Polymers with upper critical solution temperature in aqueous solution

Abstract

Several embodiments relate generally to temperature-responsive polymers, and more specifically to polymers that exhibit an upper critical solution temperature (UCST) in aqueous solution. In one embodiment, the monomeric compound contains one or more amide or thioamide groups, one or more ureido or thioureido groups, and one or more ethylenically unsaturated groups. In one embodiment, the polymer, e.g., a homopolymer or copolymer, is prepared by polymerization of the monomeric compound. The copolymer is prepared by polymerization of the monomeric compound with a comonomer, e.g., a hydrophobic comonomer, a hydrophilic comonomer, a pH-responsive comonomer, a photoresponsive comonomer, or a combination thereof. The polymer exhibits a UCST of about 1°C to about 100°C in aqueous solution at 1 atmosphere.

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application is a PCT application that claims priority to co-pending U.S. Non-Provisional Patent Application No. 16 / 867,955, filed May 6, 2020, which claims the benefit of U.S. Provisional Patent Application No. 62 / 848,132, filed May 15, 2019. The above related patent applications are hereby incorporated by reference in their entireties.

[0002] Aspects relate generally to temperature-responsive polymers, and more specifically, to polymers that exhibit an upper critical solution temperature in aqueous solution. [Background technology]

[0003] Water-soluble thermoresponsive polymers are a class of polymers whose solubility changes with a change in temperature. Lower critical solution temperature (LCST) polymers are polymers that have a lower critical solution temperature, below which the polymer is soluble in solution. Above the LCST, the polymer is partially soluble or insoluble in solution. Upper critical solution temperature (UCST) polymers are polymers that have an upper critical solution temperature, above which the polymer is soluble in solution. Below the UCST, the polymer is partially insoluble or insoluble in solution. Because LCST and UCST polymers can change their physical properties in response to changes in external temperature, LCST and UCST polymers are materials under investigation for drug delivery systems, biosensors and medical applications.

[0004] While there are many examples of LCST polymers, there are few examples of UCST polymers, with only a handful. One example of a UCST polymer is based on zwitterionic polymers (e.g., poly(betaine)). However, these polymers may not be suitable for electrolytes. Another example of a UCST polymer is poly(uracil acrylate) urea modified polymer. However, even hydrolysis of a small amount of the poly(uracil acrylate) side groups results in loss of UCST over time. Another example of a UCST polymer is poly(N-acryloylglycinamide) (poly(NAGA)) and its derivatives. However, the synthesis of pure N-acryloylglycinamide monomers without acrylic acid impurities remains a challenge. Summary of the Invention [Problem to be solved by the invention]

[0005] Therefore, there is a need for UCST polymers suitable for electrolytes. [Means for solving the problem]

[0006] A number of embodiments relate generally to temperature-responsive polymers, and more specifically to polymers that exhibit an upper critical solution temperature (UCST) in aqueous solution. In one embodiment, the monomeric compound comprises one or more amide or thioamide groups, one or more ureido or thioureido groups, and one or more ethylenically unsaturated groups. In one embodiment, the polymer, e.g., a homopolymer or copolymer, comprises a number of monomeric units. Each monomeric unit comprises one or more amide or thioamide groups and one or more ureido or thioureido groups. The polymer exhibits a UCST of about 1° C. to about 100° C. in aqueous solution at 1 atmosphere. In another embodiment, the copolymer comprises a number of monomeric units and a number of comonomer units. Each monomeric unit comprises one or more amide or thioamide groups and one or more ureido or thioureido groups. Each comonomer unit is selected from the group comprising hydrophobic comonomers, hydrophilic comonomers, pH-responsive comonomers, photoresponsive comonomers, and combinations thereof. The copolymer exhibits a UCST of about 1° C. to about 100° C. in aqueous solution at 1 atmosphere.

[0007] In order that the above-mentioned features of the present disclosure may be understood in detail, a more particular description of the present disclosure briefly summarized above may be obtained by reference to several embodiments, some of which are illustrated in the accompanying drawings, which are to be noted, however, that the accompanying drawings illustrate only exemplary embodiments and therefore should not be considered as limiting its scope, as other embodiments which are equally valid may be recognized. [Brief description of the drawings]

[0008] [Figure 1] 1 is a 1H NMR spectrum of a MEGA-BMA copolymer according to certain embodiments. [Diagram 2] 1 is a schematic example of a reaction scheme. [Diagram 3] 1 is a schematic example of a reaction scheme. [Figure 4] 1 is a schematic example of a reaction scheme. [Diagram 5] 1 is a schematic example of a reaction scheme. [Figure 6] 1 is a schematic example of a reaction scheme. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] For ease of understanding, wherever possible, identical reference numbers have been used to designate identical elements that are common to multiple figures. It is understood that elements and features of one embodiment may be advantageously incorporated in other embodiments without further recitation.

[0010] Several aspects are now described in more detail below, including specific aspects, formats and examples, but the disclosure is not limited to these aspects, formats or examples, which are included to enable one of ordinary skill in the art to make and use the aspects when the information in this disclosure is combined with available information and technology.

[0011] Various terms used in this specification are defined below. Terms used in the claims, unless defined below, shall be given the broadest definition given to that term by one of ordinary skill in the relevant art, as reflected in one or more publications or issued patents.

[0012] All documents described herein are incorporated herein by reference, including any priority documents and / or test procedures, to the extent not inconsistent with this document. As is apparent from the above general description and specific embodiments, while various forms of these embodiments have been illustrated and described, various modifications can be made without departing from the spirit and scope of the present disclosure. Accordingly, the present disclosure is not intended to be limited thereby. Similarly, the term "comprising" is considered synonymous with the term "including". Similarly, whenever a composition, element, or group of elements is preceded by the transition phrase "comprising", it is understood that the same composition or group of elements is also contemplated with the transition phrase "consisting essentially of", "consisting of", "selected from the group of consisting of", or "I" preceding the composition, element, or list of elements, and vice versa. For example, the terms "comprising," "consisting essentially of," and "consisting of" also include products of combinations of the elements listed after the term.

[0013] For the sake of brevity, only certain ranges are expressly disclosed herein. However, a range from any lower limit may be combined with any upper limit to recite a range that is not expressly recited, and a range from any lower limit may be combined with any other lower limit to recite a range that is not expressly recited. Similarly, a range from any upper limit may be combined with any other upper limit to recite a range that is not expressly recited. Furthermore, a range includes every point or individual value between its endpoints, even if not expressly recited. Thus, every point or individual value may be combined with any other point or individual value or other lower or upper limit to act as its own lower or upper limit to recite a range that is not expressly recited.

[0014] Certain embodiments relate to ureido amide monomer compounds that include one or more ureido and / or thioureido groups, one or more amide and / or thioamide groups, and one or more ethylenically unsaturated groups, and methods of making the ureido amide monomers. In certain embodiments, the ureido amide monomer compounds include one or more ureido groups, one or more amide groups, and one or more ethylenically unsaturated groups.

[0015] Certain embodiments relate to homopolymers or copolymers of ureidoamide monomer compounds (collectively referred to as "polyureidoamides"). The copolymers of the present disclosure can be random or block copolymers. The polyureidoamides of the present invention have an upper critical solution temperature (UCST), above which the polymer becomes soluble in a solution, e.g., an aqueous solution. The polyureidoamides can exhibit a UCST in aqueous solutions at biologically relevant temperature ranges, e.g., from about 1°C to about 100°C. The polyureidoamides can exhibit a UCST in aqueous solutions at biologically relevant electrolyte conditions, e.g., sodium ion concentrations of greater than 0 to about 160 mM.

[0016] Examples of ureido groups include -NH(CO)NH-, -NR(CO)NH-, -NH(CO)NR-, or -NR(CO)NR'-, where R and R' are each independently alkylene or haloalkylene. Examples of thioureido groups include -NH(CS)NH-, -NR(CS)NH-, -NH(CS)NR-, or -NR(CS)NR'-, where R and R' are each independently alkylene or haloalkylene. In certain embodiments, the ureido group of the ureido amide monomer is -NH(CO)NH-. Without being bound by theory, it is believed that the ureido group participates in hydrogen bonding with water molecules below the UCST.

[0017] Examples of amide groups include NH2(CO)R-, NHR'(CO)R-, or NR"R'(CO)R-, where R is alkylene or haloalkylene, and R' and R" are each independently alkyl or haloalkyl. Examples of thioamide groups include NH2(CS)R-, NHR'(CS)R-, or NR"R'(CS)R-, where R is alkylene or haloalkylene, and R' and R" are each independently alkyl or haloalkyl. In certain embodiments, the amide group of the ureidoamide monomer is NH2(CO)R-, where R is alkylene or haloalkylene. Without wishing to be bound by theory, it is believed that the amide group participates in hydrogen bonding with a water molecule below the UCST.

[0018] The ethylenically unsaturated group of the ureidoamide monomer is any ethylenically unsaturated group that is susceptible to polymerization. For example, the ethylenically unsaturated groups include methyl methacrylate, ethyl methacrylate, propyl methacrylate (all isomers), butyl methacrylate (all isomers), 2-ethylhexyl methacrylate, isobornyl methacrylate, methacrylic acid, benzyl methacrylate, phenyl methacrylate, methacrylonitrile, alpha-methylstyrene, methyl acrylate, ethyl acrylate, propyl acrylate (all isomers), butyl acrylate (all isomers), 2-ethylhexyl acrylate, isobornyl acrylate, acrylic acid, benzyl acrylate, phenyl acrylate, acrylonitrile, styrene, functional methacrylates, functional acrylates, and the like. Acrylates and functional styrene derivatives, isomers and analogs (e.g., sulfur analogs) include glycidyl methacrylate, 2-hydroxyethyl methacrylate, hydroxypropyl methacrylate (all isomers), hydroxybutyl methacrylate (all isomers), N,N-dimethylaminoethyl methacrylate, N,N-diethylaminoethyl methacrylate, triethylene glycol methacrylate, itaconic anhydride, itaconic acid, glycidyl acrylate, 2-hydroxyethyl acrylate, hydroxypropyl acrylate (all isomers), hydroxybutyl acrylate (all isomers), N,N-dimethylaminoethyl acrylate, N,N-Diethylaminoethyl acrylate, Triethylene glycol acrylate, Methacrylamide, N-Methylacrylamide, N5N-Dimethylacrylamide, N-Tert-Butyl Methacrylamide, Nn-Butyl Methacrylamide, N-Methylol Methacrylamide, N-Ethylol Methacrylamide, N-Tert-Butylacrylamide, Nn-Butylacrylamide, N-Methylol Acrylamide, N-Ethylol Acrylamide, Vinyl benzoic acid (all isomers), Diethylaminostyrene (all isomers), Alpha-Methylvinylbenzoic acid (all isomers), Diethylaminoalpha-Methylstyrene (all isomers), p-Vinylbenzenesulfonic acid, p-Vinylbenzenesulfonic acid sodium salt, Trimethoxysilylpropyl methacrylate, Triethoxysilylpropyl methacrylate, Tributoxysilylpropyl methacrylate, Dimethoxymethylsilylpropyl methacrylate, Diethoxymethylsilylpropyl methacrylate, Dibutoxymethylsilylpropyl methacrylate , diisopropoxymethylsilylpropyl methacrylate, dimethoxysilylpropyl methacrylate, diethoxysilylpropyl methacrylate, dibutoxysilylpropyl methacrylate, diisopropoxysilylpropyl methacrylate, trimethoxysilylpropyl acrylate, triethoxysilylpropyl acrylate, tributoxysilylpropyl acrylate, dimethoxymethylsilylpropyl acrylate, diethoxymethylsilylpropyl acrylate, dibutoxymethylsilylpropyl acrylate, diisopropoxymethylsilylpropyl acrylate, dimethoxysilylpropyl acrylate, diethoxysilylpropyl acrylate, dibutoxysilylpropyl acrylate, diisopropoxysilylpropyl acrylate, vinyl acetate, vinyl butyrate, vinyl benzoate, vinyl chloride, vinyl fluoride, vinyl bromide, maleic anhydride, N-phenylmaleimide, N-butylmaleimide, N-vinylpyrrolidone, N-vinylcarbazole, butadiene, ethylene and chloroprene.

[0019] The ethylenically unsaturated group may be an ethylenically unsaturated ester group represented by formula (I), including derivatives, isomers and analogs thereof: [ka] In the formula, Q 1 and Q 2 are each independently oxygen or sulfur, and R 1 and R 2 are each independently hydrogen or a group of the formula -COOR', -CSOR', -COSR', where R' is hydrogen, alkyl or haloalkyl, R 3 is hydrogen, alkyl or haloalkyl; R 4 is an alkylene or haloalkylene. The unsaturated carbon-carbon double bond of the ethylenically unsaturated ester group is polymerized into the polymer chain.

[0020] The ethylenically unsaturated group is Q in the formula 1 and Q 2 are all oxygen, i.e., may be an ethylenically unsaturated ester group represented by formula (I), i.e., also represented by formula (II), including derivatives, isomers and analogues thereof; [ka] In the formula, R 1 and R 2 are each independently hydrogen or a group of formula COOR′, where R′ is hydrogen, alkyl or haloalkyl, and R 3 is hydrogen, alkyl or haloalkyl; R 4 is an alkylene or haloalkylene. The all-oxygen ester group of the ureidoamide monomers' ethylenically unsaturated groups can be more cost-effective in the synthesis of the monomers because esters are more widely available compared to thioesters.

[0021] In certain embodiments, the ureidoamide monomeric compound comprises an ethylenically unsaturated head group, a ureido body, and an amide tail group, the ethylenically unsaturated head group being incorporated into the main chain of the polymer and the amide tail group being on a side chain of the polymer.

[0022] In one example, the ureidoamide monomeric compound includes a compound represented by formula (III), including derivatives, isomers and analogs thereof: [ka] In the formula, Q 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur, and R 2 and R 3 is independently alkylene or haloalkylene; R 3 , R 4 , R 5 and R 6 are each independently hydrogen, alkyl, or haloalkyl. In certain embodiments, the ureido amide monomeric compounds include those represented by formula (III): 1 , Q 2 , Q 3 and Q 4 are all oxygen, and R 3 , R 4 , R 5 and R 6 are all hydrogen.

[0023] In another example, the ureido amide monomer compound is represented by the formula R 1 is -C2H4- and R 2 In at least one embodiment, the ureido amide monomer represented by formula (IV) is as follows: [ka] This monomeric compound is called 2-(methacryloyloxy)ethylureidoglycinamide (also known as "MEGA").

[0024] In a particular embodiment, the ureidoamide monomer compound represented by formula (III) or (IV) is synthesized by reacting an amide hydrohalide with an acrylate. For example, the ureidoamide monomer compound of formula (IV) is synthesized by reacting an amide hydrohalide of glycinamide hydrochloride with an acrylate of 2-isocyanatoethyl methacrylate. This reaction can be carried out in an organic solvent or a polar solvent (which can be a polar organic solvent), so that the salt impurities formed during the synthesis can be precipitated in the solvent and removed by filtration.

[0025] The ureidoamide monomer compound can be obtained by precipitation, recrystallization, solvent removal (e.g., evaporation), filtration, and combinations thereof. In certain embodiments, the ureidoamide monomer compound is obtained or purified without chromatography, for example, without column chromatography or liquid chromatography. Purification without chromatography reduces the complexity and cost of the production of the monomer compound. In certain embodiments, the monomer compound is synthesized with a yield of 40% or more, for example, 50% or more, or for example, 60% or more, and purified without chromatography. This is because the monomer compound can be dissolved and recrystallized in an organic solvent to remove further impurities.

[0026] In certain embodiments, the ureidoamide monomer compounds are synthesized and purified without chromatography to yield products with less than 1% by weight acrylic acid impurities, e.g., less than 0.5% by weight acrylic acid impurities, or, e.g., no acrylic acid impurities. Low or no acrylic acid impurities reduce or eliminate irritation and corrosion to living cells, which is environmentally favorable.

[0027] In certain embodiments, the polyureidoamide comprises a plurality of ureidoamide monomeric compounds, such as compounds represented by formula (III) or (IV). For example, the polyureidoamide comprises a plurality of monomeric units represented by formula (V), including derivatives, isomers and analogs thereof: [ka] In the formula, Q 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur, and R 1 is alkyl or haloalkyl; R 2 and R 3 is independently alkylene or haloalkylene; R 4 , R 5 , R 6 and R 7 are each independently hydrogen, alkyl or haloalkyl. In certain embodiments, the polyureidoamide has the formula 1 , Q 2 , Q 3 and Q 4 are oxygen, and R 4 , R 5 , R 6 and R 7 wherein each of the monomer units is represented by formula (V), i.e., also represented by formula (VI), including derivatives, isomers and analogs thereof, [ka] In the formula, R 1 is alkyl or haloalkyl; R 2 and R 3 is independently alkylene or haloalkylene. In certain embodiments, the polyureidoamide comprises MEGA polymerized monomer units represented by formula (VI), where R 1 is -CH3, R 2 is -C2H4-, R 3 is -CH2-.

[0028] In certain embodiments, the polyureidoamide has a number of repeat units (n) of polymerized ureidoamide monomer compounds, i.e., monomer units of formula (V) or (VI), from about 10 to about 200, such as from about 40 to about 110, such as from about 50 to about 100. The ureidoamide monomers exhibit different properties when polymerized into polyureidoamides. The polymer backbone of the polyureidoamide is hydrophobic, whereas the amide tails of the ureidoamide monomer units are hydrophilic.

[0029] In certain embodiments, the polyureidoamide copolymer comprises a plurality of ureidoamide monomer compounds and one or more comonomers. In certain embodiments, the comonomers can be hydrophobic, hydrophilic, pH-responsive, photoresponsive, or combinations thereof. In certain embodiments, the comonomers are hydrophobic comonomers. The hydrophobic comonomer units, in combination with the hydrophobic polymer backbone and the hydrophilic ureidoamide monomer units, can affect the overall hydrophobicity or hydrophilicity of the polyureidoamide copolymer in response to temperature.

[0030] Examples of hydrophobic comonomers include, but are not limited to, styrene, alpha-methylstyrene, butyl acrylate, butyl methacrylate (BMA) (n-butyl methacrylate or tert-butyl methacrylate), amyl methacrylate, hexyl methacrylate, lauryl methacrylate, stearyl methacrylate, ethylhexyl methacrylate, crotyl methacrylate, cinnamyl methacrylate, oleyl methacrylate, ricinoleyl methacrylate, vinyl butyrate, vinyl tert-butylate, vinyl stearate, vinyl laurate, and derivatives, isomers, and analogs thereof (e.g., sulfur analogs). In certain embodiments, the hydrophobic comonomer is n-butyl methacrylate.

[0031] Examples of hydrophilic comonomers include, but are not limited to, acrylic acid, methacrylic acid, hydroxyethyl methacrylate, hydroxypropyl methacrylate, acrylamide, methacrylamide, hydroxyethyl acrylate, N-methylacrylamide, N,N-dimethylacrylamide, and dimethylaminoethyl methacrylate, as well as derivatives, isomers, and analogs thereof (e.g., sulfur analogs).

[0032] In certain embodiments, the comonomer units of the polyureidoamide copolymer are represented by formula (VII), including derivatives, isomers and analogs thereof: [ka] In the formula, Q 1 and Q 2 are each independently oxygen or sulfur, and R 1 and R 2 are each independently alkyl or haloalkyl. In certain embodiments, the comonomer units of the polyureidoamide copolymer are 1 and Q 2 are each independently oxygen, i.e., also represented by formula (VIII), [ka] In the formula, R 1 and R 2 are each independently alkyl or haloalkyl.

[0033] In certain embodiments, the polyureidoamide copolymer has a number of repeat units (m) of the comonomer unit of formula (VII) or (VIII) from 1 to 100, such as from 10 to 50, such as from 15 to 35.

[0034] In certain embodiments, the polyureidoamide polymer has any suitable number of repeating polymerized comonomer units, i.e., repeating units (m) of comonomer units of formula (VII) or (VIII), such as 0 for homopolymers and greater than 0 for copolymers. In certain embodiments, the percentage of comonomer units ranges from about 1% to about 50% of the total number of repeating units (monomer+comonomer), such as from about 5% to about 45%, e.g., from about 10% to about 40%, of n+m (where n>m).

[0035] In certain embodiments, the repeat unit (n) of the ureidoamide monomer compound, i.e., the monomer unit of formula (V) or (VI), is 100% for homopolymers of ureidoamide monomers, relative to the total number of repeat units of (monomer+0 comonomer), e.g., n+0. In certain embodiments, the repeat unit (n) of the ureidoamide monomer compound, i.e., the monomer unit of formula (V) or (VI), is greater than 50% to 100% for copolymers and homopolymers of ureidoamide monomers, relative to the total number of repeat units of (monomer+comonomer), e.g., n+m (where n>m). In certain embodiments, the repeat unit (n) of the ureidoamide monomer compound, i.e., the monomer unit of formula (V) or (VI), is greater than 50% to less than 100% for copolymers, e.g., about 55% to about 95% for copolymers, relative to the total number of repeat units of (monomer+comonomer), e.g., n+m (where n>m).

[0036] In certain embodiments, the polyureidoamide, e.g., a polyureidoamide homopolymer or a polyureidoamide copolymer, is a water-soluble thermoresponsive polymer whose water solubility changes in response to a change in temperature. In certain embodiments, the polyureidoamide has an upper critical solution temperature (UCST), above which the polymer becomes soluble in a solution, e.g., an aqueous solution. In certain embodiments, the polyureidoamide exhibits a UCST in aqueous solution at 1 atmosphere pressure and in a biologically relevant temperature range, e.g., from about 1°C to about 100°C, e.g., from about 34°C to about 40°C, which is the range of human body temperature, e.g., from about 15°C to about 25°C, which is the range of room temperature, or other biologically relevant temperature ranges.

[0037] The UCST of the polyureidoamide can be adjusted to any temperature in the liquid phase of the aqueous solution by the number and ratio of ureidoamide monomer units to comonomer units. In other words, the UCST of the polyureidoamide can be adjusted to any temperature above the freezing point of the aqueous solution but below the boiling point of the aqueous solution. A polyureidoamide having a UCST of about 1°C to about 100°C in aqueous solution at 1 atmosphere means that the UCST is measured at 1 atmosphere, but does not limit the use of the polyureidoamide to 1 atmosphere. A polyureidoamide having a UCST of about 1°C to about 100°C in aqueous solution at 1 atmosphere can be used at pressures below 1 atmosphere. Examples where the ambient pressure is less than 1 atmosphere and a polyureidoamide having a UCST of about 1°C to about 100°C in aqueous solution at 1 atmosphere can be used include terrestrial locations above sea level and outside of aircraft, aerospace vehicles, spacecraft, space satellites or space stations, as well as other low pressure applications involving pressures below 1 atmosphere. Polyureidamides having a UCST of about 1° C. to about 100° C. in aqueous solution at 1 atmosphere can be used at pressures above 1 atmosphere. Examples where polyureidamides having a UCST of about 1° C. to about 100° C. in aqueous solution at 1 atmosphere and ambient pressures above 1 atmosphere can be used include locations on land below sea level, inside and / or outside underwater vehicles or buildings, in pressurized aircraft cabins, and other high pressure applications involving pressures above 1 atmosphere.

[0038] In certain embodiments, the polyureidoamide may exhibit a small change in UCST (ΔT), e.g., a change of about 20° C. or less, over a wide range of salt concentrations, e.g., from greater than 0 to about 160 mM salt. For example, the polyureidoamide may exhibit a ΔT of about 20° C. or less, e.g., about 18° C. or less, e.g., about 15° C. or less, e.g., about 12° C. or less, e.g., about 10° C. or less, over a range of salt concentrations (in aqueous solution) from greater than 0 to about 160 mM, as measured by DLS. The salt of the aqueous solution may be sodium chloride. The small change in UCST over a range of salt concentrations may be used in applications where the polyureidoamide is exposed to salt-containing aqueous solutions.

[0039] The UCST of polyureidoamide homopolymers and copolymers is determined by dynamic light scattering (DLS) analysis. To determine the UCST, the polymer (15 mg) is dissolved in 1.5 mL of Milli-Q water in a 70°C water bath in a vial. The vial is kept in the water bath for at least 1 h before measurement. A cuvette is filled with the polymer solution from the vial. The cuvette is placed in the DLS instrument. DLS measurements of the Z-average particle size of the polymer solution are performed at various temperatures by cooling the polymer solution from 70°C to less than 1°C. The Z-average particle size versus temperature is plotted. The UCST is the temperature at which the curve of the Z-average particle size from low to high temperature decreases to a very small value of the Z-average particle size (typically <5 nm), indicating that the aggregated polymer has dissociated into single molecular polymer chains dissolved in the solution.

[0040] In certain embodiments, the polyureidoamides exhibit UCST in aqueous electrolyte solutions, such as saline. In certain embodiments, the polyureidoamides exhibit UCST in aqueous electrolyte solutions with biologically relevant electrolyte conditions, such as aqueous solutions with sodium ion concentrations greater than 0 to about 160 mM, such as aqueous solutions with sodium ion concentrations of 135 mM to about 145 mM, which is the range of sodium concentrations in human blood. The polyureidoamide homopolymers and copolymers surprisingly exhibited relatively stable UCST as sodium ion concentration increased over the range of sodium ion concentrations from 0 to about 160 mM. This is because sodium ion concentration has only a minimal effect on the overall hydrophobicity or hydrophilicity of the polyureidoamide. In contrast, other known UCST non-polyureidoamides exhibit very different transition temperatures depending on sodium ion concentration, with sodium ion concentration having a large effect on the overall hydrophobicity or hydrophilicity of the non-polyureidoamide polymers.

[0041] In certain embodiments, the polyureidoamide exhibits a UCST in aqueous solution under biologically relevant pH conditions, e.g., a pH of 1.5 to 8, e.g., a pH level of the human stomach of about 1.5 to about 6.5, or a pH level of human blood of about 7.35 to about 7.45, or a pH level of human skin of about 4.5 to about 6.5, or a pH level of saliva in the human mouth of about 6.5 to about 7.5, or a pH level of the human large intestine of about 4.0 to about 7.0.

[0042] In certain embodiments, polyureidoamides exhibiting a UCST can adopt various structures, such as (i) an extended random coil structure, which is hydrophilic in nature and easily wetted or solvated by aqueous liquid media above the UCST, (ii) a collapsed globular structure, which is hydrophobic in nature and not easily wetted or solvated by aqueous liquid media below the UCST, and / or (iii) an aggregate structure of multiple polyureidoamides, which is hydrophobic in nature and not easily wetted or solvated by aqueous liquid media below the UCST. In certain embodiments, the polyureidoamides are reversible between two or more of the various structures.

[0043] It is believed that the amide functional groups of the ureidoamide monomer units constituting the polyureidoamide homopolymer or copolymer participate in hydrogen bonding with water molecules at relatively low temperatures, making the polyureidoamide soluble in water at relatively low temperatures, whereas at relatively high temperatures, the hydrophobicity of the carbon skeleton of the polyureidoamide homopolymer or copolymer dominates over the hydrogen bonding of the amide functional groups, making the polyureidoamide insoluble in water at low temperatures.

[0044] The polyureidamide copolymer may include any suitable amount of comonomer. In certain embodiments, polyureidamide copolymers having a higher percentage of repeat units of hydrophobic comonomers exhibit an increased UCST compared to polyureidamide homopolymers. In certain embodiments, polyureidamide copolymers having a higher percentage of repeat units of hydrophilic comonomers exhibit a decreased UCST compared to polyureidamide homopolymers.

[0045] In certain embodiments, the polyureidoamide copolymer may include a pH-responsive comonomer in any suitable amount. The pH-responsive comonomer of the polyureidoamide copolymer affects the UCST in relation to pH. An example of a pH-responsive comonomer includes vinyl monomers such as acrylic acid, methacrylic acid and other alkyl-substituted acrylic acids, maleic anhydride, maleic acid, 2-acrylamido-2-methyl-1-propanesulfonic acid, N-vinylformamide, N-vinylacetamide, aminoethyl methacrylate, phosphorylethyl acrylate or methacrylate. Another example of a pH-responsive comonomer includes polypeptides derived from amino acids (e.g., polylysine or polyglutamic acid), or polysaccharides (e.g., alginic acid, hyaluronic acid, carrageenan, chitosan, carboxymethylcellulose), or nucleic acids, such as DNA. Another example of a pH-responsive monomer includes a monomer having a pendant pH-sensitive functional group. Examples of pH-sensitive functional groups include, but are not limited to, -OPO(OH)2, -COOH, or -NH2. In certain embodiments, a polyureidoamide homopolymer or copolymer may include a ureidoamide monomer having a pendant pH-sensitive functional group. In certain embodiments, a polyureidoamide copolymer may include a comonomer having a pendant pH-sensitive functional group.

[0046] In certain embodiments, the polyureidoamide homopolymer or copolymer may include ureidoamide monomers with pendant chromophore functional groups and / or comonomers with pendant chromophore functional groups. The chromophore functional group is any functional group that is sensitive to electromagnetic radiation (i.e., visible or non-visible light). Examples of chromophore functional groups include groups that can undergo or cause isomerization between trans and cis forms, groups that can undergo or cause a transition from a relatively non-polar, hydrophobic, non-ionized state to a hydrophilic, ionic state, and groups that polymerize with other monomer or comonomer units in response to electromagnetic radiation.

[0047] In certain embodiments, the polyureidoamide homopolymers or copolymers are stimuli-responsive polymers that undergo a transition in response to a change in temperature, e.g., a reversible or irreversible transition from hydrophilic to hydrophobic or from hydrophobic to hydrophilic character.

[0048] The polyureidamide homopolymer or copolymer may be responsive to one or more stimuli by incorporating one or more sensitivities into the polyureidamide homopolymer or copolymer. For example, the polyureidamide homopolymer or copolymer may be responsive to temperature and to one or more stimuli selected from electrolyte concentration, pH concentration, and electromagnetic radiation. For example, the polyureidamide homopolymer or copolymer may be temperature responsive and electromagnetic radiation responsive. For example, photo-stimulation of chromophore functional groups along the polymer backbone may cause the polymer to transition to a more hydrophobic or hydrophilic conformation, which may promote dissolution / wetting or precipitation of the polymer, depending on the composition and temperature of the polymer. In another example, the chromophore functional groups may absorb light and convert it into thermal energy, causing localized heating, which may stimulate a phase change in a temperature-responsive polymer when the temperature of the system is close to the phase separation temperature.

[0049] The polyureidoamide homopolymer or copolymer may be composed of a linear backbone or may be composed of two or more backbones. In certain embodiments, the polyureidoamide homopolymer or copolymer has a number average molecular weight (Mn) determined by NMR spectroscopy of about 6,000 Da to about 35,000 Da, for example, about 12,000 Da to about 29,000 Da. In certain embodiments, the polyureidoamide homopolymer or copolymer has a Mn determined by triple detection of about 7,000 Da to about 40,000 Da, for example, about 14,000 Da to about 33,000 Da. In certain embodiments, the polyureidoamide homopolymer or copolymer has a Mn determined by RI detection of about 30,000 Da to about 72,000 Da, for example, about 38,000 Da to about 64,000 Da. Mn is the number average molecular weight of a sample of polyureidamide homopolymer or copolymer exhibiting UCST.

[0050] In certain embodiments, the polyureidoamide homopolymer or copolymer has a peak molecular weight (Mp) determined by triple detection of about 16,000 Da to about 50,000 Da, for example, about 20,000 Da to about 40,000 Da. In certain embodiments, the polyureidoamide homopolymer or copolymer has an Mp determined by RI detection of about 38,000 Da to about 82,000 Da, for example, about 50,000 Da to about 75,000 Da. Mp is the molecular weight at the peak of the molecular weight distribution of a sample of polyureidoamide homopolymer or copolymer exhibiting UCST.

[0051] In certain embodiments, the polyureidamide homopolymers or copolymers have a polydispersity index (PDI) of about 1.00 to about 1.30, e.g., about 1.03 to about 1.20, as determined by triple detection gel permeation chromatography. In certain embodiments, the polyureidamide homopolymers or copolymers have a PDI of about 1.10 to about 1.45, e.g., about 1.20 to about 1.35, as determined by RI detection. In certain embodiments, the polyureidamide homopolymers or copolymers have a low PDI of less than 1.30 by triple detection gel permeation chromatography, or a low PDI of less than 1.45 by RI detection, providing a polymer with a more uniform size, shape and / or mass distribution.

[0052] The polymerization process to form the polyureidamide homopolymer or copolymer can be carried out in a solution polymerization process utilizing a solvent such as an organic solvent or an aqueous solvent. The polymerization process to form the polyureidamide homopolymer or copolymer can be carried out in a bulk polymerization process. In a bulk polymerization process, the monomers to be polymerized (and comonomers, if present) are used as the solvent or diluent, but little or no inert solvent is used as the liquid or diluent. In a bulk polymerization process, a small amount of an inert solvent can be used as a catalyst support and scavenger.

[0053] Polyureidoamide homopolymers or copolymers can be prepared by polymerizing ethylenically unsaturated monomers / comonomers by radical, coordination, ionic or other suitable polymerization techniques. The polymerization process for producing polyureidoamide homopolymers or copolymers can be living or non-living. In certain aspects, the polymerization process for producing polyureidoamide homopolymers or copolymers is by living polymerization. Living polymerization is a form of chain polymerization in which irreversible chain termination is substantially absent. A characteristic of living polymerization is that the polymer chain continues to grow as long as the monomers and reaction conditions that support polymerization are provided. The polymer chains prepared by living polymerization can exhibit well-defined molecular structure, predetermined molecular weight, and / or narrow molecular weight distribution or low polydispersity. Examples of living polymerization include ionic polymerization and controlled radical polymerization (CRP). Examples of CRP include, but are not limited to, iniferter polymerization, stable free radical mediated polymerization (SFRP), atom transfer radical polymerization (ATRP) and reversible addition-fragmentation chain transfer (RAFT) polymerization.

[0054] In certain embodiments, the polymerization process for producing polyureidoamide homopolymers or copolymers is carried out using a RAFT polymerization process. The RAFT polymerization process uses a RAFT agent. Suitable RAFT agents for use include thiocarbonylthio groups, which are divalent moieties represented by -C(S)S-. Examples of RAFT agents include, but are not limited to, xanthates, dithioesters, dithiocarbonates, dithiocarbamates, and trithiocarbonate compounds.

[0055] In certain embodiments, the RAFT agent is represented by the general formula (IX): [ka] where R* is an x-valent group, where x is an integer equal to or greater than 1, and Z is independently selected such that the agent can function as a RAFT agent in the polymerization of one or more ethylenically unsaturated monomers. The Z groups can be, independently, organic and / or substituted organic groups that function to impart suitably high reactivity of the C=S moieties in the RAFT agent toward free radical addition. The R* groups can be organic or substituted organic groups that function as free radical leaving groups under the polymerization conditions employed. The R* groups can be monovalent, divalent, trivalent or of higher valence. In certain embodiments, x is an integer ranging from 1 to 20, such as from 1 to 10, or such as from 1 to 5. Thus, R* can be an optionally substituted polymer chain, with the remainder of the RAFT agent provided as multiple groups pendant from the polymer chain.

[0056] In certain embodiments, the RAFT agent is represented by the general formula (X): [ka] wherein Z* is a y-valent group, y being an integer equal to or greater than 2, and R is independently selected such that the agent can function as a RAFT agent in the polymerization of one or more ethylenically unsaturated monomers. The Z* group can be an organic group or a substituted organic group that functions to impart suitably high reactivity of the C=S moieties in the RAFT agent toward free radical addition. The Z* group can be of divalent, trivalent or higher valence. In certain embodiments, y is an integer ranging from 2 to 20, e.g., from 2 to 10 or from 2 to 5. The R groups can independently be organic groups and / or substituted organic groups that function as free radical leaving groups under the polymerization conditions employed.

[0057] In certain embodiments, at least a portion of the RAFT agent is incorporated into a polymer, for example, in certain embodiments, at least the C=S portion of a RAFT agent of Formula (IX) or Formula (X) is incorporated into a polymer.

[0058] Examples of R* in formula (IX) and examples of R in formula (X) include optionally substituted alkyl, alkenyl, alkynyl, aryl, acyl, carbocyclyl, heterocyclyl, heteroaryl, alkylthio, alkenylthio, alkynylthio, arylthio, acylthio, carbocyclylthio, heterocyclylthio, heteroarylthio, alkylalkenyl, alkylalkynyl, alkylaryl, alkylacyl, alkylcarbocyclyl, alkylheterocyclyl, alkylheteroaryl, alkyloxyalkyl, alkenyloxyalkyl, alkynyloxyalkyl, aryloxyalkyl, alkylacyloxy, alkylcarbocyclyloxy, alkylheterocyclyloxy, alkylheteroaryloxy, alkylthioalkyl, alkenylthioalkyl, alkynylthioalkynyl, arylthioalkyl ... Examples of suitable alkyl groups include alkyl, arylthioalkyl, alkylacylthio, alkylcarbocyclylthio, alkylheterocyclylthio, alkylheteroarylthio, alkylalkenylalkyl, alkylalkynylalkyl, alkylarylalkyl, alkylacylalkyl, arylalkylaryl, arylalkenylaryl, arylalkynylaryl, arylacylaryl, arylacyl, arylcarbocyclyl, arylheterocyclyl, arylheteroaryl, alkenyloxyaryl, alkynyloxyaryl, aryloxyaryl, alkylthioaryl, alkenylthioaryl, alkynylthioaryl, arylthioaryl, arylacylthio, arylcarbocyclylthio, arylheterocyclylthio, arylheteroarylthio, and polymeric chains.

[0059] Examples of R* in formula (IX) and examples of R in formula (X) include optionally substituted alkyl, saturated, unsaturated or aromatic carbocyclic or heterocyclic rings, alkylthio, dialkylamino, organometallic species and polymer chains.

[0060] Specific examples of R* in formula (IX) and R in formula (X) include optionally substituted C1-C 18 Alkyl, C2-C 18 Alkenyl, C2-C18 Alkynyl, C6-C 18 Aryl, C1-C 18 Acyl, C3-C 18 Carbocyclyl, C2-C 18 Heterocyclyl, C3-C 18 Heteroaryl, C1-C 18 Alkylthio, C2-C 18 Alkenylthio, C2-C 18 Alkynylthio, C6-C 18 Arylthio, C1-C 18 Acylthio, C3~C 18 Carbocyclylthio, C2-C 18 Heterocyclylthio, C3-C 18 Heteroarylthio, C3-C 18 Alkyl alkenyl, C3-C 18 Alkylalkynyl, C7-C 24 Alkylaryl, C2-C 18 Alkyl acylate, C4-C 18 Alkylcarbocyclyl, C3-C 18 Alkylheterocyclyl, C4-C 18 Alkylheteroaryl, C2-C 18 Alkyloxyalkyl, C3-C 18 Alkenyloxyalkyl, C2-C 18 Alkynyloxyalkyl, C7-C 24 Aryloxyalkyl, C2-C 18 Alkyl acyloxy, C2-C 18 Alkylthioalkyl, C3-C 18 Alkenylthioalkyl, C3-C 18 Alkynylthioalkyl, C7-C 24 Arylthioalkyl, C2-C 18 Alkyl acylthio, C4-C 18 Alkylcarbocyclylthio, C3-C 18 Alkylheterocyclylthio, C4-C 18 Alkylheteroarylthio, C4-C 18 Alkyl alkenyl alkyl, C4-C 18 Alkyl alkynyl alkyl, C8-C 24Alkylarylalkyl, C3-C 18 Alkyl acyl alkyl, C 13 ~C 24 Aryl alkyl aryl, C 14 ~C 24 Arylalkenylaryl, C 14 ~C 24 Arylalkynylaryl, C 13 ~C 24 Aryl acyl aryl, C7-C 18 Aryl acylate, C9-C 18 Arylcarbocyclyl, C8-C 18 Arylheterocyclyl, C9-C 18 Aryl, Heteroaryl, C8-C 18 Alkenyloxyaryl, C8-C 18 Alkynyloxyaryl, C 12 ~C 24 Aryloxyaryl, C7-C 18 Alkylthioaryl, C8-C 18 Alkenylthioaryl, C8-C 18 Alkynylthioaryl, C 12 ~C 24 Arylthioaryl, C7-C 18 Aryl acylthio, C9-C 18 Arylcarbocyclylthio, C8-C 18 Arylheterocyclylthio, C9-C 18 arylheteroarylthio, and polymer chains having number average molecular weights in the range of about 500 to about 80,000, for example, about 500 to about 30,000.

[0061] Examples of Z in formula (IX) and examples of Z* in formula (X) include F, Cl, Br, I, alkyl, aryl, acyl, amino, carbocyclyl, heterocyclyl, heteroaryl, alkyloxy, aryloxy, acyloxy, acylamino, carbocyclyloxy, heterocyclyloxy, heteroaryloxy, alkylthio, arylthio, acylthio, carbocyclylthio, heterocyclylthio, heteroarylthio, alkylaryl, alkylacyl, alkylcarbocyclyl, alkylheterocyclyl, alkylheteroaryl, alkyloxyalkyl, aryloxyalkyl, alkylacyloxy, alkylcarbocyclyloxy, alkylheterocyclyloxy, alkylheteroaryloxy, alkylthioalkyl, arylthioalkyl, alkylacylthio, alkylcarbocyclylthio ... arylthio, alkylheteroarylthio, alkylarylalkyl, alkylacylalkyl, arylalkylaryl, arylacylaryl, arylacyl, arylcarbocyclyl, arylheterocyclyl, arylheteroaryl, aryloxyaryl, arylacyloxy, arylcarbocyclyloxy, arylheterocyclyloxy, arylheteroaryloxy, alkylthioaryl, arylthioaryl, arylacylthio, arylcarbocyclylthio, arylheterocyclylthio, arylheteroarylthio, dialkyloxy-, diheterocyclyloxy- or diaryloxy-phosphinyl, dialkyl-, diheterocyclyl- or diaryl-phosphinyl, cyano (i.e. -CN) and -SR, where R is as defined in relation to formula (IX).

[0062] Specific examples of Z in formula (IX) and Z* in formula (X) include F, Cl, C1 to C 18 Alkyl, C6-C 18 Aryl, C1-C 18 Acyl, Amino, C3~C 18 Carbocyclyl, C2-C 18 Heterocyclyl, C3-C 18 Heteroaryl, C1-C 18Alkyloxy, C6~C 18 Aryloxy, C1-C 18 Acyloxy, C3-C 18 Carbocyclyloxy, C2-C 18 Heterocyclyloxy, C3-C 18 Heteroaryloxy, C1-C 18 Alkylthio, C6~C 18 Arylthio, C1-C 18 Acylthio, C3~C 18 Carbocyclylthio, C2-C 18 Heterocyclylthio, C3-C 18 Heteroarylthio, C7-C 24 Alkylaryl, C2-C 18 Alkyl acylate, C4-C 18 Alkylcarbocyclyl, C3-C 18 Alkylheterocyclyl, C4-C 18 C4~C 18 Alkylheteroaryl, C2-C 18 Alkyloxyalkyl, C7-C 24 Aryloxyalkyl, C2-C 18 Alkyl acyloxy, C4-C 18 Alkylcarbocyclyloxy, C3-C 18 Alkylheterocyclyloxy, C4-C 18 Alkylheteroaryloxy, C2-C 18 Alkylthioalkyl, C7-C 24 Arylthioalkyl, C2-C 18 Alkyl acylthio, C4-C 18 Alkylcarbocyclylthio, C3-C 18 Alkylheterocyclylthio, C4-C 18 Alkylheteroarylthio, C8-C 24 Alkylarylalkyl, C3-C 18 Alkyl acyl alkyl, C 13 ~C 24 Aryl alkyl aryl, C 13 ~C 24 Aryl acyl aryl, C7-C 18 Aryl acylate, C9-C 18Arylcarbocyclyl, C8-C 18 Arylheterocyclyl, C9-C 18 Aryl Heteroaryl, C 12 ~C 24 Aryloxyaryl, C7-C 18 Aryl acyloxy, C9-C 18 Arylcarbocyclyloxy, C8-C 18 Arylheterocyclyloxy, C9-C 18 Arylheteroaryloxy, C7-C 18 Alkylthioaryl, C 12 ~C 24 Arylthioaryl, C7-C 18 Aryl acylthio, C9-C 18 Arylcarbocyclylthio, C8-C 18 Arylheterocyclylthio, C9-C 18 Arylheteroarylthio, dialkyloxy-, diheterocyclyloxy- or diaryloxy-phosphinyl (i.e. -P(=O)OR k 2), dialkyl-, diheterocyclyl- or diaryl-phosphinyl (i.e. -P(=O)R k 2) (wherein, R k is an optionally substituted C1 to C 18 Alkyl, optionally substituted C6-C 18 Aryl, optionally substituted C2-C 18 Heterocyclyl and optionally substituted C7-C 24 alkylaryl), cyano (i.e., -CN) and -SR, where R is as defined in relation to formula (IX).

[0063] In the examples of R*, R, Z, and Z*, it is understood that the multi-component group may include the subgroups in any order, for example, the multi-component group of alkylaryl includes arylalkyl.

[0064] Z, Z*, R or R* may be branched and / or substituted. When Z, Z*, R or R* contains an alkyl moiety which may be substituted, the optional substituents are -CH2- groups in the alkyl chain, -O-, -S-, -NR a -, -C(O)- (i.e. carbonyl), -C(O)O- (i.e. ester) and -C(0)NR a - (i.e., amide), a may be selected from hydrogen, alkyl, alkenyl, alkynyl, aryl, carbocyclyl, heteroaryl, heterocyclyl, arylalkyl, and acyl.

[0065] When referring to an x-, y-, polyvalent, or divalent "form" herein, it is intended to mean that the specified group is an x-, y-, polyvalent, or divalent radical, respectively. For example, when x or y is 2, it is intended that the specified group is a divalent radical. In that case, the divalent alkyl group is in effect an alkylene group (e.g., -CH2-). Similarly, an alkylaryl group in divalent form can be represented, for example, by -(CH4)-CH2-, a divalent alkylarylalkyl group can be represented, for example, by -CH2-(CH4)-CH2-, a divalent alkyloxy group can be represented, for example, by -CH2-O-, and a divalent alkyloxyalkyl group can be represented, for example, by -CH2-O-CH2-. When the term "optionally substituted" is used in conjunction with these x-, y-, polyvalent, or divalent groups, the group can be substituted or fused as described herein. When an x-, y-, polyvalent, or divalent group contains more than one subgroup, e.g., [group A][group B][group C] (e.g., alkylarylalkyl), one or more of these subgroups may be substituted, if possible. One example of a RAFT agent is a benzyl-terminated cyano RAFT agent, although other RAFT agents can be used.

[0066] In certain embodiments, the polyureidamide homopolymer or copolymer may carry additional components (internal and / or external). For example, a drug, therapeutic compound or bioactive agent may be included in the internal and / or external polyureidamide homopolymer or copolymer below the UCST. The drug or therapeutic compound or bioactive agent may be released from the polyureidamide homopolymer or copolymer by transitioning the polymer at a temperature above the UCST.

[0067] A number of embodiments relate generally to temperature-responsive polymers, and more specifically to polymers that exhibit an upper critical solution temperature (UCST) in aqueous solution. Certain embodiments relate to ureidoamide monomer compounds, including one or more ureido and / or thioureido groups, one or more amide and / or thioamide groups, and one or more ethylenically unsaturated groups, and methods for making ureidoamide monomers. In certain embodiments, the ureidoamide monomer compounds include one or more ureido groups, one or more amide groups, and one or more ethylenically unsaturated groups. Polymers, such as homopolymers or copolymers, of certain embodiments are made by polymerization of the ureidoamide monomer compounds. Copolymers can be made by polymerization of the monomer compounds with comonomers, such as hydrophobic comonomers, hydrophilic comonomers, pH-responsive comonomers, photoresponsive comonomers, and combinations thereof. The homopolymers or copolymers exhibit UCST in aqueous solution at a biologically relevant temperature range. In certain embodiments, the homopolymers or copolymers exhibit UCST in aqueous solution at a biologically relevant temperature range and in biologically relevant electrolyte conditions.

[0068] Item 1: A compound containing one or more amide or thioamide groups, one or more ureido or thioureido groups, and one or more ethylenically unsaturated groups.

[0069] Item 2: The compound according to any one of items 1 and 3 to 6, wherein the one or more ethylenically unsaturated groups are represented by formula (I) or formula (II).

[0070] Item 3: A compound according to any one of items 1, 2, and 4 to 6, represented by formula (III). 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur. 1 and R 2 is independently alkylene or haloalkylene. 3 , R 4 , R 5 and R 6 is independently hydrogen, alkyl or haloalkyl.

[0071] Item 4: A compound according to any one of items 1 to 3, 5 and 6, represented by formula (III). 1 , Q 2 , Q 3 and Q 4 are oxygen. 3 , R 4 , R 5 and R 6 are hydrogen.

[0072] Item 5: The compound according to any one of items 1 to 4 and 6, represented by formula (III). 1 is -C2H4-, R 2 is -CH2-.

[0073] Item 6: The compound according to any one of items 1 to 5, wherein the compound is represented by formula (IV):

[0074] Item 7: A method for producing any of the compounds according to any one of items 1 to 6, comprising purifying the compound without chromatography.

[0075] Item 8: A polymer comprising a plurality of repeat units (n) of a monomer unit, each of which independently comprises one or more amide or thioamide groups and one or more ureido or thioureido groups, n being an integer between 10 and 200. The polymer comprises a plurality of repeat units (m) of an optional comonomer unit, m being an integer between 0 and 100, n>m. The polymer comprises at least a portion of a reversible addition-fragmentation chain transfer (RAFT) agent. The polymer is configured to exhibit an upper critical solution temperature of about 1° C. to about 100° C. when present in aqueous solution at 1 atmosphere.

[0076] Item 9: The polymer according to any one of items 8 and 10 to 14, wherein the monomer unit is represented by formula (V). 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur. 1 is alkyl or haloalkyl. 2 and R 3 is independently alkylene or haloalkylene. 4 , R 5 , R 6 and R 7 are each independently hydrogen, alkyl, or haloalkyl.

[0077] Item 10: The polymer according to any one of items 8, 9, and 11 to 14, wherein the monomer unit is represented by formula (V). 1 , Q 2 , Q 3 and Q 4 are oxygen. 4 , R 5 , R 6 and R 7 are hydrogen.

[0078] Item 11: The polymer according to any one of Items 8 to 10 and 12 to 14, wherein the upper critical solution temperature is in an aqueous solution having a sodium ion concentration of more than 0 to about 160 mM.

[0079] Item 12: Number average molecular weight (M) determined by triple detection n 15. The polymer according to any one of items 8 to 11, 13 and 14, wherein the molecular weight of the polymer is from about 7,000 Da to about 40,000 Da.

[0080] Item 13: The polymer according to any one of items 8 to 12 and 14, having a polydispersity of about 1.0 to about 1.3, as determined by triple detection.

[0081] Item 14: The polymer according to any one of Items 8 to 13, wherein the polymer is configured to exhibit an upper critical solution temperature of about 5° C. to about 60° C. when present in the aqueous solution.

[0082] Item 15: A copolymer comprising a plurality of repeat units (n) of a monomer unit and a plurality of repeat units (m) of a comonomer unit. Each monomer unit independently comprises one or more amide or thioamide groups and one or more ureido or thioureido groups, where n is an integer between 10 and 200. Each comonomer unit is selected from the group consisting of hydrophobic comonomers, hydrophilic comonomers, pH-responsive comonomers, photoresponsive comonomers, and combinations thereof, where m is an integer between 1 and 100, and n>m. The copolymer comprises at least a portion of a reversible addition-fragmentation chain transfer (RAFT) agent. The copolymer is configured to exhibit an upper critical solution temperature of about 1° C. to about 100° C. in aqueous solution at 1 atmosphere.

[0083] Item 16: The copolymer according to any one of items 15 and 17 to 24, wherein the monomer unit is represented by formula (V). 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur. 1 is alkyl or haloalkyl. 2 and R 3 is independently alkylene or haloalkylene. 4 , R 5 , R 6and R 7 are each independently hydrogen, alkyl, or haloalkyl.

[0084] Item 17: The copolymer according to any one of items 15, 16 and 18 to 24, wherein the monomer unit is represented by formula (V). 1 , Q 2 , Q 3 and Q 4 are oxygen. 4 , R 5 , R 6 and R 7 are hydrogen.

[0085] Item 18: The copolymer according to any one of items 15 to 17 and 19 to 24, wherein a plurality of the comonomer units are hydrophobic comonomer units.

[0086] Item 19: The copolymer according to any one of items 15 to 18 and 20 to 24, wherein a plurality of the comonomer units are hydrophobic comonomer units that reduce UCST.

[0087] Item 20: The copolymer according to any one of items 15 to 19 and 21 to 24, wherein the comonomer unit is represented by formula (VII). 1 and Q 2 are each independently oxygen or sulfur. 1 and R 2 are each independently alkyl or haloalkyl.

[0088] Item 21: The copolymer according to any one of items 15 to 20, 22 and 23, wherein the comonomer unit is represented by formula (VII). 1 and Q 2 are oxygen atoms.

[0089] Item 22: The copolymer according to any one of Items 15 to 21 and 23, wherein the upper critical solution temperature is in an aqueous solution having a sodium ion concentration of more than 0 to about 160 mM.

[0090] Item 23: The copolymer according to any one of items 15 to 22, wherein the copolymer is configured to exhibit an upper critical solution temperature of about 5° C. to about 60° C. when present in the aqueous solution. EXAMPLES

[0091] The following are examples to illustrate various aspects of the preparation of polyureidoamide homopolymers or copolymers, which are not intended to limit the scope of the claims unless specifically recited in the claims.

[0092] Example 1: Synthesis of 2-(methacryloyloxy)ethylureidoglycinamide (MEGA) While there are many variations and alternatives for the synthesis of MEGA, a ureidoamide monomer compound, in one example of the synthesis, glycinamide hydrochloride (20 g, 18.1 mmol) available from Sigma-Aldrich, St. Louis, Missouri, and potassium carbonate (50 g, 36.2 mmol) were added to 200 mL of dry DMF and stirred for 2 hours. A needle was connected through a septum to maintain an argon environment. The mixture was then transferred to an ice bath and held with stirring for 10 minutes. 2-isocyanatoethyl methacrylate (30.9 g, 20 mmol) available from Sigma-Aldrich, St. Louis, Missouri, was then added dropwise. After the addition of 2-isocyanatoethyl methacrylate was complete, the ice bath was removed and the reaction mixture was stirred at room temperature for approximately 16 hours. The progress of the reaction was monitored by thin layer chromatography confirmation using the eluent DCM / MeOH (9 / 1, V / V). The crude mixture was then added to a large excess of hot acetone (40°C) and stirred for 30 minutes. The acetone mixture was then filtered to remove salt impurities. The filtered acetone mixture was evaporated using a rotary evaporator to remove acetone. The remaining solid was added to a large excess of chilled ether (-20°C) and kept in a freezer for several hours. This ether mixture was filtered and the solid was dried to remove all the solvent. The crude solid was added to 100 mL of acetone and shaken at 40°C for 15 minutes. The soluble fraction was collected and the insoluble fraction was added to an additional 100 mL of acetone. This process was repeated at least three times. The soluble fractions were combined and evaporated to reduce the amount of acetone so that approximately 200 mL of solution remained. The remaining solution was kept in a freezer for recrystallization. The recrystallized solid was filtered and dried under high vacuum overnight. This synthesis is represented by reaction scheme (I). [ka]

[0093] The dried solid 1 H and 13 Analysis was based on C nuclear magnetic resonance (NMR). All NMR spectra were recorded on a Bruker 500 MHz spectrometer using deuterated DMSO.

[0094] Example 2: Synthesis of benzyl-terminated cyano RAFT agents While there can be many variations and alternatives to the synthesis of a benzyl-terminated cyano RAFT agent, one example synthesis involves the synthesis of a disulfide, the synthesis of a benzyl-terminated initiator, and reaction of the disulfide with the benzyl-terminated initiator to form the benzyl-terminated cyano RAFT agent.

[0095] An example of the synthesis of a disulfide is that of bis(butylsulfanylthiocarbonyl) disulfide. Although there are many variations and alternatives to the synthesis, one example of the synthesis involves adding 1-butanethiol (18 g, 0.2 mol) dropwise to a solution of potassium hydroxide (14 g, 0.25 mol) in water (70 mL) and stirring for 30 minutes. Carbon disulfide (31 g, 0.4 mol) is then added to the reaction and stirred for an additional 40 minutes. A solution of p-tosyl chloride (19 g, 0.1 mol) in acetone (110 mL) is added in portions to the reaction and the reaction is stirred for 2 hours. The solvent is concentrated under reduced pressure and the resulting residue is redissolved in CHCl (100 mL), washed with water (3×100 mL), and dried over magnesium sulfate. The product is purified by flash column chromatography (eluent: hexane) to give the disulfide intermediate as a red oil. This synthesis is depicted in reaction scheme (II). [ka]

[0096] An example of the synthesis of a benzyl-terminated initiator is the synthesis of ACVA-benzyl. Although there are many variations and alternatives to the synthesis, in one example of the synthesis, benzyl alcohol, DCC and DMAP were dissolved in dry THF (200 mL). The solution was stirred and cooled to 0° C., and then a solution of ACVA (4,4'-azobis(4-cyanovaleric acid)) (10.0 g in 50 mL of dry THF) was added dropwise. The mixture was stirred at 0° C. for an additional 30 minutes, then at ambient temperature overnight. The salts were removed by filtration, the volatiles were removed under reduced pressure, and the crude product was purified by column chromatography (ethyl acetate / hexane=1 / 1) to give a white solid. This synthesis is represented in reaction scheme (III). [ka]

[0097] While there are many variations and alternatives possible for the synthesis of benzyl-terminated cyano RAFT agents, one example of the synthesis involves the reaction of a disulfide, namely bis(butylsulfanylthiocarbonyl) disulfide, with a benzyl-terminated initiator, for example, ACVA-benzyl. A solution of bis(butylsulfanylthiocarbonyl) disulfide (1.5 g, 4.5 mmol) and ACVA-benzyl (1.5 g, 5.4 mmol) in ethyl acetate (20 mL) was heated to reflux for 20 hours. The solvent was removed by rotary evaporation. The crude product was purified by column chromatography using eluent: hexane / ethyl acetate (1 / 1) to give the benzyl-terminated cyano RAFT agent as a yellow oil. This synthesis is depicted in reaction scheme (IV). [ka] The product 1 H and 13 C nuclear magnetic resonance (NMR) measurements were performed. All NMR spectra were recorded on a Bruker 500 MHz spectrometer using deuterated chloroform.

[0098] Example 3: Synthesis of poly(MEGA) and poly(MEGA)-co-poly(BMA) by RAFT polymerization While there are many variations and alternatives possible for the synthesis of MEGA homopolymers and copolymers, one example of the synthesis involves the RAFT process. As shown in Table 1, homopolymers (Example A) and copolymers (Examples B-E) of MEGA were synthesized with different ratios of hydrophobic monomers (e.g., n-butyl methacrylate (BMA)).

[0099] [Table 1]

[0100] Benzyl-terminated cyano RAFT (8.5 × 10 -3 g, 22.3×10 -3 mmol), various ratios of MEGA (100–60 mol equiv.) to BMA (0–40 mol equiv.) and AIBN (0.73 × 10 -3 g, 4.5×10 -3 1 mmol) was dissolved in 1.5 mL of DMSO in five different vials equipped with a magnetic stir bar. The mixture was deoxygenated by purging with argon for 40 min and then heated to 70 °C for 4 h. The reaction was stopped by cooling to 0 °C in an ice bath and exposed to air. An aliquot was taken to check the conversion rate by NMR. The crude polymer solution was precipitated in a large amount of acetone / methanol (9 / 1, v / v) (for 1 mL of DMSO polymer mixture, about 50 mL of solvent was used). The precipitated solution was stirred for at least 1 h and then filtered. The polymer was then dispersed in a large excess of acetone (1 g of polymer, 50 mL of solvent) and stirred for at least 1 h. This process was repeated once more to completely remove the solvent and unreacted monomer. The polymer was filtered and dried under high vacuum overnight to give a yellow solid product. This synthesis is represented in reaction scheme (V). [ka]

[0101] The dried solid 1H Nuclear Magnetic Resonance (NMR) was used to measure the NMR spectrum. The NMR spectrum was recorded on a Bruker 400 MHz spectrometer using deuterated DMSO. 1 The H NMR spectrum is shown in Figure 1. The hydrogen peak of the solvent (*), some of the hydrogen peaks of the RAFT agent (a-b), the hydrogen peaks of the BMA comonomer (c-e), and the hydrogen peaks of the MEGA monomer (f-j) are shown in Figure 1.

[0102] The conversion of MEGA and BMA to polymers is 1 The H NMR spectral data (e.g., FIG. 1) was used to calculate: Conversion = [(sum of polymer NH peak (a)) / (sum of polymer peak and monomer peak)] × 100%.

[0103] The repeat unit of MEGA in the polymer is 1 1 H NMR spectral data (e.g., FIG. 1) was used to calculate as follows: (sum of polymer NH2 peaks (j)) / (benzyl CH2 protons (b) as reference peak).

[0104] The repeat unit of BMA in the polymer is: 1 Using H NMR spectral data (e.g., FIG. 1), it was calculated as follows: (sum of peaks (c) and (f) at 3.9 ppm−sum of peak (i) at 3.6 ppm) / 2.

[0105] Number average molecular weight (M n ) was calculated using the NMR spectral data of the chain end benzyl CH2 protons (b) as a reference (e.g., as in Figure 1) as follows: Mn = (repeat unit x monomer MW) + (repeat unit x comonomer MW) + RAFT agent MW.

[0106] Number average molecular weight (M n) and peak molecular weight (Mp) were also determined by triple detection GPC and RI detection method.

[0107] SEC traces of MEGA homopolymers and copolymers were measured in eluent DMAc containing 0.03 wt % LiCl using polystyrene standards for calibration and a refractive index detector.

[0108] Triple detection was performed on polymer samples of known concentration prepared by dissolving the dry polymer overnight in eluent DMAc containing 0.03 wt% LiCl and passing it through a 0.45 μm PTFE syringe filter before injection. The solution was filtered using polystyrene standards for calibration and a refractive index detector. Calculations were performed using d n / d c and was based on polymer concentration.

[0109] Refractive index detection was performed on the polymer samples using polystyrene standards for calibration and a refractive index detector, as measured in eluent DMAc containing 0.03 wt % LiCl.

[0110] The molecular weight data is shown in Table 2.

[0111] [Table 2]

[0112] Dynamic light scattering (DLS) analysis was performed on MEGA homopolymers and copolymers to determine the UCST. Each dry polymer (15 mg) was dissolved in 1.5 mL of Milli-Q water at 70 °C in a vial of water containing 0, 50, 100 or 150 mmol of NaCl at 70 °C. The vials were kept in the water bath for at least 1 hour before measurement. Each vial was used to fill a cuvette with the polymer solution. Each cuvette was placed in the DLS instrument. DLS measurements of the Z-average particle size of each polymer solution were performed at various temperatures by cooling the polymer solution from 70 °C to less than 1 °C. The Z-average particle size against temperature was plotted. The UCST is the temperature at which the curve of Z-average particle size from low to high temperature decreases to a Z-average particle size of 0. The UCST data at various sodium concentrations are shown in Table 3.

[0113] [Table 3]

[0114] While the foregoing is directed to embodiments of the disclosure, other and further embodiments of the disclosure may be devised without departing from the basic scope thereof, the scope of the disclosure being determined by the following claims.

Claims

1. one or more amide or thioamide groups; one or more ureido or thioureido groups; One or more ethylenically unsaturated groups A compound comprising: Formula (I): 【Chemistry 1】 It is expressed as During the ceremony, Q 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur; R 1 and R 2 is independently alkylene or haloalkylene; R 3 , R 4 , R 5 and R 6 is independently hydrogen, alkyl or haloalkyl; compound.

2. Q 1 , Q 2 , Q 3 and Q 4 are oxygen, and R 3 , R 4 , R 5 and R 6 and n is 0 or 1. The compound of claim 1, wherein each is hydrogen.

3. R 1 Ga-C 2 H 4 - and R 2 Ga-CH 2 - is, 3. The compound of claim 2.

4. 4. A method for producing a compound according to any one of claims 1 to 3, comprising purifying the compound without chromatography.

5. A polymer comprising: a plurality of repeat units (n) of monomeric units, each repeat unit independently comprising one or more amide or thioamide groups and one or more ureido or thioureido groups, where n is an integer from 10 to 200; a plurality of repeat units (m) of optionally present comonomer units, where m is an integer from 0 to 100 and n>m; At least a portion of the reversible addition-fragmentation chain transfer (RAFT) agent and the polymer is configured to exhibit an upper critical solution temperature of between 1° C. and 70° C. when 15 mg of polymer is present in 1.5 mL of an aqueous liquid medium at 1 atmosphere; The monomer unit has the formula (II): 【Chemistry 2】 It is expressed as During the ceremony, Q 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur; R 1 is alkyl or haloalkyl; R 2 and R 3 is independently alkylene or haloalkylene; R 4 , R 5 , R 6 and R 7 are each independently hydrogen, alkyl or haloalkyl; polymer.

6. Q 1 , Q 2 , Q 3 and Q 4 are oxygen, and R 4 , R 5 , R 6 and R 7 and n is 0 or 1. The polymer of claim 5, wherein each is hydrogen.

7. 7. The polymer according to claim 5, wherein the upper critical solution temperature is in an aqueous solution having a sodium ion concentration of more than 0 to 160 mM.

8. Number average molecular weight (M) determined by triple detection n 7. The polymer according to claim 5 or 6, wherein the molecular weight of the polymer is from 7,000 Da to 40,000 Da.

9. 7. The polymer of claim 5 or 6, having a polydispersity of 1.0 to 1.3, as determined by triple detection.

10. 7. The polymer of claim 5 or 6, wherein the polymer is configured to exhibit an upper critical solution temperature of from 5° C. to 60° C. when 15 mg of polymer is present in 1.5 mL of aqueous liquid medium.

11. A copolymer comprising: a plurality of repeat units (n) of monomeric units, each repeat unit independently comprising one or more amide or thioamide groups and one or more ureido or thioureido groups, where n is an integer from 10 to 200; a plurality of repeat units (m) of comonomer units, each comonomer unit being selected from the group consisting of hydrophobic comonomers, hydrophilic comonomers, pH responsive comonomers, photoresponsive comonomers, and combinations thereof, m being an integer between 1 and 100, and n>m; At least a portion of the reversible addition-fragmentation chain transfer (RAFT) agent and the copolymer is configured to exhibit an upper critical solution temperature of from 1° C. to 70° C. when 15 mg of the copolymer is present in 1.5 mL of an aqueous liquid medium at 1 atmosphere; The monomer unit has the formula (II): 【Chemistry 3】 It is expressed as During the ceremony, Q 1 , Q 2 , Q 3 and Q 4 are each independently oxygen or sulfur; R 1 is alkyl or haloalkyl; R 2 and R 3 is independently alkylene or haloalkylene; R 4 , R 5 , R 6 and R 7 are each independently hydrogen, alkyl or haloalkyl; Copolymer.

12. 12. The copolymer of claim 11, wherein the comonomer unit is a hydrophobic comonomer unit.

13. 13. The copolymer of claim 12, exhibiting a higher upper critical solution temperature compared to a homopolymer of said monomeric unit.

14. The comonomer unit has formula (III): 【Chemistry 4】 It is expressed as During the ceremony, Q 1 and Q 2 are each independently oxygen or sulfur; R 1 and R 2 are each independently alkyl or haloalkyl; The copolymer of claim 12.

15. Q 1 and Q 2 and each is oxygen.

16. 12. The copolymer of claim 11, wherein the upper critical solution temperature is in an aqueous solution having a sodium ion concentration of greater than 0 mM to 160 mM.

17. 12. The copolymer of claim 11, wherein the copolymer is configured to exhibit the upper critical solution temperature of from 5° C. to 60° C. when 15 mg of copolymer is present in 1.5 mL of aqueous liquid medium.