Optical lens with asymmetric mirror

Abstract

1. An optical article having a base material defining a front major surface and a back major surface, at least one major surface being coated with an interference multilayer coating comprising a stack of at least one high refractive index layer having a refractive index greater than 1.55 and at least one low refractive index layer having a refractive index less than or equal to 1.55, the refractive indexes being expressed for a wavelength of 550 nm, defining highly reflective properties when the article is viewed from the front side and anti-reflective properties when the article is viewed from the back side, e.g., referred to as an asymmetric mirror, and at least one of the layers of the asymmetric mirror is a visible light absorbing substoichiometric inorganic material.

Description

[Technical field]

[0001] The present invention relates to an optical article comprising a base material defining a front major surface and a rear major surface, at least one of the major surfaces being coated with an interference multilayer coating, referred to as an asymmetric mirror, that defines highly reflective properties when the article is viewed from its front side and anti-reflective properties when the article is viewed from its rear side, and to a method for making the same.

[0002] More precisely, the invention relates to an optical article having a mirror coating that defines a reflective surface on the lens to make the wearer's eyes less perceptible to an observer, while avoiding unwanted reflections on said mirror coating towards the wearer's eyes of the array of mirrors and of the new structure coming towards the rear surface. [Background technology]

[0003] EP 3118658 discloses an optical article comprising a base material defining a front major surface and a rear major surface, at least one of the major surfaces being coated with an interference multilayer coating that defines highly reflective properties when the article is viewed from its front side and anti-reflective properties when the article is viewed from its rear side.

[0004] To this end, the present specification teaches providing an absorbing asymmetric mirror coating on the front side of the optical article, consisting of one or two absorbing metal layers (Cr, Ta, Nb, Ti or Zr) added to an interference stack, and providing a conventional anti-reflective coating, transparent to visible light, on the rear side.

[0005] The metal-containing absorbing asymmetric mirror coatings described above can have very low back reflection compared to high forward reflection, which can effectively reduce the light coming from the back side of the optical article, transmitting through the substrate, and then reflecting off the mirror coating on the front side towards the wearer's eyes.

[0006] However, due to the very strong light absorbing properties of the metallic materials used, only very thin metal layers of a few nanometers thick should be used in this optical article to ensure minimal light transmission to the wearer's eyes, but such thin metal layer thicknesses are difficult to reach or impossible to obtain or require specific methods and / or are not easy to control.

[0007] Thus, there exists an unmet need to flexibly and easily control the asymmetric reflective and transmissive properties of asymmetric mirror coatings with conventional manufacturing methods.

[0008] It is therefore an object of the present invention to provide an optical article comprising an asymmetric mirror coating which can be obtained by conventional manufacturing methods and has asymmetric reflective and transmissive properties which are flexibly and easily controlled.

[0009] Another object of the present invention is to flexibly control the transmittance of the asymmetric mirror coating within the widest performance range while still involving conventional manufacturing methods.

[0010] Another object of the present invention is to provide a process for manufacturing the above defined article, which process can be easily integrated into classical manufacturing chains and which involves materials that are compatible with and can be easily incorporated into the common materials used in the composition of mirror coatings.

[0011] The inventors have discovered that these objectives and needs can be achieved by using a specific combination of layers, involving substoichiometric materials, that are constructed in a coating mirror, which in particular allows for the definition of asymmetric reflective properties in the mirror coating while being manufactured by conventional and proven methods.

[0012] Compared with classical asymmetric mirror coatings, the asymmetric mirror coatings of the present invention have flexible asymmetric reflection properties due to the conventional and proven manufacturing methods.

[0013] The present invention thus relates to an optical article having a base material defining a front major surface and a rear major surface, at least one of the major surfaces being coated with an interference multilayer coating comprising a stack of at least one high refractive index layer having a refractive index higher than 1.55 and at least one low refractive index layer having a refractive index less than or equal to 1.55, the refractive indexes being expressed for a wavelength of 550 nm, defining highly reflective properties when the article is viewed from its front side and anti-reflective properties when the article is viewed from its rear side, e.g., referred to as an asymmetric mirror, and at least one of the layers of the asymmetric mirror being a visible light absorbing sub-stoichiometric inorganic material. Summary of the Invention [Means for solving the problem]

[0014] The invention also relates to any one of the following features taken alone or in combination: - the light absorbing substoichiometric inorganic material comprises a substoichiometric dielectric oxide or nitride material having an extinction coefficient of 0.1 or more; the light-absorbing substoichiometric inorganic material has a thickness of less than 200 nm, preferably less than 150 nm; - the near-stoichiometric inorganic material includes SiNx, where x is a predetermined number less than 1, or SiOx, where x is a predetermined number less than 2, or SiNxOy, where x and y are predetermined numbers, e.g., x<1-y / 2 and y<2(1-x); at least one substoichiometric inorganic material has a thickness of less than 30 nm, preferably less than 20 nm, preferably less than 15 nm, more preferably less than 10 nm and more than 4 nm; at least one of the visible light absorbing layers of the asymmetric mirror is a metal layer having a thickness of less than 20 nm, preferably less than 15 nm, more preferably less than 10 nm and more than 4 nm; the metal layer is sandwiched between two low refractive index layers, or between two high refractive index layers, or between one low refractive index layer and one high refractive index layer of the interference coating; If the interference coating comprises two successive metal layers, the two successive metal layers are separated by a low refractive index layer or by a high refractive index layer or by several alternating successive low and high refractive index layers. the metal layer comprises a metal species which is at least one of Al, Cr, Ta, Nb, Ti and Zr; - the front principal surface is coated with an asymmetric mirror and the rear principal surface is coated with an interference multilayer coating having anti-reflective properties when the article is viewed from the rear; - An interference multilayer coating that has anti-reflective properties when the article is viewed from the rear is an anti-reflective coating. the anti-reflective coating comprises at least one layer of a light absorbing material, the light absorbing material comprising a sub-stoichiometric inorganic material, preferably a sub-stoichiometric dielectric oxide or nitride material, comprising SiNx, where x is a predetermined number less than 1, or SiOx, where x is a predetermined number less than 2, or SiNxOy, where x and y are predetermined numbers, e.g. x<1-y / 2 and y<2(1-x). The optical article according to the invention comprises a weighted spectral reflectance average, referred to as the forward reflectance Rf, over the entire visible spectrum from 380 to 780 nm for light arriving on said front major surface at an angle of incidence of less than 15°, which weighted spectral reflectance average is greater than 2.5%; a weighted spectral reflectance average, referred to as back reflectance Rf, over the entire visible spectrum from 380 to 780 nm, for light arriving on said rear major surface at an angle of incidence of less than 15°, which is less than 2.5%, preferably less than 2%, preferably less than 1.5%, preferably less than 1%, preferably less than 0.7%, preferably less than 0.6%, preferably less than 0.5%, preferably less than 0.4%, preferably less than 0.3%, preferably less than 0.2%, The ratio of front reflectance to back reflectance at an angle of incidence of 15°, i.e. Rf / Rb, is equal to or greater than 10, preferably greater than 20, preferably greater than 30. The back reflectance Rb at angles of incidence between 35° and 45° is less than 2.5%, preferably less than 2%, preferably less than 1.5%, preferably less than 1.4%, preferably less than 1.3%. The back reflectance Rb at angles of incidence between 0° and 45° is less than 2.5%, preferably less than 2.3%, preferably less than 2.2%, preferably less than 2.1%. The back reflectance Rb at angles of incidence between -35° and 50° is less than 2.5%, preferably less than 2.3%, preferably less than 2.2%, preferably less than 2.1%.

[0015] The foregoing and other objects, features and advantages of the present invention will become readily apparent to those skilled in the art from the following detailed description taken in conjunction with the accompanying drawings. [Brief description of the drawings]

[0016] [Figure 1] 1 depicts a schematic diagram showing total forward and back reflections of an optical article whose front surface is coated with an asymmetric mirror and whose back surface is covered with an anti-reflective (AR) coating. [Diagram 2] 1 shows the reflectance curve from 280 to 780 nm taken at an incidence angle of 15° for the mirror coating of Comparative Example 1 (gold reflection color) (a) and the average optical reflectance coefficient for the same Comparative Example 1 at incidence angles including 0 to 50° (b). [Diagram 3] The average optical front reflection coefficient Rf and the average optical back reflection coefficient Rb at angles of incidence including 0° to 50° are shown for the first (gold reflection color), third (blue reflection color), fourth (green reflection color), fifth (silver reflection color), sixth, seventh, and eighth embodiments of the asymmetric mirror coating according to the present invention, respectively. [Figure 4]Figure 1 shows the front reflectance curve (Rf) and back reflectance curve (Rb) from 280 to 780 nm taken at an incidence angle of 15° for an optical article comprising a base material MR8®, on whose front surface an asymmetric mirror coating according to a second embodiment of the invention (Example 2, silver reflective color) is deposited, and on whose back surface a conventional transparent anti-reflective coating is deposited, respectively; and the same (Rf) and back reflectance (Rb) curves are shown for a second comparative mirror Example 2 deposited on the front surface of an MR8® substrate, the back surface being coated with a conventional transparent anti-reflective coating. [Diagram 5] 5 illustrates the average optical reflection coefficients for the innovative optical article of FIG. 4 and comparative examples at angles of incidence including 0° to 50°. [Figure 6-8] The average optical front reflection coefficient Rf and the average optical back reflection coefficient Rb at angles of incidence including 0° to 50° are shown for the first (gold reflection color), third (blue reflection color), fourth (green reflection color), fifth (silver reflection color), sixth, seventh, and eighth embodiments of the asymmetric mirror coating according to the present invention, respectively. [Figure 9] The same is shown for an absorbing anti-reflective coating. [Figure 10] 1 shows the reflectance curves at 280 to 780 nm taken at an incidence angle of 15° of a mirror coating of an optical article comprising an MR8® substrate, on the front surface of which an asymmetric mirror coating according to the fifth embodiment of the invention (Ex5) is deposited and on the rear surface of which an absorbing anti-reflection coating is deposited (a); and the average optical reflection coefficient at incidence angles including 0° to 50° of the innovative optical article according to this embodiment of the invention (b). [Figure 11] 5a shows the average light reflection coefficient at angles of incidence between 0° and 45° inclusive of the optical article according to FIG. 5a (Example 2 / MR8 / transparent AR) and the optical article according to FIG. 10 (Example 5 / MR8 / absorbent AR2). [Figure 12a-12b]The average optical front reflection coefficient Rf and the average optical back reflection coefficient Rb at angles of incidence including 0° to 50° are shown for the first (gold reflection color), third (blue reflection color), fourth (green reflection color), fifth (silver reflection color), sixth, seventh, and eighth embodiments of the asymmetric mirror coating according to the present invention, respectively. [Figure 13] FIG. 1 is a schematic diagram illustrating a substoichiometric monolayer deposition process for use in an asymmetric mirror according to one embodiment of the present invention. [Figure 14] 1 shows a set of graphs of typical transmission spectra of several lens substrates, each substrate provided with a sub-stoichiometric SiNx monolayer for use in an asymmetric mirror according to different embodiments of the present invention. [Figure 15] 13 shows a graph of the measured average luminescence transmission coefficient Tv for an absorbing SiNx monolayer coating according to certain embodiments, illustrating the dependence of Tv on the N2 / Ar gas flow ratio during deposition. [Figure 16] FIG. 16 is a graph showing the variation of Tv for the same SiNx monolayer coating as in FIG. 15 as a function of the thickness of such coating, illustrating the dependence of Tv on coating thickness. [Figure 17] 1 shows a set of graphs of typical transmission spectra of several lens substrates, each substrate provided with a sub-stoichiometric SiOx monolayer for use in an asymmetric mirror according to different embodiments of the present invention. [Figure 18] 1 shows a graph of measured Tv for a SiOx monolayer coating, illustrating the dependence of Tv on the O2 / Ar gas flow ratio during deposition. [Figure 19] 8 is a graph showing the variation of Tv for the same SiOx monolayer coating as in FIG. 7 as a function of the thickness of such coating, illustrating the dependence of Tv on coating thickness. [Figure 20]1 is a set of two graphs showing the refractive index at 550 nm of light absorbing SiNx and SiOx coatings deposited by magnetron sputtering in accordance with the present disclosure in certain embodiments. [Figure 21] The average optical front reflection coefficient Rf and the average optical back reflection coefficient Rb at angles of incidence including 0° to 50° are shown for the first (gold reflection color), third (blue reflection color), fourth (green reflection color), fifth (silver reflection color), sixth, seventh, and eighth embodiments of the asymmetric mirror coating according to the present invention, respectively. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0017] definition general definition The terms "comprise" (and its grammatical variations such as "comprises" and "comprising"), "have" (and its grammatical variations such as "has" and "having"), "contain" (and its grammatical variations such as "contains" and "containing") and "include" (and its grammatical variations such as "includes" and "including") are open-ended linking verbs. They are used to specify the presence of a stated feature, integer, step, or component, or group thereof, but do not exclude the presence or addition of one or more other features, integers, steps, or components, or group thereof. As a result, a method or step in a method that "comprises," "has," "contains," or "includes" one or more steps or elements has those one or more steps or elements, but is not limited to having only those one or more steps or elements.

[0018] Unless otherwise indicated, all numbers or expressions referring to quantities of ingredients, ranges, reaction conditions, and so forth used herein are understood to be modified in all instances by the term "about."

[0019] When the optical article includes one or more surface coatings, the phrase "depositing a coating or layer on the optical article" means that the coating or layer is deposited on the outermost coating of the optical article, i.e., on the coating closest to the air.

[0020] A coating "on" a surface of a lens is defined as a coating that (a) is disposed over that surface, (b) need not be in contact with that surface, i.e., one or more intervening coatings may be disposed between that surface and the subject coating (but preferably are in contact with the surface), and (c) need not completely cover that surface.

[0021] The term "coating" is understood to mean any layer, layer stack, or film that may be in contact with a substrate and / or another coating, such as a sol-gel coating or a coating made with an organic resin. Coatings may be deposited or formed by a variety of methods, including wet processing, gas processing, and film transfer.

[0022] The term "sheet" is understood to mean a single layer (monolayer), or a bilayer, i.e. a set of two layers that are in direct contact with each other. If a high-index sheet (having a refractive index higher than 1.55) has two layers, both layers are high-index layers. Similarly, if a low-index sheet (having a refractive index lower than 1.55) has two layers, both layers are low-index layers.

[0023] In the present application, a layer based on a material is defined as a layer consisting of at least 80% by weight of that material, more preferably at least 90% by weight of that material, even more preferably a layer of that material, for example a SiO2-based layer or a ZrO2-based layer comprises at least 80% by weight of SiO2 or ZrO2.

[0024] optical articles The optical article according to the present disclosure comprises at least one ophthalmic lens, or optical filter, or optical glass, or optical material suitable for human vision, e.g. at least one ophthalmic lens, or optical filter, or optical film, each comprising a substrate, or a patch intended to be fixed on the substrate or optical glass, or optical material intended for use in, e.g., an ophthalmic instrument for determining the visual acuity and / or refraction of a subject, or any kind of safety device including safety glass or safety barriers intended to face the eyes of an individual, e.g., a protective device such as a safety lens or a mask or shield.

[0025] The optical article may be implemented as an eyewear device having a frame that at least partially surrounds one or more ophthalmic lenses. By way of non-limiting example, the optical article may be a pair of glasses, sunglasses, safety goggles, sports goggles, contact lenses, intraocular implants, active lenses with amplitude modulation such as polarized lenses or with phase modulation such as autofocus lenses.

[0026] As used herein, the term "lens" refers to an organic or inorganic glass lens that includes a lens substrate that may be coated with one or more coatings of various natures.

[0027] The term "ophthalmic lens" is used to mean, for example, a lens fitted to a spectacle frame to protect the eyes and / or correct vision. The lens may be chosen from afocal, unifocal, bifocal, trifocal, progressive lenses. Although ophthalmic optical systems are the preferred field of the invention, it will be understood that the invention can be applied to other types of optical articles, such as, for example, lenses for optical instruments in photography or astronomy, optical aiming lenses, eye visors, optical systems for lighting systems, safety lenses, etc.

[0028] At least one ophthalmic lens or optical glass or optical material suitable for human vision can provide an optical function to the user, i.e. the wearer of the lens.

[0029] It may be, for example, a corrective lens for treating myopia, hyperopia, astigmatism and / or presbyopia, i.e. a spherical, cylindrical and / or addition type refractive power lens for ametropic users. The lens may have a constant refractive power, so that it provides a power similar to that provided by a single vision lens, or it may be a progressive lens with variable refractive power.

[0030] Base material / substrate As used herein, a base material has at least one surface, ie, the surface on one side, that is coated with an interference multilayer coating that provides asymmetric mirror properties.

[0031] This base material may constitute a substrate such as a lens, filter, glass, ophthalmic material, etc. as previously described, or may constitute the main part of a patch that is intended to be fixed onto such a substrate and provide the substrate with asymmetric mirror properties.

[0032] This base material or substrate may also be coated on the opposite side, i.e. the surface on the other side may also be coated, so that in such cases the optical article may have two opposite sides coated.

[0033] If the base material constitutes the substrate of an ophthalmic lens, its front surface is preferably coated with an asymmetric mirror according to the invention and its rear surface is preferably coated with an anti-reflective coating.

[0034] If the base material constitutes the main part of the patch intended to be fixed onto a substrate of an ophthalmic lens, its front surface will preferably be coated with an asymmetric mirror according to the invention and its rear surface will be adjusted to be fixed onto the substrate which will be provided with an anti-reflective coating on its rear surface.

[0035] As used herein, the rear surface of the base material or substrate is intended to mean, in the case of an ophthalmic lens, the surface closest to the wearer's eye when the article is in use. This is generally a concave surface. Conversely, the front surface of the substrate is the surface furthest away from the wearer's eye when the article is in use. This is generally a convex surface. The optical article can also be a planar article.

[0036] Clear / colored base material / substrate As used herein, unless otherwise specified, a base material, substrate, interference coating is understood to be transparent if viewing of an image through the optical article is permitted by the wearer and / or observer without adversely affecting the quality of the image. This definition of the term "transparent" may apply to all objects so modified in the description, unless otherwise specified.

[0037] In this specification, unless otherwise stated, it is understood that the base material, substrate, is colored with one coloring component (b) which acts as a selective / functional filter.

[0038] As used herein, a "selective / functional filter" corresponds to a coloring component capable of eliminating at least one band of the visible spectrum through absorption. In fact, the coloring component (b) is used to color the lens substrate, thereby achieving a given color vision correction spectral characteristic curve through a filter effect in which light having certain wavelengths is absorbed and the transmittance of the lens substrate is reduced.

[0039] The base material may have a visible light average transmission coefficient of more than 95% and therefore may be transparent to visible light, whereas the base material may be colored for selective or broader range wavefronts, i.e., have a visible light average transmission coefficient of less than 95%.

[0040] As used herein, "colored substrate" means that the light transmitted through the substrate is colored rather than white, i.e., light from a white fluorescent light source is transmitted through the substrate in such a way that to an observer the light is colored.

[0041] In a preferred embodiment, the coloring component is an absorbing dye.

[0042] As used herein, absorbing dyes can refer to both pigments and colorants, i.e., they can be insoluble or soluble in the medium.

[0043] Generally, the absorbing dyes are (a) incorporated directly into the substrate and / or into a coating that is deposited directly or indirectly on the substrate surface.

[0044] Base material Substrate, in the sense of the present invention, should be understood as meaning an uncoated substrate, which generally has two main faces. The substrate may in particular be an optically transparent material having the shape of an optical article, for example an ophthalmic lens, which is to be attached to glass. In this context, the term "substrate" is understood as meaning the base component material of an optical lens, more particularly of an ophthalmic lens. This material serves as a support for a stack of one or more coatings or layers.

[0045] The substrate may be made of inorganic glass or organic glass, preferably organic glass.The organic glass may be either thermoplastic material such as polycarbonate and thermoplastic polyurethane, or thermosetting (crosslinked) material such as diethylene glycol bis(allyl carbonate) polymer and copolymer (especially CR-39 (registered trademark) of PPG Industries), thermosetting polyurethane, polythiourethane, preferably polythiourethane resin with refractive index of 1.60 or 1.67, polyepoxide, polyepisulfide such as with refractive index of 1.74, substrate based on poly(meth)acrylate and copolymer, such as substrate containing (meth)acrylic polymer and copolymer derived from bisphenol-A, polythio(meth)acrylate, and copolymer and blend thereof. Preferred materials for the lens substrate are substrates obtained from polycarbonate (PC), diethylene glycol bis(allyl carbonate) polymers, and thermosetting polythiourethane resins, which are sold by Mitsui Toatsu Chemicals company under the MR series, in particular MR6®, MR7®, and MR8® resins. The latter substrates, as well as the monomers used in their preparation, are particularly described in U.S. Pat. Nos. 4,689,387, 4,775,733, 5,059,673, 5,087,758, and 5,191,055.

[0046] Interference coatings integrated into the base material / substrate The interference coating, i.e. either the asymmetric mirror according to the invention or the transparent or absorptive anti-reflection coating, can be associated, either by coating or lamination, to a transparent base material / substrate, i.e. a base material / substrate having an average transmission coefficient of visible light Tv of more than 96%, or any other base material / substrate (including non-transparent ones), with the latter defining an optical article having an average transmission coefficient of visible light Tv preferably in the range of 96% to 4%, more preferably in the range of 90% to 4%. In most cases the resulting optical article is a coloured optical article.

[0047] The Tv factor, also called the relative light transmission coefficient in the visible spectrum of a system, the relative average transmission coefficient of visible light or the "luminous transmittance", is defined, for example, in standard NF EN 1836 and relates to the average in the wavelength range from 380 to 780 nm, weighted according to the sensitivity of the human eye at each wavelength in the range, measured in D65 lighting conditions (daylight).

[0048] Thus, the interference coating according to the invention can be adjusted to define, for the relevant substrate, different shades of sunglasses with different average transmission coefficients of visible light Tv: - More than 80% - 43% to 80% (known as category or class 1 sunglasses), - 18 to 43% (known as class 2 sunglasses), - 8-18% (known as class 3 sunglasses), - Less than 8% (known as class 4 sunglasses).

[0049] Interference Coating The interference coating can be virtually any interference coating conventionally used in the field of optical systems, particularly ophthalmic optical systems. The interference coating can be, without limitation, an anti-reflective coating, a reflective (mirror) coating, such as a mirror reflecting infrared, visible or ultraviolet light, a filter in the visible spectrum, such as a blue cut or blue pass filter.

[0050] The multilayer interference coating of the present invention comprises a stack of at least one high refractive index layer, having a refractive index greater than 1.55, and at least one low refractive index layer, having a refractive index of 1.55 or less.

[0051] More preferably, the multilayer interference coating comprises at least two layers with a low refractive index (LI) and at least two layers with a high refractive index (HI). The total number of layers in the interference coating is preferably 3 or more, more preferably 4 or more, and preferably 8 or less than 7, more preferably 7 or less, even more preferably 5 or less, and most preferably equal to 5 or 7.

[0052] As used herein, a layer of an interference coating is defined as a layer having a thickness of 1 nm or more. Thus, when counting the number of layers in an interference coating, any layer having a thickness less than 1 nm will not be considered.

[0053] According to one embodiment of the invention, the HI and LI layers do not necessarily have to alternate with each other in the stack, but may alternate: two (or more) HI layers may be deposited on top of each other, and two (or more) LI layers may be deposited on top of each other.

[0054] In the present application, a layer of an interference coating is considered to be a layer with a high refractive index (HI) if its refractive index is greater than 1.55, preferably 1.6 or more, even more preferably 1.8 or 1.9 or more, and most preferably 2 or more. This HI layer preferably has a refractive index of 3.3 or less. A layer of an interference coating is considered to be a low refractive index layer (LI) if its refractive index is 1.55 or less, preferably 1.52 or less, more preferably 1.48 or 1.47 or less. This LI layer preferably has a refractive index of 1.1 or more.

[0055] Luminous reflectance The "average light reflectance coefficient", denoted Rv, also known as the "luminous reflectance coefficient", is as defined in the ISO 13666:1998 standard and is measured according to the ISO 8980-4 standard (at angles of incidence less than 17°, typically 15°). That is, it is the weighted spectral reflectance average over the entire visible spectrum from 380 to 780 nm. It can be measured for all angles of incidence θ, so that the function Rv(θ) is defined.

[0056] The average light reflection coefficient Rv can be defined as:

number

[0057] Highly reflective or "mirror" coatings have an average optical reflection coefficient Rv greater than 2.5%.

[0058] The average optical reflection coefficient Rv of the antireflective coating according to the present invention is preferably less than or equal to 2.5%, more preferably less than or equal to 2% or 1%, even more preferably ≦0.85%.

[0059] Interference coating according to the invention The peculiarity of the asymmetric mirror according to the invention, deposited on the main surface of a base material or substrate to constitute an optical article, is that it behaves as a mirror when the article is viewed from its front side and as an anti-reflective coating when the article is viewed from its rear or backside.

[0060] It therefore defines different reflection coefficients Rv depending on the observation direction, i.e. a high (greater than 2.5%) forward reflection coefficient, denoted Rf, and a low (less than 2.5%) backward reflection coefficient, denoted Rb. In Fig. 1, the forward reflection coefficient of the asymmetric mirror 1 deposited on the front surface 2 of the substrate 3 is denoted Rf1, and the backward reflection coefficient of the asymmetric mirror 1 is denoted Rb2. Due to the visible light absorption properties of the mirrors designed specifically for this purpose, the backward reflection coefficient Rb2 differs from the forward reflection coefficient Rf1, more precisely, the backward reflection coefficient Rb2 is minimized (less than 2.5%) and the forward reflection coefficient Rf1 is maximized.

[0061] For this purpose, the primary interference coating according to the invention comprises a stack of at least one high refractive index HI layer, having a refractive index higher than 1.55, and at least one low refractive index LI layer, having a refractive index less than or equal to 1.55, the refractive indexes being expressed for a wavelength of 550 nm, and is designed to define highly reflective properties when the article is viewed from its front side and anti-reflective properties when the article is viewed from its rear side, and is called an asymmetric mirror.

[0062] The mirror includes at least one layer that is a visible light absorbing, sub-stoichiometric inorganic material for flexible realization of the asymmetric mirror effect using conventional fabrication methods.

[0063] The sequence, combination, materials and thicknesses of the different HI and LI layers and the visible light absorbing substoichiometric inorganic material layer are particularly chosen so that the interference coating according to the invention exhibits the above mentioned asymmetric mirror properties.

[0064] This asymmetric mirror according to the invention is deposited on one of the major surfaces of the base material or substrate, preferably the front surface, and can be combined with a second interference coating deposited on the opposite surface, preferably the rear surface, designed to define anti-reflective properties when the article is viewed from its rear surface.

[0065] This second interference coating, deposited on the opposite face, may consist of an anti-reflective coating, either transparent in terms of transmittance for visible light, or of the visible light absorbing variety.

[0066] More precisely, as shown in FIG. 1, this second interference coating 4, deposited on the rear surface of the substrate and intended to face the face of the wearer, comprises a stack of at least one high refractive index HI layer, having a refractive index higher than 1.55, and at least one low refractive index LI layer, having a refractive index less than or equal to 1.55, the refractive indexes being expressed for a wavelength of 550 nm, and is designed to define antireflective properties Rb1 (less than 2.5%) when the article is viewed from its rear surface, and further to define antireflective properties Rf2 (less than 2.5%) when the coating is viewed from the front surface of the optical article.

[0067] Furthermore, according to an interesting embodiment of the invention, an anti-reflection coating can be designed to define visible light absorption characteristics, both to reduce the transmission of light coming to the asymmetric mirror 2 towards the rear surface, thus contributing to minimizing RB2, and to reduce the back reflection Rb1 at the rear interface.

[0068] These visible light absorbing properties of the antireflective coating are further obtained according to an advantageous embodiment of the present invention by virtue of at least one layer of the antireflective coating being a sub-stoichiometric inorganic material with visible light absorbing properties, so that the effect of these visible light absorbing properties can be realized with flexibility using conventional manufacturing methods.

[0069] The sequence, combination, materials and thicknesses of the different HI and LI layers and, if present, the visible light absorbing sub-stoichiometric inorganic material layer of the second interference coating according to the invention are chosen in particular so that the interference coating according to the invention exhibits the above-mentioned antireflection and visible light absorbing properties.

[0070] The asymmetric mirror coating 1 according to the invention and a second interference coating 4 determining a low back reflection, preferably of the anti-reflective type, either transparent or absorptive to visible light, are designed such that the entire optical article, comprising the asymmetric mirror coating deposited on the main face and the second interference coating deposited on the opposite face, determines a total forward reflection coefficient Rf, resulting from the addition of the front reflection coefficient Rf1 of the asymmetric mirror and the front reflection coefficient Rf2 of the second interference coating 4, better than 2.5%, and a total forward reflection coefficient Rf, resulting from the addition of the back reflection coefficient Rb1 of the asymmetric mirror and the back reflection coefficient Rb2 of the second interference coating 4, worse than 2.5%.

[0071] The asymmetric mirror coating, the second interference coating, defines its own transmission coefficient and, taking into account also the transmission coefficient of the substrate or base material (colored or non-colored), the entire optical article is designed in such a way that it can define a given transmission coefficient Tv.

[0072] The following examples of HI and LI layers can be used for an asymmetric mirror comprising at least one layer which is a visible light absorbing substoichiometric inorganic material, and for a second interference coating according to the invention which may optionally comprise at least one anti-reflection coating which is a visible light absorbing substoichiometric inorganic material, and are therefore referred to as the HI and LI layers of the interference coating according to the invention.

[0073] The interference stacks used in the present invention, either asymmetric mirrors or anti-reflection coatings, can be designed by a conventional modeling process of optical coatings, which involves modeling the at least quasi-stoichiometric inorganic material layers and / or the desired transmission coefficients, for the entire optical article or considering the interference coating alone, with specific Tv, Rv, Rf, Rb target values ​​of successive layers based on well-known matrix methods to obtain the desired asymmetric mirror effect of the asymmetric mirror according to the present invention. Thanks to the software modeling process, specific functions are available to calculate the back reflection, and it is also possible to set a target for the back reflection Rv in addition to the forward reflections Rv, h*, and C*, as well as other parameters.

[0074] The matrix method is well known in the art and a description of the process is provided, for example, by Larouche et al. in Applied Optics, 2008, 47, 13, C219-C230.

[0075] HI layer The HI layer is generally made of one or more metal oxides, including, but not limited to, zirconium oxide (ZrO2), titanium dioxide (TiO2), alumina (Al2O3), tantalum pentoxide (Ta2O5), neodymium oxide (Nd2O5), praseodymium oxide (Pr2O3), praseodymium titanate (PrTiO3), La2O3, Nb2O5, Y2O3, SiN, Si3N4, HfO2, Ce2O3, substoichiometric titanium oxides (TiOx, x<2, x preferably varies from 0.2 to 1.2, e.g., TiO, T i2O3, or Ti3O5), substoichiometric zirconium oxide (ZrOx, x<2, x preferably varies from 0.2 to 1.2), substoichiometric silicon oxide (SiOx, x<2, x preferably varies from 0.2 to 1.2, more preferably from 0.9 to 1.1, e.g., SiO), substoichiometric silicon nitride (SiNy, y<1, y preferably varies from 0.1 to 0.6), or substoichiometric silicon nitride oxide SiNxOy, where x and y are predetermined numbers, e.g., x<1-y / 2 and y<2(1-x), and mixtures thereof.

[0076] The substoichiometric materials listed above can exhibit absorbing properties in the visible range depending on the layer thickness, number of layers, and / or conditions used during deposition.

[0077] For the purposes of the present invention, a visible light absorbing layer is defined as a layer which, when deposited as a monolayer directly on the surface of a transparent substrate (e.g., a polycarbonate substrate), reduces the luminous transmittance Tv of the transparent substrate by absorption by at least 5%, preferably at least 10%, more preferably at least 20% compared to the same transparent substrate without said layer. Absorption does not include reflection.

[0078] At least one of the layers of the multilayer interference coating according to the invention is a layer containing a visible light absorbing material, which is called a "visible light absorbing layer", "light absorbing layer" or "absorber layer" and contains a visible light absorbing material, i.e., one or more visible light absorbing compounds, whose function is to reduce the transmission of visible light by absorption.

[0079] The absorber layer can be any layer known to those skilled in the art that is suitable for absorbing at least a portion of visible light (380-780 nm).

[0080] Damping coefficient k The layer of light absorbing material preferably has an extinction coefficient k at 550 nm of 0.1 or more, 0.3 or more, or 0.5 or more. In one embodiment, the layer of light absorbing material has an extinction coefficient k of 0.1 or more, 0.3 or more, or 0.5 or more for all wavelengths in the range of 400-800 nm. The extinction coefficient (also known as the extinction coefficient) of a particular substance is designated k and measures the energy loss of electromagnetic radiation traversing the medium. It is the imaginary part of the complex refractive index.

[0081] The interference stack may include at least one absorber layer, or at least two absorber layers, or at least three absorber layers. The interference stack preferably includes 1 to 3 visible light absorbing layers.

[0082] The visible light absorbing layer is generally a layer having a high refractive index, having a refractive index of at least 1.55, preferably at least 1.80, especially at least 2.0.

[0083] According to the present disclosure, the composition and / or thickness and / or number of layers of the light absorbing layers can be adjusted so that the visible light average transmission coefficient Tv of the optical lens is preferably in the range of 96% to 4% and / or so as to impart an asymmetric mirror effect to the coherent stack. For example, the value of x or y in a SiOx or SiNy layer can be varied by changing the deposition conditions (e.g., the amount of precursor gases), since stoichiometric materials such as SiN and SiO2 are not light absorbing materials in the visible range. The refractive index of substoichiometric SiNy and SiOx layers is higher than that of the corresponding stoichiometric SiN and SiO2 coatings. Lower values ​​of x and / or y provide lenses with lower transmission coefficient Tv as well as thicker light absorbing layers (the refractive index gradually increases as the layer contains less and less nitrogen or oxygen).

[0084] The number of layers and / or thickness of the light absorbing layers of the interference coating according to the present invention can also be controlled to adjust the value of the visible light average transmission coefficient Tv and / or the asymmetric mirror effect in the above ranges, so that for the resulting coated lens, the transmission of classes 1 to 4 can be realized and different asymmetric mirror effects can be defined.

[0085] The material of the absorber layer can be any material known in the art that imparts the desired light absorbing properties, for example, the light absorbing material can be a substoichiometric inorganic material having a refractive index greater than approximately 1.55.

[0086] Substoichiometric inorganic materials may result from the reaction of oxygen and / or nitrogen with at least one metal or metalloid element. Suitable metal and metalloid elements include Mg, Y, Ti, Zr, Hf, V, Cr, Nb, Ta, W, Zn, Al, In, Sn, Sb, SiGe and Bi.

[0087] Non-limiting examples of sub-stoichiometric inorganic materials are sub-stoichiometric oxides, oxynitrides or nitrides, such as sub-stoichiometric titanium oxide, sub-stoichiometric silicon oxide, sub-stoichiometric zirconium oxide, sub-stoichiometric silicon nitride, all of which are defined above, sub-stoichiometric tungsten oxides such as NiO, TiN, WO, sub-stoichiometric titanium oxynitride, sub-stoichiometric silicon oxynitride, and any mixtures thereof.

[0088] Substoichiometric inorganic materials can also be doped with oxides, nitrides and oxynitrides of elements such as Ti, Fe and Cu, which increase the refractive index and extinction coefficient k of the material.

[0089] In a preferred embodiment, the substoichiometric inorganic material is SiN y , SiO x , TiO x , and ZrO x , y<1 and x<2. Preferred ranges for x and y are as defined above, or SiNxOy, where x and y are predetermined numbers, e.g., x<1-y / 2 and y<2(1-x).

[0090] In one embodiment, the multilayer interference coating comprises at least one layer of SiO 2 as defined above. x In another embodiment, the multilayer interference coating comprises at least one SiNy layer as defined above.

[0091] In one embodiment, all high refractive index layers of the interference coating having a thickness greater than 6 nm are visible light absorbing layers.

[0092] In one embodiment, the material of the additional absorber layer can be a metal layer that is at least one of Al, Cr, Ta, Nb, Ti and Zr that is involved in the asymmetric mirror behavior.

[0093] In one embodiment, all high refractive index layers (eg, SnO2 or ITO layers) of the non-conductive interference coating are visible light absorbing layers.

[0094] Optionally, the HI layer may further comprise silica or other materials with a low refractive index, provided that the HI layer has a refractive index higher than 1.55 as indicated above. Preferred materials include ZrO2, PrTiO3, Nb2O5, Ta2O5, TiO2, Y2O3, SiOx as described above, SiNy as described above, and mixtures thereof. In one embodiment, the interference coating comprises at least one Ta2O5-based layer.

[0095] LI layer Li layers are also well known and include, but are not limited to, SiO2, MgF2, ZrF4, AIF3, Na5AI3F 14 , Na3[AIF6], or a mixture of silica and alumina, in particular silica doped with alumina, the latter contributing to an increase in the heat resistance of the interference coating. The LI layer is preferably a layer containing at least 80% by weight of silica, more preferably at least 90% by weight of silica, based on the total weight of the layer, and even more preferably consists of a silica layer.

[0096] Optionally, the LI layer may further comprise a high refractive index material, provided that the refractive index of the resulting layer is less than or equal to 1.55.

[0097] The outer layer of the interference coating, i.e., that layer furthest from the substrate, is usually a silica-based layer (e.g. an alumina-doped silica layer) containing at least 80% by weight of silica, more preferably at least 90% by weight of silica, based on the total weight of the layer, and even more preferably consists of a silica layer.

[0098] The innermost layer of the interference coating, ie, that layer in direct contact with the hard coating, is preferably a high refractive index layer.

[0099] Typically, the HI and / or LI layers have a physical thickness in the range of 5 to 250 nm, preferably 6 to 120 nm, which may vary to a considerable extent depending, for example, on the desired properties of the layer, on the layer material, on the deposition technique, and / or on the layer position in the stack.

[0100] Generally, the total thickness of the interference coating is less than 1 μm, preferably less than or equal to 800 nm, more preferably less than or equal to 500 nm, even more preferably less than or equal to 450 nm. The total thickness of the interference coating is generally greater than 100 nm, preferably greater than 200 nm, and preferably less than 1 μm, 500 nm, or 400 nm.

[0101] Furthermore, the optical article has good resistance to heat and temperature fluctuations, i.e. a high critical temperature. In this patent application, the critical temperature of the article is defined as the starting temperature at which cracks begin to appear in the coating present on the surface (on either main face) of the substrate, leading to a degradation of the coating (generally an interference coating). The critical temperature of the article coated according to the invention is preferably ≧70° C., more preferably ≧75° C., 80° C., 90° C., 100° C. or 110° C.

[0102] Antistatic layer The optical articles of the present invention can be made antistatic, i.e., not retain and / or generate significant static charge, by incorporating at least one conductive layer in the laminate present on the surface of the article, preferably in an interference coating.

[0103] The ability of a lens to remove a static charge that occurs after rubbing with a rag or after using any other procedure to generate a static charge (such as a charge applied by corona) can be quantified by measuring the time it takes the lens to dissipate its charge. Antistatic lenses thus have a discharge time of the order of several hundred milliseconds, preferably less than or equal to 500 ms, while for charged lenses the discharge time is of the order of several tens of seconds. In the present application, the discharge time is measured according to the method published in French patent application No. 2 943 798.

[0104] As used herein, "conductive layer" or "antistatic layer" is intended to mean a layer that, due to its presence on the surface of the substrate, reduces the ability of the optical article to attract dust / particles due to charge accumulation.Preferably, when provided on a non-antistatic substrate (i.e., has a discharge time longer than 500ms), the antistatic layer can make the optical article not retain and / or generate a large amount of static charge, for example, has a discharge time of 500ms or less after a static charge is applied on its surface, so that small dust particles are prevented from adhering to the optical article due to preventing the effect of static electricity.

[0105] The conductive layer may be located at various positions within the stack, typically in or in contact with the interference coating, provided that its reflective or anti-reflective properties are not affected. The conductive layer is preferably located between two layers of the interference coating and / or adjacent to a layer having a high refractive index of such an interference coating. In one embodiment, the conductive layer is located immediately below a layer having a low refractive index of the interference coating, most preferably being the penultimate layer of the interference coating by being located immediately below the LI outer layer of the interference coating.

[0106] In one embodiment, the conductive layer is in direct contact with the two layers having a refractive index of 1.55 or less, and the conductive layer is preferably located in the penultimate position of the interference coating in the direction away from the substrate.

[0107] The conductive layer must be thin enough so as not to alter the transparency of the interference coating. The conductive layer is preferably made of a conductive and highly transparent material, usually a metal oxide, which may be optionally doped. In this case, the thickness of the conductive layer is preferably in the range of 1-15 nm, more preferably 1-10 nm, ideally 2-8 nm. Preferably, the conductive layer comprises an optionally doped metal oxide selected from indium, tin, zinc oxide, and mixtures thereof. Indium-tin oxide (In2O3:Sn, indium oxide doped with tin, denoted ITO), zinc oxide doped with aluminum (ZnO:Al), indium oxide (In2O3), and tin oxide (SnO2) are preferred. In the most preferred embodiment, the conductive and highly transparent layer is a SnO2 layer.

[0108] Generally, the conductive layer contributes to obtain interference properties in the stack, but in a limited way due to its small thickness, and typically represents the layer with high refractive index in the above-mentioned coating.This is the case for layers made of conductive and highly transparent materials, such as ITO or SnO2 layers.Therefore, if a conductive layer is present, it is preferably the outermost high refractive index layer of the interference coating, or one of the outermost high refractive index layers of the interference coating, if the conductive layer is adjacent to one or more high refractive index layers.

[0109] The conductive layer can be deposited according to any suitable method, for example, preferably by ion beam assisted vacuum deposition (IAD, in particular as described in US Patent Application Publication No. 2006 / 017011 and US Patent No. 5,268,781) to enhance its transparency, or by cathode sputtering.

[0110] The conductive layer may also be a very thin layer of a noble metal (such as Ag, Au, Pt) typically less than 1 nm thick, preferably less than 0.5 nm thick.

[0111] Method of deposition The various layers of the interference coating are preferably deposited by vapor deposition under vacuum, according to one of the following methods: i) by evaporation, optionally with ion beam assistance; ii) by ion beam spraying; iii) by cathodic sputtering; iv) by plasma-assisted chemical vapor deposition. These various methods are described in the references "Thin Film Processes" and "Thin Film Processes II", edited by Vossen & Kern, Academic Press, 1978 and 1991, respectively. A particularly recommended method is evaporation under vacuum. Preferably, the deposition of each of the abovementioned layers is carried out by evaporation under vacuum. Such a process advantageously avoids heating of the substrate, which is particularly interesting for coating substrates that are sensitive to heat, such as organic glasses.

[0112] When the light absorbing layer comprises a substoichiometric inorganic material, it can be formed according to known methods. The substoichiometric composition of the material can be obtained thanks to physical or chemical vapor deposition of precursor substances, typically by magnetron sputtering.

[0113] For example, a SiNy layer can be deposited by magnetron sputtering of a silicon target in an atmosphere containing a mixture of N2 and argon with a predetermined N2 / Ar flow ratio. x The layers can be deposited by magnetron sputtering of a silicon target in an atmosphere containing a mixture of O2 and argon with a given O2 / Ar flow ratio. The value of Tv and / or the asymmetric mirror effect of the final article depends on the value of such ratio and / or on the value of the thickness and / or on the number of layers.

[0114] The silicon target mentioned above is SiN x and / or SiO x 1 is a non-limiting example of a source material for depositing a visible light absorbing material.

[0115] In a magnetron sputtering thin film deposition process, the source material may be a solid block, called a sputtering target. As a non-limiting example, the sputtering target may be a pure silicon disk, as shown in FIG.

[0116] In one embodiment, during the deposition process, a high-energy argon plasma is generated and bombarded on the Si target surface. + The ions dislodge Si atoms or clusters from the Si target, which are then deposited on the substrate surface to form a layer or thin film.

[0117] During the sputtering process, nitrogen or oxygen gas is introduced into the deposition chamber, resulting in the deposition of silicon nitride or silicon oxide materials.

[0118] When sufficient amounts of nitrogen or oxygen are introduced, optically transparent SiN or SiO2 materials having stoichiometric compositions can be deposited.

[0119] According to the present disclosure, on the other hand, as long as an insufficient amount of nitrogen or oxygen is introduced, light-absorbing SiN having a substoichiometric composition can be obtained. y (y<1) or SiO x (x<2) materials may be deposited.

[0120] Flexibility and control of the asymmetric mirror effect or transmission coefficient of asymmetric mirrors or absorptive anti-reflective coatings according to the present invention Further details regarding the deposition of the light absorbing layer and the effect of different deposition parameters on the properties of said layer are detailed below.

[0121] In one embodiment, where the coating comprises a sub-stoichiometric HI layer as the HI absorbing layer, the sub-stoichiometric composition of the material is obtained by virtue of physical or chemical vapor deposition of the material, more preferably by magnetron sputtering.

[0122] For example, in one embodiment in which the coating is made of SiNx, a predetermined thickness of a SiNx layer may be deposited by magnetron sputtering of a silicon target in an atmosphere containing a mixture of N2 and Ar having a predetermined N2 / Ar ratio.

[0123] In one such embodiment, the value of the average visible light transmission coefficient of the coating depends on the value of the SiNx layer thickness and the value of the N2 / Ar ratio.

[0124] In one embodiment in which the coating includes a layer made of SiOx as the HI absorbing layer, a predetermined thickness of the SiOx layer may be deposited by magnetron sputtering of a silicon target in an atmosphere containing a mixture of O2 and Ar having a predetermined O2 / Ar ratio.

[0125] In one such embodiment, the value of the average visible light transmission coefficient of the coating depends on the value of the SiOx layer thickness and the value of the O2 / Ar ratio.

[0126] The silicon targets mentioned above are non-limiting examples of source materials for depositing SiNx and / or SiOx light absorbing materials.

[0127] In a magnetron sputtering thin film deposition process, the source material may be a solid block, called a sputtering target. As a non-limiting example, the sputtering target may be a pure silicon disk.

[0128] In one embodiment, during the deposition process, a high energy argon plasma is generated and bombarded with the Si target surface, resulting in high energy Ar+ ions dislodging Si atoms or clusters from the Si target, which are then deposited on the substrate surface to form a layer or thin film.

[0129] During the sputtering process, nitrogen or oxygen gas is introduced into the deposition chamber, resulting in the deposition of silicon nitride or silicon oxide materials.

[0130] When sufficient amounts of nitrogen or oxygen are introduced, optically transparent SiN or SiO2 materials having stoichiometric compositions can be deposited.

[0131] According to the present disclosure, on the other hand, light absorbing SiNx (x<1) or SiOx (x<2) materials with substoichiometric compositions can be deposited as long as an insufficient amount of nitrogen or oxygen is introduced.

[0132] According to the present disclosure, the coating comprises multiple layers, i.e., the coating is a multi-layer coating.

[0133] In some embodiments, the coating may include at least one layer of sub-stoichiometric SiNx and / or SiOx, where x is a predetermined number.

[0134] In such cases, SiNx and SiN layers of predetermined thickness can be deposited by magnetron sputtering of a silicon target in an atmosphere containing a mixture of N2 and Ar with a predetermined N2 / Ar ratio. Similarly, SiOx and SiO2 layers of predetermined thickness can be deposited by magnetron sputtering of a silicon target in an atmosphere containing a mixture of O2 and Ar with a predetermined O2 / Ar ratio.

[0135] The asymmetric mirror effect and / or transmission of a base material coated with an interference coating according to the invention having such an absorbing layer can be controlled by selecting its composition and / or its thickness, so that transmission of classes 1 to 4 can be achieved for the resulting coated lens.

[0136] That is, the value of the asymmetric mirror effect and / or the average visible transmission coefficient of an interference coating depends on: the thickness of the SiNx and SiN layers and / or their number, and / or the thickness of the SiOx and SiO2 layers and / or their number, and / or - Values ​​of N2 / Ar and O2 / Ar ratios.

[0137] In one embodiment, the coating according to the present disclosure may be a colored mirror coating, i.e., the mirror coating has a predetermined color.

[0138] The colour of the mirror can be designed in a very flexible manner, whereby the mirror can exhibit at least one predefined colour, which colour has wavelengths in the visible wavelength range, including blue and / or green and / or gold and / or purple and / or pink and / or red and / or any other desired colour, or mixed colour.

[0139] Sunglasses according to the present disclosure may also include one more lens (generally two) having the characteristics of the optical article as described above.

[0140] The present disclosure also provides a method of making an optical article as described above.

[0141] In some embodiments, an optical article comprises a base material having at least one surface coated with an interference multilayer coating providing either highly reflective or anti-reflective properties, the coating comprising at least one layer of light absorbing material having adjustable composition and thickness, such that an asymmetric mirror effect is formed, and the visible light average transmission coefficient of said coating is controllable to have a value between 95% and 5%, and a method of making the optical article comprises depositing at least one layer of light absorbing material of a predetermined thickness on the base material.

[0142] In some embodiments, the depositing step may include depositing the predetermined thickness of SiNx in an atmosphere including a mixture of N2 and Ar having a predetermined N2 / Ar ratio.

[0143] In such an embodiment, the value of the average visible light transmission coefficient of the coating depends on: the value of the thickness of the deposited SiNx, and - Value of N2 / Ar ratio.

[0144] In an alternative embodiment, the deposition step may include depositing the predetermined thickness of SiOx in an atmosphere including a mixture of O2 and Ar having a predetermined O2 / Ar ratio.

[0145] In such an alternative embodiment, the value of the average visible light transmission coefficient of the coating depends on: the value of the thickness of the deposited SiOx, and - Value of O2 / Ar ratio.

[0146] FIG. 14 shows typical transmission spectra of 8-lens Orma / Titus-2.00 substrates with 260 nm SiNx monolayer coatings deposited in N2 / Ar mixed atmospheres with different ratios of N2 / Ar gas flow rates.

[0147] One side of the lens, e.g., the convex side denoted by Cx, was coated with a monolayer SiNx coating having a thickness of about 260 nm, which was deposited by magnetron sputtering in an atmosphere of N2+Ar mixture with different ratios of N2 / Ar gas flow rates.

[0148] It can be seen that as the N2 / Ar ratio decreases, the transmittance of the coated lens decreases significantly. The average luminous transmittance coefficient Tv(%) can be calculated according to the following formula:

number

[0149] The Tv values ​​of the above-mentioned absorbing SiNx monolayer are shown in Figure 15. It can be seen that Tv is approximately proportional to the ratio of N2 / Ar gas flow rates during the coating deposition.

[0150] In addition to the dependence of T on the coating composition, the transmittance of the SiNx coating also depends on the coating thickness, whereby T decreases as the coating thickness increases. In this regard, Figure 16 shows the variation of the average visible transmission coefficient T as a function of the thickness of the SiNx coating deposited by magnetron sputtering with the N2 / Ar gas flow ratio fixed at 0.2.

[0151] Similarly, substoichiometric SiOx (x<2) coatings deposited by reactive magnetron sputtering exhibit optical absorption.

[0152] In this regard, FIG. 17 shows typical transmittance spectra of eight Orma / Titus substrates, the front surface of which was coated with a monolayer SiO coating having a thickness of about 370 nm and deposited in an O2 / Ar mixture atmosphere with different ratios of O2 / Ar gas flow rates.

[0153] It can be seen that as the O2 / Ar ratio decreases, the transmittance of the lens decreases significantly, especially in the short wavelength range.

[0154] FIG. 18 shows that the Tv of the SiOx monolayer coating decreases as the O2 / Ar gas flow rate decreases, and thus it can be seen that the Tv of the SiOx monolayer coating depends on the ratio of O2 / Ar gas flow rates during deposition.

[0155] FIG. 19 shows the variation of Tv as a function of thickness of SiOx coatings deposited by magnetron sputtering at a fixed O2 / Ar gas flow ratio of 0.2.

[0156] SiO x It can be seen that Tv decreases as the coating thickness increases.

[0157] In all of the above methods, the deposition step may involve magnetron sputtering using a silicon target.

[0158] However, magnetron sputtering is mentioned only as a non-limiting example of a conventional method of depositing a material layer. As a variant, electron beam evaporation techniques may be used to form interference coatings according to the present disclosure.

[0159] In such a variant, additional gas lines for supplying N2 and / or O2 may be provided in the anti-reflective coating machine for electron beam evaporation.

[0160] More generally, the deposition process may involve using chemical or physical vapor deposition techniques.

[0161] As detailed above, absorbing materials can be incorporated into multi-layer interference AR or mirror coatings. Such absorbing interference coatings can be applied to sunglasses with a simpler production flow similar to the prior art, since no tinting step is required.

[0162] To design AR or mirror stacks with absorbing SiOx and / or SiNx materials, the optical properties of different monolayer coatings deposited by magnetron sputtering can be determined by spectroscopic ellipsometry.

[0163] Stoichiometric SiN (deposited in N2+Ar mixture atmosphere with N2 / Ar gas flow ratio greater than 1.0) and SiO2 (deposited in O2+Ar mixture atmosphere with O2 / Ar gas flow ratio greater than 1.25) coatings showed no obvious absorption in the visible light region (380-780 nm). Their refractive indices at 550 nm are 1.968 and 1.462, respectively.

[0164] FIG. 20 shows the refractive index at 550 nm of absorbing SiNx and SiOx coatings deposited by magnetron sputtering.

[0165] It should be noted that the refractive index of substoichiometric SiNx and SiOx coatings is higher than that of the corresponding stoichiometric SiN and SiO2 coatings. Typically, the refractive index increases when the ratio of N2 / Ar or O2 / Ar gas flow is decreased. In other words, the refractive index increases gradually as the coating becomes deficient in nitrogen or oxygen.

[0166] Such absorbing materials can be incorporated into multilayer interferometric AR or mirror coatings in combination with stoichiometric SiO2 and / or SiN materials.

[0167] In another embodiment, a low-temperature plasma CVD method is used to deposit a visible light absorbing layer. As raw material gases, silane gas (monosilane, dichlorosilane, etc.) and hydrogen gas, nitrogen gas, oxygen gas, or ammonium gas are mixed in a sample chamber at a predetermined flow rate ratio, thereby forming, for example, a SiOx and / or SiNy layer.

[0168] The outermost low refractive index layer of the interference coating is preferably deposited without ion assistance, preferably without concomitant treatment with energetic species. In another embodiment, the low refractive index layer of the interference coating is deposited without ion assistance, preferably without concomitant treatment with energetic species.

[0169] In one embodiment, with the exception of the conductive layer (if present in the interference coating), none of the layers of the interference coating are deposited with ion assistance (preferably none of the layers of the interference coating are deposited with concomitant treatment with energetic species).

[0170] In another embodiment, at least one HI layer of the interference coating, such as the conductive layer or the Ta2O5 layer (if present in the interference coating), is deposited under ion assistance.

[0171] Optionally, the deposition of one or more of the layers is performed by supplying a (auxiliary) gas during the deposition process of the layers in the vacuum chamber, as disclosed in US Patent Application Publication No. 2008 / 206470. In particular, an additional gas, such as a rare gas, e.g. argon, krypton, xenon, neon; oxygen, nitrogen, or a mixture of two or more of these gases, is introduced into the vacuum deposition chamber while the layers are being deposited. The gas used during this deposition process is not an ionized gas, and more preferably is not an activated gas.

[0172] This gas supply allows for the regulation of pressure, which is different from ion bombardment processes such as ion-assisted. This usually makes it possible to limit the stress of the interference coating and to strengthen the adhesion of the layer. When using such a deposition method, called deposition under gas pressure regulation, it is preferable to work under an oxygen atmosphere (so-called "passive oxygen"). The use of an additional gas supply during the deposition of a layer produces a layer that is structurally different from the layer deposited without the additional gas supply.

[0173] In one embodiment, the outermost high refractive index layers of the interference coating, except for the conductive layer (if present at the outermost position), are deposited in a vacuum chamber, in which case at least one auxiliary gas is provided during deposition. In another embodiment, the outermost high refractive index layers of the interference coating, except for the conductive layer (if present at the outermost position), are deposited in a vacuum chamber, in which case at least one auxiliary gas is provided during deposition.

[0174] Primer Coating The impact resistant primer coating that may be used in the present invention may be any coating that is typically used to improve the impact resistance of a finished optical article. By definition, an impact resistant primer coating is a coating that improves the impact resistance of a finished optical article compared to the same optical article but without the impact resistant primer coating.

[0175] Typical impact-resistant primer coatings are (meth)acrylic and polyurethane-based coatings. Specifically, the impact-resistant primer coating according to the present invention can be made from a latex composition such as a poly(meth)acrylic latex, a polyurethane latex, or a polyester latex.

[0176] Preferred primer compositions include thermoplastic polyurethane-based compositions such as those described in JP-A-63-141001 and JP-A-63-87223, poly(meth)acrylic primer compositions such as those described in US Pat. Nos. 5,015,523 and 6,503,631, thermosetting polyurethane-based compositions such as those described in EP-A-0404111, and poly(meth)acrylic or polyurethane latex-based compositions such as those described in US Pat. Nos. 5,316,791 and EP-A-0680492. Preferred primer compositions are polyurethane-based compositions and latex-based compositions, in particular polyurethane latex, poly(meth)acrylic latex, and polyester latex, and combinations thereof. In one embodiment, the impact-resistant primer comprises a colloidal filler.

[0177] Poly(meth)acrylic latexes are latexes based on copolymers made essentially of (meth)acrylates, such as, for example, ethyl (meth)acrylate, butyl (meth)acrylate, methoxyethyl (meth)acrylate, or ethoxyethyl (meth)acrylate, typically with a small amount of at least one other comonomer, such as, for example, styrene.

[0178] Commercially available primer compositions suitable for use in the present invention include Witcobond® 232, Witcobond® 234, Witcobond® 240, Witcobond® 242 compositions (available from BAXENDEN CHEMICALS), Neorez® R-962, Neorez® R-972, Neorez® R-986, and Neorez® R-9603 (available from ZENECA RESINS), and Neocryl® A-639 (available from DSM coating resins).

[0179] The thickness of the impact resistant primer coating after curing is typically in the range of 0.05 to 30 μm, preferably 0.2 to 20 μm, more specifically 0.5 to 10 μm, even 0.6 to 5 μm or 0.6 to 3 μm, and most preferably 0.8 to 1.5 μm.

[0180] The impact resistant primer coating is preferably in direct contact with the abrasion and / or scratch resistant coating. In one embodiment, its refractive index is in the range of 1.45 to 1.55. In another embodiment, its refractive index is 1.55 or greater.

[0181] Abrasion and / or scratch resistant coating The abrasion-resistant and / or scratch-resistant coating may be any layer conventionally used as an abrasion-resistant and / or scratch-resistant coating in the field of optical lenses. If this coating is present, it is usually located below and in direct contact with the first high refractive index sheet (A).

[0182] The abrasion-resistant and / or scratch-resistant coating is preferably a hard coating based on poly(meth)acrylates or silanes, which usually contains one or more inorganic fillers intended to increase the hardness and / or refractive index of the coating after curing.

[0183] The abrasion-resistant and / or scratch-resistant coating is preferably made from a composition containing at least one alkoxysilane and / or a hydrolysate thereof, for example obtained by hydrolysis using a hydrochloric acid solution and an optional condensation and / or curing catalyst.

[0184] Suitable coatings recommended for the present invention include coatings based on epoxy silane hydrolysates, such as those described in EP 0 614 957, U.S. Pat. No. 4,211,823, and U.S. Pat. No. 5,015,523.

[0185] A preferred abrasion-resistant and / or scratch-resistant coating composition is that disclosed in EP 0614957 in the name of the applicant. It comprises hydrolysates of epoxytrialkoxysilanes and dialkyldialkoxysilanes, colloidal silica, and catalytic amounts of an aluminum-based curing catalyst, such as aluminum acetylacetonate, the remainder consisting essentially of solvents conventionally used to formulate such compositions. Preferably, the hydrolysates used are those of gamma-glycidoxypropyltrimethoxysilane (GLYMO) and dimethyldiethoxysilane (DMDES).

[0186] The abrasion- and / or scratch-resistant coating composition can be deposited by known methods and then cured, preferably using heat or UV radiation. The thickness of the (cured) abrasion- and / or scratch-resistant coating typically varies from 2 to 10 μm, preferably from 3 to 5 μm.

[0187] Hydrophobic and / or oleophobic coatings (anti-fouling topcoats) The optical article according to the invention may also comprise coatings formed on the interference coating and capable of modifying its surface properties, for example hydrophobic and / or oleophobic coatings (antifouling topcoats). These coatings are preferably deposited on the outer layer of the interference coating. Usually, their thickness is less than or equal to 10 nm, preferably in the range of 1 to 10 nm, more preferably 1 to 5 nm. Antifouling topcoats are generally coatings of the fluorosilane or fluorosilazane type, preferably comprising fluoropolyether moieties, more preferably perfluoropolyether moieties. More detailed information on these coatings is disclosed in WO2012076714.

[0188] Instead of a hydrophobic coating, a hydrophilic coating (antifog coating) may be used that imparts antifog properties, or an antifog coating precursor that imparts antifog properties when combined with a surfactant. Examples of such antifog precursor coatings are described in patent application WO 2011 / 080472.

[0189] Additional coatings, such as primers, hard coats, and antifouling top coats, can be deposited on the major surface of the substrate using methods known in the art, including spin coating, dip coating, spray coating, evaporation, sputtering, chemical vapor deposition, and lamination.

[0190] Typically, an optical article according to the invention comprises a base material or substrate, the main surfaces of which are successively coated with an impact-resistant primer layer, an abrasion-resistant and / or scratch-resistant layer, an asymmetric mirror-type light-absorbing interference coating according to the invention, and a hydrophobic and / or oleophobic coating, or a hydrophilic coating imparting anti-fog properties, or an anti-fog precursor coating.

[0191] Due to the presence, of the asymmetric mirror according to the invention, an optical article is obtained, which defines high reflection properties when the article is viewed from its front side and anti-reflection properties when the article is viewed from its rear side, while having a visible light transmittance that can be obtained by conventional manufacturing methods and that can be flexibly controlled.

[0192] According to the invention, a main surface of the optical article, preferably the front surface, is covered by an asymmetric mirror according to the invention, which has a weighted spectral reflectance average, called forward reflectance Rf, over the entire visible spectrum from 380 to 780 nm for light arriving on the front main surface at an angle of incidence of less than 15°, which weighted spectral reflectance average is greater than 2.5%; - a weighted spectral reflectance average, referred to as the back reflectance Rf, over the entire visible spectrum from 380 to 780 nm, for light arriving on the rear main surface at an angle of incidence of less than 15°, which is less than 2.5%, preferably less than 2%, preferably less than 1.5%, preferably less than 1%, preferably less than 0.7%, preferably less than 0.6%, preferably less than 0.5%, preferably less than 0.4%, preferably less than 0.3%, preferably less than 0.2%, The ratio of the forward reflectance to the backward reflectance, Rf / Rb, at an angle of incidence of 15° is equal to or greater than 10, preferably greater than 20, preferably greater than 30.

[0193] From the wearer's point of view, it is important to reduce the reflection of light rays included in the range of incidence angles [30° to 45°], because light with such angles of incidence creates reflections from the back surface of the lens and discomfort.

[0194] The current absorptive interference coating can be directly used for sunglasses production on any kind of substrate without the need to tint the substrate or coating, thus simplifying the manufacturing process. In addition, the transmittance of the coated optical article can be flexibly controlled from Class 1 to Class 4.

[0195] The visible light absorption performance can be combined with other optical performance, such as high or low reflectance in the UV range, high or low reflectance in the visible range, multi-angle efficiency in reflection, e.g., low visual reflectance of visible light over a wide range of angles of incidence, by using an interference coating of the present invention on one major surface of a substrate, or the same or different interference coatings of the present invention on both surfaces of a substrate.

[0196] In each of these embodiments, the total number of layers in the interference coating, preferably the asymmetric antireflective coating, is preferably 3 or more, preferably 7 or less or 5 or less, and / or the total thickness of the interference coating (preferably the asymmetric mirror coating) is preferably less than 1 micrometer, more preferably 800 nm or less or 500 nm or less.

[0197] It is possible to design interference coatings without restrictions regarding their hue angle (h), which is related to the residual color displayed by the interference coating (color of reflected light) as described above, and is preferably in the range of 40° to 355°, more preferably 100° to 300°. In some embodiments, the optical article has a hue angle (h) in the range of 240° to 300°, preferably 250° to 290°, more preferably 260° to 280°, so that the perceived residual reflected color is blue to purple, preferably close to purple. In another embodiment, the optical article has a hue angle (h) of 135° or more, more preferably 140° or more, even more preferably in the range of 140° to 160°, thereby obtaining an interference coating with a green reflection. In another embodiment, the optical article has a hue angle (h) in the range of 40° to 90°, preferably 50° to 90°, even more preferably 50° to 70°, so that an interference coating with a gold reflection is obtained.

[0198] The color appearance coefficients of the lens of the present invention have good robustness. The robustness σh of the optical article as defined in WO 2015 / 000534 is satisfactory, and the hue angle h corresponding to green is preferably equal to or less than 8°, more preferably equal to or less than 7.5°.

[0199] The present invention further relates to a method for producing an optical article as previously described, comprising: - providing an optical lens comprising a substrate having a front major surface and a rear major surface; - depositing on at least one major surface of a substrate and on a multilayer interference coating defining an asymmetric mirror effect, the multilayer interference coating comprising a stack of at least one high refractive index layer having a refractive index above 1.55 and at least one low refractive index layer having a refractive index less than or equal to 1.55, at least one of the layers of the multilayer interference coating being a substoichiometric light-absorbing layer.

[0200] In one embodiment, the optical article is made by forming a primer coating and / or an abrasion-resistant and / or scratch-resistant coating on a substrate at a first manufacturing location, while forming other coatings at a second manufacturing location.

[0201] The following examples illustrate the invention in a more detailed but non-limiting manner. Unless otherwise specified, all thicknesses disclosed in this application refer to physical thickness. The percentages given in the tables are percentages by weight. Unless otherwise specified, the refractive indexes referred to in this invention are expressed at 20-25°C for a wavelength of 550 nm. EXAMPLES

[0202] 6. Basic Procedure The articles used in the examples were an impact-resistant primer coating as disclosed in the experimental section of WO 2010 / 109154, modified to have a refractive index of 1.6 by the addition of high refractive index colloids, an abrasion- and scratch-resistant coating (hard coat) as disclosed in Example 3 of EP 0 614 957, modified to have a refractive index of 1.6 instead of 1.5 by the addition of high refractive index colloids, an asymmetric mirror according to the invention on the front surface, and an anti-soiling coating as disclosed in the experimental section of WO 2010 / 109154, i.e. an anti-soiling coating by deposition under vacuum of Optool DSX compound sold by Daikin Industries (thickness: 2-5 nm), a polythiourethane MR8 lens substrate (Mitsui Toatsu Chemicals, Ltd.) with a diameter of 65 mm and a thickness of 1.2 mm, having a refractive power of -2.00 diopters when stated and no refractive power at all when not stated. Inc. (refractive index = 1.59). This article has the same stack on the concave or rear major surface, except that the absorbing antireflective coating or transparent antireflective coating is replaced by an asymmetric mirror.

[0203] Where specified, the various layers were deposited without heating the substrate, optionally by oxygen beam, possibly argon ion beam assisted vacuum deposition (IAD) (evaporation source: electron gun) during deposition, and, where indicated, under optional pressure regulation by (passive) supply of O2 gas or O2 / Ar, N2 / Ar gas mixtures into the chamber.

[0204] The vacuum deposition equipment making it possible to deposit the various anti-reflection layers comprises a vacuum coater Syrus 3 from Bulher Leybold Optics, which has two systems for evaporating the material: an electron gun evaporation system and a thermal evaporator (Joule effect evaporation system), as well as a Mark 2 ion gun from Veeco for use in the preliminary stage of preparation of the substrate surface by argon ion bombardment (IPC) and in the ion-assisted deposition (IAD) of the layers.

[0205] 2. Preparation of Optical Articles The lenses were placed on a carousel with a circular opening intended to receive the lens to be treated with its concave surface facing the deposition source and ion gun.

[0206] The method for producing the optical article involves introducing the lens substrate, including the primer and the abrasion-resistant coating, into a vacuum deposition chamber, followed by a pumping step until a high vacuum is created, followed by a conditioning step of the ion gun (IGC as disclosed in French patent no. 2 957 454, starting pressure 3.5×10 -5 mBar, 140V, 3.5A, Argon, 60 seconds) and start pressure 5.10 -4 The process involves a substrate surface activation step (IPC) using bombardment with an argon ion beam at 1.8 A, 100 V, 60 s at 100 mBar (ion gun set at 1.8 A, 100 V, 60 s), stopping the ion irradiation, followed by sequential deposition of the required number of layers (layers, coating layers, and antifouling coatings) at rates ranging from 0.4 to 3 nm / s, and finally a venting step.

[0207] Forming an asymmetric mirror according to the present invention includes, for example, the deposition of interference layers including a HI layer (ZrO2 at a rate of 2 nm / s, and a SnO2 layer at a rate of 1 nm / s, SiOx or SiN at a rate of 1-2 nm / s, and with gas flow ratios of O2 / Ar equal to 0.2, or N2 / Ar equal to 0.2, 0.1 and 0.05, respectively, as shown in Tables 1 and 2), a LI layer (SiO2 at a rate of 2 nm / s), and finally a deposition of an Optool DSX® layer at a rate of 0.4 nm / s until the required predetermined thickness / transmission coefficient of the layer is reached.

[0208] Forming an antireflection stack of the light-visible absorption type (AR1 or AR2) includes deposition steps of an antireflection layer, for example, including a HI layer (SiOx or SiN at a rate of 1-2 nm / s and with a gas flow ratio of O2 / Ar equal to 0.2, or N2 / Ar equal to 0.2, 0.15 and 0.05, respectively, as shown in Table 3), a LI layer (SiO2 at a rate of 2 nm / s), and finally a deposition step of an Optool DSX® layer at a rate of 0.4 nm / s until the required predetermined thickness / transmission coefficient of the layer is reached.

[0209] Forming a transparent type anti-reflection stack (conventional transparent AR) can be achieved by, for example, a deposition process of a SiO layer at a rate of 2 nm / s, 7.0×10 -5 The deposition of a ZrO2 layer at a rate of 1 nm / s under an O2 pressure of 100 mBar, followed by a surface activation step of this ZrO2 layer using an argon ion beam for 30 seconds (the same process as the IPC already performed directly on the substrate), optionally in an O2 atmosphere (5×10 -5 The process includes the deposition of a SiO2 sub-layer at a rate of 3 nm / s under a pressure of 1000 mBar, a surface activation step of the sub-layer using an Argon ion beam for 30 seconds (the same process as the IPC already performed directly on the substrate), the deposition of an anti-reflective layer comprising a HI layer (ZrO2 at a rate of 2 nm / s and a SnO2 layer at a rate of 1 nm / s) and a LI layer (SiO2 at a rate of 2 nm / s), and finally the deposition of an Optool DSXR layer at a rate of 0.4 nm / s.

[0210] The deposition of the ZrO layer was carried out under a gas supply (O, 7.5 × 10 -5 The deposition of a thin SnO2 conductive layer was carried out with oxygen ion assistance (ion gun: 2 A, 120 V).

[0211] 3. Examples of innovative asymmetric and comparison mirrors Table 1 below shows five examples of asymmetric mirror stacks consisting of interleaved SiO2 and absorbing SiNx layers with specific thicknesses and number of layers, as well as Comparative Examples 1 and 2 (Comparative Example 1 includes an additional SiN layer).

[0212] [Table 1]

[0213] Table 2 below shows two examples of asymmetric mirror stacks according to the invention, consisting of SiO2, ZrO2, and absorbing SiOx and Cr, and SiO2, ZrO2, and absorbing SiOx and Cr layers, respectively.

[0214] [Table 2]

[0215] In Tables 1 and 2, the light absorbing SiOx or SiNx layers were deposited with gas flow ratios of O2 / Ar equal to 0.2 and 0.15 or N2 / Ar equal to 0.2 and 0.15, respectively (as indicated in brackets in these tables).

[0216] 4. Examples of anti-reflective coatings Table 3 below shows three examples of antireflection stacks consisting of a conventional transparent AR with SiO2, ZrO2, SnO2, respectively, without a visible light absorbing layer, a two-layer visible light absorbing antireflection coating consisting of SiO2 and an absorbing SiOx layer, so-called AR1, and a two-layer visible light absorbing antireflection coating consisting of SiO2 and an absorbing SiNx layer, so-called AR2. Figure 9 shows the ultra-low Rf and Rb of AR2 (nearly 0% for angles of incidence between 0 and 30°, and below 2.5% for angles of incidence between 0 and 50°).

[0217] [Table 3]

[0218] In Table 3, the light absorbing SiOx or SiNx layers were deposited with gas flow ratios of O2 / Ar equal to 0.2 or N2 / Ar equal to 0.15, respectively.

[0219] 5. Test Method The following test procedures were used to evaluate the optical articles made according to the present invention: Multiple samples of each system were made for measurement, and the reported data was calculated using an average of the various samples.

[0220] Colorimetric measurements (in reflection) of surfaces coated with the laminates of the invention: the reflection coefficient Rv, the hue angle h, and the chroma C* in the international colorimetric CIE (L*, a*, b*) space were carried out with a Zeiss spectrometer, taking into account the standard illuminant D65 and the standard observer at 10° (for h and C*), and are given for an incidence angle of 15°.

[0221] The optical transmission coefficient Tv in the visible spectrum was measured in transmittance mode using a Cary 4000 spectrometer from Hunter, with the (concave) back surface of the lens (2 mm thick at the center) facing the detector and light incident on the front surface of the lens. Tv was measured under D65 lighting conditions (daylight).

[0222] The layer thickness was controlled by a quartz crystal microbalance.

[0223] For purposes of this disclosure, LI materials may be defined as materials having a refractive index less than 1.60, and sometimes less than 1.55, at a wavelength of 550 nm, and HI materials may be defined as materials having a refractive index greater than 1.60, and sometimes greater than 1.65, at 550 nm.

[0224] For all AR / mirror examples listed in Tables 1, 2, and 3, stoichiometric SiN, which has a refractive index of 1.915 at 550 nm, is an HI material, while sub-stoichiometric SiOx and SiNx are high refractive index materials. All sub-stoichiometric materials in the stack examples in Tables 1, 2, and 3 that have a refractive index greater than 2.0 at 550 nm are HI materials.

[0225] Stoichiometric SiO2, which has a refractive index of 1.462 at 550 nm, is a LI material.

[0226] 6. Optical Articles According to the Present Invention From the above defined asymmetric mirror and three anti-reflective coatings, examples 1 to 7, which are either transparent or visibly absorbing, several embodiments of optical articles according to the invention can be defined.

[0227] 7.Results 7.1 Results obtained for asymmetric mirrors according to the invention The front reflection coefficient Rf1 and the back reflection coefficient Rb2, as well as the reflection saturation c*, and the hue h*, and the transmission coefficient of the asymmetric mirror coatings of Examples 1 to 7, were fixed to predetermined values ​​to determine the behavior of the asymmetric mirror, when viewed from the front side of the asymmetric mirror coating described above, having different visible color regions such as blue, green, gold, etc., and having an imperceptible reflection when viewed from the front side.

[0228] As is evident from the different figures dedicated to the reflection spectra of the asymmetric mirror coating, the embodiment of the mirror according to the invention has the required anti-reflective behavior when viewed from the back side and highly reflective behavior when viewed from the front side. - Figure 3: Example 1: Very strong Rf (27-34%) for angles of incidence from 0 to 60°, very low Rb (less than 2.5% for angles of incidence from 0 to 60°, less than 1.5% for angles of incidence from 0 to 50°) - Figure 6: Example 3: Very strong Rf (10-18%) for angles of incidence from 0 to 60°, very low Rb (less than 2.5% for angles of incidence from 0 to 60°, less than 2% for angles of incidence from 0 to 50°) - Figure 7: Example 4: Very strong Rf (13-17%) for angles of incidence from 0 to 60°, very low Rb (less than 2.5% for angles of incidence from 0 to 50°, less than 2% for angles of incidence from 0 to 45°) - Figure 8: Example 5: Very strong Rf (11-25%) for angles of incidence from 0 to 60°, very low Rb (less than 2.5% for angles of incidence from 0 to 55°, less than 2% for angles of incidence from 0 to 50°) FIG. 12a: Example 6: Very strong Rf (15-40% for wavelengths included in the range 380-780 nm) for an angle of incidence of 15°, very low Rb for an angle of incidence of 15° FIG. 12b: Example 7: Very strong Rf (40-60% for wavelengths included in the range 380-780 nm) for an angle of incidence of 15°, very low Rb for an angle of incidence of 15°

[0229] In contrast, as is evident from FIGS. 2 and 4, which disclose the reflectances of Comparative Mirror Examples 1 and 2 above, the aforementioned Comparative Mirrors, even when including sub-stoichiometric absorbing layers, are not designed to exhibit an asymmetric mirror effect and have undesirably high back reflections (greater than 10% at all angles of incidence from 0 to 50% for Comparative Example 1, and greater than 5% at all angles of incidence from 0 to 50% for Comparative Example 2), exhibiting undesirably high reflectivity characteristics when viewed from the back surface.

[0230] 5.2 Results obtained for different embodiments of the optical article according to the invention In the above Examples 1-8, each was deposited on the front surface of an MR8® substrate, the opposite rear surface of which was coated with the transparent anti-reflective coating described above. The h*, c*, Rf at 15°, Rb at 0-50°, and Rf / Rb ratio at 15° were obtained below and are listed in Table 4 below.

[0231] [Table 4]

[0232] In the above Examples 1-8, each was deposited on the front surface of an MR8® substrate, the opposite rear surface of which was each coated with the above-mentioned absorbing anti-reflective coating AR1. Below, the h*, c*, Rf at 15°, Rb from 0 to 50°, and Rf / Rb ratio at 15° were obtained and are listed in Table 5 below.

[0233] [Table 5]

[0234] In the above Examples 1-8, each was deposited on the front surface of an MR8® substrate, the opposite rear surface of which was each coated with the above-mentioned absorbing anti-reflective coating AR2. Below, the h*, c*, Rf at 15°, Rb from 0 to 50°, and Rf / Rb ratio at 15° were obtained and are listed in Table 6 below.

[0235] [Table 6]

[0236] As is clear from the above Tables 4 to 6 and Figures 4, 5, 10, 11 and 21, for all of the optical articles so defined, very low Rb was obtained and high or very high Rf was obtained: - Figure 4: Several prototypes of the mirror coatings of Example 2 and Comparative Example 2 were made on MR8 / HC1.6 substrates. The convex surface of the lens is coated with the corresponding mirror coating, and the concave surface of the lens is coated with a conventional transparent AR coating (or any other conventional AR, e.g. SiN / SiO2, etc.) by electron beam evaporation. To characterize the inherent asymmetric reflection features, the mirror coatings were applied on a planar MR8 substrate and SMR measurements were made from both the Cx and Cc surfaces. In fact, the measured reflection is the sum of the reflections from both surfaces, as shown diagrammatically in Figure 1. Figure 4 shows the SMR reflection spectra measured at 15° on the Cx and Cc surfaces of a planar MR8 prototype with the mirror coatings of Example 2 and Comparative Example 2. It is noted that the forward reflection Rf from the Cx surface of both mirror coating samples is very strong. The back reflection Rb from the Cc surface of the comparative (conventional) mirror coating is very high, whereas the reflection from the Cc surface of the (asymmetric) mirror coating of Example 2 is very low (0.77% at 15° and less than 2% from 0° to 50° according to Table 4). - Figure 5 shows the Rf, Rb measured at different angles of incidence on the Cx and Cc surfaces of mirror coating prototypes Example 2 and Comparative Example 2 deposited on the front or Cx surface of a planar MR8®, while the Cc or back side is coated with a transparent AR coating. It should be noted that the front Rf values ​​(measured from the Cx or front surface) of both mirror coating samples are very high (more than 30%) at different angles of incidence. The rear Rb (measured from the rear Cc surface) of the comparative (conventional) mirror coating varies from 4 to 11.5% at angles of incidence from 0° to 60°. The rear Rb of the (asymmetric) mirror coating of Example 2, on the other hand, is very low (less than 1.5% at angles of incidence from 0° to 45°). The significantly lower rear Rb of the asymmetric mirror coating is promising for reducing annoying rear reflections and ghost images, especially when the mirror coating is applied on prescription lenses, compared to the conventional mirror coating. Indeed, from two photographs taken of two prototypes of the same non-planar MR8® substrate having a spherical refractive power of −2.00D coated with the absorbing mirror coating of Comparative Example 2 and the asymmetric mirror coating of Example 2, respectively, it can be seen that while a strong ghost image can be observed through the conventional mirror coating, the ghost image is significantly reduced or even canceled through the asymmetric mirror coating. - Figure 10 shows Rf, Rb measured at different angles of incidence on the Cx and Cc surfaces of the mirror coating of Example 5, where a silver reflective color is deposited on the front or Cx surface of a flat MR8®, while the Cc or back side is coated with an absorbing AR2 coating. This stack is composed of only four layers, namely two absorbing layers and two transparent layers. The theoretical front and rear Rv of this mirror stack are shown in Figure 8. As with the other asymmetric mirror coatings of Examples 1 to 4 described above according to the invention, the front reflection of this optical article is high, while the rear reflection is very low. - Figure 11 shows the even lower Rb (less than 1%) from 0 to 50° obtained when combining an asymmetric mirror with an absorbing anti-reflection coating. More precisely, the convex surface of lens α is coated with the asymmetric mirror coating of example 2, and the concave surface of this lens is coated with a conventional transparent AR. For lens β, the convex surface is coated with the asymmetric mirror coating of example 5, while its concave surface is coated with an absorbing AR2 coating as shown in Figure 9. The transmission TvD65 of these two prototypes is similar (10-12%). The back Rb of both prototypes is very low, but lens β has an even lower back Rb than lens α. This result can be interpreted because the sub-reflection from the Cx surface of lens β (i.e. Rb2 in Figure 1) is partially absorbed by the absorbing AR2 on the concave surface. Thus, the measured total back reflection Rb of lens β is mainly contributed by the sub-reflection from the AR coating on the Cc surface (i.e. RB1, which is very low). Both of these prototypes on the -2.00D MR8 substrate show no obvious ghost images. - Figure 21 shows the low (less than 1.5%) Rb between 0 and 45° obtained when an asymmetric mirror of the type of example 8 is combined with an absorbing anti-reflection coating AR2. As with the other above-mentioned examples of asymmetric mirror coatings according to the invention, the forward reflection of this optical article is high (almost 15%), while the back reflection is very low. This asymmetric mirror according to example 8 has a higher transmission than the other examples (TV 60% at 15°) and, when combined with a transparent substrate and an AR coating, makes it possible to obtain an optical article of class 1 (TV=64% at 15°).

[0237] The optical articles obtained according to the different illustrated embodiments of the invention exhibit several interesting optical properties: - a forward reflectance Rf at an angle of incidence less than 15°: greater than 2.5% (all examples), greater than 10% (all examples), greater than 20% (all examples except examples 3 to 5, whatever the anti-reflection coating used), greater than 30% (examples 2 and 7, whatever the anti-reflection coating used); a back reflectivity Rb at angles of incidence less than 15° of less than 2.5% (all examples whatever the anti-reflection coating used), less than 2% (all examples whatever the anti-reflection coating used), preferably less than 1.5% (all examples whatever the anti-reflection coating used), preferably less than 1% (all examples whatever the anti-reflection coating used, except example 1 in combination with a transparent AR coating), preferably less than 0.7% (all examples with AR2, examples 2 to 7 with AR1, examples 3, 6 and 7 with transparent AR), preferably less than 0.6% (all examples with AR2, examples 2 to 7 with AR1), preferably less than 0.5% (all examples with AR2, examples 2 to 7 with AR1), preferably less than 0.4% (all examples with AR2), preferably less than 0.3% (examples 2 to 7 with AR2), preferably less than 0.2% (examples 3 and 7 with AR2); the ratio of the forward reflectance to the backward reflectance at an angle of incidence of 15°, designated Rf / Rb, is greater than or equal to 10 (all examples whatever the antireflection coating used), preferably greater than 20 (examples 1 to 3, 6 and 7 with transparent AR, all examples with AR1 or AR2), preferably greater than 30 (examples 2, 7 with transparent AR, all examples with AR1 or AR2); the back reflectivity Rb at angles of incidence between 35° and 45° is less than 2.5% (all examples whatever the anti-reflection coating used), preferably less than 2% (all examples 1-6 with transparent AR, all examples 2-5 with AR1, all examples with AR2), preferably less than 1.5% (all examples 2-5 with transparent AR, all examples with AR2), preferably less than 1.4% (examples 2-3 with transparent AR, examples 1-5 with AR2), preferably less than 1.3% (examples 2-5 with AR2); the back reflectivity Rb at angles of incidence between 0° and 45° is less than 2.5% (all examples whatever the anti-reflection coating used), preferably less than 2.3% (all examples whatever the anti-reflection coating used), preferably less than 2.2% (all examples whatever the anti-reflection coating used, except for example 7 / AR1), preferably less than 2.1% (all examples whatever the anti-reflection coating used, except for examples 6 and 7 / AR1); The back reflectance Rb at an incidence angle of -35° to 50° is 2.5% (Examples 1 to 5 with transparent AR, all Examples with AR2), preferably less than 2.3% (Examples 1 to 5 with transparent AR, all Examples with AR2), preferably less than 2.2% (all Examples 1 to 6 with AR2), preferably less than 2.1% (all Examples 1 to 5 with AR2).

[0238] The structure of the asymmetric mirror according to the invention can be defined by at least one of the following considerations, taken alone or in any combination thereof: for asymmetric mirrors having at least two absorbing layers (both substoichiometric or one substoichiometric and one metallic), the thickness of at least one of these absorbing layers is less than 20, preferably less than 15 nm, more preferably less than 10 nm, and the thickness of the second absorbing layer is between 60 and 130 nm, preferably between 80 and 120 nm, more preferably between 90 and 120 nm; for an asymmetric mirror having three absorbing layers, the thickness of the third absorbing layer is between 5 and 120 nm, more preferably between 7 and 80 nm; for an asymmetric mirror having three absorbing substoichiometric layers, the thickness of at least one of these layers is less than 20, preferably less than 15 nm, more preferably less than 10 nm; for an asymmetric mirror having at least one absorbing sub-stoichiometric layer and at least one metal layer, the thickness of one of said at least one absorbing sub-stoichiometric layer is greater than 20 nm, preferably greater than 40 nm, preferably greater than 60 nm, preferably greater than 80 nm, and the thickness of one of said metal layers is less than 20, preferably less than 15 nm, more preferably less than 10 nm and preferably greater than 5 nm; - the first layer closest to the substrate is preferably the HI layer; - if both of the two absorbing layers are substoichiometric layers, the first layer closest to the substrate is preferably the substoichiometric layer; - if the two absorbing layers are one absorbing substoichiometric layer and one metal layer, the first layer closest to the substrate is preferably neither a metal layer nor a substoichiometric layer, but an HI layer, e.g. ZrO2; - the last layer, furthest from the substrate, is either a LI layer, such as SiO2, or a HI layer; The asymmetric mirror stack comprises at least 4 layers, preferably less than 10 layers, more preferably less than 8 layers, or exactly 8 layers, which participate in the asymmetric mirror effect.

[0239] As mentioned above, in the present invention, an asymmetric absorbing mirror coating is developed. Compared with the comparative mirror coating designed with sub-stoichiometric layers but without considering back reflection, the asymmetric mirror coating can effectively reduce the visibility of back reflection and ghost image. When the asymmetric mirror coating on the convex surface is combined with the absorbing AR coating on the concave surface, the visibility of back reflection and ghost image can be further minimized.

[0240] As mentioned above, the transmittance of the coated article can be flexibly controlled from Class 1 to Class 4 according to the European standard NF EN 1836+A1, so that the transmittance can be flexibly controlled from Class 1 to Class 4 by the thickness and / or composition of the light absorbing layer, and furthermore, an asymmetric mirror effect can be used for sunglasses applications.

[0241] Several stacks were designed using 1 to 3 absorbing layers with visible transmission (Tv) ranging from 3 to 60%. As mentioned above, the transmission can be controlled from class 1 to class 4 by the thickness and / or composition of the light absorbing layer of the anti-reflection absorbing coating, if present, and / or by virtue of the presence of an asymmetric mirror.

[0242] Although representative optical articles, sunglasses, and methods of manufacture have been described in detail herein, those skilled in the art will recognize that various substitutions and modifications may be made without departing from the scope of what is described and defined by the appended claims.

[0243] It is obviously possible to combine several of the tailored coatings with asymmetric mirror effect and anti-reflection effect as described above on both main surfaces of the lens in order to obtain a cumulative advantage depending on the required specifications.

Claims

1. 1. An optical article having a base material defining a front major surface and a back major surface, at least one major surface being coated with an interference multilayer coating comprising a stack of at least one high refractive index layer having a refractive index greater than 1.55 and at least one low refractive index layer having a refractive index less than or equal to 1.55, said refractive index expressed for a wavelength of 550 nm, defining highly reflective properties when the article is viewed from the front side and anti-reflective properties when the article is viewed from the back side, the optical article being referred to as an asymmetric mirror, and at least one of said layers of the asymmetric mirror being a visible light absorbing sub-stoichiometric inorganic material.

2. 10. The optical article of claim 1, wherein the light absorbing sub-stoichiometric inorganic material comprises a sub-stoichiometric dielectric oxide or nitride material having an extinction coefficient of 0.1 or greater.

3. 3. The optical article of claim 2, wherein the light absorbing sub-stoichiometric inorganic material has a thickness of less than 200 nm, preferably less than 150 nm.

4. 4. The optical article according to claim 3, wherein the at least one sub-stoichiometric inorganic material has a thickness of less than 30 nm, preferably less than 20 nm, preferably less than 15 nm, more preferably less than 10 nm and more than 4 nm.

5. 5. The optical article of claim 4, wherein the near-stoichiometric inorganic material comprises SiNx, where x is a predetermined number less than 1, or SiOx, where x is a predetermined number less than 2, or SiNxOy, where x and y are predetermined numbers, e.g., x<1-y / 2 and y<2(1-x).

6. 6. The optical article according to any one of claims 1 to 5, wherein at least one of the visible light absorbing layers of the asymmetric mirror is a metal layer having a thickness less than 20 nm, preferably less than 15 nm, more preferably less than 10 nm and more than 4 nm.

7. 7. The optical article of claim 6, wherein the metal layer is sandwiched between two low refractive index layers, or between two high refractive index layers, or between one low refractive index layer and one high refractive index layer of the interference coating.

8. 8. The optical article of claim 7, wherein the metal layer comprises a metal species that is at least one of Al, Cr, Ta, Nb, Ti, and Zr.

9. 6. The optical article of any one of claims 1 to 5, wherein the front major surface is coated with the asymmetric mirror and the rear major surface is coated with an interference multilayer coating having anti-reflective properties when the article is viewed from the rear side.

10. 10. The optical article of claim 9, wherein the interference multilayer coating having anti-reflective properties when the article is viewed from the back surface is an anti-reflective coating.

11. 11. The optical article of claim 10, wherein the antireflective coating comprises at least one layer of a light absorbing material, the light absorbing material comprising a sub-stoichiometric inorganic material, preferably a sub-stoichiometric dielectric oxide or nitride material, preferably comprising SiNx, where x is a predetermined number less than 1, or SiOx, where x is a predetermined number less than 2, or SiNxOy, where x and y are predetermined numbers, e.g. x<1-y / 2 and y<2(1-x).

12. a weighted spectral reflectance average, referred to as the forward reflectance Rf, over the entire visible spectrum from 380 to 780 nm for light arriving on said front principal surface at an angle of incidence of less than 15°, the weighted spectral reflectance average being greater than 2.5%; a weighted spectral reflectance average, referred to as back reflectance Rb, over the entire visible spectrum from 380 to 780 nm, for light arriving on said rear major surface at an angle of incidence of less than 15°, which is less than 2.5%, preferably less than 2%, preferably less than 1.5%, preferably less than 1%, preferably less than 0.7%, preferably less than 0.6%, preferably less than 0.5%, preferably less than 0.4%, preferably less than 0.3%, preferably less than 0.2%, 6. Optical article according to any one of claims 1 to 5, wherein the ratio of the front reflectivity to the back reflectivity, Rf / Rb, at an angle of incidence of -15° is equal to or greater than 10, preferably greater than 20, preferably greater than 30.

13. 13. The optical article of claim 12, wherein the back reflectivity Rb at angles of incidence between 35° and 45° is less than 2.5%, preferably less than 2%, preferably less than 1.5%, preferably less than 1.4%, preferably less than 1.3%.

14. 13. The optical article of claim 12, wherein the back reflectivity Rb at angles of incidence between 0° and 45° is less than 2.5%, preferably less than 2.3%, preferably less than 2.2%, preferably less than 2.1%.

15. 13. The optical article of claim 12, wherein the back reflectivity Rb at angles of incidence between 35° and 50° is less than 2.5%, preferably less than 2.3%, preferably less than 2.2%, preferably less than 2.1%.