Single piece intraocular lens with integrally coupled haptics

Abstract

Disclosed single piece IOLs and related devices including an optic portion integrally coupled to a haptic portion.

Description

[0001]Attorney Docket No. JSV7183WOPCT1 SINGLE PIECE OPTICAL DEVICES WITH INTEGRALLY COUPLED HAPTICS Cross-Reference to Related Patent Applications This application claims priority to U.S. Provisional Application No.63 / 505659, filed on June 1, 2023, which is hereby incorporated by reference in its entirety. Field of the Disclosure This disclosure is directed to single piece optical devices, including intraocular lenses, having integrally coupled haptics, and to methods of making single piece optical devices. Background of the Disclosure Cataract surgery is commonly performed to replace the natural eye lens that has become opaque. The intraocular lenses (IOLs) that are used to replace the natural crystalline lens must be soft and have excellent flexibility so that, once formed into a lens, they may be folded and passed through an incision which is typically about 2 mm. IOLs typically include a central optical part, whose overall contour is circular, and a haptic part, which is disposed at the periphery of the optical part and is intended to be positioned so as to stabilize the implant. Current manufacturing of IOLs utilizes lathing to produce the optical surface from a preformed blank. A current limitation of the lathing process is the inability to utilize multiple materials within and outside the optic zone outside of gross lamination or assembly methods. The balance of optical properties and mechanical requirements of the haptics limits the overall material choices for a single piece IOL. While it is possible to assemble the haptics at a later step, there are compromises to the manufacturing process and edge quality of the IOL overall from the additional processing steps. In particular, with lathing and molding technologies it is not possible to decouple IOL optical requirements and haptic mechanical requirements. Single piece intraocular lenses are known, including the AcrySof IOL marketed by Alcon Laboratories, in which the optic and haptic portions of the IOL are composed of the same material (usually acrylic, silicone or polymethylmethacrylate). By forming the haptic and optic from the same blank, the haptics are softer, facilitating insertion through smaller incisions. While these devices have been widely accepted, they are not without drawbacks. For example, currently available single piece IOLs should not contact the ciliary suculus, due to the possibility Attorney Docket No. JSV7183WOPCT1 of UGH (uveitis, glaucoma, hyphema) syndrome, as well as displacement over time from the originally implant location. Complications can arise in single piece haptics due to inherent features of the single piece lathing process. For example the haptic must be are the same thickness as the optic, and the devices are much more planar than multi-piece IOLs. These features can lead to improper contact with the iris. While the softer haptic material (which is inherent when made from the same material as the optic) aids insertion, the IOL may be less stable over prolonged time, leading to position shifts and deterioration of performance. There remains a need for improved optical device with single piece IOLs with discrete optic and haptic systems. There remains a need for optically opaque or translucent haptics in single piece IOLs. There remains a need for single piece IOLs with haptics and optics of different mechanical properties. There remains a need for single piece IOLs in which the haptic has increases rigidity relative to the optic. There remains a need for single piece IOLs with asymmetric polymer configurations, including core shell and other layered assemblies. There remains a need for single piece, drug-eluting IOLs in which the drug is localized in either the haptic or optic potions. There remains a need for improved methods of fabricating single piece IOLs with greater control and selectivity. There remains a need for improved methods of fabricating single piece IOLs with less restriction of the eventual shape of the haptic. Summary of the Disclosure In certain embodiments, the present disclosure provides an ophthalmic device. In particular embodiments, the ophthalmic device comprises a lens, inlay, outlay, or insert selected from an intraocular implant or lens, a contact lens, a corneal inlay, a corneal outlay, and a corneal insert. In specific embodiments, the ophthalmic device is an intraocular implant or lens. In still yet other embodiments, the present disclosure provides a method for making an ophthalmic device, the method comprising the steps of: (a) providing (b) selectively curing the mixture to form an ophthalmic device. In certain embodiments, the selective curing is performed using stereolithographic printing. In certain embodiments, the selective curing is performed using in-gel printing. In certain embodiments of either method, the method further comprises the step of extracting the ophthalmic device with a solvent. In certain embodiments, the method further comprises the step of hydrating the extracted ophthalmic device with at least one aqueous Attorney Docket No. JSV7183WOPCT1 solution. In more particular embodiments, the method further comprises a step of sterilizing the ophthalmic device. Detailed Description of the Disclosure It is to be understood that the disclosure is not limited to the details of construction or process steps set forth in the following description. The disclosure is capable of other embodiments and of being practiced or being carried out in various ways using the teaching herein. A. Definitions With respect to the terms used in this disclosure, the following definitions are provided. Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the disclosure belongs. The polymer definitions are consistent with those disclosed in the Compendium of Polymer Terminology and Nomenclature, IUPAC Recommendations 2008, edited by: Richard G. Jones, Jaroslav Kahovec, Robert Stepto, Edward S. Wilks, Michael Hess, Tatsuki Kitayama, and W. Val Metanomski. All publications, patent applications, patents, and other references mentioned herein are incorporated by reference. The term "reactive monomer mixture" refers to a mixture of components (both reactive and non-reactive) which are mixed together and when subjected to polymerization conditions, form the presently disclosed compositions and ophthalmic devices. The reactive mixture may include reactive components such as monomers, macromers, prepolymers, cross-linkers, initiators, diluents, and additional components, including, but not limited to, wetting agents, release agents, dyes, light absorbing compounds, such as ultraviolet-high energy visible light (UV / HEV) absorbers, pigments, dyes and photochromic compounds, any of which may be reactive or non-reactive but are capable of being retained within the resulting biomedical device, e.g., an ophthalmic device, as well as active components, including pharmaceutical and nutraceutical compounds, and any diluents. It will be appreciated that a wide range of additives may be added based upon the biomedical device which is made, and its intended use. In some embodiments, concentrations of components of the reactive mixture are given in weight % of all components in the reaction mixture, excluding diluent. When diluents are used their concentrations are given as weight % based upon the amount of all components in the reaction mixture and the diluent. Attorney Docket No. JSV7183WOPCT1 "Reactive components" are the components in the reactive monomer mixture which become part of the structure of the polymeric network of the resulting composition, by covalent bonding or hydrogen bonding. Diluents and processing aids which do not become part of the structure of the polymer are not reactive components. As used herein, the term "(meth)" designates optional methyl substitution. Thus, a term such as "(meth)acrylates" denotes both methacrylates and acrylates; and a term such as "(meth)acrylamidess" denotes both methacrylamides and acrylamides. The term “(meth)acryl” is inclusive of both (meth)acrylates and (meth)acrylamides. Wherever chemical structures are given, it should be appreciated that alternatives disclosed for the substituents on the structure may be combined in any combination. Thus, if a structure contained substituents R* and R**, each of which contained three lists of potential groups, 9 combinations are disclosed. The same applies for combinations of properties. When a subscript, such as "n" in the generic formula [***]n, is used to depict the number of repeating units in a polymer's chemical formula, the formula should be interpreted to represent the number average molecular weight of the macromolecule. The term "individual" includes humans and non-human vertebrates. The term "biomedical device" refers to any article that is designed to be used while either in or on mammalian tissues or fluids, and preferably in or on human tissue or fluids. Examples of these devices include but are not limited to wound dressings, sealants, tissue fillers, drug delivery systems, coatings, adhesion prevention barriers, catheters, implants, stents, and ophthalmic devices such as intraocular implants, intraocular lenses, and contact lenses. The biomedical devices may be ophthalmic devices, particularly ophthalmic implants or ophthalmic lenses made from the reactive monomer compositions described herein. The term "ocular surface" includes the surface and glandular epithelia of the cornea, conjunctiva, lacrimal gland, accessory lacrimal glands, nasolacrimal duct and meibomian gland, and their apical and basal matrices, puncta and adjacent or related structures, including eyelids linked as a functional system by both continuity of epithelia, by innervation, and the endocrine and immune systems. The term "ophthalmic device" refers to any device which resides in or on the eye or any part of the eye, including the ocular surface. These devices can provide optical correction, cosmetic enhancement, vision enhancement, therapeutic benefit (for example as bandages) or Attorney Docket No. JSV7183WOPCT1 delivery of active components such as pharmaceutical and nutraceutical components, or a combination of any of the foregoing. Examples of ophthalmic devices include but are not limited to lenses, optical and ocular inserts, including but not limited to punctal plugs, and the like. "Lenses" include soft contact lenses, hard contact lenses, hybrid contact lenses, intraocular lenses, and overlay lenses. The ophthalmic device may comprise an intraocular implant, intraocular lens, or contact lens. The term "contact lens" refers to an ophthalmic device that can be placed on the cornea of an individual's eye. The contact lens may provide corrective, cosmetic, or therapeutic benefit, including wound healing, the delivery of drugs or nutraceuticals, diagnostic evaluation or monitoring, ultraviolet (UV) light absorbing, visible (VIS) light or glare reduction, or any combination thereof. A contact lens can be of any appropriate material known in the art and can be a soft lens, a hard lens, or a hybrid lens containing at least two distinct portions with different physical, mechanical, or optical properties, such as modulus, water content, light transmission, or combinations thereof. “Intraocular lens” refers to a lens implanted in an eye. In some embodiments, the intraocular lens is implanted in the eye to replace an existing crystalline lens (such as, for example, because the existing lens has been clouded over by a cataract, or as a form of refractive surgery to change the eye's optical power).  "Target macromolecule" means the macromolecule being synthesized from the reactive monomer mixture comprising monomers, macromers, prepolymers, cross-linkers, initiators, additives, diluents, and the like. The term "polymerizable compound" means a compound containing one or more polymerizable groups. The term encompasses, for instance, monomers, macromers, oligomers, prepolymers, cross-linkers, and the like. "Polymerizable groups" are groups that can undergo chain growth polymerization, such as free radical and / or ionic polymerization (e.g., cationic polymerization), for example a carbon- carbon double bond which can polymerize when subjected to radical polymerization initiation conditions. Non-limiting examples of free radical polymerizable groups include (meth)acrylates, styrenes, vinyl ethers, (meth)acrylamides, N-vinyllactams, N-vinylamides, O-vinylcarbamates, O-vinylcarbonates, and other vinyl groups. Preferably, the free radical polymerizable groups comprise (meth)acrylate, (meth)acrylamide, N-vinyllactam, N-vinylamide, and styryl functional Attorney Docket No. JSV7183WOPCT1 groups, and mixtures of any of the foregoing. More preferably, the free radical polymerizable groups comprise (meth)acrylates, (meth)acrylamides, and mixtures thereof. The polymerizable group may be unsubstituted or substituted. For instance, the nitrogen atom in (meth)acrylamide may be bonded to a hydrogen, or the hydrogen may be replaced with alkyl or cycloalkyl (which themselves may be further substituted). A "monomer" is a mono-functional molecule which can undergo chain growth polymerization, and in particular, free radical polymerization, thereby creating a repeating unit in the chemical structure of the target macromolecule. Some monomers have di-functional impurities that can act as cross-linking agents. A "hydrophilic monomer" is a monomer which yields a clear single phase solution when mixed with deionized water at 25°C at a concentration of 5 weight percent. A "hydrophilic component" is a monomer, macromer, prepolymer, initiator, cross-linker, additive, or polymer which yields a clear single phase solution when mixed with deionized water at 25°C at a concentration of 5 weight percent. A "hydrophobic component" is a monomer, macromer, prepolymer, initiator, cross-linker, additive, or polymer which is slightly soluble or insoluble in deionized water at 25°C. A "macromolecule" is an organic compound having a number average molecular weight of greater than 1500 Daltons and may be reactive or non-reactive. A "macromonomer" or "macromer" is a macromolecule that has one group that can undergo chain growth polymerization, and in particular, free radical polymerization, thereby creating a repeating unit in the chemical structure of the target macromolecule. Typically, the chemical structure of the macromer is different than the chemical structure of the target macromolecule, that is, the repeating unit of the macromer’s pendent group is different than the repeating unit of the target macromolecule or its main chain. The difference between a monomer and a macromer is merely one of chemical structure, molecular weight, and molecular weight distribution of the pendent group. As a result, and as used herein, the patent literature occasionally defines monomers as polymerizable compounds having relatively low molecular weights of about 1,500 Daltons or less, which inherently includes some macromers. In particular, monomethacryloxypropyl terminated mono-n-butyl terminated polydimethylsiloxane (molecular weight = 500-1500 g / mol) (mPDMS) and mono-(2-hydroxy-3-methacryloxypropyl)- propyl ether terminated mono-n-butyl terminated polydimethylsiloxane (molecular weight = 500-1500 g / mol) (OH-mPDMS) may be referred to as monomers or macromers. Furthermore, Attorney Docket No. JSV7183WOPCT1 the patent literature occasionally defines macromers as having one or more polymerizable groups, essentially broadening the common definition of macromer to include prepolymers. As a result and as used herein, di-functional and multi-functional macromers, prepolymers, and cross- linkers may be used interchangeably. A "polymer" is a target macromolecule composed of the repeating units of the monomers used during polymerization. A "homopolymer" is a polymer made from one monomer; a "copolymer" is a polymer made from two or more monomers; a "terpolymer" is a polymer made from three monomers. A "block copolymer" is composed of compositionally different blocks or segments. Diblock copolymers have two blocks. Triblock copolymers have three blocks. "Comb or graft copolymers" are made from at least one macromer. A "repeating unit" is the smallest group of atoms in a polymer that corresponds to the polymerization of a specific monomer or macromer. A copolymer may be depicted via a partial chemical formula: — [XX]x—[YY]y—, wherein XX and YY are polymerized monomer units, and x and y represent the relative amounts of each monomer used to make the polymer. Unless specified to the contrary, depiction of polymer in this fashion does not convey any particle monomer sequence; polymers may be block copolymers, alternating copolymers, random copolymer, etc. An "initiator" is a molecule that can decompose into radicals which can subsequently react with a monomer to initiate a free radical polymerization reaction. A thermal initiator decomposes at a certain rate depending on the temperature; typical examples are azo compounds such as 1,1’-azobisisobutyronitrile and 4,4’-azobis(4-cyanovaleric acid), peroxides such as benzoyl peroxide, tert-butyl peroxide, tert-butyl hydroperoxide, tert-butyl peroxybenzoate, dicumyl peroxide, and lauroyl peroxide, peracids such as peracetic acid and potassium persulfate as well as various redox systems. A photo-initiator decomposes by a photochemical process; typical examples are derivatives of benzil, benzoin, acetophenone, benzophenone, camphorquinone, and mixtures thereof as well as various monoacyl and bisacyl phosphine oxides and combinations thereof. A "cross-linking agent" or “cross-linking compound” is a di-functional or multi- functional monomer or macromer which can undergo polymerization at two or more locations on Attorney Docket No. JSV7183WOPCT1 the molecule, thereby creating branch points and a polymeric network. Common examples are ethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, methylene bisacrylamide, triallyl cyanurate, and the like. A "prepolymer" is a reaction product of monomers which contains remaining polymerizable groups capable of undergoing further reaction to form a polymer. The terms "reactive mixture" and "reactive monomer mixture" refer to the mixture of components (both retained and non-retained) which are mixed together and, when subjected to polymerization conditions, result in formation of a polymeric network as well as biomedical devices, ophthalmic devices, intraocular implants, contact lenses, and intraocular lenses made therefrom. The reactive mixture may comprise retained components such as monomers, macromers, prepolymers, cross-linkers, and initiators, additives such as wetting agents, polymers, dyes, light absorbing compounds such as UV / HEV absorbers, pigments, photochromic compounds, pharmaceutical compounds, and / or nutraceutical compounds, any of which may be reactive or non-reactive but are capable of being retained within the resulting biomedical device. The reactive mixture may also contain non-retained components which are intended to be removed from the device prior to its use, such as diluents. It will be appreciated that a wide range of additives may be added based upon the biomedical device which is made and its intended use. Concentrations of components of the reactive mixture are expressed as weight percentages of all retained components in the reactive mixture, therefore excluding non-retained components such as diluent. When diluents are used, their concentrations are expressed as weight percentages based upon the amount of all components in the reactive mixture (including the diluent). "Retained components" are the polymerizable compounds (such as monomers, macromers, oligomers, prepolymers, and cross-linkers) in the reactive mixture, as well as any other components in the reactive mixture which are intended to substantially remain in the polymeric network after polymerization and all work-up steps (such as extraction steps) and packaging steps have been completed. Retained components may be retained in the polymeric network by covalent bonding, hydrogen bonding, electrostatic interactions, the formation of interpenetrating polymeric networks, or any other means. Components that are intended to release from the biomedical device once it is in use are still considered "retained components." For example, pharmaceutical or nutraceutical components in a contact lens which are intended to be released during wear are considered "retained components." Components that are intended to Attorney Docket No. JSV7183WOPCT1 be removed from the polymeric network during the manufacturing process (e.g., by extraction), such as diluents, are "non-retained components." The term "multi-functional" refers to a component having two or more polymerizable groups. The term "mono-functional" refers to a component having one polymerizable group. The terms "halogen" or "halo" indicate fluorine, chlorine, bromine, and iodine. "Alkyl" or “aliphatic” are used interchangeably herein and refer to an optionally substituted linear or branched alkyl group containing the indicated number of carbon atoms. If no number is indicated, then alkyl (including any optional substituents on alkyl) may contain any of 1 to 16 carbon atoms, including 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, and 16 carbon atoms. Preferably, the alkyl group contains 1 to 10 carbon atoms, including 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 carbon atoms, alternatively 1 to 8 carbon atoms, including 1, 2, 3, 4, 5, 6, 7, and 8 carbon atoms, alternatively 1 to 6 carbon atoms, including 1, 2, 3, and 4 carbon atoms, or alternatively 1 to 4 carbon atoms, including 1, 2, 3, and 4. Examples of alkyl include methyl, ethyl, propyl, isopropyl, butyl, iso-, sec- and tert-butyl, pentyl, hexyl, heptyl, 3-ethylbutyl, and the like. Examples of substituents on alkyl include 1, 2, or 3 groups independently selected from hydroxy, amino, amido, oxa, carboxy, alkyl carboxy, carbonyl, alkoxy, thioalkyl, carbamate, carbonate, halogen, phenyl, benzyl, and combinations thereof. "Alkylene" means a divalent alkyl group, such as -CH2-, -CH2CH2-, -CH2CH2CH2-, -CH2CH(CH3)CH2-, and - CH2CH2CH2CH2-. "Haloalkyl" refers to an alkyl group as defined above substituted with one or more halogen atoms, where each halogen is independently F, Cl, Br or I. A preferred halogen is F. Preferred haloalkyl groups contain 1-6 carbons, more preferably 1-4 carbons, and still more preferably 1-2 carbons. "Haloalkyl" includes perhaloalkyl groups, such as -CF3- or -CF2CF3-. "Haloalkylene" means a divalent haloalkyl group, such as -CH2CF2-. “Hydroxy” refers to an -OH group. “Hydroxyalkyl” refers to an alkyl group, as defined herein, substituted with at least one hydroxy group. Representative examples of hydroxyalkyl include, but are not limited to, hydroxymethyl, 2-hydroxyethyl, 3-hydroxypropyl, 2,3-dihydroxypropyl, 2,3-dihydroxypentyl, 4- hydroxybutyl, 2-ethyl-4-hydroxyheptyl, 3,4-dihydroxybutyl, and 5-hydroxypentyl. "Cycloalkyl" or “cycloaliphatic” are used interchangeably herein and refer to an optionally substituted cyclic hydrocarbon containing the indicated number of ring carbon atoms. Attorney Docket No. JSV7183WOPCT1 If no number is indicated, then cycloalkyl may contain 3 to 20 ring carbon atoms (e.g., 3 to 12 ring carbon atoms). Cycloaliphatic groups can be monocyclic, bicyclic, tricyclic, bridged, fused, and / or spirocyclic. Cycloaliphatic groups can also have one or more double bonds, provided that the group is not fully aromatic. Preferred monocyclic cycloaliphatic groups are C3-C8 cycloalkyl groups, C3-C7 cycloalkyl, more preferably C4-C7 cycloalkyl, and still more preferably C5-C6 cycloalkyl. Examples of cycloalkyl include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl and cyclooctyl. Examples of substituents on cycloalkyl include 1, 2, or 3 groups independently selected from alkyl, hydroxy, amino, amido, oxa, carbonyl, alkoxy, thioalkyl, amido, carbamate, carbonate, halo, phenyl, benzyl, and combinations thereof. "Cycloalkylene" means a divalent cycloalkyl group, such as 1,2-cyclohexylene, 1,3- cyclohexylene, or 1,4- cyclohexylene. "Heterocycloalkyl" refers to a cycloalkyl ring or ring system as defined above in which at least one ring carbon has been replaced with a heteroatom selected from nitrogen, oxygen, and sulfur. The heterocycloalkyl ring is optionally fused to or otherwise attached to other heterocycloalkyl rings and / or non-aromatic hydrocarbon rings and / or phenyl rings. Preferred heterocycloalkyl groups have from 5 to 7 members. More preferred heterocycloalkyl groups have 5 or 6 members. Heterocycloalkylene means a divalent heterocycloalkyl group. "Aryl" refers to an optionally substituted aromatic hydrocarbon ring system containing at least one aromatic ring. The aryl group contains the indicated number of ring carbon atoms. If no number is indicated, then aryl may contain 6 to 14 ring carbon atoms. The aromatic ring may optionally be fused or otherwise attached to other aromatic hydrocarbon rings or non-aromatic hydrocarbon rings. Examples of aryl groups include phenyl, naphthyl, and biphenyl. Preferred examples of aryl groups include phenyl. Examples of substituents on aryl include 1, 2, or 3 groups independently selected from alkyl, hydroxy, amino, amido, oxa, carboxy, alkyl carboxy, carbonyl, alkoxy, thioalkyl, carbamate, carbonate, halo, phenyl, benzyl, and combinations thereof. "Arylene" means a divalent aryl group, for example 1,2-phenylene, 1,3-phenylene, or 1,4-phenylene. “Arylalkyl” refers to an aryl group, as defined herein, appended to the parent molecular moiety through an alkyl group, as defined herein. Representative examples of arylalkyl include phenylmethyl (i.e. benzyl), phenylethyl, and phenylpropyl. Attorney Docket No. JSV7183WOPCT1 "Heteroaryl" refers to an aryl ring or ring system, as defined above, in which at least one ring carbon atom has been replaced with a heteroatom selected from nitrogen, oxygen, and sulfur. The heteroaryl ring may be fused or otherwise attached to one or more heteroaryl rings, aromatic or nonaromatic hydrocarbon rings or heterocycloalkyl rings. Examples of heteroaryl groups include pyridyl, furyl, and thienyl. "Heteroarylene" means a divalent heteroaryl group. "Alkoxy" refers to an alkyl group attached to the parent molecular moiety through an oxygen bridge. Examples of alkoxy groups include, for instance, methoxy, ethoxy, propoxy and isopropoxy. "Thioalkyl" means an alkyl group attached to the parent molecule through a sulfur bridge. Examples of thioalkyl groups include, for instance, methylthio, ethylthio, n-propylthio and iso-propylthio. "Aryloxy" refers to an aryl group attached to a parent molecular moiety through an oxygen bridge. Examples include phenoxy. “Arylthio” refers to an aryl group attached to a parent molecular moiety through a sulfur bridge. Examples include phenylthiol. "Cyclic alkoxy" means a cycloalkyl group attached to the parent moiety through an oxygen bridge. "Alkylamine" refers to an alkyl group attached to the parent molecular moiety through an -NH bridge. Alkyleneamine means a divalent alkylamine group, such as -CH2CH2NH-. "Siloxanyl" refers to a structure having at least one Si-O-Si bond. Thus, for example, siloxanyl group means a group having at least one Si-O-Si group (i.e. a siloxane group), and siloxanyl compound means a compound having at least one Si-O-Si group. "Siloxanyl" encompasses monomeric (e.g., Si-O-Si) as well as oligomeric / polymeric structures (e.g., -[Si- O]n-, where n is 2 or more). Each silicon atom in the siloxanyl group is substituted with independently selected RAgroups (where RAis as defined in formula A options (b)-(i)) to complete their valence. Formula A. The silicone-containing component may comprise one or more polymerizable compounds of Formula A:     wherein:  Attorney Docket No. JSV7183WOPCT1 at least one RAis a group of formula Rg-L- wherein Rg is a polymerizable group and L is a linking group, and the remaining RAare each independently: a. Rg-L-, b. C1-C16 alkyl optionally substituted with one or more hydroxy, amino, amido, oxa, carboxy, alkyl carboxy, carbonyl, alkoxy, amido, carbamate, carbonate, halo, phenyl, benzyl, or combinations thereof, c. C3-C12cycloalkyl optionally substituted with one or more alkyl, hydroxy, amino, amido, oxa, carbonyl, alkoxy, amido, carbamate, carbonate, halo, phenyl, benzyl, or combinations thereof, d. a C6-C14aryl group optionally substituted with one or more alkyl, hydroxy, amino, amido, oxa, carboxy, alkyl carboxy, carbonyl, alkoxy, amido, carbamate, carbonate, halo, phenyl, benzyl, or combinations thereof, e. halo, f. alkoxy, cyclic alkoxy, or aryloxy, g. siloxy, h. alkyleneoxy-alkyl or alkoxy-alkyleneoxy-alkyl, such as polyethyleneoxyalkyl, polypropyleneoxyalkyl, or poly(ethyleneoxy-co-propyleneoxyalkyl), or a monovalent siloxane chain comprising from 1 to 100 siloxane repeat units optionally substituted with alkyl, alkoxy, hydroxy, amino, oxa, carboxy, alkyl carboxy, alkoxy, amido, carbamate, halo or combinations thereof; and n is from 0 to 500 or from 0 to 200, or from 0 to 100, or from 0 to 20, where it is understood that when n is other than 0, n is a distribution having a mode equal to a stated value. When n is 2 or more, the SiO units may carry the same or different RAsubstituents and if different RAsubstituents are present, the n groups may be in random or block configuration. In Formula A, three RAmay each comprise a polymerizable group, alternatively two RAmay each comprise a polymerizable group, or alternatively one RAmay comprise a polymerizable group. Attorney Docket No. JSV7183WOPCT1 "Silyl" refers to a structure of formula R3Si- and "siloxy" refers to a structure of formula R3Si-O-, where each R in silyl or siloxy is independently selected from trimethylsiloxy, C1-C8 alkyl (preferably C1-C3alkyl, more preferably ethyl or methyl), and C3-C8cycloalkyl. "Alkyleneoxy" refers to groups of the general formula -(alkylene-O)p- or -(O-alkylene)p-, wherein alkylene is as defined above, and p is from 1 to 200, or from 1 to 100, or from 1 to 50, or from 1 to 25, or from 1 to 20, or from 1 to 10, wherein each alkylene is independently optionally substituted with one or more groups independently selected from hydroxyl, halo (e.g., fluoro), amino, amido, ether, carbonyl, carboxyl, and combinations thereof. If p is greater than 1, then each alkylene may be the same or different and the alkyleneoxy may be in block or random configuration. When alkyleneoxy forms a terminal group in a molecule, the terminal end of the alkyleneoxy may, for instance, be a hydroxy or alkoxy (e.g., HO-[CH2CH2O]p- or CH3O-[CH2CH2O]p-). Examples of alkyleneoxy include polyethyleneoxy, polypropyleneoxy, polybutyleneoxy, and poly(ethyleneoxy-co-propyleneoxy). "Oxaalkylene" refers to an alkylene group as defined above where one or more non- adjacent CH2 groups have been substituted with an oxygen atom, such as -CH2CH2OCH(CH3)CH2-. "Thiaalkylene" refers to an alkylene group as defined above where one or more non-adjacent CH2groups have been substituted with a sulfur atom, such as -CH2CH2SCH(CH3)CH2-. The term "linking group" refers to a moiety that links a polymerizable group to the parent molecule. The linking group may be any moiety that is compatible with the compound of which it is a part, and that does not undesirably interfere with the polymerization of the compound, is stable under the polymerization conditions as well as the conditions for the processing and storage of the final product. For instance, the linking group may be a bond, or it may comprise one or more alkylene, haloalkylene, amide, amine, alkyleneamine, carbamate, ester (-CO2-), arylene, heteroarylene, cycloalkylene, heterocycloalkylene, alkyleneoxy, oxaalkylene, thiaalkylene, haloalkyleneoxy (alkyleneoxy substituted with one or more halo groups, e.g., - OCF2-, -OCF2CF2-, -OCF2CH2-), siloxanyl, alkylenesiloxanyl, or combinations thereof. The linking group may optionally be substituted with 1 or more substituent groups. Suitable substituent groups may include those independently selected from alkyl, halo (e.g., fluoro), hydroxyl, HO-alkyleneoxy, MeO-alkyleneoxy, siloxanyl, siloxy, siloxy-alkyleneoxy-, siloxy- alkylene-alkyleneoxy- (where more than one alkyleneoxy groups may be present and wherein Attorney Docket No. JSV7183WOPCT1 each methylene in alkylene and alkyleneoxy is independently optionally substituted with hydroxyl), ether, amine, carbonyl, carbamate, and combinations thereof. The linking group may also be substituted with a polymerizable group, such as (meth)acrylate (in addition to the polymerizable group to which the linking group is linked). Preferred linking groups include C1-C8 alkylene (preferably C2-C6 alkylene) and C1-C8 oxaalkylene (preferably C2-C6oxaalkylene), each of which is optionally substituted with 1 or 2 groups independently selected from hydroxyl and siloxy. Preferred linking groups also include carboxylate, amide, C1-C8 alkylene-carboxylate-C1-C8 alkylene, or C1-C8 alkylene-amide-C1-C8 alkylene. When the linking group is comprised of combinations of moieties as described above (e.g., alkylene and cycloalkylene), the moieties may be present in any order. For instance, if in Formula A above, L is indicated as being -alkylene-cycloalkylene-, then Rg-L may be either Rg- alkylene-cycloalkylene-, or Rg-cycloalkylene-alkylene-. Notwithstanding this, the listing order represents the preferred order in which the moieties appear in the compound starting from the terminal polymerizable group (Rg or Pg) to which the linking group is attached. For example, if in Formula A, L is indicated as being alkylene-cycloalkylene, then Rg-L is preferably Rg- alkylene-cycloalkylene-. The term "electron withdrawing group" (EWG) refers to a chemical group which withdraws electron density from the atom or group of atoms to which the electron withdrawing group is attached. Examples of EWGs include, but are not limited to, cyano, amide, ester, keto, or aldehyde. A preferred EWG is cyano (CN). The terms "light absorbing compound" refers to a chemical material that absorbs light within the visible spectrum (e.g., in the 380 to 780 nm range). A "high energy radiation absorber," "UV / HEV absorber," "UV / HEV absorbing compound," or "high energy light absorbing compound" is a chemical material that absorbs various wavelengths of ultraviolet light, high energy visible light, or both. A material's ability to absorb certain wavelengths of light can be determined by measuring its UV / VIS transmission spectrum. Compounds that exhibit no absorption at a particular wavelength will exhibit substantially 100 percent transmission at that wavelength. Conversely, compounds that completely absorb at a particular wavelength will exhibit substantially 0 % transmission at that wavelength. If the amount of a material's transmission is indicated as a percentage for a particular wavelength range, it is to be Attorney Docket No. JSV7183WOPCT1 understood that the material exhibits the percent transmission at all wavelengths within that range. When the compounds described herein contain olefinic double bonds or other centers of geometric asymmetry, and unless otherwise specified, it is intended that the compounds include the cis, trans, Z- and E- configurations. Likewise, all tautomeric and salt forms are also intended to be included. The term "optional substituent" means that a hydrogen atom in the underlying moiety is optionally replaced by a substituent. Any substituent may be used that is sterically practical at the substitution site and is synthetically feasible. Identification of a suitable optional substituent is well within the capabilities of an ordinarily skilled artisan. Examples of an "optional substituent" include, without limitation, C1-C6 alkyl, C1-C6 alkoxy, C1-C6 thioalkyl, C3-C7 cycloalkyl, aryl, halo, hydroxy, amino, NR4R5, benzyl, SO3H, or SO3Na, wherein R4and R5are independently H or C1-C6alkyl. The foregoing substituents may be optionally substituted by an optional substituent (which, unless otherwise indicated, is preferably not further substituted). For instance, alkyl may be substituted by halo (resulting, for instance, in CF3). Unless otherwise indicated, ratios, percentages, parts, and the like are by weight. Unless otherwise indicated, numeric ranges, for instance as in "from 2 to 10," are inclusive of the numbers defining the range (e.g., 2 and 10). In some embodiments, the reactive monomer mixtures disclosed herein include at least one polyamide. As used herein, the term "polyamide" refers to polymers and copolymers comprising repeating units containing amide groups. The polyamide may comprise cyclic amide groups, acyclic amide groups and combinations thereof, and may be any polyamide known to those of skill in the art. Acyclic polyamides comprise pendant acyclic amide groups and are capable of association with hydroxyl groups. Cyclic polyamides comprise cyclic amide groups and are capable of association with hydroxyl groups. Polyamides suitable for use with the presently disclosed compositions and methods are disclosed in U.S. Patent Application Publication No.20180009922 for SILICONE HYDROGELS COMPRISING HIGH LEVELS OF POLYAMIDES to Alli et al., published Jan.11, 2018, and U.S. Patent Application Publication No.20180011222 for SILICONE HYDROGELS COMPRISING POLYAMIDES to Alli et al., published Jan.11, 2018, each of which are incorporated herein by reference in their entirety. Attorney Docket No. JSV7183WOPCT1 “Abbe number,” also known as the V-number or constringence of a transparent material, is a measure of the material’s dispersion, i.e., variation of refractive index versus wavelength, with high values of V indicating low dispersion. The Abbe number of a material is defined as: ; where nD, nFand nCare the refractive at the wavelengths of the Fraunhofer D-, F- and C- spectral lines (589.3 nm, 486.1 nm and 656.3 nm respectively). “Refractive index” is defined as: ; where c is the speed of light in a vacuum and v is the phase velocity of light in the medium. “T(g)” refers to glass transition temperature, which may be determined on a DSC Q2000 TA instrument at heating rates of 10°C / minute and cooling rates of 5°C / minute under a nitrogen gas atmosphere. The glass transition temperatures are determined from the first and second heating scans (1stscan and 2ndscan, respectively). B. Compositions Disclosed herein are single-piece intraocular lens including an optic portion including an optic polymer system, a haptic portion including a haptic polymer system, and an interface portion including block copolymers, wherein the block copolymer includes a optic polymer block and a haptic polymer block. As used herein, the “interface” refers to the portion of the lens wherein the optic polymer is covalently bonded to the haptic polymer. Each block copolymer includes a transition zone wherein a chain of optic polymer units extend into the optic portion, and chain of haptic polymer units monomeric units extend into the haptic portion. The interface is defined by the presence of these transition zones. As described herein, the single piece intraocular lenses of the present invention can be prepared by providing an optic portion derived from the polymerization of an optic polymer. This process results in an optic portion with residual reactive functional groups on the surface of the optic. These functional groups can serve as the basis for a further polymerization reaction to prepare the haptic polymer; the polymerization of the haptic polymer begins at the reactive functional group, resulting in the block copolymer and creating the interface. Attorney Docket No. JSV7183WOPCT1 The optic polymer system and haptic polymer are distinguished in one or more ways, for example in some implementations the one or more of monomers used to make the haptic polymer system are not used to make the optic polymer system, and vice versa. In some embodiments the haptic polymer system can be a crosslinked polymer, while the optic polymer is not crosslinked. In other embodiments, the haptic polymer and the optic polymer can each be crosslinked polymers, but the crosslinking density is not the same. As used herein, “differently crosslinked” and “crosslinked differently” includes embodiments in which one system is crosslinked and the other is not, embodiments in which both systems are crosslinked at different crosslinking densities, and embodiments in which the systems are crosslinked using different crosslinking agents. In some the haptic includes one or more polymers and / or crosslinked polymers that is not of optical quality and therefore cannot be present in the optic. In some implementations, the haptic polymer system has a different T(g) than the optic polymer system. In some implementations, the haptic polymer system is stiffer than the optic polymer system. For the purposes of the present disclosure, when a specific characteristic is used to distinguish the optic and haptic polymers, it refers to individual polymer systems, i.e., not including the interface block copolymers. In some implementations, the optic polymer can have a T(g)from -20°C. to 37°C., from - 10°C. to 37°C., from 0°C. to 37°C., from 0°C. to 30°C., from 0°C. to 20°C., from 0°C. to 10°C., from -10°C. to 10°C., from -10°C. to 5°C., or from -5°C. to 10°C. In some implementations, the haptic polymer can have a T(g)that is 5-10°C. greater than the optic polymer T(g). In some implementations, the haptic polymer can have a T(g) that is 2- 5°C. greater than the optic polymer T(g). In some implementations, the haptic polymer can have a T(g)that is 10-20°C. greater than the optic polymer T(g). In some implementations, the haptic polymer can have a T(g) that is 5-15°C. greater than the optic polymer T(g). In some implementations, the haptic polymer can have a T(g) that is 15-30°C. greater than the optic polymer T(g). In certain implementations, the haptic polymer system has a different refractive index than the optic polymer system. Generally, the optic polymer system will exhibit a refractive index of at least 1.45 and an Abbe number of at least 39. As the haptic polymer system does not directly modulate light received by the eye, it can have lower refractive indices or Abbe numbers without diminishing the optical performance of the IOL. In certain implementations, the haptic Attorney Docket No. JSV7183WOPCT1 polymer system can have a refractive index that is 90% or less, 75% or less, 50% or less, 25% or less, 10% or less, or 2% or less the refractive index of the optical polymer system. The interface portion can be a relatively minor part of the entire IOL. For example, in some implementations the interface has a width that is 5% or less the diameter of the optic. In some implementations the interface can have a width that is 2% or less, 1% or less, 0.5% or less, 0.25% or less, 0.1% or less, 0.05% or less, or 0.01% or less the diameter of the optic. In implementations when the optic is not circular, “diameter” refers to the longest axis across the surface of the optic. As used herein, width refers to axis parallel to the diameter of the optic portion. Thickness is the axis perpendicular to the diameter of the optic. In some embodiments, the thickness of the interface will be about the same as the thickness of the optic. The single piece IOLs disclosed herein may have encircling haptic system or an open loop haptic system. In some implementations, the haptic polymer system includes a poly(thiol-ene), a poly(meth)acrylate, a copolymer thereof, or a combination thereof. The haptic polymer system may include a crosslinked poly(thiol-ene), crosslinked poly(meth)acrylate, or a combination thereof. In some implementations, the crosslinked poly(thiol-ene) may be a click-crosslinked poly(thiol-ene) and the crosslinked poly(meth)acrylate may be a click-crosslinked poly(meth)acrylate. A click crosslinked polymer is one in which the crosslinking has been performed via click chemistry, either a [2,3] cycloaddition such as azide / alkyne cycloaddition or with a different 1,3 dipole such as nitrone, nitrile oxide, diazo, acyl diazo, and azoxy, tetrazine / alkene inverse demand Diels Alder cycloaddition. In some implementations, the click crosslinked polymer is crosslinked via a linker having a heterocyclic ring, for example a 1,2,3 triazine, 1,2 diazine, 1,2 diazole, 1,2 oxazole. In some implementations, the crosslinked poly(thiol-ene) may be a thiol-crosslinked poly(thiol-ene) and the crosslinked poly(meth)acrylate may be a thiol-crosslinked poly(meth)acrylate. A thiol-crosslinked polymer is one in which the crosslinking is performed by reacting a thiol with an appropriate alkene or alkyne, for example an allyl compound, a (meth)acryl compound, and the like. For example, a thiol-crosslinked poly(meth)acrylate can be prepared by crosslinking a poly(meth)acrylate having thiol groups with a thiol crosslinking compound. Suitable thiol crosslinking compounds are those having two or more thiol-reactive Attorney Docket No. JSV7183WOPCT1 functional groups, for instance (meth)acryl groups, norbornenyl groups, allyl groups, propargyl groups, maleimide groups, or a combination thereof. In some implementations, poly(meth)acrylate having thiol groups can be prepared by polymerizing a mixture including a compound of Formula (1C) and Formula (2C): wherein: Rc1is selected from H and CH3; Xc1is selected from O and NH, Rc2is a polyether, aliphatic, or cycloaliphatic group; Rc3is selected from H and CH3; Xc2is selected from O and NH, and Rc4is a polyether, aliphatic, or cycloaliphatic group; wherein Rc4does not contain a thiol group. The poly(meth)acrylate having thiol groups may be represented by the formula: HS Rc2,  wherein x and y denote the ratio of and Formula (2C). In some implementations, wherein the ratio of the compound of Formula (1C) to compound of Formula (2C) is from 1:100 to 1:1, from 1:100 to 1:70, from 1:100 to 1:50, from 1:100 to 1:25, from 1:75 to 1:25, from 1:75 to 1:50, or from 1:50 to 1:25. In certain implementations, the poly(meth)acrylate having thiol groups is formed from a mixture having the compounds of Formula (1C) and (2C) as the only reactive monomers. In Attorney Docket No. JSV7183WOPCT1 some implementations, the mixture can include additional monomer compounds, for example, a compound of Formula (3C) [Formula (3C)], wherein: Rc5is selected from H and CH3; Xc3is selected from O and NH, Rc6is a polyether, aliphatic, or cycloaliphatic group; provided that the compound of Formula (3C) is different than the compound of Formula (2C) Additional mono (meth)acryl compounds can be included in the mixture as well. In some implementations, the poly(meth)acrylate having thiol groups is crosslinked with a compound of Formula (C*): Xc*-Rc*-Xc*[Formula (C*)], wherein Rc*is a polyether, aliphatic, or cycloaliphatic group, and Xc*has the formula: , Xc**is Rc**is selected from H and CH3. In certain implementations, the ratio of the compound of Formula (1C) to compound of Formula (C*) is from 5:1 to 1:5, from 2:1 to 1:2, from 5:1 to 1:1, from 5:2.5 to 1:1, from 2.5:1 to 1:1, from 1:2.5 to 1:1, from 1:5 to 1:2.5, or from 1:5 to 1:1. In some implementations, the compound of Formula (C*) is triallyl cyanurate, divinyl benzene, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate. In some implementations, the haptic polymer system comprises a thiol-Michael polymer. Thiol-Michael polymers are those formed via reaction of thiol monomer having at least two thiol Attorney Docket No. JSV7183WOPCT1 group with a Michael monomer having at least two α,β-unsaturated systems, e.g., α,β- unsaturated carbonyl, α,β-unsaturated nitrile, α,β-unsaturated sulfone, etc. In some implementation the thiol monomer can have 2, 3, 4, 5, or 6 thiol groups. In some implementations, the thiol monomer can include a compound having the formula: RtRtRtor a combination t wherein R has the wherein n independently from 0- 5-10, 5-25, 10-50, or 25-50; Rfis in each case independently selected from null, CH2, CH2CH2, or CH2CH2CH2; and Z is in each case independently selected from null, O, C(=O), C(=O)O, or C(=O)NH. In certain implementations, the thiol monomer can include at least two thiol-containing compounds, for example a di-thiol of Formula (1T): [Formula (1T)], wherein Rthas the formula: wherein n independently from 0-50, 5-25, 10-50, or 25-50; Rfis null, CH2, CH2CH2, or CH2CH2CH2; and Z is null, O, C(=O), C(=O)O, or C(=O)NH; and and a tetra-thiol of Formula (2T): Rt*Rt*[Formula (2T)],wherein Rt*has the formula: Attorney Docket No. JSV7183WOPCT1 wherein n* independently from 0-100, preferably 1-5, 1-10, 5-10, 5-25, 10-50, or 25-50; Rf*is null, CH2, CH2CH2, or CH2CH2CH2; and Z* is null, O, C(=O), C(=O)O, or C(=O)NH. In certain implementations, the thiol monomer includes one or more compounds selected from: , In certain implementations, the thiol monomer includes a compound having the formula: , wherein n’ is from 3-10, and a , In certain Formula (1T) to the compound of Formula (2T) is from 100:1 to 1:100, from 100:1 to 1:1, from 50:1 to 1:1, from 25:1 to 1:1, from 10:1 to 1:1, from 5:1 to 1:1, from 2.5:1 to 1:1, from 100:1 to 50:1, from 75:1 to 25:1, from 50:1 to 25:1, from 50:1 to 10:1, from 10:1 to 5:1, from 10:1 to 2.5:1, from 5:1 to 2.5:1, from 10:1 to 1:10, from 5:1 to 1:5, from 2.5:1 to 1:2.5, from 1:1 to 1:2.5, from 1:1 to 1:10, from 1:1 to 1:25, from 1:1 to 50:1 from 1:25 to 50:1, from 1:50 to 1:100, from 1:25 to 1:75, from 1:25 to 1:50, from 1:2.5 to 5:1, from 1:2.5 to 1:10, from 1:5 to 1:10, or from 1:10 to 1:25. Attorney Docket No. JSV7183WOPCT1 The Michael monomer can include a compound having 2, 3, 4, 5, or 6 (meth)acryl groups, for example 2, 3, 4, 5, or 6 (meth)acrylate groups, 2, 3, 4, 5, or 6 (meth)acrylamide groups. In certain implementations, the Michael monomer include a compound having the formula:   or a combination wherein Rmhas the formula: , wherein Rmmis H or CH3; m is independently from 0-100, preferably 1-5, 1-10, 5-10, 5-25, 10-50, or 25-50; and Z1is null, O, NH. In some implementations the Michael monomer can include ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate, or a combination thereof. In some implementations, the mole ratio Michael monomer to the thiol monomer can be from 10:1 to 1:10, from 10:1 to 5:1, from 5:1 to 1:1, from 5:1 to 2.5:1, from 2.5:1 to 1:1., from 2:1 to 1:2, from 1:1 to 1:2.5, from 1:2.5 to 1:5, from 1:1 to 1:5, from 1:5 to 1:10, or from 1:1 to 1:10. For implementations in which the Michael monomer and / or the thiol monomer includes multiple compounds, the ratios above relate to the combined total of each Michael compound and / or thiol compound. Also disclosed herein are single piece IOLs having multiple distinct haptic polymer systems. In some implementations, the haptic system can include a core haptic polymer system and a shell haptic polymer system. The shell covers at least a portion of the core, and in some implementations the shell completely encapsulates the core. In some implementations the shell Attorney Docket No. JSV7183WOPCT1 haptic polymer is a biostable, biocompatible polymer system; because the core is partially or completely shielded from living tissue a considerably wider variety of polymer systems can be included. In certain implementations, the core haptic polymer can be formed from different monomers than the shell haptic polymer system. In some implementations the core haptic polymer can be differently crosslinked than the shell haptic polymer system. In some implementations the core haptic polymer system is not crosslinked and the shell haptic polymer system is crosslinked. In some implementations both the core and shell haptic polymer systems are crosslinked, and the shell haptic polymer has greater crosslinking density than the core haptic polymer system. In some implementations the shell haptic polymer system is crosslinked by a different crosslinking compound than the core haptic polymer system. In some embodiments, the shell haptic polymer system can have a different T(g) than the haptic core polymer system. In certain embodiments, the T(g)of the haptic core polymer system can be less than the T(g) of the haptic shell polymer system, for example at least 5°C. less, at least 10°C less, at least 15°C less at least 20°C less, or at least 25°C less. In certain implementations, the haptic polymer system can include one or more therapeutic agents. In core / shell and other heterogeneous haptic systems, the therapeutic agent can be present in one polymer system but not the other. For example, the therapeutic agent may be present in the core haptic polymer system but not the shell haptic polymer system. The therapeutic agent may be covalently bonded to the core haptic polymer system, or it may be dispersed (i.e., non-covalently associated) within the core haptic polymer system. Exemplary therapeutic agents include antimicrobial agents such as antibacterial and antibiotic agents , antifungal agents , antiviral agents , anti - inflammatory agents , growth factors , analgesics , anesthetics , tissue matrix degeneration inhibitors , anti - cancer agents , hemostatic agents , other agents that elicit a biological response and combinations thereof. Non - limiting examples of antimicrobial agents include Ionic Silver, Aminoglycosides, Streptomycin, Polypeptides, Bacitracin, Triclosan, Tetracyclines, Doxycycline, Minocycline, Demeclocycline, Tetracycline, Oxytetracycline, Chloramphenicol, Nitrofurans, Furazolidone, Nitrofurantoin, Beta - lactams, Penicillins, Amoxicillin, Amoxicillin + Clavulanic Acid, Azlocillin, Flucloxacillin, Ticarcillin,Piperacillin + tazobactam, Tazocin, Biopiper TZ , Zosyn, Carbapenems, Imipenem, Meropenem, Ertapenem, Doripenem, Biapenem, Panipenem / Attorney Docket No. JSV7183WOPCT1 betamipron, Quinolones, Ciprofloxacin, Enoxacin, Gatifloxacin, Gemifloxacin, Levofloxacin, Lomefloxacin, Moxifloxacin, Nalidixic Acid, Norfloxacin, Sulfonamides, Mafenide, Sulfacetamide, Sulfadiazine, Silver Sulfadiazine, Sulfadimethoxine, Sulfamethizole, Sulfamethoxazole, Sulfasalazine, Sulfisoxazole, Bactrim, Prontosil, Ansamycins, Geldanamycin, Herbimycin, Fidaxomicin, Glycopeptides, Teicoplanin, Vancomycin, Telavancin, Dalbavancin, Oritavancin, Lincosamides, Clindamycin, Lincomycin, Lipopeptide, Daptomycin, Macrolides, Azithromycin, Clarithromycin, Erythromycin, Roxithromycin, Telithromycin, Spiramycin, Oxazolidinones, Linezolid, Aminoglycosides, Amikacin, Gentamicin, Kanamycin, Neomycin, Netilmicin, Tobramycin, Paromycin, Paromomycin, Cephalosporins, Ceftobiprole, Ceftolozane, Cefclidine, Flomoxef, Monobactams, Aztreonam, Colistin, and Polymyxin B. Non - limiting examples of antifungal agents include Triclosan, Polyenes Amphotericin B Candicidin, Filipin, Hamycin, Natamycin, Nystatin, Rimocidin, Azoles, Imidazole, Triazole, Thiazole, Allylamines, Amorolfin, Butenafine, Naftifine, Terbinafine, Echinocandins, Anidulafungin, Caspofungin, Micafungin, Ciclopirox, and Benzoic Acid . Non - limiting examples of antiviral agents include uncoating inhibitors such as, for example, mantadine, Rimantadine, Pleconaril; reverse transcriptase inhibitors such as, for example, Acyclovir, Lamivudine, Antisenses, Fomivirsen, Morpholinos, Ribozymes, Rifampicin; and virucidals such as, for example, Cyanovirin - N , Griffithsin, Scytovirin, a - Lauroyl - L - arginine ethyl ester ( LAE ), and Ionic Silver Non - limiting examples of anti – inflammatory agents include non - steroidal anti - inflammatory agents ( e.g. , Salicylates , Aspirin , Diflunisal , Propionic Acid Derivatives, Ibuprofen, Naproxen, Fenoprofen, and Loxoprofen ), acetic acid derivatives ( e.g., Tolmetin, Sulindac, and Diclofenac) , enolic acid derivatives ( e.g., Piroxicam, Meloxicam, Droxicam, and Lornoxicam ), anthranilic acid derivatives ( e.g. , Mefenamic Acid , Meclofenamic Acid, and Flufenamic Acid ), selective COX - 2 inhibitors ( e.g., Celecoxib ( Celebrex ), Parecoxib, Rofecoxib ( Vioxx ), Sulfonanilides, Nimesulide, and Clonixin), immune selective anti - inflammatory derivatives, corticosteroids ( e.g. , Dexamethasone ), and iNOS inhibitors. Non - limiting examples of growth factors include those that are cell signaling molecules that stimulate cell growth, healing, remodeling, proliferation, and differentiation. Exemplary growth factors can be short - ranged ( paracrine ), long ranged ( endocrine ), or self - stimulating ( autocrine ). Further examples of the growth factors include growth hormones ( e.g., a Attorney Docket No. JSV7183WOPCT1 recombinant growth factor, Nutropin, Humatrope, Genotropin, Norditropin, Saizen, Omnitrope, and a biosynthetic growth factor), Epidermal Growth Factor ( EGF ) ( e.g., inhibitors, Gefitinib, Erlotinib, Afatinib, and Cetuximab), heparin - binding EGF like growth factors (e.g., Epiregulin, Betacellulin, Amphiregulin, and Epigen), Transforming Growth Factor alpha (TGF - a), Neuroregulin 1-4, Fibroblast Growth Factors (FGFs) (e.g., FGF1-2, FGF2, FGF11-14, FGF18, FGF15 / 19, FGF21, FGF23, FGF7 or Keratinocyte Growth Factor (KGF), FGF10 or KGF2, and Phenytoin), Insuline - like Growth Factors (IGFs) (e.g., IGF 1 , IGF-2 , and Platelet Derived Growth Factor (PDGF)), Vascular Endothelial Growth Factors (VEGFs) (e.g., inhibitors, Bevacizumab, Ranibizumab, VEGF - A, VEGF - B, VEGF - C, VEGF - D and Becaplermin). Additional non - limiting examples of the growth factors include cytokines, such as Granulocyte Macrophage Colony Stimulating Factors (GM - CSFs) (e.g., inhibitors that inhibit inflammatory responses, and GM - CSF that has been manufactured using recombinant DNA technology and via recombinant yeast - derived sources), Granulocyte Colony Stimulating Factors (G - CSF) (e.g., Filgrastim, Lenograstim, and Neupogen), Tissue Growth Factor Beta (TGFB ), Leptin , and interleukins (ILs) (e.g., IL-1a , IL-1b, Canakinumab, IL-2, Aldesleukin, Interking, Denileukin Diftitox, IL-3, IL-6, IL-8, IL-10, IL-11, and Oprelvekin). The non-limiting examples of the growth factors further include erythropoietin (e.g., Darbepoetin, Epocept, Dynepo, Epomax, Neo Recormon, Silapo, and Retacrit). Non-limiting examples of analgesics include Narcotics, Opioids, Morphine, Codeine, Oxycodone, Hydrocodone, Buprenorphine, Tramadol, Non - Narcotics, Paracetamol, acetaminophen, NSAIDS, and Flupirtine. Non-limiting examples of anesthetics include local anesthetics (e.g., Lidocaine, Benzocaine, and Ropivacaine) and general anesthetic. Non-limiting examples of tissue matrix degradation inhibitors that inhibit the action of metalloproteinases (MMPs) and other proteases include MMP inhibitors (e.g., exogenous MMP inhibitors, hydroxamate - based MMP inhibitors, Batimastat ( BB - 94 ), Ilomastat ( GM6001 ), Marimastat ( BB2516 ), Thiols, Periostat (Doxycycline), Squaric Acid, BB - 1101, Hydroxyureas, Hydrazines, Endogenous, Carbamoylphosphates, Beta Lactams, and tissue Inhibitors of MMPs (TIMPs)). Non-limiting examples of anti-cancer agentsinclude monoclonial antibodies, bevacizumab (Avastin), cellular / chemoattractants, alkylating agents (e.g., Bifunctional, Attorney Docket No. JSV7183WOPCT1 Cyclophosphamide, Mechlorethamine, Chlorambucil, Melphalan, Monofunctional, Nitrosoureas and Temozolomide), anthracyclines (e.g., Daunorubicin, Doxorubicin, Epirubicin, Idarubicin, Mitoxantrone, and Valrubicin ), cytoskeletal disrupters (e.g., Paclitaxel and Docetaxel), epothilone agents that limit cell division by inhibiting microtubule function, inhibitor agents that block various enzymes needed for cell division or certain cell functions, histone deacetylase inhibitors (e.g., Vorinostat and Romidepsin), opoisomerase I inhibitors (e.g., Irinotecan and Topotecan), topoisomeraseII inhibitors (e.g., Etoposide, Teniposide, and Tafluposide), kinase inhibitors e.g. , Bortezomib, Erlotinib, Gefitinib, Imatinib, Vemurafenib, and Vismodegib), nucleotide analogs (e.g. , Azacitidine, Azathioprine, Capecitabine, Cytarabine, Doxifluridine, Fluorouracil, 5-FU, Adrucil, Carac, Efudix, Efudex, Fluoroplex, Gemcitabine, Hydroxyurea, Mercaptopurine, and Tioguanine), peptide antibiotic agentsthat cleave DNA and disrupt DNA unwinding / winding (e.g., Bleomycin and Actinomycin), platinum - based anti - neoplastic agents that cross link DNA which inhibits DNA repair and / or synthesis (e.g., Carboplatin, Cisplatin, Oxaliplatin, and Eloxatin), retinoids (e.g., Tretinoin, Alitretinoin, and Bexarotene), vinca alkaloids agents that inhibit mitosis and microtubule formation (e.g., Vinblastine, Vincristine, Vindesine, Vinorelbine), angiostatic inhibiting agents that inhibit cell growths or cell expansion (e.g., Axitinib (Inlyta), Bevacizumab (Avastin), Cabozantinib (Cometriq), Everolimus (Afinitor, Zortress) Lenalidomide (Revlimid), Pazopanib (Votrient), Ramucirumab (Cyramza), Regorafenib (Stivarga), Sorafenib (Nexavar), Sunitinib (Sutent), Thalidomide (Synovir, Thalomid), Vandetanib (Caprelsa), Zib - aflibercept (Zaltrap), antiangiogenic polysaccharide, aplidine (dehydrodidemnin B), sapogenins viz .20 (S) -protopanaxadiol, and 20 (S) - protopanaxatriol), anti-ileus agents, pro-motility agents, immunosuppresants (e.g., Tacrolimus), blood aspect modifier agents (e.g., Vasodilator, Viagra, and Nifedipine), 3-hydroxy-3-methyl- glutaryl -CoA (HMGCOA) reductase inhibitors (e.g., Atorvastatin) and antiangiogenesis agents. Exemplary medicants also include agents that passively contribute to wound healing such as, for example, nutrients, oxygen expelling agents, amino acids, collageno synthetic agents, Glutamine, Insulin, Butyrate, and Dextran. Exemplary medicants also include anti-adhesion agents, non-limiting examples of which include Hyaluronic acid / Carboxymethyl cellulose (seprafilm), Oxidized Regenerated Cellulose (Interceed), and Icodextrin 4 % (Extraneal, Adept) .   Attorney Docket No. JSV7183WOPCT1 The types of optics that may be deployed in the single-piece IOLs is not particularly limited. In some embodiments, in some embodiments the optic polymer system includes a poly(meth)acrylate, a silicone, or a combination thereof. Exemplary silicones include those derived from precursor compositions including a vinyl functionalized siloxane. The skilled person recognizes that these types of polymer systems inherently present reactive functional groups at their boundaries which may be used to form the block copolymers at the interface. In certain implementations, the optic polymers can be made by free radical polymerization of a reactive monomer mixture comprising: (A) (i) at least one cycloaliphatic (meth)acrylate; (ii) at least one aromatic (meth)acrylate; (iii) at least one aliphatic (meth)acrylate; and (iv) at least one cross-linking agent; wherein the composition (B) (i) at least one cycloaliphatic (meth)acrylate; (ii) at least one aliphatic (meth)acrylate; and (iii) at least one cross-linking agent; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39 (hereinafter “Composition (B)”); (C) (i) at least one hydrophobic monomer; (ii) at least one acrylate monomer of the following formula (I): wherein R1is selected from hydrogen R2is a non-aromatic moiety having at least one carbon-carbon double bond; and (iii) at least one cross-linking agent (hereinafter “Composition (C)”); (D) (i) at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring; (ii) at least one monomer selected from hydrophilic monomers and hydroxyalkyl (meth)acrylate monomers, and any combinations thereof, and (iii) at least one cross-linking agent; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39 (“Composition (D)”); or (E) (i) at least one hydrophobic monomer; (ii) at least one monomer selected from hydrophilic monomers and hydroxyalkyl (meth)acrylate monomers, and any combinations thereof; and (iii) a tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate cross-linking agent; Attorney Docket No. JSV7183WOPCT1 wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39 (“Composition (E)”). Each of the compositions will now be described in more detail. 1. Composition (A) In some embodiments, the presently disclosed subject matter provides a composition, referred to herein as “Composition (A),” made by free radical polymerization of a reactive monomer mixture comprising: (a) at least one cycloaliphatic (meth)acrylate; (b) at least one aromatic (meth)acrylate; (c) at least one aliphatic (meth)acrylate; and (d) at least one cross- linking agent; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39. In some embodiments of Composition (A), the at least one cycloaliphatic (meth)acrylate comprises a cycloaliphatic group having between one and four cycloaliphatic rings. In some embodiments, the cycloaliphatic group has one cycloaliphatic ring. The cycloaliphatic ring may be a C3-C8 cycloalkyl group, a C3-C7 cycloalkyl group, a C4-C7 cycloalkyl group, or a C5-C6 cycloalkyl group. In some embodiments, the at least one cycloaliphatic (meth)acrylate has at least one cycloaliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclohexyl PEG (meth)acrylate derivatives, cyclohexyl (meth)acrylate derivatives, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3- cyclohexylpropyl (meth)acrylate, norbornyl (meth)acrylate, norbornyl PEG (meth)acrylate derivatives, isobornyl (meth)acrylate, isobornyl derivatives, norbornyl derivatives, ((1R,2S,4R)- bicyclo[2.2.1]hept-5-en-2-yl)methyl (meth)acrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, poly(ethylene glycol) dicyclopentenyl ether (meth)acrylate, 2,2-bis(cyclopent-1- en-1-yloxy)ethyl (meth)acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl (meth)acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl PEG (meth)acrylate derivates and (1R,3S,5f,7r)-2- methyladamantan-2-yl (meth)acrylate derivatives, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3-cyclohexylpropyl (meth)acrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl acrylate, cyclohexylmethyl acrylate, cyclohexylmethyl methacrylate, 2- Attorney Docket No. JSV7183WOPCT1 cyclohexylethylacrylate, 2-cyclohexylethyl methacrylate, 3-cyclohexylpropylacrylate, ethylene glycol dicyclopentenyl ether acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl acrylate, cyclohexylmethyl acrylate, 2- cyclohexylethylacrylate, 3-cyclohexylpropylacrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexylmethyl acrylate, cyclohexylmethyl methacrylate, ethylene glycol dicyclopentenyl ether acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from 2- cyclohexylethyl acrylate, 2-cyclohexylethyl methacrylate, ethylene glycol dicyclopentenyl ether acrylate, and any combination thereof. In some embodiments, the at least one cycloaliphatic (meth)acrylate is cyclohexyl acrylate. In some embodiments, the at least one cycloaliphatic (meth)acrylate is cyclohexylmethyl acrylate. In some embodiments, the at least one cycloaliphatic (meth)acrylate is 2-cyclohexylethyl acrylate. In some embodiments, the at least one cycloaliphatic (meth)acrylate is ethylene glycol dicyclopentenyl ether acrylate. In some embodiments, the cycloaliphatic (meth)acrylate does not include a substituent (e.g., a hydroxy substituent) on the cycloaliphatic moiety or anywhere else on the monomer (e.g., in a monomer such as 2-cyclohexylethyl (meth)acrylate, the monomer does not include a substituent such as a hydroxy substituent on either the cyclohexyl moiety or the ethyl moiety). In some embodiments, the reactive monomer mixture of Composition (A) comprises the at least one cycloaliphatic (meth)acrylate in amount between about 20 and about 80 weight percent, including about 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, and 80 weight percent, between about 40 and about 80 weight percent, including about 40, 45, 50, 55, 60, 65, 70, 75, and 80 weight percent, or between about 60 and about 80 weight percent, including about 60, 65, 70, 75, and 80 weight percent. In some embodiments, the weight percent of the at least one cycloaliphatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments of Composition (A), the at least one aromatic (meth)acrylate is a (meth)acrylate comprising at least one aryl group. In some embodiments, the aryl group is a phenyl group. In some embodiments, the aryl group can be present in the aromatic (meth)acrylate as part of an arylalkyl group (e.g., benzyl, 2-phenylethyl, 3-phenylpropyl, or 4- phenylbutyl), an aryloxyalkyl group (e.g., phenoxymethyl, 2-phenoxyethyl, or 3- phenoxypropyl), or an arylthioalkyl group (e.g., phenylthiomethyl, 2-phenylthioethyl, or 3- Attorney Docket No. JSV7183WOPCT1 phenylthiopropyl). In some embodiments, the at least one aromatic (meth)acrylate is selected from 2-phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 4-phenylbutyl (meth)acrylate, 3-phenoxypropyl (meth)acrylate, 1,3- bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is selected from 2- phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 3- phenoxypropyl (meth)acrylate, 1,3-bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments the aromatic (meth)acrylate is a combination of 2-phenylethyl acrylate and 2-phenylethyl methacrylate. In some embodiments, the at least one aromatic (meth)acrylate is 2-phenylethyl acrylate. In some embodiments, the at least one aromatic (meth)acrylate is 2-phenylethyl methacrylate. In some embodiments, the aromatic (meth)acrylate is 3-phenylpropyl acrylate. In some embodiments, the aromatic (meth)acrylate is 4-phenylbutyl acrylate. In some embodiments, the at least one aromatic (meth)acrylate has at least one aliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the at least one aromatic (meth)acrylate is cinnamyl (meth)acrylate. In some embodiments, the reactive monomer mixture of Composition (A) comprises the at least one aromatic (meth)acrylate in an amount between about 5 and about 50 weight percent, including about 5, 10, 15, 20, 25, 30, 35, and 40 eight percent, between about 10 and about 40 weight percent, including about 10, 15, 20, 25, 30, 35, and 40 weight percent, or between about 15 and about 40 weight percent, including about 15, 20, 25, 30, 35, and 40 weight percent. In some embodiments, the weight percent of the at least one aromatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments of Composition (A), the cycloaliphatic (meth)acrylate(s) and the aromatic (meth)acrylate(s) are present in the reactive monomer mixture in a ratio of about 95:5 to about 30:70, about 90:10 to about 40:60, or about 90:10 to about 45:55. For example, in some embodiments, the cycloaliphatic (meth)acrylate(s) and the aromatic (meth)acrylate(s) are present in the reactive monomer mixture in a ratio of about 95:5, about 90:10, about 85:15, about 80:20, about 75:25, about 70:30, about 65:35, about 60:40, about 55:45, about 50:50, about 45:55, about 40:60, about 35:65, or about 30:70. Attorney Docket No. JSV7183WOPCT1 In some embodiments of Composition (A), the at least one aliphatic (meth)acrylate comprises a linear or branched alkyl group containing between 1 and 25 carbon atoms (a C1-C25 alkyl group), including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24, and C25. In particular embodiments, the aliphatic (meth)acrylate is a C1-C20 alkyl (meth)acrylate, including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, and C20alkyl (meth)acrylate. In more particular embodiments, the C1-C20alkyl (meth)acrylate is selected from the group consisting of ethyl (meth)acrylate, n-butyl (meth)acrylate, iso-butyl (meth)acrylate, t-butyl (meth)acrylate, n-hexyl (meth)acrylate, 2- ethylhexyl (meth)acrylate, octyl (meth)acrylate, iso-decyl (meth)acrylate, heptadecyl (meth)acrylate, dodecyl (meth)acrylate, 2-propylheptyl (meth)acrylate, stearyl (meth)acrylate, and any combination thereof. In yet more particular embodiments, the aliphatic (meth)acrylate comprises a linear alkyl group containing between 4 and 8 carbon atoms (a C4-C8 linear alkyl group), including 4, 5, 6 ,7 and 8 carbon atoms. In some embodiments, the aliphatic (meth)acrylate is n-hexyl acrylate. In some embodiments, the at least one aliphatic (meth)acrylate has at least one aliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the reactive monomer mixture of Composition (A) comprises the at least one aliphatic (meth)acrylate in an amount between 1 and 40 weight percent, including about 1, 5, 10, 15, 20, 25, 30, 35, and 40 weight percent, between about 1 and about 20 weight percent, including about 1, 5, 10, 15, and 20 weight percent, or between about 1 and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the at least one aliphatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments of Composition (A), the at least one cross-linking agent is selected from the group consisting of a non-cycloaliphatic cross-linking agent, a cycloaliphatic cross- linking agent, and any combination thereof. In certain embodiments, the at least one cross- linking agent is a non-cycloaliphatic cross-linking agent selected from ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, triallyl cyanurate, methylene bis(meth)acrylamide, poly(ethylene glycol) di(meth)acrylate, bis(2-hydropropyl (meth)acrylate) terminated polydimethylsiloxanes, and any Attorney Docket No. JSV7183WOPCT1 combination thereof. In more certain embodiments, the non-cycloaliphatic cross-linking agent is ethylene glycol dimethacrylate. In particular embodiments, the at least one cross-linking agent is a cycloaliphatic cross-linking agent comprising a cycloaliphatic group having between one and four cycloaliphatic rings. In yet more particular embodiments, the cycloaliphatic cross-linking agent is tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate (e.g., tricyclo[5.2.1.02,6]decanedimethanol diacrylate). In some embodiments, the reactive monomer mixture of Composition (A) comprises the cycloaliphatic cross-linking agent in an amount between about 1 and about 20 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent, between about 3 and about 15 weight percent, including about 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, or between about 3 and about 10 weight percent, including about 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the cycloaliphatic cross-linking agent present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments of Composition (A), the reactive monomer mixture further comprises a polyamide. In some embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone), poly(N-vinyl-N-methyl acetamide), poly(N-vinyl acetamide), poly(dimethyl acrylamide), and a copolymer or a mixture thereof. In particular embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone) and poly(N-vinyl-N-methyl acetamide). In certain embodiments, the at least one polyamide is a copolymer. In some embodiments, the reactive monomer mixture of Composition (A) comprises the at least one polyamide in an amount between about 0.1 weight percent and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 0.5 weight percent and about 3 weight percent, including about 0.5, 1, 2, and 3 weight percent, or between about 0.5 weight percent and about 2 weight percent, including about 0.5, 1, and 2 weight percent. In some embodiments, the weight percent of the at least one polyamide present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (A) further comprises at least one hydroxy silicone monomer. In some embodiments, the reactive monomer mixture of Composition (A) further comprises at least one hydroxy silicone monomer. In certain embodiments, the at least one Attorney Docket No. JSV7183WOPCT1 hydroxy silicone monomer comprises mono-n-butyl terminated mono-(2-hydroxy-3- methacryloxypropyloxy)-propyl terminated polydimethylsiloxane, 3-(3-(1,1,1,3,5,5,5- heptamethyltrisiloxan-3-yl)propoxy)-2-hydroxypropyl methacrylate, 3-(3-(1,5-di-tert-butyl- 1,1,3,5,5-pentamethyltrisiloxan-3-yl)propoxy)-2-hydroxypropyl methacrylate, or any combination thereof. In some embodiments, the reactive monomer mixture of Composition (A) comprises the hydroxy silicone monomer in an amount between about 1 and about 25 weight percent, including about 1, 5, 10, 15, 20, and 25 weight percent, between about 5 and about 20 weight percent, including about 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent, or between about 10 and about 20 weight percent, including 10, 11, 13, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent. In some embodiments, the weight percent of the hydroxy silicone monomer present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (A) further comprises at least one hydroxyalkyl (meth)acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate comprises a linear, branched, or cyclic hydroxyalkyl group having between 1 and 25 carbon atoms (a C1-C25alkyl group), including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24, and C25. In some embodiments, the hydroxyalkyl (meth)acrylate is selected from 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 2,3-dihydroxypropyl (meth)acrylate, 4- hydroxybutyl (meth)acrylate, 1,1-dimethyl-2-hydroxyethyl (meth)acrylate, and any combination thereof. In some embodiments, the hydroxyalkyl (meth)acrylate is 4-hydroxybutyl acrylate or 2- hydroxyethyl methacrylate. In particular embodiments, the hydroxyalkyl (meth)acrylate is 4- hydroxybutyl acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate is 2-hydroxyethyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (A) comprises the hydroxyalkyl (meth)acrylate in an amount between about 1 and about 25 weight percent, including about 1, 5, 10, 15, 20, and 25 weight percent, between about 5 and about 20 weight percent, including about 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent, or between about 10 and about 20 weight percent, including 10, 11, 13, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent. In some embodiments, the weight percent of the hydroxyalkyl (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. Attorney Docket No. JSV7183WOPCT1 In some embodiments, the reactive monomer mixture of Composition (A) does not include a hydroxyalkyl (meth)acrylate. In some embodiments, the reactive monomer mixture of Composition (A) further comprises at least one UV / HEV absorbing compound. In some embodiments, the UV / HEV absorbing compound may take the form of Formula     Formula II wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, or NR; X is O, S, NR, SO, or SO2; Y is a linking group; Pgis a polymerizable group; R at each occurrence is independently H, C1-C6 alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y-Pg; R1and R2, when present, are independently at each occurrence C1-C6alkyl, C1-C6alkoxy, C1-C6 thioalkyl, C3-C7 cycloalkyl, aryl (preferably unsubstituted phenyl or phenyl substituted with alkyl or halo), halo, hydroxy, amino, NR3R4, or benzyl, wherein R3and R4are independently H or C1-C6alkyl, or two adjacent R1or R2groups, together with the carbon atoms to which they are attached, combine to form a cycloalkyl or aryl ring; and EWG is an electron withdrawing group. Compounds of Formula II preferably contain one or two Y-Pggroups. More preferably, the compounds contain one Y-Pggroup. In certain embodiments, the at least one UV / HEV absorbing compound is a compound of Formula II, 2-(2´-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole, 2-(2-cyano-2-(9H- thioxanthen-9-ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(9H-xanthen-9- Attorney Docket No. JSV7183WOPCT1 ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(10-methylacridin-9(10H)- ylidene)acetamido)ethyl methacrylate, 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2- yl)-4-hydroxyphenyl)propyl methacrylate, or any combination thereof. In certain embodiments, the at least one UV / HEV absorbing compound is 2-(2-cyano-2-(9H-thioxanthen-9- ylidene)acetamido)ethyl methacrylate. In certain embodiments, the at least one UV / HEV absorbing compound is 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2-yl)-4- hydroxyphenyl)propyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (A) comprises the at least one UV / HEV absorbing compound in an amount between about 0.1 and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 1 and about 4 weight percent, including about 1, 2, 3, and 4 weight percent, or between about 1 and about 3 weight percent, including about 1, 2, and 3 weight percent. In some embodiments, the weight percent of the at least one UV / HEV absorbing compound present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (A) further comprises at least one hydrophilic monomer. In some embodiments, the hydrophilic monomer is selected from vinyl pyrrolidone, N-vinyl-N-methyl acetamide, N-methyl methacrylamide, N- vinyl acetamide, N,N-dimethyl acrylamide, N-hydroxyethylacrylamide, N-(2- hydroxypropyl)acrylamide, N-(3-hydroxypropyl)acrylamide, N-(2- hydroxyethyl)(meth)acrylamide, N-(2-hydroxypropyl)(meth)acrylamide, and N-(3- hydroxypropyl)(meth)acrylamide, poly(ethylene glycol) methyl ether (meth)acrylate, poly(ethylene glycol) (meth)acrylate, and any combination thereof. In some embodiments, the hydrophilic monomer has at least one aliphatic group having at least one double bond. In some embodiments, the reactive monomer mixture of Composition (A) does not include a hydrophilic monomer. In some embodiments, Composition (A) further comprises at least one diluent in the reactive monomer mixture. In some embodiments, Composition (A) has a water content of between about 0 weight percent and about 15 weight percent, including about 0, 0.1, 0.5, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, between about 1 weight percent and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, or between about 1 weight percent Attorney Docket No. JSV7183WOPCT1 and about 8 weight percent, including about 1, 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 0.5 and less than 5 weight percent, including 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, 4.0, and 4.5 weight percent. In some embodiments, the water content is measured when the material is hydrated at 37 °C. In some embodiments, Composition (A) has a refractive index of at least 1.45 and an Abbe number of at least 45. In other embodiments, Composition (A) has a refractive index of at least 1.48 and an Abbe number of at least 50. In yet other embodiments, Composition (A) has a refractive index of at least 1.50 and an Abbe number of at least 50. In some embodiments, the indicated refractive index and the indicated Abbe number are measured when the material is in a dry state at 25 °C. In some embodiments of Composition (A), the free radical polymerization is a photopolymerization using a bisacylphosphine oxide initiator. In some embodiments, the initiator is bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide. (2) Composition (B) In some embodiments, the presently disclosed subject matter provides a composition, referred to herein as “Composition (B),” made by free radical polymerization of a reactive monomer mixture comprising: (a) at least one cycloaliphatic (meth)acrylate; (b) at least one aliphatic (meth)acrylate; and (c) at least one cross-linking agent; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39. In some embodiments of Composition (B), the at least one cycloaliphatic (meth)acrylate comprises a cycloaliphatic group having between one and four cycloaliphatic rings. In some embodiments, the cycloaliphatic group has one cycloaliphatic ring. The cycloaliphatic ring may be a C3-C8cycloalkyl group, a C3-C7cycloalkyl group, a C4-C7cycloalkyl group, or a C5-C6cycloalkyl group. In some embodiments, the at least one cycloaliphatic (meth)acrylate has at least one cycloaliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclohexyl PEG (meth)acrylate derivatives, cyclohexyl (meth)acrylate derivatives, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3- cyclohexylpropyl (meth)acrylate, norbornyl (meth)acrylate, isobornyl (meth)acrylate, isobornyl derivatives, norbornyl derivatives, ((1R,2S,4R)-bicyclo[2.2.1]hept-5-en-2-yl)methyl (meth)acrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, poly(ethylene) glycol Attorney Docket No. JSV7183WOPCT1 dicyclopentenyl ether (meth)acrylate, 2,2-bis(cyclopent-1-en-1-yloxy)ethyl (meth)acrylate, 2- (((3aR,4R,5S,7R,7aR)-octahydro-1H-4,7-methanoinden-5-yl)oxy)ethyl acrylate, 2- (((3aS,4R,6S,7R,7aR)-3a,4,5,6,7,7a-hexahydro-1H-4,7-methanoinden-6-yl)oxy)ethyl acrylate, (3aS,4S,5R,7S,7aS)-octahydro-1H-4,7-methanoinden-5-yl acrylate, (3aS,4S,5R,7S,7aS)- 3a,4,5,6,7,7a-hexahydro-1H-4,7-methanoinden-5-yl acrylate, (1R,3S,5f,7r)-2-methyladamantan- 2-yl (meth)acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl PEG (meth)acrylate derivates and (1R,3S,5f,7r)-2-methyladamantan-2-yl (meth)acrylate derivatives, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3-cyclohexylpropyl (meth)acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl acrylate, cyclohexylmethyl acrylate, 2-cyclohexylethylacrylate, 3-cyclohexylpropylacrylate, and ethylene glycol dicyclopentenyl ether acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl acrylate, cyclohexylmethyl acrylate, 2-cyclohexylethylacrylate, and 3- cyclohexylpropylacrylate. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexylmethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is 2-cyclohexylethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is ethylene glycol dicyclopentenyl ether acrylate. In some embodiments, the cycloaliphatic (meth)acrylate does not include a substituent (e.g., a hydroxy substituent) on the cycloaliphatic moiety or anywhere else on the monomer (e.g., in a monomer such as 2-cyclohexylethyl (meth)acrylate, the monomer does not include a substituent such as a hydroxy substituent on either the cyclohexyl moiety or the ethyl moiety). In some embodiments, the reactive monomer mixture of Composition (B) comprises the at least one cycloaliphatic (meth)acrylate in amount between about 20 and about 80 weight percent, including about 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, and 80 weight percent, between about 40 and about 80 weight percent, including about 40, 45, 50, 55, 60, 65, 70, 75, and 80 weight percent, or between about 60 and about 80 weight percent, including about 60, 65, 70, 75, and 80 weight percent. In some embodiments, the weight percent of the at least one cycloaliphatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. Attorney Docket No. JSV7183WOPCT1 In some embodiments of Composition (B), the at least one aliphatic (meth)acrylate comprises a linear or branched alkyl group containing between 1 and 25 carbon atoms (a C1-C25 alkyl group) , including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24, and C25. In particular embodiments, the aliphatic (meth)acrylate is a C1-C20 alkyl (meth)acrylate, including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, and C20alkyl (meth)acrylate. In more particular embodiments, the C1-C20alkyl (meth)acrylate is selected from the group consisting of ethyl (meth)acrylate, n-butyl (meth)acrylate, iso-butyl (meth)acrylate, t-butyl (meth)acrylate, n-hexyl (meth)acrylate, 2- ethylhexyl (meth)acrylate, octyl (meth)acrylate, iso-decyl (meth)acrylate, heptadecyl (meth)acrylate, dodecyl (meth)acrylate, 2-propylheptyl (meth)acrylate, stearyl (meth)acrylate, and any combination thereof. In yet more particular embodiments, the aliphatic (meth)acrylate comprises a linear or branched alkyl group containing between 4 and 8 carbon atoms (a C4-C8 linear alkyl group), including 4, 5, 6, 7, and 8 carbon atoms. In some embodiments, the aliphatic (meth)acrylate is isobutyl acrylate or n-hexyl acrylate. In some embodiments, the reactive monomer mixture of Composition (B) comprises the at least one aliphatic (meth)acrylate in an amount between 1 and 40 weight percent, between about 1 and about 20 weight percent, or between about 1 and about 10 weight percent. In some embodiments, the weight percent of the at least one aliphatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments of Composition (B), the at least one cross-linking agent is selected from the group consisting of a non-cycloaliphatic cross-linking agent, a cycloaliphatic cross- linking agent, and any combination thereof. In certain embodiments, the at least one cross- linking agent is a non-cycloaliphatic cross-linking agent selected from ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, triallyl cyanurate, methylene bis(meth)acrylamide, poly(ethylene glycol) di(meth)acrylate, bis(2-hydropropyl (meth)acrylate) terminated polydimethylsiloxanes, and any combination thereof. In more certain embodiments, the non-cycloaliphatic cross-linking agent is ethylene glycol dimethacrylate. In particular embodiments, the at least one cross-linking agent is a cycloaliphatic cross-linking agent comprising a cycloaliphatic group having between one and four cycloaliphatic rings. In yet more particular embodiments, the cycloaliphatic cross-linking Attorney Docket No. JSV7183WOPCT1 agent is tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate (e.g., tricyclo[5.2.1.02,6]decanedimethanol diacrylate). In some embodiments, the reactive monomer mixture of Composition (B) comprises the cycloaliphatic cross-linking agent in an amount between about 1 and about 20 weight percent, including about 1, 5, 10, 15, and 20 weight percent, between about 3 and about 15 weight percent, including 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15, or between about 3 and about 10 weight percent, including 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the cycloaliphatic cross-linking agent present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (B) further comprises an aromatic (meth)acrylate. In some embodiments, the aromatic (meth)acrylate is a (meth)acrylate comprising at least one aryl group. In some embodiments, the aryl group is a phenyl group. In some embodiments, the aryl group can be present in the aromatic (meth)acrylate as part of an arylalkyl group (e.g., benzyl, 2-phenylethyl, 3-phenylpropyl or 4- phenylpropyl), an aryloxyalkyl group (e.g., phenoxymethyl, 2-phenoxyethyl, or 3- phenoxypropyl), or an arylthioalkyl group (e.g., phenylthiomethyl, 2-phenylthioethyl, or 3- phenylthiopropyl). In some embodiments, the aromatic (meth)acrylate is selected from 2- phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 3- phenoxypropyl (meth)acrylate, 1,3-bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is selected from 2-phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 3-phenoxypropyl (meth)acrylate, 1,3- bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is 2-phenylethyl acrylate. In some embodiments, the aromatic (meth)acrylate is 2-phenylethyl methacrylate. In some embodiments, the aromatic (meth)acrylate is 3-phenylpropyl acrylate. In some embodiments, the aromatic (meth)acrylate is 4-phenylbutyl acrylate. In some embodiments, the reactive monomer mixture of Composition (B) comprises the aromatic (meth)acrylate in an amount between about 5 and about 50 weight percent, including about 5, 10, 15, 20, 25, 30, 35, 40, 45, and 50 weight percent, between about 10 and about 40 weight percent, including about 10, 15, 20, 25, 30, 35, and 40 weight percent, or between about Attorney Docket No. JSV7183WOPCT1 15 and about 40 weight percent, including about 15, 20, 25, 30, 35, and 40 weight percent. In some embodiments, the weight percent of the at least one aromatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (B) does not include an aromatic monomer such as an aromatic (meth)acrylate. In some embodiments, the reactive monomer mixture of Composition (B) further comprises at least one hydrophilic monomer. In some embodiments, the hydrophilic monomer is selected from vinyl pyrrolidone, N-vinyl-N-methyl acetamide, N-methyl methacrylamide, N- vinyl acetamide, N,N-dimethyl acrylamide, N-hydroxyethylacrylamide, N-(2- hydroxypropyl)acrylamide, N-(3-hydroxypropyl)acrylamide, N-(2- hydroxyethyl)(meth)acrylamide, N-(2-hydroxypropyl)(meth)acrylamide, N-(3- hydroxypropyl)(meth)acrylamide, poly(ethylene glycol) methyl ether (meth)acrylate, poly(ethylene glycol) (meth)acrylate, and any combination thereof. In some embodiments, the hydrophilic monomer has at least one aliphatic group having at least one double bond. In some embodiments, the reactive monomer mixture of Composition (B) does not include a hydrophilic monomer. In some embodiments, the reactive monomer mixture of Composition (B) further comprises at least one hydroxyalkyl (meth)acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate comprises a linear, branched, or cyclic hydroxyalkyl group having between 1 and 25 carbon atoms (a C1-C25alkyl group) , including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24, and C25. In some embodiments, the hydroxyalkyl (meth)acrylate is selected from 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, and any combination thereof. In some embodiments, the hydroxyalkyl (meth)acrylate is 4-hydroxybutyl acrylate or 2-hydroxyethyl methacrylate. In particular embodiments, the hydroxyalkyl (meth)acrylate is 4-hydroxybutyl acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate is 2-hydroxyethyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (B) comprises the hydroxyalkyl (meth)acrylate in an amount between about 1 and about 25 weight percent, including about 1, 5, 10, 15, 20, and 20 weight percent, between about 5 and about 20 weight percent, including about 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight Attorney Docket No. JSV7183WOPCT1 percent, or between about 10 and about 20 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent. In some embodiments, the weight percent of the hydroxyalkyl (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (B) does not include a hydroxyalkyl (meth)acrylate. In some embodiments, the reactive monomer mixture of Composition (B)further comprises a polyamide. In some embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone), poly(N-vinyl N-methyl acetamide), poly(N-vinyl acetamide), poly(dimethyl acrylamide), and a copolymer or a mixture thereof. In particular embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone) and poly(N-vinyl N-methyl acetamide). In certain embodiments, the at least one polyamide is a copolymer. In some embodiments, the reactive monomer mixture of Composition (B) comprises the at least one polyamide in an amount between about 0.1 weight percent and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 0.5 weight percent and about 3 weight percent, including about 0.5, 1, 2, and 3 weight percent, or between about 0.5 weight percent and about 2 weight percent, including about 0.5, 1, and 2 weight percent. In some embodiments, the weight percent of the at least one polyamide present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (B) further comprises at least one UV / HEV absorbing compound. In some embodiments, the UV / HEV absorbing compound may take the form of Formula II:   wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, or NR; Attorney Docket No. JSV7183WOPCT1 X is O, S, NR, SO, or SO2; Y is a linking group; Pgis a polymerizable group; R at each occurrence is independently H, C1-C6 alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y-Pg; R1and R2, when present, are independently at each occurrence C1-C6alkyl, C1-C6alkoxy, C1-C6thioalkyl, C3-C7cycloalkyl, aryl (preferably unsubstituted phenyl or phenyl substituted with alkyl or halo), halo, hydroxy, amino, NR3R4, or benzyl, wherein R3and R4are independently H or C1-C6alkyl, or two adjacent R1or R2groups, together with the carbon atoms to which they are attached, combine to form a cycloalkyl or aryl ring; and EWG is an electron withdrawing group. Compounds of Formula II preferably contain one or two Y-Pg groups. More preferably, the compounds contain one Y-Pggroup. In certain embodiments, the at least one UV / HEV absorbing compound is a compound of Formula II, is 2-(2´-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole, 2-(2-cyano-2- (9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(9H-xanthen-9- ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(10-methylacridin-9(10H)- ylidene)acetamido)ethyl methacrylate, 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2- yl)-4-hydroxyphenyl)propyl methacrylate, or any combination thereof. In certain embodiments, the at least one UV / HEV absorbing compound is 2-(2-cyano-2-(9H-thioxanthen-9- ylidene)acetamido)ethyl methacrylate. In certain embodiments, the at least one UV / HEV absorbing compound is 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2-yl)-4- hydroxyphenyl)propyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (B) comprises the at least one UV / HEV absorbing compound in an amount between about 0.1 and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 1 and about 4 weight percent, including about 1, 2, 3, and 4 weight percent, or between about 1 and about 3 weight percent, including about 1, 2, and 3 weight percent. In some embodiments, the weight percent of the at least one UV / HEV absorbing compound present in the reactive monomer mixture is calculated excluding a diluent. Attorney Docket No. JSV7183WOPCT1 In some embodiments, the reactive monomer mixture of Composition (B) further comprises at least one diluent in the reactive monomer mixture. In some embodiments, the reactive monomer mixture of Composition (B) has a water content of between about 0 weight percent and about 15 weight percent, including about 0, 0.1, 0.5, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, between about 1 weight percent and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, or between about 1 weight percent and about 8 weight percent, including about 1, 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 0.5 and less than 5 weight percent, including 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, 4.0, and 4.5 weight percent. In some embodiments, the water content is measured when the material is hydrated at 37 °C. In some embodiments, the reactive monomer mixture of Composition (B) has a refractive index of at least 1.45 and an Abbe number of at least 45. In other embodiments, Composition (B) has a refractive index of at least 1.48 and an Abbe number of at least 50. In yet other embodiments, Composition (B) has a refractive index of at least 1.50 and an Abbe number of at least 50. In some embodiments, the indicated refractive index and the indicated Abbe number are measured when the material is in a dry state at 25 °C. In some embodiments of Composition (B), the free radical polymerization is a photopolymerization using a bisacylphosphine oxide initiator. In some embodiments, the initiator is bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide. (3) Composition (C) In some embodiments, the presently disclosed subject matter provides a composition, referred to herein as “Composition (C),” made by free radical polymerization of a reactive monomer mixture comprising: (a) at least one hydrophobic monomer; (b) at least one acrylate monomer of the following formula (I): wherein R1is selected from hydrogen R2is a non-aromatic moiety having at least one carbon-carbon double bond; and (c) at least one cross-linking agent. In some embodiments of Composition (C), the hydrophobic monomer is a hydrophobic (meth)acrylate monomer. In some embodiments, the hydrophobic (meth)acrylate is selected from Attorney Docket No. JSV7183WOPCT1 an aliphatic (meth)acrylate, an aromatic (meth)acrylate, a cycloaliphatic (meth)acrylate, and any combination thereof. In particular embodiments, the hydrophobic (meth)acrylate is an aliphatic (meth)acrylate. In some embodiments, the aliphatic (meth)acrylate comprises a linear or branched alkyl group containing between 1 and 18 carbon atoms (a C1-C18 alkyl group), including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, and C18alkyl (meth)acrylate. In more particular embodiments, the C1-C18alkyl (meth)acrylate is selected from the group consisting of ethyl (meth)acrylate, n-butyl (meth)acrylate, iso-butyl (meth)acrylate, t-butyl (meth)acrylate, n- hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, octyl (meth)acrylate, iso-decyl (meth)acrylate, heptadecyl (meth)acrylate, dodecyl (meth)acrylate, 2-propylheptyl (meth)acrylate, stearyl (meth)acrylate, and any combination thereof. In yet more particular embodiments, the aliphatic (meth)acrylate comprises a linear alkyl group containing between 4 and 8 carbon atoms (a C4-C8linear alkyl group). In some embodiments, the aliphatic (meth)acrylate is n-hexyl acrylate. In some embodiments, the hydrophobic (meth)acrylate is an aromatic (meth)acrylate. In some embodiments, the aromatic (meth)acrylate is a (meth)acrylate comprising at least one aryl group. In some embodiments, the aryl group is a phenyl group. In some embodiments, the aryl group can be present in the aromatic (meth)acrylate as part of an arylalkyl group (e.g., benzyl, 2- phenylethyl, 3-phenylpropyl, or 4-phenylbutyl), an aryloxyalkyl group (e.g., phenoxymethyl, 2- phenoxyethyl, or 3-phenoxypropyl), or an arylthioalkyl group (e.g., phenylthiomethyl, 2- phenylthioethyl, or 3-phenylthiopropyl). In some embodiments, the aromatic (meth)acrylate is selected from 2-phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 4-phenylbutyl (meth)acrylate, 3-phenoxypropyl (meth)acrylate, 1,3- bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is selected from 2- phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 3- phenoxypropyl (meth)acrylate, 1,3-bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is 2-phenylethyl acrylate. In some embodiments, the aromatic (meth)acrylate is 2-phenylethyl methacrylate. In some embodiments, the aromatic (meth)acrylate is a combination of 2-phenylethyl acrylate and 2-phenylethyl methacrylate. In Attorney Docket No. JSV7183WOPCT1 some embodiments, the aromatic (meth)acrylate is 3-phenylpropyl acrylate. In some embodiments, the aromatic (meth)acrylate is 4-phenylbutyl acrylate. In some embodiments of Composition (C), the hydrophobic (meth)acrylate is a cycloaliphatic (meth)acrylate. In some embodiments, the cycloaliphatic (meth)acrylate comprises a cycloaliphatic group having between one and four cycloaliphatic rings. In some embodiments, the cycloaliphatic group has one cycloaliphatic ring. The cycloaliphatic ring may be a C3-C8cycloalkyl group, a C3-C7cycloalkyl group, a C4-C7cycloalkyl group, or a C5-C6cycloalkyl group. In some embodiments, the at least one cycloaliphatic (meth)acrylate has at least one cycloaliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclohexyl PEG (meth)acrylate derivatives, cyclohexyl (meth)acrylate derivatives, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3-cyclohexylpropyl (meth)acrylate, norbornyl (meth)acrylate, isobornyl (meth)acrylate, isobornyl derivatives, norbornyl derivatives, ((1R,2S,4R)-bicyclo[2.2.1]hept-5-en-2-yl)methyl (meth)acrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, poly(ethylene) glycol dicyclopentenyl ether (meth)acrylate, 2,2-bis(cyclopent-1-en-1-yloxy)ethyl (meth)acrylate, 2-(((3aR,4R,5S,7R,7aR)- octahydro-1H-4,7-methanoinden-5-yl)oxy)ethyl acrylate, 2-(((3aS,4R,6S,7R,7aR)-3a,4,5,6,7,7a- hexahydro-1H-4,7-methanoinden-6-yl)oxy)ethyl acrylate, (3aS,4S,5R,7S,7aS)-octahydro-1H- 4,7-methanoinden-5-yl acrylate, (3aS,4S,5R,7S,7aS)-3a,4,5,6,7,7a-hexahydro-1H-4,7- methanoinden-5-yl acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl (meth)acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl PEG (meth)acrylate derivates and (1R,3S,5f,7r)-2- methyladamantan-2-yl (meth)acrylate derivatives, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3-cyclohexylpropyl (meth)acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexylmethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is 2-cyclohexylethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is ethylene glycol dicyclopentenyl ether acrylate. In some embodiments, the cycloaliphatic (meth)acrylate does not include a substituent (e.g., a hydroxy substituent) on the cycloaliphatic moiety or anywhere else on the monomer Attorney Docket No. JSV7183WOPCT1 (e.g., in a monomer such as 2-cyclohexylethyl (meth)acrylate, the monomer does not include a substituent such as a hydroxy substituent on either the cyclohexyl moiety or the ethyl moiety). Composition (C) also includes at least one acrylate monomer of formula (I): wherein R1is selected from and wherein R2is a non-aromatic moiety having at least one carbon- In some embodiments, R1is hydrogen. In some embodiments, R2is methyl. In some embodiments, in the at least one acrylate monomer of formula (I), R2comprises an alkenyl or cycloalkenyl moiety. In particular embodiments, R2comprises a cyclopentenyl, cyclopentadienyl, cyclohexenyl, cyclohexadienyl, bicyclo[2.2.1]hept-5-en-2-yl, 3a,4,5,6,7,7a- hexahydro-1H-4,7-methanoindenyl, styryl, cinnamyl, or allyl moiety. In more particular embodiments, the acrylate monomer of formula (I) is selected from ethylene glycol dicyclopentenyl ether (meth)acrylate, ((1R,2S,4R)-bicyclo[2.2.1]hept-5-en-2- yl)methyl acrylate, 2-(((3aS,4R,6S,7R,7aR)-3a,4,5,6,7,7a-hexahydro-1H-4,7-methanoinden-6- yl)oxy)ethyl acrylate, poly(ethylene glycol) dicyclopentenyl ether (meth)acrylate, 2,2- bis(cyclopent-1-en-1-yloxy)ethyl (meth)acrylate, (3aS,4S,5R,7S,7aS)-3a,4,5,6,7,7a-hexahydro- 1H-4,7-methanoinden-5-yl acrylate, 2-(cyclopenta-2,4-dien-1-yloxy)ethyl acrylate, cyclopenta- 2,4-dien-1-yl acrylate, cyclopent-3-en-1-yl acrylate, 2-(cyclopent-3-en-1-yloxy)ethyl acrylate, cyclohexa-2,4-dien-1-yl acrylate, 2-(cyclohexa-2,4-dien-1-yloxy)ethyl acrylate, 2-(cyclohex-3- en-1-yloxy)ethyl acrylate, cyclohex-3-en-1-yl acrylate, 2-(2-(2-(2-(cyclohex-3-en-1- yloxy)ethoxy)ethoxy)ethoxy)ethyl acrylate, N,N-diallyl acrylamide, allyl acrylate, and 2- (allyloxy)ethyl acrylate.  In some embodiments, the reactive monomer mixture of Composition (C) further comprises a hydroxyl-containing monomer. In some embodiments, the hydroxyl-containing monomer is a hydroxyalkyl (meth)acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate comprises a linear, branched, or cyclic hydroxyalkyl group having between 1 and 25 carbon atoms (a C1-C25 alkyl group), including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24, and C25. In some embodiments, the hydroxyalkyl (meth)acrylate is selected from 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl Attorney Docket No. JSV7183WOPCT1 (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, and any combination thereof. In particular embodiments, the hydroxyalkyl (meth)acrylate is 2- hydroxyethyl methacrylate or 4-hydroxybutyl acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate is 2-hydroxyethyl methacrylate. In some embodiments, the hydroxyl-containing monomer is a hydroxysilicone monomer. In some embodiments, the hydroxysilicone monomer is selected from 3-(3-(1,1,1,3,5,5,5- heptamethyltrisiloxan-3-yl)propoxy)-2-hydroxypropyl methacrylate (SiMAA), mono-n-butyl terminated monomethacryloxypropyl terminated polydimethylsiloxane (mPDMS), and mono-(2- hydroxy-3-methacryloxypropyl)-propyl ether terminated mono-n-butyl terminated polydimethylsiloxane (OH-mPDMS). In some embodiments, the reactive monomer mixture of Composition (C) further comprises at least one hydrophilic monomer. In some embodiments, the hydrophilic monomer is selected from vinyl pyrrolidone, N-vinyl-N-methyl acetamide, N-methyl methacrylamide, N- vinyl acetamide, N,N-dimethyl acrylamide, N-hydroxyethylacrylamide, N-(2- hydroxypropyl)acrylamide, N-(3-hydroxypropyl)acrylamide, N-(2- hydroxyethyl)(meth)acrylamide, N-(2-hydroxypropyl)(meth)acrylamide, N-(3- hydroxypropyl)(meth)acrylamide, poly(ethylene glycol) methyl ether (meth)acrylate, poly(ethylene glycol) (meth)acrylate, and any combination thereof. In some embodiments, the hydrophilic monomer has at least one aliphatic group having at least one double bond. In some embodiments of Composition (C), the at least one cross-linking agent is selected from the group consisting of a non-cycloaliphatic cross-linking agent, a cycloaliphatic cross- linking agent, and any combination thereof. In certain embodiments, the at least one cross- linking agent is a non-cycloaliphatic cross-linking agent selected from ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, triallyl cyanurate, methylene bis(meth)acrylamide, poly(ethylene glycol) di(meth)acrylate, bis(2-hydropropyl (meth)acrylate) terminated polydimethylsiloxanes, and any combination thereof. In more certain embodiments, the non-cycloaliphatic cross-linking agent is ethylene glycol dimethacrylate. In particular embodiments, the at least one cross-linking agent is a cycloaliphatic cross-linking agent comprising a cycloaliphatic group having between one and four cycloaliphatic rings. In yet more particular embodiments, the cycloaliphatic cross-linking Attorney Docket No. JSV7183WOPCT1 agent is tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate (e.g., tricyclo[5.2.1.02,6]decanedimethanol diacrylate). In some embodiments, the reactive monomer mixture of Composition (C) comprises the cycloaliphatic cross-linking agent in an amount between about 1 and about 20 weight percent, including about 1, 5, 10, 15, and 20 weight percent, between about 3 and about 15 weight percent, including about 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, or between about 3 and about 10 weight percent, including about 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the cycloaliphatic cross-linking agent present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the cross-linking agent has formula: , 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, and 50. In some embodiments, n is 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, or 25. In particular embodiments, n is 20. In some embodiments, the reactive monomer mixture comprises the cross-linking agent in an amount of about 15% to about 22% by weight, or between about 16% to about 20% by weight. In particular embodiments, the cross-linking agent is present in the reactive monomer mixture in an amount of about 18% by weight. In some embodiments of Composition (C), the reactive monomer mixture further comprises a polyamide. In some embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone), poly(N-vinyl-N-methyl acetamide), poly(N-vinyl acetamide), poly(dimethyl acrylamide), and a copolymer or a mixture thereof. In particular embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone) and poly(N-vinyl-N-methyl acetamide). In certain embodiments, the at least one polyamide is a copolymer. In some embodiments, the reactive monomer mixture of Composition (C) comprises the at least one polyamide in an amount between about 0.1 weight percent and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 0.5 weight percent and about 3 weight percent, including about 0.5, 1, 2, and 3 weight percent, or between about 0.5 weight percent and about 2 weight percent, including about 0.5, 1, and 2 weight Attorney Docket No. JSV7183WOPCT1 percent. In some embodiments, the weight percent of the at least one polyamide present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (C) further comprises at least one UV / HEV absorbing compound in the reactive monomer mixture. In some embodiments, the UV / HEV absorbing compound may take the form of Formula II:   wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, or NR; X is O, S, NR, SO, or SO2; Y is a linking group; Pgis a polymerizable group; R at each occurrence is independently H, C1-C6 alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y-Pg; R1and R2, when present, are independently at each occurrence C1-C6alkyl, C1-C6alkoxy, C1-C6 thioalkyl, C3-C7 cycloalkyl, aryl (preferably unsubstituted phenyl or phenyl substituted with alkyl or halo), halo, hydroxy, amino, NR3R4, or benzyl, wherein R3and R4are independently H or C1-C6alkyl, or two adjacent R1or R2groups, together with the carbon atoms to which they are attached, combine to form a cycloalkyl or aryl ring; and EWG is an electron withdrawing group. Compounds of Formula II preferably contain one or two Y-Pg groups. More preferably, the compounds contain one Y-Pggroup. In certain embodiments, the at least one UV / HEV absorbing compound is a compound of Formula II, 2-(2´-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole, 2-(2-cyano-2-(9H- thioxanthen-9-ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(9H-xanthen-9- ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(10-methylacridin-9(10H)- Attorney Docket No. JSV7183WOPCT1 ylidene)acetamido)ethyl methacrylate, 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2- yl)-4-hydroxyphenyl)propyl methacrylate, or any combination thereof. In certain embodiments, the at least one UV / HEV absorbing compound is 2-(2-cyano-2-(9H-thioxanthen-9- ylidene)acetamido)ethyl methacrylate. In certain embodiments, the at least one UV / HEV absorbing compound is 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2-yl)-4- hydroxyphenyl)propyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (C) comprises the at least one UV / HEV absorbing compound in an amount between about 0.1 and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 1 and about 4 weight percent, including about 1, 2, 3, and 4 weight percent, or between about 1 and about 3 weight percent, including about 1, 2, and 3 weight percent. In some embodiments, the weight percent of the at least one UV / HEV absorbing compound present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (C) further comprises at least one diluent in the reactive monomer mixture. In some embodiments, Composition (C) has a water content of between about 0 weight percent and about 15 weight percent, including about 0, 0.1, 0.5, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, between about 1 weight percent and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, or between about 1 weight percent and about 8 weight percent, including about 1, 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 0.5 and less than 5 weight percent, including 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, 4.0, and 4.5 weight percent. In some embodiments, the water content is measured when the material is hydrated at 37 °C. In some embodiments, Composition (C) has a refractive index of at least 1.45 and an Abbe number of at least 45. In other embodiments, Composition (C) has a refractive index of at least 1.48 and an Abbe number of at least 50. In yet other embodiments, Composition (C) has a refractive index of at least 1.50 and an Abbe number of at least 50. In some embodiments, the indicated refractive index and the indicated Abbe number are measured when the material is in a dry state at 25 °C. Attorney Docket No. JSV7183WOPCT1 In some embodiments of Composition (C), the free radical polymerization is a photopolymerization using a bisacylphosphine oxide initiator. In some embodiments, the initiator is bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide. (4) Composition (D) In some embodiments, the presently disclosed subject matter provides a composition, referred to herein as “Composition (D),” made by free radical polymerization of a reactive monomer mixture comprising: (i) at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring; (ii) at least one monomer selected from hydrophilic monomers and hydroxyalkyl (meth)acrylate monomers, and any combinations thereof; and (iii) at least one cross-linking agent (“Composition (D)”) ; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39. In some embodiments, the at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring includes two or more separate monocyclic cycloaliphatic rings. In some embodiments, the at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring includes a single bicyclic, tricyclic, bridged, fused, and / or spirocyclic cycloaliphatic ring system. In some embodiments, the at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring has at least one cycloaliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring is selected from norbornyl (meth)acrylate, isobornyl (meth)acrylate, isobornyl derivatives, norbornyl derivatives, ((1R,2S,4R)-bicyclo[2.2.1]hept-5-en-2-yl)methyl (meth)acrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, poly(ethylene) glycol dicyclopentenyl ether (meth)acrylate, 2,2-bis(cyclopent-1-en-1-yloxy)ethyl (meth)acrylate, 2-(((3aR,4R,5S,7R,7aR)- octahydro-1H-4,7-methanoinden-5-yl)oxy)ethyl acrylate, 2-(((3aS,4R,6S,7R,7aR)-3a,4,5,6,7,7a- hexahydro-1H-4,7-methanoinden-6-yl)oxy)ethyl acrylate, (3aS,4S,5R,7S,7aS)-octahydro-1H- 4,7-methanoinden-5-yl acrylate, (3aS,4S,5R,7S,7aS)-3a,4,5,6,7,7a-hexahydro-1H-4,7- methanoinden-5-yl acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl (meth)acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl PEG (meth)acrylate derivates and (1R,3S,5f,7r)-2- methyladamantan-2-yl (meth)acrylate derivatives, and any combination thereof. In some Attorney Docket No. JSV7183WOPCT1 embodiments, the at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring is ethylene glycol dicyclopentenyl ether acrylate. In some embodiments, the cycloaliphatic (meth)acrylate containing more than one cycloaliphatic ring does not include a substituent (e.g., a hydroxy substituent) on the cycloaliphatic moiety or anywhere else on the monomer. In some embodiments, the reactive monomer mixture of Composition (D) comprises the cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring in an amount between about 40 and about 90 weight percent, including about 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, and 90 weight percent, between about 50 and about 80 weight percent, including about 50, 55, 60, 65, 70, 75, and 80 weight percent, or between about 50 and about 70 weight percent, including about 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, and 70 weight percent. In some embodiments, the weight percent of the cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (D) comprises at least one hydrophilic monomer. In some embodiments, the at least one hydrophilic monomer is selected from vinyl pyrrolidone, N-vinyl-N-methyl acetamide, N-methyl methacrylamide, N- vinyl acetamide, N,N-dimethyl acrylamide, N-hydroxyethylacrylamide, N-(2- hydroxypropyl)acrylamide, N-(3-hydroxypropyl)acrylamide, N-(2- hydroxyethyl)(meth)acrylamide, N-(2-hydroxypropyl)(meth)acrylamide, and N-(3- hydroxypropyl)(meth)acrylamide, poly(ethylene glycol) methyl ether (meth)acrylate, poly(ethylene glycol) (meth)acrylate, and any combination thereof. In some embodiments, the hydrophilic monomer is a poly(ethylene glycol)-containing monomer. In some embodiments, the poly(ethylene glycol)-containing monomer is selected from poly(ethylene glycol) methyl ether (meth)acrylate and poly(ethylene glycol) (meth)acrylate. In some embodiments, the poly(ethylene glycol)-containing monomer is poly(ethylene glycol) methacrylate. In some embodiments, the poly(ethylene glycol)-containing monomer is poly(ethylene glycol) methyl ether methacrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises a combination of poly(ethylene glycol) methacrylate and poly(ethylene glycol) methyl ether methacrylate. Attorney Docket No. JSV7183WOPCT1 In some embodiments, the poly(ethylene glycol)-containing monomer has a number- average molecular weight (Mn) of about 200 g / mol to about 1000 g / mol, including 200 g / mol, 220 g / mol, 240 g / mol, 260 g / mol, 280 g / mol, 300 g / mol, 320 g / mol, 340 g / mol, 360 g / mol, 380 g / mol, 400 g / mol, 420 g / mol, 440 g / mol, 460 g / mol, 480 g / mol, 500 g / mol, 520 g / mol, 540 g / mol, 560 g / mol, 580 g / mol, 600 g / mol, 620 g / mol, 640 g / mol, 660 g / mol, 680 g / mol, 700 g / mol, 720 g / mol, 740 g / mol, 760 g / mol, 780 g / mol, 800 g / mol, 820 g / mol, 840 g / mol, 860 g / mol, 880 g / mol, 900 g / mol, 920 g / mol, 940 g / mol, 960 g / mol, 980 g / mol, and 1000 g / mol. In some embodiments, the poly(ethylene glycol)-containing monomer has a number-average molecular weight (Mn) of about 200 g / mol to about 400 g / mol, including 200 g / mol, 220 g / mol, 240 g / mol, 260 g / mol, 280 g / mol, 300 g / mol, 320 g / mol, 340 g / mol, 360 g / mol, 380 g / mol, and 400 g / mol. In some embodiments, the poly(ethylene glycol)-containing monomer has formula: ,  wherein Raand Rbare each and methyl, and m is an integer from 2 to 25, including 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, and 25. In some embodiments, Rais hydrogen. In some embodiments, Rais methyl. In some embodiments, Rbis hydrogen. In some embodiments, Rbis methyl. In particular embodiments, Rais methyl and Rbis hydrogen. In some embodiments, Rais methyl and Rbis methyl. In some embodiments, m is an integer from 2 to 8, including 2, 3, 4, 5, 6, 7, and 8. In some embodiments, the reactive monomer mixture of Composition (D) comprises the at least one hydrophilic monomer (e.g., the poly(ethylene glycol)-containing monomer) in amount between about 1 and about 40 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, and 40 weight percent, between about 10 and about 30 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, and 30 weight percent, between about 12 and about 22 weight percent, including about 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, and 22 weight percent, or between about 14 and about 20 weight percent, including about 14, 15, 16, 17, 18, 19, and 20 weight percent. In some embodiments, the weight Attorney Docket No. JSV7183WOPCT1 percent of the at least one hydrophilic monomer (e.g., the poly(ethylene glycol)-containing monomer) present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (D) comprises at least one hydroxyalkyl (meth)acrylate monomer. In some embodiments, the hydroxyalkyl (meth)acrylate comprises a linear, branched, or cyclic hydroxyalkyl group having between 1 and 25 carbon atoms (a C1-C25alkyl group), including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24, and C25. In some embodiments, the hydroxyalkyl (meth)acrylate is selected from 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 2,3-dihydroxypropyl (meth)acrylate, 4- hydroxybutyl (meth)acrylate, 1,1-dimethyl-2-hydroxyethyl (meth)acrylate, and any combination thereof. In some embodiments, the hydroxyalkyl (meth)acrylate is 4-hydroxybutyl acrylate or 2- hydroxyethyl methacrylate. In particular embodiments, the hydroxyalkyl (meth)acrylate is 4- hydroxybutyl acrylate. In some embodiments, the hydroxyalkyl (meth)acrylate is 2-hydroxyethyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises the hydroxyalkyl (meth)acrylate in an amount between about 1 and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, between about 2 and about 8 weight percent, including about 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 4 and about 6 weight percent, including 4, 5, and 6 weight percent. In some embodiments, the weight percent of the hydroxyalkyl (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (D) comprises a combination of a hydrophilic monomer and a hydroxyalkyl (meth)acrylate monomer. In some embodiments, the reactive monomer mixture comprises a combination of a poly(ethylene glycol)-containing monomer and a hydroxyalkyl (meth)acrylate monomer. In some embodiments, the reactive monomer mixture comprises a combination of poly(ethylene glycol) methyl ether (meth)acrylate and 2-hydroxyethyl (meth)acrylate. In some embodiments, the reactive monomer mixture comprises a combination of poly(ethylene glycol) (meth)acrylate and 2-hydroxyethyl (meth)acrylate. In some embodiments, Composition (D) is made by free radical polymerization of a reactive monomer mixture comprising: (i) at least one cycloaliphatic (meth)acrylate monomer Attorney Docket No. JSV7183WOPCT1 containing more than one cycloaliphatic ring; (ii) at least one poly(ethylene glycol)-containing monomer; and (iii) at least one cross-linking agent. In some embodiments, Composition (D) is made by free radical polymerization of a reactive monomer mixture comprising: (i) at least one cycloaliphatic (meth)acrylate monomer containing more than one cycloaliphatic ring; (ii) at least one poly(ethylene glycol)-containing monomer selected from poly(ethylene glycol) (meth)acrylate and poly(ethylene glycol) methyl ether (meth)acrylate; and (iii) at least one cross- linking agent. In some embodiments, Composition (D) is made by free radical polymerization of a reactive monomer mixture comprising: (i) an ethylene glycol dicyclopentenyl ether (meth)acrylate monomer; (ii) at least one monomer selected from hydrophilic monomers and hydroxyalkyl (meth)acrylate monomers, and any combinations thereof; and (iii) at least one cross-linking agent. In some embodiments, Composition (D) is made by free radical polymerization of a reactive monomer mixture comprising: (i) an ethylene glycol dicyclopentenyl ether (meth)acrylate monomer; (ii) at least one poly(ethylene glycol)-containing monomer; and (iii) at least one cross-linking agent. In some embodiments, Composition (D) is made by free radical polymerization of a reactive monomer mixture comprising: (i) an ethylene glycol dicyclopentenyl ether (meth)acrylate monomer; (ii) at least one poly(ethylene glycol)-containing monomer selected from poly(ethylene glycol) (meth)acrylate and poly(ethylene glycol) methyl ether (meth)acrylate; and (iii) at least one cross-linking agent. In some embodiments, the reactive monomer mixture of Composition (D) further comprises at least one cycloaliphatic (meth)acrylate containing one cycloaliphatic ring. In some embodiments, the at least one cycloaliphatic (meth)acrylate containing one cycloaliphatic ring comprises a cycloaliphatic group having at least one carbon-carbon double bond. The cycloaliphatic ring may be a C3-C8 cycloalkyl group, a C3-C7 cycloalkyl group, a C4-C7 cycloalkyl group, or a C5-C6cycloalkyl group. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is selected from cyclohexyl (meth)acrylate, cyclohexyl PEG (meth)acrylate derivatives, cyclohexyl (meth)acrylate derivatives, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3- cyclohexylpropyl (meth)acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is selected from cyclohexyl Attorney Docket No. JSV7183WOPCT1 acrylate, cyclohexylmethyl acrylate, 2-cyclohexylethyl acrylate, 2-cyclohexylethyl methacrylate, 3-cyclohexylpropyl acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is selected from cyclohexyl acrylate, cyclohexyl methyl acrylate, 2-cyclohexylethyl acrylate, and 3-cyclohexylpropyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is cyclohexylmethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is cyclohexylmethyl methacrylate. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is 2-cyclohexylethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate containing one cycloaliphatic ring is 2- cyclohexylethyl methacrylate. In some embodiments, the combination thereof is a combination of cyclohexylmethyl acrylate and cyclohexylmethyl methacrylate. In some embodiments, the combination thereof is a combination of 2-cyclohexylethyl acrylate and 2-cyclohexylethyl methacrylate. In some embodiments, the cycloaliphatic (meth)acrylate does not include a substituent (e.g., a hydroxy substituent) on the cycloaliphatic moiety or anywhere else on the monomer (e.g., in a monomer such as 2-cyclohexylethyl (meth)acrylate, the monomer does not include a substituent such as a hydroxy substituent on either the cyclohexyl moiety or the ethyl moiety). In some embodiments, the reactive monomer mixture of Composition (D) comprises the at least one cycloaliphatic (meth)acrylate containing one aliphatic ring in amount between about 10 and about 25 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, and 25 weight percent, between about 10 and about 20 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent, or between about 12 and about 15 weight percent, including about 12, 13, 14, and 15 weight percent. In some embodiments, the weight percent of the at least one cycloaliphatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (D) further comprises at least one aromatic (meth)acrylate. In some embodiments, the at least one aromatic (meth)acrylate is a (meth)acrylate comprising at least one aryl group. In some embodiments, the aryl group is a phenyl group. In some embodiments, the aryl group can be present in the aromatic (meth)acrylate as part of an arylalkyl group (e.g., benzyl, 2-phenylethyl, 3-phenylpropyl, or 4- Attorney Docket No. JSV7183WOPCT1 phenylbutyl), an aryloxyalkyl group (e.g., phenoxymethyl, 2-phenoxyethyl, or 3- phenoxypropyl), or an arylthioalkyl group (e.g., phenylthiomethyl, 2-phenylthioethyl, or 3- phenylthiopropyl). In some embodiments, the at least one aromatic (meth)acrylate is selected from 2-phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 4-phenylbutyl (meth)acrylate, 3-phenoxypropyl (meth)acrylate, 1,3- bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is selected from 2- phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 3- phenoxypropyl (meth)acrylate, 1,3-bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the at least one aromatic (meth)acrylate is selected from 2-phenylethyl acrylate, 2-phenylethyl methacrylate, 3-phenylpropyl acrylate, and 4-phenylbutyl acrylate. In some embodiments, the at least one aromatic (meth)acrylate is 2-phenylethyl acrylate. In some embodiments, the at least one aromatic (meth)acrylate is 2-phenylethyl methacrylate. In some embodiments, the aromatic (meth)acrylate is 3-phenylpropyl acrylate. In some embodiments, the aromatic (meth)acrylate is 4-phenylbutyl acrylate. In some embodiments, the combination thereof is a combination of 2- phenylethyl acrylate and 2-phenylethyl methacrylate. In some embodiments, the combination thereof is a combination of 2-phenylethyl acrylate and 3-phenylpropyl acrylate. In some embodiments, the combination thereof is a combination of 2-phenylethyl methacrylate and 3- phenylpropyl acrylate. In some embodiments, the at least one aromatic (meth)acrylate has at least one aliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the at least one aromatic (meth)acrylate is cinnamyl (meth)acrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises the at least one aromatic (meth)acrylate in amount between about 7 and about 25 weight percent, including about 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, and 25 weight percent, between about 10 and about 20 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent, or between about 12 and about 15 weight percent, including about 12, 13, 14, and 15 weight percent. In some embodiments, the weight percent of the at least one aromatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. Attorney Docket No. JSV7183WOPCT1 In some embodiments, the reactive monomer mixture of Composition (D) does not include an aromatic monomer such as an aromatic (meth)acrylate. In some embodiments of Composition (D), the at least one cross-linking agent is selected from the group consisting of a non-cycloaliphatic cross-linking agent, a cycloaliphatic cross- linking agent, and any combination thereof. In certain embodiments, the at least one cross- linking agent is a non-cycloaliphatic cross-linking agent selected from ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, triallyl cyanurate, methylene bis(meth)acrylamide, poly(ethylene glycol) di(meth)acrylate, bis(2-hydropropyl (meth)acrylate) terminated polydimethylsiloxanes, and any combination thereof. In more certain embodiments, the non-cycloaliphatic cross-linking agent is ethylene glycol dimethacrylate. In particular embodiments, the at least one cross-linking agent is a cycloaliphatic cross-linking agent comprising a cycloaliphatic group having between one and four cycloaliphatic rings. In yet more particular embodiments, the cycloaliphatic cross-linking agent is tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate (e.g., tricyclo[5.2.1.02,6]decanedimethanol diacrylate). In some embodiments, the reactive monomer mixture of Composition (D) comprises the cross-linking agent in an amount between about 1 and about 20 weight percent, including about 1, 5, 10, 15, and 20 weight percent, between about 3 and about 15 weight percent, including about 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, or between about 3 and about 10 weight percent, including about 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the cycloaliphatic cross-linking agent present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the cross-linking agent has formula: , n an 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, and 50. In some embodiments, n is 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, or Attorney Docket No. JSV7183WOPCT1 25. In particular embodiments, n is 20. In some embodiments, the reactive monomer mixture comprises the cross-linking agent in an amount of about 15% to about 22% by weight, or between about 16% to about 20% by weight. In particular embodiments, the cross-linking agent is present in the reactive monomer mixture in an amount of about 18% by weight. In some embodiments of Composition (D), the reactive monomer mixture further comprises a polyamide. In some embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone), poly(N-vinyl-N-methyl acetamide), poly(N-vinyl acetamide), poly(dimethyl acrylamide), and a copolymer or a mixture thereof. In particular embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone) and poly(N-vinyl-N-methyl acetamide). In certain embodiments, the at least one polyamide is a copolymer. In some embodiments, the reactive monomer mixture of Composition (D) comprises the at least one polyamide in an amount between about 0.1 weight percent and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 0.5 weight percent and about 3 weight percent, including about 0.5, 1, 2, and 3 weight percent, or between about 0.5 weight percent and about 2 weight percent, including about 0.5, 1, and 2 weight percent. In some embodiments, the weight percent of the at least one polyamide present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (D) further comprises at least one UV / HEV absorbing compound in the reactive monomer mixture. In some embodiments, the UV / HEV absorbing compound may take the form of Formula II:   wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, or NR; X is O, S, NR, SO, or SO2; Y is a linking group; Attorney Docket No. JSV7183WOPCT1 Pg is a polymerizable group; R at each occurrence is independently H, C1-C6 alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y-Pg; R1and R2, when present, are independently at each occurrence C1-C6 alkyl, C1-C6 alkoxy, C1-C6 thioalkyl, C3-C7 cycloalkyl, aryl (preferably unsubstituted phenyl or phenyl substituted with alkyl or halo), halo, hydroxy, amino, NR3R4, or benzyl, wherein R3and R4are independently H or C1-C6alkyl, or two adjacent R1or R2groups, together with the carbon atoms to which they are attached, combine to form a cycloalkyl or aryl ring; and EWG is an electron withdrawing group. Compounds of Formula II preferably contain one or two Y-Pggroups. More preferably, the compounds contain one Y-Pg group. In certain embodiments, the at least one UV / HEV absorbing compound is a compound of Formula II, 2-(2´-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole, 2-(2-cyano-2-(9H- thioxanthen-9-ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(9H-xanthen-9- ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(10-methylacridin-9(10H)- ylidene)acetamido)ethyl methacrylate, 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2- yl)-4-hydroxyphenyl)propyl methacrylate, or any combination thereof. In certain embodiments, the at least one UV / HEV absorbing compound is 2-(2-cyano-2-(9H-thioxanthen-9- ylidene)acetamido)ethyl methacrylate. In certain embodiments, the at least one UV / HEV absorbing compound is 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2-yl)-4- hydroxyphenyl)propyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises the at least one UV / HEV absorbing compound in an amount between about 0.1 and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 1 and about 4 weight percent, including about 1, 2, 3, and 4 weight percent, or between about 1 and about 3 weight percent, including about 1, 2, and 3 weight percent. In some embodiments, the weight percent of the at least one UV / HEV absorbing compound present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (D) further comprises at least one diluent in the reactive monomer mixture. Attorney Docket No. JSV7183WOPCT1 In some embodiments, Composition (D) has a water content of between about 0 weight percent and about 15 weight percent, including about 0, 0.1, 0.5, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, between about 1 weight percent and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, or between about 1 weight percent and about 8 weight percent, including about 1, 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 0.5 and less than 5 weight percent, including 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, 4.0, and 4.5 weight percent. In some embodiments, the water content is measured when the material is hydrated at 37 °C. In some embodiments, Composition (D) has a refractive index of at least 1.45 and an Abbe number of at least 45. In other embodiments, Composition (D) has a refractive index of at least 1.48 and an Abbe number of at least 50. In yet other embodiments, Composition (D) has a refractive index of at least 1.50 and an Abbe number of at least 50. In some embodiments, the indicated refractive index and the indicated Abbe number are measured when the material is in a dry state at 25 °C. In some embodiments of Composition (D), the free radical polymerization is a photopolymerization using a bisacylphosphine oxide initiator. In some embodiments, the initiator is bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide. (5) Composition (E) In some embodiments, the presently disclosed subject matter provides a composition, referred to herein as “Composition (E),” made by free radical polymerization of a reactive monomer mixture comprising: (i) at least one hydrophobic monomer; (ii) at least one monomer selected from a hydrophilic monomers hydroxyalkyl (meth)acrylate monomers, and any combinations thereof; and (iii) a tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate cross- linking agent; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39. In some embodiments of Composition (E), the hydrophobic monomer is a hydrophobic (meth)acrylate monomer. In some embodiments, the hydrophobic (meth)acrylate is selected from a cycloaliphatic (meth)acrylate, an aliphatic (meth)acrylate, an aromatic (meth)acrylate, and any combination thereof. In some embodiments of Composition (E), the hydrophobic (meth)acrylate is a cycloaliphatic (meth)acrylate. In some embodiments, the cycloaliphatic (meth)acrylate comprises Attorney Docket No. JSV7183WOPCT1 a cycloaliphatic group having between one and four cycloaliphatic rings. In some embodiments, the cycloaliphatic group has one cycloaliphatic ring. The cycloaliphatic ring may be a C3-C8 cycloalkyl group, a C3-C7cycloalkyl group, a C4-C7cycloalkyl group, or a C5-C6cycloalkyl group. In some embodiments, the cycloaliphatic (meth)acrylate has at least one cycloaliphatic group comprising at least one carbon-carbon double bond. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclohexyl PEG (meth)acrylate derivatives, cyclohexyl (meth)acrylate derivatives, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3-cyclohexylpropyl (meth)acrylate, norbornyl (meth)acrylate, isobornyl (meth)acrylate, isobornyl derivatives, norbornyl derivatives, ((1R,2S,4R)-bicyclo[2.2.1]hept-5-en-2-yl)methyl (meth)acrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, poly(ethylene) glycol dicyclopentenyl ether (meth)acrylate, 2,2-bis(cyclopent-1-en-1-yloxy)ethyl (meth)acrylate, 2-(((3aR,4R,5S,7R,7aR)- octahydro-1H-4,7-methanoinden-5-yl)oxy)ethyl acrylate, 2-(((3aS,4R,6S,7R,7aR)-3a,4,5,6,7,7a- hexahydro-1H-4,7-methanoinden-6-yl)oxy)ethyl acrylate, (3aS,4S,5R,7S,7aS)-octahydro-1H- 4,7-methanoinden-5-yl acrylate, (3aS,4S,5R,7S,7aS)-3a,4,5,6,7,7a-hexahydro-1H-4,7- methanoinden-5-yl acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl (meth)acrylate, (1R,3S,5f,7r)-2-methyladamantan-2-yl PEG (meth)acrylate derivates and (1R,3S,5f,7r)-2- methyladamantan-2-yl (meth)acrylate derivatives, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl (meth)acrylate, cyclopentyl (meth)acrylate, cyclohexylmethyl (meth)acrylate, 2-cyclohexylethyl (meth)acrylate, 3-cyclohexylpropyl (meth)acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is selected from cyclohexyl acrylate, cyclohexylmethyl acrylate, cyclohexylmethyl methacrylate, 2-cyclohexylethyl acrylate, 2-cyclohexylethyl methacrylate, ethylene glycol dicyclopentenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is cyclohexylmethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is 2-cyclohexylethyl acrylate. In some embodiments, the cycloaliphatic (meth)acrylate is ethylene glycol dicyclopentenyl ether acrylate. In some embodiments, the cycloaliphatic (meth)acrylate does not include a substituent (e.g., a hydroxy substituent) on the cycloaliphatic moiety or anywhere else on the monomer Attorney Docket No. JSV7183WOPCT1 (e.g., in a monomer such as 2-cyclohexylethyl (meth)acrylate, the monomer does not include a substituent such as a hydroxy substituent on either the cyclohexyl moiety or the ethyl moiety). In some embodiments, the reactive monomer mixture of Composition (E) comprises the cycloaliphatic (meth)acrylate monomer in an amount between about 40 and about 90 weight percent, including about 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, and 90 weight percent, between about 50 and about 80 weight percent, including about 50, 55, 60, 65, 70, 75, and 80 weight percent, or between about 50 and about 70 weight percent, including about 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, and 70 weight percent. In some embodiments, the weight percent of the cycloaliphatic (meth)acrylate monomer present in the reactive monomer mixture is calculated excluding a diluent. In particular embodiments, the hydrophobic (meth)acrylate is an aliphatic (meth)acrylate. In some embodiments, the aliphatic (meth)acrylate comprises a linear or branched alkyl group containing between 1 and 18 carbon atoms (a C1-C18alkyl group), including C1, C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, and C18 alkyl (meth)acrylate. In more particular embodiments, the C1-C18 alkyl (meth)acrylate is selected from the group consisting of ethyl (meth)acrylate, n-butyl (meth)acrylate, iso-butyl (meth)acrylate, t-butyl (meth)acrylate, n- hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, octyl (meth)acrylate, iso-decyl (meth)acrylate, heptadecyl (meth)acrylate, dodecyl (meth)acrylate, 2-propylheptyl (meth)acrylate, stearyl (meth)acrylate, and any combination thereof. In yet more particular embodiments, the aliphatic (meth)acrylate comprises a linear alkyl group containing between 4 and 8 carbon atoms (a C4-C8 linear alkyl group). In some embodiments, the aliphatic (meth)acrylate is n-hexyl acrylate. In some embodiments, the reactive monomer mixture of Composition (E) comprises the aliphatic (meth)acrylate in an amount between about 1 and about 20 weight percent, including about 1, 5, 10, 15, and 20 weight percent, or between about 1 and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the aliphatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the hydrophobic (meth)acrylate is an aromatic (meth)acrylate. In some embodiments, the aromatic (meth)acrylate is a (meth)acrylate comprising at least one aryl group. In some embodiments, the aryl group is a phenyl group. In some embodiments, the aryl Attorney Docket No. JSV7183WOPCT1 group can be present in the aromatic (meth)acrylate as part of an arylalkyl group (e.g., benzyl, 2- phenylethyl, 3-phenylpropyl, or 4-phenylbutyl), an aryloxyalkyl group (e.g., phenoxymethyl, 2- phenoxyethyl, or 3-phenoxypropyl), or an arylthioalkyl group (e.g., phenylthiomethyl, 2- phenylthioethyl, or 3-phenylthiopropyl). In some embodiments, the aromatic (meth)acrylate is selected from 2-phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 4-phenylbutyl (meth)acrylate, 3-phenoxypropyl (meth)acrylate, 1,3- bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is selected from 2- phenylethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenylpropyl (meth)acrylate, 3- phenoxypropyl (meth)acrylate, 1,3-bis(phenylthio)-2-propyl (meth)acrylate, poly(ethylene glycol) phenyl ether (meth)acrylate, and any combination thereof. In some embodiments, the aromatic (meth)acrylate is 2-phenylethyl acrylate. In some embodiments, the aromatic (meth)acrylate is 2-phenylethyl methacrylate. In some embodiments, the aromatic (meth)acrylate is a combination of 2-phenylethyl acrylate and 2-phenylethyl methacrylate. In some embodiments, the aromatic (meth)acrylate is 3-phenylpropyl acrylate. In some embodiments, the aromatic (meth)acrylate is 4-phenylbutyl acrylate. In some embodiments, the reactive monomer mixture of Composition (E) comprises the aromatic (meth)acrylate in amount between about 7 and about 25 weight percent, including about 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, and 25 weight percent, between about 10 and about 20 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, and 20 weight percent, or between about 12 and about 15 weight percent, including about 12, 13, 14, and 15 weight percent. In some embodiments, the weight percent of aromatic (meth)acrylate present in the reactive monomer mixture is calculated excluding a diluent. The reactive monomer mixture of Composition (E) comprises at least one hydrophilic monomer. In some embodiments, the reactive monomer mixture of Composition (E) comprises at least one hydrophilic monomer selected from vinyl pyrrolidone, N-vinyl-N-methyl acetamide, N-methyl methacrylamide, N-vinyl acetamide, N,N-dimethyl acrylamide, N- hydroxyethylacrylamide, N-(2-hydroxypropyl)acrylamide, N-(3-hydroxypropyl)acrylamide, N- (2-hydroxyethyl)(meth)acrylamide, N-(2-hydroxypropyl)(meth)acrylamide, N-(3- hydroxypropyl)(meth)acrylamide, poly(ethylene glycol) methyl ether (meth)acrylate, poly(ethylene glycol) (meth)acrylate, and any combination thereof. Attorney Docket No. JSV7183WOPCT1 In some embodiments, the at least one hydrophilic monomer is a poly(ethylene glycol)- containing monomer. In some embodiments, the poly(ethylene glycol)-containing monomer is selected from poly(ethylene glycol) methyl ether (meth)acrylate and poly(ethylene glycol) (meth)acrylate. In some embodiments, the poly(ethylene glycol)-containing monomer is poly(ethylene glycol) methacrylate. In some embodiments, the poly(ethylene glycol)-containing monomer is poly(ethylene glycol) methyl ether methacrylate. In some embodiments, the reactive monomer mixture of Composition (E) comprises a combination of poly(ethylene glycol) methacrylate and poly(ethylene glycol) methyl ether methacrylate. In some embodiments, the poly(ethylene glycol)-containing monomer has a number- average molecular weight (Mn) of about 200 g / mol to about 1000 g / mol, including 200 g / mol, 220 g / mol, 240 g / mol, 260 g / mol, 280 g / mol, 300 g / mol, 320 g / mol, 340 g / mol, 360 g / mol, 380 g / mol, 400 g / mol, 420 g / mol, 440 g / mol, 460 g / mol, 480 g / mol, 500 g / mol, 520 g / mol, 540 g / mol, 560 g / mol, 580 g / mol, 600 g / mol, 620 g / mol, 640 g / mol, 660 g / mol, 680 g / mol, 700 g / mol, 720 g / mol, 740 g / mol, 760 g / mol, 780 g / mol, 800 g / mol, 820 g / mol, 840 g / mol, 860 g / mol, 880 g / mol, 900 g / mol, 920 g / mol, 940 g / mol, 960 g / mol, 980 g / mol, and 1000 g / mol. In some embodiments, the poly(ethylene glycol)-containing monomer has a number-average molecular weight (Mn) of about 200 g / mol to about 400 g / mol, including 200 g / mol, 220 g / mol, 240 g / mol, 260 g / mol, 280 g / mol, 300 g / mol, 320 g / mol, 340 g / mol, 360 g / mol, 380 g / mol, and 400 g / mol. In some embodiments, the poly(ethylene glycol)-containing monomer has formula: ,  wherein Raand Rbare each and methyl, and m is an integer from 2 to 25, including 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, and 25. In some embodiments, Rais hydrogen. In some embodiments, Rais methyl. In some embodiments, Rbis hydrogen. In some embodiments, Rbis methyl. In particular embodiments, Rais methyl and Rbis hydrogen. In some embodiments, Rais methyl and Rbis methyl. In some embodiments, m is an integer from 2 to 8, including 2, 3, 4, 5, 6, 7, and 8. In some embodiments, the hydrophilic monomer is selected from 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 2,3- Attorney Docket No. JSV7183WOPCT1 dihydroxypropyl (meth)acrylate, 4-hydroxybutyl acrylate. In some embodiments, the hydrophilic monomer is selected from 2-hydroxyethyl methacrylate and 4-hydroxybutyl acrylate. In some embodiments, the hydrophilic monomer is 4-hydroxybutyl acrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises a combination of a poly(ethylene glycol)-containing monomer and a hydrophilic monomer selected from 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 2,3-dihydroxypropyl (meth)acrylate, 4-hydroxybutyl acrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises a combination of a poly(ethylene glycol) (meth)acrylate monomer and 2-hydroxyethyl (meth)acrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises a combination of poly(ethylene glycol) methacrylate and 2-hydroxyethyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (D) comprises a combination of poly(ethylene glycol) methyl ether methacrylate and 2-hydroxyethyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (E) comprises the at least one hydrophilic monomer (e.g., the poly(ethylene glycol)-containing monomer) in amount between about 1 and about 40 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, and 40 weight percent, between about 10 and about 30 weight percent, including about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, and 30 weight percent, between about 12 and about 22 weight percent, including about 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, and 22 weight percent, between about 14 and about 20 weight percent, including about 14, 15, 16, 17, 18, 19, and 20 weight percent, between about 1 and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, between about 2 and about 8 weight percent, including about 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 4 and about 6 weight percent, including about 4, 5, and 6 weight percent. In some embodiments, the weight percent of the at least one hydrophilic monomer (e.g., the poly(ethylene glycol)- containing monomer) present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate cross- linking agent is tricyclo[5.2.1.02,6]decanedimethanol diacrylate. In some embodiments, the reactive monomer mixture of Composition (E) comprises the tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate cross-linking agent (e.g., Attorney Docket No. JSV7183WOPCT1 tricyclo[5.2.1.02,6]decanedimethanol diacrylate) in an amount between about 1 and about 20 weight percent, including about 1, 5, 10, 15, and 20 weight percent, between about 3 and about 15 weight percent, including 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15, or between about 3 and about 10 weight percent, including 3, 4, 5, 6, 7, 8, 9, and 10 weight percent. In some embodiments, the weight percent of the tricyclo[5.2.1.02,6]decanedimethanol di(meth)acrylate cross-linking agent present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, the reactive monomer mixture of Composition (E) comprises: (i) ethylene glycol dicyclopentenyl ether acrylate; (ii) a hydrophilic monomer selected from the group consisting of poly(ethylene glycol) methacrylate, poly(ethylene glycol) methyl ether methacrylate, 2-hydroxyethyl methacrylate, and any combination thereof; and (iii) a tricyclo[5.2.1.02,6]decanedimethanol diacrylate cross-linking agent; wherein the composition exhibits a refractive index of at least 1.45 and an Abbe number of at least 39. In some embodiments of Composition (E), the reactive monomer mixture further comprises a polyamide. In some embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone), poly(N-vinyl-N-methyl acetamide), poly(N-vinyl acetamide), poly(dimethyl acrylamide), and a copolymer or a mixture thereof. In particular embodiments, the at least one polyamide is selected from poly(vinyl pyrrolidone) and poly(N-vinyl-N-methyl acetamide). In certain embodiments, the at least one polyamide is a copolymer. In some embodiments, the reactive monomer mixture of Composition (E) comprises the at least one polyamide in an amount between about 0.1 weight percent and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 0.5 weight percent and about 3 weight percent, including about 0.5, 1, 2, and 3 weight percent, or between about 0.5 weight percent and about 2 weight percent, including about 0.5, 1, and 2 weight percent. In some embodiments, the weight percent of the at least one polyamide present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (E) further comprises at least one UV / HEV absorbing compound in the reactive monomer mixture. In some embodiments, the UV / HEV absorbing compound may take the form of Formula II: Attorney Docket No. JSV7183WOPCT1   wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, or NR; X is O, S, NR, SO, or SO2; Y is a linking group; Pg is a polymerizable group; R at each occurrence is independently H, C1-C6alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y-Pg; R1and R2, when present, are independently at each occurrence C1-C6 alkyl, C1-C6 alkoxy, C1-C6 thioalkyl, C3-C7 cycloalkyl, aryl (preferably unsubstituted phenyl or phenyl substituted with alkyl or halo), halo, hydroxy, amino, NR3R4, or benzyl, wherein R3and R4are independently H or C1-C6 alkyl, or two adjacent R1or R2groups, together with the carbon atoms to which they are attached, combine to form a cycloalkyl or aryl ring; and EWG is an electron withdrawing group. Compounds of Formula II preferably contain one or two Y-Pg groups. More preferably, the compounds contain one Y-Pg group. In certain embodiments, the at least one UV / HEV absorbing compound is a compound of Formula II, 2-(2´-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole, 2-(2-cyano-2-(9H- thioxanthen-9-ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(9H-xanthen-9- ylidene)acetamido)ethyl methacrylate, 2-(2-cyano-2-(10-methylacridin-9(10H)- ylidene)acetamido)ethyl methacrylate, 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2- yl)-4-hydroxyphenyl)propyl methacrylate, or any combination thereof. In certain embodiments, the at least one UV / HEV absorbing compound is 2-(2-cyano-2-(9H-thioxanthen-9- ylidene)acetamido)ethyl methacrylate. In certain embodiments, the at least one UV / HEV Attorney Docket No. JSV7183WOPCT1 absorbing compound is 3-(3-(tert-butyl)-5-(5-chloro-2H-benzo[d][1,2,3]triazol-2-yl)-4- hydroxyphenyl)propyl methacrylate. In some embodiments, the reactive monomer mixture of Composition (E) comprises the at least one UV / HEV absorbing compound in an amount between about 0.1 and about 5 weight percent, including about 0.1, 0.5, 1, 2, 3, 4, and 5 weight percent, between about 1 and about 4 weight percent, including about 1, 2, 3, and 4 weight percent, or between about 1 and about 3 weight percent, including about 1, 2, and 3 weight percent. In some embodiments, the weight percent of the at least one UV / HEV absorbing compound present in the reactive monomer mixture is calculated excluding a diluent. In some embodiments, Composition (E) further comprises at least one diluent in the reactive monomer mixture. In some embodiments, Composition (E) has a water content of between about 0 weight percent and about 15 weight percent, including about 0, 0.1, 0.5, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, and 15 weight percent, between about 1 weight percent and about 10 weight percent, including about 1, 2, 3, 4, 5, 6, 7, 8, 9, and 10 weight percent, or between about 1 weight percent and about 8 weight percent, including about 1, 2, 3, 4, 5, 6, 7, and 8 weight percent, or between about 0.5 and less than 5 weight percent, including 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, 4.0, and 4.5 weight percent. In some embodiments, the water content is measured when the material is hydrated at 37 °C. In some embodiments, Composition (E) has a refractive index of at least 1.45 and an Abbe number of at least 45. In other embodiments, Composition (E) has a refractive index of at least 1.48 and an Abbe number of at least 50. In yet other embodiments, Composition (E) has a refractive index of at least 1.50 and an Abbe number of at least 50. In some embodiments, the indicated refractive index and the indicated Abbe number are measured when the material is in a dry state at 25 °C. In some embodiments of Composition (E), the free radical polymerization is a photopolymerization using a bisacylphosphine oxide initiator. In some embodiments, the initiator is bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide. The optic portion may be prepared by the method comprising: (a) providing any one of Composition (A), Composition (B), Composition (C), Composition (D), or Composition (E); and (b) forming an optic. In other embodiments, the presently disclosed subject matter provides a Attorney Docket No. JSV7183WOPCT1 method for making an optic, the method comprising: (a) preparing a blank from any one of Composition (A), Composition (B), Composition (C), Composition (D), or Composition (E); and (b) machining an optic from the blank. In still other embodiments, the presently disclosed subject matter provides a method for making an optic, the method comprising molding an optic from any one of Composition (A), Composition (B), Composition (C), Composition (D), or Composition (E). In still other embodiments, the presently disclosed subject matter provides a method for making an optic, the method comprising molding an optic from any one of Composition (A), Composition (B), Composition (C), Composition (D), or Composition (E), and then refining the surface via lathing. In certain embodiments of the above methods, the method further comprises the step of extracting the optic with a solvent. In certain embodiments, the method further comprises the step of hydrating the extracted optic with at least one aqueous solution. In particular embodiments, the method further comprises an irradiation step using a laser, which in certain embodiments, is a two photon laser, which in more certain embodiments, is a femtosecond two photon laser The single piece IOLs of the present invention may be prepared by additive manufacturing processes, including stereolithographic printing, inverted stereolithographic printing, in-gel printing, or a combination thereof. Stereolithography is a process by which light, which may be produced by a projector or a laser, for example, a UV laser, is focused on a cross-section of a precursor composition, that is, a fluid monomer resin. The light selectively cures a layer of the resin to form a solid structure. In some examples, a plurality of layers are superimposed on top of one another to form the stereolithographically printed object. In some instances, the single piece IOL is prepared by a stereolithographic process including the steps of providing the optic on an elevator platform in vat containing a haptic precursor composition, where in the haptic precursor composition includes monomer compounds suitable for preparing the haptic polymers described herein. In some implementations, the haptic precursor system includes compounds of Formula (1C) and Formula (2C): Attorney Docket No. JSV7183WOPCT1 [Formula (1C)] [Formula (2C)] wherein: Rc1is selected from H and CH3; Xc1is selected from O and NH, Rc2is a polyether, aliphatic, or cycloaliphatic group; Rc3is selected from H and CH3; Xc2is selected from O and NH, and Rc4is a polyether, aliphatic, or cycloaliphatic group; wherein Rc4does not contain a thiol group. In some implementations, the mole ratio of the compound of Formula (1C) to compound of Formula (2C) is from 1:100 to 1:1, from 1:100 to 1:70, from 1:100 to 1:50, from 1:100 to 1:25, from 1:75 to 1:25, from 1:75 to 1:50, or from 1:50 to 1:25. The haptic precursor system can further include a compound of Formula (3C) [Formula (3C)], wherein: Rc5is selected from H and CH3; Xc3is selected from O and NH, Rc6is a polyether, aliphatic, or cycloaliphatic group; provided that the compound of Formula (3C) is different than the compound of Formula (2C) The haptic precursor can also include a compound of Formula (C*): Xc*-Rc*-Xc*[Formula (C*)], wherein Rc*is a polyether, aliphatic, or cycloaliphatic group, and Xc*has the formula: , Xc**is Rc**is selected from H and CH3. Attorney Docket No. JSV7183WOPCT1 In certain implementations, the ratio of the compound of Formula (1C) to compound of Formula (C*) is from 5:1 to 1:5, from 2:1 to 1:2, from 5:1 to 1:1, from 5:2.5 to 1:1, from 2.5:1 to 1:1, from 1:2.5 to 1:1, from 1:5 to 1:2.5, or from 1:5 to 1:1. In some implementations, the compound of Formula (C*) is triallyl cyanurate, divinyl benzene, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate. The haptic precursor may further include one or more photoinitiators. Suitable photoinitiators include diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO), an acetophenone derivative (such as dimethoxyphenylacetophenone), benzophenone, phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide (BAPO), and 2-(4-methoxystyryl)-4,6- bis(trichloromethyl)-1,3,5-triazine. The photoinitiator may be present in an amount from 0.01-5 wt.% or the precursor composition, for instance from 0.01-0.1 wt.%, from 0.05-0.5 wt.%, from 0.5-1.5%, from 1-2 wt.%, or from 1-5 wt.%. In some implementations, the haptic precursor can include a compound having the formula: RtRtRtor a combination wherein Rthas the formula: wherein n independently from 0- 5-10, 5-25, 10-50, or 25-50; Rfis in each case independently selected from null, CH2, CH2CH2, or CH2CH2CH2; and Z is in each case independently selected from null, O, C(=O), C(=O)O, or C(=O)NH. In certain implementations, the haptic precursor can include two thiol-containing compounds, a di-thiol of Formula (1T): [Formula (1T)], Attorney Docket No. JSV7183WOPCT1 wherein Rthas the formula: wherein n independently from 0- 10, 5-25, 10-50, or 25-50; f R is null, CH2, CH2CH2, or Z is null, O, C(=O), C(=O)O, or C(=O)NH; and and a tetra-thiol of Formula (2T): Rt*Rt*[Formula (2T)],wherein Rt*has the formula: wherein n* independently from 5-10, 5-25, 10-50, or 25-50; Rf*is null, CH2, CH2CH2, or CH2CH2CH2; and Z* is null, O, C(=O), C(=O)O, or C(=O)NH. In certain implementations, the haptic precursor includes one or more compounds selected from: , In certain implementations, the haptic precursor includes a compound having the formula: , Attorney Docket No. JSV7183WOPCT1 wherein n’ is from 3-10, and a compound having the formula: , In certain Formula (1T) to the compound of Formula (2T) is from 100:1 to 1:100, from 100:1 to 1:1, from 50:1 to 1:1, from 25:1 to 1:1, from 10:1 to 1:1, from 5:1 to 1:1, from 2.5:1 to 1:1, from 100:1 to 50:1, from 75:1 to 25:1, from 50:1 to 25:1, from 50:1 to 10:1, from 10:1 to 5:1, from 10:1 to 2.5:1, from 5:1 to 2.5:1, from 10:1 to 1:10, from 5:1 to 1:5, from 2.5:1 to 1:2.5, from 1:1 to 1:2.5, from 1:1 to 1:10, from 1:1 to 1:25, from 1:1 to 50:1 from 1:25 to 50:1, from 1:50 to 1:100, from 1:25 to 1:75, from 1:25 to 1:50, from 1:2.5 to 5:1, from 1:2.5 to 1:10, from 1:5 to 1:10, or from 1:10 to 1:25. The haptic precursor can include a compound having 2, 3, 4, 5, or 6 (meth)acryl groups, for example 2, 3, 4, 5, or 6 (meth)acrylate groups, 2, 3, 4, 5, or 6 (meth)acrylamide groups. In certain implementations, the haptic precursor include a compound having the formula: RmRm  or a combination wherein Rmhas the formula: , wherein Rmmis H or CH3; m is independently from 0-100, preferably 1-5, 1-10, 5-10, 5-25, 10-50, or 25-50; and Z1is null, O, NH. In some implementations the haptic precursor can include ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, Attorney Docket No. JSV7183WOPCT1 tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate, or a combination thereof. In some implementations, the mole ratio (meth)acryl monomer to the thiol monomer can be from 10:1 to 1:10, from 10:1 to 5:1, from 5:1 to 1:1, from 5:1 to 2.5:1, from 2.5:1 to 1:1., from 2:1 to 1:2, from 1:1 to 1:2.5, from 1:2.5 to 1:5, from 1:1 to 1:5, from 1:5 to 1:10, or from 1:1 to 1:10. For implementations in which the Michael monomer and / or the thiol monomer includes multiple compounds, the ratios above relate to the combined total of each Michael compound and / or thiol compound. In certain implementations, the haptic precursor is selectively irradiated at and / or adjacent to the edge of the optic to initiate photopolymerisation and therefore selectively form block copolymers defining the interface region. Further irradiation of the haptic precursor can be used to further polymerize the monomers and form the haptic portion. After a thin layer of the interface and haptic portions are formed, the elevator platform is adjusted and the process repeated multiple times to form the single piece IOL. Upon completion, the printed product (i.e., a printed lens) may be washed with a solvent to remove unreacted monomer. The product may be further heated to further cure the haptic and / or optic polymers. For example, the printed product can be heated to a temperature from 50- 100° C., from 50-75° C., or from 75-100° C., for a period of 1-24 hours, 1-6 hours, 6-12 hours, 12-18 hours, or 18-24 hours. In more particular embodiments, the method further comprises a step of sterilizing the single piece IOL. The single piece IOL may be sterilized by known means such as, but not limited to, autoclaving. The compositions described herein have been designed so that they are capable of being folded so that the intraocular lens can be inserted into the eye of an individual through a small incision. In some instances that incision will be less than 2.5 mm; in some instances that incision will be less than 2mm. The haptic portion of the lens provides the required support for the implant or lens in the eye after insertion and unfolding of the lens and tends to help stabilize the position of the lens after insertion and the closure of the incision. The shape of the haptic portion design is not particularly limited and can be any desired configuration, for example, either a plate type or graduated thickness spiral filaments, also known as a C-loop design. Attorney Docket No. JSV7183WOPCT1 The optic portion of the intraocular lens can be approximately 2-6 mm in diameter prior to hydration. The 2-6 mm diameter is fairly standard in the art and is generally chosen to cover the pupil in its fully dilated state under naturally occurring conditions. However, other sizes are contemplated and the presently disclosed subject matter is not limited to any particular diameter or size of intraocular lens. Furthermore, it is not necessary that the lens optic portion be circular; it could also be oval, square, or any other shape as desired. The intraocular lens can further include one or more non-optical haptic components extending away from the outermost peripheral surface of the optic portion. The haptic components can be of any desired shape, for example, graduated spiral filaments or flat plate sections and are used to support the lens within the posterior chamber of the eye. Lenses having any desired design configuration can be fabricated. Should the intraocular lens include other components besides the optical and haptic portions, such other portions can be made of a polymer as are the haptic and optic portions, or if desired, another material. The intraocular implants lenses may be inserted into the eye in any manner known in the art. For example, the intraocular lens may be folded prior to insertion into the eye using an intraocular lens inserter or by small, thin forceps of the type typically used by ophthalmic surgeons. After the implant or lens is in the targeted location, it is released to unfold. As is well known in the art, typically the lens that is to be replaced is removed prior to insertion of the intraocular lens. The intraocular lens of the presently disclosed subject matter can be made of a generally physiologically inert soft polymeric material that is capable of providing a clear, transparent, refractive lens body even after folding and unfolding. In some embodiments, the foldable intraocular lens of the presently disclosed subject matter can be inserted into any eye by injection whereby the mechanically compliant material is folded and forced through a small tube such as a 1 mm to 3 mm inner diameter tube.

Claims

Attorney Docket No. JSV7183WOPCT1 CLAIMS We claim:

1. A single piece intraocular lens, comprising: an optic portion comprising an optic polymer; and a haptic portion comprising a haptic polymer; wherein the optic portion and haptic portion are integrally formed at an interface, wherein the interface comprises a block copolymer comprising a block of optic polymer and a block of haptic polymer.

2. The lens of any preceding claim, wherein the block copolymer comprises a transition zone separating the optic polymer block and haptic polymer block, wherein said transition zone is located at the interface.

3. The lens of any preceding claim, wherein the optic has a diameter, and the width of the interface is 5% or less, 2% or less, 1% or less, 0.5% or less, 0.25% or less, 0.1% or less, 0.05% or less, or 0.01% or less the diameter of the optic.

4. The lens of any preceding claim, wherein: (a) the optic polymer is derived from a monomer not used to prepare the haptic polymer; (b) the haptic polymer is derived from a monomer not used to prepare the optic polymer; (c) the haptic polymer and optic polymer are crosslinked differently; (d) the haptic polymer has a different T(g) than the optic polymer; (e) the haptic polymer has a different modulus than the optic polymer; (f) the haptic polymer has a different Abbe number than the optic polymer; (g) the haptic polymer has a different refractive index than the optic polymer; or (h) a combination thereof.

5. The lens according to any preceding claim, wherein the haptic polymer comprises a poly(thiol-ene), poly(meth)acrylate, a copolymer thereof, or a combination thereof.

6. The lens according to any preceding claim, wherein the haptic polymer comprises a crosslinked poly(thiol-ene), a crosslinked poly(meth)acrylate, a crosslinked poly(thiol- ene / (meth)acrylate copolymer, or a combination thereof.Attorney Docket No. JSV7183WOPCT1 7. The lens according to any preceding claim, wherein the poly(meth)acrylate comprising thiol groups is derived from a mixture comprising a compound of Formula (1C) and Formula (2C): ]wherein: Rc1is selected from H and CH3; Xc1is selected from O and NH, Rc2is a polyether, aliphatic, or cycloaliphatic group; Rc3is selected from H and CH3; Xc2is selected from O and NH, and Rc4is a polyether, aliphatic, or cycloaliphatic group; wherein Rc4does not contain a thiol group.

8. The lens according to any preceding claim, wherein the poly(meth)acrylate comprising thiol groups is derived from a mixture comprising a compound of Formula (1C) and Formula (2C), wherein the ratio of the compound of Formula (1C) to compound of Formula (2C) is from 1:100 to 1:1, from 1:100 to 1:70, from 1:100 to 1:50, from 1:100 to 1:25, from 1:75 to 1:25, from 1:75 to 1:50, or from 1:50 to 1:

25.

9. The lens according to any preceding claim, wherein the poly(meth)acrylate comprising thiol groups is derived from a mixture comprising a compound of Formula (1C), Formula (2C), and a compound of Formula (3C): [Formula (3C)], wherein:Rc5is selected from H and CH3; Xc3is selected from O and NH; and Rc6is a polyether, aliphatic, or cycloaliphatic group; wherein: Rc6and Rc4are not the same;Attorney Docket No. JSV7183WOPCT1 Rc5and Rc3are not the same; Xc3and Xc2are not the same; or a combination thereof.

10. The lens according to any preceding claim, wherein the poly(meth)acrylate comprising thiol groups is crosslinked with a compound of Formula (C*): Xc*-Rc*-Xc*[Formula (C*)], wherein Rc*is a polyether, aliphatic, or cycloaliphatic group, and Xc*has the formula: , Xc**isRc**is selected from H and CH3.

11. The lens according to any preceding claim, wherein the ratio of the compound of Formula (1C) to compound of Formula (C*) is from 5:1 to 1:5, from 2:1 to 1:2, from 5:1 to 1:1, from 5:2.5 to 1:1, from 2.5:1 to 1:1, from 1:2.5 to 1:1, from 1:5 to 1:2.5, or from 1:5 to 1:

1.

12. The lens according to any preceding claim, the compound of Formula (C*) comprises triallyl cyanurate, divinyl benzene, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate.

13. The lens according to any preceding claim, wherein the haptic polymer comprises a thiol- Michael polymer.

14. The lens according to any preceding claim, wherein the thiol-Michael polymer is derived from a mixture comprising: a thiol monomer comprising at least two thiol groups; and a Michael monomer comprising at least two α,β unsaturated functional groups.

15. The lens according to any preceding claim, wherein the thiol monomer comprises a compound having the formula:Attorney Docket No. JSV7183WOPCT1 RtRtRtor a wherein Rthaswherein n independently 5, 1-10, 5-10, 5-25, 10-50, or 25-50;Rfis in each case independently selected from null, CH2, CH2CH2, or CH2CH2CH2; and Z is in each case independently selected from null, O, C(=O), C(=O)O, or C(=O)NH.

16. The lens according to any preceding claim, wherein the thiol monomer comprises a compound of Formula (1T): [Formula (1T)], wherein Rthas thewherein n independently1-10, 5-10, 5-25, 10-50, or 25-50; Rfis null, CH2, CH2CH2, or CH2CH2CH2; and Z is null, O, C(=O), C(=O)O, or C(=O)NH; and and a compound of Formula (2T): Rt*Rt*[Formula (2T)],wherein Rt*has thewherein n*1-10, 5-10, 5-25, 10-50, or 25-50; Rf*is null, CH2, CH2CH2, or CH2CH2CH2; and Z* is null, O, C(=O), C(=O)O, or C(=O)NH.Attorney Docket No. JSV7183WOPCT1 17. The lens according to any preceding claim, wherein the thiol monomer comprises a compound selected from: ,18. The lens according to any preceding claim, wherein the thiol monomer comprises a compound having the formula: , wherein n’ is from 3-.

19. The lens accordingof the compound of Formula (1T) to the compound of Formula (2T) is from 100:1 to 1:100, from 100:1 to 1:1, from 50:1 to 1:1, from 25:1 to 1:1, from 10:1 to 1:1, from 5:1 to 1:1, from 2.5:1 to 1:1, from 100:1 to 50:1, from 75:1 to 25:1, from 50:1 to 25:1, from 50:1 to 10:1, from 10:1 to 5:1, from 10:1 to 2.5:1, from 5:1 to 2.5:1, from 10:1 to 1:10, from 5:1 to 1:5, from 2.5:1 to 1:2.5, from 1:1 to 1:2.5, from 1:1 to 1:10, from 1:1 to 1:25, from 1:1 to 50:1 from 1:25 to 50:1, from 1:50 to 1:100, from 1:25 to 1:75, from 1:25 to 1:50, from 1:2.5 to 5:1, from 1:2.5 to 1:10, from 1:5 to 1:10, or from 1:10 to 1:

25.

20. The lens according to any preceding claim, wherein the Michael monomer a compound having the formula:Attorney Docket No. JSV7183WOPCT1 or awherein Rmhas the formula: , whereinRmmis H or CH3; m is independently from 0-100, preferably 1-5, 1-10, 5-10, 5-25, 10-50, or 25-50; and Z1is null, O, NH.

21. The lens according to any preceding claim, wherein the Michael monomer comprises ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate, or a combination thereof.

22. The lens according to any preceding claim, wherein the mole ratio Michael monomer to the thiol monomer can be from 10:1 to 1:10, from 10:1 to 5:1, from 5:1 to 1:1, from 5:1 to 2.5:1, from 2.5:1 to 1:1., from 2:1 to 1:2, from 1:1 to 1:2.5, from 1:2.5 to 1:5, from 1:1 to 1:5, from 1:5 to 1:10, or from 1:1 to 1:

10.

23. The lens according to any preceding claim, wherein the haptic portion comprises a therapeutic agent.

24. The lens according to any preceding claim, wherein the haptic portion comprises an anti- inflammatory, analgesic, antibiotic, antiviral, or a combination thereof.

25. A method for prepare the single piece intraocular lens or any preceding claim, comprising: (a) providing an optic disposed in a haptic resin; (b) selectively irradiating the resin to form the interface coupled to the optic;Attorney Docket No. JSV7183WOPCT1 (c) selectively irradiating the resin the form the haptic coupled to the interface to form a printed lens.

26. The method according to any preceding claim, wherein the selective irradiation comprises stereolithographic printing, inverted stereolithographic printing, in-gel printing, or a combination thereof.

27. The method according to any preceding claim, wherein the resin comprises a compound of Formula (1C) and Formula (2C):wherein: Rc1is selected from H and CH3; Xc1is selected from O and NH, Rc2is a polyether, aliphatic, or cycloaliphatic group; Rc3is selected from H and CH3; Xc2is selected from O and NH, and Rc4is a polyether, aliphatic, or cycloaliphatic group; wherein Rc4does not contain a thiol group.

28. The method according to any preceding claim, resin comprises a mixture of the compound of Formula (1C) to compound of Formula (2C) in a ratio from 1:100 to 1:1, from 1:100 to 1:70, from 1:100 to 1:50, from 1:100 to 1:25, from 1:75 to 1:25, from 1:75 to 1:50, or from 1:50 to 1:

25.

29. The method according to any preceding claim, wherein the resin comprises a compound of Formula (1C), Formula (2C), and a compound of Formula (3C): [Formula (3C)], wherein:Rc5is selected from H and CH3; Xc3is selected from O and NH; andAttorney Docket No. JSV7183WOPCT1 Rc6is a polyether, aliphatic, or cycloaliphatic group; wherein: Rc6and Rc4are not the same; Rc5and Rc3are not the same; Xc3and Xc2are not the same; or a combination thereof.

30. The method according to any preceding claim, wherein the resin comprises a compound of Formula (C*): Xc*-Rc*-Xc*[Formula (C*)], wherein Rc*is a polyether, aliphatic, or cycloaliphatic group, and Xc*has the formula: , Xc**isRc**is selected from H and CH3.

31. The method according to any preceding claim, wherein the ratio of the compound of Formula (1C) to compound of Formula (C*) is from 5:1 to 1:5, from 2:1 to 1:2, from 5:1 to 1:1, from 5:2.5 to 1:1, from 2.5:1 to 1:1, from 1:2.5 to 1:1, from 1:5 to 1:2.5, or from 1:5 to 1:

1.

32. The method according to any preceding claim, the resin comprises triallyl cyanurate, divinyl benzene, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate.

33. The method wherein the resin comprises: (a) a thiol monomer comprising at least two thiol groups; (b) a Michael monomer comprising at least two α,β unsaturated functional groups.

34. The method according to any preceding claim, wherein the resin comprises a compound having the formula:Attorney Docket No. JSV7183WOPCT1 RtRtRtor a wherein Rthaswherein n independently 5, 1-10, 5-10, 5-25, 10-50, or 25-50;Rfis in each case independently selected from null, CH2, CH2CH2, or CH2CH2CH2; and Z is in each case independently selected from null, O, C(=O), C(=O)O, or C(=O)NH.

35. The method according to any preceding claim, wherein the resin comprises a compound of Formula (1T): [Formula (1T)], wherein Rthas thewherein n independently1-10, 5-10, 5-25, 10-50, or 25-50; Rfis null, CH2, CH2CH2, or CH2CH2CH2; and Z is null, O, C(=O), C(=O)O, or C(=O)NH; and and a compound of Formula (2T): Rt*Rt*[Formula (2T)],wherein Rt*has thewherein n*1-10, 5-10, 5-25, 10-50, or 25-50; Rf*is null, CH2, CH2CH2, or CH2CH2CH2; and Z* is null, O, C(=O), C(=O)O, or C(=O)NH.Attorney Docket No. JSV7183WOPCT1 36. The method according to any preceding claim, wherein the resin comprises a compound selected from: ,37. The method according to any preceding claim, wherein the resin comprises a compound having the formula: , wherein n’ is from 3-.

38. The methodratio of the compound of Formula (1T) to the compound of Formula (2T) is from 100:1 to 1:100, from 100:1 to 1:1, from 50:1 to 1:1, from 25:1 to 1:1, from 10:1 to 1:1, from 5:1 to 1:1, from 2.5:1 to 1:1, from 100:1 to 50:1, from 75:1 to 25:1, from 50:1 to 25:1, from 50:1 to 10:1, from 10:1 to 5:1, from 10:1 to 2.5:1, from 5:1 to 2.5:1, from 10:1 to 1:10, from 5:1 to 1:5, from 2.5:1 to 1:2.5, from 1:1 to 1:2.5, from 1:1 to 1:10, from 1:1 to 1:25, from 1:1 to 50:1 from 1:25 to 50:1, from 1:50 to 1:100, from 1:25 to 1:75, from 1:25 to 1:50, from 1:2.5 to 5:1, from 1:2.5 to 1:10, from 1:5 to 1:10, or from 1:10 to 1:

25.

39. The method according to any preceding claim, wherein the resin comprises a compound having the formula:Attorney Docket No. JSV7183WOPCT1 or awherein Rmhas the formula: , whereinRmmis H or CH3; m is independently from 0-100, preferably 1-5, 1-10, 5-10, 5-25, 10-50, or 25-50; and Z1is null, O, NH.

40. The method according to any preceding claim, wherein the resin comprises ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerol tri(meth)acrylate, methylene bis(meth)acrylamide, pentaerythritol tetra(meth)acrylate, poly(ethylene glycol) di(meth)acrylate, or a combination thereof.

41. The method according to any preceding claim, wherein the mole ratio Michael monomer to the thiol monomer can be from 10:1 to 1:10, from 10:1 to 5:1, from 5:1 to 1:1, from 5:1 to 2.5:1, from 2.5:1 to 1:1., from 2:1 to 1:2, from 1:1 to 1:2.5, from 1:2.5 to 1:5, from 1:1 to 1:5, from 1:5 to 1:10, or from 1:1 to 1:

10.

42. The method according to any preceding claim, comprising extracting the printed lens with a solvent to remove unreacted resin.

43. The method according to any preceding claim, comprising heating the printed lens.

44. The method according to any preceding claim, comprising heating the printed lens to a temperature from 50-100° C., from 50-75° C., or from 75-100° C.

45. The method according to any preceding claim, comprising heating the printed lens for a period of 1-24 hours, 1-6 hours, 6-12 hours, 12-18 hours, or 18-24 hours.

46. The method according to any preceding claim, comprising sterilizing the printed lens.