is 13% by mass or more when the carbon black is oxidatively burned by heating in air in a thermogravimetric measurement method conforming to JIS K 6226-2:2003. In other words, the mass (carbon content) of the weight loss due to the oxidative combustion is less than 87% by mass. Recycled carbon black is also called recycled carbon, and may be represented by rCB. Carbon black obtained from a pyrolysis process and having an ash content ratio of less than 13% by mass is distinguished from recycled carbon black and is simply referred to as pyrolytic carbon black in this specification.

[0044] "Total amount of recycled carbon black (A)" refers to the total amount (g) of recycled carbon black contained in the sidewall rubber, carcass cord topping rubber, breaker topping rubber, and inner liner rubber, and is the sum of the amounts (g) of recycled carbon black contained in each of the above rubbers.

[0045] "Total amount of oil (B)" refers to the total amount of oil (g) contained in the tire. Note that it is sufficient that at least one rubber component constituting the tire contains oil.

[0046] "Total amount of filler (C)" refers to the total amount (g) of filler contained in the sidewall rubber, carcass cord topping rubber, breaker topping rubber, and inner liner rubber, and is the sum of the amounts (g) of filler contained in each of the above rubbers.

[0047] "Total amount of plasticizers other than oil (D)" refers to the total amount (g) of plasticizers other than oil contained in the tire. Note that it is sufficient that at least one rubber component constituting the tire contains a plasticizer other than oil.

[0048] "Total thickness W" refers to the total thickness (mm) of the sidewall rubber, carcass cord topping rubber, and inner liner rubber at the point where the tire is at its widest in the tire axis direction, and is measured by cutting the tire on a plane including the axis and holding it on a regular rim. For example, this corresponds to W in Figure 1. The thickness W of the sidewall rubber S (mm), Carcass cord topping rubber thickness W C (mm) and thickness of inner liner rubber W IL The same measurement is done for (mm).

[0049] "Total thickness H" refers to the total thickness (mm) of the breaker topping rubber, carcass cord topping rubber, and inner liner rubber at the position on the tire equatorial plane, and is measured by cutting the tire at the tire equatorial plane and holding it on a regular rim. For example, H in Figure 1 applies. Note that the thickness H of the breaker topping rubber is B (mm), thickness of carcass cord topping rubber H C (mm) and thickness of inner liner rubber H IL The same measurement is done for (mm).

[0050] The term "filler" refers to a reinforcing filler, and in the present invention, includes normal carbon black as well as recycled carbon black, and further includes fillers other than carbon black such as silica and other reinforcing fillers used in the tire industry. Specific examples of fillers will be described later.

[0051] "Plasticizers other than oil" refers to plasticizers other than oil that are used in the tire industry, and specific examples will be described later.

[0052] <Measurement method> "Styrene content" is 1 It is calculated by H-NMR measurement.

[0053] The "vinyl bond content (1,2-bonded butadiene unit content)" is measured by infrared absorption spectroscopy.

[0054] The "weight average molecular weight (Mw)" can be determined by converting the measured value obtained by gel permeation chromatography (GPC) (GPC-8000 series manufactured by Tosoh Corporation, detector: differential refractometer, column: TSKGEL SUPERMALTPORE HZ-M manufactured by Tosoh Corporation) into a standard polystyrene equivalent.

[0055] The "cis content (amount of cis-1,4-bonded butadiene units)" is measured by infrared absorption spectroscopy.

[0056] The "ash content of recycled carbon black" is measured by the thermogravimetric method of JIS K6226-2:2003.

[0057] "N2SA of carbon black" is a value determined by JIS K 6217-2:2017.

[0058] "N2SA of Silica" is a value measured by the BET method in accordance with ASTM D3037-93.

[0059] "Softening point of resin, etc." means the temperature at which the ball drops when the softening point as specified in JIS K 6220-1:2015 is measured using a ring and ball softening point tester, unless otherwise specified. Softening points measured by other methods are noted accordingly.

[0060] <Tires> The tire of the present invention will be described below with reference to the drawings as appropriate. However, the drawings are merely examples for the purpose of explanation.

[0061] Fig. 1 is a schematic diagram showing a part of a cross section (upper right part of the cross section) taken along the tire meridian of a tire according to an embodiment of the present invention. In Fig. 1, the tire 1 includes a pair of sidewall rubbers 3 arranged on both sides of a tread portion 2, a carcass cord topping rubber 4 constituting a carcass arranged on the inner side of the sidewall rubber 3 in the tire width direction, a breaker topping rubber 5 constituting a breaker arranged on the outer side of the carcass cord topping rubber in the tire radial direction and on the inner side of the tread portion 2, and an inner liner rubber 6 arranged on the inner side of the carcass cord topping rubber in the tire radial direction.

[0062] In the tire of the present invention, at least one rubber selected from the group consisting of a sidewall rubber, a carcass cord topping rubber, a breaker topping rubber, and an inner liner rubber contains recycled carbon black. At least one rubber member constituting the tire contains oil. Here, the rubber containing recycled carbon black and the rubber containing oil may be the same or different. Also, a form in which one rubber contains recycled carbon black and oil may be used. Therefore, at least one rubber containing recycled carbon black may also contain oil.

[0063] In a preferred embodiment, the at least one rubber containing recycled carbon black is a carcass cord topping rubber, and in a preferred embodiment, the at least one rubber containing oil is a carcass cord topping rubber.

[0064] In a preferred embodiment, the rubber containing recycled carbon black is at least two rubbers selected from the group consisting of sidewall rubber, carcass cord topping rubber, breaker topping rubber and inner liner rubber, or at least three rubbers selected from the group, or all of the sidewall rubber, carcass cord topping rubber, breaker topping rubber and inner liner rubber.

[0065] In a preferred embodiment, the oil-containing rubber is at least two rubbers selected from the group consisting of a sidewall rubber, a carcass cord topping rubber, a breaker topping rubber and an inner liner rubber, or is at least three rubbers selected from the group, or is all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[0066] In a preferred embodiment, the carcass cord topping rubber and the sidewall rubber are adjacent to each other. In a preferred embodiment, the carcass cord topping rubber and the inner liner rubber are adjacent to each other. In a preferred embodiment, the carcass cord topping rubber and the breaker topping rubber are adjacent to each other.

[0067] (Regarding formula (1)) In the tire of the present invention, when the total amount (g) of recycled carbon black contained in the sidewall rubber, carcass cord topping rubber, breaker topping rubber, and inner liner rubber is A and the total amount (g) of oil contained in the tire is B, A and B satisfy the following formula (1). (A / B)×100>1 (1)

[0068] Here, the right side of formula (1) is preferably 5, more preferably 6, even more preferably 10, even more preferably 30, even more preferably 50, even more preferably 60. On the other hand, there is no particular upper limit to the value of the left side of formula (1), but it is usually about 150, or may be about 120 or about 100.

[0069] (Regarding formula (2)) In a preferred embodiment, when the total thickness of the sidewall rubber, the carcass cord topping rubber, and the inner liner rubber at the position where the tire width is maximum in the tire rotational axis direction is W (mm), A, B, and W satisfy the following formula (2). In FIG. 1, W is the thickness W of the sidewall rubber at the position where the tire width is maximum in the tire rotational axis direction. S (mm), Carcass cord topping rubber thickness W C (mm) and thickness of inner liner rubber W IL (mm) (W S , W C , W IL not shown). (A / B) / W×1000>5 (2)

[0070] Here, the right side of formula (2) is preferably 10, more preferably 13, even more preferably 15, even more preferably 30, even more preferably 50, even more preferably 70. On the other hand, there is no particular upper limit to the value of the left side of formula (2), but it is usually about 250, or may be about 200 or about 180.

[0071] (Regarding formula (3)) In a preferred embodiment, when the total thickness of the breaker topping rubber, the carcass cord topping rubber, and the inner liner rubber at a position on the tire equatorial plane is H (mm), A, B, and H satisfy the following formula (3). In FIG. 1, H is the thickness H of the breaker topping rubber at a position on the tire equatorial plane. B (mm), thickness of carcass cord topping rubber H C (mm) and thickness of inner liner rubber H IL (mm) (H B , H C , H IL not shown). (A / B) / H×1000>6 (3)

[0072] Here, the right side of formula (3) is preferably 12, more preferably 14, even more preferably 18, even more preferably 36, even more preferably 50, even more preferably 70, even more preferably 90, even more preferably 100. On the other hand, there is no particular upper limit to the value of the left side of formula (3), but it is usually about 300, or may be about 250 or about 200.

[0073] (Regarding formula (4)) In a preferred embodiment, at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains a filler. In this case, when the total amount (g) of the filler contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is C, it is preferable that A and C satisfy the following formula (4). (A / C)×100>1.0 (4)

[0074] Here, the right side of formula (4) is preferably 2.0, more preferably 2.2, even more preferably 8.0, even more preferably 12.0, even more preferably 15.0. On the other hand, there is no particular upper limit to the value of the left side of formula (4), but it is usually about 70, or may be about 60 or about 50.

[0075] (Regarding formula (5)) In a preferred embodiment, at least one rubber component constituting the tire contains a plasticizer other than oil. In this case, when the total amount (g) of the plasticizer other than oil contained in the tire is D, it is preferable that A and D satisfy the following formula (5). A / (A+D)×100>16.0 (5)

[0076] Here, the right side of formula (5) is preferably 30.0, more preferably 50.0, even more preferably 70.0, even more preferably 80.0, even more preferably 90.0. On the other hand, there is no particular upper limit to the value of the left side of formula (5), but it is usually about 160, or may be about 140 or about 120.

[0077] (Thickness at maximum tire width W S , W C , W IL and W) The thickness W of the sidewall rubber at the point where the tire width is maximum in the tire rotational axis direction S (mm), Carcass cord topping rubber thickness W C (mm) and thickness of inner liner rubber W IL The thickness (mm) and the total thickness W (mm) which is the sum of these will be explained below.

[0078] The above W S is preferably greater than 1.5 mm, more preferably greater than 1.8 mm, and even more preferably greater than 2.1 mm. S is preferably less than 3.5 mm, more preferably less than 3.2 mm, and even more preferably less than 2.9 mm.

[0079] The above W C is preferably greater than 0.5 mm, more preferably greater than 0.7 mm, and even more preferably greater than 0.9 mm. C is preferably less than 2.0 mm, more preferably less than 1.7 mm, and even more preferably less than 1.4 mm.

[0080] The above W IL is preferably greater than 0.1 mm, more preferably greater than 0.5 mm, and even more preferably greater than 1.0 mm. IL is preferably less than 5.0 mm, more preferably less than 4.0 mm, and even more preferably less than 3.0 mm.

[0081] The above W is preferably greater than 2.1 mm, more preferably greater than 3.0 mm, and even more preferably greater than 4.0 mm, and the above W is preferably less than 10.5 mm, more preferably less than 8.9 mm, and even more preferably less than 7.3 mm.

[0082] (The thickness at the position on the tire equatorial plane H B , H C , H IL and H) Thickness H of the breaker topping rubber at the position on the tire equatorial plane B (mm), thickness of carcass cord topping rubber H C (mm) and thickness of inner liner rubber H IL The thickness (mm) and the total thickness H (mm) which is the sum of these will be explained below.

[0083] The above H B is preferably more than 1.5 mm, more preferably more than 1.8 mm, and even more preferably more than 2.1 mm. B is preferably less than 4.0 mm, more preferably less than 3.2 mm, and even more preferably less than 2.9 mm.

[0084] The above H C is preferably more than 0.5 mm, more preferably more than 0.7 mm, and even more preferably more than 0.9 mm. C is preferably less than 2.0 mm, more preferably less than 1.7 mm, and even more preferably less than 1.4 mm.

[0085] The above H IL is preferably more than 0.1 mm, more preferably more than 0.5 mm, and even more preferably more than 1.0 mm. IL is preferably less than 5.0 mm, more preferably less than 4.0 mm, and even more preferably less than 3.0 mm.

[0086] The above H is preferably greater than 2.1 mm, more preferably greater than 3.0 mm, and even more preferably greater than 4.0 mm, and the above H is preferably less than 11.0 mm, more preferably less than 8.9 mm, and even more preferably less than 7.3 mm.

[0087] <Rubber composition> The rubber compositions constituting the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber of the present invention will be described below.

[0088] <Rubber composition for sidewall rubber> Each component of the rubber composition for the sidewall rubber will be described.

[0089] (Rubber component) The rubber component preferably contains isoprene-based rubber (IR rubber) and butadiene rubber (BR). In this case, the rubber component may contain rubber components other than the IR rubber and the BR. The rubber component may also consist of only the IR rubber and the BR. The following is an explanation of each rubber that may constitute the rubber component.

[0090] <Isoprene rubber> Examples of isoprene-based rubber include natural rubber (NR), isoprene rubber (IR), modified NR, modified NR, and modified IR. Examples of NR include SIR20, RSS♯3, and TSR20, which are common in the rubber industry. Examples of IR include IR2200, which is common in the rubber industry, and are not particularly limited. Examples of modified NR include deproteinized natural rubber (DPNR), high-purity natural rubber (UPNR), and the like. Examples of modified NR include epoxidized natural rubber (ENR), hydrogenated natural rubber (HNR), and grafted natural rubber. Examples of modified IR include epoxidized isoprene rubber, hydrogenated isoprene rubber, and grafted isoprene rubber. Isoprene-based rubbers may be used alone or in combination of two or more.

[0091] The BR is not particularly limited, and examples thereof include those commonly used in the tire industry, such as BR with a high cis content, BR containing 1,2-syndiotactic polybutadiene crystals (SPB-containing BR), butadiene rubber synthesized using a rare earth catalyst (rare earth-based BR), tin-modified butadiene rubber modified with a tin compound (tin-modified BR), and other modified butadiene rubbers (modified BR). Commercially available BRs include products from Ube Industries, Ltd., JSR Corporation, Asahi Kasei Corporation, Zeon Corporation, and the like. The modified BR may be any BR having a functional group that interacts with a filler such as silica, and examples thereof include terminal-modified BR having at least one end of BR modified with a compound (modifying agent) having the above functional group (terminal-modified BR having the above functional group at the end), main-chain-modified BR having the above functional group in the main chain, main-chain terminal-modified BR having the above functional group in the main chain and at least one end (for example, main-chain terminal-modified BR having the above functional group in the main chain and at least one end modified with the above modifier), and terminal-modified BR modified (coupled) with a polyfunctional compound having two or more epoxy groups in the molecule and having a hydroxyl group or epoxy group introduced therein. Examples of the functional group include an amino group, an amide group, a silyl group, an alkoxysilyl group, an isocyanate group, an imino group, an imidazole group, a urea group, an ether group, a carbonyl group, an oxycarbonyl group, a mercapto group, a sulfide group, a disulfide group, a sulfonyl group, a sulfinyl group, a thiocarbonyl group, an ammonium group, an imide group, a hydrazo group, an azo group, a diazo group, a carboxyl group, a nitrile group, a pyridyl group, an alkoxy group, a hydroxyl group, an oxy group, and an epoxy group. These functional groups may have a substituent. Among them, an amino group (preferably an amino group in which a hydrogen atom of an amino group is substituted with an alkyl group having 1 to 6 carbon atoms), an alkoxy group (preferably an alkoxy group having 1 to 6 carbon atoms), and an alkoxysilyl group (preferably an alkoxysilyl group having 1 to 6 carbon atoms) are preferred.

[0092] The cis amount (cis content) of the BR is preferably more than 90 mass%, more preferably more than 93 mass%, even more preferably more than 95 mass%, and still more preferably 97 mass% or more. The cis amount of the BR can be measured by infrared absorption spectroscopy.

[0093] As the BR, for example, products available from Ube Industries, Ltd., JSR Corporation, Asahi Kasei Corporation, Nippon Zeon Co., Ltd., etc. may be used. The BR may be used alone or in combination of two or more kinds.

[0094] ≪SBR≫ The styrene butadiene rubber (SBR) is not particularly limited, and examples thereof include unmodified emulsion-polymerized styrene butadiene rubber (E-SBR) and solution-polymerized styrene butadiene rubber (S-SBR), and modified SBRs such as modified emulsion-polymerized styrene butadiene rubber (modified E-SBR) and modified solution-polymerized styrene butadiene rubber (modified S-SBR) obtained by modifying these. Examples of modified SBRs include modified SBRs whose terminals and / or main chains are modified, and modified SBRs (condensates, those having a branched structure, etc.) that are coupled with tin or silicon compounds. In addition, SBRs include oil-extended types in which the flexibility is adjusted by adding an extender oil, and non-oil-extended types in which no extender oil is added, and both of these can be used. Examples of such SBRs that can be used include those manufactured by JSR Corporation, Asahi Kasei Chemicals Corporation, Nippon Zeon Corporation, and ZS Elastomers Corporation. SBRs can be used alone or in combination of two or more types.

[0095] The styrene content of SBR is preferably more than 15.0% by mass, more preferably more than 20.0% by mass, and even more preferably more than 23.0% by mass, from the viewpoint of rubber strength and grip performance. Also, the styrene content is preferably less than 40.0% by mass, more preferably less than 30.0% by mass, and even more preferably less than 25.0% by mass, from the viewpoint of fuel efficiency. The styrene content of SBR is 1 This value is calculated by H-NMR measurement.

[0096] The vinyl content (amount of 1,2-bonded butadiene units) of SBR is preferably more than 10.0%, more preferably more than 15.0%, and more preferably 18.0% or more, from the viewpoint of rubber strength and grip performance. Also, the vinyl content is preferably less than 80.0%, preferably less than 50.0%, and more preferably less than 30.0%, from the viewpoint of fuel economy. The vinyl content of SBR is a value measured by infrared absorption spectroscopy.

[0097] Other Rubbers The other rubbers that can be used other than the above are not particularly limited, and rubbers used in the tire field can be used. For example, diene rubbers such as acrylonitrile butadiene rubber (NBR), chloroprene rubber (CR), and styrene-isoprene-butadiene copolymer rubber (SIBR) can be used. The other rubbers can be used alone or in combination of two or more.

[0098] ≪Content≫ The content of the IR rubber in 100% by mass of the rubber component is preferably more than 5% by mass, more preferably more than 10% by mass, even more preferably more than 20% by mass, and even more preferably more than 30% by mass. Meanwhile, the content is preferably less than 80% by mass, more preferably less than 70% by mass, even more preferably less than 60% by mass, and even more preferably less than 50% by mass. By keeping it within the above range, cut resistance tends to be improved.

[0099] The BR content in 100% by mass of the rubber component is preferably more than 15% by mass, more preferably more than 30% by mass, even more preferably more than 40% by mass, and even more preferably more than 50% by mass. Meanwhile, the BR content is preferably less than 90% by mass, more preferably less than 80% by mass, even more preferably less than 70% by mass, and even more preferably less than 60% by mass. By keeping the BR content within the above range, cut resistance tends to be improved.

[0100] The total content of the IR rubber and BR in 100% by mass of the rubber component is preferably more than 80% by mass, more preferably more than 90% by mass, and further preferably more than 95% by mass, and may be 100% by mass.

[0101] (Filler) The filler may include recycled carbon black (rCB). The filler may also include carbon black other than rCB, or silica. When the filler includes silica, it may further include a silane coupling agent. The filler may further include other fillers other than carbon black and silica.

[0102] <Carbon black content> When carbon black is contained, the total content of carbon black including recycled carbon black is preferably more than 30 parts by mass, more preferably more than 40 parts by mass, and even more preferably more than 50 parts by mass, based on 100 parts by mass of the rubber component. On the other hand, the total content is preferably less than 150 parts by mass, more preferably less than 110 parts by mass, and even more preferably less than 80 parts by mass. When the carbon black content is within the above range, sufficient reinforcing properties and good dispersion in the rubber are obtained, and sufficient rubber strength and crack growth resistance tend to be obtained.

[0103] The content of recycled carbon black in the total content of carbon black is preferably less than 60% by mass, more preferably less than 50% by mass, and even more preferably less than 45% by mass, from the viewpoint of reinforcing properties. On the other hand, the content is preferably more than 1% by mass, more preferably more than 5% by mass, even more preferably more than 10% by mass, even more preferably more than 20% by mass, even more preferably more than 30% by mass, and even more preferably more than 35% by mass, from the viewpoint of the effects of the present invention. The content of recycled carbon black in the total content of carbon black may be even lower, may be less than 30% by mass, may be less than 20% by mass, may be less than 10% by mass, or may be 0% by mass. This is because other components may contain recycled carbon black.

[0104] <Silica content> When silica is contained, the content per 100 parts by mass of the rubber component is not particularly limited, but from the viewpoint of ensuring fuel economy, wet grip performance, and sufficient reinforcement, it is preferably more than 1 part by mass, more preferably more than 5 parts by mass, more preferably more than 10 parts by mass, and even more preferably more than 20 parts by mass. Also, from the viewpoints of dispersibility of silica, processability, and wet grip performance, the content is preferably less than 150 parts by mass, more preferably less than 100 parts by mass, even more preferably less than 50 parts by mass, and even more preferably less than 30 parts by mass.

[0105] <Silane coupling agent content> When silane coupling agent is contained, the content of silane coupling agent is preferably more than 1 part by mass, more preferably more than 3 parts by mass, even more preferably more than 5 parts by mass, and even more preferably more than 7 parts by mass, based on 100 parts by mass of silica.On the other hand, the content is preferably less than 20 parts by mass, more preferably less than 18 parts by mass, even more preferably less than 16 parts by mass, and even more preferably less than 14 parts by mass.By making it within the above range, cut resistance tends to be improved.

[0106] <Recycled Carbon Black> In the present invention, recycled carbon black refers to carbon black obtained from a pyrolysis process of products such as used tires that contain carbon black, and in which the mass ratio of ash (ash content), which is a component that does not burn, is 13% by mass or more when oxidatively burned by heating in air in a thermogravimetric measurement method conforming to JIS K 6226-2:2003. Recycled carbon black has a characteristic that it is difficult to absorb oil because of its high ash content. The ash content of recycled carbon black is preferably 14% by mass or more, more preferably 15% by mass or more, even more preferably 16% by mass or more, and even more preferably 17% by mass or more.

[0107] Recycled carbon black can be obtained from the pyrolysis process of used pneumatic tires. For example, European Patent Application Publication No. 3427975, referring to "Rubber Chemistry and Technology", Vol. 85, No. 3, pp. 408-449 (2012), in particular pp. 438, 440, and 442, describes that recycled carbon black can be obtained by pyrolysis of organic materials at 550-800°C with the exclusion of oxygen, or by vacuum pyrolysis at relatively low temperatures (

[0027] ). Carbon black obtained from such pyrolysis processes is usually devoid of functional groups on its surface, as mentioned in

[0004] of Japanese Patent No. 6856781 (Comparison of Surface Morphology and Chemistry of Pyrolytic Carbon Black with Commercial Carbon Black, Powder Technology 160 (2005) 190-193).

[0108] The recycled carbon black of the present invention may lack functional groups on its surface, or may be treated to include functional groups on its surface. The treatment to include functional groups on the surface of the recycled carbon black can be carried out by a conventional method. For example, in European Patent Application Publication No. 3173251, carbon black obtained from a pyrolysis process is treated with potassium permanganate under acidic conditions to obtain carbon black having hydroxyl and / or carboxyl groups on its surface. In Japanese Patent No. 6856781, carbon black obtained from a pyrolysis process is treated with an amino acid compound containing at least one thiol or disulfide group to obtain a carbon black with an activated surface. The recycled carbon black of the present invention also includes carbon blacks that have been treated to include functional groups on their surfaces.

[0109] <Carbon black other than rCB> Carbon black other than rCB is not particularly limited, and examples thereof include N134, N110, N220, N234, N219, N339, N330, N326, N351, N550, N600, N660, and N762. Commercially available products include those from Asahi Carbon Co., Ltd., Cabot Japan Co., Ltd., Tokai Carbon Co., Ltd., Mitsubishi Chemical Corporation, Lion Corporation, Shinnikka Carbon Co., Ltd., Columbia Carbon Co., Ltd., and the like. These carbon blacks may be used alone or in combination of two or more kinds.

[0110] The nitrogen adsorption specific surface area (N2SA) of the carbon black is not particularly limited, but from the viewpoint of obtaining sufficient reinforcement and good abrasion resistance, it is preferable that the nitrogen adsorption specific surface area (N2SA) is 30 m 2 / g or more is preferable, and 40m 2 / g is more preferable, and 50m 2 More preferably, it is more than 60m 2 More preferably, it is more than 70m 2 From the viewpoint of excellent dispersibility and low heat generation, the N2SA has a viscosity of 300 m / g or more. 2 / g is preferable, and 200m 2 / g is more preferable, and 150m 2 / g is more preferable, and 120m 2 / g is more preferable, and 110m 2 / g is more preferable, and 100m 2 / g is more preferable, and 90m 2 It is more preferable that the N of carbon black in this specification is less than 1 / g. 2 SA is a value measured in accordance with JIS K 6217-2:2017.

[0111] <Silica> As the silica, dry process silica (anhydrous silica), wet process silica (hydrated silica), etc. can be used. Among them, wet process silica is preferred because it has a large number of silanol groups. As commercially available products, products from Evonik Degussa, Rhodia, Tosoh Silica, Solvay Japan, Tokuyama, etc. can be used. Silica may be used alone or in combination of two or more kinds.

[0112] The nitrogen adsorption specific surface area (N2SA) of the silica is preferably 50 m 2 / g, more preferably 100m 2 / g, more preferably 150m 2 / g, particularly preferably 170m 2 The upper limit of the N2SA of silica is not particularly limited, but is preferably 350 m 2 / g, more preferably less than 250m 2 / g, more preferably less than 200m 2 / g. By keeping it within the above range, cut resistance tends to be improved. The N2SA of silica is a value measured by the BET method in accordance with ASTM D3037-93.

[0113] <Silane coupling agent> When silica is used as the filler, it is preferred that a silane coupling agent is further contained. The silane coupling agent is not particularly limited, and examples thereof include bis(3-triethoxysilylpropyl)tetrasulfide, bis(2-triethoxysilylethyl)tetrasulfide, bis(4-triethoxysilylbutyl)tetrasulfide, bis(3-trimethoxysilylpropyl)tetrasulfide, bis(2-trimethoxysilylethyl)tetrasulfide, bis(2-triethoxysilylethyl)trisulfide, bis(4-trimethoxysilylbutyl)trisulfide, bis(3-triethoxysilylpropyl)disulfide, bis(2-triethoxysilylethyl)disulfide, bis(4-triethoxysilylbutyl)disulfide, bis(3-trimethoxysilylpropyl)disulfide, bis(2-trimethoxysilylethyl)disulfide, bis(4-trimethoxysilylbutyl)disulfide, 3-trimethoxysilylpropyl-N,N-dimethylthiocarbamate, Examples of such silanes include sulfide-based silanes such as bamoyl tetrasulfide, 2-triethoxysilylethyl-N,N-dimethylthiocarbamoyl tetrasulfide, and 3-triethoxysilylpropyl methacrylate monosulfide; mercapto-based silanes such as 3-mercaptopropyltrimethoxysilane, 2-mercaptoethyltriethoxysilane, and Momentive's NXT and NXT-Z; vinyl-based silanes such as vinyltriethoxysilane and vinyltrimethoxysilane; amino-based silanes such as 3-aminopropyltriethoxysilane and 3-aminopropyltrimethoxysilane; glycidoxy-based silanes such as γ-glycidoxypropyltriethoxysilane and γ-glycidoxypropyltrimethoxysilane; nitro-based silanes such as 3-nitropropyltrimethoxysilane and 3-nitropropyltriethoxysilane; and chloro-based silanes such as 3-chloropropyltrimethoxysilane and 3-chloropropyltriethoxysilane. Commercially available products include those manufactured by Evonik Degussa, Momentive, Shin-Etsu Silicones, Tokyo Chemical Industry, Azumax, and Dow Corning Toray Co., Ltd. These may be used alone or in combination of two or more.

[0114] Other fillers The other fillers are not particularly limited, and materials known in the field of the tire industry can be used, such as inorganic fillers such as calcium carbonate, talc, alumina, clay, aluminum hydroxide, aluminum oxide, mica, etc. These may be used alone or in combination of two or more kinds.

[0115] (oil) The oil is not particularly limited, and any oil normally used in the tire industry can be suitably used, such as paraffinic, aromatic, and naphthenic process oils. In addition, process oils with a low content of polycyclic aromatic compounds (PCA) compounds can be used as an environmental measure. Examples of low PCA content process oils include Treated Distillate Aromatic Extract (TDAE) obtained by re-extracting aromatic process oils, aroma substitute oils that are mixtures of asphalt and naphthenic oils, mild extraction solvates (MES), and heavy naphthenic oils. Among them, aromatic process oils are preferred, and TDAE oils are more preferred. For example, oils manufactured and sold by H&R, JXTG Energy, Idemitsu Kosan, Sankyo Yuka Kogyo, etc. can be used. One type of oil or a combination of two or more types of oils can be used.

[0116] When oil is contained, the content per 100 parts by mass of the rubber component is preferably more than 1 part by mass, more preferably more than 3 parts by mass, and even more preferably more than 5 parts by mass, from the viewpoint of the effects of the present invention. The content is preferably less than 20 parts by mass, more preferably less than 15 parts by mass, and even more preferably less than 10 parts by mass. The oil content includes the amount of oil contained in the rubber component as an extender oil and the amount of oil contained in other components such as sulfur.

[0117] (Plasticizers other than oil) The rubber composition may contain a plasticizer other than oil. Examples of the plasticizer other than oil include resins, ester-based plasticizers, liquid polymers, liquid resins, and the like.

[0118] (resin) The resin is not particularly limited, and any resin commonly used in the rubber industry can be suitably used, such as the adhesive resin described below. These resins may be used alone or in combination of two or more kinds.

[0119] The softening point of these resins is preferably in the range of less than 180°C from the viewpoint of optimally exerting the function as a plasticizer. The upper limit of the softening point is preferably less than 170°C, more preferably less than 150°C, and even more preferably less than 130°C. However, the "resin" referred to here does not include liquid resins that are liquid at room temperature (25°C). In this specification, the softening point of a resin is the temperature at which the ball drops when the softening point specified in JIS K 6220-1 is measured using a ring and ball softening point measuring device.

[0120] (Ester plasticizer) The ester-based plasticizer is not particularly limited, and any of those commonly used in the rubber industry can be suitably used. For example, dibutyl adipate (DBA), diisobutyl adipate (DIBA), dioctyl adipate (DOA), di-2-ethylhexyl azelate (DOZ), dibutyl sebacate (DBS), diisononyl adipate (DINA), diethyl phthalate (DEP), dioctyl phthalate (DOP), diundecyl phthalate (DUP), dibutyl phthalate (DBP), dioctyl sebacate (DOS), tributyl phosphate (TBP), trioctyl phosphate (TOP), triethyl phosphate (TEP), trimethyl phosphate (TMP), thymidine triphosphate (TTP), tricresyl phosphate (TCP), trixylenyl phosphate (TXP), and the like can be mentioned. Among them, DOS and TOP are preferred from the viewpoint of the balance between the plasticizing effect and the abrasion resistance at low temperatures, and DOS is preferred from the viewpoint of excellent fuel economy. The ester-based plasticizers may be used alone or in combination of two or more kinds.

[0121] (Liquid Polymer) The liquid polymer is a polymer that is liquid at room temperature (25°C), and examples thereof include liquid diene polymers. Examples of liquid diene polymers include liquid styrene butadiene copolymers (liquid SBR), liquid butadiene polymers (liquid BR), liquid isoprene polymers (liquid IR), and liquid styrene isoprene copolymers (liquid SIR). The number average molecular weight (Mn) of the liquid diene polymer, measured by gel permeation chromatography (GPC) in terms of polystyrene, is preferably more than 1000, more preferably more than 3000, and is preferably less than 100,000, more preferably less than 15,000. The Mn of the liquid polymer is a value measured by gel permeation chromatography (GPC) in terms of polystyrene. Examples of the liquid diene polymer that can be used include products from Sartomer Co., Ltd. and Kuraray Co., Ltd. The liquid polymers may be used alone or in combination of two or more kinds.

[0122] (liquid resin) The liquid resin is a resin that is liquid at room temperature (25°C), and is not particularly limited, but examples thereof include liquid aromatic vinyl polymers, coumarone-indene resins, indene resins, terpene resins, rosin resins, and hydrogenated products thereof. Examples of liquid resins that can be used include products from Maruzen Petrochemical Co., Ltd., Sumitomo Bakelite Co., Ltd., Yasuhara Chemical Co., Ltd., Tosoh Corporation, Rutgers Chemicals, BASF, Arizona Chemical Co., Ltd., Nippon Paint Chemical Co., Ltd., Nippon Shokubai Co., Ltd., ENEOS Corporation, Arakawa Chemical Industries Co., Ltd., and Taoka Chemical Co., Ltd. The liquid resins may be used alone or in combination of two or more kinds.

[0123] When the rubber composition contains a plasticizer other than oil, the content thereof is preferably in a range that satisfies the above formula (5).

[0124] (Other compounding agents) Other compounding ingredients that may be used include resins, antioxidants, waxes, stearic acid, zinc oxide, vulcanizing agents, and vulcanization accelerators.

[0125] <Resin> Here, the resin is a resin that is solid at room temperature (25°C). Such a resin is not particularly limited, and resins commonly used in the tire industry, such as aromatic petroleum resins, can be used. Examples of aromatic petroleum resins include phenolic resins, coumarone-indene resins, styrene resins, terpene resins, acrylic resins, rosin resins, and dicyclopentadiene resins (DCPD resins). The resins can be used alone or in combination of two or more.

[0126] When a resin is contained, the content per 100 parts by mass of the rubber component is preferably more than 2 parts by mass, more preferably more than 3 parts by mass, and even more preferably more than 4 parts by mass, while the content is preferably less than 20 parts by mass, more preferably less than 15 parts by mass, and even more preferably less than 10 parts by mass.

[0127] <Anti-aging agent> The antiaging agent is not particularly limited, and any of those commonly used in the tire industry can be suitably used. Examples of the antiaging agent include quinoline-based antiaging agents, quinone-based antiaging agents, phenol-based antiaging agents, phenylenediamine-based antiaging agents, and carbamic acid metal salts. Among them, phenylenediamine-based antiaging agents are preferred because they can better improve the ozone resistance.

[0128] When an antioxidant is contained, the content thereof per 100 parts by mass of the rubber component is preferably more than 0.5 parts by mass, more preferably more than 0.8 parts by mass, and even more preferably more than 1.0 part by mass, while the content is preferably less than 7.0 parts by mass, more preferably less than 5.0 parts by mass, and even more preferably 3.0 parts by mass or less.

[0129] <Wax> The wax is not particularly limited, and any wax commonly used in the tire industry can be suitably used, such as petroleum wax, mineral wax, and synthetic wax. Of these, petroleum wax is preferred. Petroleum wax includes, for example, paraffin wax, microcrystalline wax, and selected special waxes thereof, and paraffin wax is preferred. Waxes that can be used include, for example, those manufactured and sold by Ouchi Shinko Chemical Industry Co., Ltd., Nippon Seiro Co., Ltd., Paramelt Co., Ltd., and the like. Waxes can be used alone or in combination of two or more kinds.

[0130] When the wax is contained, the content thereof per 100 parts by mass of the rubber component is preferably more than 0.3 parts by mass, more preferably more than 0.7 parts by mass, and even more preferably more than 1.0 part by mass, while the content is preferably less than 4.0 parts by mass, more preferably less than 3.0 parts by mass, and even more preferably less than 2.5 parts by mass.

[0131] <Stearic acid> When stearic acid is contained, the content per 100 parts by mass of the rubber component is preferably more than 0.5 parts by mass, more preferably more than 0.7 parts by mass, and even more preferably 1.0 part by mass or more from the viewpoint of processability, while the content is preferably less than 10 parts by mass, more preferably less than 5 parts by mass, and even more preferably less than 3 parts by mass from the viewpoint of vulcanization speed.

[0132] <Zinc oxide> When zinc oxide is contained, the content per 100 parts by mass of the rubber component is preferably more than 0.5 parts by mass, more preferably more than 0.7 parts by mass, and even more preferably more than 1 part by mass from the viewpoint of processability, while the content is preferably 10 parts by mass or less, more preferably less than 7 parts by mass, and even more preferably 5 parts by mass or less from the viewpoint of abrasion resistance.

[0133] <Vulcanizing agent> The vulcanizing agent is not particularly limited, and known vulcanizing agents can be used, such as organic peroxides, sulfur-based vulcanizing agents, resin vulcanizing agents, and metal oxides such as magnesium oxide. Among these, sulfur-based vulcanizing agents are preferred. As the sulfur-based vulcanizing agent, for example, sulfur donors such as sulfur and morpholine disulfide can be used. Among these, it is preferred to use sulfur. The vulcanizing agent can be used alone or in combination of two or more.

[0134] Examples of sulfur include powdered sulfur, precipitated sulfur, colloidal sulfur, surface-treated sulfur (oil-treated sulfur, special sulfur treated with a dispersant, master batch-type sulfur, etc.), and insoluble sulfur (oil-treated insoluble sulfur, etc.), and any of these can be used suitably. Among these, powdered sulfur is preferred. Examples of sulfur that can be used include those manufactured and sold by Tsurumi Chemical Industry Co., Ltd., Karuizawa Sulfur Co., Ltd., Shikoku Chemical Industry Co., Ltd., Flexis Co., Ltd., Nippon Kanzuri Kogyo Co., Ltd., Hosoi Chemical Industry Co., Ltd., etc.

[0135] When the vulcanizing agent is contained, the content relative to 100 parts by mass of the rubber component is preferably more than 0.4 parts by mass, more preferably more than 0.5 parts by mass, even more preferably more than 1.0 parts by mass, and even more preferably more than 1.5 parts by mass. On the other hand, the content is preferably less than 6.0 parts by mass, more preferably 5.0 parts by mass or less, and even more preferably less than 4.0 parts by mass. When the content of the vulcanizing agent is within the above range, there is a tendency that an appropriate reinforcing effect is obtained, and the effect of the present invention tends to be better exhibited. In addition, when the vulcanizing agent contains a component other than sulfur, such as oil-treated sulfur, the content of the vulcanizing agent means the content of the sulfur component itself.

[0136] <Vulcanization accelerator> The vulcanization accelerator is not particularly limited, and known vulcanization accelerators can be used, such as sulfenamide-based, thiazole-based, thiuram-based, thiourea-based, guanidine-based, dithiocarbamic acid-based, aldehyde-amine-based or aldehyde-ammonia-based, imidazoline-based, or xanthate-based vulcanization accelerators. Among them, sulfenamide-based, thiuram-based, and guanidine-based are preferred, and sulfenamide-based are more preferred. As the vulcanization accelerator, for example, those manufactured and sold by Ouchi Shinko Chemical Industry Co., Ltd., Sanshin Chemical Industry Co., Ltd., etc. can be used. These vulcanization accelerators can be used alone or in combination of two or more.

[0137] Examples of sulfenamide vulcanization accelerators include N-tert-butyl-2-benzothiazolylsulfenamide (TBBS), N-cyclohexyl-2-benzothiazolylsulfenamide (CBS), and N,N'-dicyclohexyl-2-benzothiazolylsulfenamide (DZ). Examples of thiuram vulcanization accelerators include tetramethylthiuram monosulfide, tetramethylthiuram disulfide, and tetrabenzylthiuram disulfide (TBzTD). Examples of guanidine vulcanization accelerators include 1,3-diphenylguanidine (DPG), di-orthotolylguanidine, and orthotolylbiguanidine.

[0138] The content of the vulcanization accelerator relative to 100 parts by mass of the rubber component is preferably more than 0.3 parts by mass, more preferably more than 0.4 parts by mass, and even more preferably more than 0.5 parts by mass. On the other hand, the content is preferably less than 4.0 parts by mass, more preferably less than 3.0 parts by mass, and even more preferably less than 2.0 parts by mass. When the content of the vulcanization accelerator is within the above range, the breaking strength and elongation tend to be secured, and the effects of the present invention tend to be more favorably exhibited.

[0139] <Rubber composition for carcass cord topping rubber> Each component of the rubber composition for the carcass cord topping rubber will be described.

[0140] (Rubber component) The rubber component preferably contains IR rubber and SBR. In this case, the rubber component may contain rubber components other than IR rubber and SBR. The rubber component may also consist of only IR rubber and SBR. The components that may constitute the rubber component are described in the section on rubber composition for sidewall rubber.

[0141] ≪Content≫ The content of the IR rubber in 100% by mass of the rubber component is preferably more than 35% by mass, more preferably more than 40% by mass, even more preferably more than 50% by mass, and even more preferably more than 60% by mass. On the other hand, the content is preferably less than 95% by mass, more preferably less than 90% by mass, even more preferably less than 85% by mass, and even more preferably less than 80% by mass.

[0142] The content of SBR in 100% by mass of the rubber component is preferably more than 5% by mass, more preferably more than 10% by mass, even more preferably more than 15% by mass, and even more preferably more than 20% by mass, while the content is preferably less than 60% by mass, more preferably less than 50% by mass, even more preferably less than 40% by mass, and even more preferably less than 35% by mass.

[0143] The total content of the IR rubber and SBR in 100% by mass of the rubber component is preferably more than 80% by mass, more preferably more than 90% by mass, and further preferably more than 95% by mass, and may be 100% by mass.

[0144] (Filler) The filler may include recycled carbon black (rCB). The filler may also include carbon black other than rCB and silica. When the filler includes silica, it may further include a silane coupling agent. The filler may further include other fillers other than carbon black and silica. The components that may constitute the filler are as described in the section on the rubber composition for sidewall rubber.

[0145] <Carbon black content> When carbon black is contained, the total content of carbon black including recycled carbon black is preferably more than 30 parts by mass, more preferably more than 40 parts by mass, and even more preferably more than 50 parts by mass, based on 100 parts by mass of the rubber component. On the other hand, the total content is preferably less than 150 parts by mass, more preferably less than 110 parts by mass, and even more preferably less than 80 parts by mass. When the carbon black content is within the above range, sufficient reinforcing properties and good dispersion in the rubber are obtained, and sufficient rubber strength and crack growth resistance tend to be obtained.

[0146] The content of recycled carbon black in the total content of carbon black is preferably less than 60% by mass, more preferably less than 50% by mass, even more preferably less than 45% by mass, even more preferably less than 35% by mass, and even more preferably less than 25% by mass, from the viewpoint of reinforcing properties. On the other hand, the content is preferably more than 1% by mass, more preferably more than 5% by mass, even more preferably more than 10% by mass, and even more preferably more than 20% by mass, from the viewpoint of the effects of the present invention. Note that the content of recycled carbon black in the total content of carbon black may be even lower, may be less than 20% by mass, may be less than 10% by mass, or may be 0% by mass. This is because other components may contain recycled carbon black.

[0147] <Silica content> When silica is contained, the content per 100 parts by mass of the rubber component is not particularly limited, but from the viewpoint of ensuring fuel economy, wet grip performance, and sufficient reinforcement, it is preferably more than 1 part by mass, more preferably 5 parts by mass or more, more preferably more than 10 parts by mass, and even more preferably more than 20 parts by mass. Also, from the viewpoints of dispersibility of silica, processability, and wet grip performance, the content is preferably less than 150 parts by mass, more preferably less than 100 parts by mass, even more preferably less than 50 parts by mass, and even more preferably less than 30 parts by mass.

[0148] <Silane coupling agent content> When a silane coupling agent is contained, the content of the silane coupling agent can be similarly applied to the explanation given for the rubber composition for the sidewall rubber.

[0149] (oil) As for the oil, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0150] (Plasticizers other than oil) As for plasticizers other than oil, the explanation given for the rubber composition for the sidewall rubber can be similarly applied as long as it does not contradict the explanation given for the rubber composition for the carcass cord topping rubber.

[0151] (Other compounding agents) As for the other compounding ingredients, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0152] <Rubber composition for breaker topping rubber> Each component of the rubber composition for the breaker topping rubber will be described.

[0153] (Rubber component) The rubber component preferably contains an isoprene-based rubber (IR-based rubber). In this case, the rubber component may contain a rubber component other than the IR-based rubber. The rubber component may also consist of only the IR-based rubber. The components that may constitute the rubber component are described in the section on the rubber composition for sidewall rubber.

[0154] ≪Content≫ The content of the IR rubber in 100% by mass of the rubber component is preferably more than 80% by mass, more preferably more than 90% by mass, further preferably more than 95% by mass, and may be 100% by mass.

[0155] (Filler) The filler may include recycled carbon black (rCB). The filler may also include carbon black other than rCB and silica. When the filler includes silica, it may further include a silane coupling agent. The filler may further include other fillers other than carbon black and silica. The components that may constitute the filler are as described in the section on the rubber composition for sidewall rubber.

[0156] <Carbon black content> When carbon black is contained, the total content of carbon black including recycled carbon black is preferably more than 30 parts by mass, more preferably more than 35 parts by mass, and even more preferably more than 40 parts by mass, based on 100 parts by mass of the rubber component. On the other hand, the total content is preferably less than 150 parts by mass, more preferably less than 110 parts by mass, and even more preferably less than 80 parts by mass. When the carbon black content is within the above range, sufficient reinforcing properties and good dispersion in the rubber are obtained, and sufficient rubber strength and crack growth resistance tend to be obtained.

[0157] The content of recycled carbon black in the total content of carbon black is preferably less than 60% by mass, more preferably less than 50% by mass, even more preferably less than 45% by mass, even more preferably less than 35% by mass, and even more preferably less than 25% by mass, from the viewpoint of reinforcing properties. On the other hand, the content is preferably more than 1% by mass, more preferably more than 5% by mass, even more preferably more than 10% by mass, and even more preferably more than 20% by mass, from the viewpoint of the effects of the present invention. Note that the content of recycled carbon black in the total content of carbon black may be even lower, may be less than 20% by mass, may be less than 10% by mass, or may be 0% by mass. This is because other components may contain recycled carbon black.

[0158] <Silica content> When silica is contained, the content per 100 parts by mass of the rubber component is not particularly limited, but from the viewpoint of ensuring fuel economy, wet grip performance, and sufficient reinforcement, it is preferably more than 1 part by mass, more preferably more than 5 parts by mass, more preferably 10 parts by mass or more, and even more preferably more than 20 parts by mass. Also, from the viewpoints of dispersibility of silica, processability, and wet grip performance, the content is preferably less than 150 parts by mass, more preferably less than 100 parts by mass, even more preferably less than 50 parts by mass, and even more preferably less than 30 parts by mass.

[0159] <Silane coupling agent content> When a silane coupling agent is contained, the content of the silane coupling agent can be similarly applied to the explanation given for the rubber composition for the sidewall rubber.

[0160] (Organic Cobalt Acid) The rubber composition may contain an organic cobalt acid. The organic cobalt acid acts to crosslink the cord and the rubber, and by compounding this component, the adhesion between the cord and the rubber can be improved. Examples of the organic cobalt acid include cobalt stearate, cobalt naphthenate, cobalt neodecanoate, and boron-3 cobalt neodecanoate. Among these, cobalt stearate is preferred in that it functions as a processing aid (reduces viscosity).

[0161] From the viewpoint of adhesion, the content of the organic acid cobalt is preferably more than 0.05 parts by mass, more preferably more than 0.08 parts by mass, and even more preferably more than 0.09 parts by mass, calculated as cobalt, per 100 parts by mass of the rubber component, while from the viewpoint of the rupture properties of the rubber, the content is preferably less than 0.30 parts by mass, more preferably less than 0.25 parts by mass, and even more preferably less than 0.20 parts by mass.

[0162] (thermosetting resin) The rubber composition may contain a thermosetting resin. This can strengthen the adhesion between the cord and the rubber. Examples of the thermosetting resin include cashew oil modified phenolic resin, resorcinol resin, and modified resorcinol resin. By including at least one of these compounds, the elongation at break and the complex modulus of elasticity can be improved. The thermosetting resin may be used alone or in combination of two or more.

[0163] The cashew oil modified phenolic resin is, for example, a resin obtained by modifying a phenolic resin obtained by reacting phenol with an aldehyde such as formaldehyde, acetaldehyde, or furfural using an acid or alkali catalyst, with cashew oil, and examples of such resins include those manufactured by Sumitomo Bakelite Co., Ltd. The resorcinol resin is, for example, a resorcinol-formaldehyde condensate, and examples of such resins include those manufactured by Sumitomo Chemical Co., Ltd. The modified resorcinol resin is, for example, a resorcinol resin in which a part of the repeating unit is alkylated, and examples of such resins include those manufactured by Indospec, Taoka Chemical Co., Ltd., Uniroyal, Schenectady Chemical Co., and Ashland Chemical Co.

[0164] When a thermosetting resin is contained, the content thereof per 100 parts by mass of the rubber component is preferably more than 0.5 parts by mass, more preferably more than 0.7 parts by mass, and even more preferably more than 1.2 parts by mass, from the viewpoints of complex elastic modulus and durability. On the other hand, the content thereof is preferably less than 10 parts by mass, more preferably less than 7 parts by mass, and even more preferably less than 3 parts by mass, from the viewpoints of fuel economy, elongation at break, processability (sheet rollability) and durability.

[0165] The thermoplastic resin can be used in combination with a curing agent, which can strengthen the adhesion between the cord and the rubber. The curing agent is not particularly limited, but includes partial condensates of hexamethoxymethylolmelamine (HMMM) and hexamethylolmelamine pentamethylether (HMMPME). Of these, partial condensates of hexamethylolmelamine pentamethylether (HMMPME) are preferred. The curing agents may be used alone or in combination of two or more.

[0166] When a curing agent is contained, the content per 100 parts by mass of the rubber component is preferably more than 0.5 parts by mass, more preferably more than 1.0 parts by mass, and even more preferably more than 1.5 parts by mass from the viewpoint of the complex modulus (E*). On the other hand, the content is preferably less than 5 parts by mass, more preferably less than 3 parts by mass, and even more preferably less than 2 parts by mass from the viewpoint of the elongation at break.

[0167] (oil) As for the oil, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0168] (Plasticizers other than oil) As for plasticizers other than oil, the explanation given for the rubber composition for the sidewall rubber can be similarly applied as long as it does not contradict the explanation given for the rubber composition for the breaker topping rubber.

[0169] (Other compounding agents) As for the other compounding ingredients, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0170] (Organic Thiosulfate Compounds) In the rubber composition of the present invention, an organic thiosulfate compound can be used in combination with sulfur as a vulcanizing agent. The organic thiosulfate compound is not particularly limited, but is preferably a compound represented by the following chemical formula (1) and / or a hydrate thereof. MO3S-S-(CH2)qS-SO3M (1) (In the formula, q represents an integer of 3 to 10. M may be the same or different and represents lithium, potassium, sodium, magnesium, calcium, barium, zinc, nickel, or cobalt.)

[0171] In the chemical formula (1), q is preferably an integer of 3 to 6, M is more preferably potassium or sodium, and the hydrate of the compound represented by the chemical formula (1) is preferably, for example, a sodium salt monohydrate, a sodium salt dihydrate, etc. As the compound represented by the chemical formula (1) and its hydrate, a derivative derived from sodium thiosulfate, for example, sodium 1,6-hexamethylene-dithiosulfate dihydrate, is preferred.

[0172] <Rubber composition for inner liner rubber> Each component of the rubber composition for the inner liner rubber will be described.

[0173] (Rubber component) The rubber component preferably contains butyl-based rubber and isoprene-based rubber (IR-based rubber). In this case, the rubber component may contain rubber components other than the butyl-based rubber and the IR-based rubber. The rubber component may also be composed of only the butyl-based rubber and the IR-based rubber.

[0174] <Butyl rubber> Examples of butyl-based rubbers include butyl rubber (IIR), halogenated butyl rubbers such as brominated butyl rubber (Br-IIR) and chlorinated butyl rubber (Cl-IIR). Among these, halogenated butyl rubber is preferred, and brominated butyl rubber and chlorinated butyl rubber are more preferred, in that they can improve sheet processability and air barrier properties in a well-balanced manner. These may be used alone or in combination.

[0175] As for butyl rubber, in addition to regular butyl rubber (butyl rubber other than recycled butyl rubber), recycled butyl rubber can be used in combination. Recycled butyl rubber usually has a high content of non-halogenated butyl rubber (regular butyl rubber), so by using it in combination with halogenated butyl rubber, good air barrier properties and vulcanization speed can be ensured. Recycled butyl rubber may be used alone or in combination of two or more types.

[0176] <Isoprene rubber> For the IR rubber, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0177] Other Rubbers The rubber component may contain other rubber components in addition to the butyl rubber and isoprene rubber. Examples of the rubber components include diene rubbers such as butadiene rubber (BR), styrene butadiene rubber (SBR), styrene isoprene butadiene rubber (SIBR), chloroprene rubber (CR), and acrylonitrile butadiene rubber (NBR). The explanation given for the rubber composition for the sidewall rubber can be applied to these other rubber components. These other rubber components may be used alone or in combination of two or more kinds.

[0178] ≪Content≫ From the viewpoint of sufficient air barrier properties, the content of the butyl-based rubber in 100% by mass of the rubber component is preferably more than 70% by mass, more preferably more than 75% by mass, and further preferably 80% or more by mass.

[0179] The content of recycled butyl rubber in 100% by mass of the rubber component is preferably more than 5% by mass, more preferably more than 8% by mass, and even more preferably more than 10% by mass, from the viewpoint of fully utilizing the merits of using recycled butyl rubber. From the viewpoint of sufficient fracture properties and vulcanization speed, the content is preferably less than 50% by mass, more preferably less than 30% by mass, and even more preferably less than 20% by mass.

[0180] From the viewpoint of ensuring sufficient air barrier properties, the content of the isoprene-based rubber in 100% by mass of the rubber component is preferably less than 25% by mass, more preferably less than 23% by mass, and even more preferably 20% by mass or less.

[0181] (Filler) The filler may include recycled carbon black (rCB). The filler may also include carbon black other than rCB and silica. When the filler includes silica, it may further include a silane coupling agent. The filler may further include other fillers other than carbon black and silica. The components that may constitute the filler are as described in the section on the rubber composition for sidewall rubber.

[0182] <Pulverized bituminous coal> From the viewpoints of sheet processability and air permeability resistance, the rubber composition of the present invention may further contain pulverized bituminous coal as a filler.

[0183] <Carbon black content> When carbon black is contained, the total content of carbon black including recycled carbon black is preferably more than 30 parts by mass, more preferably more than 40 parts by mass, and even more preferably more than 50 parts by mass, based on 100 parts by mass of the rubber component. On the other hand, the total content is preferably less than 150 parts by mass, more preferably less than 110 parts by mass, and even more preferably less than 80 parts by mass. When the carbon black content is within the above range, sufficient reinforcing properties and good dispersion in the rubber are obtained, and sufficient rubber strength and crack growth resistance tend to be obtained.

[0184] The content of recycled carbon black in the total content of carbon black is preferably less than 60% by mass, more preferably less than 50% by mass, even more preferably less than 45% by mass, even more preferably less than 35% by mass, and even more preferably less than 25% by mass, from the viewpoint of reinforcing properties. On the other hand, the content is preferably more than 1% by mass, more preferably more than 5% by mass, even more preferably more than 10% by mass, and even more preferably more than 15% by mass, from the viewpoint of the effects of the present invention. Note that the content of recycled carbon black in the total content of carbon black may be even lower, may be less than 15% by mass, may be less than 10% by mass, or may be 0% by mass. This is because other components may contain recycled carbon black.

[0185] <Silica content> When silica is contained, the content per 100 parts by mass of the rubber component is not particularly limited, but from the viewpoint of ensuring fuel economy, wet grip performance, and sufficient reinforcement, it is preferably more than 1 part by mass, more preferably more than 5 parts by mass, more preferably more than 10 parts by mass, and even more preferably more than 20 parts by mass. Also, from the viewpoints of dispersibility of silica, processability, and wet grip performance, the content is preferably less than 150 parts by mass, more preferably less than 100 parts by mass, even more preferably less than 50 parts by mass, and even more preferably less than 30 parts by mass.

[0186] <Silane coupling agent content> When a silane coupling agent is contained, the content of the silane coupling agent can be similarly applied to the explanation given for the rubber composition for the sidewall rubber.

[0187] <Content of crushed bituminous coal> When bituminous coal pulverized material is contained, the content per 100 parts by mass of the rubber component is preferably more than 1 part by mass, more preferably more than 5 parts by mass, and even more preferably more than 10 parts by mass, while the content is preferably less than 20 parts by mass, more preferably less than 15 parts by mass, and even more preferably less than 12 parts by mass.

[0188] (Adhesive resin) The rubber composition may contain a tackifying resin. Examples of the tackifying resin include mixed resins, non-reactive alkylphenol resins, C5 petroleum resins, and coumarone-indene resins. Among these, it is preferable to contain a mixed resin because it improves air barrier properties and molding tackiness.

[0189] The mixed resin refers to a resin obtained by copolymerizing an aromatic hydrocarbon structure monomer and an aliphatic hydrocarbon structure monomer. Examples of the aromatic hydrocarbon structure monomer used in the mixed resin include monomers having a phenol structure, a coumarone structure, an indene structure, and a coumarone-indene structure, and examples of the aliphatic hydrocarbon structure monomer include monomers having an aliphatic hydrocarbon structure such as C2, C3, C5, C8, and C9. Examples of the mixed resin include those manufactured by Struktol, Rhein Chemie Corp., and Flow Polymers Inc. The non-reactive alkylphenol resin refers to a resin having an alkyl chain at the ortho-position and para-position (especially the para-position) of the hydroxyl group of the benzene ring in the chain, and making a small contribution to the crosslinking reaction during vulcanization. For example, those manufactured by Struktol and Schenectady Chemical Co., Ltd. can be used. Examples of C5-based petroleum resin include those manufactured by Maruzen Petrochemical Co., Ltd. The coumarone-indene resin is a resin containing coumarone and indene, and products manufactured by Nippon Paint Chemical Co., Ltd., Rutgers Chemicals, etc. can be used.

[0190] When a tacky resin is used, the content per 100 parts by mass of the rubber component is preferably more than 1 part by mass, more preferably more than 3 parts by mass, and even more preferably 5 parts by mass or more, from the viewpoints of air barrier property and molding tackiness. On the other hand, the content is preferably less than 30 parts by mass, more preferably less than 20 parts by mass, and even more preferably less than 10 parts by mass, from the viewpoints of molding tackiness and embrittlement resistance at low temperatures.

[0191] (oil) As for the oil, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0192] (Plasticizers other than oil) As for plasticizers other than oil, the explanation given for the rubber composition for the sidewall rubber can be similarly applied as long as it does not contradict the explanation given for the rubber composition for the inner liner rubber.

[0193] (Other compounding agents) As for the other compounding ingredients, the explanation given for the rubber composition for the sidewall rubber can be similarly applied.

[0194] <Other rubber components that make up tires> The tire according to the present invention may include rubber members other than those described above. Such other rubber members are not particularly limited, and various rubber members generally used in tires may be used.

[0195] In the case where the tire according to the present invention includes other rubber components, the other rubber components may contain oil. The explanation given for the rubber composition for the sidewall rubber is similarly applicable to the oil.

[0196] In the case where the tire according to the present invention includes other rubber components, the other rubber components may contain a plasticizer other than oil. The explanation given for the rubber composition for the sidewall rubber is similarly applicable to the plasticizer other than oil.

[0197] <Application> The tire according to the present invention can be suitably used as a pneumatic tire, regardless of whether it is a pneumatic tire or a non-pneumatic tire. The tire according to the present invention can be used for various purposes such as passenger car tires, heavy load tires such as trucks and buses, motorcycle tires, and high performance tires.

[0198] <Production method> The tire of the present invention can be manufactured by a known method.

[0199] (Production of Rubber Composition) First, each rubber composition related to the tire of the present invention is manufactured. Each of these rubber compositions can be manufactured by a known method. For example, the above-mentioned components can be manufactured by kneading them using a rubber kneading device such as an open roll or an internal kneader (Banbury mixer, kneader, etc.). The kneading process includes, for example, a base kneading process in which compounding agents and additives other than the vulcanizing agent and the vulcanization accelerator are kneaded, and a final kneading (F kneading) process in which the vulcanizing agent and the vulcanization accelerator are added to the kneaded product obtained in the base kneading process and kneaded. Furthermore, the base kneading process can be divided into a plurality of processes as desired. The kneading conditions are not particularly limited, but for example, the base kneading process includes kneading for 3 to 10 minutes at a discharge temperature of 150 to 170°C, and the final kneading process includes kneading for 1 to 5 minutes at 50 to 110°C.

[0200] (Tire manufacturing) Each rubber composition obtained above is extruded in the unvulcanized stage according to the shape of the desired tire component, or when used as a topping rubber, it is extruded once in a shape such as a sheet, and then used as a topping rubber to prepare the desired tire component, and each tire component thus obtained is molded together with other tire components in a tire building machine by a normal method to obtain an unvulcanized tire. The tire of the present invention can be obtained by heating and pressurizing this unvulcanized tire in a vulcanizer (vulcanization). The vulcanization conditions are not particularly limited, and examples include a method of vulcanization at 150 to 200 ° C for 5 to 30 minutes. EXAMPLES

[0201] The following examples (working examples) are considered to be preferable for carrying out the present invention, but the scope of the present invention is not limited to these working examples. Tires obtained according to each table were examined using the various chemicals shown below, and the results calculated based on the evaluation method shown below are shown as durability indices at the bottom of each table.

[0202] <Material> The materials used in the examples and comparative examples will be collectively described below. Isoprene rubber: NR (TSR20) BR: UBEPOL BR150B (manufactured by Ube Industries, Ltd., cis content: 97% by mass, Mw: 440,000) SBR: SBR1502 (manufactured by JSR Corporation, styrene content: 23.5% by mass, vinyl content: 18% by mole, Mw: 500,000) Butyl rubber: Chlorobutyl HT1066 (Exxon Mobil, chlorobutyl rubber) Carbon black 1: Show Black N330 (manufactured by Cabot Japan Co., Ltd., N2SA: 75 m 2 / g) Carbon black 2: Show Black N550 (Cabot Japan Co., Ltd., N2SA: 42m 2 / g) Carbon black 3: Show Black N660 (manufactured by Cabot Japan Co., Ltd., N2SA: 35m 2 / g) Carbon black 4: Show Black N326 (Cabot Japan Co., Ltd., N2SA: 78m 2 / g) Silica: Ultrasil VN3 (Evonik Degussa, N2SA: 175m 2 / g) Bituminous coal pulverized material: Austin Black 325 (manufactured by Coal Fillers Inc., average particle size: 5.5 μm, oil content: 17 mass%, specific gravity: 1.3, N2SA: 9.0 m 2 / g) Recycled carbon black (rCB): Carbon black obtained from the pyrolysis process of tires (ash content: 17% by mass) Pyrolytic carbon black: Carbon black obtained from the pyrolysis process of tires (ash content: 10% by mass) Silane coupling agent: Si266 (Evonik Degussa, bis(3-triethoxysilylpropyl) disulfide) Organic cobalt acid: Co-STEARATE (DIC Corporation, cobalt stearate, cobalt content: 9.5% by mass, stearic acid content: 90.5% by mass) Organic thiosulfate compound: DURALINK HTS (Flexis Corporation, sodium 1,6-hexamethylene dithiosulfate dihydrate) Adhesive resin: Struktol 40MS (Struktol, ethylene propylene styrene copolymer, ethylene propylene content 82% by mass, softening point: 98 to 106°C) Thermosetting resin 1: Sumikanol 620 (manufactured by Taoka Chemical Co., Ltd., modified resorcinol resin (modified resorcinol-formaldehyde condensate)) Hardener: Sumikanol 507A (manufactured by Sumitomo Chemical Co., Ltd., modified etherified methylol melamine resin (partial condensate of hexamethylol melamine pentamethyl ether (HMMPME), containing 35% by mass of silica and oil) Oil: VivaTec400 (H&R, TDAE oil, Tg: -58°C) Wax: Ozoace 0355 (Nippon Seiro Co., Ltd., paraffin-based) Anti-aging agent: Antigen 6C (Sumitomo Chemical Co., Ltd., N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine) Zinc oxide: Zinc oxide type 2 (manufactured by Mitsui Mining & Smelting Co., Ltd.) Stearic acid: Beads Camellia Stearic Acid (NOF Corp.) Sulfur 1: HK-200-5 (Hosoi Chemical Industry Co., Ltd., powdered sulfur, oil content: 5% by mass) Sulfur 2: Seimisulfur (manufactured by Nippon Kanretsu Kogyo Co., Ltd., insoluble sulfur, oil content: 10% by mass) Sulfur 3: Myucron OT-20 (manufactured by Shikoku Kasei Co., Ltd., insoluble sulfur, oil content: 20% by mass) Sulfur 4: Powdered sulfur manufactured by Tsurumi Chemical Industry Co., Ltd. (oil content: 0% by mass) Vulcanization accelerator 1: Noccela NS (manufactured by Ouchi Shinko Chemical Industry Co., Ltd., N-tert-butyl-2-benzothiazolyl sulfenamide (TBBS)) Vulcanization accelerator 2: Santocure TBSI (N-tert-butylbis(1,3-benzothiazole-2-sulfene)imide) manufactured by Flexis Co., Ltd.

[0203] [ka]

[0204] <Rubber composition for sidewall rubber> According to the compounding recipe shown in Table 1, chemicals other than sulfur and vulcanization accelerator are kneaded for 5 minutes at a discharge temperature of 150°C using a 1.7L Banbury mixer manufactured by Kobe Steel, Ltd. Next, sulfur and vulcanization accelerator are added to the kneaded mixture obtained, and the mixture is kneaded with an open roll for 4 minutes until the temperature reaches 105°C, to obtain an unvulcanized rubber composition.

[0205] [Table 1]

[0206] <Rubber composition for carcass cord topping rubber> According to the compounding recipe shown in Table 2, an unvulcanized rubber composition is obtained by treating in the same manner as in the case of the rubber composition for the sidewall rubber.

[0207] [Table 2]

[0208] <Rubber composition for breaker topping rubber> According to the compounding recipe shown in Table 3, an unvulcanized rubber composition is obtained by treating in the same manner as in the case of the rubber composition for the sidewall rubber.

[0209] [Table 3]

[0210] <Rubber composition for inner liner rubber> According to the compounding recipe shown in Table 4, an unvulcanized rubber composition is obtained by treating in the same manner as in the case of the rubber composition for the sidewall rubber.

[0211] [Table 4]

[0212] <Tires> Using the unvulcanized rubber composition described above, each component of a tire is molded according to the description in Tables 5 and 6, and then laminated with other components to produce an unvulcanized tire. The unvulcanized tire is press-vulcanized at 170°C for 12 minutes to obtain a test tire (total tire weight 8.2 kg).

[0213] <Evaluation> Each test tire was fitted to all wheels of a vehicle (domestic FF vehicle, 2000cc displacement) and filled with air to an internal pressure of 250kPa. The vehicle was then overloaded and driven around a test course on a dry road surface at a speed of 50km / h for 10 laps, and then repeatedly driven over uneven surfaces at a speed of 80km / h to cause the tires to sustain the specified damage. The vehicle was then driven around again at a speed of 50km / h, and the speed was gradually increased, and the speed at which the driver felt something was wrong was measured.

[0214] Next, the result of Comparative Example 1 is set as 100, and the durability is relatively evaluated by indexing it according to the following formula. A larger value indicates better durability. Durability=[(Test tire measurement result) / (Comparative example 1 measurement result)]×100

[0215] [Table 5]

[0216] [Table 6]

[0217] [Table 7]

[0218] [Table 8]

[0219] <Embodiment> The following are preferred embodiments.

[0220] [1] A tire comprising a pair of sidewall rubbers arranged on both sides of a tread portion, a carcass cord topping rubber constituting a carcass arranged on the inner side of the sidewall rubber in the tire width direction, a breaker topping rubber constituting a breaker arranged on the outer side of the carcass in the tire radial direction and on the inner side of the tread portion, and an inner liner rubber arranged on the inner side of the carcass in the tire radial direction, at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains recycled carbon black, the total amount (g) of the recycled carbon black contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is A, At least one rubber component constituting the tire contains oil, and the total amount (g) of oil contained in the tire is B. A tire in which A and B satisfy the following formula (1), and the right side of formula (1) is preferably 5, more preferably 6, even more preferably 10, even more preferably 30, even more preferably 50, and even more preferably 60. (A / B)×100>1 (1) [2] The tire according to the above [1], wherein the right side of formula (1) is 5. [3] The tire according to the above [1], wherein the right side of formula (1) is 6. [4] A tire according to any one of the items [1] to [3] above, wherein A, B and W satisfy the following formula (2), where W (mm) is a total thickness of the sidewall rubber, the carcass cord topping rubber and the inner liner rubber at a position where the tire width is maximum in the tire rotational axis direction, and the right-hand side of formula (2) is preferably 10, more preferably 13, even more preferably 15, even more preferably 30, even more preferably 50, and even more preferably 70. (A / B) / W×1000>5 (2) [5] A tire according to any one of the items [1] to [4] above, wherein when a total thickness of the breaker topping rubber, the carcass cord topping rubber, and the inner liner rubber at a position on the tire equatorial plane is H (mm), A, B, and H satisfy the following formula (3), and preferably the right side of formula (3) is 12, more preferably 14, even more preferably 18, even more preferably 36, even more preferably 50, even more preferably 70, even more preferably 90, and even more preferably 100. (A / B) / H×1000>6 (3) [6] The tire according to any one of the above [1] to [5], wherein at least one rubber containing the recycled carbon black also contains the oil. [7] The tire according to any one of the above [1] to [6], wherein at least one rubber containing the recycled carbon black is a carcass cord topping rubber. [8] The tire according to any one of the items [1] to [7], wherein the rubber containing the recycled carbon black is at least two rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber. [9] The tire according to any one of the items [1] to [7], wherein the rubber containing the recycled carbon black is at least three rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber.

[10] The tire according to any one of the above [1] to [7], wherein the rubber containing the recycled carbon black is all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[11] The tire according to any one of the items [1] to

[10] , wherein the oil-containing rubber is at least two rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber.

[12] The tire according to any one of the items [1] to

[10] , wherein the oil-containing rubber is at least three rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber.

[13] The tire according to any one of the above [1] to

[10] , wherein the oil-containing rubber is all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

[14] A tire according to any one of the items [1] to

[13] above, wherein at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains a filler, and when the total amount (g) of the filler contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is C, A and C satisfy the following formula (4), preferably the right-hand side of formula (4) is 2.0, more preferably 2.2, and even more preferably 8.0. (A / C)×100>1.0 (4)

[15] A tire according to any one of the items [1] to

[14] above, wherein at least one rubber component constituting the tire contains a plasticizer other than oil, and when the total amount (g) of the plasticizers other than oil contained in the tire is D, A and D satisfy the following formula (5), preferably the right-hand side of formula (5) is 30.0, more preferably 50.0, even more preferably 70.0, even more preferably 80.0, and even more preferably 90.0. A / (A+D)×100>16.0 (5) [Explanation of symbols]

[0221] 1 Tire 2 Tread section 3 Sidewall rubber 4 Carcass cord topping rubber 5 Breaker Topping Rubber 6 Inner liner rubber W Total thickness of sidewall rubber, carcass cord topping rubber and inner liner rubber at the widest point of the tire H Total thickness of breaker topping rubber, carcass cord topping rubber and inner liner rubber at the position of the tire equatorial plane EP tire equatorial plane

Claims

1. A tire comprising: a pair of sidewall rubbers arranged on both sides of a tread portion; a carcass cord topping rubber constituting a carcass arranged on the inner side of the sidewall rubber in the tire width direction; a breaker topping rubber constituting a breaker arranged on the outer side of the carcass in the tire radial direction and on the inner side of the tread portion; and an inner liner rubber arranged on the inner side of the carcass in the tire radial direction, at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains recycled carbon black, the total amount (g) of the recycled carbon black contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is A, At least one rubber member constituting the tire contains oil, and the total amount (g) of oil contained in the tire is B. A tire in which A and B satisfy the following formula (1). (A / B)×100>6 (1)

2. 2. The tire according to claim 1, wherein A, B and W satisfy the following formula (2), where W (mm) is the total thickness of the sidewall rubber, the carcass cord topping rubber and the inner liner rubber at the position where the tire width is maximum in the tire rotation axis direction. (A / B) / W×1000>5 (2)

3. 3. The tire according to claim 1, wherein A, B and H satisfy the following formula (3), where H (mm) is the total thickness of the breaker topping rubber, the carcass cord topping rubber and the inner liner rubber at a position on the tire equatorial plane. (A / B) / H×1000>6 (3)

4. 3. The tire of claim 1 or 2, wherein at least one rubber containing said recycled carbon black also contains said oil.

5. 3. The tire of claim 1 or 2, wherein the at least one rubber containing recycled carbon black is a carcass cord topping rubber.

6. 3. The tire according to claim 1, wherein the rubber containing recycled carbon black is at least two rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

7. 3. The tire according to claim 1, wherein the rubber containing recycled carbon black is at least three rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

8. 3. The tire according to claim 1, wherein the rubber containing recycled carbon black is all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

9. 3. The tire according to claim 1, wherein the oil-containing rubber is at least two rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

10. 3. The tire according to claim 1, wherein the oil-containing rubber is at least three rubbers selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

11. 3. The tire according to claim 1, wherein the oil-containing rubber is present in all of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber and the inner liner rubber.

12. 3. The tire according to claim 1 or 2, wherein at least one rubber selected from the group consisting of the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber contains a filler, and when the total amount (g) of the filler contained in the sidewall rubber, the carcass cord topping rubber, the breaker topping rubber, and the inner liner rubber is C, A and C satisfy the following formula (4). (A / C)×100>1.0 (4)

13. 3. The tire according to claim 1 or 2, wherein at least one rubber member constituting the tire contains a plasticizer other than oil, and when a total amount (g) of the plasticizer other than oil contained in the tire is D, A and D satisfy the following formula (5). A / (A+D)×100>16.0 (5)