Battery and manufacturing method thereof

A layered separator with larger and smaller inorganic particles addresses voids and contact issues in electrodes with through holes, improving ion permeability and reducing resistance in batteries.

JP7601018B2Active Publication Date: 2024-12-17TOYOTA JIDOSHA KK
View PDF 5 Cites 0 Cited by

Patent Information

Application Number
JP2022011523
Authority / Receiving Office
JP · JP
Patent Type
Patents
Current Assignee / Owner
Filing Date
2022-01-28
Publication Date
2024-12-17
Estimated Expiration
2042-01-28

AI Technical Summary

Technical Problem

Existing separators for electrodes with through holes, such as those with honeycomb structures, face challenges in preventing contact and void formation, leading to potential short circuits and increased battery resistance.

Method used

A layered separator structure is employed, with a first layer of larger inorganic particles covering the inner wall of the through holes, followed by a second layer of smaller particles to fill voids and maintain ion permeability, reducing voids and battery resistance.

Benefits of technology

The layered separator effectively minimizes voids and short circuits, enhancing ion permeability and reducing battery resistance while maintaining high reaction area and energy density.

✦ Generated by Eureka AI based on patent content.

Smart Images

  • Figure 0007601018000003
    Figure 0007601018000003
  • Figure 0007601018000004
    Figure 0007601018000004
  • Figure 0007601018000005
    Figure 0007601018000005
Patent Text Reader

Abstract

To reduce voids, in a coating type separator formed on an inner wall of through-holes.SOLUTION: A battery includes a first electrode, a second electrode, and a separator. The first electrode includes a first principal surface and a second principal surface. The first electrode has a plurality of through-holes. The through-holes penetrate through the first electrode from the first principal surface to the second principal surface. The separator covers an inner wall of the through-holes. The second electrode is arranged in the through-holes. The separator includes a first layer and a second layer. The first layer is arranged between the inner wall and the second layer. The first layer includes a first inorganic particle group having a first average particle diameter. The second layer includes a second inorganic particle group having a second average particle diameter. The second average particle diameter is smaller than the first average particle diameter.SELECTED DRAWING: Figure 6
Need to check novelty before this filing date? Find Prior Art

Description

[Technical field]

[0001] The present disclosure relates to batteries and methods for making the same. [Background technology]

[0002] JP 2020-123484 A (Patent Document 1) discloses an electrode having a plurality of through holes and a separator layer laminated on the inner walls of the through holes. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2020-123484 A Summary of the Invention [Problem to be solved by the invention]

[0004] The battery includes a first electrode and a second electrode. The second electrode has a polarity different from that of the first electrode. To prevent contact between the first electrode and the second electrode, a separator is disposed between the first electrode and the second electrode. The separator is electrically insulating. The separator is porous and ion-permeable. The electrodes are generally in sheet form. A film-shaped separator is used to correspond to the sheet-shaped electrodes. For example, microporous films made of polyolefin are widely used as separators.

[0005] Electrodes with special structures are also being considered. For example, a through hole is formed in the first electrode. The inner wall of the through hole is covered with a separator. A second electrode is placed in the through hole whose inner wall is covered with the separator. Because the electrodes are not sheet-shaped, it is difficult to avoid contact between the first electrode and the second electrode due to the film-shaped separator.

[0006] Therefore, for example, the use of a coating type separator is considered. That is, a coating type separator can be formed by coating an inner wall of a through hole with a group of inorganic particles. However, according to the new findings of the present disclosure, voids (air bubbles) tend to remain in the coating type separator formed on the inner wall of the through hole. At the position where the void exists, the dielectric strength may be locally reduced. For example, a short circuit path may be formed by a part of an electrode penetrating into the void. For example, a pinhole may be formed by the void.

[0007] An object of the present disclosure is to reduce voids in a coating-type separator formed on the inner wall of a through-hole. [Means for solving the problem]

[0008] The technical configuration and effects of the present disclosure will be described below. However, the mechanism of action in this specification includes assumptions. The mechanism of action does not limit the technical scope of the present disclosure.

[0009] 1. The battery includes a first electrode, a second electrode, and a separator. The first electrode includes a first main surface and a second main surface. The second main surface is opposite to the first main surface. A plurality of through holes are formed in the first electrode. The through holes penetrate the first electrode from the first main surface to the second main surface. The separator covers the inner wall of the through hole. The second electrode has a polarity different from that of the first electrode. The second electrode is disposed in the through hole. The second electrode extends along the axial direction of the through hole. The separator includes a first layer having a first thickness and a second layer having a second thickness. The first layer is disposed between the inner wall and the second layer. The first layer includes a first group of inorganic particles having a first average particle size. The second layer includes a second group of inorganic particles having a second average particle size. The second average particle size is smaller than the first average particle size.

[0010] In coated separators, the smaller the particle size of the inorganic particles, the smaller the void size tends to be. Therefore, by using inorganic particles with a small particle size, it is expected that the voids will be reduced. However, the smaller the particle size of the inorganic particles, the denser the coated separator becomes, and the lower the ion permeability may be. In other words, the battery resistance may increase.

[0011] In the battery of "1." above, the separator includes a first layer and a second layer. The first layer (lower layer) is closer to the inner wall than the second layer (upper layer). The first layer is formed of a first group of inorganic particles (large particle group). The second layer is formed of a second group of inorganic particles (small particle group). When the second layer is formed, some of the small particle group may fill the voids in the first layer. In other words, it is considered that the voids may be reduced. Furthermore, since the first layer is formed of the large particle group, the separator may be appropriately sparse. Therefore, an increase in battery resistance may be reduced.

[0012] 2. The first electrode may, for example, form a honeycomb core.

[0013] That is, the through holes may be arranged in a honeycomb pattern in a cross section perpendicular to the axial direction of the first electrode. As an electrode with a special structure, an electrode with a honeycomb structure is promising. By having an electrode with a honeycomb structure, it is expected that the reaction area and the active material density will be increased. In other words, it is expected that both input / output characteristics and energy density will be achieved.

[0014] When the first electrode has a honeycomb structure, it is considered difficult to apply a separator other than a coated separator. When the first electrode has a honeycomb structure, it is considered difficult to detect defects in the coated separator formed on the inner wall of the through hole. It is also considered difficult to remove defects in the coated separator without destroying the honeycomb structure. The separator in "1." above is considered effective for electrodes with a honeycomb structure.

[0015] 3. Voids may be formed in the first layer, and the voids may be filled with a portion of the second inorganic particle group.

[0016] 4. The second average particle size may be, for example, smaller than the first thickness.

[0017] Although the mechanism is unclear, the size of the voids may depend on the thickness of the first layer (first thickness). It is expected that the second inorganic particle group will be able to fill the voids more easily because the particle size of the second inorganic particle group is smaller than the first thickness.

[0018] 5. The ratio of the second average particle size to the first thickness may be, for example, 1 / 300 or less, because this is expected to reduce voids.

[0019] 6. The first average particle size may be, for example, 0.3 to 2 μm.

[0020] 7. The first thickness may be, for example, 10 to 150 μm.

[0021] 8. The second thickness may be, for example, 30 μm or less.

[0022] 9. The ratio of the second thickness to the first thickness may be, for example, 0.5 or less, because this can reduce an increase in battery resistance.

[0023] 10. The first layer may further include a first binder. The second layer may further include a second binder.

[0024] 11. The first inorganic particle group and the second inorganic particle group may each independently contain at least one type selected from the group consisting of aluminum oxide, aluminum oxide hydrate, aluminum hydroxide, and titanium oxide.

[0025] 12. The first electrode may be, for example, columnar. The first and second principal surfaces may be located at both ends of the first electrode in the axial direction.

[0026] 13. The battery may further include an electrolyte.

[0027] 14. A method for producing a battery includes the following steps (a) to (c): (a) A first electrode having a plurality of through holes formed therein is prepared. (b) A separator is formed to cover the inner wall of the through hole. (c) After (b), a second electrode is disposed in the through hole. The above (b) includes the following (b1) and (b2). (b1) A first layer is formed by applying a first paste to the inner wall of the through hole. (b2) A second layer is formed by applying a second paste onto the surface of the first layer. The second electrode has a polarity different from that of the first electrode. The first paste includes a first group of inorganic particles having a first average particle size. The second paste includes a second group of inorganic particles having a second average particle size. The second average particle size is smaller than the first average particle size.

[0028] According to the manufacturing method of the above "14.", the battery of the above "1." can be manufactured.

[0029] 15. The first electrode includes a first main surface and a second main surface. The second main surface is opposite to the first main surface. The through hole penetrates the first electrode from the first main surface to the second main surface. The above step (b1) may include suctioning the first paste from the first main surface or the second main surface. The above step (b2) may include suctioning the second paste from the first main surface or the second main surface.

[0030] By sucking the paste into the through-hole, the paste can be applied to the inner wall of the through-hole.

[0031] 16. The first paste may further include a first binder and a first dispersion medium. The second paste may further include a second binder and a second dispersion medium.

[0032] 17. The method for producing a battery may further include: (d) (d) The separator is impregnated with the electrolyte.

[0033] Hereinafter, an embodiment of the present disclosure (hereinafter may be abbreviated as "the present embodiment") and an example of the present disclosure (hereinafter may be abbreviated as "the present embodiment") will be described. However, the present embodiment and the example do not limit the technical scope of the present disclosure. [Brief description of the drawings]

[0034] [Figure 1] FIG. 1 is a schematic diagram showing an example of a battery according to the present embodiment. [Diagram 2] FIG. 2 is a schematic diagram showing an example of the first electrode. [Diagram 3] FIG. 3 is a schematic cross-sectional view showing a first example of a through hole. [Figure 4] FIG. 4 is a schematic cross-sectional view showing a second example of the through hole. [Diagram 5] FIG. 5 is a schematic cross-sectional view of a battery element. [Figure 6] FIG. 6 is a schematic cross-sectional view of the separator. [Figure 7] FIG. 7 is a schematic flow chart of the battery manufacturing method in this embodiment. [Figure 8] FIG. 8 is a first diagram showing the process of forming the separator in this embodiment. [Figure 9] FIG. 9 is a second diagram showing the process of forming the separator in this embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0035] <Definitions of terms, etc.> In this specification, the words "comprise," "include," "have," and variations thereof (e.g., "consisting of") are open-ended. The open-ended form may or may not include additional elements in addition to the required elements. The word "consisting of" is closed-ended. However, even in the closed form, additional elements that are normally associated impurities or unrelated to the disclosed technology are not excluded. The word "consisting essentially of..." is semi-closed. In the semi-closed form, the addition of elements that do not substantially affect the basic and novel characteristics of the disclosed technology is permitted.

[0036] In this specification, expressions such as "may" and "can" are used in the permissive sense of "possibly" rather than in the obligatory sense of "must".

[0037] In this specification, the order of execution of multiple steps, operations, and the like included in various methods is not limited to the order described unless otherwise specified. For example, multiple steps may proceed simultaneously. For example, multiple steps may be performed in sequence.

[0038] Geometric terms (e.g., "parallel," "perpendicular," "orthogonal," etc.) in this specification should not be interpreted in a strict sense. For example, "parallel" may deviate slightly from the strict meaning of "parallel." Geometric terms in this specification may include, for example, tolerances, errors, etc. in design, work, manufacturing, etc. The dimensional relationships in each figure may not match the actual dimensional relationships. In order to facilitate understanding of the disclosed technology, the dimensional relationships (length, width, thickness, etc.) in each figure may be changed. Furthermore, some configurations may be omitted.

[0039] In this specification, a numerical range such as "m to n%" includes an upper limit and a lower limit unless otherwise specified. That is, "m to n%" indicates a numerical range of "m% or more and n% or less". Furthermore, "m% or more and n% or less" includes "more than m% and less than n%". Furthermore, a numerical value arbitrarily selected from within the numerical range may be set as a new upper limit or lower limit. For example, a new numerical range may be set by arbitrarily combining a numerical value within the numerical range with a numerical value described in another part of this specification, in a table, in a figure, or the like.

[0040] In this specification, all numerical values ​​are modified by the term "about". The term "about" may mean, for example, ±5%, ±3%, ±1%, etc. All numerical values ​​may be approximations that may vary depending on the application of the disclosed technology. All numerical values ​​may be expressed in significant figures. Measurements may be average values ​​of multiple measurements. The number of measurements may be three or more, five or more, or ten or more. In general, the more measurements are made, the more reliable the average value is expected to be. Measurements may be rounded off based on the number of significant figures. Measurements may include errors associated with, for example, the detection limit of a measuring device.

[0041] In this specification, when a compound is expressed by a stoichiometric composition formula (e.g., "LiCoO2", etc.), the stoichiometric composition formula is merely a representative example of the compound. The compound may have a non-stoichiometric composition. For example, when lithium cobalt oxide is expressed as "LiCoO2", unless otherwise specified, the lithium cobalt oxide is not limited to the composition ratio of "Li / Co / O=1 / 1 / 2" and may contain Li, Co, and O in any composition ratio. Furthermore, doping, substitution, etc. with trace elements may be allowed.

[0042] In this specification, the term "solid content" refers to the total mass fraction of solid components in a coating material (e.g., a paste, etc.). Components dissolved in a dispersion medium are considered to be solid components.

[0043] In this specification, the "average particle size" refers to the particle size at which the cumulative frequency from the smaller particle size side reaches 50% in the volume-based particle size distribution. The average particle size can be measured by a laser diffraction method.

[0044] The "battery" in this specification may be any battery system. In this embodiment, as an example, a configuration in which the battery is a lithium ion battery is described. The second electrode has a polarity different from that of the first electrode. The first electrode may be a positive electrode or a negative electrode. In this embodiment, as an example, a configuration in which the first electrode is a negative electrode is described.

[0045] <Battery> FIG. 1 is a schematic diagram showing an example of a battery in this embodiment. Hereinafter, the "battery in this embodiment" may be abbreviated as "this battery". The battery 100 includes a battery element 50. The battery 100 may further include, for example, an electrolyte, an exterior body, etc. (none of which are shown). The exterior body may house the battery element 50 and the electrolyte. The exterior body may be, for example, a metal container or a pouch made of a metal foil laminate film. The electrolyte may be impregnated into the battery element 50. The battery element 50 includes a first electrode 10, a second electrode 20, and a separator 30. The battery element 50 may further include a current collector, a terminal, etc. (none of which are shown).

[0046] 《1st electrode》 2 is a schematic diagram showing an example of a first electrode. The first electrode 10 may have any shape. The first electrode 10 may be, for example, columnar. The first electrode 10 may be, for example, cylindrical or prismatic.

[0047] 2, the first electrode 10 extends in the Z-axis direction. The direction in which the first electrode 10 extends is also referred to as the "axial direction." In this embodiment, a cross section perpendicular to the axial direction is also referred to as the "XY plane." A cross section parallel to the axial direction is also referred to as the "YZ plane."

[0048] The first electrode 10 has a diameter d. The diameter d indicates the maximum width in the XY plane. The diameter d may be, for example, 1 to 1000 mm, or 10 to 100 mm. The first electrode 10 has a height h. The height h indicates the maximum width in the YZ plane. The height h may be, for example, 1 to 1000 mm, 5 to 500 mm, or 10 to 100 mm. The ratio of the height h to the diameter d may be, for example, 0.1 to 10, or 0.1 to 1.

[0049] In the present battery 100, the first electrode 10 is a negative electrode. The first electrode 10 includes a negative electrode active material. The first electrode 10 may further include a conductive material, a binder, and the like. The first electrode 10 may include, for example, by mass fraction, 1 to 10% of a binder, 0 to 10% of a conductive material, and the remainder being a negative electrode active material.

[0050] The negative electrode active material may contain any component. The negative electrode active material may contain at least one selected from the group consisting of graphite, soft carbon, hard carbon, silicon, silicon oxide, tin, tin oxide, and lithium titanate. The conductive material may contain, for example, acetylene black, carbon nanotubes, etc. The binder may contain, for example, styrene butadiene rubber (SBR), carboxymethyl cellulose (CMC), etc.

[0051] The first electrode 10 includes a first main surface 11 and a second main surface 12. The first main surface 11 and the second main surface 12 are disposed at both ends in the axial direction. The second main surface 12 is the opposite surface to the first main surface 11. Each of the first main surface 11 and the second main surface 12 may be parallel to the XY plane or may be non-parallel. Each of the first main surface 11 and the second main surface 12 may be a flat surface or a curved surface.

[0052] A plurality of through holes 13 are formed in the first electrode 10. The plurality of through holes 13 may be arranged regularly or randomly. The plurality of through holes 13 may be formed, for example, in a honeycomb shape. That is, the first electrode 10 may form a honeycomb core. In the XY plane, the through holes 13 are arranged at a density of, for example, 0.1 to 10 holes / mm. 2 The density may be

[0053] The through holes 13 penetrate the first electrode 10 from the first main surface 11 to the second main surface 12. That is, the through holes 13 have openings in each of the first main surface 11 and the second main surface 12. The direction (axial direction) in which the multiple through holes 13 extend may be parallel to the axial direction of the first electrode 10. In the XY plane, the through holes 13 may have any cross-sectional shape. The cross-sectional shape of the through holes 13 may be, for example, a circular shape or a polygonal shape. The polygon may be, for example, a 3- to 12-sided shape. The polygon may be a regular polygon.

[0054] 3 is a schematic cross-sectional view showing a first example of a through hole. In the XY plane, the cross-sectional shape of through hole 13 may be, for example, a quadrangle. "Hole diameter" indicates the maximum width of through hole 13 in the XY plane. Through hole 13 may have a hole diameter of, for example, 0.1 to 10 mm, may have a hole diameter of 0.5 to 5 mm, or may have a hole diameter of 1 to 3 mm.

[0055] The walls separating the through holes 13 are also called "ribs." In the XY plane, the ribs may extend, for example, in a mesh pattern. The ribs may have a thickness of, for example, 50 to 500 μm, or 100 to 300 μm.

[0056] 4 is a schematic cross-sectional view showing a second example of the through hole. In the XY plane, the planar shape of the through hole 13 may be, for example, a hexagonal shape. When the planar shape of the through hole 13 is a hexagonal shape, for example, distortion caused by charging and discharging tends to be alleviated.

[0057] <Separator> 5 is a schematic cross-sectional view of a battery element. The separator 30 covers the inner wall of the through-hole 13. The separator 30 is interposed between the first electrode 10 and the second electrode 20. The separator 30 extends so as to separate the second electrode 20 from the first electrode 10.

[0058] 6 is a schematic cross-sectional view of a separator. Separator 30 includes a first layer 31 and a second layer 32. First layer 31 is disposed between the inner wall of through-hole 13 (first electrode 10) and second layer 32. First layer 31 may be in direct contact with the inner wall. Second layer 32 may be in direct contact with first layer 31. Second layer 32 may be in direct contact with second electrode 20.

[0059] The first layer 31 has a first thickness T1. The second layer 32 has a second thickness T2. The second thickness T2 may be, for example, equal to or less than the first thickness T1. That is, the relationship "T2 / T1≦1" may be satisfied, the relationship "T2 / T1<1" may be satisfied, the relationship "T2 / T1≦0.9" may be satisfied, the relationship "T2 / T1≦0.6" may be satisfied, or the relationship "T2 / T1≦0.5" may be satisfied. By satisfying the relationship "T2 / T1≦0.5", an increase in the battery resistance may be reduced. For example, the relationship "0.3≦T2 / T1" may be satisfied.

[0060] The first thickness T1 may be, for example, 10 to 150 μm, 30 to 100 μm, or 30 to 70 μm. The second thickness T2 may be, for example, 1 to 60 μm, 10 to 40 μm, or 10 to 30 μm.

[0061] The first layer 31 contains the first inorganic particle group 1. The first inorganic particle group 1 has a first average particle diameter D150. The second layer 32 contains the second inorganic particle group 2. The second inorganic particle group 2 has a second average particle diameter D250. The second average particle diameter D250 is smaller than the first average particle diameter D150. That is, the relationship of "D250 < D150" is satisfied. For example, the relationship of "0 < D250 / D150 < 1" may be satisfied, or the relationship of "0.1 < D250 / D150 < 1" may be satisfied, or the relationship of "0.125 ≤ D250 / D150 ≤ 0.5" may be satisfied, or the relationship of "0.125 ≤ D250 / D150 ≤ 0.25" may be satisfied.

[0062] The first average particle diameter D150 may be, for example, 0.3 to 2 μm, or may be 0.8 to 1.5 μm. The second average particle diameter D250 may be, for example, 0.05 to 0.3 μm, or may be 0.1 to 0.2 μm.

[0063] Void 3 may be formed in the first layer 31. A part of the second inorganic particle group 2 may be filled in the void 3. By filling the void 3 with a part of the second inorganic particle group 2, an improvement in short-circuit resistance is expected. Table 1 below shows the relationship between the first thickness T1 and the average diameter of the void 3. The average diameter of the void 3 can be measured in an X-ray CT image.

[0064]

Table 1

[0065] As shown in Table 1 above, the size of the void 3 tends to depend on the first thickness T1. The second average particle diameter D250 of the second inorganic particle group 2 may be smaller than the first thickness T1, for example. Thereby, it is expected that the second inorganic particle group 2 can easily enter the void 3.

[0066] The average diameter of the voids 3 may be 1 / 2 to 1 / 3 of the first thickness T1. The second average particle diameter D250 of the second inorganic particle group 2 may be, for example, 1 / 2 or less of the first thickness T1. That is, the relationship "D250 / T1≦1 / 2" may be satisfied. For example, the relationship "D250 / T1≦1 / 3" may be satisfied, or the relationship "D250 / T1≦1 / 10" may be satisfied, or the relationship "D250 / T1≦1 / 100" may be satisfied, or the relationship "D250 / T1≦1 / 300" may be satisfied. By satisfying the relationship "D250 / T1≦1 / 300", improvement of short circuit resistance is expected.

[0067] The first inorganic particle group 1 and the second inorganic particle group 2 contain an electrically insulating inorganic compound. The first inorganic particle group 1 and the second inorganic particle group 2 may have the same composition or may have different compositions. For example, the first inorganic particle group 1 and the second inorganic particle group 2 may each independently contain at least one selected from the group consisting of aluminum oxide, aluminum oxide hydrate, aluminum hydroxide, and titanium oxide. For example, the first inorganic particle group 1 and the second inorganic particle group 2 may each independently contain at least one selected from the group consisting of alumina, boehmite, gibbsite, and titania.

[0068] The first layer 31 may further include a first binder (not shown). The second layer 32 may further include a second binder (not shown). The first binder and the second binder may have the same composition or may have different compositions. The first binder and the second binder may each independently include at least one selected from the group consisting of polyvinylidene fluoride (PVDF), vinylidene fluoride-hexafluoropropylene copolymer (PVDF-HFP), and polytetrafluoroethylene (PTFE).

[0069] The first layer 31 may contain, for example, 1 to 20% by mass of the first binder, and the remainder being the first inorganic particle group 1. The second layer 32 may contain, for example, 1 to 20% by mass of the second binder, and the remainder being the second inorganic particle group 2.

[0070] 《Second electrode》 The second electrode 20 is disposed in the through hole 13. The second electrode 20 may be columnar (pillar-shaped). The second electrode 20 extends along the axial direction of the through hole 13. The second electrode 20 may extend to the outside of the through hole 13.

[0071] In the present battery 100, the second electrode 20 is a positive electrode. The second electrode 20 includes a positive electrode active material. The second electrode 20 may further include a conductive material, a binder, and the like. The second electrode 20 may include, for example, by mass fraction, 1 to 10% of a binder, 1 to 10% of a conductive material, and the remainder being a positive electrode active material.

[0072] The positive electrode active material may include any component. The positive electrode active material may include at least one selected from the group consisting of lithium cobalt oxide, lithium nickel oxide, lithium manganate, lithium nickel cobalt manganate, lithium nickel cobalt aluminate, and lithium iron phosphate. The conductive material may include, for example, acetylene black. The binder may include, for example, PVDF.

[0073] 《Electrolyte》 The battery 100 may further include an electrolytic solution. The electrolytic solution includes a supporting electrolyte and a solvent. The supporting electrolyte is dissolved in the solvent. The supporting electrolyte may include any component. The supporting electrolyte may include at least one selected from the group consisting of LiPF6, LiBF4, and Li(FSO2)2N. The concentration of the supporting electrolyte may be, for example, 0.5 to 2 mol / kg.

[0074] The solvent is aprotic. The solvent may contain any component. The solvent may contain at least one selected from the group consisting of ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and diethyl carbonate (DEC). The electrolyte may further contain any additive in addition to the supporting electrolyte and the solvent.

[0075] <Battery manufacturing method> 7 is a schematic flow chart of a method for manufacturing a battery in this embodiment. Hereinafter, "the method for manufacturing a battery in this embodiment" may be abbreviated as "this manufacturing method". This manufacturing method includes "(a) preparation of a first electrode", "(b) formation of a separator", and "(c) arrangement of a second electrode". This manufacturing method may further include, for example, "(d) impregnation of an electrolyte solution", etc.

[0076] (a) Preparation of the first electrode This manufacturing method includes preparing a first electrode 10. The first electrode 10 has a plurality of through holes 13 formed therein. The first electrode 10 may be prepared by any method. For example, the first electrode 10 may be prepared by extrusion molding.

[0077] For example, a negative electrode paste is prepared by mixing a negative electrode active material, a binder, and a dispersion medium. For example, an appropriate dispersion medium can be selected depending on the type of binder, etc. The dispersion medium may contain, for example, water, etc. A mold is prepared. The mold has an extrusion port (die). The extrusion port corresponds to the shape of the first electrode 10. A molded body is formed by extruding the negative electrode paste from the extrusion port. The molded body is formed to have a plurality of through holes 13. The molded body is dried, and the first electrode 10 can be prepared.

[0078] (b) Formation of the separator This manufacturing method includes forming a separator 30. The separator 30 covers the inner wall of the through-hole 13. That is, this manufacturing method includes "(b1) Formation of a first layer" and "(b2) Formation of a second layer".

[0079] (b1) Formation of the first layer This manufacturing method includes forming a first layer 31 by applying a first paste to the inner wall of the through hole 13. The first paste includes a first inorganic particle group 1. The first paste may further include a first binder and a first dispersion medium. For example, the first inorganic particle group 1, the first binder, and the first dispersion medium are mixed to prepare the first paste. For example, an appropriate material may be selected as the first dispersion medium depending on the type of the first binder, etc. The first dispersion medium may include, for example, N-methyl-2-pyrrolidone (NMP), etc.

[0080] Any application method may be used. For example, the first paste may be sucked from the first main surface 11 or the second main surface 12. For example, the first paste is placed on the first main surface 11. The first paste may be sucked from the second main surface 12 side, for example, by a vacuum pump or the like. This allows the first paste to adhere to the inner wall of the through hole 13. Hereinafter, this method is also referred to as the "suction method." The suction method is suitable as a method for applying the paste to the inner wall of the through hole 13. On the other hand, the suction method may easily cause gas (air bubbles) to be mixed into the paste. The gas mixed into the paste may form voids 3. In this manufacturing method, the first layer 31 and the second layer 32 are formed in sequence, so that the voids 3 can be reduced.

[0081] The first layer 31 can be formed by drying the first paste attached to the inner wall. The first thickness T1 of the first layer 31 can be adjusted, for example, by the solid content of the first paste. The lower the solid content, the thinner the first thickness T1 tends to be. The solid content of the first paste may be, for example, 45 to 65%, or 55 to 65%.

[0082] (b2) Formation of the second layer This manufacturing method includes forming a second layer 32 by applying a second paste to the surface of the first layer 31. The second paste includes a second inorganic particle group 2. The second paste may further include a second binder and a second dispersion medium. For example, the second inorganic particle group 2, the second binder, and the second dispersion medium are mixed to prepare the second paste. For example, an appropriate material may be selected as the second dispersion medium depending on the type of the second binder, etc. The second dispersion medium may include, for example, NMP, etc.

[0083] The second paste may also be applied by a suction method. That is, the second paste may be suctioned from the first main surface 11 or the second main surface 12. This allows the second paste to adhere to the surface of the first layer 31. The second layer 32 may be formed by drying the second paste adhered to the first layer 31. The second thickness T2 of the second layer 32 may be adjusted, for example, by the solid content of the second paste. The solid content of the second paste may be, for example, 45 to 65%, or 45 to 55%.

[0084] (c) Arrangement of the second electrode The method includes, after the separator 30 is formed, disposing the second electrode 20 in the through hole 13 .

[0085] For example, prior to disposing the second electrode 20, an insulating treatment may be applied to the end faces (first main surface 11 and second main surface 12). For example, a resin particle group may be attached to the end faces by electrodeposition or the like. This may form an insulating film (not shown). The insulating film may inhibit contact between the second electrode 20 and the first electrode 10 when the second electrode 20 is inserted into the through-hole. The resin particle group may contain, for example, polyimide or the like.

[0086] The second electrode 20 may be disposed by any method. For example, a positive electrode paste is prepared by mixing a positive electrode active material, a conductive material, a binder, and a dispersion medium. For example, the positive electrode paste may be pressed into the through-hole 13. This allows the positive electrode paste to fill the through-hole 13. The positive electrode paste is dried, whereby the second electrode 20 may be formed.

[0087] In this manner, the battery element 50 can be formed. A current collector may be attached to the battery element 50. For example, a metal wire may be wound around the side surface of the first electrode 10. The metal wire may function as a current collector for the first electrode 10. For example, a metal foil may be attached to at least one of the first main surface 11 and the second main surface. The metal foil is in contact with the second electrode 20. The metal foil may function as a current collector for the second electrode 20. Furthermore, a terminal may be connected to each current collector.

[0088] (d) Impregnation of electrolyte The manufacturing method may include impregnating the separator 30 with an electrolytic solution. For example, an exterior body is prepared. The battery element 50 is housed in the exterior body. The electrolytic solution is injected into the exterior body. After the electrolyte solution is injected, the exterior body is sealed. The separator 30 may be impregnated with the electrolytic solution. In this manner, the battery 100 can be manufactured. EXAMPLES

[0089] <Production of test batteries> Test batteries No. 1 to 9 were produced as follows. Hereinafter, for example, "test battery No. 1" may be abbreviated as "No. 1."

[0090] No.1 (a) Preparation of the first electrode The following materials were prepared: Negative electrode active material: natural graphite (D50: 15 μm) Binder: CMC Dispersion medium: Ion-exchanged water

[0091] A negative electrode paste was prepared by mixing 100 parts by mass of a negative electrode active material, 10 parts by mass of a binder, and 60 parts by mass of a dispersion medium. The negative electrode paste was extruded from a mold to form a compact. The compact was dried at 120°C for 3 hours to form a first electrode. The first electrode had the following structure.

[0092] Shape: Cylindrical (diameter: 20 mm, height: 10 mm) Arrangement of through holes: Regular (honeycomb) Through hole: Regular hexagon (length of one side: 700 μm, rib thickness: 200 μm)

[0093] (b) Formation of the separator (b1) Formation of the first layer The following materials were prepared: First inorganic particle group: boehmite (D150: 0.5μm) First binder: PVDF (product name "KF Polymer", grade "♯8500", manufactured by Kureha Corporation) First dispersion medium: NMP

[0094] A first paste was prepared by mixing 57 parts by mass of the first inorganic particle group, 5 parts by mass of the first binder, and 38 parts by mass of the first dispersion medium. 3 to 5 g of the first paste was placed on the first main surface of the first electrode. The first paste was sucked into the through holes from the second main surface side by a vacuum pump. As a result, the first paste was attached to the inner walls of the through holes. The first electrode (honeycomb electrode) to which the first paste was attached was dried at 120°C for 15 minutes. As a result, a first layer was formed. The average thickness (first thickness) of the first layer was measured by an optical microscope. The first thickness was 65 μm.

[0095] (b2) Formation of the second layer The following materials were prepared: Second inorganic particle group: Aluminum oxide (D250: 0.1 μm) Second binder: PVDF (product name "KF Polymer", grade "♯8500", manufactured by Kureha Corporation) Second dispersion medium: NMP

[0096] A second paste was prepared by mixing 45 parts by mass of the second inorganic particle group, 7 parts by mass of the second binder, and 48 parts by mass of the second dispersion medium. 3 to 5 g of the second paste was placed on the first main surface of the first electrode. The second paste was sucked into the through holes from the second main surface side by a vacuum pump. This caused the second paste to adhere to the surface of the first layer. The first electrode to which the second paste was attached was dried at 120°C for 15 minutes. This formed the second layer. The thickness of the entire separator (the total thickness of the first layer and the second layer) was measured by an optical microscope. The thickness of the entire separator was 87 μm. That is, the thickness of the second layer (the second thickness) was 22 μm.

[0097] Fig. 8 is the first diagram showing the process of forming the separator in this embodiment. Fig. 8 shows an X-ray CT image after the formation of the first layer 31. A plurality of through holes 13 are formed in the first electrode 10 (honeycomb electrode). The inner walls of the through holes 13 are covered with the first layer 31.

[0098] Fig. 9 is a second diagram showing the process of forming the separator in this example. Fig. 9 shows an X-ray CT image after the first layer 31 is formed and an X-ray CT image after the second layer 32 is formed. After the first layer 31 is formed, spherical voids 3 are observed in the first layer 31. After the second layer 32 is formed (after the separator 30 is formed), the voids 3 become smaller. This is thought to be because a part of the second inorganic particle group 2 is filled in the voids 3.

[0099] (c) Placement of the second electrode An electrocoating paint (product name "Elecoat PI", manufactured by Shimizu Corporation) was prepared. The electrocoating paint contained a dispersoid and a dispersion medium. The dispersoid contained a resin particle group (polyimide). The dispersion medium contained water. A Ni flat wire (thickness: 50 μm, width: 3 mm) was prepared. The Ni flat wire was wrapped around the side of the first electrode. The Ni flat wire was connected to a power source. The first electrode was immersed in the electrocoating paint. A voltage of 30 V was applied for 2 minutes with the first electrode as the cathode and the working electrode as the anode. As a result, the first principal surface and the second principal surface were covered with an insulating film. After the formation of the insulating film, the first electrode was lightly washed with water to remove excess electrocoating paint. After washing, the first electrode was heat-treated at 180°C for 1 hour.

[0100] The following materials were prepared: Positive electrode active material: Lithium cobalt oxide (D50: 10 μm) Conductive material: Acetylene black Binder: PVDF (product name "KF Polymer", grade "♯1300", manufactured by Kureha Corporation) Dispersion medium: NMP

[0101] A positive electrode paste was prepared by mixing 64 parts by mass of a positive electrode active material, 4 parts by mass of a conductive material, 2 parts by mass of a binder, and 30 parts by mass of a dispersion medium. A plastic syringe was prepared. A first electrode (honeycomb electrode) was fixed in the barrel of the syringe. 3.5 g of positive electrode paste was placed between the first electrode and the plunger in the barrel. The positive electrode paste was pushed into the first electrode by the plunger. That is, the positive electrode paste was pressed into the through hole. When the positive electrode paste was discharged from the opening on the opposite side to the pushing side, the plunger was stopped from pushing. After the positive electrode paste was pressed into the first electrode, the first electrode was dried at 120°C for 3 hours. As a result, a second electrode was formed in the through hole. A battery element was formed as described above.

[0102] In the battery element, the DC resistance between the first electrode and the second electrode was measured by a tester. In Table 2 below, "OK" indicates that the DC resistance was 1 MΩ or more. "NG" indicates that the DC resistance was less than 1 MΩ. In the samples that showed an "OK" result, the DC resistance exceeded the measurement limit.

[0103] 0.5 g of positive electrode paste was applied to each of the first and second principal surfaces. Aluminum (Al) foil was attached to the first and second principal surfaces using the positive electrode paste as an adhesive. The Al foil was a current collector for the first electrode (positive electrode). The Al foil had a thickness of 15 μm. The battery element was dried at 120° C. for 15 minutes. A Ni flat wire (thickness: 50 μm, width: 3 mm) was wound around the side surface (outer peripheral surface) of the second electrode for one revolution. The Ni flat wire was a current collector for the second electrode (negative electrode). Stainless steel lead tabs (terminals) were welded to the Al foil and Ni flat wire, respectively.

[0104] (d) Impregnation of electrolyte A pouch made of an aluminum laminate film was prepared as an exterior body. The battery element was housed in the exterior body. 5 g of an electrolyte was injected into the exterior body. After the electrolyte was injected, the exterior body was vacuum sealed. The electrolyte had the following composition.

[0105] Electrolyte composition Supporting electrolyte: LiPF6 (concentration: 1mol / kg) Solvent: EC / EMC / DMC=1 / 1 / 1 (volume ratio)

[0106] Thus, a test battery was manufactured. The test battery had a design capacity of 400 mAh.

[0107] First charge / discharge Charging, resting, and discharging were carried out in sequence under the following conditions. Charging: CCCV, CC current = 40mA, CV voltage = 4.2V, final current = 10mA Pause: 10 minutes Discharge: CCCV, CC current = 40mA, CV voltage = 3V, final current = 10mA

[0108] Note that "CC" stands for constant current type, "CV" stands for constant voltage type, and "CCCV" stands for constant current-constant voltage type.

[0109] After the initial charge and discharge, the voltage of the test battery was adjusted according to the following conditions. Charging: CCCV, CC current = 40mA, CV voltage = 3.85V, final current = 10mA

[0110] After adjusting the voltage, the test battery was discharged for 5 seconds with a CC current of 200 mA. The voltage drop 5 seconds after the start of discharge was measured. The battery resistance was calculated from the voltage drop and the discharge current. The battery resistance is shown in Table 2 below.

[0111] No.2~9 Test batteries were manufactured having the separators shown in Table 2 below, respectively. The first thickness and the second thickness were adjusted by the solid content of the first paste and the second paste.

[0112] In No. 6, titanium oxide was used as the first inorganic particle group instead of boehmite.

[0113] In No. 9, the second layer was not formed. That is, in No. 9, the separator is the first layer. In No. 9, the insulation was insufficient, so the battery resistance was not measured.

[0114] [Table 2]

[0115] <Result> In Nos. 1 to 8, sufficient insulation was achieved. In Nos. 1 to 8, the separator had a first layer and a second layer, and the second average particle diameter was smaller than the first average particle diameter. In Nos. 1 to 8, it is considered that voids were reduced.

[0116] In No. 9, the insulation was insufficient. In No. 9, the separator has a single-layer structure. In No. 9, it is believed that large voids remain.

[0117] Nos. 1 to 6 had smaller battery resistance than Nos. 7 to 8. Nos. 1 to 6 satisfied the relationship "T2 / T1≦0.5."

[0118] The present embodiment and the present embodiment are illustrative in all respects. The present embodiment and the present embodiment are not restrictive. The technical scope of the present disclosure includes all modifications within the meaning and scope equivalent to the description of the claims. For example, it is also intended from the beginning that any configuration may be extracted from the present embodiment and the present embodiment, and that they may be arbitrarily combined. [Explanation of symbols]

[0119] 1 first inorganic particle group, 2 second inorganic particle group, 3 void, 10 first electrode, 11 first main surface, 12 second main surface, 13 through hole, 20 second electrode, 30 separator, 31 first layer, 32 second layer, 50 battery element, 100 battery.

Claims

1. A first electrode; A second electrode; Separator and Including, the first electrode includes a first major surface and a second major surface; The second main surface is an opposite surface to the first main surface, A plurality of through holes are formed in the first electrode, the through hole penetrates the first electrode from the first main surface to the second main surface, the separator covers an inner wall of the through hole, the second electrode has a polarity different from that of the first electrode; the second electrode is disposed in the through hole, The second electrode extends along an axial direction of the through hole, the separator includes a first layer having a first thickness and a second layer having a second thickness; the first layer is disposed between the inner wall and the second layer; the first layer includes a first group of inorganic particles having a first average particle size; the second layer includes a second inorganic particle group having a second average particle size, The second average particle size is smaller than the first average particle size, the first layer has voids formed therein; The voids are filled with a portion of the second inorganic particle group. battery.

2. The first electrode forms a honeycomb core.

10. The battery of claim 1.

3. The second average particle size is smaller than the first thickness. The battery according to claim 1 or 2.

4. A ratio of the second average particle diameter to the first thickness is 1 / 300 or less. The battery according to any one of claims 1 to 3.

5. The first average particle size is 0.3 to 2 μm. The battery according to any one of claims 1 to 4.

6. The first thickness is 10 to 150 μm. The battery according to any one of claims 1 to 5.

7. The second thickness is 30 μm or less. The battery of any one of claims 1 to 6.

8. a ratio of the second thickness to the first thickness is less than or equal to 0.5; The battery of any one of claims 1 to 7.

9. the first layer further comprises a first binder; the second layer further comprises a second binder; The battery of any one of claims 1 to 8.

10. The first inorganic particle group and the second inorganic particle group each independently contain at least one selected from the group consisting of aluminum oxide, aluminum oxide hydrate, aluminum hydroxide, and titanium oxide. The battery of any one of claims 1 to 9.

11. The first electrode is columnar, the first principal surface and the second principal surface are located at both ends of the first electrode in an axial direction, The battery of any one of claims 1 to 10.

12. Further comprising an electrolyte; The battery of any one of claims 1 to 11.

13. (a) preparing a first electrode having a plurality of through holes formed therein; (b) forming a separator covering the inner wall of the through hole; and (c) after (b), disposing a second electrode in the through hole. Including, The (b) is (b1) applying a first paste to the inner wall of the through hole to form a first layer; and (b2) applying a second paste onto a surface of the first layer to form a second layer; Including, the second electrode has a polarity different from that of the first electrode; The first paste contains a first group of inorganic particles having a first average particle size, The second paste includes a second inorganic particle group having a second average particle size, The second average particle size is smaller than the first average particle size. How batteries are manufactured.

14. the first electrode includes a first major surface and a second major surface; The second main surface is an opposite surface to the first main surface, the through hole penetrates the first electrode from the first main surface to the second main surface, The step (b1) includes suctioning the first paste from the first principal surface or the second principal surface; The step (b2) includes suctioning the second paste from the first principal surface or the second principal surface. A method for producing the battery according to claim 13.

15. The first paste further includes a first binder and a first dispersion medium, The second paste further includes a second binder and a second dispersion medium. A method for producing the battery according to claim 13 or 14.

16. (d) impregnating the separator with an electrolyte solution. Further comprising: A method for producing the battery according to any one of claims 13 to 15.

Citation Information

Patent Citations

  • Secondary battery and method of manufacturing the same

    JP2020123484A

  • Secondary battery

    JP2020123543A

  • Battery

    JP2022014065A

  • Electrode assembly and rechargeable battery with the same

    KR1020080082289A

  • Method for manufacturing separator-integrated electrode comprising inorganic layers with multilayer structure, and separator-integrated electrode manufactured thereby