Quick-drying, highly elastic fabrics and related textile products

Abstract

To provide a quick-drying, highly elastic fabric and its textile product, which is related to home textiles having advantages of quick-drying and high elasticity. [Solution] The quick-drying, highly elastic home textile includes an upper fabric layer 1 and a lower fabric layer 5, with pearl cotton material layers 3 placed under the upper fabric and on the lower fabric layer, and adjacent layers are arranged face to face. It can be used as a home textile for futons, futons, cushions, pillows, neck pillows, carpets, carpet underlays, quilted pads, Simmons pads, mattresses, dehumidifying pads, moisture absorbing pads, sofas, etc.

Description

[Technical field]

[0001] The present invention relates to a quick-drying, highly elastic home textile, specifically to a kind of quick-drying, highly elastic fabric and its textile products. [Background technology]

[0002] Filling materials for home textiles and household products such as futons, mattresses, cushions, pillows, neck pillows, carpets, carpet underlays, quilting pads, Simmons pads, mattresses, dehumidifying pads, moisture absorbing pads, sofas, etc. are required to be soft, flexible, heat retaining, washable, quick drying, and have good bounce back and do not harden even after repeated use.

[0003] In the current market, polyester fiber filling is used, which is loosened, sorted, and messed in sorting equipment, laid on a net, and then fixed with hot melt or adhesive spray to make a cotton-like sheet. It is soft and fluffy, but has low durability and elasticity, and especially futons and pads have problems such as sinking after long-term use, and many gaps remain even after washing, making it difficult to dry. It is especially difficult to dry on cloudy and rainy days, and a large amount of bacteria will grow, which not only causes health hazards but also produces unpleasant odors, making it difficult to meet the demands of busy life in modern society. Summary of the Invention [Problem to be solved by the invention]

[0004] The object of the present invention is to provide a quick-drying, highly elastic fabric and its textile products, which have the advantages of quick-drying and high elasticity. [Means for solving the problem]

[0005] The quick-drying, highly elastic home textile comprises an upper fabric layer (1) and a lower fabric layer (5), with a pearl cotton material layer (3) placed under the upper fabric layer (1) and on the lower fabric layer (5), with adjacent layers arranged face to face.

[0006] The application of the pearl cotton material layer (3) gives the home textile quick-drying and high resilience properties.

[0007] In the above technical proposal, the number of layers of the pearl cotton material layer (3) is one or more, for example, 1 to 10 layers. More specific non-limiting examples include 1 layer, 2 layers, 3 layers, 4 layers, 5 layers, 6 layers, 7 layers, 8 layers, 9 layers, etc. Only under the same comparison conditions, the pearl cotton layer (3) in the embodiment of the present invention has one layer of pearl cotton.

[0008] Technical experts in the industry know that pearl cotton, also known as EPE pearl cotton material, is polyethylene foam cotton, a new environmentally friendly packaging material, which can be produced by adding various auxiliaries to high pressure low density polyethylene and foaming. Only under comparable comparison conditions, the sheet-shaped and mesh-shaped pearl cotton used in this invention are produced by foaming and extruding the combination of the following components in a single screw extruder: LDPE masterbatch, weight ratio is 100. Micron silicon dioxide airgel, weight occupancy ratio is 0.8. Nano silicon dioxide, weight ratio is 1.2. Talc, weight ratio is 3.0. Glycerol monostearate, weight share is 3.0. Norbutane, weight share is 26.

[0009] In the above technical solution, at least one embodiment of the present invention installs an upper cotton-like sheet layer (2) under the upper fabric layer (1) and on the pearl cotton material layer (3), and / or installs a lower cotton-like sheet layer (4) under the pearl cotton material layer (3) and on the lower fabric layer (5).

[0010] The cotton-like sheet of the cotton-like sheet layer is a fiber net made of fibers known in the existing technology, and is a sheet-like material connected by heating or adhesive spraying, and is characterized by being fluffy and soft. In order to obtain the fluffy and soft texture, at least one kind of fiber is selected from a group of materials consisting of polyester fiber, acrylic fiber, vinylon fiber, nylon fiber, cellulose fiber, wool, silk thread, seaweed fiber, PLA fiber, etc. Each sheet of the cotton-like sheet layer may have the same or different chemical composition. The composition of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) may be the same or different.

[0011] In the above technical solution, the fiber for making the cotton-like sheet can be selected to have a fineness of 0.1 dtex-50 dtex, non-limiting examples include 0.5 dtex, 1 dtex, 5 dtex, 10 dtex, 15 dtex, 20 dtex, 25 dtex, 30 dtex, 35 dtex, 40 dtex, 45 dtex, etc. Or / alternatively, the fiber for making the cotton-like sheet can be selected to have a length of 10 mm to 200 mm, such as, but not limited to, 15 mm, 20 mm, 25 mm, 30 mm, 35 mm, 40 mm, 45 mm, 50 mm, 60 mm, 70 mm, 80 mm, 90 mm, 100 mm, 110 mm, 120 mm, 130 mm, 140 mm, 150 mm, 160 mm, 170 mm, 180 mm, 190 mm, etc.

[0012] In the above technical proposal, 2 The weight of the cotton sheet per unit can be selected from 10 to 1000g. 2 As a non-limiting example, the weight of the cotton-like sheet can be 15 g / m 2 , 20g / m 2 , 30g / m 2 , 40g / m 2 , 50g / m 2 , 60g / m 2 , 70g / m 2 , 80g / m 2 , 90g / m 2 , 100g / m 2 , 150g / m 2 , 200g / m2 , 250g / m 2 , 300g / m 2 , 350g / m 2 , 400g / m 2 , 450g / m 2 , 500g / m 2 , 550g / m 2 , 600g / m 2 , 650g / m 2 , 700g / m 2 , 750g / m 2 , 800g / m 2 , 850g / m 2 , 900g / m 2 , 950g / m 2 etc.

[0013] In the above technical solution, the thickness of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) is independently selected from 3 to 300. Non-limiting examples include 4 mm, 5 mm, 6 mm, 7 mm, 8 mm, 9 mm, 10 mm, 15 mm, 20 mm, 25 mm, 30 mm, 35 mm, 40 mm, 45 mm, 50 mm, 60 mm, 70 mm, 80 mm, 90 mm, 100 mm, 150 mm, 200 mm, 250 mm, etc.

[0014] Under the same comparative conditions, the cotton-like sheet of the cotton-like sheet layer in the embodiment and comparative example of the present invention uses 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, and is manufactured through the following steps at a thermal melting temperature of 150°C, by mixing-arranging-laying on a net-heat fusing-cutting the edges-rolling. The weight of this cotton-like sheet is 60g / m2. 2and the thickness is 5mm. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a length of 60 mm, and the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a length of 51 mm. The thickness of the cotton-like sheet layer can be increased by increasing the number of layers of the cotton-like sheet. That is, the thickness of the cotton-like sheet layer = the number of layers of the cotton-like sheet layer x the thickness of the sheet. In the examples and comparative examples of the present invention, the thickness of the cotton-like sheet layer is different from the thickness of the cotton-like sheet layer of 5 mm, and is achieved by increasing the number of layers used in the cotton-like sheet layer. Based on the thickness of the cotton-like sheet of 5 mm, the thickness of the cotton-like sheet layer can be calculated in mm, which is the number of layers of the cotton-like sheet x 5. Of course, the thickness of the cotton-like sheet can also be increased by increasing the weight of the cotton-like sheet and / or the fineness of the normal melting point polyester fiber, and a comparable technical effect can be obtained, although it is not specifically shown in the examples and comparative examples.

[0015] In the above technical solution, in at least one embodiment, the pearl cotton of the pearl cotton material layer (3) is columnar pearl cotton, block pearl cotton, sheet pearl cotton or mesh pearl cotton. Compared with other types of pearl cotton, mesh pearl cotton is more advantageous in enhancing the elasticity and flexibility of the present invention.

[0016] In the above technical solution, the mesh pearl cotton can be two-dimensional mesh pearl cotton or three-dimensional mesh pearl cotton. The effect of three-dimensional mesh is better, but two-dimensional mesh pearl cotton is easier to manufacture than three-dimensional mesh pearl cotton. In the embodiment of the present invention, only under the same comparative conditions, two-dimensional mesh pearl cotton is generally adopted.

[0017] In the above technical solution, in at least one embodiment, the mesh pearl cotton is made by pearl cotton strips crossing each other and fusing and bonding with each other at the crossing points, or by a mesh distributed on the membrane sheet.

[0018] In the above technical solution, at least one implementation of the mesh pearl cotton has a square shape.

[0019] In the above technical solution, at least one of the implementations has a diamond-shaped mesh of the mesh-like pearl cotton.

[0020] In the above technical solution, in at least one embodiment, the length of the long diagonal of the diamond is L and the length of the short diagonal is W, and the ratio of L to W is greater than 1 and not greater than 100. For example, but not limited to, the ratio of L to W can be 1, 1.5, 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 30, 40, 50, 60, 70, 80, 90, etc., with 1.5 to 10 being preferred. Only under comparable comparison conditions, in the present invention, this ratio is mainly limited to 3.33.

[0021] In the above technical solution, in at least one embodiment, L is 5-100 mm. For example, but not limited to, L is 10 mm, 15 mm, 20 mm, 25 mm, 30 mm, 35 mm, 40 mm, 45 mm, 50 mm, 60 mm, 70 mm, 80 mm, 90 mm, etc., with 10-50 mm being preferred.

[0022] In the above technical solution, in at least one embodiment, the cross section of the pearl cotton strip is circular.

[0023] In the above technical proposal, in at least one embodiment, the ratio of the thickness of the joint to the diameter of the cross section is greater than 1 and less than 2. For example, but not limited to, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, etc. In this case, the thickness of the joint is also the thickness of the net-like mesh pearl cotton. Only under comparable comparison conditions, this ratio is limited to 1.5 in this invention.

[0024] In the above technical solution, in at least one embodiment, the thickness of the pearl cotton is 1 to 100 mm, for example, but not limited to, the thickness of the pearl cotton can be 2 mm, 3 mm, 4 mm, 5 mm, 6 mm, 7 mm, 8 mm, 9 mm, 10 mm, 15 mm, 20 mm, 30 mm, 40 mm, 50 mm, 60 mm, 70 mm, 80 mm, 90 mm, etc.

[0025] In the above technical solution, at least one embodiment has a circle diameter of 1-100mm. For example, but not limited to, the circle diameters are 2mm, 3mm, 4mm, 5mm, 6mm, 7mm, 8mm, 9mm, 10mm, 15mm, 20mm, 30mm, 40mm, 50mm, 60mm, 70mm, 80mm, 90mm, etc., but by way of example only, the embodiment of the present invention further focuses on the circle diameter in the range of 1-20mm.

[0026] In the above technical solution, at least one embodiment is that the above-mentioned upper fabric layer (1) and lower fabric layer (5) are independently selected from knitted fabric, shuttle fabric, nonwoven fabric, non-spun felt, leather, fur, or synthetic leather.

[0027] In the above technical solution, the upper fabric layer (1) and the lower fabric layer (5) may or may not be made of the same material. Only under comparable comparison conditions, in the examples and comparative examples of the present invention, the upper fabric layer (1) and the lower fabric layer (5) both have a weight of 85g / m 2The Spring Yasin fleece has a warp specification of polyester DTY75D / 36F, density of 41 threads / inch, and a weft specification of polyester DTY150D / 288F, density of 28 threads / inch. After disclosing the above characteristics of Spring Yasin fleece, technicians in the industry can purchase this fabric from the market, or manufacture it based on existing technology. For example, polyester DTY75D / 36F is used as the warp yarn, polyester DTY150D / 288F is used as the weft yarn, and a base fabric is made by weaving it with a water jet loom, and then the following processes are carried out: sanding -- rinsing -- dyeing -- widening, forming -- winding, and the fabric specification is 75D*150D / 41*28, and the above Spring Yasin fleece can be obtained.

[0028] In the above technical solution, at least one implementation is that these layers are joined together by sewing or compounding.

[0029] In the above technical solution, at least one embodiment is that the above-mentioned products are a quilt, a futon, a cushion, a pillow, a neck pillow, a carpet, a carpet underlay, a quilted pad, a Simmons pad, a mattress, a dehumidifying pad, a moisture absorbing pad, or a sofa.

[0030] In the above technical solution, at least one of the implementations uses a sewing method of lockstitch, split hem, backstitch, hem seam, sandwich seam, back seam, outside fold seam, rolled seam or quilting. Only under comparable comparison conditions, this invention sews each layer together and connects them all by quilting. Specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, and the quilting flower pattern is a square with a diagonal length of 2 inches, the stitching is 9 stitches / 3 cm, and is connected by quilting.

[0031] Those skilled in the art will understand that, if necessary, there is a way to wrap the edges of the product of the present invention to prevent the edges from becoming loose during storage, transportation and use, and to ensure the structure is stable, and that the techniques of the art can be reasonably selected to do so, without the need for creative labor.

[0032] All of the above-mentioned products can achieve comparable technical effects. Only under comparable comparison conditions, the embodiments and comparative examples of the present invention take a quilted pad as an example, the size of the quilted pad is 100cm x 200cm, and the edge of the quilted pad is wrapped with a polyester warp knit pile of 110g / square. The suede side of the fabric for wrapping the edge is on the outside, the width is 6.2cm, and the stitching distance is 9 stitches / 3cm. Effect of the Invention

[0033] <Performance test> 1) The method for evaluating quick-drying properties is as follows: The quilted pads made in the examples and comparative examples are taken and placed in a washing machine, and washed according to the C4M method set in accordance with JIS L 1930-2014, the home washing test method for Japanese textile products. After washing, the test specimens are taken out and hung in a constant temperature and humidity room with an air speed of 5m / min, a temperature of 25°, and a relative humidity of 65%. The mass of the quilted pad is measured every 10 minutes, and the time when the mass becomes 1.1 times or less than 1.1 times the sample is recorded, and the quick-drying effect is evaluated according to Table 1. JPEG0003250386000002.jpg24170

[0034] 2) Compression elasticity evaluation Take the quilted pads made in the examples and comparative examples, remove the wrapped edges, and cut out a prototype with a length x width of 20CM x 20CM. Take 10 of these prototypes, stack them in a transparent container with a bottom of 20CM x 20CM and a height of 80CM, place them under the pressure arm of a single-arm fabric strength tester of model number HD026, use a press with a diameter of 20CMM, apply a gravity of 4.9 Newtons (N) for 10 minutes, measure the total height H0 of the 10 prototypes, continue to increase the pressure to 196 Newtons (N), apply the 10 prototypes for 120 hours, measure the total height H1 of the 10 prototypes, reduce the pressure, and again apply a gravity of 4.9 Newtons (N) on top for 10 minutes, measure the height H2 of the 10 prototypes. Compression resilience = (H2-H1) / (H0-H1) *100%, and the evaluation method is as shown in Table 2. JPEG0003250386000003.jpg28170

[0035] 3) Flexibility evaluation Take the quilted pads made in the examples and comparative examples, remove the wrapped edges, and cut a prototype with a length x width of 20CM x 20CM. Take 10 of these prototypes, stack them in a transparent container with a bottom of 20CM x 20CM and a height of 80CM, place them under the pressure arm of the model HD026 single-arm fabric strength tester, use a plate with a diameter of 20CM, and apply a gravity of 4.9 Newtons (N) on top for 10 minutes, measure the total height H1 of the 10 prototypes, increase the pressure of the pressure arm to compress the H1 height to 60%, and read the maximum pressure value. The evaluation method is as shown in Table 3. JPEG0003250386000004.jpg32170

[0036] The present invention will be described in detail below with reference to the accompanying drawings and specific implementation methods. [Brief description of the drawings]

[0037] [Figure 1] FIG. 2 is a schematic top view of the embodiment of the present invention; [Diagram 2] FIG. 2 is a schematic diagram of a longitudinal section cut-away view in the first embodiment of the present invention; [Diagram 3] FIG. 2 is a schematic diagram of a longitudinal section cut-away view in the second embodiment of the present invention; [Figure 4] FIG. 1 is a schematic diagram of a conventional vertical cross-sectional view. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0038] <Comparative Example 1> Please refer to Figures 1 and 4. 1. Manufacture of quilted pads The manufacture of spun household goods includes an upper fabric layer (1) and a lower fabric layer (5), with a cotton-like sheet layer (2a) disposed beneath the upper fabric layer (1) and upon the lower fabric layer (5), with adjacent layers disposed face-to-face.

[0039] The cotton-like sheet of the cotton-like sheet layer is made of 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, and is manufactured through the following process at a heat melting temperature of 150°C, by mixing, arranging, laying on a net, heat melting, cutting the edges, and rolling. The weight of this cotton-like sheet is 60g / m 2 The thickness is 5mm. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a length of 60mm, and the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a length of 51mm. The thickness of this cotton-like sheet layer is 10mm, and is achieved by using two sheets for the cotton-like sheet layer.

[0040] The upper fabric layer (1) and the lower fabric layer (5) together weigh 85 g / m 2 The Spring Yasin fleece has a warp specification of polyester DTY75D / 36F, density of 41 threads / inch, and a weft specification of polyester DTY150D / 288F, density of 28 threads / inch. After disclosing the above characteristics of Spring Yasin fleece, technicians in the industry can purchase this fabric from the market, or manufacture it based on existing technology. For example, polyester DTY75D / 36F is used as the warp yarn, polyester DTY150D / 288F is used as the weft yarn, and a base fabric is made by weaving it with a water jet loom, and then the following processes are carried out: sanding -- rinsing -- dyeing -- widening, forming -- winding, and the fabric specification is 75D*150D / 41*28, and the above Spring Yasin fleece can be obtained.

[0041] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0042] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0043] 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 374 minutes, rated as grade 5. Compression elasticity: The compression elasticity is 36%, rated as grade 5. Flexibility: The indentation hardness is 34 Newtons, rated as grade 1. EXAMPLES

[0044] Please refer to Figures 1 and 2. 1. Manufacture of quilted pads The quick-drying, highly elastic home textile comprises an upper fabric layer (1) and a lower fabric layer (5), with a pearl cotton material layer (3) placed under the upper fabric layer (1) and on the lower fabric layer (5), with adjacent layers arranged face to face. The pearl cotton of the above-mentioned pearl cotton material layer (3) is a mesh-like pearl cotton. The aforementioned mesh-like pearl cotton is formed by pearl cotton strips that cross each other and bond at the crossing points. The mesh of the pearl cotton mentioned above is diamond-shaped. The long diagonal L of the aforementioned rhombus is 10 mm, and the short diagonal W is 3 mm. Pearl cotton strips are circular in cross section. The diameter of the aforementioned circle is 4 mm. The ratio of thickness to cross-sectional diameter of the aforementioned joint is 1.5, and the thickness is 6 mm. Mesh pearl cotton m 2 Weight per unit is 50g / m 2 It is.

[0045] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0046] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0047] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2 The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0048] 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 94 minutes, rated as grade 2. Compression elasticity: Compression elasticity is 96%, rated as first class. Flexibility: Indentation hardness 113 Newtons, rated grade 2. EXAMPLES

[0049] Please refer to Figures 1 and 2. The quick-drying, highly elastic home textile comprises an upper fabric layer (1) and a lower fabric layer (5), characterized in that a pearl cotton material layer (3) is placed under the upper fabric layer (1) and on the lower fabric layer (5) and is disposed face-to-face between each adjacent layer.

[0050] The pearl cotton of the above-mentioned pearl cotton material layer (3) is a sheet-like pearl cotton. The pearl cotton is 6mm thick. Pearl cotton sheet m 2 Weight per unit is 82g / m 2 It is.

[0051] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2 The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0052] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0053] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2 The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0054] 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 81 minutes, rated as grade 2. Compression elasticity: The compression elasticity is 84%, rated as grade 2. Flexibility: Indentation hardness is 178 Newtons, rated as grade 3. EXAMPLES

[0055] Please refer to Figures 1 and 3. The quick-drying, highly elastic home textile comprises an upper fabric layer (1) and a lower fabric layer (5), a pearl cotton material layer (3) is placed under the upper fabric layer (1) and on the lower fabric layer (5), an upper cotton-like sheet layer (2) is placed under the upper fabric layer (1) and on the pearl cotton material layer (3), and a lower cotton-like sheet layer (4) is placed under the pearl cotton material layer (3) and on the lower fabric layer (5), and is arranged in a face-to-face direction between each adjacent layer.

[0056] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2 The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0057] The sheet of the cotton-like sheet layer is made of 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, which is mixed--arranged--layed on a net--heat melted--cut the edges--wound through the following process at a heat melting temperature of 150°C. The sheet has a density of 60g / m 2 , and 5mm thick. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a fiber length of 60 mm, while the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a fiber length of 51 mm.

[0058] The thickness of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) is 25 mm, which is achieved by using five layers of sheets for the cotton-like sheet layer. The pearl cotton of the above-mentioned pearl cotton material layer (3) is a mesh-like pearl cotton. The aforementioned mesh-like pearl cotton is made by crossing strips of pearl cotton with each other and fusing and bonding them together at the crossing points. The mesh of the pearl cotton mentioned above is diamond-shaped. The length L of the long diagonal of the above-mentioned rhombus is 10 mm, and the length W of the short diagonal is 3 mm. The pearl cotton strips described above are circular in cross section. The diameter of the aforementioned circle is 4 mm. The ratio of thickness to cross-sectional diameter of the joint mentioned above is 1.5, and the thickness is 6 mm. Mesh pearl cotton m 2 Weight per unit is 50g / m 2 It is.

[0059] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0060] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0061] 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 468 minutes, rated as grade 5. Compression elasticity: The compression elasticity is 57%, rated as grade 4. Flexibility: Indentation hardness is 46 Newtons, rated as grade 1. EXAMPLES

[0062] Please refer to Figures 1 and 3. The quick-drying, highly elastic home textile includes an upper fabric layer (1) and a lower fabric layer (5), a pearl cotton material layer (3) is placed under the upper fabric layer (1) and on the lower fabric layer (5), an upper cotton-like sheet layer (2) is placed under the upper fabric layer (1) and on the pearl cotton material layer (3), and a lower cotton-like sheet layer (4) is placed under the pearl cotton material layer (3) and on the lower fabric layer (5), and is arranged in a face-to-face direction between each adjacent layer.

[0063] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2 The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0064] The sheet of the cotton-like sheet layer is made of 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, which is mixed--arranged--layed on a net--heat melted--cut the edges--wound through the following process at a heat melting temperature of 150°C. The sheet has a density of 60g / m 2 , and 5mm thick. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a fiber length of 60mm, while the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a fiber length of 51mm.

[0065] The thickness of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) is 15 mm, and each is achieved by using three layers of sheets. The pearl cotton of the above-mentioned pearl cotton material layer (3) is a mesh-like pearl cotton. The aforementioned mesh-like pearl cotton is made by crossing strips of pearl cotton with each other and fusing and bonding them together at the crossing points. The mesh of the pearl cotton mentioned above is diamond-shaped. The length L of the long diagonal of the above-mentioned rhombus is 10 mm, and the length W of the short diagonal is 3 mm. The pearl cotton strips described above are circular in cross section. The diameter of the aforementioned circle is 4 mm. The ratio of thickness to cross-sectional diameter of the aforementioned joint is 1.5, and the thickness is 6 mm. Mesh pearl cotton m 2 Weight per unit is 50g / m 2 It is.

[0066] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0067] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad. 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 326 minutes, rated as grade 4. Compression elasticity: The compression elasticity is 74%, rated as grade 3. Flexibility: Indentation hardness is 59 Newtons, rated as grade 1. EXAMPLES

[0068] Please refer to Figures 1 and 3. The quick-drying, highly elastic home textile comprises an upper fabric layer (1) and a lower fabric layer (5), with a pearl cotton material layer (3) placed under the upper fabric layer (1) and on the lower fabric layer (5), an upper cotton-like sheet layer (2) placed under the upper fabric layer (1) and on the pearl cotton material layer (3), and a lower cotton-like sheet layer (4) placed under the pearl cotton material layer (3) and on the lower fabric layer (5), and arranged in a face-to-face direction between each adjacent layer.

[0069] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2 The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0070] The sheet of the cotton-like sheet layer is made of 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, which is mixed--arranged--layed on a net--heat melted--cut the edges--wound through the following process at a heat melting temperature of 150°C. The sheet has a density of 60g / m 2 , and 5mm thick. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a fiber length of 60mm, while the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a fiber length of 51mm.

[0071] The thickness of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) is 5 mm, and each is realized by using a single sheet for the cotton-like sheet layer. The pearl cotton of the above-mentioned pearl cotton material layer (3) is a mesh-like pearl cotton. The aforementioned mesh-like pearl cotton is made by crossing strips of pearl cotton with each other and fusing and bonding them together at the crossing points. The mesh of the pearl cotton mentioned above is diamond-shaped. The length L of the long diagonal of the above-mentioned rhombus is 10 mm, and the length W of the short diagonal is 3 mm. Pearl cotton strips are circular in cross section. The diameter of the aforementioned circle is 4 mm. The ratio of thickness to cross-sectional diameter of the aforementioned joint is 1.5, and the thickness is 6 mm. Mesh pearl cotton m 2 Weight per unit is 50g / m 2 It is.

[0072] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0073] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0074] 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 116 minutes, rated as grade 2. Compression elasticity: The compression elasticity is 92%, rated as first class. Flexibility: Indentation hardness is 63 Newtons, rated as grade 1. EXAMPLES

[0075] Please refer to Figures 1 and 3. The quick-drying, highly elastic home textile comprises an upper fabric layer (1) and a lower fabric layer (5), with a pearl cotton material layer (3) placed under the upper fabric layer (1) and on the lower fabric layer (5), an upper cotton-like sheet layer (2) placed under the upper fabric layer (1) and on the pearl cotton material layer (3), and a lower cotton-like sheet layer (4) placed under the pearl cotton material layer (3) and on the lower fabric layer (5), and arranged in a face-to-face direction between each adjacent layer.

[0076] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2 The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0077] The sheet of the cotton-like sheet layer is made of 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, which is mixed--arranged--layed on a net--heat melted--cut the edges--wound through the following process at a heat melting temperature of 150°C. The sheet has a density of 60g / m 2 , and 5mm thick. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a fiber length of 60mm, while the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a fiber length of 51mm.

[0078] The thickness of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) is 5 mm, and each is realized by using a single cotton sheet for the cotton-like sheet layer. The pearl cotton of the above-mentioned pearl cotton material layer (3) is a mesh-like pearl cotton. The aforementioned mesh-like pearl cotton is made by crossing strips of pearl cotton with each other and fusing and bonding them together at the crossing points. The mesh of the pearl cotton mentioned above is diamond-shaped. The length L of the long diagonal of the above-mentioned rhombus is 30 mm, and the length W of the short diagonal is 9 mm. The pearl cotton strips described above are circular in cross section. The diameter of the aforementioned circle is 6 mm. The ratio of thickness to cross-sectional diameter of the joint mentioned above is 1.5, and the thickness is 9 mm. Mesh pearl cotton m 2 Weight per unit is 53g / m 2 It is.

[0079] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0080] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0081] 2. Quilting pad performance test The test confirmed the following performance: Quick drying: Drying time is 109 minutes, rated as grade 2. Compression elasticity: The compression elasticity is 88%, rated as grade 2. Flexibility: Indentation hardness is 106 Newtons, rated as grade 2. EXAMPLES

[0082] Please refer to Figures 1 and 3. The quick-drying, highly elastic home textile includes an upper fabric layer (1) and a lower fabric layer (5), in which a pearl cotton material layer (3) is placed under the upper fabric layer (1) and on the lower fabric layer (5), an upper cotton-like sheet layer (2) is placed under the upper fabric layer (1) and on the pearl cotton material layer (3), and a lower cotton-like sheet layer (4) is placed under the pearl cotton material layer (3) and on the lower fabric layer (5), and is arranged in a face-to-face direction between each adjacent layer.

[0083] The upper fabric layer (1) and the lower fabric layer (5) are 85 g / m 2 The Spring Yasin fleece is of the type 75D*150D / 41*28, with the warp yarn of polyester DTY75D / 36F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F and the weft yarn of polyester DTY150D / 288F. Having disclosed the above characteristics of Spring Yasin fleece, the technician can purchase the fabric from the market, or can manufacture it based on the existing technology. For example, the warp yarn is polyester DTY75D / 36F, the weft yarn is polyester DTY150D / 288F, and the fabric is woven by a water jet loom to make a base material, which is then sanded--rinsed--dyed--widened, shaped--wound, and the fabric is manufactured to the specifications of 75D*150D / 41*28 to obtain the above Spring Yasin fleece.

[0084] The sheet of the cotton-like sheet layer is made of 85% (by mass) of normal melting point polyester fiber and 15% (by mass) of low melting point polyester fiber, which is mixed--arranged--layed on a net--heat melted--cut the edges--wound through the following process at a heat melting temperature of 150°C. The sheet has a density of 60g / m 2 , and 5mm thick. Among them, the normal melting point polyester (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 3.33 dtex and a fiber length of 60mm, while the low melting point polyester fiber (supplied by China Petrochemical Yizheng Chemical Fiber Co., Ltd.) has a fineness of 4.44 dtex and a fiber length of 51mm.

[0085] The thickness of the upper cotton-like sheet layer (2) and the lower cotton-like sheet layer (4) is 5 mm, and each is realized by using a single cotton-like sheet for the cotton-like sheet layer. The pearl cotton of the above-mentioned pearl cotton material layer (3) is a mesh-like pearl cotton. The aforementioned mesh-like pearl cotton has pearl cotton strips that cross each other and can be fused and joined together at the crossing points. The mesh of the pearl cotton mentioned above is diamond-shaped. The length L of the long diagonal of the above-mentioned rhombus is 40 mm, and the length W of the short diagonal is 12 mm. Pearl cotton strips are circular in cross section. The diameter of the aforementioned circle is 8 mm. The ratio of thickness to cross-sectional diameter of the aforementioned joint is 1.5, and the thickness is 12 mm. This pearl cotton m 2 Weight per unit is 71g / m 2 It is.

[0086] Each layer is joined by quilting. More specifically, the sewing thread is made of three strands of polyester DTY150D / 12F, the diagonal length of the quilting flower is 2 inches square, and the stitching distance is 9 stitches / 3 cm.

[0087] Then, cut it to a size of 100 cm x 200 cm and wrap it around 110 g / m 2The suede side of the edge wrapping fabric is on the outside, 6.2 cm wide, and the stitching is 9 stitches / 3 cm apart. The finished product is a quilted pad.

[0088] 2. The following performance was confirmed in the quilted pad performance test. Quick drying: Drying time is 103 minutes, rated as grade 2. Compression elasticity: The compression elasticity is 81%, rated as grade 2. Flexibility: Indentation hardness is 124 Newtons, rated as grade 2. [Explanation of symbols]

[0089] 1 Top fabric layer 2 Upper cotton sheet 2a Cotton-like sheet layer 3 Pearl cotton material layer 4 Lower cotton-like sheet layer 5 Bottom fabric layer 6. Border 7. Stitching Thread 8 Cutting lines showing how to draw a cutting equation

Claims

1. The quick-drying, highly elastic fabric comprises an upper fabric layer (1) and a lower fabric layer (5), a pearl cotton material layer (3) is placed under the upper fabric layer (1) and on the lower fabric layer (5), and is disposed in a face-to-face direction between each adjacent layer, an upper cotton-like sheet layer (2) is placed under the upper fabric layer (1) and on the pearl cotton material layer (3), and / or a lower cotton-like sheet layer (4) is placed under the pearl cotton material layer (3) and on the lower fabric layer (5).

2. The quick-drying, highly elastic fabric according to claim 1, wherein the pearl cotton material layer (3) is made of columnar pearl cotton, block pearl cotton, sheet pearl cotton or net pearl cotton.

3. The quick-drying, highly elastic fabric according to claim 2, characterized in that the mesh-like pearl cotton is made by intersecting pearl cotton strips and fusing and bonding them at the intersections, or by meshes distributed on a membrane sheet.

4. 4. The quick-drying, highly elastic fabric according to claim 3, wherein the mesh of the pearl cotton is rhombus-shaped.

5. The long diagonal length of the rhombus is represented as L, the short diagonal length is represented as W, and the ratio of L to W is greater than 1 and less than 100, and / or the value range of L is 5 to 100 mm.

6. The quick-drying, highly elastic fabric described in claim 5, characterized in that the mesh pearl cotton strip has a circular cross section, and / or the ratio of the thickness of the joint part to the cross-sectional diameter is greater than or equal to 1 and less than or equal to 2.

7. The quick-drying, highly elastic fabric according to claim 6, wherein the thickness of the mesh-like pearl cotton is 1 to 100 mm.

8. The quick-drying, highly elastic fabric according to claim 7, characterized in that the upper fabric layer (1) and the lower fabric layer (5) are independently selected from knitted fabric, shuttle fabric, nonwoven fabric, non-spun felt, leather, fur, or synthetic leather, and / or each layer is joined by sewing or compounding.

9. A textile product comprising the quick-drying, highly elastic fabric according to any one of claims 1 to 8, and used for futons, futon mattresses, cushions, pillows, neck pillows, carpets, carpet underlays, quilting pads, Simmons pads, mattresses, dehumidifying pads, moisture absorbing pads, sofas, etc.

10. 10. The spinning article according to claim 9, wherein the sewing method is selected from a lock stitch, a split hem stitch, a backstitch, a hollow stitch, a sandwich stitch, a back stitch, a foldover stitch, a rolled stitch, and a quilting stitch.