Hydrogenation methods for olefins

Abstract

An integrated process for hydrogenating olefins is described in which a hydrogen stream is produced from the electrolysis of water. The water is obtained from a first reaction step in which a first feed stream containing oxygenated hydrocarbons is reacted to produce a first reaction product stream containing olefins and a second reaction product stream containing water. The second reaction product stream is electrolyzed to produce an electrolyzer product stream containing hydrogen. The hydrogen is used to hydrogenate the olefins. A paraffin stream can be obtained from the hydrogenation effluent.

Description

[Technical Field]

[0001] (Priority statement) This application claims priority to U.S. Provisional Patent Application No. 63 / 411,693, filed on 30 September 2022, which is incorporated in its entirety herein.

[0002] (Field of Invention) This field concerns the hydrogenation of olefin-containing streams using hydrogen streams generated by the electrolysis of water. [Background technology]

[0003] Because high energy output is required to power aircraft, jet fuel is one of the few petroleum fuels that cannot be easily replaced by electric motor systems. Jet fuel consists of 75% paraffin and 25% aromatic compounds, as described in ASTM D1655. Synthetic hydrocarbons from sources including alcohol-to-jet (ATJ-SPK) and hydrothermal conversion of fatty acid esters (CHJ) can also be used as jet fuel, as described in ASTM D7566. These sources may have a low aromatic content of about 0.5% by weight. Significant incentives are currently available for green jet fuel in certain regions.

[0004] Ethanol is a bio-derived alcohol that can be dehydrated to ethylene. Ethylene can be dimerized into olefins, such as C4, C6, and C8 olefins. Olefin oligomerization is a process that allows smaller olefins to be oligomerized into larger olefins. More specifically, olefins, including dimerized olefins, can be converted into distillates containing products in the jet fuel and diesel range. Oligomerized distillates can be saturated for use as transport fuels with high stability.

[0005] Processes utilizing electrochemical cells for chemical transformations are also described. Generally, an electrochemical cell includes an anode, a cathode, and an electrolyte. By placing a catalyst on the anode, on the cathode, and / or in the electrolyte, a desired chemical reaction can be promoted. During operation, reactants or a solution containing reactants are supplied into the cell. Then, a voltage (potential difference) is applied between the anode and the cathode to promote the desired electrochemical reaction. When water is a reactant and products containing oxygen and hydrogen are produced, the reaction is often called hydrolysis or electrolysis, and the reactor is called an electrolytic cell.

[0006] Therefore, there is a need for a method for hydrogenating olefins that would enable the use of bio-derived raw materials such as ethanol as a transport fuel source. [Overview of the project]

[0007] The inventors have devised an integrated method for hydrogenating olefins in which a hydrogen stream is produced from the electrolysis of water. Water is obtained from a first reaction step in which a first feed stream is reacted to produce a first reaction product stream containing olefins and a second reaction product stream containing water, and the second reaction product stream is electrolyzed to produce an electrolytic cell product stream containing hydrogen. The paraffin stream can be obtained from the hydrogenation distillate. [Brief explanation of the drawing]

[0008] [Figure 1] This is a schematic plan view of the method disclosed herein.

[0009] definition The term "communication" means that fluid flow is operably permitted between the enumerated components, and this can be characterized as "fluid communication."

[0010] The term "downstream communication" means that at least a portion of the fluid flowing to the downstream-communicating object can be operably flowed from the fluid-communicating object.

[0011] The term "upstream communication" means that at least a portion of the fluid flowing from an upstream communication object can flow operably into a fluid-communicated object.

[0012] The term "direct communication" means that the fluid flow from the upstream component enters the downstream component without passing through any other intervening vessel.

[0013] The term "indirect communication" refers to a situation where a fluid flow from an upstream component enters a downstream component after passing through an intervening container.

[0014] As used herein, the terms “dominant,” “dominant,” or “dominantly” mean more than 50%, preferably more than 75%, and more preferably more than 90%.

[0015] The term “column” refers to a distillation column (singular or plural) for separating one or more different volatile components. Unless otherwise specified, each column includes a condenser at the top of the column to condense and reflux a portion of the top flow returning to the top of the column, and a reboiler at the bottom of the column to vaporize a portion of the bottom flow and return it to the bottom of the column. The feedstock to the column may be preheated. The top pressure is the pressure of the top vapor at the vapor outlet of the column. The bottom temperature is the temperature at the bottom liquid outlet. The top line and bottom line refer to the net lines from column to column downstream of any reflux or reboil. A stripper column omits the reboiler at the bottom of the column and instead may provide the required heat and separation propulsion from a fluidized inert medium such as vapor. A stripping column typically feeds the feedstock to a top tray and removes the main product from the bottom.

[0016] As used herein, the term “separator” means a vessel having an inlet and at least a top vapor outlet and a bottom liquid outlet, and which may also have an aqueous outlet from the boot. A flash drum is a type of separator that can be downstream-communicated with a separator that can operate at higher pressures. As used herein, the term “boiling temperature” means the atmospheric equivalent boiling point (AEBP) calculated from the observed boiling point and distillation pressure using the formulas provided in ASTM D1160 Appendix A7, entitled “Practice for Converting Observed Vapor Temperatures to Atmospheric Equivalent Temperatures”.

[0017] The term “unit” should be understood to refer to one or more process steps involving a chemical transformation. At the heart of a unit are one or more catalytic reactors or separation vessels necessary to achieve the transformation. A unit may further include additional separation vessels containing fractionation columns for separating the product stream. A unit may further include pretreatment steps for the chemical transformation. In summary, a “unit” includes one or more reactors or separation vessels, as well as separation and pretreatment steps, whether shown in the figures or explicitly discussed herein.

[0018] As used herein, the terms "T5," "T90," or "T95" refer to the boiling point of 5 mass percent, 90 mass percent, or possibly 95 mass percent of the sample, respectively, using ASTM D-86 or TBP.

[0019] As used herein, the term “initial boiling point” (IBP) means, depending on the context, the temperature at which the sample begins to boil, using ASTM D-7169, ASTM D-86, or TBP.

[0020] As used herein, the term "end point" (EP) may, in some cases, mean the temperature at which the sample has completely evaporated, using ASTM D-7169, ASTM D-86, or TBP.

[0021] As used herein, the terms "diesel" and / or "distillate" mean hydrocarbons that boil within the range of "diesel cut points" including an IBP of 125 °C (257 °F) to 175 °C (347 °F) or a T5 of 150 °C (302 °F) to 200 °C (392 °F), and a T95 of 343 °C (650 °F) to 399 °C (750 °F) using the TBP distillation method or a T90 of 280 °C (536 °F) to 340 °C (644 °F) using ASTM D-86. The term "green diesel" or "green distillate" means diesel containing hydrocarbons that are not sourced from fossil fuels.

[0022] As used herein, the term "jet fuel" means hydrocarbons that boil within the range of a T10 of 190 °C (374 °F) to 215 °C (419 °F) and an end point of 290 °C (554 °F) to 310 °C (590 °F). The term "green jet fuel" means jet fuel containing hydrocarbons that do not originate from fossil fuels.

[0023] As used herein, "electrolyzer" is intended to denote a device that includes a cathode (negative charge), an anode (positive charge), and a membrane. The overall system may also include pumps, vents, storage tanks, power sources, separators, and / or other components. Typically, these devices are used to cause an electrochemical reaction such as the electrolysis of water within the cell stack of an electrolyzer unit. Electricity is applied to the anode and cathode across the membrane, which, in the case of the electrolysis of water, separates water into its constituent molecules, hydrogen (H2) and oxygen (O2).

[0024] The term "cathode" means an electrode from which conventional current exits a polarized electrical device and into which electrons flow from an external or external circuit connected to the cell. Reduction reactions occur at the cathode.

[0025] The term "anode" means an electrode through which conventional current enters a polarized electrical device and electrons flow out to an external or external circuit connected to the cell. The oxidation reaction occurs at the anode.

Best Mode for Carrying Out the Invention

[0026] The disclosed method includes providing a first feed stream containing an oxygenated hydrocarbon to a first reaction unit, reacting the first feed stream to produce a first reaction product stream containing olefins and a second reaction product stream containing water, electrolyzing the second reaction product stream to produce an electrolytic cell product stream containing hydrogen, providing a first hydrogenated feed stream containing hydrogen and a second hydrogenated feed stream containing olefins to a hydrogenation unit, and hydrogenating the second hydrogenated feed stream on a hydrogenation catalyst under hydrogenation reaction conditions to form a hydrogenated product stream containing paraffins.

[0027] Referring again to the drawing of FIG. 1, the first feed stream in line 12 to the first reaction unit 10 can contain an oxygenated hydrocarbon. The oxygenated hydrocarbon can include ethanol, propanol, other alcohols, and / or triglycerides. Preferably, the oxygenated hydrocarbon has a biological source such as fermentation or is obtained from vegetable oil. In an exemplary embodiment, the first feed stream in line 12 can contain ethanol. The first feed stream in line 12 can predominantly contain ethanol. The first reaction unit 10 can include ethanol dehydration.

[0028] Dehydration converts ethanol to ethylene and water. Ethanol dehydration is a highly endothermic reaction. Steam can be added to the reactor to assist in controlling the heat absorption and reducing coke deposition to improve catalyst stability. The recycle stream of water in line 17 can additionally include a portion of the mixed first feed stream in line 14. Unconverted ethanol can also be recycled in the recycle feed stream in line 15 to include a portion of the mixed first feed stream in line 14.

[0029] The mixed first feed stream may be heated in one or more stages by a heat exchanger, a combustion heater, or a combination thereof. In an exemplary embodiment, some of the heat generated in the hydrogenation unit 50 is captured as high-temperature steam and used to help heat the first mixed feed stream in line 14 to a temperature of about 400°C. Thus, the hydrogenation unit 50 and the first reaction unit 10 can be thermally integrated. More than 10%, 25%, or 50% of the heat required for the reaction in the first reaction unit 10 may be supplied through thermal integration from the hydrogenation unit 50. A combustion heater may also help to provide sufficient heat. The first mixed feed stream may be further heated to a dehydration reaction temperature of 400°C to 550°C at a pressure of 317 kPa (gauge) (45 psig) to 2068 kPa (300 psig) or 345 kPa (50 psig) to 630 kPa (gauge) (90 psig) before passing over the dehydration catalyst. The permissible pressure can range from 1379 kPa (200 psig) to 1724 kPa (250 psig).

[0030] In one embodiment, the ethanol dehydration catalyst may be an alumina-based catalyst. The dehydration catalyst may substantially contain gamma alumina.

[0031] In another embodiment, the first reaction unit 10 may include hydrogenation. A suitable feed stream in line 12 to the hydrogenation unit may include triglycerides derived from vegetable oil. Renewable feedstocks that can be used in the present invention include either glycerides or free fatty acids (FFAs). Examples of these feedstocks include, but are not limited to, canola oil, corn oil, soybean oil, rapeseed oil, tall oil, sunflower oil, hemp seed oil, olive oil, linseed oil, coconut oil, castor oil, peanut oil, palm oil, mustard oil, cottonseed oil, animal fat, yellow and brown grease, lard, whale oil, milk fat, fish oil, algal oil, sewage sludge, cuphea oil, camelina oil, jatropha oil, curcas oil, babassu oil, palm kernel oil, cranbe oil, and others. Biorenewable is another term used to describe these feedstocks. Typical vegetable oils or animal fat glycerides, FFAs, and fatty acid alkyl esters contain aliphatic hydrocarbon chains with 8 to 24 carbon atoms in their structure, and in this case, the majority of the oil contains high concentrations of fatty acids with 16 and 18 carbon atoms. Mixtures or co-supplies of renewable feedstocks and fossil fuel-derived hydrocarbons can also be used as feedstocks. Other feedstock components that can be used as co-supplies in combination with the feedstocks listed above include used motor oils and industrial lubricants, used paraffin waxes, liquids obtained from downstream liquefaction processes such as Fischer-Tropsch technology following gasification of coal, biomass, or natural gas, liquids obtained from the thermal or chemical depolymerization of waste plastics such as polypropylene, high-density polyethylene, and low-density polyethylene, and other synthetic oils produced as by-products from petrochemical and chemical processes. Mixtures of the above feedstocks can also be used as co-supplies. One advantage of using co-supplies is that what has been considered waste from fossil fuel-based processes or other processes can be transformed into valuable co-supplies for current processes.In this alternative embodiment, the first feed stream in line 12 may be brought into contact with a multifunctional catalyst or set of catalysts having hydrogenation, deoxygenation, isomerization, and selective hydrocracking functions to produce a reaction distillate containing water, carbon oxides, light hydrocarbon gases, hydrogen, and paraffinic hydrocarbons. To produce a liquid stream containing paraffinic hydrocarbons, water, carbon oxides, light hydrocarbon gases, and hydrogen are separated from the reaction distillate.

[0032] As described above, a multifunctional catalyst or set of catalysts possesses deoxygenation, hydrogenation, isomerization, and selective hydrocracking functions. The deoxygenation and hydrogenation functions may be the same or separate active sites, and the catalyst complex may contain noble metals such as platinum group metals, for example, but not limited to ruthenium, rhodium, palladium, platinum, and mixtures thereof, at levels ranging from 0.05 to 2.0 wt%. Some catalysts may contain up to 10 wt% platinum or palladium on carbon. Examples of other active sites that may be used to provide deoxygenation and hydrogenation functions are base metal sulfides such as NiMo sulfide or NiW sulfide. Base metals are metals that oxidize when heated in air, and in addition to nickel, molybdenum, and tungsten, which may be catalyst components herein, other base metals include iron, lead, zinc, copper, tin, germanium, chromium, titanium, cobalt, rhenium, indium, gallium, uranium, dysprosium, thallium, and mixtures and compounds thereof. With respect to isomerization and selective hydrocracking functions, the second part of the catalyst complex may contain a zeolite having an acidic functional group capable of catalyzing isomerization and selective hydrocracking reactions. The zeolite concentration may range from 1 to 99% by weight of the catalyst complex, depending on the type of zeolite used and the operating conditions. In one embodiment, the zeolite has medium to large sized pores with 10 to 12 membered rings, such as BEA, MOR, MFI, or FAU. In other embodiments, the functional group is an amorphous acid moiety found in materials such as amorphous silica-alumina. In another embodiment, to maximize the accessibility of large triglyceride molecules to the catalytically active site, part of the support is 150 m 2It has a large external surface area greater than 1 / g, or large mesopores with an average pore diameter greater than 45 angstroms. The highly porous structure with large openings is beneficial because it reduces diffusion problems that can prevent large glyceride molecules from contacting the active site of the catalyst. Furthermore, the large pores hinder the diffusion resistance to the range-of-flight paraffins produced in this catalytic process, leading to further decomposition to lighter products with lower values. An example of a catalyst or catalyst set that successfully catalyzes deoxygenation, hydrogenation, isomerization, and selective hydrocracking reactions within the same reaction zone is platinum dispersed on a Y-zeolite-containing support. Another example is platinum and palladium on a Y-zeolite-containing support bonded to amorphous silica-alumina. Examples of catalyst sets include NiMo sulfide supported on amorphous silica-alumina and platinum supported on amorphous silica-alumina.

[0033] In this embodiment, the inlet temperature of the catalyst bed in the first reaction unit 10 may be in the range of 150°C to 454°C (300°F to 850°F), and the inlet pressure should be greater than 1379 kPa gauge to 13790 kPa gauge (200 to 2000 psig). The feed stream is mixed with enough hydrogen to provide a hydrogen circulation rate of 168 to 1684 nl / l (1000 to 10000 standard cubic feet / barrel, hereafter SCFB) and sent into the reactor containing the catalyst or set of catalysts. Hydrogen can be obtained mainly from a recirculated gas stream that can pass through a purification facility for removing acidic gases. Fresh hydrogen can also be delivered from the first electrolytic product stream. The hydrogen-rich gas mixed with the feed material and any recirculated stream containing hydrocarbons in one embodiment contain at least 90 mole percent hydrogen. The feed rate at liquid-space velocity (LHSV) is typically 0.3 to 5 hr -1 This is a wide range, and in one embodiment, an LHSV of less than 1.2 is used.

[0034] The first reaction unit 10 may generate multiple product streams after the reaction of the first feed stream. These may include a recirculated feed stream in line 15, a first reaction product stream in line 16, and a second reaction product stream in line 18. Additional streams may be generated. A light gas stream and / or a heavy olefin stream may be generated. The first reaction product stream in line 16 may contain olefins. The second reaction product stream in line 18 may contain water, preferably predominantly water. The second reaction product stream in line 18 may be sent to a surge tank 19 for sufficient product accumulation or for processing and / or purification before further processing.

[0035] If the first reaction unit includes ethanol dehydration, the first reaction product stream in line 16 may contain, or predominantly contain, ethylene. The first reaction product stream in line 16 may exit the first reaction unit 10 at a pressure of 317 kPa (gauge) (45 psig) to 630 kPa (gauge) (90 psig) or 345 kPa (gauge) (50 psig) to 414 kPa (gauge) (60 psig). The first reaction product stream may be compressed using one or more compression steps before further reaction in the second reaction unit 30. A first-stage compressor may compress the first reaction product stream to a first pressure of 350 kPa (gauge) (50 psig) to 1225 kPa (gauge) (175 psig). The second-stage compressor can compress the first reaction product flow to a second pressure of 455 kPa (gauge) (165 psig) to 3220 kPa (gauge) (460 psig). The third-stage compression can compress the first reaction product flow to a third pressure of 5.6 MPaG (800 psig) to 8.4 MPaG (1200 psig).

[0036] In one embodiment, a second reaction product stream containing water may be generated after one or more compression steps. Preferably, the second reaction product stream is in the liquid phase. The second reaction product stream in line 18 may be supplied to the electrolytic cell unit 20 by the electrolytic cell supply line 22, either directly or after passing through the surge tank 19. The electrolytic cell unit includes an electrolytic cell.

[0037] The electrolytic cell unit 20 may include an electrolytic cell catalyst. The electrolytic cell catalyst may include platinum (Pt). The electrolytic cell catalyst may include platinum supported on carbon. The amount of platinum supported on carbon is 0.1 mg / cm³. 2 ~1 mg / cm³ 2 The electrolytic cell feed stream containing water from the second reaction product stream may be further increased to include an alkaline aqueous solution. Potassium hydroxide (KOH) may be a preferred component of the electrolytic cell feed stream due to its high conductivity. Other electrolytes such as bicarbonates, sulfates, or chlorides (KHCO3, K2SO4, and KCl) may also be used. No electrolytes may be used. The concentration of KOH in the electrolytic cell feed stream may be in the range of 0.1M to 1.5M. The current density in the electrolytic cell unit 20 may be related to the concentration of KOH in the electrolytic cell anode reactant, with higher current densities being achieved at higher KOH concentrations. The concentration of KOH in the electrolytic cell feed stream may be in the range of 0.1M to 1.5M. A voltage of 1.5V to 5V may be applied between the anode and cathode in the electrolytic cell unit 20. Lower applied voltages are preferred. A voltage of less than 2V may be applied between the electrolytic cell anode and the electrolytic cell cathode.

[0038] The electrolytic cell 20 converts water into hydrogen and oxygen. The first electrolytic product stream in line 26 may contain hydrogen, preferably predominantly hydrogen. The first electrolytic product stream may contain more than 95% hydrogen, or more than 98% hydrogen, or more than 99% hydrogen. The first electrolytic product stream may contain nearly 100% hydrogen, for example, 99.9% hydrogen. In one embodiment, the first electrolytic product stream in line 26 is at a temperature of 40°C (104°F) to 120°C (248°F) and a pressure of 35 barg (508 psig) to 70 barg (1015 psig). The second electrolytic product stream in line 28 may contain oxygen. The second electrolytic product stream may predominantly contain oxygen. Oxygen is a valuable product and can be recovered for use as a feedstock for fuel cells for power generation, or for medical purposes or other industrial applications.

[0039] The method may further include reacting the first reaction product stream in line 16 in a second reaction unit 30 to produce a third reaction product stream in line 36 containing an olefin having a higher average molecular weight than the first reaction product stream in line 16. An exemplary method in the second reaction unit 30 includes one or more oligomerization steps on one or more oligomerization catalysts in an oligomerization unit under oligomerization conditions to provide the third reaction product stream in line 36 containing the olefin.

[0040] Oligomerization may involve dimerizing an olefin stream containing ethylene, followed by further oligomerization of the ethylene dimer and ethylene oligomer. The resulting oligomer can be separated to provide a distillate stream, which can then be saturated to provide a distillate fuel. The saturated stream can be recycled to the ethylene dimerization as a diluent to absorb the heat generated by dimerization and / or oligomerization. Furthermore, to manage the heat generation, the olefin stream in line 16 may be split and loaded into two or more catalyst beds. The dimerization products from the catalyst bed, which may contain unconverted olefins, are also sent to the downstream bed, thereby increasing the overall conversion rate per pass. In addition, the dimerization products from the upstream catalyst bed act as an additional diluent to absorb the heat generated in the downstream catalyst bed.

[0041] The feed stream for the second reaction unit in line 16 may contain a considerable amount of ethylene. The feed stream may predominantly contain ethylene. In one embodiment, the feed stream may contain at least 95 mol% ethylene.

[0042] The second reaction unit feed stream in line 16 may have a temperature of 60°C (140°F) to 190°C (374°F), preferably 100°C (212°F) to 170°C (338°F), and a pressure of 5.6 MPag (800 psig) to 8.4 MPag (1200 psig).

[0043] The second reaction unit 30 may include a dimerization reactor 32 and an oligomerization reactor 34. The dimerization reactor and the oligomerization reactor may be one reactor or multiple reactors. The feed stream of the second reaction unit may first come into contact with a dimerization catalyst to dimerize ethylene into a dimer, and then come into contact with an oligomerization catalyst to oligomerize the dimerized ethylene. The oligomerization catalyst may be placed upstream of the dimerization catalyst.

[0044] The dimerization reaction takes 0.5 to 10 hours based on olefins. -1 In LHSV, this can predominantly occur in the liquid phase or the gas-liquid mixed phase. The inventors have found that most of the ethylene in the olefin stream is converted to higher olefins. Typically, at least 90–95 mol% of the ethylene dimerizes throughout the dimerization catalyst bed. Ethylene first dimerizes on the catalyst to butene.

[0045] The dimerization catalyst may include a metal-supported catalyst. The dimerization catalyst is preferably an amorphous silica-alumina base having a metal from either Group VIII and / or Group VIB of the periodic table using Chemical Abstracts Service notation. In one embodiment, the catalyst has a Group VIII metal promoted by a Group VIB metal. Typically, since silica and alumina are present only in the base, the silica-to-alumina ratio is the same for both the catalyst and the base. The metal can be impregnated onto the silica-alumina base or ion-exchanged in the silica-alumina base. Co-mulling is also considered. The catalysts of the present invention may have a low-temperature acidity ratio of at least 0.15, preferably 0.2, and more preferably 0.25, as measured by Ammonia Temperature Programmed Desorption (ammonia TPD) as described below. In addition, preferred catalysts have a low-temperature acidity ratio of 50-400 m, as determined by the nitrogen BET method. 2 It has a surface area of ​​ / g.

[0046] Preferred dimerization catalysts are described below. Preferred dimerization catalysts include amorphous silica-alumina supports. One of the components of the catalyst support used in the present invention is alumina. The alumina can be any of various hydrated aluminum oxides or alumina gels, such as alpha-alumina monohydrate with a boehmite or pseudoboehmite structure, alpha-alumina trihydrate with a gibbsite structure, or beta-alumina trihydrate with a bayerite structure. Particularly preferred alumina is available from Sasol North America Alumina Product Group under the trademark Catapal. This material is extremely high-purity alpha-alumina monohydrate (pseudoboehmite) and has been shown to yield high-purity gamma-alumina after calcination at high temperatures. Another component of the catalyst support is amorphous silica-alumina. Preferred silica-alumina with a silica-to-alumina ratio of 2.6 is available, for example, from CCIC, a subsidiary of JGC in Japan.

[0047] Another component used in the preparation of the catalyst used in the present invention is a surfactant. The surfactant is preferably mixed with the above-mentioned alumina and silica-alumina powder. The resulting mixture of surfactant, alumina, and silica-alumina is then formed, dried, and calcined as described below. Calcination effectively removes the organic components of the surfactant by combustion, but only after the surfactant has faithfully performed its function according to the present invention. Any suitable surfactant can be used according to the present invention. Preferred surfactants are selected from a range of commercially available surfactants marketed by Solvay SA under the trademark "Antarox". "Antarox" surfactants are generally characterized as modified linear aliphatic polyethers and are low-foaming biodegradable detergents and wetting agents.

[0048] A suitable silica-alumina mixture is prepared by mixing proportional volumes of silica-alumina and alumina to achieve a desired silica-to-alumina ratio. In one embodiment, 75-95% by weight of amorphous silica-alumina and 10-20% by weight of alumina powder having a silica-to-alumina ratio of 2.6 provides a suitable carrier. In another embodiment, other ratios of amorphous silica-alumina to alumina may be preferred.

[0049] Any convenient method can be used to incorporate the surfactant into the mixture of silica-alumina and alumina. Preferably, the surfactant is mixed during the mixing and formation of alumina and silica-alumina. A preferred method is to mix an aqueous solution of the surfactant with the alumina and silica-alumina blend before the final formation of the support. Preferably, the surfactant is present in the paste or dough in an amount of 0.01 to 10% by weight, based on the weight of alumina and silica-alumina.

[0050] A monobasic acid such as nitric acid or formic acid may be added to the mixture in an aqueous solution to dissolve the alumina in the binder. Additional water may be added to the mixture to provide sufficient wettability to form a dough with sufficient viscosity for extrusion or spray drying.

[0051] The paste or dough may be prepared in the form of molded particles. A preferred method involves extruding a dough mixture of alumina, silica-alumina, a surfactant, and water through a die having an opening of the desired size and shape, then dividing the extruded material into extruders of the desired length and drying them. A further calcination step may be used to provide additional strength to the extruders. Generally, calcination is carried out in a stream of dry air at a temperature of 260°C (500°F) to 815°C (1500°F).

[0052] The extruded particles can have any suitable cross-sectional shape, i.e., symmetric or asymmetric, but in most cases, they have a symmetric cross-sectional shape, preferably spherical, cylindrical, or multi-lobed. The cross-sectional diameter of the particles can be as small as about 40 μm. However, it is usually from 0.635 mm (0.25 inch) to 12.7 mm (0.5 inch), preferably from 0.79 mm (1 / 32 inch) to 6.35 mm (0.25 inch), and most preferably from 0.06 mm (1 / 24 inch) to 4.23 mm (1 / 6 inch).

[0053] Typical properties of the amorphous silica-alumina carriers utilized herein are a total pore volume, an average pore diameter, and a surface area large enough to provide substantial space and area for depositing the active metal components. The total pore volume of the carrier measured by the conventional mercury porosimeter method is usually from 0.2 to 2.0 cc / gram, preferably from 0.25 to 1.0 cc / gram, and most preferably from 0.3 to 0.9 cc / gram. Usually, the amount of the pore volume of the carrier in pores with a diameter larger than 100 angstroms is less than 0.1 cc / gram, preferably less than 0.08 cc / gram, and most preferably less than 0.05 cc / gram. The surface area measured by the B.E.T. method is typically more than 50 m 2 / gram, for example, more than 200 m 2 / gram, preferably at least 250 m 2 / gram, and most preferably from 300 m 2 gram to 400 m 2 / gram.

[0054] To prepare the catalyst, the carrier material is compounded with one or more precursors of at least one metal component from Group VIII or Group VIB of the periodic table, such as by single or multiple impregnation of calcined amorphous refractory oxide carrier particles. The Group VIII metal, preferably nickel, must be present at a concentration of 0.5 to 15% by weight, and the Group VIB metal, preferably tungsten, must be present at a concentration of 0 to 12% by weight. Impregnation can be achieved by any method known in the art, for example, by spray impregnation, in which a solution containing the metal precursor in a dissolved form is sprayed onto the carrier particles. Another method is a multi-dip procedure, in which the carrier material is repeatedly brought into contact with the impregnation solution with or without intermittent drying. Yet another method includes immersing the carrier in a large volume of impregnation solution or circulating the carrier therein, and yet another method is a pore volume or pore saturation technique, in which the carrier particles are introduced into an impregnation solution of just enough volume to fill the pores of the carrier. In some cases, the pore saturation technique may be modified to utilize an impregnation solution having a volume between 10 percent less and 10 percent more than the volume required to just fill the pores.

[0055] When the active metal precursor is incorporated by impregnation, the metal is converted to its respective oxide form by subsequent or second calcination at a high temperature, for example, 399°C (750°F) to 760°C (1400°F). In some cases, calcination may be performed after each impregnation of the individual active metals. Subsequent calcination yields a catalyst containing the active metals in their respective oxide forms.

[0056] A preferred dimerization catalyst of the present invention is an amorphous silica-alumina substrate impregnated with 0.5 to 15 wt% nickel in the form of a 3.175 mm (0.125 inch) extruded material, having a density of 0.45 to 0.65 g / mL. The metal may also be incorporated onto the support by other methods such as ion exchange and co-mulling.

[0057] The dimerization catalyst can be regenerated when deactivated. Preferred regeneration conditions include, for example, exposing the catalyst to hot air at 500°C for 3 hours in situ. To promote regeneration without downtime, a swing bed arrangement may be used with an alternative dimerization reactor. The regeneration gas may contain air with increased or decreased oxygen concentration. The activity and selectivity of the regenerated catalyst are comparable to those of a fresh catalyst.

[0058] To control heat generation, the feed stream in line 16 may be diluted by a diluent stream to provide a diluted olefin stream to aid in heat absorption. The diluent stream may include a paraffin stream in diluent line 58. The first diluted olefin stream may contain 25% by weight or less of olefin, preferably 10% by weight or less of olefin, and more preferably 6% by weight or less of olefin. The first diluted olefin stream may contain 25% by weight or less of ethylene, preferably 10% by weight or less of ethylene, and more preferably 6% by weight or less of ethylene. A dimerization stream may be generated in line 33.

[0059] The second reaction unit 30 may further include an oligomerization reactor 34.

[0060] The oligomerization reactor 34 can be downstream-communicated with the dimerization reactor 32 by line 33. Alternatively, the oligomerization reactor 34 can be upstream-communicated with the dimerization reactor 32. The oligomerization reactor 34 preferably operates in a downward flow operation. However, an upward flow operation may be preferable. The input oligomerization stream is brought into contact with the oligomerization catalyst to dimerize and trimerize C2-C8 olefins to provide olefins in the distillate range. Most of the butene in the input oligomerization stream is oligomerized. In the embodiment, at least 99 mol% of the butene in the input oligomerization stream is oligomerized. The third reaction product stream in line 36, which has a higher average carbon number than the second reaction unit feed stream in line 16, exits the oligomerization reactor 34 and the second reaction unit 30 in line 36.

[0061] The oligomerization catalyst may include a zeolite catalyst. The zeolite may constitute 5 to 95% by weight, for example, 5 to 85% by weight, of the catalyst. Preferred zeolites include those having structures from one of the following classes: MFI, MEL, ITH, IMF, TUN, FER, BEA, FAU, BPH, MEI, MSE, MWW, UZM-8, MOR, OFF, MTW, TON, MTT, AFO, ATO, and AEL. The three-letter codes indicating the zeotype are as defined by the Structure Commission of the International Zeolite Association and are managed at http: / / www.iza-structure.org / databases. UZM-8 is as described in U.S. Patent No. 6,756,030. In a preferred embodiment, the oligomerization catalyst may include a zeolite having a skeleton with a 10-membered ring pore structure. Examples of suitable zeolites having a 10-membered ring pore structure include TON, MTT, MFI, MEL, AFO, AEL, EUO, and FER. In a more preferred embodiment, the oligomerization catalyst comprising a zeolite having a 10-membered ring pore structure may include a one-dimensional pore structure. The one-dimensional pore structure represents a zeolite containing non-crossing pores substantially parallel to one of the crystal axes. The pores preferably extend through the zeolite crystal. A suitable example of a zeolite having a 10-membered ring one-dimensional pore structure is MTT. In a further embodiment, the oligomerization catalyst comprises an MTT zeolite.

[0062] Oligomerized catalysts can be formed by combining zeolite with a binder and then molding the catalyst into pellets. The pellets can be optionally treated with a phosphorus reagent to produce zeolites having 0.5–15% by weight of phosphorus components of the treated catalyst. Binders are used to impart hardness and strength to the catalyst. Examples of binders include alumina, aluminum phosphate, silica, silica-alumina, zirconia, titania, and combinations of these metal oxides, as well as other refractory oxides, and clays such as montmorillonite, kaolin, palygorskite, smectite, and attapulgite. Preferred binders are aluminum-based binders such as alumina, aluminum phosphate, silica-alumina, and clays.

[0063] One of the components of the catalyst binder used in the present invention is alumina. The alumina source can be any of various hydrated aluminum oxides or alumina gels, such as alpha-alumina monohydrate with a boehmite or pseudo-boehmite structure, alpha-alumina trihydrate with a gibbsite structure, or beta-alumina trihydrate with a bayerite structure. Preferred alumina is available from UOP LLC under the trademark VERSAL. Preferred alumina is available from Sasol North America Alumina Product Group under the trademark Catapal. This material is extremely high-purity alpha-alumina monohydrate (pseudo-boehmite) and has been shown to yield high-purity gamma-alumina after calcination at high temperatures.

[0064] A suitable oligomerized catalyst is prepared by mixing proportional volumes of zeolite and alumina to achieve the desired zeolite-to-alumina ratio. In one embodiment, the MTT content may be 5-85% by weight, for example, 20-82% by weight of MTT zeolite, with the remaining alumina powder providing a suitably supported catalyst. Silica supports are also considered.

[0065] A monobasic acid such as nitric acid or formic acid may be added to the mixture in an aqueous solution to dissolve the alumina in the binder. Additional water may be added to the mixture to provide sufficient wettability to form a dough with sufficient viscosity for extrusion or spray drying. Extrusion aids such as cellulose ether powder may also be added. Preferred extrusion aids are available from The Dow Chemical Company under the trademark Methocel.

[0066] The paste or dough may be prepared in the form of molded particles, a preferred method of which is to extrude the dough through a die having an opening of the desired size and shape, and then divide the extruded material into extruders of the desired length and dry them. Further calcination steps may be used to provide additional strength to the extruders. Generally, calcination is carried out in an airflow at temperatures of 260°C (500°F) to 815°C (1500°F). The MTT catalyst does not have the selectivity to neutralize acidic sites such as amines.

[0067] Extruded particles may have any suitable cross-sectional shape, i.e., symmetric or asymmetric, but in most cases they have a symmetrical cross-sectional shape, preferably spherical, cylindrical, or multi-lobed. The cross-sectional diameter of the particles can be as small as about 40 μm. However, it is usually 0.635 mm (0.25 inches) to 12.7 mm (0.5 inches), preferably 0.79 mm (1 / 32 inch) to 6.35 mm (0.25 inches), and most preferably 0.06 mm (1 / 24 inch) to 4.23 mm (1 / 6 inch).

[0068] The oligomerization reactor 32 may be operated at temperatures ranging from 180°C (356°F) to 260°C (500°F). The oligomerization reactor in the second reaction unit 30 may be operated at pressures ranging from 2.1 MPa (300 psig) to 8.4 MPaG (1200 psig), more preferably 4.9 MPa (710 psig) to 7.6 MPa (1100 psig) or 5.6 MPaG (800 psig) to 6.9 MPa (1000 psig).

[0069] When the oligomerization reaction in the second reaction unit 30 is carried out according to the above process conditions, a C4 olefin conversion rate of 95% or more or 97% or more is achieved. The resulting third reaction product stream in line 36 may contain an olefin and multiple olefin products which are hydrocarbons in the distillate range.

[0070] The oligomerized catalyst can be regenerated when deactivated. Preferred regeneration conditions include, for example, exposing the oligomerized catalyst to hot air at 500°C for 3 hours in situ. To promote regeneration without downtime, a rocking bed configuration may be used with an alternative oligomerization reactor. A regeneration gas stream may be introduced into the oligomerization reactor in a second reactor unit 30 that requires regeneration. The regeneration gas may contain air with increased or decreased oxygen concentration. The activity and selectivity of the regenerated catalyst are comparable to that of a fresh catalyst.

[0071] The third reaction product stream in line 36 may be separated in an optional separation unit 40 to supply the hydrogenation unit 50 with distillates or products within a specific boiling point range, such as gasoline or jet fuel, as a second hydrogenation feed stream in line 52. Multiple streams may be generated, some of which may be discharged from the process or recycled within the process. In a preferred embodiment, the second hydrogenation feed stream in line 52 mainly consists of distillates. Alternatively, the third reaction product stream in line 36 may be supplied directly to the hydrogenation unit 50 as a second hydrogenation feed stream in line 52.

[0072] A first hydrogenation feed stream, including the first electrolytic cell product stream from line 26, is supplied to the hydrogenation unit 50. In a preferred embodiment, the first electrolytic cell product stream may be supplied to the hydrogenation unit 50 without changing the flow temperature or pressure. A second hydrogenation feed stream, including olefins, from line 52 is also supplied to the hydrogenation unit 50. In one embodiment, the second hydrogenation feed stream and the first electrolytic cell product stream may originate from the first feed stream in line 12. The hydrogenation unit 50 may be downstream-communicated with the first reaction unit 10 and the electrolytic cell unit 20.

[0073] The hydrogenation unit 50 performs the hydrogenation of olefins to paraffins. Hydrogenation is typically carried out using conventional hydrogenation or hydrogenation catalysts, which may include, for example, metal catalysts containing palladium, rhodium, nickel, ruthenium, platinum, rhenium, cobalt, molybdenum, or combinations thereof, and supported metal catalysts thereof. The catalyst support may be any solid inert substance, including but not limited to oxides such as silica, alumina, titania, calcium carbonate, barium sulfate, and carbon. The catalyst support may be in the form of powder, granules, pellets, etc.

[0074] In exemplary embodiments, hydrogenation is carried out in a hydrogenation reactor 50 containing an alumina-supported platinum catalyst, for example, 0.5% to 0.9% by weight of the alumina-supported platinum catalyst. The hydrogenation reactor converts the olefin into a paraffin product having the same carbon number distribution as the olefin, thereby forming a distillate range paraffin suitable for use as jet fuel and diesel fuel. Excess hydrogen, such as 1.5 to 2.5 stoichiometric hydrogens, can be used to ensure complete saturation.

[0075] The hydrogenation reaction conditions may include temperatures of 100°C to 300°C, 150°C to 250°C, or 165°C to 200°C. The hydrogenation reaction conditions may also include pressures of 400 psig to 800 psig or 500 psig to 700 psig, and space velocity per hour (WHSV) of 1 to 5, 1.8 to 4.2, or 2 to 3. The hydrogenation reaction conditions may further include a hydrogen-to-olefin molar ratio of 1 to 5, 1.5 to 4, or 2 to 3.

[0076] The hydrogenation unit 50 generates a hydrogenation product stream containing paraffin in line 56. A portion of this hydrogenation product stream can be separated and used as a diluent stream in line 58, and can be supplied to a second reaction unit 30 to help control exothermic reactions or can be recycled within the hydrogenation unit 50. In one embodiment, the olefin content in the second mixed hydrogenation feed stream in line 55 may be 5% to 50%, 6% to 30%, or 7% to 20% by weight.

[0077] The disclosed process can efficiently produce green jet fuel and green diesel fuel that meet applicable fuel requirements, starting from ethanol. The carbon recovery rate in the process can exceed 95%. The hydrogen used to produce paraffin that meets SPK standards is generated by the electrolysis of water produced in the first reaction unit.

[0078] Specific Embodiments The following will be explained in conjunction with specific embodiments, but it should be understood that this explanation is intended to illustrate the scope of the preceding explanation and the attached claims, and is not intended to limit them.

[0079] A first aspect of the present invention is a method for hydrogenating an olefin, comprising: providing a first feed stream containing an oxygen-containing hydrocarbon to a first reaction unit; reacting the first feed stream to produce a first reaction product stream containing an olefin and a second reaction product stream containing water; electrolyzing the second reaction product stream to produce an electrolytic cell product stream containing hydrogen; providing a first hydrogenation feed stream containing hydrogen and a second hydrogenation feed stream containing an olefin to a hydrogenation unit; and hydrogenating the second hydrogenation feed stream on a hydrogenation catalyst under hydrogenation reaction conditions in the presence of the first hydrogenation feed stream to form a hydrogenation product stream containing paraffin, wherein the first hydrogenation feed stream and the second hydrogenation feed stream are obtained from the first feed stream. One embodiment of the present invention is one or all of the embodiments described above to the first embodiment of this paragraph, wherein the first feed stream contains ethanol. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the first embodiment of this paragraph, wherein the first feed stream comprises a triglyceride. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the first embodiment of this paragraph, wherein the first reaction unit comprises dehydration from an alcohol to an olefin under dehydration reaction conditions. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the first embodiment of this paragraph, wherein the dehydration reaction conditions include a temperature of 400°C to 550°C and a pressure of 317 kPa (gauge) (45 psig) to 2068 kPa (300 psig). One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the first embodiment of this paragraph, wherein the catalyst comprises gamma alumina. One embodiment of the present invention is one or all of the embodiments described earlier in this paragraph to the first embodiment of this paragraph, wherein the electrolytic cell product stream contains more than 95% hydrogen at a pressure of 35 barg (508 psig) to 70 barg (1015 psig). One embodiment of the present invention is one or all of the embodiments described earlier in this paragraph to the first embodiment of this paragraph, further comprising compressing the electrolytic cell product stream to hydrogenation reaction conditions.

[0080] A second aspect of the present invention is a method for hydrogenating an olefin, comprising: providing a first feed stream containing an oxygen-containing hydrocarbon to a first reaction unit; reacting the first feed stream to produce a first reaction product stream containing an olefin and a second reaction product stream containing water; electrolyzing the second reaction product stream to produce an electrolytic cell product stream containing hydrogen; providing a first hydrogenation feed stream containing the electrolytic cell product stream and a second hydrogenation feed stream containing the first reaction product stream to a hydrogenation unit; and hydrogenating the second hydrogenation feed stream on a hydrogenation catalyst under hydrogenation reaction conditions in the presence of the first hydrogenation feed stream to form a hydrogenation product stream containing paraffin. One embodiment of the present invention is one, any, or all of the embodiments described in the preceding paragraph to the second embodiment of this paragraph, wherein the first feed stream contains ethanol. One embodiment of the present invention is one, any, or all of the embodiments described in the preceding paragraph to the second embodiment of this paragraph, wherein the first feed stream contains a triglyceride. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the second embodiment of this paragraph, wherein the first reaction unit includes dehydration from alcohol to olefin under dehydration reaction conditions. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the second embodiment of this paragraph, wherein the dehydration reaction conditions include a temperature of 400°C to 550°C and a pressure of 317 kPa (gauge) (45 psig) to 2068 kPa (300 psig). One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the second embodiment of this paragraph, wherein the catalyst includes gamma alumina. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the second embodiment of this paragraph, wherein the electrolytic cell product stream contains more than 95% hydrogen at a temperature of 40°C (104°F) to 120°C (248°F). One embodiment of the present invention is one, any, or all of the embodiments described in the preceding paragraph to the second embodiment described in this paragraph, further comprising compressing the electrolytic cell product stream to hydrogenation reaction conditions.

[0081] A third aspect of the present invention is a method for hydrogenating an olefin, comprising: providing a first feed stream containing an oxygen-containing hydrocarbon to a first reaction unit; reacting the first feed stream to produce a first reaction product stream containing an olefin and a second reaction product stream containing water; electrolyzing the second reaction product stream to produce an electrolytic cell product stream containing hydrogen; reacting the first reaction product stream on an oligomerization catalyst in an oligomerization unit under oligomerization conditions to provide a third reaction product stream containing an olefin; providing a first hydrogenation feed stream containing hydrogen and a second hydrogenation feed stream containing an olefin to a hydrogenation unit; and hydrogenating the second hydrogenation feed stream on a hydrogenation catalyst under hydrogenation reaction conditions to form a hydrogenation product stream containing paraffin, wherein the first hydrogenation feed stream and the second hydrogenation feed stream are obtained from the first feed stream, and the first hydrogenation feed stream contains an electrolytic cell product stream. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the third embodiment of this paragraph, wherein the oligomerization reaction conditions include a temperature of 100°C to 260°C and a pressure of 2.1 MPa to 8.4 MPa. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the third embodiment of this paragraph, wherein the oligomerization catalyst includes a zeolite or metal-supported catalyst having a 10-membered ring one-dimensional pore structure. One embodiment of the present invention is one or all of the embodiments described in the preceding paragraph to the third embodiment of this paragraph, wherein the second hydrogenation feed stream includes a third reaction product stream.

[0082] Without further detail, it is expected that those skilled in the art will be able to utilize the invention to the fullest extent without departing from the spirit and scope of the invention, and will readily identify its essential characteristics, and will be able to make various changes and modifications to the invention to suit various uses and conditions. Accordingly, the prior preferred specific embodiments should be interpreted as merely illustrative and not to limit the remainder of this disclosure in any way, but are intended to cover various modifications and equivalent configurations that fall within the scope of the appended claims.

[0083] In the above, all temperatures are given in degrees Celsius, and all parts and percentages are based on weight unless otherwise indicated.

Claims

1. A method for hydrogenating olefins, To supply a first feed stream containing oxygenated hydrocarbons to a first reaction unit, The first supply stream is reacted to produce a first reaction product stream containing olefins and a second reaction product stream containing water, The second reaction product stream is electrolyzed to produce an electrolytic cell product stream containing hydrogen, The hydrogenation unit is provided with a first hydrogenation supply stream containing hydrogen and a second hydrogenation supply stream containing olefin, In the presence of the first hydrogenation feed stream, under hydrogenation reaction conditions, the second hydrogenation feed stream is hydrogenated on the hydrogenation catalyst to form a hydrogenation product stream containing paraffin, Includes, A method wherein the first hydrogenation feed stream and the second hydrogenation feed stream are obtained from the first feed stream.

2. A method for hydrogenating olefins, A first feed stream containing oxygenated hydrocarbons is supplied to the first reaction unit, The first supply stream is reacted to produce a first reaction product stream containing olefins and a second reaction product stream containing water, The second reaction product stream is electrolyzed to produce an electrolytic cell product stream containing hydrogen, A first hydrogenation supply stream containing the electrolytic cell product stream and a second hydrogenation supply stream containing the first reaction product stream are supplied to the hydrogenation unit. Under hydrogenation reaction conditions in the presence of the first hydrogenation feed stream, the second hydrogenation feed stream is hydrogenated on a hydrogenation catalyst to form a hydrogenation product stream containing paraffin, Methods that include...

3. A method for hydrogenating olefins, A first feed stream containing oxygenated hydrocarbons is supplied to the first reaction unit, The first supply stream is reacted to produce a first reaction product stream containing olefins and a second reaction product stream containing water, The second reaction product stream is electrolyzed to produce an electrolytic cell product stream containing hydrogen, The first reaction product stream is reacted on an oligomerization catalyst in an oligomerization unit under oligomerization conditions to provide a third reaction product stream containing an olefin. A first hydrogenation supply stream containing hydrogen and a second hydrogenation supply stream containing olefin are supplied to the hydrogenation unit. The process includes hydrogenating the second hydrogenation feed stream on a hydrogenation catalyst under hydrogenation reaction conditions to form a hydrogenation product stream containing paraffin, A method comprising the first hydrogenation feed stream and the second hydrogenation feed stream being obtained from the first feed stream, wherein the first hydrogenation feed stream includes the electrolytic cell product stream.