Metal-fixture feedthrough, its manufacturing method and its use

Abstract

To provide a metal / fixing material feed-through for an airbag and / or an igniter of a belt tensioner, as well as a manufacturing method for the same.SOLUTION: The metal / fixing material feed-through has at least one metal pin 5, where the at least one metal pin 5 is fused and embedded into a penetration opening part 4 of a base body 1, in glass or a glass ceramic fixing material 10. A surface 110 of the glass or the glass ceramic fixing material 10 is a freely fused surface, which is on the same flat surface shared with an end face of the at least one metal pin 5. The freely fused surface does not have air bubble exposed in a region of an ignition cable in particular.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] The present invention generally relates to metal and fastener feedthroughs for feedthrough elements, for example for sensor feedthroughs and / or for large feedthroughs and / or for feedthroughs in transistor outline housings and / or for battery or capacitor feedthroughs, as well as such feedthroughs themselves. In particular, feedthroughs for ignition devices, such as those used for pyrotechnic ignition of personal protection devices, are provided, but also feedthroughs which can be used in particular for airbag igniters and / or belt tensioners and / or gas generators. In particular, the present invention relates to the design of the base of such feedthrough elements, to the manufacturing method thereof and to their application.

[0002] The sensor feedthrough can in particular supply power to the sensor element and / or transfer its signal to an evaluation unit. Large feedthroughs are generally used in safety containers, for example in liquid gas tanks and / or reactors.

[0003] In principle, a feedthrough for a battery or capacitor is understood to be a feedthrough through the housing of a battery or capacitor, including the accumulator. The term also encompasses the field of supercapacitors, also called supercaps. Usually, the feedthrough serves to contact the electrodes inside the housing of the battery or capacitor.

[0004] The transistor outline housing, also called TO housing, is a conductive electronic housing. Basically, the TO housing consists of two components: the base and the cap. The base ensures, among other things, the power supply of the enclosed components, while the cap, in the optoelectronic domain, serves to safely transmit optical signals. This includes both the transmitters (e.g. laser diodes) and receivers (e.g. photodiodes) of optical signals. The TO base is the mechanical foundation for assembling electronic and optical components, such as semiconductors, laser diodes, or simple electrical circuits. At the same time, the TO base supplies the protected components with power by means of connection pins.

[0005] In motor vehicles, airbags and / or belt tensioners are used in particular as devices for protecting people by pyrotechnics. Such safety systems can significantly reduce the risk of injury. However, a prerequisite is that the respective safety system does not fail in the event of a crash. Particular attention is paid here to the igniters of such pyrotechnic devices, which are essential for the functioning of such safety devices. In particular, the igniters must still function without problems many years after their manufacture. The average service life of such igniters is often said to be 15 years. In order to ensure a long-term problem-free functioning, it is necessary to ensure that the propellant present in the igniter does not change over time. Such changes can be caused, for example, by the ingress of moisture into the igniter. It is therefore important to seal the propellant of the igniter gas-tight. The igniter must also release the gas of the propellant to be ignited in the correct direction to ignite the propellant of the gas generator of the safety system.

[0006] To ensure this, igniters known from the prior art have a cap or cover and a relatively dense base, between which the propellant is enclosed in a cavity formed by these parts. The electric current for igniting the propellant is conducted via the base by means of an electrical connection. The base therefore as a rule has a through-opening in which a metal pin is present, which, on the one hand, can be supplied with power by means of a plug-in connection, and which, on the other hand, is connected, for example, by an ignition bridge, which, when energized, comes into contact with the propellant and brings about its ignition. The base is therefore also generally referred to as a feed-through element. In the design of the feed-through element, it must be ensured that in any case, when the propellant is ignited, the cap or cover or a part of it breaks off, but the electrical feed-through is not pushed out of the base.

[0007] In such a feed-through element, the base body is made of metal and the ignition bridge is realized by a welded bridge wire. In this embodiment, the metal pin is fixed as a needle in an electrically insulating fastener in the through opening of the base body. Usually, a glass material, in particular a glass solder, is used as the fastener. The metal pin is thus insulated from the external conductor by the glass. Likewise, ceramics, glass ceramics and / or polymers are also possible as insulating materials.

[0008] The second metal pin as a needle is welded or soldered to the outer conductor, also called or represented as the base or bottom plate. Thus, on the upper side of the feed-through element (i.e. the side facing the ignition cap of the final assembled ignition device), the bridge wire as the ignition bridge (often made of tungsten alloy) contacts the surface of the glass material. Since a rough surface can damage the bridge wire, the surface of the glass material usually needs to be polished so that the bridge wire is not damaged and the ignition element has a long life, for example in automotive use.

[0009] An ignition device of the aforementioned type is known, for example, from EP 1 813 906 B1.

[0010] EP 0 586 133 A1 describes the manufacture of a metal-fixture feedthrough for an airbag igniter, in which a contact needle is vitrified into a glass material in a through opening, and the surfaces of the substrate and the fixation material are polished before the attachment of the bridge wire.

[0011] A TO housing is shown, for example, in US Patent No. 8,908,728, where it is contemplated that a ground pin may be connected to the substrate in order to electrically ground the substrate.

[0012] Against this background, the object of the present invention is to provide a metal-fixture feedthrough for a feedthrough element, in particular for an igniter of an airbag and / or a belt tensioner, as well as a manufacturing method, in which the disadvantages of the prior art are avoided and in which grinding of the surfaces is avoided.

[0013] This problem is solved by a metal-fastening feedthrough and a method for its production according to the independent claims. Preferred embodiments and applications are evident from the dependent claims.

[0014] The metal-fixing material feed-through according to the invention comprises in particular a metal substrate and at least one through-opening in which at least one metal pin is fused and embedded in the electrically insulating glass or glass-ceramic fastening material and is thus fastened. The surface of the glass or glass-ceramic fastening material is a free-melting surface, which is particularly advantageously free of exposed bubbles. Free-melting in the context of the present invention means that the surface forms spontaneously upon cooling of the molten glass material. This surface visually resembles a fire-polished surface and is visible to the naked eye, in particular since it may have a mirror-like luster.

[0015] The surface of the free-melted fastener lies in one plane with the end face of at least one metal pin melt-embedded in the fastener, which of course means the metal pin end face closest to the fastener and provided for connection to a conductor or an ignition conductor, i.e. the upper side of the metal-fastener feed-through.

[0016] Usually, the production of a metal-fixture feedthrough starts with a pressing, which is placed in the through-opening together with a metal pin and then heated, so that the pressing melts and connects with the substrate and the metal pin. The pressing is usually produced by grinding a glass or glass-ceramic material, adding mainly organic binders and pressing it in a mold. It is also possible to sinter the pressing before the metal pin is melt-embedded. Likewise, a glass-ceramic material can be formed from a previously amorphous glass material during heating and / or cooling.

[0017] In the fusion embedment of the metal pin and in the connection with the substrate, the binder burns out. Usually, the glass or glass-ceramic fastener in the through opening is mixed with air bubbles and has protrusions on the surface of the substrate. Similarly, the metal pin is also arranged so that it protrudes from the surface of the substrate. It is therefore assumed that in order to obtain a flat surface lying in one plane, the surface must be polished flat.

[0018] In contrast, according to the invention, the surface of the fastener is free melted during the melting process, in which case, in particular, at least one metal pin is also arranged in the through-opening so that its end face is in one plane with the surface of the base body. The inventors have found that the free melting results in a smooth surface of the glass or glass-ceramic fastener, which does not require polishing.

[0019] Likewise, the present invention contemplates that a conductor, in particular an ignition conductor, is attached between the base and the at least one metal pin, electrically connecting the base and the at least one metal pin, and the surface of the fastener is free of exposed air bubbles, at least in the area of ​​the conductor.

[0020] Particularly advantageously, the entire surface of the fastener is free of exposed bubbles. However, it is technically sufficient and in accordance with the invention if the entire surface of the fastener is substantially free of melt bubbles, whereby the number of exposed bubbles on the surface is understood to be a maximum of 5. These bubbles may be distributed on the surface, but as explained above, they must not be distributed in the areas where the ignition line is present, i.e., in particular, where the fastener rests.

[0021] Usually, for the substrate, standard steels such as St35 and / or St37 and / or St38, or stainless steels and / or non-corrosive steels are used as materials for the substrate. Stainless steel according to DIN EN 10020 is the name of alloyed or non-alloyed steels whose sulfur and phosphorus content (so-called iron content) does not exceed 0.035%. According to this, further heat treatment (e.g. tempering) is often intended. Stainless steels include, for example, high purity steels in which components such as aluminum and silicon are separated from the melt by a special manufacturing process, as well as high alloy tool steels intended for subsequent heat treatment. These contain, in particular, chromium. For example, the following can be used: X12CrMoS17, X5CrNi1810, XCrNiS189, X2CrNi1911, X12CrNi177, X5CrNiMo17-12-2, X6CrNiMoTi17-12-2, X6CrNiTi1810, and X15CrNiSi25-20, X10CrNi1808, X2CrNiMo17-12-2, X6CrNiMoTi17-12-2.

[0022] However, in order to ensure maximum manufacturing efficiency of the feed-through according to the invention, it may be advantageous for the metal substrate not to consist of stainless steel. Instead, the substrate is advantageously formed from a steel of the 1.01xx to 1.07xx group (unalloyed quality steel), whereby the steel groups are designated according to DIN EN 10027-2, where the first digit denotes the main group of the material and the series of digits after the first point denotes the steel group number.

[0023] To ensure the best possible corrosion resistance, the substrate may be coated with a metal. Preferably, a nickel coating is used. This is particularly true for substrates made from unalloyed steel qualities.

[0024] The glass or glass-ceramic fastener is advantageously selected such that its thermal expansion is lower than that of the metal substrate. On melting and subsequent cooling, the substrate contracts, so to speak, relative to the solidified fastener, so that a so-called pressure feedthrough, also called pressure glass containment, is obtained. This means that the substrate exerts an axial pressure on the fastener, which increases the mechanical retention in the through opening.

[0025] In this way, a hermetically sealed metal-fixture feedthrough is achieved.

[0026] The inventors have found that in the above-mentioned process, in particular when the surface is free-melted, the glass or glass-ceramic fastener may indeed have bubbles in its volume with a bubble fraction BV, but at its surface it may have a glass skin with a bubble fraction significantly smaller than BV. The glass skin is particularly preferably substantially bubble-free, which means that there are a maximum of 5 bubbles or even that it is completely bubble-free. In particular, the glass skin and / or the surface of the fastener is bubble-free in the area where the ignition wire is placed.

[0027] Due to the free melted surface of the fastener, its roughness is less than in the case of conventional polished metal-fastener feedthroughs. In particular, the average roughness values ​​Ra of the surfaces of glass or glass-ceramic fasteners are less than 0.1 μm, in particular in the range of 0.02 μm to 0.05 μm. In contrast, typical Ra values ​​for conventional polished metal-fastener feedthroughs are 0.2 μm to 0.5 μm. Higher roughness values ​​of conventional polished fasteners essentially result from residual grinding marks, in particular in the form of grooves.

[0028] The average roughness value Ra is defined according to DIN EN ISO 4287:2010 and is determined as known to the person skilled in the art. The average roughness or average roughness value Ra represents the average distance from the measuring points in a vertical cross section, i.e. the profile of the microstructure, to the center line. The center line intersects with the actual profile in the relevant section such that the sum of the profile deviations (relative to the center line) is minimal. The average roughness Ra corresponds to the arithmetic mean of the absolute deviations from the center line.

[0029] Furthermore, the smoother surface of the metal-fixture feed-through according to the invention has the advantage that, compared to the prior art, the risk of damage to the bridge wire when it rests on the fixture is reduced. In airbag igniters or belt tensioners, the bridge wire is in contact with the ignition material, which can often be present in powder form. Even if the powder particle size is usually larger than the grinding groove, powder wear and thus very fine particles occur in the course of the product's life, which can get caught in the groove under the bridge wire and subject it to mechanical stress. This is avoided by the metal-fixture feed-through according to the invention.

[0030] In a further preferred embodiment, the substrate is formed such that there is a continuous transition from the surface of the substrate to the inner wall of the through-opening, in particular the gradient increases in the direction of the inner wall of the through-opening. A continuous transition means that if the cross section of this region is interpreted as a curve, the first derivative of this curve has a stationary profile. In contrast, substrates from the prior art have sharp creases, so that the first derivative of their cross sections is non-stationary. This form has the advantage that it is possible to simply manufacture the substrate, and in particular the through-opening, by a molding and / or punching process, without the need to use an additional post-processing step to achieve a perpendicular angle. A further advantage of this substrate design is that the volume of the compression material involved in the filling level of the fastening material in the through-opening is less important with respect to volumetric variations. This means that for a given volumetric variation, the filling level in the through-opening changes by less than the diameter of the fastening material, which is less important for the installation of the bridge wire than a step that may possibly occur in the event of insufficient filling.

[0031] Furthermore, the continuous transition has the effect of providing a thin layer of fastener in the area that slopes flat to the through opening. Surprisingly, it has been shown that, even though this is a pressure glass encapsulation, no fastener delamination is observed.

[0032] Particularly preferably, a groove is provided between the inner wall of the through-opening and the glass or glass-ceramic fastener in the area of ​​the surface. A groove generally denotes a depression in the surface of the fastener. The width B of the groove is preferably at most 0.13 mm, particularly preferably 0.005 mm to 0.13 mm or 0.01 to 0.13 mm. Particularly preferably, the depth T of this groove is at most 0.03 mm, in particular at most 0.015 mm, particularly preferably the depth T is 0.05 mm to 0.025 mm.

[0033] The formation of the grooves can be promoted by the aforementioned configuration of the transition from the surface of the base body to the inner wall of the through opening, i.e. this configuration and the presence of the grooves work together in a particularly advantageous manner.

[0034] The presence of the groove has the advantage that it makes it possible to achieve a stop against film coatings on the surface of the fastener and / or on the surface of the substrate, in particular during operation of the metal-fastener feedthrough. Such films may in particular be water-containing films and / or coatings which may arise in long-term operation and which in the worst case may cause a reduction in the contact resistance, short circuits and / or electrochemical corrosion and thus damage to the components comprising the metal-fastener feedthrough.

[0035] It is particularly advantageous that the grooves can be formed spontaneously upon melting and subsequent cooling of the fixing material. This is believed to result from the adhesive and wettability of the glass or glass-ceramic fixing material. Similarly, it is also possible to imprint the grooves, as long as the heated fixing material is still moldable.

[0036] The embodiment in which the glass or glass ceramic fastener rests and / or rests on the surface of at least one metal pin without groove formation is preferred. This means that the aforementioned grooves are only present in the transition area from the fastener to the base body, but not in the transition area from the fastener to the metal pin. This can be achieved if the radius of the rounding possibly present in the metal pin, i.e. the radius of the protruding part from the end face to the side, is smaller than the radius of the transition from the surface of the base body to the inner wall of the through-opening.

[0037] As already explained, the grooves here can advantageously act as a stopper against disturbing surface coating films which can affect the electrical behavior of the conductor, in particular the ignition behavior, while on the other hand the grooves are advantageously dimensioned in such a way that disturbing large particles cannot be caught between the grooves and the conductor and mechanically overstress the latter.

[0038] In particular, the metal pin is arranged such that its upper side, i.e. the flat end face, is in one plane with the surface of the glass or glass-ceramic fastening material. Advantageously, the metal pin is chamfered, i.e. in particular the transition between the upper side of the metal pin and the side wall of the metal pin is rounded, the transition point between this rounding and the side wall being below the surface of the glass or glass-ceramic fastening material.

[0039] In particular, the groove is circumferential and in particular circular: the through-opening is preferably designed circularly in top view, the groove running circularly, possibly at a distance, along the inner wall of the through-opening.

[0040] Particular preference is given to a metal-fixture feedthrough, in which an electrical conductor, in particular a linear conductor, in particular an ignition conductor, is attached between the substrate and the at least one metal pin, electrically conductively connecting the substrate and the at least one metal pin. The conductor rests at least partially on the surface of the glass or glass-ceramic fixture, preferably bridging the groove. In this region, in which the groove is bridged, there is free space below the conductor. It is likewise possible to fill this free space and / or to coat it, for example, with a plastic, in particular a hydrophobic plastic or one with a hydrophobic surface. As explained, the groove can in particular serve as a release edge for conductive coatings or corrodible films. The surrounding edge, so to speak, protects the fixture and / or the at least one metal pin from these coatings and / or films.

[0041] In a further preferred embodiment, the substrate is made of steel, in particular non-corrosive stainless steel, at the interface with the glass or glass ceramic fastener.Also preferably, at least one metal pin is made of steel, in particular non-corrosive stainless steel, at the interface with the glass or glass ceramic fastener.Particularly advantageously, steel and / or stainless steel exhibit wettability and / or adhesion to glass, which at least aids in the formation of the groove.

[0042] It is advantageous and included in the present invention if the upper side of the metal pin is in the same plane as the surface of the glass or glass ceramic fastener. In particular, the transition between the upper side of the metal pin and the side wall of the metal pin may be rounded, the transition point between this roundness and the side wall being below the surface of the glass or glass ceramic fastener. That is to say, this roundness is, so to speak, recessed into the fastener. This has the advantage that the possibility of crack formation at the interface between the metal pin and the fastener is reduced compared to a sharp transition in which the side wall of the metal pin is in direct contact with the surface of the metal pin perpendicularly.

[0043] As explained, the upper side of the metal pin, i.e. the end face of the metal pin, is in one plane with the surface of the glass or glass-ceramic fastener. In particular, the transition between the upper side of the metal pin and the side wall of the metal pin may be rounded, the transition point between this roundness and the side wall being below the surface of the glass or glass-ceramic fastener. That is to say, this roundness is, so to speak, recessed into the fastener. This has the advantage that the possibility of crack formation at the interface between the metal pin and the fastener is reduced compared to a sharp transition in which the side wall of the metal pin abuts directly perpendicularly to the surface of the metal pin.

[0044] It is also intended that an electrical conductor, in particular an ignition conductor, is attached between the base body and the at least one metal pin, which electrically connects the base body and the at least one metal pin. This is usually welded. This conductor rests at least partially on the surface of the glass or glass-ceramic fastener. In particular, it bridges the groove described.

[0045] The invention likewise comprises a method for producing a metal-fastener feedthrough, in particular a metal-fastener feedthrough for an igniter of an airbag and / or a belt tensioner, having at least one metal pin, which at least one metal pin is melt-embedded in a through opening of a substrate in a glass or glass-ceramic fastener by heating and subsequent cooling, the glass or glass-ceramic fastener having a surface between the at least one metal pin and the substrate, in which the heated fastener is free-melted at this surface when the at least one metal pin is melt-embedded in the glass or glass-ceramic fastener.

[0046] In this process, the fastening material is anglased on the inner wall of the through opening and on the outer wall of at least one metal pin.

[0047] All the features previously described for the metal-fastener feedthrough are also applicable to this method.

[0048] The claimed method includes a portion of an overall manufacturing process for a feedthrough and / or an airbag igniter or belt tensioner.

[0049] The substantially bubble-free surface of the fastener is preferably formed in a free melt, particularly spontaneously. Substantially bubble-free means that the surface has a maximum of 5 bubbles, which of course also includes a completely bubble-free surface. Preferably, the surface of the glass or glass-ceramic fastener has an average roughness value Ra of less than 0.1 μm, in particular Ra is in the range of 0.015 μm to 0.055 μm, particularly advantageously 0.02 μm to 0.05 μm. In a preferred embodiment, the glass or glass-ceramic fastener abuts against the surface of at least one metal pin without groove formation. This means that it is particularly advantageous that grooves are present between the substrate and the fastener, but not between the fastener and the metal pin.

[0050] The through-opening itself is preferably designed circularly in top view, and the groove particularly preferably runs circularly along the inner wall of the through-opening. A circular through-opening can be obtained in particular by punching and / or molding. However, drilling and other suitable methods are likewise possible.

[0051] As already explained, a particularly advantageous method is to produce the base body and / or the through-opening by molding and / or punching. The base body can be produced in a particularly material-efficient manner by molding, with at least one through-opening being punched out.

[0052] It is particularly advantageous if the base body is shaped or shaped in such a way that there is a continuous transition from the surface of the base body to the inner wall of the through-opening, in particular with a gradient that increases in the direction of the inner wall of the through-opening. This corresponds, so to speak, to a rounding with a gradual incline. This shape can be produced in particular in the punching process of the through-opening.

[0053] In a preferred method, a groove (55) is formed autonomously between the inner wall of the through-opening and the glass or glass-ceramic fastening material in the area of ​​the surface during heating and / or cooling, or it is imprinted, for example, with a stamping or embossing tool. In particular, the groove preferably has a width B of at most 0.13 mm. Particularly preferably, the depth T of the groove is at most 0.03 mm, in particular at most 0.015 mm, particularly preferably the depth T is between 0.05 mm and 0.025 mm.

[0054] Likewise, the grooves can be impressed with a suitable tool, for example with a stamp, or produced by removing material.

[0055] In further processing, electrical conductors may be attached, in particular welded, between the metal pin and the surface of the substrate as described.

[0056] Likewise, it is often the case that at least one further conductor, in particular a metal pin, is conductively connected to the substrate. This is typically an earth or ground conductor. The described conductive connection between the metal pin and the substrate is typically a solder connection. It is also possible to weld this conductor to the substrate.

[0057] A preferred application of the metal-fastener feed-through according to the invention and / or the result of the method according to the invention is an airbag igniter and / or a belt tensioner and / or a gas generator.

[0058] In the case of airbag igniters and / or belt tensioners and / or gas generators, the metal pins fixed in the through-openings are generally gold-coated at least in partial regions along their axis, as are the ground pins soldered to the base body. The gold coating provides permanent insensitivity to corrosion and a permanent contact. In many cases, the metal pins are gold-coated in their end regions. Thus, the regions of the metal pins which are present in the plug connection during assembly for the purpose of using the ignition device are preferably gold-plated. In this way, the contact resistance at the plug contacts can be reduced.

[0059] In an advantageous embodiment, at least two metal pins are electrically conductively connected to one another on the side of the base body facing the propellant by an ignition bridge, which can be formed by the ignition wire already described.

[0060] As mentioned above, the roughness, or rather the smoothness in the context of the present invention, of the fixing surface can be characterized by the average roughness Ra. Similarly, the average roughness depth Rz can also be expressed as known to those skilled in the art.

[0061] In the tests which are also examples, the described metal-fastener feedthroughs were produced by the described method and the roughness of the fastener surface which was free melted according to the invention was determined. In table 1, for comparison, the measured values ​​of the fastener surface polished according to the prior art are given. As a measuring method, a tactile measurement known to the person skilled in the art using a Hommel Taster is applied.

[0062] [Table 1]

[0063] In the following, the invention will be explained in more detail with the aid of figures. The figures are not to scale and the illustrated embodiments are schematic. These figures also represent exemplary embodiments. All reference symbols shown in the figures apply to the respective other figures. [Brief description of the drawings]

[0064] [Figure 1] A known ignition device includes a prior art metal-and-fixture feedthrough having a polished surface on which an ignition wire rests. [Diagram 2] 1 is a cross-section of a metal-fixture feedthrough according to the present invention parallel to its axial centerline. [Diagram 3] 3 is a cutaway from FIG. [Figure 4] 1 is a photograph of a top view of a metal-fixture feedthrough according to the present invention and a measurement curve of the groove.

[0065] FIG. 1 shows an ignition device known from the prior art for pyrotechnical protection devices, here an airbag ignition device as an example. In this case, FIG. 1 shows, inter alia, a cross-section of a metal-fixing material feedthrough. The metal-fixing material feedthrough comprises a metal carrier part with a base body (1), which here has a disk-shaped basic shape. Basic shapes with open areas are likewise known and are included in the present invention. The metal-fixing material feedthrough according to the invention is often also called a base element or, for short, a base or, in English, a header. Furthermore, a metal pin (5) is arranged as a functional element in the through opening (4) of the base body (1). The through opening (4) is punched out of the base body (1). The metal pin (5) serves to contact the electric current with the ignition bridge (9), via which the propellant (25) enclosed in the finished igniter is ignited. The ignition bridge is placed on the upper side (11) of the base body. The upper side refers to the side facing the propellant. The ignition device is closed by a cap (2) which, together with the base body (1), forms a cavity for containing a propellant (25). Usually, the cap (2) is welded to the base body.

[0066] In the prior art, current feedthroughs in the through openings (4) are especially designed as glass-to-metal feedthroughs, in which the glass acts as a fastener (10) in the metal substrate (3) between the metal pin (5) and the wall of the through opening (4). Likewise, it is also possible to use high-performance polymers or other suitable materials in the through openings, as well as glass-ceramic materials.

[0067] In the example shown in Fig. 1, the through opening (4) is arranged eccentrically with respect to the axial center axis of the base body (1). This ensures sufficient space for fixing the second metal pin (6) even in the case of a small radius of the base body (3). The second metal pin (6) is butt-soldered to the base body (1) by a solder connection and therefore serves as a ground pin, also called ground needle (6). As the solder material (7), in particular a metal solder material, in particular a hard solder, is used. The solder material (7) forms a meniscus between the surface of the base body and the ground needle (6).

[0068] In contrast thereto, FIG. 2 shows a cross section of a metal-fixing material feedthrough according to the invention parallel to and passing through its axial central axis. The substrate (1) has a first surface (11), here the upper side, and a second surface (12), here the lower side, which in many embodiments extends parallel thereto. The upper side (11) usually faces the propellant (25), and the electrical contact is usually made on the lower side (12). The metal substrate (1) has a through opening (4), through which a metal pin (5) is guided as a needle. The through opening (4) may be punched out of the substrate (1). Here, the substrate (1) as a whole represents a punched part, since in this example the outer contour of the substrate (1) was likewise punched out of a metal strip. However, it is likewise possible and within the scope of the invention that the substrate is produced from wiring material by cold forming. Within the through opening (4), a metal pin (5) is fused and embedded, i.e. fixed, as a first needle, also called a contact needle, electrically insulated from the substrate (1) by means of a glass or glass-ceramic fixing material (10).

[0069] A first metal pin (5) is in particular hermetically sealed in a first through opening (4) of the metal substrate (1). The glass or glass-ceramic fastener (10) of this metal-fastener feedthrough is completely surrounded by the material of the substrate (1), which represents the outer conductor.

[0070] The glass or glass-ceramic fastening material (10) has in particular a lower coefficient of thermal expansion than the metal of the substrate (1), so that the substrate (1) on cooling after glass-encapsulation of the metal pin (5) in the fastening material (10) contracts, as it were, relative to this fastening material (10) and thus to the glass-metal feedthrough, thus exerting a permanent mechanical pressure on this glass-metal feedthrough and on the fastening material (10). In this way, a particularly tight and mechanically stable connection is created between the metal pin (5), the fastening material (10) and the substrate (1). This arrangement is called pressure glass-encapsulation and is preferred, for example, for airbag igniters. The use of glass and / or glass-ceramic materials is likewise possible and falls within the scope of the invention.

[0071] The surface (110) of the fastener (10) on the upper side (11) of the substrate (1) is a free-melt surface, which is in one plane with the end face (50) of the fusion-embedded metal pin (5) and advantageously also with the upper side (11) of the substrate. As already explained, the free-melt surface has a reduced bubble proportion compared to the volume of the fastener (10), and is advantageously characterized by a bubble-free glass skin (40) exposed on its surface (110), at least in the region of the ignition conductor.

[0072] The ignition conductor (9) is placed on the surface (110) of the fastener and is welded to both the metal pin (5) and the base (1), i.e., to the end face (50) of the metal pin (5) and the surface (110) of the base (1). The groove (55) is not shown.

[0073] The second metal pin (6) is connected to the base (1) as a ground needle by a solder material (7).

[0074] Figure 3 shows a cut-away from Figure 2, which is illustrated as a dashed rectangle, corresponding to an enlarged area of ​​the base (1), the fastener (10) and the end face (50) of the metal pin (5). For clarity, the ignition wire (9) is not shown.

[0075] However, in FIG. 3, a groove (55) can be seen which is present between the base (1) and the fixing material (10). The groove has a width B and a depth T. The groove (55) may in particular be formed as a meniscus-type profile attached to the base (1) and the fixing material (10). The width B of the groove is at most 0.13 mm, in particular 0.005 mm to 0.13 mm or 0.01 to 0.13 mm, and the depth T is at most 0.03 mm, in particular at most 0.015 mm, in particular 0.025 mm to 0.05 mm.

[0076] In particular, the radius of the transition from the surface (11) of the base to the inner wall (100) of the through opening may be greater than the radius of the transition between the outer wall of the fused-in metal pin (5) and the end face (50) of said metal pin (5). For the sake of clarity, this radius is not shown in Figure 3. This ratio also results in particular in the presence of the groove (55) at the transition to the base (1) but not at the transition to the metal pin (5).

[0077] Likewise, in Fig. 3 a glass skin (40) is shown which has a significantly lower bubble content than the volume of the fastener (10). In Fig. 3 the glass skin (40) is present on the upper side (11) of the metal-fastener feedthrough. It is likewise possible and within the scope of the invention if a glass skin is also present on the lower side (12). This applies in particular if the fastener (10) on the lower side (12) is also free melted.

[0078] The glass skin is visible by optical methods, in particular by microscope, although its thickness may be in the range of atomic layers.

[0079] The inner wall (100) of the through-opening (4) is in direct contact with the fastening material (10), which is glazed to the inner wall (100). It is also possible for a glass skin with a reduced bubble content to be present between the inner wall (100) of the through-opening and the fastening material (10). The same applies to the interface between the fastening material (10) and the outer wall of the metal pin (5).

[0080] FIG. 4 shows a photograph of a top view of a metal-fixture feedthrough according to the invention and a measurement curve of the groove. The through-opening is circular and filled with the fastener (10). A metal pin (5) is glass-encapsulated in it, the end face (50) of which is visible. The inner wall (110) of the through-opening is furthermore particularly highlighted by a dashed line. As explained, this is an unpolished surface, the fastener surface is free-melted. No exposed air bubbles are visible. The glass skin is, so to speak, smooth or tight.

[0081] Also shown are measurements of the groove (55) for its depth T and width B. The measurements were made using a digital measuring microscope.

[0082] Up until now, especially in the case of industrial mass production of airbag igniters and / or belt tensioners, metal-fixture feedthroughs have been ground on their upper side, which removes both the metal and the fixture surfaces. This is usually followed by a cleaning step.

[0083] In contrast, the metal-fixture feed-throughs according to the invention have the advantage that their fixing surface is free-melted. As a result, the metal surface is not polished and a processing step can be omitted. Furthermore, the glass or glass-ceramic fixing materials according to the invention have the property of forming an at least almost bubble-free surface when free-melted, so that the risk of exposed bubbles is significantly reduced. Exposed bubbles are undesirable in the installation of ignition wires and must therefore be avoided. [Explanation of symbols]

[0084] 1 Base 2 Cap 4 Feedthrough opening 5. Functional element, first metal pin 6 Conductor, second metal pin, ground pin 7 Metal Solder Materials 9 Bridge wire, ignition conductor 10 Electrical insulating fasteners 11 Surface of the substrate, upper side 12 Surface of the substrate, underside 25 Propellant 50 End face of first metal pin 55 Groove 40 Glass Skin 100 Inner wall of through opening 110 Surface of fixing material B Groove width T-slot depth

Claims

1. A metal-and-fixture feedthrough for an igniter of an airbag and / or a belt tensioner, comprising at least one metal pin (5), said at least one metal pin (5) being fused and embedded in a through-opening (4) of a base body (1) in a glass or glass-ceramic fixing material (10), the surface (110) of the glass or glass-ceramic fastening material (10) is a free melt surface and is in one plane with the end face (50) of the at least one metal pin (5); and 10. A metal-fixture feedthrough, characterized in that the surface (110) of the glass or glass-ceramic fixture (10) has an average roughness value Ra according to DIN EN ISO 4287 of less than 0.1 μm or in the range of 0.015 μm to 0.05 μm.

2. 2. The metal-fixture feedthrough according to claim 1, characterized in that an electrical conductor (9) or an ignition conductor (9) is attached between the base body (1) and the at least one metal pin (5), electrically connecting the base body (1) and the at least one metal pin (5), and a surface (110) of the glass or glass-ceramic fixing material (10) is free of exposed air bubbles in the area of ​​the electrical conductor (9) or the ignition conductor (9).

3. 3. The metal-fixture feedthrough according to claim 1 or 2, characterized in that the glass or glass-ceramic fixture (10) has bubbles in its volume with a bubble fraction BV and at its surface (110) has a glass skin (40) with a bubble fraction significantly smaller than BV, with a maximum of 5 bubbles, or without any bubbles.

4. 4. The metal-fixing material feedthrough according to claim 1, wherein there is a continuous transition from the surface (11) of the base body to the inner wall (100) of the through opening (4).

5. 5. The metal-fastening material feedthrough according to claim 4, characterized in that a groove (55) is present between the inner wall of the through opening (4) and the glass or glass-ceramic fastening material (10) in the area of ​​its surface (110).

6. 6. The metal-fixing material feedthrough according to claim 5, characterized in that the groove (55) has a width B of maximum 0.13 mm or between 0.005 mm and 0.13 mm or between 0.01 and 0.13 mm and / or the groove (55) has a depth T of maximum 0.03 mm or maximum 0.015 mm or a depth T of 0.05 mm to 0.025 mm.

7. 7. The metal-fastener feedthrough according to claim 1, wherein the glass or glass-ceramic fastener (10) abuts the surface of the at least one metal pin (5) without groove formation.

8. 7. The metal-fixing material feedthrough according to claim 5 or 6, characterized in that the through opening (4) is circular in top view and the groove (55) runs along the inner wall (100) of the through opening (4) in a circular manner.

9. 9. The metal-fixing material feedthrough according to claim 5, 6 or 8, characterized in that an electrical conductor (9) or an ignition conductor (9) is attached between the base body (1) and the at least one metal pin (5), electrically connecting the base body (1) and the at least one metal pin (5), the electrical conductor (9) or the ignition conductor (9) resting at least partially on the surface (110) of the glass or glass-ceramic fastener (10) and bridging the groove (55).

10. 10. The metal-fastening feedthrough according to claim 5, 6, 8 or 9, characterized in that the substrate (1) consists of steel, in particular non-corrosive stainless steel, at least at the interface to the glass or glass-ceramic fastening (10), in particular the steel and / or stainless steel of the substrate (1) exhibits wettability and / or adhesion properties to glass that at least assist in the formation of the groove (55).

11. A method for producing a metal-fastener feedthrough, in particular a metal-fastener feedthrough for an igniter of an airbag and / or a belt tensioner, comprising at least one metal pin (5), said at least one metal pin (5) being fused and embedded in a through-opening (4) of a base body (1) in a glass or glass-ceramic fastener (10), said glass or glass-ceramic fastener (10) having a surface (110) between said at least one metal pin (5) and said base body (1), 10. A method for manufacturing a glass or glass-ceramic fastener, comprising the steps of: melting and embedding the at least one metal pin (5) in the glass or glass-ceramic fastener (10) and causing the heated fastener to be free-melted at the fastener surface (110), such that the surface (110) of the glass or glass-ceramic fastener (10) has an average roughness value Ra according to DIN EN ISO 4287 of less than 0.1 μm or in the range of 0.015 μm to 0.05 μm.

12. 11. Use of a metal-fastener feedthrough according to any one of claims 1 to 10 in an airbag igniter and / or a belt tensioner or for producing an airbag igniter and / or a belt tensioner.