FIBER-REINFORCED RESIN MOLDED ARTICLE AND METHOD FOR MANUFACTURING SAME

Description

Technical Field

[0001] The present invention relates to a fiber-reinforced resin molding and a method for producing same.Background Art

[0002] A fiber-reinforced resin molding configured comprising FRP (Fiber Reinforced Plastic), which is a type of composite material, is known from the prior art (refer, for example, to JP 4615398 B).

[0003] JP 4615398 B discloses a carbon fiber composite material molding obtained by sandwiching a core layer of nonwoven fabric between two carbon fiber layers, which form skin layers, to form a stacked body, and impregnating the stacked body with an impregnating resin, followed by curing. JP H10-296866 A discloses a structure having a core layer and a pair of skin layers. The pair of skin layers has fibers and a matrix resin that covers the fibers. The skin layers join to both sides of the core layer. JP 2986564 B discloses a structure which has a core and a pair of skin layers. The core has syntactic foam and is sandwiched by a pair of sheets.Prior Art Documents Patent Documents Summary of the Invention Problem to be Solved by the Invention

[0004] In the carbon fiber composite material molding described above, the skin layers and the core layer are joined only by resin, and the joining force between the skin layers and the core layer is low; consequently, when a load is applied to the carbon fiber composite material molding, there is the possibility that the skin layers and the core layer between the layers will separate.

[0005] Thus, the object of the present invention is to prevent the skin layer from separating from the core layer by increasing the joining force between the skin layer and the core layer.Means of Achieving the Object

[0006] A first feature of the present invention is a fiber-reinforced resin molding comprising a core layer comprising a nonwoven fabric and impregnating resin that has been impregnated into the nonwoven fabric, and a pair of skin layers comprising fibers and a matrix resin that covers the fibers. The skin layers have recesses that are formed in the core layer side surfaces and in which some of the fibers in the matrix resin are exposed, and portions of the nonwoven fabric and the impregnating resin penetrate the recesses.

[0007] A second aspect of the present invention is a method for producing a fiber-reinforced resin molding. The production method includes a step for forming recesses in which some of the fibers in the matrix resin the skin layers are exposed to the core layer side surfaces, and a step for disposing a nonwoven fabric between a pair of the skin layers, causing portions of the nonwoven fabric and the impregnating resin to penetrate the recesses, and joining the skin layers and the core layer in that state.Effects of the Invention

[0008] According to the present invention, it is possible to prevent separation of the skin layers from the core layer by increasing the joining force between the skin layers and the core layer.Brief Description of the Drawings

[0009] [Figure 1] Figure 1 is an exploded perspective view of a fiber-reinforced resin molding according to an embodiment of the present invention. [Figure 2] Figure 2 is a cross-sectional view of the fiber-reinforced resin molding according to the embodiment of the present invention. [Figure 3A] Figure 3A is an explanatory view of a method for producing the fiber-reinforced resin molding according to the embodiment of the present invention. [Figure 3B] Figure 3B is an explanatory view of a method for producing the fiber-reinforced resin molding according to the embodiment of the present invention. [Figure 3C] Figure 3C is an explanatory view of a method for producing the fiber-reinforced resin molding according to the embodiment of the present invention. [Figure 3D] Figure 3D is an explanatory view of a method for producing the fiber-reinforced resin molding according to the embodiment of the present invention. [Figure 3E] Figure 3E is an explanatory view of a method for producing the fiber-reinforced resin molding according to the embodiment of the present invention. [Figure 4A] Figure 4A is an explanatory view of a method for producing the fiber-reinforced resin molding according to another embodiment of the present invention. [Figure 4B] Figure 4B is an explanatory view of a method for producing the fiber-reinforced resin molding according to another embodiment of the present invention. [Figure 4C] Figure 4C is an explanatory view of a method for producing the fiber-reinforced resin molding according to another embodiment of the present invention. [Figure 4D] Figure 4D is an explanatory view of a method for producing the fiber-reinforced resin molding according to another embodiment of the present invention. [Figure 4E] Figure 4E is an explanatory view of a method for producing the fiber-reinforced resin molding according to another embodiment of the present invention. Embodiments to Carry Out the Invention

[0010] An embodiment of the present invention will be described in detail below with reference to the drawings.

[0011] A fiber-reinforced resin molding 10 according to an embodiment of the present invention will now be described with reference to Figures 1 to 3.

[0012] The fiber-reinforced resin molding 10 can be applied, for example, to vehicle component members, such as a hood (bonnet), a bumper, a trunk lid, a rear gate, a fender panel, a side body panel, and a roof panel. In addition, the fiber-reinforced resin molding 10 is not limited to vehicle component members and can be applied to various types of component members.

[0013] The fiber-reinforced resin molding 10 comprises a core layer 11 and a pair of skin layers 12, 12 that are joined to both surfaces of the core layer 11, as illustrated in Figures 1 and 2.

[0014] The core layer 11 is a nonwoven fabric layer comprising a nonwoven fabric 13 and an impregnating resin 14 that has been impregnated in the nonwoven fabric 13. The thickness of the core layer 11 is, for example, about 0.2 mm-10.0 mm. The nonwoven fabric 13 is formed from known fibers, such as cotton, rayon, nylon, polyester, polypropylene, and aramid fibers. The impregnating resin 14 is formed from a thermosetting resin, such as epoxy resin, unsaturated polyester resin, vinyl ester resin, and phenol resin. In addition, the impregnating resin 14 may be formed from a thermoplastic resin, such as polyamide resin, polyolefin resin, dicyclopentadiene resin, and polyurethane resin.

[0015] The skin layers 12 are made up of a fiber layer comprising fibers 15 and a matrix resin 16 that covers the fibers 15. That is, the skin layers 12 are what is referred to as an FRP (fiber-reinforced resin). The thicknesses of the skin layers 12 are, for example, about 0.4 mm to 5.0 mm. The fibers 15 can be formed from various fibers, such as carbon fiber, glass fiber, and aramid fiber (Kevlar fiber). The matrix resin 16 can be formed from thermosetting resin, such as epoxy resin, unsaturated polyester resin, vinyl ester resin, and phenol resin. In addition, the matrix resin 16 can be formed from a thermoplastic resin, such as polyamide resin, polyolefin resin, dicyclopentadiene resin, and polyurethane resin.

[0016] The impregnating resin 14 of the core layer 11 and the matrix resin 16 of the skin layers 12 can be of the same or of different types. From the standpoint of enhancing the joining force between the core layer 11 and the skin layers 12, the impregnating resin 14 of the core layer 11 and the matrix resin 16 of the skin layers 12 are preferably resins that have high affinity.

[0017] The skin layers 12 have a plurality of recesses 18 formed on side surface 17 facing the core layer 11 such that portions of the fibers 15 in the matrix resin 16 are exposed. The matrix resin 16 of the skin layers 12 and the impregnating resin 14 of the core layer 11 are joined (bonded), in a state in which portions of the nonwoven fabric 13 and the impregnating resin 14 have penetrated the recesses 18. Thus, the fiber-reinforced resin molding 10 has a plurality of mixed regions 20 which is formed in the joint portion 19 between the core layer 11 and the skin layers 12 and in which the nonwoven fabric 13 and the fibers 15 are mixed.

[0018] The recesses 18 and the mixed regions 20 are arranged at intervals in the longitudinal direction and the lateral direction on the surfaces of the skin layers 12, as illustrated in Figure 1. In the figure, the recesses 18 and the mixed regions 20 are arranged at equal intervals, but no limitation is imposed thereby, and the intervals need not be equal.

[0019] In addition, the positions of the recesses 18 and the mixed regions 20 in the in-plane direction of the skin layers 12 (direction that is parallel to the surface) are asymmetrical relative to the core layer 11 between one and the other of the pair of skin layers 12, 12, as illustrated in Figure 2. That is, the recesses 18 and the mixed regions 20 are arranged in different locations between one and the other of the pair of skin layers 12, 12. However, no limitation is imposed thereby; the positions of the recesses 18 and the mixed regions 20 in the in-plane direction of the skin layer 12 can be symmetrical relative to the core layer 11 between one and the other of the pair of skin layers 12, 12.

[0020] Next, a method for producing the fiber-reinforced resin molding 10 according to the present embodiment will be described.1. Application of Wax

[0021] First, a wax 21 is applied to a sheet or a bundle of fiber 15, as illustrated in Figure 3A, in randomly distributed fashion and the applied wax 21 is cured and hardened.

[0022] Thermoplastic resins such as polyvinyl alcohol (PVA), polyethylene (PE), or polypropylene (PP), for example, may be used as the wax 21. Polyethylene and polypropylene have relatively low melting points; therefore, when polyethylene or polypropylene is used as the wax 21, it is necessary to set the injection temperature of the matrix resin 16 to be less than or equal to the melting points of polyethylene and polypropylene.2. Injection of Matrix Resin into the Mold

[0023] Next, the fibers 15 are placed in the mold and the matrix resin 16 is injected into the mold to impregnate the fibers 15 with the matrix resin 16, as illustrated in Figure 3B. Then, the impregnated matrix resin 16 is cured and hardened to prepare the skin layer 12.3. Removal of Wax

[0024] Next, the wax 21 is melted with warm water or a solvent to form recesses 18 on the skin layer 12, as illustrated in Figure 3C.

[0025] That is, in the present embodiment, the lost wax method is used to form the recesses 18 on the skin layer 12.4. Stacking

[0026] Next, the nonwoven fabric 13 is stacked between a pair of skin layers 12, 12 to prepare a stacked body 22, as illustrated in Figure 3D.5. Injection of Impregnating Resin into the MOLD

[0027] Next, the stacked body 22 is placed in a mold, impregnating resin 14 is injected into the mold, and the nonwoven fabric 13 is impregnated with the impregnating resin14, as illustrated in Figure 3E. In this step to inject the impregnating resin 14 into a mold, portions of the nonwoven fabric 13 and the impregnating resin 14 are made to penetrate each recess 18, and the fibers 15 that are exposed due to the removal of the wax 21 become entangled with the nonwoven fabric 13. Then, the impregnating resin 14 is cured and hardened to prepare a fiber-reinforced resin molding 10.

[0028] That is, in the present embodiment, the RTM molding (Resin Transfer Molding) method is used to mold the stacked body 22.

[0029] The action and effects of the present embodiment will be described below. (1) A fiber-reinforced resin molding 10 according to the present embodiment comprises a core layer 11 comprising a nonwoven fabric 13 and impregnating resin 14 that has been impregnated into the nonwoven fabric 13; and a pair of skin layers 12, 12 comprising fibers 15 and a matrix resin 16 that covers the fibers 15 and that are joined to both surfaces of the core layer (11). The skin layers 12 have recesses 18 that are formed on side surfaces 17 facing the core layer 11 such that a portion of the fibers 15 in the matrix resin 16 are exposed, and portions of the nonwoven fabric 13 and the impregnating resin 14 have penetrated the recesses 18.

[0030] In the fiber-reinforced resin molding 10 according to the present embodiment, the matrix resin 16 of the skin layer 12 and the impregnating resin 14 of the core layer 11 are joined in a state in which portions of the nonwoven fabric 13 and the impregnating resin 14 have penetrated the recesses 18. That is, mixed regions 20, in which the nonwoven fabric 13 and the fibers 15 are mixed, are formed in the joint portion 19 between the core layer 11 and the skin layer 12. Thus, it is possible to enhance the joining force between the skin layer 12 and the core layer 11 and to reduce the possibility that the skin layer 12 and the core layer 11 will separate between the layers, even if a load is applied to the fiber-reinforced resin molding 10.

[0031] Therefore, according to the fiber-reinforced resin molding 10 of the present embodiment, it is possible to prevent the skin layer 12 from separating from the core layer 11 by increasing the joining force between the skin layer 12 and the core layer 11.

[0032] (2) The positions of the recesses 18 in the in-plane direction of the skin layer 12 are asymmetrical relative to the core layer 11 between one and the other of the pair of skin layers 12, 12.

[0033] Thus, it is possible to shift the positions of the mixed regions 20, in which the nonwoven fabric 13 and the fibers 15 are mixed, in the in-plane direction of the skin layer 12 between one and the other of the pair of skin layers 12, 12, and to thereby prevent the generation of locations with low densities of the nonwoven fabric 13 in the core layer 11.

[0034] (3) The method for producing a fiber-reinforced resin molding 10 according to the present embodiment comprises a step (Step 1) for forming recesses 18 in which portions of the fibers 15 in the matrix resin 16 are exposed on side surfaces 17 of the skin layer 12 facing the core layer 11, and a step (Step 2) for disposing the nonwoven fabric 13 between the pair of skin layers 12, 12, causing some of the nonwoven fabric 13 and impregnating resin 14 to penetrate the recesses 18, and joining the skin layer 12 and the core layer 11 in that state.

[0035] As a result, the matrix resin 16 of the skin layer 12 and the impregnating resin 14 of the core layer 11 are joined in a state in which some of the nonwoven fabric 13 and the impregnating resin 14 have penetrated the recesses 18. That is, mixed regions 20, in which the nonwoven fabric 13 and the fibers 15 are mixed, are formed in the joint portion 19 between the core layer 11 and the skin layer 12. Thus, it is possible to enhance the joining force between the skin layer 12 and the core layer 11 and to reduce the possibility that the skin layer 12 and the core layer 11 will separate between the layers, even if a load is applied to the fiber-reinforced resin molding 10.

[0036] Therefore, according to the method for producing a fiber-reinforced resin molding 10 of the present embodiment, it is possible to prevent the skin layer 12 from separating from the core layer 11 by increasing the joining force between the skin layer 12 and the core layer 11.

[0037] (4) The recesses 18 are formed using a lost wax method.

[0038] Thus, it is possible to precisely form the recesses 18 on the skin layer 12.[Another Embodiment]

[0039] A method for producing a fiber-reinforced resin molding 10 according to another embodiment will be described with reference to Figure 4.1. Application of wax

[0040] First, wax 21 is applied to a sheet or a bundle of fibers 15, as illustrated in Figure 4A, in randomly distributed fashion and the applied wax 21 is cured and hardened.2. Injection of matrix resin into the mold

[0041] Next, the fibers 15 are placed in the mold and the matrix resin 16 is injected into the mold to impregnate the fibers 15 with the matrix resin 16, as illustrated in Figure 4B. The impregnated matrix resin 16 is then cured and hardened to prepare the skin layer 12.3. Removal of the wax

[0042] Next, the wax 21 is melted with warm water or a solvent to form recesses 18 on the skin layer 12, as illustrated in Figure 4C.4. Stacking

[0043] Next, a nonwoven fabric-containing adhesive (nonwoven fabric 13 that has been impregnated with impregnating resin 14 in advance) is stacked between a pair of skin layers 12, 12 to prepare a stacked body 23, as illustrated in Figure 4D.5. Forming the fiber-reinforced resin molding

[0044] Next, the stacked body 23 is placed in a mold, and a fiber-reinforced resin molding 10 is formed inside the mold, as illustrated in Figure 4E. In this step to form the fiber-reinforced resin molding 10 in a mold, portions of the nonwoven fabric 13 and the impregnating resin 14 are made to penetrate each recess 18, and the fibers 15 that are exposed due to the removal of the wax 21 become entangled with the nonwoven fabric 13. The impregnating resin 14 is cured and hardened to prepare a fiber-reinforced resin molding 10.

[0045] In this embodiment, a hot press molding method or an autoclave molding method may be used as the method for forming the fiber-reinforced resin molding 10.

[0046] By using such a method for producing a fiber-reinforced resin molding 10, it is possible to prevent the skin layer 12 from separating from the core layer 11 by increasing the joining force between the skin layer 12 and the core layer 11.Descriptions of the Reference Symbols

[0047] 10Fiber-reinforced resin molding 11Core layer 12Skin layer 13Nonwoven fabric 14Impregnating resin 15Fiber 16Matrix resin 17Core layer side surface 18Recess 19Joint portion 20Mixed region

Claims

1. A fiber-reinforced resin molding (10) comprising: a core layer (11) comprising a nonwoven fabric (13) and an impregnating resin (14) that has been impregnated in the nonwoven fabric (13); and a pair of skin layers (12) comprising fibers (15) and a matrix resin (16) that covers the fibers (15), and joined to both sides of the core layer (11); wherein the skin layers (12) have recesses (18) formed on a core layer side surface such that portions of the fibers (15) in the matrix resin (16) are exposed, and portions of the nonwoven fabric (13) and the impregnating resin (14) have entered the recesses (18).

2. The fiber-reinforced resin molding (10) as recited in claim 1, wherein positions of the recesses (18) in an in-plane direction of the skin layers (12) are asymmetrical relative to the core layer (11) between one and the other of the pair of skin layers (12).

3. A method for producing a fiber-reinforced resin molding (10) according to claim 1 provided with a core layer (11) comprising a nonwoven fabric (13) and an impregnating resin (14) that has been impregnated in the nonwoven fabric (13), and a pair of skin layers (12) comprising fibers (15) and a matrix resin (16) that covers the fibers (15), and joined to both surfaces of the core layer (11), comprising the steps of: forming recesses (18) in which portions of the fibers (15) in the matrix resin (16) are exposed on side surfaces of the skin layers (12) facing the core layer (11); and disposing the nonwoven fabric (13) between the pair of the skin layers (12), causing portions of the nonwoven fabric (13) and the impregnating resin (14) to enter the recesses (18), and joining the skin layers (12) and the core layer (11) in that state.

4. The method for producing a fiber-reinforced resin molding (10) according to claim 3, wherein the recesses (18) are formed by using a lost wax method.