Household article with antibacterial coating and manufacturing method thereof

Abstract

The invention discloses various garbage cans, coatings thereof and coatings for other household articles. In certain embodiments, the disclosed coatings are antibacterial. Further disclosed are various methods for forming antibacterial coatings for household articles. In some embodiments, the antimicrobial coating includes a substrate and an antimicrobial agent. In some embodiments, the coating may be applied to household articles, where the coating leaves a finished product surface that is substantially free of stripes. Some embodiments relate to protective films that can be removed from coated household articles without leaving residues.

Description

[0001] This application is a divisional application of the invention patent application entitled “Household products with antibacterial coating and method for manufacturing the same” filed on November 10, 2016 and application number 201610988552.7.

[0002] CROSS-REFERENCE TO RELATED APPLICATIONS

[0003] This application claims the benefit of U.S. Provisional Application No. 62 / 253,612, filed on November 10, 2015, entitled “Antibacterial Coating for Household Products and Method of Making the Same,” the entire contents of which are incorporated herein by reference. Technical Field

[0004] The present disclosure relates generally to the field of household articles having antimicrobial coatings and methods of making the same. Background Art

[0005] Household items and / or their components include surfaces that can be exposed to contaminants during use. For example, trash cans are often exposed to raw meat, food, and other forms of trash. Soap dispensers are exposed to the dirty hands of users. Such exposure of household items to contaminants can lead to the accumulation and growth of bacteria and other microorganisms. Summary of the invention

[0006] Certain embodiments disclosed herein relate to coatings for household products. In some embodiments, the coating comprises a polymer substrate configured to adhere to a surface of the household product. In some embodiments, the coating comprises an antimicrobial agent dispersed on or within the substrate.

[0007] Any embodiments described above or elsewhere herein may include one or more of the following features.

[0008] In some embodiments, the antimicrobial agent comprises zeolite. In some embodiments, the antimicrobial agent comprises silver ions. In some embodiments, the antimicrobial agent comprises copper ions. In some embodiments, the antimicrobial agent comprises ammonium.

[0009] In some embodiments, the antimicrobial agent comprises at least about 2% and / or less than or equal to about 5% by weight of the substrate. In some embodiments, the antimicrobial agent comprises silver ions equal to or at least about 2% by weight and / or less than or equal to about 5% by weight. In some embodiments, the antimicrobial agent comprises copper ions equal to or at least about 4.0% by weight and / or less than or equal to about 7.0% by weight. In some embodiments, the antimicrobial agent comprises ammonium equal to or at least about 0.1% by weight and / or less than or equal to about 2.0% by weight. In some embodiments, the antimicrobial agent comprises a zeolite having antimicrobial ions adhered to, deposited thereon, or diffused therein. In some embodiments, the antimicrobial agent comprises AGION®. In some embodiments, the antimicrobial agent is present in an amount of about 1.25% by weight relative to the substrate.

[0010] In some embodiments, the polymer substrate comprises polyethylene. In some embodiments, the polymer substrate comprises a material that resists fingerprints and smudges or allows them to be wiped off more easily.

[0011] In some embodiments, the coating is durable enough that it can withstand repeated cleaning or washing without losing its antimicrobial properties.

[0012] Some embodiments relate to a coating for household items, comprising a polymer substrate configured to adhere to a surface of the household item and an antimicrobial agent or combination of antimicrobial agents dispersed on or within the substrate, for example, wherein the one or more antimicrobial agents include one or more of zeolite, silver ions, copper ions, or ammonium. In some embodiments, the coating is an antimicrobial agent.

[0013] In some embodiments, the polymer substrate comprises polyethylene.

[0014] In some embodiments, the coating includes equal to or greater than about 0.1 wt % and / or less than or equal to about 1.5 wt % of the antimicrobial agent.

[0015] In some embodiments, the antimicrobial agent comprises zeolite at a level of about 68% by weight or greater and / or less than or equal to about 94% by weight. In some embodiments, the antimicrobial agent comprises silver ions at a level of about 2% by weight or greater and / or less than or equal to about 5% by weight. In some embodiments, the antimicrobial agent comprises copper ions at a level of about 4.0% by weight or greater and / or less than or equal to about 7.0% by weight. In some embodiments, the antimicrobial agent comprises ammonium ions (or ammonium salts) at a level of about 0.1% by weight or greater and / or less than or equal to about 2.0% by weight. In some embodiments, the antimicrobial agent comprises AGION®. In some embodiments, the antimicrobial agent is present in an amount of about 1.25% by weight relative to the substrate.

[0016] In some embodiments, the polymer substrate includes a material that resists fingerprints and smudges or allows them to be wiped off more easily. In some embodiments, the coating is durable enough that it can withstand repeated cleaning or washing without losing its antimicrobial properties.

[0017] Some embodiments are directed to a metal sheet including a coating including any one or more of the above-described features.

[0018] Some embodiments relate to household items, such as a trash can including a coating, the coating including any one or more features described in this specification. In some embodiments, the coating is located on the outer surface of the trash can. In some embodiments, the trash can includes a metal body and a coating located on the metal body.

[0019] Some embodiments relate to a trash can comprising a metal body, a lid coupled to the body and configured to move between an open position and a closed position, and a base on which the metal body is configured to rest. In some embodiments, the outer surface of the metal body comprises a coating comprising a substrate having an antimicrobial agent dispersed on or within the substrate, the antimicrobial agent comprising silver ions. In some embodiments, the thickness and / or composition and / or reflectivity of the coating on the substrate surface are substantially equal or uniform. For example, the coating may be substantially free of streaks.

[0020] In some embodiments, the antimicrobial agent comprises zeolite. In some embodiments, the substrate comprises polyethylene. In some embodiments, the antimicrobial agent comprises copper ions. In some embodiments, the antimicrobial agent comprises ammonium. In some embodiments, the coating reduces the amount of bacteria on the coating by about 9.5×10 6 The coating reduces the number of E. coli on the coating from about 2.3×10 5 The CFU / vector was reduced to less than about 5 CFU / vector.

[0021] Some embodiments relate to trash cans including a metal body forming at least a portion of a container configured to receive trash. In some embodiments, the outer surface of the metal body includes a coating. In some embodiments, the coating includes a substrate having an antimicrobial agent dispersed on or within the substrate. In some embodiments, the thickness and / or composition and / or reflectivity of the coating on the surface of the substrate is substantially equal or uniform. For example, the coating may be substantially free of striations.

[0022] In some embodiments, the antimicrobial agent comprises one or more of zeolite, silver ions, copper ions, or ammonium. In some embodiments, the antimicrobial agent comprises a zeolite having antimicrobial ions adhered to, deposited thereon, or diffused therein. In some embodiments, the antimicrobial agent comprises AGION®.

[0023] In some embodiments, the substrate comprises polyethylene.

[0024] In some embodiments, the coating is applied to a metal sheet used to fabricate the metal body by applying a slurry including a solvent, a base material, and an antimicrobial agent to the metal sheet using a reverse rolling apparatus.

[0025] In some embodiments, the coating includes a fingerprint-resistant material or a material from which fingerprints can be easily removed, such as by wiping without the need for solutions or excessive or vigorous rubbing of the surface from which the fingerprints were created.

[0026] In some embodiments, after the bacteria are exposed to the coating for about 24 hours, the amount of bacteria remaining on the coating is reduced by at least about 95% compared to the initial exposure. In some embodiments, after the bacteria are exposed to the coating for about 24 hours, the amount of bacteria remaining on the coating is reduced by at least about 99.99% compared to the initial exposure. In some embodiments, after the bacteria are exposed to the coating for about 24 hours, the amount of bacteria remaining on the coating is reduced by about 95% to about 100%. In some embodiments, the coating reduces the amount of E. coli from about 2.3×10 5 CFU / 50 mm×50 mm carrier to less than or equal to about 5 CFU / carrier. In some embodiments, the coating reduces the amount of Staphylococcus aureus from about 3.85×10 5 The CFU / 50 mm x 50 mm carrier is reduced to less than or equal to about 5 CFU / carrier.

[0027] Some embodiments relate to methods for coating metal surfaces. In some embodiments, the method for coating a metal surface includes obtaining a solution of a polymer substrate in a solvent. In some embodiments, the method includes dispersing an antimicrobial agent on or in the solution to form a mixture. In some embodiments, the method includes stirring the mixture to form a substantially uniform slurry. In some embodiments, the method includes obtaining a sheet. In some embodiments, the method includes applying the slurry as a layer to the sheet. In some embodiments, the method includes curing the slurry on the sheet to provide a coated sheet. In some embodiments, the resulting coated metal sheet is substantially traceless. Some embodiments relate to methods for manufacturing a metal sheet having an antimicrobial coating. In some embodiments, the method includes providing a metal sheet. In some embodiments, the method includes applying a slurry comprising an antimicrobial agent and a solvent to the metal sheet. In some embodiments, the method includes drying the slurry on the metal sheet to provide an antimicrobial coating. In some embodiments, the metal sheet is shaped to provide a portion of the surface of a household item. In some embodiments, the slurry is applied to the metal sheet using a reverse rolling device.

[0028] In some embodiments, the method includes applying an acrylic and / or silicone resin and / or silicone rubber adhesive on the coated portion of the coated metal sheet and then applying a protective film over such adhesive on the coated metal sheet.

[0029] In some embodiments, the antimicrobial agent used in the method comprises zeolite (and / or any of silver ions, copper ions, or ammonium).

[0030] Some embodiments relate to metal sheets comprising a coating, layer and / or sheet. In some embodiments, the coating comprises a polymer substrate configured to adhere to a surface of a household item. In some embodiments, the coating comprises an antimicrobial agent dispersed on or within the substrate. In some embodiments, the coating is an antimicrobial agent. In some embodiments, the coating comprises a protective film that protects the layer from wear during transportation of the metal sheet. In some embodiments, the coating comprises an acrylic and / or silicone resin and / or silicone rubber adhesive that adheres the protective film to the coating. In some embodiments, after removing the protective film, the adhesive leaves substantially no residue on the coating.

[0031] Some embodiments relate to coatings for household goods, including coatings comprising antimicrobial agents. In some embodiments, the coating further comprises an anti-fingerprint agent, such as an agent that resists the formation of visible fingerprints and / or an agent that allows fingerprints to be easily removed. In some embodiments, the coating is applied to the surface of household goods. Any feature, structure, component or step described and / or shown in any embodiment in this specification can be used or replaced with any feature, structure, component or step described and / or shown in any other embodiment in this specification. Anything disclosed and / or shown in this specification is intended to be interchangeable and combinable. BRIEF DESCRIPTION OF THE DRAWINGS

[0032] The embodiments of the present invention are described in detail below with reference to the accompanying drawings, wherein:

[0033] Figure 1 A trash can with an antimicrobial coating is shown.

[0034] Figure 2 yes Figure 1 A front view of a trash can and a close-up view of a section of a portion of the trash can.

[0035] Figure 3A-3B is a photograph of a sheet including one or more coatings containing an antimicrobial agent.

[0036] Figures 4A-4B yes Figure 3A-3B Close-up of a portion of a photograph.

[0037] Figure 5 is a graph showing the growth of E. coli on uncoated and coated metal sheets.

[0038] Figure 6 is a graph showing the growth of Staphylococcus aureus on uncoated and coated metal sheets.

[0039] Figure 7 is a process flow diagram showing the preparation of an antimicrobial coating on a metal sheet.

[0040] Figure 8A diagram showing a coated sheet using a reverse rolling process.

[0041] Fig. 9 is a process flow diagram showing the protection of an antimicrobial coating on a metal sheet.

[0042] Figures 10A-10B is a photograph of a partially removed protective film applied to a sheet including a coating containing an antimicrobial agent. DETAILED DESCRIPTION

[0043] Various antimicrobial coatings and methods of forming and using the same are described below to illustrate various embodiments that can be used to achieve one or more desired improvements. These embodiments are merely illustrative and are not intended to limit the general inventions proposed and the various aspects and features of these inventions in any way. In addition, the wording and terminology used in this application are for descriptive purposes and should not be considered restrictive. The features, structures, or steps disclosed in this application are not necessary or essential.

[0044] Overview

[0045] Some embodiments disclosed herein relate to coatings for household items. In certain embodiments, the coating is antimicrobial. As used herein, the term "antimicrobial agent" and its derivatives describe properties that kill microorganisms and / or prevent or slow the growth of microorganisms. As used herein, the term "microorganism" and its derivatives refer to organisms that are too small to be seen by the naked eye, such as various bacteria, archaea, fungi, and protists.

[0046] As will be described in more detail below, in some embodiments, the coating includes a substrate and an antimicrobial agent distributed in the substrate. In certain embodiments, the coating is applied to a metal (e.g., stainless steel or aluminum) that forms part of a household item (e.g., a trash can). In some variations, the coating includes an antimicrobial agent, a substrate, and a compound that facilitates avoiding or wiping away fingerprints. This combination coating can be applied to a surface that can form part of a household item (e.g., a metal sheet).

[0047] like Figure 1 and Figure 2As shown, certain embodiments are disclosed in the context of a coating 120 for a trash can 100 including a metal sheet 110, because the coating may have a specific purpose herein. However, various aspects of the present disclosure may be used for common sheet items and for other household items having metal or non-metal parts. For example, some exemplary household items are: soap dispensers, mirrors (e.g., metal trim on mirrors, shelves, etc.), soap boxes, grocery bag dispensers, shower / sink storage baskets, appliance containers, organizers (e.g., for drawers or countertops), paper towel racks, dish racks, wall-mounted liquid pumps (e.g., for soap, shampoo, etc.), toilet plunger handles, household appliance handles (e.g., for microwave ovens, refrigerators, dishwashers, ovens, coffee pots, etc.), household appliances (e.g., refrigerators, microwave ovens, dishwashers, ovens, blenders, coffee machines, trash compactors, BBQ grills, etc.), sink accessories (e.g., handles, faucets, etc.), liquid dispensers (e.g., for beverages), washing machines, dryers, and components thereof, etc. In some variations, the coating is applied to a handle, trim, or removable inner bucket (e.g., a removable insert that fits within a larger trash can body) of a trash can. In some embodiments, the coatings described herein may be applied to a handheld device or a touch screen.

[0048] In some embodiments, the household items are broadly metal items. In some variations, the household items include stainless steel. In some embodiments, the metal of the household items includes one or more of stainless steel, brass, copper, steel, aluminum, iron, platinum, gold, silver, zinc, other metals, their metal alloys, etc. In certain embodiments, the household items are made of non-metallic materials (e.g., plastic, glass, etc.) and / or composite materials.

[0049] In some variations, the coating is configured to adhere to one or more surfaces of household goods. In some embodiments, the coating is applied to the sheet surface for making household goods. For example, as discussed in more detail below, the coating can be applied to a metal sheet that subsequently forms a part of household goods (such as the body and / or lid of a trash can). In some variations, for example, the coating can be applied to the inner and outer surfaces of household goods (such as the two sides of the stainless steel sheet for making a trash can). In some variations, the coating is only applied to the selected surface of household goods. For example, in some embodiments, the coating is only applied to the outside of household goods (such as a trash can, etc.). In other variations, the coating is only applied to the inside of household goods (such as a trash can, etc.). In some embodiments, the coating is applied to one or more of the inside, outside, lid, handle or pedal of household goods (such as a trash can, etc.).

[0050] In some variations, the coatings and methods of coating materials described herein increase or maximize the antimicrobial effect of the antimicrobial agent in the coating without substantially affecting the appearance of the household product. For example, in some embodiments, the antimicrobial coating is smooth and uniform without visible streaks and / or is transparent (or substantially transparent). In some embodiments, the antimicrobial coating is substantially smooth and / or substantially uniform and / or substantially average or uniform in reflectivity on a particular surface of the coating or a particular portion of the surface of the coating, without substantially visible streaks and / or is transparent (or substantially transparent). Figure 3A-3B 4A-4B show examples of side-by-side arrangements of antimicrobial coatings that are either streaky or smooth and uniform with no visible streaks. For example, Figure 3B and Figure 4B The coating is basically free of streaks, and Figure 3A and Figure 4A In some embodiments, the antimicrobial coating shows an unobstructed view of the surface below the coating, such as the top of the surface coated with the coating. In some embodiments, the coating is colorless or substantially colorless. In some embodiments, the coating has a blue color.

[0051] In certain embodiments, the coating is generally flat and / or substantially flat. In some embodiments, the coating is substantially uniform and / or smooth. In some variations, the coating is generally continuous. In some embodiments, the above properties of the coating make it appear substantially free of stripes, wherein the stripes are generally not visible upon casual visual observation.

[0052] Certain substrates

[0053] In certain embodiments, as disclosed above, the coating comprises a substrate and one or more antimicrobial agents. In certain embodiments, the antimicrobial agent is dispersed under the substrate, within the substrate (e.g., uniformly throughout the substrate or as a gradient), or on the substrate (e.g., adhered and / or functionalized to the substrate surface). In some embodiments, the substrate is any material that provides support for the antimicrobial agent while allowing bacteria or other microorganisms in contact with the coating to enter the antimicrobial agent. In some embodiments, the substrate is substantially transparent (e.g., selected to be substantially optically transparent to the naked eye).

[0054] In certain embodiments, the substrate comprises a polymer material. For example, the substrate may comprise polyethylene. In some variations, the substrate comprises a mixture of more than one polymer material.

[0055] Although polymeric substrates are described herein, any other substrate may be used, keeping in mind that in some embodiments, the purpose of the substrate (i.e., substrate, support, etc.) is to provide a substrate that can support the antimicrobial agent while being attached to the household product in a manner that does not substantially distort the appearance of the product. For example, in some embodiments, the substrate comprises a cross-linkable polymeric substrate or a copolymeric substrate.

[0056] In some embodiments, the substrate itself is formulated with one or more polymers having an antimicrobial effect. For example, in certain embodiments, the substrate comprises a polymeric material comprising one or more polymeric antimicrobial materials (e.g., polyethyleneimine, NIPAM, or other cationic or polycationic polymers).

[0057] Certain antimicrobial agents

[0058] Some embodiments relate to an antimicrobial agent that is attached to a surface (e.g., a metal part) of a household item. In some embodiments, the antimicrobial agent is attached to the surface of the household item via a substrate, as described elsewhere in this application. In some embodiments, the substrate and the antimicrobial agent form a coating. In some embodiments, the antimicrobial agent itself provides a coating and / or is a coating on the household item. In some embodiments, as described above and as described above, Figure 2 As shown, the coating includes an antimicrobial agent 220 dispersed within a substrate 210. In certain embodiments, such as Figure 2 In the enlarged cross-sectional view shown, at least a portion of the antimicrobial agent 220 is exposed on the outer surface of the coating 120. In some variations, the antimicrobial agent 220 is able to directly contact microorganisms on the surface of the coating 120 because the antimicrobial agent 220 is detached from and / or protrudes (e.g., extends to the outside) from the substrate 210. In some embodiments, the antimicrobial agent can diffuse to the surface of the coating over time to directly interact with microorganisms on the surface of the household product.

[0059] In some embodiments, the antimicrobial agent comprises an antimicrobial zeolite. In some embodiments, the antimicrobial zeolite comprises one or more antimicrobial metal ions, antimicrobial metals, or antimicrobial organic ions. In some embodiments, the antimicrobial agent and / or antimicrobial zeolite comprises water. For example, in some embodiments, when the antimicrobial agent comprises a zeolite, some of the water may be trapped or adhered to the zeolite. In some embodiments, the antimicrobial zeolite or antimicrobial agent comprises one or more of silver ions, copper ions, or copper metal, or ammonium. In some embodiments, the antimicrobial zeolite and / or antimicrobial agent comprises each of silver ions, copper (ionic or metallic), and ammonium. In some embodiments, the antimicrobial agent comprises AGION® available from Sciessent LLC of Wakefield, Massachusetts. In some embodiments, the weight percentage of zeolite (e.g., aluminosilicate portion of zeolite without water, antimicrobial anions, or antimicrobial organic cations) in the antimicrobial zeolite and / or antimicrobial agent is equal to or greater than about 68% and / or less than or equal to about 94%. In some embodiments, the weight percentage of zeolite in the antibacterial agent and / or antibacterial zeolite is equal to or at least about 60%, about 65%, about 70%, about 80%, about 90%, about 95%, about 99%, values ​​between the above values, ranges across the above values, or other values. In some embodiments, the weight percentage of zeolite in the antibacterial agent and / or antibacterial zeolite is less than or equal to about 99%, about 95%, about 90%, about 85%, about 80%, about 75%, about 70%, about 65%, about 60%, values ​​between the above values, ranges across the above values, or other values. In some embodiments, the antibacterial agent includes one or more antibacterial zeolites and / or other antibacterial entities (e.g., silver ions, copper ions, ammonium, etc.).

[0060] In some embodiments, the silver ions may be present in an amount equal to or greater than about 2% by weight of the antimicrobial zeolite (and / or the weight of the antimicrobial agent) and / or less than or equal to about 5% by weight of the antimicrobial zeolite (and / or the weight of the antimicrobial agent). In some embodiments, the weight percentage of silver ions in the antimicrobial zeolite (and / or the antimicrobial agent) is equal to or greater than at least: about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, values ​​between the above values, ranges spanning the above values, or other values. In some embodiments, the weight percentage of silver ions in the antimicrobial zeolite (and / or antimicrobial agent) is less than or equal to: about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, values ​​between the above values, ranges spanning the above values, or other values.

[0061] In some embodiments, copper ions or metallic copper may be present in an amount equal to or greater than about 4% by weight of the antimicrobial zeolite (and / or the weight of the antimicrobial agent) and / or less than or equal to about 7% by weight of the antimicrobial zeolite (and / or the weight of the antimicrobial agent). In some embodiments, the weight percentage of copper ions or metallic copper in the antimicrobial zeolite (and / or the antimicrobial agent) is equal to or at least about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, values ​​between the above values, ranges spanning the above values, or other values. In some embodiments, the weight percentage of copper ions or metallic copper in the antibacterial zeolite (and / or in the antibacterial agent) is less than or equal to: about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, values ​​between the above values, ranges spanning the above values, or other values.

[0062] In some embodiments, ammonium may be present in an amount equal to or greater than about 0% by weight of the antimicrobial zeolite (and / or the weight of the antimicrobial agent) and / or less than or equal to about 2% by weight of the antimicrobial zeolite (and / or the weight of the antimicrobial agent). In some embodiments, the weight percentage of ammonium in the antimicrobial zeolite (and / or in the antimicrobial agent) is equal to or at least about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, values ​​between the above values, ranges across the above values, or other values. In some embodiments, the weight percentage of ammonium in the antimicrobial zeolite (and / or in the antimicrobial agent) is less than or equal to about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, values ​​between the above values, ranges across the above values, or other values.

[0063] In some embodiments, the antibacterial agent includes water. For example, zeolite can also be hygroscopic and can naturally absorb water from the environment. In some embodiments, water can be present in an amount equal to or greater than about 0% of the weight of the antibacterial zeolite (and / or the weight of the antibacterial agent) and / or less than or equal to about 18% of the weight of the antibacterial zeolite (and / or the weight of the antibacterial agent). In some embodiments, the weight percentage of water in the antibacterial zeolite (and / or the antibacterial agent) is equal to or at least: about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, about 15.0%, about 20.0%, values ​​between the above values, ranges across the above values, or other values. In some embodiments, the weight percentage of water in the antibacterial zeolite (and / or in the antibacterial agent) is less than or equal to: about 0.5%, about 1.0%, about 2.0%, about 3.0%, about 4.0%, about 5.0%, about 6.0%, about 7.0%, about 8.0%, about 9.0%, about 10.0%, about 15.0%, about 20.0%, values ​​between the above values, ranges across the above values, or other values. In certain embodiments, the antibacterial zeolite includes about 18% water by weight ("AC10N"), about 5% water by weight ("AC10D"), or about 2% water by weight ("AC10H").

[0064] In some embodiments, one or more antimicrobial agents are supported by a sub-support structure, which may or may not be antimicrobial itself. For example, in some embodiments, one or more antimicrobial agents are supported on nanoparticles (e.g., particles with an average particle size of about 10 nm or more to about 1000 nm or less) or microparticles (e.g., particles with an average particle size of about 1 μm or more to about 1000 μm or less). In some embodiments, the sub-support comprises zeolite. In some embodiments, the sub-support structure may comprise any of the weight percentages of silver ions, copper ions, ammonium and / or water described elsewhere in this application. In some embodiments, as described above, the antimicrobial agent comprises a zeolite sub-support having one or more antimicrobial ions adhered thereto (or diffused therein). In some embodiments, the average particle size of the zeolite (or other sub-support structure) is equal to or less than: about 100 μm, about 10 μm, about 1 μm, a value in the range between the above values, a value between the above values, or other values. In some embodiments, the average particle size of the zeolite (and / or other sub-support structure) is less than about 6 μm.

[0065] In some variations, the antimicrobial agent does not include zeolite (e.g., zeolite sub-support structure) or other sub-support structure, but includes one or more of free silver (e.g., silver ions, silver salts, metallic silver, etc.), copper (copper ions, copper salts, or metallic copper, etc.), organosilane, ammonium or cationic materials (e.g., 3-(trimethoxysilyl)-propyldimethyloctadecyl ammonium chloride, etc.) that provide an antimicrobial effect. For example, in some embodiments, the coating includes silver ions.

[0066] In some embodiments, the substrate supporting the antimicrobial agent comprises the entire dry weight of the coating. In some embodiments, the antimicrobial agent accounts for equal to or less than about 1.25% by weight (i.e., weight percentage) of the total coating weight. In some embodiments, the coating comprises an antimicrobial agent at a weight ratio equal to or greater than about 0.1% and / or a weight ratio less than or equal to about 1.5%. In some embodiments, the coating comprises an antimicrobial agent at a weight ratio equal to or greater than about 1.1% and / or a weight ratio less than or equal to about 1.3%. In some embodiments, the coating comprises an antimicrobial agent at a weight ratio equal to or greater than about 1.1% and / or a weight ratio less than or equal to about 1.2%. In some embodiments, the weight percentage of the antimicrobial agent in the coating is at least: about 0.0001%, about 0.001%, about 0.01%, about 0.1%, about 0.5%, about 1.0%, about 1.25%, about 1.5%, about 2.0%, values ​​between the above values, values ​​greater than the above values, values ​​less than the above values, or other values. In some embodiments, the weight percentage of the antimicrobial agent in the sub-support is less than or equal to: about 0.0001%, about 0.001%, about 0.01%, about 0.1%, about 0.5%, about 1.0%, about 1.25%, about 1.5%, about 2.0%, values ​​between the above values, values ​​spanning the above values, or other values.

[0067] As described below in Examples 2 and 3, and as Figure 5 and Figure 6 As shown, after being exposed to the coating for a period of about 24 hours, the antimicrobial coating kills substantially all bacteria present on the coating. Figure 5 ) showed that after a period of about 24 hours of exposure to the coating, both coatings including about 1.25 wt % AGION® or about 1.5 wt % AGION® killed substantially all of the E. coli present on the coating. Figure 6% AGION®) was slightly more effective in killing S. aureus than a coating comprising about 1.5 wt % AGION® after exposure to the coating for a period of about 24 hours. This result surprisingly shows that lower doses of AGION® can be used to achieve a kill rate close to 100% relative to larger doses of AGION®. Without being bound by any particular mechanism, it is believed that lower doses of AGION® (e.g., 1.25 wt % or less) allow it to be better dispersed within the coating (e.g., by preventing aggregation), giving it a better effect and effective antimicrobial effect.

[0068] In embodiments where the antimicrobial agent is provided without a sub-support structure (eg, without zeolite), the weight percent of the antimicrobial agent in the coating may be reduced to account for the lack of such a sub-support.

[0069] In some embodiments, the amount of bacteria remaining on the coating is reduced by equal to or at least about 95% to about 100% after the bacteria are exposed to the coating for about 24 hours. In some embodiments, the amount of bacteria present is reduced by equal to or at least about 75%, about 85%, about 95%, about 98%, about 99%, about 99.9%, about 99.99%, about 99.999%, about 99.9999%, or about 99.99999% after the bacteria are exposed to the antimicrobial coating for 24 hours. In some embodiments, the coating reduces the amount of E. coli from about 2.3×10 5 CFU / carrier is reduced to about 0 CFU / carrier and / or less than or equal to about 5 CFU / carrier (the detection limit is about 5 CFU / carrier). In some embodiments, as shown in Table 1, the coating reduces the amount of bacteria from about 2.35×10 7 The coating reduces the amount of S. aureus from about 3.85×10 5 CFU / carrier is reduced to about 0 CFU / carrier and / or less than or equal to about 5 CFU / carrier (detection limit is about 5 CFU / carrier). In some embodiments, as shown in Table 2, the coating reduces the amount of bacteria from about 9.5×10 6The colony forming units (CFU) / carrier (on the control surface) are reduced to about 0 CFU / carrier and / or less than or equal to about 5 CFU / carrier (the detection limit is about 5 CFU / carrier). In some embodiments, the coating has the above-mentioned antibacterial effect on one or more bacteria selected from Streptococcus pneumoniae, Haemophilus influenzae, Moraxella catarrhalis, Staphylococcus aureus, Escherichia coli, etc. In some embodiments, the coating has an antibacterial effect on Gram-positive bacteria and / or Gram-negative bacteria.

[0070] Characteristics of some antimicrobial coatings

[0071] As described above, the antimicrobial coating can be applied to household items. In some embodiments, the coating is sufficiently durable for long-term use (e.g., capable of maintaining integrity and substantially undiminished efficacy over a period of at least one year of regular and normal use). In some variations, the appearance of the household item remains substantially unchanged and / or the antimicrobial properties remain substantially unchanged during long-term use (e.g., one, two, three, four, or more years as can be measured over time or under conditions of accelerated stress).

[0072] In some embodiments, the coating is durable enough to withstand repeated cleaning or washing. For example, since household items such as trash cans and sink accessories are usually washed repeatedly during their use, in some variations, the coating is configured to maintain its antimicrobial properties after repeated cleaning including scrubbing and washing with soapy water. In some embodiments, the durable coating maintains its antimicrobial properties after washing with a standard wash cloth and soapy water for at least about 25 times, at least about 50 times, at least about 100 times or more. In some variations, the coating maintains its antimicrobial activity after washing with kitchen paper towels and household cleaners (e.g., bleach, ammonia-based cleaners (e.g., WINDEX® cleaners), etc.) for at least about 25 times, at least about 50 times, at least about 100 times or more.

[0073] In some variations, the coating retains its antimicrobial properties under conditions of accelerated wear intended to simulate the life of the commercial product (e.g., under conditions of thermal stress, increased humidity, exposure to simulated sunlight, etc.). In some embodiments, the coating retains its antimicrobial properties after being worn (e.g., scratched or nicked by steel wool or other abrasives). In some variations, the coating retains its antimicrobial properties after about 1000 wipes with dry lens tissue. In some embodiments, a product that retains its antimicrobial properties includes retaining at least about 75%, at least about 85%, at least about 90%, at least about 95%, at least about 99%, or more of its initial antimicrobial properties prior to use.

[0074] In some embodiments, the durability of the coating can be measured by the contact angle of a water drop or an oil drop on the coating surface. In certain variations, the contact angle of a water drop on the coating changes by less than about 10% under one or more of the above-mentioned washing and abrasion conditions. In some embodiments, the contact angle of a water drop on the coating changes by less than about 20% and / or less than about 40% under one or more of the above-mentioned washing and abrasion conditions. In some embodiments, the contact angle of an oil drop on the coating changes by less than about 10% under one or more of the above-mentioned washing and abrasion conditions. In some embodiments, the contact angle of an oil drop on the coating changes by less than about 20% or less than about 40% under one or more of the above-mentioned washing and abrasion conditions.

[0075] In some embodiments, the coating retains its antimicrobial activity even after polishing and / or stretching. Polishing may include abrasion with a cloth and a polishing agent under typical polishing conditions. In certain embodiments, the coating provided herein advantageously protects the appearance of the metal product, so that the surface of household goods does not need to be polished. In some embodiments, this property may advantageously impart even more durable antimicrobial properties to the product.

[0076] In some embodiments, the antimicrobial properties of the coating are achieved without leaching copper from the coating. In some embodiments, the antimicrobial properties of the coating are achieved without leaching silver from the coating. In some embodiments, the antimicrobial properties of the coating are achieved without leaching copper and / or ammonium from the coating.

[0077] In some embodiments, the coating is fingerprint-resistant or smudge-resistant. The term "fingerprint-resistant" or "smudge-resistant" refers to the ability of a surface to resist visible transfer of residues from physical interactions with a user, the ability to minimize, hide or obscure tactile transferable residues on the surface, and / or a combination thereof. In certain embodiments, the fingerprint-resistant surface substantially resists transfer of water-based materials and oil-based materials when in contact with a user. In some embodiments, the fingerprint-resistant surface substantially resists transfer of one or more inorganic materials and organic materials when in contact with a user. In some embodiments, fingerprint resistance is measured by using the amount of transferred residues after a user physically contacts household items. For example, after physical contact (e.g., from the user's skin), a certain amount of residue can be transferred to household items. After each interaction, the mass of residues on the coated household items can be quantified, such as by weighing the mass (or weighing the mass of a representative test piece of the material). In some embodiments, in each instance of physical contact with a portion of household items of size "4×4" (e.g., by dragging a hand across the test surface), the mass transferred from the user to the coated household items is less than or equal to: about 1 mg, about 0.02 mg, or 0.001 mg. In some embodiments, fingerprint resistance is measured qualitatively using the human eye, and after physical contact, the fingerprint / smudge resistant material shows less visible residue than a non-resistant surface. In some embodiments, the fingerprint resistance of the material is measured by determining the reflectivity before contact (e.g., when cleaning) or after one or more instances of physical contact (as described above). In some embodiments, when the fingerprint resistant material is coated on a mirror surface (or a chrome-plated surface, stainless steel, or another other reflective surface of household products), the surface reflectivity of the fingerprint resistant material remains at least about 75%, at least about 95%, or at least about 99% compared to the surface reflectivity before the physical contact instance. In some embodiments, it is advantageous that consumers are more satisfied with fingerprint resistant coatings or smudge resistant coatings for aesthetic reasons.

[0078] In certain embodiments, the antimicrobial agent is deposited directly into a fingerprint mitigation (anti-fingerprint) material to form a coating material, and the two are added together to any surface of the household item. In some embodiments, the anti-fingerprint material (e.g., compound) is applied separately before or after the antimicrobial compound. In some embodiments, the antimicrobial coating and the anti-fingerprint coating are added as separate layers that can be sandwiched on top of each other. Multiple layers can be added by repeatedly exposing, for example, a metal sheet to antimicrobial coating and anti-fingerprint coating conditions. In certain embodiments, the antimicrobial agent and anti-fingerprint material are added to the surface in a pattern (e.g., patches, stripes, etc.) that imparts antimicrobial and anti-fingerprint properties to the household item substantially over the entire coating surface.

[0079] Some methods for antimicrobial coatings

[0080] Some embodiments are directed to methods of making coated household products. Figure 7 A flow chart describing an embodiment of method 700 is provided in . As shown in certain variations, the antimicrobial agent is dispersed in a solution, such as a polymer solution and a solvent 701. The mixture is stirred to form a substantially uniform slurry 702. After the slurry is formed, a sheet is obtained 703 and the slurry is layered onto the sheet to form a coated sheet 704. For example, the slurry can be applied to a metal sheet, such as stainless steel 704. In some embodiments, after a period of time, the sheet can be cured to provide a coated sheet 705. In certain embodiments, the dried coated sheet can be cut and shaped in an appropriate manner to form walls, lids, foot pedals, and handles for metal household items including trash cans.

[0081] In some embodiments, before being applied to the sheet, the antimicrobial agent and the polymer are slurried in a solvent to form a mixture. In some variations, before being applied to the metal sheet, the slurry is continuously stirred to maintain uniform dispersion. In some embodiments, the dispersion is distributed to a coating device that applies a uniform layer of the slurry to the sheet. The solvent can then be evaporated from the slurry, leaving an antimicrobial surface on the sheet, which includes a smooth layer of the polymer in which the antimicrobial agent is dispersed. In some embodiments, the solvent evaporates to cure the polymer / antimicrobial agent. In certain embodiments, after curing, at least a portion of the antimicrobial agent protrudes from the substrate and can be used to directly interact with microorganisms on the surface of the household goods applied. In some embodiments, the antimicrobial agent can diffuse to the surface of the coating over time to directly interact with microorganisms on the surface of the household goods. In certain embodiments, the antimicrobial agent is consumed during the killing of microorganisms, while in other embodiments, it is not consumed. In some embodiments, direct contact with microorganisms and antimicrobial agents is not required.

[0082] It has been found that several coating techniques for surfaces are not suitable for distributing antimicrobial coatings without streaks. For example, coatings applied using a metered roll process result in streaky coatings (see Figure 3A and Figure 4A ). In the metered rolling process, a rolling element rolls in the direction of the sheet passing over the rolling element. In the metered rolling device, the rolling element is at least partially immersed in a reservoir of coating agent. As the rolling element rolls, it takes the coating agent from this reservoir and deposits the coating agent on the sheet as it moves. The process coats the sheet as it travels in the rolling direction.

[0083] In contrast, in various embodiments described herein, the coating apparatus applies the slurry to the sheet using a non-metered rolling process (eg, a reverse rolling technique). Figure 8An embodiment of a system 800 that can be used to apply a coating 810 by reverse rolling is shown. For example, in certain variations, in a non-metered reverse rolling process, a metal sheet 820 is pulled in a first direction 822 under a first rolling element 830 (e.g., a coating roller) of a coating device. The first rolling element 830 is in fluid communication with a reservoir 840 containing a slurry of an antimicrobial agent, a polymer, and / or a solvent formed between the first rolling element 830 and a second rolling element 832 (e.g., a doctor roller). The first rolling element 830 removes the slurry mixture from the reservoir 840 and deposits it on the surface of the first rolling element 831, distributing the slurry mixture to the sheet as the sheet passes under the first rolling element 830. During reverse rolling, an area of ​​the first rolling element 830 that is substantially adjacent to the sheet 820 travels (e.g., rolls) in a second direction 834 that is opposite to the first direction 822 (the direction of movement of the sheet). In some embodiments, when reverse rolling is used, the final coating is substantially or completely free of streaks to the naked eye (see, e.g. Figure 3B and Figure 4B ).

[0084] Without being bound by any particular mechanism, it is believed that the antimicrobial agent increases the contrast of the coating. If applied using certain methods, the contrast of the coating with the antimicrobial agent as disclosed in the present application becomes large enough to be visible to the naked eye. In some embodiments, the coating can be measured using the naked eye to see whether there are no stripes. In some embodiments, it is possible to quantify whether the coating has no stripes. In some embodiments, for example, coatings without stripes are those whose changes in transmittance between any two points on the surface are less than: about 75%, about 50%, about 30%, about 20%, about 10%, about 5%, about 2% or about 1%. In some embodiments, for example, coatings without stripes are those whose changes in reflectivity between any two points on the surface are less than: about 50%, about 25% or about 5%. In certain embodiments, the coating is applied by using other solution-based techniques (e.g., spraying, spin coating, dip coating, inkjet, etc.) that result in no stripe material.

[0085] In some embodiments, as the slurry solidifies, it forms a uniform distribution of the antimicrobial agent within the coating. In some embodiments, a gradient of the antimicrobial agent can be formed in the coating by, for example, depositing additional slurry layers (with different concentrations of antimicrobial agent) on the sheet. In some embodiments, the gradient can be formed by changing the curing rate (for example, by slowing down or increasing the curing speed using a lower or higher curing temperature, etc.). In some embodiments, the gradient can be formed by depositing additional layers of slurry with a higher or lower concentration on other partially cured slurry layers. In some embodiments, the gradient can be formed by changing the concentration of the antimicrobial agent and / or polymer in the solution. For example, in some embodiments, in a more dilute solution, the curing rate can be slowed down so that more antimicrobial agent can settle in the direction of gravity during the curing process to form a higher concentration layer in this direction. Any method described in this specification can be used to form an antimicrobial gradient, which is higher in concentration at the surface of the coating or higher in concentration at the surface of household products (which can be particularly used in applications where, for example, the antimicrobial agent diffuses to the coating surface over time). In some variations, a gradient can be used to maintain or increase the antimicrobial effect over time.

[0086] In some embodiments, the uneven application of the coating to the surface is reduced or minimized by using the disclosed method and / or substantially uniform (or uniform) coating results. In some embodiments, the visible streaks in the coating may be caused by the uneven application of the coating to the surface of the trash can. In some embodiments, the method for depositing the coating results in a substantially uniform coating thickness on the sheet. In some embodiments, the coating thickness may be equal to or greater than about 10 μm and / or less than or equal to about 20 μm. In some embodiments, the thickness may be less than or equal to: about 100 μm, about 80 μm, about 70 μm, about 60 μm, about 50 μm, about 40 μm, about 30 μm, about 20 μm, about 10 μm, about 5 μm, values ​​between the above values, across the range of the above values, or other values. In some embodiments, the thickness of the coating is substantially uniform. In some embodiments, the coating thickness varies by less than or equal to about 100%, about 90%, about 80%, about 70%, about 60%, about 50%, about 40%, about 30%, about 20%, about 10%, about 5%, about 2%, values ​​between the above values, ranges across the above values, or other values ​​measured between any two points on the coating surface. In some embodiments, this level of uniformity results in a coating that is substantially free of streaks. In some embodiments, the coating is generally planar, substantially flat, substantially smooth and uniform and / or substantially continuous, such that streaks are generally not visible upon casual visual observation.

[0087] In some embodiments, the methods described herein produce substantially optically transparent materials. For example, in certain embodiments, the optical transmittance of the coating over the visible spectrum is at least about 65%, about 75%, about 85%, about 95%, about 98%, values ​​between the above values, values ​​spanning the above values, or other values.

[0088] Some protective layer

[0089] Some embodiments relate to protective layers for the coatings disclosed herein. Fig. 9 A flow chart describing an embodiment of method 900 is provided in . As shown in certain variations, a plurality of metal sheets are obtained 901. In some embodiments, different sheet materials (plastics, composite materials, etc.) may be used. An antimicrobial agent slurry in a polymer / solvent solution is layered onto a plurality of metal sheets 902, which are then cured to form a coated sheet 903. A protective film is then adhered to the coated sheet using an adhesive 904. The sheets are then stacked 905 and conveyed to a manufacturing device 906. At the device, the protective film and adhesive are removed without leaving residue in the adhesive on the coated sheet 907. The sheets are then cut and shaped to form household products 908. In certain embodiments, as described above, the dried coated sheets are cut and shaped in an appropriate manner to form walls, lids, foot pedals, and handles for metal household products including trash cans. In some embodiments, the finished product can be protected by applying an adhesive and a protective film to the antimicrobial coated household product.

[0090] During the transport of the sheet to make household goods or during the transport of the household goods themselves, the surface of the sheet or the surface of the sheet goods can be protected by depositing a film on the surface of these goods. The protective film can be adhered to the portion of the sheet or the portion of the household goods using a rubber adhesive. However, it has been found that some rubber adhesives leave deposits (e.g., residues, etc.) on the coating (see Fig. 10A ). This can cause streaks and other visual defects 1020 on the coating 1001 after the protective film 1010 is removed, such as Fig. 10A In some cases, the residue can leave unwanted sticky areas on the coating. In some cases, these residues are not easily washed off the coating.

[0091] Certain embodiments are configured to ameliorate at least one of these or other problems. For example, some embodiments adhere or otherwise connect the protective film to the coated sheet material such that removal of the film does not leave visible residue on the coating material. In some embodiments, an acrylic adhesive or a silicone rubber adhesive is used to adhere the film to the coated sheet material, which has been found to reduce or eliminate visible residue on the coating 1001 after removal of the film 1011 (see No residue). Fig. 10B). In certain embodiments, once the protective film is removed, the use of an acrylic adhesive or a silicone or rubber adhesive results in a more visually appealing result. In some variations, substantially complete removal of the residue helps avoid areas that would otherwise block the antimicrobial activity of the coating (e.g., the top of the residue). In some embodiments, rubber may be used as an adhesive (with or without one or more other adhesives).

[0092] Some embodiments relate to methods of applying a protective film to an antimicrobial coating. In certain embodiments, the adhesive is applied to the coated sheet using a solution-based technique (e.g., spraying, spin coating, dip coating, ink jetting, rolling, etc.). Once applied, the protective film (e.g., polymer material) is deposited onto the adhesive, for example by winding the film onto the coated sheet.

[0093] Overview

[0094] Several exemplary embodiments of coatings and coating methods are disclosed. Although the present disclosure has been described according to certain exemplary embodiments and uses, other embodiments and other uses including embodiments and uses that do not provide all the features and advantages set forth in the present application are also within the scope of the present disclosure. Components, elements, features, actions or steps may be arranged or performed in a manner different from that described, and may be combined, merged, added or omitted in various embodiments. All possible combinations and sub-combinations of the elements and assemblies described in the present application are intended to be included in the present disclosure. No single feature or set of features is necessary or indispensable.

[0095] Certain features described in the context of a single embodiment of the present disclosure may also be implemented in combination in a single embodiment. Conversely, the individual features described in the context of a single embodiment may also be implemented in multiple embodiments individually or in any suitable sub-combination. In addition, although the above features may be performed in certain combinations, one or more features from the claimed combination may be deleted from the combination in some cases, and the combination may be claimed as a sub-combination or a variation of a sub-combination.

[0096] Any part of any step, process, structure and / or device disclosed or shown in one embodiment, flow chart or example in the present disclosure can be combined or used (or replaced) with other parts of any step, process, structure and / or device disclosed or shown in different embodiments, flow chart or examples. The embodiments and examples described in this application are not intended to be separated and independent from each other. Combinations, variations and other embodiments of the disclosed features are within the scope of the present disclosure.

[0097] As used herein, the terms "approximately," "about," and "substantially" refer to an amount that is close to a specified amount and still performs a desired function or achieves a desired result. For example, in some embodiments, as the context may indicate, the terms "approximately," "about," and "substantially" may refer to an amount that is less than or equal to 10% of a specified amount. As used herein, the term "generally" refers to a value, amount, or characteristic that primarily includes or tends toward a particular value, amount, or characteristic.

[0098] Some embodiments have been described in conjunction with the drawings. In addition, although the operations may be described in the drawings or described in the specification in a particular order, these operations do not need to be performed in the particular order shown or in a sequential order, or all operations are performed in order to achieve the desired result. Other operations not shown or described may be incorporated into the example methods and processes. For example, one or more additional operations may be performed before, after, simultaneously or between any operations described. In addition, in other embodiments, operations may be rearranged or reordered. Similarly, the separation of various components in the above-described embodiments should not be understood as requiring such separation in all embodiments, and it should be understood that the components and systems described may be generally integrated together into a single product or packaged into multiple products. In addition, other embodiments are within the scope of the present disclosure.

[0099] Unless otherwise expressly stated or understood in context, conditional language used in this application, such as "may", "may", "likely", "likely", "for example", etc., is generally intended to express certain embodiments that include certain features, elements and / or steps that other embodiments do not include. Therefore, such conditional language is generally not intended to imply that one or more embodiment features, elements and / or steps are in any way necessary, or that one or more embodiments must include logic for deciding, with or without creator input or prompting, whether to include or perform these features, elements and / or steps in any particular embodiment. The terms "including", "including", "having", etc. are synonymous and are used in a broad manner to include and do not exclude additional elements, features, actions, operations, etc. In addition, the term "or" is used in its inclusive sense (rather than in its exclusive sense), so that when used, for example, to connect a list of elements, the term "or" represents one, some or all of the elements in the list.

[0100] Unless expressly stated otherwise, linking language such as the phrase "at least one of X, Y, and Z" should also be understood along with the context of general usage to mean that an item or term, etc., can be X, Y, or Z. Thus, such linking language is generally not intended to imply that certain embodiments require at least one X, at least one Y, and at least one Z to be present.

[0101] In addition, although exemplary embodiments have been described, any embodiments with equivalent elements, modifications, omissions and / or combinations are also within the scope of the present disclosure. Moreover, although the present application describes certain aspects, advantages and novel features, all of these advantages may not necessarily be achieved according to any particular embodiment. For example, some embodiments within the scope of the present disclosure achieve an advantage or a group of advantages as taught by the present application without having to achieve other advantages taught or suggested by the present application. In addition, some embodiments may achieve advantages different from those taught or suggested by the present application.

[0102] In summary, various embodiments and examples of antimicrobial coatings and protective films have been disclosed. The present disclosure extends to other alternative embodiments and / or other uses of embodiments beyond the specifically disclosed embodiments and examples, as well as certain modifications and equivalents thereof. In addition, the present disclosure explicitly contemplates that the various features and aspects of the disclosed embodiments may be combined or substituted with each other. Therefore, the scope of the present disclosure should not be limited by the above-described specifically disclosed embodiments, but should be determined only by a reasonable reading of the claims.

[0103] Example

[0104] Example 1: Manufacturing of Metal Coatings

[0105] The coatings were prepared using a metered rolling process and a reverse rolling technique. Prior to coating, a slurry of polyethylene polymer and solvent was prepared. To this solution was added 1.25 wt% of AC10Dd grade AGION® (relative to the dry weight of polyethylene) to form a mixture. The mixture was stirred to obtain a homogeneous slurry. Once homogeneity was achieved, it was added to the reservoir of a metered rolling device, which distributes the slurry on a stainless steel sheet through rollers rotating in the same direction as the sheet motion. The sheet was allowed to cure. Figure 3A and Figure 4A The resulting coated sheet is shown.

[0106] A second slurry was formed using the same ingredients and techniques described above. This mixture was added to the reservoir of a reverse rolling device, which distributes the slurry across a stainless steel sheet by rotating rollers in the direction opposite to that of the sheet. The sheet was allowed to cure. Figure 3B and Figure 4B The resulting coated sheet is shown.

[0107] As shown, the antimicrobial coating produced by the reverse rolling technique is streak-free and uniform relative to the antimicrobial coating formed using the metered rolling technique.

[0108] Example 2: Antimicrobial Testing

[0109] Several experiments were conducted using the Japanese Industrial Standard ("JIS") Method Z2801 antimicrobial evaluation method to illustrate the antimicrobial activity of the coated metal sheets described in Example 1 using the reverse rolling process. JIS Method Z2801 is a quantitative test designed to evaluate the performance of antimicrobial agents on hard, non-porous surfaces. The method can be performed with contact times ranging from 10 minutes up to 24 hours. For the JIS Z2801 test, a non-antimicrobial control surface is used as a benchmark for calculating microbial reduction. This method can be used to determine the antimicrobial activity of a variety of surface arrays including plastics, metals, and ceramics. The test microorganisms selected for this test were Escherichia coli 8739 (Gram-negative bacteria) and Staphylococcus aureus 6538 (Gram-positive bacteria).

[0110] Test Method

[0111] The test microorganisms were prepared by growing in tryptic soy broth. Suspensions of the test microorganisms were standardized by dilution in nutrient broth (this gave the microorganisms a chance to proliferate during the test). Controls and test substances were wiped clean with 70% ethanol and allowed to dry prior to testing. The microorganisms (where the test parameters were 0.400 mL and a concentration of 4 × 10 5 CFU / carrier) to control and test surfaces (50 mm x 50 mm), and then the microbial inoculum was covered with a thin sterile film (40 mm x 40 mm). Covering the inoculum spreads the inoculum, prevents evaporation, and ensures intimate contact with the antimicrobial surface. The microbial concentration was determined at "time 0" by rinsing followed by dilution and plating onto tryptic soy agar. Controls were performed to verify that the neutralization / rinsing method effectively neutralizes the antimicrobial in the tested antimicrobial surface. The inoculated, covered control and antimicrobial test surfaces were incubated undisturbed at 36°C ± 1°C for 24 hours in a humid environment. After incubation, the microbial concentration was determined. The reduction of microorganisms relative to the control surface was calculated. The neutralizer was D / E broth (10 mL). The counting plate medium was tryptic soy agar. The counting plates were incubated at 36°C ± 1°C for 24 ± 6 hours.

[0112] The result is calculated using the following formula:

[0113]

[0114] Where B = number of viable test microorganisms on the control carrier after the contact time; and A = number of viable test microorganisms on the test carrier after the contact time.

[0115]

[0116] Where B = number of viable test microorganisms on the control carrier after the contact time; and A = number of viable test microorganisms on the test carrier after the contact time.

[0117] E. coli test results

[0118] Table 1.

[0119]

[0120] The data collected using E. coli on a 50 mm x 50 mm carrier covered by a 40 mm x 40 mm membrane are shown in Table 1 . Figure 5 A graph of the E. coli CFU / carrier plotted against the control and experimental samples is shown. The detection limit for this study was 5 CFU / carrier. Values ​​less than the detection limit are shown as <5.00E+00 on the table and as zero on the graph.

[0121] Test results for Staphylococcus aureus

[0122] Table 2.

[0123]

[0124]

[0125] The data collected using S. aureus on a 50 mm x 50 mm carrier covered by a 40 mm x 40 mm membrane are shown in Table 2. Figure 6 A graph of S. aureus CFU / carrier plotted against control and experimental samples is shown. The limit of detection for this study was 5 CFU / carrier. Values ​​less than the limit of detection are shown as <5.00E+00 on the table and zero on the graph.

[0126] Example 3: Antimicrobial Testing

[0127] Below is an experiment conducted using the Sciessent LLC antimicrobial evaluation method to show the antimicrobial activity of metal sheets (2" x 2") coated using the reverse rolling process described in Example 1. Certain samples were abraded prior to testing. The bacteria used were E. coli and Staphylococcus aureus.

[0128] Table 3. Escherichia coli (ATCC#:25922) test

[0129]

[0130] Tested in accordance with Sciessent LLC's standard operating procedures

[0131] *≤10 = detection limit; ** is the percentage reduction calculated using: contact time of untreated T24.

[0132] Table 4. Staphylococcus aureus (ATCC#:6538) test

[0133]

[0134] Tested in accordance with Sciessent LLC's standard operating procedures

[0135] *≤10 = detection limit; ** is the percentage reduction calculated using: contact time of untreated T24

[0136] Example 4: Application of protective film on coated sheet

[0137] The protective film coating was applied to a portion of a metal sheet coated using the reverse rolling process described in Example 1. In one experiment, a rubber adhesive (with Fig. 10A In a second experiment, the coated sheets were sprayed with acrylic and / or silicone rubber adhesive (with Fig. 10B ). Shortly after application of each adhesive, a film protective layer was applied to the adhesive on the coated sheets. After 24 hours, the protective film was removed. After removal of the protective film, residues were found on the coated sheets using the rubber adhesive. After washing several times with ethanol, the residues still remained on the coated surface (see Fig. 10A No such residue was found on sheets coated with acrylic and / or silicone rubber adhesives ( Fig. 10B ).

Claims

1. A trash can, comprising: a metal body shaped to provide at least a portion of a receptacle configured to receive trash; wherein the surface of the metal body comprises a coating deposited directly on the surface of the metal body and the coating is configured to adhere to the surface of the metal body, the coating comprises a substrate comprising polyethylene, wherein an antimicrobial agent is dispersed within the substrate, wherein the coating has a thickness of 20 μm to 50 μm on the metal body, and the amount of the antimicrobial agent in the coating is less than 2.0% by weight; The antibacterial agent comprises a sub-support having an average particle size of 1 μm to 10 μm and one or more antibacterial metal ions, wherein the one or more antibacterial metal ions comprise 2 wt % to 5 wt % of silver ions or 4 wt % to 7 wt % of copper ions; wherein the coating is smooth and substantially free of streaks; wherein the coating is directly applied to the metal sheet for forming the metal body by applying a stirred and uniform slurry including a hydrophilic solvent, polyethylene and the antimicrobial agent directly to the metal sheet using a reverse rolling device, and then drying to form a coated sheet; wherein the coated sheet is shaped to form the metal body; wherein at least a portion of the antimicrobial agent is exposed on an outer surface of the coating and is capable of directly contacting microorganisms on the surface of the coating without polishing; Wherein the coating is fingerprint resistant and substantially resistant to transfer of water-based materials and resists visible transfer of residues after physical interaction with a user.

2. The trash can of claim 1, wherein the substantially streak-free coating is substantially flat.

3. The trash can according to claim 1 or 2, wherein the anti-fingerprint material allows fingerprints to be wiped off without using liquid solutions.

4. The trash can of any one of claims 1 to 3, wherein 24 hours after the initial bacterial exposure to the coating, the amount of bacteria remaining on the coating is reduced by at least about 95% compared to the initial bacterial exposure.

5. The trash can according to any one of claims 1 to 4, wherein the coating reduces the amount of E. coli from about 2.3×10 per 50 mm×50 mm carrier to about 1.5×10 per 50 mm×50 mm carrier within a period of about 24 hours. 5 The colony forming units (CFU) were reduced to less than about 5 CFU / carrier.

6. The trash can according to any one of claims 1 to 5, wherein the coating reduces the amount of Staphylococcus aureus from about 3.85×10 per 50 mm×50 mm carrier to about 1.5×10 per 50 mm×50 mm carrier within a period of about 24 hours. 5 The CFU was reduced to less than about 5 CFU / carrier.

7. A coating for household products, comprising: a polymeric substrate comprising polyethylene and configured to be directly adhered to a surface of the household item; an antimicrobial agent dispersed in the substrate, wherein the coating has a thickness of 20 μm to 50 μm on the metal body, and the amount of the antimicrobial agent in the coating is less than 2.0% by weight; The antibacterial agent comprises a sub-support having an average particle size of 1 μm to 10 μm and one or more antibacterial metal ions, wherein the one or more antibacterial metal ions comprise 2 wt % to 5 wt % of silver ions or 4 wt % to 7 wt % of copper ions; wherein the coating is smooth and substantially free of streaks; wherein the coating is applied directly to the metal sheet for forming the household product by applying a stirred uniform slurry comprising a hydrophilic solvent, polyethylene and the antimicrobial agent directly to the metal sheet using a reverse rolling device, followed by drying to form a coated sheet; wherein said coated sheet is shaped to form said household product; wherein at least a portion of the antimicrobial agent is exposed on an outer surface of the coating and is capable of directly contacting microorganisms on the surface of the coating without polishing; Wherein the coating is fingerprint resistant and substantially resistant to transfer of water-based materials and resists visible transfer of residues after physical interaction with a user.

8. The coating of claim 7, wherein the amount of the antimicrobial agent in the coating ranges from about 0.1 wt% to about 1.5 wt%.

9. The coating according to claim 7 or 8, wherein the amount of the antimicrobial agent in the coating ranges from about 1.1 wt% to about 1.2 wt%.

10. A coating according to any one of claims 7 to 9, wherein the polymer substrate comprises a material which resists fingerprints and smudges or makes it easier to wipe away fingerprints and smudges.

11. A coating according to any one of claims 7 to 10, wherein the coating is sufficiently durable that it can withstand repeated cleaning or washing without losing its antimicrobial properties.

12. A metal sheet comprising: A coating layer, which is directly deposited on the surface of the metal sheet, comprises a polymer substrate comprising polyethylene, and an antimicrobial agent is dispersed on or inside the substrate, wherein the coating layer has a thickness of 20 μm to 50 μm on the metal body, and the amount of the antimicrobial agent in the coating layer is less than 2.0% by weight; a protective film that protects the coating from abrasion during shipping of the metal sheet; as well as one or more acrylic adhesives or silicone rubber adhesives that adhere the protective film to the coating and leave substantially no residue on the coating after the protective film is removed; The antibacterial agent comprises a sub-support having an average particle size of 1 μm to 10 μm and one or more antibacterial metal ions, wherein the one or more antibacterial metal ions comprise 2 wt % to 5 wt % of silver ions or 4 wt % to 7 wt % of copper ions; wherein the coating is smooth and substantially free of streaks; wherein the coating is applied directly to the metal sheet by applying a stirred uniform slurry comprising a hydrophilic solvent, polyethylene and the antimicrobial agent directly to the metal sheet using a reverse rolling device, and then drying to form a coated sheet; wherein the coated sheet is capable of being shaped to form a metal body; wherein at least a portion of the antimicrobial agent is exposed on an outer surface of the coating and is capable of directly contacting microorganisms on the surface of the coating without polishing; Wherein the coating is fingerprint resistant and substantially resistant to transfer of water-based materials and resists visible transfer of residues after physical interaction with a user.

13. A method for manufacturing a metal sheet having an antimicrobial coating, the method comprising: Provide metal sheets; dispersing an antimicrobial agent and a polymer base comprising polyethylene in a solvent; Applying the stirred slurry directly to the metal sheet using a reverse rolling device; Drying the stirred slurry directly on the metal sheet to provide an antibacterial coating, wherein the antibacterial coating has a thickness of 20 μm to 50 μm on the metal body, and the amount of the antibacterial agent in the coating is less than 2.0% by weight; The metal sheet is formed to provide a metal body; The antibacterial agent comprises a sub-support having an average particle size of 1 μm to 10 μm and one or more antibacterial metal ions, wherein the one or more antibacterial metal ions comprise 2 wt % to 5 wt % of silver ions or 4 wt % to 7 wt % of copper ions; wherein said antimicrobial coating produced is substantially free of striations; wherein at least a portion of the antimicrobial agent is exposed on an outer surface of the coating and is capable of directly contacting microorganisms on the surface of the coating without polishing; Wherein the coating is fingerprint resistant and substantially resistant to transfer of water-based materials and resists visible transfer of residues after physical interaction with a user.

14. A method according to claim 13, wherein the metal sheet is shaped to provide part of a surface of a household item.

15. The trash can of any one of claims 1-6, wherein the sub-support comprises zeolite.

16. The trash can of any one of claims 1-6 or 15, wherein the zeolite comprises one or more antimicrobial metal ions.

17. The trash can of any one of claims 1-6 or 15-16, wherein the zeolite comprises one or more antimicrobial metals or antimicrobial organic ions.

18. The trash can of any one of claims 1-6 or 15-17, wherein the zeolite comprises silver ions, copper ions, and ammonium.

19. The trash can of any one of claims 1-6 or 15-18, wherein the zeolite comprises water.

20. The trash can according to any one of claims 1-6 or 15-19, wherein the metal sheet is a stainless steel metal sheet.

21. The coating of any one of claims 7-11, wherein the metal sheet is a stainless steel metal sheet.

22. The metal sheet of claim 12, wherein the metal sheet is a stainless steel metal sheet.

23. The method of claim 13 or 14, wherein the metal sheet is a stainless steel metal sheet.