Hollow-core optical fiber and laser system

Abstract

To provide a hollow core photonic crystal fiber (PCF) comprising an outer cladding region and seven hollow tubes surrounded by the outer cladding region.SOLUTION: Each of hollow tubes is fused to an outer cladding to form a ring defining an inner cladding region and a hollow core region surrounded by the inner cladding region. The hollow tubes are not in contact with each other, but are space apart from adjacent hollow tubes. Each hollow tube has an average outer diameter d2 and an average inner diameter d1, and a ratio d1 / d2 is equal to or greater than about 0.8, such as equal to or greater than about 0.85, or equal to or greater than about 0.9. A laser system is also disclosed.SELECTED DRAWING: Figure 7

Description

[Technical Field]

[0001] The present invention relates to hollow-core photonic crystal fibers and laser systems comprising hollow-core optical fibers. [Background technology]

[0002] Hollow-core photonic crystal fibers (PCFs) have been known for many years and are very attractive for use in several applications due to their very low propagation losses, low nonlinear effects, and high damage thresholds compared to solid-core PCFs.

[0003] A hollow-core fiber is essentially an optical fiber that guides light within a hollow region, so that only a small fraction of the optical power propagates within the solid fiber material surrounding the core. The hollow region may be filled with air or any other gas, or may be evacuated to a very low gas pressure.

[0004] Over the years, several types of hollow-core PCFs have been developed, such as hollow-core photonic bandgap fibers as described in, for example, US Pat. No. 6,229,999 and Kagome-designed fibers as described in, for example, US Pat. No. 6,229,999.

[0005] Kagome fibers guide light by the antiresonant effect, allowing for substantially broader spectral transmission than that achieved with photonic bandgap fibers. In recent years, hollow-core anti-resonant fibers (ARFs) have been the subject of intensive research aimed at further improving the fibers, especially with regard to low loss and broad spectral transmission.

[0006] In an attempt to reduce attenuation, [1] proposed a hollow-core fiber in which the hollow core is surrounded by eight identical capillaries. It was concluded that a larger core size is preferable to reduce loss, and that loss reduction can be achieved by increasing the number of capillaries in the cladding.

[0007] Another drawback of prior art hollow-core antiresonant fibers is that they are not pure single-mode waveguides because they also support several higher-order modes (HOMs). These HOMs often have relatively low loss, making it very difficult to excite a pure LPO1 mode without HOM contamination, and furthermore, the HOMs can be excited by bending or external stresses.

[0008] In an attempt to solve this problem and achieve as high a suppression of HOM as possible while maintaining reasonably low loss in the LPO1 mode, a modified fiber design was proposed in [2]. The ARR fiber described in this paper has a central hollow core (inner diameter D) surrounded by six equally spaced, non-contacting capillary tubes (hereafter referred to as hollow tubes) with wall thickness t and inner diameter d, supported within a single thick-walled supporting capillary. The non-contacting glass elements have mode alignment to ensure resonant phase-matched coupling with the higher-order core modes, allowing them to leak at a very high rate into the supporting solid glass sheath. It was found that, with a d / D ratio ≈ 0.68 and a sufficiently thin tube wall T, i.e., t / D = 0.01, extremely high suppression of HOM can be achieved over a broad wavelength band guided by the fiber with low loss.

[0009] US Patent No. 5,999,949 describes a similar anti-resonant hollow-core fiber comprising a first tubular cladding element defining an inner cladding surface, a plurality of second tubular elements attached to the cladding surface and collectively defining a core having an effective radius, the second tubular elements being arranged in a spaced-apart relationship with adjacent ones of the second tubular elements having a gap therebetween, and a plurality of third tubular elements nested respectively within each of the second tubular elements. It was concluded that the optimal number of tubes for suppressing HOM is six. [Prior art documents] [Patent documents]

[0010] [Patent Document 1] US Patent No. 6,892,018 [Patent Document 2] U.S. Patent No. 8,306,379 [Patent Document 3] International Publication No. 15185761 [Non-patent literature]

[0011] [Non-Patent Document 1] Kolyadin et al., Optics Express, Vol. 21, 2013, pp. 9514-9519 [Non-patent document 2] Gunedi et al., "Broad-band robustly single-mode hollow-core PCF by resonant filtering of higher order modes," Cornell University Library Archive (arXiv):1508.06747 [phisics.optics], (August 27, 2015). Summary of the Invention [Problem to be solved by the invention]

[0012] It is an object of the present invention to provide a hollow-core PCF that alleviates at least one of the above-mentioned drawbacks. In one embodiment, it is an objective to provide a hollow-core PCF with high spectral transmission and high suppression of HOM.

[0013] In one embodiment, it is an object to provide a hollow-core PCF that has high single-mode transmission efficiency and is substantially bend-insensitive. In one embodiment, it is an object to provide a hollow-core PCF that can be easily designed to have a desired low-loss transmission band with a bandwidth of at least about 50 nm, preferably with a transmission loss of less than about 50 dB / km.

[0014] In one embodiment, it is an object to provide a hollow-core PCF having a transmission band comprising wavelengths ranging from about 400 nm to about 1200 nm. [Means for solving the problem]

[0015] These and other objects are solved by the present invention and the embodiments thereof as defined in the claims and as described hereinafter. It will be appreciated that the present invention or embodiments thereof have numerous additional advantages that will become apparent to those skilled in the art from the following description.

[0016] The term "radial distance" means a distance determined radially from the central axis of the hollow core. The term "radial" means a direction radially outward from the central axis of the core.

[0017] The term "substantially" as used herein should be construed to mean that normal manufacturing variations and tolerances are included. The term "about" is generally used to include that which is within the uncertainty of measurement. When the term "about" is used in a range, it should be interpreted herein to mean that that which is within the uncertainty of measurement is included in the range.

[0018] It should be noted that the term "comprises / comprising" when used in this specification should be interpreted as an open-ended term, i.e., to specify the presence of specifically stated features, such as elements, units, integers, steps, components and combinations thereof, but does not exclude the presence or addition of one or more other stated features.

[0019] Throughout this specification or the claims, the singular encompasses the plural unless otherwise specified or required by context. Diameters, thicknesses and other structural values ​​are taken to be in cross section of the hollow core PCF unless otherwise specified or clear from the context.

[0020] The hollow-core photonic crystal fiber (PCF) of the present invention comprises an outer cladding region and seven hollow tubes surrounded by the outer cladding region. Each of the hollow tubes is fused to the outer cladding to form a ring defining an inner cladding region and a hollow core region surrounded by the inner cladding region. The hollow tubes are not in contact with each other. For suppression of undesired higher-order modes, it has been found advantageous for each hollow tube to have an average outer diameter, designated d2, and an average inner diameter, designated d1, with the d1 / d2 ratio being greater than or equal to about 0.8.

[0021] The average outer diameter d2 and / or the average inner diameter of each hollow tube may be equal or different from one hollow tube to another. In one embodiment, d1 and / or d2 are substantially the same for at least three hollow tubes, such as for all seven hollow tubes.

[0022] In accordance with the present invention, and in light of all the teachings of prior art hollow-core PCFs, it has surprisingly been found that hollow-core PCFs having a seven-tube non-contact inner cladding structure provide significantly enhanced suppression of higher order modes (HOMs) than hollow-core PCFs having six tubes non-contacting the inner cladding, as previously described. In particular, and as shown in the examples, it has been found that hollow-core PCFs of the present invention having seven tubes non-contacting the inner cladding structure provide enhanced suppression of HOMs with azimuthal numbers greater than one, such as third-order HOMs, while at the same time having low loss in the fundamental mode at least in a transmission band less than 2 μm, and preferably less than 1.5 μm.

[0023] The term "transmission band" is used herein to mean a band having a bandwidth of transmission wavelengths of at least about 10 nm, such as at least about 25 nm, preferably at least about 50 nm, or even at least about 100 nm.

[0024] The term "low-loss transmission band" means a transmission band having a transmission loss of less than about 100 dB / km, preferably less than about 60 dB / km, and more preferably less than about 50 dB / km for light in its fundamental mode.

[0025] It has been found that by increasing the d1 / d2 ratio, low loss transmission bands can be achieved at even lower wavelengths, such as low loss transmission bands having wavelengths less than 1200 nm, such as less than 1 μm, such as less than 800 μm, such as less than 600 μm, etc. Advantageously, the d1 / d2 ratio is about 0.85 or greater, such as about 0.9 or greater.

[0026] The outer cladding comprises a solid cladding material and is preferably made entirely of a solid material. In one embodiment, each hollow tube is spaced substantially equally from its neighboring hollow tube, thereby achieving very high Gaussian beam quality. In an alternative embodiment, each hollow tube is spaced a different distance from its neighboring hollow tube. In the latter embodiment, the difference in distance between neighboring hollow tubes is achieved by varying the outer diameter d2 of the tube. When the inner diameter d1 and / or outer diameter d2 of the hollow tubes are different, the inner diameter d1 and outer diameter d2 are calculated as the average of d1 and d2, respectively, unless the calculation is for the thickness of the hollow tube or unless otherwise specified. Thus, the d1 / d2 ratio is determined by the average of d1 and d2. It has been found that for optimal suppression of HOM, the minimum distance between neighboring hollow tubes should be relatively small, preferably less than about half the outer diameter d2 of the hollow tube. On the other hand, this distance should not be made too small, since otherwise there is a risk that this distance will be lost completely along part or all of the length of the fiber due to surface tension and material attraction during fiber drawing. To avoid this risk, the minimum distance between adjacent hollow tubes is at least 0.01 times d2.

[0027] Advantageously, the minimum distance between adjacent hollow tubes is at least about 0.1 μm, such as at least about 1 μm, such as at least about 2 μm, such as at least about 5 μm.

[0028] In one embodiment, the minimum distance between adjacent hollow tubes is about 5 μm or less, such as about 4 μm or less. The center-to-center distance Λ between adjacent hollow tubes is between about 1.01×d2 and about 1.5×d2, such as between 1.05×d2 and 1.2×d2.

[0029] The hollow tubes advantageously have substantially parallel central axes. In practice, the central axes of the hollow tubes may deviate slightly from a straight line due to processing variations. The hollow tubes may, for example, be helical about the core at a very long pitch, for example up to 1 km, for example between 1 cm and 100 m.

[0030] Due to the structure of the hollow-core PCF, the core may, in principle, be designed with a core region of any diameter. Advantageously, the core region is substantially circular. In one embodiment, the core region is not circular, but has angles such as an ellipse or a substantially pentagon. The core diameter D is defined as the diameter of the largest circle inscribed by the seven hollow tubes.

[0031] Advantageously, the hollow core region has a core diameter D of from about 10 μm to about 100 μm, such as from about 10 μm to about 60 μm. The optimal core diameter D is found to be scalable to the central wavelength of the transmission band of the hollow-core PCF.

[0032] For a center wavelength of about 1.0 μm, the core diameter D is advantageously about 20 μm to about 50 μm, such as about 25 μm to about 40 μm. The preferred core diameter D scales directly with the center wavelength of the transmission band of the hollow-core PCF.

[0033] It has been found that hollow-core PCFs can have very high beam quality even when the core is relatively large. In one embodiment, the beam quality M 2 is about 1.75 or less, such as about 1.6 or less, such as about 1.5 or even less.

[0034] In one embodiment, the average d2 / D of the outer tube diameter to the core diameter is from about 0.5 to about 0.75, such as from about 0.65 to about 0.72, which ensures a desired minimum distance between hollow tubes and highly effective HOM suppression (especially for third- and fourth-order HOM).

[0035] Furthermore, it was shown that the modal quality of the beam obtained from hollow-core PCFs with an average d2 / D ratio of the outer tube diameter to the core diameter ranging from about 0.5 to about 0.75 was very high. It has been found that the wall thickness of the hollow tube significantly influences one or more low-loss transmission bands of a hollow-core PCF. Indeed, it has been found that the relevant wall thickness t is the wall area of ​​the hollow tube facing the core center.

[0036] It has thus been found that the wall thickness t (or the average value of t) of the region of the hollow tube facing the core center primarily affects the wavelength-related position of the low-loss transmission bands. Generally, a hollow-core PCF may have one or more low-loss transmission bands, such as one, two, three, four, or even more low-loss transmission bands. Advantageously, a hollow-core PCF has at least three low-loss transmission bands, such as at least four low-loss transmission bands. To obtain one or more low-loss bands less than 0.2 μm, it is desirable for the wall thickness t to be at most about 2.1 μm, such as at most about 1 μm, e.g., in the range of about 150 to about 350 nm, or in the range of about 650 to about 850 nm, or in the range of about 900 to about 2.1 μm.

[0037] For example, for a hollow-core PCF according to one embodiment of the present invention, it has been found that the fiber has low-loss transmission from 1030 to 1064 nm with a wall thickness t=150-350 nm, preferably 200-300 nm (the low-loss transmission band with the highest wavelength—Band I), a wall thickness t=650-850 nm, preferably 700-800 nm (the low-loss transmission band with the second highest wavelength—Band II), a wall thickness five times the first range (i.e., 5×150 nm to 5×350 nm) for the third transmission band comprising 1030-1064 nm, seven times the first range for the fourth transmission band comprising 1030-1064 nm, etc.

[0038] Advantageously, the hollow core PCF comprises at least one wavelength from between 200 nm and 4000 nm, such as between 400 and 2000 nm, such as between 800 and 1600 nm, such as between 1000 and 1100 nm, where the hollow core is designed to guide light in the fundamental mode with losses less than about 1000 dB / km.

[0039] Advantageously, the hollow core PCF has a fundamental mode low loss transmission band with a transmission loss of less than about 100 dB / km, preferably less than about 60 dB / km, more preferably less than 50 dB / km, comprising wavelengths in the interval between 1000 and 1100 nm, preferably at least 1030-1064 nm.

[0040] In one embodiment, the hollow-core PCF has a HOM transmission loss of greater than about 2000 dB / km in the low fundamental mode transmission band, thereby ensuring effective single-mode transmission.

[0041] Hollow-core PCFs have further been found to be substantially insensitive to bending; for example, a hollow-core PCF in accordance with one embodiment of the present invention has low loss of less than about 5% / km at 1030-1060 nm when wound with a diameter of about 6 cm.

[0042] Advantageously, the wall thickness t of each of the hollow tubes is substantially the same. Preferably, the hollow tubes are substantially identical and equally spaced from adjacent hollow tubes, which makes the hollow-core PCF easier to design for transmission of desired wavelengths.

[0043] In one embodiment, at least one of the tubes has a different wall thickness t than at least one other of the hollow tubes. Preferably, three of the hollow tubes have one wall thickness and the remaining four hollow tubes have another wall thickness. With this configuration, it has been found that the hollow-core PCF exhibits birefringence primarily due to the difference in wall thickness t and the relative positions of the hollow tubes with the larger and smaller wall thicknesses t.

[0044] In one embodiment, at least one of the hollow tubes has a wall thickness that is at least about 5% greater than the wall thickness of at least one of the other hollow tubes, and preferably at least one of the hollow tubes has a wall thickness that is at least about 10% greater than the wall thickness of at least one of the other hollow tubes.

[0045] In one embodiment, each of the hollow tubes is substantially circular. In practice, it is very difficult to obtain perfectly circular hollow tubes, firstly due to slight distortion when fusing each hollow tube inside the outer cladding, and secondly due to the fact that hollow tubes may be attracted to adjacent hollow tubes during fiber drawing.

[0046] In one embodiment, each of the hollow tubes has a large inner diameter D l and a long inner diameter D l Short inner diameter D perpendicular to s and D l is determined in the radial direction from the central axis of the hollow core. Advantageously, D s / D l The ratio is from about 0.5 to about 0.99, such as from about 0.8 to about 0.99.

[0047] In one embodiment, D s / D l The ratio may be greater than about 0.9, such as greater than about 0.95, which is practical to manufacture. In one embodiment, D s / D l The ratio is less than about 0.95, such as less than 0.9, which results in a relatively large core diameter D, which can further reduce the transmission loss of the fundamental mode.

[0048] In one embodiment, at least one of the hollow tubes comprises at least one nested small tube disposed within the hollow structure of the hollow tube, the small tube fused to the hollow tube and preferably aligned with the fusion to the outer cladding, i.e., furthest from the core region.

[0049] The hollow tube with one or more nested tubes may be, for example, as described for the PCF in WO 15185761, comprising second tubular elements with third tubular elements nested within each second tubular element, except that the hollow core PCF has seven second tubular elements with nested third tubular tubes.

[0050] The tubules advantageously have an average outer diameter d that is substantially smaller than the average inner diameter d of the hollow tube. sub The average outer diameter d2 sub is preferably at most about 0.9 x d2 of the hollow tube, such as at most about 0.9 x d2, and preferably the inner tubule is fused to the hollow tube at its greatest radial distance from the central axis of the core.

[0051] In one embodiment, at least one of the hollow tubes comprises one or more nodules located in a region of one or more of the hollow tubes facing the core center, preferably the nodules are located at the boundary of the hollow core region, and the nodules are preferably positioned to be anti-resonant at the operating wavelength so that light in the fundamental mode is substantially excluded from the nodules, thereby providing stronger confinement of the fundamental mode to further reduce losses of light in the fundamental mode transmitted in the core region of the hollow-core PCF.

[0052] The nodules may advantageously be in the form of nodule-like or ball-like structures, or in the form of locally thickened areas of wall extending along at least part of the length of the fiber. Such nodules are sometimes called nodes or nodules in prior art optical fibers, as described, for example, in U.S. Pat. No. 7,321,712. Advantageously, the nodules and the remainder of the hollow tube are made of the same material.

[0053] The core region and / or hollow tubes may, in principle, contain any fluid. Preferably, the core region and / or hollow tubes, independently of one another, contain a gas determined at standard ambient temperature and pressure (SATP) as an absolute pressure of exactly 100,000 Pa at a temperature of 25° C. Suitable gases include air, argon, nitrogen, or a mixture containing any of the aforementioned gases. Optionally, the hollow core region and / or hollow tubes, independently of one another, can be evacuated (evacuated to have a very low gas pressure) or filled with a pressurized gas.

[0054] In one embodiment, the hollow core region and / or hollow tube is evacuated to a pressure of about 100 hPa (1 mbar) or less, such as about 10 hPa (0.1 mbar) or less, such as about 1 hPa (0.01 mbar) or less, at standard temperature.

[0055] In one embodiment, the hollow core region and / or hollow tube is pressurized to a pressure of up to 200 kPa (2 bar), such as up to about 150 kPa (1.5 bar) at standard temperature.

[0056] The outer cladding region may, in principle, be any dimension that provides sufficient mechanical support for the hollow-core PCF relative to the hollow tube. In one embodiment, the outer cladding region has an outer diameter of at least about 125 μm, 150 μm, such as at least about 200 μm.

[0057] In general, it is desirable to fabricate hollow-core PCFs from a single material, preferably glass, and more preferably silica, optionally doped with an index-modifying dopant. In one embodiment, one or more, e.g., all, of the hollow tubes are fabricated from doped silica, while the outer cladding region is fabricated from undoped silica. The dopant may include, for example, an index-modifying material such as F, Ge, P, B, or a combination thereof.

[0058] Furthermore, it has been found that confinement losses can be reduced by providing an outer cladding region with a photonic bandgap structure surrounding the inner cladding region. The photonic bandgap structure may be provided by any means, for example, by providing a refractive index grating in the outer cladding region with concentric rings of different refractive index and / or by including a microstructure with different refractive index.

[0059] In one embodiment, the outer cladding region has a refractive index N ocand a plurality of inclusions having a refractive index different from that of the background material. Advantageously, the inclusions have a refractive index lower than that of the background material. The inclusions preferably extend substantially parallel to the core region. The inclusions may extend for a length section of the hollow-core PCF or for substantially the entire length of the hollow-core PCF.

[0060] In one embodiment, the plurality of inclusions in the outer background material are arranged in a cross-sectional pattern comprising at least two rings of inclusions surrounding the inner cladding region, such as at least three rings of inclusions, such as at least four rings.

[0061] "Ring of inclusions" refers to inclusions in the outer cladding that are aligned in a ring configuration having substantially equal radial distances from the core and surrounding the core. Typically, the ring of inclusions is not perfectly circular, but is shaped with multiple rounded corners, such as a hexagonal shape. Preferably, all inclusions in the ring of inclusions are substantially the same size and are preferably made from the same solid material, voids, and / or gas.

[0062] The background material may advantageously be silica, such as undoped or doped silica. The dopants may include refractive index modifying materials, such as, for example, F, Ge, P, B, or combinations thereof.

[0063] In one embodiment, the plurality of inclusions within the outer background material are arranged in a substantially hexagonal pattern. In one embodiment, the plurality of inclusions are voids or made from a gas such as air.

[0064] The diameter of the inclusions is advantageously selected to minimize loss at a selected wavelength or range of wavelengths, and thus the diameter can be selected to optimize the desired transmission profile.

[0065] In one embodiment, the inclusions have substantially the same diameter. Advantageously, the plurality of inclusions have an average diameter (d inc )

[0066] It has also been shown that the distance between each inclusion is related to optimizing (minimizing) confinement loss. In one embodiment, to optimize confinement loss, the inclusions have a pitch (Λ) of at most about 6 μm, such as at most about 5 μm, such as at most about 4 μm, for example, between about 2 μm and 4 μm. inc ) are placed.

[0067] In one embodiment, the inclusions have a pitch (Λ) of up to about 3.5 μm, such as up to about 3 μm, such as up to about 2.5 μm, such as between about 1.1 μm and 2 μm. inc ) are placed.

[0068] The present invention also includes a laser system for transmitting laser light to a user device, the laser system comprising a laser source and a fiber transmission cable for transmitting light from the laser source to the user device, the fiber transmission cable comprising the hollow-core PCF described above.

[0069] A fiber transmission cable comprising a hollow core PCF may preferably have a length of up to 50 m, such as from about 0.3 m to about 20 m, such as from about 1 m to about 15 m.

[0070] Advantageously, the laser source is configured to generate laser light pulses and is optically connected to the fibre transmission cable, preferably the laser source is a femtosecond laser source.

[0071] In one embodiment, the laser light source may be arranged to deliver light directly to the hollow-core PCF, for example by fusing it to the hollow-core PCF. In one embodiment, the laser light source is arranged to deliver light to the hollow-core PCF via one or more optical elements and / or via free space.

[0072] In one embodiment, the laser source has a pump duration of about 30 fs to about 30 ps, ​​for example, about 100 fs to about 10 ps. In one embodiment, the laser source has a peak power determined at the exit of the laser source of at least about 5 kW, such as at least about 10 kW, such as at least about 30 kW, such as at least about 50 kW.

[0073] The laser source is advantageously a mode-locked laser source. In one embodiment, the laser source is an actively mode-locked laser. In one embodiment, the laser source is a passively mode-locked laser. The mode-locked laser preferably comprises one or more amplifiers.

[0074] In one embodiment, the hollow-core PCF is configured to guide light, preferably single-mode light, having at least one wavelength in the range of about 200 nm to about 4.5 μm, preferably at least one wavelength in the range of 1000 nm to about 1100 nm.

[0075] In one embodiment, the hollow core PCF is configured to guide a continuous wave of light wavelengths, preferably spanning at least about 0.1 μm, such as at least about 0.3 μm, such as at least about 0.5 μm.

[0076] In one embodiment, the hollow-core PCF has a first fiber end configured to connect to a user device and a second fiber end optically connected to an output fiber of a laser source via a fiber coupling structure. The fiber coupling structure preferably provides protection for the first fiber end and preferably for an end face of the first fiber end to ensure that the end face and / or hollow core are not contaminated with dust, moisture, or the like. In addition to ensuring a secure, low-loss connection, the coupling structure may include other elements such as lenses, such as focusing lenses, graded-index elements, or those generally known in the art for hollow-core fiber coupling structures.

[0077] In one embodiment, the fiber coupling structure comprises a focusing lens, such as that described in US Pat. No. 8,854,728. In one embodiment, the fiber coupling structure comprises a graded index element (GRIN), such as that described in US Patent Application Publication No. 2003 / 0068150.

[0078] In one embodiment, the fiber coupling structure includes a protective element such as that described in US Pat. No. 7,373,062. In a preferred embodiment, the first fiber end is mounted in a ferrule structure, preferably a "photonic crystal fiber assembly." The ferrule assembly is attached to the ferrule structure described in Danish Patent Application No. 201570876 entitled "FERRULE ASSEMBLY" which is incorporated by reference into the present disclosure, provided that in the event of a conflict between the subject matter expressly disclosed herein and the incorporated subject matter, the content of the subject matter expressly disclosed herein shall prevail.

[0079] The hollow-core PCFs disclosed herein may advantageously be produced by drawing from a preform, with the drawing being carried out under controlled pressure within the hollow tube, as described, for example, in U.S. Pat. Nos. 6,954,574, 8,215,129, 7,793,521, and / or Danish Patent Application No. 201670262, entitled "A RING ELEMENT FOR A PREFORM, A PREFORM AND AN OPTICAL FIBER DRAWN FROM THE PREFORM."

[0080] The preform is advantageously manufactured by providing a hollow tube for the outer cladding region and seven hollow tubes for the inner cladding region, the hollow tube for the outer cladding region having an inner diameter that is two times larger, such as at least three times larger, such as at least four times larger, than the outer diameter of the seven hollow tubes, or, if different, the largest outer diameter of the seven hollow tubes for the inner cladding region. Preferably, the outer cladding region has an inner diameter large enough to allow the seven hollow tubes to be placed inside the hollow tube for the outer cladding region in contact with each other, without the seven hollow tubes touching each other. To position the seven hollow tubes inside the hollow tube for the outer cladding region, short sections of support elements (e.g., glass tubes or rods) may be placed at each end of the hollow tubes. After fusing the seven hollow tubes to the hollow tube for the outer cladding region, the ends of the fused hollow tubes with the support elements may be trimmed off.

[0081] The preforms can then be drawn in a fiber draw tower, preferably with individual or common pressure control of the pressure in each hollow tube simultaneously. In one embodiment, pressure control in each of one or more of the hollow tubes of the preform, also referred to as "elongated air holes" or simply "air holes," is provided by positioning a pressure tube between the air hole and a pressure source that ensures that the pressure within the hollow tube is controlled at a desired level via the pressure tube during drawing of fiber from the preform.

[0082] Advantageously, the pressure tube is a hollow pressure tube. "Inside the tube" refers to inside the hollow part of the pressure tube. Thus, in one embodiment, the method includes inserting a first end of a pressure tube into a cavity in the preform at a first end of the preform, and exposing the cavity in the preform to a controlled pressure via the pressure tube during drawing. Advantageously, at least a pressure tube length section including the first end of the pressure tube is inserted into the elongated cavity in the preform. The pressure tube length section should preferably have a length of at least about 0.5 mm, such as from about 1 mm to about 20 cm, such as from about 2 mm to about 5 cm, such as from about 0.5 to 1 cm.

[0083] In practice, the pressure tube length desirably has a length sufficient to provide a seal between the pressure tube length and the elongated hole, but cannot be too long because the length of the preform that includes the pressure tube length may not be drawn into fiber in one embodiment, or, in an alternative embodiment, if drawn into fiber, the resulting fiber will have different properties than a fiber drawn from preform material without the tube length.

[0084] It has been found that a secure gas connection can be obtained between the elongated cavity and the pressure tube by simply inserting a first end of the pressure tube into the cavity and, optionally, by causing the pressure tube length section to expand so that its outer surface conforms to the circumferential surface of the elongated cavity and / or by applying a sealant such as adhesive, epoxy, grease and / or rubber or any other flexible sealant.

[0085] The pressure tube advantageously has an outer diameter and circumference selected to fit into the cavity of the preform. The cross-sectional shape of the cavity may be circular or elliptical or any other suitable shape. The surface defining the cavity is also referred to as the circumferential surface of the elongated cavity. The pressure tube preferably has an outer cross-sectional shape corresponding to the cross-sectional shape of the cavity in the preform, but with an average diameter slightly smaller than the average diameter of the cavity in the preform, allowing the first end of the pressure tube to be inserted into the cavity.

[0086] In one embodiment, the pressure tube, or at least a pressure tube length section of the pressure tube, has an average outer diameter that is about 80% to up to 100% of the average inner diameter of the pores, such as about 90% to about 99% of the average diameter of the pores.

[0087] Advantageously, the pressure line has a supply section that is outside the cavity, i.e. the part of the pressure line that leads from the cavity to the gas connection to the pressure source. In one embodiment, the supply section of the pressure tube has a supply opening in pneumatic connection with a pressure source to control the pressure within the cavity.

[0088] In one embodiment, the supply section of the pressure tube has a supply opening located in the pressure regulation chamber. By adjusting the pressure in the pressure regulation chamber, for example by a pressure source, the pressure in the pressure tube is also adjusted, thereby adjusting the pressure in the elongated cavity.

[0089] In one embodiment, the supply section of the pressure tube has a supply opening that is directly connected to a pressure source to regulate the pressure in the pressure tube, thereby regulating the pressure in the elongated cavity. The pressure tube can in principle be made from any material. In one embodiment, the pressure tube is made from a thermoformable material, for example a material that can be formed or drawn in a fiber draw tower. Advantageously, the pressure tube is made from silica, optionally with a polymer coating. In one embodiment, at least the feed section of the pressure tube has an outer polymer coating, and optionally the pressure tube length is free of the polymer coating. The polymer coating increases the flexibility of the pressure tube and reduces the risk of the pressure tube breaking.

[0090] By providing a silica pressure tube with a pressure tube length having an uncoated pressure tube length and a pressure tube supply section with a polymer coating, a desirably large hollow cross-sectional diameter for the pressure tube can be achieved while at the same time making the pressure tube supply section desirably flexible and break-resistant.

[0091] As previously mentioned, the several cavities in the preform may be pressure controlled by pressure tubes as previously mentioned, which may be connected to the same pressure source or to different pressure sources. All features of the invention and embodiments of the invention described above, including ranges and preferred ranges, can be combined in various ways within the scope of the invention, unless there is a specific reason why such features should not be combined.

[0092] The above and / or additional objects, features and advantages of the present invention will become more apparent from the following detailed description of illustrative and non-limiting embodiments of the present invention, taken in conjunction with the accompanying drawings. [Brief explanation of the drawings]

[0093] [Figure 1] 1 shows a cross section of one embodiment of a hollow core PCF of the present invention, with one of the hollow tubes enlarged to show the inner diameter d1, outer diameter d2, and wall thickness t. [Figure 2] 1 shows a cross section of one embodiment of a hollow core PCF of the present invention, in which some of the hollow tubes have a larger wall thickness t than others of the hollow tubes. [Figure 3] FIG. 1 shows a cross section of one embodiment of a hollow core PCF of the present invention, in which the hollow tube is oval. [Figure 4] FIG. 1 shows a cross section of one embodiment of a hollow core PCF of the present invention in which a hollow tube comprises nested tubelets that are placed within the hollow structure of the hollow tube and fused to the hollow tube. [Figure 5] FIG. 1 shows a cross section of one embodiment of a hollow core PCF of the present invention, in which the hollow tube comprises nodules located in the region facing the core center. [Figure 6] FIG. 1 shows a cross section of one embodiment of a hollow-core PCF of the present invention with single-mode light launched into the hollow-core PCF. [Figure 7] 2 is a graph illustrating several low-loss transmission bands of a hollow-core PCF according to one embodiment of the present invention. [Figure 8] 1 is a graph showing a wide low-loss transmission band of a hollow-core PCF according to an embodiment of the present invention. [Figure 9] 1 is a graph showing the suppression of HOM for a prior art hollow-core PCF having six hollow tubes. [Figure 10] 10 is a graph showing the suppression of HOM for a hollow-core PCF of one embodiment of the present invention having seven hollow tubes. [Figure 11] 1 is a schematic diagram of a laser system and user equipment according to one embodiment of the present invention. [Figure 12] 1 shows a first end of a preform for one embodiment of a hollow-core PCF of the present invention having seven hollow tubes forming seven elongated cavities, with the first end of each pressure tube inserted into each cavity for pressure control of the cavities during drawing. [Figure 13a] FIG. 2 illustrates a hollow-core PCF according to one embodiment of the present invention, comprising an outer cladding region comprising a photonic bandgap structure. [Figure 13b] 13b is a graph showing transmission loss for two variations of the hollow-core PCF of the embodiment of FIG. 13a. [Figure 14] 10 is a graph showing measurements of beam quality M2 of the fiber produced in Example 1. DETAILED DESCRIPTION OF THE INVENTION

[0094] The drawings are simplified and schematic for clarity, and the same reference numerals are used throughout to refer to the same or corresponding parts. 1, the hollow-core PCF of the present invention comprises an outer cladding region 1 and seven hollow tubes 2 surrounded by the outer cladding region. Each hollow tube 2 is fused to the outer cladding 1 at a melting point 3 to form a ring defining an inner cladding region and a hollow core region 4 surrounded by the inner cladding region and having a core diameter D.

[0095] The hollow tubes do not touch each other and are generally referred to as non-touching hollow tubes. As shown in the close-up of the hollow tubes, the hollow tubes 2 each have an average outer diameter d2 and an average inner diameter d1, and a wall thickness t of each hollow tube 2 at the region facing the center. The outer cladding 1 has an inner diameter ID and an outer diameter OD. In this embodiment, the hollow tubes 2 are identical and substantially circular in cross section.

[0096] 2, the hollow-core PCF comprises an outer cladding region 11 and seven non-contacting hollow tubes 12a, 12b surrounded by the outer cladding region, the hollow tubes 12a, 12b fused to the outer cladding 11 at a melting point 13 to form a ring defining an inner cladding region and a hollow core region 14 surrounded by the inner cladding region. Three of the non-contacting hollow tubes 12a have a greater wall thickness t than the remaining four non-contacting hollow tubes 12b. As shown, each of the seven non-contacting hollow tubes 12a, 12b has a uniform thickness, which facilitates the manufacture of the hollow-core PCF.

[0097] 3, the hollow-core PCF comprises an outer cladding region 21 and seven identical, non-contacting hollow tubes 22 surrounded by the outer cladding region, the hollow tubes 22 fused to the outer cladding 21 to form a ring defining an inner cladding region and a hollow core region 24 surrounded by the inner cladding region. The hollow tubes 22 are elliptical, each having a long inner diameter D l and a long inner diameter D l Short inner diameter D perpendicular to s and Dl is determined in the radial direction.

[0098] 4, the hollow-core PCF comprises an outer cladding region 31 and seven identical, non-contacting hollow tubes 32 surrounded by the outer cladding region, which are fused to the outer cladding region 31 at melting points 33 to form a ring defining an inner cladding region and a hollow core region 34 surrounded by the inner cladding region. The hollow tube 32 comprises nested subtubes 35 disposed within the hollow structure of the hollow tube and fused to the hollow tube at melting points 33, each at a maximum radial distance from the central axis of the core.

[0099] 5, the hollow-core PCF comprises an outer cladding region 41 and seven non-contacting hollow tubes 42a, 42b surrounded by the outer cladding region, the hollow tubes 42a, 42b fused to the outer cladding 41 to form a ring defining an inner cladding region and a hollow core region 44 surrounded by the inner cladding region. Four of the non-contacting hollow tubes 12a have uniform wall thicknesses, while the remaining three non-contacting hollow tubes 42b comprise nodules 45 located in the region of each hollow tube facing the core center. Because the outer diameter d2 of each of the non-contacting hollow tubes 42a, 42b is substantially the same, the nodules 45 are located at the boundary of the hollow core region.

[0100] In the embodiment shown in FIG. 6, the hollow-core PCF has essentially the same structure as the hollow-core PCF of FIG. 1. A single-mode laser source (not shown) is positioned to irradiate the PCF with laser light at a wavelength in the low-loss transmission band of the PCF. As shown by reference numeral 6, the beam transmitted through the PCF has Gaussian beam quality and is completely single-mode even after 5 meters or even 10 meters of transmission. After 10 meters of transmission, the loss of the fundamental mode is very small, and the transmission efficiency is, for example, greater than 85%, e.g., greater than 90%.

[0101] The graph in Figure 7 shows several low-loss transmission bands for a fiber having the structure shown in Figure 1, with a core dimension D of approximately 30 μm and t=750 nm. The bands are numbered in ascending order from the longest wavelength band to the shorter wavelength band. As can be seen, the hollow-core PCF has four low-loss transmission bands, three of which have wavelengths less than 1.2 μm.

[0102] The graph in Fig. 8 shows a detailed view of the transmission loss of the hollow-core PCF in Fig. 1 for transmission band II, D = 30 μm and t = 750 nm. It can be seen that the low-loss transmission band is very wide, with a bandwidth of 200–250 nm around 1.064 μm.

[0103] Simulations were performed for a hollow-core PCF with six hollow tubes (a prior art hollow-core PCF) and a hollow-core PCF with seven hollow tubes (one embodiment of the present invention). Simulations were performed at 1032 nm with D=30 μm and t=750 nm.

[0104] 9 and 10 show the HOM extinction ratio versus d / D (D=Dcore) for a prior art hollow-core PCF with six hollow tubes (FIG. 9) and a hollow-core PCF of one embodiment of the present invention with seven hollow tubes (FIG. 10).

[0105] As can be seen in Fig. 10, an optimal d / D ratio between 0.6 and 0.75 ensures the resonant coupling of Lp11-like modes and some other higher-order HOMs to the cladding modes.

[0106] In Figure 9, it can be seen that the use of six hollow tubes allows partial suppression of the Lp11-like mode to be achieved, but higher azimuthal order modes remain unperturbed, limiting the overall quenching of the HOM.

[0107] Thus, it is clearly shown that the hollow core PCF of the present invention, which has seven hollow tubes, has significantly improved HOM suppression properties over the prior art hollow core PCF, which has six hollow tubes.

[0108] Michieletto et al., "Hollow-core fibers for high power pulse transmission" Further comparison of a hollow-core PCF according to one embodiment of the present invention with a hollow-core PCF having six hollow tubes is disclosed in "Pulse Delivery," Optics Express, pp. 7103-7119 (March 2016). The contents of this article are incorporated by reference into the present disclosure, provided that in the event of a conflict between the subject matter expressly disclosed herein and the incorporated subject matter, the content of the subject matter expressly disclosed herein shall take precedence.

[0109] The laser system shown in FIG. 11 includes a laser source 51 and a fiber transmission cable 52 for transmitting light from the laser source 51 to a user device 54. The fiber transmission cable 52 includes, as its waveguide, the aforementioned hollow-core PCF having one or more low-loss transmission bands associated with the user device 54. As shown, the fiber transmission cable 52 may be somewhat long, yet still transmit single-mode light in the fundamental mode to the user device 54 with high efficiency and low loss. The fiber transmission cable 52 has a first end 53 a and a second end 53 b. In the illustrated embodiment, the first end 53 a and the second end 53 b are each mounted within a ferrule structure for connection to the user device 54 and the laser source 54, respectively.

[0110] In an alternative embodiment not shown, the second end of the fiber transmission cable 52 is spliced ​​to the fiber output of the laser source 51 . The preform illustrated in Figure 12 is a preform for one embodiment of the hollow-core fiber described herein.

[0111] The preform comprises a preform outer cladding region 165 and seven hollow preform tubes 161a, 161b (i.e., the tubes do not touch each other) arranged in a non-contacting ring that is surrounded and fused by the preform outer cladding region 165.

[0112] Pressure tubes 164, connecting each of three of the preform tubes (main hollow tubes) to a pressure source (not shown), are provided to control the pressure in the main hollow tubes 161a during drawing. The pressure tube length 164a inserted into the bore of each main hollow tube 161a is advantageously uncoated silica, while the remaining portion of the pressure tube 164 (referred to as the pressure tube feed section) is polymer-coated silica. The pressure in the secondary hollow tube 161b is advantageously controlled by a pressure control circuit 166 called "A RING ELEMENT FOR A PREFORM, A PREFORM AND AN OPTICAL FIBER TO BE DRAWN FROM THE PREFORM" (A RING ELEMENT FOR A PREFORM, A PREFORM The pressure chamber may be controlled by a pressure chamber as illustrated in Figures 15 and 16 of Danish Patent Application No. 201670262 entitled "A method for forming a thin film of a thin film of a material containing a thin film of a metal and an optical fiber drawn from the preform."

[0113] 13a, the hollow-core PCF comprises an outer cladding region 171 and seven non-contacting hollow tubes 172 that form an inner cladding region and are surrounded by said outer cladding region 171. The hollow tubes 172 are fused inside the outer cladding 171 at a melting point 173 to form an inner cladding region and a hollow core region 174 that is surrounded by the inner cladding region. The outer cladding region comprises a photonic bandgap structure in the form of microstructures (inclusions) 175a that have a different refractive index than the cladding background material 175b.

[0114] The photonic bandgap (PBG) structure may be provided by any means, for example by providing a refractive index grating in the outer cladding region, comprising concentric rings of different refractive index, and / or by inclusion.

[0115] The inclusions 175a of the outer background material 175b are arranged in a cross-sectional pattern comprising approximately five rings. As previously mentioned, the inclusions are preferably voids or made from a gas, have a relatively small diameter, and are short and spaced to optimize (minimize) confinement loss for the desired wavelength or range of wavelengths.

[0116] Figure 13b shows the transmission loss for two variations of the hollow-core PCF of the embodiment of Figure 13a, where the two variations of the hollow-core PCF with PBG structures in each cladding are optimized to reduce confinement loss around the desired center wavelengths of 1064 nm (left) and 1550 nm (right), respectively. As can be seen, the loss is very low. Furthermore, it can be seen that this approach to confinement loss reduction can also be utilized in polarization-maintaining antiresonant fibers.

[0117] Furthermore, it has been found that confinement losses appear to be arbitrarily reduced by increasing the overall thickness of the photonic bandgap structure. Example 1 A hollow-core PCF with the structure shown in Figure 1 was fabricated using a stack-and-draw method. The fabricated fiber shown has a core diameter of approximately 30 μm, d2 of approximately 17 μm, and d2 / D of approximately 0.57. The mode field diameter measured at 1064 nm is 2 μm. Although slight dimensional variations exist in the tube, the fiber still exhibits extremely low loss and bending loss, and excellent mode quality. The mode quality factor of the fabricated fiber was measured using a camera-based MFT with a 1064 nm laser and a 5 m FUT. 2 The mode quality factor was measured with a measurement system (Spiricon M2-2OOS). Measurements were performed on a standard 8 cm spool of fiber, without any further coiling. The results are summarized in Table I and illustrated in Figure 14. The fiber output beam exhibited negligible astigmatism and imbalance, and M 2 is 1.2.

[0118] [Table 1]

Claims

1. 1. A hollow-core photonic crystal fiber (PCF) comprising: an outer cladding region; and a plurality of hollow tubes surrounded by the outer cladding region, each of the hollow tubes having an average inner diameter d1 and an average outer diameter d2; each of the hollow tubes is fused to the outer cladding region to form a ring defining an inner cladding region and a hollow core region surrounded by the inner cladding region; the hollow tubes are not in contact with each other; the hollow tubes do not comprise nested sub-tubes; each of the hollow tubes comprises a region facing a core center with a wall thickness t, the wall thickness being up to about 2.1 μm; at least one of the hollow tubes has a wall thickness different from that of at least one other of the hollow tubes; and the hollow core region and the hollow tubes are independently evacuated or filled with a pressurized gas.

2. The hollow-core PCF of claim 1 , wherein d1 / d2 is about 0.8 or greater.

3. 3. The hollow core PCF of claim 1 or claim 2, wherein the hollow tubes have a center-to-center distance Λ between adjacent hollow tubes, the distance Λ being between about 1.01 x d2 and about 1.5 x d2.

4. The hollow core PCF of any one of claims 1 to 3, wherein the hollow tubes have substantially parallel central axes.

5. The hollow-core PCF of any one of claims 1 to 4, wherein the hollow core region has a core diameter D of about 10 μm to about 100 μm.

6. The hollow core PCF of any one of claims 1 to 5, wherein each of said hollow tubes is substantially circular.

7. Each of the hollow tubes has a large inner diameter D ｌ and the long inner diameter D ｌ Short inner diameter D perpendicular to ｓ and D ｌ A hollow-core PCF according to any one of claims 1 to 6, wherein is determined in the radial direction.

8. 8. A hollow-core PCF as claimed in any one of claims 1 to 7, wherein at least one of the hollow tubes comprises one or more nodules arranged in a region facing the centre of one or more cores of the hollow tube, preferably the nodules being arranged at the boundary of the hollow core region, the nodules preferably being arranged to be anti-resonant at the operating wavelength so that light in the fundamental mode is substantially excluded from the nodules.

9. The hollow core PCF of any one of claims 1 to 8, wherein the minimum distance between adjacent hollow tubes is at least about 0.1 μm.

10. The hollow-core PCF of any one of claims 1 to 9, wherein the outer cladding region has an outer diameter of at least about 125 μm.

11. 11. A hollow core PCF according to any one of claims 1 to 10, wherein the outer cladding region and / or the hollow tube comprise a solid glass material, preferably made from silica, optionally doped with an index-modifying dopant.

12. The hollow-core PCF of any preceding claim, wherein the outer cladding region comprises a photonic bandgap structure surrounding the inner cladding region.

13. The outer cladding region has a refractive index N ｏｃ and a plurality of inclusions having a refractive index different from the refractive index of the background material, the plurality of inclusions in the outer background material preferably arranged in a cross-sectional pattern including two or more rings of inclusions surrounding the inner cladding region.

14. The hollow-core PCF of claim 13 , wherein the plurality of inclusions within the outer background material are arranged in a substantially hexagonal pattern.

15. The hollow core PCF of claim 13 or claim 14, wherein the plurality of inclusions are made from a solid material.

16. 15. The hollow core PCF of claim 13 or claim 14, wherein the plurality of inclusions are voids or made from gas.

17. The plurality of inclusions have an average diameter (d ｉｎｃ 17. The hollow core PCF of any one of claims 13 to 16, having a

18. The plurality of inclusions have a maximum pitch (Λ) of about 6 μm. ｉｎｃ 18. The hollow core PCF of any one of claims 13 to 17, wherein the PCF is arranged in a matrix.

19. 19. The hollow-core PCF of any one of claims 1 to 18, wherein the ratio of the average outer diameter d2 of the hollow tube to the core diameter D of the hollow core region, d2 / D, is from about 0.5 to about 0.

75.

20. A laser system for transmitting laser light to a user device, comprising: a laser light source; and a fiber transmission cable for transmitting light from the laser light source to the user device, wherein the fiber transmission cable comprises a hollow core PCF according to any one of claims 1 to 19.

21. 21. The laser system of claim 20, wherein the laser source is configured to generate pulses of laser light and is optically connected to the fiber transmission cable, preferably the laser source is a femtosecond laser source.

22. 21. The laser system of claim 20, wherein the laser source has a pump duration of from about 30 fs to about 30 ps.

23. 22. The laser system of claim 20 or claim 21, wherein the laser source has a peak power determined at an exit of the laser source of at least about 5 kW.

24. The laser system according to any one of claims 20 to 23, wherein the laser source is a mode-locked laser, the mode-locked laser preferably comprising one or more amplifiers.

25. 25. The laser system of any one of claims 20 to 24, wherein the hollow-core PCF is configured to guide a single mode at at least one wavelength in the range from about 200 nm to about 4.5 μm, preferably at least one wavelength in the range from 1000 nm to about 1100 nm.

26. 21. The laser system of claim 20, wherein the hollow-core PCF is configured to guide continuous wave optical wavelengths of at least about 0.1 μm bandwidth.

27. 27. The laser system of claim 20, wherein the hollow-core PCF has a first fiber end configured to be connected to the user device and a second fiber end optically connected to an output fiber of the laser source via a fiber coupling structure.

28. The fiber coupling structure includes: Condenser lens, Graded Index Element (GRIN), protective elements, and ferrule structure, 30. The laser system of claim 27, comprising at least one of:

29. 29. The laser system of claim 27 or claim 28, wherein the first fiber end is mounted within a ferrule structure.