High refractive index polysiloxane vinyl crosslinker

Abstract

The present invention provides a class of high RI polysiloxane vinyl crosslinkers. Each polysiloxane vinyl crosslinker of the present invention comprises: (1) a polysiloxane segment comprising a dimethylsiloxane unit and an aryl-containing siloxane unit, each of which has one methyl substituent and one organic substituent, and each of which has at least one aryl moiety bonded to a Si atom via a linker having at least two (preferably three) carbon atoms and up to 45 carbon atoms; and (2) an ethylenically unsaturated group. The present invention also provides an insert or silicone hydrogel contact lens comprising a crosslinked polymeric material comprising at least one repeat unit of such a class of high RI polysiloxane vinyl crosslinkers.

Description

[Technical field]

[0001] The present invention relates to high refractive index (RI) polysiloxane vinyl crosslinkers having one or more aryl-containing siloxane units, each having one methyl substituent and one or more organic substituents having at least one aryl moiety bonded to a Si atom via a flexible linker, and their use in the manufacture of high RI inserts and high RI silicone hydrogel contact lenses. [Background technology]

[0002] Recently, it has been proposed that various inserts can be incorporated into hydrogel contact lenses for a variety of purposes, such as, for example, corneal health, vision correction, diagnostics, etc. (see, e.g., U.S. Pat. Nos. 4,268,132, 4,401,371, 5,098,546, 5,156,726, 6,851,805, 7,490,936, 7,883,207, 8,154,804, 8,215,770, 8,348,424, 8,874,182, 9,176,332, 9,618,773, and 10,203,521). see, for example, U.S. Pat. Appln. Pub. Nos. 20040141150, 20040212779, 2008 / 0208335, 2009 / 0091818, 20090244477, 2010 / 0072643, 2010 / 0076553, 20110157544, 2012 / 0120365, 2012 / 0140167, 2012 / 0234453, 2014 / 0276481, and 2015 / 0145155.

[0003] The insert is typically made from a non-hydrogel material that is a non-water swellable material that cannot absorb water, has low oxygen permeability and a relatively low refractive index. High oxygen permeability of the insert is required to minimize adverse effects on corneal health. A high refractive index would be desirable to provide high optical performance, such as diffractive multifocal optics, in implantable contact lenses. It would be desirable to have an insert made from a material that has high oxygen permeability and a high refractive index. Summary of the Invention [Means for solving the problem]

[0004] In one aspect, the present invention provides a polysiloxane vinyl crosslinker having a high refractive index (RI) and a relatively low glass transition temperature (Tg). The polysiloxane vinyl crosslinker of the present invention comprises a polysiloxane segment comprising a dimethylsiloxane unit and an aryl-containing siloxane unit, the aryl-containing siloxane unit having one methyl substituent and one organic substituent having at least one aryl moiety bonded to the Si atom via a linker having at least two (preferably three) carbon atoms, and an ethylenically unsaturated group.

[0005] In another aspect, the present invention provides inserts made from crosslinked polymeric materials that include repeat units of the high RI polysiloxane vinyl crosslinker of the present invention.

[0006] In a further aspect, the present invention provides a silicone hydrogel contact lens comprising a silicone hydrogel bulk material that includes repeat units of the high RI polysiloxane vinyl crosslinker of the present invention.

[0007] In yet another aspect, the present invention provides an implantable silicone hydrogel contact lens comprising a silicone hydrogel bulk material and an insert made from a crosslinked polymeric material comprising units of the high RI polysiloxane vinyl crosslinker of the present invention (described above), the insert being embedded within the silicone hydrogel bulk material.

[0008] The present invention provides the foregoing and other features, the advantages of which will become more apparent from the following detailed description of the preferred embodiments, read in conjunction with the accompanying drawings. The detailed description and drawings are merely illustrative of the invention and are not intended to limit the scope of the invention, as defined by the appended claims and equivalents thereof. [Brief description of the drawings]

[0009] [Figure 1] 1 is a differential scanning calorimetry (DSC) diagram obtained for a high RI polysiloxane vinyl crosslinker of the present invention by using DSC. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by those skilled in the art to which this invention belongs. In general, the nomenclature and experimental procedures used herein are well known and commonly used in the art. Conventional methods are used for these procedures, such as those provided in the art and various general references. Where a term is given in the singular form, the inventors also contemplate the plural form of that term. The nomenclature used herein and the experimental procedures described below are well known and commonly used in the art.

[0011] "About" as used herein in this application means that a number referred to as "about" includes the recited number plus or minus 1-10% of the recited number.

[0012] "Contact lens" refers to a structure that can be placed on or in the eye of a wearer. A contact lens can, but need not, correct, improve, or alter the vision of the user.

[0013] "Silicone hydrogel contact lens" refers to a contact lens that includes a silicone hydrogel material as a bulk material (ie, a silicone hydrogel bulk material).

[0014] "Hydrogel" or "hydrogel material" refers to a crosslinked polymeric material that has a three-dimensional polymer network (i.e., a polymer matrix) and is insoluble in water but can retain at least 10% by weight of water within its polymeric matrix when fully hydrated (or in equilibrium).

[0015] "Silicone hydrogel" or "SiHy" interchangeably refers to a silicone-containing hydrogel comprising repeat units of at least one silicone-containing monomer and / or silicone-containing vinyl crosslinker and repeat units of at least one hydrophilic vinyl monomer, which is typically formed by copolymerization of a polymerizable composition comprising at least one silicone-containing monomer and / or silicone-containing vinyl crosslinker and at least one hydrophilic vinyl monomer.

[0016] As used in this application, the term "non-silicone hydrogel" refers to a hydrogel that does not theoretically contain silicon.

[0017] "Implantable silicone hydrogel contact lens" refers to a silicone hydrogel contact lens that includes at least one insert made from a non-hydrogel material and embedded within a silicone hydrogel material as the primary lens material of the contact lens.

[0018] "Insert" refers to any three-dimensional article made from a non-hydrogel material and having a dimension of at least 5 microns, but smaller enough to be embedded in a silicone hydrogel contact lens. In accordance with the present invention, the non-hydrogel material can be any material that can absorb less than 5% by weight of water when fully hydrated (preferably about 4% by weight or less, more preferably about 3% by weight or less, and even more preferably about 2% by weight or less).

[0019] According to the present invention, the insert of the present invention has a thickness less than any thickness of the implantable silicone hydrogel contact lens in the area where the insert is embedded. The insert can have any geometric shape and any desired function. Examples of preferred inserts include, but are not limited to, thin rigid disks with curved surfaces to provide a rigid center optic for masking astigmatism, such as rigid gas permeable (RGP) contact lenses, multifocal lens inserts, photochromic inserts, cosmetic inserts with color patterns printed thereon, and the like.

[0020] "Hydrophilic," as used herein, describes a material or portion thereof that will more readily associate with water than with lipids.

[0021] "Vinyl monomer" refers to a compound that has one and only one ethylenically unsaturated group, is soluble in a solvent, and can be polymerized actinically or thermally.

[0022] The term "soluble," in reference to a compound or material in a solvent, means that the compound or material can be dissolved in the solvent at room temperature (i.e., a temperature of about 21° C. to about 27° C.) to provide a solution having a concentration of at least about 0.5% by weight.

[0023] The term "insoluble," in reference to a compound or material in a solvent, means that the compound or material can be dissolved in the solvent at room temperature (as defined above) to provide a solution with a concentration of less than about 0.01% by weight.

[0024] The term "ethylenically unsaturated group" is used broadly herein and is intended to encompass any group that contains at least one >C=C< group. Exemplary ethylenically unsaturated groups include, without limitation, (meth)acryloyl. [ka] , vinyloxycarbonylamino ( [ka] In the formula, R o is H or C1-C4 alkyl), vinyloxycarbonyloxy [ka] , vinylaminocarbonylamino( [ka] In the formula, R o is H or C1-C4 alkyl), vinylaminocarbonyloxy [ka] , allyl, vinyl, styrenyl [ka] or other C=C containing groups.

[0025] As used herein, "actinally" in reference to curing, crosslinking or polymerization of a polymerizable composition, prepolymer or material means that the curing (e.g., crosslinking and / or polymerization) is effected by actinic radiation, such as, for example, UV radiation, ionizing radiation (e.g., gamma or X-ray radiation), microwave radiation, etc. Thermal curing or actinic curing methods are well known to those skilled in the art.

[0026] "Acrylic monomer" refers to a vinyl monomer having one and only one (meth)acryloyl group. Examples of acrylic monomers include (meth)acryloxy [or (meth)acryloyloxy] monomers and (meth)acrylamide monomers.

[0027] "(Meth)acryloxy monomer" or "(meth)acryloyloxy monomer" refers to one and only one [ka] It refers to a vinyl monomer having the group:

[0028] "(Meth)acrylamide monomer" is [ka] (In the formula, R o is H or C1-C4 alkyl It refers to a vinyl monomer having one and only one group.

[0029] The term "(meth)acrylamide" refers to methacrylamide and / or acrylamide.

[0030] The term "(meth)acrylate" refers to methacrylate and / or acrylate.

[0031] "N-vinyl amide monomer" refers to an amide compound having a vinyl group (-CH=CH2) attached directly to the nitrogen atom of the amide group.

[0032] The term "ene group" refers to a monovalent radical of CH2=CH- or CH2=CCH3- that is not covalently bonded to an oxygen or nitrogen atom, or a carbonyl group.

[0033] "Ene monomer" refers to a vinyl monomer having one and only one ene group.

[0034] "Hydrophilic vinyl monomer" refers to a vinyl monomer that typically gives rise to a homopolymer that is water soluble or capable of absorbing at least 10 weight percent water.

[0035] "Hydrophobic vinyl monomer" refers to a vinyl monomer that typically results in a homopolymer that is insoluble in water and capable of absorbing less than 10% water by weight.

[0036] As used in this application, the term "vinyl crosslinker" refers to an organic compound having at least two ethylenically unsaturated groups. "Vinyl crosslinker" refers to a vinyl crosslinker having a molecular weight of 700 Daltons or less.

[0037] Siloxane, often also referred to as silicone, refers to a molecule having at least one moiety of -Si-O-Si- in which each Si atom has two organic groups as substituents.

[0038] "Silicone-containing vinyl monomer or crosslinker" or "siloxane-containing vinyl monomer or crosslinker" refer, interchangeably, to a vinyl monomer or crosslinker having at least one moiety of -Si-O-Si-, where each Si atom has at least two substituents (organic groups).

[0039] "Polysiloxane segment" or "polydiorganosiloxane segment" means the same thing. [ka] where SN is an integer equal to or greater than 3, and R S1 and R S2 Each of C1 to C 10 Alkyl;Phenyl;C1-C4 alkyl substituted phenyl;C1-C4 alkoxy substituted phenyl;Phenyl-C1-C6 alkyl;C1-C 10 Fluoroalkyl; C1-C 10 Fluoroether;Aryl;Aryl C1-C 18 Alkyl; -alk-(OC2H4) γ1 -OR o (wherein alk is a C1-C6 alkylene diradical, R o is H or a C1-C4 alkyl group, and γ1 is an integer from 1 to 10; a hydroxyl group (-OH), a carboxyl group (-COOH), an amino group (-NR N1 R N1 '), -NR N1 -amino bond, -CONR N1 -amide bond, -CONR N1 R N1 C2-C alkoxy group having at least one functional group selected from the group consisting of an amide of -OCONH-, a urethane bond of -OCONH-, and a C1-C4 alkoxy group. 40 an organic radical, or a linear hydrophilic polymer chain, where R N1 and R N1 ' are each independently hydrogen or C1-C 15 alkyl; and organic radicals having up to 45 carbon atoms.

[0040] "Polydiorganosiloxane vinyl crosslinker" or "polysiloxane vinyl crosslinker" refer interchangeably to a compound that contains at least one polysiloxane segment and at least two ethylenically unsaturated groups.

[0041] The term "fluid" as used herein indicates that the material is capable of flowing like a liquid.

[0042] As used in this application, the term "transparent" in relation to a polymerizable composition means that the polymerizable composition is a transparent solution or liquid mixture having a light transmittance of 85% or more (preferably 90% or more) in the range of 400 to 700 nm.

[0043] As used in this application, the term "polymer" means a material formed by polymerizing / crosslinking one or more monomers or macromers or prepolymers or combinations thereof.

[0044] "Macromer" or "prepolymer" refers to a compound or polymer that contains ethylenically unsaturated groups and has a number average molecular weight greater than 700 Daltons.

[0045] As used in this application, the term "molecular weight" of a polymeric material (including monomeric or macromeric materials) refers to number average molecular weight unless otherwise specified or unless the test conditions indicate otherwise. Those skilled in the art will appreciate that molecular weight can be determined by known methods, such as GPC (gel permeation chromatography) with one or more of a refractive index detector, a low angle laser light scattering detector, a multi-angle laser light scattering detector, a differential viscometry detector, a UV detector, and an infrared (IR) detector; MALDI-TOF MS (matrix-assisted laser desorption / ionization time-of-flight mass spectrometry); 1 Know how to determine the molecular weight of polymers according to H NMR (proton nuclear magnetic resonance) spectroscopy etc.

[0046] The term "monovalent radical" refers to an organic radical obtained by removing a hydrogen atom from an organic compound and forming one bond with one other group in the organic compound. Examples include, without limitation, alkyl (by removing a hydrogen atom from an alkane), alkoxy (or alkoxyl) (by removing one hydrogen atom from the hydroxyl group of an alkyl alcohol), thiyl (by removing one hydrogen atom from the thiol group of an alkylthiol), cycloalkyl (by removing a hydrogen atom from a cycloalkane), cycloheteroalkyl (by removing a hydrogen atom from a cycloheteroalkane), aryl (by removing a hydrogen atom from the aromatic ring of an aromatic hydrocarbon), heteroaryl (by removing a hydrogen atom from any ring atom), amino (by removing one hydrogen atom from an amine), and the like.

[0047] The term "divalent radical" refers to an organic radical that is obtained by removing two hydrogen atoms from an organic compound and that forms two bonds with two other groups in the organic compound. For example, an alkylene divalent radical (i.e., alkylenyl) is obtained by removing two hydrogen atoms from an alkane, and a cycloalkylene divalent radical (i.e., cycloalkylenyl) is obtained by removing two hydrogen atoms from a cyclic ring.

[0048] In this application, the term "substituted" in connection with an alkyl or alkylenyl means that the alkyl or alkylenyl replaces one hydrogen atom of the alkyl or alkylenyl and contains at least one substituent selected from the group consisting of hydroxyl (-OH), carboxyl (-COOH), -NH, sulfhydryl (-SH), C1-C4 alkyl, C1-C4 alkoxy, C1-C4 alkylthio (alkylsulfido), C1-C4 acylamino, C1-C4 alkylamino, di-C1-C4 alkylamino, and combinations thereof.

[0049] The term "terminal ethylenically unsaturated group", as known to those skilled in the art, refers to an ethylenically unsaturated group at one of the two ends of the main chain (or backbone) of an organic compound.

[0050] "Blending vinyl monomer" refers to a vinyl monomer that is capable of dissolving both the hydrophilic and hydrophobic components of the polymerizable composition to form a solution.

[0051] A free radical initiator can be either a photoinitiator or a thermal initiator. A "photoinitiator" refers to a chemical that initiates a free radical crosslinking / polymerization reaction with the use of light. A "thermal initiator" refers to a chemical that initiates a radical crosslinking / polymerization reaction with the use of thermal energy.

[0052] In the context of silicone hydrogel bulk materials or SiHy contact lenses, "post-cure surface treatment" refers to a surface treatment process that occurs after the silicone hydrogel bulk materials or SiHy contact lenses have been formed by curing (i.e., thermally or actinically polymerizing) the SiHy lens formulation.

[0053] The terms "silicone hydrogel lens formulation" or "SiHy lens formulation", interchangeably, refer to a polymerizable composition that contains all the necessary polymerizable components to produce a silicone hydrogel (SiHy) contact lens or SiHy lens bulk material, as is well known to those skilled in the art.

[0054] In general, the present invention relates to a class of high RI polysiloxane vinyl crosslinkers comprising: (1) polysiloxane segments comprising dimethylsiloxane units and aryl-containing siloxane units, each of which has one methyl substituent and one organic substituent, each of which has at least one aryl moiety bonded to a Si atom via a linker having at least two (preferably three) carbon atoms and up to 45 carbon atoms; and (2) ethylenically unsaturated groups.

[0055] There are several potentially unique features associated with the use of the high RI polysiloxane vinyl crosslinkers of the present invention in the production of inserts or SiHy contact lenses having relatively high RI (refractive index).

[0056] First, the high RI polysiloxane vinyl crosslinker of the present invention is useful for producing inserts or SiHy contact lenses with a high refractive index (RI 1.50) and relatively high oxygen permeability. Typically, polydimethylsiloxanes have RI values ​​of 1.38 to 1.42. Although such polydimethylsiloxanes can be used to produce inserts or SiHy contact lenses with relatively high oxygen permeability, they would not be suitable for producing inserts or SiHy contact lenses with high RI. In contrast, the high RI polysiloxane vinyl crosslinker of the present invention not only contains aryl moieties that impart a high RI, but also contains dimethylsiloxane units that impart relatively high oxygen permeability to the resulting insert or SiHy contact lens. Inserts with high RI and high oxygen permeability can be used to produce implantable diffractive multifocal silicone hydrogel contact lenses. High RI SiHy contact lenses can be thinned to have high oxygen permeability.

[0057] Second, in the high RI polysiloxane vinyl crosslinker of the present invention, each aryl moiety is not directly bonded to the Si atom of the siloxane unit, but is instead bonded to the Si atom via a flexible linker. With such a flexible linker, the aryl moiety can move more easily, and the high refractive index polysiloxane vinyl crosslinker of the present invention can have a relatively low glass transition temperature (Tg). The insert or lens made from the high Tg polysiloxane may be more brittle and more prone to cracking.

[0058] In one aspect, the present invention provides a high RI polysiloxane vinyl crosslinker. The high RI polysiloxane vinyl crosslinker of the present invention comprises: (1) a polysiloxane segment comprising a dimethylsiloxane unit and an aryl-containing siloxane unit, each of which has one methyl substituent and one organic substituent, and each of which has at least one aryl moiety bonded to a Si atom via a linker having at least two (preferably three) carbon atoms and up to 45 carbon atoms; and (2) an ethylenically unsaturated group, preferably a (meth)acryloyl group. The high RI polysiloxane vinyl crosslinker of the present invention has an RI of at least 1.48 (preferably at least 1.51, more preferably at least 1.54, even more preferably 1.57) and a T of about 0° C. or less (preferably about −5.0° C. or less, more preferably about −10.0° C. or less, even more preferably about −20.0° C. or less). g has.

[0059] In a preferred embodiment, the polysiloxane segments comprise at least 30 mol % (preferably at least 40 mol %, more preferably at least 50 mol %, even more preferably at least 60 mol %, and especially preferably at least 70 mol %) of aryl-containing siloxane units.

[0060] In another preferred embodiment, the high RI polysiloxane vinyl crosslinker of the present invention can have a number average molecular weight of at least 1000 Daltons (preferably 1500 Daltons to 100,000 Daltons, more preferably 2000 to 80,000 Daltons, and even more preferably 2500 to 60,000 Daltons).

[0061] According to the present invention, the high RI polysiloxane vinyl crosslinker is preferably defined by formula (1): [ka] (In the formula: υ1 is an integer of 1 to 400 (preferably 3 to 350, more preferably 5 to 300, and even more preferably 10 to 250); ω1 is an integer of 1 to 800 (preferably 5 to 700, more preferably 10 to 600, and even more preferably 15 to 500); E1 is [ka] is a monovalent radical of; R0 is hydrogen or methyl; a1 is zero or 1; X0 is O or NR N1 and; R N1 is hydrogen or C1-C6 alkyl; L0 is a C2-C8 alkylene divalent radical or -L O '-X1-L0'-, [ka] is a divalent radical of; L0' is a C2-C8 alkylene divalent radical; L0″ is a C3-C8 alkylene divalent radical; X1 is -O-, -NR N1 -, -NHCOO-, -OCONH-, -CONR N1 - or -NR N1 CO-; q1 is an integer from 1 to 10; AR is an aryl radical; L AR teeth, [ka] is a divalent radical of; L e -CH2-CH2-, -CH2-CHR O -R1-, -CH2-CHR O -R1-O-, -CH2-CHR O-R1-O-R2-, -C3H6-O-R2-, -C3H6-O-R2-O-, [ka] is a divalent radical of; a2 is zero, 1 or 2; a3 is zero or 1; R1 is a linear or branched C1-C alkoxy group, a hydroxyl group, a carboxyl group, an amino group, an oxo group, or a combination thereof, which may be optionally substituted with a C1-C4 alkoxy group, a hydroxyl group, a carboxyl group, an amino group, an oxo group, or a combination thereof. 10 is an alkylene divalent radical; R2 is a linear or branched C1-C 10 is an alkylene divalent radical; R3 is a direct bond or a linear or branched C1-C4 alkylene divalent radical; X AR and each X2, independently of the others, is a covalent bond, a linear or branched C1-C4 alkylene divalent radical, or -O-, -S-, [ka] , -NR N2 -, -NHCOO-, -OCONH-, -NHCONR N2 -, -NR N2 CONH-, [ka] , -CONR N2 -, -NR N2 CO-, [ka] -NHCOS-, -SCONH-, -COO-, or -OCO- covalent bond; R N2is hydrogen, linear or branched C1-C6 alkyl, cyclohexyl, cyclopentyl, substituted or unsubstituted phenyl, or substituted or unsubstituted phenyl-C1-C6 alkyl, Each L x are each independently a linear or branched C1-C alkyl group which may optionally have one or more hydroxyl, C1-C4 alkoxy or C1-C4 acylamino groups; 10 an alkylene divalent radical, -CH-CHCH-CH-O-R-O-CH-CHCH-CH-; [ka] or a divalent radical obtained by removing two hydrogen atoms from two different atoms of a hydrocarbon having up to 20 carbon atoms, optionally bearing one or more hydroxyl or C1-C4-alkoxy groups, and comprising at least one divalent radical selected from the group consisting of a cycloalkylene radical, a substituted cycloalkylene radical, a phenylene radical, a substituted phenylene radical, a cycloheteroalkylene radical, and a substituted cycloheteroalkylene radical, Each R, R, and R is independently a linear or branched C1-C aryl group having zero or one hydroxyl group. 10 (an alkylene divalent radical).

[0062] In a preferred embodiment, in formula (1), a1 is zero, and then E1 is [ka] is a monovalent radical.

[0063] In another preferred embodiment, ω1 / (υ1+ω1) is about 0.30 to about 0.95 (preferably about 0.40 to about 0.90, more preferably about 0.50 to about 0.90, and even more preferably about 0.60 to about 0.85).

[0064] In another preferred embodiment, AR is a phenyl group, a substituted phenyl group, a naphthyl group, a substituted naphthyl group, anthracenyl group, a substituted anthracenyl group, a phenanthryl group, or a substituted phenanthryl group.

[0065] In another preferred embodiment, AR is [ka] is a monovalent radical of In the formula, R7, R8, R9, R 10 , R 11 , R 12 , and R 13 are each independently H, Cl, Br, F, CF3, CCl3, C1-C5 alkyl, C1-C5 alkoxy, C2-C5 acyloxy, OH, phenyl, phenoxy, benzyloxy, phenylcarbonyl, phenoxycarbonyl, phenylcarboxy (phenylcarbonyloxy), or naphthyl.

[0066] The polysiloxane vinyl crosslinker of formula (1) can be prepared in a two-step process or a three-step process.

[0067] According to the two-stage process, in the first stage, the hydrosiloxane-containing polysiloxane of formula (2) is obtained according to known procedures. [ka] (wherein E1, υ1, and ω1 are as defined above for formula (1)).

[0068] According to a two-step process, the hydrosiloxane-containing polysiloxane of formula (2) can be prepared from the polymerization of a mixture of octamethylcyclotetrasiloxane (D4) and 1,3,5,7-tetramethylcyclotetrasiloxane (H4) in the presence of a catalyst and in the presence of a 1,3-bis(E1 group) terminated tetramethyldisiloxane (e.g., 1,3-bis[3-(meth)acryloxypropyl]tetramethyldisiloxane, 1,3-bis[3-(meth)acrylamidopropyl]tetramethyldisiloxane, etc.) as a chain end block. By controlling the molar ratio of D4 to H4, the desired value of υ1 / ω1 can be obtained. It is understood that the 1,3-bis(E1 group) terminated tetramethyldisiloxane can be prepared from a 1,3-bis(hydroxyalkyl)tetramethyldisiloxane (e.g., 1,3-bis(hydroxypropyl)tetramethyldisiloxane) or a 1,3-bis(aminoalkyl)tetramethyldisiloxane (e.g., 1,3-bis(aminopropyl)tetramethyldisiloxane), for example, by reacting one of these with (meth)acryloyl chloride or vinyl isocyanate (or isopropenyl isocyanate).

[0069] In the second step of the two-step process, the hydrosiloxane-containing polysiloxane of formula (2) can be reacted with an aryl-containing ene monomer (i.e., an ene monomer containing a phenyl group, a substituted phenyl group, a naphthyl group, or a substituted naphthyl group) in a platinum-catalyzed hydrosilylation reaction known to those skilled in the art to form the polysiloxane vinyl crosslinker of formula (1).

[0070] Any aryl-containing ene monomer can be used in preparing the polysiloxane vinyl crosslinker of formula (1), so long as the aryl-containing ene monomer contains a phenyl group, a substituted phenyl group, a naphthyl group, a substituted naphthyl group, an anthracenyl group, a substituted anthracenyl group, a phenanthryl group, or a substituted phenanthryl group. Examples of such aryl-containing ene monomers include, but are not limited to, vinyl naphthalene, vinyl anthracene, vinyl phenanthrene, vinyl pyrene, vinyl biphenyl, vinyl terphenyl, vinyl phenyl naphthalene, vinyl phenyl anthracene, vinyl phenyl phenanthrene, vinyl phenyl pyrene, vinyl phenyl terphenyl, phenoxystyrene, phenyl carbonyl styrene, phenyl carboxy styrene, phenoxy carbonyl styrene, allyl naphthalene, allyl anthracene, allyl phenanthrene, allyl pyrene, allyl biphenyl, allyl terphenyl, allyl phenyl naphthalene, allyl phenyl anthracene, allyl phenyl phenanthrene, allyl phenyl pyrene, allyl phenyl terphenyl, allyl phenoxy benzene, allyl (phenyl carbonyl) benzene, allyl phenoxy benzene, allyl (phenyl carbonyl) benzene, allyl (phenyl carboxy) benzene, allyl phenyl ether, allyl benzyl ether, and allyl (phenoxy carbonyl) benzene.

[0071] Various aryl-containing ene monomers can be obtained from commercial sources or prepared according to known methods. Examples of preferred aryl-containing ene monomers include, but are not limited to, styrene, 2,5-dimethylstyrene, 2-(trifluoromethyl)styrene, 2-chlorostyrene, 3,4-dimethoxystyrene, 3-chlorostyrene, 3-bromostyrene, 3-vinylanisole, 3-methylstyrene, 4-bromostyrene, 4-tert-butylstyrene, 2,3,4,5,6-pentanefluorostyrene, 2,4-dimethylstyrene, 1-methoxy-4-vinylbenzene, 1-chloro-4-vinylbenzene, 1-Methyl-4-vinylbenzene, 1-(chloromethyl)-4-vinylbenzene, 1-(bromomethyl)-4-vinylbenzene, 3-nitrostyrene, 1,2-vinylphenylbenzene, 1,3-vinylphenylbenzene, 1,4-vinylphenylbenzene, 4-vinyl-1,1'-(4'-phenyl)biphenylene, 1-vinyl-4-(phenyloxy)benzene, 1-vinyl-3-(phenyloxy)benzene, 1-vinyl-2-(phenyloxy)benzene, 1-vinyl-4-(phenylcarbonyl (phenyl)benzene, 1-vinyl-3-(phenylcarboxy)benzene, 1-vinyl-2-(phenoxycarbonyl)benzene, allyl phenyl ether, allyl benzyl ether, 2-biphenylyl allyl ether, allyl 4-phenoxyphenyl ether, allyl 2,4,6-tribromophenyl ether, allyl phenyl carbonate, 1-allyloxy-2-trifluoromethylbenzene, allylbenzene, 1-phenyl-2-prop-2-enylbenzene, 4-phenyl-1-butene, 4-phenyl Allyl-1-buten-4-ol, 1-(4-methylphenyl)-3-buten-1-ol, 1-(4-chlorophenyl)-3-buten-1-ol, 4-allyltoluene, 1-allyl-4-fluorobenzene, 1-allyl-2-methylbenzene, 1-allyl-3-methylbenzene, 1-allyl-3-methylbenzene, 2-allylanisole, 4-allylanisole, 1-allyl-4-(trifluoromethyl)benzene, allylpentafluorobenzene, 1-allyl-2-methoxybenzene, 4-allyl-1,2-Dimethoxybenzene, 2-Allylphenol, 2-Allyl-6-methylphenol, 4-Allyl-2-methoxyphenol, 2-Allyloxyanisole, 4-Allyl-2-methoxyphenylacetate, 2-Allyl-6-methoxyphenol, 1-Allyl-2-bromobenzene, α-Vinylbenzyl alcohol, 1-Phenyl-3-buten-1-one, Allylbenzyl ether, (3-Allyloxy)propyl)benzene, Allylphenylethyl ether, 1-Benzyloxy-4-pentene, (1-Allyloxy)ethyl)benzene, 1-Phenylallylethyl ether, (2-Methyl-2-(2-propenyloxy)propyl)benzene, ((5-hexenyloxy)methyl)benzene, 1-Allyloxy-4-propoxy Benzene, 1-phenoxy-4-(3-prop-2-enoxypropoxy)benzene, 6-(4'-hydroxyphenoxy)-1-hexene, 4-but-3-enoxyphenol, 1-allyloxy-4-butoxybenzene, 1-allyloxy-4-ethoxybenzene, 1-allyl-4-benzyloxybenzene, 1-allyl-4-(phenoxy)benzene, 1-allyl-3-(phenoxy)benzene, 1-allyl-2-(phenoxy))benzene, 1-allyl-4-(phenylcarbonyl)benzene, 1-allyl-3-(phenylcarboxy)benzene, 1-allyl-2-(phenoxycarbonyl)benzene, 1,2-allylphenylbenzene, 1,3-allylphenylbenzene, 1,4-allylphenylbenzene, 4-vinyl-1,1'-(4'-phenyl)biphenylene, 1-allyl-4-(phenyloxy)benzene, 1-allyl-3-(phenyloxy)benzene, 1-allyl-2-(phenyloxy)benzene, 1-allyl-4-(phenylcarbonyl)benzene, 1-allyl-3-(phenylcarboxy)benzene, and 1-allyl-2-(phenoxycarbonyl)benzene, 1-vinylnaphthylene, 2-vinylnaphthylene, 1-allylnaphthalene, 2-allylnaphthalene, allyl-2-naphthyl ether, 2-(2-methylprop-2-ene), nyl)naphthalene, 2-prop-2-enylnaphthalene, 4-(2-naphthyl)-1-butene, 1-(3-butenyl)naphthalene, 1-allylnaphthalene, 2-allylnaphthalene, 1-allyl-4-naphthylnaphthalene, 2-(allyloxy)-1-bromonaphthalene, 2-bromo-6-allyloxynaphthalene, 1,2-vinyl(1-naphthyl)benzene, 1,2-vinyl(2-naphthyl)benzene, 1,3-vinyl(1-naphthyl)benzene, 1,3-vinyl(2-naphthyl)benzene, 1,4-vinyl(1-naphthyl) )benzene, 1,4-vinyl(2-naphthyl)benzene, 1-naphthyl-4-vinylnaphthalene, 1-allylnaphthalene, 2-allylnaphthalene, 1,2-allyl(1-naphthyl)benzene, 1,2-allyl(2-naphthyl)benzene, 1,3-allyl(1-naphthyl)benzene, 1,3-allyl(2-naphthyl)benzene, 1,4-allyl(1-naphthyl)benzene, 1,4-allyl(2-naphthyl)benzene, 1-allyl-4-naphthylnaphthalene, 1-vinylanthracene, 2-vinylanthracene, 9-vinylanthracene Allyl anthracene, 1-allylanthracene, 2-allylanthracene, 9-allylanthracene, 9-pent-4-enylanthracene, 9-allyl-1,2,3,4-tetrachloroanthracene, 1-vinylphenanthrene, 2-vinylphenanthrene, 3-vinylphenanthrene, 4-vinylphenanthrene, 9-vinylphenanthrene, 1-allylphenanthrene, 2-allylphenanthrene, 3-allylphenanthrene, 4-allylphenanthrene, 9-allylphenanthrene, and combinations thereof.

[0072] According to a three-step process, the hydrosiloxane-containing polysiloxane of formula (2) described above can be prepared by following the procedure above.

[0073] In the second step of the three-step process, the hydrosiloxane-containing polysiloxane of formula (2) is reacted with a first reactive functional group (E e ) to form a polysiloxane vinyl crosslinker having pendant reactive functional groups represented by formula (3): [ka] (Wherein, E1, υ1, ω1, and L e is as defined above for equation (1), and E e -COOH, -NHR N2 , [ka] , -NCO, -OH, -SH, -CHO, epoxy group [ka] , and aziridinyl [ka] groups).

[0074] To prepare the polysiloxane vinyl crosslinker of formula (3), the ene monomer must have a reactive functional group (-COOH, -NHR N2 , [ka] , -NCO, -OH, -SH, -CHO, [ka] Any ene monomer can be used so long as it contains a reactive functional group. Various ene monomers having reactive functional groups are available from commercial sources or can be prepared according to known methods.

[0075] Examples of commercially available carboxyl-containing ene monomers include, but are not limited to, 3-butenoic acid, 4-pentenoic acid, 5-hexenoic acid, and 6-heptenoic acid, 2,2-dimethyl-4-pentanoic acid, 2-methyl-4-pentanoic acid, 2-propyl-4-pentanoic acid, 3-methyl-4-pentanoic acid, 4-vinylcyclohexanecarboxylic acid, 2-[4-(4-pentenyl)cyclohexyl]acetic acid, 4-propenylcyclohexanecarboxylic acid, and the like. Examples of such benzoic acids include benzoic acid, 3-[2-(2-pentyl)cyclohexyl]propanoic acid, 2-(4-ethienylcyclohexyl)acetic acid, 4-[4-(2-propenyl)cyclohexyl]butanoic acid, 2-ethenylcyclohexabe-1-carboxylic acid, 2-, 3-, or 4-vinylbenzoic acid, 4-(2-propenyl)benzoic acid, 2-allylbenzoic acid, (4-vinylphenyl)acetic acid, and 2-methyl-2-(4-vinylphenyl)propanoic acid.

[0076] Examples of commercially available ene monomers having primary or secondary amino groups include, but are not limited to, allylamine, 3-butenylamine, 4-pentenylamine, 1,1-dimethylallylamine, 1-methyl-4-pentenylamine, 5-hexenylamine, 5-heptenylamine, 6-heptenylamine, N-ethyl-2-methylallylamine, N-ethylallylamine, N-allylmethylamine, N-allyl-1-pentanamine, N-allyl-2-methyl-1-pentanamine, N-allyl-2,3-dimethyl-1-pentanamine, N-allyl-1-hexaneamine, N-allyl-2-methyl-1-hexaneamine, N-allyl-1-octanamine, N N-allyl-1-ecanamine, N-allyl-1-dodecanamine, N-allyl-1-heptanamine, N-allyl-ethylenediamine, N-allyl-cyclo-hexaneamine, N-3-butenylcyclohexaneamine, N-4-pentenylcyclohexanamine, N-5-hexenylcyclohexanamine, 1-amino-4-vinyl-cyclohexane, 1-allyl-2,5-dimethylpiperazine, 1-allyl-piperazine, 4-vinylaniline, N-allylaniline, N-allyl-benzylamine, N-allyl-α-methylbenzylaniline, 4-vinylpiperidine, 3-vinylpiperidine, 2-allylpyrrolidine, 3-vinylpyrrolidine, and the like.

[0077] Examples of commercially available ene monomers having an isocyanate group include, but are not limited to, allyl isocyanate, 4-isocyanate-1-butene, 3-isocyanate-2-methylpropene, 3-isocyanate-1-butene, 3-isocyanate-3-methyl-1-butene, 3-isocyanate-2,3-dimethyl-1-butene, 4-isocyanate-2-methyl-1-butene, 4-isocyanate-3,3-dimethyl-1-butene, 3-isocyanate-3-methyl-1-pentene, 4-isocyanate-4-methyl-1-pentene, 5-isocyanate-1-pentene, 3-isocyanate-1-hexene, 3-isocyanate-5,5-dimethyl-1-hexene, 1-isocyanate-2-heptene, and the like.

[0078] Examples of commercially available hydroxyl-containing ene monomers include, but are not limited to, allyl alcohol, 2-methyl-2-propen-1-ol, 3-buten-1-ol, 3-buten-2-ol, 3-methyl-3-buten-1-ol, 2-methyl-3-buten-2-ol, 2-methyl-3-buten-1-ol, 1-penten-3-ol, 4-penten-1-ol, 4-penten-2-ol, 1-hexen-3-ol, 5-hexen-1-ol, 5-hexen-2-ol, 3-methyl-1-hexen-3-ol, 5-methyl-1-hexen-3-chol, 1-hepten-3-ol, allyloxyethanol, di(ethylene glycol) monoamines, aryloxyethanol ... Examples of such an allyl ether include allyl ether, poly(ethylene glycol) monoallyl ether, poly(propylene glycol) monoallyl ether, allyloxypropanol, 1-allyloxy-2-propanol, 4-allyloxy-1-butanol, 1-vinylcyclohexanol, 2-vinylcyclohexanol, 4-vinylcyclohexanol, 1-allylcyclohexanol, 2-allylcyclohexanol, 4-allylcyclohexanol, 4-vinylphenol, (4-vinylphenyl)methanol, (4-vinylphenyl)ethanol, 3-(4-vinylphenyl)-1-propanol, and 1-(4-vinylphenyl)-2-methyl-2-propanol.

[0079] Examples of commercially available thiol-containing ene monomers include, but are not limited to, allyl mercaptan, 3-butene-1-thiol, 3-methyl-3-butene-1-thiol, 2-methyl-3-butene-1-thiol, 2-methyl-3-butene-2-thiol, 4-pentene-1-thiol, and the like.

[0080] Examples of commercially available ene monomers having aldehyde groups include, but are not limited to, 3-butenal, 4-pentanal, 5-hexenal, 2,2-dimethyl-4-pentenal, 2-methyl-4-pentenal, and the like.

[0081] Examples of commercially available epoxy-containing ene monomers include, but are not limited to, 3,4-epoxy-1-butene, 2-methyl-2-vinyloxirane, 3,4-epoxy-1-pentene, 4,5-epoxy-1-pentene, 1,2-epoxy-5-hexene, 1,2-epoxy-6-heptene, 1,2-epoxy-7-octene, 1,2-epoxy-8-nonene, 1,2-epoxy-9-decene, allyloxy glycidyl ether, and 2-methyl-2-vinyloxirane, 4-vinyl-1-cyclohexene-1,2-epoxide, and the like.

[0082] Examples of commercially available ene monomers having aziridinyl groups include, but are not limited to, 2-vinylaziridine, 1-ariaziridine, N-allyl-2-methylaziridine, and the like.

[0083] In the present invention, all of the commercially available ene monomers mentioned above can be used. Alternatively, ene monomers having reactive functional groups can be prepared by reacting a compound having two ene groups with a mercaptan having a reactive functional group (e.g., hydroxyl, primary amino, secondary amino, carboxyl or ketone group) based on the thiol-ene "click" reaction known in the art.

[0084] In the third step, a polysiloxane vinyl crosslinker of formula (3) is reacted with a polysiloxane vinyl crosslinker (-COOH, -NHR) under well-known coupling reaction conditions in the absence or presence of a coupling agent (i.e., one having two of the reactive functional groups listed above). N2 , [ka] , -NCO, -OH, -SH, -CHO, [ka] ) to form a high RI polysiloxane vinyl crosslinker of formula (1).

[0085] Non-limiting examples of coupling reactions between pairs of compatible co-reactive functional groups, preferably selected from the group consisting of primary, secondary amino, hydroxyl, carboxyl, anhydride, aldehyde, isocyanate, epoxy, aziridine, azlactone and thiol groups, under various reaction conditions are given below for illustrative purposes: the primary / secondary amino group reacts with an aldehyde or ketone group to form a Schiff base which can be further reduced to an amine bond, the primary / secondary amino group -NHR (where R is hydrogen or C1-C6 alkyl) reacts with an acid chloride or bromide group or an acid anhydride group to form an amide bond (-CO-NR-), the amino group -NHR reacts with an N-hydroxysuccinimide ester group to form an amide bond, and the amino group -NHR reacts with a coupling agent -carbodiimide (e.g., 1 In the presence of N,N'-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC), N,N'-dicyclohexylcarbodiimide (DCC), 1-cyclohexyl-3-(2-morpholinoethyl)carbodiimide, diisopropylcarbodiimide or mixtures thereof) and N-hydroxysuccinimide, the amino group -NHR reacts with the azlactone group (ring opening) to form an alkylene-diamide bond (-CONH-CT1T2-(CH2) p1The amino group -NHR reacts with an isocyanate group to form a urea bond (-NR-C(O)-NH- with R defined above), the amino group -NHR reacts with an epoxy or aziridine group to form an amine bond (-C-NR-), the hydroxyl reacts with an isocyanate to form a urethane bond, the hydroxyl reacts with an epoxy or aziridine to form an ether bond (-O-), the hydroxyl reacts with a chloride or bromide group or an anhydride group of an acid to form an ester bond (-O-). A thiol group reacts with an epoxy group to form a tert-bond, a carboxyl group reacts with an epoxy group to form an ester bond, a thiol group (-SH) reacts with an isocyanate to form a thiocarbamate bond (-NC(O)-S-), a thiol group reacts with an epoxy or aziridine to form a thioether bond (-S-), a thiol group reacts with a chloride or bromide group or an anhydride group of an acid to form a thioester bond, and a thiol group reacts with an azlactone group in the presence of a catalyst to form a bond (-CONH-CT1T2-(CH2) p1 The thiol group reacts with an ene group or a vinylsulfonyl group to form a thioether bond (-S-) based on a thiol-ene "click" reaction under suitable reaction conditions, and the thiol group reacts with a (meth)acryloyl group to form a thioether bond based on a Michael addition under suitable reaction conditions.

[0086] The reaction conditions for the above-mentioned coupling reactions are taught in textbooks and are well known to those skilled in the art.

[0087] According to the present invention, coupling agents each having two reactive functional groups can be used in the coupling reaction. The coupling agents having two reactive functional groups can be: diisocyanate compounds, diacid halide compounds, dicarboxylic acid compounds, dicarboxylic anhydride compounds, diamine compounds, diol compounds, diepoxy compounds, diaziridine compounds, diazlactone compounds, diene compounds, divinylsulfone compounds, dithiol compounds, thiolactone compounds, amino acid compounds, hydroxy-containing amine compounds, amine compounds having one hydroxyl group or ketone group, hydroxy-containing carboxylic acid compounds, mercaptans having a hydroxyl group, a carboxyl group or an amino group.

[0088] For example, a diisocyanate, a dicarboxylic acid (preferably a dicarboxylic anhydride), a diaziridine, a diepoxy or a diazlactone compound may be selected from the group consisting of hydroxyl groups, primary amino groups, secondary amino groups and thiol groups, whether they are different or the same. e and E PC can be used for coupling of E, where the diamine, dihydroxyl, dithiol, hydroxy-containing amine or hydroxy-containing thiol compounds are different or the same and are selected from the group consisting of isocyanate groups, epoxy groups, aziridine groups and carboxylic acid groups. e and E PC can be used to couple the diepoxy compounds E e and E PC When both are aldehyde groups, a diamine compound can be used to couple E e and E PC When they are both thiol groups, a divinyl sulfone compound can be used to couple E e and E PC can be used for coupling of a primary or secondary amino group, a thiolactone compound can be used for coupling of E e and E PCcan be used to covalently bond a thiol group via a bond to either E, which is an ene group or a (meth)acryloyl group, and a mercaptan having a hydroxyl group, a carboxyl group, an amino group or a ketone group can be used to covalently bond a thiol group via a bond to either E PC The compound can be used to covalently attach a hydroxyl group, a carboxyl group, an amino group, or a ketone group via a bond to E. e and E PC It is well known how to select one or more coupling agents based on selectivity and / or differential reactivity of a given functional group to couple to form the photochromic polysiloxane vinyl crosslinker of the present invention.

[0089] Examples of commercially available dicarboxylic acid anhydrides include, but are not limited to, succinic anhydride, methylsuccinic anhydride, 2,2-dimethylsuccinic anhydride, 2,3-dimethylsuccinic acid, glutaric anhydride, 3,3-dimethylglutaric anhydride, 2,2-dimethylglutaric anhydride, 3-methylglutaric anhydride, 3,3-tetramethylglutaric anhydride, diglycolic anhydride, adipic anhydride, and the like.

[0090] In the present invention, any suitable C3 to C 24 A dicarboxylic acid compound can be used. Examples of preferred dicarboxylic acid compounds include, but are not limited to, linear or branched C3-C 24 Aliphatic dicarboxylic acids, C5-C 24 Alicyclic or aliphatic-alicyclic dicarboxylic acids, C6-C 24Examples of suitable aliphatic dicarboxylic acids include aromatic or araliphatic dicarboxylic acids, dicarboxylic acids containing amino or imido groups or N-heterocycles, and combinations thereof.Suitable aliphatic dicarboxylic acids are oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, undecane diacid, dodecane diacid, dimethylmalonic acid, octadecyl succinic acid, trimethyl adipic acid, and dimer acids (dimerization products of unsaturated aliphatic carboxylic acids, such as oleic acid).Examples of suitable alicyclic dicarboxylic acids are 1,3-cyclobutane dicarboxylic acid, 1,3-cyclopentane dicarboxylic acid, 1,3- and 1,4-cyclohexane dicarboxylic acid, 1,3- and 1,4-dicarboxymethylcyclohexane, 4,4'-dicyclohexyl dicarboxylic acid. Examples of suitable aromatic dicarboxylic acids are terephthalic acid, isophthalic acid, o-phthalic acid, 1,3-, 1,4-, 2,6- or 2,7-naphthalenedicarboxylic acid, 4,4'-biphenyldicarboxylic acid, 2,2'-biphenyldicarboxylic acid, 4,4'-diphenylsulfone-dicarboxylic acid, 1,1,3-trimethyl-5-carboxyl-3-(p-carboxyphenyl)-indane, 4,4'-diphenylether-dicarboxylic acid, bis-p-(carboxyphenyl)-methane.

[0091] Any suitable diacid halide can be used in the present invention. Examples of preferred diacid halides include, but are not limited to, fumaryl chloride, suberoyl chloride, succinyl chloride, phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride, sebacoyl chloride, adipoyl chloride, trimethyladipoyl chloride, azeloyl chloride, dodecane diacid chloride, succinyl chloride, glutaric chloride, oxalyl chloride, dimer acid chloride, and combinations thereof.

[0092] In the present invention, any suitable diamine can be used. The organic diamine may be a linear or branched C2-C 24 Aliphatic diamines, C5-C 24 Alicyclic or aliphatic-alicyclic diamines or C6-C 24The diamines may be aromatic or alkyl-aromatic. Preferred organic diamines are N,N'-bis(hydroxyethyl)ethylenediamine, N,N'-dimethylethylenediamine, ethylenediamine, N,N'-dimethyl-1,3-propanediamine, N,N'-diethyl-1,3-propanediamine, N-methyl-1,3-diaminopropane, N-methylethylenediamine, N-ethylethylenediamine, N-isopropyl-1,3-propanediamine, N-propyl-1,3-propanediamine, N-butylethylenediamine, 2, 2-Dimethyl-1,3-propanediamine, 1,4-butanediamine, 1,5-pentanediamine, hexamethylenediamine, 2-methyl-1,5-pentanediamine, 1,6-hexamethylenediamine, N,N'-dimethyl-1,6-hexamethylenediamine, 2,2,4(2,4,4)-trimethyl-1,6-hexanediamine, 1,3-diamino-2-propanol, 1,2-diaminoethane-1,2-diol, 1,1-diaminoethane-1,2-diol, 1,4-diaminoethane 2,3-butanediol, 1,3-cyclopentanediamine, 1,4-diaminocyclohexane, 1,3-bis(aminomethyl)cyclohexane, 4,4'-diaminodicyclohexylmethane, 4,4'-methylenebis(2-methylcyclohexylamine), isophoronediamine (3-aminomethyl-3,5,5-trimethylcyclohexylamine), m-xylylenediamine, p-xylylenediamine, piperazine, 1-(2-aminoethyl)piperazine, 1,4-bis(3 -aminopropyl)piperazine, 2-piperazinoethylamine, 1-Boc-piperazine, 4-(2-aminoethyl)-1-Boc-piperazine, 1-(2-N-Boc-aminoethyl)piperazine, 4-(2-aminoethyl)-1-Boc-piperazine, 4-aminopiperidine, 3-aminopiperidine, 4-aminomethylpiperidine, 2-aminomethylpiperidine, 1-Boc-piperidine-4-carboxaldehyde, 1-Boc-piperidine-4-acetaldehyde, and the like.

[0093] In the present invention, any suitable C4 to C 24Diisocyanates can be used. Examples of preferred diisocyanates include, but are not limited to, tetramethylene diisocyanate, pentamethylene diisocyanate, hexamethylene diisocyanate, heptamethylene diisocyanate, 1,6-diisocyanate-2,2,4-trimethylhexane, octamethylene diisocyanate, dodecamethylene diisocyanate, cyclohexane diisocyanate, 1,3-bis-(4,4'-isocyanatemethyl)cyclohexane, isophorone diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, toluene diisocyanate, 4,4'-diphenyl diisocyanate, 4,4'-diphenylmethane diisocyanate, p-phenylene diisocyanate, and the like.

[0094] Any suitable diepoxy compound can be used in the present invention. Examples of preferred diepoxy compounds are neopentyl glycol diglycidyl ether, 1,3-butadiene dioxide, 1,4-butanediol diglycidyl ether, 1,2,7,8-diepoxyoctane, 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane, 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate, vinylcyclohexene dioxide, 1,6-hexanediol diglycidyl ether, glycerol diglycidyl ether, ethylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, dipropylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, bis[4-(glycidyloxy)phenyl]methane, bisphenol A diglycidyl ether (2,2-bis[4-(glycidyloxy)phenyl]propane), bisphenol A propoxylate diglycidyl ether, and combinations thereof.

[0095] In the present invention, any suitable C2 to C 24Diols (i.e., compounds having two hydroxyl groups) can be used. Examples of preferred diols include, but are not limited to, ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, propylene glycol, 1,4-butanediol, various pentanediols, various hexanediols, various cyclohexanediols, 1,4-bis(2-hydroxyethyl)piperazine, bisphenol A, bisphenol F, 4,4'-methylenediphenol, and combinations thereof.

[0096] Any dimercaptan having from 2 to 24 carbon atoms may be used in the present invention to prepare the prepolymer of the present invention. Examples of dimercaptans include, but are not limited to, C2-C 12 Alkyl dimercaptans (e.g., ethyl dimercaptan, propyl dimercaptan, butyl dimercaptan, pentamethylene dimercaptan, hexamethylene dimercaptan, heptamethylene dimercaptan, octamethylene dimercaptan, nonamethylene dimercaptan, decamethylene dimercaptan, 3-ethylcyclohexane-1,2-dithiol, 3-(2-sulfanylethyl)cyclohexane-1-thiol, 3-(1-sulfanylethyl)cyclohexane-1-thiol, 2-methyl-3-phenylpropanediol, 3 ... Examples of such thiol groups include ethyl-5-(2-sulfanylpropyl)cyclohexane-1-thiol, 2-propylcyclohexane-1,4-dithiol, benzenedithiol, methyl-substituted benzenedithiol, benzenedimethanethiol, 1,1-biphenyl-4,4'-dimethanethiol, biphenyl-4,4-dithiol, ethyl ether dimercaptan, triglycol dimercaptan, tetraglycol dimercaptan, dimercaprol, 2,3-dimercaptopropanol, and dithiothreitol.

[0097] Any amino acid can be used in the present invention. Examples of amino acids include, but are not limited to, glycine, proline, alanine, valine, isoleucine, leucine, 2-aminobutyric acid, 4-aminobutyric acid, 3-aminoisobutyric acid, 3-aminobutyric acid, β-alanine, 1-amino-3-cyclopentane carboxylic acid, 3-aminocyclohexane carboxylic acid, pyrrolidine-3-carboxylic acid, 4-piperidine carboxylic acid, 3-piperidine carboxylic acid, 1-piperazine acetic acid, etc.

[0098] Examples of compounds having one amino group and one hydroxyl group or aldehyde group (or ketone group) include, but are not limited to, 1-piperazinepropanol, 2-[2-(1-piperazinyl)ethoxy]ethanol, 4-amino-1-piperazineethanol, 4-piperidinemethanol, 1-Boc-piperidine-4-carboxaldehyde, 4-formylpiperidine, N-Boc-4-piperidineacetaldehyde, and the like.

[0099] Examples of preferred commercially available thiolactones include, but are not limited to, 4-butyrothiolactone (or dihydro-2(3H)-thiophenone), 3-methyldihydro-2(3H)-thiophenone, 3-ethyldihydro-2(3H)-thiophenone, 3-(1-methylethyl)dihydro-2(3H)-thiophenone, 3,3-dimethyldihydro-2(3H)-thiophenone, 3-ethyl-3-methyldihydro-2(3H)-thiophenone, 3-acetyldihydro-2(3H)-thiophenone, N-acetylhomocysteine ​​thiolactone, N-propionylhomocysteine ​​thiolactone, N-butyrylhomocysteine ​​thiolactone, and N-carboxybutyrylhomocysteine ​​thiolactone (or 4-oxo-4-[(tetrahydro-2-oxo-3-thienyl)amino]-butanoic acid).

[0100] In the present invention, any divinyl sulfone compound can be used. Examples of preferred divinyl sulfone compounds include, but are not limited to, divinyl sulfone, bis(vinylsulfonyl) C1-C6 alkane, 1,3-bis(vinylsulfonyl)-2-propanol, 1,1-bis(vinylsulfonyl)-1-propanol, 1,5-bis(vinylsulfonyl)-3-pentanol, 1,1-bis(vinylsulfonyl)-3-methoxypropane, 1,5-bis(vinylsulfonyl)-2,4-dimethylbenzene, and 1,4-bis(vinylsulfonyl)-2,3,5,6-tetrafluorobenzene.

[0101] Examples of preferred primary and secondary amino-containing chain transfer agents include, but are not limited to, 2-mercaptoethylamine, 2-mercaptopropylamine, 3-mercaptopropylamine, 2-mercaptobutylamine, 3-mercaptobutylamine, 4-mercaptobutylamine, 5-mercaptopentylamine, 6-mercaptohexylamine, N-methylaminoethanethiol, N-ethylaminoethanethiol, N-methylaminopropanethiol, N-ethylaminopropanethiol, N-methylaminobutanethiol, N-ethylaminobutanethiol, 2-aminothiolphenol, 3-aminothiolphenol, 4-aminothiolphenol, and the like.

[0102] Examples of mercaptans having a carboxyl group include, but are not limited to, thioglycolic acid, 2-mercaptopropynoic acid, 3-mercaptopropionic acid, 4-mercaptobutyric acid, 2-methyl-3-sulfanylpropanoic acid, 2-mercaptoisobutyric acid, 6-mercaptohexanoic acid, 8-mercaptooctanoic acid, 4-mercaptobenzoic acid, 3-mercaptobenzoic acid, 4-mercaptophenylacetic acid, 2-mercapto-2-phenylacetic acid, and the like.

[0103] Examples of preferred hydroxyl-containing mercaptans include, but are not limited to, 2-mercaptoethanol, 3-mercaptopropanol, 1-mercapto-2-propanol, 2-mercapto-1-propanol, 4-mercapto-1-butanol, 2-mercapto-3-butanol, 3-mercapto-3-methyl-1-butanol, 4-mercapto-4-methyl-1-pentanol, 4-mercapto-4-methyl-2-pentanol, 6-mercapto-1-hexanol, 3-mercapto-1-hexanol, 8-mercapto-1-octanol, 9-mercapto-1-nonanol, 2-mercaptophenol, 3-mercaptophenol, 4-mercaptophenol, 2-mercaptobenzyl alcohol, 4-(6-mercaptohexyloxy)benzyl alcohol, and the like.

[0104] Examples of preferred mercaptans having a methylcarbonyl group (-COCH3) include, but are not limited to, 4-methyl-4-mercaptopentan-2-one, 3-mercapto-2-butanone, and the like.

[0105] a first reactive functional group E of one of the aryl-containing compounds e and the second functional group E AR and / or by using one or more coupling agents (i.e., any one of those described above, etc.) to increase the length of the covalent bond between E e and E AR It is desirable to convert one of the groups into a different reactive functional group that reacts with another group (for example, when a3 is an integer of 1 to 2 in the above formula (1)).

[0106] Any aryl-containing compound can be used to prepare the high RI polysiloxane vinyl crosslinkers of the present invention, so long as it contains a reactive functional group such as, for example, a hydroxyl group, a carboxyl group, a primary amino group, a secondary amino group, an isocyanate group, an epoxy group, an aziridine group, a thiol group, a ketone group, or an ethylenically unsaturated group (e.g., ene, vinyl, vinylsulfonyl, acryloyl, and methacryloyl group).

[0107] A wide variety of reactive aryl-containing compounds are available from commercial sources or can be prepared according to procedures known to those skilled in the art, including those described in the patent and literature.

[0108] The high RI polysiloxane vinyl crosslinkers of the present invention (especially those of formula (1) defined above) can be particularly useful in preparing hydrophobic crosslinked polymeric materials for forming high RI inserts and silicone hydrogel polymeric materials for forming high RI and high Dk (oxygen permeability) silicone hydrogel contact lenses, which are another aspect of the present invention. Those skilled in the art will know how to prepare hydrophobic crosslinked polymeric materials or silicone hydrogel polymeric materials from polymerizable compositions according to any known polymerization mechanism.

[0109] In another aspect, the present invention provides an insert made from a hydrophobic crosslinked polymeric material comprising repeat units (as described above) of the high RI polysiloxane vinyl crosslinker of the present invention.

[0110] In a further aspect, the present invention provides a silicone hydrogel contact lens comprising a crosslinked polymeric material that includes units of the polysiloxane vinyl crosslinker of the present invention (as described above).

[0111] According to the present invention, the insert or silicone hydrogel (SiHy) contact lens of the present invention can be manufactured according to any lens manufacturing process. Those skilled in the art are very familiar with the method of manufacturing insert or SiHy contact lens. For example, insert or SiHy contact lens can be manufactured in a conventional "spin mold" as described in, for example, US Pat. No. 3,408,429, or by a complete cast molding process in a static form as described in US Pat. Nos. 4,347,198, 5,508,317, 5,583,463, 5,789,464, and 5,849,810, or by lathe cutting of a button of polymeric material as used to make customized contact lens. In cast molding, a polymerizable composition (i.e., insert formulation or SiHy lens formulation) is typically dispensed into a mold and cured (i.e., polymerized and / or crosslinked) by heat or actinic radiation in the mold to make insert or SiHy contact lens.

[0112] Lens molds for making contact lenses, such as insert or SiHy contact lenses, are well known to those skilled in the art and are used, for example, for cast molding or spin casting. For example, a mold (for cast molding) generally includes at least two mold pieces (or parts) or mold halves, namely a first and a second mold half. The first mold half defines a first molding (or optical) surface, and the second mold half defines a second molding (or optical) surface. The first and second mold halves are configured to receive each other such that an insert molding or lens forming cavity is formed between the first and second molding surfaces. The molding surface of the mold half is the cavity forming surface of the mold and is in direct contact with the polymerizable composition.

[0113] Methods for producing mold parts for casting contact lenses or inserts are generally well known to those skilled in the art. The process of the present invention is not limited to any particular method for forming a mold. In fact, any method for forming a mold can be used in the present invention. The first and second mold halves can be formed by various techniques, such as injection molding or lathing. Examples of suitable processes for forming mold halves are disclosed in U.S. Patent Nos. 4,444,711, 4,460,534, 5,843,346, and 5,894,002.

[0114] Virtually all materials known in the art for producing molds can be used to produce molds for making contact lenses or inserts. For example, polymeric materials can be used, such as polyethylene, polypropylene, polystyrene, PMMA, Topas® COC grade 8007-S10 (a transparent amorphous copolymer of ethylene and norbornene, manufactured by Ticona GmbH, Frankfurt, Germany and Summit, New Jersey), etc. Other materials that allow UV light transmission, such as quartz glass and sapphire, could be used.

[0115] The insert formulation (i.e., polymerizable composition) for producing the insert of the present invention contains a high RI polysiloxane vinyl crosslinker, other copolymerizable components, a free radical initiator (thermal or photoinitiator) (any of those described below), optional UV absorbing vinyl monomer (any of those described below), optional UV / high energy violet light ("HEVL") absorbing vinyl monomer, optional photochromic vinyl monomer, and the like, as known to those skilled in the art.

[0116] Examples of copolymerizable components used in the insert formulation include, but are not limited to, hydrophobic acrylic monomers (any of those described below), aryl vinyl monomers (any of those described below), hydrophobic vinyl monomers other than hydrophobic acrylic monomers (any of those described below), and vinyl crosslinkers (any of those described below).

[0117] The SiHy lens formulations (i.e., polymerizable compositions) for producing the SiHy contact lenses of the present invention contain a high RI polysiloxane vinyl crosslinker, other copolymerizable components, a free radical initiator (thermal or photoinitiator) (any of those described below), optional UV absorbing vinyl monomers (any of those described below), optional UV / HEVL absorbing vinyl monomers, optional photochromic vinyl monomers, etc., as known to those skilled in the art. Numerous silicone hydrogel lens formulations have been described in numerous patents and patent applications published up to the filing date of this application and have been used in the manufacture of commercially available SiHy contact lenses. Examples of commercially available SiHy contact lenses include, but are not limited to, asmofilcon A, balafilcon A, confilcon A, derefilcon A, eflofilcon A, enfilcon A, funfilcon A, galyfilcon A, lotrafilcon A, lotrafilcon B, narafilcon A, narafilcon B, senofilcon A, senofilcon B, senofilcon C, sumafilcon A, somofilcon A, and stenfilcon A, which can be used as the lens forming composition of the present invention.

[0118] Examples of copolymerizable components used in SiHy lens formulations include, but are not limited to, (1) at least one silicone-containing vinyl monomer (any of those described below) and / or at least one silicone-containing vinyl crosslinker (any of those described below); (2) at least one hydrophilic vinyl monomer (any of those described below); (3) optionally at least one hydrophobic non-silicone vinyl monomer (any of those described below); and (4) optionally at least one non-silicone vinyl crosslinker (any of those described below).

[0119] Any hydrophobic acrylic monomer can be used in forming the insert of the present invention. Examples of hydrophobic acrylic monomers include silicone-containing acrylic monomers (any of those described above in this application), non-silicone hydrophobic acrylic monomers (any of those described above in this application), fluorine-containing acrylic monomers (any of those described above in this application), aryl acrylic monomers (any of those described above in this application), and combinations thereof.

[0120] Examples of aryl acrylic monomers include, but are not limited to, 2-ethylphenoxyacrylate; 2-ethylphenoxymethacrylate; phenylacrylate; phenylmethacrylate; benzylacrylate; benzylmethacrylate; 2-phenylethylacrylate; 2-phenylethylmethacrylate; 3-phenylpropylacrylate; 3-phenylpropylmethacrylate; 4-phenylbutylacrylate; 4-phenylbutylmethacrylate; 4-methylphenylacrylate; 4-methylphenylmethacrylate; 4-methylphenylacrylate; 2-(4-Methylphenyl)ethyl acrylate;2-(4-propylphenyl)ethyl acrylate;2-(4-propylphenyl)ethyl methacrylate;2-(4-propylphenyl)ethyl acrylate;2-(4-propylphenyl)ethyl methacrylate;2-(4-(1-methylethyl)phenyl)ethyl acrylate 2-(4-(1-methylethyl)phenyl)ethyl methacrylate;2-(4-methoxyphenyl)ethyl acrylate;2-(4-methoxyphenyl)ethyl methacrylate;2-(4-cyclohexylphenyl)ethyl acrylate;2-(4-cyclohexylphenyl)ethyl methacrylate;2-(2-chlorophenyl)ethyl acrylate;2-(2-chlorophenyl)ethyl methacrylate;2-(3-chlorophenyl)ethyl acrylate;2-(3-chlorophenyl)ethyl methacrylate;2-(4-chlorophenyl)ethyl acrylate ethyl acrylate;2-(4-chlorophenyl)ethyl methacrylate;2-(4-bromophenyl)ethyl acrylate;2-(4-bromophenyl)ethyl methacrylate;2-(3-phenylphenyl)ethyl acrylate;2-(3-phenylphenyl)ethyl methacrylate;2-(4-phenylphenyl)ethyl acrylate;2-(4-phenylphenyl)ethyl methacrylate;2-(4-benzylphenyl)ethyl acrylate;2-(4-benzylphenyl)ethyl methacrylate;2-(phenylthio)ethyl acrylate;2-(phenylthio)ethyl methacrylate; 2-benzyloxyethyl acrylate; 3-benzyloxypropyl acrylate; 2-benzyloxyethyl methacrylate; 3-benzyloxypropyl methacrylate; 2-[2-(benzyloxy)ethoxy]ethyl acrylate; 2-[2-(benzyloxy)ethoxy]ethyl methacrylate; or combinations thereof. More preferred hydrophobic acrylic monomers are 2-phenylethyl acrylate; 3-phenylpropyl acrylate; 4-phenylbutyl acrylate; 5-phenylpentyl acrylate; 2-benzyloxyethyl acrylate; 3-benzyloxypropyl acrylate; 2-[2-(benzyloxy)ethoxy]ethyl acrylate; and their corresponding methacrylates. The aryl acrylic monomers listed above can be obtained from commercial sources or prepared by methods known in the art.;

[0121] Examples of hydrophobic monomers other than hydrophobic acrylic monomers include vinyl alkanoates (any of those described above in this application), vinyloxyalkanes (any of those described above in this application), and combinations thereof.

[0122] Examples of preferred hydrophobic non-silicone vinyl monomers include non-silicone hydrophobic acrylic monomers (such as the following methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, cyclohexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, isobornyl (meth)acrylate, (meth)acrylonitrile, etc.), fluorine-containing acrylic monomers (such as perfluorohexylethyl-thio-carbonyl-aminoethyl-methacrylate, perfluoro-substituted-C2-C 12alkyl (meth)acrylates, etc.), vinyl alkanoates (e.g., vinyl acetate, vinyl propionate, vinyl butyrate, vinyl valerate, etc.), vinyloxyalkanes (e.g., vinyl ethyl ether, propyl vinyl ether, n-butyl vinyl ether, isobutyl vinyl ether, cyclohexyl vinyl ether, t-butyl vinyl ether, etc.), styrene, vinyl toluene, vinyl chloride, vinylidene chloride, 1-butene, as well as combinations thereof. Any suitable perfluoro-substituted -C2-C 12 ~C 12 Alkyl (meth)acrylates may also be used in the present invention. 12 Examples of alkyl (meth)acrylates include, but are not limited to, 2,2,2-trifluoroethyl (meth)acrylate, tetrafluoropropyl (meth)acrylate, hexafluoro-iso-propyl (meth)acrylate, hexafluorobutyl (meth)acrylate, heptafluorobutyl (meth)acrylate, octafluoropentyl (meth)acrylate, heptadecafluorodecyl (meth)acrylate, pentafluorophenyl (meth)acrylate, and combinations thereof.

[0123] Any suitable vinyl crosslinker may be used in the manufacture of the inserts of the present invention. Examples of preferred vinyl crosslinkers include, but are not limited to, polysiloxane vinyl crosslinkers (any of those described below) and / or non-silicone vinyl crosslinkers.

[0124] Examples of non-silicone vinyl crosslinkers include, but are not limited to, acrylic crosslinkers (any of those described below), aryl crosslinkers (e.g., divinylbenzene, 2-methyl-1,4-divinylbenzene, bis(4-vinylphenyl)methane, 1,2-bis(4-vinylphenyl)ethane, etc.), tetraethylene glycol divinyl ether, triethylene glycol divinyl ether, diethylene glycol divinyl ether, ethylene glycol divinyl ether, triallyl isocyanurate, triallyl cyanurate, allyl methacrylate, allyl acrylate, N-allyl-methacrylamide, N-allyl-acrylamide, or combinations thereof.

[0125] Examples of acrylic crosslinkers include, but are not limited to, ethylene glycol di(meth)acrylate; 1,3-propanediol di(meth)acrylate; 2,3-propanediol di(meth)acrylate; 1,3-butanediol di-(meth)acrylate; 1,4-butanediol di(meth)acrylate; glycerol 1,3-diglycerolate di-(meth)acrylate; 1,5-pentanediol di(meth)acrylate; 1,6-hexanediol di(meth)acrylate; diethylene glycol di(meth)acrylate; DI(METHA)ACRYLATE;TRIETHYLENE GLYCOL DI(METHA)ACRYLATE;TETRAETHYLENE GLYCOL DI(METHA)ACRYLATE;ETHYLENE BIS[OXY(2-HYDROXYPROPANE-1,3-DIYL)]DI-(METHA)ACRYLATE;BIS[2-(METHA)ACRYLOXYETHYL]PHOSPHATE;3,4-BIS[(METHA)ACRYLOYL]TETRAHYDROFURAN;DI(METHA)ACRYLAMIDE;N,N-DI(METHA)ACRYLOYL-N-METHYLAMINE;N,N-DI(METHA)ACRYLOYL-N-ETHYLAMINE ,N'-Methylenebis((meth)acrylamide);N,N'-Ethylenebis((meth)acrylamide);N,N'-Hexamethylenebis(meth)acrylamide;N,N'-Dihydroxyethylenebis(meth)acrylamide;N,N'-Propylenebis(meth)acrylamide;N,N'-2-Hydroxypropylenebis(meth)acrylamide;N,N'-2,3-Dihydroxybutylenebis(meth)acrylamide;1,3-Bis(meth)acrylamidopropan-2-yl dihydrogen phosphate; piperazine diacrylamide; pentaerythritol tri(meth)acrylate; trimethyloylpropane tri(meth)acrylate; tris(2-hydroxyethyl)isocyanurate tri(meth)acrylate; 1,3,5-tri(meth)acryloxylhexahydro-1,3,5-triazine; pentaerythritol tetra(meth)acrylate; di(trimethyloylpropane)tetra(meth)acrylate; bisphenol A di(meth)acrylate; or combinations thereof.

[0126] According to the present invention, silicone-containing vinyl monomer can be any silicone-containing vinyl monomer known to those skilled in the art.The examples of preferred silicone-containing vinyl monomer include, without limitation, the vinyl monomers each having bis(trialkylsilyloxy) alkylsilyl group or tris(trialkylsilyloxy) silyl group, polysiloxane vinyl monomer, 3-methacryloxypropyl pentamethyldisiloxane, t-butyldimethyl-siloxyethyl vinyl carbonate, trimethylsilylethyl vinyl carbonate, and trimethylsilylmethyl vinyl carbonate, and combinations thereof.

[0127] Preferred polysiloxane vinyl monomers can be obtained from commercial sources (e.g., Shin-Etsu Chemical, Gelest, etc.); can be prepared, for example, according to the procedures described in U.S. Pat. Nos. 5,070,215, 6,166,236, 6,867,245, 8,415,405, 8,475,529, 8,614,261, and 9,217,813; can be prepared by reacting hydroxyalkyl (meth)acrylates or (meth)acrylamides or (meth)acryloxypolyethylene glycols with the monomers. They can be prepared by reacting glycidyl (meth)acrylate with monocarbinol-terminated polydimethylsiloxane, monoaminopropyl-terminated polydimethylsiloxane, or monoethylaminopropyl-terminated polydimethylsiloxane; or by reacting isocyanatoethyl (meth)acrylate with monocarbinol-terminated polydimethylsiloxane according to coupling reactions well known to those skilled in the art.

[0128] Preferred silicone-containing vinyl monomers having bis(trialkylsilyloxy)alkylsilyl or tris(trialkylsilyloxy)silyl groups, respectively, can be prepared according to the procedures described in U.S. Pat. Nos. 5,070,215, 6,166,236, 7,214,809, 8,475,529, 8,658,748, 9,097,840, 9,103,965, and 9,475,827.

[0129] Any suitable polysiloxane vinyl crosslinker can be used in the present invention. Examples of preferred polysiloxane vinyl crosslinkers include di-(meth)acryloyl terminated polydimethylsiloxane; divinyl carbonate terminated polydimethylsiloxane; divinyl carbamate terminated polydimethylsiloxane; N,N,N',N'-tetrakis(3-methacryloxy-2-hydroxypropyl)-alpha,omega-bis-3-aminopropyl-polydimethylsiloxane; Macromer A, Macromer B, Macromer C, Macromer D, Macromer E, Macromer F, Macromer G, Macromer H, Macromer I ... Polysiloxane-containing macromers selected from the group consisting of Macromer C, Macromer D, and Macromer D; U.S. Pat. Nos. 4,136,250, 4,153,641, 4,182,822, 4,189,546, 4,343,927, 4,254,248, 4,355,147, 4,276,402, 4,327,203, 4,341,889, 4,486,577, and 4,543,398 4605712, 4661575, 4684538, 4703097, 4833218, 4837289, 4954586, 49 54587 specification, 5010141 specification, 5034461 specification, 5070170 specification, 5079319 specification, 5039761 specification, 5346946 specification, 5358995 specification the polysiloxane-containing macromers disclosed in U.S. Pat. Nos. 5,387,632, 5,416,132, 5,451,617, 5,486,579, 5,962,548, 5,981,675, 6,039,913, and 6,762,264; and the polysiloxane-containing macromers disclosed in U.S. Pat. Nos. 4,259,467, 4,260,725, and 4,261,875.

[0130] One preferred class of polysiloxane vinyl crosslinkers is di-(meth)acryloyloxy-terminated polysiloxane vinyl crosslinkers having dimethylsiloxane units and hydrophilized siloxane units, respectively, where the hydrophilized siloxane units are one monovalent C4-C hydroxyl group having one methyl substituent and two to six hydroxyl groups. 40 and di-(meth)acryloyloxy-terminated polysiloxane vinyl crosslinkers, each having an organic radical substituent, which can be prepared according to the procedures disclosed in U.S. Pat. No. 1,008,1697.

[0131] Another class of preferred polysiloxane vinyl crosslinkers are those vinyl crosslinkers each of which contains one unique polysiloxane segment and two terminal (meth)acryloyl groups, which can be obtained from commercial sources; can be prepared by reacting glycidyl (meth)acrylate (meth)acryloyl chloride with a diamino-terminated polydimethylsiloxane or a dihydroxyl-terminated polydimethylsiloxane; can be prepared by reacting isocyanatoethyl (meth)acrylate with a dihydroxyl-terminated polydimethylsiloxane; can be prepared by reacting an amino-containing acrylic monomer with a dicarboxyl-terminated polydimethylsiloxane in the presence of a coupling agent (carbodiimide); can be prepared by reacting a carboxyl-containing acrylic monomer with a diamino-terminated polydimethylsiloxane in the presence of a coupling agent (carbodiimide); or can be prepared by reacting a hydroxyl-containing acrylic monomer with a dihydroxyl-terminated polydisiloxane in the presence of a diisocyanate or diepoxy coupling agent.

[0132] Another class of preferred polysiloxane vinyl crosslinkers are chain extended polysiloxane vinyl crosslinkers, each of which has at least two polysiloxane segments joined by a linker between each pair of polysiloxane segments and two terminal ethylenically unsaturated groups; which can be prepared according to the procedures described in U.S. Pat. Nos. 5,034,461; 5,416,132; 5,449,729; 5,760,100; 7,423,074; 8,529,057; 8,835,525; 8,993,651; 10,301,451; and 10,465,047.

[0133] Any hydrophilic vinyl monomer can be used in the present invention. Examples of preferred hydrophilic vinyl monomers are alkyl (meth)acrylamides (as described later in this application), hydroxyl-containing acrylic monomers (as described below), amino-containing acrylic monomers (as described later in this application), carboxyl-containing acrylic monomers (as described later in this application), N-vinylamide monomers (as described later in this application), methylene-containing pyrrolidone monomers (i.e., pyrrolidone derivatives having a methylene group attached to the pyrrolidone ring at the 3- or 5-position, respectively) (as described later in this application), acrylic monomers having C1-C4 alkoxyethoxy groups (as described later in this application), vinyl ether monomers (as described later in this application), allyl ether monomers (as described later in this application), phosphorylcholine-containing vinyl monomers (as described later in this application), allyl alcohol, N-2-hydroxyethyl vinyl carbamate, N-carboxyvinyl-β-alanine (VINAL), N-carboxyvinyl-α-alanine, and combinations thereof.

[0134] Examples of alkyl(meth)acrylamides include, but are not limited to, (meth)acrylamide, N,N-dimethyl(meth)acrylamide, N-ethyl(meth)acrylamide, N,N-diethyl(meth)acrylamide, N-propyl(meth)acrylamide, N-isopropyl(meth)acrylamide, N-3-methoxypropyl(meth)acrylamide, and combinations thereof.

[0135] Examples of hydroxyl-containing acrylic monomers include, but are not limited to, N-2-hydroxylethyl(meth)acrylamide, N,N-bis(hydroxyethyl)(meth)acrylamide, N-3-hydroxypropyl(meth)acrylamide, N-2-hydroxypropyl(meth)acrylamide, N-2,3-dihydroxypropyl(meth)acrylamide, N-tris(hydroxymethyl)methyl(meth)acrylamide, 2-hydroxyethyl(meth)acrylate, 3-hydroxypropyl(meth)acrylate, 2-hydroxypropyl(meth)acrylate, glycerol methacrylate (GMA), di(ethylene glycol)(meth)acrylate, tri(ethylene glycol)(meth)acrylate, tetra(ethylene glycol)(meth)acrylate, poly(ethylene glycol)(meth)acrylate having a number average molecular weight of up to 1500, poly(ethylene glycol)ethyl(meth)acrylamide having a number average molecular weight of up to 1500, and combinations thereof.

[0136] Examples of carboxyl-containing acrylic monomers include, but are not limited to, 2-(meth)acrylamidoglycolic acid, (meth)acrylic acid, ethylacrylic acid, 3-(meth)acrylamido-propionic acid, 5-(meth)acrylamidopentanoic acid, 4-(meth)acrylamidobutanoic acid, 3-(meth)acrylamido-2-methylbutanoic acid, 3-(meth)acrylamido-3-methylbutanoic acid, 2-(meth)acrylamido-2-methyl-3,3-dimethylbutanoic acid, 3-(meth)acrylamidohexanoic acid, 4-(meth)acrylamido-3,3-dimethylhexanoic acid, and combinations thereof.

[0137] Examples of amino-containing acrylic monomers include, but are not limited to, N-2-aminoethyl(meth)acrylamide, N-2-methylaminoethyl(meth)acrylamide, N-2-ethylaminoethyl(meth)acrylamide, N-2-dimethylaminoethyl(meth)acrylamide, N-3-aminopropyl(meth)acrylamide, N-3-methylaminopropyl(meth)acrylamide, N-3-dimethylaminopropyl(meth)acrylamide, 2-aminoethyl(meth)acrylate, 2-methylaminoethyl(meth)acrylate, 2-ethylaminoethyl(meth)acrylate, 3-aminopropyl(meth)acrylate, 3-methylaminopropyl(meth)acrylate, 3-ethylaminopropyl(meth)acrylate, 3-amino-2-hydroxypropyl(meth)acrylate, trimethylammonium 2-hydroxypropyl(meth)acrylate hydrochloride, dimethylaminoethyl(meth)acrylate, and combinations thereof.

[0138] Examples of N-vinyl amide monomers include, but are not limited to, N-vinylpyrrolidone (also known as N-vinyl-2-pyrrolidone), N-vinyl-3-methyl-2-pyrrolidone, N-vinyl-4-methyl-2-pyrrolidone, N-vinyl-5-methyl-2-pyrrolidone, N-vinyl-6-methyl-2-pyrrolidone, N-vinyl-3-ethyl-2-pyrrolidone, N-vinyl-4,5-dimethyl-2-pyrrolidone, N-vinyl-5,5-dimethyl-2-pyrrolidone, N-vinyl-3,3,5-trimethyl-2-pyrrolidone, N-vinylpiperidone (also known as N-vinyl-2-piperidone), N-vinyl-3-methyl-2-piperidone, N-vinyl-4-methyl-2-piperidone, N-vinyl-5-methyl-2-piperidone, N-vinyl-6-methyl-2-piperidone, and N-vinyl-6-ethyl-2-piperidone. N-vinyl-3,5-dimethyl-2-piperidone, N-vinyl-4,4-dimethyl-2-piperidone, N-vinyl caprolactam (also known as N-vinyl-2-caprolactam), N-vinyl-3-methyl-2-caprolactam, N-vinyl-4-methyl-2-caprolactam, N-vinyl-7-methyl-2-caprolactam, N-vinyl-7-ethyl-2-caprolactam, N-vinyl-3,5-dimethyl-2-caprolactam, N-vinyl-4,6-dimethyl-2-caprolactam, N-vinyl-3,5,7-trimethyl-2-caprolactam, N-vinyl-N-methylacetamide, N-vinylformamide, N-vinylacetamide, N-vinylisopropylamide, N-vinyl-N-ethylacetamide, N-vinyl-N-ethylformamide, and mixtures thereof.

[0139] Examples of methylene-containing pyrrolidone monomers include, but are not limited to, 1-methyl-3-methylene-2-pyrrolidone, 1-ethyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 1-ethyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone, 1-n-propyl-3-methylene-2-pyrrolidone, 1-n-propyl-5-methylene-2-pyrrolidone, 1-isopropyl-3-methylene-2-pyrrolidone, 1-isopropyl-5-methylene-2-pyrrolidone, 1-n-butyl-3-methylene-2-pyrrolidone, 1-tert-butyl-3-methylene-2-pyrrolidone, and combinations thereof.

[0140] Examples of acrylic monomers having a C1-C4 alkoxyethoxy group include, but are not limited to, ethylene glycol methyl ether (meth)acrylate, di(ethylene glycol) methyl ether (meth)acrylate, tri(ethylene glycol) methyl ether (meth)acrylate, tetra(ethylene glycol) methyl ether (meth)acrylate, C1-C4-alkoxypoly(ethylene glycol) (meth)acrylates having a number average molecular weight of up to 1500, methoxy-poly(ethylene glycol)ethyl (meth)acrylamide having a number average molecular weight of up to 1500, and combinations thereof.

[0141] Examples of vinyl ether monomers include, but are not limited to, ethylene glycol monovinyl ether, di(ethylene glycol) monovinyl ether, tri(ethylene glycol) monovinyl ether, tetra(ethylene glycol) monovinyl ether, poly(ethylene glycol) monovinyl ether, ethylene glycol methyl vinyl ether, di(ethylene glycol) methyl vinyl ether, tri(ethylene glycol) methyl vinyl ether, tetra(ethylene glycol) methyl vinyl ether, poly(ethylene glycol) methyl vinyl ether, and combinations thereof.

[0142] Examples of allyl ether monomers include, but are not limited to, ethylene glycol monoallyl ether, di(ethylene glycol) monoallyl ether, tri(ethylene glycol) monoallyl ether, tetra(ethylene glycol) monoallyl ether, poly(ethylene glycol) monoallyl ether, ethylene glycol methyl allyl ether, di(ethylene glycol) methyl allyl ether, tri(ethylene glycol) methyl allyl ether, tetra(ethylene glycol) methyl allyl ether, poly(ethylene glycol) methyl allyl ether, and combinations thereof.

[0143] Examples of phosphorylcholine-containing vinyl monomers include, but are not limited to, (meth)acryloyloxyethyl phosphorylcholine, (meth)acryloyloxypropyl phosphorylcholine, 4-((meth)acryloyloxy)butyl-2'-(trimethylammonio)ethyl phosphate, 2-[(meth)acryloylamino]ethyl-2'-(trimethylammonio)-ethyl phosphate, 3-[(meth)acryloylamino]propyl-2'-(trimethylammonio)ethyl phosphate, 4-[(meth)acryloylamino]butyl-2'- (Trimethylammonio)ethyl phosphate, 5-((meth)acryloyloxy)pentyl-2'-(trimethylammonio)ethyl phosphate, 6-((meth)acryloyloxy)hexyl-2'-(trimethylammonio)-ethyl phosphate, 2-((meth)acryloyloxy)ethyl-2'-(triethylammonio)ethyl phosphate, 2-((meth)acryloyloxy)ethyl-2'-(tripropylammonio)ethyl phosphate, 2-((meth)acryloyloxy)ethyl-2'-(tributylammonio)ethyl phosphate, 2-((meth)acryloyloxy)propyl-2'-(trimethylammonio)-ethyl phosphate, 2-((meth)acryloyloxy)butyl-2'-(trimethylammonio)ethyl phosphate, 2-((meth)acryloyloxy)pentyl-2'-(trimethylammonio)ethyl phosphate, 2-((meth)acryloyloxy)hexyl-2'-(trimethylammonio)ethyl phosphate, 2-(vinyloxy)ethyl-2'-(trimethylammonio)ethyl phosphate, 2-(allyloxy)ethyl 2-(vinyloxycarbonyl)ethyl-2'-(trimethylammonio)ethyl phosphate, 2-(allyloxycarbonyl)ethyl-2'-(trimethylammonio)ethyl phosphate, 2-(vinylcarbonylamino)ethyl-2'-(trimethylammonio)ethyl phosphate, 2-(allyloxycarbonylamino)ethyl-2'-(trimethylammonio)ethyl phosphate, 2-(butenoyloxy)ethyl-2'-(trimethylammonio)ethyl phosphate,and combinations thereof.

[0144] Any suitable UV absorbing vinyl monomer and UV / HEVL absorbing vinyl monomer can be used in the polymerizable composition to prepare the preformed SiHy contact lenses of the present invention. Examples of preferred UV absorbing and UV / HEVL absorbing vinyl monomers include, but are not limited to, 2-(2-hydroxy-5-vinylphenyl)-2H-benzotriazole, 2(2-hydroxy-5-acryloyloxyphenyl)-2H-benzotriazole, 2-(2-hydroxy-3-methacrylamidomethyl-5-tert-octylphenyl)benzotriazole, 2-(2'-hydroxy-5'-methacrylamidophenyl)-5-chloro ... 2-(2'-hydroxy-5'-glycidoxypropyl-3'-t-butylphenyl)-5-chlorobenzotriazole, 2-(2'-hydroxy-5'-methacryloxypropylphenyl)benzotriazole, 2-hydroxy-5-methoxy-3-(5-(trifluoromethyl)-2H-benzo[d][1,2,3]triazol-2-yl)benzyl methacrylate (WL-1), 2-hydroxy -5-Methoxy-3-(5-methoxy-2H-benzo[d][1,2,3]triazol-2-yl)benzyl methacrylate (WL-5), 3-(5-fluoro-2H-benzo[d][1,2,3]triazol-2-yl)-2-hydroxy-5-methoxybenzyl methacrylate (WL-2), 3-(2H-benzo[d][1,2,3]triazol-2-yl)-2-hydroxy-5-methoxybenzyl methacrylate (WL-3), 3-(5-chloro-2H-benzo[d][1,2,3 ]triazol-2-yl)-2-hydroxy-5-methoxybenzyl methacrylate (WL-4), 2-hydroxy-5-methoxy-3-(5-methyl-2H-benzo[d][1,2,3]triazol-2-yl)benzyl methacrylate (WL-6), 2-hydroxy-5-methyl-3-(5-(trifluoromethyl)-2H-benzo[d][1,2,3]triazol-2-yl)benzyl methacrylate (WL-7), 4-allyl-2-(5-chloro-2H-benzo[d][1,2,3]triazol-2-yl)-6-methoxyphenol (WL-8), 2{2'-hydroxy-3'-tert-5'[3"-(4"-vinylbenzyloxy)propoxy]phenyl}-5-methoxy-2H-benzotriazole, phenol, 2-(5-chloro-2H-benzotriazol-2-yl)-6-(1,1-Dimethylethyl)-4-ethenyl-(UVAM), 2-[2'-hydroxy-5'-(2-methacryloxyethyl)phenyl)]-2H-benzotriazole (2-propenoic acid, 2-methyl-, 2-[3-(2H-benzotriazol-2-yl)-4-hydroxyphenyl]ethyl ester, Norbloc), 2{2'-hydroxy-3'-tert-butyl-5'-[3'-methacryloyloxypropoxy]phenyl}-2H-benzotriazole, 2{2'-hydroxy-3'-tert-butyl-5'-[3'- 2-{2'-hydroxy-3'-tert-butyl-5'-[3'-methacryloyloxypropoxy]phenyl}-5-methoxy-2H-benzotriazole (UV13), 2-{2'-hydroxy-3'-tert-butyl-5'-[3'-methacryloyloxypropoxy]phenyl}-5-chloro-2H-benzotriazole (UV28), 2[2'-hydroxy-3'-tert-butyl-5'-(3'-acryloyloxypropoxy)phenyl]-5-trifluoromethyl-2H-benzotriazole (UV23), 2-(2'-hydroxy-5-methacrylamidophenyl)-5 -Methoxybenzotriazole (UV6), 2-(3-allyl-2-hydroxy-5-methylphenyl)-2H-benzotriazole (UV9), 2-(2-hydroxy-3-methallyl-5-methylphenyl)-2H-benzotriazole (UV12), 2-3'-t-butyl-2'-hydroxy-5'-(3"-dimethylvinylsilylpropoxy)-2'-hydroxyphenyl)-5-methoxybenzotriazole (UV15), 2-(2'-hydroxy-5'-methacryloylpropyl-3'-tert-butylphenyl) -5-Methoxy-2H-benzotriazole (UV16), 2-(2'-hydroxy-5'-acryloylpropyl-3'-tert-butylphenyl)-5-methoxy-2H-benzotriazole (UV16A), 2-Methylacrylic acid 3-[3-tert-butyl-5-(5-chlorobenzotriazol-2-yl)-4-hydroxyphenyl]-propyl ester (16-100, CAS#96478-15-8), 2-(3-(tert-butyl)-4-hydroxy-5-(5-methoxy-2H-benzo[d][1,2,3]triazol-2-yl)phenoxy)ethyl methacrylate (16-102); phenol, 2-(5-chloro-2H-benzotriazol-2-yl)-6-methoxy-4-(2-propen-1-yl) (CAS#1260141-20-5); 2-[2-hydroxy-5-[3-(methacryloyloxy)propyl]-3-tert-butylphenyl]-5-chloro-2H-benzotriazole; phenol, 2-(5-ethenyl-2H-benzotriazol-2-yl)-4-methyl-, homopolymer (9CI) (CAS#83063-87-0). According to the present invention, the polymerizable composition comprises about 0.1% to about 3.0% by weight, preferably about 0.2% to about 2.5% by weight, more preferably about 0.3% to about 2.0% by weight of one or more UV absorbing vinyl monomers based on the amount of the total polymerizable components in the polymerizable composition.

[0145] Examples of preferred photochromic vinyl monomers include polymerizable naphthopyrans, polymerizable benzopyrans, polymerizable indenonaphthopyrans, polymerizable phenanthropyrans, polymerizable spiro(benzindoline)-naphthopyrans, polymerizable spiro(indoline)benzopyrans, polymerizable spiro(indoline)-naphthopyrans, polymerizable spiro(indoline)quinopurans, polymerizable spiro(indoline)-pyrans, polymerizable naphthoxazines, polymerizable spirobenzopyrans; These include polymerizable spirobenzopyrans, polymerizable spirobenzothiopyrans, polymerizable naphthacenediones, polymerizable spirooxazines, polymerizable spiro(indoline)naphthoxazines, polymerizable spiro(indoline)pyridobenzoxazines, polymerizable spiro(benzindoline)pyridobenzoxazines, polymerizable spiro(benzindoline)naphthoxazines, polymerizable spiro(indoline)-benzoxazines, polymerizable diarylethenes, and combinations thereof. These are as disclosed in U.S. Pat. Nos. 4,929,693, 5,166,345, 6,017,121, 7,556,750, 7,584,630, 7,999,989, 8,158,037, 8,697,770, 8,741,188, 9,052,438, 9,097,916, 9,465,234, 9,904,074, 10,197,707, 6,019,914, 6,113,814, 6,149,841, 6,296,785 and 6,348,604.

[0146] Any thermal polymerization initiator may be used in the present invention. Suitable thermal polymerization initiators are known to those skilled in the art and include, for example, peroxides, hydroperoxides, azo-bis(alkyl- or cycloalkylnitriles), persulfates, percarbonates, or mixtures thereof.Examples of suitable thermal polymerization initiators include, without limitation, benzoyl peroxide, t-butyl peroxide, t-amyl peroxybenzoate, 2,2-bis(tert-butylperoxy)butane, 1,1-bis(tert-butylperoxy)cyclohexane, 2,5-bis(tert-butylperoxy)-2,5-dimethylhexane, 2,5-bis(tert-butylperoxy)-2,5-dimethyl-3-hexyne, bis(1-(tert-butylperoxy)-1-methylethyl)benzyl, tert-butylperoxy-1-methylethyl ... benzene, 1,1-bis(tert-butylperoxy)-3,3,5-trimethylcyclohexane, di-t-butyl-dipyroxyphthalate, t-butyl hydroperoxide, t-butyl peracetate, t-butyl peroxybenzoate, t-butyl peroxyisopropyl carbonate, acetyl peroxide, lauroyl peroxide, decanoyl peroxide, dicetyl peroxydicarbonate, di(4-t-butylcyclohexyl) peroxydicarbonate (Perkadox 16S), di(2-ethylhexyl) peroxydicarbonate, t-butyl peroxypivalate (Lupersol 11); t-butyl peroxy-2-ethylhexanoate (Trigonox 21-C50), 2,4-pentanedione peroxide, dicumyl peroxide, peracetic acid, potassium persulfate, sodium persulfate, ammonium persulfate, 2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile) (VAZO 33), 2,2'-azobis[2-(2-imidazolin-2-yl)propane] dihydrochloride (VAZO 44), 2,2'-azobis(2-amidinopropane) dihydrochloride (VAZO 50), 2,2'-azobis(2,4-dimethylvaleronitrile) (VAZO 52), 2,2'-azobis(isobutyronitrile) (VAZO 64 or AIBN), 2,2'-azobis-2-methylbutyronitrile (VAZO 67), 1,1-azobis(1-cyclohexanecarbonitrile) (VAZO 88); 2,2'-azobis(2-cyclopropylpropionitrile), 2,2'-azobis(methyl isobutyrate), 4,4'-azobis(4-cyanovaleric acid), and combinations thereof.Preferably, the thermal initiator is 2,2'-azobis(isobutyronitrile) (AIBN or VAZO 64).

[0147] Suitable photoinitiators are benzoin methyl ether, diethoxyacetophenone, benzoylphosphine oxide, 1-hydroxycyclohexylphenyl ketone and Darocur and Irgacur types, preferably Darocur 1173® and Darocur 2959®, germanium-based Norrish type I photoinitiators (e.g., those described in U.S. Pat. No. 7,605,190). Examples of benzoylphosphine initiators include 2,4,6-trimethylbenzoyldiphenylphosphine oxide; bis-(2,6-dichlorobenzoyl)-4-N-propylphenylphosphine oxide; and bis-(2,6-dichlorobenzoyl)-4-N-butylphenylphosphine oxide. Reactive photoinitiators are also suitable, which can be incorporated into macromers or used as special monomers, for example. Examples of reactive photoinitiators are those disclosed in EP 632329. Preferably, the SiHy lens formulation for making SiHy contact lenses includes at least one photoinitiator capable of being initiated by visible light, such as a benzoylphosphine oxide photoinitiator, a germanium-based Norrish Type I photoinitiator, or a combination thereof.

[0148] The polymerizable composition (insert formulation or SiHy lens formulation), as known to those skilled in the art, can be a solvent-free clear liquid prepared by mixing all the polymerizable components with other necessary components, or a solution prepared by dissolving all of the desired components in any suitable solvent, such as a mixture of water and one or more water-miscible organic solvents, an organic solvent, or a mixture of one or more organic solvents. The term "solvent" refers to a chemical that cannot participate in a free radical polymerization reaction.

[0149] The solventless polymerizable composition typically contains at least one blending vinyl monomer as a reactive solvent for dissolving all other polymerizable components of the solventless SiHy lens formulation.

[0150] Examples of suitable blending vinyl monomers include, but are not limited to, C1-C 10 Examples of suitable vinyl monomers include alkyl (meth)acrylates, cyclopentyl acrylate, cyclohexyl methacrylate, cyclohexyl acrylate, isobornyl (meth)acrylate, styrene, 4,6-trimethylstyrene (TMS), t-butylstyrene (TBS), trifluoroethyl (meth)acrylate, hexafluoro-isopropyl (meth)acrylate, hexafluorobutyl (meth)acrylate, or combinations thereof. Preferably, methyl methacrylate is used as the blending vinyl monomer in preparing the solventless SiHy lens formulation.

[0151] Any solvent can be used in the present invention. Examples of preferred organic solvents include, without limitation, tetrahydrofuran, tripropylene glycol methyl ether, dipropylene glycol methyl ether, ethylene glycol n-butyl ether, ketones (e.g., acetone, methyl ethyl ketone, etc.), diethylene glycol n-butyl ether, diethylene glycol methyl ether, ethylene glycol phenyl ether, propylene glycol methyl ether, propylene glycol methyl ether acetate, dipropylene glycol methyl ether acetate, propylene glycol n-propyl ether, dipropylene glycol n-propyl ether, tripropylene glycol n-butyl ether, propylene glycol n-butyl ether, dipropylene glycol n-butyl ether, tripropylene glycol n-butyl ether, ... phenyl ether, dipropylene glycol dimethyl ether, polyethylene glycol, polypropylene glycol, ethyl acetate, butyl acetate, amyl acetate, methyl lactate, ethyl lactate, i-propyl lactate, methylene chloride, 2-butanol, 1-propanol, 2-propanol, menthol, cyclohexanol, cyclopentanol and exonorborneol, 2-pentanol, 3-pentanol, 2-hexanol, 3-hexanol, 3-methyl-2-butanol, 2-heptanol, 2-octanol, 2-nonanol, 2-decanol, 3-octanol, norborneol, tert-butanol, tert-amyl alcohol, 2-methyl-2-pentanol, 2,3-dimethyl-2-butanol, 3-methyl-3-pentanol, 1-methylcyclohexanol, 2-methyl-2-hexanol, 3,7-Dimethyl-3-octanol, 1-chloro-2-methyl-2-propanol, 2-methyl-2-heptanol, 2-methyl-2-octanol, 2-2-methyl-2-nonanol, 2-methyl-2-decanol, 3-methyl-3-hexanol, 3-methyl-3-heptanol, 4-methyl-4-heptanol, 3-methyl-3-octanol, 4-methyl-4-octanol, 3-methyl-3-nonanol, 4-methyl-4-nonanol, 3-methyl-3-octanol, 3-ethyl-3-hexanol, 3-methyl-3-heptanol, 4-ethyl-4-heptanol, 4-propyl-4-heptanol, 4-isopropyl-4-heptanol, 2,4-dimethyl-2-pentanol, 1-methylcyclopentanol, Examples of suitable cyclopentanols include 1-ethylcyclopentanol, 1-ethylcyclopentanol, 3-hydroxy-3-methyl-1-butene, 4-hydroxy-4-methyl-1-cyclopentanol, 2-phenyl-2-propanol, 2-methoxy-2-methyl-2-propanol, 2,3,4-trimethyl-3-pentanol, 3,7-dimethyl-3-octanol, 2-phenyl-2-butanol, 2-methyl-1-phenyl-2-propanol and 3-ethyl-3-pentanol, 1-ethoxy-2-propanol, 1-methyl-2-pyrrolidone, N,N-dimethylpropionamide, dimethylformamide, dimethylacetamide, dimethylpropionamide, N-methylpyrrolidone, and mixtures thereof.

[0152] In accordance with the present invention, the polymerizable composition (insert formulation or SiHy lens formulation) can be introduced (discharged) into the cavity formed by the male and female halves of the mold according to any known method.

[0153] After the polymerizable composition is dispensed into the mold, it is polymerized to produce the SiHy contact lens. Crosslinking can be initiated by heat or actinic radiation, as known to those skilled in the art.

[0154] The thermal polymerization is conveniently carried out at temperatures of, for example, 25 to 120° C., preferably 40 to 100° C. The reaction time may vary within wide limits but is conveniently, for example, 1 to 24 hours or preferably 2 to 12 hours. It is advantageous to previously degas the components and the solvent used in the polymerization reaction and to carry out the copolymerization reaction under an inert atmosphere, for example under an atmosphere of nitrogen or argon.

[0155] Actinic polymerization can then be induced by actinic radiation, such as light, especially UV or visible light of suitable wavelengths. If necessary, the spectral requirements can be appropriately controlled by the addition of suitable photosensitizers.

[0156] Opening the mold so that the molded insert or the SiHy contact lens can be removed from the mold can be done in a manner known per se.

[0157] The molded insert or SiHy contact lens can be subjected to lens extraction using a liquid extraction medium to remove unpolymerized polymerizable components and formed oligomers. In accordance with the present invention, the extraction liquid medium is any solvent capable of dissolving the organic solvent, unpolymerized polymerizable material, and oligomers in the dry contact lens. Water, any organic solvent known to those skilled in the art, or mixtures thereof can be used in the present invention. Preferably, the organic solvent used in the extraction liquid medium is water, buffered saline, C1-C3 alkyl alcohol, 1,2-propylene glycol, polyethylene glycol having a number average molecular weight of about 400 Daltons or less, C1-C6 alkyl alcohol, or combinations thereof.

[0158] After extraction, the silicone hydrogel contact lenses can be hydrated in water or an aqueous solution to replace the liquid extraction medium according to any method known to those of skill in the art.

[0159] The hydrated silicone hydrogel contact lenses may be further subjected to additional processes such as, for example, surface treatment, packaging in a lens package with a packaging solution well known to those skilled in the art; sterilization such as autoclaving at 118-124° C. for at least about 30 minutes, etc.

[0160] Lens packages (or containers) are well known to those skilled in the art for autoclaving and storing soft contact lenses. Any lens package can be used in the present invention. Preferably, the lens package is a blister package comprising a base and a cover; wherein the cover is removably sealed to the base, and wherein the base comprises a cavity for receiving a sterile packaging solution and a contact lens.

[0161] The lenses are packaged in individual packages, sealed, and sterilized (e.g., by autoclaving at about 120° C. or higher under pressure for at least 30 minutes) before being distributed to users. Those skilled in the art will be familiar with methods of sealing and sterilizing lens packages.

[0162] Although various embodiments of the present invention have been described using specific terms, devices, and methods, such description is for illustrative purposes only. The words used are words of description rather than words of limitation. It is to be understood that changes and variations may be made by those skilled in the art without departing from the spirit or scope of the present invention, as set forth in the following claims. In addition, it is to be understood that aspects of the various embodiments may be interchanged, either in whole or in part, or may be combined and / or used together in any manner, as exemplified below:

[0163] 1. (1) a polysiloxane segment comprising dimethylsiloxane units and aryl-containing siloxane units, each of which has one methyl substituent and one organic substituent, each of which has at least one aryl moiety bonded to a Si atom via a linker having at least two (preferably three) carbon atoms and up to 45 carbon atoms; (2) an ethylenically unsaturated group; 1. A polysiloxane vinyl crosslinker comprising: 2. A refractive index of at least 1.48 and a T of less than or equal to about 0°C g 2. The polysiloxane vinyl crosslinker of embodiment 1, having the formula: 3. The polysiloxane vinyl crosslinker of embodiment 2 having a refractive index of at least 1.51. 4. The polysiloxane vinyl crosslinker of embodiment 2 having a refractive index of at least 1.54. 5. The polysiloxane vinyl crosslinker of embodiment 2 having a refractive index of at least 1.57. 6. T below approximately -5.0°C g The polysiloxane vinyl crosslinker according to any one of embodiments 1 to 5, having the formula: 7. T below approximately -10.0°C g The polysiloxane vinyl crosslinker according to any one of embodiments 1 to 5, having the formula: 8. T below approximately -20.0°C g The polysiloxane vinyl crosslinker according to any one of embodiments 1 to 5, having the formula: 9. The polysiloxane vinyl crosslinker of any one of embodiments 1-5, wherein the polysiloxane segments contain at least 30 mole percent aryl-containing siloxane units. 10. The polysiloxane vinyl crosslinker of any one of embodiments 1-5, wherein the polysiloxane segments contain at least 40 mole percent aryl-containing siloxane units. 11. The polysiloxane vinyl crosslinker of any one of embodiments 1-5, wherein the polysiloxane segments contain at least 50 mole percent aryl-containing siloxane units. 12. The polysiloxane vinyl crosslinker of any one of embodiments 1-5, wherein the polysiloxane segments contain at least 60 mole percent aryl-containing siloxane units. 13. The polysiloxane vinyl crosslinker of any one of embodiments 1-5, wherein the polysiloxane segments comprise at least 70 mole percent aryl-containing siloxane units. 14. The polysiloxane vinyl crosslinker of any one of embodiments 1 to 13, having a number average molecular weight of at least 1000 Daltons. 15. The polysiloxane vinyl crosslinker of any one of embodiments 1 to 14, having a number average molecular weight of about 1,500 Daltons to about 100,000 Daltons. 16. The polysiloxane vinyl crosslinker of any one of embodiments 1 to 14, having a number average molecular weight of about 2,000 Daltons to about 80,000 Daltons. 17. The polysiloxane vinyl crosslinker of any one of embodiments 1 to 14, having a number average molecular weight of about 2,500 Daltons to about 60,000 Daltons. 18. The polysiloxane vinyl crosslinker according to any one of the preceding embodiments, defined by formula (1): [ka] (In the formula: υ1 is an integer from 1 to 400; ω1 is an integer from 1 to 800; E1 is [ka] is a monovalent radical of; R0 is hydrogen or methyl; a1 is zero or 1; X0 is O or NR N1 and; R N1 is hydrogen or C1-C6 alkyl; L0 is a C2-C8 alkylene divalent radical or -LO '-X1-L0'-, [ka] is a divalent radical of; L0' is a C2-C8 alkylene divalent radical; L0″ is a C3-C8 alkylene divalent radical; X1 is -O-, -NR N1 -, -NHCOO-, -OCONH-, -CONR N1 - or -NR N1 CO-; q1 is an integer from 1 to 10; AR is an aryl radical; L AR teeth, [ka] is a divalent radical of; L e -CH2-CH2-, -CH2-CHR O -R1-, -CH2-CHR O -R1-O-, -CH2-CHR O -R1-O-R2-, -C3H6-O-R2-, -C3H6-O-R2-O-, [ka] is a divalent radical of; a2 is zero, 1 or 2; a3 is zero or 1; R1 is a linear or branched C1-C alkoxy group, a hydroxyl group, a carboxyl group, an amino group, an oxo group, or a combination thereof, which may be optionally substituted with a C1-C4 alkoxy group, a hydroxyl group, a carboxyl group, an amino group, an oxo group, or a combination thereof. 10 is an alkylene divalent radical; R2 is a linear or branched C1-C 10 is an alkylene divalent radical; R3 is a direct bond or a linear or branched C1-C4 alkylene divalent radical; X AR and each X2, independently of the others, is a covalent bond, a linear or branched C1-C4 alkylene divalent radical, or -O-, -S-, [ka] , -NR N2 -, -NHCOO-, -OCONH-, -NHCONR N2 -, -NR N2 CONH-, [ka] , -CONR N2 -, -NR N2 CO-, [ka] -NHCOS-, -SCONH-, -COO-, or -OCO- covalent bond; R N2 is hydrogen, linear or branched C1-C6 alkyl, cyclohexyl, cyclopentyl, substituted or unsubstituted phenyl, or substituted or unsubstituted phenyl-C1-C6 alkyl; Each L x are each independently a linear or branched C1-C alkyl group which may optionally have one or more hydroxyl, C1-C4 alkoxy or C1-C4 acylamino groups; 10 An alkylene divalent radical, -CH2-CHOH-CH2-O-R4-O-CH2-CHOH-CH2-; [ka] or a divalent radical obtained by removing two hydrogen atoms from two different atoms of a hydrocarbon having up to 20 carbon atoms, optionally bearing one or more hydroxyl or 1-C4 alkoxy groups, and comprising at least one divalent radical selected from the group consisting of a cycloalkylene radical, a substituted cycloalkylene radical, a phenylene radical, a substituted phenylene radical, a cycloheteroalkylene radical, and a substituted cycloheteroalkylene radical; Each R, R, and R is independently a linear or branched C1-C aryl group having zero or one hydroxyl group. 10 (an alkylene divalent radical). 19. The polysiloxane vinyl crosslinker according to embodiment 18, wherein in formula (1), υ1 is an integer from 3 to 350. 20. The polysiloxane vinyl crosslinker according to embodiment 18, wherein in formula (1), υ1 is an integer from 5 to 300. 21. The polysiloxane vinyl crosslinker according to embodiment 18, wherein in formula (1), υ1 is an integer from 10 to 250. 22. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 22, wherein in formula (1), ω1 is an integer from 5 to 700. 23. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 22, wherein in formula (1), ω1 is an integer from 10 to 600. 24. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 22, wherein in formula (1), ω1 is an integer from 15 to 500. 25. The polysiloxane vinyl crosslinker of any one of embodiments 18 to 24, wherein in formula (1), a1 is zero. 26. The polysiloxane vinyl crosslinker of embodiment 25, wherein in formula (1), X0 is O. 27. In equation (1), X0 is NR N1 26. The polysiloxane vinyl crosslinker of embodiment 25, wherein 28. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 27, wherein in formula (1), ω1 / (υ1+ω1) is from about 0.30 to about 0.95. 29. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 27, wherein in formula (1), ω1 / (υ1+ω1) is from about 0.40 to about 0.90. 30. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 27, wherein in formula (1), ω1 / (υ1+ω1) is about 0.50 to about 0.90. 31. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 27, wherein in formula (1), ω1 / (υ1+ω1) is about 0.60 to about 0.85. 32. The polysiloxane vinyl crosslinker according to any one of embodiments 18 to 31, wherein in formula (1), AR is a phenyl group, a substituted phenyl group, a naphthyl group, a substituted naphthyl group, an anthracenyl group, a substituted anthracenyl group, a phenanthryl group, or a substituted phenanthryl group. 33. In equation (1), AR is [ka] (In the formula, R7, R8, R9, R 10 , R 11 , R 12 , and R 13 are each independently a monovalent radical of H, Cl, Br, F, CF3, CCl3, C1-C5 alkyl, C1-C5 alkoxy, C2-C5 acyloxy, OH, phenyl, phenoxy, benzyloxy, phenylcarbonyl, phenoxycarbonyl, phenylcarboxy (phenylcarbonyloxy), or naphthyl. 34. An insert made from a hydrophobic crosslinked polymeric material comprising repeat units of the polysiloxane vinyl crosslinker described in any one of embodiments 1 to 33. 35. An implantable silicone hydrogel contact lens comprising a silicone hydrogel bulk material and an insert as described in embodiment 34, wherein the insert is completely or partially embedded within the silicone hydrogel bulk material. 36. A silicone hydrogel contact lens comprising a silicone hydrogel bulk material comprising repeat units of the polysiloxane vinyl crosslinker described in any one of embodiments 1 to 33.

[0164] The above disclosure will enable those skilled in the art to carry out the present invention.Various modifications, variations and combinations can be made to the various embodiments described herein.In order to better enable the reader to understand specific embodiments and their advantages, reference to the following examples is proposed.It is intended that the present specification and examples are considered to be illustrative. EXAMPLES

[0165] Example 1 Oxygen permeability measurement Unless otherwise stated, the oxygen permeability (Dk / t) of the lens and lens material, the intrinsic (or edge-corrected) oxygen permeability (Dk i Or Dk c ) is measured according to the procedure described in ISO 18369-4.

[0166] equilibrium water content The equilibrium water content (EWC) of a contact lens is measured as follows. The amount of water (expressed as weight percent) present in hydrated hydrogel contact lenses that are fully equilibrated in saline is measured at room temperature. The lenses are quickly stacked and the lens stack is transferred to an aluminum pan on an analytical balance after wiping the lenses on a cloth. The number of lenses for each sample pan is typically five. The hydrated weight of the pan + lenses is recorded. Cover the pan with aluminum foil. Place the pan in a laboratory oven at 100±2°C to dry for 16-18 hours. Remove the pan + lenses from the oven and cool in a desiccator for at least 30 minutes. Remove only one pan from the desiccator and discard the aluminum foil. Weigh the pan + dry lens sample on an analytical balance. Repeat for all pans. The wet and dry weights of the lens sample can be calculated by subtracting the weight of the empty weighing pan.

[0167] Elasticity The storage modulus (Young's modulus) of the inserts is determined using a TA RSA-G2 DMA (Dynamic Mechanical Analyzer). The inserts are cut into 3.08 mm wide strips using a Precision Concept dry lens cutter. Five thickness values ​​are measured within a 6.5 mm gauge length. The strips are attached to the instrument using metal grips. An oscillatory temperature ramp test using a linear heating rate of 10°C to 50°C at 2°C / min is applied to the inserts to monitor the material's response to temperature increase at a constant frequency of 1 Hz, constant amplitude of 0.5% strain and a sampling rate of 10.0 pts / s. The storage modulus (E'), loss modulus (E") and tan δ data are calculated by TRIOS software.

[0168] The elastic modulus of contact lenses is measured using an MTS Insight instrument. Contact lenses are first cut into 3.12 mm wide strips using a Precision Concept two-stage cutter. Five thickness values ​​are measured within a 6.5 mm gauge length. The strips are attached to the instrument grips and submerged in PBS (phosphate buffered saline) at a controlled temperature of 21±2° C. Typically, a 5 N load cell is used for testing. A constant force and rate is applied to the sample until it breaks. Force and displacement data are collected by the TestWorks software. The elastic modulus value is calculated by the TestWorks software and is the slope or tangent of the stress versus strain curve near zero elongation in the elastic deformation region.

[0169] Refractive index The refractive index (RI) of the inserts is determined with an Abbe transmission laboratory refractometer Reichert Abbe Mark III at 25° C. The inserts are fully equilibrated in PBS saline prior to the measurements.

[0170] The refractive index (RI) of the polysiloxane vinyl crosslinker is determined by a Rudolph Research analytical refractometer (Model J357) at 20° C. The RI of distilled water (RI of 1.33299 at 20.0° C.) is used as a standard and is run before and after the measurement of the polysiloxane vinyl crosslinker.

[0171] Glass transition temperature The glass transition temperature (Tg) of the insert is defined as the peak of tan δ from the dynamic heating test by using a TA RSA-G2 DMA (Dynamic Mechanical Analyzer).

[0172] According to the present application, the glass transition temperature (Tg) of a polysiloxane vinyl crosslinker is the midpoint temperature of a differential scanning calorimetry diagram obtained using differential scanning calorimetry (DSC). Figure 1 shows a DSC diagram obtained for a polysiloxane vinyl crosslinker of the present invention, characterized by its onset temperature, midpoint temperature, inflection temperature, and end temperature.

[0173] Delamination Implantable silicone hydrogel contact lenses are tested for potential delamination using an Optimec instrument or Optical Coherence Tomography (OCT).

[0174] Regardless of the evaluation method, the contact lenses are staged for a minimum of 12 hours at room temperature after the autoclave run and before the delamination study.

[0175] After the required staging time has been met, the fully hydrated contact lens is placed into the "V" graticule assembly of the Optimec instrument (Model JCF; OPTIMEC England). After the contact lens has set under the influence of gravity, the front surface of the contact lens is carefully examined for any signs of circular patterns. Delamination will show up as a circular pattern on the Optimec image.

[0176] OCT (Thorlabs Spectral Domain Optical Coherence Tomography (Model-II) can also be utilized to study delamination. OCT allows non-invasive imaging of contact lenses to obtain high resolution cross-sectional images. For this purpose, after meeting the minimum staging requirements, the contact lens is removed from its blister and immersed in PBS solution for a minimum of 30 minutes until equilibration. A cuvette with a "V" block feature is then filled approximately 3 / 4 with fresh PBS solution and the contact lens is transferred to the cuvette using a Q-tip. The lens is allowed to float freely in the "V" shape at the bottom of the cuvette and the entire contact lens is scanned in 10 degree increments. Delamination appears in the OCT image as air pockets at the spacing surfaces of the insert and carrier.

[0177] chemicals In the following examples, the following abbreviations are used: BzA stands for benzyl acrylate; BzMA stands for benzyl methacrylate; DVBz stands for divinylbenzene; p-STTMS stands for styryltrimethoxysilane; PETA stands for pentaerythritol tetraacrylate; TrisMA stands for 3-[tris(trimethylsiloxy)silyl]propyl methacrylate; D6 stands for monobutyl terminated monomethacryloxypropyl terminated polydimethylsiloxane (MW 600-800 g / mol, from Gelest); D MA stands for N,N-dimethylacrylamide; MMA stands for methyl methacrylate; TEGDMA stands for triethylene glycol dimethacrylate; Vazo-67 stands for 2,2'-azobis(2-methylbutyronitrile); Ominirad-1173 stands for a photoinitiator made from 2-hydroxy-2-methyl-1-phenylpropanone; Nobloc is 2-[3-(2H-benzotriazol-2-yl)-4-hydroxyphenyl]ethyl methacrylate from Aldrich; RB247 is Reactive Blue 247 (2-propenoic acid, 2-methyl-,1,1'-[(9,10-dihydro-9,10-dioxo-1,4-anthracenediyl)bis(imino-2,1-ethanediyl)]) ester); TAA represents tert-amyl alcohol; PrOH represents 1-propanol; IPA represents isopropanol; PPG represents poly(propylene glycol); EGBE represents ethylene glycol butyl ether; PBS has a pH of 7.2±0.2 at 25°C and contains about 0.044% by weight NaH2PO4·H2O, about 0. represents a phosphate buffered saline solution containing 388 wt.% Na2HPO2HPO4·2H2O, and about 0.79 wt.% NaCl; wt.% represents weight percent; "H4" macromer represents a di-methacryloyloxypropyl terminated polysiloxane of formula (A) shown below (Mn about 11.3K-12.3 Kg / mol, OH content about 1.82-2.01 meq / g); "HA" macromer represents a di-methacryloyloxypropyl terminated polysiloxane of formula (A) shown below (Mn about 6.8 Kg / mol, OH content about 1.2 meq / g). [ka]

[0178] Example 2 The hydrosiloxane-containing polysiloxanes (precursors for making the polysiloxane vinyl crosslinkers of the present invention) are prepared according to the procedure shown in Scheme 1. [ka]

[0179] Synthesis of hydrosiloxane-containing polysiloxane (Mn about 5KD) 602.05 g of octamethylcyclotetrasiloxane (D4), 510.32 g of 1,3,5,7-tetramethyl-cyclotetrasiloxane (D4H), and 92.81 g of 1,3-bis(3-methacryloxypropyl)tetramethyldisiloxane are weighed and premixed in a flask and then placed in a 2 L jacketed reactor equipped with a mechanical motor, a thermocouple, and a nitrogen flow adapter. 2.4 g of triflic acid is then added to the stirred reaction mixture via pipette. The reaction is stirred at 25° C. for approximately 16 hours. After the reaction is complete, the solution is diluted with 1000 mL of toluene and then neutralized with a solid base, then stirred for 1 hour. The final mixture is filtered using a 0.45 micron glass microfiber filter. At this point, BHT and MEHQ inhibitors are added (250 ppm each). The polymer solution is concentrated on a rotary evaporator and then the residual solvent is removed under low vacuum. The resulting precursor was not purified and had a number average molecular weight of about 5,000 g / mol and an average x of about 31 ( 1 HNMR), and the average y is about 32 ( 1 HNMR).

[0180] Synthesis of hydrosiloxane-containing polysiloxane (Mn about 3KD) 100.19 g of octamethylcyclotetrasiloxane (D4), 247.39 g of 1,3,5,7-tetramethylcyclotetrasiloxane (D4H), and 51.32 g of 1,3-bis(3-methacryloxypropyl)-tetramethyldisiloxane are weighed and premixed in a flask and then placed in a 1 L jacketed reactor equipped with a mechanical motor, a thermocouple, and a nitrogen flow adapter. 0.8 g of triflic acid is then added to the stirred reaction mixture via pipette. The reaction is stirred at 25° C. for approximately 16 hours. After the reaction is complete, the solution is diluted with 200 mL of toluene and then neutralized with solid base, then stirred for 1 hour. The final mixture is filtered using a 0.45 micron glass microfiber filter. At this point, BHT and MEHQ inhibitors are added (250 ppm each). The polymer solution is concentrated on a rotary evaporator and then the residual solvent is removed under low vacuum. The resulting precursor was not purified and had a number average molecular weight of about 3,000 g / mol and an average x of about 9.4 ( 1 1 H NMR), and the average y is about 28.1 ( 1 1 H NMR).

[0181] Example 3 Synthesis of high refractive index polysiloxane vinyl crosslinkers: [ka] A 500 mL jacketed reactor equipped with a mechanical stirrer, thermocouple, nitrogen inlet, septum, and condenser was warmed to 80 °C and purged with nitrogen at a rate of 100 mL / min for 30 min. Allyl phenyl ether (about 158.62 g, i.e., 2:1 molar ratio relative to hydrosiloxane units), toluene (40 mL), and about 88.1 μL (about 25 ppm relative to precursor) of Karstedt catalyst solution were charged to the reactor. The nitrogen flow rate was reduced to 50 mL / min. Hydrosiloxane-containing polysiloxane (Mn about 3 KD) (about 60.00 g) prepared in Example 2, MEHQ inhibitor (0.0085 g), and toluene (60-80 mL) were placed in a beaker and stirred for 10 min until MEHQ was dissolved, and then loaded into two 100 mL Hamilton gas-tight syringes equipped with plastic cannulas. Each syringe containing approximately 70 mL of polymer solution is fixed to a Harvard PHD Infusion syringe pump and the feed line is inserted into the reactor via a rubber septum. A solution of hydrosiloxane-containing polysiloxane in toluene is added via the syringe pump over 5 h (rate 0.2333 mL / min). The temperature of the reactor is maintained at 80 ± 2 °C for the duration of the reaction. After the addition of the polymer, the reaction mixture is stirred for an additional hour. After this time, an IR scan of the crude reaction mixture confirms that the Si-H bonds have been completely consumed. The reaction mixture is then cooled to room temperature and the crude polymer is purified by thin-film distillation (the hot finger temperature reaches 100 °C by water reflux and the vacuum is maintained at 1.3-1.9 mbar throughout the process). The collected polymer fraction is cooled to a T of -48 °C. g and a refractive index of 1.51553 (at 20°C). 1 The 1 H NMR spectrum does not show the presence of allyl phenyl ether.

[0182] The hydrosiloxane-containing polysiloxane (Mn about 5KD) prepared in Example 2 is also used to prepare a polysiloxane vinyl crosslinker according to the above procedure. The resulting polysiloxane vinyl crosslinker has a refractive index of 1.49617 (20°C).

[0183] Example 4 In this example, the synthesis of two high refractive index polysiloxane vinyl crosslinkers (macromers) is described. A 500 mL jacketed reactor equipped with a mechanical stirrer, thermocouple, nitrogen inlet, septum, and condenser is charged with phenothiazine (0.096 g), allyl benzyl ether (about 117.9 g) in a molar ratio of about 1.6:1 relative to the hydrosiloxane units, and toluene (59 mL). The reaction mixture is purged with nitrogen at a rate of 100 mL / min for 30-40 min at room temperature. Then, about 111.2 μL (about 40 ppm with respect to the precursor) of Karstedt catalyst solution is charged to the reactor, the reactor is warmed to 95 °C, and the nitrogen flow is reduced to 50 mL / min.

[0184] The hydrosiloxane-containing polysiloxane (Mn=about 3KD; x=about 9; y=about 28) (about 48.0 g) prepared in Example 2 and toluene (24 mL) are placed in a beaker, stirred for 10 minutes, and placed in a 100 mL Hamilton gas tight syringe equipped with a plastic cannula. The syringe containing about 72 mL of the polymer solution is secured to a Harvard PHD Infusion syringe pump, and the feed line is inserted into the reactor through a rubber septum. The solution of the hydrosiloxane-containing polysiloxane in toluene is added via the syringe pump over 2 hours (at a rate of 0.6 mL / min). The temperature of the reactor is maintained at 95±2° C. for the duration of the reaction. After the addition of the polymer, the reaction mixture is stirred for an additional hour. After this time, an IR scan of the crude reaction mixture confirms that the Si-H bonds are completely consumed. The reaction mixture is then cooled to room temperature, and the crude polymer is purified by extraction with a cyclohexane / acetonitrile system. The polymer dissolves in cyclohexane (bottom layer) and the excess allyl benzyl ether partitions into the acetonitrile layer. Typically, five extractions are performed to completely remove the allyl benzyl ether. After extraction, 83.7 g of a clear, viscous, nearly odorless, amber liquid is recovered.

[0185] During optimization of the hydrosilylation reaction, it is noted that when allyl phenyl ether is used, a significant loss of terminal methacrylate double bonds, reaching up to 40%. Varying the reaction conditions, e.g., temperature, stoichiometry, order of addition, time of addition, etc., does not improve the outcome of the reaction. Increasing the inhibitor (phenothiazine) level up to 6000 ppm does not reduce the loss of double bonds. This suggests that the methacrylate groups compete with the allyl component in the hydrosilylation reaction with the silane (Si-H) to form C-Si bonds. As a result of this competition, a significant increase in the viscosity of the final macromer is observed (Table 1). In extreme cases, the final polymer may become too thick to be blended into formulations. However, very different results are observed when allyl phenyl ether is replaced by allyl benzyl ether. A very slight, negligible loss of methacrylate double bonds is observed by NMR. The viscosity of the final macromer is also lower, making it easier to handle. The results are reported in Table 1.

[0186] [Table 1]

[0187] Example 5 Insert Formulation A polymerizable composition for making the inserts (insert formulation) is prepared in air at room temperature by blending all the components (ingredients) in their desired amounts (in parts by weight) to have the composition shown in Table 2.

[0188] [Table 2]

[0189] Cast Molding Inserts The lens formulation is purged with nitrogen for 30-35 minutes at room temperature. The N2 purged polymerizable composition (30-40 mg) is introduced into a polypropylene mold, and the mold is sealed and placed in an oven. The oven is configured as follows: a nitrogen supply is connected to the oven through a high flow volumetric controller capable of controlling the flow rate of nitrogen through the oven; a vacuum pump is connected in the oven exhaust line to control the oven differential pressure.

[0190] The insert formulation (polymerizable composition) in the mold is heat cured in an oven under the following conditions: 25°C, 80 scfh (standard cubic feet per hour) N2 flow rate, hold for about 30 minutes; 25°C to 55°C at about 7°C / min; 55°C, 40 scfh N2 flow rate, hold for about 30 minutes; 55°C to 80°C at about 7°C / min; 80°C, 40 scfh N2 flow rate, hold for about 30 minutes; 80°C to 100°C at about 7°C / min; 100°C, 40 scfh N2 flow rate, hold for about 30 minutes. The mold is opened and the molded insert is removed from the mold.

[0191] The inserts may or may not be extracted. The following procedure is used to extract the inserts (if necessary): First, the inserts are extracted with PrOH for about 3 hours, rinsed twice with deionized water for about 10 minutes, and dried in a vacuum oven at 50° C. and 26 mmHg for 1 hour. The inserts obtained from insert formulation #1 have an RI of about 1.50; the inserts obtained from insert formulation #2 have an RI of about 1.51; and the inserts obtained from insert formulation #3 have an RI of about 1.55.

[0192] SiHy Lens Formulation The two SiHy lens formulations are prepared at room temperature in air by blending all the components (materials) in their desired amounts (in parts by weight) to have the compositions shown in Table 3.

[0193] [Table 3]

[0194] Fabrication of SiHy contact lenses Thermally or actinically cast SiHy contact lenses are made as follows.

[0195] Mold Assembly: A certain amount (approximately 50-60 mg) of the SiHy lens formulation prepared above is injected into a polypropylene female mold half, then a polypropylene male mold half is placed over the female mold half and the molds are tightly closed to form a mold assembly.

[0196] Heat Curing. The molded assembly (i.e., the closed mold with the SiHy lens formulation therein) is heat cured in an oven under the following conditions: 25° C., 80 scfh N2 flow rate, hold for about 30 minutes; 25° C. to 55° C. at about 7° C. / min ramp rate; 55° C. to 80° C. at about 7° C. / min ramp rate; 80° C., 40 scfh N2 flow rate, hold for about 30 minutes; 80° C. to 100° C. at about 7° C. / min ramp rate; 100° C., 40 scfh N2 flow rate, hold for about 30 minutes.

[0197] Actinic Radiation Curing. The mold assembly (i.e., the closed mold with the SiHy lens formulation #5 inside) was exposed to approximately 1 mW / cm 2 Fully cure using a double-sided UV curing oven (Wicked Engineering, UV LED Module9W 365nm / 405nm) with an intensity of 100000000000000 for 10 minutes.

[0198] Demolding and Lens Removal. The lens molds, each with a SiHy contact lens molded therein, are mechanically opened. The molded SiHy contact lenses are attached to either male or female mold halves. The molded SiHy contact lenses attached to the male mold halves are removed using an ultrasonic device; the molded SiHy contact lenses attached to the female mold halves are manually removed from the female mold halves to which the lenses were attached.

[0199] Post-Lens Removal Process. The removed raw SiHy contact lenses can be extracted with a 50:50 mixture of propylene glycol:water. Preferably, the removed raw SiHy contact lenses undergo the following extraction / hydration, coating, autoclave process: the raw SiHy contact lenses are immersed in a bath containing deionized water or an aqueous solution of Tween 80 (500 PPM) for about 60 minutes, then in a bath containing an aqueous solution of polyacrylic acid (PAA, Mw 450K) at a concentration of about 0.1% by weight at 40°C for about 120 minutes, then in a bath containing PBS solution at room temperature for about 60 minutes; packaged / sealed in polypropylene lens packaging shells (or blisters) (one lens per shell) with 0.65 mL of in-package-coating packaging saline prepared according to the procedure described in Example 19 of US Patent No. 8,480,227; and finally autoclaved at 121°C for about 45 minutes. The resulting SiHy contact lenses each have a hydrogel coating thereon.

[0200] The lens properties of the resulting SiHy contact lenses were determined according to the procedures described in Example 1 and are reported in Table 4.

[0201] [Table 4]

[0202] Fabrication of fully implantable SiHy contact lenses Thermally or actinically cast implantable SiHy contact lenses are made as follows.

[0203] Mold Assembly: The insert prepared above is placed in the central area of ​​the molding surface of a female mold half (made of polypropylene) preferably having three or more spikes distributed in a circle with a diameter sufficient to accommodate the insert to fix the position of the insert on the molding surface, a certain amount (about 50-60 mg) of the SiHy lens formulation prepared above is injected into the female mold half, the insert is allowed to soak, then a male mold half made of polypropylene is placed on top of the female mold half, and the mold is tightly closed to form a mold assembly.

[0204] Heat Curing The mold assemblies (i.e., the closed molds each containing an insert immersed in a SiHy lens formulation) are heat cured according to the procedure described above for producing SiHy contact lenses.

[0205] Actinic Radiation Curing: The mold assemblies (i.e., the closed molds each containing an insert dipped in SiHy Lens Formulation #5) are fully cured by actinic radiation according to the procedure described above for producing SiHy contact lenses.

[0206] Demolding and Lens Removal Demolding and lens removal are performed as described above for the preparation of SiHy contact lenses.

[0207] Post-Lens Removal Processing: The removed raw implantable SiHy contact lenses are subjected to the extraction / hydration, coating, and autoclaving processes described above to produce SiHy contact lenses. The resulting implantable SiHy contact lenses each have a hydrogel coating thereon.

[0208] The resulting implantable SiHy contact lenses are examined under a microscope (i.e., using OCT according to the procedure described in Example 1) for possible delamination. No delamination is observed. The implantable SiHy contact lenses exhibit a well-defined lens shape without distortion after lens removal, extraction, coating, hydration, and autoclaving. Both the insert and bulk SiHy material have minimal swelling ratios upon hydration, which is believed to result in minimal internal stresses and therefore excellent shape stability over time. Characterization of the implantable SiHy contact lenses is reported in Table 5.

[0209] [Table 5]

[0210] By having a difference of at least about 0.07, the implantable SiHy contact lenses of the present invention can be particularly useful in the manufacture of diffractive multifocal contact lenses.

[0211] Fabrication of partially implantable SiHy contact lenses Thermally or actinically cast implantable SiHy contact lenses are made as follows.

[0212] The insert-forming composition prepared above (insert formulation #2) is purged with nitrogen for 30-35 minutes at room temperature. A specific volume (e.g., 30-40 mg) of the N2 purged insert-forming composition is placed in the center of the molding surface of a female lens mold half made of polypropylene. The molding surface defines the anterior surface of the contact lens to be molded. The female lens mold half containing the insert-forming composition therein is closed with a male insert mold half made of polypropylene and designed to have an overflow groove into which excess insert-forming composition is forced upon closing to form a first mold assembly. The male insert mold half has a molding surface that defines the posterior surface of the insert to be molded. The oven is configured as follows: a nitrogen supply is connected to the oven through a high-flow volumetric controller capable of controlling the flow rate of nitrogen through the oven; and a vacuum pump is connected at the oven exhaust line to control the oven differential pressure.

[0213] The insert molding composition in the first mold assembly is heat cured in an oven under the following conditions: room temperature to 55°C at a rate of about 7°C / min; hold at 55°C for about 30-40 minutes; ramp from 55°C to 80°C at a rate of about 7°C / min; hold at 55°C for about 30-40 minutes; ramp from 80°C to 100°C at a rate of about 7°C / min; hold at 100°C for about 30-40 minutes. Open the first mold assembly. The molded insert is attached to the central region of the molding surface of the female lens mold half.

[0214] The lens forming composition (SiHy Lens Formulation #1) prepared above is purged with nitrogen for 30-35 minutes at room temperature. A specific volume (e.g., 50-60 mg) of the N2 purged lens forming composition is placed onto the molded insert attached to the central portion of the molding surface of a female lens mold half. The female lens mold half with the insert and lens forming composition attached thereon is closed with a male lens mold half made of polypropylene and designed to have an overflow groove into which excess insert forming composition is forced upon closing to form a second mold assembly. The male lens mold half has a molding surface that will be molded and define the posterior surface of a contact lens. The oven is configured as follows: a nitrogen supply is connected to the oven through a high flow volumetric controller capable of controlling the flow rate of nitrogen through the oven; and a vacuum pump is connected at the oven exhaust line to control the differential pressure of the oven.

[0215] The closed second mold assemblies, each containing a mold insert immersed in the lens forming composition within the lens molding cavity, are heat cured in an oven under the following conditions: room temperature to 55° C. at a rate of about 7° C. / min; hold at 55° C. for about 30-40 minutes; 55° C. to 80° C. at a rate of about 7° C. / min; hold at 55° C. for about 30-40 minutes; 80° C. to 100° C. at a rate of about 7° C. / min; hold at 100° C. for about 30-40 minutes. The second mold assemblies, each having a molded green implantable silicone hydrogel contact lens therein, are mechanically opened. The molded green implantable silicone hydrogel contact lenses are attached to either the male or female mold half. The molded raw implantable silicone hydrogel contact lens attached to the male mold half is removed using an ultrasonic device; the molded raw implantable silicone hydrogel contact lens attached to the female mold half is manually removed from the female mold half to which the lens was attached.

[0216] The removed raw implantable SiHy contact lenses are subjected to the extraction / hydration, coating, and autoclaving processes described above to produce SiHy contact lenses, each of which has a hydrogel coating thereon.

[0217] The resulting partially implanted SiHy contact lenses are examined for possible delamination using OCT according to the procedure described in Example 1. No delamination is observed. The implanted SiHy contact lenses show a well-defined lens shape without distortion after lens removal, extraction, coating, hydration, and autoclaving. Both the insert and bulk SiHy materials have minimal swelling ratios upon hydration, which is believed to result in minimal internal stresses and therefore excellent shape stability over time. Characterization of the implanted SiHy contact lenses is reported in Table 6.

[0218] [Table 6]

[0219] By having a difference of at least about 0.08, the partially implantable SiHy contact lenses of the present invention can be particularly useful in the manufacture of diffractive multifocal contact lenses.

[0220] All publications, patents, and patent publications cited herein above are hereby incorporated by reference in their entirety.

Claims

1. (1) a polysiloxane segment comprising a dimethylsiloxane unit and an aryl-containing siloxane unit, the aryl-containing siloxane unit having one methyl substituent and one organic substituent, the one organic substituent having at least one aryl moiety bonded to a Si atom via a linker having at least two carbon atoms and up to 45 carbon atoms; (2) an ethylenically unsaturated group; A polysiloxane vinyl crosslinker comprising: The polysiloxane vinyl crosslinker has a refractive index of at least 1.48 and a T g of less than or equal to 0° C. the polysiloxane segments comprise at least 30 mole percent aryl-containing siloxane units; the polysiloxane vinyl crosslinker has a number average molecular weight of at least 1000 Daltons; Formula (1): 【Chemistry 1】 (In the formula: υ1 is an integer from 1 to 400; ω1 is an integer from 1 to 800; E 1 is 【Chemistry 2】 is a monovalent radical of R 0 is hydrogen or methyl; a1 is zero or 1; X 0 is O or NR N1 ; R N1 is hydrogen or C 1 -C 6 alkyl; L 0 is a C 2 -C 8 alkylene divalent radical or -L O '-X 1 -L 0 ''-; 【Chemistry 3】 is a divalent radical of L 0 ' is a C 2 -C 8 alkylene divalent radical; L 0 ″ is a C 3 -C 8 alkylene divalent radical; X 1 is —O—, —NR N1 —, —NHCOO—, —OCONH—, —CONR N1 — or —NR N1 CO—; q1 is an integer from 1 to 10; AR is an aryl radical; LAR is, 【Chemistry 4】 is a divalent radical of L e is -CH 2 -CH 2 -, -CH 2 -CHR O -R 1 -, -CH 2 -CHR O -R 1 -O-, -CH 2 -CHR O -R 1 -O-R 2 -, -C 3 H 6 -O-R 2 -, -C 3 H 6 -O-R 2 -O-, 【Chemistry 5】 is a divalent radical of a2 is zero, 1 or 2; a3 is zero or 1; R 1 is a linear or branched C 1 -C 10 alkylene divalent radical optionally substituted with C 1 -C 4 alkoxy, hydroxyl, carboxyl, amino, oxo, or combinations thereof; R 2 is a linear or branched C 1 -C 10 alkylene divalent radical; R 3 is a direct bond or a linear or branched C 1 -C 4 alkylene divalent radical; X AR and each X 2 independently represent a covalent bond, a linear or branched C 1 -C 4 alkylene divalent radical, or -O-, -S-, 【Chemistry 6】 , -NR N2 -, -NHCOO-, -OCONH-, -NHCONR N2 -, -NR N2 CONH-, 【Chemistry 7】 , -CONR N2 -, -NR N2 CO-, 【Chemistry 8】 , -NHCOS-, -SCONH-, -COO-, or -OCO- covalent bond; R N2 is hydrogen, linear or branched C 1 -C 6 alkyl, cyclohexyl, cyclopentyl, substituted or unsubstituted phenyl, or substituted or unsubstituted phenyl-C 1 -C 6 alkyl; Each L x is independently a linear or branched C 1 -C 10 alkylene divalent radical, optionally bearing one or more hydroxyl or C 1 -C 4 -alkoxy or C 1 -C 4 -acylamino groups, -CH 2 -CHOH-CH 2 -O-R 4 -O-CH 2 -CHOH-CH 2 -; 【Chemistry 9】 or a divalent radical obtained by removing two hydrogen atoms from two different atoms of a hydrocarbon having up to 20 carbon atoms, optionally bearing one or more hydroxyl or C 1 -C 4 -alkoxy groups, and comprising at least one divalent radical selected from the group consisting of a cycloalkylene radical, a substituted cycloalkylene radical, a phenylene radical, a substituted phenylene radical, a cycloheteroalkylene radical, and a substituted cycloheteroalkylene radical, Each R 4 , R 5 and R 6 is, independently of the others, a linear or branched C 1 -C 10 alkylene divalent radical having zero or one hydroxyl group. A polysiloxane vinyl crosslinker defined as:

2. 2. The polysiloxane vinyl crosslinker according to claim 1, wherein in formula (1), υ1 is an integer from 3 to 350.

3. The polysiloxane vinyl crosslinker according to claim 1 or 2, wherein in formula (1), ω1 is an integer of 5 to 700.

4. The polysiloxane vinyl crosslinker according to any one of claims 1 to 3, wherein in formula (1), a1 is zero.

5. In formula (1), X ０ The polysiloxane vinyl crosslinker of claim 4 , wherein

6. In formula (1), X ０ is NR Ｎ１ 5. The polysiloxane vinyl crosslinker of claim 4, wherein

7. The polysiloxane vinyl crosslinker according to any one of claims 1 to 6, wherein in formula (1), ω1 / (υ1+ω1) is 0.30 to 0.

95.

8. 8. The polysiloxane vinyl crosslinker according to claim 1, wherein, in formula (1), AR is a phenyl group, a substituted phenyl group, a naphthyl group, a substituted naphthyl group, an anthracenyl group, a substituted anthracenyl group, a phenanthryl group, or a substituted phenanthryl group.

9. In formula (1), AR is 【Chemistry 10】 (In the formula, R ７ , R ８ , R ９ , R １０ , R １１ , R １２ , and R １３ are each independently H, Cl, Br, F, CF ３ , CCl ３ , C １ ~C ５ Alkyl, C １ ~C ５ Alkoxy, C ２ ~C ５ acyloxy, OH, phenyl, phenoxy, benzyloxy, phenylcarbonyl, phenoxycarbonyl, phenylcarboxy (phenylcarbonyloxy), or naphthyl. The polysiloxane vinyl crosslinker of any one of claims 1 to 7, wherein the monovalent radical is

10. An insert made from a hydrophobic crosslinked polymeric material comprising repeat units of a polysiloxane vinyl crosslinker according to any one of claims 1 to 9.

11. 11. An implantable silicone hydrogel contact lens comprising a silicone hydrogel bulk material and the insert of claim 10, wherein the insert is fully or partially embedded within the silicone hydrogel bulk material.

12. A silicone hydrogel contact lens comprising a silicone hydrogel bulk material comprising repeat units of the polysiloxane vinyl crosslinker of any one of claims 1 to 9.