Electrostatic image developing carrier, electrostatic image developer, process cartridge, image forming apparatus and image forming method

Abstract

To provide a carrier for electrostatic charge image development excellent in charge maintainability of toner.SOLUTION: A carrier for electrostatic charge image development has a magnetic particle and a coating resin layer that covers the magnetic particle and includes inorganic particles. When A is the net intensity of Si when X-ray fluorescence analysis is performed on a carrier A extracted from a developer A obtained by mixing a toner externally added with silica particles and a carrier, B is the net intensity of Si when X-ray fluorescence analysis is performed on a carrier B extracted from a developer B obtained by adding silica particles to the developer A and stirring the developer in a TURBULA stirrer for 20 minutes, and C is the net intensity of Si when X-ray fluorescence analysis is performed on a carrier C extracted from a mixture C obtained by stirring the carrier B extracted from the developer B and toner particles in the TURBULA stirrer for 2 minutes, the formula 1: 0<(C-A) / (B-A)≤0.40 is satisfied.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to an electrostatic image developing carrier, an electrostatic image developer, a process cartridge, an image forming apparatus, and an image forming method. [Background technology]

[0002] Methods for visualizing image information, such as electrophotography, are currently used in various fields. In electrophotography, an electrostatic image is formed as image information on the surface of an image carrier by charging and forming an electrostatic image. Then, a toner image is formed on the surface of the image carrier by a developer containing a toner, and the toner image is transferred to a recording medium, and then fixed to the recording medium. Through these steps, the image information is visualized as an image.

[0003] For example, Patent Document 1 discloses "an electrostatic latent image developing carrier comprising a plurality of carrier particles each having a carrier core and a first coating layer and a second coating layer covering the surface of the carrier core, the first coating layer and the second coating layer having a laminated structure in the order of the first coating layer and the second coating layer from the surface of the carrier core, the first coating layer containing a first thermosetting resin, the second coating layer containing a second thermosetting resin, the surface adsorption force of the first coating layer being 70 nN or more and 100 nN or less, and the pencil hardness of the second coating layer being 2H or more and 6H or less."

[0004] Patent Document 2 discloses "a two-component developer comprising a toner having a volume median particle diameter of 3 to 8 μm formed by adhering inorganic fine particles to colored particles, and a carrier having a mass average particle diameter of 20 to 40 μm formed by adhering inorganic fine particles, characterized in that the area ratio of element (A) constituting the inorganic fine particles adhered to the toner on the carrier surface as measured by an X-ray analyzer is 0.5 to 3.0 area %."

[0005] Patent Document 3 discloses "an electrostatic image developer containing a carrier having a coating resin layer on a carrier core material and a toner, the carrier containing 7 to 35 mass % of silica or carbon black in the coating resin layer, the coating resin having a weight average molecular weight (Mw) of 300,000 to 600,000, and the toner containing external additive fine particles having a number average particle diameter of 70 to 300 nm."

[0006] Patent Document 4 discloses a two-component developer for developing electrostatic latent images, which comprises "a coated carrier having at least a coating film of core particles, and a toner having particles with a volume average particle size of 5 to 10 μm, containing at least a binder resin, a colorant, and a polarity control agent, to which inorganic fine powder is externally added, and which is characterized in that, as shown in the attached drawing, when the horizontal axis is the surface hardness of the coated carrier (pencil hardness in a pencil scratch test defined in JIS K5400) and the vertical axis is the product of the square root of the specific surface area of ​​the toner's external additive in the BET method and the amount added to the toner (wt%), the relationship between these values ​​is within the range surrounded by points A, B, C, and D." [Prior art documents] [Patent documents]

[0007] [Patent Document 1] JP 2018-200372 A [Patent Document 2] JP 2007-219118 A [Patent Document 3] JP 2008-304745 A [Patent Document 4] Japanese Patent Application Publication No. 7-181748 Summary of the Invention [Problem to be solved by the invention]

[0008] The object of the present invention is to provide an electrostatic image developing carrier having magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles, the carrier having excellent toner charge retention properties compared to a carrier in which the relationship between net strengths A, B, and C of Si below satisfies Formula 1: (CA) / (BA)>0.40. [Means for solving the problem]

[0009] Means for solving the above problems include the following aspects. <1> The magnetic material has magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles, When carrier A is extracted from developer A, which is a mixture of toner to which silica particles are externally added and carrier, and the carrier A is subjected to fluorescent X-ray analysis, the net intensity of Si is defined as A, Silica particles are added to the developer A, and developer B is obtained by stirring the developer A for 20 minutes using a turbulent stirrer. The carrier B is extracted from the developer B and analyzed by fluorescent X-ray analysis. The net intensity of Si is defined as B. When carrier B taken out from developer B, toner particles, and mixture C are mixed and stirred for 2 minutes with a Turbula stirrer, carrier C is taken out from mixture C and analyzed by fluorescent X-ray analysis. The net intensity of Si is C. A carrier for developing electrostatic images which satisfies the formula 1:0<(CA) / (BA)≦0.40. <2> the coating resin layer contains silica particles as the inorganic particles, The ratio of Si on the surface of the coating resin layer, as determined by X-ray photoelectron spectroscopy (XPS), is 6 atom % or more and 12 atom % or less. <1> 2. The electrostatic image developing carrier according to claim 1 . <3> When the coating resin layer is cut in a thickness direction and a cut surface is observed, the area ratio of the inorganic particles is 10% or more and 50% or less. <1> or <2> 2. The electrostatic image developing carrier according to claim 1 . <4> The average particle size of the inorganic particles is smaller than the average thickness of the coating resin layer. <1> ~ <3> 2. The carrier for developing an electrostatic image according to claim 1 . <5> The ratio of the average particle diameter of the inorganic particles to the average thickness of the coating resin layer (average particle diameter of the inorganic particles / average thickness of the coating resin layer) is 0.005 or more and 0.15 or less. <4> 2. The electrostatic image developing carrier according to claim 1 . <6> The inorganic particles have an average particle size of 5 nm or more and 90 nm or less. <4> or <5> 2. The electrostatic image developing carrier according to claim 1 . <7> The average thickness of the coating resin layer is 0.6 μm or more and 1.4 μm or less. <4> ~ <6> 2. The carrier for developing an electrostatic image according to claim 1 . <8> The inorganic particles have the same charge polarity as that of the external additive of the toner. <1> ~ <7> 2. The carrier for developing an electrostatic image according to claim 1 . <9> The inorganic particles are inorganic oxide particles. <1> ~ <8> 2. The carrier for developing an electrostatic image according to claim 1 . <10> The content of the inorganic particles is 20% by mass or more and 50% by mass or less with respect to the resin contained in the coating resin layer. <1> ~ <9> 2. The carrier for developing an electrostatic image according to claim 1 . <11> The weight average molecular weight of the resin contained in the coating resin layer is less than 300,000. <1> ~ <10> 2. The carrier for developing an electrostatic image according to claim 1 . <12> The weight average molecular weight of the resin contained in the coating resin layer is less than 250,000. <12> 2. The electrostatic image developing carrier according to claim 1 . <13> The magnetic material has magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles, The charge amount of carrier A taken from developer A, which is a mixture of toner with silica particles added externally and carrier, is compared to the charge amount of carrier B taken from developer B, which is made by adding silica particles to developer A and stirring for 20 minutes with a turbulent stirrer. A carrier for developing electrostatic images, having a ratio (B / A) of 0.80 or more and 1.00 or less. <14> a toner for developing an electrostatic image; <1> ~ <13> 10. The electrostatic image developing carrier according to claim 9, 1. An electrostatic image developer comprising: <15> <14> and a developing unit which develops an electrostatic image formed on a surface of an image carrier into a toner image by using the electrostatic image developer, A process cartridge that is detachably attached to an image forming apparatus. <16> An image carrier; a charging means for charging the surface of the image carrier; an electrostatic image forming means for forming an electrostatic image on the charged surface of the image carrier; <14> a developing means for developing the electrostatic image formed on the surface of the image carrier into a toner image by using the electrostatic image developer; a transfer means for transferring the toner image formed on the surface of the image carrier to a surface of a recording medium; a fixing means for fixing the toner image transferred onto the surface of the recording medium; An image forming apparatus comprising: <17> a charging step of charging the surface of the image carrier; an electrostatic image forming step of forming an electrostatic image on the charged surface of the image carrier; <14> a developing step of developing the electrostatic image formed on the surface of the image carrier into a toner image by using the electrostatic image developer according to claim 1; a transfer step of transferring the toner image formed on the surface of the image carrier onto a surface of a recording medium; a fixing step of fixing the toner image transferred onto the surface of the recording medium; The image forming method according to claim 1, Effect of the Invention

[0010] <1> According to the invention, there is provided an electrostatic image developing carrier having magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles, the carrier having excellent toner charge retention properties compared to a carrier having a relationship between net strengths A, B, and C of Si below that satisfies formula 1: (CA) / (BA)>0.40. <2> According to the present invention, a carrier for developing electrostatic images is provided which has excellent toner charge retention properties compared to cases in which the ratio of Si on the surface of the coating resin layer, as determined by X-ray photoelectron spectroscopy (XPS), is less than 6 atom% or exceeds 12 atom%. <3> According to the present invention, there is provided a carrier for developing electrostatic images which, when a cross section of a coating resin layer cut along the thickness direction is observed, has excellent toner charge retention properties compared to a case in which the area ratio of inorganic particles is less than 10% or exceeds 50%. <4> According to the present invention, there is provided a carrier for developing electrostatic images which is excellent in the charge retention of the toner, as compared with a case in which the average particle size of the inorganic particles is larger than the average thickness of the coating resin layer. <5> According to the present invention, there is provided a carrier for developing electrostatic images, which has excellent toner charge retention properties compared to a carrier having a ratio of the average particle size of the inorganic particles to the average thickness of the coating resin layer (average particle size of the inorganic particles / average thickness of the coating resin layer) of less than 0.005 or more than 0.15. <6> According to the present invention, there is provided a carrier for developing electrostatic images which has excellent charge retention properties for toner compared to inorganic particles having an average particle size of less than 5 nm or more than 90 nm. <7> According to the present invention, there is provided an electrostatic image developing carrier having excellent toner charge retention properties, as compared with a case in which the average thickness of the coating resin layer is less than 0.6 μm or exceeds 1.4 μm. <8> According to the present invention, there is provided a carrier for developing electrostatic images which is excellent in the charge retention of the toner, as compared with a case in which the inorganic particles have a charge polarity different from that of the external additive of the toner. <9> According to the present invention, there is provided a carrier for developing electrostatic images which has excellent charge retention properties for toner compared to when the inorganic particles are metal oxide particles other than silica particles. <10> According to the present invention, there is provided a carrier for developing electrostatic images which has excellent toner charge retention properties compared to when the content of inorganic particles is less than 20% by mass or more than 50% by mass relative to the total mass of the coating resin layer.

[0011] <11> According to the present invention, there is provided a carrier for developing electrostatic images which is excellent in the charge retention of the toner, as compared with a case in which the weight average molecular weight of the resin contained in the coating resin layer is 300,000 or more. <12> According to the present invention, there is provided a carrier for developing electrostatic images which is excellent in the charge retention of toner, as compared with a case in which the weight average molecular weight of the resin contained in the coating resin layer exceeds 250,000.

[0012] <13> According to the invention, there is provided a carrier for developing electrostatic images, which has magnetic particles and a coating resin layer containing inorganic particles that coats the magnetic particles, and which has excellent toner charge retention properties compared to a case in which the ratio (B / A) of the charge amount of carrier A extracted from developer A, which is a mixture of toner to which silica particles have been externally added and a carrier, to the charge amount of carrier B extracted from developer B, which is obtained by adding silica particles to developer A and stirring for 20 minutes with a turbulent stirrer, is less than 0.80.

[0013] <14> , <15> , <16> or <17> According to the invention, there is provided an electrostatic image developer, a process cartridge, an image forming apparatus, or an image forming method, which has excellent toner charge retention properties compared to a case where an electrostatic image developing carrier is used, the carrier having magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles, and in which the relationship between net strengths A, B, and C of Si below satisfies Formula 1: (CA) / (BA)>0.40: [Brief description of the drawings]

[0014] [Figure 1] 1 is a schematic configuration diagram illustrating an example of an image forming apparatus according to an embodiment of the present invention. [Diagram 2] FIG. 2 is a schematic diagram illustrating an example of a process cartridge that is detachably mounted to the image forming apparatus according to the present embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Hereinafter, an embodiment of the present invention will be described as an example. These descriptions and examples are for illustrating the present invention, but are not intended to limit the present invention.

[0016] In this specification, a numerical range indicated using "~" indicates a range that includes the numerical values ​​before and after "~" as the minimum and maximum values, respectively. In the numerical ranges described in this specification, the upper or lower limit value described in one numerical range may be replaced with the upper or lower limit value of another numerical range described in another stepwise manner. In addition, in the numerical ranges described in this disclosure, the upper or lower limit value of the numerical range may be replaced with a value shown in the examples.

[0017] In this specification, the term "process" includes not only an independent process but also a process that cannot be clearly distinguished from other processes, so long as the intended purpose of the process is achieved.

[0018] When an embodiment is described with reference to the drawings in this specification, the configuration of the embodiment is not limited to the configuration shown in the drawings. Furthermore, the size of the members in each drawing is conceptual, and the relative relationship between the sizes of the members is not limited to this.

[0019] In the present specification, each component may contain multiple types of the corresponding substance. When the amount of each component in the composition is mentioned in the present disclosure, if multiple substances corresponding to each component are present in the composition, the total amount of the multiple substances present in the composition is meant unless otherwise specified.

[0020] In the present specification, the particles corresponding to each component may include multiple types. When multiple types of particles corresponding to each component are present in the composition, the particle size of each component means the value for a mixture of the multiple types of particles present in the composition, unless otherwise specified.

[0021] In this specification, "(meth)acrylic" means at least one of acrylic and methacrylic, and "(meth)acrylate" means at least one of acrylate and methacrylate.

[0022] In this specification, "toner for developing electrostatic images" is also referred to simply as "toner", "carrier for developing electrostatic images" is also referred to simply as "carrier", and "electrostatic image developer" is also referred to simply as "developer".

[0023] <Electrostatic image developing carrier> -First embodiment- The carrier according to the first embodiment has magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles. The carrier according to the first embodiment is When carrier A extracted from developer A, which is a mixture of toner to which silica particles have been externally added and carrier, is subjected to fluorescent X-ray analysis, the net Si intensity is A; when carrier B extracted from developer B, which is obtained by adding silica particles to developer A and stirring for 20 minutes in a turbulent stirrer, is subjected to fluorescent X-ray analysis, the net Si intensity is B; and when carrier C extracted from a mixture C, which is obtained by stirring carrier B extracted from developer B, toner particles, and stirring for 2 minutes in a turbulent stirrer, is subjected to fluorescent X-ray analysis, the net Si intensity is C. The formula 1:0<(CA) / (BA)≦0.40 is satisfied.

[0024] The carrier according to the first embodiment has an excellent charge retention property for the toner due to the above-mentioned structure. The reason for this is presumed to be as follows.

[0025] The toner and the carrier are mixed together in the developing means and are stirred, whereby the toner is charged. However, when the toner and carrier are continuously stirred, the external additives (especially silica particles) of the toner adhere to the carrier. If the amount of the external additives adhering to the carrier increases, the charging ability of the carrier decreases over time, and the charging property of the toner also decreases.

[0026] Therefore, the carrier according to the first embodiment is designed to satisfy the formula 1:0<(CA) / (BA)≦0.40. The net intensity A of Si corresponds to the amount of silica particles externally added to the toner that adheres to the carrier after the toner and carrier are mixed. The net strength B of Si corresponds to the amount of silica particles externally added to the toner that adheres to the carrier after the toner and carrier are subjected to a mechanical load caused by stirring over time. The net strength C of Si corresponds to the amount of silica particles adhering to the carrier after the silica particles migrate from the carrier to which the silica particles are attached to the toner particles to which the silica particles are not added, when the toner and carrier are subjected to a mechanical load caused by stirring over time.

[0027] And, satisfying the formula 1:0<(CA) / (BA)≦0.40 means that the silica particles attached to the carrier are easily detached from the carrier when the toner and carrier are subjected to mechanical load by stirring over time, which means that the adhesive force of the carrier surface (i.e., the surface of the coating resin layer) to the silica particles is weak.

[0028] Therefore, the carrier that satisfies the formula 1:0<(CA) / (BA)≦0.40 has a weak adhesive force to the silica particles, so even if the silica particles are once attached to the carrier, they are easily detached, and the decrease in the charging ability is suppressed. Therefore, the charge retention of the toner is improved.

[0029] From the above, it is presumed that the carrier according to the first embodiment has excellent charge retention properties for the toner.

[0030] -Second embodiment- The carrier according to the second embodiment has magnetic particles and a coating resin layer that coats the magnetic particles and contains inorganic particles. In the second embodiment, the ratio (B / A) of the charge amount of carrier A extracted from developer A, which is a mixture of toner to which silica particles have been externally added and a carrier, to the charge amount of carrier B extracted from developer B, which is obtained by adding silica particles to developer A and stirring for 20 minutes with a turbulent stirring device, is 0.80 or more and 1.00 or less.

[0031] The carrier according to the second embodiment also has excellent charge retention properties for the toner due to the above-mentioned configuration. This is because the coating resin layer containing inorganic fine particles becomes hard due to the filler effect, which is presumed to suppress adhesion of silica particles detached from the toner.

[0032] A carrier corresponding to both the carrier according to the first and second embodiments (hereinafter also referred to as "the carrier according to the present embodiment") will be described in detail below. However, an example of the carrier of the present invention may be a carrier corresponding to either one of the carrier according to the first and second embodiments.

[0033] The carrier according to this embodiment will be described in detail below.

[0034] (Formula 1: 0<(CA) / (BA)≦0.40) In the carrier according to the present embodiment, the "(CA) / (BA)" value is more than 0 and not more than 0.40, but from the viewpoint of improving the charge retention of the toner, it is preferably more than 0 and not more than 0.20, and more preferably more than 0 and not more than 0.10.

[0035] Here, the net intensities A to C of each Si are values ​​measured as follows.

[0036] The measurement of the net intensity A of Si will be explained. First, the toner to which the silica particles are externally added and the target carrier are placed in a V blender with an L capacity at a mass ratio of 8:92, and stirred at a stirring speed of 40 rpm for 20 minutes to obtain developer A. The "toner having silica particles externally added" to be mixed with the carrier is the "toner (T)" used in "preparation of developer" in the examples described later. Next, the mixture of toner and carrier is taken out of developer A and placed on a mesh with an opening of 0.016 mm manufactured by Asada Mesh Co., Ltd. Next, an air pressure of 0.5 MPa / cm is applied from above to the mixture placed on the mesh using an air gun. 2The air is blown onto the mixture for 90 seconds, with the air nozzle of the air gun at a distance of 10 mm or more from the mixture. This separates the toner from the carrier. Next, the separated carrier A is subjected to fluorescent X-ray analysis to measure the net intensity A of Si.

[0037] The measurement of the net strength B of Si will be explained. First, silica particles are added to developer A and stirred for 20 minutes with a Turbula stirring device, thereby obtaining developer B. Here, the silica particles added to developer A are "X24-9600A Shin-Etsu Chemical Co., Ltd." The amount of silica particles added to developer A is 0.0024 g per 15 g of the carrier of developer A. Next, the mixture of toner and carrier is taken out from developer B, and the toner is separated from the carrier. The separation method is the same as that used for measuring the Net intensity A of Si. Next, the separated carrier B is subjected to X-ray fluorescence analysis to measure the net intensity B of Si.

[0038] The measurement of the net strength C of Si will be explained. First, the mixture of toner and carrier is taken out from developer B, and the toner is separated from the carrier. The separation method is the same as that used to measure the Net intensity A of Si. Next, the separated carrier B and toner particles are placed in a 60 mL capacity Turbula stirring device in a mass ratio of 91.5:8.5 and stirred at a stirring speed of 101 rpm for 2 minutes to obtain a mixture C. The "toner particles" to be mixed with carrier B are the "toner (TA) (i.e., toner particles (TA) to which no external additives are added)" used in "Preparation of developer" in the examples described below. Next, the mixture of toner and carrier is taken out from the mixture C, and the toner particles are separated from the carrier. The separation method is the same as that used for measuring the Net intensity A of Si. Next, the separated carrier C is subjected to X-ray fluorescence analysis to measure the net intensity C of Si.

[0039] The fluorescent X-ray analysis for determining the net intensities A to C of each Si will be described. Approximately 200 mg of each carrier to be analyzed is compressed with a load of 10 t for 60 seconds using a compression molding machine to produce a disk with a diameter of 10 mm and a thickness of 2 mm. This disk is used as a sample and a total element analysis is performed under the following measurement conditions using a scanning X-ray fluorescence analyzer (Rigaku ZSX Primus II), and the net intensity (unit: kilo counts per second, kcps) of each Si to be measured is obtained. Tube voltage: 40kV ·Tube current: 70mA ·Anti-cathode: Rhodium Measurement time: 15 minutes ·Analysis diameter: 10mm in diameter

[0040] In the carrier according to this embodiment, in order to satisfy the formula 1:0<(CA) / (BA)≦0.40, it is preferable that the carrier has a suitable aspect described below.

[0041] (Career Structure) The carrier according to the present embodiment has magnetic particles and a coating resin layer that coats the magnetic particles.

[0042] [Magnetic particles] The magnetic particles are not particularly limited, and known magnetic particles used as the core material of carriers are applied.Specific examples of the magnetic particles include magnetic metal particles such as iron, nickel, and cobalt; magnetic oxide particles such as ferrite and magnetite; resin-impregnated magnetic particles in which porous magnetic powder is impregnated with resin; magnetic powder-dispersed resin particles in which magnetic powder is dispersed and mixed in resin; and the like.In this embodiment, the magnetic particles are preferably ferrite particles.

[0043] The volume average particle size of the magnetic particles is preferably from 15 μm to 100 μm, more preferably from 20 μm to 80 μm, and even more preferably from 30 μm to 60 μm. The volume average particle size of the magnetic particles is measured by the following method. The particle size distribution is measured using a laser diffraction / scattering particle size distribution measuring device (LS Particle Size Analyzer (manufactured by Beckman Coulter, Inc.). ISOTON-II (manufactured by Beckman Coulter, Inc.) is used as the electrolyte. The number of particles measured is 50,000. The measured particle size distribution is then plotted as a cumulative distribution for the volume of each divided particle size range (channel), from the smallest diameter side, and the particle size at which the cumulative 50% (D50v) is reached is defined as the "volume average particle size."

[0044] The arithmetic mean height Ra (JIS B0601:2001) of the roughness curve of the magnetic particles is preferably 0.1 μm or more and 1 μm or less, and more preferably 0.2 μm or more and 0.8 μm or less. The arithmetic mean height Ra of the roughness curve of a magnetic particle is determined by observing the magnetic particle at an appropriate magnification (for example, 1000x magnification) using a surface shape measuring device (for example, Keyence Corporation's "Ultra-Deep Color 3D Shape Measuring Microscope VK-9700"), obtaining a roughness curve at a cutoff value of 0.08 mm, and extracting a reference length of 10 μm from the roughness curve in the direction of the average line. The Ra of 100 magnetic particles is calculated as the arithmetic mean.

[0045] The magnetic force of the magnetic particles is preferably 50 emu / g or more, more preferably 60 emu / g or more, in terms of saturation magnetization in a magnetic field of 3000 oersteds. The saturation magnetization is measured using a vibrating sample magnetic measuring device VSMP10-15 (manufactured by Toei Kogyo Co., Ltd.). The measurement sample is packed in a cell with an inner diameter of 7 mm and a height of 5 mm and set in the device. The measurement is performed by applying a magnetic field and sweeping up to a maximum of 3000 oersteds. The applied magnetic field is then reduced, and a hysteresis curve is prepared on a recording paper. The saturation magnetization, residual magnetization, and retentivity are determined from the curve data.

[0046] The volume resistivity of magnetic particles is 1×10 5 Ω cm or more 1×10 9 Ω cm or less is preferable, and 1×10 7 Ω cm or more 1×10 9 Ω·cm or less is more preferable. The volume resistivity (Ω·cm) of magnetic particles is measured as follows: 2 The object to be measured is placed flat on the surface of the circular jig on which the electrode plate is arranged, with a thickness of 1 mm to 3 mm, to form a layer. 2 The layer is sandwiched between two electrode plates. In order to eliminate any gaps between the objects being measured, a 4 kg load is placed on the electrode plates placed on the layer, and then the layer thickness (cm) is measured. Both electrodes above and below the layer are connected to an electrometer and a high-voltage power supply generator. A high voltage is applied to both electrodes so that the electric field is 103.8 V / cm, and the current value (A) that flows at this time is read. The measurement environment is a temperature of 20°C and a relative humidity of 50%. The formula for calculating the volumetric electrical resistivity (Ω·cm) of the object being measured is as shown below. R = E × 20 / (II 0 ) / L In the above formula, R is the volume resistivity of the object to be measured (Ω cm), E is the applied voltage (V), I is the current value (A), and I 0 is the current value (A) at an applied voltage of 0 V, and L is the layer thickness (cm). The coefficient 20 is the area of ​​the electrode plate (cm 2 )

[0047] [Coating resin layer] The coating resin layer contains a resin and inorganic particles.

[0048] -resin- Examples of resins contained in the coating resin layer include styrene-acrylic resins; polyolefin resins such as polyethylene and polypropylene; polyvinyl or polyvinylidene resins such as polystyrene, acrylic resin, polyacrylonitrile, polyvinyl acetate, polyvinyl alcohol, polyvinyl butyral, polyvinyl chloride, polyvinyl carbazole, polyvinyl ether, and polyvinyl ketone; vinyl chloride-vinyl acetate copolymers; straight silicone resins or modified products thereof consisting of organosiloxane bonds; fluororesins such as polytetrafluoroethylene, polyvinyl fluoride, polyvinylidene fluoride, and polychlorotrifluoroethylene; polyesters; polyurethanes; polycarbonates; amino resins such as urea-formaldehyde resins; and epoxy resins.

[0049] The coating resin layer preferably contains an acrylic resin having an alicyclic structure. The polymerization component of the acrylic resin having an alicyclic structure is preferably a lower alkyl ester of (meth)acrylic acid (for example, a (meth)acrylic acid alkyl ester having an alkyl group with 1 to 9 carbon atoms), and specific examples thereof include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, hexyl (meth)acrylate, cyclohexyl (meth)acrylate, and 2-ethylhexyl (meth)acrylate. These monomers may be used alone or in combination of two or more. The acrylic resin having an alicyclic structure preferably contains cyclohexyl (meth)acrylate as a polymerization component. The content of the monomer unit derived from cyclohexyl (meth)acrylate contained in the acrylic resin having an alicyclic structure is preferably 75% by mass or more and 100% by mass or less, more preferably 85% by mass or more and 100% by mass or less, and even more preferably 95% by mass or more and 100% by mass or less, based on the total mass of the acrylic resin having an alicyclic structure.

[0050] The weight average molecular weight of the resin contained in the coating resin layer is preferably less than 300,000, more preferably less than 250,000, and even more preferably less than 200,000. When the weight-average molecular weight of the resin contained in the coating resin layer is reduced to the above range, the resin has a higher adhesion to the magnetic particles than when the weight-average molecular weight of the resin is 300,000 or more, and the coating resin layer is less likely to peel off during repeated image formation, which further improves the charge retention of the toner. However, the lower limit of the weight average molecular weight of the resin contained in the coating resin layer is preferably 50,000 or more, and more preferably 100,000 or more, from the viewpoint of adhesion to the magnetic particles.

[0051] Here, the weight average molecular weight is measured by gel permeation chromatography (GPC). The molecular weight measurement by GPC was performed using a Tosoh GPC HLC-8120 as the measuring device, a Tosoh TSKgel SuperHM-M (15 cm) column, and THF solvent. The weight average molecular weight was calculated from the measurement results using a molecular weight calibration curve prepared with monodisperse polystyrene standard samples.

[0052] -Inorganic particles- Examples of inorganic particles contained in the coating resin layer include metal oxide particles such as silica, titanium oxide, zinc oxide, and tin oxide, metal compound particles such as barium sulfate, aluminum borate, and potassium titanate, and metal particles such as gold, silver, and copper. In this embodiment, carbon black is not considered to be an inorganic particle. Among these, from the viewpoint of improving the charge retention of the toner, the inorganic particles are preferably inorganic oxide particles, and more preferably silica particles.

[0053] In particular, it is preferable that the inorganic particles have the same charge polarity as the external additive of the toner (particularly, silica particles). When the inorganic particles have the same charge polarity as the external additive of the toner, the electrostatic repulsion of the inorganic particles exposed from the coating resin layer works, and the adhesion of the carrier to the external additive is reduced. As a result, the charge retention of the toner is further improved. Specifically, it is preferable that the inorganic particles have the same charge polarity (negative polarity) as that of the silica particles used as the external additive of the toner.

[0054] Here, the charge polarity of particles is measured as follows. The charge polarity of particles is measured by the blow-off method. Because the particle diameter is very small compared to the carrier, it is necessary to lower the particle mixing ratio in order to reduce the proportion of particles that cannot come into contact with the carrier. For example, the carrier is mixed at a ratio of 9.9 g to 0.1 g of particles, and the polarity can be determined by measuring using the blow-off method.

[0055] The surface of the inorganic particles may be subjected to hydrophobic treatment. Examples of the hydrophobic treatment agent include known organosilicon compounds having an alkyl group (e.g., methyl group, ethyl group, propyl group, butyl group, etc.), and specific examples include alkoxysilane compounds, siloxane compounds, and silazane compounds. Among these, the hydrophobic treatment agent is preferably a silazane compound, and hexamethyldisilazane is preferable. The hydrophobic treatment agent may be used alone or in combination of two or more kinds.

[0056] Examples of methods for hydrophobizing inorganic particles with a hydrophobizing agent include a method in which supercritical carbon dioxide is used to dissolve the hydrophobizing agent in supercritical carbon dioxide and adhere the hydrophobizing agent to the surfaces of the inorganic particles; a method in which a solution containing a hydrophobizing agent and a solvent that dissolves the hydrophobizing agent is applied (e.g., sprayed or coated) to the surfaces of inorganic particles in the atmosphere to adhere the hydrophobizing agent to the surfaces of the inorganic particles; and a method in which a solution containing a hydrophobizing agent and a solvent that dissolves the hydrophobizing agent is added to an inorganic particle dispersion in the atmosphere, the solution is maintained, and then the mixed solution of the inorganic particle dispersion and the solution is dried.

[0057] The content of inorganic particles in the coating resin layer is preferably 20% by mass or more and 50% by mass or less, more preferably 25% by mass or more and 45% by mass or less, even more preferably 25% by mass or more and 40% by mass or less, and particularly preferably 30% by mass or more and 40% by mass or less, relative to the total mass of the coating resin layer. When the inorganic particles are contained in the coating resin layer in a large amount within the above range, the inorganic particles impart fine irregularities to the surface of the coating resin layer, reducing the adhesive force of the carrier to the external additives, thereby further improving the charge retention of the toner.

[0058] The resin coating layer may contain conductive particles for the purpose of controlling electrostatic charge and resistance. Examples of the conductive particles include carbon black and the above-mentioned inorganic particles having electrical conductivity.

[0059] -Resin coating layer formation method- Methods for forming a resin coating layer on the surface of magnetic particles include, for example, a wet method and a dry method. The wet method is a method that uses a solvent to dissolve or disperse the resin that constitutes the resin coating layer. On the other hand, the dry method is a method that does not use the above solvent.

[0060] Examples of wet manufacturing methods include a dipping method in which magnetic particles are dipped in a resin liquid for forming a resin coating layer to coat them, a spraying method in which the resin liquid for forming a resin coating layer is sprayed onto the surfaces of the magnetic particles, a fluidized bed method in which the resin liquid for forming a resin coating layer is sprayed onto the magnetic particles in a fluidized bed, and a kneader coater method in which the magnetic particles and the resin liquid for forming a resin coating layer are mixed in a kneader coater and the solvent is removed. These manufacturing methods may be repeated or combined. The resin liquid for forming the resin coating layer used in the wet manufacturing method is prepared by dissolving or dispersing the resin, inorganic particles, and other components in a solvent. The solvent is not particularly limited, and examples of the solvent that can be used include aromatic hydrocarbons such as toluene and xylene, ketones such as acetone and methyl ethyl ketone, and ethers such as tetrahydrofuran and dioxane.

[0061] An example of a dry manufacturing method is a method in which a mixture of magnetic particles and a resin for forming a resin coating layer is heated in a dry state to form a resin coating layer. Specifically, for example, the magnetic particles and the resin for forming the resin coating layer are mixed in a gas phase and heated and melted to form a resin coating layer.

[0062] (Si ratio on the surface of the coating resin layer) When the coating resin layer contains silica particles as inorganic particles, the ratio of Si in the surface of the coating resin layer, determined by X-ray photoelectron spectroscopy (XPS), is preferably 6 atom % or more and 12 atom % or less. When the ratio of Si is within the above range, the silica particles are appropriately exposed on the surface of the coating resin layer, fine unevenness is imparted, and the contact area with the external additive is reduced. This reduces the adhesion of the carrier to the external additive, and suppresses the decrease in the charging ability of the carrier. As a result, the charging retention of the toner is further improved. From the viewpoint of improving the charge retention of the toner, the ratio of Si on the surface of the coating resin layer is more preferably 6 atom % or more and 10 atom % or less, and further preferably 6.5 atom % or more and 9 atom % or less. The ratio of Si on the surface of the coating resin layer can be controlled by the amount of silica particles contained in the coating resin layer. The greater the amount of silica particles relative to the resin, the higher the ratio of Si on the surface of the coating resin layer.

[0063] Here, the ratio of Si on the surface of the coating resin layer is measured as follows. The carrier is used as a sample and analyzed by X-ray Photoelectron Spectroscopy (XPS) under the following conditions to measure the peak intensity of all elements. The ratio of Si (atomic %) is then calculated from the peak intensities of all elements obtained. XPS equipment: ULVAC-PHI, VersaProbe II Etching gun: Argon gun Acceleration voltage: 5kV Emission current: 20mA Sputtering area: 2mm x 2mm Sputtering rate: 3nm / min (SiO 2 Conversion)

[0064] (area ratio of inorganic particles) When the coating resin layer is cut in the thickness direction and a cut surface is observed, the area ratio of the inorganic particles is preferably 10% or more and 50% or less. When the area ratio of the inorganic particles is within the above range, the inorganic particles provide the surface of the coating resin layer with fine irregularities to reduce the adhesive force of the carrier to the external additives, thereby further improving the charge retention of the toner. From the viewpoint of improving the charge retention of the toner, the area ratio of the inorganic particles is more preferably 10% or more and 40% or less, and further preferably 15% or more and 35% or less. The area ratio of the inorganic particles can be controlled by the amount of silica particles contained in the coating resin layer, and the greater the amount of inorganic particles relative to the resin, the higher the area ratio of the inorganic particles.

[0065] Here, the carrier is embedded in epoxy resin and cut with a microtome to prepare a sample with the carrier cross section as the observation surface. An SEM image (magnification 20,000 times) of the cross section of the coating resin layer of the carrier cross section is taken with a scanning electron microscope (SEM) and is imported into an image processing and analysis device for image analysis. In a SEM image of a carrier cross section, the area of ​​the inorganic particles is measured in the cross section of the coating resin layer, and the area ratio of the inorganic particles is calculated according to the formula: area ratio of inorganic particles=total area of ​​inorganic particles / area of ​​coating resin layer×100. The inorganic particles in the cross section of the coating resin layer are identified by SEM-EDX (energy dispersive X-ray spectroscopy).

[0066] (Average particle size of inorganic particles / average thickness of coating resin layer) In the carrier according to the present embodiment, the average particle size of the inorganic particles is preferably smaller than the average thickness of the coating resin layer. Specifically, the ratio of the average particle size of the inorganic particles to the average thickness of the coating resin layer (average particle size of the inorganic particles / average thickness of the coating resin layer) is preferably 0.005 to 0.15, more preferably 0.007 to 0.05. When the average particle size of the inorganic particles is smaller than the average thickness of the coating resin layer, the inorganic particles are dispersed in the coating resin layer, and are exposed from the coating resin layer, the inorganic particles impart fine irregularities to the surface of the coating resin layer, reducing the adhesive force of the carrier to the external additive, thereby further improving the charge retention of the toner.

[0067] From the viewpoint of improving the charge retention of the toner, the average particle size of the inorganic particles is preferably 5 nm to 90 nm, more preferably 5 nm to 70 nm, even more preferably 5 nm to 50 nm, and even more preferably 8 nm to 50 nm. The average particle size of the inorganic particles contained in the coating resin layer can be controlled by the size of the inorganic particles used to form the coating resin layer.

[0068] From the viewpoint of improving the charge retention of the toner, the average thickness of the coating resin layer is preferably from 0.6 μm to 1.4 μm, more preferably from 0.8 μm to 1.2 μm, and even more preferably from 0.8 μm to 1.1 μm. The average thickness of the resin coating layer can be controlled by the amount of resin used to form the resin coating layer, and the greater the amount of resin relative to the amount of magnetic particles, the greater the average thickness of the resin coating layer.

[0069] Here, the average particle size of the inorganic particles contained in the coating resin layer and the average thickness of the coating resin layer are measured by the following method. The carrier is embedded in epoxy resin and cut with a microtome to prepare a sample with the carrier cross section as the observation surface. An SEM image (magnification 20,000) of the cross section of the coating resin layer of the carrier cross section is taken with a scanning electron microscope (SEM) and imported into an image processing analyzer for image analysis. 100 inorganic particles (primary particles) in the coating resin layer are randomly selected, and the circle equivalent diameter (nm) of each is calculated and the arithmetic average is taken, which is the average particle size (nm) of the inorganic particles. In addition, 10 locations per carrier particle are randomly selected to measure the thickness (μm) of the coating resin layer, and further measurements are taken for 100 carriers, and all are arithmetic averaged, which is the average thickness (μm) of the coating resin layer.

[0070] (Carrier characteristics) -Charge ratio of initial carrier to that after deterioration- The ratio (B / A) of the charge amount of carrier A extracted from developer A, which is a mixture of toner to which silica particles have been externally added and a carrier, to the charge amount of carrier B extracted from developer B, which is obtained by adding silica particles to developer A and stirring for 20 minutes with a turbulent stirrer, is preferably 0.8 or more and 1.0 or less, more preferably 0.9 or more and 1.0 or less, and even more preferably 0.95 or more and 1.0 or less. When the charge amount ratio of the carrier at the initial stage to that after deterioration is within the above range, the charge retention of the toner is further improved.

[0071] Carrier A and carrier B are obtained in the same manner as the measurement of the net intensity of Si.

[0072] The charge amount of Carrier A and Carrier B is measured using a blow-off powder charge amount measuring device (TB-200) manufactured by Toshiba Chemical Corporation.

[0073] - Exposed area ratio of magnetic particles - The exposed area ratio of the magnetic particles on the carrier surface according to this embodiment is more preferably 5% to 30%, more preferably 7% to 25%, and even more preferably 10% to 25%. The exposed area ratio of the magnetic particles on the carrier can be controlled by the amount of resin used to form the coating resin layer, and the greater the amount of resin relative to the amount of magnetic particles, the smaller the exposed area ratio.

[0074] The exposed area ratio of the magnetic particles on the carrier surface is a value determined by the following method. A target carrier and magnetic particles from which the resin coating layer has been removed from the target carrier are prepared. Methods for removing the resin coating layer from the carrier include, for example, a method for removing the resin coating layer by dissolving the resin component with an organic solvent, and a method for removing the resin coating layer by heating at about 800°C to eliminate the resin component. The carrier and magnetic particles are each used as measurement samples, and the Fe concentration (atomic%) on the sample surface is quantified by XPS, and the exposed area ratio (%) of the magnetic particles is calculated by (Fe concentration of the carrier)÷(Fe concentration of the magnetic particles)×100.

[0075] The volume average particle size of the carrier according to the present embodiment is preferably from 10 μm to 120 μm, more preferably from 20 μm to 100 μm, and further preferably from 30 μm to 80 μm. The volume average particle size of the carrier means a particle size D50v that is 50% cumulative from the small diameter side in the volume-based particle size distribution, and is measured in the same manner as the volume average particle size of the magnetic particles.

[0076] <Electrostatic image developer> The developer according to the present embodiment is a two-component developer containing the carrier according to the present embodiment and a toner. The toner contains toner particles and, if necessary, an external additive.

[0077] The mixture ratio (mass ratio) of the carrier to the toner in the developer is preferably from 100:1 to 100:30, more preferably from 100:3 to 100:20.

[0078] [Toner particles] The toner particles are configured to contain, for example, a binder resin, and, if necessary, a colorant, a release agent, and other additives.

[0079] -Binding resin- Examples of the binder resin include vinyl resins made of homopolymers of monomers such as styrenes (e.g., styrene, parachlorostyrene, α-methylstyrene, etc.), (meth)acrylic acid esters (e.g., methyl acrylate, ethyl acrylate, n-propyl acrylate, n-butyl acrylate, lauryl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, lauryl methacrylate, 2-ethylhexyl methacrylate, etc.), ethylenically unsaturated nitriles (e.g., acrylonitrile, methacrylonitrile, etc.), vinyl ethers (e.g., vinyl methyl ether, vinyl isobutyl ether, etc.), vinyl ketones (e.g., vinyl methyl ketone, vinyl ethyl ketone, vinyl isopropenyl ketone, etc.), and olefins (e.g., ethylene, propylene, butadiene, etc.), or copolymers of two or more of these monomers. Examples of the binder resin include non-vinyl resins such as epoxy resins, polyester resins, polyurethane resins, polyamide resins, cellulose resins, polyether resins, and modified rosin, mixtures of these with the vinyl resins, and graft polymers obtained by polymerizing vinyl monomers in the coexistence of these. These binder resins may be used alone or in combination of two or more kinds.

[0080] The binder resin is preferably a polyester resin. The polyester resin may be, for example, a known amorphous polyester resin. The polyester resin may be used in combination with a crystalline polyester resin together with the amorphous polyester resin. However, the content of the crystalline polyester resin is preferably in the range of 2% by mass to 40% by mass (preferably 2% by mass to 20% by mass) based on the total binder resin.

[0081] The "crystallinity" of a resin refers to the presence of a clear endothermic peak rather than a stepwise change in the amount of endothermic heat in differential scanning calorimetry (DSC); specifically, it refers to the half-width of the endothermic peak being within 10°C when measured at a heating rate of 10 (°C / min). On the other hand, the term "amorphous" for a resin refers to a half-width exceeding 10° C., a stepwise change in endothermic heat quantity, or no clear endothermic peak being observed.

[0082] Amorphous polyester resin The amorphous polyester resin may be, for example, a condensation polymer of a polyvalent carboxylic acid and a polyhydric alcohol. As the amorphous polyester resin, a commercially available product or a synthesized product may be used.

[0083] Examples of polyvalent carboxylic acids include aliphatic dicarboxylic acids (e.g., oxalic acid, malonic acid, maleic acid, fumaric acid, citraconic acid, itaconic acid, glutaconic acid, succinic acid, alkenylsuccinic acid, adipic acid, sebacic acid, etc.), alicyclic dicarboxylic acids (e.g., cyclohexanedicarboxylic acid, etc.), aromatic dicarboxylic acids (e.g., terephthalic acid, isophthalic acid, phthalic acid, naphthalenedicarboxylic acid, etc.), anhydrides thereof, and lower alkyl esters thereof (e.g., having 1 to 5 carbon atoms). Among these, aromatic dicarboxylic acids are preferable as polyvalent carboxylic acids. The polyvalent carboxylic acid may be a trivalent or higher carboxylic acid having a crosslinked or branched structure in combination with a dicarboxylic acid. Examples of the trivalent or higher carboxylic acid include trimellitic acid, pyromellitic acid, anhydrides thereof, and lower (e.g., carbon number 1 to 5) alkyl esters thereof. The polyvalent carboxylic acids may be used alone or in combination of two or more kinds.

[0084] Examples of polyhydric alcohols include aliphatic diols (e.g., ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, butanediol, hexanediol, neopentyl glycol, etc.), alicyclic diols (e.g., cyclohexanediol, cyclohexanedimethanol, hydrogenated bisphenol A, etc.), and aromatic diols (e.g., ethylene oxide adducts of bisphenol A, propylene oxide adducts of bisphenol A, etc.). Among these, examples of polyhydric alcohols include aromatic diols and alicyclic diols, and more preferably aromatic diols. As the polyhydric alcohol, a polyhydric alcohol having a crosslinked or branched structure of three or more may be used in combination with the diol. Examples of the polyhydric alcohol having a trihydric or higher valence include glycerin, trimethylolpropane, and pentaerythritol. The polyhydric alcohols may be used alone or in combination of two or more kinds.

[0085] The glass transition temperature (Tg) of the amorphous polyester resin is preferably 50°C or higher and 80°C or lower, and more preferably 50°C or higher and 65°C or lower. The glass transition temperature is determined from a DSC curve obtained by differential scanning calorimetry (DSC), and more specifically, it is determined from the "extrapolated glass transition onset temperature" described in the method for determining glass transition temperature in JIS K7121:1987 "Method for measuring transition temperature of plastics."

[0086] The weight average molecular weight (Mw) of the amorphous polyester resin is preferably 5,000 or more and 1,000,000 or less, and more preferably 7,000 or more and 500,000 or less. The number average molecular weight (Mn) of the amorphous polyester resin is preferably 2,000 or more and 100,000 or less. The molecular weight distribution Mw / Mn of the amorphous polyester resin is preferably 1.5 or more and 100 or less, and more preferably 2 or more and 60 or less. The weight average molecular weight and number average molecular weight are measured by gel permeation chromatography (GPC). The molecular weight measurement by GPC is performed using a Tosoh GPC HLC-8120GPC as the measuring device, a Tosoh TSKgel SuperHM-M (15 cm) column, and THF solvent. The weight average molecular weight and number average molecular weight are calculated from the measurement results using a molecular weight calibration curve created with a monodisperse polystyrene standard sample.

[0087] The amorphous polyester resin can be obtained by a known production method, for example, by carrying out the reaction while removing water and alcohol generated during condensation by setting the polymerization temperature to 180° C. or higher and 230° C. or lower, and reducing the pressure in the reaction system as necessary. If the raw material monomer is not soluble or compatible at the reaction temperature, a high boiling point solvent may be added as a solubilizing agent to dissolve it. In this case, the polycondensation reaction is carried out while distilling off the solubilizing agent. If a monomer with poor compatibility is present in the copolymerization reaction, it is recommended that the monomer with poor compatibility is condensed in advance with the acid or alcohol to be polycondensed, and then polycondensed with the main component.

[0088] Crystalline polyester resin The crystalline polyester resin may be, for example, a polycondensate of a polyvalent carboxylic acid and a polyhydric alcohol. As the crystalline polyester resin, a commercially available product or a synthesized product may be used. Here, the crystalline polyester resin is preferably a polycondensate using a straight-chain aliphatic polymerizable monomer rather than a polymerizable monomer having an aromatic ring, since it easily forms a crystalline structure.

[0089] Examples of polyvalent carboxylic acids include aliphatic dicarboxylic acids (e.g., oxalic acid, succinic acid, glutaric acid, adipic acid, suberic acid, azelaic acid, sebacic acid, 1,9-nonanedicarboxylic acid, 1,10-decanedicarboxylic acid, 1,12-dodecanedicarboxylic acid, 1,14-tetradecanedicarboxylic acid, 1,18-octadecanedicarboxylic acid, etc.), aromatic dicarboxylic acids (e.g., dibasic acids such as phthalic acid, isophthalic acid, terephthalic acid, naphthalene-2,6-dicarboxylic acid, etc.), anhydrides thereof, and lower alkyl esters thereof (e.g., having 1 to 5 carbon atoms). The polyvalent carboxylic acid may be a trivalent or higher carboxylic acid having a crosslinked or branched structure in combination with a dicarboxylic acid. Examples of the trivalent carboxylic acid include aromatic carboxylic acids (e.g., 1,2,3-benzenetricarboxylic acid, 1,2,4-benzenetricarboxylic acid, 1,2,4-naphthalenetricarboxylic acid, etc.), their anhydrides, and their lower alkyl esters (e.g., carbon number 1 to 5). As the polyvalent carboxylic acid, a dicarboxylic acid having a sulfonic acid group and a dicarboxylic acid having an ethylenic double bond may be used in combination with these dicarboxylic acids. The polyvalent carboxylic acids may be used alone or in combination of two or more kinds.

[0090] Examples of polyhydric alcohols include aliphatic diols (for example, straight-chain aliphatic diols having 7 to 20 carbon atoms in the main chain). Examples of aliphatic diols include ethylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, 1,10-decanediol, 1,11-undecanediol, 1,12-dodecanediol, 1,13-tridecanediol, 1,14-tetradecanediol, 1,18-octadecanediol, and 1,14-eicosanedecanediol. Among these, 1,8-octanediol, 1,9-nonanediol, and 1,10-decanediol are preferred as aliphatic diols. The polyhydric alcohol may be a trihydric or higher alcohol having a crosslinked or branched structure in combination with the diol. Examples of the trihydric or higher alcohol include glycerin, trimethylolethane, trimethylolpropane, and pentaerythritol. The polyhydric alcohols may be used alone or in combination of two or more kinds.

[0091] Here, the polyhydric alcohol has an aliphatic diol content of 80 mol % or more, preferably 90 mol % or more.

[0092] The melting temperature of the crystalline polyester resin is preferably 50°C or higher and 100°C or lower, more preferably 55°C or higher and 90°C or lower, and even more preferably 60°C or higher and 85°C or lower. The melting temperature is determined from a DSC curve obtained by differential scanning calorimetry (DSC) based on the "peak melting temperature" described in the method for determining melting temperature in JIS K7121:1987 "Method for measuring transition temperature of plastics."

[0093] The weight average molecular weight (Mw) of the crystalline polyester resin is preferably 6,000 or more and 35,000 or less.

[0094] The crystalline polyester resin can be obtained, for example, by a known production method, like the amorphous polyester.

[0095] The content of the binder resin is preferably from 40% by mass to 95% by mass, more preferably from 50% by mass to 90% by mass, and even more preferably from 60% by mass to 85% by mass, based on the total mass of the toner particles.

[0096] -Coloring agent- Examples of colorants include carbon black, chrome yellow, Hansa Yellow, benzidine yellow, threne yellow, quinoline yellow, pigment yellow, permanent orange GTR, pyrazolone orange, Balkan orange, watch young red, permanent red, brilliant carmine 3B, brilliant carmine 6B, DuPont oil red, pyrazolone red, lithol red, rhodamine B lake, lake red C, pigment red, rose bengal, aniline blue, Examples of the dyes include pigments such as ultramarine blue, chalcoil blue, methylene blue chloride, phthalocyanine blue, pigment blue, phthalocyanine green, and malachite green oxalate; and dyes such as acridine-based, xanthene-based, azo-based, benzoquinone-based, azine-based, anthraquinone-based, thioindigo-based, dioxazine-based, thiazine-based, azomethine-based, indigo-based, phthalocyanine-based, aniline black-based, polymethine-based, triphenylmethane-based, diphenylmethane-based, and thiazole-based dyes. The colorant may be used alone or in combination of two or more kinds.

[0097] The colorant may be surface-treated as necessary, or may be used in combination with a dispersant. In addition, a plurality of types of colorants may be used in combination.

[0098] The content of the colorant is preferably from 1% by mass to 30% by mass, and more preferably from 3% by mass to 15% by mass, based on the total mass of the toner particles.

[0099] -Release agent- Examples of the release agent include hydrocarbon waxes, natural waxes such as carnauba wax, rice wax, and candelilla wax, synthetic or mineral / petroleum waxes such as montan wax, and ester waxes such as fatty acid esters and montan acid esters. The release agent is not limited to these.

[0100] The melting temperature of the release agent is preferably 50°C or higher and 110°C or lower, and more preferably 60°C or higher and 100°C or lower. The melting temperature is determined from a DSC curve obtained by differential scanning calorimetry (DSC) based on the "peak melting temperature" described in the method for determining melting temperature in JIS K7121:1987 "Method for measuring transition temperature of plastics."

[0101] The content of the release agent is preferably from 1% by mass to 20% by mass, and more preferably from 5% by mass to 15% by mass, based on the total mass of the toner particles.

[0102] -Other additives- Examples of other additives include known additives such as magnetic materials, charge control agents, inorganic powders, etc. These additives are contained in the toner particles as internal additives.

[0103] -Characteristics of toner particles, etc.- The toner particles may be toner particles having a single layer structure, or may be toner particles having a so-called core-shell structure composed of a core portion (core particle) and a coating layer (shell layer) that coats the core portion. The toner particles having a core-shell structure may be composed of, for example, a core containing a binder resin and, if necessary, other additives such as a colorant and a release agent, and a coating layer containing the binder resin.

[0104] The volume average particle size (D50v) of the toner particles is preferably from 2 μm to 10 μm, and more preferably from 4 μm to 8 μm. The volume average particle size (D50v) of the toner particles is measured using a Coulter Multisizer II (manufactured by Beckman Coulter, Inc.), and the electrolyte is measured using an ISOTON-II (manufactured by Beckman Coulter, Inc.). For the measurement, 0.5 mg to 50 mg of the measurement sample is added to 2 ml of a 5 mass % aqueous solution of a surfactant (preferably sodium alkylbenzene sulfonate) as a dispersant, and this is then added to 100 ml to 150 ml of the electrolyte. The electrolyte with the sample suspended in it is dispersed for 1 minute using an ultrasonic disperser, and the particle size distribution of particles with diameters in the range of 2 μm to 60 μm is measured using a Coulter Multisizer II with an aperture diameter of 100 μm. The number of particles sampled is 50,000. The particle size distribution based on volume is plotted from the smallest diameter side, and the particle size at which the cumulative 50% is reached is defined as the volume average particle size D50v.

[0105] The average circularity of the toner particles is preferably 0.94 or more and 1.00 or less, and more preferably 0.95 or more and 0.98 or less. The average circularity of toner particles is calculated by (circular equivalent perimeter) / (perimeter) [(perimeter of a circle having the same projected area as the particle image) / (perimeter of the particle projected image)]. Specifically, it is a value measured by the following method. First, the toner particles to be measured are sucked and collected, flattened, and a still image of the particles is captured by instantaneous strobe light emission, and the particle image is analyzed by a flow-type particle image analyzer (FPIA-3000 manufactured by Sysmex Corporation). The number of samples to be taken in order to calculate the average circularity is 3,500. When the toner contains an external additive, the toner (developer) to be measured is dispersed in water containing a surfactant, and then ultrasonic treatment is performed to obtain toner particles from which the external additive has been removed.

[0106] -Method of manufacturing toner particles- The toner particles may be produced by any of a dry production method (e.g., a kneading and pulverizing method, etc.) and a wet production method (e.g., an aggregation and coalescence method, a suspension polymerization method, a dissolution suspension method, etc.). There is no particular limitation on these production methods, and any known production method may be used. Among these, it is preferable to obtain the toner particles by the aggregation and coalescence method.

[0107] Specifically, for example, when toner particles are produced by the aggregation and coalescence method, the toner particles are produced through a step of preparing a resin particle dispersion in which resin particles to be a binder resin are dispersed (resin particle dispersion preparation step), a step of aggregating resin particles (other particles, if necessary) in the resin particle dispersion (in a dispersion after mixing other particle dispersions, if necessary) to form aggregated particles (aggregated particle formation step), and a step of heating the aggregated particle dispersion in which the aggregated particles are dispersed, to fuse and coalesce the aggregated particles, thereby forming toner particles (fusion and coalescence step).

[0108] Each step will be described in detail below. In the following description, a method for obtaining toner particles containing a colorant and a release agent will be described, but the colorant and the release agent are used as necessary. Of course, additives other than the colorant and the release agent may be used.

[0109] -Resin particle dispersion preparation process- Along with a resin particle dispersion in which resin particles serving as a binder resin are dispersed, for example, a colorant particle dispersion in which colorant particles are dispersed, and a release agent particle dispersion in which release agent particles are dispersed are prepared.

[0110] The resin particle dispersion liquid is prepared, for example, by dispersing resin particles in a dispersion medium with the aid of a surfactant.

[0111] The dispersion medium used in the resin particle dispersion liquid is, for example, an aqueous medium. Examples of the aqueous medium include water such as distilled water and ion-exchanged water, alcohols, etc. These may be used alone or in combination of two or more kinds.

[0112] Examples of the surfactant include anionic surfactants such as sulfate salts, sulfonates, phosphates, and soaps; cationic surfactants such as amine salts and quaternary ammonium salts; and nonionic surfactants such as polyethylene glycols, alkylphenol ethylene oxide adducts, and polyhydric alcohols. Among these, anionic surfactants and cationic surfactants are particularly preferred. The nonionic surfactants may be used in combination with anionic surfactants or cationic surfactants. The surfactant may be used alone or in combination of two or more kinds.

[0113] In the resin particle dispersion, the resin particles are dispersed in the dispersion medium by a general dispersion method such as a rotary shear type homogenizer, a ball mill having a media, a sand mill, or a dyno mill. Depending on the type of resin particles, the resin particles may be dispersed in the dispersion medium by a phase inversion emulsification method. The phase inversion emulsification method is a method in which the resin to be dispersed is dissolved in a hydrophobic organic solvent in which the resin is soluble, a base is added to the organic continuous phase (O phase) to neutralize it, and then an aqueous medium (W phase) is added to invert the phase from W / O to O / W, thereby dispersing the resin in the aqueous medium in the form of particles.

[0114] The volume average particle size of the resin particles dispersed in the resin particle dispersion is, for example, preferably from 0.01 μm to 1 μm, more preferably from 0.08 μm to 0.8 μm, and even more preferably from 0.1 μm to 0.6 μm. The volume average particle size of the resin particles is measured by using a particle size distribution obtained by measurement using a laser diffraction particle size distribution measuring device (for example, LA-700 manufactured by Horiba, Ltd.), subtracting the cumulative distribution from the small particle size side for the volume of the divided particle size range (channel), and measuring the particle size at which the cumulative distribution is 50% of all particles as the volume average particle size D50v. The volume average particle sizes of particles in other dispersions are measured in the same manner.

[0115] The content of the resin particles in the resin particle dispersion is preferably from 5% by mass to 50% by mass, and more preferably from 10% by mass to 40% by mass.

[0116] In the same manner as the resin particle dispersion liquid, for example, a colorant particle dispersion liquid and a release agent particle dispersion liquid are also prepared. That is, the volume average particle size, dispersion medium, dispersion method, and particle content of the particles in the resin particle dispersion liquid are the same for the colorant particles dispersed in the colorant particle dispersion liquid and the release agent particles dispersed in the release agent particle dispersion liquid.

[0117] -Agglomerated particle formation process- Next, the resin particle dispersion liquid, the colorant particle dispersion liquid, and the release agent particle dispersion liquid are mixed together. Then, in the mixed dispersion, the resin particles, the colorant particles, and the release agent particles are hetero-aggregated to form aggregated particles containing the resin particles, the colorant particles, and the release agent particles and having a diameter close to that of the target toner particles.

[0118] Specifically, for example, an aggregating agent is added to the mixed dispersion, the pH of the mixed dispersion is adjusted to be acidic (e.g., pH 2 or more and 5 or less), a dispersion stabilizer is added as necessary, and then the mixed dispersion is heated to a temperature close to the glass transition temperature of the resin particles (specifically, for example, glass transition temperature of the resin particles -30°C or more and glass transition temperature -10°C or less), and the particles dispersed in the mixed dispersion are aggregated to form aggregated particles. In the aggregated particle formation process, for example, the mixed dispersion may be stirred with a rotary shear homogenizer, an aggregating agent may be added at room temperature (e.g., 25°C), the pH of the mixed dispersion may be adjusted to an acidic state (e.g., pH 2 or more and 5 or less), a dispersion stabilizer may be added as necessary, and then the mixture may be heated.

[0119] Examples of the flocculant include a surfactant having a polarity opposite to that of the surfactant contained in the mixed dispersion, an inorganic metal salt, and a divalent or higher metal complex. When a metal complex is used as the flocculant, the amount of the surfactant used is reduced, and the charging characteristics are improved. If necessary, an additive that forms a complex or a similar bond with the metal ion of the flocculant may be used together with the flocculant. As this additive, a chelating agent is preferably used.

[0120] Examples of inorganic metal salts include metal salts such as calcium chloride, calcium nitrate, barium chloride, magnesium chloride, zinc chloride, aluminum chloride, and aluminum sulfate; and inorganic metal salt polymers such as polyaluminum chloride, polyaluminum hydroxide, and calcium polysulfide. The chelating agent may be a water-soluble chelating agent, for example, oxycarboxylic acid such as tartaric acid, citric acid, gluconic acid, etc., aminocarboxylic acid such as iminodiacetic acid (IDA), nitrilotriacetic acid (NTA), ethylenediaminetetraacetic acid (EDTA), etc. The amount of the chelating agent added is preferably from 0.01 to 5.0 parts by mass, and more preferably from 0.1 to less than 3.0 parts by mass, relative to 100 parts by mass of the resin particles.

[0121] -Fusion / coalescence process- Next, the aggregated particle dispersion liquid in which the aggregated particles are dispersed is heated, for example, to a temperature equal to or higher than the glass transition temperature of the resin particles (for example, a temperature 10° C. to 30° C. higher than the glass transition temperature of the resin particles) to fuse and coalesce the aggregated particles to form toner particles.

[0122] Through the above steps, toner particles are obtained. After obtaining the aggregated particle dispersion in which the aggregated particles are dispersed, the aggregated particle dispersion and the resin particle dispersion in which the resin particles are dispersed are further mixed together to aggregate the aggregated particles so that the resin particles are further attached to the surfaces of the aggregated particles, thereby forming second aggregated particles; and the second aggregated particle dispersion in which the second aggregated particles are dispersed is heated to fuse and coalesce the second aggregated particles, thereby forming toner particles having a core-shell structure.

[0123] After the fusion and coalescence process is completed, the toner particles formed in the solution are subjected to a known washing process, solid-liquid separation process, and drying process to obtain dried toner particles. From the viewpoint of chargeability, the washing process is preferably performed by sufficient substitution washing with ion-exchanged water. From the viewpoint of productivity, the solid-liquid separation process is preferably performed by suction filtration, pressure filtration, etc. From the viewpoint of productivity, the drying process is preferably performed by freeze drying, air flow drying, fluidized drying, vibration type fluidized drying, etc.

[0124] The toner according to the present embodiment is produced, for example, by adding an external additive to the obtained toner particles in a dry state and mixing them. The mixing may be performed, for example, by using a V blender, a Henschel mixer, a Loedige mixer, etc. Furthermore, if necessary, coarse particles of the toner may be removed using a vibration sieve, an air sieve, etc.

[0125] -External additives- The external additive may be, for example, inorganic particles. Examples of the inorganic particles include SiO 2 , TiO 2 , Al 2 O 3 , CuO, ZnO, SnO 2 , CEO 2 , Fe 2 O 3 , MgO, BaO, CaO, K 2 O, Na 2 O, ZrO 2 , CaO SiO 2 , K 2 O (TiO 2 ) n , Al 2 O 3 2SiO 2 , CaCO 3 , MgCO 3 , BaSO 4 , MgSO 4 etc.

[0126] The surface of the inorganic particles as an external additive may be subjected to a hydrophobic treatment. The hydrophobic treatment may be performed, for example, by immersing the inorganic particles in a hydrophobic treatment agent. The hydrophobic treatment agent is not particularly limited, and examples thereof include silane coupling agents, silicone oils, titanate coupling agents, and aluminum coupling agents. These may be used alone or in combination of two or more. The amount of the hydrophobizing agent is usually, for example, 1 part by mass or more and 10 parts by mass or less with respect to 100 parts by mass of the inorganic particles.

[0127] Examples of external additives include resin particles (resin particles such as polystyrene, polymethyl methacrylate, and melamine resin), cleaning agents (for example, metal salts of higher fatty acids such as zinc stearate, and fluorine-based polymer particles), and the like.

[0128] The amount of the external additive is preferably from 0.01% by mass to 5% by mass, and more preferably from 0.01% by mass to 2.0% by mass, based on the toner particles.

[0129] <Image forming device, image forming method> The image forming apparatus according to the present embodiment includes an image carrier, a charging means for charging the surface of the image carrier, an electrostatic image forming means for forming an electrostatic image on the surface of the charged image carrier, a developing means for containing an electrostatic image developer and developing the electrostatic image formed on the surface of the image carrier as a toner image with the electrostatic image developer, a transfer means for transferring the toner image formed on the surface of the image carrier to the surface of a recording medium, and a fixing means for fixing the toner image transferred to the surface of the recording medium. The electrostatic image developer according to the present embodiment is used as the electrostatic image developer.

[0130] In the image forming apparatus according to this embodiment, an image forming method (the image forming method according to this embodiment) is carried out, which includes a charging step of charging the surface of an image carrier, an electrostatic image forming step of forming an electrostatic image on the surface of the charged image carrier, a developing step of developing the electrostatic image formed on the surface of the image carrier as a toner image using the electrostatic image developer according to this embodiment, a transfer step of transferring the toner image formed on the surface of the image carrier to the surface of a recording medium, and a fixing step of fixing the toner image transferred to the surface of the recording medium.

[0131] The image forming apparatus according to the present embodiment may be any of known image forming apparatuses, such as a direct transfer type apparatus in which a toner image formed on the surface of an image holder is directly transferred to a recording medium; an intermediate transfer type apparatus in which a toner image formed on the surface of an image holder is primarily transferred to the surface of an intermediate transfer body, and the toner image transferred to the surface of the intermediate transfer body is secondarily transferred to the surface of a recording medium; an apparatus equipped with a cleaning means for cleaning the surface of the image holder after the transfer of the toner image and before charging; and an apparatus equipped with a discharging means for irradiating the surface of the image holder with discharging light to discharge it after the transfer of the toner image and before charging it. When the image forming apparatus according to the present embodiment is an intermediate transfer type apparatus, the transfer means has, for example, an intermediate transfer body onto whose surface a toner image is transferred, a primary transfer means which primarily transfers the toner image formed on the surface of the image carrier onto the surface of the intermediate transfer body, and a secondary transfer means which secondarily transfers the toner image transferred onto the surface of the intermediate transfer body onto the surface of a recording medium.

[0132] In the image forming apparatus according to the present embodiment, for example, a portion including the developing means may have a cartridge structure (process cartridge) that is detachably attached to the image forming apparatus. As the process cartridge, for example, a process cartridge that contains the electrostatic charge image developer according to the present embodiment and has the developing means is preferably used.

[0133] An example of an image forming apparatus according to the present embodiment will be described below, but the present invention is not limited to this example. In the following description, the main parts shown in the drawings will be described, and the description of the rest will be omitted.

[0134] FIG. 1 is a schematic diagram showing the configuration of an image forming apparatus according to the present embodiment. The image forming apparatus shown in Fig. 1 includes first to fourth image forming units 10Y, 10M, 10C, and 10K (image forming means) of an electrophotographic type that output images of each color of yellow (Y), magenta (M), cyan (C), and black (K) based on color-separated image data. These image forming units (hereinafter sometimes simply referred to as "units") 10Y, 10M, 10C, and 10K are arranged in parallel at predetermined distances from each other in the horizontal direction. These units 10Y, 10M, 10C, and 10K may be process cartridges that are detachably attached to the image forming apparatus.

[0135] Above each of the units 10Y, 10M, 10C, and 10K, an intermediate transfer belt (one example of an intermediate transfer body) 20 is provided, which extends through each unit. The intermediate transfer belt 20 is provided wrapped around a drive roll 22 and a support roll 24, and runs in a direction from the first unit 10Y toward the fourth unit 10K. A force is applied to the support roll 24 by a spring (not shown) or the like in a direction away from the drive roll 22, and tension is applied to the intermediate transfer belt 20 wrapped around them. An intermediate transfer body cleaning device 30 is provided on the image carrier side of the intermediate transfer belt 20, facing the drive roll 22. The developing devices (an example of developing means) 4Y, 4M, 4C, and 4K of the units 10Y, 10M, 10C, and 10K are supplied with yellow, magenta, cyan, and black toners contained in toner cartridges 8Y, 8M, 8C, and 8K, respectively.

[0136] Since the first to fourth units 10Y, 10M, 10C, and 10K have the same configuration and operation, the first unit 10Y that forms a yellow image and is disposed upstream in the direction in which the intermediate transfer belt travels will be described here as a representative.

[0137] The first unit 10Y has a photoconductor 1Y that acts as an image carrier. Around the photoconductor 1Y, a charging roll (an example of a charging means) 2Y that charges the surface of the photoconductor 1Y to a predetermined potential, an exposure device (an example of an electrostatic image forming means) 3 that exposes the charged surface to a laser beam 3Y based on a color-separated image signal to form an electrostatic image, a developing device (an example of a developing means) 4Y that supplies charged toner to the electrostatic image to develop it, a primary transfer roll 5Y (an example of a primary transfer means) that transfers the developed toner image onto an intermediate transfer belt 20, and a photoconductor cleaning device (an example of a cleaning means) 6Y that removes toner remaining on the surface of the photoconductor 1Y after the primary transfer are arranged in this order. The primary transfer roll 5Y is disposed inside the intermediate transfer belt 20, and is provided at a position facing the photoconductor 1Y. A bias power supply (not shown) that applies a primary transfer bias is connected to the primary transfer rolls 5Y, 5M, 5C, and 5K of each unit. Each bias power supply changes the value of the transfer bias applied to each primary transfer roll under the control of a control unit (not shown).

[0138] Hereinafter, the operation of forming a yellow image in the first unit 10Y will be described. First, prior to operation, the surface of the photoconductor 1Y is charged to a potential of −600V to −800V by the charging roll 2Y. The photoconductor 1Y has a conductivity (for example, a volume resistivity of 1×10 at 20° C. -6 The photosensitive layer is formed by laminating a photosensitive layer on a substrate having a resistivity of Ωcm or less. This photosensitive layer is usually highly resistive (the resistance of ordinary resins), but when irradiated with a laser beam, the resistivity of the portion irradiated with the laser beam changes. Therefore, the exposed surface of the charged photoreceptor 1Y is irradiated with a laser beam 3Y from the exposure device 3 in accordance with image data for yellow sent from a control unit (not shown). As a result, an electrostatic charge image of a yellow image pattern is formed on the surface of the photoreceptor 1Y.

[0139] An electrostatic image is an image formed on the surface of the photoconductor 1Y by electrostatic charging. The laser beam 3Y reduces the resistivity of the irradiated parts of the photosensitive layer, causing the charged charges on the surface of the photoconductor 1Y to flow, while the charges remain in the parts not irradiated by the laser beam 3Y. This is a so-called negative latent image. The electrostatic image formed on the photoconductor 1Y rotates to a predetermined developing position as the photoconductor 1Y travels. At this developing position, the electrostatic image on the photoconductor 1Y is developed into a toner image by the developing device 4Y and made visible.

[0140] The developing device 4Y contains an electrostatic image developer including at least yellow toner and a carrier, for example. The yellow toner is triboelectrically charged by being stirred inside the developing device 4Y, and is held on a developer roll (an example of a developer holder) with a charge of the same polarity (negative polarity) as the charge on the photoconductor 1Y. As the surface of the photoconductor 1Y passes through the developing device 4Y, the yellow toner electrostatically adheres to the discharged latent image portion on the surface of the photoconductor 1Y, and the latent image is developed with the yellow toner. The photoconductor 1Y on which the yellow toner image has been formed continues to travel at a predetermined speed, and the toner image developed on the photoconductor 1Y is transported to a predetermined primary transfer position.

[0141] When the yellow toner image on the photoreceptor 1Y is transported to the primary transfer position, a primary transfer bias is applied to the primary transfer roll 5Y, and an electrostatic force from the photoreceptor 1Y toward the primary transfer roll 5Y acts on the toner image, and the toner image on the photoreceptor 1Y is transferred onto the intermediate transfer belt 20. The transfer bias applied at this time has a polarity (+) opposite to the polarity (-) of the toner, and is controlled to, for example, +10 μA by a control unit (not shown) in the first unit 10Y. On the other hand, the toner remaining on the photoconductor 1Y is removed and collected by the photoconductor cleaning device 6Y.

[0142] The primary transfer bias applied to the primary transfer rolls 5M, 5C, and 5K subsequent to the second unit 10M is also controlled in accordance with the first unit. In this manner, the intermediate transfer belt 20 onto which the yellow toner image has been transferred by the first unit 10Y is conveyed successively through the second to fourth units 10M, 10C, and 10K, where the toner images of each color are transferred and superimposed.

[0143] The intermediate transfer belt 20 onto which the four color toner images have been transferred in multiple layers through the first to fourth units reaches a secondary transfer section that is composed of the intermediate transfer belt 20, a support roll 24 that contacts the inner surface of the intermediate transfer belt, and a secondary transfer roll (an example of a secondary transfer means) 26 arranged on the image bearing surface side of the intermediate transfer belt 20. Meanwhile, a recording paper (an example of a recording medium) P is fed at a predetermined timing into the gap between the secondary transfer roll 26 and the intermediate transfer belt 20 via a supply mechanism, and a secondary transfer bias is applied to the support roll 24. The transfer bias applied at this time has a (-) polarity that is the same as the (-) polarity of the toner, and an electrostatic force from the intermediate transfer belt 20 toward the recording paper P acts on the toner image, and the toner image on the intermediate transfer belt 20 is transferred onto the recording paper P. The secondary transfer bias at this time is determined according to the resistance detected by a resistance detection means (not shown) that detects the resistance of the secondary transfer section, and is voltage-controlled.

[0144] Thereafter, the recording paper P is sent to a pressure contact portion (nip portion) of a pair of fixing rolls in a fixing device (one example of a fixing means) 28, where the toner image is fixed onto the recording paper P, forming a fixed image.

[0145] The recording paper P onto which the toner image is transferred can be, for example, plain paper used in electrophotographic copying machines, printers, etc. In addition to the recording paper P, other examples of the recording medium include overhead projector sheets and the like. To further improve the smoothness of the image surface after fixing, it is preferable that the surface of the recording paper P is also smooth. For example, coated paper in which the surface of ordinary paper is coated with resin or the like, art paper for printing, etc. are preferably used.

[0146] After the color image has been fixed, the recording paper P is conveyed toward the discharge section, and the series of color image forming operations is completed.

[0147] <Process cartridge> The process cartridge according to this embodiment is a process cartridge that contains the electrostatic image developer according to this embodiment, is equipped with a developing means that develops an electrostatic image formed on the surface of an image carrier using the electrostatic image developer into a toner image, and is detachably attached to an image forming apparatus.

[0148] The process cartridge according to this embodiment is not limited to the above configuration, and may be configured to include a developing means and, as necessary, at least one other means selected from an image carrier, a charging means, an electrostatic image forming means, and a transfer means.

[0149] An example of a process cartridge according to the present embodiment will be described below, but the present invention is not limited to this example. In the following description, the main parts shown in the drawings will be described, and the description of the rest will be omitted.

[0150] FIG. 2 is a schematic diagram showing the process cartridge according to the present embodiment. The process cartridge 200 shown in FIG. 2 is configured by, for example, a housing 117 having a mounting rail 116 and an opening 118 for exposure, and integrally combining and holding a photoconductor 107 (an example of an image carrier), a charging roll 108 (an example of a charging means) provided around the photoconductor 107, a developing device 111 (an example of a developing means), and a photoconductor cleaning device 113 (an example of a cleaning means), which are assembled into a cartridge. In FIG. 2, 109 indicates an exposure device (an example of an electrostatic image forming means), 112 indicates a transfer device (an example of a transfer means), 115 indicates a fixing device (an example of a fixing means), and 300 indicates a recording paper (an example of a recording medium). EXAMPLES

[0151] Hereinafter, the embodiments of the present invention will be described in detail with reference to examples, but the embodiments of the present invention are not limited to these examples. In the following description, unless otherwise specified, "parts" and "%" are based on mass.

[0152] <Example 1> [Preparation of ferrite particles] Fe 2 O 3 1318 parts and Mn(OH) 2 587 parts and Mg(OH) 2 The mixture was mixed with 96 parts of polyvinyl alcohol and 0.5 parts of polycarboxylic acid as a dispersant, and zirconia beads with a media diameter of 1 mm were added to water, and the mixture was ground and mixed in a sand mill to obtain a dispersion. The volume average particle size of the particles in the dispersion was 1.5 μm. The dispersion liquid was used as a raw material, and granulated and dried using a spray dryer to obtain granules with a volume average particle size of 37 μm. Next, in an oxygen-nitrogen mixed atmosphere with an oxygen partial pressure of 1%, main sintering was performed using an electric furnace at a temperature of 1450°C for 4 hours, and then heating was performed in the air at a temperature of 900°C for 3 hours to obtain sintered particles. The sintered particles were crushed and classified to obtain ferrite particles (1) with a volume average particle size of 35 μm. The arithmetic mean height Ra (JIS B0601:2001) of the roughness curve of the ferrite particles (1) was 0.6 μm.

[0153] [Coating agent (1)] M Resin (1) Perfluoropropylethyl methacrylate-methyl methacrylate copolymer (polymerization ratio by mass: 30:70, weight average molecular weight Mw=19000): 12.1 parts Resin (2) Cyclohexyl methacrylate resin (weight average molecular weight 350,000): 8.1 parts Carbon black (Cabot, VXC72): 0.8 parts ·Inorganic particles (1): 9 parts (Commercially available hydrophilic silica particles (fumed silica particles, no surface treatment, volume average particle size 40 nm)) Toluene: 250 parts Isopropyl alcohol: 50 parts The above materials and glass beads (diameter 1 mm, same amount as toluene) were placed in a sand mill and stirred at a rotation speed of 190 rpm for 30 minutes to obtain a coating agent (1) with a solid content of 11%.

[0154] [Preparation of carrier (1)] 1000 parts of the ferrite particles (1) and half the amount of the coating agent (1) were put into a kneader and mixed at room temperature (25° C.) for 20 minutes, then heated to 70° C. and dried under reduced pressure. The dried product was cooled to room temperature (25° C.), and half of the coating agent (1) was added and mixed at room temperature (25° C.) for 20 minutes. Then, the mixture was heated to 70° C. and dried under reduced pressure. Next, the dried product was taken out of the kneader and sieved through a mesh with 75 μm openings to remove coarse powder, thereby obtaining a carrier (1).

[0155] <Examples 2 to 33, Comparative Example 1> Carriers of each example were obtained in the same manner as in Example 1, except that the amount of resin (1), the amount of resin (2), and the type and amount of inorganic particles were changed according to Table 1.

[0156] <Various characteristics of carriers> The following characteristics of the carrier of each example were measured according to the methods already described. ·Si Net Strength A~C The ratio of silicon on the surface of the resin coating layer (referred to as "Si ratio" in the table) The area ratio of inorganic particles when observing a cross section of the coating resin layer cut along the thickness direction (referred to as "inorganic particle area ratio" in the table) Charge amount of carrier A taken out from developer A, which is a mixture of toner with silica particles added and carrier (referred to as "initial carrier charge amount CA" in the table) The charge amount of carrier B taken out from developer B, which was made by adding silica particles to developer A and stirring for 20 minutes with a turbula stirrer (referred to as "carrier charge amount CB after deterioration" in the table)

[0157] <Preparation of developer> [Preparation of amorphous polyester resin dispersion (A1)] Ethylene glycol: 37 parts Neopentyl glycol: 65 parts 1,9-nonanediol: 32 parts Terephthalic acid: 96 parts The above materials were charged in a flask, and the temperature was raised to 200°C over 1 hour. After confirming that the reaction system was stirred uniformly, 1.2 parts of dibutyltin oxide were added. The temperature was raised to 240°C over 6 hours while distilling off the water produced, and stirring was continued at 240°C for 4 hours to obtain an amorphous polyester resin (acid value 9.4 mgKOH / g, weight average molecular weight 13,000, glass transition temperature 62°C). The amorphous polyester resin was transferred to an emulsifier / disperser (Cavitron CD1010, Eurotech) in a molten state at a rate of 100 g per minute. Separately, a dilute ammonia water with a concentration of 0.37% obtained by diluting reagent ammonia water with ion-exchanged water was placed in a tank, and the dilute ammonia water was transferred to the emulsifier / disperser at a rate of 0.1 liters per minute simultaneously with the amorphous polyester resin while being heated to 120°C with a heat exchanger. The emulsifier / disperser was operated at a rotor rotation speed of 60Hz and a pressure of 5kg / cm. 2 By operating under the above conditions, a non-crystalline polyester resin dispersion (A1) having a volume average particle size of 160 nm and a solid content of 20% was obtained.

[0158] [Preparation of crystalline polyester resin dispersion (C1)] Decanedioic acid: 81 parts Hexanediol: 47 parts The above materials were charged into a flask, and the temperature was raised to 160°C over 1 hour. After confirming that the reaction system was stirred uniformly, 0.03 parts of dibutyltin oxide was added. The temperature was raised to 200°C over 6 hours while distilling off the water produced, and stirring was continued at 200°C for 4 hours. The reaction liquid was then cooled, solid-liquid separation was performed, and the solid matter was dried at a temperature of 40°C under reduced pressure to obtain a crystalline polyester resin (C1) (melting point 64°C, weight average molecular weight 15,000).

[0159] Crystalline polyester resin (C1): 50 parts Anionic surfactant (manufactured by Daiichi Kogyo Seiyaku Co., Ltd., Neogen RK): 2 parts - Ion-exchanged water: 200 parts The above materials were heated to 120°C, thoroughly dispersed using a homogenizer (Ultra Turrax T50, IKA), and then dispersed using a pressure discharge homogenizer. When the volume average particle size reached 180 nm, the particles were collected to obtain a crystalline polyester resin dispersion (C1) with a solid content of 20%.

[0160] [Preparation of release agent particle dispersion (W1)] Paraffin wax (HNP-9, manufactured by Nippon Seiro Co., Ltd.): 100 parts Anionic surfactant (manufactured by Daiichi Kogyo Seiyaku Co., Ltd., Neogen RK): 1 part Ion-exchanged water: 350 parts The above materials were mixed and heated to 100°C, dispersed using a homogenizer (IKA Ultra Turrax T50), and then dispersed using a pressure discharge Gaulin homogenizer to obtain a release agent particle dispersion in which release agent particles with a volume average particle size of 200 nm were dispersed. Ion-exchanged water was added to this release agent particle dispersion to adjust the solid content to 20%, and this was used as release agent particle dispersion (W1).

[0161] [Preparation of colorant particle dispersion (K1)] Carbon black (Cabot, Regal 330): 50 parts Anionic surfactant (manufactured by Daiichi Kogyo Seiyaku Co., Ltd., Neogen RK): 5 parts Ion-exchanged water: 195 parts The above materials were mixed and dispersed for 60 minutes using a high-pressure impact disperser (Ultimaizer HJP30006, Sugino Machine Co., Ltd.) to obtain a colorant particle dispersion (K1) with a solid content of 20%.

[0162] [Preparation of toner particles (TA)] - Ion-exchanged water: 200 parts Amorphous polyester resin dispersion (A1): 150 parts Crystalline polyester resin dispersion (C1): 10 parts Release agent particle dispersion (W1): 10 parts Colorant particle dispersion (K1): 15 parts Anionic surfactant (TaycaPower): 2.8 parts The above materials were placed in a round stainless steel flask, and 0.1N nitric acid was added to adjust the pH to 3.5, and then an aqueous solution of polyaluminum chloride in which 2 parts of polyaluminum chloride (Oji Paper Co., Ltd., 30% powder product) were dissolved in 30 parts of ion-exchanged water was added. After dispersion at 30°C using a homogenizer (IKA Ultra Turrax T50), the mixture was heated to 45°C in a heating oil bath and held until the volume average particle size became 4.9 μm. Next, 60 parts of amorphous polyester resin dispersion (A1) was added and held for 30 minutes. Next, when the volume average particle size became 5.2 μm, 60 parts of amorphous polyester resin dispersion (A1) was further added and held for 30 minutes. Next, 20 parts of a 10% NTA (nitrilotriacetic acid) metal salt aqueous solution (Chilest 70, Chelest Co., Ltd.) was added, and a 1N aqueous solution of sodium hydroxide was added to adjust the pH to 9.0. Next, 1 part of anionic surfactant (TaycaPower) was added, and the mixture was heated to 85°C while continuing to stir, and maintained at that temperature for 5 hours. The mixture was then cooled to 20°C at a rate of 20°C / min. The mixture was then filtered, thoroughly washed with ion-exchanged water, and dried to obtain toner particles (TA) having a volume average particle size of 5.7 μm and an average circularity of 0.971.

[0163] [Preparation of toner (T)] 100 parts of the toner particles (T) and 1.5 parts of hydrophobic silica particles (RY50, manufactured by Nippon Aerosil Co., Ltd.) were placed in a sample mill and mixed for 30 seconds at a rotation speed of 10,000 rpm. The mixture was then sieved through a vibrating sieve with an opening of 45 μm to obtain a toner (T) with a volume average particle size of 5.7 μm.

[0164] [Preparation of developer] The carrier and toner (T) of each example were placed in a V blender in a mixing ratio of carrier:toner=100:10 (mass ratio) and stirred for 20 minutes to obtain each developer.

[0165] <Evaluation of toner charge retention> The developer was placed in the developing device located at the black position of an image forming apparatus ("Iridesse Production Press" manufactured by Fuji Xerox Co., Ltd.). Using this image forming device, 50,000 sheets were printed, and approximately 20 g of the developer was sampled initially and after 50,000 sheets were printed, and the toner was removed from the developer by blowing off, and only the carrier was isolated. 0.8 g of the toner used in preparing the developer was added to the obtained carrier at 10 g of carrier, and the mixture was stirred for 5 minutes in a Turbula mixer, and the charge amount was measured. The ratio of the carrier charge amount between the initial developer and the developer after printing 50,000 sheets (charge ratio after printing 50,000 sheets to the initial) was calculated, and the charge retention of the toner was evaluated according to the following criteria. A: Carrier charge ratio is 0.9 or more B: Carrier charge ratio is 0.85 or more and less than 0.9 C: Carrier charge ratio is 0.8 or more and less than 0.85 D: Carrier charge ratio is 0.7 or more and less than 0.8 E: Carrier charge ratio is less than 0.7

[0166] [Table 1-1]

[0167] [Table 1-2]

[0168] From the above results, it is understood that the toner in this embodiment has superior charge retention properties compared to the comparative example.

[0169] The abbreviations in the table are as follows: PFEM / MM: Perfluoropropylethyl methacrylate-methyl methacrylate copolymer (polymerization ratio by mass: 30:70, weight average molecular weight Mw=19000) ·CHM: Cyclohexyl methacrylate resin (weight average molecular weight Mw = 350,000) Mw: Weight average molecular weight of mixed resin or single resin

[0170] <Inorganic particles added to the carrier coating resin layer> The inorganic particles to be added to the carrier coating resin layer are as follows.

[0171] [Inorganic particles (1)] Commercially available hydrophilic silica particles (fumed silica particles, no surface treatment, volume average particle size 40 nm) were prepared and used as inorganic particles (1).

[0172] [Inorganic particles (2)] 890 parts of methanol and 210 parts of 9.8% aqueous ammonia were added and mixed in a 1.5 L glass reaction vessel equipped with a stirrer, a dropping nozzle, and a thermometer to obtain an alkaline catalyst solution. After adjusting the alkaline catalyst solution to 45°C, 550 parts of tetramethoxysilane and 140 parts of 7.6% aqueous ammonia were dropped simultaneously over a period of 450 minutes while stirring to obtain a silica particle dispersion (A). The silica particles in the silica particle dispersion (A) have a volume average particle size of 4 nm, a volume particle size distribution index (the square root of the ratio of the particle size D16v at 16% cumulative from the small diameter side in the volume-based particle size distribution to the particle size D84v at 84% cumulative (D84v / D16v) 1 / 2 )1.2. 300 parts of the silica particle dispersion (A) were put into an autoclave equipped with a stirrer, and the stirrer was rotated at a rotation speed of 100 rpm. While continuing to rotate the stirrer, liquefied carbon dioxide was injected into the autoclave from a carbon dioxide cylinder via a pump, and the inside of the autoclave was heated with a heater while the inside of the autoclave was pressurized with a pump, so that the inside of the autoclave was in a supercritical state of 150°C and 15 MPa. The pressure valve was operated to keep the inside of the autoclave at 15 MPa, and supercritical carbon dioxide was circulated to remove methanol and water from the silica particle dispersion (A). When the amount of carbon dioxide supplied to the autoclave reached 900 parts, the supply of carbon dioxide was stopped, and a powder of silica particles was obtained. The inside of the autoclave was kept at 150°C and 15 MPa by a heater and a pump to maintain the supercritical state of carbon dioxide, and while continuing to rotate the stirrer of the autoclave, 50 parts of hexamethyldisilazane per 100 parts of silica particles was injected into the autoclave by an entrainer pump, and the temperature inside the autoclave was raised to 180°C and reacted for 20 minutes. Next, supercritical carbon dioxide was again circulated in the autoclave to remove excess hexamethyldisilazane. Next, the stirring was stopped, the pressure valve was opened to release the pressure inside the autoclave to atmospheric pressure, and the temperature was lowered to room temperature (25°C). Thus, silica particles surface-treated with hexamethyldisilazane were obtained. The silica particles had a volume average particle size of 4 nm. The obtained silica particles were designated as inorganic particles (2).

[0173] [Inorganic particles (3)] In the same manner as in the preparation of inorganic particles (2), the amount of tetramethoxysilane and 7.6% aqueous ammonia added when preparing silica particle dispersion (A) was increased to change the volume average particle size of the silica particles in the silica particle dispersion to 6 nm, and silica particles surface-treated with hexamethyldisilazane were obtained. The silica particles had a volume average particle size of 7 nm. The obtained silica particles were designated inorganic particles (3).

[0174] [Inorganic particles (4)] Commercially available hydrophobic silica particles (fumed silica particles surface-treated with hexamethyldisilazane, volume average particle size 12 nm) were prepared and used as inorganic particles (4).

[0175] [Inorganic particles (5)] Commercially available hydrophilic silica particles (fumed silica particles, no surface treatment, volume average particle size 62 nm) were prepared and used as inorganic particles (5).

[0176] [Inorganic particles (6)] Commercially available hydrophobic silica particles (fumed silica particles surface-treated with hexamethyldisilazane, volume average particle size 88 nm) were prepared and used as inorganic particles (6).

[0177] [Inorganic particles (7)] Commercially available hydrophobic silica particles (fumed silica particles surface-treated with hexamethyldisilazane, volume average particle size 93 nm) were prepared and used as inorganic particles (7).

[0178] [Inorganic particles (8)] Commercially available calcium carbonate particles (volume average particle size: 40 nm) were prepared and used as inorganic particles (8).

[0179] [Inorganic particles (9)] Commercially available barium carbonate particles (volume average particle size: 40 nm) were prepared and used as inorganic particles (9).

[0180] [Inorganic particles (10)] Commercially available barium sulfate particles (BARIFINE BF-40, volume average particle size 10 nm) were prepared and used as inorganic particles (10).

[0181] [Inorganic particles (11)] Commercially available barium sulfate particles (BARIFINE BF-20, volume average particle size 30 nm) were prepared and used as inorganic particles (11).

[0182] [Inorganic particles (12)] Commercially available barium sulfate particles (BARIFINE BF-21, volume average particle size 50 nm) were prepared and used as inorganic particles (12).

[0183] [Inorganic particles (13)] Commercially available barium sulfate particles (BARIFINE BF-10, volume average particle size 60 nm) were prepared and used as inorganic particles (13). [Explanation of symbols]

[0184] 1Y, 1M, 1C, 1K Photoconductor (an example of an image carrier) 2Y, 2M, 2C, 2K Charging roll (an example of a charging means) 3 Exposure device (an example of an electrostatic image forming means) 3Y, 3M, 3C, 3K laser beam 4Y, 4M, 4C, 4K developing device (an example of developing means) 5Y, 5M, 5C, 5K Primary transfer roll (an example of a primary transfer means) 6Y, 6M, 6C, 6K Photoconductor cleaning device (an example of a cleaning means) 8Y, 8M, 8C, 8K toner cartridges 10Y, 10M, 10C, 10K Image forming units 20 Intermediate transfer belt (an example of an intermediate transfer body) 22 Driving Roll 24 Support roll 26 Secondary transfer roll (an example of a secondary transfer means) 28 Fixing device (an example of a fixing means) 30 Intermediate transfer body cleaning device P Recording paper (an example of a recording medium) 107 Photoconductor (an example of an image carrier) 108 Charging roll (an example of charging means) 109 Exposure device (an example of electrostatic image forming means) 111 Developing device (an example of developing means) 112 Transfer device (an example of a transfer means) 113 Photoconductor cleaning device (an example of a cleaning means) 115 Fixing device (an example of fixing means) 116 Mounting Rail 117 Cabinet 118 Exposure Aperture 200 Process Cartridge 300 Recording paper (an example of a recording medium)

Claims

1. a coating resin layer that coats the magnetic particles and contains silica particles as inorganic particles and an acrylic resin having an alicyclic structure as a coating resin; When carrier A is extracted from developer A, which is a mixture of toner to which silica particles are externally added and carrier, and the carrier A is subjected to fluorescent X-ray analysis, the net intensity of Si is defined as A, Silica particles are added to the developer A, and developer B is obtained by stirring the developer A for 20 minutes using a turbulent stirrer. The carrier B is extracted from the developer B and subjected to fluorescent X-ray analysis. The net intensity of Si is defined as B. When carrier B extracted from developer B, toner particles, and mixture C obtained by stirring the mixture C for 2 minutes with a turbulent stirrer are subjected to fluorescent X-ray analysis, the net intensity of Si is C. Formula 1: 0<(C−A) / (B−A)≦0.40 is satisfied, The electrostatic image developing carrier, wherein the ratio of Si on the surface of the coating resin layer, as determined by X-ray photoelectron spectroscopy (XPS), is 6.5 atom % or more and 12 atom % or less.

2. 2. The carrier for developing electrostatic images according to claim 1, wherein when the cut surface of the coating resin layer is cut in the thickness direction, the area ratio of the inorganic particles is 10% or more and 50% or less.

3. 3. The carrier for developing electrostatic images according to claim 1, wherein the average particle size of the inorganic particles is smaller than the average thickness of the coating resin layer.

4. 4. The carrier for developing electrostatic images according to claim 3, wherein the ratio of the average particle size of the inorganic particles to the average thickness of the coating resin layer (average particle size of the inorganic particles / average thickness of the coating resin layer) is 0.005 or more and 0.15 or less.

5. 5. The carrier for developing electrostatic images according to claim 3, wherein the inorganic particles have an average particle size of 5 nm or more and 90 nm or less.

6. 6. The carrier for developing electrostatic images according to claim 3, wherein the average thickness of the coating resin layer is from 0.6 μm to 1.4 μm.

7. 7. The carrier for developing electrostatic images according to claim 1, wherein the inorganic particles are particles having the same charge polarity as that of an external additive of the toner.

8. 8. The carrier for developing electrostatic images according to claim 1, wherein the content of the inorganic particles is from 20% by mass to 50% by mass based on the resin contained in the coating resin layer.

9. 9. The carrier for developing electrostatic images according to claim 1, wherein the weight average molecular weight of the resin contained in the coating resin layer is less than 300,000.

10. 10. The electrostatic image developing carrier according to claim 9, wherein the weight average molecular weight of the resin contained in the coating resin layer is less than 250,000.

11. a toner for developing an electrostatic image; A carrier for developing an electrostatic image according to any one of claims 1 to 10, 1. An electrostatic image developer comprising:

12. a developing unit that contains the electrostatic image developer according to claim 11 and develops an electrostatic image formed on a surface of an image carrier into a toner image by using the electrostatic image developer, A process cartridge that is detachably attached to an image forming apparatus.

13. An image carrier; a charging means for charging the surface of the image carrier; an electrostatic image forming means for forming an electrostatic image on the charged surface of the image carrier; a developing unit that contains the electrostatic image developer according to claim 11 and develops the electrostatic image formed on the surface of the image carrier into a toner image by the electrostatic image developer; a transfer means for transferring the toner image formed on the surface of the image carrier to a surface of a recording medium; a fixing means for fixing the toner image transferred onto the surface of the recording medium; An image forming apparatus comprising:

14. a charging step of charging a surface of an image carrier; an electrostatic image forming step of forming an electrostatic image on the charged surface of the image carrier; a developing step of developing the electrostatic image formed on the surface of the image carrier into a toner image by using the electrostatic image developer according to claim 11; a transfer step of transferring the toner image formed on the surface of the image carrier onto a surface of a recording medium; a fixing step of fixing the toner image transferred onto the surface of the recording medium; The image forming method according to claim 1,