Anti-collision pressure vessel steel for storing and transporting boron trifluoride and production method thereof

Anti-collision pressure vessel steel produced by using specific components and controlled rolling and cooling processes solves the safety problem of boron trichloride during transportation, achieving efficient energy absorption and material stability under collision conditions, thus ensuring transportation safety.

CN117551939BActive Publication Date: 2026-07-03武汉钢铁有限公司
View PDF 3 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
武汉钢铁有限公司
Filing Date
2023-10-16
Publication Date
2026-07-03

AI Technical Summary

Technical Problem

Existing technologies cannot effectively guarantee the safety of pressure vessels during the transportation of boron trichloride in the event of a collision, nor can they guarantee the dynamic yield strength and dynamic elongation after fracture of the material, which may lead to the risk of tank deformation, leakage and explosion.

Method used

The impact-resistant pressure vessel steel is produced using specific components and processes, including a reasonable ratio of elements such as C, Si, Mn, Al, V, and Nb. Through controlled rolling and controlled cooling processes, the microstructure is controlled to be ferrite + pearlite + bainite, ensuring a match between static and dynamic mechanical properties.

Benefits of technology

In the event of a collision, the steel plate can effectively absorb energy, prevent tank deformation and leakage, and ensure transportation safety. The dynamic yield strength and elongation after fracture are within a specific range, which improves the safety of transporting boron trichloride.

✦ Generated by Eureka AI based on patent content.

Smart Images

  • Figure BDA0004494227890000121
    Figure BDA0004494227890000121
  • Figure BDA0004494227890000131
    Figure BDA0004494227890000131
  • Figure BDA0004494227890000132
    Figure BDA0004494227890000132
Patent Text Reader

Abstract

A collision-resistant pressure vessel steel for storing and transporting boron trifluoride, comprising the following components (wt%): C: 0.10–0.20%, Si: 0.20–0.40%, Mn: 1.25–1.70%, Al: 0.025–0.045%, P≤0.015%, S≤0.005%, V: 0.010–0.025%, Nb: 0.014–0.035%. The process involves: smelting, casting into a billet, heating the billet, rough rolling, finish rolling, cooling, normalizing, and stress relief. The static yield strength Rel of this invention is 350–430 MPa, and the dynamic yield strength Re is 470–675 MPa; the tensile strength is 510–580 MPa; the yield-to-tensile ratio is ≤0.85; and the static elongation after fracture A is 25–41% and the dynamic elongation after fracture A... d The strength-ductility product is 15950–22320 MPa·% at 30–39.1%; the drop hammer tear (DWTT) energy is 17–20 kJ; when the impact velocity is 5–50 m / s and the impact displacement is 1.5 m, the steel plate absorbs 2.70–3.20 kJ of energy, and the ferrite grain size does not exceed 0.029 μm.
Need to check novelty before this filing date? Find Prior Art

Citation Information

Patent Citations

  • A 355MPa grade low-temperature impact-resistant steel plate and its manufacturing method

    CN112746222B

  • Low-temperature marine steel plate with excellent plasticity and manufacturing method thereof

    CN115287431A

  • Q370 vessel steel with excellent simulated post-weld heat treatment performance and production method

    CN103361550A