Manufacturing method of honeysuckle plasterboard

Abstract

The invention discloses a manufacturing method of a honeysuckle plasterboard, and relates to the field of plasterboard manufacturing, the manufacturing method of the honeysuckle plasterboard comprises the following steps: S1, a honeysuckle tea manufacturing step: firstly selecting tea leaves, then manufacturing the selected tea leaves into dry tea with the water content of 6% through a green tea manufacturing mode, and removing old leaves, broken leaves, leaf powder and impurities to obtain honeysuckle tea; compared with the prior art, the honeysuckle plasterboard has the advantages that the overall structure and the effect of a traditional plasterboard can be changed, meanwhile, in the using process of the whole honeysuckle plasterboard, the antibacterial and disease-resistant effects can be effectively achieved, the antibacterial characteristic of honeysuckle can be effectively utilized, the situation that bacteria and molds grow on the surface of the plasterboard can be reduced, and the service life of the plasterboard is prolonged. Meanwhile, the honeysuckle can be added into the gypsum board, the environment-friendly effect is achieved, meanwhile, the fragrance of the honeysuckle in the honeysuckle gypsum board can improve the taste of the gypsum board, and the honeysuckle gypsum board can be durable and smells pleasant in the long-time use process.

Description

Technical Field

[0001] The invention relates to the field of gypsum board production, in particular to a method for producing a honeysuckle gypsum board. Background Art

[0002] Gypsum board is a material made of building gypsum as the main raw material. It is a building material with light weight, high strength, thin thickness, easy processing, good sound insulation, heat insulation and fire resistance, and is one of the new lightweight boards that are currently being developed. Decorative gypsum board. Decorative gypsum board is a board with various patterns and decorations made of building gypsum as the main raw material and a small amount of fiber materials, such as gypsum printed board, perforated ceiling board, gypsum relief ceiling board, paper gypsum facing decorative board, etc. It is a new type of interior decoration material, suitable for medium and high-end decoration, with the characteristics of light weight, fire resistance, moisture resistance, easy processing, and simple installation. In particular, the new resin imitation facing waterproof gypsum board is covered with resin and the surface is imitation pattern. Its color pattern is realistic, novel and generous, the board has high strength, pollution resistance, and is easy to clean, and can be used to decorate the wall.

[0003] The overall structure and function of traditional gypsum board are relatively simple. During the use of the entire gypsum board, it cannot effectively play an antibacterial and anti-disease role, and cannot effectively utilize the antibacterial characteristics of honeysuckle to reduce the growth of bacteria and mold on the surface of the gypsum board. At the same time, it is impossible to add honeysuckle to the gypsum board to achieve environmental protection. At the same time, traditional gypsum boards have a strong smell of gypsum and an overall heavy odor. It is difficult to be durable and smell pleasant during long-term use.

[0004] Therefore, those skilled in the art provide a method for making a honeysuckle gypsum board to solve the problems raised in the above background technology. Summary of the invention

[0005] The purpose of the present invention is to provide a method for preparing a honeysuckle gypsum board to solve the problems proposed in the above background technology that the overall structure and function of the traditional gypsum board are relatively simple, the entire gypsum board cannot effectively play an antibacterial and anti-disease role during use, and the antibacterial characteristics of honeysuckle cannot be effectively utilized to reduce the growth of bacteria and mold on the surface of the gypsum board. At the same time, it is impossible to add honeysuckle to the gypsum board to achieve environmental protection. At the same time, traditional gypsum boards have a strong gypsum smell and a heavy overall odor. During long-term use, it is difficult to achieve durability and a pleasant smell.

[0006] To achieve the above object, the present invention provides the following technical solutions: A method for making a honeysuckle gypsum board, comprising the following steps: S1: The production steps of honeysuckle tea are as follows: first, tea leaves are selected, and then dry tea is made through the production method of green tea, with a moisture content of 6%, old leaves, broken leaves, leaf ends and impurities are removed, and honeysuckle is harvested at the same time, and honeysuckle between May and July can be fully selected, and the flowers that have been opened are harvested, and then the dry tea and fresh honeysuckle are placed together, and then spread in layers, each time at intervals of 3 hours, and then the honeysuckle is taken out, the dry tea is stirred, and finally the fresh honeysuckle is taken out, and then exposed to the sun, after the fresh honeysuckle is fully dried, the dried fresh honeysuckle is crushed, and then mixed in a ratio of 1:12 between honeysuckle and dry tea to make honeysuckle tea; S2: the preparation step of honeysuckle tea, mixing the prepared honeysuckle tea with water, taking out 1 gram of honeysuckle tea, and then adding 50 milliliters of water to prepare a portion of honeysuckle tea, which can be set to a certain number, and the water temperature can be selected to be 90° hot water; S3: The steps of making the honeysuckle gypsum board are as follows: first, the raw materials of the gypsum board are selected, and honeysuckle tea, retarder solution and gypsum powder are selected, and the ratio of honeysuckle tea to gypsum powder is 7:10, and then appropriate amounts of starch and foaming agent are added. When making, the mass retarder solution, honeysuckle tea and gypsum powder are uniformly stirred and mixed into a slurry by a mixer, and the gypsum slurry is uniformly sprinkled on the face paper after being fully stirred by the mixer, and then poured into a flat plate to form a flat slab, and then the flat plate is pulled out to form; S4: The step of drying the slab is to put the slab into a plastic compression molding machine for compression, take out the slab and place it at room temperature for 16 hours under pressure to allow the gypsum to fully hydrate. After the initial gypsum board has completed the initial and final setting, the slab is finally dried in a drying room equipped with an electric blast drying oven. After leaving the drying room, the production process of the honeysuckle gypsum board is completed. As a preferred embodiment of the present invention: in the production step of the honeysuckle tea, when selecting tea leaves, fresh tea leaves with one bud and one leaf or one bud and two leaves can be selected, and the honeysuckle is harvested before 9 am, and the dry tea and fresh honeysuckle are placed together and spread out in multiple layers, so that the dry tea can fully absorb the smell of the fresh honeysuckle.

[0007] As a preferred embodiment of the present invention: in the production step of the honeysuckle gypsum board, the mass fraction of the retarder solution is 1%, the gypsum powder is hemihydrate gypsum, and the mass of the retarder solution accounts for 0.05% of the mass of the gypsum powder.

[0008] As a preferred embodiment of the present invention: in the step of drying the slab, the setting pressure of the plastic compression molding machine is 0.25 MPa, the pressurization time is 20 min, and the drying temperature in the electric blast drying oven is set to 35°C.

[0009] Compared with the prior art, the present invention has the following beneficial effects: The method for making a honeysuckle gypsum board of the present invention can change the overall structure and relatively simple functions of a traditional gypsum board. At the same time, the entire honeysuckle gypsum board can effectively play an antibacterial and disease-resistant role during use, and can effectively utilize the antibacterial characteristics of honeysuckle to reduce the growth of bacteria and mold on the surface of the gypsum board. At the same time, by adding honeysuckle to the gypsum board, it can play an environmental protection role. At the same time, the fragrance of honeysuckle in the honeysuckle gypsum board can improve the taste of the gypsum board. The honeysuckle gypsum board can be durable and have a pleasant smell during long-term use. DETAILED DESCRIPTION

[0010] In an embodiment of the present invention, a method for making a honeysuckle gypsum board includes the following steps: S1: The production steps of honeysuckle tea are as follows: first, tea leaves are selected, and then dry tea is made through the production method of green tea, with a moisture content of 6%, old leaves, broken leaves, leaf ends and impurities are removed, and honeysuckle is harvested at the same time, and honeysuckle between May and July can be fully selected, and the flowers that have been opened are harvested, and then the dry tea and fresh honeysuckle are placed together, and then spread in layers, each time at intervals of 3 hours, and then the honeysuckle is taken out, the dry tea is stirred, and finally the fresh honeysuckle is taken out, and then exposed to the sun, after the fresh honeysuckle is fully dried, the dried fresh honeysuckle is crushed, and then mixed in a ratio of 1:12 between honeysuckle and dry tea to make honeysuckle tea; S2: the preparation step of honeysuckle tea, mixing the prepared honeysuckle tea with water, taking out 1 gram of honeysuckle tea, and then adding 50 milliliters of water to prepare a portion of honeysuckle tea, which can be set to a certain number, and the water temperature can be selected to be 90° hot water; S3: The steps of making the honeysuckle gypsum board are as follows: first, the raw materials of the gypsum board are selected, and honeysuckle tea, retarder solution and gypsum powder are selected, and the ratio of honeysuckle tea to gypsum powder is 7:10, and then appropriate amounts of starch and foaming agent are added. When making, the mass retarder solution, honeysuckle tea and gypsum powder are uniformly stirred and mixed into a slurry by a mixer, and the gypsum slurry is uniformly sprinkled on the face paper after being fully stirred by the mixer, and then poured into a flat plate to form a flat slab, and then the flat plate is pulled out to form; S4: The step of drying the slab is to put the slab into a plastic compression molding machine for compression, take out the slab and place it at room temperature for 16 hours under pressure to allow the gypsum to fully hydrate. After the initial gypsum board has completed the initial and final setting, the slab is finally dried in a drying room equipped with an electric blast drying oven. After leaving the drying room, the production process of the honeysuckle gypsum board is completed. It can change the overall structure and relatively simple functions of traditional gypsum board. At the same time, the entire honeysuckle gypsum board can effectively play an antibacterial and anti-disease role during use. It can effectively utilize the antibacterial characteristics of honeysuckle to reduce the growth of bacteria and mold on the surface of the gypsum board.

[0011] In the production steps of honeysuckle tea, when selecting tea leaves, fresh tea leaves with one bud and one leaf or one bud and two leaves can be selected, and the honeysuckle should be harvested before 9 am. The dry tea and fresh honeysuckle are placed together and spread out in multiple layers so that the dry tea can fully absorb the smell of the new honeysuckle. In the production steps of honeysuckle gypsum board, the mass fraction of the retarder solution is 1%, and the gypsum powder is semi-hydrated gypsum, and the mass of the retarder solution accounts for 0.05% of the mass of the gypsum powder. In the drying step of the slab, the setting pressure of the plastic molding machine is 0.25MPa, the pressurization time is 20min, and the drying temperature in the electric blast drying oven is set to 35℃.

[0012] At the same time, adding honeysuckle to the gypsum board can play an environmental protection role. At the same time, the fragrance of honeysuckle in the honeysuckle gypsum board can improve the taste of the gypsum board. The honeysuckle gypsum board can be durable and smell pleasant after long-term use.

[0013] The working principle of the present invention is: a method for making a honeysuckle gypsum board comprises the following steps: S1: The production steps of honeysuckle tea are as follows: first, tea leaves are selected, and then dry tea is made through the production method of green tea, with a moisture content of 6%, old leaves, broken leaves, leaf ends and impurities are removed, and honeysuckle is harvested at the same time, and honeysuckle between May and July can be fully selected, and the flowers that have been opened are harvested, and then the dry tea and fresh honeysuckle are placed together, and then spread in layers, each time at intervals of 3 hours, and then the honeysuckle is taken out, the dry tea is stirred, and finally the fresh honeysuckle is taken out, and then exposed to the sun, after the fresh honeysuckle is fully dried, the dried fresh honeysuckle is crushed, and then mixed in a ratio of 1:12 between honeysuckle and dry tea to make honeysuckle tea; in the production steps of honeysuckle tea, when selecting tea leaves, fresh tea leaves with one bud and one leaf and one bud and two leaves can be selected, and the harvesting time of honeysuckle is before 9 am, the dry tea and the fresh honeysuckle are placed together, and spread in layers for multiple times, so that the dry tea can fully absorb the smell of the new honeysuckle. S2: the preparation step of honeysuckle tea, mixing the prepared honeysuckle tea with water, taking out 1 gram of honeysuckle tea, and then adding 50 milliliters of water to prepare a portion of honeysuckle tea, which can be set to a certain number, and the water temperature can be selected to be 90° hot water; S3: The production steps of honeysuckle gypsum board are as follows: first, the raw materials of the gypsum board are selected, and honeysuckle tea, retarder solution and gypsum powder are selected, and the ratio of honeysuckle tea to gypsum powder is 7:10, and then an appropriate amount of starch and foaming agent are added. During the production, the mass retarder solution, honeysuckle tea and gypsum powder are uniformly stirred into a slurry by a mixer, and the gypsum slurry is evenly sprinkled on the face paper after being fully stirred by the mixer, and then poured into a flat plate to form a flat slab, and then the flat plate is pulled out to form; in the production steps of the honeysuckle gypsum board, the mass fraction of the retarder solution is 1%, and the gypsum powder is semi-hydrated gypsum, and the mass of the retarder solution accounts for 0.05% of the mass of the gypsum powder. S4: The slab is dried in a plastic compression molding machine, and the slab is taken out and placed at room temperature for 16 hours under pressure to fully hydrate the gypsum. After the initial gypsum board is initially and finally set, the slab is dried in a drying room, which is equipped with an electric blast drying oven. After leaving the drying room, the production process of the honeysuckle gypsum board is completed. In the slab drying step, the plastic compression molding machine is set to a pressure of 0.25MPa, the pressurization time is 20min, and the drying temperature in the electric blast drying oven is set to 35°C. It can change the overall structure and relatively simple function of the traditional gypsum board. At the same time, the entire honeysuckle gypsum board can effectively play an antibacterial and anti-disease role during use. It can effectively utilize the antibacterial characteristics of honeysuckle to reduce the growth of bacteria and mold on the surface of the gypsum board. At the same time, by adding honeysuckle to the gypsum board, it can play an environmental protection role. At the same time, the fragrance of honeysuckle in the honeysuckle gypsum board can improve the taste of the gypsum board. The honeysuckle gypsum board can be durable and pleasant in long-term use.

[0014] What is described above is only a preferred specific implementation manner of the present invention, but the protection scope of the present invention is not limited thereto. Any technician familiar with the technical field can make equivalent replacements or changes according to the technical scheme and inventive concept of the present invention within the technical scope disclosed by the present invention, which should be covered by the protection scope of the present invention.

Claims

1. A method for making a honeysuckle gypsum board, characterized in that: The method for making a honeysuckle gypsum board comprises the following steps: S1: The production steps of honeysuckle tea are as follows: first, tea leaves are selected, and then dry tea is made through the production method of green tea, with a moisture content of 6%, old leaves, broken leaves, leaf ends and impurities are removed, and honeysuckle is harvested at the same time, and honeysuckle between May and July can be fully selected, and the flowers that have been opened are harvested, and then the dry tea and fresh honeysuckle are placed together, and then spread in layers, each time at intervals of 3 hours, and then the honeysuckle is taken out, the dry tea is stirred, and finally the fresh honeysuckle is taken out, and then exposed to the sun, after the fresh honeysuckle is fully dried, the dried fresh honeysuckle is crushed, and then mixed in a ratio of 1:12 between honeysuckle and dry tea to make honeysuckle tea; S2: the preparation step of honeysuckle tea, mixing the prepared honeysuckle tea with water, taking out 1 gram of honeysuckle tea, and then adding 50 milliliters of water to prepare a portion of honeysuckle tea, which can be set to a certain number, and the water temperature can be selected to be 90° hot water; S3: The steps of making the honeysuckle gypsum board are as follows: first, the raw materials of the gypsum board are selected, and honeysuckle tea, retarder solution and gypsum powder are selected, and the ratio of honeysuckle tea to gypsum powder is 7:10, and then appropriate amounts of starch and foaming agent are added. When making, the mass retarder solution, honeysuckle tea and gypsum powder are uniformly stirred and mixed into a slurry by a mixer, and the gypsum slurry is uniformly sprinkled on the face paper after being fully stirred by the mixer, and then poured into a flat plate to form a flat slab, and then the flat plate is pulled out to form; S4: The step of drying the slab is to put the slab into a plastic compression molding machine for compression, take out the slab and place it at room temperature for 16 hours under pressure to allow the gypsum to fully hydrate. After the initial gypsum board has completed the initial and final setting, the slab is finally dried in a drying room equipped with an electric blast drying oven. After leaving the drying room, the production process of the honeysuckle gypsum board is completed.

2. The method for making a honeysuckle gypsum board according to claim 1, characterized in that: In the production steps of the honeysuckle tea, when selecting tea leaves, fresh tea leaves with one bud and one leaf or one bud and two leaves can be selected, and the honeysuckle is harvested before 9 am. The dry tea and fresh honeysuckle are placed together and spread out in multiple layers so that the dry tea can fully absorb the smell of the new honeysuckle.

3. The method for making a honeysuckle gypsum board according to claim 1, characterized in that: In the manufacturing steps of the gypsum board, the mass fraction of the retarder solution is 1%, the gypsum powder is semi-hydrated gypsum, and the mass of the retarder solution accounts for 0.05% of the mass of the gypsum powder.

4. The method for making a honeysuckle gypsum board according to claim 1, characterized in that: In the drying step of the slab, the setting pressure of the plastic compression molding machine is 0.25 MPa, the pressurization time is 20 minutes, and the drying temperature in the electric blast drying oven is set to 35°C.