NEW POLYOLS PRODUCED ON SITE, METHOD FOR THEIR PRODUCTION, FOAMS MADE FROM THESE POLYOLS PRODUCED ON SITE AND METHOD FOR THEIR PRODUCTION

Description

FIELD

[0001] The invention relates to novel in-situ formed polyol blends, a process for preparing these novel in-situ formed polyol blends, viscoelastic flexible polyurethane foams comprising these in-situ formed polyol blends, and a process for preparing these viscoelastic polyurethane foams from these in-situ formed polyol blends. The novel in-situ formed polyol blends provide simpler formulation processes by eliminating the need for blending two or more polyols while maintaining good physical properties in foams comprising these in-situ formed polyol blends.BACKGROUND

[0002] In-situ formed polyol blends are important and / or highly desirable because they eliminate the need to blend two or more polyols. This helps to simplify formulation processes and also makes polyol blend formulations accessible when there is no capacity to separately store and / or blend together individual components. Foams prepared from these in-situ formed blends maintain good physical properties.

[0003] The popularity of viscoelastic polyurethane foam, also referred to as memory foam or low resilience foam, has significantly increased in recent years as pillows, toppers or layers in mattresses and bed in a box foams. It is also used in other home and office furnishings as well as automotive applications. This increased use has created a demand for better quality viscoelastic foams with high air flows and improved physical properties such as reduced compression sets and better tear strength.

[0004] US 9 951 174 B2 is related to a novel polyol composition and a process for preparing these polyol compositions. These polyol compositions comprise (a) an in-situ formed polyol blend which comprises (i) one or more polyether monols and (ii) one or more polyether polyols, and (b) a polyether polyol. This prior art is also related to a process for preparing an open celled, flexible polyurethane foam in which the isocyanate-reactive component comprises this polyol composition, and to a viscoelastic polyurethane foam wherein the isocyanate-reactive comprise the latter polyol composition.

[0005] In US 6 491 846 B1 a process for the in-situ production of a blend of a polyether monol and a polyether polyol is disclosed, wherein the process comprises introducing a monol and a double metal cyanide catalyst into a reaction vessel, feeding an epoxide mixture into the vessel and allowing the epoxide to react with the initial starter and continuing to polymerize by feeding epoxide until the equivalent weight of the monol reaches the desired level, then continuously adding a polyfunctional starter to the reaction vessel while continuing to feed an epoxide mixture, completing addition of the starter, and allowing the mixture to continue to polymerize until the resultant blend of the monol and polyether polyol has an equivalent weight of from 350 to 750, and an average functionality of from 2 to 4.SUMMARY

[0006] The novel in-situ formed polyol blends have an overall functionality of 2 to 3 and an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g. These polyol blends comprise: (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on the total weight of monol initiated oxyalkylene ether (a), (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (b), (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (c), and (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein the in-situ formed polyol blend comprises from 10 to 40% by weight of (a) the monol initiated oxyalkylene ether, from 10 to 30% by weight of (b) the polyether polyol, from 20 to 65% by weight of (c) the polyether polyol, and from 5 to 20% by weight of (d) the polyether polyol, with the sum of the %'s by weight of components (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend.

[0007] The process of preparing the in-situ formed polyol blend having an overall functionality of 2 to 3, and an overall hydroxyl number of 50 to 150 mg KOH / g, comprises: I) introducing into a reaction vessel a mixture comprising: (1) an initially charged starter (S i ) comprising a monofunctional compound having a calculated hydroxyl number of less than or equal to 80 mg KOH / g, and (2) a DMC (double metal cyanide) catalyst; II) feeding (1) an epoxide comprising propylene oxide and ethylene oxide in a weight ratio of 100:0 to 80:20, into the reaction vessel; III) allowing the epoxide mixture and the initially charged starter (S i ) to react and to polymerize by feeding the epoxide until the equivalent weight of the monofunctional compound is increased by at least 10% by weight and reaches a value between 1,500 g / mol and 6,000 g / mol; IV) continuously adding (1) a continuously added starter (S c ) having a nominal functionality of greater than 2 to 6, and an equivalent weight of 28 g / mol to 400 g / mol into the reaction vessel while continuing to feed epoxide; V) completing addition of the continuously added starter (S c ); VI) allowing the mixture to continue to polymerize in the reaction vessel thereby forming (1) an intermediate in-situ formed polyol blend which has an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, an overall functionality of 2 to 3, and which comprises (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on 100% by weight of (a), (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of the polyether polyol (b), and (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of the polyether polyol (c); VII) feeding (1) an epoxide comprising propylene oxide while continuously adding (2) a continuously added starter (S c ) having a nominal functionality of 2 to 8, and an equivalent weight of 28 to 400 g / mol into the reaction vessel; VIII) completing addition of the continuously added starter (S c ) and epoxide thereby forming in addition to (a), (b) and (c); (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein the in-situ formed polyol blend comprises from 10 to 40% by weight of (a) the monol initiated oxyalkylene ether, from 10 to 30% by weight of (b) the polyether polyol, from 20 to 65% by weight of (c) the polyether polyol, and from 5 to 20% by weight of (d) the polyether polyol, with the sum of the %'s by weight of components (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend.

[0008] The process of preparing the viscoelastic flexible polyurethane foams comprises reacting: (A) a diisocyanate and / or polyisocyanate component, (B) an isocyanate-reactive component comprising: (1) an in-situ formed polyol blend having an overall functionality of 2 to 3, an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, which comprises: (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on the total weight of monol initiated oxyalkylene ether (a), (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (b), (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (c), and (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein the in-situ formed polyol blend comprises from 10 to 40% by weight of (a) the monol initiated oxyalkylene ether, from 10 to 30% by weight of (b) the polyether polyol, from 20 to 65% by weight of (c) the polyether polyol, and from 5 to 20% by weight of (d) the polyether polyol, with the sum of the %'s by weight of components (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend; in the presence of: (C) a blowing agent; (D) a catalyst; and (E) a surfactant.

[0009] The viscoelastic flexible polyurethane foams comprise the reaction product of: (A) a diisocyanate and / or polyisocyanate component, (B) an isocyanate-reactive component comprising: (1) an in-situ formed polyol blend having an overall functionality of 2 to 3, an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, which comprises: (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on the total weight of monol initiated oxyalkylene ether (a), (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (b), (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (c), and (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein the in-situ formed polyol blend comprises from 10 to 40% by weight of (a) the monol initiated oxyalkylene ether, from 10 to 30% by weight of (b) the polyether polyol, from 20 to 65% by weight of (c) the polyether polyol, and from 5 to 20% by weight of (d) the polyether polyol, with the sum of the %'s by weight of components (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend; in the presence of: (C) a blowing agent; (D) a catalyst; and (E) a surfactant. DETAILED DESCRIPTION

[0010] Various embodiments are described and illustrated in this specification to provide an overall understanding of the structure, function, properties, and use of the disclosed inventions.

[0011] The grammatical articles "one", "a", "an", and "the", as used in this specification, are intended to include "at least one" or "one or more", unless otherwise indicated. Thus, the articles are used in this specification to refer to one or more than one (i.e., to "at least one") of the grammatical objects of the article. By way of example, "a component" means one or more components, and thus, possibly, more than one component is contemplated and may be employed or used in an implementation of the described embodiments. Further, the use of a singular noun includes the plural, and the use of a plural noun includes the singular, unless the context of the usage requires otherwise.

[0012] Equivalent weights and molecular weights given herein in g / mol are number average equivalent weights and number average molecular weights respectively, unless indicated otherwise, and were determined by GPC as described herein.

[0013] All number average and weight average, M n and M w , respectively, molecular weights herein were determined by gel-permeation chromatography (GPC) using a method based on DIN 55672-1 employing chloroform as the eluent with a mixed bed column (Agilent PL Gel; SDVB; 3 micron Pore diameter: 1xMixed-E + 5 micron Pore diameter: 2xMixed-D), refractive index (RI) detection and calibrated with polyethylene glycol.

[0014] All overall hydroxyl numbers (i.e. OH numbers) herein were determined according to ASTM D4274-11, and are reported in mg KOH / g.

[0015] The molecular weight is the number average equivalent weight multiplied by the starter functionality. The hydroxyl number equals 56,100 divided by the equivalent weight.

[0016] As used herein, the term "nominal functionality" refers to the functionality of a polyether polyol which is based solely on the functionality of the starter compound or initiator used in preparing the polyether polyol. The nominal functionality is typically used to describe the functionality of a specific compound.

[0017] As used herein, the term "overall functionality" refers to the average number of reactive groups (e.g. hydroxyl, amine, etc.) which are present per molecule of the polyether polyol or polyether polyol blend being described. This term is typically used when either a polyether polyol is prepared from two or more starter compounds or initiators that have different functionalities and / or when a blend of polyether polyols is used in which the individual polyether polyols have different functionalities.

[0018] As used herein, the term "in-situ formed" with respect to a polyol blend means producing the polyol blend during the course of an alkoxylation reaction in which at least one epoxide is added to a mixture of an initial starter (S i ) and alkoxylation catalyst to initiate the alkoxylation and then at least one continuous starter (S c ) feed is added during the course of the alkoxylation to form a blend of polyether polyols that can vary in molecular weight and functionality.

[0019] Isocyanate index is the relative stoichiometric amount of isocyanate functional groups necessary to react with the isocyanate reactive groups present in the overall foam formulation. It is expressed as a percentage in this application; thus equal stoichiometric amounts of isocyanate functional groups and isocyanate reactive functional groups in the formulation provide an isocyanate index of 100%.

[0020] As used herein, the term "viscoelastic flexible foam" or "viscoelastic flexible polyurethane foam" refers to low-resilience polyurethane foam and is commonly referred to as memory foam. These foams typically provide uniform support of any weight placed on the foam targeted to relieve pressure points, and the foam recovers slowly to its original shape once the weight is removed. These foams are mainly used for bedding, pillows, etc.

[0021] The in-situ formed polyol blend having an overall functionality of 2 to 3, an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, comprises: (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on the total weight of monol initiated oxyalkylene ether (a); (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (b); (c) a polyether polyol having a calculated hydroxyl number of 80 to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (c); and (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein the in-situ formed polyol blend comprises from 10 to 40% by weight of (a) the monol initiated oxyalkylene ether, from 10 to 30% by weight of (b) the polyether polyol, from 20 to 65% by weight of (c) the polyether polyol, and from 5 to 20% by weight of (d) the polyether polyol, with the sum of the %'s by weight of components (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend.

[0022] Suitable monol initiated oxyalkylene ethers (a) have a calculated hydroxyl number of less than or equal to 56 mg KOH / g and containing less than or equal to 20% by weight of copolymerized oxyethylene. These monols have a calculated hydroxyl number of less than or equal to 56 mg KOH / g, or of less than or equal to 28 mg KOH / g.

[0023] Suitable initially charged starters (S i ) for (a) include polyoxyalkylene monols formed by addition of multiple equivalents of epoxide to amonofunctional starter. Monofunctional starters useful herein may be linear or branched compounds, and / or may be naturally-derived or synthetic compounds. Some suitable monofunctional starters include compounds such as, for example, methanol, ethanol, phenols, allyl alcohol, butyl carbitol, longer chain alcohols, etc., and mixtures thereof. Examples of suitable longer chain alcohols include C 10 , C 12 , C 13 , C 14 and / or C 15 monols, which may be used individually or as mixtures. Suitable monoethers include a hydrocarbyl residue (Z) in which the hydrocarbyl residue is a C 4 -C 60 , and preferably a C 9 -C 30 alkyl, aryl or aralkyl group. The hydrocarbyl residue is typically derived from a monohydroxyl compound such as an alcohol or a phenol. Also suitable are monoethers derived from phenols substituted with C 4 -C 15 alkyl groups such as, for example, nonylphenol, etc. Suitable epoxides can include, for example, ethylene oxide, propylene oxide, butylene oxide, styrene oxide, etc. and mixtures thereof. The epoxides can be polymerized with the monofunctional starters using well-known techniques and a variety of catalysts, including alkali metals, alkali metal hydroxides and alkoxides, double metal cyanide complexes, and many more. Suitable initially charged monofunctional starters (S i ) can also be made, for example, by first producing a diol or triol and then converting all but one of the remaining hydroxyl groups to an ether, an ester or other non-reactive group. Suitable initially charged monofunctional starters (S i ) include those monols described in, for example, U.S. Patents 6,391,935 and 6,821,308. Suitable polyoxyalkylene monols to be used as the initially charged starter (S i ) may contain up to 50% by weight, based on 100% by weight of the polyoxyalkylene monol, of copolymerized oxyethylene.

[0024] In one embodiment, the initially charged starter (S i ) for the monol initiated oxyalkylene ether (a) comprises a polyoxypropylene monol having a calculated hydroxyl number of less than or equal to 80 mg KOH / g. These compounds facilitate DMC catalyzed addition of epoxide and provide good build ratios for the production of the in-situ formed polyol blends.

[0025] The monol initiated oxyalkylene ether (a) may also be characterized in one embodiment as containing up to 20% by weight of copolymerized oxyethylene, based on the total weight of the monol initiated oxyalkylene ether (a). This weight percentage includes the initiator or starter and all of the added epoxide(s). These monol initiated oxyalkylene ethers (a) may contain less than or equal to 20% by weight, or less than or equal to 15% by weight, or less than or equal to 10% by weight, based on 100% by weight of the monol initiated oxyalkylene ether (a), of copolymerized oxyethylene. These monol initiated oxyalkylene ethers (a) may also contain more than 0%, or at least 2% or at least 5%, based on the total weight of the monol initiated oxyalkylene ether (a), of copolymerized oxyethylene. The amount of copolymerized oxyethylene present in the monol initiated oxyalkylene ethers (a) may vary between any combination of these upper and lower values, inclusive, such as, more than 0% to less than or equal to 20%, or at least 2% to less than or equal to 15%, or at least 5% to less than or equal to 10% by weight.

[0026] The monol initiated oxyalkylene ethers (a) can have virtually any desired arrangement of oxyalkylene units with the proviso that these contain less than 20% of copolymerized oxyethylene, based on the total weight of the monol initiated oxyalkylene ether (a). This weight percentage includes the initiator or starter and all of the added epoxide(s). Some examples of suitable monol initiated oxyalkylene ethers (a) include PO homopolymers, block EO-PO copolymers, random EO / PO copolymers, PO polymers that are "tipped" with EO or with a mixture of EO and PO are possible. These "tipped" PO polymers should use a mixture of EO and PO to achieve a particular oxyethylene content and / or a desired primary hydroxyl content, or any other desired configuration. The so-called PO homopolymers are suitable with the proviso that they satisfy the above described amounts of copolymerized oxyethylene.

[0027] In one embodiment, the monol initiated oxyalkylene ether (a) comprises an oxypropylene block next to the monofunctional starter followed by a mixed oxypropylene and oxyethylene block at the end of the chain. In another embodiment, the oxyalkylene block at the end of the chain comprises copolymerized oxypropylene and copolymerized oxyethylene wherein the copolymerized oxyethylene content is 20% by weight or less, based on 100% by weight of the oxyalkylene block.

[0028] Suitable polyether polyols for component (b) typically have a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, and a nominal functionality of 2. These polyether polyols may have hydroxyl numbers of at least 80 mg KOH / g, or at least 100 mg KOH / g. The polyether polyols may also have hydroxyl numbers of less than or equal to 220 mg KOH / g, or of less than or equal to 180 mg KOH / g. Suitable polyether polyols may also have a calculated hydroxyl number ranging between any combination of these upper and lower values, inclusive, such as 80 mg KOH / g to 220 mg KOH / g, or of 100 mg KOH / g to 180 mg KOH / g. These polyether polyols (b) may be prepared from starters such as, for example, propylene glycol, dipropylene glycol, ethylene glycol, tripropylene glycol, water, methyl-1,3-propanediol, and the like, and mixtures thereof.

[0029] Suitable polyether polyols for component (b) contain from 5 to 45% by weight of copolymerized oxyethylene. These polyether polyols may contain at least 5%, or at least 10%, or at least 15%, of copolymerized oxyethylene, based on the total weight of the polyether polyol (b). These polyether polyols may contain 45% or less, or 40% or less, or 35% or less of copolymerized oxyethylene, based on the total weight of the polyether polyol (b). The total weight of the polyether polyol includes the starter or initiator, and all of the added epoxide(s). Suitable polyether polyols herein may contain any amount of copolymerized oxyethylene between the above disclosed upper and lower values, inclusive, unless otherwise stated, such as at least 5% to 45% by weight or less, or at least 10% to 40% by weight or less, or at least 15% to 35% by weight or less.

[0030] These polyether polyols (b) can be block EO-PO copolymers, EO-capped polyoxypropylenes, random EO / PO copolymers, PO polymers that are "tipped" with a mixture of EO and PO to achieve the desired amount of copolymerized oxyethylene and / or a particular primary hydroxyl content, random EO / PO copolymers that vary the ratio of EO to PO along the chain to provide EO rich end groups or PO rich end groups or any other desired configuration. The epoxides can be polymerized using well-known techniques and a variety of catalysts, including alkali metals, alkali metal hydroxides and alkoxides, double metal cyanide complexes, and many more.

[0031] In one embodiment, the polyether polyol (b) has an initial mixed oxypropylene and oxyethylene block that has a low copolymerized oxyethylene content (i.e. ≤ 20% by weight oxyethylene content based on 100% by weight of the oxyalkylene block or ≤ 20 / 80 EO / PO) followed by a second mixed oxypropylene and oxyethylene block that has a higher copolymerized oxyethylene content compared to the first block (i.e. ≥ 40% by weight oxyethylene content based on 100% by weight of the second oxyalkylene block or ≥ 40 / 60 EO / PO).

[0032] Suitable polyether polyols for component (c) typically have a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8. These polyether polyols may also have hydroxyl numbers of at least 80 mg KOH / g or at least 100 mg KOH / g. The polyether polyols may also have hydroxyl numbers of less than or equal to 220 mg KOH / g or of less than or equal to 180 mg KOH / g. Suitable polyether polyols may also have a calculated hydroxyl number ranging between any combination of these upper and lower values, inclusive, such as 80 mg KOH / g to 220 mg KOH / g or 100 mg KOH / g to 180 mg KOH / g. The polyether polyols may also have a nominal functionality of greater than 2, or of at least 3. The nominal functionality of the polyether polyols may also be less than or equal to 8, or less than or equal to 6. Suitable polyether polyols may have a nominal functionality ranging between any combination of these upper and lower values, inclusive, such as greater than 2 to 8, or at least 3 to 6. These polyether polyols (c) may be prepared from starters such as, for example, glycerin, trimethylolpropane, pentaerythritol, sucrose, sorbitol, and the like, and mixtures thereof.

[0033] Suitable polyether polyols for component (c) contain from 5 to 45% by weight of copolymerized oxyethylene. These polyether polyols may contain at least 5%, or at least 10%, or at least 15%, of copolymerized oxyethylene, based on the total weight of the polyether polyol (c). These polyether polyols may contain 45% or less, or 40% or less, or 35% or less of copolymerized oxyethylene, based on the total weight of the polyether polyol (c). The total weight of the polyether polyol includes the starter or initiator, and all of the added epoxide(s). Suitable polyether polyols herein may contain any amount of copolymerized oxyethylene between the above disclosed upper and lower values, inclusive, unless otherwise stated, such as at least 5% to 45% by weight or less, or at least 10% to 40% by weight or less, or at least 15% to 35% by weight or less.

[0034] These polyether polyols (c) can be block EO-PO copolymers, EO-capped polyoxypropylenes, random EO / PO copolymers, PO polymers that are "tipped" with a mixture of EO and PO to achieve the desired amount of copolymerized oxyethylene and / or a particular primary hydroxyl content, random EO / PO copolymers that vary the ratio of EO to PO along the chain to provide EO rich end groups or PO rich end groups or any other desired configuration. The epoxides can be polymerized using well-known techniques and a variety of catalysts, including alkali metals, alkali metal hydroxides and alkoxides, double metal cyanide complexes, and many more.

[0035] In one embodiment, the polyether polyol (c) has an initial mixed oxypropylene and oxyethylene block that has a low copolymerized oxyethylene content (i.e. ≤ 20% by weight oxyethylene content based on 100% by weight of the oxyalkylene block or ≤ 20 / 80 EO / PO) followed by a second mixed oxypropylene and oxyethylene block that has a higher copolymerized oxyethylene content compared to the first block (i.e. ≥ 40% by weight oxyethylene content based on 100% by weight of the second oxyalkylene block or ≥ 40 / 60 EO / PO).

[0036] Suitable polyether polyols for component (d) typically have a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, and a nominal functionality of 2 to 8. These polyether polyols may also have hydroxyl numbers of at least 80 mg KOH / g or of at least 100 mg KOH / g. The polyether polyols may also have hydroxyl numbers of less than or equal to 220 mg KOH / g or of less than or equal to 180 mg KOH / g. Suitable polyether polyols may also have a calculated hydroxyl number ranging between any combination of these upper and lower values, inclusive, such as 80 mg KOH / g to 220 mg KOH / g, or 100 mg KOH / g to 180 mg KOH / g. The polyether polyols may also have a nominal functionality of at least 2, or of at least 3. The nominal functionality of the polyether polyols may also be less than or equal to 8, or less than or equal to 6. Suitable polyether polyols may have a nominal functionality ranging between any combination of these upper and lower values, inclusive, such as 2 to 8, or 3 to 6. These polyether polyols (d) may be prepared from starters such as, for example, glycerin, trimethylolpropane, pentaerythritol, sucrose, sorbitol, and the like, and mixtures thereof.

[0037] Suitable polyether polyols for component (d) contain 100% by weight of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d). Propylene oxide can be polymerized with the starter compound using well-known techniques and a variety of catalysts, including alkali metals, alkali metal hydroxides and alkoxides, double metal cyanide complexes, and many more.

[0038] The in-situ formed polyol blend comprises from 10% to 40% by weight, or from 25 to 35% by weight of (a) the monol initiated oxyalkylene ether; from 10 to 30% by weight, or from 15 to 25% by weight of (b) the polyether polyol; from 20 to 65% by weight, or from 30 to 55% by weight of (c) the polyether polyol; and from 5 to 20% by weight, or from 5 to 15 % by weight of (d) the polyether polyol, with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend.

[0039] The process for preparing the in-situ formed polyol blend having an overall functionality of 2 to 3 and an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g comprises I) introducing into a reaction vessel a mixture comprising: (1) an initially charged starter (S i ) comprising a monofunctional compound having a calculated hydroxyl number of less than or equal to 80 mg KOH / g, and (2) a DMC (double metal cyanide) catalyst, II) feeding (1) an epoxide comprising propylene oxide and ethylene oxide in a weight ratio of 100:0 to 80:20, into the reaction vessel; III) allowing the epoxide mixture and the initially charged starter (S i ) to react and continue polymerizing by feeding the epoxide until the equivalent weight of the monofunctional compound is increased by at least 10% by weight and reaches a value between 1,500 g / mol and 6,000 g / mol; IV) continuously adding (1) a continuously added starter (S c ) having a functionality of greater than 2 to 6, and an equivalent weight of 28 g / mol to 400 g / mol into the reaction vessel while continuing to feed epoxide; V) completing addition of the continuously added starter (S c ); and VI) allowing the mixture to continue to polymerize in the reaction vessel thereby forming (1) an intermediate in-situ formed polyol blend having an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, an overall functionality of 2 to 3, and which comprises (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than 20% by weight of copolymerized oxyethylene, based on 100% by weight of the monol initiated oxyalkylene ether (a), b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 and containing from 5 to 45% by weight of copolymerized oxyethylene, based on 100% by weight of the polyether polyol (b), and (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on 100% by weight of the polyether polyol (c); VII) feeding (1) an epoxide comprising propylene oxide; while continuously adding (2) a continuously added starter (S c ) having a nominal functionality of greater than 2 to 6, and an equivalent weight of 28 g / mol to 400 g / mol into the reaction vessel; VIII) completing addition of the continuously added starter (S c ) and epoxide thereby forming in addition to (a), (b) and (c), (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein the in-situ formed polyol blend comprises from 10 to 40% by weight of (a) the monol initiated oxyalkylene ether, from 10 to 30% by weight of the polyether polyol (b), from 20 to 65% by weight of the polyether polyol (c), and from 5 to 20% by weight of the polyether polyol (d), with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend.

[0040] In general, any epoxide polymerizable using DMC catalysis can be used in the in-situ production of the polyol blend comprising a monol initiated oxyalkylene ether (a) and the three polyether polyols (b), (c) and (d). Suitable epoxides include ethylene oxide, propylene oxide, butylene oxides (e.g., 1,2-butylene oxide, isobutylene oxide), styrene oxide, and the like, and mixtures thereof. Polymerization of epoxides using DMC catalysts and hydroxyl-containing starters results in polyether polyols, as is well understood in the art.

[0041] Other monomers that will copolymerize with an epoxide in the presence of a DMC catalyst may be included in the process of the invention to make other types of epoxide polymers. Some examples include epoxides copolymerize with oxetanes as described in U.S. Patent 3,404,109 to give polyethers, or with anhydrides to give polyesters or polyetheresters as described in U.S. Patents 5,145,883 and 3,538,043 or with carbon dioxide to form polyether carbonate polyols such as those described in U.S. Patents 4,826,887, 4,826,952, 4,826,953, 6,713,599, 7,977,501, 8,134,022, 8,324,419, 8,946,466 and 9,249,259, and U.S. Published Patent Application 2015 / 0232606.

[0042] In accordance with this process, an initially charged starter (S i ) is used, and the initially charged starter (S i ) is different than the continuously added starter (S c ). The initially charged starter (S i ) is comprised of, either totally or in large part, a compound having one active hydrogen per molecule that can serve as a site for epoxide addition, and having a calculated hydroxyl number of less than or equal to 80 mg KOH / g, or of less than or equal to 56 mg KOH / g. The suitable starters for the initially charged starter (S i ) are the same monofunctional starters described above as suitable starters for the monol initiated oxyalkylene ether (a). These are formed by addition of multiple equivalents of epoxide to a monofunctional starter such as, for example, methanol, ethanol, phenols, allyl alcohol, butyl carbitol, longer chain alcohols, etc., and mixtures thereof. Examples of suitable longer chain alcohols include C 10 , C 12 , C 13 , C 14 and / or C 15 monols, which may be used individually or as mixtures. Suitable monoethers include a hydrocarbyl residue (Z) in which the hydrocarbyl residue is a C 4 -C 60 , and preferably a C 9 -C 30 alkyl, aryl or aralkyl group. The hydrocarbyl residue is typically derived from a monohydroxyl compound such as an alcohol or a phenol. Also suitable are monoethers derived from phenols substituted with C 4 -C 15 alkyl groups such as, for example, nonylphenol, etc. Suitable epoxides can include, for example, ethylene oxide, propylene oxide, butylene oxide, styrene oxide, etc. and mixtures thereof. The epoxides can be polymerized using well-known techniques and a variety of catalysts, including alkali metals, alkali metal hydroxides and alkoxides, double metal cyanide complexes, and many more. Suitable initially charged monofunctional starters (S i ) can also be made, for example, by first producing a diol or triol and then converting all but one of the remaining hydroxyl groups to an ether, an ester or other non-reactive group.

[0043] One suitable class of polyether monol starters or initially charged starters (S i ) includes polyoxypropylene monols having a calculated hydroxyl number of less than or equal to 80 mg KOH / g, or of less than or equal to 56 mg KOH / g. These compounds facilitate DMC catalyzed addition of epoxide and provide suitable build ratios for the production of the in-situ formed polyether polyol blends herein.

[0044] In the process of the present invention, the quantity of an initially charged starter (S i ) used depends on many factors, including, for example, the reactor dimensions, the identity of the initially charged starter (S i ), the equivalent weights of the initially charged starter (S i ) and of the target product, the equivalent weight of the continuously added starter (S c ), and other factors.

[0045] Any DMC catalyst known in the art is suitable for use in the process of the present invention. These well-known catalysts are the reaction products of a water-soluble metal salt (e.g., zinc chloride) and a water-soluble metal cyanide salt (e.g., potassium hexacyanocobaltate). Preparation of suitable DMC catalysts is described in many references, including, for example, U.S. Patents 5,158,922, 4,477,589, 3,427,334, 3,941,849, 5,470,813, and 5,482,908. One suitable type of DMC catalysts is zinc hexacyanocobaltate.

[0046] The DMC catalyst includes an organic complexing agent. As disclosed in the preceding references, the complexing agent is needed for an active catalyst. Suitable complexing agents are water-soluble heteroatom-containing organic compounds that can complex with the DMC compound, as well as water-soluble aliphatic alcohols. An example of a suitable aliphatic alcohol is tert-butyl alcohol. The DMC catalyst may include, in addition to the organic complexing agent, a polyether, as is described in U.S. Patent 5,482,908.

[0047] Suitable DMC catalysts for use in the process are highly active catalysts such as those described in U.S. Patents 5,482,908 and 5,470,813. High activity allows the catalysts to be used at very low concentrations, and possibly at concentrations which are low enough to overcome any need to remove the catalyst from the finished blends of in-situ formed polyol blends.

[0048] The process of the invention also requires a continuously added starter (S c ) as described in detail herein. Conventional processes for making polyether polyols, including KOH-catalyzed and DMC-catalyzed processes, charges the catalyst and all the starter to be used to the reactor at the start of the polymerization, and then adds the epoxide continuously. In the process of forming an in-situ formed polyol blend suitable for the invention, the DMC catalyst and an initial monofunctional starter (or initially charged starter) (S i ) are charged to the reactor followed by epoxide feed and polymerization until the monol reaches the desired equivalent weight. At this point, a first feed (i.e. as described in step IV)(1) above) of continuously added starter (S c ) is begun and it proceeds at a continuous controlled rate relative to the continuing epoxide feed until the addition of the first feed of continuously added starter (S c ) is completed. Epoxide feed is continued until the desired calculated hydroxyl number of the first feed of continuously added starter (S c ) components is reached. The continuously added starter (S c ) may be mixed with the epoxide and added to the reactor, or it may be added to the reactor as a separate stream. It is also possible that DMC catalyst can be added continuously with the continuously added starter (S c ). In the process of the present invention to form an in-situ formed polyol blend, a second feed (i.e. as described in step VII)(2) above) of continuously added starter (S c ) can be started with the epoxide feed after the completion of the first feed of continuously added starter (S c ). The second feed of continuously added starter (S c ) can be the same starter compound as was used for the first feed of continuously added starter (S c ), or it can be a different starter compound. The epoxide and the epoxide composition can be the same during the second feed of continuously added starter (S c ) feed as during the first feed of continuously added starter (S c ) feed, or the epoxide and the epoxide composition can be different during the second feed of continuously added starter (S c ) feed as during the first feed of continuously added starter (S c ) feed. The skilled artisan knows and understands that the lowest equivalent weight substance preferably reacts with alkylene oxide in the presence of DMC catalyst, hence the continuously added starter (S c ) will preferentially react with the alkylene oxide present. This is commonly known and referred to by one of ordinary skill in the art as "catch up kinetics". This allows the in-situ production of different components of the polyol blend while only minimally affecting the other, higher equivalent weight components. Catch up kinetics is described in "Chemistry and Technology of Polyols for Polyurethanes", 2nd Edition, Volume 1, 2016, M. lonescu, pages 189-190.

[0049] The continuously added starter (S c ) is typically a (low) equivalent weight starter or polyol or a blend of (low) equivalent weight starters or polyols. (Low) equivalent weight polyols as defined in this application having from 2 hydroxyl groups to 8 hydroxyl groups. It also may be beneficial to add more than one continuously added starter (S c ) having different functionalities either simultaneously or sequentially. The functionality of the continuously added starter (S c ) or multiple continuously added starters (S c ) should be chosen such that the average functionality of the resultant polyol is from 2 to 6, or from 2 to 3. These polyols may have at least 2 hydroxyl groups. These polyols may also have 8 hydroxyl groups or less, or 6 hydroxyl groups or less, or 3 hydroxyl groups or less. The polyols used for the continuously added starter (S c ) may contain any number of hydroxyl groups which ranges between any combination of these upper and lower values, inclusive, such as from at least 2 hydroxyl groups to 8 hydroxyl groups or less, or 2 hydroxyl groups to 6 hydroxyl groups, or 2 hydroxyl groups to 3 hydroxyl groups.

[0050] Suitable polyols for the continuously added starter (S c ) have a nominal functionality of 2 to 8 and an equivalent weight of 28 to 400.

[0051] Examples of suitable polyols to be used as the continuously added starter (S c ) include compounds such as, for example, glycerin, propylene glycol, dipropylene glycol, ethylene glycol, trimethylolpropane, sucrose, sorbitol, tripropylene glycol, and the like, and mixtures thereof. In one embodiment, the first feed of continuously added starter (S c ) comprises propylene glycol and glycerin and the second feed of continuously added starter (S c ) comprises glycerin. Equivalent weight polyether polyols prepared by multiple epoxide addition to these polyols or other starters with two or more active hydrogens may also be employed as the continuously added starter (S c ).

[0052] The continuously added starter (S c ) can also be other compounds having at least two active hydrogens per molecule, which are known to be suitable initiators for conventional DMC-catalyzed epoxide polymerizations, including compounds such as, for example, alcohols, thiols, aldehydes and ketones containing enolizable hydrogens, malonic esters, phenols, carboxylic acids and anhydrides, aromatic amines, acetylenes, and the like, and mixtures thereof. Examples of suitable active hydrogen-containing compounds appear in U.S. Patents 3,900,518, 3,941,849, and 4,472,560.

[0053] As described previously, a wide variety of epoxides can be employed in the current process. Propylene oxide and ethylene oxide are the most commonly used epoxides. A unique feature of the current process is that the compositions of the epoxide can be varied to control the composition of the monol initiated oxyalkylene ether (a) and polyether polyol constituents (b), (c) and (d) in the final product. For example, propylene oxide can be added alone during polymerization of the monol initiated oxyalkylene ether (a), prior to the start of the addition of the continuously added starter (S c ). After the first feed of continuously added starter (S c ) is started, a blend of ethylene oxide and propylene oxide can be fed to yield a high functionality polyether polyol comprised of a poly(oxyethylene-oxypropylene) copolymer. Because oxide addition via DMC catalysis occurs predominantly on the lower equivalent weight polyether polyol, the monol initiated oxyalkylene ether component can remain largely poly(oxypropylene). By reversing these sequences, the monol initiated oxyalkylene ether could be produced with higher poly(oxyethylene) content and the polyether polyol (from the first feed of continuously added starter (S c )) could be predominantly poly(oxypropylene).

[0054] The epoxide composition may also be varied during the initial polymerization of the monol initiated oxyalkylene ether and / or at some point during and / or after the addition of the continuously added starter (S c ). This provides flexibility for controlling the distribution of oxyethylene or oxypropylene within the monol initiated oxyalkylene ether and polyether polyols and allows some control of the primary versus secondary hydroxyl content of the monol initiated oxyalkylene ether and polyether polyols, and thus, the relative reactivity of the constituents in the final composition. In this way, it is possible to design the product to meet the reactivity and performance requirements of the intended applications such as viscoelastic polyurethane foams.

[0055] An example of the process to prepare an in-situ formed multifunctional polyol blend is by first alkoxylating a monol, diol, and triol with a DMC catalyst following the procedure described in U.S Patent 6,491,846and then alkoxylating a triol. By way of example, the monol starter or initially charged starter (S i ) may comprise a 1600 MW (35 OH#) monol inhibited with BHT made from the propoxylation of Neodol 25 (available from Shell) with a DMC catalyst. In a typical reaction to make the in-situ formed polyol blend, the monol starter (or initially charged starter) (S i ) is charged at room temperature followed by addition of the DMC catalyst as dry powder. Alternatively, the monol starter or initially charged starter (S i ) may be heated before addition to the reactor or it may be charged to a heated reactor. The DMC catalyst may also be added as a slurry in the monol starter or initially charged starter (S i ). After charging the monol starter or initially charged starter (S i ) and DMC catalyst, vacuum is pulled on the reactor contents. The reactor contents are heated to the reaction temperature. This may be followed by nitrogen stripping under vacuum. Vacuum and nitrogen stripping can occur before, during or after the reactor contents have reached the reaction temperature. After nitrogen stripping is stopped, the vacuum can be continued without nitrogen stripping. Before starting the oxide feed to the reactor, the reactor is blocked in under vacuum and can remain under vacuum for a given time to check for any leaks to the reactor. The DMC catalyst is then activated by adding a portion of propylene oxide or a mixture of propylene and ethylene oxide and allowing it to react. Prior to oxide addition, the reactor can be under vacuum or can be pressured up using nitrogen or other inert gas. After the DMC catalyst activation is complete as evidenced by a decrease in reactor pressure or by a specific temperature change, the oxide feed is restarted. The DMC catalyst can also be activated by starting the oxide feeds at a reduced rate and continuously adding the oxide feeds until the reactor temperature increases and the reactor pressure decreases and the reactor cooling system indicates that the reactor has switched from heating to cooling indicating that the catalyst is active and the reaction is proceeding. After detecting the activation either through the batch addition of oxide or the continuous feeding of oxide, the propylene and / or ethylene oxide feed rates are ramped up to the set point typically in 5 to 30 minutes. The typical reaction temperature for the DMC catalyzed reaction is 130 to 150°C with a mixture of propylene oxide and / or ethylene oxide. After the monol starter or initially charged starter (S i ) has increased in molecular weight by at least 10% through the addition of propylene and / or ethylene oxide, a mixture of glycerin that has been acidified with phosphoric acid and propylene glycol is continuously added along with a mixture of propylene oxide and ethylene oxide until a targeted calculated hydroxyl number is reached. The continuously added starter (S c ), i.e. propylene glycol and / or glycerin feeds, may be started at the target feed rates or ramped to the target feed rates. The continuously added starter (S c ), i.e. propylene glycol and / or glycerin feeds, may be started simultaneously or at different times. Additionally the continuously added starter (S c ), i.e. propylene glycol and / or glycerin feeds, may be fed at a constant maximum feed rate or the feed rate of one or both may be varied during this step. After the target calculated hydroxyl number is reached, the continuously added starter (S c ), i.e. propylene glycol and / or glycerin feeds, are stopped either at their target feed rates or by ramping down the feed rates. Propylene oxide and ethylene oxide are continuously added after the continuously added starter (S c ) are stopped until a target calculated hydroxyl number is reached. The feeding of alkylene oxide after the continuously added starter (S c ) stops is referred to as a non-CAOS cap. Alternatively, the non-CAOS cap may be eliminated and the continuously added starter (S c ), e.g. propylene glycol and / or glycerin feeds, continued until the target calculated hydroxyl number is reached. After the continuously added starter (S c ) is stopped and the propylene oxide and ethylene oxide are fed to react away the continuously added starter (S c ), the propylene oxide and ethylene oxide are continuously added at a different weight ratio that is higher in ethylene oxide until a target calculated hydroxyl number is reached. This change in the propylene oxide and ethylene oxide weight ratio from a ratio low in ethylene oxide to one that is higher in ethylene oxide may be accomplished by stopping the oxide feeds and restarting at the desired ratio or by simultaneously ramping down the propylene oxide feed and ramping up the ethylene oxide feed to the new peak feed rates and ratios. After the calculated hydroxyl number is reached, the ethylene oxide feed is stopped and the continuously added starter (S c ), e.g. glycerin feed, is resumed (i.e. a second feed of continuously added starter (S c )). The continuously added glycerin feed (S c ) may be started directly at the target feed rate or ramped up to the target rate. The continuously added starter (S c ), e.g. glycerin, and propylene oxide addition are continued until a target calculated hydroxyl number is reached. After this, the continuously added starter (S c ), e.g. glycerin, feed is stopped directly or ramped down and propylene oxide addition continues until a target calculated hydroxyl number is reached. This corresponds to a non-CAOS cap in the all propylene oxide triol. The propylene oxide rate may be stopped directly or ramped down to zero. This in-situ formed multifunctional polyol blend can have an overall functionality of 2 to 3 and an overall calculated hydroxyl number of 50 to 150 mg KOH / g. At the conclusion of the oxide feeds, all feed lines are blown out with nitrogen into the reactor and the reactor contents are held at the reaction temperature (cooked-out) until the reactor pressure levels off. After this the product is stripped under vacuum simultaneously or continuously with nitrogen sparging and / or steam in one or more steps. The polyol is then cooled typically to 80 to 100°C and one or more antioxidants are added followed by mixing. The product is then cooled to 40 to 80°C and discharged from the reactor. Antioxidant addition can occur at different temperatures and the final polyether polyol can be discharged from the reactor at different temperatures.

[0056] The process for the production of a viscoelastic polyurethane foam comprises reacting (A) a diisocyanate and / or a polyisocyanate component, with (B) an isocyanate-reactive component comprising (1) the in-situ formed polyol blend having an overall functionality of 2 to 3 and an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g which is described herein, in the presence of (C) a blowing agent, (D) a catalyst, and (E) a surfactant.

[0057] Suitable diisocyanates and polyisocyanates to be used as component (A) in the viscoelastic foams herein and the process of making these foams include, for example, isocyanate-functional compounds which contain two or more free NCO groups per molecule and are known to be useful for preparing flexible polyurethane foam. Suitable isocyanate-functional compounds include aromatic, aliphatic, and cycloaliphatic di- and / or polyisocyanates. Some examples include toluene diisocyanates (TDI), diphenylmethane diisocyanates (MDI), naphthalene diisocyanates, isophorone diisocyanate, hexamethylene diisocyanates (HDI), polymeric MDIs, and polyisocyanates modified with carbodiimide, ester, urea, urethane, allophanate, isocyanurate, biuret, or other functionalities, and the like, and mixtures thereof. Suitable polyisocyanates include toluene diisocyanate (TDI, which is usually a mixture of 2,4- and 2,6-isomers), diphenylmethane diisocyanate (MDI which is usually a mixture of the 2,2'-, the 2,4'- and the 4,4'-isomers), and various mixtures thereof. In one embodiment, the isocyanate-functional compound comprises toluene diisocyanate, preferably a mixture of 2,4- and 2,6-isomers .

[0058] The isocyanate-reactive component (B) comprises the in-situ formed polyol blend (1) described herein which has an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g and an overall functionality of 2 to 3. This polyol blend may have a hydroxyl number of at least 50 mg KOH / g, or at least 70 mg KOH / g, or at least 85 mg KOH / g. This polyol blend may also have a hydroxyl number of 150 mg KOH / g or less, or 130 mg KOH / g or less, or of 115 mg KOH / g or less. The in-situ formed polyol blend may have a hydroxyl number ranging between any combination of these upper and lower values, inclusive, such as 50 mg KOH / g to 150 mg KOH / g , or 70 mg KOH / g to 130 mg KOH / g, or 85 mg KOH / g to 115 mg KOH / g.

[0059] In the isocyanate-reactive component (B), the in-situ formed polyol blend (1) also typically has an overall functionality of 2 to 3. This in-situ formed polyol blend may have an overall functionality of 2, or at least 2.2. The overall functionality of this in-situ formed polyol blend may also be 3 or less, or 2.8 or less. The in-situ formed polyol blend (1) may have an overall functionality ranging between any combination of these upper and lower values, inclusive, such as 2 to 3, or 2.2 to 2.8.

[0060] The composition of the in-situ formed polyol blend (1) is as described hereinabove.

[0061] In addition to the in-situ formed polyol blend (1), the isocyanate-reactive component (B) for the viscoelastic flexible polyurethane foams and process of preparing the viscoelastic flexible foams may additionally comprise a conventional polyether polyol, a polyester polyol, a polyether carbonate polyol, a polyetherester polyol, polymer polyols, amine-terminated polyethers, polythioethers, polyacetals, polycarbonates, etc., as well as various chain extenders and / or crosslinking agents, both of which may contain hydroxyl groups and / or amine groups capable of reacting with the isocyanate groups of the isocyanate component.

[0062] The in-situ formed polyol blend (1) essentially corresponds to the in-situ formed polyol blend described herein above, and is characterized by the same overall hydroxyl numbers and average functionalities.

[0063] As previously described, the in-situ formed polyol blends (1) comprise (a) a monol initiated oxyalkylene ether having a hydroxyl number of less than or equal to 56 mg KOH / g and containing less than or equal to 20% by weight of copolymerized oxyethylene, (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 6, and containing from 5 to 45% by weight of copolymerized oxyethylene, and (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of copolymerized oxypropylene.

[0064] In addition, in the process of preparing the viscoelastic flexible polyurethane foam, the isocyanate-reactive component (B) which comprises (1) the in-situ formed polyol blend described above may additionally comprise at least one of: (2)(a) a polyether polyol having an OH number of 20 mg KOH / g to 240 mg KOH / g, an average functionality of 2 to 8, and containing at least 50% by weight of copolymerized oxyethylene, based on 100% by weight of component (2)(a); and / or (2)(b) a filled polyol.

[0065] In one embodiment, these isocyanate-reactive components additionally comprise (2)(a) one or more polyether polyols having an OH number of 20 mg KOH / g to 240 mg KOH / g, an average functionality of 2 to 8, and containing at least 50% by weight of copolymerized oxyethylene, based on the total weight of component (2)(a).

[0066] Suitable compounds to be used as polyether polyols (2)(a) include those polyols which have a functionality of 2 to 8, a calculated hydroxyl number of at least 20 mg KOH / g to 240 mg KOH / g, and contain at least 50% of copolymerized oxyethylene, based on 100% by weight of the polyether polyol (2)(a). Suitable polyether polyols for component (2)(a) may commonly be referred to as cell opening polyols.

[0067] These polyether polyols for component (2)(a) may have hydroxyl numbers of at least 20 mg KOH / g, or at least 30 mg KOH / g, or at least 35 mg KOH / g. In addition, the polyether polyols generally have hydroxyl numbers of 240 mg KOH / g or less, or 170 mg KOH / g or less, or 50 mg KOH / g or less. The suitable polyether polyols of the present invention may be characterized by a calculated hydroxyl number between any of the above values, inclusive, unless otherwise stated, such as, 20 to 240 mg KOH / g, or 30 mg KOH / g to 170 mg KOH / g, or 35 to 50 mg KOH / g.

[0068] The average functionality of these polyether polyols (2)(a) ranges from at least 2, or at least 2.5. The average functionality is also typically 8 or less, or 6 or less. The average functionality of the polyether polyols (2)(a) may range between any combination of these upper and lower values, inclusive, such as at least 2 to 8 or less, or at least 2.5 to 6 or less.

[0069] Suitable polyether polyols used as component (2)(a) also contain at least 50% to 99% by weight or less of copolymerized oxyethylene, based on 100% by weight of the polyether polyol. This weight percent includes the starter or initiator, and the all of the added epoxide(s). These polyether polyols may contain at least 50%, or at least 60% or at least 70% by weight, of copolymerized oxyethylene, based on 100% by weight of the polyether polyol. These polyether polyols may also contain 99% or less, or 90% or less, or 85% or less of copolymerized oxyethylene, based on 100% by weight of the polyether polyol. Suitable polyether polyols herein may contain any amount of copolymerized oxyethylene between the above disclosed values, inclusive, such as at least 50% to 99% or less, or at least 60% to 90% or less, or at least 70% to 85% by weight or less, of copolymerized oxyethylene.

[0070] Some examples of suitable polyether polyols for component (2)(a) include those compounds which are conveniently made by reacting compounds having two or more active hydrogens (e.g., glycols, triols, tetrols, hexols, polyfunctional amines and other polyfunctional starters known to those in the art) with one or more equivalents of an epoxide as described earlier. Examples of suitable starters for these polyether polyols (2)(a) include low molecular weight starters such as, for example, glycerin, propylene glycol, dipropylene glycol, ethylene glycol, trimethylolpropane, sucrose, sorbitol, tripropylene glycol, and the like, and mixtures thereof.

[0071] Suitable epoxides for component (2)(a) can include, for example, ethylene oxide, propylene oxide, butylene oxide, styrene oxide, etc. and mixtures thereof. The epoxides can be polymerized using well-known techniques and a variety of catalysts, including alkali metals, alkali metal hydroxides and alkoxides, double metal cyanide complexes and many more.

[0072] These polyether polyols can have any desired arrangement of oxyalkylene units with the proviso that they contain at least 50% of copolymerized oxyethylene, based on the 100% by weight of the polyether polyol. Thus, the polyether polyols (2)(a) can be EO homopolymers, block EO-PO copolymers, EO-capped polyoxypropylenes, PO capped polyoxyethylenes, random EO / PO copolymers, PO polymers that are "tipped" with a mixture of EO and PO to achieve the desired amount of copolymerized oxyethylene and / or a particular primary hydroxyl content, random EO / PO copolymers that vary the ratio of EO to PO along the chain to provide EO rich end groups or PO rich end groups or any other desired configuration.

[0073] In one embodiment, the isocyanate-reactive component may additionally comprise (2)(b) a filled polyol which is also known as a polymer polyol. Examples of suitable filled polyols for the invention include, for example, (i) styrene / acrylonitrile polymer polyols, (ii) polyisocyanate polyaddition (PIPA) polyols which are dispersions of polyurethanes formed by the in-situ reaction of an isocyanate and an alkanolamine, (iii) polyhydrazodicarbonamide dispersion polyols (also known as PHD polyols), and (iv) mixtures thereof.

[0074] Suitable (i) SAN polymer polyols herein are prepared by free radical polymerization of monomers (i.e. styrene and acrylonitrile) in a polyol carrier (or base polyol) to produce a free radical polymer dispersed in the polyol carrier (or base polyol). Conventionally, the solids content of SAN polymer polyols is from 5% up to 60% by weight of solids, based on the total weight of the SAN polymer polyol composition. The solids content may be at least 5%, or at least 10% by weight of solids, based on the total weight of the SAN polymer polyol composition. The solids content may also be 60% by weight or less, or 50% by weight or less, based on the total weight of the SAN polymer polyol composition. The amount of solids content may range between any combination of these upper and lower values, inclusive, such as from 5% to 60%, or from 10% to 50% by weight of solids, based on the total weight of the SAN polymer polyol composition.

[0075] Examples of suitable SAN polymer polyols to be used as component (2)(b) herein include those SAN polymer polyols disclosed in, for example, but are not limited to, U.S. Patents 5,321,077, 5,324,774, 5,364,906, 5,358,984, 5,453,469, 5,488,085, 5,496, 894, 5,554,662, 5,594,066, 5,814,699, 5,824,712, 5,916,994, 5,995,534, 5,990,185, 6,117,937, 6,455,603, 6,472,447, 6,624,209, 6,713,599, 6,756,414, 7,179,882, 7,759,423, etc..

[0076] The SAN polymer polyols suitable for the present invention are prepared by the in-situ polymerization of acrylonitrile and styrene, in a base polyol. Suitable base polyols may be conventional polyether polyols, polyester polyols, poly(oxyalkylene) polyols, etc. Methods for preparing SAN polymer polyols are known and described in, for example, United States Patents 3,304,273; 3,383,351; 3,523,093; 3,652,639; 3,823,201; 4,104,236; 4,111,865; 4,119,586; 4,125,505; 4,148,840; 4,172,825; 4,524,157; 4,690,956; Re-28,715; and Re-29,118.

[0077] One suitable SAN polymer polyol to be used as component (2)(b) in the present invention comprises the free radical polymerization product of styrene and acrylonitrile in a base polyol, wherein the base polyol has a nominal functionality of 3, a molecular weight of 4750 g / mol, and an OH number of 35 mg KOH / g. The solids content of this SAN polymer polyol is 43% solids, in which the styrene to acrylonitrile content is 64% to 36%.

[0078] Another suitable SAN polymer polyol for component (2)(b) in the present invention comprises the free radical polymerization product of styrene and acrylonitrile in a base polyol, wherein the base polyol has a nominal functionality of 3, a molecular weight of 3000 g / mol, and an OH number of 56 mg KOH / g. The solids content of this SAN polymer polyol is 49% solids, in which the styrene to acrylonitrile content is 67% to 33%.

[0079] Suitable polyisocyanate polyaddition (PIPA) polyols for component (2)(b) contain polyurethane particles dispersed in a polyol carrier (i.e. base polyol). The polyurethane particles in PIPA polyols are formed in-situ by the reaction of an isocyanate with an alkanolamine (e.g., triethanolamine). The solids content of the PIPA polyols may typically range from 5% up to 60% by weight, based on the total weight of the PIPA composition. The solids content may be at least 5%, or at least 10% by weight of solids, based on the total weight of the PIPA composition. The solids content may also be 60% by weight of less, or 50% by weight or less, based on the total weight of the PIPA composition. The amount of solids content may range between any combination of these upper and lower values, inclusive, such as from 5% to 60%, or from 10% to 50% by weight of solids, based on the total weight of the PIPA composition.

[0080] Examples of suitable PIPA polyols can be found in, for example, U.S. Patents 4,374,209 and 5,292,778.

[0081] Suitable polyhydrazodicabonamide polyols (which are also commonly referred to as PHD polyols or PHD dispersion polyols) to be used as component (2)(b) of the present invention include, for example, those compounds which are typically prepared by the in-situ polymerization of an isocyanate mixture with an amine group containing compound such as, a diamine and / or a hydrazine, in a base polyol. Suitable base polyols typically comprise polyether polyols and polyoxyalkylene polyols. Methods for preparing PHD polymer polyols are described in, for example, U.S. Patents 4,089,835 and 4,260,530.

[0082] PHD polyols typically have solids contents within the range of 3 to 30 weight %, based on the total weight of the PHD polyol. The solids content of the PHD polyols may be at least 3%, or at least 5% by weight, based on the total weight of the PHD polyol. The solids content of the PHD polyols may also be 30% or less, or 25% by weight or less, based on the total weight of the PHD polyol. The PHD polyols may have a solids content that ranges between any combination of these upper and lower values, inclusive, such as from 3% to 30% by weight, or from 5 to 25% by wt., based on the total weight of the PHD polyol.

[0083] As previously stated, PHD polyols are typically prepared by the in-situ polymerization of an isocyanate mixture in a polyol. More specifically, the isocyanate mixture typically comprises 80 parts by weight, based on the total weight of the isocyanate mixture, of 2,4-toluene diisocyanate, and 20 parts by weight, based on the total weight of the isocyanate mixture, of 2,6-toluene diisocyanate.

[0084] Suitable amine group containing compounds to be polymerized with the isocyanate compound include in preparing the PHD polyols, for example, compounds such as polyamines, hydrazines, hydrazides, ammonia or mixtures of ammonia and / or urea and formaldehyde.

[0085] Suitable polyamines include divalent and / or higher valent primary and / or secondary aliphatic, araliphatic, cycloaliphatic and aromatic amines, e.g. ethylene diamine; 1,2- and 1,3-propylene diamine; tetramethylene diamine; hexamethylene diamine; dodecamethylene diamine; trimethyl diaminohexane; N,N'-dimethyl-ethylenediamine; 2,2'-bisaminopropyl-methylamine; higher homologues of ethylene diamine, such as diethylene triamine, triethylene tetramine and tetraethylene pentamine; homologues of propylene diamine, such as dipropylene triamine, piperazine, N,N'-bis-aminoethyl-piperazine, triazine, 4-aminobenzylamine, 4-aminophenyl ethylamine, 1-amino-3,3,5-trimethyl-5-aminomethylcyclohexane, 4,4'-diaminodicyclohexyl-methane and -propane, 1,4-diaminocyclohexane, phenylenediamines, naphthylene diamines; condensates of aniline and formaldehyde; tolylene diamines; the bis-aminomethylbenzenes and derivatives of the above mentioned aromatic amines monoalkylated on one or both nitrogen atoms. The polyamines generally have a relative molecular mass of 48 g / mol to 10,000 g / mol. They may also have relative molecular masses of 60 g / mol to 1000 g / mol, or of 62 g / mol to 200 g / mol.

[0086] The hydrazines used may be hydrazine itself or monosubstituted or N,N'-disubstituted hydrazines. The substituents may be C 1 to C 6 alkyl groups, cyclohexyl groups or phenyl groups. The hydrazines generally have a relative molecular mass of 32 g / mol to 200 g / mol. Hydrazine itself is suitable for the invention herein.

[0087] Suitable hydrazides include the hydrazides of divalent or higher valent carboxylic acids such as carbonic acid, oxalic acid, malonic acid, succinic acid, adipic acid, sebacic acid, azelaic acid, maleic acid, fumaric acid, phthalic acid, isophthalic acid, and terephthalic acid; the esters of a hydrazine monocarboxylic acid with dihydric or higher hydric alcohols and phenols such as ethanediol, propane-1,2-diol, butane-1,2-diol, -1,3-diol and -1,4-diol, hexanediol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol and hydroquinone; and the amides of hydrazinomonocarboxylic acid (semicarbazides), e.g. with the above mentioned diamines and polyamines. The hydrazides generally have a relative molecular mass of 70 g / mol to 10,000 g / mol, or of 75 g / mol to 1000 g / mol, or of 90 g / mol to 500 g / mol. Any combination of these upper and lower limits for molecular weights can be used for the hydrazides herein.

[0088] In special cases, a proportion of isocyanates or amines, hydrazines and hydrazides which have an average functionality higher than 2 may also be used, especially in combination with the corresponding monofunctional compounds.

[0089] In accordance with the present invention, preferred base polyols for preparing the PHD polyols comprise polyether polyols and poly(oxyalkylene) polyols.

[0090] PHD polymer modified polyols are typically prepared by the in-situ polymerization of an isocyanate mixture with a diamine and / or hydrazine in a base polyol, preferably, a polyether polyol. Methods for preparing PHD polymer polyols are described in, for example, United States Patents 4,089,835, 4,260,530 and 4,324,715.

[0091] In one embodiment, a foam modifier or foam processing aid is added to the formulation to enhance processing and help stabilize the viscoelastic flexible foam against cold flow and / or dishing by providing dimensional stability against deformation and reduced settling of the viscoelastic flexible foam. These processing aids or modifiers are typically chain extenders and / or cross-linking agents.

[0092] In addition, the foam modifiers or processing aids may have an OH number of at least 300 mg KOH / g or of at least 600 mg KOH / g.

[0093] Suitable blowing agents (C) for the present invention include, for example chemical blowing agents, i.e. isocyanate reactive agents that generate blowing gases, such as for example water and formic acid and physical blowing agents such as acetone, carbon dioxide, chlorofluorocarbons, highly fluorinated and / or perfluorinated hydrocarbons, chlorinated hydrocarbons, aliphatic and / or cycloaliphatic hydrocarbons such as propane, butane, pentane, hexane, etc., or acetals such as methylal. These physical blowing agents are usually added to the polyol component of the system. However, they can also be added in the isocyanate component or as a combination of both the polyol component and the isocyanate component. It is also possible to use them together with highly fluorinated and / or perfluorinated hydrocarbons, in the form of an emulsion of the polyol component. If emulsifiers are used, they are usually oligomeric acrylates which contain polyoxyalkylene and fluoroalkane radicals bonded as side groups and have a fluorine content of 5 to 30% by weight. Such products are sufficiently well known from plastics chemistry, and are described in U.S. Patent 4,972,002.

[0094] The amount of blowing agent or blowing agent mixture used may range from 0.5 to 20% by weight, based on 100% by weight of (B) the isocyanate-reactive component. As used herein with respect to the amount of blowing agent, the isocyanate-reactive component includes (1) the in-situ formed polyol blend having an overall functionality of 2 to 3 and an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g as described herein. In some instances, the amount of blowing agent present may be at least 0.5% or at least 0.75% by weight, based on 100% by weight of component (B). The amount of blowing agent present may also be 20% or less, or 10% by weight or less, based on 100% by weight of component (B). The blowing agent may be present in any amount ranging between any combination of these upper and lower above values, inclusive, such as at least 0.5% to 20% or less, or at least 0.75% to 10% by weight or less, based on 100% by weight of component (B).

[0095] When water is the blowing agent, the amount of water typically present can range from at least 0.5 to 10%, based on 100% by weight of component (B) the isocyanate-reactive component. In some instances, the amount of blowing agent present may be at least 0.5% or at least 0.75% by weight, based on 100% by weight of component (B). The amount of water present as a blowing agent may also be 10% or less, or 7% by weight or less, based on 100% by weight of component (B). The blowing agent may be present in any amount ranging between any combination of these upper and lower values, inclusive, such as at least 0.5% to 10% or less, or at least 0.75% to 7% by weight or less, based on 100% by weight of component (B). The addition of water can be effected in combination with the use of the other blowing agents described. In accordance with the present invention, water is the preferred blowing agent. Also, preferred is the use of water along with pressurized carbon dioxide that is dispersed in the polyol or resin blend and frothed by passing through a pressure let down device such as employed for example in the Henecke Novaflex, CarDio (Cannon Viking Limited) and Beamech (CO 2 ) machines, which are known by those skilled in the art.

[0096] The viscoelastic flexible foam is produced in the presence of a surfactant, which helps to stabilize the viscoelastic flexible foam until it cures. Suitable surfactants are those well known in the polyurethane industry. A wide variety of organosilicone surfactants are commercially available. Examples of suitable surfactants are Niax L-620 surfactant, a product of Momentive Performance Materials, and Tegostab B8244, a product of Evonik-Goldschmidt. Many other silicone surfactants known to those in the art may be substituted for these suitable silicones. The surfactant is typically used in an amount within the range of at least 0.1 to 4 parts, based on 100% by weight of component (B). The surfactant may be present in amounts ranging from at least 0.1, or at least 0.2 parts, based on 100% by weight of component (B).

[0097] The surfactant may be also present in amounts ranging from 4 parts or less, or 3 parts or less, based on 100% by weight of component (B). The amount of surfactant may range between any combination of these upper and lower values, inclusive, such as at least 0.1 to 4 parts, or at least 0.2 to 3 parts, based on 100% by weight of component (B).

[0098] At least one polyurethane catalyst is required to catalyze the reactions of the isocyanate-reactive components and water with the polyisocyanate. It is common to use both an organoamine and an organotin compound for this purpose. Suitable polyurethane catalysts are well known in the art; an extensive list appears in U.S. Patent 5,011,908. Suitable organotin catalysts include tin salts and dialkyltin salts of carboxylic acids. Examples include stannous octoate, dibutyltin dilaurate, dibutyltin diacetate, stannous oleate, and the like. Stannous octoate is particularly preferred. Preferred organoamine catalysts are tertiary amines such as trimethylamine, triethylamine, triethylenediamine, bis(2,2'-dimethyl-amino)ethyl ether, N-ethylmorpholine, diethylenetriamine, and the like.

[0099] The polyurethane catalysts are typically used in an amount within the range of 0.01 to 3 parts, based on 100% by weight of component (B). The polyurethane catalysts may be present in amounts of at least 0.01, or at least 0.1 parts, based on 100% by weight of component (B). The polyurethane catalysts may be present in amounts of 3 parts or less, or 2 parts or less based on 100% by weight of component (B). The polyurethane catalysts may be present in any amount ranging between any combination of these upper and lower values, inclusive, such as at least 0.01 to 3 parts, or at least 0.1 to 2 parts, based on 100% by weight of component (B).

[0100] Flame retardants, antioxidants, pigments, dyes, liquid and solid fillers, and many other commercial additives can also be included in the viscoelastic flexible foams in conventional amounts.

[0101] The viscoelastic foams of the invention comprise the reaction product of (A) a diisocyanate and / or a polyisocyanate component, with (B) an isocyanate-reactive component comprising (1) the in-situ formed polyol blend having an overall functionality of 2 to 3 and an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g which is described herein, in the presence of (C) a blowing agent, (D) a catalyst, and (E) a surfactant. Suitable components for these foams are as described hereinabove.

[0102] The viscoelastic flexible foams are prepared using methods that are well known in the industry. These methods may include continuous or discontinuous free-rise slabstock foam processes and molded foam processes. In a typical slabstock process, the isocyanate is continuously mixed together with the other formulation chemicals by passing through a mixing head and then into a trough which overflows onto a moving conveyor.

[0103] Alternatively, the reacting mixture is deposited directly onto the moving conveyor. In another embodiment, high pressure liquid carbon dioxide is fed into one or more of the formulation components, typically the polyol, entering into the mixing head and the resin blend is passed through a frothing device where the pressure is let down and the resultant froth is deposited onto the conveyor. The viscoelastic flexible foam expands and rises as it moves down the conveyor to form a continuous foam slab that is cut into blocks or buns of the desired length for curing and storage. After curing for one or more days, these foam buns can be cut into the desired shapes for the end-use applications. In the discontinuous process, the reactants are quickly mixed together through a head or in a large mixing chamber. The reaction mixture is then deposited into a large box or other suitable container where foam expansion occurs to form a bun of the lateral dimensions of the container.

[0104] A typical molded viscoelastic flexible foam process usually employs a one-shot approach in which a specific amount of the isocyanate stream (the "A" side) is rapidly combined and mixed with a specific amount of the remaining formulation components (the "B" side). An additional stream may be employed to bring in one or more specific components not included with the "B" side stream. The mixture is quickly deposited into a mold that is then closed. The viscoelastic flexible foam expands to fill the mold and produce a part with the shape and dimensions of the mold.

[0105] Although less preferred, an isocyanate-terminated prepolymer approach to making the viscoelastic flexible foams can also be used. In this approach, a significant portion of the isocyanate-reactive mixture is reacted with the polyisocyanate, and the resulting isocyanate-terminated prepolymer is then reacted with the remaining components.

[0106] As used and referred to throughout the specification, air flow was measured in accordance with the NOPCO test procedure described by R.E. Jones and G. Fesman, "Journal of Cellular Plastics," January, 1965,Vol. No. 1, pp. 200-216 using a Amscor Model 1377 automated foam porosity tester. A 2 inch x 2 inch x 1 inch piece of foam was cut from near the center of the test specimens which itself was cut from the foam blocks after production. Air flow, expressed as standard cubic feet per minute (i.e. scfpm), was measured through the 1 inch thickness at a pressure differential of 0.5 inches of water less than atmospheric pressure (1 inch = 2.54 cm; 1 cubic foot = 28.32 liters). The air flow was in the direction of rise of the foam.

[0107] The test used to define foam recovery rate from deformation is the 95% height recovery time as described in ASTM D3574-17. A recovery rate of less than 3 seconds, indicates a fast recovering foam such as observed for resilient foam types. A recovery rate of greater than or equal to 3 seconds is indicative of a slow recovery foam often referred to as "viscoelastic" or "memory" foam.

[0108] Other viscoelastic flexible foam physical properties reported in the examples were measured per the standard procedures described in ASTM D3574-17 having the title "Standard Test Methods for Flexible Cellular Materials-Slab, Bonded, and Molded Urethane Foams".

[0109] Commercial production of viscoelastic flexible foams involves mixing together a suitable polyisocyanate, and an isocyanate-reactive component which comprises the in-situ formed polyol blend described above, in the presence of a blowing agent, a surfactant, a catalyst, and optionally, various other compounds which are known in the field of polyurethane chemistry to be suitable for preparing viscoelastic flexible foams.

[0110] Those skilled in the art will readily understand that known variations of the conditions of the following procedures can be used. Unless otherwise noted, all temperatures are degrees Celsius and all parts and percentages are parts by weight and percentages by weight, respectively.EXAMPLES

[0111] Test Methods: The physical properties reported herein were measured per the standard procedures described in ASTM D3574-17 having the title "Standard Test Methods for Flexible Cellular Materials-Slab, Bonded, and Molded Urethane Foams" unless otherwise stated.

[0112] Hydroxyl Numbers: The overall hydroxyl numbers were determined in accordance with ASTM D-4274-11, and are reported in mg KOH / g.

[0113] Viscosity: The viscosities of the polyether polyols were determined at 25°C using an Anton Paar SVM 3000 / G2 Stabinger Viscometer.

[0114] Other foam physical properties reported herein were measured per the standard procedures described in ASTM D3574-17.

[0115] As used herein, "pphp" represents parts per hundred parts polyol.

[0116] The following materials were used in the working examples: Polyol A:An in-situ formed multifunctional polyol prepared by alkoxylating a monol, diol, and triol with a DMC catalyst. The starter comprises a 1600 g / mol MW (35 mg KOH / g) OH#) monol made from the propoxylation of Neodol 25 (a blend of C12, C13, C14 and C15 high purity, lightly branched, primary alcohols produced by Shell). 3390 g of this 1600 g / mol MW monol are alkoxylated with 3287 g of a mixture of propylene oxide and ethylene oxide in a weight ratio of 82 / 18 to a hydroxyl number of 17.8 mg KOH / g. The alkoxide mixture was charged at a combined feed rate of 60.26 g / min. The resulting 17.8 hydroxyl number monol contains a total of 8.5% ethylene oxide. Next, a mixture of 1107 g glycerin and propylene glycol in a 62.3 to37.7 wt% ratio was continuously added at a combined feed rate of 7.91 g / min along with mixture of 8437 g propylene oxide and ethylene oxide in a weight ratio of 82 / 18 until a calculated hydroxyl number of 123 mg KOH / g was reached. The alkoxide mixture was charged at a combined feed rate of 60.26 g / min. At this point, the propylene glycol and glycerin feeds were stopped and an additional 441 g of the propylene oxide and ethylene oxide mixture were continuously added until a calculated hydroxyl number of 120 mg KOH / g was reached. At this point the reactor contains a mixture of the previously mentioned 17.8 mg KOH / g hydroxyl number monol, a diol intermediate with a calculated hydroxyl number of 187 mg KOH / g and a triol intermediate with a calculated hydroxyl number of 187 mg KOH / g. At this point 3333 g of a mixture of propylene oxide and ethylene oxide were continuously added in a weight ratio of 55 / 45 at a combined feed rate of 60.26 g / min until the calculated hydroxyl number of the diol and triol components reached 140 mg KOH / g. The diol and triol components each contain a total of 23 % ethylene oxide with 12 % ethylene oxide in the internal block and 11% ethylene oxide in the external block. This in-situ formed polyol blend contains 33 weight % monol, 22 weight % diol and 45 weight % triol. The in-situ formed polyol blend had an overall functionality of 2.4, total ethylene oxide content of 18.5% and an overall hydroxyl number of 100 mg KOH / g.Polyol B:An in-situ formed multifunctional polyol blend prepared by first alkoxylating a monol, diol, and triol with a DMC. The starter comprised a 1600 g / mol MW (35 mg KOH / g OH#) monol made from the propoxylation of Neodol 25 (a blend of C12, C13, C14 and C15 high purity, lightly branched, primary alcohols produced by Shell). 3030 g of this 1600 g / mol MW monol are alkoxylated with 2938 g of a mixture of propylene oxide and ethylene oxide in a weight ratio of 82 / 18, respectively, to a calculated hydroxyl number of 17.8 mg KOH / g. The alkoxide mixture was charged at a combined feed rate of61.56 g / min. The resulting 17.8 mg KOH / g hydroxyl number monol contains a total of 8.5% ethylene oxide. Next, a mixture of 984 g glycerin and propylene glycol in a 62.2 to 37.8 wt% ratio was continuously added at a combined feed rate of 8.05 g / min along with mixture of 7523 g propylene oxide and ethylene oxide in a weight ratio of 82 / 18 until a calculated hydroxyl number of 123 mg KOH / g was reached. The alkoxide mixture was charged at a combined feed rate of 61.56 g / min. At this point, the propylene glycol and glycerin feeds were stopped and an additional 396 g of the propylene oxide and ethylene oxide mixture were continuously added until a calculated hydroxyl number of 120 mg KOH / gwas reached. At this point the reactor contains a mixture of the previously mentioned 17.8 mg KOH / g calculated hydroxyl number monol, a diol intermediate with a calculated hydroxyl number of 187 mg KOH / g and a triol intermediate with a calculated hydroxyl number of 187 mg KOH / g. At this point 2975 g of a mixture of propylene oxide and ethylene oxide were continuously added in a weight ratio of 55 / 45 at a combined feed rate of 61.56 g / min until the calculated hydroxyl number of the diol and triol components reached 140 mg KOH / g. The diol and triol components each contain a total of 23 % ethylene oxide with 12 % ethylene oxide in the internal block and 11% ethylene oxide in the external block. After this the ethylene oxide feed was stopped and 1784 g of propylene oxide and 168 g of glycerin were then continuously added at feed rates of 61.56 and 5.79 g / min respectively, until the calculated hydroxyl number of the triol propoxylate reached 149 mg KOH / g. After this the glycerin feed was stopped and an additional 198 g of propylene oxide was continuously added until a calculated hydroxyl number of 140 mg KOH / g was reached for the triol propoxylate. This in-situ formed polyol blend now contains 30 weight % of a monol containing 8.5 % ethylene oxide, 19 weight % of a diol containing 23% ethylene oxide, 40 weight % of a triol containing 23% ethylene oxide and 11% of a triol propoxylate. The in-situ formed polyol blend had an overallfunctionality of 2.4, total ethylene oxide content of 16.4% and an overall hydroxyl number of 104 mg KOH / g.Polyol C:An in-situ formed multifunctional polyol blend prepared by first alkoxylating a monol, diol, and triol with a DMC catalyst. The starter comprises a 1600 g / mol MW (35 mg KOH / g OH#) monol made from the propoxylation of Neodol 25 (a blend of C12, C13, C14 and C15 high purity, lightly branched, primary alcohols produced by Shell). 3030 g of this 1600 MW monol are alkoxylated with 2939 g of a mixture of propylene oxide and ethylene oxide in a weight ratio of 85 / 15, respectively, to a calculated hydroxyl number of 17.8 mg KOH / g. The alkoxide mixture was charged at a combined feed rate of 61.56 g / min. The resulting 17.8 mg KOH / g calculated hydroxyl number monol contains a total of 8.5% ethylene oxide. Next, a mixture of 1152 g glycerin and propylene glycol in a 67.7 to 32.3 wt% ratio was continuously added at a combined feed rate of 7.54 g / min along with mixture of 9408 g propylene oxide and ethylene oxide in a weight ratio of 85 / 15 until a calculated hydroxyl number of 126 mg KOH / g was reached. The alkoxide mixture was charged at a combined feed rate of 61.56 g / min. At this point, the propylene glycol and glycerin feeds were stopped and an additional 495 g of the propylene oxide and ethylene oxide mixture were continuously added until a calculated hydroxyl number of 123 mg KOH / g was reached. At this point the reactor contains a mixture of the previously mentioned 17.8 mg KOH / g calculated hydroxyl number monol, a diol intermediate with a calculated hydroxyl number of 187 mg KOH / g and a triol intermediate with a calculated hydroxyl number of 187 mg KOH / g. At this point 2976 g of a mixture of propylene oxide and ethylene oxide were continuously added in a weight ratio of 55 / 45 at a combined feed rate of 61.56 g / min until the calculated hydroxyl number of the diol and triol components reached 140 mg KOH / g. The diol and triol components each contain a total of 20 % ethylene oxide with 10.5 % ethylene oxide in the internal block and 9.5 % ethylene oxide in the externalblock. This in-situ formed polyol blend contains 30 weight % monol, 19 weight % diol and 51 weight % triol. The in-situ formed polyol blend had an overall functionality of 2.4, total ethylene oxide content of 16.4% and an overall hydroxyl number of about 103 mg KOH / g.Polyol D:A glycerin started poly(oxypropyleneoxyethylene) polyol having a hydroxyl number of 37 mg KOH / g, and containing 73% of copolymerized oxyethylenePolyol E:A glycerin starter poly(oxypropylene) polyol having a hydroxyl number of 168 mg KOH / gFoam Modifier A:A foam modifier having a hydroxyl number of 1240 mg KOH / g, commercially available from Momentive Performance Materials as Arcol DP-1022Foam Modifier B:A delayed action crosslinking agent available from Evonik Industries as Ortegol 204Surfactant A:A silicone surfactant commercially available from Momentive Performance Materials as Niax L-618Catayst A:An amine catalyst, commercially available from Momentive Performance Materials as Niax A-33Catalyst B:An amine catalyst, commercially available from Momentive Performance Materials as Niax A-1Catalyst C:Tin octoate, commercially available from Evonik as Dabco T-9Isocyanate A:Toluene diisocyanate having 80% of the 2,4 isomer and 20% of the 2,6 isomer

[0117] The free-rise bench scale foams of Table 1 were prepared using the following procedure. The polyols, water, silicone surfactants, amine catalysts, and any other non-isocyanate additives were added to a cylindrical container fitted with baffles. The contents were mixed at 2400 rpm for 60 seconds with an agitator having two turbine impellers. Tin Catalyst C, if employed, was added at this time. The mixture was then degassed for 15 seconds. After degassing, the contents were mixed at 2400 rpm for 15 seconds, during which period the isocyanate was added when 10 seconds of mixing time remained. The mixture was then poured into a 14 x 14 x 6-inch cardboard box, where it rose freely until the reaction was complete. A batch size sufficient to give a bun at least 6 inches high was employed. The freshly prepared bun was cured for 20 minutes in an oven at 120°C and then allowed to cure at ambient conditions for a minimum of 1 day. Observations made during foaming and curing are set forth in the Tables. The buns were then trimmed to 12 x 12 x 4 inches and were roller crushed 3 times to a minimum thickness of 0.5 inches. These samples were then conditioned for at least 16 hours at standard temperature (~23°C) and humidity (~50%) before being tested. Table 1: Foam Formulations Isocyanate-Reactive Component Example 1 (control)Example 2Example 3Polyol A83.00Polyol B93.00Polyol C93.00Polyol D7.007.007.00Polyol E10.00Surfactant A0.800.800.80Foam Modifier A1.501.501.50Foam Modifier B0.600.600.60Water (distilled)1.101.101.10Catalyst A0.580.580.58Catalyst B0.070.070.07Catalyst C0.030.030.03A-Side (isocyanate) Isocyanate A31.9331.6831.54Isocyanate Index100.00100.00100.00 Table 2: Foam Properties Physical Properties Units Example 1 Example 2 Example 3 Actual Densitykg / m 3< (lb / ft 3< )61.4 (3.83)60.4 (3.77)60.7 (3.79)Airflowm 3< / min (ft 3< / min)0.153 (5.41)0.139 (4.92)0.137 (4.85)IFD 25%N (lbf)43.1 (9.70)45.6 (10.26)50.4 (11.32)IFD 65%N (lbf)98.1 (22.07)102.2 (22.97)110.9 (24.94)IFD 25% ReturnN (lbf)40.1 (9.03)42.2 (9.49)46.9 (10.55)Return Val. 25%%93.0392.593.25S.F. 65% / 25%NA2.272.242.2Tensile StrengthkPa (psi)72.59 (10.53)73.56 (10.67)60.63 (8.78)Elongation%253.43251.3231.3Tear StrengthN / m (pli)196.2 (1.12)187.4 (1.07)189.1 (1.08)75% Compression Set%1.401.521.5290% Compression Set%1.701.91.9775% HACS%1.781.631.76Resilience (Ball Rebound)%1.471.03.850% Wet Set%0.520.650.6975% Wet Set%0.370.650.6890% Wet Set%0.220.330.69Visco RecoverySec4.594.52ND* *ND - Not Determined Example 1 is a control of a blended polyol which is not made in-situ. Example 2 is representative of the invention. Example 3 is a comparative example.

Claims

1. An in-situ formed polyol blend having an overall functionality of 2 to 3, an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, and comprising: (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on the total weight of monol initiated oxyalkylene ether (a); (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / gto 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (b); (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / gto 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (c); and (d) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% by weight of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein said in-situ formed polyol blend comprises from 10 to 40% by weight of said monol initiated oxyalkylene ether (a), from 10 to 30% by weight of said polyether polyol (b), from 20 to 65% by weight of said polyether polyol (c), and from 5 to 20% by weight of said polyether polyol (d), with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of said in-situ formed polyol blend.

2. The in-situ formed polyol blend of Claim 1, wherein (d) the polyether polyol has a functionality of at least 3 and a calculated hydroxyl number of 100 mg KOH / g to 180 mg KOH / g.

3. The in-situ formed polyol blend of Claim 1 or claim 2, wherein the monol initiated oxyalkylene ether (a) comprises an oxypropylene block next to the monofunctional starter followed by a mixed oxyalkylene block at the end of the chain which comprises copolymerized oxypropylene and copolymerized oxyethylene, wherein the mixed oxyalkylene block at the end of the chain which comprises copolymerized oxypropylene and copolymerized oxyethylene contains 20% by weight or less of copolymerized oxyethylene, based on 100% by weight of the mixed oxyalkylene block.

4. The in-situ formed polyol blend of one of Claim 1 to claim 3, wherein the polyether polyol (b) has an initial mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing 20% by weight or less of copolymerized oxyethylene, based on 100% by weight of the mixed oxyalkylene block, which is followed by a second mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing at least 40% by weight of copolymerized oxyethylene, based on 100% by weight of the second mixed oxyalkylene block.

5. The in-situ formed polyol blend of one of Claim 1 to claim 4, wherein the polyether polyol (c) has an initial mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing 20% by weight or less of copolymerized oxyethylene, based on 100% by weight of the mixed oxyalkylene block, which is followed by a second mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing at least 40% by weight of copolymerized oxyethylene, based on 100% by weight of the second mixed oxyalkylene block.

6. The in-situ formed polyol blend of one of Claim 1 to claim 5, which comprises from 25 to 35% by weight of said monol initiated oxyalkylene ether (a); from 15 to 25% of said polyether polyol (b); from 30 to 55% by weight of said polyether polyol (c); and from 5 to 15% by weight of said polyether polyol (d), with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of the in-situ formed polyol blend.

7. A process of preparing the in-situ formed polyol blend having an overall functionality of 2 to 3, and an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, comprising: I) introducing into a reaction vessel a mixture comprising: (1) an initially charged starter (Si) comprising a monofunctional compound having a calculated hydroxyl number of less than or equal to 80 mg KOH / g, and (2) a DMC (double metal cyanide) catalyst; II) feeding (1) an epoxide comprising propylene oxide and ethylene oxide in a weight ratio of 100:0 to 80:20, into the reaction vessel; III) allowing the epoxide mixture and the initially charged starter (Si) to react and to polymerize by feeding the epoxide until the equivalent weight of the monofunctional compound is increased by at least 10% by weight and reaches a value between 1,500 g / mol and 6,000 g / mol; IV) continuously adding (1) a continuously added starter (Sc) having a nominal functionality of greater than 2 to 6, and an equivalent weight of 28 g / mol to 400 g / mol into the reaction vessel while continuing to feed epoxide; V) completing addition of the continuously added starter (Sc); VI) allowing the mixture to continue to polymerize in the reaction vessel thereby forming (1) an intermediate in-situ formed polyol blend which has an overall calculated hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, an overall functionality of 2 to 3, and which comprises (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on 100% by weight of (a), (b) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of 2 and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of the polyether polyol (b), and (c) a polyether polyol having a calculated hydroxyl number of 80 mg KOH / g to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of the polyether polyol (c); VII) feeding (1) an epoxide comprising propylene oxide while continuously adding (2) a continuously added starter (Sc) having a nominal functionality of 2 to 8, and an equivalent weight of 28 g / mol to 400 g / mol into the reaction vessel; VIII) completing addition of the continuously added starter (Sc) and epoxide thereby forming in addition to (a), (b) and (c); (d) a polyether polyol having a calculated hydroxyl number of 80 to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein said in-situ formed polyol blend comprises from 10 to 40% by weight of said monol initiated oxyalkylene ether (a), from 10 to 30% by weight of said polyether polyol (b), from 20 to 65% by weight of said polyether polyol (c), and from 5 to 20% by weight of said polyether polyol (d), with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of said in-situ formed polyol blend.

8. The process of Claim 7, wherein the monol initiated oxyalkylene ether (a) comprises an oxypropylene block next to the monofunctional starter followed by a mixed oxyalkylene block at the end of the chain which comprises copolymerized oxypropylene and copolymerized oxyethylene, wherein the mixed oxyalkylene block at the end of the chain which comprises copolymerized oxypropylene and copolymerized oxyethylene contains 20% by weight or less of copolymerized oxyethylene, based on 100% by weight of the mixed oxyalkylene block.

9. The process of Claim 7 or claim 8, wherein the polyether polyol (b) has an initial mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing 20% by weight or less of copolymerized oxyethylene, based on 100% by weight of the mixed oxyalkylene block, which is followed by a second mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing at least 40% by weight of copolymerized oxyethylene, based on 100% by weight of the second mixed oxyalkylene block.

10. The process of one of claim 7 to Claim 9, wherein the polyether polyol (c) has an initial mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing 20% by weight or less of copolymerized oxyethylene, based on 100% by weight of the mixed oxyalkylene block, which is followed by a second mixed oxyalkylene block which comprises copolymerized oxypropylene and copolymerized oxyethylene containing at least 40% by weight of copolymerized oxyethylene, based on 100% by weight of the second mixed oxyalkylene block.

11. The process of one of Claim 7 to claim 10, wherein said initially charged starter (Si) has a calculated hydroxyl number of less than 56 mg KOH / g.

12. The process of one of Claim 7 to claim 11, wherein said initially charged starter (Si) comprises a monol initiated oxyalkylene ether which comprises the reaction product of a monofunctional starter and an epoxide.

13. The process of one of Claim 7 to claim 12, wherein said in-situ formed polyol blend comprises from 25 to 35% by weight of said monol initiated oxyalkylene ether (a); from 15 to 25% of said polyether polyol (b); from 30 to 55% by weight of said polyether polyol (c); and from 5 to 15% by weight of said polyether polyol (d), with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of said in-situ formed polyol blend.

14. An isocyanate-reactive component comprising (1) said in-situ formed polyol blend of one of Claim 1 to claim 6, and (2) at least one of (2)(a) a polyether polyol having a calculated hydroxyl number of 20 to 240 mg KOH / g, an average functionality of 2 to 8, and containing at least 50% of copolymerized oxyethylene, based on 100% by weight of component (2)(a), and (2)(b) a filled polyol.

15. A viscoelastic flexible polyurethane foam comprising the reaction product of: (A) a diisocyanate and / or polyisocyanate component, (B) an isocyanate-reactive component comprising: (1) an in-situ formed polyol blend having an overall functionality of 2 to 3, an overall hydroxyl number of 50 mg KOH / g to 150 mg KOH / g, which comprises: (a) a monol initiated oxyalkylene ether having a calculated hydroxyl number of less than or equal to 56 mg KOH / g, and containing less than or equal to 20% by weight of copolymerized oxyethylene, based on the total weight of monol initiated oxyalkylene ether (a), (b) a polyether polyol having a calculated hydroxyl number of 80 to 220 mg KOH / g, a nominal functionality of 2, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (b), (c) a polyether polyol having a calculated hydroxyl number of 80 to 220 mg KOH / g, a nominal functionality of greater than 2 to 8, and containing from 5 to 45% by weight of copolymerized oxyethylene, based on the total weight of polyether polyol (c), and (d) a polyether polyol having a calculated hydroxyl number of 80 to 220 mg KOH / g, a nominal functionality of 2 to 8, and containing 100% of polyoxypropylene, based on the total weight of polyoxyalkylene in polyether polyol (d); wherein said in-situ formed polyol blend comprises from 10 to 40% by weight of said monol initiated oxyalkylene ether (a), from 10 to 30% by weight of said polyether polyol (b), from 20 to 65% by weight of polyether polyol (c), and from 5 to 20% by weight of polyether polyol (d), with the sum of the %'s by weight of (a), (b), (c) and (d) totaling 100% by weight of said in-situ formed polyol blend; in the presence of: (C) a blowing agent; (D) a catalyst; and (E) a surfactant.