Method for manufacturing spot welded joints

Abstract

A method for manufacturing a spot-welded joint according to one embodiment of the present disclosure comprises: a step for performing main energization on a sheet set including one or more steel members having a tensile strength of 980 MPa or more; and a step for performing post-energization on the sheet set. The main energization is controlled by a means other than adaptive control. An instantaneous heat generation amount per unit volume and unit time is calculated on the basis of the energization duration in the post-energization and from a predetermined cumulative heat generation amount per unit volume with which good post-energization can be performed on the sheet set. The post-energization is adaptively controlled by adjusting the post-energization by a post-heat current or by an inter-electrode voltage or an inter-electrode resistance that causes the calculated instantaneous heat generation amount per unit volume and per unit time to be generated.

Description

Technical Field

[0001] The present disclosure relates to a method for manufacturing a spot weld joint. This application claims priority based on Japanese Patent Application No. 2024-040451 filed in Japan on March 14, 2024, and incorporates its content herein by reference.

Background Art

[0002] In the spot weld of high-strength steel, cold cracking may occur. Cold cracking is a general term for cracks that occur after the temperature of the weld joint drops to near room temperature after welding. Cold cracking in high-strength steel is considered to be caused by delayed fracture due to hydrogen embrittlement of high-strength steel.

[0003]

[0004] Patent Document 1 discloses a resistance spot welding method in which two or more stacked steel plates are sandwiched between a pair of welding electrodes, energized while pressing the steel plates, and nuggets are formed on the overlapping surfaces of the steel plates to join the steel plates together. After the joining, vibration is directly or indirectly applied to the nugget so that the vibration frequency of the steel plate is 100 Hz or more and the maximum amplitude of the steel plate satisfies 10 nm to 500 μm.

[0005] Patent Document 2 discloses a welding method for steel plates using an apparatus in which a high-frequency heating coil is wound around an electrode for resistance welding. In this method, the workpiece is melted and solidified by resistance welding to form a nugget, and then tempered by high-frequency heating in the molten and solidified area and the heat-affected zone. In this tempering process, the heating temperature is kept below the A3 transformation point of the workpiece, and the method of heating up to the A3 transformation point by high-frequency heating is performed by detecting the impedance change when the high-frequency heating coil reaches the A2 transformation point, and stopping the high-frequency heating or reducing the heat input by high-frequency heating after a time of 1 second or less has elapsed since the detection. Subsequently, the welding method is performed by air cooling at a cooling rate of 20°C / s or more, or by pressurizing and holding the electrode for resistance welding to cool at a cooling rate of 20°C / s or more. [Prior art documents] [Patent Documents]

[0006] [Patent Document 1] Patent No. 7243928 [Patent Document 2] Patent No. 5459750 [Overview of the project] [Problems that the invention aims to solve]

[0007] The technology described in Patent Document 1 improves delayed fracture resistance by releasing hydrogen from within the nugget to the outside of the steel plate by applying vibration to the nugget. However, applying vibration to the nugget requires a vibration application device, which reduces manufacturing efficiency. It is preferable to suppress delayed fracture using existing spot welding equipment.

[0008] The technology described in Patent Document 2 involves heating the welded area with high frequency after spot welding and then performing tempering. However, high-frequency heating equipment is required to perform tempering using high frequency, which reduces manufacturing efficiency. It is preferable to suppress delayed fracture using existing spot welding equipment.

[0009] One method for preventing delayed fracture that can be implemented with existing spot welding equipment is post-welding. Post-welding refers to passing a post-thermal current through the plate assembly. The term "post-thermal current" is defined in JIS Z 3001-6:2013 "Welding Terminology - Part 6: Resistance Welding" as "a current that is passed through the hardened weld after welding in resistance welding such as spot welding, projection welding, and upset welding of steel materials that harden by welding, for the purpose of tempering or annealing. It is also called tempering current."

[0010] Reducing the hardness of steel also reduces its susceptibility to hydrogen embrittlement. Therefore, reducing the hardness of the nugget by post-electric current application can suppress delayed fracture.

[0011] However, in plate assemblies including high-strength steel members, the effect of post-current application is often not reliably obtained. This is because it is difficult to maintain a constant diameter for the nuggets formed by the initial current application.

[0012] "Main current application" refers to the process of passing a welding current through the plate assembly. The term "welding current" is defined in JIS Z 3001-6:2013 "Welding Terminology - Part 6: Resistance Welding" as "the (main) current applied to form a weld." The plate assembly melts due to the welding current. When the welding current is stopped, the molten metal solidifies into a nugget due to heat transfer from the plate assembly to the electrodes. Subsequent current is then applied to the nugget formed by the main current application.

[0013] Under strictly controlled welding conditions, the nugget diameter will be constant if the welding current, welding time, and pressure during the main welding process are kept constant. However, disturbances exist in normal welding environments. Typical examples of disturbances are plate gaps and current shunting. Plate gaps refer to the gaps between multiple steel members that make up a plate assembly. Current shunting refers to the current flowing in parallel circuits formed by previously welded points and the workpiece, in addition to the main welding current. In welding environments where disturbances exist, the diameters of multiple nuggets obtained by performing multiple main welding processes are usually not constant.

[0014] Variations in nugget diameter cause variations in the cross-sectional area of ​​the current path, leading to variations in the resistance and heat generation of the current path. Consequently, variations in nugget diameter also cause variations in the mechanical properties of the welded joint after current is applied.

[0015] If the actual nugget diameter is smaller than the target nugget diameter, the electrical resistance between the electrodes increases during post-current application. This results in excessive resistive heat generation during post-current application, causing the temperature of the weld to rise to the re-quenching temperature range, leading to re-quenching of the weld. As a result, the nugget hardens, making it more susceptible to cold cracking.

[0016] On the other hand, if the actual nugget diameter is larger than the target nugget diameter, the electrical resistance between the electrodes during subsequent energization becomes smaller, resulting in insufficient resistive heating during subsequent energization. As a result, the nugget does not soften sufficiently, and cold cracking is not adequately suppressed.

[0017] As explained above, due to the presence of disturbances in the welding environment and variations in nugget diameter, a stable low-temperature crack suppression effect cannot be obtained with normal post-current application. In view of these circumstances, the present disclosure aims to provide a method for manufacturing spot-welded joints that can stably reduce the hardness of the nugget in a welding environment with disturbances and suppress low-temperature cracking in high-strength steel members. [Means for solving the problem]

[0018] The gist of this disclosure is as follows:

[0019] (1) A method for manufacturing a spot-welded joint according to one aspect of the present disclosure comprises the steps of: applying current to a plate assembly including one or more steel members having a tensile strength of 980 MPa or more; and applying current to the plate assembly afterwards, wherein the initial current application is controlled by means other than adaptive control, and the instantaneous heat generation per unit volume and unit time is calculated based on the currenting time of the subsequent current application from a predetermined cumulative heat generation per unit volume that allows the plate assembly to be properly subsequently currented, and the subsequent current application is adaptively controlled by adjusting the electrode resistance or electrode voltage or subsequent thermal current that generates the calculated instantaneous heat generation per unit volume and unit time. (2) Preferably, in the method for manufacturing a spot welded joint described in (1) above, the cumulative heat generated in the first half of the post-energization is set to be 2 / 3 or more of the total cumulative heat generated during the post-energization. (3) Preferably, in the method for manufacturing a spot welded joint described in (1) or (2) above, before the main energization, a test plate assembly that simulates the plate assembly is subjected to multiple main energization tests and post-test energization tests, the diameter of the nuggets formed during the multiple main energization tests is made substantially the same, and the cumulative heat generated per unit volume during the post-test energization tests in which the test plate assembly is successfully energized is set to the cumulative heat generated per unit volume that is determined in advance to enable the plate assembly to be successfully energized. (4) Preferably, in the method for manufacturing a spot welded joint described in (3) above, the cumulative amount of heat generated during the post-test energization that does not cause cracks in the welded portion of the test plate assembly is set to the cumulative amount of heat generated per unit volume that is determined in advance to allow the plate assembly to be energized properly afterward. (5) Preferably, in the method for manufacturing a spot welded joint described in (3) above, the cumulative heat generated during the post-test energization that minimizes the hardness of the nugget of the test plate assembly is set to the cumulative heat generated per unit volume that has been determined in advance to enable the post-test energization of the plate assembly to proceed smoothly. (6) Preferably, in the method for manufacturing the spot welding joint according to (3) above, the cumulative heat generation amount of the post-welding energization that maximizes the cross-tensile strength of the welded portion of the test plate set is set to the cumulative heat generation amount per unit volume that has been previously determined to enable good post-welding energization of the plate set. (7) Preferably, in the method for manufacturing the spot welding joint according to (3) above, the diameter of the nugget formed in the plate set is within the range of 0.7 times to 1.3 times the diameter of the nugget formed in the test plate set.

Effects of the Invention

[0020] According to the present disclosure, it is possible to provide a method for manufacturing a spot welding joint that can stably reduce the hardness of the nugget and suppress low-temperature cracking in high-strength steel members in a welding environment where disturbances exist.

Brief Description of the Drawings

[0021] [Figure 1] It is a schematic diagram of spot welding. [Figure 2] It is a graph showing the relationship between the current (welding current) and the nugget diameter in this energization. [Figure 3] It is a graph showing the Vickers hardness distribution of various nuggets after adaptively controlled post-welding energization. [Figure 4] It is a graph showing the Vickers hardness distribution of various nuggets after constant current controlled post-welding energization. [Figure 5] It is a cross-sectional view explaining the measurement positions of the Vickers hardness shown in the graphs of FIGS. 3 and 4.

Modes for Carrying Out the Invention

[0022] The method for manufacturing a spot-welded joint 1 according to this disclosure comprises the steps of: applying current to a plate assembly 11 containing one or more steel members 111 (high-strength steel members 111H) having a tensile strength of 980 MPa or more; and applying current to the plate assembly 11 afterward. The instantaneous heat generation per unit volume and unit time is calculated based on the currenting time of the subsequent current application, using a predetermined cumulative heat generation per unit volume that allows for good subsequent current application to the plate assembly 11. The subsequent current application is adaptively controlled by adjusting the inter-electrode resistance, inter-electrode voltage, or welding current that generates the calculated instantaneous heat generation per unit volume and unit time. The method for manufacturing a spot-welded joint 1 according to this disclosure will be described in detail below.

[0023] (board group 11) In the manufacturing method of the spot-welded joint 1, spot welding is performed on a plate assembly 11. The plate assembly 11 is a workpiece created by stacking steel members 111, which are the base material for welding. The shape of the steel members 111 included in the plate assembly 11 is not particularly limited. The steel members 111 can have any three-dimensional shape. For example, if the steel members 111 are hat-shaped members, the plate assembly 11 is formed by stacking the flange portions of the hat-shaped members. The hat-shaped members are joined by spot welding the stacked flange portions to create the spot-welded joint 1. Alternatively, the steel members 111 may be steel plates. The number of steel members 111 included in the plate assembly 11 can be any value of 2 or more.

[0024] One or more of the steel members 111 included in the plate assembly 11 are high-strength steel members 111H with a tensile strength of 980 MPa or higher. The tensile strength of the high-strength steel members 111H may be 1000 MPa or higher, 1200 MPa or higher, or 1500 MPa or higher. There is no particular upper limit on the tensile strength of the high-strength steel members 111H. For example, the tensile strength of the high-strength steel members 111H may be 2500 MPa or less, 2200 MPa or less, or 2000 MPa or less. In addition, the plate assembly 11 may include low-strength steel members 111L with a tensile strength of less than 980 MPa.

[0025] The high-strength steel member 111H increases the strength of the spot-welded joint 1. On the other hand, cold cracking is likely to occur in the welded joint 12 formed on the high-strength steel member 111H.

[0026] (Power on) The spot welding method according to this embodiment includes both initial energization and post-energization. During initial energization, the plate assembly 11 is sandwiched between a pair of spot welding electrodes 2, and a welding current is passed through the plate assembly 11 while applying pressure to it. The welding current is also referred to as the initial current. The welding current generates resistive heating in the plate assembly 11, causing it to melt.

[0027] After the main current is applied, the plate assembly 11 is held between the pair of electrodes 2, and the current flowing through the electrodes 2 is reduced to zero or close to zero. Since a coolant flows inside the spot welding electrodes 2, heat is transferred from the plate assembly 11 to the electrodes 2 while the plate assembly 11 is being pressurized by the electrodes 2. This cools the plate assembly 11, solidifies the molten metal, and forms a nugget 121. The time from the end of the welding current to the start of the post-heat current is called the cooling time or chill time. The nugget 121 joins multiple steel members 111 included in the plate assembly 11. A heat-affected zone 122 is formed around the nugget 121. The portion including the nugget 121 and the heat-affected zone 122 is called the welded portion 12.

[0028] The current supply is controlled by means other than adaptive control. For example, the current supply is controlled by constant current control. Constant current control is a method of controlling the supply of current to the main supply circuit in resistance welding that has the function of detecting fluctuations in the current of the main circuit for each half cycle or each cycle of main current supply and automatically correcting these fluctuations (see JIS Z 3001-6:2013). Note that constant current control is, (1) The power supply shall be a DC power supply and the current shall be controlled to be constant, (2) The power source shall be an AC power source, and the effective current shall be controlled to be constant. It is a concept that includes both.

[0029] The welding current may be controlled by upslope control or downslope control. Upslope control is a control method that continuously increases the current from a predetermined value or zero over a set period of time, while downslope control is a control method that continuously decreases the current to a predetermined value or zero over a set period of time (see JIS Z 3001-6:2013). The waveform of the welding current may be a sine wave, a square wave, or a non-sinusoidal wave (triangular wave, ramp wave, or Sinc wave).

[0030] The welding current, applied pressure, and welding time (the time the welding current is applied) during this energization are not particularly limited. A person skilled in the art can select welding conditions suitable for the thickness, composition, and number of steel members 111 included in the plate assembly 11.

[0031] (Powered on afterwards) After the nuggets 121 are formed by the initial energization, the plate assembly 11 is energized again. During the re-energization, the plate assembly 11 is sandwiched between a pair of electrodes, and a re-thermal current is passed through the plate assembly 11 while applying pressure to it. The re-thermal current generates resistive heating in the plate assembly 11, tempering the nuggets 121.

[0032] Post-energization is adaptively controlled. Adaptive control is a type of control that changes the characteristics of the control system to satisfy the required conditions in response to disturbances such as the characteristics of the controlled object and the environment. In the post-energization of the manufacturing method of the spot welded joint 1 according to this embodiment, the cumulative heat generation amount Q per unit volume is used as an indicator for adaptive control. The amount of Joule heat generated during post-energization is controlled so that the cumulative heat generation amount Q per unit volume is set to a predetermined value.

[0033] The cumulative heat generation Q per unit volume during post-energization is the cumulative value of the value q calculated by the following formula A, accumulated over the period from the start to the end of post-energization. q = (V × I) / (S × t) ... Equation A In equation A, V is the voltage between electrodes, I is the welding current, S is the cross-sectional area of ​​the current path, and t is the total plate thickness (mm) of the steel members 111 included in the plate assembly 11. The value q obtained by equation A is the instantaneous heat generation q per unit volume and unit time. This is because the residual heat current generates resistive heating by passing through the columnar portion with a contact area S and a total plate thickness t.

[0034] Furthermore, rewriting equation A using equation B results in equation C. R=(r×t) / S…Formula B q = (V × I × R) / (r × t) 2 ) =(V 2 ) / (r×t 2 )…Formula C In equation B, r is the resistivity of the material to be welded (plate assembly 11). The R obtained by equation B is the resistance of the columnar portion with cross-sectional area S and total plate thickness t.

[0035] As is clear from equation C, the instantaneous heat generation q per unit volume and unit time can be calculated from the inter-electrode voltage V, the total plate thickness t of the plate assembly 11, and the resistivity r of the plate assembly 11, and is not affected by the cross-sectional area S of the current path. On the other hand, the resistivity of the plate assembly 11 changes depending on the temperature of the plate assembly 11. Even if I and V remain constant from the start to the end of current flow, q will not remain constant. Furthermore, if scattering occurs, the total plate thickness t of the plate assembly 11 in the area clamped by the electrode 2 decreases significantly.

[0036] If the instantaneous heat generation amount q per unit volume and unit time is accumulated from the start to the end of the subsequent energization, it becomes the cumulative heat generation amount Q per unit volume during the subsequent energization. This cumulative heat generation amount Q per unit volume can also be calculated without using the cross-sectional area S of the current path.

[0037] In the manufacturing method of the spot-welded joint 1 according to this embodiment, the cumulative heat generation Q per unit volume is used as an indicator for adaptive control of post-energization. Specifically, (1) First, the cumulative heat generation Q per unit volume required to properly energize the board assembly 11 is determined in advance. (2) Next, based on the cumulative heat generation Q per unit volume that allows the board assembly 11 to be properly energized afterward, and the energizing time (re-heating time) for the re-energization, the instantaneous heat generation q per unit volume and unit time that can reproduce the cumulative heat generation Q is calculated. (3) Then, the subsequent energization is adaptively controlled so that the calculated instantaneous heat generation q per unit volume and unit time is obtained. Adaptive control is performed by adjusting the inter-electrode resistance, inter-electrode voltage, or after-heat current. A predetermined instantaneous heat generation rate q per unit volume and unit time may be achieved by adjusting the after-heat current. Alternatively, a predetermined instantaneous heat generation rate q per unit volume and unit time may be achieved by adjusting the inter-electrode resistance or inter-electrode voltage. For example, it is preferable to automatically control the current value and energization time by providing real-time feedback of the inter-electrode voltage during energization to reproduce optimal conditions.

[0038] There are no limitations on the method for determining the cumulative heat generation Q required for successful post-energization in the plate assembly 11. The cumulative heat generation Q can be determined by simulation. Alternatively, the cumulative heat generation Q can be determined by post-test energization. Post-test energization is performed prior to the main energization and post-energization to obtain the spot welded joint 1 to be manufactured, in order to explore appropriate conditions. An example of post-test energization is described below.

[0039] Prior to energizing the assembly after the test, a plate assembly 11 simulating the plate assembly 11 to be welded is first prepared. Hereinafter, the plate assembly 11 to be welded will be referred to as the "actual plate assembly" or simply as the "plate assembly," and the plate assembly 11 simulating the actual plate assembly will be referred to as the "test plate assembly." The actual plate assembly and the test plate assembly only need to have the same steel type, plate thickness, number of base material sheets, and stacking order. For example, the plate assembly 11 to be welded may be made by stacking the flat sections of steel members 111 obtained by press-forming steel plates. The plate assembly 11 simulating this may be made by stacking steel plates before press-forming or other processes.

[0040] When applying the final current to the test plate assembly, disturbances should be suppressed as much as possible to minimize variations in nugget diameter. Disturbances include, for example, plate gaps and current shunting. Furthermore, the diameter of the nugget 121 produced by applying the final current to the test plate assembly should be the same as the target diameter of the nugget 121 of the spot welded joint 1 to be manufactured. Preferably, the welding current, current application time, and pressure applied during the final current application to the test plate assembly (hereinafter referred to as "test final current application") should be the same as those applied during the final current application to the actual plate assembly (hereinafter referred to as "actual final current application"). The test final current application should be performed multiple times.

[0041] The nuggets 121 formed on the test board assembly are energized after the main test energization. The main test energization and post-test energization are performed multiple times. The cumulative heat generation is varied during the multiple post-test energizations. Multiple nuggets 121 produced in this way are evaluated. The cumulative heat generation during the post-test energization in which a good nugget 121 could be produced is used as the predetermined cumulative heat generation per unit volume that allows the board assembly 11 to be energized successfully after post-test energization.

[0042] For example, by observing the welded joint 12 formed on the test plate assembly, it is possible to determine whether or not cold cracking occurred after energizing following the test. The cumulative heat generated during any subsequent energizing that did not cause cold cracking in the welded joint 12 may be used as a predetermined cumulative heat generated per unit volume that allows the plate assembly 11 to be energized successfully afterward.

[0043] Furthermore, the hardness of the nuggets 121 formed on the test board assembly can be measured by cutting them and performing a Vickers hardness test on the cross-section. The cumulative heat generated during energization after minimizing the hardness of the nuggets 121 on the test board assembly may be used as the predetermined cumulative heat generated per unit volume required to enable good post-energy conduction of the board assembly 11. Alternatively, any cumulative heat generated that allows the hardness of the nuggets 121 on the test board assembly to be below a predetermined value may be used as the predetermined cumulative heat generated per unit volume required to enable good post-energy conduction of the board assembly 11.

[0044] Alternatively, the cross-tensile strength of the weld 12 can be measured by performing a cross-tensile test on the weld 12 provided on the test plate assembly. The cumulative heat generated after energizing the weld 12 of the test plate assembly, which maximizes its cross-tensile strength, may be used as the predetermined cumulative heat generated per unit volume required to properly energize the plate assembly 11. In addition, any cumulative heat generated that allows the cross-tensile strength of the weld 12 of the test plate assembly to be greater than or equal to a predetermined value may be used as the predetermined cumulative heat generated per unit volume required to properly energize the plate assembly 11. The cross-tensile test is performed, for example, in accordance with JIS Z 3137:1999 "Specimen dimensions and test method for cross-tensile testing of resistance spot and projection welded joints".

[0045] (Effects and Benefits) In the manufacturing method of the spot-welded joint 1 according to this embodiment, the plate assembly 11 includes a high-strength steel member 111H. This makes it possible to manufacture a spot-welded joint 1 with high strength. However, cold cracking is likely to occur in the welded portion 12 provided on the high-strength steel member 111H. Also, since the nugget diameter tends to vary during this energizing process, it is difficult to stably suppress cold cracking by performing appropriate post-energing.

[0046] Therefore, in the manufacturing method of the spot-welded joint 1 according to this embodiment, the cumulative heat generation Q per unit volume that allows for good post-current application to the plate assembly 11 is determined in advance. Then, the post-current application is adaptively controlled to reproduce this cumulative heat generation. This makes it possible to stably suppress low-temperature cracking.

[0047] The reason why the effects of post-energization are unstable is that disturbances change the nugget diameter, which in turn changes the resistance of the current path. In conventional post-energization, the optimal post-heat current and energizing time (post-heat time) were identified, and constant current control was performed during the actual post-energization to reproduce these values. However, if the diameter of nugget 121 during the actual post-energization is smaller than that of the test post-energization, the resistance increases. When post-energization is controlled by constant current, the voltage between electrodes increases in response to the increase in resistance. As a result, the amount of heat input during post-energization becomes excessive.

[0048] However, the inventors have found that this problem can be avoided by adaptively controlling the post-energy supply with the cumulative heat generation amount as the control target. When the post-energy supply is adaptively controlled with the cumulative heat generation amount as the control target, the post-heat current decreases in response to the increase in resistance. As a result, the cumulative heat generation during post-energy supply in the actual operation is approximately the same as the cumulative heat generation during post-energy supply in the test. According to the inventors' experimental results, by keeping the cumulative heat generated during post-energization constant, the effects of post-energization could also be kept within a certain range. In other words, by using post-energization in the actual process that reproduces the cumulative heat generated during post-energization after a test that can suppress cold cracking, cold cracking could be stably suppressed. That is, in the manufacturing method of the spot-welded joint 1 according to this embodiment, even if the nugget diameter varies due to disturbances during the actual energization, the optimal energizing conditions were automatically applied to the plate assembly 11 during post-energization, thereby suppressing cold cracking.

[0049] In conventional technology, it is believed that the nugget diameter is stabilized by adaptive control of the current flow. However, in the manufacturing method of the spot welded joint 1 according to this embodiment, the current flow is not adaptively controlled. According to the inventors' findings, if significant disturbances exist in the welding environment, adaptive control of the current flow can cause significant spatter. When suppression of cold cracking is required, there is little advantage in adaptive control of the current flow. Rather, from the viewpoint of suppressing the risk of significant spatter during the current flow and enhancing the cold crack suppression effect, it is preferable not to adaptively control the current flow. Adaptive control during post-current flow does not increase the risk of spatter. This is because a stable current path, the nugget, exists when post-current flow is performed.

[0050] The most basic embodiment of the method for manufacturing the spot-welded joint 1 according to this embodiment has been described above. A more preferred embodiment will be described below.

[0051] (Cumulative heat generation during the first half of the power-on period) It is preferable that the cumulative heat generated during the first half of the post-energization period be at least two-thirds of the total cumulative heat generated during the post-energization period. The cumulative heat generated during the first half of the post-energization period is the value obtained by accumulating the instantaneous heat generated per unit volume and unit time q from the start of the post-energization period until half of the post-energization period (post-heating period) has elapsed. The total cumulative heat generated during the post-energization period is the value obtained by accumulating the instantaneous heat generated per unit volume and unit time q from the start to the end of the post-energization period.

[0052] By setting the cumulative heat generated in the first half of the post-energy application to at least two-thirds of the total cumulative heat generated during the post-energy application, the adaptive control of the post-energy application can be further stabilized. This is because keeping the cumulative heat generated in the first half of the post-energy application within the aforementioned range makes it easier to avoid excessive heat generation in the second half. Furthermore, by securing most of the necessary heat generation in the first half of the post-energy application and fine-tuning the heat generation in the second half, even more precise control of the heat generation can be achieved.

[0053] (Method for determining the predetermined cumulative heat generation per unit volume that allows the board assembly 11 to be properly energized afterwards) The method for determining the predetermined cumulative heat generation per unit volume required to successfully energize the board assembly 11 is not particularly limited. As described above, this heat generation can be estimated by simulation. On the other hand, as described above, this heat generation can also be estimated by performing test energization and post-test energization on a test board assembly that simulates the actual board assembly. That is, before the actual energization, test energization and post-test energization are performed multiple times on a test board assembly that simulates the actual board assembly, the diameter of the nuggets 121 formed in multiple test energizations is made approximately the same, and the cumulative heat generation per unit volume of the post-test energization in which the test board assembly was successfully energized can be taken as the predetermined cumulative heat generation per unit volume required to successfully energize the board assembly 11. If the diameter of the nuggets 121 formed in multiple test energizations is within ±10% of the target diameter, the diameter of the nuggets 121 formed in multiple test energizations is considered to be approximately the same. Preferably, the diameter of the nugget 121 formed during multiple test energizations is within ±5% of the target diameter.

[0054] When powering on after testing, for example, one of the following values ​​can be used as the predetermined cumulative heat generation per unit volume that allows the board assembly 11 to be properly powered on afterward. (1) Cumulative heat generation after energizing the test plate assembly without causing cracks in the welded joint 12 (2) The cumulative amount of heat generated after powering up the test board assembly to minimize the hardness of the nugget 121. (3) Cumulative heat generation during post-test energization to maximize the cross tensile strength of the welded joint 12 of the test plate assembly

[0055] (Difference between the nugget diameter of the test board assembly and the nugget diameter of the final board assembly) In the environment in which the manufacturing method of the spot welded joint 1 according to this embodiment is carried out, disturbances may be present. Therefore, the diameter of the nugget 121 formed by the actual energization may vary from the target value. This is because adaptively controlled post-energization can sufficiently mitigate the effects of variations in the diameter of the nugget 121. On the other hand, by bringing the diameter of the nugget 121 formed by the actual energization closer to the diameter of the nugget 121 formed by the test energization, the low-temperature crack resistance of the spot welded joint 1 can be further improved. For example, it is preferable to set the diameter of the nugget 121 formed in the actual plate assembly to a range of 0.7 to 1.3 times the diameter of the nugget 121 formed in the test plate assembly.

[0056] Furthermore, JIS Z 3001-6:2013 "Welding Terminology - Part 6: Resistance Welding" defines the nugget diameter as "the diameter of the nugget portion measured at the joint interface by a cross-sectional test of the spot weld or projection weld." If there are three or more steel members 111 and two or more joint interfaces of the steel members 111, there will be two measurement locations for the diameter of the nugget 121. The manufacturing method of the spot welded joint 1 according to this embodiment aims to suppress low-temperature cracking of the high-strength steel member 111H. Therefore, when comparing the nugget diameter of the actual plate assembly with the nugget diameter of the test plate assembly, the nugget diameter measured at the joint interface of the high-strength steel member 111H is used for comparison. For example, if there are two or more joint interfaces of the high-strength steel member 111H, such as when three high-strength steel members 111H are stacked, it is preferable that the nugget diameter measured at at least one joint interface falls within the above range, and it is even more preferable that the nugget diameter measured at all joint interfaces falls within the above range.

[0057] While embodiments of the present disclosure have been described above, the disclosure is not limited thereto and can be modified as appropriate without departing from the technical idea. A more preferred example of the method for manufacturing the spot-welded joint 1 according to the present embodiment will be described below.

[0058] (Vickers hardness and thickness of high-strength steel member 111H) The Vickers hardness of the high-strength steel member 111H is not particularly limited. For example, it is preferable that the Vickers hardness of the high-strength steel member 111H be HV300 or higher, HV400 or higher, HV500 or higher, or HV650 or higher. The Vickers hardness of the high-strength steel member 111H may be HV500 or lower, HV650 or lower, or HV850 or lower. The thickness of the high-strength steel member 111H is also not particularly limited. For example, the thickness of the high-strength steel member 111H may be 1.0 mm or higher, 1.4 mm or higher, or 1.8 mm or higher. The thickness of the high-strength steel member 111H may be 1.8 mm or lower, 2.0 mm or lower, or 2.6 mm or lower.

[0059] (Tensile strength, Vickers hardness, and thickness of low-strength steel member 111L) The plate assembly 11 may have a low-strength steel member 111L with a tensile strength of 980 MPa or less. The configuration of the low-strength steel member 111L is not particularly limited. A configuration suitable for the application of the spot-welded joint 1 can be applied to the low-strength steel member 111L. For example, the tensile strength of the low-strength steel member 111L may be 270 MPa or more, 440 MPa or more, or 590 MPa or more. The tensile strength of the low-strength steel member 111L may be 440 MPa or less, 590 MPa or less, or 780 MPa or less. The Vickers hardness of the low-strength steel member 111L may be HV80 or more, HV120 or more, or HV180 or more. The Vickers hardness of the low-strength steel member 111L may be HV150 or less, HV200 or less, or HV280 or less. The thickness of the low-strength steel member 111L is also not particularly limited. For example, the thickness of the low-strength steel member 111L may be 0.5 mm or more, 0.6 mm or more, or 0.7 mm or more. The thickness of the low-strength steel member 111L may be 1.2 mm or less, 1.4 mm or less, or 1.6 mm or less.

[0060] (Surface treatment) The steel member 111 may have a surface treatment. For example, it is preferable to provide a plating on the surface of the steel member 111 in order to improve corrosion resistance and aesthetics. Examples of plating types include Al-based plating, Al-based alloying plating, Zn-based plating, and Zn-based alloying plating. Al-based plating is a plating in which the Al content is 50% by mass or more. Al-based alloying plating is a plating in which the Al content is 50% by mass or more, and a portion of it is alloyed with the underlying steel member 111. Zn-based plating is a plating in which the Zn content is 50% by mass or more. Zn-based alloying plating is a plating in which the Zn content is 50% by mass or more, and a portion of it is alloyed with the underlying steel member 111.

[0061] (Plate thickness ratio of board assembly 11) The plate thickness ratio of the plate assembly 11 is not particularly limited. The plate thickness ratio is the value obtained by dividing the total thickness of the plate assembly 11 by the thickness of the thinner of the steel members 111 arranged on the surface of the plate assembly 11. For example, the plate thickness ratio of the plate assembly 11 may be 3 or more, 4 or more, or 5 or more. The plate thickness ratio of the plate assembly 11 may be 6 or less, 7 or less, or 9 or less.

[0062] The tensile strength of the steel member 111 shall be measured in accordance with JIS Z 2241:2011 "Tensile Test Method for Metallic Materials". The shape of the test specimen can be appropriately selected according to the shape of the steel member 111. If it is difficult to take a test specimen from the steel member 111, the tensile strength of the steel member 111 may be estimated by measuring the Vickers hardness of the steel member 111 and converting the Vickers hardness to tensile strength using a known conversion table. The hardness of the steel member 111 shall be measured in accordance with JIS Z 2244:2009 "Vickers Hardness Test - Test Method". The test force shall be 0.5 kg during measurement. [Examples]

[0063] The effects of one aspect of this disclosure will be further illustrated by the examples. However, the conditions in the examples are merely examples of conditions adopted to confirm the feasibility and effectiveness of this disclosure. This disclosure is not limited to these examples of conditions. This disclosure may adopt various conditions as long as they do not depart from its gist and achieve its objectives.

[0064] (1. Nugget firmness evaluation) Various spot-welded joints were fabricated in a strictly controlled welding environment with virtually no disturbances. The conditions were as follows: Two spot welds were performed for each condition. ●Board set Created by layering two 1.5 GPa cold-rolled steel sheets (30 mm long, 50 mm wide, 1.6 mm thick). ●Optimal conditions for the above board assembly Current settings: Welding time 360 ​​msec, welding current 4.4 kA Cooling time: 1000msec Nugget diameter: 3√t (=3.79mm) Post-energization: Post-heating time 980msec, Post-heating current 3.7kA ● Spot welding conditions Optimal power supply conditions: ±0.2, ±0.4, or ±0.8kA Cooling time 1000msec Post-energization (1) Adaptive control with the cumulative heat generation under optimal conditions as the control target value. (2) Constant current control under the same conditions as the optimal conditions for power supply

[0065] By applying the above-described optimal conditions to the plate assembly and performing both main and post-main current application, we were able to obtain a nugget free from cold cracking. Then, using the above-described optimal conditions as a baseline, we conducted a spot welding experiment simulating actual welding. In the spot welding experiment, the welding current was varied within a range of ±0.8kA relative to the optimal conditions. This simulated the fluctuations in nugget diameter caused by disturbances. Post-welding current in the spot welding experiments was controlled either adaptively or with a constant current. In spot welding experiments where post-welding current was adaptively controlled, the instantaneous heat generation per unit volume and unit time was calculated based on the current generation time of the post-welding, using the cumulative heat generation per unit volume under optimal post-welding conditions. The post-welding current in the spot welding experiments was then adaptively controlled by adjusting the inter-electrode resistance, inter-electrode voltage, or post-heat current to generate the calculated instantaneous heat generation per unit volume and unit time. In spot welding experiments where post-welding current was controlled with a constant current, the optimal post-welding conditions described above were reproduced.

[0066] The welds of the spot-welded joints obtained in the above experiment were cut, and the diameter of the nugget and the Vickers hardness of the weld were measured. The nugget hardness was measured as shown in Figure 5. The hardness of the nugget 121 was measured continuously along the dashed line X, which is parallel to the joint interface of the steel plate and slightly away from the joint interface. The starting point of the continuous hardness measurement was the center of the nugget 121. The ending point of the continuous hardness measurement was outside the heat-affected zone 122.

[0067] Figure 2 shows the relationship between the welding current and the nugget diameter during this energization process. It was confirmed that variations in the welding current caused variations in the nugget diameter.

[0068] Figure 3 shows the hardness distribution of the nugget and its surrounding area after adaptive control and subsequent energization. Figure 4 shows the hardness distribution of the nugget after constant current control and subsequent energization.

[0069] In spot-welded joints subjected to adaptive control followed by energization, it was observed that the hardness increased from the center to the edges of the nugget, decreased sharply at the outside of the nugget (heat-affected zone), and then recovered outside the heat-affected zone. Due to differences in nugget diameter, the location of the softest point varied among the spot-welded joints. However, in spot-welded joints subjected to adaptive control followed by energization, the hardness inside the nugget, the hardness at the edges of the nugget, and the hardness of the heat-affected zone were at the same level regardless of the nugget diameter. In other words, adaptive control followed by energization was able to consistently exert its effects regardless of variations in nugget diameter.

[0070] On the other hand, in spot-welded joints after constant-current control and subsequent energization, the internal hardness of the nugget varied considerably. Due to variations in nugget diameter, the constant-current control and subsequent energization were unable to consistently exert their effects.

[0071] (2. Evaluation of resistance to low-temperature cracking) A plate assembly was created by overlapping steel plates 1 and 2 as shown in Table 1. Spot welded joints were manufactured by applying initial and post-current to this plate assembly. The welded joints of the spot welded joints were then observed to check for the presence or absence of cold cracking. The control method for post-current application and the presence or absence of cold cracking are described in Table 1.

[0072] In all conditions, the target nugget diameter for this welding was set at 3.48 mm. The conditions for post-welding with constant current were optimized for a nugget with a diameter of 3.48 mm. In post-welding with adaptive control, the cumulative heat generated during post-welding with constant current control optimized for a nugget with a diameter of 3.48 mm was used as the control target value.

[0073] [Table 1]

[0074] In Example 1, cracks occurred in the welded area because no power was applied afterward. In Examples 2 and 6, the welding environment was strictly controlled, and the nugget diameter was set to the same value as the target value. As a result, cracking of the welded area was suppressed. In Examples 3, 4, and 5, the nugget diameter became smaller than the target value due to disturbances. In Example 3, the heat input during post-energization was excessive, causing cracks to form in the weld. In Examples 7, 8, and 9, the nugget diameter became smaller than the target value due to disturbances. However, in Examples 7, 8, and 9, the post-energy application was adaptively controlled, so no cracks occurred in the weld. [Explanation of Symbols]

[0075] 1. Spot welded joint 11 Board set 111 Steel parts 111H High strength steel parts 111L Low strength steel parts 12 Welded parts 121 Nuggets 122 Heat-affected zone 2 electrodes X Hardness measurement section

Claims

1. A process of applying current to a plate assembly containing one or more steel members with a tensile strength of 980 MPa or more, The process of energizing the aforementioned plate assembly, A method for manufacturing a spot welded joint comprising, The aforementioned energization is controlled by means other than adaptive control, From the cumulative heat generation per unit volume that can be properly energized after the board assembly is installed, the instantaneous heat generation per unit volume and per unit time is calculated based on the energizing time of the subsequent energization. A method for manufacturing a spot welded joint, wherein the subsequent energization is adaptively controlled by adjusting the inter-electrode resistance, inter-electrode voltage, or subsequent thermal current that generates the calculated instantaneous heat generation amount per unit volume and unit time.

2. The method for manufacturing a spot welded joint according to claim 1, characterized in that the cumulative amount of heat generated in the first half of the subsequent energization is 2 / 3 or more of the total cumulative amount of heat generated during the subsequent energization.

3. Prior to the main power-on, the test board assembly simulating the board assembly is subjected to multiple test main power-on and post-test power-on cycles. The diameter of the nuggets formed during multiple test energizations is kept approximately the same. Of the multiple post-test energizations, the cumulative heat generation per unit volume for the post-test energizations in which the test board assembly was successfully energized is defined as the predetermined cumulative heat generation per unit volume for which the board assembly can be successfully energized. A method for manufacturing a spot welded joint according to claim 1 or 2, characterized by the above.

4. The method for manufacturing a spot welded joint according to claim 3, characterized in that the cumulative amount of heat generated during the post-test energization that does not cause cracks in the welded portion of the test plate assembly is set to a predetermined cumulative amount of heat per unit volume that allows the plate assembly to be energized properly afterward.

5. The method for manufacturing a spot welded joint according to claim 3, characterized in that the cumulative heat generated during post-test energization, which minimizes the hardness of the nugget of the test plate assembly, is set to a predetermined cumulative heat generated per unit volume that allows the plate assembly to be energized properly afterward.

6. The method for manufacturing a spot welded joint according to claim 3, characterized in that the cumulative heat generated after energizing the test plate assembly to maximize the cross tensile strength of the welded portion is set to a predetermined cumulative heat generated per unit volume that allows the plate assembly to be energized properly afterward.

7. The method for manufacturing a spot-welded joint according to claim 3, characterized in that the diameter of the nugget formed on the plate assembly is within the range of 0.7 to 1.3 times the diameter of the nugget formed on the test plate assembly.