Process for producing an oven-hardenable modeling clay

Abstract

Process for producing an oven-hardenable modelling clay, the modelling clay consists of at least a binder and a plasticizer, wherein the binder and the plasticizer are formed as plastisol, the plastisol is essentially composed of PVC and plasticizer, wherein the plasticizer is a phthalate-free plasticizer, the mass having a total plasticizer content of 38 to 52 wt.%, characterized by that the phthalate-free plasticizer is based exclusively on citric acid and is acetyl tributyl citrate, tri-(2-ethylhexyl) acetyl citrate, trioctyl citrate, tridecyl citrate, tributyl citrate, trihexyl citrate, triethyl citrate, or a mixture of at least two of these substances. that the procedure / process is designed as follows, that the PVC powder and the amount of plasticizer with any other additives and / or additives are subjected to a mixing process and that the mixing process takes place at a mixing temperature of 55 to 70°C.

Description

[0001] The invention relates to a method for producing an oven-hardenable modeling clay.

[0002] Plastic, oven-hardening masses for shaping and modeling objects are known in principle.

[0003] Modelling materials also include so-called clays, or polymer clays in the case of polymer-containing materials.

[0004] For example, DE 25 15 757 C3 discloses a plastic mass that can be shaped by hand and hardened by heating. Such a mass essentially consists of polyvinyl chloride (PVC), filler and phthalate-containing plasticizer.

[0005] Furthermore, modeling clays are known from DE 10 2005 059 143 A1 which do not contain phthalate-containing plasticizers.

[0006] Furthermore, DE 102018007756 A1 discloses modeling clays containing plastic fibers as fillers to create leather-like surfaces. Such modeling clays can contain both phthalate-containing and phthalate-free plasticizers.

[0007] The production of ester-based plasticizer mixtures is known from US 2017253724 A1. Such plasticizer mixtures can be mixed with PVC, for example.

[0008] The disadvantage of such masses according to the state of the art is that they are not resistant to aging and the blocks of modeling clay show an increase in hardness during longer storage, even in unopened packaging.

[0009] This results in the modeling clay being difficult for the user to knead.

[0010] This is still the ideal case of aging, because long storage times can even lead to modeling blocks becoming unusable because they can no longer be kneaded by hand.

[0011] This is due to the fact that the plasticizer interacts with the compound even at room temperature. This is referred to as an aging process of PVC-containing modeling compounds in the uncured state.

[0012] In state-of-the-art modeling clays, the powdered raw materials are mixed with the plasticizer at temperatures between 20 and 30°C. This achieves a plasticizer absorption of 25–30% by weight. Over time, e.g., during extended storage, individual PVC agglomerates disintegrate, which in turn generates a need for plasticizer because the surface area of the PVC grains has increased.

[0013] The plasticizer previously stored in the interstices of the PVC particles, which is largely responsible for the soft kneading / moldability of the modeling clay, is no longer present in this case. Instead, the plasticizer accumulates on the newly created surfaces of the disintegrated agglomerates. As a result, this phenomenon causes the hardness of the uncured modeling clay to increase over time.

[0014] The object of the invention is therefore to provide a production process for a modeling or molding compound which does not have the disadvantages mentioned above and, in particular, to minimize the aging process during storage of PVC-containing modeling compounds in the uncured state and thus to ensure greater storage stability.

[0015] Furthermore, it is the object of the invention to increase the flexibility of the modeling mass after oven hardening and, if necessary, to improve the transparency - up to glass clarity - of the hardened mass.

[0016] The problem is solved with the features included in claims 1 to 5.

[0017] The oven-curable modeling clay produced according to the invention consists of at least a binder and a plasticizer, with the binder being present as a plastisol, which is essentially composed of PVC and a plasticizer, and optionally other additives. The modeling clay may contain, for example, at least one filler as a further additive.

[0018] A moldable mass is one in which the plasticizer content in the mixture is adjusted such that the plasticizer, on the one hand, adheres to the surface of the PVC particles and, on the other hand, in the spaces between the solid particles at a level that creates a moldable resistance. If the plasticizer content is too low, i.e., the plasticizer only adheres to the surface of the solid particles without also being present in the spaces, the mass is too hard or very difficult to mold.

[0019] If, on the other hand, the surfaces of the solid particles and the spaces between the solid particles are completely covered or even oversaturated with plasticizer, the resulting modeling clay would flow too much and would therefore no longer be modelable.

[0020] To transform the now modeled objects into a permanently solid state, heat must be applied. This is called oven curing. The plasticizer, or rather the plasticizer content, is responsible for the hardening process, which, due to interactions with the PVC, causes the compound to harden.

[0021] However, it has been shown that even when stored at room temperature, the plasticizer exhibits a certain affinity for the PVC grain or PVC solid particles. This causes the PVC grain, which partially consists of agglomerates, to disintegrate, thus generating new surfaces / surface areas. Through these newly created surfaces, the plasticizer, which was stored in the interstices, migrates to these newly created surfaces. As a result, the hardness of the modeling clay increases, as its malleability decreases due to the lack of the liquid plasticizer in the interstices.

[0022] The particular advantages of the compositions produced according to the invention lie in the fact that, using the inventive method, agglomerate degradation (= aging process) can be brought forward into the production process by mixing at higher temperatures and with larger amounts of plasticizer. This ultimately improves the storage stability and hardness increase of the uncured composition over time, for example, by selectively adding additional plasticizer after the "aging process during the production process" has been initiated.

[0023] A further advantage of the increased proportion / content of plasticizer in the modeling clay is that the system's gelling ability during the curing process is improved, resulting in greater elasticity after oven curing. Surprisingly, it has been shown that mixing at higher temperatures and the associated plasticizer contents, as well as reducing the use of fillers and / or additives, can significantly increase transparency after oven curing.

[0024] The binder used, which is essentially PVC, and the added plasticizer form a plastisol. The PVC can be in the form of emulsifier-containing or emulsifier-free emulsion PVC, suspension PVC, and microbead suspension PVC, or a mixture of the individual PVC types.

[0025] Phthalate-free plasticizers are used as plasticizers. The total plasticizer content is between 38 and 52 wt.%.

[0026] The phthalate-free plasticizer is based exclusively on citric acid.

[0027] The phthalate-free plasticizers are acetyl tributyl citrate (ATBC), tri-(2-ethylhexyl) acetyl citrate, trioctyl citrate, tridecyl citrate, tributyl citrate, trihexyl citrate, and triethyl citrate. Any mixture of all of the aforementioned plasticizers is possible.

[0028] A stabilizer improves PVC stability, ie, it prevents, among other things, the release of hydrogen chloride. Inorganic and organic salts of the metals calcium, zinc, tin, magnesium, sodium, and potassium are primarily used for this purpose, e.g., calcium stearate, sodium stearate, potassium stearate, zinc stearate, magnesium stearate, tin stearate, and / or mixtures of the metal salts.

[0029] The fillers used are essentially inorganic and / or organic fillers, e.g. kaolin, chalk, silica, talc, aluminum hydroxide and / or clay powder, which have a grain size of < 250 µm, preferably less than 100 µm.

[0030] Additional fillers may include metallic glitter, glitter powder and glitter flakes or mixtures of these substances in order to achieve special optical effects, for example.

[0031] So-called lightweight fillers can also be used as fillers, or other fillers can be added. Examples of lightweight fillers are hollow spheres, especially hollow glass microspheres, e.g., from 3M or Lehmann & Voss. Depending on the lightweight filler content, a desired density can be achieved, which is advantageously in the range of 0.3 to 1.1 g / ml. The size of commercially available lightweight fillers can also be freely selected, with their size preferably being in the range of 10 to 400 µm.

[0032] Polymer-based fillers can also be used. Examples of this group include PAMA, PMMA, and / or polyethylene.

[0033] Pigments can be used as colorants in pure form, as powder pigments, preferably as azo-free color pigment, effect pigment and / or azo-free laked dye. As a selection of a variety of possible color pigments, we offer Pigment Yellow 14 (CI 21095), Pigment Red 254 (CI 56110), Pigment Orange 34 (CI 21110), Pigment Red 122 (CI 73915), Pigment Green 7 (CI 74260), Pigment White 6 (CI 77891), Pigment Black 7 (CI 77266), Pigment Red 101 (CI 77491), Pigment Violet 23 (CI 51319), Pigment Blue 29 (CI 77007), Pigment Yellow 185 (CI 56290), Pigment Yellow 1 (CI11680), Pigment Red 48:2 (CI 15865:2), Pigment Red 53:1 (CI 15585:1), Pigment Orange 34 (CI 21115), Pigment Yellow 83 (CI 21108) and Pigment Blue 15 (CI 74160).

[0034] The addition of these colorants gives the modeling clay a brilliant appearance.

[0035] Other colorants include pearlescent pigments, mica iron metal luster pigments, polyester glitter pigments and luminescent pigments.

[0036] It can be seen that differently colored modeling clays can be mixed, blended or kneaded together as desired, creating a marbling effect.

[0037] The invention will be illustrated in more detail using a framework example and some recipe examples.

[0038] Framework example - particularly preferred composition 45 - 62 wt.% binder 38 - 52 wt.% plasticizers 0 - 17 wt.% Fillers 0 - 15 wt.% other additives Stabilizers, co-stabilizers, colorants and / or fillers are examples of other additives that may be used.

[0039] Recipe example 1 - yellow modeling clay 51 wt.% E-PVC and S-PVC 42 wt.% Plasticizer based on ATBC 6 wt.% stabilizer 0.5 wt.% filler 0.5 wt.% Pigment Yellow 83 Recipe example 2 - Modeling clay, transparent after hardening 48% by weight E-PVC and S-PVC 52 wt.% Plasticizer based on ATBC

[0040] State of the art - comparative formulation according to DE 10 2005 059 143 59 wt.% PVC 24% by weight Citric acid-based plasticizer 1 wt.% Stabilizers 7 wt.% Co-stabilizers 4 wt.% filler 1 wt.% Pigment Red 254

[0041] The phthalate-free plasticizer used in the invention is based exclusively on citric acid.

[0042] The desired consistency of the mass can easily be adjusted by varying the binder content and / or plasticizer content.

[0043] The present invention will be presented in more detail in the following tables. Table 1: Hardness increase of the uncured mass as a function of time at 40°C. 30 days / 40°C 90 days / 40°C Mass produced according to the invention Recipe example 2 Delta H 10% Delta H 13% Mass according to the state of the art comparative example Delta H 245% Delta H 386%

[0044] It has been shown that the mass not yet cured in the oven according to the application documents shows a significantly lower increase in hardness compared to the state of the art when stored at 40°C over time (30 or 90 days), as can be seen from Table 1. Table 2: Flexibility of the cured mass Flexibility / deflection until break in mm Mass produced according to the invention Recipe example 2 28 Mass according to the state of the art comparative example 6

[0045] These higher fracture strengths were determined and confirmed using a texture analyzer. Round fracture bars with a length of 10 cm and a diameter of 1 cm were used as test specimens.

[0046] The process according to the invention for producing such modeling materials is described below.

[0047] As background to the process according to the invention, it should be noted that the mixing process of the individual components in the mass takes place at elevated temperatures, around 55 to 70°C, preferably around 58 to 65°C. This initiates agglomerate breakdown during the mixing process, whereby an increased plasticizer content is or can be added to the solid phase of the PVC. Due to the early creation of new surfaces, due to agglomerate breakdown, more plasticizer can be added / introduced during the mixing process.

[0048] The method / process for producing the oven-curable composition according to the invention can be described as follows.

[0049] In this process, PVC powder and the amount of plasticizer with any other additives and / or additives are added to the mixing process at a mixing temperature of approximately 55 to 70°C.

[0050] The particularly preferred components of the mass in the process include 45 - 62 wt.% binder 38 - 52 wt.% plasticizers 0 - 17 wt.% Fillers 0 - 15 wt.% other additives

[0051] By incorporating / introducing a higher amount of plasticizer into the PVC system of the modeling clay, the increase in hardness of the modeling clay over time is reduced and thus the storage stability is significantly improved.

[0052] Surprisingly, it has been shown that the more plasticizer added to the PVC powder, the greater the resulting flexibility of the compound after the curing process. This higher plasticizer content significantly increases the flexibility of the cured compound. It has also been surprisingly shown that greater transparency can be achieved by the process according to the invention.

[0053] The mass is used in the production of plastic, hand-formable and heat-hardening masses, as modeling masses for use by children and for the production of arts and / or industrial objects and the products made from them, such as seal impressions and jewelry.

[0054] The mass or modeling clay is also used for therapeutic purposes in the medical field to train and rehabilitate haptic skills.

[0055] Items and objects made from modeling clay are hardened by heat after being shaped to create the items and objects.

Claims

[1] Process for the preparation of an oven-hardenable modelling clay, the modelling clay consists of at least a binder and a plasticizer, wherein the binder and the plasticizer are formed as plastisol, The plastisol consists essentially of PVC and plasticizer, wherein the plasticizer is a phthalate-free plasticizer, the mass having a total content of 38 to 52 wt.% plasticizer, characterized by , that the phthalate-free plasticizer is based exclusively on citric acid and is acetyl tributyl citrate, tri-(2-ethylhexyl) acetyl citrate, trioctyl citrate, tridecyl citrate, tributyl citrate, trihexyl citrate, triethyl citrate, or a mixture of at least two of these substances. that the procedure / process is designed as follows, that the PVC powder and the amount of plasticizer with any other additives and / or additives are subjected to a mixing process and that the mixing process takes place at a mixing temperature of 55 to 70°C. [2] Method according to claim 1, characterized by that the mass consists of at least 45 - 62 wt.% binder 38 - 52 wt.% plasticizers 0 - 17 wt.% Fillers 0 - 15 wt.%. other additives [3] Method according to one of the preceding claims, characterized by that the filler is inorganic and / or organic. [4] Method according to one of the preceding claims, characterized by that the filler is kaolin, talc, chalk, silica, aluminum hydroxide, clay powder and / or a lightweight filler. [5] Method according to one of the preceding claims, characterized by that a colorant is used as another additive and that the colorant is in the form of a pigment, a powder pigment, preferably an azo-free color pigment, an effect pigment and / or an azo-free laked dye.