Solid depilatory wax and preparation method thereof

Abstract

The present invention discloses a solid depilatory wax and a preparation method thereof, relating to the technical field of depilatory wax. The solid depilatory wax comprises the following raw material components by mass fraction: 30-70% natural resin, 5-20% fatty alcohol, 3-20% natural wax, 2-10% tackifier, 0.2-5% natural plant oil, 0.2-5% anti-inflammatory, soothing and repairing agent, 0.2-3% skin conditioner, 0.2-3% antioxidant, and 0.2-2% stabilizer; wherein the tackifier is selected from at least one of polyisobutylene, hydrogenated polydicyclopentadiene, hydrogenated (styrene / methylstyrene / indene) copolymer, and hydrogenated (styrene / butadiene) copolymer; and the anti-inflammatory, soothing and repairing agent comprises component A and component B, wherein component A is guaiacyl ether, and component B is peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract, and scutellaria baicalensis extract. The depilatory wax provided by the present invention has a low melting point and a good depilatory effect, and can improve the damaged skin barrier function caused by hair plucking, thereby preventing skin or skin follicle inflammation caused by hair removal.

Description

Technical Field

[0001] The invention relates to the technical field of depilatory wax, in particular to solid depilatory wax and a preparation method thereof. Background Art

[0002] With the continuous development of society and the improvement of living standards, people pay more and more attention to their own image, especially women in the process of social interaction, who need to remove excess hair on certain parts of the body. At present, the main methods of human hair removal are laser hair removal, physical hair removal and chemical hair removal.

[0003] Laser hair removal requires high technical skills and is not effective for melanin-deficient hair growth cycles. It also poses a safety risk of damaging the skin on darker skin and areas with heavy pigmentation. Chemical hair removal uses chemical reactions to soften hair quickly, allowing it to be easily removed, but it cannot remove hair from the root. Long-term use can cause hair coarsening, pigmentation, skin allergies, and roughness. Physical hair removal includes epilators and waxing. Epilators cut hair on the surface, but when hair regrows, it grows thicker and denser, affecting appearance. Waxing uses the stickiness of wax or polymers to remove hair. It is suitable for large-area hair removal and primarily uses cold or hot wax. Cold waxing is expensive and ineffective. Currently available hot wax has a high melting point and can easily cause burns if not used properly. Hair is also removed along with the wax, causing damage to the skin's stratum corneum and inflammation. Summary of the Invention

[0004] The main purpose of the present invention is to provide a solid depilatory wax and a preparation method thereof, aiming to solve the problems that the melting point of existing depilatory wax is too high, it is easy to burn, and it is easy to cause skin inflammation during depilation.

[0005] To achieve the above object, the present invention provides a solid depilatory wax and a preparation method thereof, wherein the solid depilatory wax comprises the following raw material components in mass fractions:

[0006] Natural resin 30-70%, fatty alcohol 5-20%, natural wax 3-20%, tackifier 2-10%, natural plant oil 0.2-5%, anti-inflammatory soothing repair agent 0.2-5%, skin conditioning agent 0.2-3%, antioxidant 0.2-3%, stabilizer 0.2-2%;

[0007] wherein the tackifier is selected from at least one of polyisobutylene, hydrogenated polydicyclopentadiene, hydrogenated (styrene / methylstyrene / indene) copolymer and hydrogenated (styrene / butadiene) copolymer;

[0008] The anti-inflammatory, soothing and repairing agent comprises component A and component B, wherein the component A is guaiacyl ether, and the component B is peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract.

[0009] Preferably, the mass ratio of component A to component B is 1-2:2-5.

[0010] Preferably, the natural resin is selected from at least one of masson pine resin, Yunnan pine resin, Chinese pine resin, wetland pine resin, Simao pine resin, torch pine resin and rubber tree resin.

[0011] Preferably, the fatty alcohol is selected from at least one of coconut alcohol, myristyl alcohol, cetyl alcohol, stearyl alcohol and cetearyl alcohol.

[0012] Preferably, the natural wax is selected from at least one of palm wax, rice bran wax, candelilla wax, sunflower wax, sumac wax and beeswax.

[0013] Preferably, the natural vegetable oil is selected from at least one of camellia seed oil, Yunnan camellia seed oil, jojoba seed oil, coconut oil, wheat germ oil and macadamia seed oil.

[0014] Preferably, the skin conditioning agent is selected from at least one of C30-45 alkyl dimethicone, shea butter and cyclopentasiloxane.

[0015] Preferably, the antioxidant is selected from at least two of tocopheryl acetate, butylated hydroxytoluene, butylated hydroxyanisole, ascorbyl palmitate, monoglyceride citrate, nordihydroguaiaretic acid and ergothioneine.

[0016] Preferably, the stabilizer is selected from at least one of titanium dioxide, zinc oxide, silicon dioxide and mica powder.

[0017] The present invention also provides a method for preparing the solid depilatory wax as described above, the method comprising the following steps:

[0018] (1) heating and dissolving a fatty alcohol, a tackifier, a natural wax, and a natural resin at 105 to 115° C. under stirring to obtain a mixture;

[0019] (2) Cooling the mixture to 95-100° C., then adding natural plant oil, antioxidant, anti-inflammatory soothing and repairing agent, skin conditioner and stabilizer under stirring, followed by granulation to obtain solid depilatory wax.

[0020] In the technical solution provided by the present invention, through the reasonable design of various raw material components, the solid depilatory wax has a low melting point, is not easy to burn the skin, and is safe and reliable; at the same time, the solidification and dripping temperatures of the depilatory wax are similar, so that the wax liquid does not drip and can quickly solidify, and has good skin adhesion. After the wax is applied, a wax film can be formed on the skin and hair, and the wax film is in close contact with the hair, with strong adhesion, and no empty shell is formed between the two, thereby achieving a good depilatory effect and a high depilatory rate; in addition, through the addition of an anti-inflammatory soothing and repairing agent, the solid depilatory wax can relieve pain and inflammation, enhance skin immunity, and has the effect of soothing and repairing the skin barrier function damaged and microvascular dilation caused by depilation. DETAILED DESCRIPTION

[0021] To make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention are described clearly and completely below. Where specific conditions are not specified in the embodiments, conventional conditions or conditions recommended by the manufacturer are used. Where the manufacturer of the reagents or instruments is not specified, all are conventional products that can be purchased commercially.

[0022] It should be noted that, in the embodiments, those without specifying specific conditions are carried out according to conventional conditions or the conditions recommended by the manufacturer. Reagents used or instruments without specifying manufacturers are conventional products that can be purchased commercially. In addition, the technical solutions between the various embodiments can be combined with each other, but must be based on those of ordinary skill in the art being able to realize the basis. When the combination of the technical solutions is mutually contradictory or cannot be realized, it should be considered that the combination of such technical solutions does not exist, nor is it within the scope of protection claimed in the present invention. Based on the embodiments in the present invention, all other embodiments obtained by those of ordinary skill in the art without making creative work premise belong to the scope of protection of the present invention.

[0023] The present invention provides a solid depilatory wax and a preparation method thereof, aiming to provide a depilatory wax with a low melting point, analgesic, irritation-relieving, anti-allergic, and anti-inflammatory effects, while also improving the skin's resistance to irritation, reducing skin inflammation caused by depilation, and repairing damaged skin and stratum corneum wounds. In one embodiment, the solid depilatory wax comprises the following raw material components by mass fraction: 30-70% natural resin, 5-20% fatty alcohol, 3-20% natural wax, 2-10% tackifier, 0.2-5% natural plant oil, 0.2-5% anti-inflammatory, soothing, and repairing agent, 0.2-3% skin conditioner, 0.2-3% antioxidant, and 0.2-2% stabilizer.

[0024] The thickener is selected from at least one of polyisobutylene, hydrogenated polydicyclopentadiene, hydrogenated (styrene / methylstyrene / indene) copolymer and hydrogenated (styrene / butadiene) copolymer. By selecting the above-mentioned thickener, the wax film has a strong adhesion to the skin and hair, thereby achieving a good depilatory effect and a high depilatory rate.

[0025] In the present invention, the anti-inflammatory soothing and repairing agent comprises component A and component B, wherein component A is guaiacyl guanidine, and component B is peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract.

[0026] Guaichuansu has anti-inflammatory and soothing effects; Mentha Haplocalyx oil can dispel wind-heat, calm itching; Portulaca Oleracea extract inhibits the activity of nitric oxide synthase, thereby inhibiting the intracellular nitric oxide response triggered by lipopolysaccharide, preventing the production of inflammatory factors, and achieving significant anti-inflammatory, anti-irritation and soothing effects; Golden Chamomile (Chrysanthellum Indicum) extract has a good soothing effect on the skin, repairs sensitive skin, reduces fine red blood vessels, and reduces redness; Houttuynia Cordata extract contains flavonoids such as quercetin, quercetin and rutin, among which quercetin has the highest content and has anti-inflammatory and anti-allergic effects; Scutellaria baicalensis extract contains a large amount of baicalin, which can be anti-inflammatory, soothing and antibacterial. The present invention uses the above six ingredients in combination to synergistically improve the analgesic and anti-inflammatory effects of depilatory wax, enhance skin immunity, and repair skin barrier. The lack of any of the above components will lead to a significant decrease in its anti-inflammatory and soothing effects.

[0027] In the present invention, the melting point of the depilatory wax is low through the synergistic combination of natural resin, fatty alcohol, natural wax and tackifier, and no high temperature pain is felt after being applied to the skin; at the same time, the solidification and dripping temperatures of the depilatory wax are similar, so that the wax liquid will not drip after being applied to the skin and hair, and has good skin adhesion, can quickly form a wax film on the surface of the skin and hair, and the wax film has good adhesion to the hair, thereby achieving a good depilation effect and a high depilation rate.

[0028] The present invention does not limit the addition amounts of component A and component B. In a preferred embodiment, the mass ratio of component A to component B is 1-2:2-5. Further preferably, the mass ratio of the peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract, and scutellaria baicalensis extract is 1:1:1:1:1-2.

[0029] In the present invention, the natural resin is a plant-derived resin, which serves as a thickener. The natural resin may be a pine resin and / or a rubber tree resin. In a specific embodiment, the natural resin is selected from at least one of masson pine pine, Yunnan pine pine, Chinese pine pine, elliott pine, Simao pine, torch pine pine, and rubber tree resin, preferably masson pine pine and rubber tree resin.

[0030] The present invention does not limit the specific type of the fatty alcohol. Preferably, the fatty alcohol is selected from at least one of coconut alcohol, myristyl alcohol, cetyl alcohol, stearyl alcohol and cetearyl alcohol.

[0031] In this embodiment, the natural wax is selected from at least one of palm wax, rice bran wax, candelilla wax, sunflower wax, sumac wax and beeswax. By selecting the above natural waxes, the melting point of the depilatory wax is lowered.

[0032] In order to make the skin moist and slippery after applying the depilatory wax, in this embodiment, the natural plant oil is selected from at least one of camellia (CAMELLIA JAPONICA) seed oil, Yunnan camellia (CAMELLIA RETICULATA) seed oil, jojoba (SIMMONDSIA CHINENSIS) seed oil, coconut (COCOS NUCIFERA) oil, wheat (TRITICUM VULGARE) germ oil and macadamia (MACADAMIA TERNIFOLIA) seed oil.

[0033] In order to further improve the water-locking and moisturizing effect of the skin, in this embodiment, the skin conditioning agent is selected from at least one of C30-45 alkyl polydimethylsiloxane, shea butter and cyclopentasiloxane.

[0034] In this embodiment, the antioxidant is selected from at least two of tocopheryl acetate, butylated hydroxytoluene, butylated hydroxyanisole, ascorbyl palmitate, monoglyceride citrate, nordihydroguaiaretic acid and ergothioneine, so that the depilatory wax has excellent antioxidant effect.

[0035] In this embodiment, the stabilizer is selected from at least one of titanium dioxide, zinc oxide, silicon dioxide and mica powder. By selecting the above stabilizer, factors such as irritation and allergy of the depilatory wax to the skin can be reduced.

[0036] In the present invention, by adding an anti-inflammatory soothing and repairing agent, the solid depilatory wax can relieve pain and inflammation, enhance skin immunity, and soothe and repair the skin barrier function damaged and microvascular dilation caused by hair plucking; by the combined use of anti-inflammatory soothing and repairing agent, natural plant oil and skin conditioner, the anti-inflammatory and soothing effect is further improved, so that the depilatory wax has excellent moisturizing, anti-inflammatory and soothing effects, thereby effectively preventing the skin (or skin follicle) from drying, redness or inflammation after hair removal.

[0037] The present invention also provides a method for preparing the solid depilatory wax as described above. In one embodiment, the method comprises the following steps:

[0038] (1) heating and dissolving a fatty alcohol, a tackifier, a natural wax, and a natural resin at 105 to 115° C. under stirring to obtain a mixture;

[0039] (2) Cooling the mixture to 95-100° C., then adding natural plant oil, antioxidant, anti-inflammatory soothing and repairing agent, skin conditioner and stabilizer under stirring, followed by granulation to obtain solid depilatory wax.

[0040] During specific implementation, in step (1), the stirring speed is 10 to 30 r / min; and / or, in step (2), the stirring speed is 10 to 30 r / min.

[0041] The technical solutions of the present invention are further described in detail below in conjunction with specific embodiments. It should be understood that the following embodiments are only used to explain the present invention and are not used to limit the present invention.

[0042] Example 1

[0043] The solid depilatory wax comprises the following raw material components by mass fraction:

[0044] 55% natural resin, the natural resin is a mixture of masson pine gum and rubber tree resin in a mass ratio of 1:1,

[0045] 15% natural wax, the natural wax is a mixture of palm wax and rice bran wax in a mass ratio of 3:1,

[0046] Fatty alcohol 15%, wherein the fatty alcohol is myristyl alcohol,

[0047] 5% tackifier, wherein the tackifier is polyisobutylene,

[0048] 3% natural vegetable oil, wherein the natural vegetable oil is a mixture of camellia seed oil and coconut oil in a mass ratio of 2:1,

[0049] 3% anti-inflammatory soothing repair agent, the anti-inflammatory soothing repair agent is a mixture of guaiacyl ether and component B in a mass ratio of 1:5, and component B is a mixture of peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract in a mass ratio of 1:1:1:1:2,

[0050] Skin conditioning agent 2%, the skin conditioning agent is C30-45 alkyl polydimethylsiloxane,

[0051] 1% antioxidant, wherein the antioxidant is a mixture of tocopherol acetate and butylated hydroxytoluene in a mass ratio of 2:3,

[0052] 1% stabilizer, wherein the stabilizer is a mixture of titanium dioxide and mica powder in a mass ratio of 5:1;

[0053] Wherein, the preparation method of the solid depilatory wax comprises the following steps:

[0054] (1) heating the fatty alcohol, tackifier, natural wax, and natural resin to 110° C. under stirring (at a speed of 20 r / min) until all of them are dissolved to obtain a mixture;

[0055] (2) The mixture is cooled to 100° C., and then natural vegetable oil, antioxidant, anti-inflammatory soothing repair agent, skin conditioner and stabilizer are added under stirring (rotation speed of 20 r / min), and then sent to a drum granulator for granulation. After passing the inspection, the mixture is packaged to obtain solid depilatory wax.

[0056] Example 2

[0057] The solid depilatory wax comprises the following raw material components by mass fraction:

[0058] 40% natural resin, the natural resin is a mixture of Yunnan pine gum and Chinese pine gum in a mass ratio of 3:1,

[0059] 20% natural wax, wherein the natural wax is beeswax,

[0060] 18% fatty alcohol, wherein the fatty alcohol is a mixture of cetyl alcohol and stearyl alcohol in a mass ratio of 1:1,

[0061] 8% tackifier, wherein the tackifier is hydrogenated polydicyclopentadiene,

[0062] 4% natural vegetable oil, the natural vegetable oil is Yunnan camellia seed oil,

[0063] 3% anti-inflammatory soothing repair agent, the anti-inflammatory soothing repair agent is a mixture of guaiacyl ether and component B in a mass ratio of 2:3, and component B is a mixture of peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract in a mass ratio of 1:1:1:1:1,

[0064] 2% skin conditioner, the skin conditioner is shea butter,

[0065] 3% antioxidant, wherein the antioxidant is a mixture of ergothioneine and butylated hydroxytoluene in a mass ratio of 1:1,

[0066] Stabilizer 2%, the stabilizer is mica powder,

[0067] Wherein, the preparation method of the solid depilatory wax comprises the following steps:

[0068] (1) heating the fatty alcohol, tackifier, natural wax, and natural resin to 110° C. under stirring (at a speed of 20 r / min) until all of them are dissolved to obtain a mixture;

[0069] (2) The mixture is cooled to 100° C., and then natural vegetable oil, antioxidant, anti-inflammatory soothing repair agent, skin conditioner and stabilizer are added under stirring (rotation speed of 20 r / min), and then sent to a drum granulator for granulation. After passing the inspection, the mixture is packaged to obtain solid depilatory wax.

[0070] Example 3

[0071] The solid depilatory wax comprises the following raw material components by mass fraction:

[0072] 60% natural resin, the natural resin is slash pine gum,

[0073] Fatty alcohol 15%, wherein the fatty alcohol is stearyl alcohol,

[0074] 12% natural wax, wherein the natural wax is rice bran wax,

[0075] 3% tackifier, wherein the tackifier is a mixture of a hydrogenated (styrene / methylstyrene / indene) copolymer and a hydrogenated (styrene / butadiene) copolymer in a mass ratio of 2:1,

[0076] 3% natural vegetable oil, wherein the natural vegetable oil is a mixture of wheat germ oil and macadamia nut seed oil in a mass ratio of 3:1,

[0077] 3% anti-inflammatory soothing repair agent, the anti-inflammatory soothing repair agent is a mixture of guaiacyl ether and component B in a mass ratio of 1:3, and component B is a mixture of peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract in a mass ratio of 1:1:1:1:1.5,

[0078] Skin conditioning agent 1%, the skin conditioning agent is cyclopentasiloxane,

[0079] 1% antioxidant, wherein the antioxidant is a mixture of tocopherol acetate and monoglyceride citrate in a mass ratio of 2:1,

[0080] 2% stabilizer, wherein the stabilizer is titanium dioxide,

[0081] Wherein, the preparation method of the solid depilatory wax comprises the following steps:

[0082] (1) heating the fatty alcohol, tackifier, natural wax, and natural resin to 110° C. under stirring (at a speed of 20 r / min) until all of them are dissolved to obtain a mixture;

[0083] (2) The mixture is cooled to 100° C., and then natural vegetable oil, antioxidant, anti-inflammatory soothing repair agent, skin conditioner and stabilizer are added under stirring (rotation speed of 20 r / min), and then sent to a drum granulator for granulation. After passing the inspection, the mixture is packaged to obtain solid depilatory wax.

[0084] Example 4

[0085] The solid depilatory wax comprises the following raw material components by mass fraction:

[0086] 65% natural resin, the natural resin is a mixture of masson pine gum and rubber tree resin in a mass ratio of 2:1,

[0087] Fatty alcohol 12%, wherein the fatty alcohol is coconut oil alcohol,

[0088] Natural wax 8%, wherein the natural wax is sunflower wax,

[0089] 3% tackifier, wherein the tackifier is hydrogenated polydicyclopentadiene,

[0090] 3% natural vegetable oil, the natural vegetable oil is camellia seed oil,

[0091] 4% anti-inflammatory soothing repair agent, the anti-inflammatory soothing repair agent is a mixture of guaiacyl ether and component B in a mass ratio of 1:4, and component B is a mixture of peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract in a mass ratio of 1:1:1:1:1,

[0092] Skin conditioning agent 2%, the skin conditioning agent is C30-45 alkyl polydimethylsiloxane,

[0093] 2% antioxidant, wherein the antioxidant is a mixture of butylated hydroxytoluene and butylated hydroxyanisole in a mass ratio of 2:5,

[0094] 1% stabilizer, wherein the stabilizer is silicon dioxide;

[0095] Wherein, the preparation method of the solid depilatory wax comprises the following steps:

[0096] (1) heating the fatty alcohol, tackifier, natural wax, and natural resin to 110° C. under stirring (at a speed of 20 r / min) until all of them are dissolved to obtain a mixture;

[0097] (2) The mixture is cooled to 100° C., and then natural vegetable oil, antioxidant, anti-inflammatory soothing repair agent, skin conditioner and stabilizer are added under stirring (rotation speed of 20 r / min), and then sent to a drum granulator for granulation. After passing the inspection, the mixture is packaged to obtain solid depilatory wax.

[0098] Comparative Example 1

[0099] The method described in Example 1 was followed, except that no tackifier was added and an equal amount of natural resin was used instead.

[0100] Comparative Example 2

[0101] The process described in Example 1 was followed, except that guaiazulene was not added (ie, an equal amount of component B was used instead).

[0102] Comparative Example 3

[0103] The method described in Example 1 was followed, except that peppermint oil and Houttuynia cordata extract were not added.

[0104] Comparative Example 4

[0105] The method described in Example 1 was followed, except that no golden chamomile extract was added.

[0106] 1. The solid depilatory waxes prepared in Examples 1-4 and Comparative Examples 1-4 were tested for melting point and depilatory rate. The testing method is as follows:

[0107] Melting point test: The melting point test was carried out according to the determination method in GB / T 12766-2008 Determination of melting point of animal fats and oils.

[0108] Hair removal rate test: 48 volunteers aged 18 to 35 were recruited and divided into 8 groups, with 6 volunteers in each group (half male and half female). The volunteers were tested with the solid depilatory wax prepared in Examples 1-4 and Comparative Examples 1-4. The test method was as follows: First, skin with evenly distributed hair on the volunteers' calves was selected. A rectangular area (10 cm × 5 cm) with a length and width of 10 cm and 5 cm, respectively, was marked on the skin surface. The melted solid depilatory wax was then evenly applied to the marked rectangular area. After the depilatory wax film formed, it was removed. The 10 cm × 5 cm skin area was then divided into 100 small squares of equal size. Finally, the residual hair in each small square was observed. If no hair remained in the small square, the hair removal was successful. The number of small squares with successful hair removal was counted and the hair removal rate was calculated by dividing the number of small squares with successful hair removal by the total number of small squares (100). The average value was taken. The test results are shown in Table 1.

[0109] Table 1

[0110]

[0111]

[0112] As can be seen from Table 1, the depilatory wax provided by the present invention has a low melting point and a good depilatory effect.

[0113] 2. The solid depilatory waxes prepared in Examples 1-4 and Comparative Examples 1-4 were subjected to a skin irritation test. The test method was as follows: a skin irritation test was performed according to the repetitive open smear test method in the human skin patch test method in the "Technical Specifications for Safety of Cosmetics" (2015 edition) issued by the State Food and Drug Administration. The test results are shown in Table 2.

[0114] Table 2

[0115]

[0116] As can be seen from Table 2, the solid depilatory wax provided by the present invention can improve the damaged skin barrier function caused by hair plucking, and prevent skin or skin follicle inflammation caused by hair removal.

[0117] The above are merely preferred embodiments of the present invention and are not intended to limit the scope of the present invention. Those skilled in the art will readily appreciate that the present invention is susceptible to various modifications and variations. Any modifications, equivalent substitutions, or improvements made within the spirit and principles of the present invention shall be included within the scope of the present invention.

Claims

1. A solid depilatory wax, characterized in that, The solid depilatory wax comprises the following raw material components by mass fraction: Natural resin 30~70%, fatty alcohol 5~20%, natural wax 3~20%, tackifier 2~10%, natural plant oil 0.2~5%, anti-inflammatory soothing repair agent 0.2~5%, skin conditioning agent 0.2~3%, antioxidant 0.2~3%, stabilizer 0.2~2%; Wherein, the tackifier is selected from at least one of polyisobutylene, hydrogenated polydicyclopentadiene, hydrogenated (styrene / methylstyrene / indene) copolymer and hydrogenated (styrene / butadiene) copolymer; The anti-inflammatory, soothing and repairing agent comprises component A and component B, wherein component A is guaiacyl ether, and component B is peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract; The mass ratio of component A to component B is 1-2:2-5; The mass ratio of the peppermint oil, purslane extract, golden chamomile extract, houttuynia cordata extract and scutellaria baicalensis extract is 1:1:1:1:1-2; The fatty alcohol is selected from at least one of coconut oil alcohol, myristyl alcohol, cetyl alcohol, stearyl alcohol and cetearyl alcohol; The skin conditioning agent is selected from at least one of C30-45 alkyl dimethicone, shea butter and cyclopentasiloxane.

2. The solid depilatory wax according to claim 1, wherein The natural resin is selected from at least one of masson pine resin, Yunnan pine resin, Chinese pine resin, wetland pine resin, Simao pine resin, torch pine resin and rubber tree resin.

3. The solid depilatory wax according to claim 1, wherein The natural wax is selected from at least one of palm wax, rice bran wax, candelilla wax, sunflower wax, sumac wax and beeswax.

4. The solid depilatory wax according to claim 1, wherein The natural vegetable oil is selected from at least one of camellia seed oil, Yunnan camellia seed oil, jojoba seed oil, coconut oil, wheat germ oil and macadamia seed oil.

5. The solid depilatory wax according to claim 1, wherein The antioxidant is selected from at least two of tocopheryl acetate, butylated hydroxytoluene, butylated hydroxyanisole, ascorbyl palmitate, monoglyceride citrate, nordihydroguaiaretic acid and ergothioneine.

6. The solid depilatory wax according to claim 1, wherein The stabilizer is selected from at least one of titanium dioxide, zinc oxide, silicon dioxide and mica powder.

7. A method for preparing the solid depilatory wax according to any one of claims 1 to 6, characterized in that: The method comprises the following steps: (1) While stirring, heating and dissolving fatty alcohol, tackifier, natural wax and natural resin at 105-115° C. to obtain a mixture; (2) Cooling the mixture to 95-100° C., then adding natural plant oil, antioxidant, anti-inflammatory soothing repair agent, skin conditioner and stabilizer under stirring, followed by granulation to obtain solid depilatory wax.