COMPOUND, MANUFACTURING METHOD FOR IT AND USE IN A LITHIUM-ION SECONDARY BATTERY

Description

Technical field

[0001] The present disclosure belongs to the field of anode materials for lithium-ion batteries, and relates to a composite, a preparation method and a use thereof, for instance a Si-O-C-Li composite, a preparation method thereof and a use in lithium-ion secondary batteries.Background

[0002] Lithium-ion secondary batteries are widely used in portable electronic products, electric vehicles and energy storage. However, during the initial charge, electrolyte is unstable and forms a SEI film on the surface of electrodes, consuming a large amount of lithium, resulting in low initial coulombic efficiency. For graphite, 5-20% of lithium is used to form the SEI film in the first cycle, while Si, Sn and SiO x need to consume 20-50% of lithium. In this regard, researchers have made a series of optimized designs, such as preparation of nanowires, porous nanostructures and carbon coating and the like. Although the cycling performance is improved, the contact area with the electrolyte is increased, the initial efficiency is reduced, cathode material is consumed in large amount, and energy density is lowered. Obviously, it is imperative to carry out lithium supplement to anode materials in advance.

[0003] At present, there are mainly three methods for doping SiO x with lithium: directly coating a lithium layer on the surface of pole pieces, electrochemically plating lithium on the surface of pole pieces, or mixing SiO x with a lithium compound followed by calcination. The lithium source selected is mainly concentrated on metallic lithium, and some have tried LiOH and LiH.

[0004] CN 1246917C discloses a lithium-containing silicon oxide powder and a production method thereof, which comprises calcining a mixture of raw material powder capable of producing SiO gas with metallic lithium or lithium compound powder at 800 to 1300 °C to obtain a lithium-containing silicon oxide powder, which can increase the capacity and the initial efficiency of the material. However, the introduction of a lithium source during the synthesis stage of raw materials greatly promotes growth of Si grains and reduces cycling.

[0005] CN 100434362C discloses a method for preparing a silicon / lithium-rich phase composite anode material for lithium secondary battery by high-energy ball milling, in which silicon monoxide and metallic lithium are high-energy ball milled, and then heat-treated in vacuum to obtain the silicon / lithium-rich phase composite anode material, with its specific capacity and cycling improved. However, the Li 2 O produced by directly reacting bare silicon monoxide with metallic lithium is easy to absorb moisture and react, which affects the late stability of the material, and makes mass production difficult to achieve.

[0006] CN 103840136A discloses an anode material for electricity storage devices and a preparation method thereof. In the presence of a solvent, a Si-based material capable of occluding and releasing lithium ions is blended with a lithium metal by mixing, and then heat-treated to form lithium silicate to produce an anode material pre-doped with lithium. However, the produced lithium silicate phase that is not subjected to secondary treatment shows strong alkalinity, and it is difficult to process in the later stage and cannot be used in bulk.

[0007] US 2014 / 030599 A1 describes an electrode active material for a secondary battery, which comprises a porous silicon oxide-based composite.

[0008] US 2015 / 221950 A1 describes a negative electrode active material containing particles made of SiO X containing a lithium silicate phase, where 50% to 100% of the surface of each particle made of SiO X is covered by carbon.

[0009] EP 2372817A1 describes a negative electrode material comprising a silicon-silicon oxide composite and a carbon coating formed on a surface of the silicon-silicon oxide composite, wherein at least the silicon-silicon oxide composite is doped with lithium.

[0010] US 2015 / 280223 A1 describes surface-modified silicon nanoparticles comprising a Li x Si y O z top film and a carbon (C) coating layer on the surface of the nanoparticles.

[0011] WO 2016 / 121324 A1 describes a negative electrode active material particle having a lithium silicate phase represented by Li 2z SiO (2+z) {0 < z < 2} and silicon particles dispersed in the lithium silicate phase.

[0012] JP 2007 059213 A describes a negative electrode having a carbonaceous material, composite particles comprising a silicon oxide dispersed in the carbonaceous material, silicon dispersed in the silicon oxide, a lithium silicate phase contained in the silicon oxide and containing Li 4 SiO 4 as the main component.

[0013] JP 2016 192385 A describes a negative-electrode active material, which includes a first chemical element composed of lithium, silicon or tin and a second chemical element composed of oxygen or fluorine.

[0014] US 2016 / 260967 A1 describes a process for producing a silicon, silicon oxide, lithium composite (SSLC) material for use as a negative electrode active material for non-aqueous battery cells.Summary

[0015] The following is a summary of the subject matter that is described in greater detail by the present disclosure. The summary is not intended to be limiting as to the protection scope of the claims.

[0016] It's an object of the present disclosure to provide a composite, a preparation method thereof and an anode material and a lithium-ion secondary battery comprising the same. The method of the present disclosure is simple, and has low requirements on equipments and low cost, and the composite obtained therefrom has a stable structure, which can effectively avoid the failure of active ingredients due to infiltration of components such as air into the interior of particles, and the structure and properties of the composite do not deteriorate during long-term storage. A battery made of the anode material containing the composite exhibits high delithiation capacity, high initial coulombic efficiency and good cycling performance, which has a charge capacity of 1920 mAh / g or more, a discharge capacity of 1768 mAh / g or more and an initial efficiency of 90.2% or more.

[0017] In order to achieve the above object, the present disclosure adopts the following technical solutions: In a first aspect, the present disclosure provides a Si-O-C-Li composite, which comprises nano-silicon, a silicon-oxygen-lithium compound, silicon oxide and a carbon coating, wherein the silicon-oxygen-lithium compound is partially crystalline, and the nano-silicon and the silicon-oxygen-lithium compound are grown from in-situ reduction of a carbon-coated silicon oxide which comprises a silicon oxide and a carbon coating coated on the surface of the silicon oxide such that there is no clear interface between the nano-silicon and the silicon-oxygen-lithium compound; and the nano-silicon is dispersed in the silicon-oxygen-lithium compound to form fusion particles of the nano-silicon and the silicon-oxygen-lithium compound, and the fusion particles are dispersed in the silicon oxide as a matrix in a sea-island form to form composite particles, with the carbon coating coated on the surface of the composite particles.

[0018] In this preferred technical solution, the silicon oxide has a chemical composition of SiO x , in which 0<x<2. Wherein, x may possess a value of 0.1, 0.2, 0.5, 0.6, 0.8, 1, 1.2, 1.5, 1.75 or 1.8 and the like.

[0019] In the present disclosure, a carbon-coated silicon oxide and a reducing agent are used as raw materials. Through the steps such as primary treatment and heat treatment and the like, the reducing agent undergoes a redox reaction with the silicon oxide in the interior of the carbon coating, and nano-silicon is grown from in-situ reduction, and a silicon-oxygen-lithium compound is produced.

[0020] In the present disclosure, since the nano-silicon is grown from in-situ reduction of a carbon-coated silicon oxide, there is no clear interface between the nano-silicon and the silicon-oxygen-lithium compound obtained by the reaction, and this structural feature is closely related to the preparation method of the present disclosure.

[0021] The method of the present disclosure can effectively reduce or even avoid the agglomeration problem among nano-silicons, thereby reducing the silicon expansion problem in the process of application to a battery, and improving the cycle life of the battery.

[0022] The nano-silicon of the present disclosure has a diameter in nanoscale.

[0023] In the present disclosure, the composite has such a structure that: nano-silicon is dispersed in the silicon-oxygen-lithium compound to form fusion particles, and the fusion particles are dispersed in the silicon oxide served as a matrix in a sea-island form to form composite particles, with the carbon coating coated on the surface of the composite particles (see Fig. 2 for a schematic structural view of the composite).

[0024] In the present disclosure, the expression "the fusion particles are dispersed in the silicon oxide served as a matrix in a sea-island form" means that all directions of the fusion particles are surrounded by the silicon oxide that is served as a matrix.

[0025] In the present disclosure, since the nano-silicon is grown from in-situ reduction of a carbon-coated silicon oxide, there is no clear interface between the nano-silicon and the silicon-oxygen-lithium compound obtained by the reaction, and this structural feature is closely related to the preparation method of the present disclosure.

[0026] Preferably, the silicon-oxygen-lithium compound comprises any one selected from the group consisting of Li 2 SiO 3 , Li 4 SiO 4 , Li 2 Si 2 O 5 , Li 2 Si 3 O 7 , and a mixture of at least two selected therefrom; e.g. a mixture of Li 2 SiO 3 and Li 4 SiO 4 , a mixture of Li 2 SiO 3 and Li 2 Si 2 O 5 , a mixture of Li 4 SiO 4 and Li 2 Si 3 O 7 , a mixture of Li 2 SiO 3 , Li 2 Si 2 O 5 and Li 2 Si 3 O 7 and the like.

[0027] Preferably, the carbon coating has a thickness of 3-800 nm, e.g. 3 nm, 5 nm, 10 nm, 20 nm, 30 nm, 40 nm, 50 nm, 60 nm, 70 nm, 85 nm, 90 nm, 100 nm, 110 nm, 120 nm, 135 nm, 145 nm, 160 nm, 175 nm, 190 nm, 200 nm, 215 nm, 225 nm, 245 nm, 260 nm, 280 nm, 300 nm, 320 nm, 340 nm, 360 nm, 380 nm, 400 nm, 415 nm, 430 nm, 450 nm, 475 nm, 500 nm, 520 nm, 540 nm, 560 nm, 580 nm, 600 nm, 625 nm, 650 nm, 680 nm, 700 nm, 730 nm, 750 nm, 775 nm or 800 nm and the like, preferably 10-500 nm.

[0028] Preferably, the carbon coating contains hard carbon.

[0029] Preferably, the carbon coating comprises a carbon matrix and carbon nanotubes and / or graphene sheets embedded in the carbon matrix, and the carbon matrix is obtained by cracking an organic carbon source via carbonization treatment.

[0030] Preferably, based on 100 wt% of the total mass of the carbon coating, the carbon nanotubes and / or graphene sheets in the carbon coating have a mass percent of 0.05-20 wt%, e.g. 0.05 wt%, 0.1 wt%, 0.2 wt%, 0.25 wt%, 0.4 wt%, 0.55 wt%, 0.6 wt%, 0.8 wt%, 1 wt%, 1.5 wt%, 2 wt%, 3 wt%, 3.5 wt%, 4 wt%, 5 wt%, 6 wt%, 7 wt%, 7.5 wt%, 8.5 wt%, 9 wt%, 10 wt%, 11 wt%, 12.5 wt%, 14 wt%, 15 wt%, 16 wt%, 17 wt%, 18 wt%, 19 wt% or 20 wt% and the like.

[0031] Preferably, based on 100 wt% of the total mass of the composite, the carbon coating has a mass percent of 0.1-50 wt%, e.g. 0.1 wt%, 0.3 wt%, 0.5 wt%, 1 wt%, 2 wt%, 2.5 wt%, 3 wt%, 5 wt%, 7 wt%, 10 wt%, 12 wt%, 14 wt%, 16 wt%, 18 wt%, 20 wt%, 23 wt%, 25 wt%, 30 wt%, 33 wt%, 36 wt%, 40 wt%, 42 wt%, 45 wt%, 48 wt% or 50 wt% and the like, further preferably 1-20 wt%.

[0032] The composite provided by the present disclosure is structurally stable during long-term storage in air, and the "long-term" means that the time is 7 days or more.

[0033] In a second aspect, the present disclosure provides a method of preparing the composite according to the first aspect, and the method comprises the following steps: (1) blending a carbon-coated silicon oxide and a lithium source by solid-phase mixing mode to implement primary treatment to form a pre-lithium precursor; (2) heat-treating the pre-lithium precursor in vacuum or a non-oxidizing atmosphere to implement structural adjustment and secondary treatment to form the composite, wherein the temperature of the heat-treating is 160-1000 °C, and the time for the heat-treating is 2-12 h; (3) subjecting the composite to surface treatment to obtain a surface-treated composite; wherein the manner of the surface treatment is any one selected from the group consisting of impurity removal, coating, cladding, film plating, spraying, and a combination of at least two selected therefrom; the manner of the impurity removal is any one selected from the group consisting of washing, impregnation, and a combination of at least two selected therefrom; and wherein in step (1) of the present disclosure, the lithium source undergoes a redox reaction with the silicon oxide in the interior of the carbon coating, and in-situ redox growth results in nano-silicon and a silicon-oxygen-lithium compound.

[0034] The method of the present disclosure can effectively reduce or even avoid the agglomeration problem among nano-silicons, thereby reducing the silicon expansion problem in the process of application to batteries, and improving the cycle life of the batteries.

[0035] The step of surface treatment can remove the residual lithium or lithium-containing compound on the surface of the composite obtained in the step (2), or compound the residual lithium or lithium-containing compound on the surface to the interior.

[0036] The manner in which the residual lithium or the lithium-containing compound can be removed, such as impurity removal mode (washing or impregnation, and the like), for example, may be performed by impregnating the composite into the impurity removing solution.

[0037] The manner in which the residual lithium or the lithium-containing compound can be compounded to the interior is exemplified as coating, cladding, film plating or spraying and the like. The substance coated, cladded, film plated or sprayed may be but not limited to a carbon layer, a polymer and the like.

[0038] Preferably, the silicon oxide has a chemical composition of SiO x , in which 0<x<2, exemplarily, x may possess a value of 0.3, 0.5, 0.8, 1, 1.2, 1.5, 1.75 or 1.8 and the like.

[0039] Preferably, the carbon coating has a thickness of 3-800 nm, e.g. 3 nm, 10 nm, 20 nm, 40 nm, 50 nm, 70 nm, 100 nm, 120 nm, 140 nm, 200 nm, 220 nm, 240 nm, 265 nm, 290 nm, 320 nm, 350 nm, 400 nm, 425 nm, 450 nm, 480 nm, 500 nm, 550 nm, 575 nm, 600 nm, 650 nm, 675 nm, 700 nm, 750 nm or 800 nm and the like, preferably 10-500 nm.

[0040] Preferably, the carbon coating contains hard carbon.

[0041] Preferably, the carbon coating comprises a carbon matrix and carbon nanotubes and / or graphene sheets embedded in the carbon matrix, and the carbon matrix is obtained by cracking an organic carbon source via carbonization treatment.

[0042] The "carbon nanotubes and / or graphene sheets" as used in the present disclosure means that it may be carbon nanotubes, graphene sheets, or a mixture of carbon nanotubes and graphene sheets.

[0043] Preferably, the organic carbon source comprises any one selected from the group consisting of phenolic resin, epoxy resin, polyurethane, asphalt, coal tar, polythiophene, polyolefin, saccharides, polyhydric alcohols, phenolic resin derivatives, epoxy resin derivatives, polyurethane derivatives, asphalt derivatives, coal tar derivatives, polythiophene derivatives, saccharides derivatives, polyhydric alcohols derivatives, and a combination of at least two selected therefrom.

[0044] Preferably, the temperature of the carbonization treatment is 500-1300 °C, e.g. 500 °C, 550 °C, 600 °C, 625 °C, 650 °C, 700 °C, 750 °C, 800 °C, 900 °C, 1000 °C, 1100 °C, 1150 °C, 1250 °C or 1300 °C and the like, preferably 600-1000 °C.

[0045] Preferably, the time for the carbonization treatment is 1-10 h, e.g. 1 h, 1.5 h, 2 h, 3 h, 4 h, 5 h, 6 h, 8 h, 9 h or 10 h and the like, preferably 2-6 h.

[0046] Preferably, based on 100 wt% of the total mass of the carbon coating, the carbon nanotubes and / or graphene sheets in the carbon coating has a mass percent of 0.05-20 wt%, e.g. 0.05 wt%, 0.1 wt%, 0.3 wt%, 0.5 wt%, 0.8 wt%, 1 wt%, 1.5 wt%, 2 wt%, 3 wt%, 4 wt%, 5 wt%, 6 wt%, 7 wt%, 7.5 wt%, 8.5 wt%, 9 wt%, 10 wt%, 11 wt%, 12.5 wt%, 14 wt%, 15 wt%, 16 wt%, 17 wt%, 18 wt%, 19 wt% or 20 wt% and the like.

[0047] Preferably, in the carbon-coated silicon oxide in step (1), the mass ratio of the silicon oxide to the carbon coating is 100:(2-15), e.g. 100:2, 100:3, 100:5, 100:6.5, 100:8, 100:9, 100:10, 100:12, 100:13, 100:14 or 100:15 and the like.

[0048] Preferably, the lithium source in step (1) is lithium-containing compound with strong alkalinity, lithium-containing compound with reducibility, or elemental lithium, in which "lithium-containing compound with strong alkalinity" means that 1 M of the aqueous solution of the lithium-containing compound has a pH greater than 10, e.g. LiNH 2 , Li 2 CO 3 , lithium oxide, lithium metal, lithium hydride, lithium hydroxide, lithium acetate, lithium oxalate, lithium formate, phenyl lithium, alkyl lithium, t-butyl lithium, n-butyl lithium or lithium t-butoxide and the like. However, it does not limit to the above-listed substances, other substances which can achieve the same effect can also be used in the present disclosure.

[0049] Preferably, the mass ratio of the carbon-coated silicon oxide to the lithium source in step (1) is 1:(0.01-0.3), preferably 1:(0.05-0.2), e.g. 1:0.01, 1:0.03, 1:0.05, 1:0.08, 1:0.1, 1:0.12, 1:0.15, 1:0.17, 1:0.2, 1:0.23, 1:0.25, 1:0.26, 1: 0.28 or 1:0.3 and the like.

[0050] Preferably, the solid-phase mixing mode in step (1) comprises any one selected from the group consisting of ball milling, VC mixing, fusion, mixing, kneading, dispersion, and a combination of at least two selected therefrom.

[0051] Preferably, the time for the blending in step (1) is 2-12 h, e.g. 2 h, 2.5 h, 3 h, 3.5 h, 4h, 5 h, 5.5 h, 6 h, 8 h, 9 h, 10 h or 12 h and the like.

[0052] Preferably, the mixing is performed in vacuum condition.

[0053] Preferably, the apparatus used for the dispersion is a high-speed disperser.

[0054] The step (1) of the present disclosure comprises blending in solid-phase mixing mode, so that the lithium source is sufficiently contacted with the carbon-coated silicon oxide, and the dispersion is more uniform, and primary treatment is implemented to obtain a pre-lithium precursor.

[0055] Preferably, the non-oxidizing atmosphere in step (2) comprises any one selected from the group consisting of hydrogen atmosphere, nitrogen atmosphere, helium atmosphere, neon atmosphere, argon atmosphere, krypton atmosphere, xenon atmosphere, and a combination of at least two selected therefrom.

[0056] The temperature of the heat-treating in step (2) is 160-1000 °C, e.g. 160 °C, 200 °C, 230 °C, 265 °C, 300 °C, 350 °C, 450 °C, 500 °C, 550 °C, 600 °C, 700 °C, 750 °C, 850 °C, 900 °C or 1000 °C and the like, preferably 300-900 °C, further preferably 400-860 °C.

[0057] The time for the heat-treating in step (2) is 2-12 h, e.g. 2 h, 3 h, 3.5 h, 4 h, 5 h, 5.5 h, 6 h, 8 h, 9.5 h, 10.5 h, 11 h or 12 h and the like, preferably 2-9 h.

[0058] In the present disclosure, via the heat treatment in vacuum or non-oxidizing atmosphere in step (2), the lithium source infiltrates into the interior of the carbon-coated silicon oxide to react in situ with the silicon oxide to produce nano-silicon and generate a silicon-oxygen-lithium compound, so that the substance species in the interior of the carbon coating are adjusted, moreover, the adjustment of the product structure is also achieved to obtain the composite of the present disclosure (which is a Si-O-C-Li composite).

[0059] Preferably, a surface treatment of the composite is continued, to obtain a surface-treated composite (which is also a Si-O-C-Li composite).

[0060] When the composite comprises nano-silicon, a silicon oxide, a silicon-oxygen-lithium compound and a carbon coating, it indicates that the silicon oxide in the raw material carbon-coated silicon oxide is not completely reacted, with surplus silicon oxide.

[0061] In a third aspect, the present disclosure provides an anode material, which comprises the composite according to the first aspect.

[0062] In a fourth aspect, the present disclosure provides a use of the composite according to the first aspect in lithium-ion secondary batteries.

[0063] The lithium-ion secondary battery comprises the anode material according to the third aspect. The anode material may be used in combination with a carbon material capable of intercalating and deintercalating lithium ions.

[0064] As compared to the prior art, the present disclosure has the following beneficial effects: (1) In the present disclosure, a composite having excellent properties is prepared by mixing a carbon-coated silicon oxide with a specific lithium source by solid phase mixing, then performing heat treatment under specific conditions, and finally performing surface treatment. The method of the present disclosure has a green and environment-friendly working process, no formation of toxic and harmful intermediate products, easily obtainable raw materials, simple process, low requirements on equipments, low cost and is easy for large-scale commercial production. (2) The Si-O-C-Li composite of the present disclosure comprises nano-silicon, a silicon oxide, a silicon-oxygen-lithium compound and a carbon coating, and has such a structure that: nano-silicon is dispersed in the silicon-oxygen-lithium compound to form fusion particles, and the fusion particles are dispersed in a silicon oxide served as a matrix in a sea-island form to form composite particles, with the carbon coating coated on the surface of the composite particles. In the present disclosure, nano-silicon is first dispersed in the silicon-oxygen-lithium compound, and then the obtained fusion particles are dispersed in a silicon oxide served as a matrix in a sea-island form. In the two structures, nano-Si is embedded in the nearby matrix, and will not agglomerate with each other, let alone directly exposed, which can alleviate the volume expansion problem of silicon. The composite of the present disclosure has a stable structure, which can avoid the failure of active ingredients due to the infiltration of components such as air into the interior of the particles, and the structure and properties of the composite will not deteriorate during long-term storage. (3) The composite of the present disclosure has a stable structure and excellent performances, and is particularly suitable for use in anode materials for lithium ion batteries. The present disclosure uses a silicon-oxygen-lithium compound formed in situ to isolate the electrolyte, and the irreversible lithium-consuming phase in the material is pre-reacted. On one hand, irreversible lithium loss during the initial charge-discharge process can be reduced, and the capacity and initial coulombic efficiency are increased; on the other hand, the structure of the composite of the present disclosure can effectively suppress the expansion problem of Si when used in a lithium ion battery, reduce the expansion of the pole pieces, and prolong the cycle life. A battery made of the anode material containing the composite exhibits high delithiation capacity, high initial coulombic efficiency and excellent cycling performance, which has a charge capacity of 1920 mAh / g or more, a discharge capacity of 1768 mAh / g or more, and an initial efficiency of 90.2% or more. (4) In addition, the anode material comprising the composite of the present disclosure can also be used in combination with other anode materials having the ability to intercalate and deintercalate lithium, and has a good application prospect. Brief Description of the Drawings

[0065] Fig. 1 is a schematic structural view of a composite (not in accordance with the invention) comprising nano-silicon, a lithium-containing compound and a carbon coating, wherein reference number 1 represents a carbon coating, reference number 2 represents a silicon-oxygen-lithium compound, and reference number 3 represents nano-silicon; Fig. 2 is a schematic structural view of a composite comprising nano-silicon, a silicon oxide, a silicon-oxygen-lithium compound and a carbon coating, wherein reference number 1 represents a carbon coating, reference number 2 represents a silicon-oxygen-lithium compound, reference number 3 represents nano-silicon, and reference number 4 represents a silicon oxide; Fig. 3 is a SEM image of the composite obtained in Example 1 of the present disclosure. Detailed Description

[0066] The technical solutions of the present disclosure will be further described below in conjunction with the accompanying drawings and specific embodiments.Example 1

[0067] 50 g of SiO x (x=0.95) with carbon coating on the surface and 12.5 g of lithium source LiNH 2 were high-speed dispersed until homogeneously mixed; then the mixture was heat treated at 500 °C for 2 h in an argon atmosphere, naturally cooled to room temperature to take out a composite. Then impurity removal was performed by means of impregnation, and the composite was dried to obtain a surface-treated composite.

[0068] Fig. 3 is a SEM image of the composite obtained in the present example. It can be seen from the figure that dark regions formed by a nano-silicon inlaid silicon-oxygen-lithium compound were uniformly distributed in the particle, which formed a sea-island structure in which the silicon-oxygen-lithium compound inlaid with nano-silicon was served as islands, and silicon oxide was served as the sea.Example 2

[0069] 500 g of SiO x (x=0.95) with carbon coating on the surface and 125 g of lithium source Li 2 CO 3 were high-speed dispersed until homogeneously mixed; then the mixture was heat treated at 500 °C for 2 h in an argon atmosphere, naturally cooled to room temperature to take out a composite. Then impurity removal was performed by means of impregnation, and the composite was dried to obtain a surface-treated composite.Example 3

[0070] 50 g of SiO x (x=0.95) with carbon coating on the surface and 10.8 g of lithium metal powder as a lithium source were mixed in a vacuum state for 3 h; then the mixture was heat treated at 500 °C for 2 h in an argon atmosphere, naturally cooled to room temperature to take out a composite. Then impurity removal was performed by means of impregnation, and the composite was dried to obtain a surface-treated composite.Example 4

[0071] 500 g of SiO x (x=0.95) with carbon coating on the surface and 108 g of lithium oxide powder as a lithium source were mixed in a vacuum state for 3 h; then the mixture was heat treated at 500 °C for 2 h in an argon atmosphere, naturally cooled to room temperature to take out a composite. Then impurity removal was performed by means of impregnation, and the composite was dried to obtain a surface-treated composite.Example 5

[0072] 500 g of SiO x (x=0.5) with carbon coating on the surface and 108 g of lithium metal powder as a lithium source were ball milled for 8 h; then the mixture was heat treated at 800 °C for 1.5 h in an argon atmosphere, naturally cooled to room temperature to take out a composite. Then impurity removal was performed by means of impregnation, and the composite was dried to obtain a surface-treated composite.Example 6

[0073] 100 g of SiO x (x=1.5) with carbon coating on the surface and 30 g of lithium source LiNH 2 were high-speed dispersed until homogeneously mixed; then the mixture was heat treated at 300 °C for 6 h in a nitrogen atmosphere, naturally cooled to room temperature to take out a composite. Then impurity removal was performed by means of impregnation, and the composite was dried to obtain a surface-treated composite.Example 7

[0074] 200 g of SiO x (x=0.7) with carbon coating on the surface and 45 g of lithium source Li 2 CO 3 were VC mixed for 2 h; then the mixture was heat treated at 900 °C for 2 h in an argon atmosphere, naturally cooled to room temperature to take out a composite. Then a layer of polymer film was sprayed on the surface of the composite, filtered and dried to obtain a surface-treated composite.Comparison Example 1

[0075] 50 g of SiO was mixed with 6.3 g of citric acid homogeneously, and then the mixture was fired in a nitrogen atmosphere box-type furnace at a firing temperature of 800 °C. After 2 h of heat preservation, a SiO raw material having a carbon coating layer was obtained by naturally cooling to room temperature.Electrochemical performance test

[0076] The anode materials for lithium ion batteries prepared in Examples 1-7 and the Comparative Example were used as active materials respectively, and PI was used as a binder. After conductive carbon black was added, a slurry was obtained by stirring and then coated on a copper foil, and finally anode plates were obtained by oven drying and rolling, wherein active material : conductive agent : binder = 85:15:10. Lithium metal sheet was used as the counter electrode, PP / PE was used as the diaphragm, LiPF 6 / EC+DEC+DMC (the volume ratio of EC, DEC and DMC is 1:1:1) was used as the electrolyte, and simulated batteries were assembled in a glove box filled with argon. The electrochemical performances of the batteries were tested with a LAND or Xinwei 5V / 10mA battery tester, in which the charge-discharge voltage was set as 1.5V and the charge-discharge rate was set as 0.1C, and the test results were shown in Table 1. Table 1Specific surface area (m 2< / g)Charge capacity (mAh / g)Discharge capacity (mAh / g)Initial efficiency (%)Comparison Example 12.71892140074Example 11.82042185090.6Example 22.32006181090.2Example 31.92044186091.0Example 42.02026184090.8Example 51.62001184292.1Example 62.62080186889.8Example 72.01920176892.1

[0077] As can be seen from the comparison of Examples 1-7 and Comparative Example 1, the lithium-ion secondary batteries made of the anode materials containing the composite of the present disclosure exhibit high delithiation capacity, high initial coulombic efficiency and excellent cycling performance, which has a charge capacity of 1920 mAh / g or more, a discharge capacity of 1768 mAh / g or more and an initial efficiency of 90.2% or more, and the electrochemical performances are significantly superior to those of the battery made of a conventional carbon-coated SiO anode material.

Claims

1. A composite, which is a Si-O-C-Li composite comprising nano-silicon (3), a silicon-oxygen-lithium compound (2), silicon oxide (4) and a carbon coating (1), wherein the silicon-oxygen-lithium compound is partially crystalline, and the nano-silicon and the silicon-oxygen-lithium compound are grown from in-situ reduction of a carbon-coated silicon oxide which comprises a silicon oxide and a carbon coating coated on the surface of the silicon oxide such that there is no clear interface between the nano-silicon and the silicon-oxygen-lithium compound; and the nano-silicon is dispersed in the silicon-oxygen-lithium compound to form fusion particles of the nano-silicon and the silicon-oxygen-lithium compound, and the fusion particles are dispersed in the silicon oxide as a matrix in a sea-island form to form composite particles, with the carbon coating coated on the surface of the composite particles.

2. The composite according to claim 1, wherein the silicon oxide has a chemical composition of SiOx, in which 0<x<2.

3. The composite according to claim 1 or claim 2, wherein the composite has at least one of features (1)-(6): (1) the silicon-oxygen-lithium compound comprises any one selected from the group consisting of Li2SiO3, Li4SiO4, Li2Si2O5, Li2Si3O7, and a mixture of at least two selected therefrom; (2) the carbon coating has a thickness of 3-800 nm; (3) the carbon coating contains hard carbon; (4) the carbon coating comprises a carbon matrix and carbon nanotubes and / or graphene sheets embedded in the carbon matrix; (5) based on 100 wt% of the total mass of the carbon coating, the carbon nanotubes and / or graphene sheets in the carbon coating have a mass percent of 0.05-20 wt%; (6) based on 100 wt% of the total mass of the composite, the carbon coating has a mass percent of 0.1-50 wt%.

4. A method of preparing the composite according to any one of claims 1 to 3, comprising the following steps: (1) blending a carbon-coated silicon oxide and a lithium source by solid-phase mixing mode to implement primary treatment to form a pre-lithium precursor; (2) heat-treating the pre-lithium precursor in vacuum or a non-oxidizing atmosphere to implement structural adjustment and secondary treatment to form the composite according to any of claims 1 to 6, wherein the temperature of the heat-treating is 160-1000 °C, and the time for the heat-treating is 2-12 h; (3) subjecting the composite to surface treatment to obtain a surface-treated composite; wherein the manner of the surface treatment is any one selected from the group consisting of impurity removal, coating, cladding, film plating, spraying, and a combination of at least two selected therefrom; the manner of the impurity removal is any one selected from the group consisting of washing, impregnation, and a combination of at least two selected therefrom; and wherein in step (1) of the present disclosure, the lithium source undergoes a redox reaction with the silicon oxide in the interior of the carbon coating, and in-situ redox growth results in nano-silicon and a silicon-oxygen-lithium compound.

5. The method according to claim 4, wherein a carbon matrix of the carbon coating is obtained by cracking an organic carbon source via carbonization treatment.

6. The method according to claim 4 or claim 5, wherein the lithium source in step (1) is any one selected from the group consisting of lithium-containing compound with strong alkalinity, lithium-containing compound with reducibility, elemental lithium, and a combination of at least two selected therefrom.

7. The method according to any one of claims 4 to 6, wherein the carbon-coated silicon oxide in step (1) comprises a silicon oxide and a carbon coating coated on the surface of the silicon oxide; the method has at least one feature of (1)-(15) below; (1) the silicon oxide has a chemical composition of SiOx, in which 0<x<2; (2) the carbon coating has a thickness of 3-800 nm; (3) the carbon coating contains hard carbon; (4) the carbon coating comprises a carbon matrix and carbon nanotubes and / or graphene sheets embedded in the carbon matrix, and the carbon matrix is obtained by cracking an organic carbon source via carbonization treatment; (5) the organic carbon source comprises any one selected from the group consisting of phenolic resin, epoxy resin, polyurethane, asphalt, coal tar, polythiophene, polyolefin, saccharides, polyhydric alcohols, phenolic resin derivatives, epoxy resin derivatives, polyurethane derivatives, asphalt derivatives, coal tar derivatives, polythiophene derivatives, saccharides derivatives, polyhydric alcohols derivatives, and a combination of at least two selected therefrom; (6) the temperature of the carbonization treatment is 500-1300 °C; (7) the time for the carbonization treatment is 1-10 h; (8) based on 100 wt% of the total mass of the carbon coating, the carbon nanotubes and / or graphene sheets in the carbon coating has a mass percent of 0.05-20 wt%; (9) in the carbon-coated silicon oxide in step (1), the mass ratio of the silicon oxide to the carbon coating is 100:(2-15); (10) the mass ratio of the carbon-coated silicon oxide to the lithium source in step (1) is 1:(0.01-0.3); (11) the solid-phase mixing mode in step (1) comprises any one selected from the group consisting of ball milling, mixing by a VC mixer, fusion, mixing, kneading, dispersion, and a combination of at least two selected therefrom; (12) the time for the blending in step (1) is 2-12 h; (13) the mixing is performed in vacuum condition; (14) the apparatus used for the dispersion is a high-speed disperser; (15) the non-oxidizing atmosphere in step (2) comprises any one selected from the group consisting of hydrogen atmosphere, nitrogen atmosphere, helium atmosphere, neon atmosphere, argon atmosphere, krypton atmosphere, xenon atmosphere, and a combination of at least two selected therefrom.

8. An anode material comprising the composite according to any one of claims 1 to 3.

9. A lithium-ion secondary battery comprising the composite according to any one of claims 1 to 3.