COOLING DEVICE FOR AN ADDITIVE METAL PART MANUFACTURING SYSTEM

Abstract

The present invention relates to a cooling device (20) for an additive manufacturing system (10) of a metal part (11) by superimposing molten metal beads (12) onto a substrate (14). The cooling device (20) comprises at least one movable cooler (22). The cooler (20) incorporates, at least in part, a cooling circuit (24) for the cooling device (20). The cooling circuit (24) is traversed by a cooling fluid. The cooler (20) comprises at least one wall configured to face the metal beads (12) superimposed on the substrate (14). The cooling device (24) comprises at least one metal insert (26) that covers at least a portion of the wall of the cooler (22). The metal insert (26) is made of a metal having a melting point below 700°C. Figure for the abstract: 1a

Description

Title of the invention: COOLING DEVICE FOR A MANUFACTURING SYSTEM ADDITIVE FOR A METAL PART Technical field of the invention

[0001] The present invention relates to a cooling device for an additive manufacturing system of a metal part by superimposing molten metal cords. Technical background

[0002] During the additive manufacturing of metal parts, molten metal beads are layered on top of each other on a substrate until the desired part is formed. The deposition of the molten metal beads is therefore accompanied by a significant input of heat.

[0003] In order to maintain good geometric stability of the stacked metal cords, the heat supplied by their deposition must be evacuated at least in part during the inter-pass time, that is to say the time between each deposition of a metal cord or a set of metal cords.

[0004] Several methods of heat dissipation have already been proposed in the prior art. For example, the metal cord(s) can be cooled solely by contact with the atmosphere, but this type of cooling requires a significant interpass time. Other solutions propose cooling the metal cords by thermal conduction with the substrate on which they are laid.

[0005] However, these prior art cooling methods are not optimal in that they are accompanied by a high interpass time and / or a cooling efficiency that decreases as the metal beads move away from the substrate.

[0006] Furthermore, it must be considered that the superposition of the metal cords forms a structure whose peripheral surfaces are irregular.

[0007] The aim of the invention is therefore to propose a cooling device for an additive manufacturing system which improves the cooling of the metal beads as they are superimposed in such a way as to reduce the inter-pass time. Summary of the invention

[0008] The invention proposes a cooling device for an additive manufacturing system of a metal part by superimposing molten metal beads onto a substrate along a superposition direction,

[0009] the cooling device comprising at least one movable cooler at least in a direction perpendicular to the direction of superposition of the molten metal beads on the substrate,

[0010] the cooler incorporating at least in part a cooling circuit for the cooling device, the cooling circuit being traversed by a cooling fluid,

[0011] the cooler comprising at least one wall configured to be opposite the metal cords superimposed on the substrate,

[0012] the cooling device comprising at least one metallic insert which covers at least part of the wall of the cooler,

[0013] the metal insert being made of a metal whose melting point is less than 700°C.

[0014] According to other features of the invention: - the metal insert is made of tin or zinc; - the cooler is a copper plate; - the cooler is mobile at least in a direction perpendicular to the direction of overlap of the metal cords on the substrate; - the substrate or cooler is mobile along a direction parallel to the direction of superposition; - the metal insert comprises a thickness of between 1mm and 30mm.

[0015] The invention also relates to an additive manufacturing system for a metal part by superimposing molten metal beads onto a substrate, the additive manufacturing system comprising at least one molten metal supply device such as to form the superimposed metal beads on the substrate in a superposition direction and the additive manufacturing system comprising at least one cooling device according to any one of the preceding characteristics.

[0016] The invention also relates to a method for the additive manufacturing of a metal part on a substrate using an additive manufacturing system according to the preceding characteristic, the manufacturing method comprising at least:

[0017] - a step of depositing at least one molten metal bead onto the substrate means of the contribution mechanism,

[0018] - a positioning step, during which the device cooler The cooling element is positioned opposite at least one molten metal bead deposited during the deposition step.

[0019] - a cooling step during which the cooler is moved perpendicular to the direction of overlap of the metal cords and in such a way as to press the metal insert against at least one metal cord deposited during the deposition step, so that in contact with at least one metal cord, the metal insert softens under the effect of the increase in its temperature by thermal conduction and thus conforms to the contours of said metal cord.

[0020] According to a feature of the process, at the end of the cooling step, a metal insert replacement step is implemented in which the metal insert softened and deformed during the cooling step is separated from the cooler and replaced by a new metal insert.

[0021] According to a feature of the process, after the replacement step, the deposition step, the positioning step and the cooling step are carried out again until the metal part is obtained. Brief description of the figures

[0022] Other features and advantages of the invention will become apparent upon reading the detailed description that follows, for an understanding of which reference should be made to the accompanying drawings in which:

[0023] [Fig.la] is a schematic view of a deposition step of an additive manufacturing process of a metal part by means of an additive manufacturing system comprising a device for supplying molten metal and a cooling device;

[0024] [Fig. 1b] is a schematic view of the metallic cords formed by the feed device at the end of the deposition step;

[0025] [Fig.le] is a schematic view of a cooling step of the additive manufacturing process implemented by means of the cooling device of the additive manufacturing system;

[0026] [Fig.ld] is a schematic view of the cooling device at the end of the cooling step of [Fig. le];

[0027] [Fig.le] is a schematic view of a new deposition and positioning step of the cooling device of the additive manufacturing system;

[0028] [Fig. 1 f] is a schematic view of the metal part manufactured at the end of the additive manufacturing process;

[0029] [Fig.2] is a diagram illustrating the steps of the additive manufacturing process of the metal part. Detailed description of the invention

[0030] In the description that follows, identical, similar or analogous elements will be designated by the same reference numerals.

[0031] Figures 1a-1e schematically illustrate an example of an additive manufacturing system 10 for a metal part 11, visible in [Fig.lf], by superimposing molten metal cords 12 onto a substrate 14.

[0032] More precisely, the system 10 of figure 1 allows the production of metal parts 11 by superimposing metal cords 12 on the substrate 14, here a metal substrate.

[0033] According to non-limiting examples, the metal used to form the metal cords 12 may be composed of titanium or nickel or an alloy of different metals including titanium and / or nickel.

[0034] It should be considered that any metal other than titanium and / or nickel could be used without departing from the scope of the invention, as long as the metal or metal alloy used is suitable for use in additive manufacturing.

[0035] The manufacturing system 10 shown in figures 1a-1e includes a device for supplying 16 of the molten metal or metal alloy onto the substrate 14 so as to form the superimposed metal cords 12 along a superposition direction D, corresponding here to a vertical direction.

[0036] According to a non-limiting example, the feed device 16 is a welding torch and the feed metal is in the form of wire.

[0037] The feed device 16 allows, for example, the metal to be deposited when it is molten, i.e. for example for titanium at a temperature above 1600°C.

[0038] The supply device 16 can be fixed or mobile relative to the substrate 14.

[0039] It should also be considered that the substrate 14, here represented in figures la-lf in a horizontal plane, could extend in a non-limiting way in a vertical plane or in a plane inclined with respect to vertical and horizontal planes without this arrangement of the substrate going out of the scope of the invention.

[0040] Once deposited by the supply device 16, the metal cords 12 cool in part by heat diffusion.

[0041] Thus, and according to a non-limiting example, following the deposition of metal or metal alloy by the filler device 16, the part manufactured by the metal cords 12 has a temperature between 0°C and 600°C.

[0042] In other words, the metal cords 12, when deposited by the supply device 16, have a temperature between 0°C and 600°C.

[0043] As can be seen in figures 1a-1e, the superposition of the metal cords 12 on top of each other forms an intermediate structure 18 with irregular contours.

[0044] An intermediate structure 18 is understood to be a structure formed by the metal cords 12 superimposed on the substrate 14 but not yet forming the desired final metal part 11.

[0045] Thus, the contours of the intermediate structure 18 formed by the superposition of the metal cords 12 have an irregular shape, that is to say a surface which is not flat.

[0046] Furthermore, it should be considered that the arrangement of the substrate 14 and the metal cords 12 as shown in Figures 1a-1f is a non-limiting example of the invention. For example, the substrate 14 may be provided to extend in a substantially vertical plane and the metal cords 12 to be superimposed on one another in a vertical direction V, that is to say against a vertical face of the substrate 14.

[0047] As seen in figures 1a-1e, the additive manufacturing system 10 includes a cooling device 20.

[0048] The cooling device 20 of the additive manufacturing system 10 has the function of cooling at least one of the metal cords 12 after its deposition by the supply device 16 mentioned above.

[0049] In the following detailed description, the term "deposited metal bead(s) 12" will be used to identify the last metal bead(s) deposited by the filler device 16 during an additive manufacturing process of the metal part 11.

[0050] The cooling device 20 includes at least one cooler 22.

[0051] According to a non-limiting example of the invention, the cooler 20 is configured to move at least perpendicularly to the superposition direction D of the metal cords 12.

[0052] In other words, the cooler 20 is configured to move relative to the metal cords 12 at least so as to be positioned in contact with them.

[0053] According to a non-limiting example, the cooler 20 is able to move parallel to the direction of superposition D of the metal cords 12 on the substrate 14.

[0054] It is therefore understood that, according to this non-limiting example, the cooler 20 moves along the superposition direction D of the metal cords 12 as the said metal cords 12 are deposited and in such a way that the cooler 20 extends in relation to each of the metal cord(s) 12 deposited.

[0055] According to another non-limiting example, the substrate 14 is able to move parallel to the direction of superposition D of the metal cords 12 on the substrate 14.

[0056] It is therefore understood that, according to this non-limiting example, the substrate 14 moves along the superposition direction D of the metal cords 12 as the said metal cords 12 are deposited and in such a way that the cooler 22 extends in relation to each of the metal cord(s) 12 deposited.

[0057] Thus, it is understood that the additive manufacturing system 10 is configured in such a way that the cooler 20 is always opposite the last metal bead(s) 20 deposited.

[0058] According to the illustrated example of the invention, the cooler 22 of the cooling device 20 takes the form of a metal plate.

[0059] Here and without limitation the cooler 22 is a copper plate.

[0060] Advantage is taken of the cooler 22 in the form of a copper plate in that the Copper has high thermal conductivity.

[0061] The cooling device 20 also includes a cooling circuit 24 through which a refrigerant fluid flows, for example a heat transfer fluid such as water.

[0062] Thus, the cooler 22 incorporates at least in part the cooling circuit 24.

[0063] In particular, the cooling circuit 24 includes refrigerant circulation channels, the circulation channels being fluidly connected to at least one refrigerant reservoir, not shown here.

[0064] Thus, at least one copper plate forming the cooler 22 incorporates at least a part of the circulation channels of the cooling circuit 24.

[0065] It is therefore understood that the cooling circuit 24 is configured in such a way that it extends at least partly into a thickness of the cooler 22 in the form of a copper plate.

[0066] Thus, the circulation of the refrigerant fluid within the cooler 22, combined with the high thermal conductivity of the cooler 22, makes it possible to cool an element in contact with the cooler 22 by transferring heat to the coolant.

[0067] The cooling device 20 further includes at least one metallic insert 26 which covers at least part of the cooler 22.

[0068] More particularly, the cooler 22 includes at least one wall, for example flat, configured to be opposite the metal cords 12 superimposed on the substrate 14, the metal insert 26 covering at least part of the flat wall, via a removable mechanical assembly.

[0069] It is then understood that the metallic insert 26 extends in relation to the molten metallic cords 12 when these are deposited by the supply device 16 on the substrate 14 as described previously.

[0070] The metal insert 26 is made of a soft metal whose melting point is less than 700°C.

[0071] By way of non-limiting example, the metal insert 26 is made of tin or zinc.

[0072] The metal insert 26 also has a thickness between 1mm and 30 mm, considering a direction perpendicular to the superposition direction D of the metal cords 12.

[0073] Furthermore, it is understood that the movement of the cooler 22 in a direction perpendicular to the superposition direction D and towards the metal cords 12, called the pressing direction P, allows the metal insert 26 carried by the cooler 22 to come into contact with at least one of the molten metal cords 12 deposited by the supply device 16.

[0074] For example, the cooler 22 and the metal insert 26 have dimensions that allow them to come into contact with at least one of the metal cords 12.

[0075] It is also understood that depending on the dimensions of the metal cords 12 deposited by the supply device 16, the cooler 22 and the metal insert 26 can be in contact with more or fewer metal cords 12.

[0076] According to the illustrated example and without limitation, the cooler 22 and the metal insert 26 are configured to be in contact with three metal cords 12 superimposed on each other.

[0077] It should be considered that the cooling device 20 may comprise more than one cooler 22 coupled to a metallic insert 26.

[0078] For example, two or three coolers 22 each coupled to a metal insert 26 as described above can be used when the manufactured metal part has large dimensions, for example with a large peripheral surface to be cooled.

[0079] Thus, as illustrated in figures 1a-1e, it can be foreseen that the cooling device 20 comprises two coolers 22 each carrying a metal insert 26 and being arranged on either side of the metal cords 12 in order to improve the cooling of said metal cords 12.

[0080] The cooling device 20 is configured such that the cooler 22 carrying the metal insert 26 is pressed against the metal cords 12 under a pressure, for example equivalent to 500 MPa.

[0081] The pressure contact of the metal insert 26 against the metal cords 12, whose temperature is between 0°C and 600°C, then has the effect of heating the metal insert 26, thus causing it to soften when it approaches its melting point.

[0082] Thus, by softening, the metal insert 28 conforms to the irregular shape of the contours of the intermediate piece 18 formed by the metal cords 12, thereby increasing the contact area with the metal cords 12, thereby increasing the thermal conduction performance.

[0083] In this way, increasing the contact area between the metal insert 12 and the metal cords 28 improves the cooling of the metal cords by increasing the transfer of calories to the cooling circuit 24 integrated into the cooler 22.

[0084] The additive manufacturing process of the metal part 11 on the substrate 14 using the additive manufacturing system 10 will now be described in relation to [Fig.2].

[0085] By way of example, the metal part 11 to be manufactured, visible in [Fig.If], is elongated in shape along a direction parallel to the direction of superposition D of the metal cords 12.

[0086] It should also be considered that the manufacturing process will be described with a cooling device 20 comprising a single cooler 22 coupled to a metallic insert 26, but that the process applies mutatis mutandis to a cooling device 20 comprising more than one cooler 22, coupled to a metallic insert 26, for example two coolers 22.

[0087] The process includes a deposition step 100, visible in [Fig.la], of at least one molten metal bead 12 on the substrate 14 by means of the supply device 16.

[0088] For example, the deposition step 100 may consist of the successive deposition of three molten metal cords 12 superimposed on each other along the superposition direction D.

[0089] Once the deposition step 100 has been carried out as seen in [Fig.lb], i.e. in the example shown, once the superposition of three molten metal cords 12 has been deposited, a positioning step 200 is implemented.

[0090] The positioning step 200 consists, among other things, of positioning the cooler 22 relative to the three metal cords 12 deposited during the previous deposition step 100.

[0091] Thus, during the positioning step 200, the substrate 14 or the cooler 22 is moved in a direction parallel to the superposition direction D, so that the cooler 22 extends in relation to the metal cords 12 deposited during the deposition step 100.

[0092] In other words, during the positioning step 200, the cooler 22 is positioned so that the metal insert 26 extends in relation to at least the three metal beads 12 deposited during the previous deposition step 100.

[0093] In the illustrated example of the invention, the substrate 14 is movable along a direction parallel to the superposition direction D, so as to position the coolers 22 opposite the three metal cords 12, as seen in [Fig.lb].

[0094] According to an example of the invention, the deposition step and the positioning step can be implemented simultaneously.

[0095] Once the cooler 22, and in particular the metal insert 26, is positioned opposite the three metal beads 12 deposited during the previous deposition step 100, a cooling step 300 is implemented, as seen in [Fig. 1e].

[0096] During the cooling step 300, the cooler 22 is moved in the direction of pressing P towards the previously deposited metal cords 12.

[0097] It is then understood that during the cooling step 300, the metal insert 26 is pressed against the three metal cords 12, for example at a pressure of 500 MPa.

[0098] Thus, the contact between the external surface of the molten metal cords 12 with the metal insert 26 has the effect of increasing the temperature of the latter, which, by this increase in its temperature, softens as mentioned previously.

[0099] Thus, contact with the molten metal cords 12 at a temperature between 0 and 600°C makes it possible to increase the temperature of the metal insert 26 until it is at least close to its melting point.

[0100] As mentioned previously, the deformation of the metal insert 26 makes it possible to increase the contact area with the irregular contours of the intermediate structure 18 formed by the metal cords 12.

[0101] Increasing the contact area thus improves the transfer of heat by thermal conduction from the metal cords 12 to the cooling circuit 24.

[0102] According to a non-limiting example, the cooling step 300 is completed when the metal cords 12 in contact with the metal insert 26 have a decrease in their peripheral temperature of between 100°C and 500°C compared to their peripheral temperature when they were deposited by the supply device 16, during the previous deposition step 100.

[0103] Once the cooling step 300 is completed, a replacement step 400 of the metal insert 26 is implemented during which the metal insert 26, deformed at the end of the cooling step, is separated from the cooler 22 by dismantling the mechanical assembly.

[0104] To do this, once the cooling step 300 is completed, the cooler 22 is moved perpendicular to the superposition direction D and opposite the metal cords 12 so as to make the metal insert 26 accessible, as seen in [Fig.ld].

[0105] Once accessible, the metal insert 26 is detached from the cooler 22 and is replaced by a new, undeformed metal insert 26 as seen in [Fig.1e].

[0106] Following the replacement step 400, the deposition step 100 can again be implemented as described above and as seen in [Fig. 1e].

[0107] It is then understood that the manufacturing process implements successively the steps described above, from the deposition step 100 to the replacement step 400 until the desired metal part 11 is obtained and visible in [Fig.lf].

[0108] Thus, we take advantage of the cooling device and the additive manufacturing process described, in that the metal insert allows, by its low melting point, to soften on contact with at least one of the metal cords and thus, to overcome the uncertainties on the locations of heat exchange between the irregular contour of the metal cords and the metal insert.

[0109] In other words, the metallic insert as described optimizes contact with the metallic cords, thus maximizing their cooling by thermal conduction and thus reducing the inter-pass time between each deposition step.

Claims

Demands

1. Cooling device (20) of a system (10) for additive manufacturing of a metal part (11) by superimposing molten metal beads (12) onto a substrate (14) along a superposition direction (D), the cooling device (20) comprising at least one cooler (22) movable at least in a direction perpendicular to the superposition direction (D) of the molten metal beads (12) onto the substrate (14), the cooler (20) incorporating at least partially a cooling circuit (24) of the cooling device (20), the cooling circuit (24) being traversed by a cooling fluid, the cooler (20) comprising at least one wall configured to be opposite the metal beads (12) superimposed on the substrate (14), the cooling device (24) comprising at least one metal insert (26) which covers at least a portion of the wall of the cooler (22),the metal insert (26) being made of a metal whose melting point is below 700°C.

2. Cooling device (20) according to the preceding claim, wherein the metal insert (26) is composed of tin or zinc.

3. Cooling device (20) according to any one of the preceding claims, wherein the cooler (22) is a copper plate.

4. Cooling device (20) according to any one of the preceding claims, wherein the substrate (14) or the cooler (22) is movable in a direction parallel to the superposition direction (D).

5. Cooling device (20) according to any one of the preceding claims, wherein the metal insert (26) comprises a thickness of between 1mm and 30mm.

6. System (10) for additive manufacturing of a metal part (11) by superimposing molten metal beads (12) onto a substrate (14), the additive manufacturing system (10) comprising at least one molten metal feed device (16) such as to form the metallic cords (12) superimposed on the substrate (14) along a superposition direction (D) and the additive manufacturing system (10) comprising at least one cooling device (20) according to any one of the preceding claims.

7. A method for additively manufacturing a metal part (11) onto a substrate (14) using an additive manufacturing system (10) according to claim 6, the manufacturing method comprising at least: - a deposition step (100) of at least one molten metal bead (12) onto the substrate (14) using the feed device (16), - a positioning step (200), during which the cooler (22) of the cooling device (20) is positioned opposite at least one molten metal bead (12) deposited during the deposition step (100), - a cooling step (300) during which the cooler (22) is moved perpendicular to the overlapping direction (D) of the metal beads (12) and such as to press the metal insert (26) against at least one metal bead (12) deposited during the deposition step (100), so that it is in contact with at least one metal bead (12),The metallic insert (26) softens due to the increase in its temperature by thermal conduction and thus conforms to the contours of said metallic cord (12).

8. A method according to the preceding claim, wherein at the end of the cooling step (300), a replacement step (400) of the metal insert (26) is implemented during which the metal insert (26) softened and deformed during the cooling step (300) is separated from the cooler (22) and is replaced by a new metal insert (26).

9. A method according to the preceding claim, wherein after the replacement step (400), the deposition step (100), the positioning step (200) and the cooling step (300) are again carried out until the metal part (H) is obtained.