Multilayer Optical Films

Abstract

The multilayer optical film includes a plurality of first polymer layers, a total of at least 10, each of the first layers having an average thickness less than about 500 nm. For p-polarized incident light, at each of a first angle of incidence and a second angle of incidence at least about 40 degrees greater than the first angle of incidence, the reflectivity of the optical film and each of the plurality of first polymer layers versus wavelength has a reflection band having a left band edge (LBE) on the short wavelength side of the reflection band and a right band edge (RBE) on the long wavelength side of the reflection band. At the first angle of incidence, the spacing between the RBEs is less than the spacing between the LBEs, and at the second angle of incidence, the spacing between the RBEs is greater than the spacing between the LBEs.

Description

[Background technology]

[0001] Multilayer optical films can include multiple alternating polymer layers to provide reflection bands. Summary of the Invention

[0002] The present disclosure generally relates to multilayer optical films. The multilayer optical films can have one or more reflection bands. The reflection band can have a left band edge on the short wavelength side of the reflection band where the reflectivity generally increases with increasing wavelength, and a right band edge on the long wavelength side of the reflection band where the reflectivity generally decreases with increasing wavelength. According to some embodiments of the present disclosure, the multilayer optical film has a reduced shift of one or both of the left and right band edges with respect to the incidence angle, compared to conventional polymeric multilayer optical films. In some embodiments, the reduced band shift is provided by including one or both of a left band edge compensator and a right band edge compensator in the multilayer optical film, where the band edge compensator can be or include, for example, a packet of optical layers having a reflectivity change with incidence angle, such that when combined with another reflector (e.g., an optical mirror or a reflective polarizer) in the multilayer optical film, it can provide a reduced band shift with incidence angle. Two band edge compensators can be used together, for example, without another reflector, to provide a narrow band reflector with a desirably low band edge shift with incidence angle.

[0003] In some aspects, the present disclosure provides a multilayer optical film including a plurality of first polymer layers, a total of at least 10, disposed on a plurality of second polymer layers, a total of at least 10, wherein each of the first and second layers has an average thickness of less than about 500 nm, such that for p-polarized incident light in a predetermined wavelength range disposed between about 200 nm and about 2000 nm, at each of a first angle of incidence and a second angle of incidence at least about 40 degrees greater than the first angle of incidence, the optical reflectance of the optical film and each of the plurality of first polymer layers with respect to wavelength is a reflection band, the reflection band having a short wavelength, The multilayer optical film includes a reflection band having a left band edge (LBE) on the long-wavelength side thereof, where the reflectance generally increases with increasing wavelength, and a right band edge (RBE) on the long-wavelength side thereof, where the reflectance generally decreases with increasing wavelength, such that at a first angle of incidence, the spacing between the RBE of the optical film and the REB of the first layer can be smaller than the spacing between the LBE of the optical film and the LBE of the first layer, and at a second angle of incidence, the spacing between the RBE of the optical film and the RBE of the first layer can be larger than the spacing between the LBE of the optical film and the LBE of the first layer.

[0004] In some aspects, the present disclosure provides a multilayer optical film comprising a plurality of first polymer layers, totaling at least 10, each of the first layers having an average thickness of less than about 500 nm, such that for substantially normally incident p-polarized incident light in a predetermined wavelength range disposed between about 200 nm and about 2000 nm, the optical reflectivity of the optical film and each of the plurality of first polymer layers versus wavelength includes a reflection band having a full width at half maximum (FWHM) and a right band edge (RBE) on the longer wavelength side of the reflection band where the reflectivity generally decreases with increasing wavelength, such that at least one of the two FWHMs overlaps with at least 50% of the other of the two FWHMs, and the wavelength at half maximum reflectivity along the RBE of the optical film and the first layers shifts to wavelengths smaller by CS and MS, respectively, as the angle of incidence of the p-polarized incident light increases by at least about 60 degrees. CS can be at least about 10 nm smaller than MS.

[0005] In some aspects, the present disclosure provides a multilayer optical film including a plurality of first polymer layers, a total of at least 10, disposed on a plurality of second polymer layers, a total of at least 10, wherein each of the first and second layers has an average thickness less than about 500 nm, and for p-polarized incident light in a predetermined wavelength range that is at least about 200 nm wide, at a first angle of incidence, the optical reflectance of the optical film includes a first reflection band having a peak reflectance that may be greater than about 50%, and the plurality of first polymer layers have a substantially constant optical reflectance with a standard deviation that may be less than about 3%, and at a second angle of incidence at least about 40 degrees greater than the first angle of incidence, the optical film and the plurality of first polymer layers have respective second and third reflection bands, each reflection band having a peak reflectance that may be greater than about 40%.

[0006] In some aspects, the present disclosure provides a multilayer optical film comprising a total of at least 10 first polymer layers disposed on a total of at least 10 second polymer layers, each of the first and second layers having an average thickness of less than about 500 nm, and arranged from about 200 nm to about 2000 nm, wherein the maximum reflectance of the optical film and the first polymer layers for p-polarized incident light in a predetermined wavelength range at least about 200 nm wide, for a first incidence angle, Cmax and Lmax, respectively, and for a second incidence angle at least about 40 degrees greater than the first incidence angle, Cmax and Lmax can be within 20% of each other, and C'max can be greater than or equal to 2L'max.

[0007] In some aspects, the present disclosure provides a multilayer optical film comprising a plurality of first polymer layers, totaling at least 10, each of the first layers having an average thickness less than about 500 nm, and for p-polarized light incident at a first angle of incidence in a predetermined wavelength range disposed between about 200 nm and about 2000 nm, the optical reflectance of the optical film and the plurality of first polymer layers versus wavelength comprises respective first and second reflection bands having respective full widths at half maximum FW1 and FW2. Upon increasing the angle of incidence by at least about 40 degrees to a second angle of incidence, the first and second reflection bands shift to respective third and fourth reflection bands of smaller wavelengths having respective full widths at half maximum FW'1 and FW'2. FW'1 can be less than about 30% smaller than FW1. FW'2 can be more than about 35% smaller than FW2.

[0008] In some aspects, the present disclosure provides a multilayer optical film including a plurality of first polymer layers disposed on and integrally formed with a plurality of second polymer layers, each of the two plurality including at least 10 polymer layers in total, each of the first and second layers having an average thickness of less than about 500 nm, arranged between about 200 nm and about 2000 nm, for p-polarized incident light in a predetermined wavelength range at least about 200 nm wide, at a first angle of incidence, the optical reflectance of the plurality of first polymer layers with respect to the wavelength includes a reflection band, but the optical reflectance of the plurality of second polymer layers with respect to the wavelength does not include the reflection band, and at a second angle of incidence at least about 40 degrees greater than the first angle of incidence, the optical reflectance of each of the plurality of first polymer layers and the plurality of second polymer layers with respect to the wavelength includes a reflection band.

[0009] In some aspects, the present disclosure provides a multilayer optical film comprising a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers and a plurality of alternating fifth and sixth polymer layers, each of the three pluralities comprising a total of at least 10 or at least 20 polymer layers, and each of the first through sixth polymer layers having an average thickness of less than about 500 nm. The first to sixth polymer layers have respective refractive indices nx1 to nx6 along the same in-plane x direction, respective refractive indices ny1 to ny6 along an in-plane y direction perpendicular to the x direction, and respective refractive indices nz1 to nz6 along a thickness direction of the polymer layers perpendicular to the x and y directions, and for at least one wavelength in a visible wavelength range spanning from about 420 nm to about 680 nm, each of nx1 and ny1 can be at least 0.02 greater than nz1, the magnitude of the maximum difference between nx3, ny3, and nz3 can be less than 0.02, and each of nx5 and ny5 can be at least 0.02 less than nz5.

[0010] In some aspects, the present specification provides a multilayer optical film comprising a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers, each of the two plurality comprising a total of at least 10 or at least 20 polymer layers, and each of the first through fourth polymer layers having an average thickness of less than about 500 nm. The first to fourth polymer layers have respective refractive indices nx1 to nx4 along the same in-plane x direction, respective refractive indices ny1 to n4 along the in-plane y direction perpendicular to the x direction, and respective refractive indices nz1 to nz4 along the thickness direction of the polymer layers perpendicular to the x and y directions, and for at least one wavelength in the visible wavelength range spanning from about 420 nm to about 680 nm, each of |nx1-nx2| and |ny1-ny2| is less than about 0.02, nz1-nz2 is greater than about 0.03, nx1 can be at least about 0.02 less than nz1, nx4-nx3 is greater than about 0.03, nz4-nz3≧nx4-nx3, and nx3 can be at least about 0.02 greater than nz3. In some embodiments, for at least one wavelength, the magnitude of the maximum difference between nx4, ny4, and nz4 can be less than about 0.02. In some embodiments, for at least one wavelength, nx4 may be at least 0.03 greater than ny4.

[0011] In some aspects, the present disclosure provides a multilayer optical film including a plurality of first polymer layers disposed on and integrally formed with a plurality of second polymer layers, each of the two plurality comprising at least 10 polymer layers in total, each of the first and second layers having an average thickness less than about 500 nm, arranged between about 200 nm and about 2000 nm, for p-polarized incident light in a predetermined wavelength range that is at least about 200 nm wide, at a first angle of incidence, the optical reflectivity of the plurality of first polymer layers for a wavelength includes a reflection band, but the optical reflectivity of the plurality of second polymer layers for a wavelength does not include the reflection band and can have a full width at half maximum (FWHM) greater than about 10 nm, and at a second angle of incidence at least about 40 degrees greater than the first angle of incidence, the optical reflectivity of each of the plurality of first polymer layers and the plurality of second polymer layers for a wavelength includes a reflection band, and each of the reflection bands can have an FWHM greater than about 10 nm.

[0012] In some aspects, the present disclosure provides a multilayer optical film that includes a plurality of first polymer layers disposed on and integrally formed with a plurality of second polymer layers, each of the two plurality including at least 10 polymer layers in total, each of the first and second layers having an average thickness of less than about 500 nm, and for p-polarized incident light in a predetermined wavelength range at least about 200 nm wide disposed between about 200 nm and about 2000 nm, at a first angle of incidence greater than about 30 degrees with respect to wavelength, the optical film, the plurality of first polymer layers, and the plurality of second polymer layers. the optical reflectance of each of the plurality of second polymer layers includes a reflection band having a left band edge (LBE) on a shorter wavelength side of the reflection band where the reflectance generally increases with increasing wavelength and a right band edge (RBE) on a longer wavelength side of the reflection band where the reflectance generally decreases with increasing wavelength, such that the RBE of the optical film substantially overlaps with the RBE of one of the plurality of first layers and the plurality of second layers and the LBE of the optical film substantially overlaps with the LBE of the other of the plurality of first layers and the plurality of second layers.

[0013] In some aspects, the present disclosure provides a multilayer optical film including a plurality of first polymer layers disposed on and integrally formed with a plurality of second polymer layers, each of the two plurality including at least 10 polymer layers in total, each of the first and second layers having an average thickness less than about 500 nm, arranged between about 200 nm and about 2000 nm, for p-polarized incident light in a predetermined wavelength range that is at least about 200 nm wide, at a first angle of incidence, the optical reflectance of the optical film and each of the plurality of first polymer layers for a wavelength include reflection bands having full width at half maximum (FWHM) within about 20% of each other, but the optical reflectance of the plurality of second polymer layers for a wavelength does not include the reflection band, and at a second angle of incidence that is at least about 40 degrees greater than the first angle of incidence, the optical reflectance of the optical film and each of the plurality of first polymer layers for a wavelength include a reflection band, and the reflection bands can have FWHMs that differ by at least about 30%.

[0014] In some aspects, the present disclosure provides a multilayer optical film including a plurality of layers totaling at least 10, each having an average thickness of less than about 500 nm, arranged between about 200 nm and about 2000 nm, for p-polarized incident light in a predetermined wavelength range at least about 200 nm wide, at increasing first, second, and third angles of incidence, the optical reflectance of the optical film versus wavelength includes first, second, and third reflection bands having respective full widths at half maximum F1, F2, and F3, where F3>F1>F2.

[0015] In some aspects, the present disclosure provides a multilayer optical film comprising a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers, each of the two plurality comprising a total of at least 10 polymer layers, each of the first through fourth polymer layers having an average thickness of less than about 500 nm, and for unpolarized incident light in a predetermined wavelength range at least about 200 nm wide disposed between about 200 nm and about 2000 nm, the optical reflectivity of the optical film with respect to wavelength includes a reflection band having a full width at half maximum of less than about 100 nm at a first angle of incidence at least less than about 25 degrees, and for at least one first wavelength within the reflection band, the optical reflectivity of the optical film is greater than about 50% at each of the first angle of incidence and a second angle of incidence at least about 60 degrees greater than the first angle of incidence.

[0016] These and other aspects will become apparent from the following detailed description, but in no way should this brief summary be construed as limiting the claimed subject matter. [Brief description of the drawings]

[0017] [Figure 1A] 1 is a schematic plot of band edge wavelength versus incidence angle according to some embodiments. [Figure 1B] 1 is a schematic plot of band edge wavelength versus incidence angle according to some embodiments. [Figure 2A] 1 is a schematic cross-sectional view of a multilayer optical film according to some embodiments. [Figure 2B] 1 is a schematic cross-sectional view of a multilayer optical film according to some embodiments. [Figure 2C] 1 is a plot of average layer thickness of layers of a multilayer optical film as a function of layer number, according to some embodiments. [Diagram 3] 1 is a schematic perspective view of exemplary layers of a multilayer optical film. [Figure 4] 2 is a schematic diagram of light entering an optical element at an entrance surface. [Figure 5A] 1 is a plot of reflectivity of a multilayer optical film and multiple first polymer layers, second polymer layers, and third polymer layers of the multilayer optical film for different angles of incidence, according to some embodiments. [Figure 5B] 1 is a plot of reflectivity of a multilayer optical film and multiple first polymer layers, second polymer layers, and third polymer layers of the multilayer optical film for different angles of incidence, according to some embodiments. [Figure 5C] 1 is a plot of reflectivity of a multilayer optical film and multiple first polymer layers, second polymer layers, and third polymer layers of the multilayer optical film for different angles of incidence, according to some embodiments. [Figure 6] 1 is a plot of wavelength at half maximum reflectance along the right bandedge of an optical film and a first layer of the optical film, as well as the shift in wavelength at half maximum reflectance with angle of incidence, according to some embodiments. [Figure 7A] FIG. 5C is a plot of the reflectance of FIGS. 5A-B showing the peak reflectance and the standard deviation σ of the reflectance. [Figure 7B] FIG. 5C is a plot of the reflectance of FIGS. 5A-B showing the peak reflectance and the standard deviation σ of the reflectance. [Figure 8A] FIG. 5C is a plot of the reflectance of FIGS. 5A-B showing maximum reflectance and full width at half maximum at different angles of incidence. [Figure 8B] FIG. 5C is a plot of the reflectance of FIGS. 5A-B showing maximum reflectance and full width at half maximum at different angles of incidence. [Figure 9A] 1 is a plot of reflectivity of a plurality of first and second polymer layers versus wavelength at respective first and second angles of incidence according to some embodiments. [Figure 9B] 1 is a plot of reflectivity of a plurality of first and second polymer layers versus wavelength at respective first and second angles of incidence according to some embodiments. [Figure 10]1 is a plot of light reflectance versus wavelength for a plurality of first polymer layers and second polymer layers, and a combination of a plurality of first polymer layers and second polymer layers, according to some embodiments. [Figure 11] 1 is a plot of normalized reflectance of an optical film including a plurality of first and second polymer layers versus wavelength at different angles of incidence according to some embodiments. [Figure 12] 4 is a plot of the full width at half maximum of the reflection band of an optical film as a function of incidence angle according to some embodiments. [Figure 13] 1 is a plot of the transmission of a multilayer optical film for unpolarized incident light at various angles of incidence, according to some embodiments. [Figure 14] 14 is a plot of the bandedge wavelength for the optical film of FIG. 13 as a function of incidence angle. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] In the following description, reference is made to the accompanying drawings, which form a part hereof, and in which are shown by way of illustration various embodiments. The drawings are not necessarily to scale. It is to be understood that other embodiments are contemplated and may be made without departing from the scope or spirit of the specification. Accordingly, the following detailed description is not to be taken in a limiting sense.

[0019] Multilayer optical films comprising alternating polymer layers can be used to provide desired reflection and transmission in desired wavelength ranges by appropriately selecting layer thicknesses and refractive index differences, as generally described in, for example, U.S. Pat. Nos. 5,882,774 (Jonza et al.), 6,179,948 (Merrill et al.), 6,783,349 (Neavin et al.), 6,967,778 (Wheatley et al.), and 9,162,406 (Neavin et al.). Alternating polymer layers typically include alternating high and low refractive index layers, which can be described as optical layers that transmit and reflect light primarily by optical interference. Multilayer optical films comprising alternating high and low refractive index layers can be described as including multiple optical repeat units, each optical repeat unit including a high and a low refractive index layer. An optical repeat unit is generally the smallest discrete unit of an optical layer that repeats along the thickness direction of an optical film. Each optical repeat unit may include one or more layers in addition to the high and low refractive index layers, for example, as described in U.S. Pat. Nos. 5,103,337 (Schrenk et al.), 5,540,978 (Schrenk), and 6,207,260 (Wheatley et al.).

[0020] Multilayer optical films can have one or more reflection bands. The reflection bands can have a left band edge (LBE) on the short wavelength side of the reflection band where reflectance generally increases with increasing wavelength, and a right band edge (RBE) on the long wavelength side of the reflection band where reflectance generally decreases with increasing wavelength. In conventional polymeric multilayer optical films, the band edges shift significantly with changes in the angle of incidence. For example, in a conventional optical film that includes alternating layers of polyethylene terephthalate (PET) and co-polymethyl methacrylate (coPMMA) and has reflection bands in the visible and near infrared wavelength ranges, the right band edge shifts approximately 130 nm to lower wavelengths as the angle of incidence changes from 0 degrees to 75 degrees. In many applications, such a shift is undesirable.

[0021] According to some embodiments herein, the multilayer optical film has reduced LBE and / or RBE shifts with incidence angle compared to conventional polymeric multilayer optical films. For example, a right band edge shift of about 130 nm for a PET / coPMMA reflector can be reduced to a shift of about 100 nm. In some embodiments, reduced band shifts are provided by including one or both of an LBE compensator and an RBE compensator in the multilayer optical film. As further described elsewhere herein, a band edge compensator can be or can include a packet of optical layers having a reflectivity change with incidence angle such that when combined with another reflector in a multilayer optical film, it can result in reduced band edge shifts with incidence angle compared to, for example, an optical film without a band edge compensator.

[0022] The multilayer optical film herein can include an LBE compensator (e.g., a conventional polymer optical film) with a first reflector. In some embodiments, the first reflector, which may be referred to as the main reflector or primary reflector, provides a majority of the width of the reflection band. For example, the reflection band of each of the optical film and the primary reflector can have a full width at half maximum (FWHM), and at a first angle of incidence, each of the two FWHMs overlaps with the other of the two FWHMs by more than 50%, or at least about 60%, or at least about 70%, or at least about 75%. The LBE compensator generally reduces the shift of the LBE of the first reflector with angle of incidence and can include multiple (or packets) of polymer layers that can include alternating first and second optical layers, where the first optical layers have a higher refractive index along a first in-plane direction than the second optical layers for the same first wavelength, and the difference in refractive index between the first and second layers along the thickness direction (orthogonal to each of the first in-plane direction and the orthogonal second in-plane direction) is at least as large as the difference in refractive index between the first and second layers along the first in-plane direction for the same first wavelength. The multilayer optical film can be, for example, a reflective polarizer (e.g., the first in-plane direction can be along the block axis) or can be an optical mirror (e.g., the refractive index along the second in-plane direction can be approximately the same as the corresponding refractive index along the first in-plane direction). For a plane of incidence (plane defined by the direction of the light and the normal to the surface on which the light is incident) that includes a first in-plane direction and p-polarized light (electric field parallel to the plane of incidence), the LBE compensator typically has a high on-axis reflectivity (e.g., similar to that of the first reflector) and decreases in reflectivity as the angle of incidence increases due to the Brewster angle effect and due to refractive index mismatch through the thickness. By positioning the normal incidence reflection band of the LBE compensator at a wavelength that overlaps with the LBE of the first reflector, the position of the LBE is shifted to lower wavelengths at low angles of incidence due to the reflection of the LBE compensator and is not substantially shifted at high angles of incidence where the reflection of the LBE compensator is weak. As a result, the shift of the LBE of the multilayer optical film is reduced compared to the LBE of the first reflector.This is shown diagrammatically in FIG. 1A, which also illustrates the reduction in RBE shift resulting from an RBE compensator, as further explained elsewhere herein.

[0023] FIG. 1A is a schematic plot of band edge wavelengths versus incidence angle for p-polarized light, according to some embodiments. The band edge wavelength may be interpreted as the wavelength along the band edge where the reflectance is halfway between the baseline reflectance for wavelengths outside the reflection band and the maximum reflectance within the reflection band (see, for example, U.S. Pat. No. 10,054,803 (Wold et al.)), or the band edge wavelength may be interpreted as the wavelength along the band edge where the reflectance is half the maximum reflectance within the reflection band, or the band edge wavelength may be interpreted as the wavelength along the band edge where the reflectance is 50%. The incidence angle is the angle of the direction of light incident on the surface relative to the normal to the surface, ranging from 0 degrees to 90 degrees. The LBE wavelength curve 161 and the RBE wavelength curve 162 (band edge wavelength as a function of incidence angle) for a first reflector (e.g., a conventional polymer optical film) are shown diagrammatically. The LBE wavelength curve 151 of a multilayer optical film including an LBE compensator and a first reflector is shown diagrammatically. The LBE compensator reduces the LBE wavelength from that of the first reflector for low angles of incidence to reduce the LBE shift. Alternatively, if an LBE compensator is included in the multilayer optical film, for example, the first reflector can be modified (e.g., by removing an optical layer adapted to reflect near the original LBE wavelength 161) to shift the LBE wavelength of the first reflector to a longer wavelength, such that when the LBE compensator is included, the multilayer optical film has a reflection band at normal incidence similar to the unmodified first reflector. This is shown diagrammatically in FIG. 1B, where the LBE wavelength curve 151' of the multilayer optical film is similar to the LBE wavelength curve 161 for smaller angles of incidence and is at a higher wavelength than the LBE wavelength curve 161 for larger angles of incidence.

[0024] For s-polarized light in a plane of incidence orthogonal to the first in-plane direction (electric field orthogonal to the plane of incidence) (e.g., the light can have an electric field parallel to the first in-plane direction), the LBE compensator can have a band edge shift similar to that of the first reflector, which is typically smaller than the band edge shift of the first reflector for p-polarized light. Thus, according to some embodiments, the LBE compensator can reduce the band edge shift of p-polarized light while maintaining the low band edge shift characteristic of s-polarized light.

[0025] The multilayer optical film herein can include an RBE compensator (e.g., a conventional polymer optical film) with a first reflector. The RBE compensator generally reduces the shift of the RBE of the first reflector with the angle of incidence and can include a plurality (or packet) of polymer layers that can include alternating first and second optical layers, with the first and second optical layers having substantially matched (e.g., within about 0.02 or within about 0.015) refractive indices along each of the orthogonal first and second in-plane directions, and substantially mismatched (e.g., differing by more than about 0.02 or at least about 0.03) refractive indices along the thickness direction orthogonal to each of the first and second in-plane directions for the same first wavelength. The RBE compensator typically has a low reflectivity at normal incidence for each polarization state. For p-polarized light, the RBE compensator typically has an increasing reflectivity as the angle of incidence increases due to the refractive index mismatch in the thickness direction. By positioning the reflection band of the RBE compensator at wavelengths that overlap the RBE of the first reflector at high angles of incidence, the position of the RBE is shifted to longer wavelengths at higher angles of incidence by the reflection of the RBE compensator, and is not substantially shifted at low angles of incidence where the reflection of the RBE compensator is weak. As a result, the shift of the RBE of the multilayer optical film is reduced compared to the RBE of the first reflector. This is shown diagrammatically in Figures 1A-1B, which show a schematic of an RBE wavelength curve 152 for a multilayer optical film including an RBE compensator and a first reflector. The RBE wavelength curve 152 is at a longer wavelength than the RBE wavelength curve 162 of the first reflector at higher angles of incidence, resulting in a reduced RBE shift. According to some embodiments, for s-polarized light, the RBE compensator can have a reflectivity that increases similar to that of a conventional multilayer optical film such that the RBE maintains the low band edge shift characteristic s-polarized light.

[0026] In some embodiments, the multilayer optical film herein includes an RBE compensator and an LBE compensator with a first reflector (e.g., a conventional polymeric optical film) to reduce both the LBE and RBE shifts with incidence angle of the first reflector. In other embodiments, only one of an RBE compensator and an LBE compensator is included. In some embodiments, the multilayer optical film includes an RBE compensator and an LBE compensator without including a first reflector. The combination of an RBE compensator and an LBE compensator can result in a narrow band reflector with reduced LBE and RBE band edge shifts with incidence angle compared to that of a conventional polymeric optical film with a similar narrow reflection band at normal incidence. In some embodiments, the reflection band has a full width at half maximum of less than about 100 nm at normal incidence, and there is at least one wavelength at which the optical film has a reflectivity of greater than about 50% over a range of angles of incidence, e.g., from 0 to about 75 degrees. In contrast, in conventional optical films that have a narrow reflection band at normal incidence, due to the shift of the band edges with incidence angle, there are no wavelengths where the reflectance remains above about 50% for a wide range of incidence angles.

[0027] 2A is a schematic cross-sectional view of a multilayer optical film 100 including a plurality of 10 layers 11, 12, a plurality of 20 layers 21, 22, and a plurality of 30 layers 31, 32. In some embodiments, one of the plurality of 10, 20, 30 layers is a first reflector (e.g., an optical mirror or a reflective polarizer), another one of the plurality of 10, 20, 30 layers is an LBE compensator, and the remaining one of the plurality of 10, 20, 30 layers is an RBE compensator. In some embodiments, any one of the plurality of 10, 20, 30 layers (e.g., any one of the first reflector, the LBE compensator, or the RBE compensator) is omitted. In some cases, one of the plurality 10, 20, and 30 may be referred to as a plurality of first polymer layers, one of the other two of the plurality 10, 20, and 30 may be referred to as a plurality of second polymer layers, or the other two of the plurality 10, 20, and 30 may be referred to collectively as a plurality of second polymer layers. The plurality 10, 20, 30 layers may be arranged in any order, with any one of the three plurality 10, 20, 30 disposed between the other two of the three plurality (e.g., the plurality 10 layers may be disposed between the plurality 20 layers and the plurality 30 layers as shown, or the plurality 20 layers may be disposed between the plurality 10 layers and the plurality 30 layers, or the plurality 30 layers may be disposed between the plurality 10 layers and the plurality 20 layers). Regardless of where the layers are positioned relative to one another in the multilayer optical film, the reflection provided by the LBE compensator is generally to the left of the reflection provided by the RBE compensator (a plot of reflectance versus wavelength for several angles of incidence--see, e.g., FIG. 5B), and the reflection provided by the primary reflector is between the reflection provided by the LBE compensator and the reflection provided by the RBE compensator, so that the layer of the LBE compensator may be referred to as the left layer or left packet, the layer of the RBE compensator may be referred to as the right layer or right packet, and the layer of the first reflector or primary reflector may be referred to as the middle layer or middle packet. The reflectivity of a multilayer optical film may be referred to as the composite reflectivity of the various layers or layers of the film.The reflectivity may be characterized for incident light 140 at various angles of incidence and / or for various polarization states (e.g., p-polarized, s-polarized, or unpolarized), as further described elsewhere herein.

[0028] Each of the plurality of layers 10, 20, 30, when included in the optical film 100, may, for example, comprise at least 10 layers in total, or at least 20 layers in total, or at least 30 layers in total, or at least 40 layers in total, such as up to 1000 layers in total, or up to 600 layers in total, or up to 400 layers in total, or up to 300 layers in total. In some embodiments, the total number of layers 11, 12, 21, 22, 31, 32 may, for example, be at least 10, or at least 20, or at least 40, or at least 60, or at least 100, and / or may be less than 2000, or less than 1000. The plurality of layers 10, 20, and / or 30 may comprise more layers than are shown diagrammatically in FIG. 2A. This is, for example, diagrammatically shown in FIG. 2B for the plurality of 20 layers 21, 22 and the plurality of 30 layers 31, 32. In the embodiment of FIG. 2B, layers 11, 12 of the plurality 10 are omitted.

[0029] Each layer of the plurality of layers 10, 20, 30 may be referred to as an optical layer and may have an average thickness of, for example, less than about 500 nm, or less than about 400 nm, or less than about 300 nm, or less than about 250 nm, or less than about 200 nm. Each of the layers may have an average thickness of, for example, more than about 30 nm, or more than about 40 nm, or more than about 50 nm, or more than about 60 nm. The average thickness of a layer is an unweighted average of the thickness of the layer over the area of ​​the layer. The layers in the plurality of layers 10, 20, 30 may be numbered sequentially from one side of the optical film 100 to the opposite side of the optical film. FIG. 2C is a plot of the average layer thickness of the layers in the plurality of layers 10, 20, and 30 as a function of layer number according to some embodiments.

[0030] Each of the plurality 10, 20, 30 layers may include layers arranged in an optical repeat unit, where the optical repeat unit includes at least a first optical layer and a second optical layer (e.g., layers 11, 12, or 21, 22, or 31, 32). The optical repeat unit may include only the first optical layer and the second optical layer, or may include one or more additional layers. For example, the optical repeat unit may include one or more thin (e.g., less than half the thickness of each of the first optical layer and the second optical layer) layers for improved peel resistance.

[0031] The multilayer optical film 100 may include layers in addition to the plurality of 10, 20, 30 layers. Some of these layers may have a thickness greater than about 500 nm. For example, the optical film 100 may include skin layers 155 and 156 as the outermost layers of the optical film, each having an average thickness greater than about 500 nm, or greater than about 1 micrometer, or greater than about 2 micrometers. The skin layers 155, 156 may have a thickness of, for example, up to about 20 micrometers. The optical film 100 may also include protective boundary layers 153, 154 or 153', 154' between adjacent plurality of 10, 20, or 30 layers, and the protective boundary layers 153, 154, 153', 154' may have an average thickness greater than about 1 micrometer or greater than about 2 micrometers, or any of the ranges described for the skin layers 155, 156. In some embodiments, the plurality (eg, one of 10, 20, or 30) layers can include, for example, two or more packets of layers separated by a protective boundary layer.

[0032] As used herein, a first element "integrally formed" with a second element means that the first and second elements are manufactured together, rather than being manufactured separately and then bonded. Integral forming includes manufacturing the first element and then manufacturing the second element on the first element. An optical film that includes multiple layers is integrally formed when the layers are manufactured together (e.g., combined as a melt stream and then cast on a chill roll to form a cast film having each layer, and then orienting the cast film), rather than being manufactured separately and then bonded.

[0033] Suitable materials for the various layers of the multilayer optical film 100 include, for example, polyethylene naphthalate (PEN), coPEN (copolyethylene naphthalate terephthalate copolymer), polyethylene terephthalate (PET), polyhexylethylene naphthalate copolymer (PHEN), glycol modified PET (PETG), glycol modified PEN (PENG), various other copolyesters as described elsewhere herein, syndiotactic polystyrene (sPS), polymethyl methacrylate (PMMA), coPMMA (copolymer of methyl methacrylate and ethyl acrylate), or blends thereof. Other suitable materials for the various layers in the multilayer optical film 100 include those described, for example, in U.S. Patent Nos. 5,103,337 (Schrenk et al.), 5,540,978 (Schrenk), 5,882,774 (Jonza et al.), 6,179,948 (Merrill et al.), 6,207,260 (Wheatley et al.), 6,783,349 (Neavin et al.), 6,967,778 (Wheatley et al.), 9,069,136 (Weber et al.), and 9,162,406 (Neavin et al.). Suitable sPS can be obtained, for example, from Idemitsu Kosan Co., Ltd. (Tokyo, Japan). Atactic polystyrene (aPS) can optionally be blended with sPS (e.g., about 5 to about 30 weight percent aPS) to adjust the refractive index of the resulting layer and / or to reduce the haze of the layer (e.g., by reducing the crystallinity of the layer). Suitable PMMA can be obtained, for example, from Arkema Inc. (Philadelphia, PA). Suitable PET can be obtained, for example, from Nan Ya Plastics Corporation, America (Lake City, SC). PETG can be described as PET in which some of the glycol units of the polymer have been replaced with different monomer units, typically monomer units derived from cyclohexanedimethanol.PETG can be produced by replacing a portion (e.g., about 15 to about 60 mole percent or about 30 to about 40 mole percent) of the ethylene glycol used in the transesterification reaction to produce the polyester with, for example, cyclohexanedimethanol. A suitable PETG copolyester includes GN071 available from Eastman Chemical Company (Kingsport, TN). PEN and coPEN can be produced, for example, as described in U.S. Pat. No. 10,001,587 (Liu). Glycol-modified polyethylene naphthalate (PENG) can be described as a PEN in which a portion of the glycol units of the polymer have been replaced with different monomer units, and can be produced, for example, by replacing a portion (e.g., about 15 to about 60 mole percent or about 30 to about 40 mole percent) of the ethylene glycol used in the transesterification reaction to produce the polyester with cyclohexanedimethanol. PHEN can be prepared, for example, as described for PEN in U.S. Patent No. 10,001,587 (Liu), except that a portion of the ethylene glycol used in the transesterification reaction (e.g., about 15 to about 60 mole percent, or about 30 to about 50 mole percent, or about 40 mole percent) is replaced with hexanediol. Other suitable copolyesters include, for example, those available under the tradename TRITAN from Eastman Chemical Company (Kingsport, Tenn.) and OKP-1 available from Osaka Gas Chemicals. Co., Ltd. (Osaka, Japan).

[0034] Copolyesters can include aromatic and aliphatic groups. The refractive index of such copolyesters can be adjusted by appropriately selecting the type and amount of aromatic and aliphatic groups. For example, reducing the aromatic content of the copolyester generally reduces the overall refractive index of the copolyester and the birefringence of an oriented layer of the copolyester. As another example, using an aromatic group containing two fused aromatic rings (e.g., as in PEN) gives a higher birefringence after orientation than using an aromatic group with a single aromatic ring (e.g., as in PET). As yet another example, incorporating a stilbene group has generally been found to increase the refractive index and birefringence. As yet another example, replacing a portion of the dimethyl terephthalate or terephthalic acid in PET with dimethyl cyclohexanedicarboxylate replaces the aromatic ring with an aliphatic ring and generally reduces the birefringence. Related useful copolyesters are described, for example, in U.S. Pat. No. 9,477,011 (Liu et al.).

[0035] The various layers of the multilayer optical film 100 can be characterized by their refractive indices along a first in-plane direction (e.g., x-direction), an orthogonal second in-plane direction (e.g., y-direction), and / or a thickness direction (z-direction) orthogonal to the first and second in-plane directions. In embodiments where the refractive indices of multiple layers are specified, the refractive indices along the x-, y-, and z-directions may be represented as nxi, nyi, and nzi, respectively, where "i" is 1, 2, etc. FIG. 3 is a schematic perspective view of exemplary layers of a multilayer optical film. The refractive indices nxi, nyi, and nzi along the x-, y-, and z-directions are shown for layer "i," which may correspond, for example, to any of layers 11, 12, 21, 22, 31, or 32 shown in FIG. 2A. The refractive index may be specified for at least one wavelength in a given wavelength range described elsewhere herein and / or for at least one wavelength in the visible range, for example, from about 400 nm to about 700 nm, or from about 420 nm to about 680 nm, or from about 450 nm to about 650 nm. The at least one wavelength may be or include, for example, at least one of a wavelength of about 532 nm, a wavelength of about 550 nm, a wavelength of about 589 nm, or a wavelength of about 633 nm. Refractive indices, also referred to as indices of refraction, may be measured, for example, using a refractometer, for example, according to the ASTM D542-14 test method.

[0036] In some embodiments, the multilayer optical film includes a plurality of polymer layers (e.g., one of a plurality of 10, 20, or 30) for reducing the shift of the left band edge with a change in the angle of incidence (e.g., an LBE compensator). In some embodiments, the plurality of polymer layers includes a plurality of alternating first and second optical layers having respective refractive indices nx1 and nx2 along the same in-plane x direction, respective refractive indices ny1 and ny2 along an in-plane y direction orthogonal to the x direction, and respective refractive indices nz1 and nz2 along the thickness direction (z direction) of the polymer layers orthogonal to the x and y directions, where nz2-nz1≧nx2-nx1≧0.02 for at least one wavelength within the predetermined wavelength range. The optical reflectance may be specified, for example, for p-polarized incident light incident on the multilayer optical film at a plane of incidence that includes the x direction. The predetermined wavelength range can be a wavelength range for which the multilayer optical film is configured to have a reflection band, as further described elsewhere herein (e.g., the predetermined wavelength range can be a visible wavelength range spanning from about 420 nm to about 680 nm). The alternating layers may alternatively be labeled differently, for example, when other alternating layers are described. For example, a plurality of polymer layers may be described as including alternating third and fourth optical layers having respective refractive indices nx3 and nx4 along the x-direction, respective refractive indices ny3 and ny4 along the y-direction, and respective refractive indices nz3 and nz4 along the thickness direction (z-direction). In this case, the above relationship between the refractive indices for at least one wavelength within a given wavelength range may be written as nz4-nz3≧nx4-nx3≧0.02. More generally, this relationship may be written as nzj-nzi≧nxj-nxi≧0.02, where "i" and "j" are integers labeling the "ith" and "jth" layers. The difference nzj-nzi for at least one wavelength may be denoted as Δnz, the difference nxj-nxi for at least one wavelength may be denoted as Δnx, and similarly the difference nyj-nyi for at least one wavelength may be denoted as Δny. In some embodiments where Δnz≧Δnx≧0.02, Δnx is 0.025, or above 0.03, or above 0.04, or 0.05, or 0.06 or more.In some embodiments, Δnz≧Δnx, and Δnx is greater than about 0.02, or greater than about 0.025, or greater than about 0.04, or greater than about 0.05, or greater than about 0.06. In some embodiments, Δnz≧Δnx≧0.02, and Δnz≧Δny≧0.02. In some embodiments, Δny is 0.025, or 0.03, or 0.04, or 0.05, or 0.06 or more. In some embodiments, Δnz≧Δny, and Δny is greater than about 0.02, or greater than about 0.025, or greater than about 0.04, or greater than about 0.05, or greater than about 0.06. In some embodiments, Δnz-Δnx is 0.01, or 0.015, or 0.02, or 0.025, or 0.03, or 0.035, or 0.04 or more. In some such embodiments, or in other embodiments, Δnz-Δny is 0.01, or 0.015, or 0.02, or 0.025, or 0.03, or 0.035, or 0.04 or more. Δnx and Δny may each be, for example, up to about 0.2, or up to about 0.15, or up to about 0.12, or up to about 0.1. Δnz may be, for example, up to about 0.22, or up to about 0.2, or up to about 0.18, or up to about 0.16. Δnz-Δnx and / or Δnz-Δny may be, for example, up to about 0.1, or up to about 0.08, or up to about 0.06.

[0037] In some embodiments, for at least one wavelength (and, for example, for a layer of an LBE compensator), nxi (e.g., nx1 or nx3) is at least about 0.02, or at least about 0.025, or at least about 0.03, or at least about 0.04, or at least about 0.05, greater than nzj (e.g., nz1 or nx3). In some such embodiments, or in other embodiments, for at least one wavelength, the magnitude of the maximum difference between nxj, nyj, and nzj (e.g., nx2, ny2, and nz2, or nx4, ny4, and nz4) is less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01. In some such embodiments, or in other embodiments, for at least one wavelength, each of nxj and nyj is at least about 0.02, or at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06 greater than each of nxi and nyi. Each of nxj and nyj may be, for example, at most about 0.2, or at most about 0.15, or at most about 0.12, or at most about 0.1 greater than each of nxi and nyi. In some embodiments, for at least one wavelength, the absolute value of the difference between the refractive index of the first optical layer (or the i-th optical layer) along the x direction and the refractive index of the first optical layer (or the i-th optical layer) along the y direction is less than about 0.05, or less than about 0.04, or less than about 0.03, or less than about 0.025, or less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01. In some embodiments, for at least one wavelength and for each of the first and second optical layers (or for each of the ith and jth optical layers), the absolute value of the difference between the refractive index of the layer along the x direction and the refractive index of the layer along the y direction is less than about 0.05, or less than about 0.04, or less than about 0.03, or less than about 0.025, or less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01.

[0038] Suitable materials for the ith (e.g., first or third) optical layer (e.g., of an LBE compensator) include, for example, copolyesters such as those available under the tradename TRITAN from Eastman Chemical Company. Suitable materials for the jth (e.g., second or fourth) optical layer (e.g., of an LBE compensator) include, for example, PHEN, PENG, or OKP-1. For example, the ith optical layer may be a TRITAN copolyester layer having refractive indices of 1.561, 1.561, and 1.529 in the x, y, and z directions, respectively, at a wavelength of 633 nm, and the jth optical layer may be an OKP-1 layer having an isotropic refractive index of about 1.64 at a wavelength of 633 nm, or a PENG or PHEN layer having an isotropic refractive index of about 1.63 at a wavelength of 633 nm.

[0039] In some embodiments, the multilayer optical film includes a plurality of polymer layers (e.g., one of a plurality of 10, 20, or 30) for reducing the shift of the right band edge with a change in the angle of incidence (e.g., an RBE compensator). In some embodiments, the plurality of polymer layers includes a plurality of alternating first and second optical layers having respective refractive indices nx1 and nx2 along the same in-plane x direction, respective refractive indices ny1 and ny2 along the in-plane y direction perpendicular to the x direction, and respective refractive indices nz1 and nz2 along the thickness direction (z direction) of the polymer layers perpendicular to the x and y directions, where each of |nx1-nx2| and |ny1-ny2| is less than about 0.02 and nz1-nz2 is greater than about 0.02 or greater than about 0.03 for at least one wavelength within the predetermined wavelength range. As further described elsewhere herein, the first and second layers may be labeled differently. For example, the layers may be referred to as the third and fourth layers, or the fifth and sixth layers, or more generally, the "ith" and "jth" layers. In some embodiments, for at least one wavelength, each of |nxi-nxj| and |nyi-nyj| (e.g., each of |nx1-nx2| and |ny1-ny2|) is less than about 0.015, or less than about 0.012, or less than about 0.01. In some such embodiments, or in other embodiments, for at least one wavelength, nzi-nzj (e.g., nz1-nz2, or nz3-nz4, or nz5-nz6) is greater than about 0.04, or greater than about 0.05, or greater than about 0.07, or greater than about 0.08, or greater than about 0.09, or greater than about 0.1. In some such embodiments, or in other embodiments, for at least one wavelength, each of |nxi-nyi| and |nxj-nyj| (e.g., each of |nx1-ny1| and |nx2-ny2|) is less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01. The difference nzi-nzj for at least one wavelength can be, for example, up to about 0.2, or up to about 0.16, or up to about 0.14.

[0040] In some embodiments, for at least one wavelength in the predetermined wavelength range (and, for example, for a layer of an RBE compensator), nxi (e.g., nx1, nx3, or nx5) is less than nzi (e.g., nz1, or nz3, or nz5) by at least about 0.02, and / or nxj (e.g., nx2, or nx4, or nx6) is greater than nzj (e.g., nz2, or nz4, or nz6) by at least about 0.02. In some such embodiments, or in other embodiments, for at least one wavelength in the predetermined wavelength range, nxi is less than nzi by at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06. In some such embodiments, or in other embodiments, for at least one wavelength in the predetermined wavelength range, nxj is greater than nzj by at least about 0.025, or at least about 0.03, or at least about 0.04, or at least about 0.05. As further described elsewhere herein, the reflectance or other optical properties can be determined for p-polarized incident light incident on the multilayer optical film. The p-polarized incident light can be incident on a plane of incidence that includes the x-direction. For a reflective polarizer, nyi and nzi can be similar (e.g., within about 0.02) and / or nyj and nzj can be similar (e.g., within about 0.02) and / or |nyj-nyi| can be less than about 0.02 for at least one wavelength. For an optical mirror, each of |nxi-nyi| and |nxj-nyj| can be, for example, less than about 0.03, or less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01 for at least one wavelength. In some embodiments, for at least one wavelength within a given wavelength range, nyi (e.g., ny1, ny3, or ny5) is less than nzi (e.g., nz1, nz3, or nz5) by at least about 0.02, and nyj (e.g., ny2, ny4, or ny6) is greater than nzj (e.g., nz2, nz4, or nz6) by at least about 0.02.In some such embodiments, or in other embodiments, nyi is at least about 0.03, or at least about 0.04, or at least about 0.05, or at least 0.06 less than nzi for at least one wavelength. In some such embodiments, or in other embodiments, nyj is at least about 0.025, or at least about 0.03, or at least about 0.04, or at least about 0.05 greater than nzj for at least one wavelength. In some embodiments, nxi and / or nyi may be, for example, about 0.2, or about 0.15, or about 0.12, or about 0.1, or about 0.08 less than nzi for at least one wavelength. In some embodiments, nyj may be, for example, up to about 0.2, or up to about 0.15, or up to about 0.12, or up to about 0.1, or up to about 0.08 greater than nzj for at least one wavelength.

[0041] Suitable materials for the ith (e.g., first, third, or fifth) optical layer (e.g., of an RBE compensator) include, for example, sPS. Suitable materials for the jth (e.g., second, fourth, or sixth) optical layer (e.g., of an RBE compensator) include, for example, copolyesters such as those available from Eastman Chemical Company under the tradename TRITAN. For example, the ith optical layer may be an sPS layer having refractive indices of about 1.55, 1.55, and 1.49 in the x, y, and z directions, respectively, at a wavelength of 633 nm, and the jth optical layer may be a TRITAN copolyester layer having refractive indices of 1.561, 1.561, and 1.529 in the x, y, and z directions, respectively, at a wavelength of 633 nm. In some embodiments, the ith optical layer is negatively birefringent and the jth optical layer is positively birefringent. PEN, PET, and TRITAN copolyester are examples of positively birefringent thermoplastic polymers, and sPS is an example of a negatively birefringent thermoplastic polymer. Whether a polymer exhibits positive or negative birefringence may depend on the geometry of the crystallites formed when the polymer is oriented, as described, for example, in U.S. Pat. No. 9,069,136 (Weber et al.). Suitable positively birefringent thermoplastic polymers include those that form crystallites with an axis of symmetry substantially aligned with the stretch direction, while suitable negatively birefringent thermoplastic polymers include those that form crystallites with a disk-shaped unit cell structure with the minimum unit cell dimension substantially aligned with the stretch direction. Further examples of positively and negatively birefringent thermoplastic polymers and isotropic thermoplastic polymers are described, for example, in U.S. Pat. Nos. 8,854,730 (Wang et al.) and 9,069,136 (Weber et al.).

[0042] In some embodiments, the multilayer optical film 100 includes a first reflector (e.g., one of a plurality of 10, 20, 30 layers) that includes alternating high and low refractive index optical layers. These optical layers can be formed from any suitable polymeric material conventionally used in reflective polymeric multilayer optical films. Suitable exemplary materials are described, for example, in U.S. Pat. Nos. 5,882,774 (Jonza et al.), 6,179,948 (Merrill et al.), 6,783,349 (Neavin et al.), 6,967,778 (Wheatley et al.), and 9,162,406 (Neavin et al.). The high refractive index layers can be positively birefringent layers, such as, for example, PET or PEN layers, and the low refractive index layers can be substantially isotropic layers, such as, for example, PMMA or coPMMA layers. In some cases, the low refractive index layer may be labeled as the ith layer (e.g., the first or third optical layer), and the high refractive index layer may be labeled as the jth layer (e.g., the second or fourth optical layer). In some embodiments, for at least one wavelength in the predetermined wavelength range, the magnitude of the maximum difference between nxi, nyi, and nzi is less than about 0.015, or less than about 0.012, or less than about 0.01. In some embodiments, for at least one wavelength in the visible wavelength range, each of nxj and nyj is at least about 0.02, or at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06, or at least about 0.08, or at least about 0.1, or at least about 0.12, or at least about 0.15 greater than nzj. Each of nxj and nyj is greater than nzj, for at least one wavelength within the predetermined wavelength range, for example, by up to about 0.3, or up to about 0.25, or up to about 0.2.

[0043] In some embodiments, the multilayer optical film 100 includes a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers and a plurality of alternating fifth and sixth polymer layers. Any one of the three plurality (e.g., one of a plurality of 10, 20, 30) can be disposed between the other two of the three plurality. Each of the three plurality can include at least 20 polymer layers in total, or the total number of each plurality can be within the ranges described elsewhere herein. Each of the first through sixth polymer layers has an average thickness of less than about 500 nm, or the average thickness can be within the ranges described elsewhere herein for the optical layers. The first to sixth polymer layers have respective refractive indices nx1 to nx6 along the x direction in the same plane (xy plane), respective refractive indices ny1 to ny6 along the in-plane y direction perpendicular to the x direction, and respective refractive indices nz1 to nz6 along a thickness direction of the polymer layers (z direction) perpendicular to the x and y directions, wherein for at least one wavelength in a visible wavelength range spanning from about 420 nm to about 680 nm, each of nx1 and ny1 is at least 0.02 greater than nz1, the magnitude of the maximum difference between nx3, ny3, and nz3 is less than 0.02, and each of nx5 and ny5 is at least 0.02 less than nz5. In some embodiments, for at least one wavelength, the maximum difference between nx2, ny2, and nz2 is less than 0.02, nx4 and ny4 are each at least 0.02 greater than nz4, |nx5-nx6| and |ny5-ny6| are each less than 0.02, and nz5-nz6 is greater than 0.02. In some embodiments, for at least one wavelength, nx1 and ny1 are each at least about 0.03 greater than nz1, the maximum difference between nx2, ny2, and nz2 is less than about 0.02, nx4 and ny4 are each at least about 0.03 greater than nz4, |nx5-nx6| and |ny5-ny6| are each less than about 0.02, nx5 and ny5 are each at least about 0.03 less than nz5, and nz5-nz6 is greater than about 0.03.The at least one wavelength may include, for example, one or more wavelengths within the range of about 450 nm to about 650 nm, or about 532 nm to about 633 nm, and may include the wavelength(s) described elsewhere herein to specify the refractive index (e.g., about 633 nm).

[0044] The first and second layers may be, for example, as described for the respective first and second optical layers of the LBE compensator. In some embodiments, for at least one wavelength, each of nx1 and ny1 is greater than nz1 by at least about 0.02, or at least about 0.025, or an amount within a range described elsewhere herein. In some embodiments, for at least one wavelength in the visible range, the magnitude of the maximum difference between nx2, ny2, and nz2 is less than about 0.02, or less than about 0.015, or within a range described elsewhere herein. In some such embodiments, or in other embodiments, for at least one wavelength in the visible wavelength range, each of nx2 and ny2 is greater than each of nx1 and ny1 by at least about 0.02, or at least about 0.025, or an amount within a range described elsewhere herein. In some such, or other, embodiments, for at least one wavelength in the visible wavelength range, nz2-nz1≧nx2-nx1≧0.02, nz2-nz1≧nx2-nx1≧0.025, or nz2-nz1 and nx2-nx1 can be within ranges described elsewhere herein. In some such, or other, embodiments, for at least one wavelength in the visible wavelength range, nz2-nz1≧ny2-ny1≧0.02, or nz2-nz1 and ny2-ny1 can be within ranges described elsewhere herein.

[0045] The third and fourth layers may be, for example, as described for the respective low and high index optical layers of the first reflector. In some embodiments, for at least one wavelength in the visible range, the magnitude of the maximum difference between nx3, ny3, and nz3 is less than about 0.02, or less than about 0.015, or the maximum difference may be within the ranges described elsewhere herein. In some such embodiments, or in other embodiments, for at least one wavelength in the visible wavelength range, each of nx4 and ny4 is greater than nz4 by at least about 0.02, or at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06, or an amount within the ranges described elsewhere herein.

[0046] The fifth and sixth layers may be, for example, as described for the respective first and second optical layers of the RBE compensator. In some embodiments, for at least one wavelength in the visible wavelength range, nx5 and ny5 are less than nz5 by at least about 0.02, or at least about 0.025, or an amount described elsewhere herein. In some such embodiments, or in other embodiments, for at least one wavelength in the visible wavelength range, each of nx6 and ny6 is greater than nz6 by at least about 0.02, or at least about 0.025, or an amount within a range described elsewhere herein. In some such embodiments, or in other embodiments, for at least one wavelength in the visible wavelength range, each of |nx5-nx6| and |ny5-ny6| is less than about 0.02, or less than about 0.015, or within a range described elsewhere herein. In some such embodiments, or in other embodiments, for at least one wavelength in the visible wavelength range, nz5-nz6 is greater than about 0.02, or greater than about 0.03, or greater than about 0.05, or within a range described elsewhere herein.

[0047] In some embodiments, the multilayer optical film 100 is an optical mirror. In some embodiments, for each of the first through sixth polymer layers, and for at least one wavelength in the visible wavelength range, the absolute value of the difference between the refractive index of the layer along the x direction and the refractive index of the layer along the y direction is less than about 0.05, or less than about 0.04, or less than about 0.03, or less than about 0.025, or less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01.

[0048] In some embodiments, the multilayer optical film comprises a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers, each of the two pluralities comprising a total of at least 10 or at least 20 polymer layers, and each of the first through fourth polymer layers having an average thickness of less than about 500 nm. The first to fourth polymer layers have respective refractive indices nx1 to nx4 along the x direction in the same plane (xy plane), respective refractive indices ny1 to n4 along the in-plane y direction perpendicular to the x direction, and respective refractive indices nz1 to nz4 along the thickness direction (z direction) of the polymer layer perpendicular to the x and y directions, and for at least one wavelength (e.g., 633 nm or another wavelength described elsewhere herein to specify a refractive index) in a predetermined wavelength range (which may be a visible wavelength range spanning from about 420 nm to about 680 nm, or may be another predetermined wavelength range described elsewhere herein), each of |nx1-nx2| and |ny1-ny2| is less than about 0.02, nz1-nz2 is greater than about 0.03, nx1 is at least about 0.02 less than nz1, nx4-nx3 is greater than about 0.03, nz4-nz3≧nx4-nx3, and nx3 is at least about 0.02 less than nz3. The first and second polymer layers may be as described elsewhere herein for an RBE compensator, and the third and fourth layers may be as described elsewhere herein for an LBE compensator. In some embodiments, for at least one wavelength, each of |nx1-nx2| and |ny1-ny2| is less than 0.015, or less than 0.012, or less than 0.01. In some such embodiments, or in other embodiments, for at least one wavelength, nz1-nz2 is greater than about 0.05, or greater than about 0.07, or greater than about 0.08, or greater than about 0.09, or greater than about 0.1, and nz1-nz2 may be, for example, up to about 0.25 or up to about 0.2.In some such embodiments, or in other embodiments, for at least one wavelength, nx1 may be at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06 less than nz1, and nx1 may be, for example, up to about 0.25 or up to about 0.2 less than nz1. In some such embodiments, or in other embodiments, for at least one wavelength, nx4-nx3 may be, for example, greater than about 0.04, or greater than about 0.05, or greater than about 0.06. In some such embodiments, or in other embodiments, for at least one wavelength, nz4-nz3 may be greater than nx4-nx3, or nz4-nz3 may be at least about 0.02, or at least about 0.03, or at least about 0.04 greater than nx4-nx3. In some such embodiments, or in other embodiments, for at least one wavelength, nx3 is at least about 0.03, or at least about 0.04, or at least about 0.05, greater than nz3, and nx3 may be, for example, up to about 0.2, or up to about 0.15, greater than nz3. In some such embodiments, or in other embodiments, for at least one wavelength, the magnitude of the maximum difference between nx4, ny4, and nz4 is, for example, less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01 (e.g., in the case of an optical mirror), or nx4 is, for example, at least about 0.02, or at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06, greater than ny4, and nx4 may be, for example, up to about 0.25, or up to about 0.2, greater than ny4 (e.g., in the case of a reflective polarizer). In some embodiments where nx4 is at least about 0.03, or at least about 0.04, or at least about 0.05, or at least about 0.06 greater than ny4, the magnitude of the difference between ny4 and nz4 is less than about 0.025, or less than about 0.02, or less than about 0.015, or less than about 0.01. In some embodiments, for at least one wavelength, nz4-nz3 and / or nx4-nx3 may be, for example, up to about 0.25 or up to about 0.2.

[0049] 4 is a schematic diagram of light 40, 40' incident on an optical element 200 at an incidence plane 42 (a plane defined by the direction of the light and the normal to the surface of the optical element). The optical element 200 can correspond to, for example, an optical film 100 or any of a plurality of layers 10, 20, 30. The light 40 is incident on the optical element 200 at a first incidence angle θ1, and the light 40' is incident on the optical element 200 at a second incidence angle θ2 that is greater than θ1. In some embodiments, for example, 0 degrees≦θ1<45 degrees, θ1+40 degrees≦2<85 degrees, or 0 degrees≦θ1<30 degrees, and θ1+45 degrees≦θ2<80 degrees. The first incidence angle θ1 can be less than about 40 degrees, or less than about 30 degrees, or less than about 25 degrees, or less than about 20 degrees, or less than about 15 degrees, or less than about 10 degrees, or less than about 5 degrees, or less than about 3 degrees. The first angle of incidence θ1 can be, for example, about 0 degrees (e.g., about 2 degrees or less). The second angle of incidence θ2 can be, for example, at least about 30 degrees, or at least about 35 degrees, or at least about 40 degrees, or at least about 45 degrees, or at least about 50 degrees, or at least about 55 degrees, or at least about 60 degrees, or at least about 65 degrees greater than the first angle of incidence θ1. The second angle of incidence θ2 can be, for example, more than about 30 degrees, or more than about 35 degrees, or more than about 40 degrees, or more than about 45 degrees, or more than about 50 degrees, or more than about 55 degrees, or more than about 60 degrees, or more than about 65 degrees. The second angle of incidence θ2 can be, for example, up to 90 degrees, or up to about 85 degrees, or up to about 80 degrees. The second angle of incidence θ2 can be, for example, about 45 degrees, or about 60 degrees, or about 75 degrees. A p-polarized light (electric field at the plane of incidence 42) state 41 is shown. The plane of incidence 42 includes a first in-plane direction (x-direction), which may be along the block axis for a reflective polarizer. When light reflectivity or other properties are described for p-polarized light at a first angle of incidence θ1 and a second angle of incidence θ2 (θ1 is 0 degrees, so the light at the first angle of incidence is normally incident), it should be understood that the normally incident light is polarized in the same plane of incidence 42 as the light at the second angle of incidence θ2.

[0050] In some embodiments, the optical reflectance of the optical element 200 is specified for at least a portion of a wavelength range from λ1 to λ2. The wavelength λ1 can be, for example, about 150 nm, or about 200 nm, or about 300 nm, or about 350 nm, or about 400 nm. The wavelength λ2 can be, for example, about 2500 nm, or about 2200 nm, or about 2000 nm, or about 1800 nm. In some embodiments, the optical reflectance of the optical element 200 is specified for a predetermined wavelength range from λa to λb. The predetermined wavelength range from λa to λb can be at least about 200 nm wide, or at least about 250 nm wide, or at least about 300 nm wide. The predetermined wavelength range from λa to λb can be, for example, up to about 2200 nm, or up to about 2000 nm, or up to about 1800 nm, or up to about 1500 nm, or up to about 1200 nm. As shown diagrammatically in FIG. 4, the predetermined wavelength range λa-λb may be located between wavelengths λ1 and λ2b. The predetermined wavelength range may be a wavelength range in which the multilayer optical film is configured to have a reflection band. For example, the layer thickness profile of the optical film may be selected to provide reflection over a desired portion of the predetermined wavelength range, or transmission over a different desired portion of the predetermined wavelength range. The predetermined wavelength range λa-λb may be a visible wavelength range, a near infrared wavelength range, or a visible / near infrared wavelength range. The wavelength λa may be, for example, about 300 nm, or about 350 nm, or about 380 nm, or about 400 nm, or about 420 nm, or about 450 nm. The wavelength λb may be, for example, about 2000 nm, or about 1600 nm, or about 1000 nm, or about 700 nm, or about 680 nm, or about 650 nm. λb is about 1000 or more, and λa may be, for example, about 680 nm, or about 700 nm, or about 720 nm, or about 750 nm. In some embodiments, the wavelength range of λa to λb is, for example, about 380 nm to about 720 nm, or about 400 nm to about 700 nm, or about 420 nm to about 680 nm, or about 450 nm to about 650 nm.

[0051] Figure 5A is a plot of the reflectivity C1 of a multilayer optical film and the reflectivities L1, M1, and R1 of the respective first, second, and third polymer layers for p-polarized light at a first incidence angle according to some embodiments. Figure 5B is a plot of the reflectivity C2 of a multilayer optical film and the reflectivities L2, M2, and R2 of the respective first, second, and third polymer layers for p-polarized light at a second incidence angle. Figure 5C is a plot of the reflectivity C3 of a multilayer optical film and the reflectivities L3, M3, and R3 of the respective first, second, and third polymer layers for p-polarized light at a third incidence angle. The multilayer optical film includes a second plurality of polymer layers and a plurality of optical layers corresponding to the first and third plurality of polymer layers, but the reflectivity L1 of the first plurality of polymer layers has been shifted to a lower wavelength than the reflectivity of the corresponding plurality of polymer layers of the multilayer optical film to facilitate illustration of reflection bands 50 and 70 and reflection bands 50' and 70', and similarly, the reflectivity R2 of the third plurality of polymer layers has been shifted to a higher wavelength than the corresponding plurality of polymer layers of the multilayer optical film to facilitate illustration of reflection bands 50' and 80' and reflection bands 50'' and 80''. In particular, reflection bands 70 and 70' have been shifted to the left for ease of illustration, and reflection bands 80' and 80'' have been shifted to the right for ease of illustration.

[0052] The plots of Figures 5A-5C were calculated using conventional optical modeling techniques assuming a first reflector having alternating high and low index optical layers, where the high index layers have indices of refraction of 1.65, 1.65, and 1.49 in the x, y, and z directions, and the low index layers have an isotropic index of 1.49; an RBE compensator having alternating high and low index optical layers, where the high index layers have indices of refraction of 1.55, 1.55, and 1.62 in the x, y, and z directions, and the low index layers have indices of refraction of 1.55, 1.55, and 1.49 in the x, y, and z directions; and an LBE compensator having alternating high and low index optical layers, where the high index layers have an isotropic index of 1.65, and the low index layers have indices of refraction of 1.55, 1.55, and 1.49 in the x, y, and z directions (indices of refraction are specified at 633 nm). The angles of incidence in Figures 5A-5C were 0 degrees, 60 degrees, and 75 degrees, respectively. Spectra were calculated at 1 nm wavelength intervals (i.e., adjacent wavelengths differing by 1 nm) and smoothed using a moving average that replaces the reflectance at a wavelength with the average of the reflectance at that wavelength and its four nearest neighbors. The smoothing procedure was applied four times to the same spectrum to generate the final spectrum. This procedure was chosen because it has been found to generally provide good agreement between calculated and measured spectra.

[0053] In some embodiments, the multilayer optical film 100 includes a plurality of first polymer layers (e.g., 11, 12, or 21, 22, or 31, 32) totaling at least 10 (e.g., one of 10, 20, or 30), each of the first layers having an average thickness less than about 500 nm. The number of polymer layers in the plurality of first polymer layers can be any of the ranges described elsewhere herein. The average thickness of the polymeric first layers can be any of the ranges described elsewhere herein for optical layers. The multilayer optical film 100 further includes a plurality of second polymer layers totaling at least 10, each of the second polymer layers having an average thickness less than about 500 nm. The plurality of first polymer layers may be disposed on and / or integrally formed with the plurality of second polymer layers. In some embodiments, the multilayer optical film 100 includes at least one layer (e.g., 153, or 154, or 153' and 154') disposed between the first and second polymer layers, which has an average thickness greater than about 1 micrometer or any range described elsewhere herein for protective boundary layers. The multilayer optical film 100 further includes a third polymer layer, a total of at least 10, each of the third layers having an average thickness less than about 500 nm. The third polymer layer may be disposed on and / or integrally formed with the first and second polymer layers. In some embodiments, the multilayer optical film 100 includes at least one layer (e.g., 153, or 154, or 153' and 154') disposed between the first and second polymer layers, which has an average thickness greater than about 1 micrometer or any range described elsewhere herein for protective boundary layers. The number of polymer layers in the plurality of second polymer layers and / or the number of polymer layers in the plurality of third polymer layers can be in any of the ranges described elsewhere herein. The average thickness of the second polymer layer and / or the third polymer layer can be in any of the ranges described elsewhere herein for the optical layers.For p-polarized incident light (e.g., light 40, 40′ having p-polarized state 41) in a predetermined wavelength range (e.g., λa to λb described elsewhere herein) disposed between about 200 nm and about 2000 nm, at each of a first incidence angle θ1 and a second incidence angle θ2 that is, for example, at least about 40 degrees greater than the first incidence angle (e.g., corresponding to the second incidence angle in FIG. 5B or the third incidence angle in FIG. 5C), a relationship between the optical film (e.g., optical reflectance C1, and optical reflectance C2 or C3) and the plurality of first polarization axes versus wavelength is obtained. The optical reflectance of each of the reflector layers (e.g., optical reflectance M1, and optical reflectance M2 or M3) has a reflection band (e.g., reflection band 50 of optical reflectance C1, and reflection band 50' or 50'' of respective optical reflectance C2 or C3; and reflection band 60 of optical reflectance M1, and reflection band 60' or 60'' of respective optical reflectance M2 or M3), and the reflection bands have a left band edge (LBE) where the reflectance on the short wavelength side of the reflection band generally increases with increasing wavelength (e.g., LBE 51 of reflection band 50, and reflection band 52 of respective reflection band 53). and a right band edge (RBE) where the reflectance on the long wavelength side of the reflection band generally decreases with increasing wavelength (e.g., RBE 52 of reflection band 50, and RBE 52' or 52" of reflection band 50' or 50", RBE 62 of reflection band 60, and RBE 62' or 62" of reflection band 60' or 60", respectively), thereby providing a first incidence angle of 0.0°. At a first incidence angle, the spacing d1 between the RBE of the optical film and the RBE of the first layer is smaller than the spacing d2 between the LBE of the optical film and the LBE of the first layer, and at a second incidence angle, the spacing d1' or d1" between the RBE of the optical film and the RBE of the first layer is larger than the spacing d2' or d2" between the LBE of the optical film and the LBE of the first layer. In some embodiments, for p-polarized light and the first incidence angle, the optical reflectivity of the plurality of second polymer layers versus wavelength does not have a reflection band within the predetermined wavelength range.In some embodiments, for p-polarized incident light over a given wavelength range, at a first angle of incidence, the optical film has a peak optical reflectance greater than about 50% and the plurality of second polymer layers have a substantially constant optical reflectance with a standard deviation of less than about 3%, and at a second angle of incidence, the optical film and the plurality of second polymer layers each have a peak optical reflectance greater than about 40%. The peak optical reflectance and / or standard deviation can be within any of the respective ranges described elsewhere herein.

[0054] The difference between the second angle of incidence and the first angle of incidence can be in any of the ranges described elsewhere herein. In some embodiments, the spacing between the RBEs at the first angle of incidence is, for example, less than about 8 nm, or less than about 6 nm, or less than about 5 nm, or less than about 4 nm. In some such embodiments, or in other embodiments, at the first angle of incidence, the spacing between the LBEs is, for example, greater than about 10 nm, or greater than about 12 nm, or greater than about 14 nm, or greater than about 16 nm, or greater than about 18 nm, or greater than about 20 nm. In some such embodiments, or in other embodiments, at the second angle of incidence, the spacing between the LBEs is, for example, less than about 8 nm, or less than about 6 nm, or less than about 5 nm, or less than about 4 nm. At the first angle of incidence, the spacing between the LBEs may be, for example, up to about 100 nm, or up to about 50 nm. At the second angle of incidence, the spacing between the RBEs may be, for example, up to about 100 nm, or up to about 50 nm.

[0055] The plurality of first polymer layers may be as described elsewhere herein for the first reflector or primary reflector. The optical film may further include one or both of the LBE or RBE compensators herein. For example, the optical film may include a plurality of second polymer layers totaling at least 10 (or within ranges described elsewhere herein), each of the second layers having an average thickness less than about 500 nm (or the average thickness may be within ranges described elsewhere herein), and the plurality of second polymer layers may be or may include a plurality of alternating first and second optical layers. The first and second optical layers may be as described elsewhere herein for the LBE or RBE compensators. In some embodiments, the first and second optical layers are as described elsewhere herein for an LBE compensator, and the multilayer optical film 100 further comprises a plurality of third polymer layers totaling at least 10 (or within ranges as described elsewhere herein), each of the third layers having an average thickness of less than about 500 nm (or within ranges as described elsewhere herein), and the plurality of third polymer layers can be or can include a plurality of alternating third and fourth optical layers, which can be as described elsewhere herein for an RBE compensator.

[0056] In some embodiments, the plurality of first polymer layers may be as described elsewhere herein for the first reflector or primary reflector. For example, the plurality of first polymer layers may include an optical mirror (e.g., for substantially normally incident light and for at least one wavelength in a predetermined wavelength range, the optical mirror may have an optical reflectance of greater than about 60% or greater than about 70% for each of two mutually orthogonal polarization states) or a reflective polarizer (e.g., for substantially normally incident light and for at least one wavelength in a predetermined wavelength range, the reflective polarizer may have an optical reflectance of greater than about 60% or greater than about 70% for light having a first polarization state (e.g., polarized along the x-axis) and an optical transmittance of greater than about 60% or greater than about 70% for light having an orthogonal second polarization state (e.g., polarized along the y-axis)). In some such embodiments, or in other embodiments, the multilayer optical film 100 further includes a plurality of second polymer layers. In some embodiments, the plurality of second polymer layers includes a plurality of alternating first and second optical layers having respective refractive indices nx1 and nx2 along the same in-plane x direction, respective refractive indices ny1 and ny2 along an in-plane y direction orthogonal to the x direction, and respective refractive indices nz1 and nz2 along a thickness direction of the second polymer layers orthogonal to the x and y directions (e.g., the plurality of second polymer layers can include a right band edge compensator including a plurality of alternating first and second optical layers), and for at least one wavelength within the predetermined wavelength range, each of |nx1-nx2| and |ny1-ny2| is less than about 0.02 and nz1-nz2 is greater than about 0.03.In some such embodiments, the multilayer optical film further comprises a plurality of third polymer layers, at least 10 in total, each of the third layers having an average thickness of less than about 500 nm, the plurality of third polymer layers comprising a plurality of alternating third and fourth optical layers having respective refractive indices nx3 and nx4 along the x direction, respective refractive indices ny3 and ny4 along the y direction, and respective refractive indices nz3 and nz4 along the thickness direction (e.g., the plurality of third polymer layers can comprise a left band edge compensator comprising a plurality of alternating third and fourth optical layers), and p-polarized incident light can be incident on the multilayer optical film at an incidence surface comprising the x direction, and for at least one wavelength within the predetermined wavelength range, nz4-nz3≧nx4-nx3≧0.02. Alternatively, the plurality of second polymer layers can comprise alternating third and fourth optical layers (e.g., the plurality of second polymer layers can comprise a left band edge compensator comprising a plurality of alternating third and fourth optical layers). In some embodiments, the plurality of second polymer layers includes a plurality of alternating first and second optical layers having respective refractive indices nx1 and nx2 along the same in-plane x direction, respective refractive indices ny1 and ny2 along an in-plane y direction orthogonal to the x direction, and respective refractive indices nz1 and nz2 along a thickness direction of the second polymer layers orthogonal to the x and y directions (e.g., the plurality of second polymer layers can include a left band edge compensator including a plurality of alternating first and second optical layers), where nz2-nz1≧nx2-nx1≧0.02 for at least one wavelength within the predetermined wavelength range. The refractive index difference can be within any corresponding range described elsewhere herein for a corresponding LBE or RBE compensator.

[0057] In some embodiments, the plurality of first polymer layers define a primary reflector, and the plurality of second polymer layers define at least one of a right band edge compensator or a left band edge compensator. In some embodiments, each of the plurality of first polymer layers and the plurality of second polymer layers includes a plurality of alternating first and second optical layers. In some embodiments, the multilayer optical film includes a right band edge compensator including a plurality of alternating first and second optical layers of the plurality of second polymer layers. In some such embodiments, or in other embodiments, the plurality of first polymer layers define a primary reflector (e.g., an optical mirror or a reflective polarizer) such that at a first angle of incidence, the reflection band of each of the optical film and the plurality of first polymer layers includes a full width at half maximum (FWHM), and each of the two FWHMs overlaps by more than 50% (or within a range described elsewhere herein) of the other of the two FWHMs. In some such or other embodiments, the multilayer optical film further comprises a plurality of third polymer layers comprising a plurality of alternating first and second optical layers. In some such embodiments, the multilayer optical film comprises a left band edge compensator comprising a plurality of alternating first and second optical layers of a plurality of polymeric third layers. In some embodiments, the multilayer optical film comprises a left band edge compensator comprising a plurality of alternating first and second optical layers of a plurality of second polymer layers. The left and right band edge compensators may be as described elsewhere herein.

[0058] In some embodiments, the multilayer optical film 100 includes a plurality (e.g., one of 10, 20, or 30 different ones) of first polymer layers disposed over and integrally formed with a plurality (e.g., one of 10, 20, 30) of second polymer layers, each of the two plurality includes a total of at least 10 polymer layers (or the total number of each plurality can be within ranges described elsewhere herein) and each of the first and second layers has an average thickness of less than about 500 nm (or the average thickness can be within ranges described elsewhere herein for the optical layers). In some embodiments, for p-polarized incident light (40, 40') in a predetermined wavelength range (e.g., λa to λb) that is at least about 200 nm wide, arranged from about 200 nm to about 2000 nm, at a first incidence angle θ1, the optical reflectivity of the plurality of first polymer layers (optical reflectivity M1) with respect to wavelength has a reflection band 60, the optical reflectivity of the plurality of second polymer layers (optical reflectivity R1) has no reflection band, and at a second incidence angle θ2 (or the first and second incidence angles can be any of the ranges described elsewhere herein) that is at least about 40 degrees greater than the first incidence angle (e.g., corresponding to the second incidence angle of FIG. 5B or the third incidence angle of FIG. 5C), the optical reflectivity of each of the plurality of first polymer layers (optical reflectivity M2 or M3) and the plurality of second polymer layers (optical reflectivity R2 or R3) with respect to wavelength has a reflection band (60' and 80', or 60'' and 80''). A reflectance band generally refers to a single restricted region of increased reflectance on a plot of reflectance versus wavelength, where the reflectance achieves a value of at least 20% within that region, and where the reflectance is less than about 0.6 times the maximum reflectance within the adjacent wavelength ranges on either side of the region.

[0059] The plurality of first polymer layers can be as described elsewhere herein for the first or primary reflector. The plurality of second polymer layers can be as described elsewhere herein for the RBE compensator. The multilayer optical film 100 may further include a plurality (e.g., one of the remaining 10, 20, or 30) of third polymer layers disposed on and integrally formed with the plurality of first and second polymer layers. The plurality of polymer third layers can be as described elsewhere herein for the LBE compensator. For example, the plurality of second polymer layers can be or include a plurality of alternating first and second optical layers that can be as described for the RBE compensator, and the plurality of third polymer layers, when included in the optical film, can be or include a plurality of alternating third and fourth optical layers that can be as described for the LBE compensator.

[0060] In some embodiments, the multilayer optical film 100 includes a plurality (e.g., one of 10, 20, or 30) of first polymer layers (e.g., 11, 12, or 21, 22, or 31, 32) totaling at least 10 (or the total number can be any range described elsewhere herein), each of the first layers having an average thickness less than about 500 nm (or the average thickness can be any range described elsewhere herein for optical layers), such that for p-polarized incident light (40, 40') at substantially normal incidence (e.g., within 20 degrees, or within 10 degrees, or within 5 degrees of normal incidence) in a predetermined wavelength range (e.g., λa to λb) located between about 200 nm and about 2000 nm, the optical film (e.g., optical reflectance C1) and the plurality of first polymer layers (e.g., For example, the optical reflectance M1) of each of the optical films has reflection bands 50 and 60 having full widths at half maximum (FWHM) 53 and 63 and right band edges (RBE) 52 and 62 on the long wavelength side of the reflection band where the reflectance generally decreases with increasing wavelength, where at least one of the two FWHMs overlaps with the other of the two FWHMs by at least 50%, or at least about 60%, or at least about 70%, or at least about 75% (see, for example, FIG. 5A ), and where an increase in the angle of incidence of p-polarized incident light of at least about 60 degrees causes the wavelengths at half maximum reflectance along the RBE of the optical film and the first layer to shift by CS and MS, respectively, to smaller wavelengths (e.g., W1, W2 shift to W1', W2', or to W1'', W2'', where CS is at least about 10 nm smaller than MS. In some embodiments, each of the two FWHMs overlaps with the other of the two FWHMs by at least 50%, or at least about 60%, or at least about 70%, or at least about 75% (see, e.g., FIG. 5A). In some embodiments, the CS is smaller than the MS, e.g., by at least about 12 nm, or at least about 14 nm, or at least about 16 nm, or at least about 18 nm. In some embodiments, the CS is smaller than the MS, e.g., by up to about 40 nm, or up to about 35 nm, or up to about 30 nm.6 is a plot of the wavelength at half maximum reflectance along the RBE of an optical film (wavelength C-WI) and the first layer of the optical film (wavelength M-WI), and the shift in wavelength at half maximum reflectance along the RBE of an optical film (C shift) and the first layer (M shift) versus angle of incidence, according to some embodiments. Figure 6 was calculated using the same model as Figures 5A-5C.

[0061] The plurality of first polymer layers may be as described elsewhere herein for the first or primary reflector. In some embodiments, the optical film includes an RBE compensator as described elsewhere herein to reduce CS to MS. For example, the multilayer optical film 100 may include a plurality of second polymer layers that may be or include a plurality of alternating first and second optical layers that may be as described elsewhere herein for the RBE compensator. The optical film may also optionally include an LBE compensator as described elsewhere herein. For example, the multilayer optical film 100 may include a plurality of third polymer layers that may be or include a plurality of alternating third and fourth optical layers that may be as described elsewhere herein for the LBE compensator.

[0062] 7A-7B are plots of the reflectances R1, C1, R2 and C2 of FIGS. 5A-5B, showing the peak reflectances and the standard deviation σ of the reflectance R1 for the reflection bands 50, 50', 80'.

[0063] In some embodiments, the multilayer optical film 100 includes a plurality (e.g., one of 10, 20, or 30) of first polymer layers (e.g., 11, 12, or 21, 22, or 31, 32) totaling at least 10 (or the total number can be any range described elsewhere herein), each of the first layers having an average thickness of less than about 500 nm (or the average thickness can be any range described elsewhere herein for optical layers), such that the optical reflectance (optical reflectance) of the optical film is less than about 100 nm for p-polarized incident light 40, 40 and a first incidence angle θ1 in a predetermined wavelength range (e.g., λa to λb) that is at least about 200 nm wide. The reflectance C1) includes a first reflection band 50 having a peak reflectance 54 of greater than about 50%, the plurality of first polymer layers have a substantially constant (e.g., maximum difference in reflectance in a given wavelength range of less than about 10% or less than about 5%) light reflectance (light reflectance R1) with a standard deviation σ of less than about 3%, and for a second incidence angle θ2 at least about 40 degrees greater than the first incidence angle θ1 (or the first and second incidence angles can be within any range described elsewhere herein), the optical film and the plurality of polymer layers have respective second reflection bands 50' and third reflection bands 80' each having a peak reflectance of greater than about 40% (56, 86, respectively). The multilayer optical film 100 further includes a plurality of second polymer layers, at least 10 in total, each of the second polymer layers having an average thickness of less than about 500 nm. The multilayer optical film 100 further comprises a plurality of third polymer layers, a total of at least 10, each of the third polymer layers having an average thickness of less than about 500 nm. The number of polymer layers in the plurality of second polymer layers and / or the number of polymer layers in the plurality of third polymer layers can be in any of the ranges described elsewhere herein. The average thickness of the second polymer layers and / or the third polymer layers can be in any of the ranges described elsewhere herein for optical layers. The light reflectance R1 shown in FIG. 7A has an average of 9.2% and a standard deviation σ of 0.31% in the wavelength range of 420 nm to 680 nm (σ is expressed as a percentage because it is the standard deviation of the reflectance expressed as a percentage).For each of the first reflection band, the second reflection band, and the third reflection band, the reflection band can be positioned within a predetermined wavelength range such that the reflection band includes a left band end positioned within the predetermined wavelength range on the short wavelength side of the reflection band, where the reflectance generally increases with increasing wavelength, and a right band end positioned within the predetermined wavelength range on the long wavelength side of the reflection band, where the reflectance generally decreases with increasing wavelength.

[0064] For measured reflectance spectra, the standard deviation of the light reflectance can be calculated directly from the measured reflectance values. In the case of calculated light reflectance, the light reflectance can be smoothed as described elsewhere herein before calculating the standard deviation, as this has been found to provide a closer match with experimental results. In some embodiments, the standard deviation σ is less than about 2%, or less than 1%, or less than 0.8%, or less than 0.6%, or less than 0.5%, or less than 0.4%. The standard deviation σ may be as low as, for example, about 0.2%, or about 0.1%, or about 0.05%, or about 0.03%. In some embodiments, the peak reflectance 54 is greater than about 65%, or greater than about 80%, or greater than about 90%, or greater than about 95%. In some such embodiments, or in other embodiments, each of the peak reflectances 56 and 86 is greater than about 50%, or greater than about 60%, or greater than about 70%, or greater than about 80%. In some such embodiments, or in other embodiments, the peak reflectance 56 is greater than about 90%, or greater than about 95%.

[0065] The plurality of first polymer layers can be as described elsewhere herein for an RBE compensator. For example, the plurality of first polymer layers can be or include a plurality of alternating first and second optical layers, which can be as described elsewhere herein for an RBE compensator. The multilayer optical film 100 can include a first reflector, as described elsewhere herein. The multilayer optical film 100 can also optionally include an LBE compensator, as described elsewhere herein. For example, the multilayer optical film 100 can include a plurality of second polymer layers, which can be or include a plurality of alternating third and fourth optical layers, which can be as described elsewhere herein for an LBE compensator.

[0066] 8A-8B are plots of the reflectivities L1, C1, L2, and C2 of FIGS. 5A-5B showing the maximum reflectivities and full widths at half maximum at different angles of incidence.

[0067] In some embodiments, the multilayer optical film 100 includes a plurality (e.g., one of 10, 20, or 30) of first polymer layers (e.g., 11, 12, or 21, 22, or 31, 32) totaling at least 10 (or the total number can be within any range described elsewhere herein), each of the first layers having an average thickness less than about 500 nm (or the average thickness can be within any range described elsewhere herein for optical layers). The plurality of first polymer layers may be as described elsewhere herein for an LBE compensator. For example, the plurality of first polymer layers may be or include a plurality of alternating first and second optical layers, which may be as described elsewhere herein for an LBE compensator. The multilayer optical film 100 may include a first reflector as described elsewhere herein. The multilayer optical film 100 may also optionally include an RBE compensator as described elsewhere herein. For example, the multilayer optical film 100 can include a plurality of second polymer layers that can be or include a plurality of alternating third and fourth optical layers, which can be as described elsewhere herein with respect to the RBE compensator.

[0068] In some embodiments, for p-polarized incident light 40, 40' in a predetermined wavelength range (e.g., λa to λb) located between about 200 nm and about 2000 nm, the maximum reflectances of the optical film and the first polymer layers are Cmax and Lmax at a first angle of incidence θ1, and C'max and L'max at a second angle of incidence θ2 at least 40 degrees greater than the first angle of incidence θ1, where Cmax and Lmax are within 20% of each other (|Cmax-Lmax|<20%), and C'max≧2L'max. In some embodiments, Cmax and Lmax are within 15% of each other, or within 10% of each other, or within 5% of each other. In some embodiments, C'max≧2.1L'max, or C'max≧2.2L'max, or C'max≧2.3L'max, or C'max≧2.4L'max. C'max may be, for example, up to about 8 times, or up to about 6 times, or up to about 5 times, of L'max.

[0069] In some embodiments, for p-polarized light incident at a first angle of incidence θ1 in a predetermined wavelength range (e.g., λa to λb) disposed between about 200 nm and about 2000 nm, the optical reflectance of the optical film (optical reflectance C1) and the optical reflectance of the plurality of first polymer layers (optical reflectance M1) versus wavelength include respective first and second reflection bands 50 and 70 having full widths at half maximum FW1 and FW2, respectively, and upon increasing the angle of incidence by at least about 40 degrees (or any range amount described elsewhere herein) to a second angle of incidence θ2, the first and second reflection bands shift to respective third reflection bands 50' and fourth reflection bands 70' at smaller wavelengths having respective full widths at half maximum FW'1 and FW'2. FW'1 can be less than about 30% smaller than FW1 ((FW1-FW'1) / FW1 x 100%) and FW'2 can be more than about 35% smaller than FW2 ((FW2-FW'2) / FW2 x 100%) more than about 35%. In some embodiments, FW'1 is less than FW1, e.g., about 28% less, or about 27% less, or about 26% less. In some embodiments, FW'2 is more than FW2, e.g., about 38% more, or about 40% more, or about 41% more. In some embodiments, (FW1-FW'1) / FW1 x 100% is, e.g., about 5% more, or about 10% more. In some embodiments, (FW2-FW'2) / FW2 x 100% is, e.g., about 70% less, or about 60% less.

[0070] 9A-9B are plots of reflectance versus wavelength for a plurality of first and second polymer layers (e.g., corresponding to LBE and RBE compensators described elsewhere herein) for a first angle of incidence (FIG. 9A) and for a second, larger angle of incidence (FIG. 9B) according to some embodiments. The plots in FIGS. 9A-9B were calculated generally as described in FIGS. 5A-5C. FIG. 10 is a plot of light reflectance versus wavelength for an optical film including a plurality of polymer first and second layers (e.g., corresponding to LBE and RBE compensators described elsewhere herein) and a plurality of polymer first and second layers for an angle of incidence that may correspond to the second angle of incidence in FIG. 9B according to some embodiments. FIG. 11 is a plot of normalized reflectance versus wavelength for an optical film including a plurality of polymer first and second layers (e.g., corresponding to LBE and RBE compensators described elsewhere herein) for different angles of incidence according to some embodiments. In FIG. 11, each reflectance curve is normalized by dividing by the maximum reflectance so that each reflectance curve has a maximum value of 1. The optical reflectances Ca, Cb, and Cc are for angles of incidence of 0 degrees, 45 degrees, and 60 degrees, respectively. The full width at half maximum (FWHM) for these angles of incidence is shown diagrammatically in FIG. 11. The reflectance curves in FIG. 11 are scaled so that the maximum reflectance is 1 for each of the angles of incidence shown. FIG. 12 is a plot of FWHM as a function of angle of incidence according to some embodiments. The optical films in FIG. 9A-FIG. 12 do not include a first or primary reflector in addition to the LBE and RBE compensators.

[0071] In some embodiments, the multilayer optical film 100 includes a plurality (e.g., one of 10, 20, or 30) of first polymer layers disposed on and integrally formed with a plurality (e.g., one of 10, 20, or 30) of second polymer layers, each of the two plurality includes at least 10 polymer layers in total (or the total number in each of the plurality can be any of the ranges described elsewhere herein) and each of the first and second layers has an average thickness less than about 500 nm (or the average thickness can be any of the ranges described elsewhere herein for optical layers). The plurality of first polymer layers can be as described elsewhere herein for an LBE compensator, and the plurality of second polymer layers can be as described elsewhere herein for an RBE compensator. For example, the plurality of first polymer layers can be or include a plurality of alternating first and second optical layers, which can be as described elsewhere herein for an LBE compensator, and the plurality of second polymer layers can be or include a plurality of alternating third and fourth optical layers, which can be as described elsewhere herein for an RBE compensator.

[0072] In some embodiments, for p-polarized incident light 40, 40' in a predetermined wavelength range (e.g., λa to λb) that is at least about 200 nm wide, arranged between about 200 nm and about 2000 nm, at a first incidence angle θ1, the optical reflectance of the plurality of first polymer layers with respect to wavelength (optical reflectance La) includes a reflection band 90, while the optical reflectance of the plurality of second polymer layers with respect to wavelength (optical reflectance Ra) does not include a reflection band, and at a second incidence angle θ2 that is about 40 degrees greater than the first incidence angle θ1 (or the first and second incidence angles can be any range described elsewhere herein), the optical reflectance of each of the plurality of first polymer layers (optical reflectance Lb) and the plurality of second polymer layers (optical reflectance Rb) with respect to wavelength includes a reflection band 90', 91'. In some embodiments, the reflection band 90 has a full width at half maximum (FWHM) that is greater than about 10 nm, and each of the reflection bands 90', 91' has a FWHM that is greater than about 10 nm. In some such embodiments, or in other embodiments, the FWHM of the reflective band 90 is greater than about 20 nm, greater than about 30 nm, or greater than about 40 nm, or greater than about 50 nm, or greater than about 60 nm, or greater than about 70 nm. In some such embodiments, or in other embodiments, each of the reflective bands 90', 91' has an FWHM greater than about 20 nm, or greater than about 30 nm, or greater than about 40 nm, or greater than about 50 nm. Each of the reflective bands 90, 90', 91' can have an FWHM of, for example, less than about 300 nm, or less than about 200 nm, or less than about 100 nm, or less than about 90 nm, or less than about 80 nm.

[0073] In some embodiments, for p-polarized incident light 40, 40′ in a predetermined wavelength range (e.g., λa to λb) that is at least about 200 nm wide and disposed between about 200 nm and about 2000 nm, at at least one incidence angle greater than about 30 degrees (e.g., at least a first incidence angle that may correspond to θ2), the optical reflectance of each of the optical film (optical reflectance C1′), the plurality of first polymer layers (optical reflectance L1′), and the plurality of second polymer layers (optical reflectance R1′) with respect to wavelength is within a reflection band (i.e., The optical film includes three reflective bands (92, 93, and 94) having a left band edge (LBE) on the short wavelength side of the reflection band where reflectivity generally increases with increasing wavelength, and a right band edge (RBE) on the long wavelength side of the reflection band where reflectivity generally decreases with increasing wavelength, such that the RBE of the optical film substantially overlaps with the RBE of one of the plurality of first layers and the plurality of second layers, and the LBE of the optical film substantially overlaps with the LBE of the other of the plurality of first layers and the plurality of second layers. A first band edge can be described as substantially overlapping a second band edge if the band edges are within, for example, about 7 nm or about 5 nm of each other along at least a majority of the length of the second band edge. For example, as shown in FIG. 10, the LBE of reflection band 92 substantially overlaps with the LBE of reflection band 93, and the RBE of reflection band 92 substantially overlaps with the RBE of reflection band 94. The first angle of incidence can be within any of the ranges described elsewhere herein for θ2. For example, the first angle of incidence can be greater than about 35 degrees, or greater than about 40 degrees, or greater than about 45 degrees, or greater than about 50 degrees, or greater than about 55 degrees, e.g., up to about 80 degrees.

[0074] In some embodiments, for p-polarized incident light 40, 40' in a predetermined wavelength range (e.g., λa to λb) located between about 200 nm and about 2000 nm and at least about 200 nm wide, at a first incident angle θ1, the optical reflectance of each of the optical film (optical reflectance Ca of FIG. 11 ) and the plurality of first polymer layers (optical reflectance La of FIG. 9A ) versus wavelength includes reflection bands 90, 95, but the optical reflectance of the plurality of second polymer layers versus wavelength does not include these reflection bands, and these reflection bands have full width at half maximum (FWHM) within about 20% of each other; and at a second incident angle θ2 that is at least about 40 degrees (or any amount in a range described elsewhere herein) greater than the first incident angle θ1, the optical reflectance of each of the optical film (optical reflectance C1' of FIG. 10 ) and the plurality of first polymer layers (optical reflectance L1' of FIG. 10 ) versus wavelength includes reflection bands 92, 93, and these reflection bands have FWHMs that differ by at least about 30%. Reflection band 90 has a FWHM of FWa (see, e.g., FIG. 9A) and reflection band 95 has a FWHM of FW1 (see, e.g., FIG. 11), which may be, for example, within about 20%, or within about 15%, or within about 10% of each other. Reflection band 92 has a FWHM of FW'c and reflection band 93 has a FWHM of FW'a (see, e.g., FIG. 10), which may differ, for example, by at least about 30% (e.g., FW'c-FW'a may be greater than 0.3 FW'a), or by at least about 40%, or by at least about 50%. FW'c and FW'a may differ, for example, by up to about 200% (e.g., FW'c may be up to about three times FW'a), or by up to about 150%.

[0075] In some embodiments, the multilayer optical film 100 includes a total of at least 10 layers (e.g., at least one of 10, 20, or 30), each of which has an average thickness less than about 500 nm (or the average thickness can be within the ranges described elsewhere herein for the optical layers). The total number of layers in the plurality can be within any of the ranges described, for example, for one or two of the plurality of 10, 20, and 30. The layers can be or include a plurality of first polymer layers and a plurality of second polymer layers, where the plurality of first polymer layers can be as described elsewhere herein for the LBE compensator and the plurality of second polymer layers can be as described elsewhere herein for the RBE compensator. In some embodiments, for p-polarized incident light 40, 40' in a predetermined wavelength range (e.g., λa to λb) that is at least about 200 nm wide, located between about 200 nm and about 2000 nm, at increasing first, second, and third angles of incidence (and / or angles of incidence θa, θb>θa, and θc>θb), the optical reflectivity of the optical film versus wavelength includes first, second, and third reflection bands 95, 96, and 97 (see, e.g., FIG. 11) having respective full widths at half maximum F1, F2, and F3, where F3>F1>F2. The first angle of incidence may correspond to θ1 shown in FIG. 4, the second angle of incidence may correspond to the angle of incidence of light 140 shown in FIG. 2A, and the third angle of incidence may correspond to θ2 shown in FIG. 4. The first angle of incidence, the second angle of incidence, and the third angle of incidence may be, for example, 0 degrees, 45 degrees, and 60 degrees, respectively. In some embodiments, the second angle of incidence is at least 30 degrees greater than the first angle of incidence, and F1 is less than about 12 nm, or less than about 10 nm, or less than about 9 nm, greater than F2. In some such embodiments, or in other embodiments, F1 is at least about 5 nm, or at least about 6 nm, greater than F2. In some embodiments, for example, the third angle of incidence is at least 45 degrees greater than the first angle of incidence, and F3 is at least about 10 nm, or at least about 15 nm, or at least about 20 nm, greater than F1.In some such embodiments, or in other embodiments, F3 is greater than F1, e.g., less than about 80, or less than about 60, or less than about 50. The first, second, and third angles of incidence may alternatively be referred to as θa, θb, and θc, respectively. Exemplary angles of incidence θa, θb, and θc, and corresponding exemplary FWHMs F1, F2, and F3 are shown in FIG. 12. In some embodiments, 0 degrees≦θa<θb<θc<90 degrees. In some such embodiments, or in other embodiments, θc<80 degrees or θc<75 degrees.

[0076] FIG. 13 is a plot of the transmittance of a multilayer optical film for unpolarized incident light at various angles of incidence, according to some embodiments. The notation Tw refers to the transmittance for an angle of incidence of w degrees (e.g., T60 is the transmittance for an angle of incidence of 60 degrees). Since light absorption is typically negligible, the reflectance R is 1 minus the transmittance, which is a good approximation. The reflectance has a reflection band 99 with a full width at half maximum (FWHM) of FW0, which is about 72 nm in the illustrated embodiment. At each angle of incidence shown, there is a wavelength range 122 where the reflectance is greater than 50%. The optical film of FIG. 13 includes an RBE compensator and an LBE compensator, and does not include an additional first or primary reflector.

[0077] 14 is a plot of the band edge wavelength for the optical film of FIG. 13 as a function of incidence angle. The left and right band edge wavelengths were determined as the wavelengths at which the transmission along the band edge is 50%. The right and left band edge wavelengths for comparative conventional optical mirrors with the same band edges at normal incidence are shown for comparison (RBE Comparative Example and LBE Comparative Example). For the comparative optical mirror, for example, there are no wavelengths at which the reflectance of the optical mirror exceeds 50% at each of the incidence angles of 0 degrees and 60 degrees.

[0078] In some embodiments, the multilayer optical film 100 includes a plurality (e.g., one of 10, 20, or 30) of alternating first and second polymer layers disposed on and integrally formed with a plurality (e.g., one of 10, 20, or 30) of alternating third and fourth polymer layers, each of the two plurality includes a total of at least 10 polymer layers (or the total number of each plurality can be within any range described elsewhere herein), and each of the first through fourth polymer layers has an average thickness of less than about 500 nm (or the average thickness can be within any range described elsewhere herein for the optical layers). In some embodiments, for unpolarized incident light 140 in a predetermined wavelength range (e.g., λa-λb) disposed between about 200 nm and about 2000 nm, the optical reflectance of the optical film with respect to wavelength includes a reflection band 99 (see, e.g., FIG. 13) having a full width at half maximum FW0 of less than about 100 nm for at least a first angle of incidence θ1 less than about 25 degrees, and for at least one first wavelength within the reflection band 99 (e.g., a wavelength within range 122), the optical reflectance of the optical film is greater than about 50% for each of the first angle of incidence θ1 and a second angle of incidence θ2 that is at least about 60 degrees greater than the first angle of incidence θ1. The first angle of incidence θ1 and the second angle of incidence θ2 can be within any range described elsewhere herein. The full width at half maximum FW0 can be, for example, less than about 90 nm, or less than about 80 nm, or less than about 75 nm. The full width at half maximum FW0 can be, for example, greater than about 30 nm or greater than about 50 nm. In some embodiments, for at least one first wavelength, the optical reflectance of the optical film is greater than about 55%, or greater than about 58%, or greater than about 60% at each of the first and second angles of incidence. In some embodiments, for at least one first wavelength, the optical reflectance of the optical film 100 is greater than about 50% at each angle of incidence in the range of 0 degrees to about 75 degrees. In some embodiments, the optical film 100 has a maximum reflectance of greater than about 80%, or greater than about 85%, or greater than about 90%, or greater than about 95% within a given wavelength range for substantially normally incident light and for each of two mutually orthogonal polarization states (e.g., polarized along the x direction and polarized along the y direction).

[0079] The first and second polymer layers may be as described elsewhere herein for an RBE compensator. The third and fourth polymer layers may be as described elsewhere herein for an LBE compensator. In some embodiments, the first through fourth polymer layers have respective refractive indices nx1 through nx4 along the same in-plane (xy-plane) x-direction, respective refractive indices ny1 through n4 along the in-plane y-direction perpendicular to the x-direction, and respective refractive indices nz1 through nz4 along the thickness direction (z-direction) of the polymer layers perpendicular to the x-direction and y-direction, where |nx1-nx2| and |ny1-ny2| are each less than about 0.02, nz1-nz2 is greater than about 0.03, and nz4-nz3≧nx4-nx3≧0.03 for at least one wavelength in the visible wavelength range spanning from about 420 nm to about 680 nm. Each of |nx1-nx2| and |ny1-ny2| can be less than about 0.015 or can be within a range described elsewhere herein for an RBE compensator. nz1-nz2 can be greater than about 0.05 or can be within a range described elsewhere herein for an RBE compensator. nz4-nz3 can be equal to or greater than nx4-nx3 and can be equal to or greater than 0.04 or can be within a range described elsewhere herein for an LBE compensator. The at least one wavelength can be about 633 nm or can be other wavelength(s) described elsewhere herein for determining the refractive index. In some embodiments, for each of the first through fourth polymer layers, and for at least one wavelength in the visible wavelength range, the absolute value of the difference between the refractive index of the layer along the x direction and the refractive index of the layer along the y direction is less than about 0.05, or less than about 0.04, or less than about 0.03, or less than about 0.025, or less than about 0.02, or less than about 0.015, or less than about 0.012, or less than about 0.01.

[0080] Terms such as "about" will be understood by those of skill in the art in the context in which they are used and described herein. Unless otherwise clear to one of skill in the art in the context in which the use of "about" as applied to quantities describing feature sizes, quantities, and physical properties is used and described herein, "about" will be understood to mean within 10 percent of a particular value. A quantity given as about a particular value may be exactly that particular value. For example, unless otherwise clear to one of skill in the art in the context in which it is used and described herein, an amount having a value of about 1 means that the amount has a value between 0.9 and 1.1, and may even be 1.

[0081] All references, patents, or patent applications referenced above are hereby incorporated by reference in their entirety. In the event of any inconsistency or contradiction between any of the incorporated references and this application, the information in the foregoing description shall prevail.

[0082] Descriptions of elements in the drawings should be understood to apply equally to corresponding elements in other drawings unless otherwise indicated. Although specific embodiments have been illustrated and described herein, those skilled in the art will appreciate that the specific embodiments illustrated and described may be replaced by various alternative and / or equivalent embodiments without departing from the scope of the present disclosure. The present application is intended to cover any adaptations, or variations, or combinations of the specific embodiments discussed herein. Accordingly, the present disclosure is intended to be limited only by the claims and the equivalents thereof.

Claims

1. 1. A multilayer optical film comprising a plurality of first polymer layers, a total of at least 10, disposed on a plurality of second polymer layers, a total of at least 10, wherein each of the first layers and the second layers has an average thickness of less than about 500 nm, such that, for p-polarized incident light in a predetermined wavelength range at least about 200 nm wide disposed between about 200 nm and about 2000 nm, at each of a first angle of incidence and a second angle of incidence at least about 40 degrees greater than the first angle of incidence: a multilayer optical film, wherein the optical reflectance of each of the optical film and the plurality of first polymer layers versus wavelength comprises a reflection band including a left band edge (LBE) on a shorter wavelength side of the reflection band where the reflectance generally increases with increasing wavelength and a right band edge (RBE) on a longer wavelength side of the reflection band where the reflectance generally decreases with increasing wavelength, whereby at the first angle of incidence, a spacing between the RBE of the optical film and the RBE of the first layer is smaller than the spacing between the LBE of the optical film and the LBE of the first layer, and at the second angle of incidence, a spacing between the RBE of the optical film and the RBE of the first layer is larger than the spacing between the LBE of the optical film and the RBE of the first layer.

2. the plurality of second polymer layers include a plurality of alternating first and second optical layers having the same respective refractive indices nx1 and nx2 along an in-plane x direction, ny1 and ny2 along an in-plane y direction orthogonal to the x direction, and nz1 and nz2 along a thickness direction of the second polymer layer orthogonal to the x direction and the y direction, and for at least one wavelength within the predetermined wavelength range: each of |nx1-nx2| and |ny1-ny2| is less than about 0.02; 10. The multilayer optical film of claim 1, wherein nz1-nz2 is greater than about 0.

03.

3. 2. The multilayer optical film of claim 1, further comprising a plurality of third polymer layers totaling at least 10, each of the third layers having an average thickness less than about 500 nm, the plurality of third polymer layers comprising a plurality of alternating third and fourth optical layers having the same respective refractive indices nx3 and nx4 along an in-plane x-direction, ny3 and ny4 along an in-plane y-direction orthogonal to the x-direction, and nz3 and nz4 along a thickness direction of the third polymer layer orthogonal to the x-direction and the y-direction, wherein nz4-nz3≧nx4-nx3≧0.02 for at least one wavelength in the predetermined wavelength range.

4. 2. The multilayer optical film of claim 1, wherein for the p-polarized incident light, at the first incidence angle, the optical reflectivity of the second polymer layers with respect to wavelength does not include a reflection band within the predetermined wavelength range.

5. For the p-polarized incident light in the predetermined wavelength range, at the first angle of incidence, the optical film has a peak light reflectance greater than about 50%, and the plurality of second polymer layers have a substantially constant light reflectance with a standard deviation of less than about 3%; The multilayer optical film of any one of claims 1 to 4, wherein at the second angle of incidence, the optical film and each of the plurality of second polymer layers have a peak optical reflectance greater than about 40%.

6. 5. The multilayer optical film of claim 1, wherein the reflection bands of the optical film and each of the plurality of first polymer layers include a full width at half maximum (FWHM), and at the first angle of incidence, at least one of the two FWHMs overlaps with at least 50% of the other of the two FWHMs, and at the second angle of incidence, the wavelengths at half maximum reflectance along the RBE of the optical film and the first layers shift to wavelengths smaller by CS and MS, respectively, and CS is at least about 10 nm smaller than MS.

7. 1. A multilayer optical film comprising a plurality of first polymer layers, a total of at least 10, disposed on a plurality of second polymer layers, a total of at least 10, each of the first and second layers having an average thickness of less than about 500 nm, wherein the optical film and the plurality of first polymer layers have maximum reflectivities, for p-polarized incident light, at a first angle of incidence, Cmax and Lmax, respectively, at a second angle of incidence at least about 40 degrees greater than the first angle of incidence, Cmax and Lmax within 20% of each other, and C'max > 2L'max, in a predetermined wavelength range at least about 200 nm wide, disposed between about 200 nm and about 2000 nm.

8. 8. The multilayer optical film of claim 7, wherein for the p-polarized incident light, at the first angle of incidence, the optical reflectivities of the optical film and the plurality of first polymer layers versus wavelength include respective first and second reflection bands with respective full widths at half maximum FW1 and FW2, and upon increasing the angle of incidence of the p-polarized incident light from the first angle of incidence to the second angle of incidence, the first and second reflection bands shift to respective third and fourth reflection bands of smaller wavelengths having respective full widths at half maximum FW'1 and FW'2, where FW'1 is less than about 30% smaller than FW1 and FW'2 is more than about 35% smaller than FW2.

9. 1. A multilayer optical film comprising a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers and a plurality of alternating fifth and sixth polymer layers, each of the three plurality comprising a total of at least 20 polymer layers, each of the first through sixth polymer layers having an average thickness of less than about 500 nm, the first through sixth polymer layers comprising the same respective refractive indices nx1 through nx6 along an in-plane x-direction, respective refractive indices ny1 through ny6 along an in-plane y-direction orthogonal to the x-direction, and respective refractive indices nz1 through nz6 along a thickness direction of the polymer layers orthogonal to the x-direction and the y-direction, for at least one wavelength in a visible wavelength range spanning from about 420 nm to about 680 nm; Each of nx1 and ny1 is at least 0.02 greater than nz1; the magnitude of the maximum difference between nx3, ny3, and nz3 is less than 0.02; A multilayer optical film, wherein each of nx5 and ny5 is at least 0.02 less than nz5.

10. 1. A multilayer optical film comprising a plurality of first polymer layers disposed on and integrally formed with a plurality of second polymer layers, each of said two plurality comprising a total of at least 10 polymer layers, each of said first layers and said second layers having an average thickness of less than about 500 nm, for p-polarized incident light in a predetermined wavelength range at least about 200 nm wide disposed between about 200 nm and about 2000 nm: at a first angle of incidence, the optical reflectance of the plurality of first polymer layers versus wavelength includes a reflection band, but the optical reflectance of the plurality of second polymer layers versus wavelength does not include a reflection band, the reflection band having a full width at half maximum (FWHM) greater than about 10 nm; at a second angle of incidence at least about 40 degrees greater than the first angle of incidence, the optical reflectivity of each of the plurality of first polymer layers and the plurality of second polymer layers versus wavelength comprises reflection bands, each of the reflection bands having a FWHM greater than about 10 nm.

11. 11. The multilayer optical film of claim 10, wherein for the p-polarized incident light, at the first incident angle, the optical reflectivity of the optical film versus wavelength includes a reflection band having a FWHM within about 20% of the FWHM of the reflection bands of the first polymer layers, and for the p-polarized incident light and the second incident angle, the optical reflectivity of the optical film versus wavelength includes a reflection band having a FWHM that differs by at least about 30% from the FWHM of the reflection bands of the first polymer layers.

12. For said p-polarized incident light, at least one angle of incidence greater than about 30 degrees:

11. The multilayer optical film of claim 10, wherein the optical reflectance of each of the optical film, the plurality of first polymer layers, and the plurality of second polymer layers versus wavelength comprises a reflection band including a left band edge (LBE) on a shorter wavelength side of the reflection band where the reflectance generally increases with increasing wavelength, and a right band edge (RBE) on a longer wavelength side of the reflection band where the reflectance generally decreases with increasing wavelength, such that the RBE of the optical film substantially overlaps with the RBE of one of the plurality of first layers and the plurality of second layers, and the LBE of the optical film substantially overlaps with the LBE of the other of the plurality of first layers and the plurality of second layers.

13. 13. The multilayer optical film of claim 10, wherein for the p-polarized incident light, at angles of incidence θa, θb>θa, θc>θb, the optical reflectivity of the optical film versus wavelength includes a first reflection band, a second reflection band, and a third reflection band having respective full widths at half maximum F1, F2, and F3, where F3>F1>F2.

14. 1. A multilayer optical film comprising a plurality of alternating first and second polymer layers disposed on and integrally formed with a plurality of alternating third and fourth polymer layers, each of the two plurality comprising a total of at least 10 polymer layers, each of the first through fourth polymer layers having an average thickness of less than about 500 nm, such that for unpolarized incident light in a predetermined wavelength range disposed from about 200 nm to about 2000 nm and having a width of at least about 200 nm, the optical reflectivity of the optical film versus wavelength comprises a reflection band having a full width at half maximum of less than about 100 nm at least at a first angle of incidence less than about 25 degrees, and for at least one first wavelength within the reflection band, the optical reflectivity of the optical film is greater than about 50% at each of the first angle of incidence and a second angle of incidence at least about 60 degrees greater than the first angle of incidence.

15. The first polymer layer to the fourth polymer layer have respective refractive indices nx1 to nx4 along the same in-plane x direction, respective refractive indices ny1 to n4 along an in-plane y direction perpendicular to the x direction, and respective refractive indices nz1 to nz4 along a thickness direction of the polymer layer perpendicular to the x direction and the y direction, and for at least one wavelength in the predetermined wavelength range, each of |nx1-nx2| and |ny1-ny2| is less than about 0.02; nz1-nz2 is greater than about 0.03; nx1 is at least about 0.02 less than nz1; nx4-nx3 is greater than about 0.03; nz4-nz3≧nx4-nx3, 15. The multilayer optical film of claim 14, wherein nx3 is at least about 0.02 greater than nz3.