Grease composition

Abstract

The present invention provides a grease composition which contains (A) a base oil, (B) a urea-based thickening agent and (C) a fat or oil curing agent, wherein: particles containing the urea-based thickening agent (B) in the grease composition satisfy requirement (I); the grease composition is liquefied if heated to a certain temperature or higher, and is returned to a solid state if cooled to room temperature after being heated to the certain temperature or higher; and the grease composition is highly responsive to the application of a shear stress, and is likely to be softened when a shear stress is applied thereto. Requirement (I): The area-based arithmetic mean particle diameter of the particles is 2.0 μm or less as determined by a laser diffraction / scattering method.

Description

Technical Field

[0001] The present invention relates to a grease composition.

Background Art

[0002] Grease compositions are easier to seal than lubricating oils and enable miniaturization and weight reduction of the machines to which they are applied. Therefore, they have been widely used conventionally for lubricating various sliding parts in automobiles, electric devices, industrial machines, and industrial equipment.

[0003] In addition, due to the increasing awareness of energy conservation in recent years, low torque characteristics are also required for grease compositions. For example, in Patent Document 1, a grease composition containing a base oil, a thickener, and an amino acid-based gelling agent has been proposed as a grease composition having low torque characteristics. Further, in Patent Document 2, a grease composition containing a saturated fatty acid triglyceride as a base oil and a glycerin fatty acid ester as a thickener has been proposed as a grease composition having low torque characteristics.

Prior Art Documents

Patent Documents

[0004]

Patent Document 1

Patent Document 2

Summary of the Invention

Problems to be Solved by the Invention

[0005] By the way, for example, in a factory robot, the filling of a grease composition into unit-type devices such as a speed reducer, a servo motor, a controller, and a torch is mainly performed by drum pumping, in which the grease composition contained in a drum can is filled via a hose using a pump. However, drum pumping is a method of filling grease compositions in their characteristic solid state, which makes it difficult for the grease composition to reach gaps and corners in unit-type equipment when injecting it. Furthermore, in order to inject the appropriate amount of grease composition without insufficient filling, it is necessary to supply an excess amount of grease composition compared to the amount that should actually be filled, resulting in a lot of waste.

[0006] Therefore, the inventors diligently studied and investigated the above problem, and arrived at the following idea. In other words, we conceived the idea that by heating a solid grease composition to a certain temperature or higher to liquefy it, immersing the device in the liquefied grease composition, removing it, and returning it to room temperature to solidify the grease composition, we could ensure that the solid grease composition filled all the gaps in the device while also efficiently filling it with the appropriate amount of solid grease composition without waste.

[0007] Therefore, in order to realize the above idea, the inventors focused on grease compositions containing oil hardening agents, as described in Patent Documents 1 and 2, and conducted diligent research. However, it was found that grease compositions containing oil hardening agents have insufficient responsiveness to the application of shear stress and do not soften easily when shear stress is applied. As mentioned above, awareness of energy conservation has been increasing in recent years. For this reason, grease compositions are also required to have high responsiveness to the application of shear stress and to soften easily when shear stress is applied.

[0008] Therefore, the object of the present invention is to provide a grease composition that liquefies when heated above a certain temperature, returns to a solid state when returned to room temperature after being heated above a certain temperature, and moreover, exhibits high responsiveness to the application of shear stress and softens easily when shear stress is applied. [Means for solving the problem]

[0009] In diligent research to solve the above problems, the inventor conceived the idea of ​​using a combination of an oil curing agent and a urea-based thickener. Furthermore, the inventor diligently investigated the particle size of the particles containing the urea-based thickener. As a result, the inventor found that by adjusting the arithmetic mean particle size based on area, measured by laser diffraction and scattering, to a predetermined range, and by using a grease composition containing an oil curing agent, the above problems could be solved, thus completing the present invention.

[0010] In other words, the present invention provides the following [1]. [1] A grease composition containing a base oil (A), a urea-based thickener (B), and an oil hardening agent (C), A grease composition wherein the particles containing the urea-based thickener (B) in the grease composition satisfy the following requirement (I). Requirement (I): The arithmetic mean particle diameter based on area, when the particles are measured by laser diffraction / scattering, is 2.0 μm or less. [Effects of the Invention]

[0011] According to the present invention, it is possible to provide a grease composition that liquefies when heated above a certain temperature, returns to a solid state when returned to room temperature after being heated above a certain temperature, and moreover, exhibits high responsiveness to the application of shear stress and softens easily when shear stress is applied. [Brief explanation of the drawing]

[0012] [Figure 1] This is a schematic cross-sectional view of a grease manufacturing apparatus used in one aspect of the present invention. [Figure 2] Figure 1 is a schematic diagram of the cross-section of the first uneven portion on the container body side of the grease manufacturing apparatus, in a direction perpendicular to the axis of rotation. [Figure 3] This is a schematic diagram of the cross-section of the grease manufacturing apparatus used in Comparative Example 2. [Figure 4] These are the rheometer measurement results for Examples 1 and 2 and Comparative Example 1. [Figure 5]These are the rheometer measurement results for Comparative Examples 2-4. [Modes for carrying out the invention]

[0013] In this specification, the lower and upper limits described in steps for a preferred numerical range (e.g., a range of content, etc.) can be combined independently. For example, from the description "preferably 10 to 90, more preferably 30 to 60", the "preferred lower limit (10)" and the "more preferred upper limit (60)" can be combined to arrive at "10 to 60". Furthermore, in this specification, the numerical values ​​in the examples are values ​​that can be used as upper or lower limits.

[0014] In this invention, room temperature means 20°C to 30°C. In this invention, room temperature means 25°C. Furthermore, in this invention, heating means heating to a temperature higher than room temperature, and specifically means heating to 60°C to 80°C.

[0015] [Grease composition] The grease composition of the present invention is a grease composition containing a base oil (A), a urea-based thickener (B), and an oil hardening agent (C), wherein the particles containing the urea-based thickener (B) in the grease composition satisfy the following requirement (I). Requirement (I): The arithmetic mean particle diameter based on area, when the particles are measured by laser diffraction / scattering, is 2.0 μm or less. In the following explanation, "base oil (A)", "urea-based thickener (B)", and "oil hardening agent (C)" will also be referred to as "component (A)", "component (B)", and "component (C)", respectively.

[0016] In a grease composition according to one aspect of the present invention, the total content of component (A), component (B), and component (C) is preferably 60% by mass or more, more preferably 70% by mass or more, even more preferably 80% by mass or more, and even more preferably 90% by mass or more, based on the total amount (100% by mass) of the grease composition. Also, it is usually 100% by mass or less, preferably less than 100% by mass, more preferably 99% by mass or less, and even more preferably 98% by mass or less. Furthermore, a grease composition according to one embodiment of the present invention may contain other components other than components (A), (B), and (C), as long as they do not impair the effects of the present invention.

[0017] <Requirement (I)> The grease composition of the present invention satisfies the following requirement (I) in the particles containing the urea-based thickener (B) in the grease composition. Requirement (I): The arithmetic mean particle diameter based on area, when the particles are measured by laser diffraction / scattering, is 2.0 μm or less. By satisfying the above requirement (I), a grease composition that softens when shear stress is applied is obtained.

[0018] The above requirement (I) can also be considered a parameter indicating the state of aggregation of the urea-based thickener (B) in the grease composition. Here, the "particles containing urea-based thickener (B)" that are measured by laser diffraction and scattering refer to particles formed by the aggregation of urea-based thickener (B) contained in the grease composition. If the grease composition contains additives other than the urea-based thickener (B), the particle size specified in requirement (I) above can be obtained by measuring a grease composition prepared under the same conditions without the additive using laser diffraction / scattering. However, if the additive is liquid at room temperature (25°C) or dissolves in the base oil (A), the grease composition containing the additive may be used as the measurement target.

[0019] Urea-based thickeners (B) are usually obtained by reacting an isocyanate compound with a monoamine, but because the reaction rate is very fast, the urea-based thickener (B) tends to aggregate, and large particles (micelle particles, so-called "clumps") are easily generated in excess. As a result of the inventors' diligent research, it was found that when the particle size specified in requirement (I) above exceeds 2.0 μm, the grease composition has insufficient responsiveness to shear stress and does not soften easily even when shear stress is applied. On the other hand, it was found that by reducing the particle size specified in requirement (I) above to 2.0 μm or less, a grease composition with high responsiveness to shear stress and that softens easily when shear stress is applied can be obtained. This effect is presumed to be due to the fact that by reducing the particle size to 2.0 μm or less as defined in requirement (I) above, the grease itself is composed of fine bundles with a narrow distribution of thickness and length, and therefore it is more easily changed to liquid properties with small stress. Furthermore, by reducing the particle size to 2.0 μm or less as defined in requirement (I) above, the retention capacity of the base oil (A) by these particles is improved. Therefore, it is presumed that the base oil (A) is distributed well, and consequently, the effect of the oil hardening agent (C) being distributed well to the lubricating part is also improved. From the above viewpoint, in a grease composition according to one embodiment of the present invention, the particle size defined in requirement (I) above is preferably 1.5 μm or less, more preferably 1.0 μm or less, even more preferably 0.9 μm or less, even more preferably 0.8 μm or less, still more preferably 0.7 μm or less, even more preferably 0.6 μm or less, even more preferably 0.5 μm or less, and even more preferably 0.4 μm or less. Also, it is usually 0.01 μm or more.

[0020] <Requirement (II)> Here, it is preferable that the grease composition according to one aspect of the present invention further satisfies the following requirement (II). Requirement (II): The specific surface area of ​​the particle measured by laser diffraction and scattering is 0.5 × 10 5 cm 2 / cm 3 That's all. The specific surface area defined in the above requirement (II) is a secondary index indicating the state of refinement of the particles containing the urea-based thickener (B) in the grease composition and the presence of large particles (lumps). That is, by satisfying the above requirement (I) and further satisfying the above requirement (II), it indicates that the state of refinement of the particles containing the urea-based thickener (B) in the grease composition is better, and the presence of large particles (lumps) is more suppressed. Therefore, a grease composition having a higher responsiveness to shear stress and being more likely to soften when a shear stress is applied can be obtained. From the above viewpoints, the specific surface area defined in the above requirement (II) is preferably 0.7×10 5 cm 2 / cm 3 or more, more preferably 0.8×10 5 cm 2 / cm 3 or more, still more preferably 1.2×10 5 cm 2 / cm 3 or more, even more preferably 1.5×10 5 cm 2 / cm 3 or more, still even more preferably 1.8×10 5 cm 2 / cm 3 or more, even more preferably 2.0×10 5 cm 2 / cm 3 or more. Incidentally, the specific surface area is usually 1.0×10 6 cm 2 / cm 3 or less.

[0021] In this specification, the values defined in the above requirement (I), and further the above requirement (II), are values measured by the method described in the examples described later. Also, the values defined in the above requirement (I), and further the above requirement (II), can be adjusted mainly by the production conditions of the urea-based thickener (B). Hereinafter, while paying attention to the specific means for satisfying the above requirement (I), and further the above requirement (II), the details of each component contained in the grease composition of the present invention will be described.

[0022] <Base oil (A)> The base oil (A) contained in the grease composition of the present invention can be any base oil that has been conventionally used as a lubricating oil base oil, and examples include one or more selected from mineral oil and synthetic oil.

[0023] Examples of mineral oils include distillates obtained by atmospheric or vacuum distillation of paraffinic crude oil, intermediate crude oil, or naphthenic crude oil, and refined oils obtained by refining these distillates according to conventional methods. Examples of purification methods include solvent dewaxing, hydrogenation isomerization, hydrogenation finishing, and clay treatment. Mineral oil may be used alone or in combination of two or more types.

[0024] For example, a Group II or III base oil from the API (American Petroleum Institute) base oil category can be used. In addition, GTL (Gas To Liquids) base oils obtained by isomerizing wax produced from natural gas by the Fischer-Tropsch process or the like are also suitably used.

[0025] Furthermore, as the mineral oil, for example, brightstock can be used. Bright stock refers to a high-viscosity base oil produced from the vacuum distillation residue of crude oil through a selection of processes including solvent delamination, solvent extraction, solvent dewaxing, and hydrorefining. There are no particular restrictions on the type of crude oil used to produce bright stock; examples include paraffinic crude oil and naphthenic crude oil.

[0026] In a grease composition according to one embodiment of the present invention, the mineral oil content is preferably 60% by mass or more, more preferably 70% by mass or more, even more preferably 80% by mass or more, and even more preferably 90% by mass or more, based on the total amount (100% by mass) of the base oil (A). Also, it is usually 100% by mass or less, preferably less than 100% by mass, more preferably 99% by mass or less, and even more preferably 98% by mass or less.

[0027] Examples of synthetic oils include hydrocarbon oils, aromatic oils, ester oils, ether oils, and synthetic oils obtained by isomerizing waxes (GTL waxes) produced by the Fischer-Tropsch process, etc. Synthetic oils may be used individually or in combination of two or more types.

[0028] Examples of hydrocarbon oils include normal paraffins, isoparaffins, polybutenes, polyisobutylenes, 1-decene oligomers, poly-α-olefins (PAOs) such as 1-decene and ethylene co-oligomers, and their hydrogenated products.

[0029] Examples of aromatic oils include alkylbenzenes such as monoalkylbenzenes and dialkylbenzenes; alkylnaphthalenes such as monoalkylnaphthalenes, dialkylnaphthalenes, and polyalkylnaphthalenes; and so on.

[0030] Examples of ester oils include diester oils such as dibutyl sebacate, di-2-ethylhexyl sebacate, dioctyl adipate, diisodecyl adipate, ditridecyl adipate, ditridecyl glutarate, and methylacetyl ricinolate; aromatic ester oils such as trioctyl trimellitate, tridecyl trimellitate, and tetraoctyl pyromelitate; polyol ester oils such as trimethylolpropane caprylate, trimethylolpropane veralgonate, pentaerythritol-2-ethylhexanoate, and pentaerythritol veralgonate; and complex ester oils such as oligoesters of polyhydric alcohols and mixed fatty acids of dibasic and monobasic acids.

[0031] Examples of ether-based oils include polyglycols such as polyethylene glycol, polypropylene glycol, polyethylene glycol monoether, and polypropylene glycol monoether; and phenyl ether-based oils such as monoalkyltriphenyl ether, alkyldiphenyl ether, dialkyldiphenyl ether, pentaphenyl ether, tetraphenyl ether, monoalkyltetraphenyl ether, and dialkyltetraphenyl ether.

[0032] The base oil (A) of this embodiment preferably has a kinematic viscosity of 10 mm at 40°C. 2 / s or more, more preferably 25mm 2 / s or more, more preferably 40mm 2 The kinematic viscosity of the base oil (A) at 40°C is 40 mm². 2 When the value is 1 / s or higher, the effects of the present invention can be more easily achieved. Furthermore, the base oil (A) of this embodiment preferably has a kinematic viscosity of 415 mmHg at 40°C. 2 / s or less, more preferably 300mm 2 / s or less, more preferably 200 mm 2 / s or less, more preferably 100 mm 2 / s or less, and more preferably 80 mm 2 It is less than / s. The kinematic viscosity of base oil (A) at 40°C is 80 mmHg. 2 When the value is less than or equal to / s, the effects of the present invention can be more easily realized. The upper and lower limits of these numerical ranges can be combined in any way. Specifically, preferably 10 to 300 mm. 2 / s, more preferably 25-200mm 2 / s, more preferably 40-100mm 2 It is / s. In one aspect of the present invention, the base oil (A) used may be a mixed base oil obtained by combining a high-viscosity base oil and a low-viscosity base oil to adjust the kinematic viscosity to the above range.

[0033] The base oil (A) of this embodiment has a kinematic viscosity at 100°C of preferably 1.0 to 50.0 mm, from the viewpoint of making it easier to exhibit the effects of the present invention. 2 / s, more preferably 5.0~20.0mm 2 It is / s.

[0034] The viscosity index of the base oil (A) used in one aspect of the present invention is preferably 90 or higher, more preferably 110 or higher, and even more preferably 130 or higher. In this specification, kinematic viscosity and viscosity index refer to values ​​measured or calculated in accordance with JIS K2283:2000.

[0035] In a grease composition according to one aspect of the present invention, the content of base oil (A) is preferably 50% by mass or more, more preferably 55% by mass or more, even more preferably 60% by mass or more, even more preferably 62% by mass or more, based on the total amount (100% by mass) of the grease composition, and also preferably 98.5% by mass or less, more preferably 97% by mass or less, even more preferably 95% by mass or less, even more preferably 93% by mass or less, even more preferably 92% by mass or less, even more preferably 90% by mass or less, and even more preferably 85% by mass or less.

[0036] <Urea-based thickener (B)> The urea-based thickener (B) contained in the grease composition of the present invention may be any compound having a urea bond, but a diurea compound having two urea bonds is preferred, and a diurea compound represented by the following general formula (b1) is more preferred. R 1 -NHCONH-R 3 -NHCONH-R 2 (b1) In one embodiment of the present invention, the urea-based thickener (B) may consist of one type or a mixture of two or more types.

[0037] In the above general formula (b1), R 1 and R 2 Each of these independently represents a monovalent hydrocarbon group having 6 to 24 carbon atoms.1 and R 2 They may be the same or they may be different from each other. 3 This represents a divalent aromatic hydrocarbon group having 6 to 18 carbon atoms.

[0038] In the above general formula (b1) R 1 and R 2 The number of carbon atoms in the monovalent hydrocarbon group that can be selected is 6 to 24, but preferably 6 to 20, and more preferably 6 to 18. Also, R 1 and R 2 Examples of monovalent hydrocarbon groups that can be selected include saturated or unsaturated monovalent chain hydrocarbon groups, saturated or unsaturated monovalent alicyclic hydrocarbon groups, and monovalent aromatic hydrocarbon groups.

[0039] Here, in the general formula (b1) above, R 1 and R 2 In the above, when the content of chain hydrocarbon groups is X molar equivalents, the content of alicyclic hydrocarbon groups is Y molar equivalents, and the content of aromatic hydrocarbon groups is Z molar equivalents, it is preferable that the following requirements (a) and (b) are met. Requirement (a): The value of [(X+Y) / (X+Y+Z)] × 100 is 90 or greater (preferably 95 or greater, more preferably 98 or greater, and even more preferably 100). Requirement (b): The X / Y ratio is 0 / 100 (X=0, Y=100) to 100 / 0 (X=100, Y=0) (preferably 10 / 90 to 90 / 10, more preferably 20 / 80 to 80 / 20, and even more preferably 40 / 60 to 80 / 20). Furthermore, the alicyclic hydrocarbon group, the chain hydrocarbon group, and the aromatic hydrocarbon group are R in the general formula (b1) above. 1 and R 2 Since it is a group selected as such, the sum of the values ​​of X, Y, and Z is 2 molar equivalents per mole of the compound represented by the general formula (b1) above. Furthermore, the values ​​of requirements (a) and (b) above represent the average value of the total amount of the compound group represented by the general formula (b1) above contained in the grease composition. By using a compound represented by the general formula (b1) above that satisfies the above requirements (a) and (b), it is easy to obtain a grease composition with excellent low-temperature properties. The values ​​of X, Y, and Z can be calculated from the molar equivalents of each amine used as a raw material.

[0040] Examples of monovalent saturated hydrocarbon groups include linear or branched alkyl groups having 6 to 24 carbon atoms. Specifically, these include hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, octadecenyl, nonadecyl, and eicosyl groups. Examples of monovalent unsaturated chain hydrocarbon groups include straight-chain or branched alkenyl groups having 6 to 24 carbon atoms. Specifically, these include hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl, dodecenyl, tridecenyl, tetradecenyl, pentadecenyl, hexadecenyl, heptadecenyl, octadecenyl, nonadecenyl, icocenyl, oleyl, geranyl, farnesyl, and linoleyl groups. Furthermore, the monovalent saturated-chain hydrocarbon group and the monovalent unsaturated-chain hydrocarbon group may be linear or branched.

[0041] Examples of monovalent saturated alicyclic hydrocarbon groups include cycloalkyl groups such as cyclohexyl, cycloheptyl, cyclooctyl, and cyclononyl groups; and cycloalkyl groups substituted with C1-C6 alkyl groups such as methylcyclohexyl, dimethylcyclohexyl, ethylcyclohexyl, diethylcyclohexyl, propylcyclohexyl, isopropylcyclohexyl, 1-methylpropylcyclohexyl, butylcyclohexyl, pentylcyclohexyl, pentyl-methylcyclohexyl, and hexylcyclohexyl groups (preferably cyclohexyl groups substituted with C1-C6 alkyl groups).

[0042] Examples of monovalent unsaturated alicyclic hydrocarbon groups include cycloalkenyl groups such as cyclohexenyl, cycloheptenyl, and cyclooctenyl groups; and cycloalkenyl groups substituted with C1-C6 alkyl groups such as methylcyclohexenyl, dimethylcyclohexenyl, ethylcyclohexenyl, diethylcyclohexenyl, and propylcyclohexenyl groups (preferably cyclohexenyl groups substituted with C1-C6 alkyl groups).

[0043] Examples of monovalent aromatic hydrocarbon groups include phenyl, biphenyl, terphenyl, naphthyl, diphenylmethyl, diphenylethyl, diphenylpropyl, methylphenyl, dimethylphenyl, ethylphenyl, and propylphenyl groups.

[0044] In the above general formula (b1) R 3 The number of carbon atoms in the divalent aromatic hydrocarbon group that can be selected is 6 to 18, preferably 6 to 15, and more preferably 6 to 13. R 3 Examples of divalent aromatic hydrocarbon groups that can be selected include phenylene group, diphenylmethylene group, diphenylethylene group, diphenylpropylene group, methylphenylene group, dimethylphenylene group, and ethylphenylene group. Among these, phenylene groups, diphenylmethylene groups, diphenylethylene groups, or diphenylpropylene groups are preferred, with diphenylmethylene groups being more preferred.

[0045] In a grease composition according to one embodiment of the present invention, the content of component (B) is preferably 0.5% by mass or more, more preferably 0.6% by mass or more, even more preferably 0.7% by mass or more, even more preferably 0.8% by mass or more, and still more preferably 1.0% by mass or more, based on the total amount (100% by mass) of the grease composition. Furthermore, the content of component (B) is preferably 15.0% by mass or less, more preferably 13.0% by mass or less, even more preferably 10.0% by mass or less, even more preferably 8.0% by mass or less, and still still preferably 6.0% by mass or less, based on the total amount (100% by mass) of the grease composition. If the content of component (B) is within the above range, it is easy to adjust the consistency of the resulting grease composition to an appropriate range. On the other hand, if the content of component (B) is 20.0% by mass or less, it will liquefy more easily when heated (in other words, its fluidity will increase more easily), resulting in a grease composition that is easy to handle when immersing equipment and filling the equipment with the grease composition.

[0046] <Method for producing urea-based thickener (B)> Urea-based thickeners (B) can usually be obtained by reacting an isocyanate compound with a monoamine. This reaction is preferably carried out by adding a solution β, in which a monoamine is dissolved in the base oil (A), to a heated solution α obtained by dissolving the isocyanate compound in the base oil (A) as described above. For example, when synthesizing the compound represented by the general formula (b1), the isocyanate compound is R in the general formula (b1). 3 A diisocyanate having a group corresponding to the divalent aromatic hydrocarbon group shown is used, and as the monoamine, R 1 and R 2 Using an amine having a group corresponding to the monovalent hydrocarbon group shown, the desired urea-based thickener (B) can be synthesized by the above method.

[0047] Furthermore, in order to satisfy the above requirement (I), and moreover, the above requirement (II), it is preferable to manufacture a grease composition containing component (A) and component (B) using a grease manufacturing apparatus as shown in [1] below, from the viewpoint of micronizing the urea-based thickener (B) in the grease composition. [1] A container body having an introduction section into which grease raw material is introduced, and a discharge section for discharging grease to the outside, The container body comprises a rotor having a rotation axis in the axial direction of the inner circumference of the container body and rotatably mounted inside the container body, The rotor is, (i) Along the surface of the rotor, irregularities are provided alternately, and the irregularities are inclined with respect to the rotation axis, (ii) Having the ability to feed from the introduction section toward the discharge section A grease manufacturing apparatus equipped with a first uneven surface.

[0048] The grease manufacturing apparatus described in [1] above will be explained below, but unless otherwise specified, the "preferred" provisions described below refer to embodiments from the viewpoint of micronizing the urea-based thickener (B) in the grease composition in order to satisfy requirement (I) above, and furthermore, requirement (II) above.

[0049] Figure 1 is a schematic cross-sectional view of the grease manufacturing apparatus described in [1] above, which may be used in one aspect of the present invention. The grease manufacturing apparatus 1 shown in Figure 1 comprises a container body 2 into which grease raw materials are introduced, and a rotor 3 having a rotating shaft 12 on the central axis of the inner circumference of the container body 2, and rotating about the rotating shaft 12 as its central axis. The rotor 3 rotates at high speed around the rotating shaft 12, applying a high shear force to the grease raw material inside the container body 2. This produces grease containing a urea-based thickener (B). The container body 2 is preferably divided into an inlet section 4, a retention section 5, a first inner circumferential surface 6, a second inner circumferential surface 7, and a discharge section 8, in that order from the upstream side, as shown in Figure 1. The container body 2 preferably has a frustoconical inner surface, as shown in Figure 1, where the inner diameter gradually widens from the inlet 4 towards the discharge 8. The inlet section 4, which forms one end of the container body 2, is equipped with a plurality of solution inlet tubes 4A and 4B for introducing grease raw material from outside the container body 2.

[0050] The retention section 5 is located downstream of the introduction section 4 and is a space for temporarily retaining the grease raw material introduced from the introduction section 4. If the grease raw material remains in this retention section 5 for a long time, the grease adhering to the inner surface of the retention section 5 will form large clumps, so it is preferable to transport it to the first inner surface 6 downstream as quickly as possible. More preferably, it is preferable to transport it directly to the first inner surface 6 without passing through the retention section 5. The first inner surface 6 is located downstream of the retention area 5, and the second inner surface 7 is located downstream of the first inner surface 6. As will be described in more detail later, it is preferable to provide the first uneven surface 9 on the first inner surface 6 and the second uneven surface 10 on the second inner surface 7 in order to make the first inner surface 6 and the second inner surface 7 function as high-shear sections that impart high shear force to the grease raw material or grease. The discharge section 8, which is the other end of the container body 2, is the part that discharges the grease that has been agitated on the first inner surface 6 and the second inner surface 7, and is equipped with a discharge port 11 for discharging the grease. The discharge port 11 is formed in a direction perpendicular to or approximately perpendicular to the rotation axis 12. As a result, the grease is discharged from the discharge port 11 in a direction perpendicular to or approximately perpendicular to the rotation axis 12. However, the discharge port 11 does not necessarily have to be perpendicular to the rotation axis 12, and may be formed in a direction parallel to or approximately parallel to the rotation axis 12.

[0051] The rotor 3 is rotatably mounted on the central axis of the frustoconical inner surface of the container body 2, with the rotation axis 12 being the axis of rotation, and rotates counterclockwise when the container body 2 is viewed from upstream to downstream, as shown in Figure 1. The rotor 3 has an outer surface that expands in accordance with the expansion of the inner diameter of the frustum of the container body 2, and a constant distance is maintained between the outer surface of the rotor 3 and the inner surface of the frustum of the container body 2. The outer circumferential surface of the rotor 3 is provided with a first uneven portion 13 of the rotor, which has alternating irregularities arranged along the surface of the rotor 3.

[0052] The first protrusions 13 of the rotor are inclined with respect to the rotation axis 12 of the rotor 3 in the direction from the inlet 4 to the discharge 8, and have the ability to feed in the direction from the inlet 4 to the discharge 8. That is, the first protrusions 13 of the rotor are inclined in a direction that pushes the solution downstream when the rotor 3 rotates in the direction shown in Figure 1.

[0053] The difference in height between the recess 13A and the protrusion 13B of the first uneven portion 13 of the rotor is preferably 0.3 to 30, more preferably 0.5 to 15, and even more preferably 2 to 7, when the diameter of the recess 13A on the outer surface of the rotor 3 is 100. The number of protrusions 13B of the first concave portion 13 of the rotor in the circumferential direction is preferably 2 to 1000, more preferably 6 to 500, and even more preferably 12 to 200.

[0054] The ratio of the width of the protrusion 13B to the width of the recess 13A of the first uneven portion 13 of the rotor [width of protrusion / width of recess] in a cross section perpendicular to the rotation axis 12 of the rotor 3 is preferably 0.01 to 100, more preferably 0.1 to 10, and even more preferably 0.5 to 2. The inclination angle of the first grooved portion 13 of the rotor with respect to the rotating shaft 12 is preferably 2 to 85 degrees, more preferably 3 to 45 degrees, and even more preferably 5 to 20 degrees.

[0055] Preferably, the first inner circumferential surface 6 of the container body 2 is provided with a first uneven portion 9, which has multiple irregularities formed along the inner circumferential surface. Furthermore, it is preferable that the protrusions of the first protrusions 9 on the container body 2 side are inclined in the opposite direction to the first protrusions 13 of the rotor. In other words, it is preferable that the multiple protrusions of the first protrusion portion 9 on the container body 2 side are inclined in a direction that pushes the solution downstream when the rotation axis 12 of the rotor 3 rotates in the direction shown in Figure 1. The stirring capacity and discharge capacity are further enhanced by the first protrusion portion 9 having multiple protrusions on the first inner circumferential surface 6 of the container body 2.

[0056] The depth of the first uneven portion 9 on the container body 2 side is preferably 0.2 to 30, more preferably 0.5 to 15, and even more preferably 1 to 5, when the inner diameter (diameter) of the container is 100. The number of protrusions on the first protrusion portion 9 on the container body 2 side is preferably 2 to 1000, more preferably 6 to 500, and even more preferably 12 to 200.

[0057] The ratio of the width of the recesses in the first uneven portion 9 on the container body 2 side to the width of the protrusions between the grooves [width of recesses / width of protrusions] is preferably 0.01 to 100, more preferably 0.1 to 10, and even more preferably 0.5 to 2 or less. The inclination angle of the first uneven portion 9 on the container body 2 side with respect to the rotation axis 12 is preferably 2 to 85 degrees, more preferably 3 to 45 degrees, and even more preferably 5 to 20 degrees. Furthermore, by providing the first uneven portion 9 on the first inner circumferential surface 6 of the container body 2, the first inner circumferential surface 6 can be made to function as a shearing portion that imparts high shear force to the grease raw material or grease; however, the first uneven portion 9 is not necessarily required.

[0058] It is preferable that a second rotor surface 14, which has alternating grooves and protrusions, is provided on the outer circumferential surface of the rotor downstream of the first grooved portion 13, along the surface of the rotor 3. The second uneven portion 14 of the rotor is inclined with respect to the rotation axis 12 of the rotor 3 and has the ability to suppress the flow of the solution, pushing it back to the upstream side from the inlet portion 4 towards the discharge portion 8.

[0059] The step size of the second uneven portion 14 of the rotor is preferably 0.3 to 30, more preferably 0.5 to 15, and even more preferably 2 to 7, when the diameter of the recess on the outer surface of the rotor 3 is taken as 100. The number of protrusions in the second uneven portion 14 of the rotor in the circumferential direction is preferably 2 to 1000, more preferably 6 to 500, and even more preferably 12 to 200.

[0060] The ratio of the width of the protrusions to the width of the recesses [width of protrusions / width of recesses] of the second uneven portion 14 of the rotor in a cross section perpendicular to the rotation axis of the rotor 3 is preferably 0.01 to 100, more preferably 0.1 to 10, and even more preferably 0.5 to 2. The inclination angle of the second grooved portion 14 of the rotor with respect to the rotating shaft 12 is preferably 2 to 85 degrees, more preferably 3 to 45 degrees, and even more preferably 5 to 20 degrees.

[0061] Preferably, the second inner circumferential surface 7 of the container body 2 is provided with a second uneven portion 10, which has multiple uneven surfaces formed adjacent to the downstream portion of the unevenness in the first uneven portion 9 on the container body 2 side. Preferably, multiple irregularities are formed on the inner circumferential surface of the container body 2, and each irregularity is inclined in the opposite direction to the inclination direction of the second irregular portion 14 of the rotor. In other words, it is preferable that the multiple irregularities of the second irregularity portion 10 on the container body 2 side are inclined in a direction that pushes the solution back upstream when the rotation axis 12 of the rotor 3 rotates in the direction shown in Figure 1. The irregularities of the second irregularity portion 10 provided on the second inner circumferential surface 7 of the container body 2 further enhance the stirring capacity. In addition, the second inner circumferential surface 7 of the container body can function as a shearing section that imparts a high shear force to the grease raw material or grease.

[0062] The depth of the recess in the second uneven portion 10 on the container body 2 side is preferably 0.2 to 30, more preferably 0.5 to 15, and even more preferably 1 to 5, when the inner diameter (diameter) of the container body 2 is 100. The number of recesses in the second uneven portion 10 on the container body 2 side is preferably 2 to 1000, more preferably 6 to 500, and even more preferably 12 to 200.

[0063] The ratio of the width of the protrusions to the width of the recesses [width of protrusions / width of recesses] of the second uneven portion 10 on the container body 2 side in a cross section perpendicular to the rotation axis 12 of the rotor 3 is preferably 0.01 to 100, more preferably 0.1 to 10, and even more preferably 0.5 to 2 or less. The inclination angle of the second recessed portion 10 on the container body 2 side with respect to the rotation axis 12 is preferably 2 to 85 degrees, more preferably 3 to 45 degrees, and even more preferably 5 to 20 degrees. The ratio of the length of the first protrusion 9 on the container body 2 side to the length of the second protrusion 10 on the container body 2 side [length of the first protrusion / length of the second protrusion] is preferably 2 / 1 to 20 / 1.

[0064] Figure 2 is a cross-sectional view of the first uneven portion 9 on the container body 2 side of the grease manufacturing apparatus 1, in a direction perpendicular to the rotation axis 12. As shown in Figure 2, the first uneven portion 13 of the rotor is provided with multiple scrapers 15 whose tips protrude further toward the inner circumferential surface of the container body 2 than the tip of the protrusion 13B of the first uneven portion 13. Although not shown in the figure, the second uneven portion 14 is also provided with multiple scrapers, similar to the first uneven portion 13, whose tips protrude toward the inner circumferential surface of the container body 2. The scraper 15 scrapes off the grease adhering to the inner circumferential surface of the first uneven portion 9 and the second uneven portion 10 on the container body 2. The amount of protrusion of the tip of the scraper 15 relative to the amount of protrusion of the convex portion 13B of the first concave portion 13 of the rotor is preferably such that the ratio [R2 / R1] of the radius of the tip of the scraper 15 (R2) to the radius of the tip of the convex portion 13B (R1) is greater than 1.005 and less than 2.0.

[0065] The number of scrapers 15 is preferably 2 to 500, more preferably 2 to 50, and even more preferably 2 to 10. In the grease manufacturing apparatus 1 shown in Figure 1, a scraper 15 is provided, but the apparatus may not have a scraper 15, or it may have a scraper 15 provided intermittently.

[0066] To produce grease containing a urea-based thickener (B) using the grease manufacturing apparatus 1, the aforementioned grease raw materials, solution α and solution β, are introduced from the solution introduction pipes 4A and 4B of the introduction section 4 of the container body 2, respectively, and the rotor 3 is rotated at high speed, thereby producing a grease base material containing a urea-based thickener (B). Furthermore, even when an oil curing agent (C) and an additive (D) are blended into the grease base material obtained in this manner, the urea-based thickener (B) in the grease composition can be micronized to satisfy requirement (I) and even requirement (II) above.

[0067] As a condition for high-speed rotation of the rotor 3, the shear rate applied to the grease raw material is preferably 10 2 s -1 The above is more comfortable 10 3 s -1 More preferably 10 4 s -1 That's all, and also, usually 10 7 s -1 The following applies:

[0068] Furthermore, the ratio (Max / Min) of the maximum shear rate (Max) to the minimum shear rate (Min) during high-speed rotation of the rotor 3 is preferably 100 or less, more preferably 50 or less, and even more preferably 10 or less. By ensuring that the shear rate is as uniform as possible with respect to the mixture, the urea-based thickener (B) and its precursors in the grease composition can be more easily refined, resulting in a more uniform grease structure.

[0069] Here, the maximum shear rate (Max) is the highest shear rate applied to the mixture, and the minimum shear rate (Min) is the lowest shear rate applied to the mixture, and are defined as follows. • Maximum shear rate (Max) = (Linear velocity at the tip of the protrusion 13B of the first protrusion 13 of the rotor) / (Gap A1 between the tip of the protrusion 13B of the first protrusion 13 of the rotor and the protrusion 9 of the first protrusion 9 of the first inner surface 6 of the container body 2) * Minimum shear rate (Min) = (linear velocity of the recess 13A of the first protrusion 13 of the rotor) / (gap A2 between the recess 13A of the first protrusion 13 of the rotor and the recess of the first protrusion 9 of the first inner surface 6 of the container body 2) Gap A1 and Gap A2 are as shown in Figure 2.

[0070] Because the grease manufacturing apparatus 1 is equipped with a scraper 15, grease adhering to the inner surface of the container body 2 can be scraped off, preventing lumps from forming during mixing, and enabling the continuous production of finely textured grease containing urea-based thickener (B) in a short time. Furthermore, the scraper 15 scrapes off the adhering grease, preventing the stagnant grease from becoming resistance to the rotation of the rotor 3. This reduces the rotational torque of the rotor 3, thereby reducing the power consumption of the drive source and enabling efficient continuous production of grease.

[0071] Since the inner circumferential surface of the container body 2 is frustoconical in shape, with the inner diameter increasing from the inlet 4 to the discharge 8, centrifugal force has the effect of discharging grease or grease raw material downstream, reducing the rotational torque of the rotor 3 and enabling continuous production of grease. The rotor 3 has a first uneven portion 13 on its outer circumferential surface, and the first uneven portion 13 is inclined with respect to the rotation axis 12 of the rotor 3, providing a feeding capability from the introduction portion 4 to the discharge portion 8. The second uneven portion 14 of the rotor is also inclined with respect to the rotation axis 12 of the rotor 3, providing a feeding suppression capability from the introduction portion 4 to the discharge portion 8. As a result, a high shear force can be imparted to the solution, and even after the additive is blended, the urea-based thickener (B) in the grease composition can be micronized to satisfy requirement (I) and further requirement (II) above.

[0072] A first uneven portion 9 is formed on the first inner circumferential surface 6 of the container body 2, and since it is inclined in the opposite direction to the first uneven portion 13 of the rotor, in addition to the effect of the first uneven portion 13 of the rotor, it is possible to further sufficiently stir the grease raw material while pushing the grease or grease raw material downstream, and even after the additive is blended, the urea-based thickener (B) in the grease composition can be made finer so as to satisfy the above requirement (I) and further requirement (II). Furthermore, since a second uneven portion 10 is provided on the second inner circumferential surface 7 of the container body 2, and a second uneven portion 14 is provided on the outer circumferential surface of the rotor 3, it is possible to prevent the grease raw material from flowing out of the first inner circumferential surface 6 of the container body more than necessary. This imparts a high shear force to the solution, highly dispersing the grease raw material, and even after the additive is blended, the urea-based thickener (B) can be finely milled to satisfy the above requirement (I), and furthermore, requirement (II).

[0073] <Oil hardening agent (C)> The grease composition of the present invention comprises a grease hardener (C) along with components (A) and (B). The grease composition of the present invention, by containing an oil hardening agent (C), can be made into a grease composition that is solid at room temperature and becomes liquid when heated. Furthermore, its ability to fill (adhere to) equipment can be improved. In the present invention, the oil hardening agent is a substance that, when added to and dissolved in liquid oil, can thicken, solidify, and / or sol-gelify the oil at room temperature, and has the property of solidifying the grease composition at room temperature. Furthermore, "liquefaction" refers to a state in which the viscosity at 70°C is approximately 5,000 mPa·s or less.

[0074] Examples of oil hardening agents (C) include glycerin fatty acid esters (C1), amino acid-based oil gelling agents (C2), amine-based hardening agents (C3), and sorbitol-based hardening agents (C4). These may be used individually or in combination of two or more. Among these, it is preferable to use glycerin fatty acid ester (C1) from the viewpoint of the effects of the present invention and ease of availability.

[0075] -Glycerin fatty acid ester (C1)- Examples of glycerol fatty acid esters (C1) include glycerol fatty acid esters and polyglycerol fatty acid esters.

[0076] Polyglycerol fatty acid esters contain fatty acids and polyglycerol as constituent components. Regarding the fatty acids that make up polyglycerol fatty acid esters (hereinafter referred to as "constituent fatty acids"), it is preferable that straight-chain fatty acids with 16 to 18 carbon atoms account for 45% or more of the total constituent fatty acids in terms of molecular weight.

[0077] For the polyglycerin constituting the polyglycerin fatty acid ester, it is preferable to use one with an average degree of polymerization of 10 or more based on its hydroxyl value. More preferably, the average degree of polymerization of the polyglycerin is 20 or more, even more preferably 30 or more, and even more preferably 40 or more.

[0078] The average degree of polymerization of polyglycerin, based on its hydroxyl value, is calculated using end-group analysis. The hydroxyl value used to calculate the average degree of polymerization using end-group analysis can be calculated in accordance with the "Standard Test Methods for Analysis of Fats and Oils (I), 1996 Edition," compiled by the Japan Oil Chemists' Society.

[0079] The esterification rate of the polyglycerol fatty acid ester is preferably 70% or higher. More preferably, the esterification rate of the polyglycerol fatty acid ester is 80% or higher, and even more preferably 90% or higher.

[0080] The esterification rate is calculated using the average degree of polymerization (n) of polyglycerin, determined from the hydroxyl value by end-group analysis, the number of hydroxyl groups in this polyglycerin (n+2), and the number of moles of fatty acids attached to the polyglycerin (M). Esterification rate (%) = (M / (n+2)) × 100 This is the value calculated using [the formula / method].

[0081] In the present invention, polyglycerin fatty acid esters can be those produced by conventional methods, and more specifically, those produced by charging the above components in a composition that satisfies the above conditions, adding a catalyst such as sodium hydroxide, and subjecting it to an esterification reaction under normal or reduced pressure can be used. Furthermore, in the present invention, commercially available polyglycerin fatty acid esters may be used, and for example, TAISET AD (manufactured by Taiyo Kagaku Co., Ltd.), TAISET50 (manufactured by Taiyo Kagaku Co., Ltd.), Ryoto Polyglyceryl B-100D (manufactured by Mitsubishi Chemical Corporation), etc., can be suitably used.

[0082] In the grease composition of the present invention, the melting point of the oil curing agent (C) is preferably 50°C or higher, and more preferably 60°C or higher, from the viewpoint of being solid at room temperature and liquefying when heated. Furthermore, the melting point of the oil curing agent (C) is higher than room temperature, specifically, preferably 20°C or higher than room temperature, and more preferably 30°C or higher than room temperature. Furthermore, the melting point of the oil curing agent (C) is preferably 100°C or lower, and more preferably 80°C or lower. In this specification, the melting point of the oil hardening agent (C) refers to the value measured in accordance with JIS K0064.

[0083] In the grease composition of the present invention, the content of the oil curing agent (C) is preferably 0.1 to 10.0% by mass, more preferably 0.5 to 8.0% by mass, and even more preferably 1.0 to 6.0% by mass, based on the total amount (100% by mass) of the grease composition, from the viewpoint of having a solid state at room temperature and becoming liquid when heated.

[0084] The ratio of urea-based thickener (B) to oil hardening agent (C) [(B) / (C)] is preferably 0.3 to 10, more preferably 0.4 to 5, and even more preferably 0.5 to 3 by mass, from the viewpoint of ensuring that the mixture is solid at room temperature, liquefies when heated, and softens when shear stress is applied.

[0085] <Additive (D)> A grease composition according to one aspect of the present invention may contain additives (D) other than components (B) and (C) that are commonly used in greases, as long as the effects of the present invention are not impaired. Examples of additives (D) include extreme pressure agents, antioxidants, rust inhibitors, dispersants, and metal deactivators. Each additive (D) may be used individually or in combination of two or more.

[0086] Examples of extreme pressure additives include one or more selected from organometallic extreme pressure additives, sulfur-based extreme pressure additives, phosphorus-based extreme pressure additives, and sulfur-phosphorus-based extreme pressure additives.

[0087] As organometallic extreme pressure additives, one or more can be selected from, for example, organomolybdenum compounds such as molybdenum dialkyldithiocarbamate (MoDTC) and molybdenum dialkyldithiophosphate (MoDTP), and organozinc compounds such as zinc dialkyldithiocarbamate (ZnDTC) and zinc dialkyldithiophosphate (ZnDTP).

[0088] As sulfur-based extreme pressure agents, one or more selected from, for example, sulfurized oils and fats, sulfurized fatty acids, sulfurized esters, sulfurized olefins, monosulfides, polysulfides, dihydrocarbyl polysulfides, thiadiazole compounds, alkylthiocarbamoyl compounds, thiocarbamate compounds, thioterpene compounds, and dialkylthiodipropionate compounds can be used.

[0089] Examples of phosphorus-based extreme pressure agents include phosphate esters such as aryl phosphates, alkyl phosphates, alkenyl phosphates, and alkylaryl phosphates; acidic phosphate esters such as monoaryl acid phosphates, diaryl acid phosphates, monoalkyl acid phosphates, dialkyl acid phosphates, monoalkenyl acid phosphates, and diaryl acid phosphates; phosphate esters such as aryl hydrogen phosphates, alkyl hydrogen phosphates, aryl phosphates, alkyl phosphates, alkenyl phosphates, and arylalkyl phosphates; acidic phosphate esters such as monoalkyl acid phosphates, dialkyl acid phosphates, monoalkenyl acid phosphates, and diaryl acid phosphates; and one or more selected from the amine salts thereof.

[0090] As sulfur-phosphorus extreme pressure agents, for example, one or more selected from monoalkylthiophosphates, dialkyldithiophosphates, trialkyltrithiophosphates, and their amine salts, as well as zinc dialkyldithiophosphate (Zn-DTP), can be used.

[0091] Examples of antioxidants include amine-based antioxidants such as diphenylamine compounds and naphthylamine compounds, and phenol-based antioxidants such as monocyclic phenol compounds and polycyclic phenol compounds. Examples of rust inhibitors include carboxylic acid-based rust inhibitors such as alkenyl succinic acid polyhydric alcohol esters, zinc stearate, thiadiazole and its derivatives, and benzotriazole and its derivatives. Examples of dispersants include ashless dispersants such as succinimide and boron-based succinimide. Examples of metal deactivators include benzotriazole compounds.

[0092] In a grease composition according to one aspect of the present invention, the content of additive (D) is appropriately set according to the type of additive, but each is independently typically 0.01 to 20% by mass, preferably 0.01 to 15% by mass, more preferably 0.01 to 10% by mass, and even more preferably 0.01 to 7% by mass, based on the total amount (100% by mass) of the grease composition.

[0093] <Physical properties of the grease composition> (Consistency of non-mixing) The immiscibility consistency of a grease composition according to one embodiment of the present invention at 25°C is preferably 220 to 430, more preferably 240 to 360, even more preferably 250 to 350, and even more preferably 255 to 330, from the viewpoint of handling at room temperature. In this specification, the impurity consistency of the grease composition refers to the value measured at 25°C in accordance with JIS K2220:2013 (Clause 7).

[0094] (Consistency of mixing) The consistency of the grease composition according to one embodiment of the present invention at 25°C is preferably 220 or higher, more preferably 250 or higher, even more preferably 300 or higher, even more preferably 330 or higher, preferably 500 or lower, more preferably 450 or lower, even more preferably 440 or lower, and even more preferably 430 or lower, from the viewpoint of softening when shear stress is applied. In this specification, the consistency of the grease composition refers to the value measured at 25°C in accordance with JIS K2220:2013 (Clause 7).

[0095] (Difference between miscible and improper consistency) In one embodiment of the present invention, the difference obtained by subtracting the value of the unmixed consistency from the value of the mixed consistency of the grease composition at 25°C is preferably 10 to 150, more preferably 30 to 130, even more preferably 40 to 120, and even more preferably 50 to 110, from the viewpoint of fluidity due to softening when shear stress is applied. The larger the difference between the value of the mixed consistency and the value of the unmixed consistency, the more the grease composition is sheared and softened by mixing.

[0096] (dropping point) The dropping point of a grease composition according to one embodiment of the present invention is preferably 50 to 300, more preferably 120 to 280, even more preferably 150 to 270, even more preferably 180 to 260, and still more preferably 190 to 250, from the viewpoint of grease fluidity. In this specification, the dropping point of a grease composition refers to the value measured in accordance with JIS K2220:2013 (Clause 8).

[0097] (Solid at room temperature, becomes liquefied when heated) In one embodiment of the present invention, a grease composition can be confirmed to be solid at room temperature and to become liquefied when heated by the method described in the examples below.

[0098] (Rheological properties) A grease composition according to one aspect of the present invention, when measured by the method described in the examples below, the strain is 1 × 10 -3 %~1×10 3 By measuring the storage modulus of elasticity with respect to strain within a percentage range and determining the absolute value of the maximum slope when the storage modulus of elasticity decreases, the rheological properties (in this invention, the property of becoming soft and fluid under shear) can be evaluated. The larger the absolute value of this slope, the higher the responsiveness to strain (shear stress), and the more easily the grease composition softens when shear stress is applied.

[0099] <Method for producing grease composition> The grease composition of the present invention can be produced by mixing a base oil (A), a grease containing a urea-based thickener (B), an oil hardening agent (C), and an additive (D) as needed. For example, it can be manufactured by mixing a grease (base grease) containing a base oil (A) and a urea-based thickener (B), adding an additive (D) as needed and mixing, cooling it to about 70°C to 80°C by natural cooling, and then adding and mixing in an oil hardening agent (C).

[0100] <Applications of grease compositions> The grease composition of the present invention is solid at room temperature, liquefies when heated, and softens when shear stress is applied. Therefore, a grease composition according to one embodiment of the present invention can be used as a lubricant in lubrication parts such as bearing parts, sliding parts, gear parts, and joint parts of devices where such characteristics are required. More specifically, it is preferable to use it in hub units, electric power steering systems, drive electric motor flywheels, ball joints, wheel bearings, spline parts, constant velocity joints, clutch boosters, servo motors, blade bearings, or bearing parts of generators. Furthermore, fields in which the grease composition of the present invention can be suitably used include the automotive industry, office equipment industry, machine tool industry, wind turbine industry, construction industry, agricultural machinery industry, or industrial robot industry. Examples of lubrication parts in automotive devices that can suitably use the grease composition of the present invention include bearing parts in devices such as radiator fan motors, fan couplings, alternators, idler pulleys, hub units, water pumps, power windows, wipers, electric power steering, drive motor flywheels, ball joints, wheel bearings, spline sections, and constant velocity joints; bearing parts in devices such as door locks, door hinges, and clutch boosters; bearing parts, gear sections, and sliding parts of servo motors, blade bearings, or generators; and the like. Examples of lubrication parts in office equipment that can suitably use the grease composition of the present invention include, for example, the fixing rolls in printers and other devices, and the bearings and gear parts in polygon motors and other devices. Examples of lubrication parts in machine tool equipment that can suitably use the grease composition of the present invention include spindles, servo motors, bearing parts in reduction gears of machine robots, and the like. Examples of lubrication parts in wind turbine equipment that can suitably use the grease composition of the present invention include blade bearings and bearing parts of generators, etc. Examples of lubrication parts in devices for construction or agricultural machinery that can suitably use the grease composition of the present invention include bearing parts such as ball joints and spline sections, gear sections, and sliding parts. Furthermore, it can be suitably used in speed reducers for industrial robots and speed increasers for wind power generation equipment. Examples of such reduction gears and speed increasers include reduction gears and speed increasers consisting of gear mechanisms. However, the application of the grease composition according to one embodiment of the present invention is not limited to reduction gears and speed increasers consisting of gear mechanisms, but can also be applied to traction drives, for example. Furthermore, examples of reduction gears include RV type, harmonic type, cyclo type, etc., and the grease composition can be suitably used with any of them. Furthermore, in one aspect of the present invention, a device is provided which has the grease composition of the present invention in lubrication parts such as bearing parts, sliding parts, gear parts, and joint parts, preferably a speed reducer or speed increaser. Furthermore, in one aspect of the present invention, a lubrication method is provided for lubricating lubrication parts (for example, bearing parts, sliding parts, gear parts, joint parts, etc.) of a device such as a speed reducer or speed increaser using the grease composition of the present invention.

[0101] According to one aspect of the present invention, the following [1] to [9] are provided. [1] A grease composition containing a base oil (A), a urea-based thickener (B), and an oil hardening agent (C), A grease composition wherein the particles containing the urea-based thickener (B) in the grease composition satisfy the following requirement (I). Requirement (I): The arithmetic mean particle diameter based on area, when the particles are measured by laser diffraction / scattering, is 2.0 μm or less. [2] The grease composition according to [1], wherein the particles containing the urea-based thickener (B) in the grease composition further satisfy the following requirement (II). Requirement (II): The specific surface area of ​​the particle measured by laser diffraction and scattering is 0.5 × 10⁻⁶. 5 cm 2 / cm 3 That's all. [3] The grease composition according to [1] or [2], wherein the content of the oil hardening agent (C) is 0.1% by mass to 10% by mass on a basis of the total amount of the grease composition. [4] The grease composition according to any one of [1] to [3], wherein the melting point of the oil hardening agent (C) is 100°C or less. [5] The grease composition according to any one of [1] to [4], wherein the content of the urea-based thickener (B) is 1.0% by mass to 15.0% by mass on a basis of the total amount of the grease composition. [6] The kinematic viscosity of the base oil (A) at 40°C is 10 mm 2 / s~80mm 2 A grease composition according to any one of the above [1] to [5], wherein the value is / s. [7] A grease composition according to any one of [1] to [6], wherein the consistency of the mixture is 300 to 500. [8] A grease composition according to any one of [1] to [7] above, used for lubricating the lubrication parts of a speed reducer or speed increaser. [9] A lubrication method for lubricating a lubrication part of a speed reducer or speed increaser with a grease composition according to any one of [1] to [8] above. [Examples]

[0102] The present invention will be specifically described by the following examples, but the present invention is not limited to the following examples.

[0103] [Various physical properties] The measurement methods for various physical properties were as follows: (1) Kinematic viscosity at 40°C, kinematic viscosity at 100°C, and viscosity index of base oil (A) Measurements and calculations were performed in accordance with JIS K2283:2000. (2) Melting point of oil hardening agent (C) Measurements were taken in accordance with JIS K0064. (3) Impurity consistency of the grease composition (1 / 4) Measurements were taken at 25°C in accordance with JIS K2220:2013 (Clause 7). (4) Consistency of the grease composition (1 / 4) Measurements were taken at 25°C in accordance with JIS K2220:2013 (Clause 7). (5) Difference between the miscible and improper consistency of the grease composition The difference was calculated by subtracting the value of the unmixed consistency (3) from the value of the mixed consistency (4) above. (6) Dropping point of the grease composition Measurements were taken in accordance with JIS K2220:2013 (Clause 8).

[0104] [Raw materials] In Examples 1-2 and Comparative Examples 1-4, the base oil (A) and oil hardener (C) used as raw materials for preparing the grease composition were as follows.

[0105] <Base oil (A)> • Base oil (A1): Base oil classified as Group III in the API classification (kinematic viscosity at 40°C: 19 mm²) 2 / s, 100℃ kinematic viscosity: 4.2mm 2 / s, viscosity index: 126) • Base oil (A2): Brightstock (40°C kinematic viscosity: 409 mmHg) 2 / s, 100℃ kinematic viscosity: 30.9mm 2 / s, viscosity index: 107) <Oil hardening agent (C)> • Glycerin fatty acid ester (C1): Glycerin fatty acid ester (product name: TAISET AD, manufactured by Taiyo Kagaku Co., Ltd., melting point: 60°C)

[0106] (Example 1) (1) Synthesis of urea grease The base oil was a mixture of base oil (A1) and base oil (A2). Solution α was prepared by adding 2.47 parts by mass of diphenylmethane-4,4'-diisocyanate (MDI) to 48.00 parts by mass of base oil (A) heated to 70°C. In addition, a mixed base oil of base oil (A1) and base oil (A2) was prepared separately. Solution β was prepared by adding 1.51 parts by mass of cyclohexylamine and 1.03 parts by mass of octadecylamine (stearylamine) to 47.00 parts by mass of base oil (A) heated to 70°C. Then, using the grease manufacturing apparatus 1 shown in Figure 1, equal amounts of solution α heated to 70°C were simultaneously introduced into the container body 2 from solution introduction pipe 4A and solution β heated to 70°C from solution introduction pipe 4B. With the rotor 3 rotating, solutions α and β were continuously introduced into the container body 2. After that, the mixture was heated to 160°C using the stirring device shown in Figure 3, stirred for 1 hour, and then homogenized by roll milling to synthesize urea grease (b1). The rotational speed of the rotor 3 of the grease manufacturing device 1 used was set to 8,000 rpm. The maximum shear rate (Max) at this time was 10,500 s. -1The mixture was stirred with a ratio of the maximum shear rate (Max) to the minimum shear rate (Min) [Max / Min] of 3.5. Furthermore, the urea-based thickener (B1) contained in the obtained urea grease (b1) is R in the general formula (b1) 1 and R 2 However, it is a cyclohexyl group or an octadecyl group (stearyl group), R 3 This corresponds to a compound in which the group is a diphenylmethylene group. Furthermore, the molar ratio (cyclohexylamine / octadecylamine) of cyclohexylamine and octadecylamine used as raw materials is 80 / 20. (2) Preparation of grease composition In (1) above, the urea grease (b1) discharged from the grease manufacturing apparatus 1 shown in Figure 1 was stirred and then cooled to 70°C by natural cooling. Next, glycerin fatty acid ester (C1) was added to the urea grease (b1), which had been cooled to 70°C by natural cooling, in the amounts shown in Table 1, and mixed to obtain the grease composition of Example 1.

[0107] (Example 2, Comparative Example 1) The grease compositions for Example 2 and Comparative Example 1 were obtained in the same manner as the grease composition for Example 1, except that the amounts of the compounds were changed as shown in Table 1.

[0108] (Comparative Example 2) (1) Synthesis of urea grease The base oil was a mixture of base oil (A1) and base oil (A2). Solution α was prepared by adding 2.47 parts by mass of diphenylmethane-4,4'-diisocyanate (MDI) to 48.00 parts by mass of base oil (A) heated to 70°C. In addition, a mixed base oil of base oil (A1) and base oil (A2) was prepared separately. Solution β was prepared by adding 1.51 parts by mass of cyclohexylamine and 1.03 parts by mass of octadecylamine (stearylamine) to 47.00 parts by mass of base oil (A) heated to 70°C. Then, using the grease manufacturing apparatus 1 shown in Figure 3, solution β, heated to 70°C, was added to solution α, heated to 70°C, and the stirring blade was rotated. The temperature was raised to 160°C while stirring was continued, and the temperature was held for 1 hour to synthesize urea grease (b2). The maximum shear rate in this case is approximately 100 seconds. -1 The minimum shear rate is 1.23s. -1 Furthermore, the ratio of the maximum shear rate (Max) to the minimum shear rate (Min) (Max / Min) was approximately 81. Furthermore, the urea-based thickener (B2) contained in urea grease (b2) is R in the general formula (b1) above. 1 and R 2 However, it is a cyclohexyl group or an octadecyl group (stearyl group), R 3 This corresponds to a compound in which the group is a diphenylmethylene group. Furthermore, the molar ratio (cyclohexylamine / octadecylamine) of cyclohexylamine and octadecylamine used as raw materials is 80 / 20. (2) Preparation of grease composition In (1) above, the urea grease (b2) discharged from the grease manufacturing apparatus 1 shown in Figure 3 was stirred and then cooled to 70°C by natural cooling. Next, glycerin fatty acid ester (C1) was added to the urea grease (b2), which had been cooled to 70°C by natural cooling, in the amounts shown in Table 1, and mixed to obtain the grease composition of Comparative Example 2.

[0109] (Comparative Examples 3-4) The grease compositions of Comparative Examples 3 and 4 were obtained in the same manner as the grease composition of Comparative Example 2, except that the amounts of the compounds were changed as shown in Table 1.

[0110] [Requirements] The following calculations were performed for the urea grease synthesized in Examples 1-2 and Comparative Examples 1-4.

[0111] (1) Calculation of particle size of particles containing urea-based thickeners: Requirement (I) The particle size of the particles containing the urea-based thickener in the grease composition was evaluated. Specifically, the urea grease synthesized in Example 1 and the urea grease synthesized in Comparative Example 1 were used as measurement samples, and the particle size of the particles containing the urea-based thickener (B) was determined by the following procedure. First, after the measurement sample was degassed under vacuum, it was filled into a 1 mL syringe, and 0.10 to 0.15 mL of the sample was extruded from the syringe. The extruded sample was placed on the surface of the plate-shaped cell of the fixture for the paste cell. Next, another plate-shaped cell was placed on top of the sample to obtain a measurement cell in which the sample was sandwiched between two cells. Next, using a laser diffraction particle size analyzer (manufactured by Horiba, Ltd., trade name: LA-920), the arithmetic mean particle size based on the area of the particles in the sample of the measurement cell was measured. Here, the "arithmetic mean particle size based on the area" means a value obtained by arithmetically averaging the particle size distribution based on the area. The particle size distribution based on the area shows the frequency distribution of the particle size in the entire particles to be measured, based on the area calculated from the particle size (specifically, the cross-sectional area of the particles having the particle size). Further, the value obtained by arithmetically averaging the particle size distribution based on the area can be calculated by the following formula (1).

[0112]

Number

[0113] (2) Calculation of the specific surface area of the particles containing the urea-based thickener: Requirement (II) Using the particle size distribution of the particles containing the thickener in the grease composition measured in the column of the above requirement (I), the specific surface area was calculated. Specifically, using the particle size distribution, the total surface area (unit: cm 3 ) of the particles per unit volume (1 cm 2 ) was calculated, and this was taken as the specific surface area (unit: cm 2 / cm 3 ).

[0114] Table 1 shows the composition and physical properties of the grease composition.

[0115] [Table 1]

[0116] The grease compositions obtained in Examples 1-2 and Comparative Examples 1-4 were subjected to the following tests to confirm that they are solid at room temperature and liquefy when heated.

[0117] [Confirmation that it is solid at room temperature and becomes liquefied when heated] The grease composition of Example 1 was heated to 70°C at room temperature to liquefy it. A bearing was placed in the liquefied grease composition, and the state of filling the gaps in the bearing was visually confirmed. The state of filling was also visually confirmed after returning to room temperature, and the retention capacity of the grease composition was confirmed by inverting the bearing so that the open surface was facing downwards and determining whether or not there was any leakage. In addition, in Comparative Example 1, the filling state in the bearing gap, the filling state after returning to room temperature, and the retention performance of the grease composition were confirmed in the same manner as in Example 1.

[0118] The results of this test confirmed that the grease composition of Example 1 was solid at room temperature, liquefied when heated to 70°C, and easily filled the gaps in the bearing. Furthermore, after returning to room temperature, the grease composition solidified and was sufficiently retained in the gaps in the bearing. On the other hand, the grease composition of Comparative Example 1, which does not contain the oil hardening agent (C), remained liquefied even after being heated to 70°C and then returned to room temperature. As a result, the grease composition did not fill the gaps in the bearing, and leakage from the bearing was observed. In other words, the grease composition of Comparative Example 1, which does not contain the oil hardening agent (C), did not return to a solid state after being heated to 70°C and then returned to room temperature, thus losing its performance as a grease composition.

[0119] Next, the rheological properties were evaluated based on Examples 1-2 and Comparative Examples 1-4 described above.

[0120] [Evaluation of rheological properties] At room temperature (25°C), using the Anton-Paar MCR302 device, a strain of 1 × 10⁻⁶ was measured. -3 %~1×10 3 The storage modulus was measured within a range of %. Furthermore, the storage modulus against strain was plotted, and the maximum slope (negative number) when the storage modulus decreases was compared.

[0121] The rheometer measurement results for Examples 1-2 and Comparative Example 1 are shown in Figure 4. The rheometer measurement results for Comparative Examples 2-4 are shown in Figure 5. The rheological curves (change in storage modulus with respect to strain) of Examples 1-2 showed a larger maximum slope (negative number) when the storage modulus decreased compared to the rheological curves of Comparative Examples 1-4. In other words, the degree of decrease in the storage modulus with respect to strain (responsiveness to decrease) was high, indicating that it was more prone to becoming fluid with strain. From these results, it can be seen that the urea-based thickener (B) that satisfies requirement (I) has a high responsiveness to the application of shear stress and softens easily. Furthermore, the results shown in Comparative Example 1 revealed that urea grease without the oil hardening agent (C) could be liquefied by heating, but did not return to a solid state when returned to room temperature. However, the grease compositions of Examples 1 and 2 could be liquefied by heating and returned to a solid state when returned to room temperature. From this, it can be said that a grease composition containing a urea-based thickener (B) and an oil hardening agent (C) is a grease composition in which the urea-based thickener (B) does not inhibit the properties exhibited by the oil hardening agent (C) (the property of being able to be liquefied by heating and returning to a solid state when returned to room temperature), and moreover, it is a grease composition with excellent rheological properties (high responsiveness to the application of shear stress and easy softening). [Explanation of Symbols]

[0122] 1. Grease manufacturing equipment 2. Container body 3 rotors 4. Introduction 4A, 4B Solution introduction tube 5 Retention part 6 First uneven part 7 Second uneven part 8 Discharge part 9. First uneven portion on the container body side 10 Second uneven portion on the container body side 11 Discharge port 12 rotation axes 13 First uneven portion of the rotor 13A Recess 13B protrusion 14. Second uneven section of the rotor 15 Scrapers A1, A2 gap

Claims

1. A grease composition containing a base oil (A), a urea-based thickener (B), and an oil hardening agent (C), The particles containing the urea-based thickener (B) in the grease composition satisfy the following requirement (I): The content of the urea-based thickener (B) is 0.5% by mass to 15.0% by mass on a basis of the total amount of the grease composition. The oil hardening agent (C) is capable of thickening, solidifying, and / or sol-gelling liquid oils at room temperature. The oil hardening agent (C) is a glycerin fatty acid ester with a melting point of 50 to 80°C. A grease composition in which the content of the oil hardening agent (C) is 0.1% by mass to 10% by mass based on the total amount of the grease composition. Requirement (I): The arithmetic mean particle diameter based on area, when the particles are measured by laser diffraction / scattering, is 2.0 μm or less.

2. The grease composition according to claim 1, wherein the particles containing the urea-based thickener (B) in the grease composition further satisfy the following requirement (II). Requirement (II): The specific surface area of ​​the particle measured by laser diffraction / scattering is 0.5 × 10 ５ cm ２ / cm ３ That's all.

3. The grease composition according to claim 1 or 2, wherein the melting point of the oil hardening agent (C) is 100°C or lower.

4. The kinematic viscosity of the base oil (A) at 40°C is 10 mm². ２ / s ~ 80mm ２ The grease composition according to claim 1 or 2, wherein the ratio is / s.

5. The grease composition according to claim 1 or 2, wherein the consistency of the mixture is 300 to 500.

6. A grease composition according to claim 1 or 2, used for lubricating the lubrication parts of a speed reducer or speed increaser.

7. A lubrication method for lubricating a lubrication part of a speed reducer or speed increaser using the grease composition described in claim 1 or 2.