Epoxy resin curable composition and adhesive containing the same

Abstract

Provided is an epoxy resin curable composition that cures quickly and has a high hardness and excellent color tone after curing. This epoxy resin curable composition, which contains an epoxy resin hav

Description

Technical Field

[0001] The present invention relates to an epoxy resin curable composition that cures quickly, has high hardness after curing, has strong adhesive strength, and provides a cured product having an excellent color tone. Background Art

[0002] In the related art, an epoxy resin has excellent adhesiveness, chemical resistance, and physical properties, and is widely used as an adhesive and the like. For applications requiring rapid curing and high adhesive strength, a method of adding a thiol compound as a curing agent and amines as a curing accelerator is known.

[0003] Many terminal thiol group-containing compounds having no polysulfide skeleton in the main chain have been reported as compounds capable of rapidly reacting a thiol group with an epoxy group (see, for example, Patent Literature 1). Among them, as a curing agent for an epoxy resin having both economic efficiency and safety, a 28 02 25 compound containing a polyether skeleton in the main chain and containing three or more thiol groups in one molecule is widely commercially available. Examples of the compound containing a polyether skeleton in the main chain and three or more thiol groups in one molecule include "Polythiol QE-340M" manufactured by Toray Fine Chemicals Co., Ltd., and "Capcure (Registered Trade Mark (RTM))3-800" and "GPM-800" manufactured by Gabriel Performance Products, LLC.

[0004] Examples of an amine widely used as a curing accelerator for a thiol group and an epoxy group include tertiary amines such as 2,4,6-tris(dimethylaminomethyl) phenol (ANCAMINE (RTM) K-54 manufactured by Evonik Industries AG), N,N-dimethylpropylamine, and bis (2-dimethylaminoethyl) ether.

[0005] However, an epoxy resin curable composition known in the related art turns yellow and is colored when cured, and thus has a problem in applications required to be close to colorless and to have an excellent color tone, such as an adhesive for glass and an adhesive for a decorative item.

[0006] A colorless epoxy resin curable composition known in the related art cures slowly, is not suitable for applications requiring rapid curing, and does not 28 02 25 necessarily have sufficient hardness and adhesive strength. As described above, it has been difficult for an epoxy resin curable composition containing an epoxy resin, a thiol compound, and an amine compound to have quick curing, hardness, adhesive strength, and a color tone. Citation List Patent Literature

[0007] Patent Literature 1: JP 8-269203 A Summary of Invention Technical Problem

[0008] The present invention provides an epoxy resin curable composition that cures quickly, has high hardness after curing, and has an excellent color tone. Solution to Problem

[0009] An epoxy resin curable composition of the present invention contains an epoxy resin containing two or more epoxy groups in one molecule, a thiol compound A containing two or more thiol groups in one molecule, an amine compound containing two or more primary amino groups and / or 28 02 25 secondary amino groups in one molecule and containing no tertiary amino group, and a thiol compound B represented by any one of the following General Formulas (1) to (3), in which the thiol compound A and the thiol compound B are different from each other, and a molar ratio Ma / Mo is 0.29 to 0.80 and a molar ratio Me / Me is 0.02 to 0.4, in which Me is the number of moles of the epoxy groups contained in the epoxy resin curable composition, Ma is the number of moles of the thiol groups in the thiol compound A, and Mb is the number of moles of the thiol groups in the thiol compound B, (Ra) n — C— (R3-O~CO-R1-SH) 4-n (1) (in General Formula (1), Rx,s each independently represent an alkylene group having 1 to 10 carbon atoms, R2 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, R3' s each independently represent an alkylene group having 1 to 3 carbon atoms, n represents an integer of 0 to 2, and -SH is bonded to any carbon atom of R1), [Chern. 1] (R2) n-C-(R^-O-R^SH) 4-n (3) (in General Formula (3), R2,s each independently represent an alkylene group having 1 to 10 carbon atoms, R2 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, R3's each independently represent an alkylene group having 1 to 3 carbon atoms, n represents an integer of 0 to 2, and -SH is bonded to any carbon atom of R1) . 28 02 25 Advantageous Effects of Invention

[0010] The epoxy resin curable composition of the present invention cures quickly, has high hardness after curing, and has strong adhesive strength and an excellent color tone .

[0011] When the epoxy resin curable composition of the present invention is used as an adhesive, the adhesive strength is strong to various adherends such as a metal and glass. The epoxy resin curable composition can be used as an adhesive, a sealing material, a potting material, a coating agent, a modifier for a resin, or the like.

[0012] In particular, since the epoxy resin curable composition of the present invention has an excellent color 28 02 25 tone, it is optimal for an adhesive for glass, an adhesive for a decorative item, an adhesive for a timepiece part, an adhesive for electrical and electronic applications, a potting material for electrical and electronic applications, and an adhesive for DIY. Description of Embodiments

[0013] The epoxy resin curable composition of the present invention contains an epoxy resin containing two or more epoxy groups in one molecule, a thiol compound A containing two or more thiol groups in one molecule, an amine compound containing two or more primary amino groups and / or secondary amino groups in one molecule and containing no tertiary amino group, and a thiol compound B that is represented by a specific structural formula and is different from the thiol compound A.

[0014] Examples of the epoxy resin containing two or more epoxy groups in one molecule include an epoxy resin obtained by adding epichlorohydrin to a polyhydric phenol such as bisphenol A, bisphenol F, resorcinol, hydroquinone, pyrocatechol, 4,4-dihydroxybiphenyl, or 1,5-hydroxynaphthalene, an epoxy resin obtained by adding epichlorohydrin to a polyhydric alcohol such as ethylene 28 02 25 glycol, propylene glycol, or glycerin, an epoxy resin obtained by adding epichlorohydrin to an aromatic dicarboxylic acid such as oxybenzoic acid or phthalic acid, and a polysulfide polymer containing an epoxy group at a terminal (trade names: "FLEP-50" and "FLEP-60", both manufactured by Toray Fine Chemicals Co., Ltd.). The epoxy resin containing two or more epoxy groups in one molecule is preferably a liquid at normal temperature from the viewpoint of workability and suppression of mixing failure. Examples of the epoxy resin containing two or more epoxy groups in one molecule include jER-828 (trade name, manufactured by Mitsubishi Chemical Group Corporation), DER-331 (trade name, manufactured by The Dow Chemical Company), jER-825 (trade name, manufactured by Mitsubishi Chemical Group Corporation), jER-827 (trade name, manufactured by Mitsubishi Chemical Group Corporation), jER-806 (trade name, manufactured by Mitsubishi Chemical Group Corporation), and jER-807 (trade name, manufactured by Mitsubishi Chemical Group Corporation).

[0015] An epoxy equivalent of the epoxy resin containing two or more epoxy groups in one molecule is preferably 50 to 1,000 g / eq. The epoxy equivalent of the epoxy resin containing two or more epoxy groups in one molecule is more preferably 100 to 300 g / eq.

[0016] 28 02 25 When the epoxy resin curable composition contains at least two types of thiol compounds including the thiol compound A and the thiol compound B, the epoxy resin curable composition cures quickly, has high hardness after curing, and has high adhesive strength and an excellent color tone.

[0017] The thiol compound B is a compound different from the thiol compound A, and is a thiol compound represented by any one of the following General Formulas (1) to (3). (Rr) n — C— (R3-O~CO-R1-SH) 4-n (1) (In General Formula (1), Rx,s each independently represent an alkylene group having 1 to 10 carbon atoms, R2 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, R3' s each independently represent an alkylene group having 1 to 3 carbon atoms, n represents an integer of 0 to 2, and -SH is bonded to any carbon atom of R1. ) [Chern. 2] 28 02 25 (R2) n-C-(R^-O-R^SH) 4-n (3) (In General Formula (3), R2,s each independently represent an alkylene group having 1 to 10 carbon atoms, R2 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, R3's each independently represent an alkylene group having 1 to 3 carbon atoms, n represents an integer of 0 to 2, and -SH is bonded to any carbon atom of R1. )

[0018] In General Formula (1), a plurality of R2,s are each independently an alkylene group having 1 to 10 carbon atoms, preferably an alkylene group having 2 to 7 carbon atoms, more preferably an alkylene group having 2 to 4 carbon atoms. The plurality of R2,s may be the same as or different from each other. Examples of the alkylene group R1 include a methylene group, an ethylene group, a propylene group, a 1-methylethylene group, a butylene group, an ethylethylene group, and a dimethylethylene group .

[0019] In General Formula (1), a plurality of R3's are each independently an alkylene group having 1 to 3 carbon atoms and preferably an alkylene group having 1 to 2 carbon atoms. The plurality of R3's may be the same as or different from each other. Examples of the alkylene group 28 02 25 R3 include a methylene group, an ethylene group, a propylene group, and a methylethylene group.

[0020] In General Formula (1), a plurality of R2's are each independently a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, and preferably hydrogen, an alkyl group having 1 to 4 carbon atoms, or a hydroxyalkyl group having 1 to 2 carbon atoms. The plurality of R3' s may be the same as or different from each other. Examples of the alkyl group R3 include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, and a tert-butyl group. Examples of the hydroxyalkyl group include a methylol group, a hydroxyethyl group, and a hydroxypropyl group.

[0021] In General Formula (1), n represents an integer of 0 to 2, and -SH is bonded to any carbon atom constituting the alkylene group R1.

[0022] Examples of the thiol compound B represented by General Formula (1) include l,4-bis(3-mercaptopropionyloxy) butane, 1,4-bis (3-mercaptobutyryloxy)butane, trimethylolpropane tris(3-mercaptopropionate), trimethylolpropane tris(3- 28 02 25 mercaptobutyrate), trimethylolpropane tris(3-mercaptoisobutyrate), trimethylolpropane tris(2-mercaptoisobutyrate), trimethylolpropane tristhioglycolate, pentaerythritol tetrakis(3-mercaptopropionate), pentaerythritol tetrakis(3-mercaptobutyrate), pentaerythritol tetrakis(3-mercaptoisobutyrate), pentaerythritol tetrakis(2-mercaptoisobutyrate), and pentaerythritol tetrakisthioglycolate.

[0023] In General Formula (3), a plurality of Ri's are each independently an alkylene group having 1 to 10 carbon atoms, preferably an alkylene group having 2 to 7 carbon atoms, more preferably an alkylene group having 2 to 4 carbon atoms. The plurality of R3's may be the same as or different from each other. Examples of the alkylene group R1 include a methylene group, an ethylene group, a propylene group, a 1-methylethylene group, a butylene group, an ethylethylene group, and a dimethylethylene group .

[0024] In General Formula (3), a plurality of R3's are each independently an alkylene group having 1 to 3 carbon atoms and preferably an alkylene group having 1 to 2 carbon atoms. The plurality of R3's may be the same as or different from each other. Examples of the alkylene group 28 02 25 R3 include a methylene group, an ethylene group, a propylene group, and a methylethylene group.

[0025] In General Formula (3), a plurality of R2's are each independently a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, and preferably hydrogen, an alkyl group having 1 to 4 carbon atoms, or a hydroxyalkyl group having 1 to 2 carbon atoms. The plurality of R3' s may be the same as or different from each other. Examples of the alkyl group R3 include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, and a tert-butyl group. Examples of the hydroxyalkyl group include a methylol group, a hydroxyethyl group, and a hydroxypropyl group.

[0026] In General Formula (3), n represents an integer of 0 to 2, and -SH is bonded to any carbon atom constituting the alkylene group R1.

[0027] Examples of the thiol compound B represented by General Formula (3) include trimethylolpropane monopropanethiol, trimethylolpropane bis(propanethiol), trimethylolpropane tris(propanethiol), pentaerythritol monopropanethiol, pentaerythritol bis(propanethiol), pentaerythritol tris(propanethiol), and pentaerythritol 28 02 25 tetrakis(propanethiol).

[0028] The thiol compound A is a compound different from the thiol compound B described above, and is a thiol compound containing two or more thiol groups in one molecule. The thiol compound A preferably contains a polyether moiety in the main chain, and may contain a thiol group on a carbon adjacent to a carbon having a hydroxy group. Furthermore, the thiol compound A preferably does not contain a carbonyl group. When the thiol compound A does not contain a carbonyl group, hydrolysis of a cured product is suppressed and water resistance is improved, which is preferable.

[0029] A structure having a polyether moiety in the main chain is preferably represented by the following General Formula (4), and a terminal thiol group is preferably represented by the following Formula (5). [Chern. 3] R1 (4) (Where, R1 is a residue obtained by removing m hydrogen atoms from a polyvalent amine or polyhydric alcohol having 10 or fewer carbon atoms, R2 is an alkylene 28 02 25 group having 2 to 4 carbon atoms, n is an integer of 1 to 200, and m is an integer of 2 to 8.) [Chern. 4] ---CH2CHCH2SH (5) I OH

[0030] In General Formula (4), R1 is a residue obtained by removing m hydrogen atoms from a polyvalent amine or polyhydric alcohol having 10 or fewer carbon atoms. Examples of the polyvalent amine or polyhydric alcohol having 10 or fewer carbon atoms include glycerin, trimethylolpropane, trimethylolethane, hexanetriol, diglycerin, pentaerythritol, triethanolamine, ethylenediamine, and sucrose. These polyvalent amines and polyhydric alcohols may be used alone or in combination. Among the polyols described above, glycerin, trimethylolpropane, and trimethylolethane are particularly preferable .

[0031] In General Formula (4), R2 is an alkylene group having 2 to 4 carbon atoms. Examples of the alkylene group having 2 to 4 carbon atoms include ethylene, n-propylene, isopropylene, n-butylene, and isobutylene.

[0032] 28 02 25 In General Formula (4), n is an integer of 1 to 200 and preferably an integer of 1 to 100. In addition, m is an integer of 2 to 8 and preferably an integer of 2 to 5.

[0033] Examples of the thiol compound A that has a structure represented by General Formulas (4) and (5) and does not contain a carbonyl group include "Polythiol QE-340M" manufactured by Toray Fine Chemicals Co., Ltd., and "Capcure (RTM) 3-800" and "GPM-800" manufactured by Gabriel Performance Products, LLC.

[0034] The thiol compound A containing two or more thiol groups in one molecule preferably contains at least one thiol group represented by Formula (5), and more preferably contains two or more thiol groups. In the thiol compound A, all thiol groups may be contained as a structure represented by Formula (5).

[0035] In the thiol compound A containing two or more thiol groups in one molecule, a content of the thiol groups is preferably 1 to 50 mass%, and the content of the thiol groups is more preferably 5 to 20 mass%.

[0036] The fact that the thiol compound A does not contain a carbonyl group means that the thiol compound A does not 28 02 25 contain a carbonyl group, a carboxy group, a thiocarboxy group, an amide group, an ester bond, a thioester bond, and the like.

[0037] In the epoxy resin and the thiol compound described above, a molar ratio Ma / Mo of the number of moles Ma of the thiol groups derived from the thiol compound A to the number of moles Me of the epoxy groups derived from the epoxy resin present in the epoxy resin curable composition is 0.29 to 0.8, and a molar ratio Ms / Me of the number of moles Me of the thiol groups derived from the thiol compound B to the number of moles Me of the epoxy groups derived from the epoxy resin present in the epoxy resin curable composition is 0.02 to 0.4.

[0038] When the molar ratio MA / Me is less than 0.29, a curing rate is reduced. In addition, when the molar ratio Ma / Mo exceeds 0.8, a Shore D hardness of the cured product of the epoxy resin curable composition cannot be increased. On the other hand, when the molar ratio MB / Me is less than 0.02, the Shore D hardness of the cured product cannot be increased. In addition, when the molar ratio Ms / Me exceeds 0.4, the Shore D hardness of the cured product of the epoxy resin curable composition is rather decreased. A blending amount of each component can be determined so that the 28 02 25 molar ratio Ma / Me is preferably 0.29 to 0.7, more preferably 0.29 to 0.65, and still more preferably 0.29 to 0.57. The blending amount of each component can be determined so that the molar ratio Mb / Mo is preferably 0.02 to 0.3, more preferably 0.03 to 0.2, and still more preferably 0.04 to 0.14.

[0039] In the epoxy resin curable composition, a molar ratio Mb / Ma of the number of moles Mb of the thiol groups derived from the thiol compound B to the number of moles Ma of the thiol groups derived from the thiol compound A present in the composition is 0.02 to 0.5, preferably 0.04 to 0.4, and more preferably 0.13 to 0.34. When the molar ratio Mb / Ma is 0.02 or more, the Shore D hardness of the cured product is increased, which is preferable. In addition, the molar ratio Mb / Ma is 0.5 or less, the curing rate is increased, which is preferable.

[0040] The blending amount of the thiol compound A can be appropriately designed so as to satisfy the molar ratio Ma / Mo described above and preferably to satisfy the molar ratio Mb / Ma according to the physical properties of the epoxy resin curable composition. For example, it is preferable to blend 50 to 150 parts by mass of the thiol compound A with respect to 100 parts by mass of an epoxy 28 02 25 resin containing two or more epoxy groups in one molecule. When the amount of the thiol compound A is 50 to 150 parts by mass with respect to 100 parts by mass of the epoxy resin, the epoxy resin curable composition cures quickly, has high hardness of a cured product, and has sufficient adhesive strength. The blending amount of the thiol compound A with respect to 100 parts by mass of the epoxy resin is more preferably 60 to 120 parts by mass and more preferably 70 to 100 parts by mass.

[0041] The blending amount of the thiol compound B can be appropriately designed so as to satisfy the molar ratio Mb / Mo described above and to satisfy the molar ratio Mb / Ma according to the physical properties of the epoxy resin curable composition. For example, it is preferable to blend 1 to 40 parts by mass of the thiol compound B with respect to 100 parts by mass of an epoxy resin containing two or more epoxy groups in one molecule. When the amount of the thiol compound B is 1 to 40 parts by mass with respect to 100 parts by mass of the epoxy resin, a cured product having a high Shore D hardness and an excellent curing rate can be obtained. The blending amount of the thiol compound B with respect to 100 parts by mass of the epoxy resin is more preferably 1 to 20 parts by mass and more preferably 2 to 12 parts by mass.

[0042] 28 02 25 The epoxy resin curable composition contains an amine compound containing two or more primary amino groups and / or a secondary amino groups in one molecule and containing no tertiary amino group. The amine compound may contain only primary amino groups derived from primary amines, may contain only secondary amino groups derived from secondary amines, or may contain a primary amino group derived from a primary amine and a secondary amino group derived from a secondary amine.

[0043] The amine compound is preferably an aliphatic amine. Examples of the aliphatic amine include ethylenediamine, 1,2-diaminopropane, 1,3-diaminopropane, 1,5-diaminopentane, hexamethylenediamine, tetramethylenediamine, trimethylhexamethylenediamine, 2-methyl-l,5-diaminopentane, polyetherdiamine, 1,3-diaminopropane, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, dipropylenetriamine, and bis(hexamethylene)triamine. The amine compound is preferably not an amine in which the amino group of the aliphatic amine is composed only of a secondary amino group. That is, the aliphatic amine may contain at least one primary amino group.

[0044] 28 02 25 The amine compound is an amine containing two or more primary amino groups and / or secondary amino groups in one molecule and containing no tertiary amino group. Examples of the amine compound include ethylenediamine, 1,2-diaminopropane, 1,3-diaminopropane, 1,5-diaminopentane, hexamethylenediamine, tetramethylenediamine, trimethylhexamethylenediamine, 2-methyl-l,5-diaminopentane, polyetherdiamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, dipropylenetriamine, bis(hexamethylene)triamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, dipropylenetriamine, and bis(hexamethylene) triamine . Examples of the amine containing two or more amino groups in one molecule and containing no tertiary amino group in the molecule preferably include ethylenediamine, diethylenetriamine, triethylenetetramine, 1,3-diaminopropane, and tetraethylenepentamine.

[0045] The amine compound preferably contains three or more primary amino groups and / or secondary amino groups in one molecule. The amine having three or more amino groups in one molecule is preferably diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, dipropylenetriamine, or 28 02 25 bis(hexamethylene) triamine, and more preferably triethylenetetramine .

[0046] The amine compound is particularly preferably a modified product obtained by using an amine containing three or more primary amino groups and / or secondary amino groups in one molecule as a raw material. As the modified product obtained by using an amine containing three or more amino groups in one molecule as a raw material, a modified product of diethylenetriamine, a modified product of triethylenetetramine, a modified product of tetraethylenepentamine, and the like are particularly preferable, and among them, a modified product obtained by reacting an amino group of triethylenetetramine with a mono- or polyepoxy compound is more preferable. Examples of the modified product obtained by using an amine containing three or more amino groups in one molecule as a raw material include "BB-AMINE 3138" manufactured by BB RESINS SRL.

[0047] The modified product obtained by using an amine containing three or more amino groups in one molecule as a raw material preferably has an amine value of 500 to 2,500 KOHmg / g, and more preferably has an amine value of 800 to 1,700 KOHmg / g.

[0048] 28 02 25 The blending amount of the amine compound can be appropriately designed depending on the physical properties of the cured product. For example, it is preferable to blend 1 to 30 parts by mass of the amine compound with respect to 100 parts by mass of an epoxy resin containing two or more epoxy groups in one molecule. When the amount of the amine compound is 1 to 30 parts by mass with respect to 100 parts by mass of the epoxy resin, it is possible to obtain a cured product that cures quickly, has sufficient adhesive strength, and has excellent color toning property. The blending amount of the amine compound with respect to 100 parts by mass of the epoxy resin is more preferably 2 to 30 parts by mass and more preferably 5 to 30 parts by mass .

[0049] The epoxy resin curable composition of the present invention cures at room temperature. The epoxy resin curable composition has an excellent color tone close to colorless and / or white after curing. In the present invention, the excellent color tone means that a cured product having a thickness of 8 mm has a chromaticity a* of -10 to +10 and a chromaticity b* of -15 to +15 in an L*a*b* color system. When the chromaticity a'‘ is out of the range of -10 to +10, the color tone becomes 28 02 25 dark. A cured product having a thickness of 8 mm of the epoxy resin curable composition preferably has a chromaticity a* of -8 to +8 and a chromaticity b* of -13 to +15 in the I / a+b" color system. A cured product having a thickness of 8 mm of the epoxy resin curable composition after curing for 24 hours under conditions of 23°C and 50%RH more preferably has a chromaticity a* of -8 to +5 and a chromaticity b4 of -10 to +15 in the L‘a‘b‘ color system. The chromaticity a* of the cured product is more preferably -7 to +3 and still more preferably -5 to +1. The chromaticity b4 of the cured product is more preferably -7 to +13, still more preferably -5 to +12, and particularly preferably -1 to +11.

[0050] In the color tone of the cured product having a thickness of 8 mm of the epoxy resin curable composition, a lightness L* is preferably 50 or more, more preferably 55 or more, and still more preferably 60 or more, in a color space of the L4a4b* color system.

[0051] The color space of the L*a*b* color system is one of color display methods established by the International Commission on Illumination (CIE) in 1976, and represented by the lightness (L* value), the degree of magenta and green (a* value), and the degree of yellow and blue (b* 28 02 25 value) by physically measuring the stimulus amount of color light that causes color sensation. When the V value is 0, black is represented, when the L* value is 100, white is represented, when the a* value is a negative value, a color close to green is represented, when the a* value is a positive value, a color close to red is represented, when the b* value is a negative value, a color close to blue is represented, and when the b* value is a positive value, a color close to yellow is represented.

[0052] The measurement method of the L‘a*b* color space is obtained by performing measurement using a color difference meter (for example, trade name "CR-300" manufactured by Minolta Co., Ltd., color difference meter) which is a measurement apparatus specified in Japanese Industrial Standards JIS Z 8781-4:2013.

[0053] The epoxy resin curable composition preferably has a curing time of 1 to 20 minutes. As for the curing time of the epoxy resin curable composition, when 10 g of the epoxy resin curable composition is used and cured at 23°C and 50%RH, the curing time is more preferably 1 to 15 minutes and still more preferably 1 to 10 minutes. When the curing time is 1 to 15 minutes, it is suitable and preferable for applications requiring rapid curing.

[0054] 28 02 25 The measurement of the curing time was performed with reference to the method for determining a pot life of a multi-component adhesive described in JIS K 6870 (Method 1) . The curing time was defined as a point at which a thiol compound and an amine compound were mixed at a predetermined ratio with 10 g of an epoxy resin under conditions of 23°C and 50%RH, a toothpick was put in the epoxy resin curable composition, and the toothpick stopped moving.

[0055] When the epoxy resin curable composition is applied to a thickness of 6.0 mm or more and is cured at 23°C and 50%RH, a Shore D hardness in accordance with JIS K7215 after 3 hours from the start of curing is preferably 70 or more, and the Shore D hardness in accordance with JIS K7215 after 24 hours from the start of curing is preferably 75 or more. When the Shore D hardness after 3 hours from the start of curing is 70 or more, a cured product having high adhesive strength is obtained, which is preferable. The Shore D hardness after 3 hours from the start of curing is more preferably 71 to 85 and still more preferably 73 to 84. In addition, when the Shore D hardness after 24 hours from the start of curing is 75 or more, a cured product having high adhesive strength is obtained, which is 28 02 25 preferable. The Shore D hardness after 24 hours from the start of curing is more preferably 76 to 85 and still more preferably 78 to 84.

[0056] The epoxy resin curable composition may further contain a filler, a plasticizer, a flexibility imparting agent, a coupling agent, an antioxidant, a thixotropy imparting agent, a dispersant, and the like as long as the object of the present invention is not impaired.

[0057] The epoxy resin curable composition of the present invention adheres well to a metal, glass, stone, concrete, and the like, and can be used as an adhesive having an excellent color tone. The adhesive containing the epoxy resin curable composition is preferable as, for example, an adhesive for an iron plate, an adhesive for glass, an adhesive for a decorative item, an adhesive for a timepiece part, and an adhesive for DIY, and is particularly preferable as an adhesive for glass, an adhesive for a decorative item, an adhesive for a timepiece part, and an adhesive for DIY. Examples

[0058] Examples and Comparative Examples are described 28 02 25 below. In the following Examples, a general reagent purchased from a reagent manufacturer was used as a raw material unless otherwise specified. The following apparatus and method were used for the analysis.

[0059] • Curing Time The curing time of the epoxy resin curable composition was defined as a curing time when a toothpick was put into the epoxy resin curable composition and the toothpick stopped moving with reference to the method for determining a pot life of a multi-component adhesive described in JIS K 6870 (Method 1). Specifically, under conditions of 23°C and 50%RH, the epoxy resin curable composition obtained by mixing the raw materials according to each example was pierced with a toothpick, and the point at which the toothpick did not move was measured as the curing time. The curing time was measured from the start of mixing, and was determined in units of minutes by checking the state of the toothpick every 30 seconds. In Examples 1 to 4 and Comparative Examples 1 to 12, a thiol compound A, a thiol compound B, and an amine compound were mixed at ratios shown in Tables 1 and 2 with 10 g of an epoxy resin.

[0060] ■ Hardness (Shore D Hardness) 28 02 25 The hardness of the epoxy resin curable composition was measured by the method specified in JIS K 7215. Specifically, the epoxy resin curable composition was poured into a plurality of containers having an inner diameter of 31 mm and a depth of 8 mm in a room at a temperature of 23°C and a humidity of 50%RH, and after 3 hours and 24 hours from the start of mixing of the epoxy resin curable composition, samples for measurement having a diameter of 31 x 8 mm were obtained. The flat surface of the sample was measured using a type D durometer. The measurement was performed three times for each measurement sample, and an average value was taken as a hardness value.

[0061] • Lightness and Chromaticity The lightness and chromaticity of the cured product of the epoxy resin were measured. Specifically, the epoxy resin curable composition according to each example was placed in a container having an inner diameter of 31 mm and a depth of 8 mm and curing was performed under conditions of 23°C and 50%RH using a color difference meter ("CR-300" manufactured by Minolta Co., Ltd.) specified in JIS Z 8781-4. After 24 hours, the cured product of the epoxy resin was taken out from the container, and the lightness L\ the chromaticity a*, and the chromaticity b* of the cured product of the epoxy resin having a thickness of 8 mm were 28 02 25 measured at room temperature. The measurement results of the chromaticities a* and b* were shown in Tables 1 and 2.

[0062] Example 1 Under conditions of 23°C and 50%RH, 7.9 g (79 parts by mass) of "Polythiol QE-340M" manufactured by Toray Fine Chemicals Co., Ltd. as a thiol compound A containing two or more thiol groups in one molecule, 1.0 g (10 parts by mass) of "TMMP" (trimethylolpropane tris (3-mercaptopropionate) manufactured by SC Organic Chemical Co., Ltd., in General Formula (1), n was 1, R1 was an ethylene group, R2 was an ethyl group, and R3 was a methylene group, abbreviated as "TMMP" below and in the tables) as a thiol compound B, and 1.1 g (11 parts by mass) of "BB-AMINE 3138" manufactured by BB RESINS SRL as an amine compound containing two or more primary amino groups and / or a secondary amino groups in one molecule and containing no tertiary amino group were mixed with 10 g (100 parts by mass) of "jER828" (bisphenol A type epoxy resin, epoxy equivalent of 184 to 194 g / eq) manufactured by Mitsubishi Chemical Group Corporation as an epoxy resin containing two or more epoxy groups in one molecule with a spatula for 15 seconds, thereby obtaining an epoxy resin curable composition. Note that the number of moles Me of the epoxy groups contained in the epoxy resin curable composition, the number of moles Ma of the 28 02 25 thiol groups derived from the thiol compound A, and the number of moles Mb of the thiol groups derived from the thiol compound B were shown in Table 1. In addition, the molar ratios Ma / Mo, Mb / Mo, and Mb / Ma were calculated and described.

[0063] When the curing time at 23°C was measured using the obtained epoxy resin curable composition, the epoxy resin curable composition was cured in 6 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 73, and the Shore D hardness after 24 hours from the start of curing was 78. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -3 and the chromaticity b* was 7. These results are shown in Table 1.

[0064] Example 2 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the thiol compound B was changed from TMMP to 1.0 g (10 parts by mass) of "PEMP" (pentaerythritol tetrakis(3-mercaptopropionate), in General Formula (1), n was 0, R1 was an ethylene group, and R3 was a methylene group, abbreviated as "PEMP" below and in the tables) manufactured by SC Organic Chemical Co., Ltd.

[0065] 28 02 25 When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 6 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 77, and the Shore D hardness after 24 hours from the start of curing was 80. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a" was -3 and the chromaticity b* was 7. These results are shown in Table 1.

[0066] Example 3 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 4.0 g (40 parts by mass) and the amount of the thiol compound B was changed to 0.3 g (3 parts by mass).

[0067] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 6 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 76, and the Shore D hardness after 24 hours from the start of curing was 80. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was 28 02 25 measured, the chromaticity a* was -5 and the chromaticity b* was 7. These results are shown in Table 1.

[0068] Example 4 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 4.0 g (40 parts by mass), the amount of the thiol compound B was changed to 0.3 g (3 parts by mass), and the amount of the amine compound was changed to 3.0 g (30 parts by mass).

[0069] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 3 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 82, and the Shore D hardness after 24 hours from the start of curing was 81. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -5 and the chromaticity b* was 11. These results are shown in Table 1.

[0070] Comparative Example 1 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 8.9 g (89 28 02 25 parts by mass) and the thiol compound B was not blended.

[0071] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 6 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 72, and the Shore D hardness after 24 hours from the start of curing was 73. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -5 and the chromaticity b4 was 7. These results are shown in Table 1.

[0072] Comparative Example 2 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 0.1 g (1 part by mass) and the amount of the thiol compound B was changed to 8.8 g (88 parts by mass).

[0073] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 11 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 37, and the Shore D hardness after 24 hours from the start of curing was 47. Furthermore, when the chromaticity of 28 02 25 the cured product of the epoxy resin curable composition was measured, the chromaticity a* was 0 and the chromaticity b* was 10. These results are shown in Table 1.

[0074] Comparative Example 3 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 11.9 g (119 parts by mass) and the amount of the thiol compound B was changed to 4.0 g (40 parts by mass).

[0075] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 7 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 18, and the Shore D hardness after 24 hours from the start of curing was 18. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was 0 and the chromaticity b* was 10. These results are shown in Table 1.

[0076] Comparative Example 4 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the 28 02 25 amount of the thiol compound A was changed to 11.9 g (119 parts by mass) and the amount of the thiol compound B was changed to 0.3 g (3 parts by mass).

[0077] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 7 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 42, and the Shore D hardness after 24 hours from the start of curing was 40. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a+ was -2 and the chromaticity b* was 8. These results are shown in Table 1.

[0078] Comparative Example 5 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 4.0 g (40 parts by mass) and the amount of the thiol compound B was changed to 4.0 g (40 parts by mass).

[0079] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 6 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 76, and the Shore D hardness after 24 hours from the start of 28 02 25 curing was 74. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -1 and the chromaticity b* was 8. These results are shown in Table 2.

[0080] Comparative Example 6 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 11.9 g (119 parts by mass), the amount of the thiol compound B was changed to 4.0 g (40 parts by mass), and the amount of the amine compound was changed to 3.0 g (30 parts by mass).

[0081] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 4 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 7, and the Shore D hardness after 24 hours from the start of curing was 5. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was 2 and the chromaticity b* was 10. These results are shown in Table 2.

[0082] Comparative Example 7 28 02 25 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 11.9 g (119 parts by mass), the amount of the thiol compound B was changed to 4.0 g (40 parts by mass), and the amount of the amine compound was changed to 0.5 g (5 parts by mass).

[0083] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 24 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 19, and the Shore D hardness after 24 hours from the start of curing was 19. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -2 and the chromaticity b* was 8. These results are shown in Table 2.

[0084] Comparative Example 8 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 11.9 g (119 parts by mass), the amount of the thiol compound B was changed to 0.3 g (3 parts by mass), and the amount of the amine compound was changed to 3.0 g (30 parts by mass).

[0085] 28 02 25 When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 3 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 21, and the Shore D hardness after 24 hours from the start of curing was 18. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was 0 and the chromaticity b* was 10. These results are shown in Table 2.

[0086] Comparative Example 9 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 11.9 g (119 parts by mass), the amount of the thiol compound B was changed to 0.3 g (3 parts by mass), and the amount of the amine compound was changed to 0.5 g (5 parts by mass).

[0087] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 14 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 34, and the Shore D hardness after 24 hours from the start of curing was 51. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition 28 02 25 was measured, the chromaticity a* was -4 and the chromaticity b* was 6. These results are shown in Table 2.

[0088] Comparative Example 10 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 4.0 g (40 parts by mass), the amount of the thiol compound B was changed to 4.0 g (40 parts by mass), and the amount of the amine compound was changed to 3.0 g (30 parts by mass).

[0089] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 3 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 52, and the Shore D hardness after 24 hours from the start of curing was 50. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -5 and the chromaticity b* was 12. These results are shown in Table 2.

[0090] Comparative Example 11 An epoxy resin curable composition was obtained in the same manner as that of Example 1, except that the amount of the thiol compound A was changed to 4.0 g (40 28 02 25 parts by mass), the amount of the thiol compound B was changed to 4.0 g (40 parts by mass), and the amount of the amine compound was changed to 0.5 g (5 parts by mass).

[0091] When the curing time at 23°C was measured in the same manner as that of Example 1, the epoxy resin curable composition was cured in 30 minutes. In addition, the Shore D hardness after 3 hours from the start of curing was 51, and the Shore D hardness after 24 hours from the start of curing was 77. Furthermore, when the chromaticity of the cured product of the epoxy resin curable composition was measured, the chromaticity a* was -2 and the chromaticity b" was 8. These results are shown in Table 2.

[0092] [Table 1] Table 1 Example 1 Example 2 Example 3 Example 4 Comparative Example 1 Comparative Example 2 Comparative Example 3 Comparative Example 4 Epoxy resin (parts by mass) 100 100 100 100 100 100 100 100 Thiol compound A (parts by mass) 79 79 40 40 89 1 119 119 Thiol compound B TMMP (parts by mass) 10 0 3 3 0 88 40 3 PEMP (parts by mass) 0 10 0 0 0 0 0 0 Amine compound (parts by mass) 11 11 11 30 11 11 11 11 Number of moles Me of epoxy groups (mol) 0.59 0.59 0.59 0.59 0.59 0.59 0.59 0.59 Number of moles Ma of thiol groups derived from thiol compound A (mol) 0.34 0.34 0.17 0.17 0.38 0.01 0.50 0.50 Number of moles Mb of thiol groups derived from thiol compound B (mol) 0.08 0.08 0.02 0.02 0.00 0.66 0.30 0.02 Molar ratio Ma / Mc 0.57 0.57 0.29 0.29 0.64 0.02 0.86 0.86 Molar ratio Me / Me 0.13 0.14 0.04 0.04 0.00 1.12 0.51 0.04 Molar ratio Mb / Ma 0.22 0.24 0.13 0.13 0.00 66.00 0.60 0.04 Curing time (min) 6 6 6 3 6 11 7 7 Hardness Shore D 3 hours 73 77 76 82 72 37 18 42 24 hours 78 80 80 81 73 47 18 40 Chromaticity a* -3 -3 -5 -5 -5 0 0 -2 b* 7 7 7 11 7 10 10 8

[0093] [Table 2] Table 2 Comparative Example 5 Comparative Example 6 Comparative Example 7 Comparative Example 8 Comparative Example 9 Comparative Example 10 Comparative Example 11 Epoxy resin (parts by mass) 100 100 100 100 100 100 100 Thiol compound A (parts by mass) 40 119 119 119 119 40 40 Thiol compound B TMMP (parts by mass) 40 40 40 3 3 40 40 PEMP (parts by mass) 0 0 0 0 0 0 0 Amine compound (parts by mass) 11 30 5 30 5 30 5 Number of moles Me of epoxy groups (mol) 0.59 0.59 0.59 0.59 0.59 0.59 0.59 Number of moles Ma of thiol groups derived from thiol compound A (mol) 0.17 0.50 0.50 0.50 0.50 0.17 0.17 Number of moles Mb of thiol groups derived from thiol compound B (mol) 0.30 0.30 0.30 0.02 0.02 0.30 0.30 Molar ratio Ma / Mo 0.29 0.86 0.86 0.86 0.86 0.29 0.29 Molar ratio Me / Me 0.51 0.51 0.51 0.04 0.04 0.51 0.51 Molar ratio Mb / Ma 1.77 0.60 0.60 0.04 0.04 1.77 1.77 Curing time (min) 6 4 24 3 14 3 30 Hardness Shore D 3 hours 76 7 19 21 34 52 51 24 hours 74 5 19 18 51 50 77 Chromaticity a* -1 2 -2 0 -4 -5 -2 b‘ 8 10 8 10 6 12 8

Claims

19 11 241. An epoxy resin curable composition comprising an epoxy resin containing two or more epoxy groups in one molecule, a thiol compound A containing two or more thiol groups in one molecule, an amine compound containing two or more primary amino groups and / or secondary amino groups in one molecule and containing no tertiary amino group, and a thiol compound B represented by any one of the following General Formulas (1) to (3), wherein the thiol compound A and the thiol compound B are different from each other, and a molar ratio MA / Me is 0.29 to 0.80 and a molar ratio MB / Me is 0.02 to 0.4, in which Me is the number of moles of the epoxy groups contained in the epoxy resin curable composition, Ma is the number of moles of the thiol groups in the thiol compound A, and Mb is the number of moles of the thiol groups in the thiol compound B,(R2) n-C- (R3-O-CO-R1-SH) 4-n (1)(in General Formula (1), R2,s each independently represent an alkylene group having 1 to 10 carbon atoms, R2 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, R3's each independently represent an alkylene group having 1 to 3 carbon atoms, n represents an integer of 0 to 2, and -SH is bonded to any carbon atom of R1) , [Chern. 1]19 11 24(R2) n-C- (R3-O-R1-SH) 4-n (3)(in General Formula (3), R2's each independently represent an alkylene group having 1 to 10 carbon atoms, R2 represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, or a hydroxyalkyl group having 1 to 3 carbon atoms, R3's each independently represent an alkylene group having 1 to 3 carbon atoms, n represents an integer of 0 to 2, and -SH is bonded to any carbon atom of R1), and wherein a molar ratio Mb / Ma of the number of moles Mb of the thiol groups in the thiol compound B to the number of moles Ma of the thiol groups in the thiol compound A is 0.02 to 0.

5.

2. The epoxy resin curable composition according to claim 1, wherein the thiol compound A does not contain a carbonyl group.

3. The epoxy resin curable composition according to claim 1 or 2, wherein a chromaticity a4 and a chromaticity b* in an L*a*b* color system of a cured product are -10 to +10 and -15 to +15, respectively, as measured by a method according to the description.

4. The epoxy resin curable composition according to any19 11 24one of claims 1 to 3, wherein a curing time when 10 g of the epoxy resin curable composition is used and cured at 23°C and 50%RH is 1 to 15 minutes, as measured by a method according to the description.

5. The epoxy resin curable composition according to any one of claims 1 to 4, wherein when the epoxy resin curable composition is applied to a thickness of 6.0 mm or more and is cured at 23°C and 50%RH, a Shore D hardness as measured by a method according to the description and in accordance with JIS K7215 after 3 hours from a start of curing is 70 or more, and the Shore D hardness as measured by a method according to the description and in accordance with JIS K7215 after 24 hours from the start of curing is 75 or more .

6. The epoxy resin curable composition according to any one of claims 1 to 5, wherein the epoxy resin curable composition is used for an adhesive.

7. An adhesive comprising the epoxy resin curable composition according to any one of claims 1 to 6.