Bath towel, bath towel cloth and preparation method of bath towel cloth

Abstract

The invention provides a preparation method of bath towel cloth, which comprises the following steps: 1) taking viscose rayon, sizing and drying the viscose rayon, and using the viscose rayon as warp; 2, viscose rayon is taken, every 2-6 pieces of viscose rayon are twisted in a reinforced mode, then silk steaming and shaping are conducted, one part of viscose rayon is used as first weft yarn according to the left twisting position, and the other part of viscose rayon is used as second weft yarn according to the right twisting position; 3) taking polyester copper fibers, carrying out reinforced twisting on every 2-6 polyester copper fibers, then carrying out silk steaming and shaping, taking one part as a third weft according to a left twisting position, and taking the other part as a fourth weft according to a right twisting position; 4) performing warp knitting on the warp and the first weft and the fourth weft or the second weft and the third weft to obtain a white body; 5, the white body is subjected to sand washing, dyeing, drying and shaping, and the bath towel cloth is obtained.The viscose rayon and the polyester copper fibers used for preparing the bath towel cloth are subjected to specific pretreatment, spinning is conducted according to a specific weaving method, and the bath towel cloth and the bath towel with the sterilization and bacteriostasis effects can be obtained.

Description

Technical Field

[0001] The invention relates to the technical field of textiles, in particular to a bath towel, a bath towel cloth and a preparation method thereof. Background Art

[0002] Bath towels are generally made of chemical fiber products with a rough surface texture into a capsule shape, which allows people to insert their hands into the bath towel when taking a bath, rub them on the body, and achieve the purpose of decontamination and cleaning.

[0003] Bath towels are generally made from viscose rayon. Polyester copper-based fiber is a new antibacterial textile fiber that has emerged in recent years. During the melt spinning process, copper oxide powder is dispersed in the melt to obtain fibers containing copper oxide particles. This fiber combines the inhibitory effect of copper on bacteria, viruses and fungi, and has good antibacterial and antiviral effects. Since copper can stimulate the regeneration of collagen in the skin, copper-based antibacterial fibers can promote skin metabolism after contact with the skin, making healthy skin smoother and damaged skin heal faster. It has high application value in the fields of functional medical dressings and antibacterial textiles.

[0004] However, among the prior art that can be retrieved, copper fiber is generally used to produce towel-type antibacterial products, and there is no method for preparing bath towel cloth. When preparing bath towel cloth with polyester copper fiber, the biggest technical difficulty is how to weave polyester copper fiber and viscose rayon. The properties of polyester copper fiber and viscose rayon are very different, and the bath towel cloth cannot be shaped after weaving according to the traditional process. In addition, the use of bath towel cloth requires it to have a certain degree of astringency and cannot damage the skin when used, and at the same time, it has high requirements for wear resistance. Polyester copper fiber is not easy to shape, and it is easy to pilling, and its strength and wear resistance are poor. The method used to prepare towel products cannot be used to prepare copper fiber bath towel cloth with antibacterial effect. Summary of the invention

[0005] In order to solve the above problems, the present invention provides a bath towel, a bath towel cloth and a preparation method thereof, and the specific technical scheme is: A method for preparing a bath towel comprises the following steps: 1) Take viscose rayon, starch it, dry it and use it as warp; 2) Take viscose rayon, twist every 2-6 strands, and then steam the yarn to set the yarn. The twist is carried out at a twist of 1600-2800 per meter. A part of the yarn is twisted in the left twist position as the first weft, and a part of the yarn is twisted in the right twist position as the second weft. The temperature of steaming and setting the yarn is 70-100℃; 3) Take polyester copper fiber, strengthen twist every 2-6 strands, and then steam and shape it, wherein the strengthening twist is implemented at a twist of 1600-2800 per meter, and a part of it is used as the third weft by strengthening twist in the left twist position, and a part of it is used as the fourth weft by strengthening twist in the right twist position, and the temperature of steaming and shaping is 70-100℃; 4) warp knitting the warp thread, the first weft thread and the fourth weft thread, or warp knitting the warp thread, the second weft thread and the third weft thread, and then obtaining a blank; 5) The white blank obtained in step 4) is sand washed, dyed, dried and shaped to obtain a bath towel cloth.

[0006] Furthermore, in step 1), the viscose rayon is 150D-450D viscose rayon.

[0007] Furthermore, in step 2), the viscose rayon is 150D-450D viscose rayon.

[0008] Furthermore, the polyester copper fiber in step 3) is 40-10 polyester copper fiber.

[0009] Furthermore, in step 4), the number of the first latitude lines is the same as the number of the fourth latitude lines, and the number of the second latitude lines is the same as the number of the third latitude lines.

[0010] The present invention also claims protection for the bath towel obtained by the above preparation method.

[0011] The present invention also claims a bath towel comprising the bath towel cloth.

[0012] The present invention performs specific pretreatment on viscose rayon and polyester copper fiber used for preparing bath towel cloth, and weaves them according to a specific weaving method, so as to obtain a bath towel cloth with bactericidal and antibacterial effects, whose surface astringency is appropriate, and after the polyester copper fiber is twisted to a specific degree, the surface is smooth, does not damage the skin when used, and can improve its wear resistance.

[0013] The technical key points of the present invention are the twist and setting temperature of the polyester copper fiber during pretreatment, the twist and setting temperature of the viscose rayon used as the first weft and the fourth weft, the second weft and the third weft during pretreatment, and the weaving method of the polyester copper fiber and the viscose rayon.

[0014] The combination of the above schemes is the basis for achieving the purpose of the present invention. By relying on the combination of the above schemes, a polyester copper fiber bath towel cloth with good durability, certain astringency and no damage to the skin can be prepared. DETAILED DESCRIPTION

[0015] The following will be combined with the embodiments of the present invention to clearly and completely describe the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only part of the embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by ordinary technicians in this field without creative work, any modifications, equivalent substitutions, improvements, etc., should be included in the protection scope of the present invention.

[0016] Example 1 A method for preparing a bath towel comprises the following steps: 1) Take 150D viscose rayon, starch it, dry it and use it as the warp; 2) Take 150D viscose rayon, twist every 2 strands, and then steam the yarn to set the yarn. The twist is 1600 twists per meter, and the temperature of steaming and setting the yarn is 70℃. The left twist is used as the first weft. 3) Take 40-count polyester copper fibers, twist every 2 strands, and then steam them to set the shape. The twist is implemented at a twist of 1600 per meter, and the temperature of steaming and setting is 70°C. Twist them at the right twist position to use as the fourth weft. 4) warp-knitting the warp threads, the first weft thread, and the fourth weft thread to obtain a blank; 5) The white blank obtained in step 4) is sand washed, dyed, dried and shaped to obtain a bath towel cloth.

[0017] After testing, it was found that the bath towel cloth obtained by the above method is of low astringency, suitable for the elderly, children and people with sensitive skin, and has good durability and shaping effect, and improved antibacterial properties.

[0018] Example 2 A method for preparing a bath towel comprises the following steps: 1) Take 450D viscose rayon, starch it, dry it and use it as the warp; 2) Take 450D viscose rayon, twist every 6 strands, and then steam the yarn to set the yarn. The twist is 2800 twists per meter, and the temperature of steaming and setting the yarn is 100℃. The right twist is used as the second weft. 3) Take 40-count polyester copper fibers, twist every 6 strands, and then steam them to set the shape. The twist is strengthened at a twist of 2800 per meter, and the temperature of steaming and setting is 100°C. The left twist is strengthened and used as the third weft. 4) knitting the warp thread, the second weft thread, and the third weft thread to obtain a blank; 5) The white blank obtained in step 4) is sand washed, dyed, dried and shaped to obtain a bath towel cloth.

[0019] After testing, the bath towel cloth obtained by the above method is of medium astringency, suitable for ordinary adults, and has good durability and shaping effect, and improved antibacterial properties.

[0020] Example 3 A method for preparing a bath towel comprises the following steps: 1) Take 300D viscose rayon, starch it, dry it and use it as the warp; 2) Take 300D viscose rayon, twist every 4 strands, and then steam the yarn to set the yarn. The twist is 1600 twists per meter, and the temperature of steaming and setting the yarn is 85℃. The left twist is used as the first weft. 3) Take 40-count polyester copper fibers, twist every 4 strands, and then steam them to set the shape. The twist is implemented at a twist of 1600 per meter, and the temperature of steaming and setting is 85°C. Twist them at the right twist position to use as the fourth weft. 4) warp-knitting the warp threads, the first weft thread, and the fourth weft thread to obtain a blank; 5) The white blank obtained in step 4) is sand washed, dyed, dried and shaped to obtain a bath towel cloth.

[0021] After testing, it was found that the bath towel cloth obtained by the above method is of high astringency, suitable for manual laborers, and has good durability and shaping effect, and improved antibacterial properties.

[0022] Comparative Example 1 The difference between this comparative example and Example 1 is that polyester copper fiber is not added, and only steps 1) and 2) are used to weave a blank, and the other steps are the same as those in Example 1.

[0023] After testing, the bath towel cloth obtained by the above method has average antibacterial properties.

[0024] Comparative Example 2 The difference between this comparative example and Example 2 is that no polyester copper fiber is added, and only steps 1) and 2) are used to weave a blank, and the other steps are the same as those in Example 2.

[0025] After testing, the bath towel cloth obtained by the above method has average antibacterial properties.

[0026] Comparative Example 3 The difference between this comparative example and Example 3 is that no polyester copper fiber is added, and only steps 1) and 2) are used to weave a blank, and the other steps are the same as those in Example 3.

[0027] After testing, the bath towel cloth obtained by the above method has average antibacterial properties.

Claims

1. A method for preparing a bath towel, characterized in that: The following steps are involved: 1) Take viscose rayon, starch it, dry it and use it as warp; 2) Take viscose rayon, twist every 2-6 strands, and then steam the yarn to set the yarn. The twist is carried out at a twist of 1600-2800 per meter. A part of the yarn is twisted in the left twist position as the first weft, and a part of the yarn is twisted in the right twist position as the second weft. The temperature of steaming and setting the yarn is 70-100℃; 3) Take polyester copper fiber, strengthen twist every 2-6 strands, and then steam and shape it, wherein the strengthening twist is implemented at a twist of 1600-2800 per meter, and a part of it is used as the third weft by strengthening twist in the left twist position, and a part of it is used as the fourth weft by strengthening twist in the right twist position, and the temperature of steaming and shaping is 70-100℃; 4) warp knitting the warp thread, the first weft thread and the fourth weft thread, or warp knitting the warp thread, the second weft thread and the third weft thread, and then obtaining a blank; 5) The white blank obtained in step 4) is sand washed, dyed, dried and shaped to obtain a bath towel cloth.

2. The preparation method according to claim 1, characterized in that: Step 1) The viscose rayon is 150D-450D viscose rayon.

3. The preparation method according to claim 1, characterized in that: Step 2) The viscose rayon is 150D-450D viscose rayon.

4. The preparation method according to claim 1, characterized in that: The polyester copper fiber in step 3) is 40-10 polyester copper fiber.

5. The preparation method according to claim 1, characterized in that: In step 4), the number of the first latitude line is the same as the number of the fourth latitude line, and the number of the second latitude line is the same as the number of the third latitude line.

6. A bath towel, characterized in that: The bath towel is prepared by the preparation method described in any one of claims 1 to 5.

7. A bath towel, characterized in that: It also includes the bath towel cloth according to claim 6, wherein the bath towel cloth is arranged on a bath towel.