Solvent management with two-phase ethylene feed to the second reactor to increase ethylene-based polymer production

Abstract

Ethylene monomer, optionally hydrogen, optionally C3-C 12 introducing a first feed comprising an alpha-olefin comonomer and a hydrocarbon solvent into a first polymerization reactor to produce a first reactor product comprising an ethylene-based polymer by solution polymerization at a temperature of 100 to 225°C; and reacting the first reactor product with ethylene monomer, the hydrocarbon solvent, optionally hydrogen, and optionally a C3 to C6 12 and introducing a two-phase second feed comprising an alpha-olefin comonomer into a second polymerization reactor to produce an ethylene-based polymer by solution polymerization, wherein the weight ratio of the sum of the hydrocarbon solvent plus the comonomer to the ethylene monomer in the two-phase second feed is from 0.1 to 2.0.

Description

[Technical Field]

[0001] (CROSS-REFERENCE TO RELATED APPLICATIONS) This application claims priority to U.S. Provisional Patent Application No. 63 / 404,744, filed September 8, 2022, which is incorporated herein by reference in its entirety.

[0002] FIELD OF THE INVENTION This specification relates generally to ethylene-based polymers, and more particularly to an improved polymerization process involving two-phase ethylene feed. [Background technology]

[0003] Solution polymerization processes for producing ethylene-based polymers (e.g., LLDPE) utilize a hydrocarbon solvent in their reactor to carry out a single liquid-phase polymerization reaction. The solvent serves multiple functions: dissolving the polymer and ethylene gas and providing a single liquid-phase environment for the polymerization reaction, while also removing a portion of the heat of reaction. Because plant throughput is limited by the total solvent devolatilization capacity of the back-end equipment, the polymer concentration exiting the reactor section, or, in other words, the amount of solvent used to produce each product, determines the maximum total polymer production rate. Therefore, any process improvement that results in a reduction in solvent usage will help increase overall plant capacity.

[0004] Traditionally, ethylene monomer is dissolved in a solvent and comonomer and fed as a single liquid phase feed stream to ensure consistent reactor feed, but single liquid phase feeds imply that large amounts of solvent are required to completely dissolve the fresh ethylene, thereby limiting reactor polymer concentration and thereby plant capacity.

[0005] Thus, there is a continuing need for improved polymerization processes that can increase the production of ethylene-based polymers. Summary of the Invention

[0006] Embodiments of the present disclosure fulfill this need for improved production of ethylene-based polymers by applying a two-phase ethylene in a solvent feed stream to feed the second reactor. Without being bound by theory, this two-phase feed injection technique increases the overall polymer concentration, reduces the overall solvent charge, and subsequently helps increase the production rate of existing dual reactor polymerization systems.

[0007] According to one embodiment, a series dual reactor solution polymerization process is provided. The dual reactor solution polymerization process comprises a series dual reactor solution polymerization process comprising a step of polymerizing ethylene monomer, optionally one or more C3-C6 monomers, 12 introducing a first feed comprising an alpha-olefin comonomer, optionally hydrogen, and a hydrocarbon solvent into a first polymerization reactor to produce a first reactor product comprising an ethylene-based polymer by solution polymerization at a temperature of 100 to 225°C; and reacting the first reactor product with a first feed comprising an alpha-olefin comonomer, optionally hydrogen, and a hydrocarbon solvent to produce a first reactor product comprising an ethylene-based polymer; 12 introducing an alpha-olefin comonomer, and optionally a two-phase second feed comprising hydrogen, into a second polymerization reactor to produce an ethylene-based polymer by solution polymerization, wherein the weight ratio of the total of the hydrocarbon solvent and the comonomer to the ethylene monomer in the two-phase second feed is from 0.1 to 2.2.

[0008] Additional features and advantages are set forth in the following Detailed Description, and in part will be readily apparent to those skilled in the art from that description or will be recognized by practicing the embodiments described herein, including the drawings, the following Detailed Description, and the claims. [Brief explanation of the drawings]

[0009] [Figure 1] FIG. 1 is a schematic diagram of the present dual reactor series polymerization process, according to one or more embodiments of the present disclosure. DETAILED DESCRIPTION OF THE INVENTION

[0010] Specific embodiments of the present application will now be described. However, this disclosure may be embodied in different forms and should not be construed as limited to the embodiments set forth in this disclosure. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the present subject matter to those skilled in the art.

[0011] definition The term "polymer" refers to a polymeric compound prepared by polymerizing monomers, whether of the same or different types. Thus, the generic term polymer encompasses the term "homopolymer," which is typically used to refer to a polymer prepared from only one type of monomer, as well as "copolymer," which refers to a polymer prepared from two or more different monomers. As used herein, the term "interpolymer" refers to a polymer prepared by polymerization of at least two different types of monomers. Thus, the generic term "interpolymer" includes copolymers and polymers, such as terpolymers, prepared from three or more different types of monomers.

[0012] "Polyethylene" or "ethylene-based polymer" means a polymer containing greater than 50% by weight of units derived from ethylene monomers. This includes polyethylene homopolymers or copolymers (meaning units derived from ethylene and two or more comonomers). The comonomers may include olefinic comonomers as well as polar comonomers. Common forms of polyethylene known in the art include low density polyethylene (LDPE), linear low density polyethylene (LLDPE), ultra low density polyethylene (ULDPE), very low density polyethylene (VLDPE), single-site catalyzed linear low density polyethylene (m-LLDPE), including both linear and substantially linear low density resins, medium density polyethylene (MDPE), and high density polyethylene (HDPE).

[0013] The term "LLDPE" includes resins made using Ziegler-Natta catalyst systems, as well as resins made using single-site catalysts, including, but not limited to, bis-metallocene catalysts (sometimes referred to as "m-LLDPE") and constrained geometry catalysts, and resins made using post-metallocene, molecular catalysts. LLDPE includes linear, substantially linear, or heterogeneous polyethylene copolymers or homopolymers. LLDPE contains less long chain branching than LDPE and includes substantially linear ethylene polymers as further defined in U.S. Pat. Nos. 5,272,236, 5,278,272, 5,582,923, and 5,733,155; homogeneously branched linear ethylene polymer compositions such as those in U.S. Pat. No. 3,645,992; heterogeneously branched ethylene polymers such as those prepared according to the process disclosed in U.S. Pat. No. 4,076,698; and / or blends thereof (such as those disclosed in U.S. Pat. No. 3,914,342 or 5,854,045).

[0014] The terms "comprising," "including," "having," and their derivatives are not intended to exclude the presence of any additional component, step, or procedure, whether or not it is specifically disclosed. For the avoidance of doubt, all compositions claimed through the use of the term "comprising" may include any additional additive, adjuvant, or compound, whether polymeric or not, unless stated to the contrary. In contrast, the term "consisting essentially of" excludes from the scope of any succeeding description any other component, step, or procedure, excepting those that are not essential to operability. The term "consisting of" excludes any component, step, or procedure not specifically delineated or listed.

[0015] Embodiments of the present disclosure are directed to a dual reactor solution polymerization system 5 and method as shown in Figure 1. The method comprises the steps of: 12 The method includes introducing a first feed 10 comprising an alpha-olefin comonomer, optionally hydrogen, and a hydrocarbon solvent into a first polymerization reactor 40 to produce a first reactor product 47 comprising an ethylene-based polymer by solution polymerization at a temperature of 100-225° C. In further embodiments, the temperature may be 100-205° C., 120-180° C., or 150-180° C. Subsequently, the first reactor product 47 is mixed with the ethylene monomer, the hydrocarbon solvent, optionally hydrogen, and optionally one or more C3-C6 olefins. 12 A two-phase second feed 48 containing an alpha-olefin comonomer is fed to a second polymerization reactor 50 to produce an ethylene-based polymer 65 by solution polymerization.

[0016] The two-phase second reactor feed 48, comprising a gas phase and a liquid phase, has a weight ratio of the sum of hydrocarbon solvent and comonomer to ethylene monomer of 0.1 to 2.2, 0.6 to 1.6, 0.8 to 1.2, or 1.0 to 1.2. Without being bound by theory, a weight ratio greater than 2.2 may result in a single liquid phase feed, which results in significantly lower reactor polymer concentrations. In embodiments, the two-phase second feed comprises 7 to 100 volume percent gas phase, or 7 to 60 volume percent gas phase. In one or more embodiments, the two-phase second reactor feed may be introduced into the reactor at a temperature of 10 to 100°C, 15 to 80°C, 15 to 60°C, 20 to 80°C, or 20 to 60°C. Without being bound by theory, it is believed that the ratio of the total hydrocarbon solvent and comonomer to the ethylene monomer can increase the saturation temperature, and therefore, a two-phase second reactor feed having a higher ratio (i.e., closer to 2) can correlate to a higher temperature, such as 50-100° C. Furthermore, without being limited by theory, a two-phase second reactor feed having a temperature of 100° C. or less allows for operation with less gelling within the reactor.

[0017] A variety of reactors are contemplated as suitable for the polymerization system 5. In one embodiment, the first polymerization reactor 40, the second polymerization reactor 50, or both, comprise a loop reactor. Alternatively, the first polymerization reactor 40, the second polymerization reactor 50, or both, comprise a continuously stirred tank reactor.

[0018] 1, first feed 10 may be a single-phase liquid feed. In one or more embodiments, the weight ratio of the total hydrocarbon solvent and comonomer to ethylene monomer in first feed 10 is greater than 2.2 to 10, 4 to 8, or 4 to 6.

[0019] A variety of hydrocarbon solvents are contemplated as suitable for use in system 5. In one or more embodiments, the hydrocarbon solvent comprises an aromatic hydrocarbon solvent, an aliphatic hydrocarbon solvent, or a mixture thereof.

[0020] Additionally, various catalysts are contemplated as suitable for use in the first polymerization reactor 40 and the second polymerization reactor 50. These may include Ziegler-Natta catalyst systems, single-site catalysts, and multi-site catalysts, such as, but not limited to, bis-metallocene catalysts, constrained geometry catalysts, post-metallocene catalysts, molecular catalysts, bis-phenyl-phenoxy catalysts, and heterogeneous Ziegler-Natta catalysts. In embodiments, the first polymerization reactor 40 may utilize a bis-phenyl-phenoxy catalyst. In other embodiments, the second polymerization reactor 50 may utilize a heterogeneous Ziegler-Natta catalyst.

[0021] In further embodiments, the polymerization system may include additional polymerization reactors downstream of the first polymerization reactor 40 and the second polymerization reactor 50. These reactors may be loop reactors, continuous stirred tank reactors, pipe flow reactors, plug flow reactors, tubular reactors, or combinations thereof.

[0022] Test Method density Samples for density measurements are prepared according to ASTM D1928. Polymer samples are pressed at 190°C and 30,000 psi for 3 minutes, then 21°C and 207 MPa for 1 minute. Measurements are made within 1 hour of pressing the sample using ASTM D792, Method B.

[0023] Melt Index (I2) Melt index, or I2, (grams / 10 minutes or dg / min) is measured according to ASTM D 1238, Condition 190°C / 2.16 kg, Procedure B. [Example]

[0024] The embodiments will be further clarified by the following examples.

[0025] Six samples were prepared: Comparative Example A, which included a single liquid phase feed to the second reactor, and Inventive Examples 1-4, which included a two-phase vapor-liquid feed to the second reactor.

[0026] Comparative Example A and Inventive Examples 1-4 were prepared by solution polymerization in a dual series loop reactor system according to U.S. Patent No. 5,977,251 in the presence of a first catalyst system (Catalyst 1) as set forth in Table 1 below in the first reactor and a second catalyst system (Catalyst 2) as set forth in Table 1 below in the second reactor. Inventive Example 4 was similarly prepared by solution polymerization in a dual series loop reactor system according to U.S. Patent No. 5,977,251 in the presence of a first catalyst system (Catalyst 3) as set forth in Table 1 below in the first reactor and a second catalyst system (Catalyst 4) as set forth in Table 1 below in the second reactor.

[0027] [Table 1]

[0028] In Comparative Example A (left column of Table 2), a second reactor solvent plus comonomer to ethylene ratio of 2.4 was applied to maintain a single liquid phase feed at a feed temperature of 40°C.

[0029] [Table 2]

[0030] In contrast, Inventive Example 1 applied a lower second reactor solvent plus comonomer to ethylene ratio of 1.23, which put the second reactor feed into the two-phase vapor-liquid regime. This resulted in a 9.5% production rate increase compared to the design capacity of Comparative Example A, whereas Comparative Example A did not. Meanwhile, the total solvent amount required for the two-phase feed recipe remained within the maximum total solvent processing constraint. Inventive Examples 2-4, which also had second reactor solvent to ethylene ratios of 2.2 or less, also showed improved production rates compared to the design capacity of Comparative Example A.

[0031] It will be apparent to those skilled in the art that various modifications and variations can be made to the embodiments described herein without departing from the spirit and scope of the claimed subject matter. Accordingly, this specification is intended to cover all such modifications and variations of the various embodiments described herein, provided they come within the scope of the appended claims and their equivalents.

Claims

1. 1. A dual reactor solution polymerization process comprising: Ethylene monomer, optionally one or more C ３ ~C １２ introducing a first feed comprising an alpha-olefin comonomer, optionally hydrogen, and a hydrocarbon solvent into a first polymerization reactor to produce a first reactor product comprising an ethylene-based polymer by solution polymerization at a temperature from 100 to 225°C; the first reactor product and a mixture of ethylene monomer, a hydrocarbon solvent, optionally hydrogen, and optionally one or more C ３ ~C １２ and introducing into a second polymerization reactor a two-phase second feed comprising an alpha-olefin comonomer to produce an ethylene-based polymer by solution polymerization, wherein a weight ratio of the sum of the hydrocarbon solvent and the comonomer to ethylene monomer in the two-phase second feed is from 0.1 to 2.

2.

2. 10. The process of claim 1, wherein the weight ratio of the total of the hydrocarbon solvent and the comonomer to the ethylene monomer in the two-phase second feed is from 0.6 to 1.

6.

3. The method of claim 1 , wherein the two-phase second feed comprises a liquid phase and a vapor phase.

4. 3. The method of claim 2, wherein the two-phase second feed comprises 7 to 98 volume percent of the gas phase.

5. The two-phase second feed is C ３ ~C １２ The process of any one of claims 1 to 4, comprising an alpha-olefin comonomer.

6. The method of any one of claims 1 to 5, wherein the first polymerization reactor, the second polymerization reactor, or both comprise a loop reactor.

7. The method of any one of claims 1 to 6, wherein the first feed is a single-phase liquid feed.

8. 8. The process of any one of claims 1 to 7, wherein the weight ratio of the sum of the hydrocarbon solvent and the comonomer to ethylene monomer in the first feed is greater than 2.2 to 10.

9. The method of any one of claims 1 to 8, wherein the hydrocarbon solvent comprises an aromatic hydrocarbon solvent, an aliphatic hydrocarbon solvent, or a mixture thereof.

10. An ethylene-based polymer produced from the process of any one of claims 1 to 9.

Images