Low-dusting pet urine treatment material

Abstract

To provide a pet urination treatment material having excellent dust emission suppression function, and hardly decreasing dust emission suppressibility, even when receiving an impact by transportation or the like.SOLUTION: A pet urination treatment material has a dust suppressant as a surface treatment agent on the surface of the urination treatment material. In the pet urination treatment material, the dust suppressant contains an inorganic salt of a polyvalent metal, and a water-soluble organic substance.SELECTED DRAWING: Figure 4

Description

Technical Field

[0001] The present invention relates to a urine treatment material for pets, and more particularly, to a low-dust urine treatment material for pets that is excellent in dust generation suppression ability and is less likely to have a reduced dust generation suppression ability even when subjected to impacts during transportation or the like, and a method for producing the same.

Background Art

[0002] Conventionally, a urine treatment material for pets (also called cat litter, toilet sand, etc.) used for treating pet urine has been known, and this is spread on a pet toilet container such as a urine tray and used. When a pet urinates in a toilet lined with such a urine treatment material for pets, the urine is absorbed by the urine treatment material, and the owner removes only the used portion that has absorbed the urine with a scoop or the like and sequentially replenishes the reduced amount for use. The raw materials and configurations of the urine treatment materials for pets vary widely for each product, but typical ones include those made of clay raw materials, those made of wood raw materials, those made of paper raw materials, etc. The required properties include water absorption, aggregation and solidification properties, deodorization properties, odor elimination properties, etc.

[0003] Well, until about several decades ago, pet toilets were often placed in places such as dirt floors where some dirt was acceptable. However, in recent years, due to changes in housing conditions, the number of condominiums and apartments has increased, and the number of people keeping pets indoors has also increased. Inevitably, the placement of pet toilets indoors has been increasing. Since the pet toilet has come to be placed indoors like this, there has been attention paid to problems on the hygienic aspect due to fine powder flying from the packaging bag when transferring the urine treatment material for pets into the pet toilet container and scattering around the toilet container, and problems on the health aspect due to people and pets inhaling the scattered fine powder. Thus, the dust generation suppression effect, which was not so highly regarded in conventional urine treatment materials for pets, has also come to be required.

[0004] As raw materials for the urine treatment material for pets, conventionally (1) Natural bentonite, or clayey raw material consisting of activated bentonite containing alkaline components, which is made from said bentonite. (2) Wood-based raw materials consisting of wood-derived materials such as wood powder (sawdust) or wood chips (fine chips), (3) Paper-based raw materials consisting of recycled paper or recycled pulp or other paper-derived materials, These are known, and in addition to these, in recent years, (4) Plant fiber raw materials derived from soybeans, corn, etc., such as okara Products utilizing these materials are increasing, and many pet urine treatment materials consist of a base material that uses one of these (1) to (4) as the main ingredient. And these substrates are (1) Clay-based base material, which is mainly made from (A) (B) Plant-derived cellulosic base material, which has one of (2) to (4) as its main ingredient. These are broadly classified into two types, and the urine treatment material substrate targeted by the dust suppression treatment of the present invention is a substrate belonging to either classification (A) or (B).

[0005] The degree of fine powder generation varies depending on the shape and raw materials of pet urine treatment materials. Even with granular or flake-shaped pet urine treatment materials of a certain size, some of the product may break or crumble due to vibrations and shocks during transportation, resulting in powdered product being mixed into the packaging bag. Since the product is transported through various companies, it is practically difficult to suppress the generation of fine powder by improving handling during the transportation process.

[0006] As an invention that focuses on such dust suppression effects, Patent Document 1 describes a technique for improving the powdering prevention properties of a granular molded body formed from a water-swellable clay mineral by treating the surface of the granular molded body with polyalkylene glycol, paraffin wax, higher fatty acids, etc. Patent Document 2 describes a technique for making granules containing coal ash, wood flour, clay, etc. less likely to scatter by coating them with cellulose, superabsorbent polymer powder, fibrous material, gypsum, etc. Patent Document 3 describes a technique for surface-treating the surface of a urine treatment material base material with a dust suppressant containing sodium silicate, glycerin, and diol-type or triol-type polypropylene glycol. [Prior art documents] [Patent Documents]

[0007] [Patent Document 1] Japanese Patent Publication No. 2006-42798 [Patent Document 2] Japanese Patent Publication No. 2005-211018 [Patent Document 3] Japanese Patent Publication No. 2015-84727 [Overview of the project] [Problems that the invention aims to solve]

[0008] However, while the inventions described in References 1-3 suppress dust generation to some extent immediately after manufacturing, the dust suppression ability of the pet urine treatment material was significantly reduced when it was subjected to impact. In other words, after manufacturing, the pet urine treatment material is packaged and transported to warehouses and retail stores, but due to vibrations during transport and impacts such as the bags being thrown around in storage after purchase, the dust suppression ability was often reduced when it was actually used in homes.

[0009] This invention has been made in view of the above problems, and its objective is to provide a low-dusting pet urine treatment material that has excellent dust suppression capabilities and whose dust suppression ability does not deteriorate even when subjected to impact during transport, etc.

[0010] Another object of the present invention is to provide a method for manufacturing a low-dusting pet urine treatment material having the above-mentioned properties.

[0011] Another object of the present invention is to provide a dust suppressant that can be used in low-dusting pet urine treatment materials.

[0012] Other objects and effects of the present invention will be readily understood by those skilled in the art by referring to the following description. [Means for solving the problem]

[0013] The inventors of this invention, from the perspective of a supplier of this product, have strived to further improve the important dust suppression performance required for pet urine treatment materials in order to meet current and future needs and to further enhance customer satisfaction, and have arrived at the present invention.

[0014] In other words, the low-dusting pet urine treatment material according to the present invention is a low-dusting pet urine treatment material having a dust-inhibiting agent as a surface treatment agent on the surface of the urine treatment material base material, wherein the dust-inhibiting agent comprises at least an inorganic salt of a polyvalent metal and a water-soluble organic substance.

[0015] With this configuration, a pet urine treatment material is obtained that has excellent dust suppression capabilities and whose dust suppression capabilities do not deteriorate even when subjected to impact during transport, etc.

[0016] In a preferred embodiment of the present invention, the inorganic salt of the polyvalent metal is preferably at least one of magnesium chloride, calcium chloride, or aluminum chloride. With such a configuration, a low-dusting pet urine treatment material with superior dust suppression effect can be obtained.

[0017] In a preferred embodiment of the present invention, it is preferable that the water-soluble organic substance has a solubility of 30 g or more in 100 g of water. According to such a configuration, a low-dust-generation urine treatment material for pets with an excellent dust generation suppressing effect can be obtained.

[0018] In a preferred embodiment of the present invention, it is preferable that the water-soluble organic substance has a hydroxy group.

[0019] In a preferred embodiment of the present invention, it is preferable that the water-soluble organic substance having a hydroxy group is a saccharide.

[0020] In a preferred embodiment of the present invention, it is preferable that the saccharide is glucose. According to such a configuration, a low-dust-generation urine treatment material for pets with an excellent dust generation suppressing effect can be obtained.

[0021] In a preferred embodiment of the present invention, the urine treatment material base material is (A) a natural bentonite or a clay-based raw material composed of an activated bentonite containing an alkali component using the bentonite as a raw material, (B) a plant-derived cellulosic raw material such as okara, pulp, or wood powder, and preferably contains either or both of the raw materials (A) and (B).

[0022] In a preferred embodiment of the present invention, the dust generation inhibitor contains the inorganic salt of the polyvalent metal at a concentration of 5 to 30% by weight, the water-soluble organic substance at a concentration of 10 to 55% by weight, and the inorganic salt of the polyvalent metal and the glucose at a weight ratio of 1:0.33 to 1:11. When the urine treatment material base material is (A) a natural bentonite or a clay-based raw material composed of an activated bentonite containing an alkali component using the bentonite as a raw material, it is used in a range of 0.1 to 2 parts by weight with respect to 100 parts by weight of the urine treatment material base material. When the urine treatment material base material is (B) a plant-derived cellulosic raw material such as okara, pulp, or wood flour, it is preferable to use it in an amount of 0.1 parts by weight or more per 100 parts by weight of the urine treatment material base material.

[0023] Furthermore, the present invention can also be considered as an invention of a dust suppressant.

[0024] The dust suppressant according to the present invention is a dust suppressant used in a pet urine treatment material base material, and is characterized in that it contains an inorganic salt of a polyvalent metal at a concentration of 5 to 30 weight percent, a water-soluble organic substance at a concentration of 10 to 55 weight percent, and the weight ratio of the inorganic salt of the polyvalent metal to the water-soluble organic substance is 1:0.33 to 1:11, the water-soluble organic substance has a solubility of 30 g or more per 100 g of water, and is used in an amount of 0.1 parts by weight or more per 100 parts by weight of the pet urine treatment material base material.

[0025] With this configuration, a dust suppressant can be obtained that provides a high dust suppression effect when used with clay-based substrates such as natural bentonite, okara-based substrates, pulp-based substrates, etc.

[0026] Furthermore, the present invention can also be considered as a method for manufacturing a low-dusting pet urine treatment material.

[0027] The method for manufacturing a low-dusting pet urine treatment material according to the present invention is: The steps include preparing a base material for urine treatment, The steps include preparing a dust suppressant and The step includes surface treatment of the surface of the urine treatment material substrate with the dust suppressant, The aforementioned urine treatment material base material is (A) Natural bentonite, or clayey raw material consisting of activated bentonite containing alkaline components, which is made from said bentonite. (B) Plant-derived cellulosic raw materials such as okara, pulp, and wood flour, It contains either or both of the ingredients of (A) and (B), The dust suppressant comprises at least a polyvalent metal ion and a water-soluble organic substance, wherein the polyvalent metal ion is a magnesium, calcium, or aluminum ion, and the water-soluble organic substance has a solubility of 30 g or more per 100 g of water. [Effects of the Invention]

[0028] The pet urine treatment material according to the present invention has excellent dust suppression capabilities, and its dust suppression capabilities do not easily deteriorate even when subjected to impact during transport or other means. [Brief explanation of the drawing]

[0029] [Figure 1] This is a diagram showing the configuration and dust generation amount of Example 1. [Figure 2] This is a diagram showing the configuration and dust generation amount of Example 2. [Figure 3] This chart shows the increase and decrease in dust generation before and after vibration in Example 3. [Figure 4] This is a chart (part 1) showing the change in the amount of dust generated after the container is opened. [Figure 5] This is a chart (part 2) showing the change in the amount of dust generated after the container is put in. [Figure 6] This figure shows an example of a vibrator used in vibration testing. [Figure 7] This graph shows the verification results of the preparation procedure for dust suppressants. [Figure 8] This graph shows the verification results for polyvalent metal salts. [Figure 9] This graph shows the verification results for water-soluble organic substances. [Figure 10] This graph shows the results of the verification regarding the mixing ratio. [Figure 11] This is graph (1) showing the verification results for the substrate. [Figure 12] This is graph (part 2) showing the verification results for the substrate. [Modes for carrying out the invention]

[0030] In the following, preferred embodiments of the low-dusting pet urine treatment material according to the present invention will be described in detail.

[0031] As mentioned earlier, the low-dusting pet urine treatment material according to the present invention is made by surface-treating a substrate for urine treatment material with a dust-suppressing agent.

[0032] [Dust suppressant] First, let's explain the dust suppressant. The dust suppressant used in this invention contains at least an inorganic salt of a polyvalent metal and a water-soluble organic substance. The inorganic salt of a polyvalent metal alone does not have a dust suppression effect, and some water-soluble organic substances have a dust suppression effect even when used alone, but using both together improves the dust suppression effect compared to using the water-soluble organic substance alone. At present, it is unclear what mechanism of action improves the dust suppression effect when the inorganic salt of a polyvalent metal and the water-soluble organic substance are used together.

[0033] In this invention, an inorganic salt of a polyvalent metal is used as a dust suppressant. As will be described in detail later, according to the inventors' verification, even with metal salts, monovalent metal salts such as lithium, sodium, and cesium only provide the dust suppression effect derived from the water-soluble organic matter when used in combination with water-soluble organic matter, and no synergistic effect was observed. The same was true for organic acid salts, and no improvement in dust suppression effect was observed by using water-soluble organic matter and organic acid salts of polyvalent metals in combination.

[0034] The inorganic salts of polyvalent metals used in this invention are not particularly limited, but calcium chloride, magnesium chloride, magnesium nitrate, aluminum chloride, and aluminum nitrate are preferred due to their ease of availability and handling, and the fact that the coated surface is colorless. Furthermore, although the mechanism of action is unknown, inorganic salts of polyvalent metals that are hygroscopic often show a significant improvement in dust suppression when used in combination with water-soluble organic substances.

[0035] The amount of the inorganic salt of the polyvalent metal is preferably in the range of 5 to 30 parts by weight per 100 parts by weight of the dust suppressant, and more preferably in the range of 20 to 30 parts by weight.

[0036] In the present invention, a water-soluble organic substance is used as the dust suppressant. The water-soluble organic substance used here is not particularly limited, but ethanol, polyethylene glycol, propylene glycol, glycerin, glucose, sorbitol, ε-caprolactam, sugars, and other compounds having a hydroxyl group are preferred.

[0037] In the present invention, it is preferable that the water-soluble organic substance has a solubility of 30 g or more per 100 g of water. Furthermore, the amount of water-soluble organic substance blended is preferably in the range of 10 to 55 parts by weight per 100 parts by weight of dust suppressant, and more preferably in the range of 30 to 45 parts by weight.

[0038] Furthermore, in the present invention, the ratio of the inorganic salt of the polyvalent metal to the water-soluble organic substance is preferably in the range of 1:0.3 to 11.

[0039] In the dust suppressant of the present invention, raw materials other than inorganic salts of polyvalent metals and water-soluble organic substances may be added, to the extent that the objective of the invention is not impaired.

[0040] Furthermore, in the present invention, it is preferable to add the dust suppressant by a method that allows the dust suppressant to be unevenly distributed on the surface of the urinary treatment material substrate, such as by spraying it onto the surface of the urinary treatment material substrate, rather than by kneading the dust suppressant into the raw materials of the urinary treatment material substrate.

[0041] [Base material for urine treatment materials] Next, we will explain the base material for the urine treatment material. Various types of urine treatment material base materials that may generate dust can be used as the urine treatment material base material for the pet urine treatment material of the present invention. Specifically, (A) clayey raw material consisting of natural bentonite or activated bentonite containing alkaline components made from said bentonite, (B) cellulosic raw material derived from plants such as okara, pulp, and wood flour can be used as the urine treatment material base material obtained by molding such raw materials.

[0042] Furthermore, when clayey raw materials are used, those consisting of natural bentonite or activated bentonite obtained by alkali treatment of the bentonite are used. Natural bentonite and activated bentonite that constitute the clayey raw materials are often made from natural raw materials, and are often preferable, as they can exhibit better water absorption and cohesive solidification properties. Here, Ca-type smectite is a clay mineral that is generally found in the middle layer of smectite clay deposits, and is a clay in which a large amount of exchangeable cations such as Ca ions and Mg ions exist between the layers of the smectite structure. While a urine treatment material base material that uses such Ca-type smectite as the main raw material has excellent properties such as water absorption and cohesive solidification, it has the problem of being brittle and easily chipped. By surface treatment with the dust suppressant of the present invention, dust generation can be suppressed even in a urine treatment material base material made from such brittle raw materials.

[0043] [Manufacturing method] Next, an example of a method for producing a low-dusting pet urine treatment material according to the present invention will be described. For the dust suppressant, a polyvalent metal salt is added to a predetermined amount of water and stirred while heating. Once the polyvalent metal salt has dissolved, a water-soluble organic substance is added and further heating and stirring is performed to obtain an aqueous solution of the dust suppressant. There is no difference in effect whether the water-soluble organic substance is added first and then the polyvalent metal salt is added after it has dissolved. Depending on the type of polyvalent metal salt and water-soluble organic substance used, it is often a viscous, colorless, transparent solution. By spraying the obtained liquid dust suppressant onto the surface of the urine treatment material substrate, the low-dusting pet urine treatment material according to the present invention can be obtained.

[0044] Regarding the amount of dust suppressant to be sprayed, if the urine treatment material base material is made from clayey raw materials, it is preferable to use 0.1 to 2 parts by weight of the dust suppressant solution per 100 parts by weight of the urine treatment material base material. If the urine treatment material base material is made from plant-derived cellulosic raw materials, it is preferable to use 0.1 parts by weight or more of the dust suppressant solution per 100 parts by weight of the urine treatment material base material. This is because, in the case of urine treatment materials made from clayey raw materials, solidification is of paramount importance, so it is preferable to use the dust suppressant within a range that does not inhibit solidification. On the other hand, with plant-derived cellulosic raw materials, solidification is not as important as with clayey raw materials, or generally, they do not have solidification properties to begin with. Therefore, even if the amount sprayed is increased, there is almost no effect on solidification, etc., so it is possible to increase the amount sprayed to achieve a dust suppression effect. Note that the amount sprayed here includes the weight of water.

[0045] [Regarding the surface treatment process] Next, the process of surface-treating the urine treatment material substrate with a dust-generating inhibitor in the present invention will be described. As for surface treatment with a dust-generating inhibitor, general coating methods such as spraying a liquid dust-generating inhibitor onto the urine treatment material substrate and then shaking it in a case can be used as appropriate. However, from the viewpoint of evenly adhering the dust-generating inhibitor to the surface of the urine treatment material substrate, it is preferable to shake the entire urine treatment material substrate in a container while dropping or spraying a liquid dust-generating inhibitor onto it, and then, if necessary, transfer it to a suitable container and treat it uniformly by vibration or rotation. As an example, surface treatment can be performed by the following procedure. A stainless steel drum is placed on a pot mill turntable, the urine treatment material substrate is placed in the stainless steel drum, and an aqueous dust-generating inhibitor is dropped onto it while shaking the entire drum at a speed of about 5 to 30 rpm. After sealing the stainless steel drum, rotating it at a predetermined rotation speed for about 30 seconds to 5 minutes allows an appropriate amount of dust-generating inhibitor to adhere to the surface of the urine treatment material substrate.

[0046] As mentioned earlier, the low-dusting pet urine treatment material according to the present invention is characterized by low dust generation immediately after manufacturing, as well as minimal decrease in dust suppression ability after impact. In order to evaluate both of these, the present invention examines the amount of dust generated and the change in the amount of dust generated.

[0047] In this invention, the method for measuring the amount of dust generated will be described later, but if the amount of dust generated is 100 cpm or less, most people will not notice the generation of dust; if the amount of dust generated is around 100 to 300 cpm, most people will not be bothered by the dust; and if the amount of dust generated is around 300 to 500 cpm, some dust will be noticeable. Therefore, in this invention, it is preferable that the amount of dust generated by the pet urine treatment material is 300 cpm or less, and more preferably 100 cpm or less. When using a pet toilet of a typical size, the amount of pet urine treatment material to be replenished per use is generally around 100 to 250 g, so if the amount of dust generated per 1 kg is 400 cpm or less, the amount of dust generated when replenishing will be 100 cpm or less, which is considered to be a level at which most people will not notice the generation of dust.

[0048] In the present invention, when the dust suppressant is a clayey raw material, it is preferable to use it in an amount of 0.1 to 2 parts by weight per 100 parts by weight of the urine treatment material base material, and more preferably in an amount of 0.4 to 1.2 parts by weight. By using the dust suppressant within the above range, sufficient dust suppression ability can be obtained without impairing the urine absorption and solidification properties of the pet urine treatment material.

[0049] On the other hand, when the urine treatment material base material is a cellulosic raw material derived from plants, it is preferable to use a dust suppressant solution in an amount of 0.1 parts by weight or more per 100 parts by weight of the urine treatment material base material, and more preferably in the range of 0.1 to 2 parts by weight. This is because cellulosic raw materials derived from plants have a low bulk density, and the volume per 100 parts by weight of the urine treatment material base material becomes large, so it is preferable to spray a larger amount than with clay-based raw materials in order to obtain a sufficient effect.

[0050] [Basic performance as a pet urine treatment material] As mentioned earlier, the low-dusting pet urine treatment material according to the present invention is primarily intended to suppress dust generation, but at the same time, it is also configured to satisfy the basic performance requirements of a pet urine treatment material, such as water absorption capacity (urine absorption capacity) and solidification strength.

[0051] Here, the solidification strength of pet urine treatment material refers to the strength of the solidified mass after urine absorption. If the solidification strength is high, the mass will not break down when removed after absorption, and even if it is accidentally dropped on the floor, it will maintain its shape, allowing for hygienic removal of the solidified mass after absorption. Furthermore, if the water absorption capacity of the pet urine treatment material is high, urine can be quickly absorbed with a small amount of material, which prevents it from flowing downwards and reduces the amount used per use, making it economically advantageous. [Examples]

[0052] The following describes embodiments of the present invention, but the present invention is not limited to the following configurations.

[0053] [Manufacturing of base materials for urine treatment] Dioctahedral-type smectite clay, mined from a subbentonite deposit in Shibata City, Niigata Prefecture, was used as the raw material. Water was added as needed to obtain a coarse material with a moisture content of 33%. 10 kg of this coarse material (dry weight at 150°C) and 300 g (= 5.7 equivalents) of sodium carbonate powder (Na2CO3), an activated bentonitizing agent, were placed in the same polyethylene bag and shaken well. The mixture was then passed through a single-screw horizontal extruder equipped with a 10 mm pore diameter molding plate three times for mixing and kneading. The coarse granules were granulated using a disc pelletizer (rotary roll vertical extruder) equipped with a 3 mm pore diameter molding plate, dried at 170°C in a rotary small drying oven, and then subjected to a crusher and sieve to obtain a self-adhesive urine treatment material base.

[0054] [Manufacturing of dust suppressants] To 100g of water, 247.09g of magnesium chloride (anhydrous equivalent) was added and heated while stirring to dissolve it. Then, 231.4g of ethanol was added and the mixture was heated and stirred further to obtain the aqueous dust suppressant according to Example 1-1.

[0055] [Manufacturing of low-dust pet urine treatment materials] A stainless steel drum (300 mm in diameter x 200 mm in height) was placed on a pot mill turntable, and 2 kg of urine treatment material base was placed in the stainless steel drum. While rotating it at a speed of about 10 rpm to shake the entire contents, 20 g (1.0 weight percent) of dust suppressant was dropped into it. Then, by rotating it at a speed of about 10 rpm for about 1 minute, a low-dusting pet urine treatment material according to Example 1-1 was obtained in which 1.0 weight percent of the dust suppressant was impregnated onto the surface of the urine treatment material base.

[0056] Next, by changing a portion of the formulation in Example 1-1 to the configuration shown in Figure 1, low-dusting pet urine treatment materials for Examples 1-2 to 1-12 and Comparative Examples 1-1 and 1-2 were obtained. In Example 1 and subsequent examples, EtOH represents ethanol, PEG represents polyethylene glycol, PG represents propylene glycol, GL represents glycerin, Glc represents glucose, Sor represents sorbitol, and CPL represents ε-caprolactam. The number indicated in the type name of PEG represents the average molecular weight.

[0057] [Measurement of dust generation: Measured after 1 minute] For each example and comparative example of low-dusting pet urine treatment material, 2 kg of material is prepared as a sample after spraying it with a dust suppressant and leaving it overnight or longer to allow the dust suppressant to settle. A wooden semi-sealed container for dust measurement, approximately 45 cm high, 35 cm long, and 35 cm wide, is prepared with a circular flat-bottomed tray placed inside and connected to a dust meter. A round-bottomed container with a manually operated circular hole with a diameter of 5 cm at the bottom is also prepared. 1 kg of the sample is transferred to the round-bottomed container. The circular hole at the bottom of the round-bottomed container is opened inside the semi-sealed container for dust measurement, and the entire sample is allowed to fall naturally from a distance of 30-40 cm to the circular flat-bottomed tray. After standing for 1 minute, the amount of dust (unit: cpm) obtained by aspirating the atmosphere inside the semi-sealed container for dust measurement for 1 minute using a dust meter (light scattering method, digital dust meter LD-5D, manufactured by Shibata Scientific Co., Ltd.) is measured. This measurement was performed twice, and the average value was taken as the dust generation amount (cpm). Strictly speaking, the dust amount here is expressed as the amount of scattered light (cpm value) due to the dust material. However, since the amount of scattered light due to the dust material is proportional to the concentration of dust suspended in the air (quantity per unit space), this was used as the dust generation amount (cpm / kg) representing the dust generation potential of each sample. In the "immediate measurement" described later, the dust amount is measured immediately after dropping without allowing it to stand for one minute.

[0058] [Dust generation suppression rate] The dust reduction rate I(%), which indicates how much the amount of dust generated by the low-dusting pet urine treatment material in each example and comparative example is reduced compared to the amount of dust generated before impregnation of each example and comparative example, which corresponds to the blank sample, is shown by the following formula. Here, DX represents the amount of dust generated by the target sample (after impregnation), and DB represents the amount of dust generated by the untreated material (before impregnation). I = (1 - DX / DB) × 100 ... Equation (1) In other words, the dust suppression rate obtained by the above formula (1) indicates the percentage of dust suppression. If I is 60, it means that 60% of the dust generated in the untreated sample is suppressed, and the amount of dust generated by the sample is 40% of the dust generated by the untreated sample DB.

[0059] [Vibration Test] In this vibration test, the amount of dust generated after transporting a predetermined sample was measured beforehand. A comparative test was then conducted to determine how much vibration was required to generate the same amount of dust as after transport. Based on the results of this comparative test, the vibration treatment conditions were set. In other words, each sample after the vibration test was subjected to the same level of vibration as it was after transport. Figure 6 shows the structure of the vibrator used for vibration testing. In the figure, 1 is a self-made vibrator, 2 is a vibration generator (small electromagnetic feeder CF-2, manufactured by Shinko Electric Co., Ltd.), 3 is a controller (controller for small electromagnetic feeder C8-1VF, manufactured by Shinko Electric Co., Ltd.), 4 is a mounting stand, and 5 is a sample bag. The low-dusting pet urine treatment material for each example and comparative example is used as a sample, and 2 kg of each is placed in a commercially available nylon poly bag (330 mm long x 260 mm wide x 0.095 mm thick, outer layer nylon / inner layer polyethylene), and the opening of the nylon poly bag is closed to form sample bag 5. Sample bag 5 is placed on mounting stand 4, and vibration is applied for 10 minutes using a half-wave drive method with an output voltage of 190 V and a vibration frequency of 50 Hz, after which the amount of dust generated is measured and defined as the amount of dust generated after vibration (cpm).

[0060] [Verification results for Example 1] Example 1 is an example using magnesium chloride, an inorganic salt of a polyvalent metal, and various water-soluble organic substances, and the results are shown in Figure 1. As shown in Figure 1, Comparative Example 1-1, which used only magnesium chloride as a dust suppressant, showed an increase in dust generation after surface treatment, whereas Examples 1-1 to 1-12, which used magnesium chloride in combination with various water-soluble organic substances as a dust suppressant, all showed a significant decrease in dust generation. Furthermore, the dust suppression effect of Examples 1-1 to 1-12 was higher than that of Comparative Example 1-2, which is the applicant's prior art. [Examples]

[0061] [Manufacturing of low-dusting pet urine treatment material according to Example 2] In Example 1-1, by changing the composition of the polyvalent metal inorganic salt and water-soluble organic matter to the configuration shown in Figure 2, low-dusting pet urine treatment materials related to Examples 2-1 to 2-6 and Comparative Examples 2-1 to 2-5 were obtained.

[0062] [Verification results for Example 2] Example 2 is an example using inorganic salts of various metals other than magnesium chloride and various water-soluble organic substances, and the results are shown in Figure 2. As shown in Figure 2, the amount of dust generated was significantly reduced in all of Examples 2-1 to 2-5. Comparative Examples 2-1 to 2-4, which used inorganic salts of monovalent metals, also showed a reduction in dust generation, but the reduction was smaller compared to Examples 1, 2-1 to 2-5, and the results were almost the same as Comparative Examples 1-2 and 2-5, which used water-soluble organic substances alone. From these results, it is considered that inorganic salts of monovalent metals do not produce a synergistic effect in suppressing dust generation even when used in combination with water-soluble organic substances. [Examples]

[0063] [Manufacturing of low-dusting pet urine treatment material according to Example 3] In Examples 1-10, by changing the amount of glucose in the dust suppressant to the configuration shown in Figure 3, a low-dusting pet urine treatment material according to Examples 3-1 and 3-2 was obtained. Comparative Example 3-1 is a so-called blank sample in which no dust suppressant was used.

[0064] [Verification results for Example 3] Example 3 is an example to verify the change in dust generation before and after vibration treatment when vibration is applied to a low-dusting pet urine treatment material. Figure 3 shows the change in dust generation before and after vibration treatment. Comparative Example 3-1, which was a blank sample, showed a significant increase in dust generation after vibration treatment. In contrast, the samples of Examples 3-1 and 3-2 according to the present invention not only had a low dust generation even before vibration treatment, but the increase in dust generation was also relatively suppressed even after vibration treatment. It is presumed that the dust suppression ability does not easily decrease even when vibration is applied during transportation, etc., and that a certain degree of dust suppression effect is maintained even when the material reaches the user. Figures 4 and 5 show the results of verifying the amount of dust generated when a user actually uses the low-dusting pet urine treatment material. When measuring the amount of dust generation, the "immediate measurement" described above was performed by measuring the amount of dust generation every 30 seconds from immediately after introduction. Figure 4 shows the amount of dust generated by the low-dusting pet urine treatment material before vibration treatment, and Figure 5 shows the amount of dust generated by the low-dusting pet urine treatment material after vibration treatment. While dust generation is generally considered to be at a level that is not noticeable to humans if it is 100 cpm or less, Example 3-2, a low-dusting pet urine treatment agent according to the present invention, produced a level of dust that was not noticeable immediately after application before vibration treatment, and even after vibration treatment, the dust level became unnoticeable within about 30 seconds. In contrast, Comparative Example 3-1, which is additive-free, required a longer time for the dust generation to subside, approximately 180 seconds before vibration treatment and 210 seconds after vibration treatment, compared to the present invention. [Examples]

[0065] [Manufacturing of low-dusting pet urine treatment material according to Example 4] In the preparation procedure for the dust suppressant of Example 3-1, a low-dusting pet urine treatment material according to Example 4-1 was obtained by adding glucose first and dissolving it, and then adding magnesium chloride.

[0066] [Verification results for Example 4] Example 4 is an example to verify whether the order in which the inorganic salt of a polyvalent metal and the water-soluble organic matter are added during the preparation of the dust suppressant makes a difference in the effectiveness of the dust suppressant. The results of Example 4 are shown in Figure 7. The amount of dust generated in Examples 3-1 and 4-1 was almost the same, suggesting that the order in which the inorganic salt of a polyvalent metal and the water-soluble organic matter are added does not affect the performance of the dust suppressant. [Examples]

[0067] [Manufacturing of low-dusting pet urine treatment material according to Example 5] In Example 3-1, a low-dusting pet urine treatment material according to Example 5-1 was obtained in the same manner as in Example 3-1, except that the amount of impregnation was changed to 0.8 weight percent. In Example 5-1, a low-dusting pet urine treatment material according to Comparative Example 5-1 was obtained by changing 20 weight percent magnesium chloride in the dust suppressant to 20 weight percent magnesium acetate.

[0068] [Verification results for Example 5] Example 5 is an example to compare and verify the dust suppression effect of an inorganic salt of a polyvalent metal with the effect of an organic acid salt of a polyvalent metal. The results of Example 5 are shown in Figure 8. For reasons that are not entirely clear, magnesium chloride, an inorganic salt of a polyvalent metal, showed a high dust suppression effect when used in combination with a water-soluble organic substance (Example 5-1), while magnesium acetate, an organic acid salt of a polyvalent metal, did not show a dust suppression effect (Comparative Example 5-1), and the results were similar to those of Comparative Example 3-1, which was a blank sample. Based on these results, it was decided to use an inorganic salt of a polyvalent metal in the present invention. [Examples]

[0069] [Manufacturing of low-dusting pet urine treatment material according to Example 6] In Example 5-1, a low-dusting pet urine treatment material according to Example 6-1 was obtained by changing the glucose in the dust suppressant to fructose. In Example 5-1, a low-dusting pet urine treatment material according to Comparative Example 6-1 was obtained by changing the 30% by weight glucose in the dust suppressant to 20% by weight lactose and changing the amount added to 1.0% by weight. The reason why the amount of lactose is less than that of glucose and fructose is that it was not possible to add 30% by weight lactose due to its low solubility.

[0070] [Verification results for Example 6] Example 6 is an example to verify the effect of differences in the type and solubility of water-soluble organic substances on the dust suppression effect. The results of Example 6 are shown in Figure 9. Both glucose and fructose are sugars with high solubility in water, and both showed a high dust suppression effect when used in combination with an inorganic salt of a polyvalent metal (Examples 5-1, 6-1). On the other hand, Comparative Example 6-1, which contained lactose, showed a decrease in dust generation, but the results were inferior to Examples 5-1 and 6-1. This is thought to be partly due to the fact that the amount of lactose added cannot be increased because its solubility in water is low, at 16.4 g / 100 g at 20°C. From the results of Example 6, it is considered preferable that the water-soluble organic substance used in the present invention has a solubility in water of more than 30 g / 100 g at room temperature, as this makes it easier to achieve the objectives of the present invention. [Examples]

[0071] [Manufacturing of low-dusting pet urine treatment material according to Example 7] In Examples 1-10, by changing the proportions of magnesium chloride and glucose in the dust suppressant to the configuration shown in Figure 10, low-dusting pet urine treatment materials according to Examples 7-1 to 7-8 were obtained.

[0072] [Verification results for Example 7] Example 7 is an example to verify the appropriate mixing ratio of a polyvalent metal inorganic salt and a water-soluble organic substance. The results of Example 7 are shown in Figure 10. Example 7-4, which used a ratio of magnesium chloride:glucose = 30:10, and Example 7-7, which used a ratio of magnesium chloride:glucose = 5:55, showed a significant dust suppression effect compared to the conventional technology, Comparative Example 1-2. On the other hand, Example 7-5, which contained 35 weight percent magnesium chloride, was unsuitable for practical use because the magnesium chloride did not completely dissolve. Similarly, Example 7-8, which contained 60 weight percent glucose, dissolved glucose once but then precipitated, making it unsuitable for practical use as well. From these results, the mixing ratio of the polyvalent metal inorganic salt should be in the range of 5 to 30 weight percent, and the mixing ratio of the water-soluble organic substance should be in the range of 10 to 55 weight percent. Furthermore, the appropriate mixing ratio range for the polyvalent metal inorganic salt and the water-soluble organic substance should be in the range of 1:0.333 to 1:11. [Examples]

[0073] [Manufacturing of low-dusting pet urine treatment material according to Example 8] A pet urine treatment material made from okara (soy pulp) (Okara Cat Litter Green, manufactured by Hitachi Kako Co., Ltd.) was dried overnight in a dryer set to 90°C. Then, a dust suppressant with the same composition as in Example 3-1 was added to 1 kg of the pet urine treatment material in the following proportions: Example 8-1: 0% by weight, Example 8-2: 0.2% by weight, Example 8-3: 0.4% by weight, Example 8-4: 0.6% by weight, Example 8-5: 0.8% by weight, and Example 8-6: 1.0% by weight, thereby obtaining a low-dusting pet urine treatment material according to Example 8. The pet urine treatment material made from okara used in this example does not solidify when it absorbs urine and is flushed down the toilet after use.

[0074] In Example 8 and Example 9 (described later), in addition to the aforementioned "measurement after 1 minute," a "measurement immediately after" was also performed when measuring the amount of dust generated. This was because, in Examples 8 and 9, which used substrates made from okara (soy pulp) and pulp, the time during which dust was airborne was shorter compared to other examples using clay substrates. Therefore, after 1 minute of standing, the dust had almost completely subsided by the time of measurement, making it difficult to distinguish between the two.

[0075] [Verification results for Example 8] Example 8 is an example to verify the effect of using the dust-generating inhibitor according to the present invention on a pet urine treatment material made from okara (soy pulp). The results of Example 8 are shown in Figure 11. As is clear from the results shown in Figure 11, a dust-generating inhibitory effect was obtained even for a pet urine treatment material made from okara when using the dust-generating inhibitor according to the present invention. Furthermore, regarding the amount of additive, the dust-generating inhibitory effect improved as the amount of additive increased in the range of 0.2 to 1.0 weight percent. [Examples]

[0076] [Manufacturing of low-dusting pet urine treatment material according to Example 9] A pulp-based pet urine treatment material (DeoSand Multiple Cat Paper Litter, manufactured by Uni-Charm Corporation) was dried overnight in a dryer set to 90°C. Then, a dust-generating inhibitor with the same composition as in Example 3-1 was added to 1 kg of the pet urine treatment material in the following proportions: Example 9-1: 0.0% by weight, Example 9-2: 0.2% by weight, Example 9-3: 0.4% by weight, Example 9-4: 0.6% by weight, Example 9-5: 0.8% by weight, and Example 9-6: 1.0% by weight, to obtain the low-dusting pet urine treatment material according to Example 9. The pulp-based pet urine treatment material used in this example is in a form that solidifies after absorbing urine.

[0077] [Verification results for Example 9] Example 9 is an example to verify the effect of using the dust suppressant according to the present invention on a pulp-based pet urine treatment material. The results of Example 9 are shown in Figure 12. As is clear from the results shown in Figure 12, the dust suppression effect was obtained even for pulp-based pet urine treatment materials by using the dust suppressant according to the present invention. Furthermore, regarding the amount of impregnation, the dust suppression effect improved as the amount of impregnation increased up to 0.6 weight percent, but it plateaued thereafter. [Industrial applicability]

[0078] As described above, the low-dusting pet urine treatment material according to the present invention exhibits minimal reduction in dust suppression ability even when subjected to impact during transport or other means, and excellent dust suppression ability can be expected.

Claims

1. A pet urine treatment material having a dust-inhibiting agent as a surface treatment agent on the surface of the urine treatment material base material, The aforementioned urine treatment material base material is (A) A clay-based raw material consisting of natural bentonite, or activated bentonite containing alkaline components, made from said bentonite, (B) Plant-derived cellulosic raw materials such as okara, pulp, and wood flour, Contains one or both of the following ingredients: The dust suppressant contains at least a polyvalent metal inorganic salt at a concentration of 5 to 30 weight percent and a water-soluble organic substance at a concentration of 10 to 55 weight percent, in a weight ratio of 1:0.33 to 1:

11. The inorganic salt of the polyvalent metal comprises at least one of the following: calcium chloride, magnesium chloride, magnesium nitrate, aluminum chloride, and aluminum nitrate. The aforementioned water-soluble organic substance is characterized by having a hydroxyl group and containing at least one of ethanol, polyethylene glycol, propylene glycol, glycerin, glucose, sorbitol, and ε-caprolactam, as a pet urine treatment material.

2. The pet urine treatment material according to claim 1, characterized in that the water-soluble organic substance has a solubility of 30 g or more per 100 g of water.

3. The aforementioned dust suppressant is When the urine treatment material base material is (A) clayey raw material, it is used in an amount of 0.1 to 2 parts by weight per 100 parts by weight of the urine treatment material base material. The pet urine treatment material according to claim 1, characterized in that, when the urine treatment material base material is (B) a cellulosic raw material derived from plants, it is used in an amount of 0.1 parts by weight or more per 100 parts by weight of the urine treatment material base material.

4. A dust suppressant used in pet urine treatment material base material, comprising a polyvalent metal inorganic salt at a concentration of 5 to 30 weight percent, a water-soluble organic substance at a concentration of 10 to 55 weight percent, and the polyvalent metal inorganic salt and the water-soluble organic substance in a weight ratio of 1:0.33 to 1:

11. The inorganic salt of the polyvalent metal comprises at least one of the following: calcium chloride, magnesium chloride, magnesium nitrate, aluminum chloride, and aluminum nitrate. The aforementioned water-soluble organic substance has a hydroxyl group and comprises at least one of ethanol, polyethylene glycol, propylene glycol, glycerin, glucose, sorbitol, and ε-caprolactam. The aforementioned water-soluble organic substance has a solubility of 30 g or more per 100 g of water, and is used in an amount of 0.1 parts by weight or more per 100 parts by weight of the pet urine treatment material base material, characterized in that it is a dust suppressant.

5. The steps include preparing a base material for urine treatment, The steps include preparing a dust suppressant and The step includes surface treatment of the surface of the urine treatment material substrate with the dust suppressant, The aforementioned urine treatment material base material is (A) A clay-based raw material consisting of natural bentonite, or activated bentonite containing alkaline components, made from said bentonite, (B) Plant-derived cellulosic raw materials such as okara, pulp, and wood flour, Contains one or both of the following ingredients: The dust suppressant contains at least a polyvalent metal inorganic salt at a concentration of 5 to 30 weight percent and a water-soluble organic substance at a concentration of 10 to 55 weight percent, in a weight ratio of 1:0.33 to 1:

11. The inorganic salt of the polyvalent metal comprises at least one of the following: calcium chloride, magnesium chloride, magnesium nitrate, aluminum chloride, and aluminum nitrate. The aforementioned water-soluble organic substance has a hydroxyl group and comprises at least one of ethanol, polyethylene glycol, propylene glycol, glycerin, glucose, sorbitol, and ε-caprolactam. A method for producing a low-dusting pet urine treatment material, characterized in that the water-soluble organic substance has a solubility of 30 g or more per 100 g of water.