Compositions of acid and anhydride copolymers

Abstract

TITLE: Compositions of acidic and anhydride copolymers. The present invention relates to compositions comprising acrylic and methacrylic copolymers, these copolymers comprising methyl methacrylate, methacrylic acid, and acrylic acid with mass proportions of methyl methacrylate / (meth)acrylic acid close to 50 / 50, and of which a portion of the acidic functions can be anhydrized. The present invention also relates to processes for obtaining these copolymers as well as the use of these copolymers.

Description

Title of the invention: Acid and anhydride copolymer compositions

[0001] The present invention relates to compositions comprising acrylic and methacrylic copolymers, these copolymers comprising methyl methacrylate, methacrylic acid, and acrylic acid with mass proportions of methyl methacrylate / (meth)acrylic acid close to 50 / 50, and of which a portion of the acidic functions may be anhydrized. The present invention also relates to processes for obtaining these copolymers as well as the use of these copolymers.

[0002] Compositions comprising methyl methacrylate (MMA) and methacrylic acid (MAA) or acrylic acid (AA) are well known in the prior art, in particular compositions comprising a majority of MMA. These compositions are sometimes anhydrous.

[0003] Numerous references to these compositions can be found in the prior art:

[0004] GB 478323 in 1936 discloses copolymer compositions of methacrylic esters or mixtures of methacrylic esters with small proportions of acrylic and / or methacrylic acids. These copolymers are presented as aids in the formulation of pigments.

[0005] GB 698193 in 1950 discloses copolymer compositions of methacrylic esters and monomers, including methacrylic acid. These copolymers are described as having improved temperature resistance.

[0006] GB 1437176 in 1972 discloses thermoplastic copolymers suitable for molding or extrusion comprising 50 to 99% of units derived from an ethylenically unsaturated principal monomer that is principally an alkyl methacrylate or styrene and 50 to 1% of a mixture of ethylenically unsaturated acid anhydride and carboxylic acid units derived from an alpha-substituted acrylic acid, it being understood that at least

[0007] 5% and preferably at least 10% of the units in this mixture are anhydride units.

[0008] EP 0076691 in 1982 claims copolymers having glutaric anhydride entities produced by anhydrization of copolymers comprising, among others, methyl methacrylate and comonomers such as acrylic acid or methacrylic acid. These copolymers are then anhydrized and imidized with the aim of increasing their thermal stability.

[0009] Continuing the same technical problem, EP0264508 in 1985 disclosed copolymer compositions comprising a vinyl monomer, acrylic acid and methacrylic acid, the acid monomers being able to represent up to 50% of the composition of the copolymers even though only compositions with a very high proportion of methyl methacrylate are exemplified.

[0010] EP 0774471 in 1995 discloses a suspension process using compositions of methyl methacrylate and methacrylic acid with mass proportions of methacrylic acid of up to 40% also showing the interest of these compositions in improving the temperature properties of these copolymer compositions.

[0011] EP 1496067 in 2002 claims copolymer compositions comprising glutaric entities obtained by anhydrization of copolymers including, among others, methyl methacrylate and methacrylic acid, for improving the temperature resistance of these copolymers, as well as their resistance to chemical agents and scratch resistance. These compositions have a majority of methyl methacrylate in their composition.

[0012] More recently, EP 2447292 in 2010 discloses aqueous-soluble copolymer compositions in which a majority of acid monomers are present. Compositions with a high acrylic acid content are exemplified, typically 80%, with another methacrylic ester comonomer.

[0013] Finally, in EP 3330302 in 2015, compositions with cyclic structures and predominantly methacrylic ester monomers and other monomers with vinyl motifs are disclosed. These compositions exhibit good optical, thermal, and mechanical strength properties.

[0014] In all cases, the presence of methacrylic or acrylic acid allows for an improvement of certain properties such as the glass transition temperature, scratch resistance and the preservation of certain mechanical properties at higher temperatures compared to polymers containing only methyl methacrylate, but also their solubility in aqueous solutions for the majority proportions of (meth)acrylic acid.

[0015] The presence of acidic entities within the macromolecular chain sometimes results, whether desired or undesired, in the cyclization of some of the acidic entities, whether adjacent or not, into glutaric anhydride entities, which leads to a strengthening of the aforementioned properties. Thus, in addition to the functions of methyl methacrylate and methacrylic acid, this type of copolymer can exhibit glutaric anhydride functions. Depending on the conditions, the acidic groups of the initial copolymer tend to cyclize by reaction either with a group neighboring acid (water loss), or with a neighboring methyl ester group (methanol loss).

[0016] In the majority of compositions described in the prior art, the quantities of methacrylic acid present are less than 20% by weight, bringing these compositions closer to PMMA in terms of properties and applications, but there are also compositions with major proportions of acidic monomeric entities that are soluble in aqueous media.

[0017] Compositions with methyl methacrylate and acidic entities content around 50% by mass of monomers are, on the other hand, much less described.

[0018] These compositions, whether anhydrous or not, can be of interest as such or in blend formulations with other polymers. They differ from low-acid compositions in that their properties are far removed from those of PMMA, and their solubilities in aqueous solutions can be advantageous in the fields of packaging and the delayed and / or controlled release of active ingredients in humid environments.

[0019] They can also improve the thermomechanical properties of sacrificial polymer formulations in 3D printing while maintaining the solubility of the sacrificial formulation in aqueous media. Indeed, in 3D printing processes using fused filament deposition, it is sometimes necessary to support the polymer to be printed with a formulation that prevents the structure from collapsing during the 3D printing process. Once the part is complete, the sacrificial composition is removed by dissolving it in a solvent, generally an aqueous solution. 3D printing processes are increasingly in demand for obtaining complex objects. This avoids the need to manufacture molds, which are difficult to produce. When small batches of parts need to be prepared, these processes have a much lower carbon footprint than conventional processes such as molding or injection molding.In particular, these are processes where there is little material waste.

[0020] Sacrificial supports soluble in aqueous media may exhibit certain properties insufficient for their use as supports. It is sometimes necessary to combine several soluble or dispersible materials to meet the requirements for rheology, temperature resistance, and good solidification. Thus, the compositions of the invention make it possible to overcome these deficiencies, in whole or in part, with respect to properties such as mechanical, rheological, glass transition temperature, and solubility in aqueous media.

[0021] These compositions with high methacrylic acid content, when wholly or partially anhydroused, exhibit, however, a high viscosity at melting, which makes them difficult to extrude or mold. During the extrusion of With such compositions, flow rates remain limited, and numerous black spots resulting from degradation are found in the finished material. Furthermore, their viscosity limits the range of suitable rheology for use in 3D printing processes employing these sacrificial materials.

[0022] The applicant has thus discovered that replacing a small part of the methacrylic acid with acrylic acid (AA) makes it possible to significantly improve the fluidity of the copolymers without prejudice to the other properties sought with these copolymers with high levels of acid monomer, typically close to 50 / 50 MMA / MAA.

[0023] In addition, the process used allows the presence of glutaric rings to be adjusted by the subsequent anhydrization in proportions of up to 40% by mass of anhydride entities because the fluidity of the copolymer results in better quality in terms of external pollution from the processing tools, as well as better flow rates of the machines.

[0024] This results in compositions whose glass transition temperature and other properties can be adjusted.

[0025] It is therefore possible to obtain copolymers with high anhydrization rates without being penalized by the viscosities generated on copolymers where only MMA and AMA are present.

[0026] The overall scheme leading to the anhydrization of these compounds is recalled in [Fig.1].

[0027] Summary of the invention.

[0028] The invention relates to a composition comprising a statistical copolymer comprising the following monomers:

[0029] -Methyl methacrylate of 50 to 60 wt%, inclusive of terminals,

[0030] -Methacrylic acid of 40 to 50% mass, inclusive,

[0031] - Acrylic acid of 2 to 8% by mass, inclusive of terminals,

[0032] and of which part of the acrylic acid and methacrylic acid functions is anhydrous in a proportion between 0 and 40% by mass of anhydride entities. Description of the implementation methods

[0033] The compositions of the invention are expressed by mass of the monomers methyl methacrylate, methacrylic acid, and acrylic acid. The proportion of anhydride is measured by proton NMR, incorporating the respective molar masses of the monomers into the calculation, with the anhydride entity being considered to have a molecular mass of 154g.

[0034] The compositions comprising the copolymers of the invention include methyl methacrylate, all or part of which may be recycled methyl methacrylate, i.e. from a recycling process by depolymerization of PMMA and its copolymers, followed by a purification step aimed at obtaining a methyl methacrylate content greater than 99%.

[0035] In addition, the compositions comprising the copolymers of the invention include methyl methacrylate, all or part of which may be derived from a bio-based renewable resource, i.e. having a 14C / 12C ratio between 0.9 and 1.3 10 12.

[0036] The compositions comprising the copolymers of the invention include methacrylic acid, all or part of which may be derived from a renewable resource 1 / 110 1 O bio-based, that is to say, having a C / C ratio between 0.9 and 1.3 10.

[0037] The compositions comprising the copolymers of the invention include acrylic acid, all or part of which may be derived from a bio-based renewable resource. 14 12 12 that is to say presenting a C / C ratio between 0.9 and 1.3 10.

[0038] Thus the copolymers of the compositions of the invention can have a 14C / 12C ratio ranging from 0 to 1.3 10 12, and preferably between 0.5 and 1.3 10 12, and preferably between 0.8 and 1.3 10 12.

[0039] This ratio can be measured using conventional carbon-14 dating techniques, and in particular ASTM D6866-24. The 14C / 12C ratio, with a value of 1.3 × 10¹², corresponds to the ratio measured in living organisms. Given the half-life of carbon-14 of 5730 years, this ratio is considered to remain within this order of magnitude for many years due to the precision of the measurement.

[0040] The copolymers of the compositions of the invention may have an anhydration rate in the form of glutaric rings of between 0 and 40% by mass of anhydride entities.

[0041] The copolymers present in the compositions of the invention can be obtained by processes known to those skilled in the art, including bulk, solvent, emulsion, and suspension processes. Preferably, these are suspension or solvent-phase processes, and more preferably suspension and solvent-phase processes such as ethanol, toluene, and methyl ethyl ketone, alone or in mixtures, and preferably an ethanol-toluene or ethanol-methyl ethyl ketone mixture.

[0042] The syntheses are carried out in a radical or radical controlled manner.

[0043] When it is necessary to obtain the copolymers of the compositions of the invention with determined anhydration cyclization rates, the copolymers resulting from the synthesis undergo a second transformation step using a tool compounding equipment, including single and twin screw extruders, continuous mixers, mixing reactors, and atomizers.

[0044] Preferably, a twin-screw extruder equipped with a degassing device for removing effluents (residual solvent, water, and methanol) or a mixing reactor equipped with a degassing device for removing effluents (residual solvent, water, and methanol) is used. Even more preferably, a mixing reactor is used.

[0045] Thus, for example, a copolymer obtained by solvent extraction can be treated in a temperature-controlled, vacuum-controlled mixing reactor with a flow rate that allows adjustment of the residence time to separate the solvent and carry out the anhydration transformation of some of the acidic functional groups from the copolymerized acrylic monomers. The product from the mixing reactor is recovered by an extrusion granulation step.

[0046] Similarly, a copolymer obtained by the suspension route will be separated from the aqueous phase by filtration and then treated in an extruder to carry out the anhydration transformation of part of the acid functions from the copolymerized (meth)acrylic monomers.

[0047] Thus, copolymers can be obtained with an anhydrization rate varying from 0 to 40% by mass of anhydride entities, preferably between 10 and 40%, preferably between 20 and 35%, and even more preferably between 25 and 35%.

[0048] Starting from monomeric compositions comprising the monomers MMA, MAA, and AA, a whole family of copolymers can be obtained, including these polymerized monomers, as well as an adjustable level of glutaric anhydride functions through subsequent anhydration and cyclization processes, depending on the conditions of the second transformation step. This makes it possible to obtain products with varied properties depending on the synthesis conditions of this second step, starting from compositions comprising the same MMA / MAA / AA monomers.

[0049] Regarding the monomeric proportions MMA / MAA / AA of the copolymers present in the compositions of the invention, they shall be part of the following sets:

[0050] -Methyl methacrylate (MMA) of 50 to 60 wt%, preferably of 52 to 58 wt%, and preferably between 53 and 57 wt% inclusive.

[0051] -Methacrylic acid of 40 to 50% by mass, preferably of 40 to 46% by mass inclusive,

[0052] -Acrylic acid of 2 to 8% by mass, and preferably of 3 to 7% by mass, and preferably of 4 to 6% by mass, inclusive.

[0053] The anhydrization of the copolymers of the compositions of the invention is carried out in a step subsequent to the synthesis of the copolymers. This step can advantageously can be carried out directly following the synthesis in a tool such as a single and twin screw extruder, a continuous mixer, a mixing reactor, or an atomizer.

[0054] The synthesis of the copolymers of the compositions of the invention can be carried out in the presence of a chain limiter such as a mercaptan, in particular an alkyl mercaptan whose alkyl chain, branched or unbranched, has between 4 and 8 carbon atoms.

[0055] The copolymers of the compositions of the invention have a molecular mass by weight between 50000 and 200000 g / mol, preferably between 50000 and 150000 g / mol, preferably between 60000 and 120000 g / mol, and even more preferably between 60000 and 95000, measured by size exclusion chromatography with polystyrene standards.

[0056] The dispersity of the copolymers of the compositions of the invention is between 1.2 and 3 and preferably between 1.2 and 2.

[0057] The viscosities of the copolymers of the compositions of the invention at 30% mass in a mixture of solvents of 68% mass of ethanol and 32% mass of toluene are between 8000 and 25000 and preferably 10000 to 20000 mPa.s.

[0058] The copolymers of the compositions of the invention can be used in sacrificial polymer compositions in 3D printing by molten filament deposition, as an adhesion promoter, as a formulation additive to improve the thermomechanical properties of polymer formulations, capsules of active ingredients soluble in aqueous media, to name only the main ones.

[0059] Example 1:

[0060] In this series of examples, the tests were conducted in monomer proportions of 55% by mass MMA and 45% by mass (meth)acrylic acid, or 45% by mass is the sum of methacrylic acid and acrylic acid. These proportions are those of the reactor charge.

[0061] This series of examples is carried out using a solvent process.

[0062] The reagents are as follows:

[0063] - Initiator: Luperox 575 (tert-amyl peroxy-2-ethylhexanoate, from Arkema).

[0064] - Methacrylic acid (AMA) (Aldrich source).

[0065] - Acrylic acid (AA) (origin Aldrich).

[0066] - Methyl methacrylate (MMA) (Aldrich source).

[0067] - Ethanol (from Aldrich).

[0068] - Toluene (Aldrich source).

[0069] The syntheses are carried out in a 4 litre reactor under stirring in a closed stainless steel reactor under nitrogen atmosphere for 210 minutes with the quantities of reactants in Table 1.

[0070] [Tables 1] [Table 1 Reference Test 1 (3% AA) Test 2 (5% AA) | Luperox 57SE (g) 5 5 5 | Methacrylate (g) 66 66 66 1 | Methacrylic acid (g) ..................SB................. w | Acid (g) 0 3:6 60 Ethanol (g) 116 116 116 b | Toluene (g) 548 548 548 | Reactor temperature 105 105

[0071] The final conversions are 95%.

[0072] The final mixture is transferred to a mixing reactor (residence time of 30 minutes at 210°C under vacuum to evaporate the solvent and residual monomers). A measurement of the anhydrization rate is carried out on these products at the reactor outlet and shows that they are damaged.

[0073] The reference has a molecular mass by weight of 72000 g / mol compared to 76000 for test 1 and 77000 for test 2. The measurements are carried out by SEC with calibration using polystyrene samples.

[0074] Reference tests 1 and 2 are then processed in a LIST-type mixing reactor followed by a twin-screw L / D 45 extruder and granulation. The residence time is adjusted based on the residence time in the mixing reactor. A 150 µm filter is fitted in the extruder just before the die.

[0075] The anhydration rate (% Panh) is thus measured after a residence time of 3 and 15 minutes (Table 2):

[0076] The proportion of anhydride (PAnh) is measured by proton NMR and integrating into the calculation the respective molar masses of the other monomers, the anhydride entity being considered to have a molecular mass of 154g.

[0077] The concentrations are calculated from the 1H NMR spectra:

[0078] -The content of polymerized methacrylic acid is calculated on the signal of the acid OH around 12 ppm on the spectrum without TFA (trifluoroacetic acid).

[0079] -The content of polymerized methyl methacrylate is calculated on the signal of OCH3 ester between 3.2 and 3.7 ppm on the spectrum + TFA.

[0080] -The content of polymerized acrylic acid is neglected.

[0081] - The Panh content is calculated on the 1H spectrum by difference in the zone of aliphatic protons between 0.0 and 2.5 ppm on the spectrum in the presence of TFA.

[0082] [Tables2] Table 2 % Panh 3 minutes % Panh 15 minutes Anhydrous Reference 20 32 Test 1 anhydrous 21 30 Test 2 anhydrous 20 30

[0083] Viscosity measurements are carried out at 10 and 30% mass of copolymer in a mixture of solvents (68% mass of ethanol and 32% mass of toluene).

[0084] A rheometer with imposed constraints, type MCR301 from ANTON PAAR, is used. The standard used is 1TSO 3219-2:2021.

[0085] The measurements are carried out by stress sweep in flow at 20°C. The geometry used is of the duvet type for which temperature regulation is ensured by the Peltier effect. The duvet geometry used is given in [Fig.1].

[0086] The composition to be studied is introduced into the air gap of the duvet geometry using a disposable pipette. The shear gradient range varies logarithmically from 0.1 to 100 s⁻¹ with 10 measurements per decade.

[0087] The granules from the extruder are examined using the OCS PS25C device to determine the amount of contamination in the form of black spots. The device performs an image analysis on 2 liters of granules. The granules are conveyed by means of a vibrating conveyor belt under a camera that inspects the surface of the granules and captures images of the identified defects.

[0088] The size of the defects is measured and the software distributes the number of defects by size class. In particular, pollution with a size greater than 600 pm is reported.

[0089] The measurements of the reference tests, 1 and 2 anhydrized for 15 minutes, are thus evaluated in viscosity and a count of the pollution in the form of black dots is evaluated (Table 3).

[0090] [Tables3] Table 3 Viscosity (mPa): mass viscosity (mP-a. 30% mass pbHuUum >600 ★ reference anhydride 36.7 36400 lis essas 1. anhydrized 26.1 19100 19 essas 2 anhydrine 26 15800 | 16

[0091] It should be noted that the anhydrized reference material exhibits a much higher viscosity than the anhydrized test materials 1 and 2. This results in significant contamination during extrusion due to the excessive viscosity of the reference material.

Claims

Demands

1. Composition comprising a statistical copolymer resulting from a polymerization comprising the following monomers: -Methyl methacrylate of 50 to 60 wt% inclusive, -Methacrylic acid of 40 to 50 wt% inclusive, -Acrylic acid of 2 to 8 wt% inclusive, and wherein a portion of the acrylic acid and methacrylic acid functions is anhydrized in a proportion of between 0 and 40 wt% of anhydride entities.

2. Composition according to claim 1 comprising methyl methacrylate, of which all or part may be recycled methyl methacrylate.

3. Composition according to claim 1 or 2 comprising methyl methacrylate, all or part of which may be derived from a bio-based renewable resource, i.e. having a 14C / 12C ratio between 0.9 and 1.3 10 12 measured according to ASTM D6866-24.

4. Composition according to claim 1 to 3 comprising (meth)acrylic acid, all or part of which may be derived from a bio-based renewable resource, i.e. having a 14C / 12C ratio between 0.9 and 1.3 10 12 measured according to ASTM D6866-24.

5. A method for synthesizing one of the compositions according to claims 1 to 4 characterized by its implementation in suspension or in solvent phase followed optionally by a transformation step in a single or twin screw extruder, a continuous mixer, a mixing reactor.

6. Use of the compositions according to any one of claims 1 to 4 in sacrificial polymer compositions in 3D printing by fused filament deposition, as an adhesion promoter, as a formulation additive to improve the thermomechanical properties of polymer formulations and capsules of active ingredients soluble in aqueous media.