Health-care decorative panels that can release negative ions for making furniture and decoration

Abstract

The invention relates to a health care veneer board capable of releasing negative ions and used for manufacturing furniture and decorating. The health care veneer board is characterized by comprising a base material layer, tourmaline powder and auxiliary agent layers and veneer layers, which are sequentially connected, wherein the tourmaline powder and auxiliary agent layers are sprayed and stuck on the base material layer; the tourmaline powder and auxiliary agent layers are fixed on the base material layer by the veneer layers; the veneer layers can be treated by antistatic coating spraying. The health care veneer board has the beneficial effects that the tourmaline powder and auxiliary agent layers are only sprayed onto the surface of an artificial board, so that the health care veneer board is good in effect, easy to obtain and low in cost. The veneer material is good in breathability and is capable of well releasing the negative ions. The health care veneer board is capable of decomposing or neutralizing formaldehyde and TVOC which are released by boards, and has a control function for the release of pollutants. According to the health care veneer board, the finished product artificial board base material is sprayed, the application scope is wide and the operation is easy. After spraying, due to the protection function of the tourmaline powder, the indexes of the board can be respectively improved to the different extents.

Description

technical field

[0001] The invention belongs to the field of production and processing of man-made panels and products thereof, and relates to a health-care decorative panel material capable of releasing negative ions for making furniture and decoration. Background technique

[0002] Nowadays, wood-based panels are widely used in construction, furniture, decoration and other fields. With the continuous progress of science and technology, tourmaline stone is gradually valued by manufacturers. It mainly has the functions of releasing negative ions and reducing formaldehyde and volatile organic compounds. Lin stone is gradually used in the production of wood-based panels. In 2008, the Chinese Academy of Forestry Sciences disclosed a method for producing negative ion wood-based panels with tourmaline stone CN 101269513B. The main technology is to mix tourmaline stone powder with glue The adhesive is mixed with wood fibers or shavings and hot-pressed into boards. Due to the addi...

Examples

preparation example Construction

[0035] The present invention can release negative ions and is used for making furniture and the preparation method of the health care board of decoration decoration, is characterized in that: comprises the following steps:

[0036] A. After the tourmaline ore is selected, it is ground into nano-scale ultrafine powder by a grinder;

[0037] B. Mix the finely ground tourmaline powder and the auxiliary agent at a weight ratio of 1:1 to 1:200 to form a mixed solution. The auxiliary agent can disperse the tourmaline powder and make the tourmaline powder evenly distributed on the base. material surface. Then spray / roll the mixed solution evenly on one or both sides of the base material layer until the base material layer is completely covered. -145℃, time 5-600 seconds) or baking method (temperature 15-105℃, time 20-800 seconds) to remove the volatile solvent and water in the mixture to form tourmaline powder and auxiliary layer;

[0038] C. Put the plate processed in step B on th...

Embodiment 1

[0042] The preparation method of the health-care board for making furniture and decoration that can release negative ions of the present invention comprises the following steps:

[0043] A. After the tourmaline ore is selected, it is ground into nano-scale ultrafine powder by a grinder;

[0044]B. Mix the finely ground tourmaline powder and anhydrous ethanol at a weight ratio of 1:1 to form a mixed solution, and then spray the mixed solution evenly on one or both sides of the fiberboard to completely cover the fiberboard. (Temperature 150°C, time 5 seconds) Remove the solvent in the auxiliary agent mixture to form tourmaline powder and auxiliary agent layer;

[0045] C. Put the sheet processed in step B on the automatic hot-pressing machine production line, and hot-press the melamine-impregnated adhesive film paper under the conditions of a temperature of 260 ° C, a pressure of 5 MPa, and a time of 5 s for finishing.

[0046] D. Use the anti-static material polyvinyl chloride...

Embodiment 2

[0048] The preparation method of the health-care board for making furniture and decoration that can release negative ions of the present invention comprises the following steps:

[0049] A. After the tourmaline ore is selected, it is ground into nano-scale ultrafine powder by a grinder;

[0050] B. Mix the finely ground tourmaline powder with a 1% sodium carboxymethyl cellulose deionized aqueous solution in a weight ratio of 1:200 to form a mixed solution. Then, evenly roll the mixed solution on one or both sides of the particleboard until the substrate layer is completely covered, and remove the volatile solvent in the mixed solution by baking (temperature 105°C, time 800 seconds);

[0051] C. Put the plate processed in step B on the automatic hot press production line, and press the surface to form a decorative layer under the conditions of a temperature of 60 ° C, a pressure of 30 MPa, and a time of 150 s.

[0052] D. The board is treated with anti-static, and the surface ...

technical field

[0001] The invention belongs to the field of production and processing of man-made panels and products thereof, and relates to a health-care decorative panel material capable of releasing negative ions for making furniture and decoration. Background technique

[0002] Nowadays, wood-based panels are widely used in construction, furniture, decoration and other fields. With the continuous progress of science and technology, tourmaline stone is gradually valued by manufacturers. It mainly has the functions of releasing negative ions and reducing formaldehyde and volatile organic compounds. Lin stone is gradually used in the production of wood-based panels. In 2008, the Chinese Academy of Forestry Sciences disclosed a method for producing negative ion wood-based panels with tourmaline stone CN 101269513B. The main technology is to mix tourmaline stone powder with glue The adhesive is mixed with wood fibers or shavings and hot-pressed into boards. Due to the addi...

Examples

preparation example Construction

[0035] The present invention can release negative ions and is used for making furniture and the preparation method of the health care board of decoration decoration, is characterized in that: comprises the following steps:

[0036] A. After the tourmaline ore is selected, it is ground into nano-scale ultrafine powder by a grinder;

[0037] B. Mix the finely ground tourmaline powder and the auxiliary agent at a weight ratio of 1:1 to 1:200 to form a mixed solution. The auxiliary agent can disperse the tourmaline powder and make the tourmaline powder evenly distributed on the base. material surface. Then spray / roll the mixed solution evenly on one or both sides of the base material layer until the base material layer is completely covered. -145℃, time 5-600 seconds) or baking method (temperature 15-105℃, time 20-800 seconds) to remove the volatile solvent and water in the mixture to form tourmaline powder and auxiliary layer;

[0038] C. Put the plate processed in step B on th...

Embodiment 1

[0042] The preparation method of the health-care board for making furniture and decoration that can release negative ions of the present invention comprises the following steps:

[0043] A. After the tourmaline ore is selected, it is ground into nano-scale ultrafine powder by a grinder;

[0044]B. Mix the finely ground tourmaline powder and anhydrous ethanol at a weight ratio of 1:1 to form a mixed solution, and then spray the mixed solution evenly on one or both sides of the fiberboard to completely cover the fiberboard. (Temperature 150°C, time 5 seconds) Remove the solvent in the auxiliary agent mixture to form tourmaline powder and auxiliary agent layer;

[0045] C. Put the sheet processed in step B on the automatic hot-pressing machine production line, and hot-press the melamine-impregnated adhesive film paper under the conditions of a temperature of 260 ° C, a pressure of 5 MPa, and a time of 5 s for finishing.

[0046] D. Use the anti-static material polyvinyl chloride...

Embodiment 2

[0048] The preparation method of the health-care board for making furniture and decoration that can release negative ions of the present invention comprises the following steps:

[0049] A. After the tourmaline ore is selected, it is ground into nano-scale ultrafine powder by a grinder;

[0050] B. Mix the finely ground tourmaline powder with a 1% sodium carboxymethyl cellulose deionized aqueous solution in a weight ratio of 1:200 to form a mixed solution. Then, evenly roll the mixed solution on one or both sides of the particleboard until the substrate layer is completely covered, and remove the volatile solvent in the mixed solution by baking (temperature 105°C, time 800 seconds);

[0051] C. Put the plate processed in step B on the automatic hot press production line, and press the surface to form a decorative layer under the conditions of a temperature of 60 ° C, a pressure of 30 MPa, and a time of 150 s.

[0052] D. The board is treated with anti-static, and the surface ...