Sound boards and percussion instruments

Abstract

A sound bar (10) is provided with an elongated member having an elongated percussion surface (10a). The weight of a percussion-surface-side region (R), which is a region of unform thickness from the percussion surface (10a) of the elongated member, changes along the longitudinal direction of the percussion surface (10a).

Description

[Technical field]

[0001] The present invention relates to sound plates and percussion instruments. [Background technology]

[0002] Percussion instruments such as marimbas and xylophones have multiple sound plates as sound generating bodies. These sound plates emit sound when struck by a mallet. Wood such as rosewood, birch, paduk, and quince are used as materials for these sound plates. In addition, sound plates made by laminating wood and fiber-reinforced plastic sheets have been proposed to obtain excellent sound quality and durability against strikes (see Patent Document 1). [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Japanese Patent Publication No. 2003-84759 Summary of the Invention [Problem to be solved by the invention]

[0004] As described in Patent Document 1, conventional sound boards are formed by laminating multiple functional layers intended to enhance specific functions such as sound quality and strength. The overall size of conventional sound boards is controlled based on the quality of each functional layer so that the sound board can emit a sound in a desired range.

[0005] In response to this, the inventors of the present invention have conducted intensive research in order to gain new knowledge on how to increase the freedom in designing sound plates while focusing on the issues that sound plates have.

[0006] The present invention has been made based on the above circumstances, and an object of the present invention is to increase the degree of freedom in designing sound plates. [Means for solving the problem]

[0007] A soundboard in one embodiment of the present invention comprises a long member having a long striking surface, and the weight of a striking surface side region of the long member within an equal thickness range from the striking surface varies along the longitudinal direction of the striking surface.

[0008] The elongated member is impregnated with a different material in a thickness direction of the elongated member from the striking surface, and the amount of the different material impregnated varies along the longitudinal direction of the striking surface.

[0009] The impregnation depth of the different material monotonically increases or monotonically decreases from a central region in the longitudinal direction of the striking face of the elongated member toward both sides in the longitudinal direction.

[0010] In the striking surface side region, the density of the different material monotonically increases or decreases from a central region in the longitudinal direction of the striking surface toward both sides in the longitudinal direction.

[0011] The elongated member comprises a surface layer having the striking surface and a base that is directly or indirectly laminated to the surface of the surface layer opposite the striking surface, the specific gravity of the surface layer being different from the specific gravity of the base, and the thickness of the surface layer varying along the longitudinal direction of the striking surface.

[0012] The base is made of wood.

[0013] The base is a laminate in which a plurality of plate materials are laminated, and the lamination direction of the plurality of plate materials is perpendicular to the thickness direction of the base.

[0014] The surface layer includes oriented fibers.

[0015] The elongated member further includes an intermediate layer disposed between the surface layer and the base, the intermediate layer containing oriented fibers, and the direction of the fibers of the intermediate layer is perpendicular to the direction of the fibers of the surface layer in a planar view.

[0016] It is preferable that the thickness of the surface layer monotonically increases or monotonically decreases from a central region in the longitudinal direction of the hitting face to both sides in the longitudinal direction.

[0017] A percussion instrument in one embodiment of the present invention comprises a plurality of the sound plates, and at least two of the plurality of sound plates have different directions of increase and decrease in weight along the longitudinal direction of the striking surface in the striking surface side region, or the layer structures of the at least two sound plates are different. The layered structure of the at least two sound plates differs in weight at both ends of the elongated member in the longitudinal direction of the striking surface or in thickness of the elongated member in the central region in the longitudinal direction of the striking surface.

[0018] It is preferable that the material of the outermost layer on the striking surface side of all of the plurality of sound plates is the same.

[0019] In the present invention, "the weight of the striking surface side region changes along the longitudinal direction of the striking surface" means that the weight of the striking surface side region changes relatively along the longitudinal direction of the striking surface, and includes a configuration in which the weight of the striking surface side region changes continuously (gradually) as well as a configuration in which the weight of the striking surface side region changes stepwise. Also, "the fiber direction of the intermediate layer is perpendicular to the fiber direction of the surface layer in a plan view" means that the fiber direction of the intermediate layer (for example, the direction along the center of the wood if the intermediate layer contains wood) and the fiber direction of the surface layer are approximately perpendicular to each other in a plan view, and are not limited to a configuration in which the fiber direction of the intermediate layer and the fiber direction of the surface layer are strictly perpendicular to each other. Effect of the Invention

[0020] In one embodiment of the sound board of the present invention, the weight of the striking surface side area within an equal thickness range from the striking surface varies along the longitudinal direction of the striking surface, thereby increasing the design freedom in terms of sound quality, strength, overall thickness of the sound board, etc. [Brief description of the drawings]

[0021] [Figure 1] FIG. 1 is a schematic cross-sectional view of a sound plate according to one embodiment of the present invention, cut along a plane parallel to a side surface. [Diagram 2] FIG. 2 is a schematic cross-sectional view of the tone plate of FIG. 1 cut along a plane perpendicular to the side surface. [Diagram 3] FIG. 3 is a schematic plan view of the tone plate of FIG. [Figure 4] FIG. 3 is a schematic cross-sectional view corresponding to FIG. 1, showing an example of the surface layer of the tone plate of FIG. [Diagram 5] FIG. 5 is a schematic perspective view showing an example of a base for the tone plate of FIG. [Figure 6] FIG. 6 is a schematic cross-sectional view corresponding to FIG. 1, of a sound bar according to a different embodiment from the sound bar of FIG. [Figure 7] FIG. 7 is a schematic cross-sectional view corresponding to FIG. 1, of a sound bar according to a different embodiment from the sound bars of FIGS. [Figure 8] FIG. 8 is a schematic plan view of the tone plate of FIG. [Figure 9] FIG. 9 is a schematic diagram showing the striking surface side of the intermediate layer of the tone plate of FIG. [Figure 10] FIG. 10 is a schematic plan view showing a percussion instrument according to an embodiment of the present invention. [Figure 11] FIG. 11 is a schematic perspective view showing a sound board according to a different embodiment from the sound boards in FIGS. [Figure 12] FIG. 12 is a cross-sectional view of the tone plate of FIG. 11 taken along line AA. [Figure 13] FIG. 13 is a cross-sectional view of the tone plate of FIG. 11 taken along line BB. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0022] Hereinafter, the embodiments of the present invention will be described in detail with reference to the drawings as appropriate. It should be noted that the numerical values ​​described in this specification can be arbitrarily combined with the upper limit value and the lower limit value described. In this specification, all numerical ranges from the upper limit value to the lower limit value that can be combined are described as suitable ranges.

[0023] [First embodiment] <Sound plate> The sound board 10 in FIG. 1 and FIG. 2 has a long striking surface 10a. The weight of the striking surface side region R of the sound board 10, which is in a uniform thickness range from the striking surface 10a, changes along the longitudinal direction of the striking surface 10a. In other words, the weight of the region (striking surface side region R) between the striking surface 10a and a virtual surface parallel to the striking surface 10a, which is provided at a certain depth position from the striking surface 10a, increases and decreases along the longitudinal direction of the striking surface 10a. Note that the "striking surface side region in a uniform thickness range from the striking surface" refers to a region in the sound board 10 that is in a uniform depth range from the striking surface in the normal direction. The "striking surface" here refers to the main surface that produces sound when struck, and is composed of a flat surface, a curved surface, etc.

[0024] The sound plate 10 is used for percussion instruments such as marimba, xylophone, and vibraphone. Usually, these percussion instruments have a plurality of long sound plates. These sound plates have a striking surface that is struck by a mallet, and a concave portion is provided on the surface opposite to the striking surface. Generally, a sound plate for a high range is shorter in length in the longitudinal direction and has a larger overall thickness than a sound plate for a low range. The sound plate 10 in FIG. 1 can be used, for example, as a sound plate for a high range, although it is not particularly limited thereto.

[0025] The sound board 10 is a long member, and includes a surface layer 1 having a striking surface 10a, and a base 2 that is directly or indirectly laminated on the surface of the surface layer 1 opposite to the striking surface 10a. As described above, the sound board 10 has a striking surface side region R whose weight changes along the longitudinal direction of the striking surface 10a. In the sound board 10, the striking surface side region R can be an area sandwiched between the striking surface 10a and a virtual plane parallel to the striking surface 10a that passes through the part where the thickness of the surface layer 1 is maximum.

[0026] The sound plate 10 has a surface layer 1 laminated on a base 2. The sound plate 10 may have layers other than the surface layer 1 and the base 2, or may not have layers other than the surface layer 1 and the base 2. The surface layer 1 and the base 2 are fixed together using, for example, an adhesive.

[0027] The surface layer 1 and the base 2 have different specific gravities. The thickness of the surface layer 1 changes along the longitudinal direction of the striking surface 10a. By configuring the sound board 10 in this way, the weight of the striking surface side region R can be easily changed along the longitudinal direction of the striking surface 10a.

[0028] (surface) The surface layer 1 is a thin plate. The striking surface 10a constitutes the outermost surface of the sound board 10 that is struck with a mallet. The striking surface 10a is elongated, and more specifically, rectangular in plan view.

[0029] The material of the surface layer 1 is not particularly limited, and examples thereof include wood, resin, fiber-reinforced plastic (FRP), paper, metal, ceramic, elastomer, etc. The material of the surface layer 1 can be selected based on the sound quality required for the sound board 10. For example, a material containing oriented fibers is preferably used as the material of the surface layer 1. Examples of materials containing oriented fibers include wood, fiber-reinforced plastic, paper, etc. If the sound board 10 is intended to produce a woody sound, wood is used as the material of the surface layer 1.

[0030] The surface layer 1 may be provided as a functional layer that serves to increase the strength of the sound plate 10. In this case, the specific gravity of the surface layer 1 is greater than the specific gravity of the base 2, for example.

[0031] When the material of the surface layer 1 is wood, examples of the wood include rosewood, paduk, quince, maple, hard maple, hornbeam, beech, oak, matsuwa, mahogany, and birch.

[0032] When the material of the surface layer 1 is wood, the wood may be, for example, a board with a grain. For example, as shown in FIG. 3, the wood is a straight-grain board. By using a straight-grain board, the appearance of the sound board 10 can be improved. From the viewpoint of improving the appearance of the sound board 10, the grain of the wood is aligned along the longitudinal direction of the striking surface 10a. Note that "straight-grained" here refers to a sound board material cut so that the average angle of the annual rings is within the range of ±45° to the vertical (thickness direction of the surface layer) when viewed from the end of the wood (a cross section where the annual rings are seen as concentric circles).

[0033] As shown in FIG. 1, the thickness of the surface layer 1 decreases monotonically from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction. With this configuration, the strength and weight of the sound board 10 can be changed from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction in accordance with the thickness of the surface layer 1. For example, if the sound board 10 is used as a sound board for a high range, the sound quality, strength, and overall thickness of the sound board 10 can be easily adjusted by making the weight of the both sides in the longitudinal direction of the striking surface 10a smaller than that of the central region.

[0034] The difference between the maximum thickness and the minimum thickness of the surface layer 1 (the difference between the maximum thickness and the minimum thickness based on the flat surface of the striking surface 10a) can be set within a range that increases the degree of freedom in the design of the sound plate 10, and is not particularly limited. The lower limit of the difference may be, for example, 0.10 mm or 0.20 mm. On the other hand, the upper limit of the difference may be, for example, 4 mm or 2 mm.

[0035] The surface layer may be impregnated with a different material in the thickness direction from the striking surface 10a. A configuration in which a different material is impregnated will be described with reference to Fig. 4. The surface layer 11 in Fig. 4 can be used in place of the surface layer 1 in Fig. 1.

[0036] The surface layer 11 in FIG. 4 has a base material and a different material impregnated in the base material. The base material is a material such as porous that can be impregnated with the different material. The base material is not particularly limited, but may be wood, for example. With this configuration, the sound board 10 is likely to produce a woody sound. In addition, the surface layer 11 is impregnated with the different material, which makes it easier to increase the strength of the surface layer 11. The specific type and configuration of the wood constituting the base material may be the same as that of the surface layer 1 in FIG. 1.

[0037] The dissimilar material is preferably one having a larger specific gravity than the base material. The dissimilar material may be, for example, a resin. The resin is not particularly limited, but may be a thermosetting resin that has a low viscosity and is easily impregnated into the base material. Examples of the thermosetting resin include epoxy resin, phenol resin, urea resin, polyester, acrylic resin, silicate resin, melamine resin, polyurethane, etc.

[0038] The different materials may contain a filler (fine particles). Examples of the filler include talc and glass fiber. When the different materials contain the filler, the strength of the surface layer 11 can be further increased.

[0039] The amount of the different material impregnated varies along the longitudinal direction of the striking surface 10a. With this configuration, the weight of the striking surface region R can be easily varied along the longitudinal direction of the striking surface 10a.

[0040] The dissimilar material is, for example, impregnated into the entire area of ​​the surface layer 11. With this configuration, the impregnation depth of the dissimilar material can be controlled by the thickness of the surface layer 11. That is, the impregnation depth of the dissimilar material can be made to match the thickness of the surface layer 11. As a result, it becomes easy to selectively arrange the dissimilar material in a desired range on the striking surface 10a side, and it is easy to increase the degree of freedom in designing the sound board 10. In addition, with this configuration, it is easy to make the specific gravity of the surface layer 11 larger than that of the base 2.

[0041] The impregnation depth of the different material, for example, increases or decreases monotonically from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction. By impregnating the entire region of the surface layer 11 with the different material, the impregnation depth of the different material can be easily increased or decreased monotonically from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction in accordance with the thickness of the surface layer 11. For example, when the sound board 10 is used as a sound board for a high range, the sound quality, strength, and overall thickness of the sound board 10 can be easily adjusted by making the impregnation depth of the different material in both longitudinal side regions of the striking surface 10a smaller than that in the central region. Furthermore, when viewed in the thickness direction of the sound board 10 at the point where the impregnation depth of the different material is greatest and at equal thickness in the longitudinal direction of the striking surface 10a, the density of the different material monotonically increases or decreases from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction.

[0042] In the striking surface side region R, the density of the different material may, for example, monotonically increase or decrease from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction. By impregnating the entire region of the surface layer 11 with the different material, the density of the different material in the striking surface side region R can be easily monotonically increased or decreased from the central region in the longitudinal direction of the striking surface 10a to both sides in the longitudinal direction in accordance with the thickness of the surface layer 11. For example, when the sound board 10 is used as a sound board for a high range, the sound quality, strength, and overall thickness of the sound board 10 can be easily adjusted by making the density of the different material in both longitudinal direction regions of the striking surface 10a smaller than that in the central region.

[0043] (Base) The base 2 supports the surface layer 1 from its back side. The base 2 also controls the sound quality emitted from the sound plate 10. As shown in FIG. 1, a recess 2a is provided on the back side of the base 2. The recess 2a is formed in the center part of the base 2 in the longitudinal direction. The recess 2a crosses the back side of the base 2 in the short direction. The base 2 has a thin-walled part 2b recessed by the recess 2a. By providing the recess 2a on the back side of the base 2, the sound plate 10 is tuned so that the ratio of the vibration frequencies in each mode between the fundamental mode and the higher modes is approximately an integer multiple.

[0044] The material of the base 2 is not particularly limited, and examples thereof include the materials exemplified for the surface layer 1. As described later, the base 2 may be formed using a plurality of plate materials made of, for example, the materials exemplified for the surface layer 1. In this case, for example, all the plate materials constituting the base 2 are made of the same material.

[0045] The base 2 is, for example, wood. Examples of wood that constitute the base 2 include wood exemplified for the surface layer 1. The sound board 10 is likely to produce woody sound because the base 2 is made of wood. The base 2 may be impregnated with the above-mentioned different materials. In addition, when the base 2 includes a plurality of board materials, only some of the plurality of board materials may be impregnated with the different materials. In addition, when both the surface layer 1 and the base 2 include wood and the surface layer 1 is not impregnated with the different materials, the type of wood used for the base 2 may be different from the type of wood used for the surface layer 1 in order to make the specific gravity of the surface layer 1 different from the specific gravity of the base 2.

[0046] The base 2 may be made of a single plate material. Alternatively, the base 2 may be a laminate of multiple plate materials. In this case, the base 2 can be formed by fixing multiple plate materials with an adhesive. Fig. 5 is a schematic perspective view showing an example of the base of the sound plate of Fig. 1. The XYZ axes in Fig. 5 indicate the longitudinal direction of the base 2, the thickness direction of the base 2, and the width direction of the base in the X-axis direction, the Y-axis direction, and the Z-axis direction, respectively. The XYZ axes are also applied to the drawings of other embodiments. However, since the sound plate 60 of other embodiments is tubular, the thickness direction and width direction of the base are not defined by the Y-axis direction and the Z-axis direction. The base 2 may be formed by stacking a plurality of plate materials in the thickness direction of the base 2 (Y-axis direction in FIG. 5). On the other hand, as shown in FIG. 5, the stacking direction of the plurality of plate materials 2c (Z-direction in FIG. 5) and the thickness direction of the base 2 (Y-axis direction in FIG. 5) may be perpendicular to each other. In other words, the base 2 may be provided by stacking a plurality of plate materials 2c in a planar direction (for example, X-axis direction or Z-axis direction in FIG. 5) perpendicular to the thickness direction of the base 2 (Y-direction in FIG. 5). According to this configuration, the adhesive for bonding the plurality of plate materials 2c is not arranged in a film shape in the planar direction (XZ plane direction in FIG. 5). As a result, it is possible to suppress the attenuation of vibration in the planar direction caused by the adhesive, and it is easy to generate a sound with a good extension.

[0047] <Manufacturing method> Next, a description will be given of an example of a manufacturing method of the sound plate 10. The manufacturing method of the sound plate includes a step of forming a surface layer (forming step) and a step of laminating the surface layer formed in the forming step and a base (laminating step).

[0048] (Formation process) In the forming step, for example, a surface layer 1 or surface layer 11 having a flat striking surface 10a and a curved surface opposing the striking surface 10a is formed. In the forming step, for example, the entire surface layer is curved in an arch shape, and then one of the curved surfaces is subjected to a flattening process such as cutting to form a desired shape. The forming step may be performed before or after the lamination step.

[0049] The procedure for impregnating the surface layer with the different material in the forming step will be described below. When the entire area of ​​the surface layer is impregnated with the different material, in the forming step, the base material constituting the surface layer is immersed in a solution containing the different material, and then the different material is cured by heating or the like.

[0050] In the forming process, for example, the base material and the solution are placed in a chamber, the chamber is depressurized, and the base material is immersed in the solution. In addition, in the forming process, for example, the chamber is pressurized to atmospheric pressure or higher while the base material is immersed in the solution. By depressurizing the chamber in the forming process, the air present in the base material can be removed, and the dissimilar material can be easily introduced into the voids in the base material. Furthermore, by pressurizing the chamber while the base material is immersed in the solution, the dissimilar material can be easily pushed into the base material. According to this procedure, the dissimilar material can be easily impregnated evenly into the inside of the base material, and the dissimilar material can be easily impregnated over the entire area of ​​the base material. As a result, it is easy to control the impregnation depth of the dissimilar material in the sound board 10. Note that in the forming process, the procedure may be repeated two or more times.

[0051] In the method for manufacturing the sound plate, the different material may be impregnated only in a portion of the surface layer. In this case, in the forming step, only the range of the base material from the striking surface side to a desired thickness is immersed in the solution.

[0052] (Layer structure) In the lamination step, the surface layer formed in the formation step and a separately prepared base are fixed together with an adhesive.

[0053] <Advantages> There are various issues with sound plates depending on the instrument, and even within a single instrument depending on the pitch. For example, in the case of marimbas and xylophones, there are issues with sound plates that are specific to the pitch. To give a specific example, there are the following. The central area in the longitudinal direction of the sound plate on the treble side, which is frequently struck, has the problem that the striking surface is dented by striking because a hard mallet is used. On the other hand, when wood is impregnated with resin (hereinafter, wood impregnated with resin is also called "resin-impregnated wood"), it becomes harder than normal wood of the same material. Therefore, the advantage of using resin-impregnated wood for sound plates is that it is effective in increasing the hardness of the surface by using resin-impregnated wood as a material including the surface, but the disadvantage is that the sound quality differs from that of the original wood material by the amount of resin contained, so the more resin-impregnated wood there is in the sound plate, the further away it becomes from the sound quality that is characteristic of a marimba or xylophone.

[0054] Furthermore, resin-impregnated wood has a higher specific gravity than regular wood of the same material. In general, there is a positive correlation between specific gravity and hardness, and between hardness and elastic modulus. The harder the wood material is and the thicker it is, the greater its resistance to dents. Also, as the elastic modulus increases, the pitch of the sound produced rises. On the other hand, when resin-impregnated wood becomes thicker, the weight on both ends increases due to its high specific gravity, lowering the pitch and reducing the amount of space that can be removed for tuning.

[0055] After the sound plate is molded, the pitch of the sound plate needs to be tuned. This tuning is done by grinding the center of the back of the sound plate or both ends of the sound plate in the longitudinal direction. In other words, the pitch is lowered by grinding the center of the sound plate to reduce its rigidity, and the pitch is raised by reducing the mass of both ends. This cutting of the sound plate involves cutting the thickness of the sound plate, which reduces the strength of the cut areas. Therefore, it is necessary to adjust the thickness within the range of the normal lifespan of the sound plate (the range where the wood does not crack) and within the range where the striking surface is not dented by playing. On the other hand, in this type of tuning, if there is a resin-impregnated layer or resin layer on the surface side, even if the wood is cut by grinding both ends of the sound plate, the thick surface layer in the center and the thin layers at both ends remain as they are until the highly rigid resin-impregnated layer or resin layer is reached, making it easier to fine-tune the pitch, and the strength of the sound plate is maintained even when it is cut, making it less likely to cause a dent on the striking surface, and the limit of cutting can be increased, allowing for a wider range of adjustment compared to conventional methods.

[0056] In addition, with the emphasis on environmental protection, some natural woods are rare, difficult to obtain, or expensive, but soundboards are sometimes made from such materials. When making soundboards from such materials, wood grains suitable for soundboards are carefully selected, and among such carefully selected woods, it is very difficult to obtain large veneers. However, by using materials with higher rigidity than the wood used as the material, such as resin-impregnated materials or resin materials, even if only partially, in the right places, the overall dimensions of the soundboard can be reduced even if a soundboard with the same pitch is made, and even small materials that could not be used before can be used as soundboards. In other words, rare woods can be effectively used to maintain the enjoyment of music with soundboards while reducing the waste of rare woods and contributing to society. In addition, by using resin-impregnated woods or resin materials in the right places, the use of rare woods is kept to a minimum, and the above-mentioned disadvantages are reduced.

[0057] The sound board 10 of this embodiment is easy to utilize the advantages of the material when focusing on such problems of the sound board. Since the weight of the striking surface side region R of the sound board 10, which is in the uniform thickness range from the striking surface 10a, changes along the longitudinal direction of the striking surface 10a, the degree of freedom in design of the sound quality, strength, and overall thickness of the sound board 10 can be increased, and the ease of fine adjustment in tuning can be increased and the adjustment range can be expanded.

[0058] In the sound board 10 of this embodiment, the thickness of the resin-impregnated wood is made thicker in the central area in the longitudinal direction where the sound board is frequently struck than at both ends, so that the dent resistance is increased and the elastic modulus is increased, so that the pitch is higher and the amount of cutting required for tuning is increased. In addition, the weight per given volume of the striking surface side region R of the sound board 10 can be made smaller at both ends of the striking surface 10a in the longitudinal direction by monotonically decreasing the weight from the central area in the longitudinal direction of the striking surface 10a to both ends in the longitudinal direction. Therefore, the sound board 10 can be suitably used as a sound board for a high range.

[0059] [Second embodiment] <Sound plate> The sound board 20 in Fig. 6 has a long striking surface 20a. The weight of the striking surface side region R of the sound board 20, which is in a uniform thickness range from the striking surface 20a, varies along the longitudinal direction of the striking surface 20a. The sound board 20 can be used in place of the sound board 10 in Fig. 1. The thickness of the sound board 20 can be approximately the total thickness of the surface layer 1 and the base 2 in Fig. 1.

[0060] The sound plate 20 includes a base material 21 having a striking surface 20a. The base material 21 is impregnated with a different material 22 in the thickness direction from the striking surface 20a.

[0061] The amount of the different material 22 impregnated varies along the longitudinal direction of the striking surface 20a. As the amount of the different material 22 impregnated varies, the weight of the striking surface region R of the sound board 20 varies along the longitudinal direction of the striking surface 20a.

[0062] (base material) The base material 21 is made of a porous material or the like that can be impregnated with the different material 22. The base material 21 is not particularly limited, but may be made of wood, for example. Examples of wood used as the base material 21 include the wood exemplified for the surface layer 1 in FIG.

[0063] The striking surface 20a is provided with a plurality of pores 20b. The plurality of pores 20b can be formed, for example, by laser incising, piercing with a needle, or spraying with a fluid. The depth of the plurality of pores 20b decreases monotonically from the central region in the longitudinal direction of the striking surface 20a to both sides in the longitudinal direction. The plurality of pores 20b are arranged at approximately equal intervals along the longitudinal direction of the striking surface 20a. In the sound board 20, the striking surface side region R can be an area sandwiched between the striking surface 20a and a virtual plane parallel to the striking surface 20a that passes through the deepest parts of the plurality of pores 20b.

[0064] (different materials) The dissimilar material 22 is filled into the multiple pores 20b. That is, the arrangement and content of the dissimilar material 22 are adjusted by the arrangement and size of the multiple pores 20b. Examples of materials used for the dissimilar material 22 include the materials exemplified for the sound plate 10 in Fig. 1. Note that the dissimilar material 22 may also be impregnated into portions other than the multiple pores 20b, as long as the overall content is adjusted by the multiple pores 20b.

[0065] The impregnation depth of the dissimilar material 22 decreases monotonically from the central region in the longitudinal direction of the striking surface 20a to both sides in the longitudinal direction. More specifically, the impregnation depth of the dissimilar material 22 decreases stepwise from the central region in the longitudinal direction of the striking surface 20a to both sides in the longitudinal direction so as to correspond to the depth of the multiple pores 20b.

[0066] In the striking surface side region R, for example, the density of the dissimilar material 22 may monotonically decrease from the central region in the longitudinal direction of the striking surface 20a toward both sides in the longitudinal direction. More specifically, the density of the dissimilar material 22 in the striking surface side region R decreases stepwise from the central region in the longitudinal direction of the striking surface 20a toward both sides in the longitudinal direction so as to correspond to the depth of the multiple pores 20b.

[0067] <Advantages> Since the weight of the striking surface side region R of the sound board 20, which is within an equal thickness range from the striking surface 20a, changes along the longitudinal direction of the striking surface 20a, the degree of freedom in designing the sound quality, strength, overall thickness of the sound board 20, etc. can be increased.

[0068] [Third embodiment] <Sound plate> The sound board 30 of Fig. 7 to Fig. 9 has a long striking surface 30a. The weight of the striking surface side region R of the sound board 30, which is in a uniform thickness range from the striking surface 30a, varies along the longitudinal direction of the striking surface 30a. The sound board 30 includes a surface layer 31 having the striking surface 30a, and a base 32 indirectly laminated on the surface of the surface layer 31 opposite to the striking surface 30a. The sound board 30 also includes an intermediate layer 33 disposed between the surface layer 31 and the base 32.

[0069] The surface layer 31, the intermediate layer 33, and the base 32 are fixed, for example, by using an adhesive. The surface layer 31, the intermediate layer 33, and the base 32 are arranged in this order from the striking surface 30a side to the back side. The sound board 30 may have layers other than the surface layer 31, the intermediate layer 33, and the base 32, or may not have layers other than the surface layer 31, the intermediate layer 33, and the base 32. The sound board 30 can be used, for example, as a sound board for a low range, although it is not particularly limited.

[0070] (surface) The surface layer 31 contains oriented fibers. The surface layer 31 contains, for example, wood as a material containing oriented fibers. The thickness of the surface layer 31 increases monotonically from the central region in the longitudinal direction of the striking surface 30a to both sides in the longitudinal direction. The longitudinal length of the surface layer 31 is greater than that of the surface layer 1 in FIG. 1. The specific configuration of the surface layer 31 can be the same as that of the surface layer 1 in FIG. 1 or the surface layer 11 in FIG. 4, except that the thickness increase / decrease direction and the longitudinal length are different. In the sound board 30, the striking surface side region R can be a region sandwiched between the striking surface 30a and a virtual plane parallel to the striking surface 30a that passes through the part where the thickness of the surface layer 31 is maximum.

[0071] (Base) The base 32 supports the surface layer 31 and the intermediate layer 33 from the rear surface side. The base 32 also controls the sound quality emitted from the sound plate 30.

[0072] A recess 32a is provided on the back surface of the base 32. The recess 32a is formed in the center portion of the base 32 in the longitudinal direction. The recess 32a crosses the back surface of the base 32 in the short direction. The base 32 has a thin portion 32b recessed by the recess 32a. The thickness of the thin portion 32b of the base 32 is smaller than the thickness of the thin portion 2b of the base 2 in FIG. 1. Furthermore, the length of the base 32 in the longitudinal direction is larger than the length of the base 2 in FIG. 1. The base 32 can be configured similarly to the base 2 in FIG. 1, except that the thickness of the thin portion 32b is smaller and the length of the longitudinal direction is larger.

[0073] (Middle class) The intermediate layer 33 contains oriented fibers. The intermediate layer 33 contains, for example, wood as a material containing oriented fibers. More specifically, the intermediate layer 33 is made of wood. Since the intermediate layer 33 contains wood, the soundboard 30 can have wood as the main component of all of the surface layer 31, the intermediate layer 33, and the base 32. Examples of wood contained in the intermediate layer 33 include the wood exemplified for the surface layer 1 in FIG. 1.

[0074] The sound plate 30 is prone to cracking due to the small thickness of the thin portion 32b of the base 32. The intermediate layer 33 is provided mainly to suppress this cracking. The intermediate layer 33 may be configured by laminating multiple veneers in the thickness direction, but may also be configured from a single veneer.

[0075] The direction of the fibers of the intermediate layer 33 is, for example, perpendicular to the direction of the fibers of the surface layer 31 in a plan view. More specifically, as shown in Figs. 8 and 9, the grain 33a of the wood of the intermediate layer 33 is perpendicular to the grain 31a of the wood of the surface layer 31 in a plan view. With this configuration, cracks in the sound board 30 can be more reliably suppressed. Also, by making the grain 33a of the wood of the intermediate layer 33 perpendicular to the grain 31a of the wood of the surface layer 31 in a plan view, the grain 33a of the wood of the intermediate layer 33 can be easily made to cross the crack propagation direction. Therefore, even if a wood with a relatively low specific gravity is used for the intermediate layer 33, it is easy to suppress cracks in the sound board 30. As a result, the degree of freedom in the thickness of the intermediate layer 33 and the degree of freedom in the selection of the type of wood are increased, making it easier to improve the sound quality of the sound board 30.

[0076] <Manufacturing method> The manufacturing method of the sound plate 30 includes, for example, a step of forming a surface layer 31 (forming step), and a step of laminating the surface layer 31 formed in the forming step, an intermediate layer 33, and a base 32 in this order (lamination step).

[0077] The forming step can be performed in the same procedure as the forming step in the manufacturing method of the sound plate 10 in Fig. 1. In the lamination step, for example, the surface layer 31, the intermediate layer 33 and the base 32 are fixed with an adhesive.

[0078] <Advantages> There are various issues with sound plates depending on the instrument, and even within a single instrument depending on the pitch. For example, in the case of marimbas and xylophones, there are issues with sound plates that are specific to the pitch. Specific examples include the following. Mainly, there is a demand for increasing the mass of both end regions in the longitudinal direction of the sound plate for the bass side sound plate. The more the mass of both end regions increases, the less the amount of hollowing out in the central region (hollowing out amount of the recess 32a). This increases the thickness of the central region and improves durability. In addition, resin-impregnated wood has a higher specific gravity than normal wood of the same material, so it can be effectively used to increase the mass. The disadvantage is that the sound quality differs from that of the original wood material by the amount of resin contained, so the more resin-impregnated wood increases in relation to the entire sound plate, the further away the sound quality becomes from that of a marimba or xylophone.

[0079] As explained in the first embodiment, the tone plate needs to be tuned after the plate body is formed. Furthermore, with the emphasis on environmental protection, some natural woods are rare and difficult to obtain, and some are expensive.

[0080] The sound board 30 of this embodiment is easy to utilize the advantages of the material when focusing on such problems of the sound board. The thickness of the surface layer 31 of the sound board 30 increases monotonically from the central area in the longitudinal direction of the striking surface 30a to both sides in the longitudinal direction. With this configuration, the strength and weight of the sound board 30 can be changed from the central area in the longitudinal direction of the striking surface 30a to both sides in the longitudinal direction in correspondence with the thickness of the surface layer 31. For example, if the sound board 30 is used as a sound board for a low range, the weight of both sides in the longitudinal direction of the striking surface 30a can be made larger than that of the central area, thereby increasing the degree of freedom in designing the sound quality, strength, and overall thickness of the sound board 30, increasing the ease of fine adjustment in tuning, and widening the adjustment range. And, when using rare wood, it can be effectively utilized.

[0081] Generally, a sound plate is more likely to produce low-pitched sounds by increasing the flexibility of the central region in the longitudinal direction. Conventionally, a method for increasing the flexibility of the central region in the longitudinal direction is to deepen the depth of the recess provided on the back surface of the base. In contrast, the sound plate 30 is designed to have a weight of the striking surface side region R that increases monotonically from the central region in the longitudinal direction of the striking surface 30a toward both sides in the longitudinal direction, thereby relatively reducing the strength of the central region in the longitudinal direction and improving the flexibility of the central region. Therefore, the sound plate 30 can be suitably used as a sound plate for a low-pitched range.

[0082] [Fourth embodiment] <Percussion> The percussion instrument 40 of FIG. 10 includes a plurality of sound plates 50. Each of the plurality of sound plates 50 has a long striking surface 50a. At least one of the plurality of sound plates 50 has a weight of a striking surface side region of equal thickness from the striking surface 50a that changes along the longitudinal direction of the striking surface 50a. The percussion instrument 40 may include, for example, any of the sound plates 10 of FIG. 1, 20 of FIG. 6, and 30 of FIG. 7 as a sound plate whose weight of the striking surface side region changes along the longitudinal direction of the striking surface 50a. The percussion instrument 40 may be, for example, a marimba, a xylophone, a vibraphone, etc.

[0083] The percussion instrument 40 includes, for example, two or more sound plates 50 whose weight in the striking surface side area changes along the longitudinal direction of the striking surface 50a. In addition, for example, at least two of these sound plates 50 have different weight increase / decrease directions along the longitudinal direction of the striking surface 50a in the striking surface side area (in other words, at least two sound plates 50 have different degrees of weight increase / decrease along the longitudinal direction of the striking surface 50a in the striking surface side area), or have different overall layer structures. For example, the sound plate 10 in FIG. 1, the sound plate 20 in FIG. 6, and the sound plate 30 in FIG. 7 have different layer structures. The weights of both ends of these sound plates 10, 20, and 30 are different from each other, and the thicknesses of the sound plates 10, 20, and 30 in the central area in the longitudinal direction of the striking surface are different. In addition, the sound board 30 in Fig. 7 differs from the sound board 10 in Fig. 1 and the sound board 20 in Fig. 6 in the weight increase / decrease direction along the longitudinal direction of the striking surface 50a in the striking surface side region. The percussion instrument 40 is configured to have two or more sound boards 50 with different overall layer structures or weight increase / decrease directions along the longitudinal direction of the striking surface 50a, making it easy to control the sound quality, range, strength, thickness, etc. of the multiple sound boards 50 to the desired quality.

[0084] In the percussion instrument 40, the material of the outermost layer on the striking surface 50a side is the same for all the sound plates 50. In the percussion instrument 40, the material of the outermost layer on the striking surface 50a side may be the same by forming the surface layer of all the sound plates 50 from wood, or the material of the outermost layer on the striking surface 50a side may be the same by forming the surface layer of all the sound plates 50 as a layer of wood impregnated with a different material. In the percussion instrument 40, the material of the outermost layer on the striking surface side is the same for all the sound plates 50, so that it is easy to uniformize the quality of all the sound plates 50. Note that, for example, when wood is used as the material of the outermost layer on the striking surface side, the type of wood placed on the outermost layer is made the same from the viewpoint of promoting uniformity of the quality of all the sound plates 50. In addition, the grain of the wood placed on the outermost layer on the striking surface side and the type of different material impregnated into this wood may be the same. In addition, the type of coating or paint may be the same.

[0085] <Advantages> Since the percussion instrument 40 is equipped with the sound plate of the present disclosure, it is possible to increase the degree of freedom in designing the sound quality, strength, overall thickness of the sound plate, and the like.

[0086] [Other embodiments] The above-described embodiments do not limit the configuration of the present invention. Therefore, the above-described embodiments may include omissions, substitutions, or additions of components of each part of the embodiments based on the description in this specification and common general technical knowledge, and all of these should be interpreted as falling within the scope of the present invention.

[0087] The sound board is not limited to the configurations described in the first to third embodiments described above, as long as the weight of the striking surface side region in a uniform thickness range from the striking surface changes along the longitudinal direction of the striking surface. As an example, the sound board can also be configured as shown in Figures 11 to 13. The sound board 60 in Figures 11 to 13 has a long striking surface 60a. The sound board 60 is tubular, and its outer circumferential surface constitutes the striking surface 60a. The longitudinal direction of the striking surface 60a is along the central axis of the sound board 60. As shown in Figures 12 and 13, the sound board 60 is impregnated with a different material 62 in the thickness direction from the striking surface 60a. The amount of the different material 62 impregnated changes along the longitudinal direction of the striking surface 60a. With this configuration, the sound board 60 has a weight of the striking surface side region in a uniform thickness range from the striking surface 60a changing along the longitudinal direction of the striking surface 60a.

[0088] The weight of the striking surface side region is not particularly limited in the direction of increase or decrease as long as it changes along the longitudinal direction of the striking surface. For example, the weight of the striking surface side region may be monotonically increased from the longitudinal center region of the striking surface toward both sides in the configuration of FIG. 1, and may be monotonically decreased from the longitudinal center region of the striking surface toward both sides in the configuration of FIG. 7. More specifically, the thickness of the surface layer in FIG. 1 may be monotonically increased from the longitudinal center region of the striking surface toward both sides, and the thickness of the surface layer in FIG. 7 may be monotonically decreased from the longitudinal center region of the striking surface toward both sides. Furthermore, the sound plate in FIG. 1 may be used for the low range, and the sound plate in FIG. 7 may be used for the high range.

[0089] In the configuration of FIG. 6 in which the different materials are filled in the pores, the shape and arrangement of the pores are not particularly limited. For example, the sound plate may change the amount of impregnation of the different materials along the longitudinal direction of the striking surface by changing the interval between the pores in the longitudinal direction of the striking surface. With this configuration, the density of the different materials can be changed while keeping the impregnation depth of the different materials constant. In addition, the sound plate may change the diameter of the pores instead of or in addition to the depth of the pores, thereby changing the amount of impregnation of the different materials along the longitudinal direction of the striking surface. Furthermore, the interval, depth, diameter, etc. of the pores may be set so that the content of the different materials monotonically increases or monotonically decreases from the central region in the longitudinal direction of the striking surface to both sides in the longitudinal direction.

[0090] The sound plate may also have a layer other than the intermediate layer between the surface layer and the base.

[0091] In the above embodiment, the configuration in which the different material is impregnated into wood has been described. However, the base material in which the different material is impregnated may be, for example, a woven fiber material or a nonwoven fiber material.

[0092] The intermediate layer may be made of a fiber-reinforced resin such as carbon fiber reinforced plastic (CFRP).

[0093] If the surface layer contains wood, the grain of the wood does not have to be aligned along the longitudinal direction of the striking surface. Furthermore, the direction of the fibers of the surface layer and the direction of the fibers of the intermediate layer do not have to be perpendicular in a plan view. For example, the fibers of the surface layer and the fibers of the intermediate layer may be arranged parallel in a plan view.

[0094] The percussion instruments to which the sound plate is applied are not limited to the above-mentioned percussion instruments. The sound plate may be used for castanets, wood blocks, cajons, mokugyo, chimes, etc. The shape of the striking surface of the sound plate can be designed based on the percussion instrument to which it is applied.

[0095] This application is based on a Japanese application (Patent Application No. 2021-063501) filed on April 2, 2021, the contents of which are incorporated herein by reference. [Industrial Applicability]

[0096] As described above, a sound plate according to one aspect of the present invention is suitable for increasing the degree of freedom in design. [Explanation of symbols]

[0097] 1, 11, 31 surface layer 1a, 31a, 33a wood grain 2, 32 bases 2a, 32a recess 2b, 32b Thin wall part 2c board material 10, 20, 30, 50, 60 tone plates 10a, 20a, 30a, 50a, 60a hitting surface 20b Pore 21 Base material 22, 62 Different materials 33 Middle Class 40 Percussion R hitting surface side area

Claims

1. A long member having a long striking surface, The weight of a striking surface side region of the elongated member that is within a uniform thickness range from the striking surface varies along a longitudinal direction of the striking surface, A different material is impregnated into the elongated member in a thickness direction of the elongated member from the striking surface, A soundboard in which the amount of impregnation of the different material varies along the longitudinal direction of the striking surface.

2. 2. The sound plate according to claim 1, wherein the impregnation depth of the different material monotonically increases or monotonically decreases from a central region in the longitudinal direction of the striking surface of the elongated member to both sides in the longitudinal direction.

3. 3. The sound plate according to claim 1, wherein in the striking surface region, the density of the different material monotonically increases or monotonically decreases from a central region in the longitudinal direction of the striking surface to both sides in the longitudinal direction.

4. A long member having a long striking surface, The weight of a striking surface side region of the elongated member that is within a uniform thickness range from the striking surface varies along a longitudinal direction of the striking surface, The elongated member is A surface layer having the striking surface; a base that is directly or indirectly laminated on the surface of the surface layer opposite to the striking surface; Equipped with The specific gravity of the surface layer is different from the specific gravity of the base, A soundboard in which the thickness of the surface layer varies along the longitudinal direction of the striking surface.

5. 5. The sound plate according to claim 4, wherein the base is made of wood.

6. 6. The sound plate according to claim 4, wherein the base is a laminate in which a plurality of plate materials are laminated, and the lamination direction of the plurality of plate materials is perpendicular to the thickness direction of the base.

7. 7. A sound plate according to claim 4, wherein the surface layer contains oriented fibers.

8. The elongated member further includes an intermediate layer disposed between the surface layer and the base, The intermediate layer includes oriented fibers, 8. The sound plate according to claim 7, wherein the direction of the fibers of the intermediate layer is perpendicular to the direction of the fibers of the surface layer in a plan view.

9. 9. A sound plate according to claim 4, wherein the thickness of the surface layer monotonically increases or monotonically decreases from a central region in the longitudinal direction of the striking surface to both sides in the longitudinal direction.

10. A sound plate according to any one of claims 1 to 9, A percussion instrument, wherein at least two of the plurality of sound plates have different weight increase / decrease directions along the longitudinal direction of the striking surface in the striking surface side region, or the layer structures of the at least two sound plates are different.

11. 11. The percussion instrument according to claim 10, wherein the layered structure of the at least two sound plates differs in weight at both ends of the elongated member in the longitudinal direction of the striking surface or in thickness of the elongated member in a central region in the longitudinal direction of the striking surface.

12. 12. The percussion instrument according to claim 10, wherein the material of the outermost layer on the striking surface side of all of the plurality of sound plates is the same.