A Low-Temperature Preparation Method for Nano-α-Al₂O₃ Ceramics
By combining cold sintering and low-temperature annealing, the problem of preparing nano-α-Al2O3 ceramics at low temperatures was solved, and high-quality nano-α-Al2O3 ceramics were prepared efficiently and economically.
CN118479866BActive Publication Date: 2026-06-02CHENGDU UNIV
Patent Information
- Application Number
- CN202410406115.4
- Authority / Receiving Office
- CN · China
- Patent Type
- Patents(China)
- Current Assignee / Owner
- Filing Date
- 2024-04-07
- Publication Date
- 2026-06-02
- Estimated Expiration
- 2044-04-07
AI Technical Summary
Technical Problem
Existing technologies make it difficult to prepare high-purity and highly uniform nanostructured α-Al2O3 ceramics at low temperatures, and the high sintering temperature of traditional methods makes preparation difficult.
Method used
Hydrate (α-AlOOH) was prepared by cold sintering, and the phase transformation from α-AlOOH to α-Al2O3 was achieved by low-temperature annealing. Nano-α-Al2O3 ceramics were prepared by combining cold sintering and low-temperature annealing.
Benefits of technology
High-quality nano-α-Al2O3 ceramics were successfully prepared at low temperatures, overcoming the technical difficulties of traditional high-temperature sintering, with a short cycle and strong operability.
✦ Generated by Eureka AI based on patent content.
Smart Images
Figure CN118479866B_ABST
Abstract
The application belongs to the technical field of ceramic low-temperature sintering, and particularly relates to a low-temperature preparation method of nano alpha-Al2O3 ceramic. The application adopts a cold sintering process, takes aluminum hydroxide powder as raw material, and takes 2-20 wt.% deionized water as solvent to obtain dense alpha-AlOOH ceramic under 500-2000 Mpa uniaxial pressure, 200-500 DEG C heating temperature and 50-300 min holding time; then, through a low-temperature annealing process, complete phase change from alpha-AlOOH to alpha-Al2O3 is realized under 400-600 DEG C annealing temperature and 2-6 h holding time, and finally alpha-Al2O3 ceramic sintered body with 30-50 nm grain size is obtained. The method overcomes the technical difficulty that traditional alpha-Al2O3 ceramic sintering temperature is high and it is difficult to obtain nano-crystal structure ceramic sintered body, and provides a process method for preparing alpha-Al2O3 ceramic with nano-crystal structure at low temperature, which has short preparation period and strong operability.
Need to check novelty before this filing date? Find Prior Art
Citation Information
Patent Citations
Cold sintering mold
CN216992369U
A process for the preparation of high surface area alpha alumina and the use thereof
EP3689822A1